JP5895857B2 - Method for producing liquid silicone rubber coating composition for curtain airbag - Google Patents

Description

The present invention is suitable for manufacturing an air bag of a vehicle or the like in which a silicone rubber coating film is formed on a fiber cloth such as 6,6-nylon, 6-nylon, and polyester, and is particularly mounted on a driver seat or a passenger seat. Unlike air bags that are used, curtain air bags that are housed along the roof side from the front pillar and are required to maintain a constant inflation time in order to protect the head and prevent popping out in the event of a collision or vehicle fall It is related with the manufacturing method of the liquid silicone rubber coating agent composition excellent in the low combustion rate property prescribed | regulated to FMVSS-302 when it uses for a curtain air bag use suitable for the liquid silicone rubber coating agent composition suitable for producing.

  Conventionally, the following are known as silicone rubber compositions for air bags aimed at forming a rubber film on the fiber surface. That is, Patent Document 1 (Japanese Patent No. 3165312) discloses an American FMVSS-302 (Federal Motor Vehicle Safety Standard-302) obtained by adding an inorganic filler and an organopolysiloxane resin to an addition-curable composition. A liquid silicone rubber coating agent composition for an air bag having an excellent combustion rate as defined in 1 is disclosed. Patent Document 2 (Japanese Patent Application Laid-Open No. 2006-82443) discloses a liquid for an air bag excellent in the combustion rate defined in FMVSS-302 comprising a resin film layer laminated on the fiber surface via an addition-curable composition. A silicone rubber coating composition is disclosed. Patent Document 3 (Japanese Patent Application Laid-Open No. 2010-53493) is excellent in the burning rate defined in FMVSS-302, which is obtained by adding reinforcing silica fine powder and aluminum hydroxide to an addition-curable composition. A silicone rubber coating composition for air bags with low surface tack is disclosed.

  However, when these compositions are used for curtain airbag applications, there is a problem that it is difficult to meet the high demands on the recent burning rate. However, the required characteristics of the low burning rate cannot be satisfied.

Japanese Patent No. 3165312 JP 2006-82443 A JP 2010-53493 A

This invention is made | formed in view of the said situation, and when it uses for a curtain airbag use, even if there is little coating amount (covering amount) with respect to a curtain airbag base fabric, it is prescribed | regulated to FMVSS-302. it is an object to provide a method for producing a liquid silicone rubber coating composition that gives a cured film having excellent low burn rate of (coating layer).

  As a result of intensive studies to achieve the above object, the present inventors have the following components (A) to (H) as essential components and bonded to two or more silicon atoms in one molecule of the component (A). FMVSS is produced by controlling the weight loss after heating for 3 hours at 150 ° C. of the organopolysiloxane containing an alkenyl group to a specific mass% or less and through the following first to third steps. The present inventors have found that a liquid silicone rubber coating agent composition excellent in low burning rate property as defined in -302 can be obtained constantly and has led to the present invention.

Therefore, this invention provides the manufacturing method of the liquid silicone rubber coating agent composition for curtain airbags shown below.

That is, the present invention is,
(A) Organopolysiloxane containing an alkenyl group bonded to two or more silicon atoms in one molecule: 100 parts by mass
(B) three-dimensional network organopolysiloxane resin (provided that the organopolysiloxane resin does not contain silicon-bonded hydrogen atoms): 0.1 to 50 parts by mass;
(C) Silica fine powder having a BET specific surface area of 50 m ² / g or more: 10 to 30 parts by mass,
(D) Silica surface treatment agent: 3 to 20 parts by mass,
(E) Water: 0.5-5 parts by mass
(F) Organohydrogenpolysiloxane containing hydrogen atoms bonded to at least two silicon atoms in one molecule: The number of hydrogen atoms bonded to silicon atoms contained in one molecule of this component is (A) An amount of 1 to 10 per component and a total of one silicon-bonded alkenyl group in component (B),
(G) addition reaction catalyst: effective amount,
(H) Organosilicon compound containing an adhesion-imparting functional group: A method for producing a liquid silicone rubber coating agent composition for curtain airbags comprising 0.1 to 10 parts by mass as an essential component, the component (A) And controlling the weight loss after heating at 150 ° C. for 3 hours to 1.0% by mass or less, and
[I] a first step of kneading a part of the component (A) and all of the component (C), the component (D) and the component (E) at a temperature of less than 130 ° C .;
[Ii] a second step of heat-treating the mixture obtained in the first step at 130 to 200 ° C., and [iii] the remainder of the component (A) and the component (B) in the mixture after the heat treatment And the manufacturing method of the liquid silicone rubber coating agent composition for curtain airbags which has a 3rd process which knead | mixes the whole quantity of (F)-(H) component.
In this case, further, 0.1 to 5 parts by mass of (I) at least one condensation catalyst selected from an organic titanium compound and an organic zirconium compound is contained with respect to 100 parts by mass of the component (A). It is preferable to add and knead in three steps.

（式中、Ｒ¹は互いに同一又は異種の非置換もしくは置換の１価炭化水素基である。ｎは２〜１０の整数である。）
なお、シリカ表面処理剤がヘキサメチルジシラザンであることが好ましい。 Further, (J) the organic phosphazene compound represented by the following general formula (1) is contained in an amount of 0.1 to 10 parts by mass with respect to 100 parts by mass of component (A), and in the third step of [iii] above. It is also preferable to add and knead.

(In the formula, R ¹ are the same or different unsubstituted or substituted monovalent hydrocarbon groups. N is an integer of 2 to 10.)
The silica surface treatment agent is preferably hexamethyldisilazane.

  According to the present invention, when used for the silicone rubber coating layer of the curtain airbag base fabric, the coating fabric is defined in FMVSS-302 even if the coating amount (covering amount) on the curtain airbag base fabric is small. A liquid silicone rubber coating composition that gives a cured film (coating layer) excellent in low burning rate is obtained. A curtain airbag having a silicone rubber coating layer made of a cured product of the composition on at least one surface of the substrate is excellent in low burning rate.

  Hereinafter, the present invention will be described in more detail. In the present invention, the viscosity is a value measured with a rotational viscometer (BL type, BH type, BS type, cone plate type, etc.) at room temperature (meaning 25 ° C., the same applies hereinafter).

<Liquid silicone rubber coating composition>
The liquid silicone rubber coating agent composition for curtain airbags of the present invention comprises the following components (A) to (H) and is liquid at room temperature (25 ° C.).
Hereinafter, each component will be described in detail.

[(A) component]
The organopolysiloxane of component (A) contains two or more alkenyl groups bonded to silicon atoms in one molecule and is a base polymer (main agent) of the composition of the present invention.

  Examples of the molecular structure of the component (A) include linear, cyclic, branched, etc. The main chain is basically composed of repeating diorganosiloxane units, and both ends of the molecular chain are triorganosiloxy groups. A linear diorganopolysiloxane blocked with is preferred. In addition, when the molecular structure of the organopolysiloxane of component (A) is linear or branched, the position of the silicon atom to which the alkenyl group is bonded in the molecule of the organopolysiloxane is at the end of the molecular chain (that is, tricyclic). Either one of the organosiloxy group) and the middle of the molecular chain (that is, a difunctional diorganosiloxane unit or a trifunctional monoorganosyl seroxyoxane unit located at the non-terminal end of the molecular chain) may be used. Particularly preferably, the component (A) is a linear diorganopolysiloxane containing alkenyl groups bonded to silicon atoms at both ends of the molecular chain.

  (A) As an alkenyl group couple | bonded with the silicon atom in a component, C2-C8 normally, Preferably C2-C4 is mentioned, for example. Specific examples thereof include a vinyl group, an allyl group, a propenyl group, a butenyl group, a pentenyl group, a hexenyl group, a cyclohexenyl group, a heptenyl group, and the like, and a vinyl group is particularly preferable.

  The content of the alkenyl group bonded to the silicon atom in the component (A) is 0.001 to the whole monovalent organic group bonded to the silicon atom (that is, an unsubstituted or substituted monovalent hydrocarbon group). It is preferably 10 mol%, particularly preferably about 0.01 to 5 mol%.

  (A) As monovalent organic group couple | bonded with silicon atoms other than the alkenyl group of a component, it is C1-C12 normally, preferably C1-C12 of the same or different unsubstituted or substituted mutually. About a monovalent hydrocarbon group. When the monovalent hydrocarbon group is substituted, examples of the substitution include those substituted with halogen. Specific examples of the monovalent organic group (unsubstituted or substituted monovalent hydrocarbon group) include alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a cyclohexyl group, and a heptyl group. Aryl groups such as phenyl, tolyl, xylyl and naphthyl; aralkyl groups such as benzyl and phenethyl; halogens such as chloromethyl, 3-chloropropyl and 3,3,3-trifluoropropyl Examples thereof include a substituted alkyl group, and a methyl group and a phenyl group are particularly preferable. In addition, (A) component does not contain an epoxy group.

  The viscosity of component (A) at 25 ° C. is preferably in the range of 100 to 500,000 mPa · s, particularly preferably in the range of 300 to 100,000 mPa · s. When the viscosity is within this range, the workability of the resulting composition is good, and the physical properties of the resulting silicone rubber are good. In the present invention, the viscosity can be measured, for example, with a rotational viscometer (BL type, BH type, BS type, cone plate type, etc.) at room temperature (25 ° C.).

  Specific examples of the organopolysiloxane of component (A) include: a trimethylsiloxy group-capped dimethylsiloxane / methylvinylsiloxane copolymer with both ends of a molecular chain, a trimethylsiloxy group-capped methylvinylpolysiloxane with a molecular chain at both ends, and a trimethylsiloxy group with both ends of a molecular chain. Siloxy group-blocked dimethylsiloxane / methylvinylsiloxane / methylphenylsiloxane copolymer, dimethylvinylsiloxy group-blocked dimethylpolysiloxane at both ends of the molecular chain, dimethylvinylsiloxy group-blocked methylvinylpolysiloxane at both ends of the molecular chain, dimethylvinyl at both ends of the molecular chain Siloxy group-blocked dimethylsiloxane / methylvinylsiloxane copolymer, dimethylvinylsiloxy group-blocked dimethylsiloxane / methylvinylsiloxane / methylphenylsiloxane copolymer, molecular chain Terminal divinylmethylsiloxy group-blocked dimethylpolysiloxane, molecular chain both ends divinylmethylsiloxy group-blocked dimethylsiloxane / methylvinylsiloxane copolymer, molecular chain both ends trivinylsiloxy group-blocked dimethylpolysiloxane, molecular chain both ends trivinylsiloxy group Examples thereof include a blocked dimethylsiloxane / methylvinylsiloxane copolymer and a mixture of two or more of these organopolysiloxanes.

  The (A) component organopolysiloxane may be used alone or in combination of two or more. In addition, the organosilicon compound [(H) component] which has the epoxy group mentioned later is excluded as organopolysiloxane of (A) component.

  In the present invention, in order to stably develop a liquid silicone rubber coating agent composition that provides a cured film (coating layer) excellent in low burning rate property as defined in FMVSS-302, organopolysiloxane of component (A) Regarding the whole, the heating loss of the component (A) after heating at 150 ° C. for 3 hours is 1.0% by mass or less (0 to 1.0% by mass), preferably 0.5% by mass or less (0 to 0.5% by mass). %) In advance. When this heating loss (that is, the heating loss of the entire component (A)) exceeds 1.0% by mass, the low burning rate property defined in the target FMVSS-302 is not stably exhibited. In order to obtain the above-mentioned value for the heating loss after heating at 150 ° C. for 3 hours, a cyclic siloxane such as organocyclotrisiloxane or organocyclotetrasiloxane and hexaorganodisiloxane are usually added in the presence of an acid catalyst or an alkali catalyst. The alkenyl group-containing organopolysiloxane (A) produced by heat-equilibration polymerization is heated at a temperature of about 100 to 200 ° C. for a predetermined time to remove volatile components. . In that case, the heat treatment may be performed at normal pressure, but it is desirable to perform the treatment under a reduced pressure of 100 mmHg or less. The treatment time may be appropriately set by sampling under each treatment condition and monitoring the heating loss after heating at 150 ° C. for 3 hours.

[Component (B)]
Component (B) is an organopolysiloxane resin having a three-dimensional network (resin-like) structure, and preferably a trifunctional RSiO _3/2 unit (wherein R is the same or different from each other, unsubstituted or substituted carbon number 1). -10, preferably a monovalent hydrocarbon group having 1 to 8 carbon atoms) and at least one branched siloxane unit selected from tetrafunctional SiO ₂ units. Organopolysiloxane resin having a three-dimensional network structure which may optionally contain a functional RSiO _1/2 unit and / or a bifunctional RSiO _2/2 unit (wherein the organo group includes an alkenyl group) It can be.) However, this organopolysiloxane resin does not contain silicon-bonded hydrogen atoms (SiH groups). Moreover, it does not contain an epoxy group.

  This same or different unsubstituted or substituted monovalent hydrocarbon group having 1 to 10 carbon atoms; R represents an alkenyl group and a monovalent organic group (unsubstituted or substituted 1) exemplified in the component (A). Valent hydrocarbon groups), specifically, vinyl groups, allyl groups, propenyl groups, butenyl groups, pentenyl groups, hexenyl groups, cyclohexenyl groups, heptenyl groups and other alkenyl groups, methyl groups, Alkyl groups such as ethyl, propyl, butyl, pentyl, hexyl, cyclohexyl and heptyl; aryl groups such as phenyl, tolyl, xylyl and naphthyl; aralkyl groups such as benzyl and phenethyl A halogen-substituted alkyl group such as a chloromethyl group, a 3-chloropropyl group, and a 3,3,3-trifluoropropyl group; To, methyl group, vinyl group, is preferably a phenyl group.

Specific examples of the (B) component organopolysiloxane resin include a siloxane unit represented by the formula: R ′ ₃ SiO _0.5 , a siloxane unit represented by the formula: R ′ ₂ R ″ SiO _0.5 and a formula: R ′ ₂ SiO An organosiloxane copolymer comprising a siloxane unit represented by the formula: siloxane unit represented by SiO ₂ , a siloxane unit represented by the formula: R ′ ₃ SiO _0.5 and a siloxane unit represented by the formula: R ′ ₂ R ″ SiO _0.5 And an organosiloxane copolymer comprising a siloxane unit represented by the formula: SiO ₂ , a siloxane unit represented by the formula: R ′ ₂ R ″ SiO _0.5 , a siloxane unit represented by the formula: R ′ ₂ SiO and a formula: SiO ₂ organosiloxane copolymers consisting of siloxane units represented in the formula: R'R "siloxane units represented by the formula SiO: siloxane represented by R'SiO _1.5 Position or the formula:. R "organosiloxane copolymers consisting of siloxane units represented by SiO _1.5, and mixtures of two or more of these organopolysiloxanes of the above formula R 'is other than alkenyl groups Examples of the same or different unsubstituted or substituted monovalent hydrocarbon group include, for example, alkyl groups such as methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, cyclohexyl group, and heptyl group; Aryl groups such as phenyl group, tolyl group, xylyl group and naphthyl group; Aralkyl groups such as benzyl group and phenethyl group; Halogenated groups such as chloromethyl group, 3-chloropropyl group and 3,3,3-trifluoropropyl group Examples thereof include an alkyl group, etc. In addition, R ″ in the above formula is an alkenyl group, and examples thereof include a vinyl group and an allyl group. Group, butenyl group, pentenyl group, hexenyl group, heptenyl group and the like.

  The amount of component (B) used in the present invention is 0.1 to 50 parts by weight, preferably 0.5 to 30 parts by weight, based on 100 parts by weight of organopolysiloxane of component (A). It is more preferable to set it as 1-10 mass parts, and it is still more preferable to set it as less than 1-5 mass parts (1-4.9 mass parts). If the blending amount is too small, the low combustion rate property defined in FMVSS-302 required for the present invention cannot be obtained, and if the blending amount is too large, the cost becomes high and it tends to be uneconomical.

  The three-dimensional network organopolysiloxane resin (B) can be used alone or in combination of two or more.

[Component (C)]
The silica fine powder of component (C) used in the present invention acts as a reinforcing filler. That is, it imparts high tearability to the silicone rubber obtained from the composition of the present invention. By using silica fine powder as a reinforcing filler, a coating film satisfying the tear strength characteristics necessary for the present invention can be obtained. It becomes possible to form. Such fine silica powder has a specific surface area (BET method) is 50 m ² / g or more, preferably 50 to 400 m ² / g, particularly preferably must be a 100 to 300 m ² / g, a specific surface area of 50 m ² If it is less than / g, satisfactory tear strength characteristics cannot be imparted.

  In the present invention, such a silica fine powder may be a known one conventionally used as a reinforcing filler for silicone rubber, provided that the specific surface area is within the above range. Examples include silica (fumed silica) and precipitated silica (wet silica). These can be used alone or in combination of two or more.

  The compounding amount of the component (C) used in the present invention is 10 to 30 parts by mass, particularly preferably 10 to 20 parts by mass with respect to 100 parts by mass of the organopolysiloxane of the component (A). If the blending amount is too small, the strength required for the present invention cannot be obtained. If the blending amount is too large, the thixotropy of the composition is increased, the fluidity is lowered, and the coating operation is deteriorated.

[(D) component]
The component (D) silica surface treating agent not only acts as a wetter that improves the wettability and dispersibility of the component (A) and the component (B) by performing the surface treatment of the component (C). In addition, the pseudo-crosslinking (creep hardening) of the component (C) by the component (H) is suppressed, and the composition plays a role of reducing the burning rate defined in FMVSS-302.

  As the silica surface treating agent of component (D), hexamethyldisilazane, 1,3-divinyl-1,1,3,3-tetramethyldisilazane, 1,3-dimethyl-1,1,3,3- Alkyl such as tetravinyldisilazane, 1,1,1,3,3,5,5,5-octamethyltrisilazane, 1,1,1,3,5,5,5-heptamethyl-3-vinyltrisilazane Examples include organosilazanes such as silazane and alkenyl group-containing alkylsilazane, and organosilicon compounds such as dimethylamino group-containing organoaminosilane such as dimethylaminotrimethylsilane and dimethylaminodimethylvinylsilane, and organosilanes such as organochlorosilane and organoalkoxysilane. .

  The addition amount of this (D) component is 3-20 mass parts with respect to 100 mass parts of (A) component, Preferably it is 5-15 mass parts. When the addition amount is less than 3 parts by mass, the surface treatment of the component (C) cannot be performed sufficiently, and when it is more than 20 parts by mass, it becomes excessive, which is not economical. (D) The silica surface treating agent of a component can be used 1 type or in combination of 2 or more types.

[(E) component]
The (E) component water plays a role of accelerating the decomposition of the (D) component and increasing the surface treatment rate of the (C) component. The addition amount of this (E) component is 0.5-5 mass parts with respect to 100 mass parts of (A) component, Preferably it is 0.5-2 mass parts. When the amount added is more than 5 parts by mass, no further improvement in characteristics can be expected, and the step of removing water after heat treatment of the silicone rubber composition becomes long, which is not preferable for production. Moreover, when there is little addition amount, the surface treatment of (C) component cannot fully be performed.

[(F) component]
The organohydrogenpolysiloxane of component (F) acts as a cross-linking agent (curing agent) by hydrosilylation addition reaction with the alkenyl group in components (A) and (B), and its molecular structure is particularly There are no restrictions, and various conventionally manufactured products such as linear, cyclic, branched, and three-dimensional network (resin-like) structures can be used, but at least 2, preferably 3 It is necessary to have a hydrogen atom (hydrosilyl group represented by SiH) bonded to at least one silicon atom, and substantially does not contain a hydroxyl group bonded to a silicon atom (ie, silanol group) in the molecule. Usually, it is desirable to have 2 to 300, preferably 3 to 200, more preferably about 4 to 100 SiH groups. The organohydrogenpolysiloxane of component (F) may be used alone or in combination of two or more. In addition, as organohydrogenpolysiloxane of (F) component, the organosilicon compound [(H) component] which has the epoxy group mentioned later is remove | excluded.

As the organohydrogenpolysiloxane, those represented by the following average composition formula (2) can be used.
R ² _a H _b SiO _{(4-ab) / 2} (2)

In the above formula (2), R ² is the same or different from each other and excludes an aliphatic unsaturated bond such as an alkenyl group, preferably an unsubstituted or substituted monovalent carbon atom bonded to a silicon atom having 1 to 10 carbon atoms. Examples of the unsubstituted or substituted monovalent hydrocarbon group in R ² include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, Alkyl group such as neopentyl group, hexyl group, cyclohexyl group, octyl group, nonyl group, decyl group, aryl group such as phenyl group, tolyl group, xylyl group, naphthyl group, benzyl group, phenylethyl group, phenylpropyl group, etc. Aralkyl groups or those obtained by substituting some or all of the hydrogen atoms of these groups with halogen atoms such as fluorine, bromine and chlorine, such as chloromethyl Group, chloropropyl group, bromoethyl group, trifluoropropyl group and the like. The unsubstituted or substituted monovalent hydrocarbon group for R ² is preferably an alkyl group or an aryl group, and more preferably a methyl group or a phenyl group. A is 0.7 to 2.1, b is 0.001 to 1.0, and a + b is a positive number satisfying 0.8 to 3.0, preferably a is 1.0 to 2 0.0 and b are 0.01 to 1.0, and a + b is 1.5 to 2.5.

  SiH groups containing at least 2 (usually 2 to 300), preferably 3 or more (for example, 3 to 200), more preferably about 4 to 100 in one molecule are represented by molecular chain terminal, molecular chain It may be located anywhere in the middle, or may be located in both. The molecular structure of the organohydrogenpolysiloxane may be any of linear, cyclic, branched, and three-dimensional network structures, but the number of silicon atoms in one molecule (or the degree of polymerization) is Usually 2 to 300, preferably 3 to 150, more preferably about 4 to 100 are desirable, and the viscosity at 25 ° C. is usually 0.1 to 1,000 mPa · s, preferably 0.5 to 500 mPa. -About s, a liquid thing is used at room temperature (25 degreeC). The degree of polymerization can be determined, for example, as number average degree of polymerization (number average molecular weight) or weight average degree of polymerization (weight average molecular weight) in terms of polystyrene in GPC (gel permeation chromatography) analysis using toluene as a developing solvent. .

Examples of the organohydrogenpolysiloxane of component (F) include 1,1,3,3-tetramethyldisiloxane, 1,3,5,7-tetramethylcyclotetrasiloxane, and tris (hydrogendimethylsiloxy). Methylsilane, tris (hydrogendimethylsiloxy) phenylsilane, methylhydrogencyclopolysiloxane, methylhydrogensiloxane-dimethylsiloxane cyclic copolymer, trimethylsiloxy group-blocked methylhydrogenpolysiloxane, molecular chain both-end trimethyl Siloxy group-blocked dimethylsiloxane / methylhydrogensiloxane copolymer, trimethylsiloxy group-blocked dimethylsiloxane / methylhydrogensiloxane / methylphenylsiloxane copolymer at both ends of the molecular chain Molecular chain both ends trimethylsiloxy group-blocked dimethylsiloxane / methylhydrogensiloxane / diphenylsiloxane copolymer, molecular chain both ends dimethylhydrogensiloxy group-blocked methylhydrogenpolysiloxane, molecular chain both ends dimethylhydrogensiloxy group-blocked dimethylpoly Siloxane, dimethylhydrogensiloxy group-capped dimethylsiloxane / methylhydrogensiloxane copolymer, both ends of molecular chain dimethylhydrogensiloxy group-capped dimethylsiloxane / methylphenylsiloxane copolymer, dimethylhydrogen, both ends of molecular chain Siloxy group-blocked dimethylsiloxane / diphenylsiloxane copolymer, molecular chain both ends dimethylhydrogensiloxy group-blocked methylphenylpolysiloxane, molecule Both terminals and dimethylhydrogensiloxy group-blocked diphenyl polysiloxane, in each of these exemplified compounds, those in which a part of the methyl group or entirely substituted with other alkyl groups such as ethyl group, a propyl group, the formula: R ³ ₃ Organosiloxane copolymer comprising a siloxane unit represented by SiO _0.5 and a siloxane unit represented by the formula: R ³ ₂ HSiO _0.5 and a siloxane unit represented by the formula: SiO ₂ , a siloxane unit represented by the formula: R ³ ₂ HSiO _0.5 And an organosiloxane copolymer composed of a siloxane unit represented by SiO ₂ , a siloxane unit represented by formula: R ³ HSiO and a siloxane unit represented by formula: R ³ SiO _1.5 or a siloxane unit represented by formula: HSiO _1.5 An organosiloxane copolymer comprising two or more of these organopolysiloxanes A mixture consisting of the above is mentioned. R ³ in the above formula is a monovalent hydrocarbon group other than an alkenyl group, and the same groups as described above are exemplified.

  Component (F) is blended in an amount of 1 to 10 moles of silicon-bonded hydrogen atoms in component (F) with respect to 1 mole (or individual) of silicon-bonded alkenyl groups in (A) and (B). (Or individual), preferably in an amount in the range of 1 to 5 mol (or individual). When the number of silicon-bonded hydrogen atoms in component (F) is less than 1 mole relative to 1 mole of silicon-bonded alkenyl groups in component (A) and component (B), the composition does not cure sufficiently, When this exceeds 10 mol, the heat resistance of the resulting silicone rubber is extremely poor.

[(G) component]
Any addition reaction catalyst for component (G) may be used as long as it promotes the hydrosilylation addition reaction between the silicon-bonded alkenyl group in components (A) and (B) and the SiH group in component (F). Although a catalyst may be used, usually a platinum group metal catalyst can be preferably used. (G) A component may be used individually by 1 type, or may use 2 or more types together. Examples of the component (G) include platinum group metals such as platinum, palladium and rhodium, chloroplatinic acid, alcohol-modified chloroplatinic acid, chloroplatinic acid and olefins, coordination compounds of vinylsiloxane or acetylene compounds, tetrakis ( Platinum group metal compounds such as platinum such as triphenylphosphine) palladium and chlorotris (triphenylphosphine) rhodium, and palladium and rhodium are exemplified, and platinum compounds are particularly preferable.

  The compounding amount of the component (G) may be an effective amount as an addition reaction catalyst, preferably a catalytic metal element (platinum group metal element) relative to the total mass of the component (A), the component (B) and the component (F). The mass is usually 0.5 to 1,000 ppm, preferably 1 to 500 ppm, and more preferably 10 to 100 ppm. If the blending amount is within this range, the addition reaction is likely to be sufficiently promoted, the curing is likely to be sufficient, and the rate of the addition reaction is easily improved as the blending amount is increased. It tends to be advantageous.

[(H) component]
Component (H) is an organosilicon compound having an epoxy group and a silicon atom-bonded alkoxy group in one molecule, and the organosilicon compound has an epoxy group and a silicon atom-bonded alkoxy group in one molecule. Any organosilicon compound can be used, but from the viewpoint of adhesion development, at least one epoxy group and at least two silicon-bonded alkoxy groups (for example, trialkoxysilyl group, organodialkoxysilyl group) Etc.), for example, organosilane, or cyclic or linear organosiloxane having 2 to 30 silicon atoms, preferably about 4 to 20 silicon atoms, and having at least one epoxy group And at least two silicon-bonded alkoxy groups. (H) A component may be used individually by 1 type, or may use 2 or more types together.

  The epoxy group is a silicon atom in the form of, for example, a glycidoxyalkyl group such as a glycidoxypropyl group; an epoxy-containing cyclohexylalkyl group such as a 2,3-epoxycyclohexylethyl group or a 3,4-epoxycyclohexylethyl group. It is preferable that it is couple | bonded with. A silicon atom-bonded alkoxy group is bonded to a silicon atom, for example, a trialkoxysilyl group such as a trimethoxysilyl group or a triethoxysilyl group; a methyldimethoxysilyl group, an ethyldimethoxysilyl group, a methyldiethoxysilyl group, an ethyldi It is preferable to form an alkyl dialkoxysilyl group such as an ethoxysilyl group.

  In addition, the component (H) includes, for example, alkenyl groups such as vinyl groups, acrylic groups, (meth) acryloxy groups, and hydrosilyl groups (SiH) as functional groups other than epoxy groups and silicon-bonded alkoxy groups in one molecule. It may or may not have at least one functional group selected from the group consisting of groups.

  Examples of the organosilicon compound of component (H) include γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, and γ-glycidoxypropylmethyl. Diethoxysilane, (3,4-epoxycyclohexylethyl) trimethoxysilane, (3,4-epoxycyclohexylethyl) triethoxysilane, (3,4-epoxycyclohexylethyl) methyldimethoxysilane, (3,4-epoxycyclohexyl) Ethyl) methyldiethoxysilane, (2,3-epoxycyclohexylethyl) trimethoxysilane, (2,3-epoxycyclohexylethyl) triethoxysilane, (2,3-epoxycyclohexylethyl) methyldimethoxysilane, (2, -Epoxy cyclohexyl ethyl) Epoxy functional group-containing silane coupling agents such as methyldiethoxysilane (ie, epoxy functional group-containing organoalkoxysilane), and organic silanes and organopolysiloxanes represented by the following chemical formula Examples thereof include silicon compounds, mixtures of two or more of these, or one or more partially hydrolyzed condensates of these.

（式中、ｈは１〜１０の整数、ｋは０〜１００の整数、好ましくは０〜２０の整数、ｐは１〜１００の整数、好ましくは１〜２０の整数、ｑは１〜１０の整数である。）

(In the formula, h is an integer of 1 to 10, k is an integer of 0 to 100, preferably 0 to 20, an p is an integer of 1 to 100, preferably an integer of 1 to 20, and q is 1 to 10. (It is an integer.)

  The amount of component (H) is 0.1 to 10 parts by weight, preferably 0.25 to 5 parts by weight, based on 100 parts by weight of organopolysiloxane (A). When the blending amount is less than 0.1 parts by mass, the resulting composition does not have sufficient adhesive strength. When the blending amount exceeds 10 parts by mass, even if the blending amount is increased, the resulting composition is difficult to improve the adhesive force, becomes expensive and tends to be uneconomical.

  Moreover, when (H) component contains an alkenyl group and / or SiH group, (F) with respect to 1 mol (or individual) of silicon atom-bonded alkenyl groups in component (A), component (B) and component (H) ) Component and (H) component have silicon atom-bonded hydrogen atoms in the range of 1 to 10 mol (or individual), preferably 1 to 8 mol (or individual), more preferably 1 to 6 mol (or individual). Is the amount. When the silicon atom-bonded hydrogen atom in the component (F) and the component (H) is less than 1 mol with respect to 1 mol of the silicon atom-bonded alkenyl group in the component (A), the component (B), and the component (H), The composition does not cure sufficiently and does not have sufficient adhesion. On the other hand, if it exceeds 10 moles, the resulting silicone rubber is extremely inferior in heat resistance, making it difficult to improve the adhesive strength, resulting in high costs and being uneconomical.

[Other ingredients]
In addition to the components (A) to (H), the composition of the present invention can contain other optional components as long as the object of the present invention is not impaired. Specific examples thereof include the following. Each of these other components may be used alone or in combination of two or more.

[Component (I)]
The condensation catalyst of component (I) is at least one selected from organic titanium compounds and organic zirconium compounds, and acts as a condensation promoter for promoting adhesion. (I) A component may be used individually by 1 type, or may use 2 or more types together. Specific examples of the component (I) include, for example, organic titanates such as titanium tetraisopropoxide, titanium tetranormal butoxide, and titanium tetra-2-ethylhexoxide, titanium diisopropoxybis (acetylacetonate), Titanium-condensation promoters (titanium compounds) such as titanium diisopropoxybis (ethyl acetoacetate), titanium tetraacetylacetonate, etc., organic zirconium esters such as zirconium tetranormal propoxide, zirconium tetranormal butoxide, Organic zirconium clay such as zirconium tributoxy monoacetylacetonate, zirconium monobutoxyacetylacetonate bis (ethylacetoacetate), zirconium tetraacetylacetonate Zirconium condensation promoter such as compound (zirconium compounds).

  The organic titanium compound and organic zirconium compound of component (I) are optional components that are blended as necessary, and the blending amount is usually 5 parts by mass or less (0 to 100 parts by mass of component (A)). However, when the component (I) is added, it is preferably in the range of 0.1 to 5 parts by mass, more preferably 0.2 to 2 parts by mass. When the blending amount is less than 0.1 parts by mass, the obtained cured product may be liable to deteriorate the adhesion durability under high temperature and high humidity, and when the blending amount exceeds 5 parts by mass, it is obtained. In some cases, the heat resistance of the cured product tends to decrease.

（式中、Ｒ¹は互いに同一又は異種の非置換もしくは置換の１価炭化水素基である。ｎは２〜１０の整数であり、好ましくは３、４又は５である。） [(J) component]
When the organic phosphazene compound as the component (J) is used in a predetermined amount in the silicone rubber coating composition of the air bag base fabric, at least one of the coated fabric (that is, the cured film (coating layer) of the composition of the present invention) is used. The base fabric on the surface is not only excellent in the low burning rate property defined in FMVSS-302, but also surprisingly provides a low surface adhesive cured film (coating layer) excellent in blocking resistance. Therefore, it is effective as a flame retardant and anti-blocking agent. The organic phosphazene compound is represented by the following general formula (1).

(In the formula, R ¹ is the same or different unsubstituted or substituted monovalent hydrocarbon group. N is an integer of 2 to 10, preferably 3, 4 or 5.)

R ¹ in the general formula (1) is an unsubstituted or substituted monovalent hydrocarbon group, which may be the same or different from each other, more preferably 1 to 10 carbon atoms, particularly 1 to 8 carbon atoms. A chain, branched or cyclic alkyl group, or 1 to 4, particularly 1 to 2, an aromatic hydrocarbon group having 6 to 40 carbon atoms which may contain a phenyl group or a phenylene skeleton (an aryl group, An aralkyl group).

等が挙げられる。 As R ¹ , specifically,

Etc.

なお、本発明において、有機ホスファゼン化合物は、１種単独で用いても２種以上を併用してもよい。 Specific examples of the organic phosphazene compound include those shown below.

In addition, in this invention, an organic phosphazene compound may be used individually by 1 type, or may use 2 or more types together.

  The organic phosphazene compound is an optional component blended as necessary, and the blending amount thereof is usually about 10 parts by mass or less (0 to 10 parts by mass) per 100 parts by mass of the component (A). When mix | blending an organic phosphazene compound, Preferably it is 0.1-10 mass parts, More preferably, it is 0.25-5 mass parts. If the blending amount is less than 0.1 parts by mass, the cured film of the resulting composition may not exhibit low burning rate and low surface tackiness, and if the blending amount exceeds 10 parts by mass, Even when the blending amount is increased, the resulting composition is difficult to improve the low burning rate property and the low surface tackiness, becomes high in cost, and tends to be uneconomical.

-Reaction control agent If a reaction control agent is a compound which has a hardening inhibitory effect with respect to the addition reaction catalyst of the said (G) component, it will not specifically limit, A conventionally well-known thing can be used. Specific examples thereof include phosphorus-containing compounds such as triphenylphosphine; nitrogen-containing compounds such as tributylamine, tetramethylethylenediamine, and benzotriazole; sulfur-containing compounds; acetylene-based compounds such as acetylene alcohols; and containing two or more alkenyl groups. Compounds; hydroperoxy compounds; maleic acid derivatives and the like.

  Since the degree of the effect of inhibiting the curing by the reaction control agent varies depending on the chemical structure of the reaction control agent, it is preferable to adjust the addition amount of the reaction control agent to an optimum amount for each reaction control agent to be used. By adding an optimal amount of the reaction control agent, the composition is excellent in long-term storage stability and curability at room temperature.

Inorganic filler (C) Examples of the inorganic filler other than the silica fine powder of component C include, for example, crystalline silica (for example, quartz powder having a BET specific surface area of less than 50 m ² / g), a hollow filler made of organic resin, poly Methyl silsesquioxane fine particles (so-called silicone resin powder), fumed titanium dioxide, magnesium oxide, zinc oxide, iron oxide, aluminum hydroxide, magnesium carbonate, calcium carbonate, zinc carbonate, layered mica, carbon black, diatomaceous earth, glass Inorganic fillers such as fibers; fillers obtained by subjecting these inorganic fillers to surface hydrophobic treatment with organosilicon compounds such as organoalkoxysilane compounds, organochlorosilane compounds, organosilazane compounds, and low molecular weight siloxane compounds; silicone rubber powders; silicone resins Powder etc. Can be mentioned.

Other components In addition, for example, an organopolysiloxane containing one silicon-bonded hydrogen atom in one molecule and no other functional group, one silicon-bonded alkenyl group in one molecule An organopolysiloxane containing no other functional groups, a non-functional organopolysiloxane containing no silicon-bonded hydrogen atoms, silicon-bonded alkenyl groups, or other functional groups (so-called dimethyl silicone oil), An organic solvent, an anti-creep hardening agent, a plasticizer, a thixotropic agent, a pigment, a dye, an antifungal agent and the like can be blended.

[Method for Preparing Composition]
The liquid silicone rubber coating composition of the present invention can be prepared by mixing the above-mentioned components according to a conventional method, but when used for curtain airbag applications, the low combustion defined in FMVSS-302. In order to obtain a liquid silicone rubber coating composition having excellent speed, it is essential to ensure uniform dispersibility of the component (C) in the matrix of the components (A) and (C). From this point of view, it is necessary to produce the composition through the following steps [i] to [iii].
[I] A part of the component (A) and the components (C), (D) and (E) are all at a temperature of less than 130 ° C, preferably 10 to 125 ° C, more preferably 25 to 120. First step of kneading, preferably at 25 to 100 ° C., usually at room temperature (25 ° C.), preferably 0.1 to 5 hours, more preferably 0.5 to 2 hours,
[Ii] The mixture obtained in the first step is 130 to 200 ° C., preferably 140 to 190 ° C., more preferably 145 to 180 ° C., preferably 0.5 to 8 hours, more preferably 1 to 5 The second step of heat treatment for time, and [iii] the mixture after the heat treatment, the remainder of the component (A) and the total amount of the components (B) and (F) to (H) are 10 to 120 ° C., Usually, a third step of kneading at room temperature (25 ° C.), preferably for 0.1 to 3 hours, more preferably for 0.5 to 1.5 hours.
If the heat treatment temperature in the second step is too low, a cured silicone rubber excellent in combustion resistance cannot be obtained.
Other optional components including the inorganic filler other than the component (C) are blended and kneaded in the third step ([iii]).

  The viscosity of the liquid silicone rubber coating agent composition thus obtained can be usually about 10 to 500 Pa · s, preferably about 20 to 200 Pa · s at 25 ° C.

<Air bag>
The liquid silicone rubber coating composition thus obtained is excellent in adhesion to the airbag fabric, and is stored along the roof side from the front pillar. It is suitable for producing a curtain airbag that is required to maintain a constant expansion time in order to prevent popping out.

  In the present invention, a known structure is used as an air bag, particularly a curtain air bag, on which a silicone rubber coating layer made of a cured product of the above composition is formed. Specific examples thereof include 6,6-nylon. 6-Nylon, aramid fiber, various polyamide fibers, various polyester fibers and other synthetic fibers are used as the base fabric, and the outer peripheral parts of the two plain weave base fabrics whose inner surfaces are rubber coated are bonded together with an adhesive. And a plain weave type airbag produced by stitching the adhesive layers, and a bag weave type airbag using the woven fabric as a base fabric to form a bag portion by weaving.

[Production method]
The liquid silicone rubber coating composition is applied to at least one surface of a substrate made of a fiber cloth, in particular, one surface, and is heated in a hot air drying oven and cured to cure the silicone rubber coating. A layer can be formed. A curtain airbag can be manufactured using the silicone rubber coating base fabric for curtain airbags obtained in this way.

Here, as a base material which consists of fiber cloths, the base material which makes the base fabric the woven fabric of the various synthetic fibers mentioned above is mentioned. Further, as a method for coating the substrate with the composition, a conventional method can be adopted, but the thickness (or surface coating amount) of the coating layer is preferably 5 to 150 g / m ² , more preferably. Is about 10 to 80 g / m ² , more preferably about 15 to 60 g / m ² .

  The liquid silicone rubber coating composition of the present invention can be cured by a known curing method under known curing conditions. Specifically, for example, the composition can be cured by heating at 120 to 180 ° C. for 1 to 10 minutes.

  EXAMPLES Hereinafter, although a preparation example, an Example, and a comparative example are shown and this invention is demonstrated concretely, this invention is not restrict | limited to the following Example. The viscosity was measured with a rotational viscometer. Moreover, room temperature means 25 degreeC.

[Preparation Example 1]
43 parts by weight of dimethylpolysiloxane having both ends blocked with vinyldimethylsiloxy groups and having a viscosity at 25 ° C. of about 30,000 mPa · s at 0.3 ° C. for 3 hours at 150 ° C. Both ends of the chain are blocked with vinyldimethylsiloxy groups, 17 parts by weight of dimethylpolysiloxane having a viscosity at 25 ° C. of about 1000 mPa · s at 0.2 ° C. for 3 hours at 150 ° C. and hexamethyl Dissolve 8 parts by mass, 2 parts by mass of water, and 40 parts by mass of silica fine powder (Aerosil 300, manufactured by Nippon Aerosil Co., Ltd.) having a specific surface area of about 300 m ² / g by BET method are charged into a kneader and 1 at room temperature. Mixed for hours. Thereafter, the temperature was raised to 150 ° C., followed by mixing for 2 hours. Thereafter, the temperature is lowered to room temperature, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the viscosity at 25 ° C. is 0.3% by mass at 150 ° C. for 3 hours, and the viscosity at 25 ° C. is about 30,000 mPa · s. 24 parts by mass of dimethylpolysiloxane, 5 mol% of vinylmethylsiloxane units and 95 mol% of dimethylsiloxane units among the bifunctional diorganosiloxane units constituting the main chain, both ends of the molecular chain blocked with trimethylsiloxy groups 5 parts by weight of dimethylpolysiloxane having a viscosity of about 700 mPa · s at 25 ° C. with a weight loss of 1.5% by mass at 150 ° C. for 3 hours was added and mixed until uniform, and a base compound (I ) In addition, the heating loss (150 degreeC, 3 hours) of the whole (A) component was 0.3 mass%.

[Preparation Example 2] (Comparative Preparation Example 1)
43 parts by mass of dimethylpolysiloxane having both ends blocked with vinyldimethylsiloxy groups and a viscosity of about 30,000 mPa · s at 25 ° C. at 1.2 ° C. for 3 hours at 150 ° C. Both ends of the chain are blocked with vinyldimethylsiloxy groups, the loss on heating at 150 ° C. for 3 hours is 1.1% by mass, the viscosity at 25 ° C. is 17 parts by mass of dimethylpolysiloxane having a viscosity of about 1,000 mPa · s, hexamethyl Dissolve 8 parts by mass, 2 parts by mass of water, and 40 parts by mass of silica fine powder (Aerosil 300, manufactured by Nippon Aerosil Co., Ltd.) having a specific surface area of about 300 m ² / g by BET method are charged into a kneader and 1 at room temperature. Mixed for hours. Thereafter, the temperature was raised to 150 ° C., followed by mixing for 2 hours. Thereafter, the temperature is lowered to room temperature, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the viscosity at 25 ° C. is 2.3% by mass at 150 ° C. for 3 hours, and the viscosity at 25 ° C. is about 30,000 mPa · s. 24 parts by mass of dimethylpolysiloxane, 5 mol% of vinylmethylsiloxane units and 95 mol% of dimethylsiloxane units among the bifunctional diorganosiloxane units constituting the main chain, both ends of the molecular chain blocked with trimethylsiloxy groups 5 parts by weight of dimethylpolysiloxane having a viscosity of about 700 mPa · s at 25 ° C. with a weight loss of 1.5% by mass at 150 ° C. for 3 hours was added and mixed until uniform, and the base compound (II ) In addition, the heat loss (150 degreeC, 3 hours) of the whole (A) component was 1.2 mass%.

[Preparation Example 3] (Comparative Preparation Example 2)
43 parts by weight of dimethylpolysiloxane having both ends blocked with vinyldimethylsiloxy groups and having a viscosity at 25 ° C. of about 30,000 mPa · s at 0.3 ° C. for 3 hours at 150 ° C. Both ends of the chain are blocked with vinyldimethylsiloxy groups, 17 parts by weight of dimethylpolysiloxane having a viscosity at 25 ° C. of about 1000 mPa · s at 0.2 ° C. for 3 hours at 150 ° C. and hexamethyl Dissolve 8 parts by mass, 2 parts by mass of water, and 40 parts by mass of silica fine powder (Aerosil 300, manufactured by Nippon Aerosil Co., Ltd.) having a specific surface area of about 300 m ² / g by BET method are charged into a kneader and 1 at room temperature. Mixed for hours. Thereafter, the temperature was raised to 120 ° C., followed by mixing for 2 hours. Thereafter, the temperature is lowered to room temperature, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the viscosity at 25 ° C. is 0.3% by mass at 150 ° C. for 3 hours, and the viscosity at 25 ° C. is about 30,000 mPa · s. 24 parts by mass of dimethylpolysiloxane, 5 mol% of vinylmethylsiloxane units and 95 mol% of dimethylsiloxane units among the bifunctional diorganosiloxane units constituting the main chain, both ends of the molecular chain blocked with trimethylsiloxy groups 5 parts by weight of dimethylpolysiloxane having a viscosity of about 700 mPa · s at 25 ° C. with a weight loss of 1.5% by mass at 150 ° C. for 3 hours was added and mixed until uniform, and the base compound (III ) In addition, the heating loss (150 degreeC, 3 hours) of the whole (A) component was 0.3 mass%.

[Example 1]
At 25 ° C., 76.5 parts by mass of the base compound (I) obtained in Preparation Example 1 was blocked with vinyldimethylsiloxy groups at both ends of the molecular chain, and the loss on heating at 150 ° C. for 3 hours was 0.3% by mass. 10 parts by mass of dimethylpolysiloxane having a viscosity of about 30,000 mPa · s, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 0.2% by mass. At 25 ° C., 35.5 parts by mass of dimethylpolysiloxane having a viscosity of about 1,000 mPa · s, both molecular chain ends blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 0.2% by mass. 5 parts by weight of dimethylpolysiloxane having a viscosity of about 5,000 mPa · s, 39.5 mol% of (CH ₃ ) ₃ SiO _1/2 units and (CH ₃ ) ₂ (CH ₂ ═CH) SiO _1/2 units 6 .5 mol% organopolysiloxane resin 5 parts by weight of the three-dimensional network structure iO ₂ units 54 mol% and consisting of, a viscosity at 25 ° C. is 45 mPa · s, with both molecular chain terminals trimethyl having silicon-bonded hydrogen atom in a molecular chain side chains Siloxy group-blocked dimethylsiloxane / methylhydrogensiloxane copolymer (silicon-bonded hydrogen atom content = 1.08 mass%) 6.4 parts by mass, 1-ethynylcyclohexanol 0.09 parts by mass, chloroplatinic acid / 1 , 3-divinyltetramethyldisiloxane complex containing 0.38 parts by mass of a dimethylpolysiloxane solution containing 1% by mass as a platinum atom content, 0.3 parts by mass of γ-glycidoxypropyltrimethoxysilane, titanium tetra-2- 0.2 parts by mass of ethyl hexoxide was mixed at room temperature for 1 hour to obtain Composition A (component (A) and (B). To silicon-bonded vinyl in min (F) molar ratio of SiH groups in component; the SiH / SiVi = 5) was prepared. In addition, the heating loss (150 degreeC, 3 hours) of the whole (A) component was 0.3 mass%.
Various tests (hardness, elongation at break, tensile strength, tear strength measurement, Scott stagnation test, and flammability test) shown below were performed using the obtained composition A.

<Measurement method of hardness, elongation at break, tensile strength, tear strength>
The composition A is press-cured at 150 ° C. for 5 minutes and then post-cured at 150 ° C. for 1 hour to prepare a sheet according to JIS K 6249. The sheet is hardened according to JIS K 6249, and stretched when cut. The tensile strength and tear strength were measured. The results are shown in Table 1.

<Scott itch test>
The Scott stagnation test was performed using a Scott stagnation tester. The above silicone rubber coated nylon base fabric is subjected to a stagnation test 500 times at a pressing pressure of 5 kgf, and then the state of destruction of the coating part is visually confirmed, and the case where the silicone rubber coating layer is not peeled off from the coating surface is passed. The case where it peeled was evaluated as disqualified. The results are shown in Table 1.

<Flammability test>
The flammability of the silicone rubber-coated nylon base fabric was evaluated by the method prescribed in FMVSS-302. The flame burning rate by FMVSS-302 is preferably 20 mm / min or less. The results are shown in Table 1.

得られた組成物Ｂについて、実施例１と同様にして、硬さ、切断時伸び、引張り強さ、引裂き強さの測定、及びスコット揉み試験、燃焼性試験を行った。結果を表１に示す。 [Example 2]
At 25 ° C., 76.5 parts by mass of the base compound (I) obtained in Preparation Example 1 was blocked with vinyldimethylsiloxy groups at both ends of the molecular chain, and the loss on heating at 150 ° C. for 3 hours was 0.3% by mass. 10 parts by mass of dimethylpolysiloxane having a viscosity of about 30,000 mPa · s, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 0.2% by mass. At 25 ° C., 35.5 parts by mass of dimethylpolysiloxane having a viscosity of about 1,000 mPa · s, both molecular chain ends blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 0.2% by mass. 5 parts by weight of dimethylpolysiloxane having a viscosity of about 5,000 mPa · s, 39.5 mol% of (CH ₃ ) ₃ SiO _1/2 units and (CH ₃ ) ₂ (CH ₂ ═CH) SiO _1/2 units 6 .5 mol% organopolysiloxane resin 5 parts by weight of the three-dimensional network structure iO ₂ units 54 mol% and consisting of, a viscosity at 25 ° C. is 45 mPa · s, with both molecular chain terminals trimethyl having silicon-bonded hydrogen atom in a molecular chain side chains 6.4 parts by mass of siloxy group-blocked dimethylsiloxane / methylhydrogensiloxane copolymer (silicon atom-bonded hydrogen atom content = 1.08% by mass), 0.5 parts by mass of organic phosphazene compound represented by the following formula (3) 0.09 parts by mass of 1-ethynylcyclohexanol, 0.38 parts by mass of a dimethylpolysiloxane solution containing 1% by mass of a chloroplatinic acid / 1,3-divinyltetramethyldisiloxane complex as a platinum atom content, Sidoxypropyltrimethoxysilane 0.3 parts by mass, titanium tetra-2-ethylhexoxide 0.2 parts by mass Are mixed at room temperature for 1 hour to obtain a composition B (molar ratio of SiH groups in component (F) to silicon atom-bonded vinyl groups in components (A) and (B); SiH / SiVi = 5). Prepared. In addition, the heating loss (150 degreeC, 3 hours) of the whole (A) component was 0.3 mass%.

About the obtained composition B, it carried out similarly to Example 1, and measured hardness, elongation at the time of cutting | disconnection, tensile strength, tearing strength, a Scott stagnation test, and a combustibility test. The results are shown in Table 1.

[Comparative Example 1]
At 25 ° C., 76.5 parts by mass of the base compound (II) obtained in Preparation Example 2 was blocked with vinyldimethylsiloxy groups at both ends of the molecular chain, and the loss on heating at 150 ° C. for 3 hours was 1.2% by mass. 10 parts by weight of dimethylpolysiloxane having a viscosity of about 30,000 mPa · s, both ends of the molecular chain are blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 1.1% by weight at 25 ° C. At 25 ° C., 35.5 parts by mass of dimethylpolysiloxane having a viscosity of about 1,000 mPa · s, both ends of the molecular chain blocked with vinyldimethylsiloxy groups, and the loss on heating at 150 ° C. for 3 hours is 1.1% by mass. 5 parts by weight of dimethylpolysiloxane having a viscosity of about 5,000 mPa · s, 39.5 mol% of (CH ₃ ) ₃ SiO _1/2 units and (CH ₃ ) ₂ (CH ₂ ═CH) SiO _1/2 units 6 .5 mol% Organopolysiloxane resin 5 parts by weight of the three-dimensional network consisting of SiO ₂ units 54 mol%, a viscosity at 25 ° C. is 45 mPa · s, with both molecular chain terminals trimethyl having silicon-bonded hydrogen atom in a molecular chain side chains Siloxy group-blocked dimethylsiloxane / methylhydrogensiloxane copolymer (silicon-bonded hydrogen atom content = 1.08 mass%) 6.4 parts by mass, 1-ethynylcyclohexanol 0.09 parts by mass, chloroplatinic acid / 1 , 3-divinyltetramethyldisiloxane complex containing 0.38 parts by mass of a dimethylpolysiloxane solution containing 1% by mass as a platinum atom content, 0.3 parts by mass of γ-glycidoxypropyltrimethoxysilane, titanium tetra-2- 0.2 parts by mass of ethyl hexoxide was mixed at room temperature for 1 hour, and composition C ((A) component and (B The molar ratio of SiH groups (F) in the component to silicon-bonded vinyl groups in component; SiH / SiVi = 5) was prepared. In addition, the heat loss (150 degreeC, 3 hours) of the whole (A) component was 1.2 mass%.
About the obtained composition C, the hardness, elongation at break, tensile strength, tear strength, Scott stagnation test, and flammability test were performed in the same manner as in Example 1. The results are shown in Table 1.

[Comparative Example 2]
Example 1 except that 76.5 parts by mass of the base compound (III) obtained in Preparation Example 3 was used instead of 76.5 parts by mass of the base compound (I) obtained in Preparation Example 1 of Example 1. A composition D was prepared with the same formulation. In addition, the heating loss (150 degreeC, 3 hours) of the whole (A) component was 0.3 mass%.
About the obtained composition D, it carried out similarly to Example 1, and measured hardness, elongation at the time of cutting | disconnection, tensile strength, tear strength, and a Scott sag test and a flammability test. The results are shown in Table 1.

  According to the present invention, when used in a silicone rubber coating layer of an air bag base fabric, the coating fabric provides a cured film (coating layer) excellent in low burning rate property defined in FMVSS-302. A coating agent composition is obtained.

Claims (4)

(A) Organopolysiloxane containing an alkenyl group bonded to two or more silicon atoms in one molecule: 100 parts by mass
(B) three-dimensional network organopolysiloxane resin (provided that the organopolysiloxane resin does not contain silicon-bonded hydrogen atoms): 0.1 to 50 parts by mass;
(C) Silica fine powder having a BET specific surface area of 50 m ² / g or more: 10 to 30 parts by mass,
(D) Silica surface treatment agent: 3 to 20 parts by mass,
(E) Water: 0.5-5 parts by mass
(F) Organohydrogenpolysiloxane containing hydrogen atoms bonded to at least two silicon atoms in one molecule: The number of hydrogen atoms bonded to silicon atoms contained in one molecule of this component is (A) An amount of 1 to 10 per component and a total of one silicon-bonded alkenyl group in component (B),
(G) addition reaction catalyst: effective amount,
(H) Organosilicon compound containing an adhesion-imparting functional group: A method for producing a liquid silicone rubber coating agent composition for curtain airbags comprising 0.1 to 10 parts by mass as an essential component, the component (A) And controlling the weight loss after heating at 150 ° C. for 3 hours to 1.0% by mass or less, and
[I] a first step of kneading a part of the component (A) and all of the component (C), the component (D) and the component (E) at a temperature of less than 130 ° C .;
[Ii] a second step of heat-treating the mixture obtained in the first step at 130 to 200 ° C., and [iii] the remainder of the component (A) and the component (B) in the mixture after the heat treatment And a method for producing a liquid silicone rubber coating composition for curtain airbags, comprising a third step of kneading the total amount of components (F) to (H).   Further, (I) at least one condensation catalyst selected from organic titanium compounds and organic zirconium compounds is contained in an amount of 0.1 to 5 parts by mass with respect to 100 parts by mass of component (A), and the third step of [iii] above The method for producing a liquid silicone rubber coating composition for a curtain airbag according to claim 1, wherein the composition is added and kneaded. Furthermore, (J) 0.1 to 10 parts by mass of an organic phosphazene compound represented by the following general formula (1) with respect to 100 parts by mass of component (A) is added in the third step of [iii] above, The manufacturing method of the liquid silicone rubber coating agent composition for curtain airbags of Claim 1 or 2 knead | mixed.

(In the formula, R ¹ are the same or different unsubstituted or substituted monovalent hydrocarbon groups. N is an integer of 2 to 10.)   The method for producing a liquid silicone rubber coating composition for a curtain airbag according to any one of claims 1 to 3, wherein the silica surface treatment agent is hexamethyldisilazane.