JP5922278B1 - Metal spraying method - Google Patents
Metal spraying method Download PDFInfo
- Publication number
- JP5922278B1 JP5922278B1 JP2015072629A JP2015072629A JP5922278B1 JP 5922278 B1 JP5922278 B1 JP 5922278B1 JP 2015072629 A JP2015072629 A JP 2015072629A JP 2015072629 A JP2015072629 A JP 2015072629A JP 5922278 B1 JP5922278 B1 JP 5922278B1
- Authority
- JP
- Japan
- Prior art keywords
- coating
- sprayed coating
- metal spraying
- base material
- thermal spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】 溶射被膜に対し特有の配合による塗料を塗布し含浸させることにより、該溶射被膜の封孔処理及び強度増強に加えて、同溶射被膜の基材表面に対する付着強度の増強をも図ることができる金属溶射方法の提供。【解決手段】 基材1の表面1aに金属溶射を行い、該溶射により形成された溶射被膜2に、アルコキシ基、グリシド基及び炭素数が6〜10のアルキル基を含有するシリコーン化合物混合体とヘキサメチル系ポリイソシアネートとを1:1〜7の重量比で配合して成る一液型塗料5を含浸し硬化させることにより、上記溶射被膜2に封孔処理を施しつつ該溶射被膜2の強度を増強すると共に該溶射被膜2の基材表面1aに対する付着強度の増強を図ることができる。又上記塗料5は溶射被膜2上に耐熱性・対候性が著しく良好で且つ高強度の塗膜5′を形成する。【選択図】 図2PROBLEM TO BE SOLVED: To increase adhesion strength of a thermal spray coating on a substrate surface in addition to sealing treatment and strength enhancement of the thermal spray coating by applying and impregnating a paint with a specific composition to the thermal spray coating. Provide a metal spraying method that can be used. SOLUTION: A metal compound is sprayed on a surface 1a of a base material 1, and a silicone compound mixture containing an alkoxy group, a glycid group, and an alkyl group having 6 to 10 carbon atoms is formed on a sprayed coating 2 formed by the spraying. By impregnating and curing a one-component paint 5 containing hexamethyl polyisocyanate in a weight ratio of 1: 1 to 7, the sprayed coating 2 is subjected to sealing treatment to increase the strength of the sprayed coating 2. In addition to the enhancement, the adhesion strength of the thermal spray coating 2 to the substrate surface 1a can be enhanced. The coating 5 forms a highly strong coating 5 'on the sprayed coating 2 with extremely good heat resistance and weather resistance. [Selection] Figure 2
Description
本発明は、鉄等の金属又はコンクリート又はモルタルから成る基材の表面に金属溶射を施す方法に関する。 The present invention relates to a method for performing metal spraying on the surface of a substrate made of a metal such as iron or a concrete or mortar.
従来の金属溶射方法として、下記特許文献1は、鉄から成る基材の表面に金属溶射被膜を形成し、該溶射被膜にシランカップリング剤を含浸し硬化させて封孔処理を施し、該シランカップリング剤の被膜上に塗料を塗布して塗膜を形成する金属溶射方法を開示している。
As a conventional metal spraying method, the following
又下記特許文献2は、鉄から成る基材の表面に金属溶射被膜を形成し、該溶射被膜に芳香族オリゴマー、エポキシポリオール樹脂、イソシアネート樹脂、顔料及び有機溶剤を含む封孔処理剤を含浸し硬化させて封孔処理を施す金属溶射方法を開示している。
Further,
上記特許文献1の金属溶射方法はシランカップリング剤の硬化により封孔処理を施すと共に該封孔処理によって溶射被膜自体の強度を向上させることができ、上記特許文献2の金属溶射方法は芳香族オリゴマーにより封孔処理剤の含浸性を改善しつつエポキシポリオール樹脂とイソシアネート樹脂との反応により封孔処理剤を硬化反応させて封孔処理を施すと共に該封孔処理によって溶射被膜自体の強度を向上させることができる。
The metal spraying method of
然し乍ら、上記特許文献1・2の金属溶射方法にあっては、予め基材表面をブラスト処理により粗面化して凹凸形状を形成し、該凹凸形状を有する基材表面に金属溶射を施しアンカー効果を得ることにより、溶射被膜の基材表面に対する付着強度を確保する必要がある。
However, in the metal spraying method of
又上記特許文献1・2の金属溶射方法においては、基材が鉄の場合に限定しており、基材がコンクリート又はモルタルの場合を一切想定していない。
Moreover, in the metal spraying method of the said
本発明は、基材表面に予め凹凸形状を付与する工程を排し、溶射被膜に対し特有の配合による塗料を塗布し含浸させることにより、該溶射被膜の封孔処理及び強度増強に加えて、同溶射被膜の基材表面に対する付着強度の増強をも図ることができ、且つ基材がコンクリート又はモルタルの場合にあっても確実に溶射被膜を基材表面に付着させることができる画期的な金属溶射方法を提供する。 The present invention eliminates the step of previously imparting a concavo-convex shape to the surface of the substrate, and by applying and impregnating a paint with a specific composition to the spray coating, in addition to sealing treatment and strength enhancement of the spray coating, It is possible to increase the adhesion strength of the thermal spray coating to the substrate surface, and to make sure that the thermal spray coating is reliably adhered to the substrate surface even when the substrate is concrete or mortar. A metal spraying method is provided.
要述すると、本発明に係る金属溶射方法は、基材の表面に金属溶射を行い、該溶射により形成された溶射被膜に、アルコキシ基、グリシド基及び炭素数が6〜10のアルキル基を含有するシリコーン化合物混合体とヘキサメチル系(HDI系)ポリイソシアネートとを1:1〜7の重量比で配合して成る一液型塗料、即ち硬化前は含浸性が高い一方、硬化後は高い接着強度を発揮する塗料を含浸し硬化させることにより、上記溶射被膜に封孔処理を施しつつ該溶射被膜の強度を増強すると共に該溶射被膜の基材表面に対する付着強度の増強を図ることができる。又上記塗料は溶射被膜上に耐熱性・対候性が著しく良好で且つ高強度の塗膜を形成する。 In short, the metal spraying method according to the present invention performs metal spraying on the surface of a substrate, and the sprayed coating formed by the spraying contains an alkoxy group, a glycidic group, and an alkyl group having 6 to 10 carbon atoms. One-part paint containing a mixture of silicone compounds and hexamethyl (HDI) polyisocyanate in a weight ratio of 1: 1 to 7, that is, high impregnation before curing, but high adhesion strength after curing By impregnating and curing the coating material that exhibits the above, it is possible to enhance the strength of the thermal spray coating while sealing the thermal spray coating and to enhance the adhesion strength of the thermal spray coating to the substrate surface. Further, the above-mentioned paint forms a high strength coating film with extremely good heat resistance and weather resistance on the sprayed coating.
上記シリコーン化合物に含有される炭素数が6〜10のアルキル基は上記シリコーン化合物混合体とヘキサメチル系ポリイソシアネート等の他のポリマー、モノマーとの相溶性を著しく向上する。 Alkyl group having a carbon number that will be contained in the upper Symbol silicone compound 6-10 significantly improved the silicone compound mixture and hexamethylphosphoric polyisocyanate other polymers, such as, compatibility with monomers.
好ましくは、上記塗料に触媒としてチタンアルコラート又はスズ脂肪酸を配合し、該塗料を効率良く硬化反応させる。 Preferably, a titanium alcoholate or a tin fatty acid is blended as a catalyst in the paint, and the paint is efficiently cured.
又上記シリコーン化合物混合体における上記アルコキシ基の割合を重量比で35%〜40%とし、同シリコーン化合物混合体における上記グリシド基の割合を重量比で10%〜15%とし、上記塗料の硬化反応性、強度物性、消泡性等の性能物性を向上する。加えて該シリコーン化合物混合体における上記アルキル基の割合を重量比で10%〜22%とすることにより、該シリコーン化合物混合体とヘキサメチル系ポリイソシアネートとの相溶性を著しく向上する。 Further, the proportion of the alkoxy group in the silicone compound mixture is 35% to 40% by weight, the proportion of the glycid group in the silicone compound mixture is 10% to 15% by weight, and the curing reaction of the paint is performed. Performance properties such as properties, strength properties, and defoaming properties. In addition by 10% to 22% by weight the proportion of the upper Kia alkyl group in the silicone compound mixture, a significantly improved compatibility with the silicone compound mixture and hexamethylphosphoric polyisocyanate.
又上記シリコーン化合物混合体として、好ましくは長鎖アルキルアルコキシシランとグリシド基含有アルコキシシランの混合体を用いる。 The silicone compound mixture is preferably a mixture of a long-chain alkyl alkoxysilane and a glycid group-containing alkoxysilane.
本発明にあっては、基材がコンクリート又はモルタルの場合には、該基材内に埋設されている補強鉄筋と上記溶射被膜間を繋ぐ導電部材を設け、該導電部材の一端部を上記補強鉄筋に係合させると共に同他端部を上記基材の表面から突出させて上記溶射被膜内に埋設することにより、該溶射被膜と上記補強鉄筋間の通電を促し、有効に基材及び補強鉄筋を保護する。 In the present invention, when the base material is concrete or mortar, a conductive member that connects between the reinforcing steel bar embedded in the base material and the thermal spray coating is provided, and one end of the conductive member is reinforced by the reinforcement Engaging with the reinforcing bar and projecting the other end from the surface of the base material and embedding it in the thermal spray coating, energization between the thermal spray coating and the reinforcing steel bar is promoted, and the base material and the reinforcing steel bar are effectively provided. Protect.
本発明に係る金属溶射方法によれば、アルコキシ基、グリシド基及び炭素数が6〜10のアルキル基を含有するシリコーン化合物混合体とヘキサメチル系ポリイソシアネートとを1:1〜7の重量比で配合した、硬化前は含浸性が高く硬化後は高い接着強度を発揮する塗料を溶射被膜に含浸し硬化させることにより、該塗料が溶射被膜に存する微細孔に入り込んで硬化して同微細孔を適切に封孔しつつ該溶射被膜自体の強度を増強できると共に、同塗料が上記溶射被膜の裏面と基材表面間に画成される微細空隙に充填され硬化し同溶射被膜の付着強度を増強することができる。 According to the metal spraying method of the present invention, a silicone compound mixture containing an alkoxy group, a glycidic group and an alkyl group having 6 to 10 carbon atoms and a hexamethyl polyisocyanate are blended at a weight ratio of 1: 1 to 7. In addition, by impregnating the thermal spray coating with a coating that exhibits high impregnation before curing and high adhesive strength after curing, the coating penetrates into the micropores present in the thermal spray coating and cures appropriately. In addition to enhancing the strength of the sprayed coating itself, the coating material fills and cures the fine voids defined between the back surface of the sprayed coating and the substrate surface, thereby enhancing the adhesion strength of the sprayed coating. be able to.
又上記塗料により溶射被膜の基材表面に対する付着強度を増強することができるため、基材がコンクリート又はモルタルの場合であっても、適切に基材表面に金属溶射を施すことができる。 In addition, since the adhesion strength of the sprayed coating to the substrate surface can be enhanced by the coating material, even if the substrate is concrete or mortar, metal spraying can be appropriately applied to the substrate surface.
以下本発明に係る金属溶射方法の実施形態を図1乃至図6に基づいて説明する。 Hereinafter, an embodiment of a metal spraying method according to the present invention will be described with reference to FIGS.
図1に示すように、本発明に係る金属溶射方法にあっては、必要に応じて、基材1の表面1aに対し既知のディスクサンダー等を用いてケレン処理を行い、汚れや油分、劣化した塗膜、浮きサビ等を除去し、該基材1の表面1aに既知の溶射機を用いて金属溶射を行い溶射被膜2を形成する。
As shown in FIG. 1, in the metal spraying method according to the present invention, if necessary, the
該溶射被膜2は50〜500μmの厚さになるように形成する。最も好ましい厚さは50〜150μmである。
The
上記溶射する金属としては、基材1が金属から成る場合には該基材1を構成する金属よりもイオン化傾向が大きい(卑なる)金属を用いる。例えば、基材1が鉄(鋼)で構成されている場合には、亜鉛、アルミニウム、マグネシウム又はこれらの合金等を溶射する。又基材1がコンクリート又はモルタルから成る場合にも、補強鉄筋(鉄)よりもイオン化傾向が大きい金属、即ち上記のように、亜鉛、アルミニウム、マグネシウム又はこれらの合金等を溶射する。尚本発明にあっては、特に溶射方式は問わない。
As the metal to be sprayed, when the
図1の状態では、溶射被膜2の裏面2bは基材表面1aに密着している部分と、同基材表面1aから離間して該基材表面1aとの間に微細空隙4を画成している部分とが存し、該微細空隙4の存在により溶射被膜2の基材表面1aに対する付着強度は弱い状態である。又溶射被膜2中には微細孔3が形成されている。
In the state of FIG. 1, the
本発明にあっては、図1の状態から、溶射被膜2の表面2aにシリコーン化合物混合体とヘキサメチル系ポリイソシアネートとを配合して成る一液型且つ無溶剤型の塗料5をハケ、ローラ、スプレー等の既知塗布手段により塗布し、該溶射被膜2内に同塗料5を含浸する。
In the present invention, from the state of FIG. 1, a one-component and
上記シリコーン化合物混合体は、アルコキシ基、グリシド基及び炭素数が6〜10のアルキル基を含有し、好ましくは、該シリコーン化合物混合体における上記アルコキシ基の割合を重量比で35%〜40%とし、同シリコーン化合物混合体における上記グリシド基の割合を重量比で10%〜15%とし、上記塗料5の硬化反応性、強度物性、消泡性等の性能物性を向上する。加えて該シリコーン化合物混合体における上記アルキル基の割合を重量比で10%〜22%とすることにより、該シリコーン化合物混合体とヘキサメチル系ポリイソシアネートとの相溶性を著しく向上する。
The silicone compound mixture are alkoxy groups contain alkyl groups of glycidic Moto及beauty carbon number is 6 to 10, preferably 35% to 40% the proportion of the alkoxy group in the silicone compound mixture in a weight ratio of And the proportion of the glycid group in the silicone compound mixture is 10% to 15% by weight to improve the performance properties of the
上記シリコーン化合物混合体の具体例としては長鎖アルキルアルコキシシランとグリシド基含有アルコキシシランの混合体が挙げられる。 Specific examples of the silicone compound mixture include a mixture of a long-chain alkyl alkoxysilane and a glycid group-containing alkoxysilane.
又上記シリコーン化合物混合体と上記ヘキサメチル系ポリイソシアネートは1:1〜1:7の重量比で配合する。当該比率の範囲で配合することにより硬化前の含浸性と硬化後の接着強度を兼ね備えた塗料5とする。逆に言えば、当該比率の範囲外では所望の含浸性、接着強度を得ることができない。
The silicone compound mixture and the hexamethyl polyisocyanate are blended at a weight ratio of 1: 1 to 1: 7. By blending in the range of the ratio, a
好ましくは上記塗料5中に触媒としてチタンアルコラート又はスズ脂肪酸を配合することにより、該塗料5を効率良く硬化反応させることができ、硬化時間を短縮できると共に有効に硬化させることができる。
Preferably, by blending titanium alcoholate or tin fatty acid as a catalyst in the
上記塗料5はシリコーン化合物混合体が変質して生成されるシラノールと、ヘキサメチル系ポリイソシアネートが変質して生成されるポリウレアとが硬化反応して、硬化後は高い接着強度を発揮する。
In the
又上記塗料5はシリコーン化合物混合体の量を調整し気温25℃で50〜500mPa・s、好ましくは200mPa・s以下の低粘度の液体となるように調整する。
The
上記のように含浸性が高く且つ低粘度である塗料5は、図2に示すように、溶射被膜2に形成されている微細孔3に容易に入り込むと共に、該微細孔3を通じ、上記した溶射被膜裏面2bと基材表面1a間に画成された微細空隙4に容易に達し同微細空隙4内に充填され硬化する。
The
そして、上記塗料5は微細孔3内で隙間なく硬化する共に、微細空隙4内で隙間なく硬化し硬化後には高い接着強度を発揮する。同微細空隙4内で硬化した塗料5は基材表面1aと強固に接着すると共に溶射被膜2にアンカー効果を付与する。又上記塗料5の未含浸分は上記溶射被膜2の表面2a上に耐熱性・対候性が良好で且つ強固な塗膜5′を形成する。
And the said
即ち、上記塗料5は微細孔3に入り込んで硬化することにより、該微細孔3を適切に封孔すると同時に溶射被膜2自体の強度を増強する。加えて溶射被膜裏面2bと基材表面1a間の微細空隙4に充填され硬化することにより溶射被膜2と基材表面1aとを強固に結合して基材表面1aに対する付着強度を増強することができる。又溶射被膜2の表面2a上に塗膜5′を形成し該溶射被膜2を適切に保護する。
That is, the
又本発明に係る金属溶射方法にあっては、図1・図2に示す如く、溶射被膜2の裏面2bの一部は基材1の表面1aに密着しており、基材1が金属の場合には、基材1から溶射被膜2への電流の流れが阻害されることはなく、基材1の金属よりイオン化傾向の大きい金属から成る溶射被膜2が犠牲となって溶解し、適切に基材1を保護する。
In the metal spraying method according to the present invention, as shown in FIGS. 1 and 2, a part of the
又基材1がコンクリート又はモルタルの場合には、図3乃至図6に示すように、基材1内に埋設されている補強鉄筋7と溶射被膜2間を繋ぐボルト、アンカーピン等の導電部材6を設け、該補強鉄筋7と溶射被膜2間の通電を促し、該溶射被膜2が犠牲陽極となって有効に基材1及び上記補強鉄筋7を保護する。
When the
詳述すると、図3(A)・(B)に示すように、まず基材1に孔を穿設し、該孔に導電部材6たるボルトを差し入れ、該導電部材6の一端部6aを基材1内に埋設されている補強鉄筋7(横筋7a)と接触させ係合させると共に同他端部6bを基材1の表面1aから突出させた状態にし、上記孔に注入する接着剤等で固定する。
More specifically, as shown in FIGS. 3A and 3B, first, a hole is formed in the
又は具体的には図示しないが、基材1の表層を補強鉄筋7が露出するまでハツリ、導電部材6の一端部6aと補強鉄筋7とを結束した後、上記ハツった部分をモルタルで埋戻すことにより導電部材6を固定しても良い。
Or, although not specifically shown, the surface layer of the
又導電部材6の他例として、図3(C)に示すように、一端部6aが拡開するアンカーピンを導電部材6として利用し、該一端部6aを拡開させて補強鉄筋7(横筋7a)と係合させることも実施に応じ任意である。
Further, as another example of the
なお、図3(A)乃至(C)は導電部材6の一端部6aを補強鉄筋7の内、横筋7aのみと係合させた例を示しているが、これに加えて縦筋7bとも係合させる場合若しくは縦筋7bのみと係合させる場合も、実施に応じ任意である。又本発明における導電部材6の一端部6aと補強鉄筋7との係合は、該導電部材6と補強鉄筋7間で通電可能であれば、特に形態は問わない。
3A to 3C show an example in which one
次いで、図4に示すように、基材表面1aに金属溶射を施す際に、上記導電部材6の他端部6b上にも金属溶射を施し、形成された溶射被膜2内に該導電部材6の他端部6bを埋設し、上記補強鉄筋7と溶射被膜2間を繋ぐ。
Next, as shown in FIG. 4, when metal spraying is performed on the
あとは、図5に示すように、上記形成した溶射被膜2の表面2aに上記塗料5を塗布し、該溶射被膜2内に同塗料5を含浸する。
After that, as shown in FIG. 5, the
この場合にも、図6に示すように、上記塗料5は溶射被膜2の微細孔3内で隙間なく硬化する共に、微細空隙4内で隙間なく硬化し硬化後には高い接着強度を発揮する。同微細空隙4内で硬化した塗料5は基材表面1aと強固に接着すると共に溶射被膜2にアンカー効果を付与する。
Also in this case, as shown in FIG. 6, the
又図6中で5′′として示すように、上記塗料5の一部は基材表面1aに染み込んで硬化し、上記微細空隙4内で硬化した塗料5と一体化して、上記アンカー効果を補完する。更には上記塗料5の未含浸分は上記溶射被膜2の表面2a上に耐熱性・対候性が良好で且つ強固な塗膜5′を形成する。
Also, as indicated by 5 ″ in FIG. 6, a part of the
上記のとおり、基材1がコンクリート又はモルタルの場合にも溶射被膜2の付着強度の増強を図ることができると共に、溶射被膜2と補強鉄筋7間を繋ぎ両者間の通電を促す導電部材6を設けることにより、溶射被膜2が犠牲陽極となって有効に基材1及び補強鉄筋7を保護する。
As described above, even when the
以上説明したように、本発明に係る金属溶射方法にあっては、従来のように、アンカー効果を得るために基材表面に凹凸形状を付与する前処理は不要である。 As described above, in the metal spraying method according to the present invention, as in the prior art, a pretreatment for imparting an uneven shape to the substrate surface in order to obtain the anchor effect is unnecessary.
そして、凹凸形状を付与しない基材の表面に直接金属溶射を施し、溶射被膜形成後に硬化前は含浸性が高く且つ低粘度であり硬化後は高度の接着強度を発揮する塗料を微細孔を通じて含浸し、該微細孔の封孔、上記溶射被膜自体の強度増強及び上記溶射被膜の基材表面に対する付着強度増強を同時に図る比類なき溶射方法である。 The surface of the base material that does not give the uneven shape is directly metal sprayed, and after forming the sprayed coating, it is impregnated through fine holes with a coating that has high impregnation and low viscosity before curing and exhibits high adhesive strength after curing. In addition, this is a unique thermal spraying method that simultaneously seals the fine holes, increases the strength of the thermal spray coating itself, and increases the adhesion strength of the thermal spray coating to the substrate surface.
又既知の方式で基材表面に金属溶射を施し、該溶射により形成した溶射被膜に塗料を塗布し含浸させる簡易な方法であるため、特に既設構造物に金属溶射を行う際には現場で容易に実施でき効果的である。 In addition, it is a simple method in which metal spraying is performed on the surface of the substrate by a known method, and the sprayed coating formed by the spraying is applied and impregnated. Can be implemented effectively.
更に基材1がコンクリート又はモルタルである場合にも、該基材の表面に適切に溶射被膜を形成し、該溶射被膜の基材表面に対する付着強度を増強できると共に、該溶射被膜と基材内の補強鉄筋を繋ぐ導電部材によって有効に基材及び補強鉄筋を保護することができる。
Furthermore, even when the
尚本書面において、下限値と上限値間を「〜」で示した数値範囲は、該下限値と上限値間の全ての数値(整数値と小数値)を表したものである。請求項の記載においても同様である。 In this document, the numerical range indicated by “˜” between the lower limit value and the upper limit value represents all numerical values (integer values and decimal values) between the lower limit value and the upper limit value. The same applies to the claims.
1…基材、1a…基材表面、2…溶射被膜、2a…溶射被膜表面、2b…溶射被膜裏面、3…微細孔、4…微細空隙、5…塗料、5′…塗膜、5′′…基材内に含浸し硬化した塗料、6…導電部材、6a…導電部材の一端部、6b…導電部材の他端部(突出部)、7…補強鉄筋、7a…横筋、7b…縦筋。
DESCRIPTION OF
Claims (5)