JP5858387B2 - Polyester synthesis using organic catalyst - Google Patents
Polyester synthesis using organic catalyst Download PDFInfo
- Publication number
- JP5858387B2 JP5858387B2 JP2012555708A JP2012555708A JP5858387B2 JP 5858387 B2 JP5858387 B2 JP 5858387B2 JP 2012555708 A JP2012555708 A JP 2012555708A JP 2012555708 A JP2012555708 A JP 2012555708A JP 5858387 B2 JP5858387 B2 JP 5858387B2
- Authority
- JP
- Japan
- Prior art keywords
- polyester
- catalyst
- acid
- synthesized
- synthesizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、有機触媒を用いて、ジオールとジカルボン酸またはヒドロキシカルボン酸からポリエステルを合成するポリエステル合成方法に関するものである。 The present invention relates to a polyester synthesis method in which a polyester is synthesized from a diol and a dicarboxylic acid or hydroxycarboxylic acid using an organic catalyst.
一般にポリエステルの合成にはジカルボン酸とジオールまたはヒドロキシカルボン酸の直接重合法が採用されているが、２００〜２５０℃等の非常に高温でエステル化をさせるのが一般的である。このため、環境低負荷が望まれ、低炭素化・省エネルギー化が課題とされる昨今の世界情勢から、反応の低温化が必要である。 In general, a direct polymerization method of a dicarboxylic acid and a diol or a hydroxycarboxylic acid is employed for the synthesis of the polyester, but the esterification is generally performed at a very high temperature such as 200 to 250 ° C. For this reason, it is necessary to lower the temperature of the reaction due to the recent global situation where low environmental impact is desired and low carbon and energy saving are the issues.
また、脂肪族ポリエステルにおいては、耐熱性に劣り、熱分解してしまうこともあることからも、２００℃よりも低い低温での反応が必要となる。しかし、低温で反応させるためにはこの反応を効率よく触媒する触媒の検索が必須となるが、ほとんどのルイス酸触媒は、水をはじめとするプロトン性の化合物に対する安定性が非常に低く困難であった。 Moreover, since aliphatic polyester is inferior in heat resistance and may be thermally decomposed, a reaction at a low temperature lower than 200 ° C. is required. However, in order to react at a low temperature, it is essential to search for a catalyst that efficiently catalyzes this reaction. However, most Lewis acid catalysts are very low in stability with respect to protic compounds such as water, and are difficult. there were.
近年、このような観点から触媒が開発され高分子量の脂肪族ポリエステルも製造されるにいたっている。たとえば、1,4-ブタンジオールとコハク酸等に触媒としてアセトアセトイル型亜鉛キレート化合物等を用いて脂肪族ポリエステルが合成され、市販されている（特許文献１、非特許文献１）。この例では、一旦分子量が15000程度のポリエステルを合成し、これをジイソシアネートを用いて結合して分子量が、35000程度のポリマーを得ているが、この高分子量の脂肪族ポリエステルを直接合成するに至っておらず、反応温度も200℃程度と高い。更に、最近ではジオールとジカルボン酸にスズジスタノキサン（非特許文献２）または、塩化ハフニウム・THF錯体（非特許文献３）を用いて分子量が、1-10万程度の脂肪族ポリエステルが合成されるに至っている。しかし、いずれも有機溶媒を用いる溶液重縮合法であった。最近では、深刻化する環境問題を背景に、有機溶媒やスズなどの重金属触媒の使用に対する法的な規制が大きくなってきている。 In recent years, catalysts have been developed from this point of view, and high molecular weight aliphatic polyesters have also been produced. For example, aliphatic polyesters are synthesized using 1,4-butanediol, succinic acid, and the like using a acetoacetoyl zinc chelate compound as a catalyst, and are commercially available (Patent Document 1, Non-Patent Document 1). In this example, a polyester having a molecular weight of about 15000 is once synthesized and bonded using diisocyanate to obtain a polymer having a molecular weight of about 35,000. However, this high molecular weight aliphatic polyester has been directly synthesized. The reaction temperature is as high as about 200 ° C. Furthermore, recently, an aliphatic polyester having a molecular weight of about 100,000 is synthesized using diol and dicarboxylic acid using tin distannoxane (Non-patent Document 2) or hafnium chloride / THF complex (Non-patent Document 3). Has reached the point. However, all were solution polycondensation methods using an organic solvent. In recent years, legal restrictions on the use of organic solvents and heavy metal catalysts such as tin have been increasing against the background of increasing environmental problems.
本願発明者は、すでに、希土類トリフラートがカルボン酸とアルコールのエステル化を触媒することを見出しており、溶媒を用いない塊状重合により８０℃の温度で高分子量と目される分子量１万のポリエステルを得ており、１８０℃では３万の分子量のポリエステルを合成している（特許文献２）。さらに、その触媒をポリスチレン樹脂に担持させることで、回収に分液操作を必要としない触媒の合成に成功している(特許文献３)。 The present inventor has already found that rare earth triflate catalyzes esterification of carboxylic acid and alcohol, and has a molecular weight of 10,000, which is regarded as a high molecular weight at a temperature of 80 ° C. by bulk polymerization without using a solvent. Polyester having a molecular weight of 30,000 is synthesized at 180 ° C. (Patent Document 2). Furthermore, by supporting the catalyst on a polystyrene resin, a catalyst that does not require a liquid separation operation for recovery has been successfully synthesized (Patent Document 3).
しかし、このとき用いた金属触媒が高価であるという欠点があった。このため、金属触媒よりも一般的に安価である非金属の有機触媒で、２００℃よりも低温で高分子量のポリエステルを合成できることが望まれる。 However, there is a drawback that the metal catalyst used at this time is expensive. For this reason, it is desired that a high molecular weight polyester can be synthesized at a temperature lower than 200 ° C. with a nonmetallic organic catalyst that is generally cheaper than a metal catalyst.
ちなみに、非金属の有機触媒を用いたポリエステル合成例として、p‐トルエンスルホン酸などのスルホン酸やリン酸などのリン化合物(非特許文献４)、またはスルホン酸・ホスフィン塩、スルホン酸・アミン塩(特許文献４)、窒素化合物(特許文献５)、さらに酵素を用いた例(非特許文献５)が挙げられる。これらのうち、含窒素有機化合物1，3−ビス(2，4，6−トリメチルフェニル)−2−メトキシイミダゾリジンを用いた場合では、２５０℃でポリエステル合成が可能であるが、従来の有機触媒を用いた場合よりも、反応のさらなる低温化が望まれ、さらに、ポリエステル合成に対する活性の向上が望まれる。 Incidentally, examples of polyester synthesis using a non-metallic organic catalyst include sulfonic acids such as p-toluenesulfonic acid and phosphorus compounds such as phosphoric acid (Non-Patent Document 4), sulfonic acid / phosphine salts, sulfonic acid / amine salts. (Patent Document 4), nitrogen compounds (Patent Document 5), and examples using enzymes (Non-Patent Document 5). Among these, when nitrogen-containing organic compound 1,3-bis (2,4,6-trimethylphenyl) -2-methoxyimidazolidine is used, polyester synthesis is possible at 250 ° C. It is desired to further lower the temperature of the reaction, compared with the case of using, and further to improve the activity for polyester synthesis.
また、スルホン酸に関しては、ｐ−トルエンスルホン酸やメタンスルホン酸を用いて１２０℃以上の温度でポリエステルを合成することが特許文献６の実施例に記載され、ｐ−トルエンスルホン酸やメタンスルホン酸を用いて１００℃以上の温度でプレポリマーを合成した後、プレポリマーの固相重合によりポリエステルを得ることが特許文献７の実施例に記載されている。なお、特許文献６、７には、１００℃よりも低温で高分子量のポリエステルを合成できたという事実は記載されていない。 As for the sulfonic acid, synthesis of polyester at a temperature of 120 ° C. or higher using p-toluenesulfonic acid or methanesulfonic acid is described in Examples of Patent Document 6, and p-toluenesulfonic acid or methanesulfonic acid is used. It is described in the example of Patent Document 7 that a polyester is obtained by synthesizing a prepolymer at a temperature of 100 ° C. or higher by using solid state polymerization of the prepolymer. Patent Documents 6 and 7 do not describe the fact that a high molecular weight polyester could be synthesized at a temperature lower than 100 ° C.
また、ｐ−トルエンスルホン酸やメタンスルホン酸を用いたエステル化反応が特許文献８の実施例に記載されている。 In addition, an esterification reaction using p-toluenesulfonic acid or methanesulfonic acid is described in Examples of Patent Document 8.
一方で、ビス(パーフルオロアルカンスルホニル)イミドが低分子エステル化合物の合成に高活性であることが報告されている(特許文献９)。しかし、これはポリエステル合成を目指したものではない。また、エステル化反応の繰り返しによりポリエステルは合成されるため、一般的に、低分子エステル化合物の合成で高活性な触媒が、ポリエステル合成でも高活性を示すとは限らない。 On the other hand, bis (perfluoroalkanesulfonyl) imide has been reported to be highly active in the synthesis of low molecular ester compounds (Patent Document 9). However, this is not aimed at polyester synthesis. In addition, since polyester is synthesized by repeating esterification reaction, generally, a highly active catalyst for synthesizing low molecular weight ester compounds does not always exhibit high activity for polyester synthesis.
なお、ビス(パーフルオロアルカンスルホニル)イミドに関しては、その酸性度の強弱についての報告（非特許文献６）はあるが、ポリエステル合成の触媒として有効であることの報告はなされていない。 As for bis (perfluoroalkanesulfonyl) imide, there is a report (Non-patent Document 6) regarding the strength of acidity, but no report has been made that it is effective as a catalyst for polyester synthesis.
同様に、ビス(パーフルオロアルカンスルホニル)イミドに関しては、例えば、ビストリフルオロメタンスルホニルイミドをアシル化反応の触媒として使用することが、特許文献１０、１１に記載されているが、ビス(パーフルオロアルカンスルホニル)イミドがポリエステル合成の触媒として有効であることまでは記載されていない。 Similarly, regarding bis (perfluoroalkanesulfonyl) imide, for example, the use of bistrifluoromethanesulfonylimide as a catalyst for the acylation reaction is described in Patent Documents 10 and 11, but bis (perfluoroalkane) is used. No mention has been made that sulfonyl) imide is effective as a catalyst for polyester synthesis.
本発明は、上記点に鑑み、有機触媒によるポリエステル合成方法において、１００℃よりも低温で高分子量のポリエステルを合成できるポリエステル合成方法を提供することを目的とする。 In view of the above points, an object of the present invention is to provide a polyester synthesis method capable of synthesizing a high molecular weight polyester at a temperature lower than 100 ° C. in a polyester synthesis method using an organic catalyst.
本発明者は、ｐ−トルエンスルホン酸がポリエステル合成に有用であることから、酸性度の大きなプロトン酸であるビス(パーフルオロアルカンスルホニル)イミドまたはパーフルオルアルカンスルホン酸に着眼し、これらを用いることでポリエステルの合成を行った。まず、この触媒を1.0mol%で等モル量の3‐メチル‐1，5‐ペンタンジオールとアジピン酸の60℃での重縮合を試みたところ、12時間で数平均分子量15000を超えるポリエステルが得られ、さらに高分子量生成中に触媒の昇華が見られた。この発見をもとに触媒量、重合温度の最適化、昇華による触媒の回収および精製を行い、本発明を完成させた。 The present inventor focuses on bis (perfluoroalkanesulfonyl) imide or perfluoroalkanesulfonic acid, which is a protonic acid having a high acidity, and uses these because p-toluenesulfonic acid is useful for polyester synthesis. In this way, polyester was synthesized. First, polycondensation of this catalyst with 1.0 mol% equimolar amounts of 3-methyl-1,5-pentanediol and adipic acid at 60 ° C yielded a polyester with a number average molecular weight exceeding 15,000 in 12 hours. Furthermore, sublimation of the catalyst was observed during high molecular weight generation. Based on this discovery, the present invention was completed by optimizing the catalyst amount and polymerization temperature, and recovering and purifying the catalyst by sublimation.
即ち、本発明の第１の特徴は、下記の一般式（Ｉ）で表される低級ビス（パーフルオロアルカンスルホニル）イミドを触媒として用いて、原料であるジオールとジカルボン酸またはヒドロキシカルボン酸の直接重合法によりポリエステルを合成することにある。 That is, the first feature of the present invention is that a lower bis (perfluoroalkanesulfonyl) imide represented by the following general formula (I) is used as a catalyst to directly produce a diol and a dicarboxylic acid or hydroxycarboxylic acid as raw materials. It is to synthesize polyester by a polymerization method.
一般式（Ｉ）中のＲｆは、炭素数１〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。
また、本発明の第２の特徴は、下記の一般式（ＩＩ）で表される低級パーフルオロアルカンスルホン酸を触媒として用いて、原料であるジオールとジカルボン酸またはヒドロキシカルボン酸の直接重合法によりポリエステルを合成することにある（請求項４）。この第２の特徴では、一般式（ＩＩ）中のＲｆは、炭素数４〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。
また、本発明の第３の特徴は、下記の一般式（ＩＩ）で表される低級パーフルオロアルカンスルホン酸を触媒として用いて、原料であるジオールとジカルボン酸またはヒドロキシカルボン酸の直接重合法によりポリエステルを合成するとともに、塊状重合によりポリエステルを合成することにある（請求項６）。この第３の特徴では、一般式（ＩＩ）中のＲｆは、炭素数１〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。
Rf in one general formula (I) shows a perfluoroalkyl group having a linear or branched chain of 1 to 10 carbon atoms.
In addition, the second feature of the present invention is that the lower perfluoroalkanesulfonic acid represented by the following general formula (II) is used as a catalyst, and a direct polymerization method of a raw material diol and dicarboxylic acid or hydroxycarboxylic acid. It is to synthesize polyester (claim 4) . In the second feature, Rf in the general formula (II) represents a perfluoroalkyl group having a linear or branched chain having 4 to 10 carbon atoms.
In addition, the third feature of the present invention is that by a direct polymerization method of diol and dicarboxylic acid or hydroxycarboxylic acid as raw materials using lower perfluoroalkanesulfonic acid represented by the following general formula (II) as a catalyst. In addition to synthesizing polyester, polyester is synthesized by bulk polymerization. In the third feature, Rf in the general formula (II) represents a perfluoroalkyl group having a linear or branched chain having 1 to 10 carbon atoms.
ここで、一般式（Ｉ）、（ＩＩ）中のＲｆ基については、ポリエステル合成に対する活性の向上の観点では、炭素数が多いもの、すなわち、フッ素含有率が高く、酸性度が高いものであることが好ましいが、炭素数の増加に伴って有機触媒が高価となるため、炭素数を１〜１０としている（第２の特徴では、炭素数を４〜１０としている）。 In here, the general formula (I), Rf group in (II), in view of the improvement of activity against polyester synthesis, there are many carbon atoms, i.e., fluorine content is high, but high acidity Although it is preferable that the organic catalyst becomes expensive as the number of carbons increases, the number of carbons is set to 1 to 10 (in the second feature, the number of carbons is set to 4 to 10) .
本発明の第４の特徴は、ビス(ノナフルオロブタンスルホニル)イミドを触媒として用いた場合、ジカルボン酸とジオールの重縮合やヒドロキシカルボン酸の重縮合に有効となる酸触媒の回収に、昇華を利用できるところにある（請求項３）。従来の酸触媒では分液操作が必要であり、かつ分液により得られた触媒は純粋なものではない可能性があるが、これによると、昇華操作により容易かつ純粋な触媒の除去・回収が可能である。
The fourth feature of the present invention is that, when bis (nonafluorobutanesulfonyl) imide is used as a catalyst, sublimation is performed for recovering an acid catalyst effective for polycondensation of dicarboxylic acid and diol or polycondensation of hydroxycarboxylic acid. It can be used (Claim 3) . Conventional acid catalysts require a liquid separation operation, and the catalyst obtained by liquid separation may not be pure, but according to this, it is easy to remove and recover a pure catalyst by sublimation operation. Is possible.
本発明によれば、ジオールとジカルボン酸またはヒドロキシカルボン酸からポリエステルを合成する場合に、１００℃よりも低温において高分子量のポリエステルを合成できる。上記の通り、p−トルエンスルホン酸がポリエステル合成に有用であることは周知であるが、本発明の触媒は、汎用酸触媒のp−トルエンスルホン酸と比べ、ポリエステル合成において高い活性を示した（後述の実施例１〜１１と比較例１を参照）。 According to the present invention, when a polyester is synthesized from a diol and a dicarboxylic acid or a hydroxycarboxylic acid, a high molecular weight polyester can be synthesized at a temperature lower than 100 ° C. As described above, it is well known that p-toluenesulfonic acid is useful for polyester synthesis. However, the catalyst of the present invention showed higher activity in polyester synthesis than p-toluenesulfonic acid, which is a general-purpose acid catalyst ( (See Examples 1 to 11 and Comparative Example 1 below).
本発明によれば、後述の実施例で明らかにするが、一例として、60℃の塊状重合で高分子量と目される10000以上の分子量のポリエステルを得ることができた。このような低温での合成が可能であり、環境低負荷が望まれ、低炭素化・省エネルギー化が課題とされる中で、本発明ではそれらが大きく改善できた。 According to the present invention, as will be clarified in Examples described later, as an example, a polyester having a molecular weight of 10,000 or more, which is regarded as a high molecular weight by bulk polymerization at 60 ° C., could be obtained. Such low-temperature synthesis is possible, environmental load is desired, and low carbon and energy saving are the issues. In the present invention, they can be greatly improved.
ビス(ノナフルオロブタンスルホンニル)イミドについては、昇華により回収または精製可能なため、分液操作の必要がなく容易に回収または精製・再利用できるようになった。 Since bis (nonafluorobutanesulfonyl) imide can be recovered or purified by sublimation, it can be easily recovered, purified or reused without the need for a liquid separation operation.
本発明で用いる上記一般式（Ｉ）、（ＩＩ）で表される触媒において、一般式（Ｉ）、（ＩＩ）中のＲｆは、炭素数１〜１０の直鎖または分岐鎖を有する低級パーフルオロアルキル基を示し、具体的には、たとえば、トリフルオロメチル基、ペンタフルオロエチル基、ｎ−ヘプタフルオロプロピル基、ｉｓｏ−ヘプタフルオロプロピル基、ｎ−ノナフルオロブチル基、ｉｓｏ−ノナフルオロブチル基、ｓｅｃ−ノナフルオロブチル基、ｔｅｒｔ−ノナフルオロブチル基、ｎ−ウンデカフルオロペンチル基、ｎ−トリデカフルオロヘキシル基、ｎ−ペンタデカフルオロヘプチル基、ｎ−ヘプタデカフルオロオクチル基、ｎ−ノナデカフルオロノニル基、ｎ−ヘンイコサフルオロデシル基などを挙げることができる。 In the catalysts represented by the above general formulas (I) and (II) used in the present invention, Rf in the general formulas (I) and (II) is a lower part having a linear or branched chain having 1 to 10 carbon atoms. A fluoroalkyl group, specifically, for example, trifluoromethyl group, pentafluoroethyl group, n-heptafluoropropyl group, iso-heptafluoropropyl group, n-nonafluorobutyl group, iso-nonafluorobutyl group , Sec-nonafluorobutyl group, tert-nonafluorobutyl group, n-undecafluoropentyl group, n-tridecafluorohexyl group, n-pentadecafluoroheptyl group, n-heptadecafluorooctyl group, n-nona Examples include a decafluorononyl group and an n-henicosafluorodecyl group.
ただし、ポリエステル合成においてより高い活性を得るためには、一般式（Ｉ）、（ＩＩ）中のＲｆが炭素数４〜１０の直鎖または分岐鎖を有する低級パーフルオロアルキル基であることが好ましい。 However, in order to obtain higher activity in the polyester synthesis, Rf in the general formulas (I) and (II) is preferably a lower perfluoroalkyl group having a linear or branched chain having 4 to 10 carbon atoms. .
本発明において合成されるポリエステルに特に制限はなく、合成されたポリマーまたは化合物に主結合として、本発明の触媒の作用により生成されたエステル結合が含まれておればよく、エステル結合以外の結合が含まれることを除外するものではない。このポリエステルは、ジオールとジカルボン酸またはヒドロキシカルボン酸により生成すれば、芳香族、脂肪族またはこれらの混合のいずれでもよい。このポリエステルの数平均分子量（Ｍｎ）は、実用的には７０００以上、特に１００００以上であることが望ましい。 The polyester synthesized in the present invention is not particularly limited, and the synthesized polymer or compound may contain an ester bond generated by the action of the catalyst of the present invention as a main bond. It does not exclude inclusion. This polyester may be aromatic, aliphatic or a mixture thereof as long as it is produced from a diol and a dicarboxylic acid or a hydroxycarboxylic acid. The number average molecular weight (Mn) of this polyester is preferably 7000 or more, particularly 10,000 or more practically.
このポリエステルに用いるジオール、ジカルボン酸、ヒドロキシカルボン酸については特に制限がないが、脂肪族ポリエステルの合成において、ジオールとジカルボン酸を原料として用いるときでは、ジオールとして、化学式がＨＯ−Ｒ１−ＯＨ（Ｒ１は、直鎖、分岐鎖もしくは環状構造を有する脂肪族炭素骨格を示す。）で表されるもの、例えば、エチレングリコール、１,４−ブタンジオール、１,６−へキサンジオール、3‐メチル‐1，5‐ペンタンジオール、デカメチレングリコール、ネオペンチルグリコール、１，４−シクロへキサンジメタノール等を用い、ジカルボン酸として、化学式がＨＯＯＣ−Ｒ２−ＣＯＯＨ（Ｒ２は、直鎖、分岐鎖もしくは環状構造を有する脂肪族炭素骨格を示す。）またはその無水物で表されるもの、例えば、コハク酸、メチルコハク酸、アジピン酸、スベリン酸、セバシン酸、ドデカン酸、などやこれらの無水物、例えば、無水コハク酸、無水アジピン酸等を用いることができる。また、複数種のこれらを用いてもよい。The diol, dicarboxylic acid, and hydroxycarboxylic acid used in this polyester are not particularly limited, but in the synthesis of aliphatic polyester, when diol and dicarboxylic acid are used as raw materials, the chemical formula is HO—R 1 —OH ( R 1 represents an aliphatic carbon skeleton having a linear, branched or cyclic structure.), For example, ethylene glycol, 1,4-butanediol, 1,6-hexanediol, 3- Methyl-1,5-pentanediol, decamethylene glycol, neopentyl glycol, 1,4-cyclohexanedimethanol, etc. are used, and the dicarboxylic acid has a chemical formula of HOOC-R 2 -COOH (R 2 is a straight chain, An aliphatic carbon skeleton having a branched chain or a cyclic structure) or an anhydride thereof; Eg to succinic acid, methyl succinic acid, adipic acid, suberic acid, sebacic acid, dodecanoic acid, and anhydrides thereof, for example, can be used succinic acid anhydride, adipic anhydride. Moreover, you may use multiple types of these.
脂肪族ポリエステルの合成において、ヒドロキシカルボン酸を原料として用いるときでは、乳酸、グリコール酸、リンゴ酸などを用いることができる。また、複数種のこれらを用いてもよい。 In the synthesis of the aliphatic polyester, when hydroxycarboxylic acid is used as a raw material, lactic acid, glycolic acid, malic acid and the like can be used. Moreover, you may use multiple types of these.
触媒の使用量は、原料、すなわち、投入するジオールとジカルボン酸またはヒドロキシカルボン酸に対して、０重量％超、２．６重量％以下、もしくは、０ｍｏｌ％超、１．０ｍｏｌ％以下とすることができる。 The amount of catalyst used should be more than 0% by weight, 2.6% by weight or less, or more than 0% by mole and 1.0% by mole or less based on the raw material, ie, the diol and dicarboxylic acid or hydroxycarboxylic acid to be added. Can do.
また、ジオールとジカルボン酸の投入量は、ほぼ化学量論比とすることが好ましい。重合においては、上記の成分以外に溶媒、酸化防止剤、紫外吸収剤、結晶核剤を適宜使用してもよい。 Moreover, it is preferable that the input amount of the diol and the dicarboxylic acid is approximately stoichiometric. In the polymerization, in addition to the above components, a solvent, an antioxidant, an ultraviolet absorber, and a crystal nucleating agent may be appropriately used.
ジオールとジカルボン酸またはヒドロキシカルボン酸の直接重合法によりポリエステルを合成するのであれば、重合形式はいかなるものであってもいいが、一般式（Ｉ）、（ＩＩ）で表される触媒には溶媒を用いない塊状重合が適している。反応圧は、重合反応形式により当該分野で適切な圧を用いればよいが、塊状重合の場合には、脱水を促進するため0.3−3.0mmHgが好ましい。 As long as the polyester is synthesized by a direct polymerization method of a diol and a dicarboxylic acid or a hydroxycarboxylic acid, any type of polymerization may be used, but the catalyst represented by the general formulas (I) and (II) is a solvent. Bulk polymerization without using is suitable. The reaction pressure may be an appropriate pressure in the field depending on the polymerization reaction mode, but in the case of bulk polymerization, 0.3 to 3.0 mmHg is preferable in order to promote dehydration.
反応温度は、脱水可能な温度および触媒の活性が適切となる温度で行うことが好ましい。具体的には、脱水可能な温度は３５℃以上であることや、後述の実施例での反応温度からわかるように、例えば、反応温度を３５℃〜８５℃とすることが可能である。特に、本発明では、反応温度を８０℃以下としたり、６０℃以下としたりすることも可能である。 The reaction temperature is preferably a temperature at which dehydration is possible and a temperature at which the activity of the catalyst is appropriate. Specifically, the dehydrating temperature is 35 ° C. or higher, and the reaction temperature can be set to 35 ° C. to 85 ° C., for example, as can be seen from the reaction temperature in Examples described later. In particular, in the present invention, the reaction temperature can be 80 ° C. or lower or 60 ° C. or lower.
一般式（Ｉ）、（ＩＩ）で表される触媒によれば、塊状重合により低温(60℃)でポリエステル反応を触媒作用し、分子量が10000以上のポリエステルを合成できる。また、後述の実施例で用いた触媒の価格は、２０１１年２月現在で126〜3660円/gであり、特許文献２に記載の金属触媒の価格は、２０１１年２月現在で10000円/g以上であることから、本発明によれば、金属触媒に比べて安価な有機触媒を用いることができる。
According to the catalysts represented by the general formulas (I) and (II), the polyester reaction can be catalyzed at a low temperature (60 ° C.) by bulk polymerization to synthesize a polyester having a molecular weight of 10,000 or more. Further, the price of the catalyst used in the examples described later is 126 to 3660 yen / g as of February 2011, and the price of the metal catalyst described in
加えて、ビス(ノナフルオロブタンスルホニル)イミドに関しては、触媒が加熱・減圧操作により昇華されるため、分液操作が必要なく触媒除去が簡便である。さらに、昇華しやすい性質を持つため、触媒の精製に利用できる。 In addition, with regard to bis (nonafluorobutanesulfonyl) imide, the catalyst is sublimated by heating and depressurizing operation, and therefore, a liquid separation operation is not necessary and the catalyst removal is simple. Furthermore, since it has the property of being easily sublimated, it can be used for catalyst purification.
また、一般式（Ｉ）、（ＩＩ）で表される触媒は非金属触媒であるため、合成されたポリエステルが生命体やマイクロ電子デバイスに与える影響はない。それらの理由から工業的応用範囲がより広がると考えられる。 In addition, since the catalysts represented by the general formulas (I) and (II) are non-metallic catalysts, the synthesized polyester does not affect living organisms and microelectronic devices. For these reasons, it is considered that the industrial application range is further expanded.
以下、実施例にて本発明を例証するが、本発明を限定することを意図するものではない。 The following examples illustrate the invention, but are not intended to limit the invention.
実施例１〜１１および比較例１では、ジカルボン酸として、下記式（ＩＩＩ）で表されるアジピン酸(ナカライテスク製「ADA」と略す。)を用い、ジオールとして、下記式（ＩＶ）で表される3‐メチル‐1，5‐ペンタンジオール(和光純薬製「MPD」と略す。)を用いた。 In Examples 1 to 11 and Comparative Example 1, adipic acid (abbreviated as “ADA” manufactured by Nacalai Tesque) represented by the following formula (III) is used as the dicarboxylic acid, and the diol is represented by the following formula (IV). 3-methyl-1,5-pentanediol (abbreviated as “MPD” manufactured by Wako Pure Chemical Industries, Ltd.) was used.
触媒としては、実施例１、２では下記式（Ｖ）で表されるビス(ノナフルオロブタンスルホニル)イミド(三菱マテリアル電子化成製「Nf2NH」と略す。)を用い、実施例３、４、５では下記式（ＶＩ）で表されるノナフルオロブタンスルホン酸(ALDRICH製「NfOH」と略す。)を用い、実施例６、７、８では下記式（ＶＩＩ）で表されるビス(トリフルオロメタンスルホニル)イミド(ALDRICH製「Tf2NH」略す。)を用い、実施例９、１０、１１では下記式（ＶＩＩＩ）で表されるトリフルオロメタンスルホン酸(東京化成工業製「TfOH」と略す。)を用いた。As the catalyst, in Examples 1 and 2, bis (nonafluorobutanesulfonyl) imide represented by the following formula (V) (abbreviated as “Nf 2 NH” manufactured by Mitsubishi Materials Electronic Chemicals) was used. In No. 5, nonafluorobutanesulfonic acid represented by the following formula (VI) (abbreviated as “NfOH” manufactured by ALDRICH) was used. In Examples 6, 7, and 8, bis (trifluoro) represented by the following formula (VII) was used. In Examples 9, 10 and 11, trifluoromethanesulfonic acid represented by the following formula (VIII) (“TfOH” manufactured by Tokyo Chemical Industry Co., Ltd.) is used, using lomethanesulfonyl) imide (abbreviated “Tf 2 NH” manufactured by ALDRICH). ) Was used.
なお、「Nf2NH」、「Tf2NH」は、それぞれ、一般式（Ｉ）中のＲｆ基の炭素数が４、１のものであり、「NfOH」、「TfOH」は、それぞれ、一般式（ＩＩ）中のＲｆ基の炭素数が４、１のものである。“Nf 2 NH” and “Tf 2 NH” are those in which the Rf group in the general formula (I) has 4 or 1 carbon atoms, respectively. “NfOH” and “TfOH” The Rf group in formula (II) has 4 or 1 carbon atoms.
また、比較例１、２では、触媒として、p−トルエンスルホン酸(ナカライテスク製「PTSA」と略す。)を用いた。 In Comparative Examples 1 and 2, p-toluenesulfonic acid (abbreviated as “PTSA” manufactured by Nacalai Tesque) was used as a catalyst.
また、実施例１２〜１６では、触媒として式（Ｖ）で表されるNf2NHを用いた。In Examples 12 to 16, Nf 2 NH represented by the formula (V) was used as a catalyst.
実施例１２では、ジカルボン酸として、下記式（ＩＸ）で表されるドデカン二酸(東京化成工業製)を用い、ジオールとして、下記式（Ｘ）で表される1，12-ドデカンジオール(東京化成工業製)を用いた。 In Example 12, dodecanedioic acid (manufactured by Tokyo Chemical Industry Co., Ltd.) represented by the following formula (IX) is used as the dicarboxylic acid, and 1,12-dodecanediol (Tokyo) represented by the following formula (X) is used as the diol. Kasei Kogyo) was used.
実施例１３では、ジカルボン酸として、式（ＩＩＩ）で表されるＡＤＡを用い、ジオールとして、下記式（ＸＩ）で表されるジエチレングリコール(和光純薬製)を用いた。 In Example 13, ADA represented by the formula (III) was used as the dicarboxylic acid, and diethylene glycol (manufactured by Wako Pure Chemical Industries) represented by the following formula (XI) was used as the diol.
実施例１４では、ジカルボン酸として、式（ＩＩＩ）で表されるＡＤＡを用い、ジオールとして、下記式（ＸＩＩ）で表されるトリエチレングリコール(和光純薬製)を用いた。 In Example 14, ADA represented by the formula (III) was used as the dicarboxylic acid, and triethylene glycol (manufactured by Wako Pure Chemical Industries) represented by the following formula (XII) was used as the diol.
実施例１５および比較例２では、ジカルボン酸として、下記式（ＸＩＩＩ）で表されるマレイン酸(ナカライテスク製)を用い、ジオールとして、下記式（ＸＩＶ）で表される4，4-イソプロピリデン(2−フェノキシエタノール)(和光純薬製)を用いた。 In Example 15 and Comparative Example 2, maleic acid (manufactured by Nacalai Tesque) represented by the following formula (XIII) was used as the dicarboxylic acid, and 4,4-isopropylidene represented by the following formula (XIV) was used as the diol. (2-Phenoxyethanol) (manufactured by Wako Pure Chemical Industries) was used.
実施例１６では、ジカルボン酸として、下記式（ＸＶ）で表されるフタル酸(ナカライテスク製)を用い、ジオールとして、式（ＩＶ）で表されるＭＰＤを用いた。 In Example 16, phthalic acid (manufactured by Nacalai Tesque) represented by the following formula (XV) was used as the dicarboxylic acid, and MPD represented by the formula (IV) was used as the diol.
（実施例１〜１１および比較例１）
攪拌機を備えた容積が10mLのナスフラスコに、表1に示すジオール、ジカルボン酸および触媒を入れた。このとき、ジオールおよびジカルボン酸の使用量は7.0ミリモルずつであり、触媒の使用量（原料に対する濃度）は、表１に示す通りであり、0.1〜1.0wt%の範囲内もしくは0.10〜0.88mol%の範囲内である。(Examples 1 to 11 and Comparative Example 1)
The diol, dicarboxylic acid and catalyst shown in Table 1 were placed in an eggplant flask having a volume of 10 mL equipped with a stirrer. At this time, the amount of diol and dicarboxylic acid used is 7.0 mmol each, and the amount of catalyst used (concentration with respect to the raw material) is as shown in Table 1, within the range of 0.1 to 1.0 wt% or 0.10 to 0.88 mol%. Is within the range.
そして、80℃で系の均一化を行った後、系を60℃にして、徐々に減圧していき、ジオールとジカルボン酸との直接重縮合を行い、最終的には系を1mmHg以下で減圧しつつ生成する水分を除去した。具体的には、0.3mmHgの減圧下、60℃で18時間加熱した。その結果、赤褐色ワックス状の重合体が得られた。 After homogenizing the system at 80 ° C, the system was gradually reduced in pressure to 60 ° C, and direct polycondensation of diol and dicarboxylic acid was performed. Finally, the system was depressurized at 1 mmHg or less. However, the generated water was removed. Specifically, it was heated at 60 ° C. for 18 hours under a reduced pressure of 0.3 mmHg. As a result, a reddish brown waxy polymer was obtained.
表１に、得られた重合体の分子量Ｍｎと、分子量分布（Ｍｗ／Ｍｎ）とを示す。分子量、分子量分布は、サイズ排除クロマトグラフィーで測定した結果である。また、図１に、実施例１で合成したポリエステルのプロトン核磁気共鳴（ＮＭＲ）スペクトルを示し、図２に、想定するポリエステルの構造を示す。図１、２中のa-fはNMRの帰属を示している。 Table 1 shows the molecular weight Mn and the molecular weight distribution (Mw / Mn) of the obtained polymer. The molecular weight and molecular weight distribution are the results of measurement by size exclusion chromatography. FIG. 1 shows a proton nuclear magnetic resonance (NMR) spectrum of the polyester synthesized in Example 1, and FIG. 2 shows an assumed polyester structure. In FIGS. 1 and 2, a-f indicates the assignment of NMR.
表１に示されるように、実施例１〜１１では、分子量10000以上のポリエステルを合成することができ、特に、実施例１、４、１０では、分子量20000程度のポリエステルを合成することができた。 As shown in Table 1, in Examples 1 to 11, a polyester having a molecular weight of 10,000 or more could be synthesized. In particular, in Examples 1, 4, and 10, a polyester having a molecular weight of about 20,000 could be synthesized. .
これに対して、比較例１で得られたポリエステルの分子量は、6000程度であった。よって、実施例１〜１１と比較例１とから、ビス(パーフルオロアルカンスルホニル)イミドまたはパーフルオロアルカンスルホン酸は、0.1mol%といった低触媒濃度において、汎用酸触媒であるPTSAと比べて、高分子量体のポリエステル合成が可能であることがわかる。 On the other hand, the molecular weight of the polyester obtained in Comparative Example 1 was about 6000. Therefore, from Examples 1 to 11 and Comparative Example 1, bis (perfluoroalkanesulfonyl) imide or perfluoroalkanesulfonic acid is higher than PTSA, which is a general acid catalyst, at a low catalyst concentration of 0.1 mol%. It can be seen that a polyester having a molecular weight can be synthesized.
また、実施例1と6とを比較することにより、一般式（I）の触媒において、フッ素含有率が大きなものほど、活性が高いことが分かる。同様に、実施例3と9とを比較することにより、一般式（II）の触媒において、フッ素含有率が大きなものほど、活性が高いことが分かる。 Further, by comparing Examples 1 and 6, it can be seen that the higher the fluorine content in the catalyst of the general formula (I), the higher the activity. Similarly, by comparing Examples 3 and 9, it can be seen that the larger the fluorine content in the catalyst of the general formula (II), the higher the activity.
なお、従来の有機触媒を用いたポリエステル合成においては、本実施例のように、有機触媒としてフッ素含有イミド化合物を用いた例はなく、さらにノナフルオロブタンスルホン酸のようにフッ素含有量を上昇させることにより、ポリエステル合成に対する活性の向上を目指した例はない。また、実施例１および２において、ポリエステル合成中に触媒の昇華がみられ、触媒を回収することができた。 In addition, in the polyester synthesis using the conventional organic catalyst, there is no example using the fluorine-containing imide compound as the organic catalyst as in this example, and the fluorine content is further increased like nonafluorobutanesulfonic acid. Therefore, there is no example which aimed at the improvement of the activity with respect to polyester synthesis. In Examples 1 and 2, sublimation of the catalyst was observed during the synthesis of the polyester, and the catalyst could be recovered.
なお、本実施例では、原料としてジカルボン酸とジオールとを用いたが、原料としてヒドロキシカルボン酸を用いた場合においても、本実施例と同様に、低温で高分子量のポリエステルの合成が期待できる。一般的に、原料としてジカルボン酸とジオールとを用いたポリエステル合成に対して高活性な触媒は、原料としてヒドロキシカルボン酸を用いたポリエステル合成においても高活性を示すからである。
（実施例１２〜１４）
攪拌機を備えた容積が10mLのナスフラスコに、表２に示すジオール、ジカルボン酸および触媒を入れた。このとき、ジオールおよびジカルボン酸の使用量は7.0mmolずつであり、触媒の使用量（原料に対する濃度）は、表２に示す通り、0.1mol%もしくは0.5mol%である。In this example, dicarboxylic acid and diol were used as raw materials. However, when hydroxycarboxylic acid is used as a raw material, synthesis of high molecular weight polyester can be expected at a low temperature as in this example. This is because, in general, a highly active catalyst for polyester synthesis using dicarboxylic acid and diol as raw materials also shows high activity in polyester synthesis using hydroxycarboxylic acid as a raw material.
(Examples 12 to 14)
The diol, dicarboxylic acid and catalyst shown in Table 2 were placed in a 10 mL eggplant flask equipped with a stirrer. At this time, the amount of diol and dicarboxylic acid used is 7.0 mmol each, and the amount of catalyst used (concentration relative to the raw material) is 0.1 mol% or 0.5 mol% as shown in Table 2.
そして、実施例１２は９０℃、実施例１３、１４は８０℃で系の均一化を行った後、系を実施例１２は８５℃、実施例１３、１４は６０℃にして、徐々に減圧していき、ジオールとジカルボン酸との直接重縮合を行い、最終的には系を1mmHg以下で減圧しつつ生成する水分を除去した。具体的には、0.3mmHgの減圧下、各温度で表２に示す時間加熱した。その結果、各重合体が得られた。 Then, after homogenizing the system at 90 ° C. for Example 12 and at 80 ° C. for Examples 13 and 14, the system was 85 ° C. for Example 12 and 60 ° C. for Examples 13 and 14 and gradually reduced in pressure. Then, direct polycondensation of diol and dicarboxylic acid was carried out, and finally the water produced was reduced while the system was decompressed at 1 mmHg or less. Specifically, heating was performed at each temperature for a time shown in Table 2 under a reduced pressure of 0.3 mmHg. As a result, each polymer was obtained.
表２に、得られた重合体の分子量Ｍｎと、分子量分布（Ｍｗ／Ｍｎ）とを示す。分子量、分子量分布は、サイズ排除クロマトグラフィーで測定した結果である。 Table 2 shows the molecular weight Mn and the molecular weight distribution (Mw / Mn) of the polymer obtained. The molecular weight and molecular weight distribution are the results of measurement by size exclusion chromatography.
表２に示されるように、Nf2NHはADAとMPDの組み合わせ以外のモノマーを用いたポリエステル合成においても60℃または85℃といった低温で10000程度またはそれ以上の高分子量体のポリエステルを合成できた。As shown in Table 2, Nf 2 NH was able to synthesize high-molecular-weight polyesters of about 10,000 or more at a low temperature of 60 ° C. or 85 ° C. even in polyester synthesis using monomers other than the combination of ADA and MPD. .
（実施例１５、１６および比較例２）
攪拌機を備えた容積が10mLのナスフラスコに、表３に示すジオール、ジカルボン酸および触媒を入れた。このとき、ジオールおよびジカルボン酸の使用量は5.0mmolずつであり、触媒の使用量（原料に対する濃度）は、表３に示す通り、0.5mol%もしくは1.0mol%である。(Examples 15 and 16 and Comparative Example 2)
The diol, dicarboxylic acid and catalyst shown in Table 3 were placed in a 10 mL eggplant flask equipped with a stirrer. At this time, the amount of diol and dicarboxylic acid used is 5.0 mmol each, and the amount of catalyst used (concentration relative to the raw material) is 0.5 mol% or 1.0 mol% as shown in Table 3.
そして、実施例１５、比較例２は100℃で、実施例１６は110℃で系の均一化を行った後、系を80℃にして、徐々に減圧していき、ジオールとジカルボン酸との直接重縮合を行い、最終的には系を1mmHg以下で減圧しつつ生成する水分を除去した。具体的には、0.3mmHgの減圧下、80℃で表３に示した時間加熱した。その結果、各重合体が得られた。 In Example 15 and Comparative Example 2, the system was homogenized at 100 ° C., and in Example 16 at 110 ° C., the system was then brought to 80 ° C., and the pressure was gradually reduced to obtain a mixture of diol and dicarboxylic acid. Direct polycondensation was performed, and finally the water generated was reduced while the system was decompressed at 1 mmHg or less. Specifically, it was heated at 80 ° C. under a reduced pressure of 0.3 mmHg for the time shown in Table 3. As a result, each polymer was obtained.
表３に、得られた重合体の分子量Ｍｎと、分子量分布（Ｍｗ／Ｍｎ）とを示す。分子量、分子量分布は、サイズ排除クロマトグラフィーで測定した結果である。 Table 3 shows the molecular weight Mn and the molecular weight distribution (Mw / Mn) of the obtained polymer. The molecular weight and molecular weight distribution are the results of measurement by size exclusion chromatography.
表３に示されるように、Nf2NHを用いて芳香族ポリエステルの合成ができた。実施例１５、１６では、80℃といった低温で分子量7000以上のポリエステルを合成することができた。As shown in Table 3, an aromatic polyester was synthesized using Nf 2 NH. In Examples 15 and 16, a polyester having a molecular weight of 7000 or more could be synthesized at a low temperature of 80 ° C.
これに対して、比較例２で得られたポリエステルの分子量は、2000程度であった。よって、実施例１５と比較例２とから、脂肪族ポリエステル合成の場合と同様に、汎用酸触媒であるPTSAと比べて、高分子量体の芳香族ポリエステル合成が可能であることがわかる。 On the other hand, the molecular weight of the polyester obtained in Comparative Example 2 was about 2000. Therefore, it can be seen from Example 15 and Comparative Example 2 that, similar to the case of aliphatic polyester synthesis, it is possible to synthesize a high molecular weight aromatic polyester as compared with PTSA which is a general-purpose acid catalyst.
Claims (12)
（一般式（Ｉ）中のＲｆは、炭素数１〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。） Polyester with an organic catalyst that synthesizes polyester by direct polymerization of diol and dicarboxylic acid or hydroxycarboxylic acid as raw materials using lower bis (perfluoroalkanesulfonyl) imide represented by the following general formula (I) as a catalyst Synthesis method.
(Rf in the general formula (I) represents a perfluoroalkyl group having a linear or branched chain having 1 to 10 carbon atoms.)
（一般式（ＩＩ）中のＲｆは、炭素数４〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。） A polyester synthesis method using an organic catalyst in which a polyester is synthesized by a direct polymerization method of a diol and a dicarboxylic acid or a hydroxycarboxylic acid as raw materials using a lower perfluoroalkanesulfonic acid represented by the following general formula (II) as a catalyst.
(Rf in the general formula (II) represents a perfluoroalkyl group having a linear or branched chain having 4 to 10 carbon atoms.)
（一般式（ＩＩ）中のＲｆは、炭素数１〜１０の直鎖または分岐鎖を有するパーフルオロアルキル基を示す。） Using the lower perfluoroalkanesulfonic acid represented by the following general formula (II) as a catalyst, a polyester is synthesized by a direct polymerization method of a raw material diol and a dicarboxylic acid or a hydroxycarboxylic acid, and the polyester is obtained by bulk polymerization. A method for synthesizing polyester using an organic catalyst.
(Rf in the general formula (II) represents a perfluoroalkyl group having a linear or branched chain having 1 to 10 carbon atoms.)