JP5693799B2 - Photo-curable sealing material, sealing method, sealing material and casing using the same - Google Patents

Description

  The present invention relates to a photocurable sealing material, a sealing method, a sealing material, and a casing using the same. More particularly, the present invention relates to a photocurable sealing material that is easily and instantaneously cured to a deep part by ultraviolet rays or the like.

  In recent years, it has high sealing properties such as waterproof and airtightness for electronic products such as mobile phones, digital cameras and video cameras, household appliances such as refrigerators, air conditioners and washing machines, and precision equipment such as cameras and watches. Customer demand for the products they have is increasing. In addition, for example, a hard resin such as nylon / GF has been conventionally used in a cellular phone, but in recent years, a cheaper general-purpose resin such as ABS or ABS / PC has been used. However, since ABS or ABS / PC is flexible and easily deformed, there is a problem that sufficient sealing characteristics cannot be obtained with a conventional sealing material. Therefore, there is a demand for a sealing material having higher flexibility and tensile strength than conventional sealing materials.

  Conventional sealing materials include, for example, hot-melt adhesives, one-component urethane-based reactive hot-melt adhesives, thermoplastic hot-melt sealing materials, moisture-curable hot-melt sealing materials, thermosetting sealing materials, and molded rubber sealing Materials (gaskets), two-component urethane foam sealants, and the like are known. However, all have problems such as inadequate heat resistance and waterproofing, poor operability such as prevention of moisture contamination, heat damage to equipment for heating, housing, bad operability due to manufacturing using molds, etc. In particular, when a flexible general-purpose resin is used for a housing of an electronic product, a home appliance, a precision instrument, etc., a sufficiently satisfactory performance cannot be exhibited.

  Since the photocurable sealing material can be produced on the housing without using a mold, it is superior in operability as compared with a conventional sealing material. Photocurable sealing materials mainly include photocurable sealing materials that use radical polymerization of acryloyl groups and ene-thiol-based photocurable sealing materials that use an ene-thiol reaction. The photocurable sealing material using radical polymerization of an acryloyl group is described in, for example, Patent Documents 1 and 2, and includes a composition comprising a urethane acrylate oligomer, an acrylate monomer, and a photopolymerization initiator (and a photosensitizer). It is generated by curing with light or the like. However, the photocurable sealing materials of Patent Documents 1 and 2 do not have sufficient flexibility and tensile strength required for housings such as electronic products, home appliances, and precision devices.

  Examples of the ene-thiol-based photocuring sealant are described in Patent Documents 3 to 6. Patent Document 3 discloses a photocurable resin composition containing a compound having a polyene, a polythiol, and a bromine-substituted aromatic ring, and the cured product of this composition has a high refractive index and is bonded. It describes that it is excellent in strength and surface curability, and the refractive index can be adjusted with high accuracy. Patent Document 4 discloses an ene-thiol photocurable resin composition containing a polyene compound and a (poly) thiol monomer comprising a polymercaptocarboxylic acid amide compound, and the composition is based on oxygen. It is described that there is no inhibition of polymerization, the composition can be cured in a short time, the volume shrinkage is small, the amount of photoinitiator used can be reduced, and the moisture resistance is greatly improved. Patent Document 5 discloses a curable composition containing a thiol compound containing two or more groups having a specific structure and an urethane compound containing an ethylenically unsaturated double bond having a specific structure. It is described that the product has high adhesion to the substrate, reactivity, and transparency, and high heat resistance and hardness. Patent Document 6 discloses a photocurable resin composition that contains a polybutadiene (meth) acrylate, a polythiol compound, and a photoradical initiator and is cured by irradiation with an ultraviolet LED, and the composition is rapidly cured. It is described that it has excellent surface curability, moisture resistance and airtightness. However, none of Patent Documents 3 to 6 mentions flexibility, tensile strength, and the like required for a housing of an electronic product, a home appliance, a precision device, or the like.

  Patent Documents 7 and 8 describe photocurable sealing materials that simultaneously and competitively carry out radical polymerization reaction of acryloyl group and ene-thiol reaction. Patent Documents 7 and 8 include (A) an oligomer having a (meth) acryloyl group, (B) a (meth) acrylate monomer, and (C) a polythiol compound, and the functional group ratio between the acryloyl group and the mercapto group is 100. : 0.1 to 100: 5n (n is the number of mercapto groups in one molecule of the polythiol compound). It is described that this gasket material can improve elongation at break and suppress the occurrence of cracks and cracks. The polythiol compounds specifically used in the examples of Patent Document 7 are compounds having primary thiols, but the cured material for gaskets obtained in the examples are all flexible, elongation at break (Strength) or compression / recovery rate is insufficient, and in the examples, those that satisfy all the functions that can be used for casings of electronic products, home appliances, precision equipment, etc. are found. I can't. In addition, when an attempt was made to reexamine the sealing material described in Table 2 of Patent Document 7, production of the energy ray curable oligomer A (trade name “Lighttack PUA-KH32M” manufactured by Kyoeisha Chemical Co., Ltd.) as a raw material was discontinued. It was. Therefore, when the oligomer and the monomer included were appropriately mixed and retested, as described in the comparative example of the present specification, only an extremely hard sealing material having a hardness of 50 or more was obtained. It was inappropriate.

WO96 / 10594 JP 2004-26919 A JP 2003-277505 A JP 2007-70417 A WO2007 / 086461 WO2010 / 071711 JP 2010-260918 A WO2010 / 126040

  The problem to be solved by the present invention has a high compression recovery rate, a high tensile strength, an excellent elongation rate, and a low hardness as required, thereby providing excellent sealing properties such as airtightness and waterproofness, Is to provide a sealing material with less surface tack. Another object of the present invention is to provide a photocurable sealing material which is easily and instantly cured to the deep part of the photocurable sealing material to produce the same sealing material and has good storage stability until use.

  As a result of intensive studies to solve the above problems, the present inventors have (A) an oligomer having a (meth) acryloyl group having a weight average molecular weight of 10,000 to 30,000, and (B) a (meth) acrylate monomer. And (C) when photocuring a photocurable sealing material containing a polythiol compound in a specific ratio, surprisingly, the tensile strength (elongation at break) is much higher than those described in any of the patent documents. The present invention was completed by finding that it has a high compression recovery rate at the same time. That is, the present invention is as follows.

[1] A photocurable sealing comprising (A) an oligomer having a (meth) acryloyl group having a weight average molecular weight of 10,000 to 30,000, (B) a (meth) acrylate monomer, and (C) a polythiol compound. Materials for
(A) 5-100 parts by weight of (B) (meth) acrylate is included with respect to 100 parts by weight of the oligomer having a (meth) acryloyl group,
(A) A photocurable sealing material comprising a (meth) acryloyl group contained in both an oligomer having a (meth) acryloyl group and a (B) (meth) acrylate monomer and a mercapto group of (C) a polythiol compound. The ratio of the number present is 100: 5n to 100: 25n (n is the number of mercapto groups in one molecule of the polythiol compound).
Photo-curable sealing material.

  [2] The photocurable sealing material according to [1], further comprising (D) 0.1 to 15 parts by weight of (D) a carbodiimide compound with respect to 100 parts by weight of the oligomer (A) having a (meth) acryloyl group.

  [3] The photocurable sealing material according to [1] or [2], wherein the (C) polythiol compound has 2 to 6 mercapto groups in one molecule and the mercapto group is secondary.

  [4] (C) The photothiol sealing according to [1] or [2], wherein the polythiol compound is an ester produced from a polyhydric alcohol having 2 to 6 hydroxyl groups and β-mercaptobutanoic acid. material.

  [5] The photocurable sealing according to any one of [1] to [4], wherein the (B) (meth) acrylate monomer is a monofunctional (meth) acrylate, a polyfunctional (meth) acrylate, or a combination thereof. Materials.

  [6] (A) An oligomer having a (meth) acryloyl group is a urethane (meth) acrylate oligomer, a polyester (meth) acrylate oligomer, a polyether (meth) acrylate oligomer, an epoxy (meth) acrylate oligomer, or a conjugate. The photocurable sealing material according to any one of [1] to [5], which is at least one selected from the group comprising diene polymer (meth) acrylate oligomers and hydrogenated products thereof.

  [7] The photocurable sealing material according to any one of [1] to [6], further comprising (E) a photoradical polymerization initiator and / or (F) a viscosity modifier.

  [8] A sealing method by photocuring the photocurable sealing material according to any one of [1] to [7].

  [9] A sealing material produced by photocuring the photocurable sealing material according to any one of [1] to [7].

  [10] A housing using a sealing material generated by photocuring the photocurable sealing material according to any one of [1] to [7].

  [11] A stabilizer for an ene-thiol-based photocurable resin material containing a carbodiimide compound.

  The photo-curing sealing material of the present invention has a high compression recovery rate, high tensile strength and excellent flexibility, and thereby has excellent sealing properties such as airtightness and waterproofness, and also has a low surface tack. Material is provided. In addition, the photocurable sealing material of the present invention can be easily and instantaneously cured to the depth of the photocurable sealing material to produce the same sealing material, and has good storage stability until use. Have.

The photocurable sealing material of the present invention will be described sequentially.
(A) The weight average molecular weight of the oligomer (A) having a (meth) acryloyl group having a weight average molecular weight of 10,000 to 30,000 is 10,000 to 30,000, preferably a weight average An oligomer having a molecular weight of 12,000 to 25,000 is exemplified, and an oligomer having a weight average molecular weight of 15,000 to 22,000 is more preferred. The oligomer (A) is preferably an oligomer having at least two (meth) acrylate groups in the molecule, and the number of (meth) acrylate groups in one molecule of the oligomer (A) is, for example, 2 -10, preferably 2-6, more preferably 2-4, and particularly preferably 2.

  As the oligomer of (A), for example, urethane (meth) acrylate oligomer, polyester (meth) acrylate oligomer, polyether (meth) acrylate oligomer, acrylic (meth) acrylate oligomer, epoxy (meth) acrylate oligomer, Examples thereof include silicone (meth) acrylates such as conjugated diene polymer (meth) acrylate oligomers such as polybutadiene oligomers and hydrogenated products thereof.

  As the urethane-based (meth) acrylate oligomer, for example, a polyol such as polyether polyol, polyester polyol, and carbonate diol is reacted with a polyisocyanate to obtain a polyurethane oligomer, and the oligomer is esterified with (meth) acrylic acid. The oligomer obtained by converting is mentioned.

  As the polyester-based (meth) acrylate oligomer, for example, a polyester oligomer having hydroxyl groups at both ends is obtained by condensing a polyvalent carboxylic acid and a polyhydric alcohol or by adding a polyvalent carboxylic acid alkylene oxide. And an oligomer obtained by esterifying the hydroxyl group with (meth) acrylic acid.

  Examples of the polyether (meth) acrylate oligomer include an oligomer obtained by esterifying a hydroxyl group of a polyether polyol with (meth) acrylic acid.

  Examples of the acrylic (meth) acrylate oligomer include telechelic polyacrylate having a highly controlled structure by applying an atom transfer radical polymerization (ATRP) method.

  Examples of the epoxy-based (meth) acrylate oligomer include oligomers obtained by esterification by reacting (meth) acrylic acid with the oxirane ring of a relatively low molecular weight bisphenol-type epoxy resin and novolac-type epoxy resin. In addition, a carboxyl-modified epoxy acrylate oligomer obtained by partially modifying the epoxy-based (meth) acrylate oligomer with a dicarboxylic acid anhydride is also included.

  Examples of the conjugated diene polymer (meth) acrylate oligomer include SBR diacrylate obtained by esterifying a liquid styrene-butadiene copolymer with acrylic acid, polyisoprene acrylate obtained by esterifying polyisoprene with acrylic acid, Examples thereof include polybutadiene acrylate obtained by esterifying polybutadiene with acrylic acid, polybutadiene acrylate obtained by reacting 1,2-polybutadiene having a hydroxyl group at the molecular end with (meth) acrylate having an isocyanate group.

  Examples of the silicone (meth) acrylate include an ester compound of a hydroxyl group of an alcoholic siloxane compound and acrylic acid.

  As the oligomer (A), one kind may be used alone, but two or more kinds may be used in combination. Preferred oligomers (A) include urethane (meth) acrylate oligomers, and examples include urethane polyester (meth) acrylate oligomers.

  In the urethane (meth) acrylate oligomer having two (meth) acryloyl groups, which is a preferred oligomer (A), polyether diol, polyester diol and carbonate diol having two hydroxyl groups used in the production thereof Include the following.

  Examples of the polyether diol include polyethylene glycol, polypropylene glycol, polytetramethylene glycol, polyhexamethylene glycol and 1,3-butylene glycol, 1,4-butylene glycol, neopentyl glycol, cyclohexanedimethanol, 2,2- Examples thereof include polyether diols obtained by adding ethylene oxide or propylene oxide to bis (4-hydroxycyclohexyl) propane, bisphenol A and the like.

  Examples of the polyester diol include polyethylene glycol, polypropylene glycol, polytetramethylene glycol, 1,3-butylene glycol, 1,4-butylene glycol, 1,6-hexanediol, neopentyl glycol, and 1,4-cyclohexanedimethanol. , 2,2-bis (4-hydroxycyclohexyl) propane, bisphenol A, etc. added with ethylene oxide or propylene oxide, alcohol added with ε-caprolactone, adipic acid, sebacic acid, azelaic acid, dodecanedicarboxylic acid, etc. And polyester diols obtained by reacting with dicarboxylic acids or anhydrides.

  Examples of the carbonate diol include diaryl carbonates such as diphenyl carbonate, bis-chlorophenyl carbonate, dinaphthyl carbonate, phenyl-toluyl carbonate, phenyl-chlorophenyl carbonate, 2-tolyl-4-tolyl-carbonate, dimethyl carbonate, and diethyl carbonate. Or dialkyl carbonates and 1,6-hexanediol, neopentyl glycol, 1,4-butanediol, 1,8-octanediol, 1,4-cyclohexanedimethanol, 2-methylpropanediol, dipropylene glycol, And carbonate diols obtained by reaction with diols such as dibutylene glycol.

(B) (Meth) acrylate monomer (Meth) acrylate monomer includes (meth) acrylate monomer having at least one (meth) acryloyl group in the molecule. Specifically, (meth) acryloyl group is 1 And monofunctional monomers having two, bifunctional monomers having three, trifunctional monomers having three, tetrafunctional monomers having four, and the like.

  Examples of the monofunctional monomer include methyl methacrylate, butyl methacrylate, 2-phenoxyethyl acrylate, ethoxylated 2-phenoxyethyl acrylate, 2- (2-ethoxyethoxy) ethyl acrylate, cyclic trimethylolpropane, acrylic acid formal, β-carboxyethyl acrylate, lauryl methacrylate, isooctyl acrylate, stearyl methacrylate, isodecyl acrylate, isobornyl methacrylate, benzyl acrylate, hydroxypivalyl hydroxypivalate diacrylate, ethoxylated 1,6-hexanediol diacrylate, Dipropylene glycol diacrylate, tricyclodecane dimethanol diacrylate, ethoxylated dipropylene glycol diacrylate Rate, neopentyl glycol diacrylate, propoxylated neopentyl glycol diacrylate, ethoxylated bisphenol-A dimethacrylate, 2-methyl-1,3-propanediol diacrylate, ethoxylated 2-methyl-1,3-propanediol Diacrylate, 2-butyl-2-ethyl-1,3-propanediol diacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, 2-hydroxyethyl methacrylate phosphoric acid, tris (2-hydroxyethyl) isocyanurate triacrylate, penta Erythritol triacrylate, ethoxylated trimethylolpropane triacrylate, propoxylated trimethylolpropane triacrylate, trimethylol Propane trimethacrylate, pentaerythritol tetraacrylate, ethoxylated pentaerythritol tetraacrylate, di-trimethylolpropane tetraacrylate, propoxylated pentaerythritol tetraacrylate, pentaerythritol tetraacrylate, dipentaerythritol hexaacrylate, methacrylate, hydroxyethyl acrylate (HEA ), 2-hydroxyethyl methacrylate (HEMA), tripropylene glycol dimethacrylate, 1,4-butanediol dimethacrylate, 1,6-hexanediol dimethacrylate, allylated cyclohexyl dimethacrylate, isocyanurate dimethacrylate, ethoxylated trimethylol Propane trimethacrylate, professional Kishireto glycerol trimethacrylate, trimethylolpropane trimethacrylate, tris (acryloxyethyl) isocyanurate, and include combinations of two or more thereof.

  Examples of the bifunctional monomer include 1,6-hexanediol diacrylate, bisphenol A ethoxylated acrylate, polyethylene glycol diacrylate (200-600), tripropylene glycol diacrylate, neopentyl glycol propoxylate (2), and ethoxylation. (2) Neopentyl glycol diacrylate, dipropylene glycol diacrylate, trimethylolpropane ethoxylated (3) methyl ether diacrylate, and combinations of two or more thereof.

  Examples of the trifunctional monomer include trimethylolpropane triacrylate, trimethylolpropane propoxylated (5-20) triacrylate, propoxylated (4) glycerol triacrylate, ethoxylated (3) trimethylolpropane triacrylate, propoxy And pentalysitol triacrylate, and combinations of two or more thereof.

  Examples of the tetrafunctional monomer include ditrimethylolpropane tetraacrylate, dipentaerythritol mono-hydroxypentaacrylate, and combinations of two or more thereof.

  One (meth) acrylate monomer may be used alone, but two or more types may be used in combination. Preferred (meth) acrylate monomers include monofunctional monomers, and combinations of monofunctional monomers and bifunctional monomers are also preferred. More preferred is a monofunctional monomer.

  As the usage-amount of (meth) acrylate, the range of 5-100 weight part is used with respect to 100 weight part of (A) oligomer which has a (meth) acryloyl group. By using an amount in this range, the viscosity reduction, flexibility, compression recovery rate, and tensile strength of the sealing agent of the present invention can be improved. Preferable amount of (meth) acrylate is 10 to 80 parts by weight, more preferably 40 to 70 parts by weight. Depending on the application of the sealing material of the present invention, the type and amount of (meth) acrylate monomer can be appropriately adjusted in order to obtain properties such as viscosity, flexibility, compression recovery rate, and tensile strength.

(C) Polythiol compound Examples of the polythiol compound include compounds having 2 to 10 mercapto groups in the molecule, preferably those having 2 to 6 mercapto groups in the molecule, and more preferably And those having 3 to 4 mercapto groups in the molecule.

  As a polythiol compound, the thing of patent documents 3-8 is mentioned, for example. These polythiol compounds will be specifically described below.

As a polythiol compound, for example,
(A) A polythiol compound containing a hydrocarbon structure (aliphatic polythiols such as C _2-20 alkane polythiol, araliphatic polythiols such as xylylene dithiol, and halogen atoms of halohydrin adducts of alcohols are substituted with mercapto groups. Polythiols, polythiol compounds consisting of hydrogen sulfide reaction products of polyepoxide compounds, etc.)
(B) Formula (1)

(In the formula, R ¹ and R ² independently represent a hydrogen atom or a C _1-10 alkyl group.
m is 0, 1 or 2, and n is 0 or 1. )
And a polythiol compound containing an ether structure represented by formula (2):

(Wherein R ¹ , R ² , m and n are as defined above.)
The polythiol compound containing the ester structure shown by these is mentioned. Among these polythiol compounds, (b) a polythiol compound containing an ether structure and (c) a polythiol compound containing an ester structure are preferred, and (c) a polythiol compound containing an ester structure is more preferred.
(A) Examples of the polythiol compound containing a hydrocarbon structure include 2,5-hexanedithiol, 2,9-decanedithiol, 1,4-bis (1-mercaptoethyl) benzene, and the like.
(B) Examples of the polythiol compound having an ether structure include a 2-mercaptoethyl ether group, a 2-mercaptopropyl ether group, a 3-mercaptopropyl ether group, a 2-mercaptobutyl ether group, a 3-mercaptobutyl ether group, and a 4-mercapto group. Examples thereof include compounds having a structure such as a butyl ether group, a 5-mercaptopentyl ether group, and a 5-mercaptohexyl ether group.
(C) The polythiol compound containing an ester structure is produced by esterifying a mercapto group-containing carboxylic acid and a polyhydric alcohol, which is a compound having a hydrogen atom bonded to the left end of the structure of the formula (2). Compounds are included.

  Specific examples of the mercapto group-containing carboxylic acid which is a compound having a hydrogen atom bonded to the left end of the structure of the formula (2) include thioglycolic acid, 2-mercaptopropionic acid, 3-mercaptobutyric acid, 2-mercaptoisobutyric acid, Examples include 3-mercaptoisobutyric acid, 3-mercaptopropionic acid, 3-mercapto-3-phenylpropionic acid, 3-mercapto-3-methylbutyric acid, etc., preferably 3-mercaptobutyric acid, 3-mercapto-3-phenylpropion An acid, 3-mercapto-3-methylbutyric acid, etc. are mentioned, More preferably, 3-mercaptobutyric acid is mentioned.

Specific examples of the polyhydric alcohol include C _2-20 alkylene glycol (C _2-10 alkylene group is preferable, and the carbon chain thereof may be branched. Examples thereof include ethylene glycol, trimethylene glycol, 1 , 2-propylene glycol, 1,2-butanediol, 1,3-butanediol, 2,3-butanediol, tetramethylene glycol, 1,5-pentanediol, 1,6-hexanediol, 1,8-octane Diol, 1,9-nonanediol, 1,12-dodecanediol, cyclohexane-1,4-dimethanol, hydrogenated bisphenol A, etc.), diethylene glycol, poly (oxyalkylene) glycol, glycerin, triethylene glycol , Polyethylene glycol, dipropylene glycol , Tripropylene glycol, polypropylene glycol, polytetramethylene ether glycol, trimethylolpropane, ditrimethylolpropane, pentaerythritol, dipentaerythritol, cyclohexanediol, cyclohexanedimethanol, norbornene dimethanol, norbornanedimethanol, polycarbonate diol, both Terminal hydroxypolysilicone, aromatic ring-containing polyol, tris-2-hydroxyethyl isocyanurate, 2,2-bis [4- (2-hydroxyethyloxy) phenyl] propane, hydrogenated bisphenol A, 4,4′- (9-Fluorenylidene) bis (2-phenoxyethanol), cyclohexane-1,4-dimethanol ethylene oxide adduct, hydrogenated bisphenol A ethylene oxide adduct, cyclohexane-1,4-dimethanol-propylene oxide adduct, hydrogenated bisphenol A propylene oxide adduct, and the like.

  Preferred polyhydric alcohols include alkylene glycols such as ethylene glycol, 1,2-propylene glycol, 1,2-butanediol, etc., where the alkylene main chain has 2 carbon atoms, trimethylolpropane, polycarbonate diol, cyclohexanediol, cyclohexanediol. Examples of the polyol containing an aromatic ring include 2,2-bis [4- (2-hydroxyethyloxy) phenyl] propane and 4,4 ′-(9-fluorenylidene). ) Diphenol, 4,4 ′-(9-fluorenylidene) bis (2-phenoxyethanol), and the like.

  Examples of these polythiol compounds include formulas (3) and (4)

(In the formula, R ^{3 to} R ⁶ independently represent a hydrogen atom or a C _1-10 alkyl group.
L-C (O) -O- represents the structure represented by the formula (2). )
The polythiol compound shown by these is mentioned. As the C _1-10 alkyl group of R ^{3 to} R ⁶ in Formula (3), a linear or branched C _1-3 alkyl group is preferable, and specifically, a methyl group, an ethyl group, or an n-propyl group. , An isopropyl group, and the like. Among them, a methyl group and an ethyl group are preferable. A polythiol compound in which R ³ is a hydrogen atom, a methyl group, or an ethyl group, and R ^{4 to} R ⁶ are all hydrogen atoms is particularly preferable.

  Specific examples of these polythiol compounds include di (1-mercaptoethyl ester) phthalate, di (2-mercaptopropyl ester) phthalate, di (3-mercaptobutyl ester) phthalate, and di (3-mercaptoisobutyl phthalate). Ester), ethylene glycol bis (3-mercaptobutyrate), propylene glycol bis (3-mercaptobutyrate), diethylene glycol bis (3-mercaptobutyrate), butanediol bis (3-mercaptobutyrate), octanediol bis ( 3-mercaptobutyrate), trimethylolpropane tris (3-mercaptobutyrate), pentaerythritol tetrakis (3-mercaptobutyrate), dipentaerythritol hexakis (3-mercaptobutyrate), 1, -Butanediol bis (3-mercaptobutyrate), 1,4-butanediol bis (3-mercaptobutyrate), neopentyl glycol bis (3-mercaptobutyrate), 1,6-hexanediol bis (3-mercapto) Butyrate), 1,8-octanediol bis (3-mercaptobutyrate), 1,9-nonanediol bis (3-mercaptobutyrate), cyclohexane-1,4-dimethanol bis (3-mercaptobutyrate) , Diethylene glycol bis (3-mercaptobutyrate), triethylene glycol bis (3-mercaptobutyrate), polyethylene glycol bis (3-mercaptobutyrate), dipropylene glycol bis (3-mercaptobutyrate), tripropylene glycol bis (3-Mel Ptobutyrate), polypropylene glycol bis (3-mercaptobutyrate), polytetramethylene ether glycol bis (3-mercaptobutyrate), bis (3-mercaptobutyrate) of cyclohexane-1,4-dimethanol ethylene oxide adduct, Bis (3-mercaptobutyrate) of hydrogenated bisphenol A ethylene oxide adduct, bis (3-mercaptobutyrate) of cyclohexane-1,4-dimethanol propylene oxide adduct, bis of hydrogenated bisphenol A propylene oxide adduct (3-mercaptobutyrate), glycerol tris (3-mercaptobutyrate), diglycerol tetrakis (3-mercaptobutyrate), trimethylolpropane tris (3-mercaptobutyrate), dito Limethylolpropane tetrakis (3-mercaptobutyrate), pentaerythritol tetrakis (3-mercaptobutyrate), dipentaerythritol hexakis (3-mercaptobutyrate), ethylene glycol bis (2-mercaptopropionate), propylene glycol Bis (2-mercaptopropionate), diethylene glycol bis (2-mercaptopropionate), butanediol bis (2-mercaptopropionate), octanediol bis (2-mercaptopropionate), trimethylolpropane tris ( 2-mercaptopropionate), pentaerythritol tetrakis (2-mercaptopropionate), dipentaerythritol hexakis (2-mercaptopropionate), ethylene glyco Rubis (3-mercaptoisobutyrate), propylene glycol bis (3-mercaptoisobutyrate), diethylene glycol bis (3-mercaptoisobutyrate), butanediol bis (3-mercaptoisobutyrate), octanediol bis (3 -Mercaptoisobutyrate), trimethylolpropane tris (3-mercaptoisobutyrate), pentaerythritol tetrakis (3-mercaptoisobutyrate), dipentaerythritol hexakis (3-mercaptoisobutyrate), ethylene glycol bis ( 2-mercaptoisobutyrate), propylene glycol bis (2-mercaptoisobutyrate), diethylene glycol bis (2-mercaptoisobutyrate), butanediol bis (2-mercaptoiso) Tyrate), octanediol bis (2-mercaptoisobutyrate), trimethylolpropane tris (2-mercaptoisobutyrate), pentaerythritol tetrakis (2-mercaptoisobutyrate), dipentaerythritol hexakis (2-mercaptoiso) Butyrate), ethylene glycol bis (4-mercaptovalerate), propylene glycol bis (4-mercaptoisovalerate), diethylene glycol bis (4-mercaptovalerate), butanediol bis (4-mercaptovalerate), octanediol Bis (4-mercaptovalerate), trimethylolpropane tris (4-mercaptovalerate), pentaerythritol tetrakis (4-mercaptovalerate), dipentaerythritol hexa Kiss (4-mercaptovalerate), ethylene glycol bis (3-mercaptovalerate), propylene glycol bis (3-mercaptovalerate), diethylene glycol bis (3-mercaptovalerate), butanediol bis (3-mercaptovalerate) ), Octanediol bis (3-mercaptovalerate), trimethylolpropane tris (3-mercaptovalerate), pentaerythritol tetrakis (3-mercaptovalerate), dipentaerythritol hexakis (3-mercaptovalerate), hydrogen Bisphenol A bis (3-mercaptobutyrate), bisphenol A dihydroxyethyl ether-3-mercaptobutyrate, 4,4 ′-(9-fluorenylidene) bis (2-phenoxyethyl (3-me Captobutyrate)), ethylene glycol bis (3-mercapto-3-phenylpropionate), propylene glycol bis (3-mercapto-3-phenylpropionate), diethylene glycol bis (3-mercapto-3-phenylpropionate), Butanediol bis (3-mercapto-3-phenylpropionate), octanediol bis (3-mercapto-3-phenylpropionate), trimethylolpropane tris (3-mercapto-3-phenylpropionate), tris-2- (3-mercapto-3-phenylpropionate) ethyl isocyanurate, pentaerythritol tetrakis (3-mercapto-3-phenylpropionate), dipentaerythritol hexakis (3-mercapto-3-fe Lupropionate), ethylene glycol bisthioglycolate), trimethylene glycol bis (thioglycolate), propylene glycol bis (thioglycolate), 1,3-butanediol bis (thioglycolate), 1,4-butanediol bis (Thioglycolate), neopentyl glycol bis (thioglycolate), 1,6-hexanediol bis (thioglycolate), 1,8-octanediol bis (thioglycolate), 1,9-nonanediol bis ( Thioglycolate), cyclohexane-1,4-dimethanol bis (thioglycolate), diethylene glycol bis (thioglycolate), triethylene glycol bis (thioglycolate), polyethylene glycol bis (thioglycolate), dipropylene glycol Recall bis (thioglycolate), tripropylene glycol bis (thioglycolate), polypropylene glycol bis (thioglycolate), polytetramethylene ether glycol bis (thioglycolate), cyclohexane-1,4-dimethanol ethylene oxide addition Bis (thioglycolate), hydrogenated bisphenol A ethylene oxide adduct bis (thioglycolate), cyclohexane-1,4-dimethanol propylene oxide adduct bis (thioglycolate), hydrogenated bisphenol A propylene Oxide adducts bis (thioglycolate), glycerol tris (thioglycolate), diglycerol tetrakis (thioglycolate), trimethylolpropane tris (thioglycolate), ditrimethyl Propanetetrakis (thioglycolate), pentaerythritol tetrakis (thioglycolate), dipentaerythritol hexakis (thioglycolate), ethylene glycol bis (3-mercaptopropionate), trimethylene glycol bis (3-mercapto) Propionate), propylene glycol bis (3-mercaptopropionate), 1,3-butanediol bis (3-mercaptopropionate), 1,4-butanediol bis (3-mercaptopropionate), neo Pentyl glycol bis (3-mercaptopropionate), 1,6-hexanediol bis (3-mercaptopropionate), 1,8-octanediol bis (3-mercaptopropionate), 1,9-nonanediol Screw (3-Mel Ptopropionate), cyclohexane-1,4-dimethanol bis (3-mercaptopropionate), diethylene glycol bis (3-mercaptopropionate), triethylene glycol bis (3-mercaptopropionate), polyethylene glycol Bis (3-mercaptopropionate), dipropylene glycol bis (3-mercaptopropionate), tripropylene glycol bis (3-mercaptopropionate), polypropylene glycol bis (3-mercaptopropionate), polytetra Methylene ether glycol bis (3-mercaptopropionate), bis (3-mercaptopropionate) of cyclohexane-1,4-dimethanol ethylene oxide adduct, hydrogenated bisphenol A ethylene oxide Bis (3-mercaptopropionate) of idoid adduct, bis (3-mercaptopropionate) of cyclohexane-1,4-dimethanol propylene oxide adduct, bis (3-mercaptopropionate) of hydrogenated bisphenol A propylene oxide adduct Mercaptopropionate), glycerol tris (3-mercaptopropionate), diglycerol tetrakis (3-mercaptopropionate), trimethylolpropane tris (3-mercaptopropionate), ditrimethylolpropane tetrakis (3-mercapto) Propionate), pentaerythritol tetrakis (3-mercaptopropionate), dipentaerythritol hexakis (3-mercaptopropionate), and the like.

  Among these polythiol compounds, poly (3-mercaptobutyrate) isomers are preferred, particularly polyethylene glycol bis (3-mercaptobutyrate), pentaerythritol tetrakis (3-mercaptobutyrate), dipentaerythritol hexakis (3 -Mercaptobutyrate) and the like are preferable. Furthermore, the structure of the specific example of a preferable polythiol compound is shown below.

(In the formula, n is an integer of 1 to 10.)
Preferable polythiol compounds include compounds having a secondary mercapto group. The secondary thiol compound is superior in its storage stability to the primary thiol compound. Further, the sealing material produced using the photocurable sealing material of the present invention has sealing properties superior to those of conventionally known photocurable sealing materials, but a polythiol compound having a secondary thiol is used. In this case, the coating stability during coating and the stability of sealing properties are excellent. In particular, excellent characteristics regarding hardness and flexibility can be stably obtained. The reason for this is presumed that, for example, the balance between the radical reaction and the heat addition reaction in the ene-thiol reaction is preferably adjusted by steric hindrance around the thiol group.

  The amount of polythiol compound used is (A) (meth) acryloyl group contained in both (A) (meth) acryloyl group-containing oligomer and (B) (meth) acrylate monomer, and (C) mercapto group of polythiol compound. The ratio of the number present in the photocurable sealing material is an amount that is 100: 5n to 100: 25n (where n is the number of mercapto groups in one molecule of the polythiol compound). The amount that the ratio is 100: 7n to 100: 20n is mentioned, and the amount that the ratio is 100: 9n to 100: 17n is more preferable.

(D) Carbodiimide compound The carbodiimide compound refers to a hydrolysis-resistant stabilizer (hydrolysis-resistant agent) that suppresses a hydrolysis chain by removing a hydroxyl group or a carboxyl group generated by hydrolysis of a resin such as polyester. Examples of the carbodiimide compound include a monocarbodiimide compound and a polycarbodiimide compound, which are widely known, and any of them can be used. The carbodiimide compounds are, for example, JP-A-9-309871, JP-A-9-249801, JP-A-9-208649, JP-A-9-296097, JP-A-8-81533, JP-A-8-27092, JP-A-9-136869, JP-A-9-136869. 9-124582, JP-A-9-188807, JP-A-2005-82642, JP-A-2005-53870, JP-A-2012-36392, JP-A 2010-163203, JP-A-2011-174094, WO2008 / 072514, JP-A-2012-81759, Examples described in JP 2012-52014 A, JP 2012-7079 A, and the like.

For example, the ^{formula: R 12 - (- N =} C = N-R 11 -) m -R 13
[Wherein R ¹¹ are the same or different and each represents a divalent aromatic group and / or an aliphatic group.

In the case of an aromatic oligomeric carbodiimide or an aromatic polymer carbodiimide, R ¹¹ may be substituted with an aliphatic and / or alicyclic substituent and / or an aromatic substituent having at least one carbon atom. Good. Here, these substituents may have a hetero atom, and these substituents may be substituted at at least one ortho position of the aromatic group to which the carbodiimide group is bonded.

R ¹² is C ₁ -C ₁₈ alkyl, C ₅ -C ₁₈ cycloalkyl, aryl, C ₇ -C ₁₈ aralkyl, -R ¹¹ -NH-COS-R ¹⁴ , -R ¹¹ COOR ¹⁴ , -R ¹¹ -OR. _{^{14, -R 11 -N (R 14}} ) 2, -R 11 -SR 14, -R 11 -OH, R 11 -NH 2, -R 11 -NHR 14, -R 11 - ^epoxy, -R 11 -NCO , ^-R 11 -NHCONHR ^14, a ^-R 11 -NHCONR ¹⁴ R ¹⁵ or ^-R 11 -NHCOOR ^16.

R ¹³ is, -N = C = N- aryl, -N = C = N- alkyl, -N = C = N- cycloalkyl, -N = C = N- ^{aralkyl, -NCO,} -NHCONHR ^14, -NHCONHR ^{14 R 15, -NHCOOR 16, -NHCOS} -R 14, -COOR 14, -OR 14, _{^{epoxy, -N (R 14) 2,}} -SR 14, -OH, -NH 2, a -NHR ^14.

R ¹⁴ and R ¹⁵ are the same or different and are C ₁ -C ₂₀ alkyl, C ₃ -C ₂₀ cycloalkyl, C ₇ -C ₁₈ aralkyl, oligo / polyethylene glycols and / or oligo / polypropylene glycol. It is kind.

R ¹⁶ has one of the above definitions of R ¹⁴ or is a polyester group or a polyamide group.

In the case of oligomeric carbodiimide, m is 1-5.
In the case of polymer carbodiimide, m is an integer greater than 5. ]
The compound represented by these is mentioned.

  Preferable carbodiimide compounds include aliphatic polycarbodiimide compounds having a plurality of —N═C═N—, more preferably linear aliphatic polymer compounds. Specific examples include aliphatic polycarbodiimide compounds (manufactured by Nisshinbo Chemical Co., Ltd .: Elasto Stub H01).

  As the usage-amount of a carbodiimide compound, the range of 0.1-15 weight part is mentioned with respect to 100 weight part of oligomers which have (A) (meth) acryloyl group, for example, Preferably 0.5-12 weight part is mentioned. More preferably, 1-10 weight part is mentioned.

  As described in Examples 9 to 11 described later, when the photocurable sealing material described in [1] was stored at 23 ° C., it was stable for one month but then gelled. When a carbodiimide compound is added to this material, it is stable for 6 months or more and has excellent storage stability. Moreover, there was almost no influence on the physical properties of the photocuring property and the sealing material produced by photocuring. The present inventors confirmed that the reaction between the active thiol group and the double bond contained in the ene-thiol-based photocurable resin material progresses during storage and gels, and the carbodiimide compound becomes the most active thiol group. It is presumed that the storage stabilization effect by the carbodiimide compound is produced by preferentially binding and inactivating. In addition, it has not been known so far that the carbodiimide compound has an effect of improving the storage stability of the ene-thiol-based photocurable resin material, and this effect cannot be easily recalled by those skilled in the art. Absent.

  Said carbodiimide compound can also be used as a stabilizer for ene-thiol-based photocurable resin materials. Examples of the ene-thiol-based photocurable sealing material include those generally known. For example, the ene-thiol-based photocurable sealing material described in [1], and Patent Documents 3 to 8 are described. And a photo-curable resin material. The amount of the carbodiimide compound added to the ene-thiol-based photocurable resin material is appropriately changed with reference to the amount used for the ene-thiol-based photocurable sealing material described in [1]. be able to.

(E) Photoradical polymerization initiator As the photoradical polymerization initiator, for example, an intramolecular cleavage type and / or a hydrogen abstraction type photoradical polymerization initiator can be used, and preferably an intramolecular cleavage type photoradical polymerization initiation is performed. Agents. As the radical ultraviolet polymerization initiator, known ones can be suitably used. Specific examples include benzoins such as benzoin, benzoin methyl ether, and benzoin ethyl ether, and alkyl ethers thereof; acetophenone, 2, 2 Acetophenones such as -dimethoxy-2-phenylacetophenone, 1,1-dichloroacetophenone, 4- (1-t-butyldioxy-1-methylethyl) acetophenone, diethoxyacetophenone; 2-methylanthraquinone, 2-amylanthraquinone, 2 Anthraquinones such as t-butylanthraquinone and 1-chloroanthraquinone; thioxanthones such as 2,4-dimethylthioxanthone, 2,4-diisopropylthioxanthone and 2-chlorothioxanthone; acetophenone dimethyl Ketals such as tar and benzyldimethyl ketal; benzophenone, 4- (1-t-butyldioxy-1-methylethyl) benzophenone, 3,3 ′, 4,4′-tetrakis (t-butyldioxycarbonyl) benzophenone, etc. Benzophenones; 2-methyl-1- [4- (methylthio) phenyl] -2-morpholino-propan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -1-butanone, etc. Α-aminoalkylphenones of 1-hydroxy-cyclohexyl-phenyl-ketone, 2-hydroxy-1 {4- [4- (2-hydroxy-2-methyl-propionyl) -benzyl] phenyl} -2-methyl- Α such as propan-1-one and 2-hydroxy-2-methyl-1-phenyl-propan-1-one Phenylglyoxylates such as alkylphenylglyoxylate; diethoxyacetophenone; acylphosphine oxides such as 2,4,6-trimethylbenzoylphenylethoxyphosphine oxide; bis (5,2,4- Examples thereof include titanocene compounds such as cyclopentadien-1-yl) -bis (2,6-difluoro-3- (1H-pyrrol-1-yl) -phenyl) titanium, and combinations of two or more thereof.

  Preferred radical photopolymerization initiators include intramolecular molecules such as bezoins, ketals, α-bidoxyalkylphenones, α-aminoalkylphenones, acylphosphine oxides, phenylglyoxylates, acetophenones, and titanocene compounds. A cleavage type photo radical initiator is mentioned.

  Although it does not restrict | limit especially as addition amount of radical photopolymerization initiator, For example, 0.1-10 weight part is mentioned with respect to 100 weight of the total weight of each component of (A)-(C). Preferably, 0.2-5 weight part is mentioned, More preferably, 0.5-2 weight part is mentioned.

(F) Viscosity modifier The viscosity modifier is not particularly limited, but white carbon, colloidal silica, silica sand (silica powder), aerosil, diatomaceous earth, hydrophobic calcium carbonate, glass balloon, glass beads, polyvinylpyrrolidone Etc. These viscosity modifiers may be used alone or in combination of two or more. Preferable viscosity modifiers include inorganic viscosity modifiers such as Aerosil.

  Although it does not restrict | limit especially as an addition amount of a viscosity modifier, For example, 0.1-20 weight part is mentioned with respect to 100 weight of the total weight of each component of (A)-(C), Preferably 0.2-10 weight part is mentioned.

(G) Sensitizers Not only ultraviolet rays but also sensitizers can be added so that they can be cured by using visible light and near infrared rays. Examples of the sensitizer include chalcone derivatives, unsaturated ketones such as dibenzalacetone, 1,2-diketone derivatives such as camphorquinone, benzoin derivatives, fluorene derivatives, naphthoquinone derivatives, anthraquinone derivatives, xanthene derivatives, thioxanthenes. Derivatives, xanthone derivatives, thioxanthone derivatives, coumarin derivatives, ketocoumarin derivatives, cyanine derivatives, merocyanine derivatives, oxonol derivatives and other polymethine dyes, acridine derivatives, azine derivatives, thiazine derivatives, oxazine derivatives, indoline derivatives, azulene derivatives, azulene derivatives, Squarylium derivatives, porphyrin derivatives, tetraphenylporphyrin derivatives, triarylmethane derivatives, tetrabenzoporphyrin derivatives, tetrapyrazinoporphy Gin derivatives, phthalocyanine derivatives, tetraazaporphyrazine derivatives, tetraquinoxalyloporphyrazine derivatives, naphthalocyanine derivatives, subphthalocyanine derivatives, pyrylium derivatives, thiopyrylium derivatives, tetraphyrin derivatives, annulene derivatives, spiropyran derivatives, spirooxazine derivatives, thiospiropyran Derivatives, metal arene complexes, organic ruthenium complexes, and the like can be given.

  The addition amount of the sensitizer is not particularly limited, and examples thereof include 0.1 to 10 parts by weight with respect to 100 parts of the total weight of the components (A) to (C). Preferably 0.2-5 weight part is mentioned, More preferably, 0.5-2 weight part is mentioned.

Other components Other components can be further added to the photocurable sealing material of the present invention. Examples of other components include a sensitizer, a thickener, a polymerization inhibitor, a pigment, an adhesion improver, an antioxidant, a curing accelerator, a filler, a plasticizer, a surfactant, a lubricant, and an antistatic agent. Etc. An appropriate amount of these components can be added depending on the purpose.

Preparation of Photocurable Sealing Material The photocurable sealing material of the present invention comprises (A) an oligomer having a (meth) acryloyl group having a weight average molecular weight of 10,000 to 30,000, and (B) (meth). Acrylate monomer, (C) polythiol compound, and (D) carbodiimide compound, (E) photo radical polymerization initiator, (F) sensitizer, (G) sensitizer, and / or other components as necessary It can be prepared by mixing using a mixer such as a mixer, a ball mill, or a three roll mill at room temperature or under heating conditions. Moreover, it can also adjust as needed by adding a solvent etc. as a diluent, melt | dissolving, and mixing. Examples of the solvent used as the diluent include esters such as ethyl acetate, butyl acetate and isopropyl acetate, ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone, cyclic ethers such as tetrahydrofuran and dioxane, N, N-dimethylformamide and the like. And amides, aromatic hydrocarbons such as toluene, and halogenated hydrocarbons such as methylene chloride.

Application Method of Photocurable Sealing Material The method of curing the photocurable sealing material of the present invention is not particularly limited, and can be carried out, for example, by irradiating energy rays. Examples of the energy rays used include light, radiation, electromagnetic waves, and the like, and specifically, ultraviolet rays, visible light, infrared rays, α rays, β rays, γ rays, electron rays, and the like. From the viewpoint of operability, productivity and economy, it is preferable to use ultraviolet rays. The irradiation time of the energy beam can be appropriately selected depending on the type of energy beam used. As the ultraviolet light source, for example, a light source such as ultra-high pressure mercury, a metal halide light source, a laser, or an LED can be used. When using α-rays, β-rays, γ-rays, electron beams, etc., curing can proceed quickly without the inclusion of a photo-radical polymerization initiator, but photo-radical polymerization is used when ultraviolet rays are used. It is preferred to add an initiator to the photocurable sealing material of the present invention.

The case where the photocurable sealing material of the present invention is applied to a gasket in a housing will be described below. When the casing is composed of two parts that sandwich the gasket, the casing of the present invention can be manufactured according to the following steps (1) to (4).
(1) Uniformly apply a photo-curable sealing material to the groove (gasket application part) of one of the parts;
(2) By irradiating the coated part with ultraviolet rays or the like, the photocurable sealing material is cured to produce a gasket;
(3) Incorporate equipment to be housed inside if necessary; and (4) Fit the other part into that part.

  In the present invention, a “casing” is a box containing a machine or electrical device having some function, which protects the device from impact, pressure, electromagnetic waves, water, dust, light, etc. means. Specifically, electronic products such as a mobile phone, a digital camera, and a video camera, home appliances such as a refrigerator, an air conditioner, and a washing machine, precision devices such as a camera and a watch, and the like can be given. When the sealing material of the present invention is used in a housing, it prevents water, pressure, dust and the like from being mixed, and does not impair the protective action of the housing as a whole.

Characteristics of the sealing material The sealing material of the present invention has a high compression recovery rate, high tensile strength, excellent flexibility, low hardness as required, and thereby excellent sealing characteristics such as airtightness and waterproofness, Furthermore, there is little surface tack. Further, the hardness of the sealing material is preferably 40 or less, more preferably 30 or less, still more preferably 20 or less, and particularly preferably 15 or less in terms of a value measured with a type A durometer. In order to reduce the hardness, by increasing the content of the (B) (meth) acrylate monomer and / or the (C) polythiol compound, the desired hardness can be adjusted. They are described in more detail in the examples.

  Hereinafter, the present invention will be described in detail with reference examples and examples. In addition, these Examples are provided only for description of this invention, and do not limit this invention at all.

[Test method]
(1) Tensile strength at break and elongation rate A sheet of a cured UV resin having a thickness of 1 mm was punched into a dumbbell No. 3 type according to JIS K 6251 to obtain a test piece. A tensile test was conducted under the conditions of a test temperature of 23 ° C. and a tensile speed of 100 m / min, and the tensile strength and elongation at break were measured.
-Tensile strength at break [MPa] = Breaking strength / Film cross-sectional area-Elongation rate [%] = (Amount of elongation at break / Standard length [20 mm]) x 100
(2) Hardness In accordance with JIS K 6253, the thickness of the UV resin cured product is about 1 mm, and the thickness is about 10 mm. The specimen is a type A durometer at 23 ° C. under 50-60% RH. Shore hardness A was measured with a polymer meter.
(3) Compression recovery property A sheet of a cured UV resin cut to 25 mm square is laminated to a thickness of about 5 mm, and the specimen is compressed by 25% and 50%, respectively, and tested in accordance with JIS K 6253. The compression recovery property was measured at a temperature of 70 ° C.
(4) Surface tack After UV curing, a 1 mm thick sheet of cured UV resin was allowed to stand at 23 ° C. for 2 hours, and then the tack on the irradiated surface was evaluated by touch. The evaluation was as follows.

○: Almost no tack △: Some tack is present ×: Strong tack is present (5) Storage stability A UV curable resin is placed in a light-shielded container and left in a 40 ° C. environment for 2 weeks. The viscosity at 0.5 rpm was measured using a Brookfield viscometer, and it was confirmed whether the change rate was within 10% compared to the initial viscosity.

  Moreover, the storage stability in Table 3 was evaluated based on the viscosity change and state change of the viscosity after standing at each temperature for each time.

○: Change rate within 10% with respect to initial viscosity ×: Significant thickening and occurrence of gelation
Example 1
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, As tetrafunctional (secondary) polythiol A, a pentaerythritol tetrakis (3-mercaptobutyrate) having a molecular weight of 544.8 (manufactured by Showa Denko KK: Karenz MT PE1), 8 parts by weight, a viscosity modifier (manufactured by Nippon Aerosil Co., Ltd.) : AEROSIL 200) After 8 parts by weight of the mixture were uniformly vacuum mixed with a stirrer, 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan KK: Irgacure 184) was used as a photopolymerization initiator, and 1 part as a stabilizer. , 4-Benzenediol (manufactured by Mitsui Chemicals, Inc .: Hydroquinone) 0.02 It was added in an amount unit, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 2
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, As tetrafunctional (secondary) polythiol A, a pentaerythritol tetrakis (3-mercaptobutyrate) having a molecular weight of 544.8 (manufactured by Showa Denko KK: Karenz MT PE1), a viscosity modifier (manufactured by Nippon Aerosil Co., Ltd.) : AEROSIL 200) After 8 parts by weight of the mixture were uniformly vacuum mixed with a stirrer, 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan KK: Irgacure 184) was used as a photopolymerization initiator, and 1 part as a stabilizer. , 4-Benzenediol (Mitsui Chemicals, Inc .: Hydroquinone) 0.0 Was added parts by weight were uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 3
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, As tetrafunctional (primary) polythiol B, pentaerythritol tetrakis (3-mercaptopropionate) having a molecular weight of 488.64 (manufactured by SC Organic Chemical Co., Ltd .: PEMP), 17 parts by weight, viscosity modifier (manufactured by Nippon Aerosil Co., Ltd.) : AEROSIL 200) After 8 parts by weight of the mixture were uniformly vacuum mixed with a stirrer, 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan KK: Irgacure 184) was used as a photopolymerization initiator, and 1 part as a stabilizer. , 4-Benzenediol (manufactured by Mitsui Chemicals, Inc .: Hydroquinone) 0.02 Part by weight was added, and the mixture was uniformly mixed and degassed with a stirrer to obtain a photocurable sealing material of the present invention.

Example 4
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, As tetrafunctional (secondary) polythiol A, pentaerythritol tetrakis (3-mercaptobutyrate) having a molecular weight of 544.8 (manufactured by Showa Denko KK: Karenz MT PE1), 17 parts by weight, viscosity modifier (manufactured by Nippon Aerosil Co., Ltd.) : AEROSIL 200) After 8 parts by weight of the mixture were uniformly vacuum mixed with a stirrer, 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan KK: Irgacure 184) was used as a photopolymerization initiator, and 1 part as a stabilizer. , 4-Benzenediol (Mitsui Chemicals, Inc .: Hydroquinone) 0.0 Was added parts by weight were uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 5
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, 1,3,5-tris (3-mercaptobutyloxyethyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) having a molecular weight of 567.7 as trifunctional (secondary) polythiol C -After uniformly mixing 8 parts by weight of Trion (manufactured by Showa Denko KK: Karenz MT NR1) and 8 parts by weight of a viscosity modifier (manufactured by Nippon Aerosil Co., Ltd .: AEROSIL 200) with a stirrer, as a photopolymerization initiator 2 parts by weight of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184), 1, - benzenediol (Mitsui Chemicals Co., Ltd.: hydroquinone) was added 0.02 part by weight, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 6
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, 1,3,5-tris (3-mercaptobutyloxyethyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) having a molecular weight of 567.7 as trifunctional (secondary) polythiol C -After uniformly mixing 12 parts by weight of Trion (manufactured by Showa Denko KK: Karenz MT NR1) and 8 parts by weight of a viscosity modifier (manufactured by Nippon Aerosil Co., Ltd .: AEROSIL200) with a stirrer, as a photopolymerization initiator 2 parts by weight of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan Ltd .: Irgacure 184), 1 as a stabilizer 4- benzenediol (Mitsui Chemicals Co., Ltd.: hydroquinone) was added 0.02 part by weight, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 7
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, 1,4-bis (3-mercaptobutyryloxy) butane (made by Showa Denko KK: Karenz MT BD1) with a molecular weight of 294.4 as a bifunctional (secondary) polythiol D, a viscosity modifier (Nippon Aerosil) (Product: AEROSIL200) 8 parts by weight uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan, Inc .: Irgacure 184) as a photopolymerization initiator, As stabilizer, 0.04 part by weight of 1,4-benzenediol (manufactured by Mitsui Chemicals, Inc .: hydroquinone) And pressurized, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material of the present invention.

Example 8
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 18,000 (manufactured by Nippon Gosei Kagaku: UV-3000B), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as an acrylic monomer, Dipentaerythritol hexakis (3-meltcaptopropionate) having a molecular weight of 783.03 as hexafunctional (primary) polythiol E (SC Organic Chemical Co., Ltd .: DPMP) 11 parts by weight, viscosity modifier (Nippon Aerosil Co., Ltd.) ): AEROSIL 200) After 8 parts by weight of the mixture were uniformly vacuum-mixed with a stirrer, 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184) as a photopolymerization initiator, stabilizer 1,4-benzenediol (manufactured by Mitsui Chemicals, Inc .: hydroquinone) 02 parts by weight was added, and the mixture was uniformly mixed and degassed with a stirrer to obtain a photocurable sealing material of the present invention.

Comparative Example 1
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 13,000 (Nippon Kayaku Co., Ltd .: KAYARAD UX-3204), phenol acrylate as an acrylic monomer (Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) After 60 parts by weight and 8 parts by weight of a viscosity modifier (manufactured by Nippon Aerosil Co., Ltd .: AEROSIL 200) were uniformly vacuum mixed with a stirrer, 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan Ltd.) was used as a photopolymerization initiator. ): Irgacure 184) 2 parts by weight, 0.02 part by weight of 1,4-benzenediol (manufactured by Mitsui Chemicals, Inc .: hydroquinone) as a stabilizer is added, uniformly mixed and defoamed with a stirrer, and light cured A sex sealing material was obtained.

Comparative Example 2
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 13,000 (Nippon Kayaku Co., Ltd .: KAYARAD UX-3204), phenol acrylate as an acrylic monomer (Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) 60 parts by weight, 5 parts by weight of pentaerythritol tetrakis (3-mercaptobutyrate) (manufactured by Showa Denko KK: Karenz MT PE1) having a molecular weight of 544.8 as a tetrafunctional (secondary) polythiol A, a viscosity modifier (Nippon Aerosil) (Product: AEROSIL200) 8 parts by weight uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan, Inc .: Irgacure 184) as a photopolymerization initiator, 1,4-Benzenediol (made by Mitsui Chemicals, Inc .: Hydroquino) as a stabilizer ) Was added 0.02 part by weight, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material.

Comparative Example 3
100 parts by weight of urethane acrylic oligomer A having a weight average molecular weight of 13,000 (Nippon Kayaku Co., Ltd .: KAYARAD UX-3204), phenol acrylate as an acrylic monomer (Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) 60 parts by weight, 38 parts by weight of tetraerythritol tetrakis (3-mercaptobutyrate) (manufactured by Showa Denko KK: Karenz MT PE1) having a molecular weight of 544.8 as a tetrafunctional (secondary) polythiol A, a viscosity modifier (Nippon Aerosil) (Product: AEROSIL200) 8 parts by weight uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (BASF Japan, Inc .: Irgacure 184) as a photopolymerization initiator, 1,4-Benzenediol (made by Mitsui Chemicals, Inc .: Hydroxy) as a stabilizer Down) were added 0.02 part by weight, and uniformly mixed degassed stirrer, to obtain a photocurable sealing material.

Comparative Example 4
100 parts by weight of urethane acrylic oligomer B having a weight average molecular weight of 4,500 (manufactured by Kyoeisha Co., Ltd .: UF-8001G), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as the acrylic monomer 7 parts by weight of pentaerythritol tetrakis (3-mercaptobutyrate) (manufactured by Showa Denko KK: Karenz MT PE1) having a molecular weight of 544.8 as a tetrafunctional (secondary) polythiol A, a viscosity modifier (Nippon Aerosil Co., Ltd.) Product: 8 parts by weight of AEROSIL 200) were uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184) as a photopolymerization initiator, as a stabilizer. 0.02 part by weight of 1,4-benzenediol (manufactured by Mitsui Chemicals, Inc .: hydroquinone) Was added and uniformly mixed and defoamed with a stirrer to obtain a photocurable sealing material.

Comparative Example 5
100 parts by weight of urethane acrylic oligomer B having a weight average molecular weight of 4,500 (manufactured by Kyoeisha Co., Ltd .: UF-8001G), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as the acrylic monomer 17 parts by weight of pentaerythritol tetrakis (3-mercaptobutyrate) (manufactured by Showa Denko KK: Karenz MT PE1) having a molecular weight of 544.8 as a tetrafunctional (secondary) polythiol A, a viscosity modifier (Nippon Aerosil Co., Ltd.) Product: 8 parts by weight of AEROSIL 200) were uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184) as a photopolymerization initiator, as a stabilizer. 1,2-benzenediol (by Mitsui Chemicals, Inc .: hydroquinone) 0.02 weight Then, the mixture was uniformly mixed and defoamed with a stirrer to obtain a photocurable sealing material.

Comparative Example 6
100 parts by weight of urethane acrylic oligomer B having a weight average molecular weight of 4,500 (manufactured by Kyoeisha Co., Ltd .: UF-8001G), 60 parts by weight of phenol acrylate (manufactured by Daiichi Pharmaceutical Co., Ltd .: New Frontier PHE-2) as the acrylic monomer As tetrafunctional (secondary) polythiol A, a pentaerythritol tetrakis (3-mercaptobutyrate) having a molecular weight of 544.8 (manufactured by Showa Denko KK: Karenz MT PE1), 23 parts by weight, viscosity modifier (Nippon Aerosil Co., Ltd.) Product: 8 parts by weight of AEROSIL 200) were uniformly mixed with a stirrer, and then 1 part of 1-hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184) as a photopolymerization initiator, as a stabilizer. 1,2-benzenediol (by Mitsui Chemicals, Inc .: hydroquinone) 0.02 weight Then, the mixture was uniformly mixed and defoamed with a stirrer to obtain a photocurable sealing material.

Comparative Example 7
100 parts by weight of urethane acrylic oligomer B having a weight average molecular weight of 4,500 (manufactured by Kyoeisha Co., Ltd .: UF-8001G), pentaerythritol tetrakis (3-mercaptobutyrate) having a molecular weight of 544.8 as a tetrafunctional (secondary) polythiol A (Showa Denko Co., Ltd .: Karenz MT PE1) 4 parts by weight and a viscosity modifier (Nippon Aerosil Co., Ltd .: AEROSIL200) 8 parts by weight were uniformly vacuum mixed with a stirrer and then 1- 2 parts by weight of hydroxy-cyclohexyl-phenyl-ketone (manufactured by BASF Japan Ltd .: Irgacure 184) and 0.02 part by weight of 1,4-benzenediol (manufactured by Mitsui Chemicals, Inc .: hydroquinone) as a stabilizer are added. By uniformly mixing and defoaming with a stirrer, a photocurable sealing material was obtained.

Test example 1
After each of the photocurable sealing materials obtained in Examples 1 to 8 and Comparative Examples 1 to 7 was formed into a sheet having a thickness of about 1 mm, an electrodeless metal halide lamp type UV irradiation apparatus (FOTOCURE TFL- manufactured by Tokyo Hoton) was used. 150. Base material-lamp distance d = 53 mm, UV-A wave integrated light quantity: about 7000 mJ / cm ² ) was cured by UV irradiation to prepare a sealing material, respectively. The integrated light quantity was measured with UV Power Pack manufactured by EIT.

  About the obtained sealing material, the physical property was tested with the said test method. The results are described below.

  The sealing material of the present invention obtained in Examples 1 to 8 has a high compression recovery rate, a high tensile strength, an excellent flexibility, and a low hardness as compared with the comparative example. In addition, thiol addition shows good adhesion, low surface tack, and good storage stability.

  The experiments of Comparative Examples 4 to 7 were further tried to approximate the experiment described in Table 2 of Patent Document 7 as much as possible. Low. In Comparative Example 6, the amount of the thiol compound was increased in order to make the hardness as low as possible. However, the hardness still exceeded 50 and could not be used as a casing sealing material.

  As shown in Comparative Examples 1 and 2, when the polythiol compound is not added and the acryloyl group / thiol group ratio is 100 / 5n or less, the hardness is high and good softness cannot be obtained, and the elongation is low. On the contrary, as shown in Comparative Example 3, when the polythiol compound was added until the acryloyl group / thiol group ratio exceeded 100 / 25n, sufficient cohesive force was not obtained and the film physical properties could not be measured.

Examples 9-11
In Example 4, a polycarbodiimide compound (Nisshinbo Chemical Co., Ltd .: Elasto Stub H01) was added in the amount shown in Table 3 below to obtain a photocurable sealing material of the present invention.

  From this experiment, it is understood that storage stability is remarkably improved by adding a carbodiimide compound. For example, when the photocurable sealing material of Example 4 was stored at 23 ° C., it was stable for one month but then gelled. The photocurable sealing materials of Examples 9 to 11 to which a carbodiimide compound was added were stable for 6 months or more and had excellent storage stability. In addition, since the temperature of 23 degreeC is an upper limit temperature in cold dark place preservation | save, the stability in this temperature is equivalent to the storage stability in cold dark place preservation | save.

  According to the present invention, it has a high compression recovery rate, high tensile strength, excellent flexibility, low hardness as required, and thereby has excellent sealing properties such as airtightness and waterproofness, and also has less surface tack. Material is provided. In addition, a photocurable sealing material having storage stability can be provided by easily and instantaneously curing to the deep part of the photocurable sealing material to produce the same sealing material.

Claims (11)

(A) A photocurable sealing material comprising an oligomer having a (meth) acryloyl group having a weight average molecular weight of 10,000 to 30,000, (B) a (meth) acrylate monomer, and (C) a polythiol compound. Because
(A) 5-100 parts by weight of (B) (meth) acrylate is included with respect to 100 parts by weight of the oligomer having a (meth) acryloyl group,
(A) A photocurable sealing material comprising a (meth) acryloyl group contained in both an oligomer having a (meth) acryloyl group and a (B) (meth) acrylate monomer and a mercapto group of (C) a polythiol compound. The ratio of the number present is 100: 5n to 100: 25n (n is the number of mercapto groups in one molecule of the polythiol compound).
Photo-curable sealing material.   2. The photocurable sealing material according to claim 1, further comprising (D) a carbodiimide compound in an amount of 0.1 to 15 parts by weight based on 100 parts by weight of the oligomer (A) having a (meth) acryloyl group. (C) the polythiol compound has 2 to 6 mercapto groups in one molecule, two carbon atoms that are bonded to the carbon atom to which the mercapto group is bonded, according to claim 1 or 2 Photo-curable sealing material.   (C) The photocurable sealing material according to claim 1 or 2, wherein the polythiol compound is an ester produced from a polyhydric alcohol having 2 to 6 hydroxyl groups and β-mercaptobutanoic acid.   The photocurable sealing material according to claim 1, wherein the (B) (meth) acrylate monomer is monofunctional (meth) acrylate, polyfunctional (meth) acrylate, or a combination thereof.   (A) Oligomer having (meth) acryloyl group is urethane (meth) acrylate oligomer, polyester (meth) acrylate oligomer, polyether (meth) acrylate oligomer, epoxy (meth) acrylate oligomer, conjugated diene polymer system The photocurable sealing material according to any one of claims 1 to 5, which is at least one selected from the group comprising (meth) acrylate oligomers and hydrogenated products thereof.   The photocurable sealing material according to any one of claims 1 to 6, further comprising (E) a photoradical polymerization initiator and / or (F) a viscosity modifier.   The sealing method by photocuring the photocurable sealing material in any one of Claims 1-7.   The sealing material produced | generated by photocuring the photocurable sealing material in any one of Claims 1-7.   The housing | casing using the sealing material produced | generated by photocuring the photocurable sealing material in any one of Claims 1-7.   The stabilizer for ene-thiol type photocurable resin materials containing a carbodiimide compound.