JP5801765B2 - Non-aqueous secondary battery electrolyte and non-aqueous secondary battery - Google Patents

Description

  The present invention relates to an electrolyte for a non-aqueous secondary battery and a non-aqueous electrolyte secondary battery.

  Recently, secondary batteries called lithium ion batteries, which are attracting attention, use secondary batteries (so-called lithium ion secondary batteries) that use insertion and extraction of lithium in charge and discharge reactions, and precipitation and dissolution of lithium. They are roughly classified into secondary batteries (so-called lithium metal secondary batteries). These realize charging and discharging with a large energy density compared to lead batteries and nickel cadmium batteries. In recent years, application to portable electronic devices such as camera-integrated VTRs (video tape recorders), mobile phones, and notebook personal computers has become widespread by utilizing this characteristic. With the further expansion of applications, the development of secondary batteries that are lighter and have higher energy density as power sources for portable electronic devices is being promoted. Furthermore, in recent years, miniaturization, long life, and high safety have been strongly demanded.

  As an electrolytic solution of a lithium ion secondary battery or a lithium metal secondary battery (hereinafter, these may be simply referred to as a lithium secondary battery), a carbonate ester solvent such as propylene carbonate or diethyl carbonate, Combinations with electrolyte salts such as lithium hexafluorophosphate are widely used. This is because they have high conductivity and are stable in potential.

  On the other hand, since such a low molecular weight organic compound is contained as a component, it is important to impart flame retardancy from the viewpoint of safety. For the purpose of this improvement, a technique for incorporating a cyclic phosphazene or a phosphoric acid compound in an electrolytic solution has been proposed (see Patent Documents 1 and 2).

International Publication No. 2002/082575 Pamphlet JP 2011-108649 A

  Certainly, cyclic phosphazene has the effect of imparting flame retardancy, and its addition to the electrolyte is a very useful technique for enhancing the safety and reliability of lithium secondary batteries. However, on the other hand, according to the present inventors' confirmation, it has been found that this flame retardant generates impurities during use and becomes a factor of deteriorating cycle characteristics and the like.

  Therefore, the present invention, when using an electrolyte containing a specific flame retardant, suppresses the generation of impurities therefrom, and achieves a high level of flame retardancy and good battery performance. An object is to provide a battery electrolyte and a non-aqueous electrolyte secondary battery.

（式中、Ｒ ^ａ は水素原子、直鎖、分岐もしくは環状のアルキル基またはアリール基を表す。Ｒ ^ｂ はヒドロキシル基を有するアルキル基またはヒドロキシル基を有するアリール基を表す。ここで、これらのアルキル基およびアリール基は置換基を有してもよく、またこれらのアルキル基は、直鎖、分岐もしくは環状のアルキル鎖の途中に−Ｏ−が介在していてもよい。ただし、式（５Ｅ）におけるＲ ^ｂ の炭素数は６〜３０である。Ｒ ^ｃ は、カルボアニオン、スルホアニオンもしくはホスホアニオンを含む基を有するアルキル基、または、カルボアニオン、スルホアニオンもしくはホスホアニオンを含む基を有するアリール基を表す。Ｍはアルカリ金属またはアルカリ土類金属を表す。ただし、アルカリ土類金属の場合、２価の金属塩となるため、Ｍ ^＋ を１／２Ｍ ^２＋ と置き換える。Ｘはアニオンを表す。ｎは１〜２０の整数を表す。ｘおよびｙは２〜１０の整数を表す。）
〔２〕アルキル基およびアリール基が有してもよい置換基が、ハロゲン原子、ヒドロキシル基、アルキル基、オキシエチレン基、ポリオキシエチレン基、アリール基、アルコキシ基、アシル基、アシルアミノ基、カルバモイル基、アミノ基およびヘテロ環基から選択される〔１〕に記載の非水二次電池用電解液。
〔３〕正極がニッケルもしくはマンガンを有する活物質を含む〔１〕または〔２〕に記載の非水二次電池用電解液。
〔４〕ホスファゼン化合物が、下記式（３）で表される〔１〕〜〔３〕のいずれか１項に記載の非水二次電池用電解液。

（式中、Ｒ^１〜Ｒ^６は１価の置換基を表す。ｎは１以上の整数を表す。）
〔５〕ホスファゼン化合物が、下記式（３Ａ）または（３Ｂ）で表される〔１〕〜〔４〕のいずれか１項に記載の非水二次電池用電解液。

（式中、Ｒ^２１〜Ｒ ^２８は１価の置換基を表す。ｎは１以上の整数を表す。）
〔６〕式（３Ａ）および（３Ｂ）において、Ｒ^２１〜Ｒ^２８がアルキル基、アルコキシ基、アミノ基、フッ素原子またはそれらの組合せである〔５〕に記載の非水二次電池用電解液。
〔７〕非プロトン性溶媒が、下記式（４Ａ）〜（４Ｃ）のいずれかで表される化合物もしくはその組合せである〔１〕〜〔６〕のいずれか１項に記載の非水二次電池用電解液。

（式中、Ｒ^３１〜Ｒ^３６はそれぞれ水素原子、アルキル基またはアリール基を表す。）
〔８〕 〔１〕〜〔７〕のいずれか１項に記載の非水二次電池用電解液、第一族もしくは第二族に属する金属イオンの挿入放出が可能な正極、および、第一族もしくは第二族に属する金属イオンの挿入放出もしくは溶解析出が可能な負極をそれぞれ具備する非水電解液二次電池。
〔９〕正極がニッケルもしくはマンガンを有する活物質を含む〔８〕に記載の非水電解液二次電池。
〔１０〕電解質とともに非プロトン性溶媒中に含有する非水二次電池用電解液の添加剤キットであって、
下記式（５Ａ）〜（５Ｉ）または（５Ｊ−１）のいずれかで表される界面活性剤、および、ホスファゼン化合物からなる難燃化剤を組み合わせ、界面活性剤の使用量が難燃化剤１００質量部に対し０．１質量部〜１０質量部である添加剤キット。

（式中、Ｒ ^ａ は水素原子、直鎖、分岐もしくは環状のアルキル基またはアリール基を表す。Ｒ ^ｂ はヒドロキシル基を有するアルキル基またはヒドロキシル基を有するアリール基を表す。ここで、これらのアルキル基およびアリール基は置換基を有してもよく、またこれらのアルキル基は、直鎖、分岐もしくは環状のアルキル鎖の途中に−Ｏ−が介在していてもよい。ただし、式（５Ｅ）におけるＲ ^ｂ の炭素数は６〜３０である。Ｒ ^ｃ は、カルボアニオン、スルホアニオンもしくはホスホアニオンを含む基を有するアルキル基、または、カルボアニオン、スルホアニオンもしくはホスホアニオンを含む基を有するアリール基を表す。Ｍはアルカリ金属またはアルカリ土類金属を表す。ただし、アルカリ土類金属の場合、２価の金属塩となるため、Ｍ ^＋ を１／２Ｍ ^２＋ と置き換える。Ｘはアニオンを表す。ｎは１〜２０の整数を表す。ｘおよびｙは２〜１０の整数を表す。）
〔１１〕アルキル基およびアリール基が有してもよい置換基が、ハロゲン原子、ヒドロキシル基、アルキル基、オキシエチレン基、ポリオキシエチレン基、アリール基、アルコキシ基、アシル基、アシルアミノ基、カルバモイル基、アミノ基およびヘテロ環基から選択される〔１０〕に記載の添加剤キット。
The above problem has been solved by the following means.
[1] An electrolyte for a non-aqueous electrolyte secondary battery comprising a positive electrode, a negative electrode, and an electrolyte in contact with both,
An electrolyte , a surfactant represented by any of the following formulas (5A) to (5I) or (5J-1) , and a phosphazene compound are contained in an aprotic solvent, and the content of the surfactant There nonaqueous liquid electrolyte for a secondary battery Ru 0.1 parts by mass to 10 parts by mass der respect phosphazene compound 100 parts by mass.

(In the formula, R ^a represents a hydrogen atom, a linear, branched or cyclic alkyl group, or an aryl group. R ^b represents an alkyl group having a hydroxyl group or an aryl group having a hydroxyl group. The group and the aryl group may have a substituent, and these alkyl groups may have —O— interposed in the middle of a linear, branched or cyclic alkyl chain, provided that the formula (5E) The carbon number of R ^b is 6 to 30. R ^c is an alkyl group having a group containing a carbanion, a sulfoanion or a phosphoanion, or an aryl group having a group containing a carbanion, a sulfoanion or a phosphoanion. M represents an alkali metal or an alkaline earth metal, provided that it is a divalent metal salt in the case of an alkaline earth metal. Therefore, M ⁺ is replaced with 1 / 2M ²⁺ , X represents an anion, n represents an integer of 1 to 20, and x and y represent an integer of 2 to 10).
[2] The substituent that the alkyl group and aryl group may have is a halogen atom, hydroxyl group, alkyl group, oxyethylene group, polyoxyethylene group, aryl group, alkoxy group, acyl group, acylamino group, carbamoyl group The electrolyte solution for nonaqueous secondary batteries as described in [1] selected from an amino group and a heterocyclic group.
[ 3 ] The electrolyte solution for a non-aqueous secondary battery according to [1] or [2] , wherein the positive electrode contains an active material having nickel or manganese.
[4] phosphazene compound is represented by the following formula (3) represented by [1] to the non-aqueous liquid electrolyte for a secondary battery according to any one of [3].

(In the formula, R ^{1 to} R ⁶ represent a monovalent substituent. N represents an integer of 1 or more.)
[5] phosphazene compound, a non-aqueous liquid electrolyte for a secondary battery according to any one of the following formulas (3A) or represented by (3B) [1] to [4].

(In the formula , R ²¹ to R ²⁸ represent a monovalent substituent. N represents an integer of 1 or more.)
[6] In formula (3A) and ^{(3B), R} 21 ~R ²⁸ is an alkyl group, an alkoxy group, an amino group, a non-aqueous secondary according to the fluorine atom or is a combination thereof [5] Battery electrolyte.
[7] an aprotic solvent, a non-aqueous secondary according to any one of a compound or a combination thereof represented by any one of the following formulas (4A) ~ (4C) [1] to [6] Battery electrolyte.

^(Wherein, R 31 ^{to R 36} each represent a hydrogen atom, an alkyl Motoma other represents an aryl group.)
[ 8 ] [1] Non-aqueous liquid electrolyte for a secondary battery according to any one of to [7], the clan Moshiku positive electrode capable of inserting the release of metal ions belonging to the second group, and, first family Moshiku the nonaqueous electrolyte secondary battery insertion release Moshiku metal ion belonging to group II is comprising respective anode capable dissolution and deposition.
[ 9 ] The nonaqueous electrolyte secondary battery according to [ 8 ], wherein the positive electrode includes an active material having nickel or manganese.
[10] A additive kit of the non-aqueous liquid electrolyte for a secondary battery you contained together with an electrolyte in an aprotic solvent,
A surfactant represented by any one of the following formulas (5A) to (5I) or (5J-1) is combined with a flame retardant comprising a phosphazene compound , and the amount of the surfactant used is a flame retardant. The additive kit which is 0.1 mass part-10 mass parts with respect to 100 mass parts .

(In the formula, R ^a represents a hydrogen atom, a linear, branched or cyclic alkyl group, or an aryl group. R ^b represents an alkyl group having a hydroxyl group or an aryl group having a hydroxyl group. The group and the aryl group may have a substituent, and these alkyl groups may have —O— interposed in the middle of a linear, branched or cyclic alkyl chain, provided that the formula (5E) The carbon number of R ^b is 6 to 30. R ^c is an alkyl group having a group containing a carbanion, a sulfoanion or a phosphoanion, or an aryl group having a group containing a carbanion, a sulfoanion or a phosphoanion. M represents an alkali metal or an alkaline earth metal, provided that it is a divalent metal salt in the case of an alkaline earth metal. Therefore, M ⁺ is replaced with 1 / 2M ²⁺ , X represents an anion, n represents an integer of 1 to 20, and x and y represent an integer of 2 to 10).
[11] The substituent that the alkyl group and the aryl group may have is a halogen atom, hydroxyl group, alkyl group, oxyethylene group, polyoxyethylene group, aryl group, alkoxy group, acyl group, acylamino group, carbamoyl group [10] The additive kit according to [10], which is selected from an amino group and a heterocyclic group.

  In the present specification, when simultaneously defining a plurality of substituents or the number of substituents, it means that they may be different from each other. Further, adjacent substituents may be bonded to each other or condensed to form a ring.

  When using an electrolyte containing a specific flame retardant, the electrolyte for a non-aqueous secondary battery and the non-aqueous electrolyte secondary battery of the present invention suppress the generation of impurities from the flame retardant, Achieving high levels of both flame retardancy and good battery performance (especially rate characteristics).

It is sectional drawing which shows typically the mechanism of the lithium secondary battery which concerns on preferable embodiment of this invention. It is sectional drawing which shows the specific structure of the lithium secondary battery which concerns on preferable embodiment of this invention.

  The electrolyte used for the non-aqueous electrolyte secondary battery of the present invention contains a specific flame retardant and a surfactant in an aprotic solvent. Thereby, the improvement effect of the flame retardance which contained the flame retardant is maintained, the fall of the rate characteristic by it is suppressed, and both can be satisfied at a high level. The reason for this includes unclear points, but including the estimation is as follows. That is, it is considered that by containing a relatively small amount of the surfactant, the active site on the electrode surface is covered with the surfactant and the contact with the flame retardant is reduced. As a result, the amount of decomposition of the flame retardant and the solvent is reduced, and the lithium conductive resistance component is reduced, which is considered to improve the battery characteristics. Hereinafter, the present invention will be described in detail based on preferred embodiments thereof.

[Flame retardant]
In the present invention, the phosphazene compound is contained in the electrolyte for a non-aqueous secondary battery. The phosphazene compound means a compound group having a double bond containing phosphorus and nitrogen as constituent elements, and among them, a cyclic phosphazene compound is preferable, and a compound represented by the following formula (3) is more preferable.

・ R ^{1 to} R ⁶
In the formula, R ^{1 to} R ⁶ represent a monovalent substituent. Among the monovalent substituents, preferred are a specific nitrogen-containing group such as an alkyl group, an aryl group, an alkoxy group, an aryloxy group and an amino group (described later), and a halogen atom such as fluorine, chlorine and bromine. At least one of the substituents R ^{1 to} R ⁶ is preferably a fluorine atom. The alkyl group is preferably an alkyl group having 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms, more preferably 1 to 4 carbon atoms, and more preferably 6 to 12 carbon atoms, and still more preferably 6 carbon atoms. An optionally substituted aryl group having 1 to 8 carbon atoms, 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms, more preferably an alkoxy group having 1 to 4 carbon atoms, and 6 to 12 carbon atoms. And more preferably an aryloxy group having 6 to 8 carbon atoms which may be substituted, a specific nitrogen-containing group such as an amino group having 1 to 12 carbon atoms, fluorine and chlorine.
Among these, an alkyl group, an alkoxy group, a specific nitrogen-containing group, a fluorine atom, and a chlorine atom are preferable, and three or more fluorine atoms are more preferable.
A substituent consisting of an alkoxy group, a specific nitrogen-containing group and a fluorine atom is more preferred, and a substituent consisting of a specific nitrogen-containing group and a fluorine atom is still more preferred.

At least one of the substituents of R ^{1 to} R ⁶ is preferably —NR ^A R ^B , —N═R ^C , or an azide group, and at least one other is preferably a halogen atom. Among them, all of R ^{1 to} R ⁶ are a group selected from —NR ^A R ^B , —N═R ^C , and an azide group or a combination thereof (hereinafter, this may be referred to as “specific nitrogen-containing group”). , And preferably in combination with a halogen atom. As the halogen atom, fluorine is preferred. The number of the specific nitrogen-containing group is not particularly limited, but is preferably 1 to 4, more preferably 1 to 3, particularly preferably 1 to 2, and further preferably 1. . As a substitution position, it is preferable that one specific nitrogen-containing group is substituted on one phosphorus atom.

R ^{1 to} R ⁶ may be bonded to each other to form a ring containing a phosphorus atom. R ^{1 to} R ⁶ may be different from each other or the same. In particular, when forming a ring, it is preferable that R ¹ and R ² , R ³ and R ⁴ , R ⁵ and R ⁶ form a ring.

The substituents R ^{1 to} R ⁶ are preferably an alkyl group, an aryl group, an alkoxy group, an aryloxy group, a thioalkyl group, a thioaryl group, the specific nitrogen-containing group, and a halogen atom. Particularly preferably, an alkyl group having 1 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, a thioalkyl group having 1 to 6 carbon atoms, A thioaryl group having 6 to 12 carbon atoms, a halogen atom (preferably chlorine or fluorine), and the specific nitrogen-containing group, and particularly preferably the specific nitrogen-containing group, fluorine atom, alkyl group having 1 to 6 carbon atoms, or It is a C1-C6 alkoxy group. The alkyl group and aryl group may be substituted. The alkyl group may be linear or branched.

・ N
n represents an integer of 1 or more, preferably 1 to 3, more preferably 1 to 2, and still more preferably 1.

・ R ^A , R ^B
R ^A and R ^B are a hydrogen atom, an alkyl group, an aryl group, an alkenyl group, an alkynyl group, a heterocyclic group, a cyano group, a silyl group, or the following formula (1A), (1B), (1C), or (1D) It is a substituent represented by these.

Among R ^A and R ^B , an alkyl group, an aryl group, a substituent represented by formula (1A) or formula (1D) is preferable, and an alkyl group having 1 to 6 carbon atoms, particularly preferably 1 to 1 carbon atoms is preferable. A fluorine-substituted alkyl group having 6 carbon atoms, an alkyl group having an ether group having 1 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, and a substituent represented by the formula (1A) having 1 to 7 carbon atoms. More preferably, it is a C1-C4 alkyl group and a C1-C4 fluorine-substituted alkyl group, and among them, a substituent having a total carbon number of 6 or less. The total number of carbon atoms is particularly preferably 4 or less. R ^A and R ^B may be bonded to each other or condensed to form a ring containing a nitrogen atom. The alkyl group may be linear or branched. R ^A and R ^B may be the same as or different from each other.

・ R ^1A1 , R ^1C1 , R ^1D1 , R ^1D2
In the formula, R ^1A1 , R ^1C1 , R ^1D1 , and R ^{1D2 each} represents an alkyl group, an alkoxy group, an aryl group, an aryloxy group, a halogen atom, or an amino group. Preferred examples of these substituents include the following examples. That is, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an aryl group having 6 to 12 carbon atoms, an aryloxy group having 6 to 12 carbon atoms, chlorine, and fluorine are preferable, and 1 to 6 carbon atoms are preferable. More preferred are an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, chlorine and fluorine. These substituents may be further substituted. * Represents a bond.

・ R ^1B1 , R ^1B2
R ^1B1 and R ^1B2 represent a hydrogen atom, an alkyl group, an aryl group, an alkoxycarbonyl group, an aryloxycarbonyl group, an alkylsulfonyl group, an arylsulfonyl group, a silyl group, or a phosphonyl group. Preferred examples of these substituents include the following examples. That is, an alkyl group having 1 to 6 carbon atoms, an alkoxycarbonyl group having 1 to 7 carbon atoms, an aryl group having 6 to 12 carbon atoms, an aryloxycarbonyl group having 7 to 12 carbon atoms, and an alkylsulfonyl group having 1 to 6 carbon atoms An arylsulfonyl group having 6 to 12 carbon atoms, a silyl group having 1 to 6 carbon atoms, and a phosphonyl group having 1 to 12 carbon atoms, an alkyl group having 1 to 6 carbon atoms, an alkoxycarbonyl group having 1 to 7 carbon atoms, Particularly preferred are an alkylsulfonyl group having 1 to 6 carbon atoms, a silyl group having 1 to 6 carbon atoms, and a phosphonyl group having 1 to 12 carbon atoms.

・ X ^A1 , X ^D1 , R ^1D3
In the formula, X ^A1 represents an oxygen atom or a sulfur atom.
X ^D1 represents an oxygen atom, a sulfur atom, or a nitrogen atom. When X ^D1 is an oxygen atom or a sulfur atom, R ^1D3 is not a substituent. When X ^D1 is a nitrogen atom, R ^1D3 is an alkyl group (preferably having 1 to 8 carbon atoms), an aryl group (preferably having 6 to 12 carbon atoms), a silyl group (preferably having 1 to 21 carbon atoms), or a phosphonyl group. (Preferably having 1 to 18 carbon atoms).

・ Rc
Rc represents a substituent represented by any one of formulas (C1) to (C6).

R ^X1 , R ^X2 and R ^{X3 each} represents an alkyl group, an aryl group, an alkoxy group, an aryloxy group, an alkylthio group, an arylthio group, a heterocyclic group, a halogen atom, or a silyl group. Preferred are an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an alkylthio group having 1 to 6 carbon atoms, a chlorine atom, a fluorine atom, and a silyl group having 1 to 15 carbon atoms. R ^Y1 and R ^Y2 represent a halogen atom.
There is no particular limitation on the kind and number of substituents R ¹ to R ^6, from the viewpoint of ensuring flame retardance of maintaining the battery performance is two or more fluorine atoms of all substituents, remaining The substituent is the specific nitrogen-containing group and the alkoxy group, and more preferably, three or more of all the substituents are fluorine atoms. Most preferably, 4 or more are fluorine atoms. Alternatively, from the same viewpoint, it is preferable that all of R ^{1 to} R ⁶ are composed of a halogen atom (preferably a fluorine atom) and the specific nitrogen-containing group, and 1 to 3 of them are the specific nitrogen-containing groups. It is preferably a group, more preferably 1 or 2 of the specific nitrogen-containing group, and still more preferably when the specific nitrogen-containing group is 1.

  The compound represented by the above formula (3) is preferably a compound represented by the following formula (3A) or (3B).

・ R ^{21 to} R ^28
Wherein, R 21 ^{to R 28} have the same meanings as ^R 1 to R ⁶ in the formula (1). Among these, a halogen atom, an alkyl group, an aryl group, an alkoxy group, an aryloxy group, a thioalkyl group, a thioaryl group, and the specific nitrogen-containing group are preferable. Particularly preferably, the alkyl group having 1 to 6 carbon atoms, the aryl group having 6 to 12 carbon atoms, the alkoxy group having 1 to 6 carbon atoms, the aryloxy group having 6 to 12 carbon atoms, the alkylthio group having 1 to 6 carbon atoms, An arylthio group having 6 to 12 carbon atoms, a halogen atom (preferably chlorine or fluorine), and the specific nitrogen-containing group, and particularly preferably the specific nitrogen-containing group, fluorine atom, an alkyl group having 1 to 6 carbon atoms, or It is a C1-C6 alkoxy group. The alkyl group and aryl group may be substituted. The alkyl group may be linear or branched. At least one of R ^{21 to} R ²⁸ is the aforementioned —NR ^A R ^B , —N═R ^C , or an azide group or a combination thereof (specific nitrogen-containing group), and at least one other is a fluorine atom. As a more preferred form, the substituent is a compound comprising a specific nitrogen-containing group and a fluorine atom, and the number of the specific nitrogen-containing groups is 1 to 4, preferably 1 to 3, particularly preferably 1 to 2, and more preferably. 1 and when all other than the specific nitrogen-containing group are fluorine atoms.

-The specific nitrogen-containing group The preferred specific nitrogen-containing group, the number and substitution position thereof, the relationship with the halogen atom, the preferred range thereof, and the like are the same as those in the formula (3). Specifically, the type and number of substituents R ^{21 to} R ²⁸ are not particularly limited, but from the viewpoint of ensuring flame retardancy while maintaining battery performance, two or more of the substituents are fluorine atoms. And the remaining substituents are the specific nitrogen-containing group and the alkoxy group, and more preferably three or more of all substituents are fluorine atoms. Most preferably, when 4 or more are fluorine atoms. Furthermore, it is preferable when there are 5 fluorine atoms. Alternatively, from the same viewpoint, all of R ^{21 to} R ²⁸ are preferably composed of a halogen atom (preferably a fluorine atom) and the specific nitrogen-containing group, and 1 to 3 of them are the specific nitrogen-containing group. It is preferable that the number of the specific nitrogen-containing groups is 1 or 2, and it is more preferable that the number of the specific nitrogen-containing groups is 1.

  Specific examples of the compound represented by the general formula (3) are shown below, but the present invention is not construed as being limited thereto.

The compound represented by the above formula (3) can be synthesized by a conventional method, but for example, the method described in German Patent No. 213991 can be referred to.
Alternatively, the target product can be obtained by introducing the same amino group as the target product into hexachlorocyclotriphosphazene and then fluorinating with a fluorinating agent such as sodium fluorinated or potassium fluorinated. The amination of chlorocyclotriphosphazene and fluorocyclotriphosphazene in the above method can be used as an acid remover that produces the same amine as the target product, but the same amine, inorganic base and organic as the target product. It can be similarly synthesized by coexisting bases. The inorganic base is preferably an inorganic base composed of an anion and a metal cation. Particularly preferably, the anion is a hydroxide, a carbonate, a bicarbonate, a fluoride, and the metal cation is an alkali metal, A combination selected from alkaline earth metals is preferred. The metal cation is preferably selected from sodium, potassium, magnesium, and calcium. Preferable examples include hydroxides such as sodium hydroxide and potassium hydroxide, carbonates such as potassium carbonate, sodium carbonate and sodium hydrogen carbonate, fluorides such as sodium fluorinated and potassium fluorinated, and triethylamine as the organic base. Examples thereof include trialkylamines such as diisopropylethylamine, methylmorpholine and diazabicycloundecene, and aromatic bases such as pyridine and lutidine. The solvent used at the time of synthesis is a commonly used solvent and can be used without any problem, but preferably an ester solvent, an ether solvent, a nitrile solvent, and an aliphatic solvent. Specifically, ester solvents such as ethyl acetate and butyl acetate, ether solvents such as diethyl ether, tert-butyl methyl ether and cyclopentyl methyl ether, nitrile solvents such as acetonitrile, and aliphatic solvents such as hexane and decane. Etc. Among these, ether solvents and nitrile solvents are preferable.

  The content of the flame retardant in the electrolytic solution of the present invention is not particularly limited, but is preferably 0.01 to 5 mol / L, more preferably 0.02 to 1 mol / L, and 0.05 to 0.5 mol / L. Particularly preferred. By applying the flame retardant in such a range, the combined use effect (interaction) with the surfactant described later can be suitably obtained, and the compatibility between the flame retardant and the battery characteristics such as the rate characteristics is extremely high. Can be achieved.

[Surfactant]
In the present invention, the electrolytic solution contains a surfactant. This surfactant is preferably a compound represented by any of the following formulas (5A) to (5J).

・ R ^a
In the formula, R ^a represents an alkyl group (preferably having 1 to 24 carbon atoms) or an aryl group (preferably having 6 to 24 carbon atoms). The alkyl group and aryl group may be substituted with a fluorine atom or the like. In this case, a fluorine-containing alkyl group having 1 to 16 carbon atoms or a fluorine-containing aryl group having 6 to 24 carbon atoms is preferable. The alkyl group and aryl group may be further substituted, and examples of the substituent include the substituent T described below. As a substituent which an alkyl group and an aryl group have, a hydroxyl group, an alkoxy group (preferably 1 to 6 carbon atoms), an acyl group (preferably 1 to 6 carbon atoms), a carbamoyl group, an amino group (NR ₂ : R is A hydrogen atom or an alkyl group having 1 to 6 carbon atoms). When R ^a is an alkyl group, an ether group (—O—) may be interposed in the middle of the alkyl chain. When R ^a is an alkyl group, it may be linear or branched, or may form a ring to form a cyclic alkyl group. Even in the case of a cyclic structure, a hetero atom such as an ether group (—O—) may be present (eg, a cyclic structure group of sorbitan monoester). Incidentally, a plurality of R ^a in one molecule is meant to be different from each other.

・ R ^b
R ^b represents an alkyl group having a hydroxyl group (preferably having 1 to 24 carbon atoms) or an aryl group having a hydroxyl group (preferably having 6 to 24 carbon atoms). The alkyl group and aryl group may be substituted with a fluorine atom or the like. In this case, a fluorine-containing alkyl group having 1 to 16 carbon atoms or a fluorine-containing aryl group having 6 to 14 carbon atoms is preferable. The alkyl group and aryl group may be further substituted, and examples of the substituent include the substituent T described below. It should be noted that a plurality of R ^b in one molecule may be different from each other.

・ R ^c
R ^c is an alkyl group (preferably having 1 to 24 carbon atoms) having a group containing a carbanion, sulfoanion, or phosphoanion, or an aryl group having a group containing a carbanion, sulfoanion, or phosphoanion (preferably Represents 6 to 24 carbon atoms). The alkyl group and aryl group may be substituted with a fluorine atom or the like, and at this time, it is preferably a fluorine-containing alkyl group having 1 to 16 carbon atoms or a fluorine-containing aryl group having 6 to 14 carbon atoms. The alkyl group and aryl group may be further substituted, and examples of the substituent include the substituent T described below. It should be noted that a plurality of R ^c in one molecule may be different from each other.

When R ^{a to} R ^c are a fluorine atom-substituted alkyl group or an aryl group, a perfluorinated alkyl group or aryl group is particularly preferable.

・ M
M represents an alkali metal or an alkaline earth metal. However, in the case of an alkaline earth metal, it becomes a divalent metal salt, so M ⁺ is replaced with 1 / 2M ²⁺ . Examples of such metal salts include sodium salts, potassium salts, lithium metal alkali metal salts, beryllium salts, magnesium salts, and alkaline earth metal salts calcium salts, more preferably magnesium salts, sodium salts, Potassium salt and lithium salt are preferable, and lithium salt is particularly preferable. A plurality of M in one molecule may be different from each other.

・ X
X may be any anion, but preferred examples include carboxylate anions such as formate anion and acetate anions, and halide ions such as fluoride, chlorinated compounds, bromides, and iodides. Particularly preferred are fluoride, chlorinated compound and bromide.

・ N
n is an integer of 1-20.

  The formula (5J) is preferably represented by the following (5J-1).

In the formula, Ra and X are as defined in the above formula (5J). x and y each represents an integer of 2 to 10.

In the formulas (5A), (5B), (5C), (5D), (5E), and (5F), R ^a preferably has an alkyl group (preferably having 6 to 30 carbon atoms) and a polyoxyethylene group. Alkyl group (preferably 6-30 carbon atoms), perfluoroalkyl group (preferably 1-20 carbon atoms), aryl group (preferably 6-30 carbon atoms), aryl group having polyoxyethylene group (preferably carbon And a perfluoroaryl group (preferably having a carbon number of 6 to 18), particularly preferably an alkyl group, an alkyl group having a polyoxyethylene group, or a perfluoroalkyl group.

In the formula (5E) (5F), R ^b is preferably an alkyl group having 1 to 10 hydroxyl groups (preferably having 1 to 30 carbon atoms), and an aryl group having 1 to 10 hydroxyl groups (preferably having 6 carbon atoms). To 30), more preferably an alkyl group having 1 to 5 hydroxyl groups (preferably having 1 to 20 carbon atoms).

In the formula (5G), R ^a is preferably an alkyl group (preferably having 4 to 15 carbon atoms), an alkyl group having a polyoxyethylene group (preferably having 6 to 20 carbon atoms), or a perfluoroalkyl group (preferably carbon). 1-15), an aryl group (preferably 6-25 carbon atoms), an aryl group having a polyoxyethylene group (preferably 8-30 carbon atoms), a perfluoroaryl group (preferably 6-18 carbon atoms). More preferably, 1 or 2 of R ^a is a short-chain alkyl group such as a methyl group or an ethyl group. R ^c is preferably a carbanion, a sulfoanion or a phosphoanion, particularly preferably a carbanion.

  The formula (5H) is preferably represented by the following (5H-1).

  x represents an integer of 1 to 20. Ra has the same meaning as (5H) above.

In the formula (5I), R ^a is preferably a hydrogen atom, an alkyl group, an alkyl group having a polyoxyethylene group, a perfluoroalkyl group, an aryl group, an aryl group having a polyoxyethylene group, or a perfluoroaryl group. Particularly preferred is when it consists of a hydrogen atom, an alkyl group or an aryl group.

  The surfactant is an anionic activator comprising a sulfate ester, sulfonate ester or phosphate ester, a cation activator comprising an aliphatic amine salt or a quaternary ammonium salt, or oxyethylene ether, ester ether, or polyvalent Nonionic activators consisting of alcohol esters are preferred. At this time, the metal that forms the salt is preferably the same as those mentioned for M above.

  More specifically, anionic activators include aliphatic monocarboxylates, polyoxyethylene alkyl ether carboxylates, N acylalkyl salts, alpha sulfo fatty acid ester salts, dialkyl sulfonates, alkyl sulfonates. , Alkyl benzene sulfonate, alkyl naphthalene sulfonate, N methyl N acyl taurate, alkyl sulfate, polyoxyethylene alkyl ether sulfate, oil sulfate, alkyl phosphate, polyoxyethylene alkyl ether phosphate, poly Examples thereof include oxyethylene alkylphenyl phosphate.

  Cationic activators include monoalkylamine salts, dialkylamine salts, trialkylamine salts, halogenated (iodinated, chlorinated, brominated, fluorinated) alkyltrimethylammonium, halogenated (iodinated, chlorinated, brominated) And dialkyldimethylammonium fluoride).

Nonionic activators include glycerin fatty acid ester, sucrose fatty acid ester, polyoxyethylene alkyl ether, polyoxyethylene alkylphenyl ether, polyoxyethylene polyoxypropylene glycol, fatty acid polyethylene glycol and the like.
Examples of amphoteric surfactants include alkyl betaines, alkyl diethylene triamino carboxylic acids, and alkyl amine oxides.
The surfactant used in the present invention is a surfactant represented by any one of the above formulas (5A) to (5I) or (5J-1), and ^Ra is a hydrogen atom, a straight chain, A branched or cyclic alkyl group or an aryl group, and R ^b is an alkyl group having a hydroxyl group or an aryl group having a hydroxyl group. Here, these alkyl groups and aryl groups may have a substituent, and these alkyl groups may have —O— in the middle of a linear, branched or cyclic alkyl chain. However, carbon number of ^Rb in Formula (5E) is 6-30. R ^c is an alkyl group having a group containing a carbanion, sulfoanion or phosphoanion, or an aryl group having a group containing a carbanion, sulfoanion or phosphoanion. M is an alkali metal or alkaline earth metal. However, in the case of an alkaline earth metal, since it becomes a divalent metal salt, M ⁺ is replaced with 1 / 2M ²⁺ . X is an anion. n is an integer of 1 to 20, and x and y are integers of 2 to 10.

In this invention, the compounding quantity of surfactant is important and the said surfactant is contained by 0.1 mass part or more with respect to 100 mass parts of said flame retardants .
The surfactant is more preferably contained in an amount of 0.5 parts by mass or more, particularly preferably 1 part by mass or more, relative to 100 parts by mass of the flame retardant . The upper limit value is not especially preferably contained under 10 parts by mass or less, more preferably it is contained in the following 7 parts by mass, and particularly preferably contained 5 parts by mass or less.
However, in this invention, an upper limit is 10 mass parts or less.
By blending a surfactant in such a range, a good combined effect (interaction) with the flame retardant can be obtained, and both high flame retardancy and high rate characteristics can be effectively achieved. Can do.

[Aprotic solvent]
The nonaqueous electrolytic solution of the present invention contains an aprotic solvent, and the aprotic solvent contains a compound represented by the following formula (4A), (4B), or (4C) or a combination thereof. Is preferred.

・ R ^{31 to} R ³⁶
In the formula, each of R ^{31 to} R ³⁶ represents a hydrogen atom, an alkyl group that may be substituted with fluorine, an alkyl group having an ether chain, or an aryl group that may be substituted with fluorine. Preferable examples of the alkyl group and aryl group include the following examples. That is, among them, linear and branched alkyl groups, alkyl groups having a fluorine atom, and alkyl groups having an ether chain are preferable. Particularly preferred are alkyl groups having 1 to 6 carbon atoms, alkyl groups partially substituted with fluorine having 1 to 6 carbon atoms, and alkyl groups having an ether group having 1 to 6 carbon atoms. As described above, adjacent substituents may form a ring. In particular, substituents R ³¹ and R ³² , R ³³ and R ³⁴ in formula (4B) form a ring. Also good. Further, the substituents R ³¹ and R ³² , R ³³ and R ³⁴ , R ³⁵ and R ³⁶ in the formula (4C) may form a ring.

When the aprotic solvent contains a compound represented by the formula (4A) and a compound selected from the group consisting of a compound represented by the formula (4B) and a compound represented by (4C), Ratio (M _4B /) between the volume (M _4B ) of the compound represented by the formula ( _4B ) and the total volume (M _AC ) of the compound represented by the formula (4A) and the compound represented by the formula (4C). M _AC ) is preferably 0.2 to 5, and more preferably 0.3 to 1. By setting this ratio to be equal to or less than the above upper limit value, it is possible to maintain a favorable battery characteristic without preventing a significant increase in viscosity and excessively reducing lithium ion conductivity with a sufficient dielectric constant. On the other hand, by setting it to the lower limit value or more, good battery characteristics can be realized without excessively reducing the dielectric constant.

In addition, in this specification, it uses for the meaning containing the salt and its ion besides the said compound itself about the display of a compound. Moreover, it is the meaning including the derivative | guide_body which changed the predetermined part in the range with the desired effect.
In the present specification, a substituent that does not specify substitution / non-substitution (the same applies to a linking group) means that the group may have an arbitrary substituent. This is also synonymous for compounds that do not specify substitution / non-substitution. Preferred substituents include the following substituent T.

Examples of the substituent T include the following.
An alkyl group (preferably an alkyl group having 1 to 20 carbon atoms, such as methyl, ethyl, isopropyl, t-butyl, pentyl, heptyl, 1-ethylpentyl, benzyl, 2-ethoxyethyl, 1-carboxymethyl, etc.), alkenyl A group (preferably an alkenyl group having 2 to 20 carbon atoms, such as vinyl, allyl, oleyl, etc.), an alkynyl group (preferably an alkynyl group having 2 to 20 carbon atoms, such as ethynyl, butadiynyl, phenylethynyl, etc.), A cycloalkyl group (preferably a cycloalkyl group having 3 to 20 carbon atoms, such as cyclopropyl, cyclopentyl, cyclohexyl, 4-methylcyclohexyl, etc.), an aryl group (preferably an aryl group having 6 to 26 carbon atoms, for example, Phenyl, 1-naphthyl, 4-methoxyphenyl, -Chlorophenyl, 3-methylphenyl, etc.), a heterocyclic group (preferably a heterocyclic group having 2 to 20 carbon atoms, preferably a 5- or 6-membered heterocycle having at least one oxygen atom, sulfur atom, nitrogen atom) A cyclic group is preferable, for example, 2-pyridyl, 4-pyridyl, 2-imidazolyl, 2-benzimidazolyl, 2-thiazolyl, 2-oxazolyl, etc., an alkoxy group (preferably an alkoxy group having 1 to 20 carbon atoms, for example, Methoxy, ethoxy, isopropyloxy, benzyloxy, etc.), aryloxy groups (preferably aryloxy groups having 6 to 26 carbon atoms, such as phenoxy, 1-naphthyloxy, 3-methylphenoxy, 4-methoxyphenoxy, etc.), An alkoxycarbonyl group (preferably an alkoxycarbonyl having 2 to 20 carbon atoms) Nyl groups such as ethoxycarbonyl, 2-ethylhexyloxycarbonyl, etc., amino groups (preferably including amino groups having 0 to 20 carbon atoms, alkylamino groups, arylamino groups, such as amino, N, N-dimethyl Amino, N, N-diethylamino, N-ethylamino, anilino, etc.), sulfamoyl groups (preferably sulfonamido groups having 0 to 20 carbon atoms, such as N, N-dimethylsulfamoyl, N-phenylsulfamoyl) Etc.), an acyl group (preferably an acyl group having 1 to 20 carbon atoms, such as acetyl, propionyl, butyryl, benzoyl, etc.), an acyloxy group (preferably an acyloxy group having 1 to 20 carbon atoms, such as acetyloxy, Benzoyloxy, etc.), carbamoyl groups (preferably C 1-20 carbon atoms) Rubamoyl groups such as N, N-dimethylcarbamoyl and N-phenylcarbamoyl), acylamino groups (preferably having 1 to 20 carbon atoms, such as acetylamino and benzoylamino), sulfonamido groups (preferably Is a sulfamoyl group having 0 to 20 carbon atoms, such as methanesulfonamide, benzenesulfonamide, N-methylmethanesulfonamide, N-ethylbenzenesulfonamide, etc., an alkylthio group (preferably an alkylthio having 1 to 20 carbon atoms). Groups such as methylthio, ethylthio, isopropylthio, benzylthio, etc., arylthio groups (preferably arylthio groups having 6 to 26 carbon atoms, such as phenylthio, 1-naphthylthio, 3-methylphenylthio, 4-methoxyphenylthio ), An alkyl or arylsulfonyl group (preferably an alkyl or arylsulfonyl group having 1 to 20 carbon atoms, such as methylsulfonyl, ethylsulfonyl, benzenesulfonyl, etc.), a hydroxyl group, a cyano group, a halogen atom (for example, a fluorine atom, chlorine) Atoms, bromine atoms, iodine atoms, etc.), more preferably alkyl groups, alkenyl groups, aryl groups, heterocyclic groups, alkoxy groups, aryloxy groups, alkoxycarbonyl groups, amino groups, acylamino groups, hydroxyl groups or halogen atoms. And particularly preferably an alkyl group, an alkenyl group, a heterocyclic group, an alkoxy group, an alkoxycarbonyl group, an amino group, an acylamino group or a hydroxyl group.
In addition, each of the groups listed as the substituent T may be further substituted with the substituent T described above.

  When the compound or substituent / linking group contains an alkyl group / alkylene group, alkenyl group / alkenylene group, etc., these may be cyclic or chain-like, and may be linear or branched, and substituted as described above. It may be substituted or unsubstituted. Moreover, when an aryl group, a heterocyclic group, etc. are included, they may be monocyclic or condensed and may be similarly substituted or unsubstituted.

(Electrolytes)
Examples of the electrolyte that can be used in the electrolytic solution of the present invention include metal ions or salts thereof, and metal ions or salts thereof belonging to Group 1 or Group 2 of the periodic table are preferred. Specifically, it is appropriately selected depending on the purpose of use of the electrolytic solution, and examples thereof include lithium salt, potassium salt, sodium salt, calcium salt, magnesium salt and the like. Of these, lithium salts are preferred from the viewpoint of output. When the electrolytic solution of the present invention is used as an electrolyte of a non-aqueous electrolytic solution for a lithium secondary battery, a lithium salt may be selected as a metal ion salt. The lithium salt is not particularly limited as long as it is a lithium salt usually used for an electrolyte of a non-aqueous electrolyte solution for a lithium secondary battery. For example, those described below are preferable.

(L-1) Inorganic lithium salts: inorganic fluoride salts such as LiPF ₆ , LiBF ₄ , LiAsF ₆ , LiSbF ₆ ; perhalogenates such as LiClO ₄ , LiBrO ₄ , LiIO ₄ ; inorganic chloride salts such as LiAlCl ₄ etc.

(L-2) Fluorine-containing organic lithium salt: Perfluoroalkane sulfonate such as LiCF ₃ SO ₃ ; LiN (CF ₃ SO ₂ ) ₂ , LiN (CF ₃ CF ₂ SO ₂ ) ₂ , LiN (FSO ₂ ) ₂ , Perfluoroalkanesulfonylimide salts such as LiN (CF ₃ SO ₂ ) (C ₄ F ₉ SO ₂ ); perfluoroalkanesulfonylmethide salts such as LiC (CF ₃ SO ₂ ) ₃ ; Li [PF ₅ (CF ₂ CF ₂ CF ₃ )], Li [PF ₄ (CF ₂ CF ₂ CF ₃ ) ₂ ], Li [PF ₃ (CF ₂ CF ₂ CF ₃ ) ₃ ], Li [PF ₅ (CF ₂ CF ₂ CF ₂ CF _{3 )], Li [PF 4 (} CF 2 CF 2 CF 2 CF 3) 2], Li [PF 3 (CF 2 CF 2 CF 2 CF 3) 3] fluoroalkyl fluoride such as potash Acid salts, and the like.

  (L-3) Oxalatoborate salt: lithium bis (oxalato) borate, lithium difluorooxalatoborate and the like.

Among these, LiPF ₆ , LiBF ₄ , LiAsF ₆ , LiSbF ₆ , LiClO ₄ , Li (Rf ¹ SO ₃ ), LiN (Rf ¹ SO ₂ ) ₂ , LiN (FSO ₂ ) ₂ , and LiN (Rf ¹ SO ₂ ) (Rf ² SO ₂ ) ₂ is preferred, such as LiPF ₆ , LiBF ₄ , LiN (Rf ¹ SO ₂ ) ₂ , LiN (FSO ₂ ) ₂ , and LiN (Rf ¹ SO ₂ ) (Rf ² SO ₂ ) ₂ The lithium imide salt is more preferable. Here, Rf ¹ and Rf ² each represent a perfluoroalkyl group.

  In addition, the lithium salt used for electrolyte solution may be used individually by 1 type, or may combine 2 or more types arbitrarily.

  The content of the electrolyte (preferably a metal ion belonging to Group 1 or Group 2 of the periodic table or a metal salt thereof) in the electrolytic solution is added in an amount so as to be a preferable concentration described in the electrolytic solution preparation method below. The This concentration is appropriately selected depending on the purpose of use of the electrolytic solution, but is generally 10% by mass or more and 50% by mass or less, more preferably 15% by mass or more and 30% by mass or less, based on the total mass of the electrolytic solution. In addition, when evaluating as an ion density | concentration, what is necessary is just to calculate by salt conversion with the metal applied suitably.

(Other ingredients)
The electrolytic solution of the present invention may contain at least one selected from a negative electrode film forming agent, a flame retardant, and an overcharge inhibitor. Although the content rate of these functional additives in a non-aqueous electrolyte solution does not have limitation in particular, 0.001 mass%-10 mass% are preferable with respect to the whole non-aqueous electrolyte solution, respectively.

[Method for preparing electrolytic solution]
The non-aqueous electrolyte solution is prepared by a conventional method by dissolving the above components in the non-aqueous electrolyte solvent, including an example in which a lithium salt is used as a metal ion salt.

  In the present invention, “non-water” means that water is not substantially contained, and a trace amount of water may be contained as long as the effects of the invention are not hindered. In view of obtaining good characteristics, the water content is preferably 200 ppm (mass basis) or less, and more preferably 100 ppm or less. Although there is no particular lower limit, it is practical that it is 10 ppm or more considering inevitable mixing. The viscosity of the electrolytic solution of the present invention is not particularly limited, but is preferably 10 to 0.1 mPa · s, more preferably 5 to 0.5 mPa · s at 25 ° C.

(kit)
The electrolytic solution of the present invention may be a kit composed of a plurality of liquids or powders. For example, the first agent (first liquid) is composed of an electrolyte and an organic solvent, and the second agent (second liquid) is composed of a flame retardant or a surfactant and an organic solvent. The form which mixes and mixes may be sufficient. At this time, in the kit of the present invention, the flame retardant and the surfactant are classified as separate agents, or other additives are classified as the first agent, the second agent, and / or other agents ( It may be contained in the third agent).

[Secondary battery]
In this invention, it is preferable to set it as the nonaqueous electrolyte secondary battery containing the said nonaqueous electrolyte. As a preferred embodiment, a lithium secondary battery will be described with reference to FIG. 1 schematically showing the mechanism. However, the present invention is not construed as being limited by the same figure and the explanation based thereon.

  The lithium secondary battery 10 of the present embodiment includes the non-aqueous electrolyte 5 of the present invention, a positive electrode C (positive electrode current collector 1, positive electrode active material layer 2) capable of inserting and releasing lithium ions, A negative electrode A (negative electrode current collector 3, negative electrode active material layer 4) capable of insertion / release or dissolution / precipitation. In addition to these essential members, considering the purpose of use of the battery, the shape of the potential, etc., a separator 9 disposed between the positive electrode and the negative electrode, a current collecting terminal (not shown), an outer case, etc. (Not shown). If necessary, a protective element may be attached to at least one of the inside of the battery and the outside of the battery. With this structure, lithium ions are transferred a and b in the electrolyte 5, charging α and discharging β can be performed, and the operating mechanism 6 is operated or stored via the circuit wiring 7. be able to.

(Battery shape)
The battery shape to which the lithium secondary battery of the present embodiment is applied is not particularly limited, and examples thereof include a bottomed cylindrical shape, a bottomed square shape, a thin shape, a sheet shape, and a paper shape. Any of these may be used. Further, it may be of a different shape such as a horseshoe shape or a comb shape considering the shape of the system or device to be incorporated. Among them, from the viewpoint of efficiently releasing the heat inside the battery to the outside, a square shape such as a bottomed square shape or a thin shape having at least one surface that is relatively flat and has a large area is preferable.

  In a battery having a bottomed cylindrical shape, since the outer surface area with respect to the power generating element to be filled becomes small, it is preferable to design so that Joule heat generated by the internal resistance at the time of charging and discharging efficiently escapes to the outside. Moreover, it is preferable to design so that the filling ratio of the substance having high thermal conductivity is increased and the temperature distribution inside is reduced. The bottomed cylindrical secondary battery will be described later with reference to FIG.

(Members constituting the battery)
The lithium secondary battery of the present embodiment is configured to include an electrolytic solution 5, positive and negative electrode composites C and A, and a separator basic member 9, based on FIG. 1. Hereinafter, each of these members will be described.

(Electrode mixture)
The electrode mixture is formed by applying a dispersion such as an active material, a conductive agent, a binder, and a filler on a current collector (electrode base material) and forming it into a sheet shape. In a lithium battery, a positive electrode mixture whose active material is a positive electrode active material and a negative electrode mixture whose active material is a negative electrode active material are usually used. Next, each component in the dispersion (mixture, electrode composition) constituting the electrode mixture will be described.
-Positive electrode active material In this invention, it is preferable to use the material which has a 4.25V or more charge area | region for a positive electrode active material. Specifically, a lithium-containing transition metal oxide having a lithium insertion / release potential peak at 4.25 V or more with respect to lithium is preferable. The charge / discharge potential peak at this time can be specified by preparing a thin film electrode of a positive electrode active material by a sol-gel method or a sputtering method and performing electrochemical measurement (cyclic voltammetry).

The following are mentioned as a positive electrode active material which has the said specific charge area | region.
(I) LiNi _x Mn _y Co _z O ₂ (x> 0.2, y> 0.2, z ≧ 0, x + y + z = 1),
Representative:
LiNi _1/3 Mn _1/3 Co _1/3 O ₂ (also described as LiNi _0.33 Mn _0.33 Co _0.33 O ₂ )
LiNi _1/2 Mn _1/2 O ₂ (also described as LiNi _0.5 Mn _0.5 Co _0.33 O ₂ )
(Ii) LiNi _x Mn _y O ₄ (x> 0.2, y> 0.7, x + y = 1)
Representative:
LiNi _1/4 Mn _3/4 O ₂ (also described as LiNi _0.5 Mn _1.5 O ₄ )
(Iii) LiNi _x Co _y Al _z O ₂ (x> 0.7, y> 0.1, 0.1>z> 0.05, x + y + z = 1)
Representative:
LiNi _0.8 Co _0.15 Al _0.05 O ₂

The following can be used as the positive electrode active material having the specific charging region.
(A) LiCoMnO ₄
(B) Li ₂ FeMn ₃ O ₈
(C) Li ₂ CuMn ₃ O ₈
(D) Li ₂ CrMn ₃ O ₈
(E) Li ₂ NiMn ₃ O ₈

  The phosphazene compound is a compound with relatively strong oxidation and reduction resistance, but it is considered that decomposition proceeds more during charge and discharge at a high potential with a high potential positive electrode containing manganese and nickel. When the surfactant of the present invention is used, a stable film is formed by the interaction of the polar groups in the surfactant with the phosphazene compound effectively on the highly active manganese and nickel sites, and excessive decomposition. It is thought that it is suppressing. It is presumed that the battery characteristics such as rate characteristics are improved by this effect.

In the non-aqueous electrolyte secondary battery of the present invention, a particulate positive electrode active material may be used. The average particle size of the positive electrode active material used is not particularly limited, but is preferably 0.1 μm to 50 μm. No particular limitation is imposed on the specific surface area, preferably from 0.01m ² / g~50m ² / g by the BET method. Further, the pH of the supernatant when 5 g of the positive electrode active material is dissolved in 100 ml of distilled water is preferably 7 or more and 12 or less.

  A pulverizer or a classifier commonly used to make the positive electrode active substance have a predetermined particle size can be used. For example, a mortar, a ball mill, a vibration ball mill, a vibration mill, a satellite ball mill, a planetary ball mill, a swirling air flow type jet mill, a sieve, or the like is used. The positive electrode active material obtained by the firing method may be used after being washed with water, an acidic aqueous solution, an alkaline aqueous solution, or an organic solvent.

  Although the compounding quantity of a positive electrode active material is not specifically limited, It is preferable that it is 60-98 mass% in the solid component 100 mass% in the dispersion (mixture) which makes an electrode compound material. More preferably, it is 70-95 mass%.

・ Negative electrode active material The negative electrode active material is not particularly limited as long as it can reversibly insert and release lithium ions. Carbonaceous materials, metal oxides such as tin oxide and silicon oxide, metal composite oxides, Examples thereof include lithium alloys such as lithium alone and lithium aluminum alloys, and metals capable of forming an alloy with lithium such as Sn and Si.

  These may be used individually by 1 type, or may use 2 or more types together by arbitrary combinations and a ratio. Of these, carbonaceous materials or lithium composite oxides are preferably used from the viewpoint of safety.

  Further, the metal composite oxide is not particularly limited as long as it can occlude and release lithium, but it preferably contains titanium and / or lithium as a constituent component from the viewpoint of high current density charge / discharge characteristics. .

  The carbonaceous material used as the negative electrode active material is a material substantially made of carbon. Examples thereof include carbonaceous materials obtained by baking various synthetic resins such as artificial pitches such as petroleum pitch, natural graphite, and vapor-grown graphite, and PAN-based resins and furfuryl alcohol resins. Furthermore, various carbon fibers such as PAN-based carbon fiber, cellulose-based carbon fiber, pitch-based carbon fiber, vapor-grown carbon fiber, dehydrated PVA-based carbon fiber, lignin carbon fiber, glassy carbon fiber, activated carbon fiber, mesophase micro Examples thereof include spheres, graphite whiskers, and flat graphite.

  These carbonaceous materials can be divided into non-graphitizable carbon materials and graphite-based carbon materials depending on the degree of graphitization. Further, the carbonaceous material preferably has the surface spacing, density, and crystallite size described in JP-A-62-222066, JP-A-2-6856, and 3-45473. The carbonaceous material does not need to be a single material, and a mixture of natural graphite and artificial graphite described in JP-A-5-90844, graphite having a coating layer described in JP-A-6-4516, or the like is used. You can also.

  The metal oxide and metal composite oxide, which are negative electrode active materials used in the nonaqueous electrolyte secondary battery, need only contain at least one of them. As the metal oxide and metal complex oxide, amorphous oxide is particularly preferable, and chalcogenite, which is a reaction product of a metal element and an element of Group 16 of the periodic table, is also preferably used. The term “amorphous” as used herein means an X-ray diffraction method using CuKα rays, which has a broad scattering band having an apex in the region of 20 ° to 40 ° in terms of 2θ values, and is a crystalline diffraction line. You may have. The strongest intensity of crystalline diffraction lines seen from 2 ° to 40 ° to 70 ° is 100 times the diffraction line intensity at the peak of the broad scattering band seen from 2 ° to 20 °. It is preferable that it is 5 times or less, and it is particularly preferable not to have a crystalline diffraction line.

Among the compound group consisting of the amorphous oxide and the chalcogenide, an amorphous oxide of a metalloid element and a chalcogenide are more preferable, and elements of Groups 13 (IIIB) to 15 (VB) of the periodic table, Particularly preferred are oxides and chalcogenides composed of one kind of Al, Ga, Si, Sn, Ge, Pb, Sb, Bi or a combination of two or more kinds thereof. Specific examples of preferable amorphous oxides and chalcogenides include, for example, Ga ₂ O ₃ , SiO, GeO, SnO, SnO ₂ , PbO, PbO ₂ , Pb ₂ O ₃ , Pb ₂ O ₄ , Pb ₃ O ₄ , Sb ₂ O ₃ , Sb ₂ O ₄ , Sb ₂ O ₅ , Bi ₂ O ₃ , Bi ₂ O ₄ , SnSiO ₃ , GeS, SnS, SnS ₂ , PbS, PbS ₂ , Sb ₂ S ₃ , Sb ₂ S ₅ , such as SnSiS ₃ may preferably be mentioned. Moreover, these may be a complex oxide with lithium oxide, for example, Li ₂ SnO ₂ .

  In the non-aqueous electrolyte secondary battery, the average particle size of the negative electrode active material used is preferably 0.1 μm to 60 μm. To obtain a predetermined particle size, a well-known pulverizer or classifier is used. For example, a mortar, a ball mill, a sand mill, a vibrating ball mill, a satellite ball mill, a planetary ball mill, a swirling air flow type jet mill or a sieve is preferably used. When pulverizing, wet pulverization in the presence of water or an organic solvent such as methanol can be performed as necessary. In order to obtain a desired particle size, classification is preferably performed. The classification method is not particularly limited, and a sieve, an air classifier, or the like can be used as necessary. Classification can be used both dry and wet.

  The chemical formula of the compound obtained by the firing method can be calculated from an inductively coupled plasma (ICP) emission spectroscopic analysis method as a measurement method and a mass difference between powders before and after firing as a simple method.

  Examples of the negative electrode active material that can be used in combination with the amorphous oxide negative electrode active material centering on Sn, Si, and Ge include carbon materials that can occlude and release lithium ions or lithium metal, lithium, lithium alloys, lithium A metal that can be alloyed with is preferable.

In the present invention, it is also preferable to use lithium titanate, more specifically, lithium-titanium oxide (Li [Li _1/3 Ti _5/3 ] O ₄ ) as the negative electrode active material.

  Although the compounding quantity of a negative electrode active material is not specifically limited in the dispersion (mixture) which comprises an electrode compound material, It is preferable that it is 60-98 mass% in 100 mass% of solid components, and it is 70-95 mass%. Is more preferable.

-Conductive material As long as the conductive material is an electron conductive material that does not cause a chemical change in the configured secondary battery, any known conductive material may be used. Usually, natural graphite (scale-like graphite, scale-like graphite, earth-like graphite, etc.), artificial graphite, carbon black, acetylene black, ketjen black, carbon fiber and metal powder (copper, nickel, aluminum, silver (Japanese Patent Laid-Open No. Sho 63- 10148,554)), metal fibers or polyphenylene derivatives (described in JP-A-59-20971) can be contained as a single type or a mixture thereof. Among these, the combined use of graphite and acetylene black is particularly preferable. The addition amount of the conductive agent is preferably 0.1 to 50% by mass, more preferably 0.5 to 30% by mass in 100% by mass of the solid component in the dispersion (mixture) forming the electrode mixture. In the case of carbon or graphite, 0.5 to 15% by mass is particularly preferable in the dispersion.

-Binder Examples of the binder include polysaccharides, thermoplastic resins, and polymers having rubber elasticity. Among them, for example, starch, carboxymethyl cellulose, cellulose, diacetyl cellulose, methyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, sodium alginate, polyacrylic acid, sodium polyacrylate, polyvinyl phenol, polyvinyl methyl ether, polyvinyl alcohol, polyvinyl pyrrolidone, poly Water-soluble polymers such as acrylonitrile, polyacrylamide, polyhydroxy (meth) acrylate, styrene-maleic acid copolymer, polyvinyl chloride, polytetrafluoroethylene, polyvinylidene fluoride, tetrafluoroethylene-hexafluoropropylene copolymer, vinylidene furo Ride-tetrafluoroethylene-hexafluoropropylene copolymer, polyethylene, polyethylene (Meth) acrylic acid ester copolymers containing (meth) acrylic acid esters such as propylene, ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, polyvinyl acetal resin, methyl methacrylate, 2-ethylhexyl acrylate, (Meth) acrylic acid ester-acrylonitrile copolymer, polyvinyl ester copolymer containing vinyl ester such as vinyl acetate, styrene-butadiene copolymer, acrylonitrile-butadiene copolymer, polybutadiene, neoprene rubber, fluororubber, poly Emulsions of ethylene oxide, polyester polyurethane resin, polyether polyurethane resin, polycarbonate polyurethane resin, polyester resin, phenol resin, epoxy resin, etc. Box) or suspension is preferred, latex polyacrylate, carboxymethyl cellulose, polytetrafluoroethylene, polyvinylidene fluoride is more preferable.

  A binder can be used individually by 1 type or in mixture of 2 or more types. When the amount of the binder added is small, the holding power and cohesive force of the electrode mixture are weakened. If the amount is too large, the electrode volume increases and the capacity per electrode unit volume or unit mass decreases. For this reason, the amount of the binder added is preferably 1 to 30% by mass and more preferably 2 to 10% by mass in 100% by mass of the solid component in the dispersion (mixture) forming the electrode mixture.

-Filler The electrode compound material may contain the filler. As the material for forming the filler, any fibrous material that does not cause a chemical change in the secondary battery of the present invention can be used. Usually, fibrous fillers made of materials such as olefin polymers such as polypropylene and polyethylene, glass, and carbon are used. Although the addition amount of a filler is not specifically limited, 0-30 mass% is preferable in the solid component 100 mass% in the dispersion (mixture) which makes an electrode compound material.

-Current collector As the positive / negative current collector, an electron conductor that does not cause a chemical change in the non-aqueous electrolyte secondary battery of the present invention is used. As the current collector of the positive electrode, in addition to aluminum, stainless steel, nickel, titanium, etc., the surface of aluminum or stainless steel is preferably treated with carbon, nickel, titanium, or silver. Among them, aluminum and aluminum alloys are preferable. More preferred.

  As the negative electrode current collector, aluminum, copper, stainless steel, nickel, and titanium are preferable, and aluminum, copper, and a copper alloy are more preferable.

  As the shape of the current collector, a film sheet shape is usually used, but a net, a punched material, a lath body, a porous body, a foamed body, a molded body of a fiber group, and the like can also be used. The thickness of the current collector is not particularly limited, but is preferably 1 μm to 500 μm. Moreover, it is also preferable that the current collector surface is roughened by surface treatment.

  An electrode mixture of the lithium secondary battery is formed by a member appropriately selected from these materials.

(Separator)
The separator that can be used in the present invention is particularly limited as long as it is a material that mechanically insulates the positive electrode and the negative electrode, has ion permeability, and is resistant to oxidation / reduction at the contact surface between the positive electrode and the negative electrode. There is no. As such a material, a porous polymer material, an inorganic material, an organic-inorganic hybrid material, glass fiber, or the like is used. These separators preferably have a shutdown function for ensuring safety, that is, a function of closing the gap at 80 ° C. or higher to increase resistance and interrupting current, and the closing temperature is 90 ° C. or higher and 180 ° C. or lower. Preferably there is.

  The shape of the hole of the separator is usually circular or elliptical, and the size is 0.05 μm to 30 μm, preferably 0.1 μm to 20 μm. Furthermore, it may be a rod-like or irregular-shaped hole as in the case of making by a stretching method or a phase separation method. The ratio of these gaps, that is, the porosity, is 20% to 90%, preferably 35% to 80%.

  The polymer material may be a single material such as cellulose nonwoven fabric, polyethylene, or polypropylene, or may be a composite material of two or more types. What laminated | stacked the 2 or more types of microporous film which changed the hole diameter, the porosity, the obstruction | occlusion temperature of a hole, etc. is preferable.

  As the inorganic substance, oxides such as alumina and silicon dioxide, nitrides such as aluminum nitride and silicon nitride, and sulfates such as barium sulfate and calcium sulfate are used, and those having a particle shape or fiber shape are used. As the form, a thin film shape such as a non-woven fabric, a woven fabric, or a microporous film is used. In the thin film shape, those having a pore diameter of 0.01 μm to 1 μm and a thickness of 5 μm to 50 μm are preferably used. In addition to the independent thin film shape, a separator formed by forming a composite porous layer containing the inorganic particles on the surface layer of the positive electrode and / or the negative electrode using a resin binder can be used. For example, alumina particles having a 90% particle diameter of less than 1 μm are formed on both surfaces of the positive electrode as a porous layer using a fluororesin binder.

(Preparation of non-aqueous electrolyte secondary battery)
As described above, the lithium secondary battery can be applied to any shape such as a sheet shape, a square shape, and a cylinder shape. The (dispersion) mixture containing the positive electrode active material and the negative electrode active material is mainly used after being applied (coated), dried and compressed on the current collector.

  Hereinafter, with reference to FIG. 2, a configuration and a manufacturing method thereof will be described using the bottomed cylindrical lithium secondary battery 100 as an example. In a battery having a bottomed cylindrical shape, since the outer surface area with respect to the power generating element to be filled becomes small, it is preferable to design so that Joule heat generated by the internal resistance at the time of charging and discharging efficiently escapes to the outside. Moreover, it is preferable to design so that the filling ratio of the substance having high thermal conductivity is increased and the temperature distribution inside is reduced. FIG. 2 shows an example of a bottomed cylindrical lithium secondary battery 100. This battery is a bottomed cylindrical lithium secondary battery 100 in which a positive electrode sheet 14 and a negative electrode sheet 16 overlapped with a separator 12 are wound and accommodated in an outer can 18. In addition, in the figure, 20 is an insulating plate, 22 is a sealing plate, 24 is a positive current collector, 26 is a gasket, 28 is a pressure-sensitive valve element, and 30 is a current interruption element. In addition, although the illustration in the enlarged circle has changed hatching in consideration of visibility, each member corresponds to the whole drawing by reference numerals.

  First, a negative electrode active material is mixed with a binder or filler used as desired in an organic solvent to prepare a slurry-like or paste-like negative electrode mixture. The obtained negative electrode mixture is uniformly applied over the entire surface of both surfaces of the metal core as a current collector, and then the organic solvent is removed to form a negative electrode active material layer. Furthermore, the laminated body (mixed material) of a collector and a negative electrode active material layer is rolled with a roll press etc., and it adjusts to predetermined thickness and obtains a negative electrode sheet (electrode sheet). At this time, the coating method of each agent, the drying of the coated material, and the method of forming the positive and negative electrodes may be in accordance with conventional methods.

  In the present embodiment, a cylindrical battery is taken as an example, but the present invention is not limited to this. For example, the positive and negative electrode sheets (compounds) produced by the above method are stacked via a separator. After being assembled, it is processed into a sheet battery as it is, or after being folded and inserted into a rectangular can, the can and the sheet are electrically connected, the electrolyte is injected, and the opening is opened using a sealing plate. The prismatic battery may be formed by sealing.

  In any embodiment, the safety valve can be used as a sealing plate for sealing the opening. In addition to the safety valve, the sealing member may be provided with various conventionally known safety elements. For example, a fuse, bimetal, PTC element, or the like is preferably used as the overcurrent prevention element.

  In addition to the safety valve, as a countermeasure against the increase in the internal pressure of the battery can, a method of cutting the battery can, a method of cracking the gasket, a method of cracking the sealing plate, or a method of cutting the lead plate can be used. Further, the charger may be provided with a protection circuit incorporating measures against overcharge and overdischarge, or may be connected independently.

  For the can and lead plate, a metal or alloy having electrical conductivity can be used. For example, metals such as iron, nickel, titanium, chromium, molybdenum, copper, and aluminum, or alloys thereof are preferably used.

  As a method for welding the cap, the can, the sheet, and the lead plate, a known method (eg, direct current or alternating current electric welding, laser welding, ultrasonic welding) can be used. As the sealing agent for sealing, a conventionally known compound or mixture such as asphalt can be used.

[Applications of non-aqueous electrolyte secondary batteries]
Since the nonaqueous electrolyte secondary battery of the present invention has good cycleability, it is applied to various applications.

  Although there is no particular limitation on the application mode, for example, when installed in an electronic device, a notebook computer, a pen input personal computer, a mobile personal computer, an electronic book player, a mobile phone, a cordless phone, a pager, a handy terminal, a mobile fax machine, a mobile phone Copy, portable printer, headphone stereo, video movie, LCD TV, handy cleaner, portable CD, minidisc, electric shaver, walkie-talkie, electronic notebook, calculator, memory card, portable tape recorder, radio, backup power supply, memory card, etc. It is done. Other consumer products include automobiles, electric vehicles, motors, lighting equipment, toys, game equipment, road conditioners, watches, strobes, cameras, medical equipment (such as pacemakers, hearing aids, and shoulder grinders). Furthermore, it can be used for various military use and space use. Moreover, it can also combine with a solar cell.

  Although the metal ion used for charge transport in the secondary battery is not particularly limited, it is preferable to use a metal ion belonging to Group 1 or Group 2 of the periodic table. Among these, it is preferable to use lithium ions, sodium ions, magnesium ions, calcium ions, aluminum ions, and the like. There are many documents and books such as the patent documents listed at the beginning for general technical matters regarding secondary batteries using lithium ions, which are helpful. In addition, for secondary batteries using sodium ions, Journal of Electrochemical Society; Electrochemical Science and Technology, USA, 1980, Vol. 127, pages 2097-2099, and the like can be referred to. For magnesium ions, see Nature 407, p. 724-727 (2000) and the like can be referred to. For calcium ions, see J.H. Electrochem. Soc. Vol. 138, 3536 (1991) and the like. In the present invention, it is preferable to apply to a lithium ion secondary battery because of its widespread use, but the other effects also have a desired effect and should not be construed as being limited thereto.

  Examples of the present invention will be described below, but the present invention is not limited to these examples.

(Example 1 / Comparative Example 1)
・ Preparation of electrolyte 1M LiPF ₆ ethylene carbonate / diethyl carbonate volume ratio 1: 2 To the electrolyte, the additive (compound) shown in Table 1 was added in the amount shown in Table 1, and the test electrolyte was added. Prepared. Here, the added amount is indicated by mass% in the total electrolytic solution.

-Production of 2032 type coin battery The positive electrode is active material: nickel manganese lithium cobaltate (LiNi _1/3 Mn _1/3 Co _1/3 O ₂ ) 85% by mass, conductive auxiliary agent: 7% by mass of carbon black, binder: PVDF (Polyvinylidene fluoride) It was produced at 8% by mass, and the negative electrode was produced at 92% by mass of active material: Gr (natural graphite) and binder: 8% by mass of PVDF. The separator is made of polypropylene and has a thickness of 25 μm. Using the above positive and negative electrodes and separator, a 2032 type coin battery was prepared for each test electrolyte, and the following items were evaluated. The results are shown in Table 1.

<Wettability>
Evaluation of wettability The contact angle was measured using the contact angle meter DropMaster700 manufactured by Kyowa Interface Science Co., Ltd. with respect to each of the positive electrodes produced above. The evaluation criteria are as follows.
It is smaller than the contact angle value in the electrolyte containing no additive. A: When the contact angle is small B: When both are equivalent C: When the contact is large <Electrolytic solution characteristics (impurity peak)>
Evaluation of Impurities Using a 2032 type battery produced by the above method, in a thermostatic chamber at 30 ° C., after charging at a constant current of 1 C until the battery voltage becomes 4.3 V at 2.0 mA, the current value at a constant voltage of 4.3 V Was 0.12 mA or charged for 2 hours, and then 1 C constant current discharge was performed until the battery voltage became 2.7 V at 2.0 mA, and one cycle was made. This was repeated, and after 400 cycles, the battery was disassembled, the electrolyte solution inside was taken out, and purity was measured for this solution using liquid chromatography LC-6A manufactured by Shimadzu Corporation. The evaluation criteria at this time are as follows.
Peaks other than added additives are in area% of the total area AA: 0 to 3% A: Area% is more than 3% and 7% or less B: Area% is more than 7% to 15% %: Area% is more than 15%.

<Flame retardance test>
The following test system was used for evaluation with reference to the UL-94HB horizontal combustion test. A glass filter paper (ADVANTEC GA-100) having a width of 13 mm and a length of 110 mm was cut out, and 1.7 ml of the prepared electrolyte solution was uniformly dropped onto the glass filter paper. After the electrolyte solution was sufficiently infiltrated into the glass filter paper, the excess electrolyte solution was wiped and hung so as to be horizontal. The evaluation was performed based on the behavior after the inner flame of the butane gas burner adjusted to a total flame length of 2 cm was ignited for 3 seconds from the position where the inner flame touched the tip of the glass filter paper and the flame was released.
AA: Non-flammable or instantaneous flame extinguishing level A: Flame is observed for a while after ignition, but flame extinguishing before spreading over the entire filter paper B: Combustion suppression effect is seen, but non-flammable, extinguishing No level C: Level at which no combustion suppression effect is observed.
<Rate characteristics>
Using a 2032 type battery produced by the above method, in a constant temperature bath at 30 ° C., constant current charging at 0.4 mA (0.2 C) until the battery voltage becomes 4.3 V, then 0.4 mA (0.2 C). ), Constant current discharge was performed until the battery voltage reached 2.75 V, and this operation was repeated three times. After charging at 0.7 mA until the battery voltage becomes 4.3 V at 1.4 mA, the battery is discharged at 1.4 mA (0.7 C) until the battery voltage becomes 2.75 V, and this is repeated 10 times. Then, after performing 0.2 C constant current charging until the battery voltage becomes 4.3 V at 0.4 mA (0.2 C), 4 C constant current until the battery voltage becomes 2.75 V at 8.0 mA (4 C). Discharge was performed and the discharge capacity was measured. The value of the discharge capacity at the time of 4C constant current discharge with respect to the discharge capacity at the time of 0.2C constant current discharge was evaluated as a rate characteristic value.
Rate characteristic value (4C) = 0.2C charge capacity during charge / discharge / discharge capacity during 4C charge / discharge x 100 (%)

  In addition, the positive electrode, the negative electrode, and the electrolyte used were those described in the table below.

Ｍｎ−１： ＬｉＮｉ_０．３３Ｍｎ_０．３３Ｃｏ_０．３３Ｏ_２
Ｇｒ：天然黒鉛
但し界面活性剤添加量中の添加量中の（）内の数字は難燃剤１００重量部中における界面活性剤の添加量（重量部）を示す。

Mn-1: LiNi _0.33 Mn _0.33 Co _0.33 O ₂
Gr: natural graphite However, the number in () in the addition amount in the addition amount of the surfactant indicates the addition amount (parts by weight) of the surfactant in 100 parts by weight of the flame retardant.

Sf-1 [5J]: polyoxyethylene alkylmethylammonium hexafluorophosphate (carbon number 20)
Sf-2 [5A]: Sodium lauryl sulfate Sf-3 [5A]: Sodium dodecylbenzenesulfonate Sf-4 [5E]: Sorbitan monolaurate
Sf-5 [5B]: lithium perfluoroalkylcarboxylate (10 carbon atoms)
Sf-6 [5B]: Glycerol monostearate Sf-7 [5E]: Sorbitan monostearate Sf-8 [5C]: Lithium bisperfluoroalkyl phosphate (10 carbon atoms)
Sf-9 [5C]: Bispolyoxyethylene alkyl ether lithium phosphate (carbon number 20)
Sf-10 [5F]: Polyoxyethylene lauryl ether (15 carbon atoms)
Sf-11 [5F]: Polyethylene glycol laurate (20 carbon atoms)
Sf-12 [5A]: N-acylmethyltaurine (carbon number 20)
Sf-13 [5J]: Lauryltrimethylammonium fluoride

Here, test no. Reference numerals 106 and 115 are reference examples. Those starting with C are comparative examples.
From the results of Table 1 above, according to the electrolyte for a non-aqueous secondary battery of the present invention containing a specific flame retardant and a surfactant, high flame retardancy and high battery performance (cycle characteristics) It can be seen that both can be achieved.

(Example 2 and Comparative Example 2)
Battery performance was evaluated in the same manner except that the positive electrode and negative electrode of Example 1 were changed as shown in the table below. In addition, Test No. However, the same thing as Example 1 and Comparative Example 1 means that it is the same test as Example 1. In comparison, only the electrode is changed without changing the addition amount.

Ｍｎ−１： ＬｉＮｉ_０．３３Ｍｎ_０．３３Ｃｏ_０．３３Ｏ_２
Ｇｒ：天然黒鉛

Mn-1: LiNi _0.33 Mn _0.33 Co _0.33 O ₂
Gr: natural graphite

  As shown in the results of Table 2 above, the non-aqueous secondary battery electrolyte containing a specific flame retardant and a specific surfactant is particularly effective when combined with a high potential positive electrode (Mn-1). Good performance improvement has been achieved. From this result, it can be seen that the electrolyte for a non-aqueous secondary battery according to the present invention has a good compatibility with a positive electrode having a high potential and exhibits particularly excellent effects.

(Example 3 and Comparative Example 3)
The battery performance was evaluated in the same manner except that the flame retardant of Example 1 was changed as shown in the table below. All the surfactants used Sf-1. The addition amount of the flame retardant was 5% by mass, and the addition amount of the surfactant was 0.2% by mass. For the rate characteristic, a value exceeding 40% was regarded as acceptable (OK). The negative electrode was black charcoal (Gr), and the positive electrode was Mn-1.

C positive electrode (positive electrode composite)
1 Positive electrode conductive material (current collector)
2 Positive electrode active material layer A Positive electrode (positive electrode mixture)
3 Negative electrode conductive material (current collector)
4 Negative electrode active material layer 5 Nonaqueous electrolyte 6 Operating means 7 Wiring 9 Separator 10 Lithium ion secondary battery 12 Separator 14 Positive electrode sheet 16 Negative electrode sheet 18 Exterior can 20 also serving as negative electrode Insulating plate 22 Sealing plate 24 Positive electrode current collector 26 Gasket 28 Pressure sensitive valve body 30 Current interrupting element 100 Bottomed cylindrical shape lithium secondary battery

Claims (11)

An electrolyte for a non-aqueous electrolyte secondary battery comprising a positive electrode, a negative electrode, and an electrolyte in contact with both,
An electrolyte , a surfactant represented by any one of the following formulas (5A) to (5I) or (5J-1) , and a phosphazene compound are contained in an aprotic solvent, and the surfactant is contained. non-aqueous liquid electrolyte for a secondary battery Ru 0.1 parts by mass to 10 parts by mass der respect amount phosphazene compound 100 parts by mass.

(In the formula, R ^a represents a hydrogen atom, a linear, branched or cyclic alkyl group, or an aryl group. R ^b represents an alkyl group having a hydroxyl group or an aryl group having a hydroxyl group. The group and the aryl group may have a substituent, and these alkyl groups may have —O— interposed in the middle of a linear, branched or cyclic alkyl chain, provided that the formula (5E) The carbon number of R ^b is 6 to 30. R ^c is an alkyl group having a group containing a carbanion, a sulfoanion or a phosphoanion, or an aryl group having a group containing a carbanion, a sulfoanion or a phosphoanion. M represents an alkali metal or an alkaline earth metal, provided that it is a divalent metal salt in the case of an alkaline earth metal. Therefore, M ⁺ is replaced with 1 / 2M ²⁺ , X represents an anion, n represents an integer of 1 to 20, and x and y represent an integer of 2 to 10). The substituent which the alkyl group and aryl group may have is a halogen atom, a hydroxyl group, an alkyl group, an oxyethylene group, a polyoxyethylene group, an aryl group, an alkoxy group, an acyl group, an acylamino group, a carbamoyl group, an amino group. The electrolyte solution for nonaqueous secondary batteries of Claim 1 selected from a group and a heterocyclic group. Non-aqueous liquid electrolyte for a secondary battery according to claim 1 or 2 comprising an active material the positive electrode has a nickel or manganese. The phosphazene compound, a non-aqueous liquid electrolyte for a secondary battery according to claim 1 represented by the following formula (3).

(In the formula, R ^{1 to} R ⁶ represent a monovalent substituent. N represents an integer of 1 or more.) The phosphazene compound represented by the following formula (3A) or non-aqueous liquid electrolyte for a secondary battery according to claim 1 which is represented by (3B).

(In the formula , R ²¹ to R ²⁸ represent a monovalent substituent. N represents an integer of 1 or more.) In the formula (3A) and ^{(3B), R} 21 ~R ²⁸ is an alkyl group, an alkoxy group, an amino group, for a non-aqueous secondary battery according to claim 5 fluorine atoms or is a combination thereof Electrolytic solution. The aprotic solvent is non-aqueous liquid electrolyte for a secondary battery according to any one of claims 1 to 6 is a compound or a combination thereof represented by any one of the following formulas (4A) ~ (4C) .

^(Wherein, R 31 ^{to R 36} each represent a hydrogen atom, an alkyl Motoma other represents an aryl group.) Non-aqueous liquid electrolyte for a secondary battery according to any one of claims 1 to 7, a family Moshiku positive electrode capable of inserting the release of metal ions belonging to the second group, and also the family properly the non-aqueous electrolyte secondary battery insertion release Moshiku metal ion belonging to group II is comprising respective anode capable dissolution and deposition. The non-aqueous electrolyte secondary battery according to claim 8 , wherein the positive electrode includes an active material having nickel or manganese. A additive kit of the non-aqueous liquid electrolyte for a secondary battery contained together with an electrolyte in an aprotic solvent,
A surfactant represented by any one of the following formulas (5A) to (5I) or (5J-1) is combined with a flame retardant comprising a phosphazene compound , and the amount of the surfactant used is the flame retardant. The additive kit which is 0.1 mass part-10 mass parts with respect to 100 mass parts of agent.

(In the formula, R ^a represents a hydrogen atom, a linear, branched or cyclic alkyl group, or an aryl group. R ^b represents an alkyl group having a hydroxyl group or an aryl group having a hydroxyl group. The group and the aryl group may have a substituent, and these alkyl groups may have —O— interposed in the middle of a linear, branched or cyclic alkyl chain, provided that the formula (5E) The carbon number of R ^b is 6 to 30. R ^c is an alkyl group having a group containing a carbanion, a sulfoanion or a phosphoanion, or an aryl group having a group containing a carbanion, a sulfoanion or a phosphoanion. M represents an alkali metal or an alkaline earth metal, provided that it is a divalent metal salt in the case of an alkaline earth metal. Therefore, M ⁺ is replaced with 1 / 2M ²⁺ , X represents an anion, n represents an integer of 1 to 20, and x and y represent an integer of 2 to 10). The substituent which the alkyl group and aryl group may have is a halogen atom, a hydroxyl group, an alkyl group, an oxyethylene group, a polyoxyethylene group, an aryl group, an alkoxy group, an acyl group, an acylamino group, a carbamoyl group, an amino group. The additive kit according to claim 10 selected from a group and a heterocyclic group.