JP5624729B2 - Resist composition and resist pattern forming method - Google Patents

Description

  The present invention relates to a resist composition, a method for forming a resist pattern using the resist composition, a novel compound useful as an acid generator for the resist composition, and an acid generator.

In lithography technology, for example, a resist film made of a resist material is formed on a substrate, and the resist film is selectively exposed to light such as light or an electron beam through a mask on which a predetermined pattern is formed. And a development process is performed to form a resist pattern having a predetermined shape on the resist film. A resist material in which the exposed portion changes to a property that dissolves in the developer is referred to as a positive type, and a resist material that changes to a property in which the exposed portion does not dissolve in the developer is referred to as a negative type.
In recent years, in the manufacture of semiconductor elements and liquid crystal display elements, pattern miniaturization has been rapidly progressing due to advances in lithography technology.
As a technique for miniaturization, the wavelength of an exposure light source is generally shortened. Specifically, conventionally, ultraviolet rays typified by g-line and i-line have been used. Currently, mass production of semiconductor elements using a KrF excimer laser or an ArF excimer laser has been started. Further, studies have been made on F2 excimer lasers having a shorter wavelength than these excimer lasers, electron beams, EUV (extreme ultraviolet rays), X-rays, and the like.

  Resist materials are required to have lithography characteristics such as sensitivity to these exposure light sources and resolution capable of reproducing a pattern with fine dimensions. As a resist material that satisfies such requirements, a chemically amplified resist containing a base resin whose solubility in an alkaline developer is changed by the action of an acid and an acid generator that generates an acid upon exposure is used. For example, a positive chemically amplified resist contains, as a base resin, a resin that increases solubility in an alkaline developer by the action of an acid and an acid generator. When the acid is generated, the exposed portion becomes soluble in the alkaline developer.

Up to now, as a base resin for chemically amplified resist, polyhydroxystyrene (PHS) having high transparency with respect to KrF excimer laser (248 nm) and a resin whose hydroxyl group is protected with an acid dissociable, dissolution inhibiting group (PHS resin) Has been used. However, since the PHS resin has an aromatic ring such as a benzene ring, the transparency to light having a wavelength shorter than 248 nm, for example, 193 nm, is not sufficient. For this reason, a chemically amplified resist having a PHS resin as a base resin component has drawbacks such as low resolution in a process using 193 nm light, for example. Therefore, as a resist base resin currently used in ArF excimer laser lithography and the like, it has a structural unit generally derived from a (meth) acrylic acid ester in the main chain because it is excellent in transparency near 193 nm. Resin (acrylic resin) is used. In the case of the positive type, such a resin includes a structural unit derived from a (meth) acrylic acid ester containing a tertiary alkyl ester type acid dissociable, dissolution inhibiting group containing an aliphatic polycyclic group, for example, 2-alkyl. Resins having structural units derived from 2-adamantyl (meth) acrylate or the like are mainly used (see, for example, Patent Document 1).
The “(meth) acrylic acid ester” means one or both of an acrylic acid ester having a hydrogen atom bonded to the α-position and a methacrylic acid ester having a methyl group bonded to the α-position. “(Meth) acrylate” means one or both of an acrylate having a hydrogen atom bonded to the α-position and a methacrylate having a methyl group bonded to the α-position. “(Meth) acrylic acid” means one or both of acrylic acid having a hydrogen atom bonded to the α-position and methacrylic acid having a methyl group bonded to the α-position.

On the other hand, various acid generators used in chemically amplified resists have been proposed so far, such as onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, Diazomethane acid generators, nitrobenzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators and the like are known.
Currently, an onium salt-based acid generator having an onium ion (cation) such as triphenylsulfonium in the cation portion is used as the acid generator (see, for example, Patent Document 2).

JP 2003-241385 A JP 2005-037888 A

J. et al. Vac. Sci. Technol. B24 (2006) 3055

As further advances in lithography technology and miniaturization of resist patterns continue in the future, there is a further demand for resist materials to form resist patterns with higher resolution while maintaining good lithography characteristics. It is growing.
In lithography by EUV, the reaction mechanism is different from that of normal optical lithography (Non-patent Document 1), and the target is to form a fine pattern of several tens of nanometers. As the resist pattern size becomes smaller in this way, the resist composition is exposed to light. High sensitivity to the light source is very important. However, in the resist composition containing the conventional onium salt acid generator as described above, the sensitivity to an exposure light source such as EUV is not sufficiently high, and desired resolution and lithography characteristics can be obtained. It is difficult and further improvement is demanded.

  The present invention has been made in view of the above circumstances, and is a novel compound useful as an acid generator for a resist composition, an acid generator using the compound, and a resist composition containing the acid generator And a resist pattern forming method using the resist composition.

In order to solve the above problems, the present invention employs the following configuration.
That is, the first aspect of the present invention is a resist composition comprising a base material component (A) whose solubility in an alkaline developer is changed by the action of an acid, and an acid generator component (B) that generates an acid upon exposure. A thing,
The acid generator component (B) contains an acid generator (B1) composed of a compound represented by the following general formula (b1-1).

［式中、Ｒ^１はアリーレン基またはアルキレン基であり、Ｒ^２、Ｒ^３はそれぞれ独立にアリール基またはアルキル基であり、Ｒ^２、Ｒ^３は相互に結合して式中のイオウ原子と共に環を形成していてもよく、Ｒ^１〜Ｒ^３のうち少なくとも１つは、アリーレン基またはアリール基であり、Ｙ^１はカルボニル基を含むｎ価の連結基であり、ｎは２または３であり、Ｘ⁻はアニオンである。］

[Wherein R ¹ is an arylene group or an alkylene group, R ² and R ³ each independently represents an aryl group or an alkyl group, and R ² and R ³ are bonded to each other to form a ring together with a sulfur atom in the formula And at least one of R ^{1 to} R ³ is an arylene group or an aryl group, Y ¹ is an n-valent linking group containing a carbonyl group , and n is 2 or 3. , X ⁻ is an anion. ]

  According to a second aspect of the present invention, there is provided a step of forming a resist film on a support using the resist composition of the first aspect, a step of exposing the resist film, and an alkali development of the resist film. A resist pattern forming method including a step of forming a resist pattern.

In the present specification and claims, the “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups unless otherwise specified.
Further, the “alkylene group” includes linear, branched and cyclic divalent saturated hydrocarbon groups unless otherwise specified.
The “lower alkyl group” is an alkyl group having 1 to 5 carbon atoms.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with a halogen atom, and examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
“Aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
The “structural unit” means a monomer unit (monomer unit) constituting a polymer compound (polymer, copolymer).
“Exposure” is a concept including general irradiation of radiation.

  According to the present invention, a novel compound useful as an acid generator for a resist composition, an acid generator comprising the compound, a resist composition containing the acid generator, and a resist pattern using the resist composition A forming method can be provided.

≪Resist composition≫
The resist composition according to the first aspect of the present invention comprises a base component (A) (hereinafter referred to as “component (A)”) whose solubility in an alkaline developer is changed by the action of an acid, and an acid upon exposure. Contains the generated acid generator component (B) (hereinafter referred to as “component (B)”).
When a resist film formed using such a resist composition is selectively exposed at the time of resist pattern formation, an acid is generated from the component (B), and the acid has a solubility in the alkaline developer of the component (A). Change. As a result, while the solubility of the exposed portion of the resist film in the alkali developer changes, the solubility of the unexposed portion in the alkali developer does not change. However, in the case of the negative type, the unexposed portion is dissolved and removed to form a resist pattern.
The resist composition of the present invention may be a negative resist composition or a positive resist composition.
The resist composition of the present invention preferably further contains a nitrogen-containing organic compound component (D) in addition to the components (A) and (B).

<(A) component>
As the component (A), organic compounds that are usually used as base material components for chemically amplified resists can be used singly or in combination of two or more.
Here, the “base material component” is an organic compound having a film forming ability, and an organic compound having a molecular weight of 500 or more is preferably used. When the molecular weight of the organic compound is 500 or more, the film-forming ability is improved and a nano-level resist pattern is easily formed.
The organic compound having a molecular weight of 500 or more includes a low molecular weight organic compound having a molecular weight of 500 or more and less than 2000 (hereinafter referred to as “low molecular compound”) and a high molecular weight resin having a molecular weight of 2000 or more (polymer material). Broadly divided. As the low molecular weight compound, a non-polymer is usually used. In the case of a resin (polymer, copolymer), a polystyrene-reduced mass average molecular weight by GPC (gel permeation chromatography) is used as the “molecular weight”. Hereinafter, the term “resin” refers to a resin having a molecular weight of 2000 or more.
As the component (A), a resin component whose alkali solubility is changed by the action of an acid can be used, and a low molecular compound component whose alkali solubility is changed by the action of an acid can also be used.

When the resist composition of the present invention is a “negative resist composition”, a base component that is soluble in an alkali developer is used as the component (A), and the negative resist composition further includes a crosslinking agent component. Is blended.
In such a negative resist composition, when an acid is generated from the component (B) by exposure, the acid acts to cause cross-linking between the base component and the cross-linking agent component, resulting in poor solubility in an alkali developer. Change. Therefore, in the formation of a resist pattern, when a resist film obtained by applying the negative resist composition on a support is selectively exposed, the exposed portion turns into poorly soluble in an alkaline developer, while not yet exposed. Since the exposed portion remains soluble in the alkali developer and does not change, a resist pattern can be formed by alkali development.
As the component (A) of the negative resist composition, a resin that is soluble in an alkali developer (hereinafter referred to as “alkali-soluble resin”) is usually used.
Examples of the alkali-soluble resin include a resin having a unit derived from at least one selected from α- (hydroxyalkyl) acrylic acid or a lower alkyl ester of α- (hydroxyalkyl) acrylic acid, and JP-A-2005-336442. Alternatively, a resin having a fluorinated alcohol disclosed in JP-A-2006-259582 is preferable because it can form a good resist pattern with little swelling. Α- (Hydroxyalkyl) acrylic acid includes acrylic acid in which a hydrogen atom is bonded to the α-position carbon atom to which the carboxy group is bonded, and a hydroxyalkyl group (preferably having 1 carbon atom) in the α-position carbon atom. One or both of [alpha] -hydroxyalkylacrylic acids to which (5) hydroxyalkyl groups) are attached.
As the crosslinking agent component, for example, it is usually preferable to use an amino crosslinking agent such as glycoluril having a methylol group or an alkoxymethyl group because a good resist pattern with less swelling can be formed. It is preferable that the compounding quantity of a crosslinking agent component is 1-50 mass parts with respect to 100 mass parts of alkali-soluble resin.

When the resist composition of the present invention is a “positive resist composition”, the component (A) is a base material component (hereinafter referred to as “(A ′) component”) whose solubility in an alkali developer is increased by the action of acid. Is used).
The component (A ′) is hardly soluble in an alkali developer before exposure. When an acid is generated from the component (B) by exposure, the solubility in the alkali developer is increased by the action of the acid. Therefore, in the formation of the resist pattern, when the resist film obtained by applying the positive resist composition on the support is selectively exposed, the exposed portion becomes insoluble to soluble in an alkaline developer. On the other hand, since the unexposed portion remains hardly soluble in alkali and does not change, a resist pattern can be formed by alkali development.

In the resist composition of the present invention, the component (A) is preferably a base material component ((A ′) component) whose solubility in an alkaline developer is increased by the action of an acid. That is, the resist composition of the present invention is preferably a positive resist composition.
The component (A ′) may be a resin component (A1) (hereinafter sometimes referred to as “component (A1)”) whose solubility in an alkaline developer is increased by the action of an acid. It may be a low molecular compound component (A2) (hereinafter sometimes referred to as “component (A2)”) whose solubility in an alkali developer increases, or a mixture thereof.

[(A1) component]
As the component (A1), resin components (base resins) that are usually used as base components for chemically amplified resists can be used singly or in combination of two or more.
In the present invention, the component (A1) preferably has a structural unit derived from an acrylate ester.
Here, in the present specification and claims, the “structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid esters” include those in which a hydrogen atom is bonded to the carbon atom at the α-position, and those in which a substituent (atom or group other than a hydrogen atom) is bonded to the carbon atom in the α-position. Include concepts. Examples of the substituent include a lower alkyl group and a halogenated lower alkyl group.
Note that the α-position (α-position carbon atom) of a structural unit derived from an acrylate ester means a carbon atom to which a carbonyl group is bonded, unless otherwise specified.
In the acrylate ester, as the lower alkyl group as a substituent at the α-position, specifically, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, tert-butyl group, pentyl group, Examples include lower linear or branched alkyl groups such as isopentyl group and neopentyl group.
Specific examples of the halogenated lower alkyl group include groups in which some or all of the hydrogen atoms of the above-mentioned “lower alkyl group as a substituent at the α-position” are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
In the present invention, the α-position of the acrylate ester is preferably a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group, and is a hydrogen atom, a lower alkyl group or a fluorinated lower alkyl group. In view of industrial availability, a hydrogen atom or a methyl group is most preferable.

In the resist composition of the present invention, it is particularly preferable that the component (A1) has a structural unit (a1) derived from an acrylate ester containing an acid dissociable, dissolution inhibiting group.
In addition to the structural unit (a1), the component (A1) preferably further has a structural unit (a2) derived from an acrylate ester containing a lactone-containing cyclic group.
The component (A1) is derived from an acrylate ester containing a polar group-containing aliphatic hydrocarbon group in addition to the structural unit (a1) or in addition to the structural units (a1) and (a2). It is preferable to have a structural unit (a3).
In addition to the structural unit (a1), the component (A1) preferably further includes a structural unit (a5) having a polymerizable group, an aromatic hydrocarbon group, and a hydroxyl group.

(Structural unit (a1))
The structural unit (a1) is a structural unit derived from an acrylate ester containing an acid dissociable, dissolution inhibiting group.
The acid dissociable, dissolution inhibiting group in the structural unit (a1) has an alkali dissolution inhibiting property that makes the entire component (A1) difficult to dissolve in an alkali developer before dissociation, and dissociates with an acid. This increases the solubility of the entire component in an alkaline developer, and those that have been proposed as acid dissociable, dissolution inhibiting groups for base resins for chemically amplified resists can be used. In general, a group that forms a cyclic or chain tertiary alkyl ester with a carboxy group in (meth) acrylic acid or the like; an acetal-type acid dissociable, dissolution inhibiting group such as an alkoxyalkyl group is widely known. .

Here, the “tertiary alkyl ester” is an ester formed by replacing a hydrogen atom of a carboxy group with a chain or cyclic alkyl group, and the carbonyloxy group (—C (═O ) -O-) shows a structure in which the tertiary carbon atom of the chain-like or cyclic alkyl group is bonded to the terminal oxygen atom. In this tertiary alkyl ester, when an acid acts, a bond is cut between an oxygen atom and a tertiary carbon atom.
The chain or cyclic alkyl group may have a substituent.
Hereinafter, a group that is acid dissociable by constituting a carboxy group and a tertiary alkyl ester is referred to as a “tertiary alkyl ester type acid dissociable, dissolution inhibiting group” for convenience.
Examples of the tertiary alkyl ester type acid dissociable, dissolution inhibiting group include an aliphatic branched acid dissociable, dissolution inhibiting group and an acid dissociable, dissolution inhibiting group containing an aliphatic cyclic group.

Here, the term “aliphatic branched” in the claims and the specification means having a branched structure having no aromaticity.
The structure of the “aliphatic branched acid dissociable, dissolution inhibiting group” is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group.
The “hydrocarbon group” may be either saturated or unsaturated, but is usually preferably saturated.
As the aliphatic branched acid dissociable, dissolution inhibiting group, a tertiary alkyl group having 4 to 8 carbon atoms is preferable, and specific examples include a tert-butyl group, a tert-pentyl group, and a tert-heptyl group. .

The “aliphatic cyclic group” means a monocyclic group or a polycyclic group having no aromaticity.
The “aliphatic cyclic group” in the structural unit (a1) may or may not have a substituent. Examples of the substituent include a lower alkyl group having 1 to 5 carbon atoms, a lower alkoxy group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated lower alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, an oxygen atom (= O) and the like.
The basic ring structure excluding the substituent of the “aliphatic cyclic group” is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group. The “hydrocarbon group” may be either saturated or unsaturated, but is usually preferably saturated. The “aliphatic cyclic group” is preferably a polycyclic group.
Examples of the aliphatic cyclic group include monocycloalkanes, bicycloalkanes, tricycloalkanes, tetracycloalkanes which may or may not be substituted with a lower alkyl group, a fluorine atom or a fluorinated alkyl group. And groups obtained by removing one or more hydrogen atoms from a polycycloalkane. More specifically, monocycloalkanes such as cyclopentane and cyclohexane, and groups obtained by removing one or more hydrogen atoms from polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane are exemplified. .

  Examples of the acid dissociable, dissolution inhibiting group containing an aliphatic cyclic group include a group having a tertiary carbon atom on the ring skeleton of a cyclic alkyl group. Specifically, 2-methyl-2 -Adamantyl group, 2-ethyl-2-adamantyl group, etc. are mentioned. Alternatively, in the structural units represented by the following general formulas (a1 ″ -1) to (a1 ″ -6), an adamantyl group like a group bonded to an oxygen atom of a carbonyloxy group (—C (O) —O—) An aliphatic cyclic group such as a cyclohexyl group, a cyclopentyl group, a norbornyl group, a tricyclodecanyl group, or a tetracyclododecanyl group, and a branched alkylene group having a tertiary carbon atom bonded thereto. Groups.

［式中、Ｒは水素原子、低級アルキル基またはハロゲン化低級アルキル基を示し；Ｒ^１５、Ｒ^１６はアルキル基（直鎖状、分岐鎖状のいずれでもよく、好ましくは炭素数１〜５である）を示す。］

[Wherein, R represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group; R ¹⁵ and R ^{16 each} represents an alkyl group (which may be linear or branched, and preferably has 1 to 5 carbon atoms. Is). ]

  In the general formulas (a1 ″ -1) to (a1 ″ -6), the lower alkyl group or halogenated lower alkyl group of R is a lower alkyl group or halogenated lower alkyl which may be bonded to the α-position of the acrylate ester. It is the same as the alkyl group.

The “acetal-type acid dissociable, dissolution inhibiting group” is generally bonded to an oxygen atom by substituting a hydrogen atom at the terminal of an alkali-soluble group such as a carboxy group or a hydroxyl group. When an acid is generated by exposure, the acid acts to break the bond between the acetal acid dissociable, dissolution inhibiting group and the oxygen atom to which the acetal acid dissociable, dissolution inhibiting group is bonded.
Examples of the acetal type acid dissociable, dissolution inhibiting group include a group represented by the following general formula (p1).

［式中、Ｒ^１’，Ｒ^２’はそれぞれ独立して水素原子または低級アルキル基を表し、ｎは０〜３の整数を表し、Ｙは低級アルキル基または脂肪族環式基を表す。］

[Wherein, R ¹ ′ and R ² ′ each independently represents a hydrogen atom or a lower alkyl group, n represents an integer of 0 to 3, and Y represents a lower alkyl group or an aliphatic cyclic group. ]

In the above formula, n is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 0.
Examples of the lower alkyl group for R ¹ ′ and R ² ′ include the same lower alkyl groups as those described above for R. A methyl group or an ethyl group is preferable, and a methyl group is most preferable.
In the present invention, it is preferable that at least one of R ¹ ′ and R ² ′ is a hydrogen atom. That is, the acid dissociable, dissolution inhibiting group (p1) is preferably a group represented by the following general formula (p1-1).

［式中、Ｒ^１’、ｎ、Ｙは上記と同様である。］

[Wherein R ¹ ′, n and Y are the same as described above. ]

Examples of the lower alkyl group for Y include the same lower alkyl groups as those described above for R.
The aliphatic cyclic group for Y can be appropriately selected from monocyclic or polycyclic aliphatic cyclic groups that have been proposed in a number of conventional ArF resists. For example, the above “aliphatic ring” Examples thereof are the same as those in the formula group.

  Examples of the acetal type acid dissociable, dissolution inhibiting group also include a group represented by the following general formula (p2).

［式中、Ｒ^１７、Ｒ^１８はそれぞれ独立して直鎖状または分岐鎖状のアルキル基または水素原子であり、Ｒ^１９は直鎖状、分岐鎖状または環状のアルキル基である。または、Ｒ^１７およびＲ^１９がそれぞれ独立に直鎖状または分岐鎖状のアルキレン基であって、Ｒ^１７の末端とＲ^１９の末端とが結合して環を形成していてもよい。］

[Wherein, R ¹⁷ and R ¹⁸ each independently represent a linear or branched alkyl group or a hydrogen atom, and R ¹⁹ represents a linear, branched or cyclic alkyl group. Alternatively, R ¹⁷ and R ¹⁹ may be each independently a linear or branched alkylene group, and the end of R ^{17 and} the end of R ¹⁹ may be bonded to form a ring. ]

In R ¹⁷ and R ¹⁸ , the alkyl group preferably has 1 to 15 carbon atoms, may be linear or branched, and is preferably an ethyl group or a methyl group, and most preferably a methyl group. In particular, it is preferable that one of R ¹⁷ and R ¹⁸ is a hydrogen atom and the other is a methyl group.
R ¹⁹ is a linear, branched or cyclic alkyl group, preferably having 1 to 15 carbon atoms, and may be any of linear, branched or cyclic.
When R ¹⁹ is linear or branched, it preferably has 1 to 5 carbon atoms, more preferably an ethyl group or a methyl group, and most preferably an ethyl group.
When R ¹⁹ is cyclic, it preferably has 4 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, one or more polycycloalkanes such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorine atom or a fluorinated alkyl group, are included. Examples include a group excluding a hydrogen atom. Specific examples include monocycloalkanes such as cyclopentane and cyclohexane, and groups obtained by removing one or more hydrogen atoms from polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.
In the above formula, R ¹⁷ and R ¹⁹ are each independently a linear or branched alkylene group (preferably an alkylene group having 1 to 5 carbon atoms), and the end of R ¹⁹ and R ¹⁷ The terminal may be bonded.
In this case, a cyclic group is formed by R ¹⁷ , R ¹⁹ , the oxygen atom to which R ¹⁹ is bonded, and the carbon atom to which the oxygen atom and R ¹⁷ are bonded. The cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

  As the structural unit (a1), one or more selected from the group consisting of structural units represented by the following general formula (a1-0-1) and structural units represented by the following general formula (a1-0-2): Is preferably used.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基を示し、Ｘ^１は酸解離性溶解抑制基を示す。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, and X ¹ represents an acid dissociable, dissolution inhibiting group. ]

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基を示し、Ｘ^２は酸解離性溶解抑制基を示し、Ｙ^２は２価の連結基を示す。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, X ² represents an acid dissociable, dissolution inhibiting group, and Y ² represents a divalent linkage. Indicates a group. ]

In general formula (a1-0-1), the lower alkyl group or halogenated lower alkyl group for R is the same as the lower alkyl group or halogenated lower alkyl group that may be bonded to the α-position of the acrylate ester. .
X ¹ is not particularly limited as long as it is an acid dissociable, dissolution inhibiting group, and examples thereof include the above-described tertiary alkyl ester type acid dissociable, dissolution inhibiting group and acetal type acid dissociable, dissolution inhibiting group. And tertiary alkyl ester type acid dissociable, dissolution inhibiting groups are preferred.

In general formula (a1-0-2), R is the same as defined above.
X ² is the same as X ¹ in formula (a1-0-1).

Examples of the divalent linking group for Y ² include an alkylene group, a divalent aliphatic cyclic group, and a divalent linking group containing a hetero atom.
As the aliphatic cyclic group, those similar to the explanation of the “aliphatic cyclic group” can be used except that a group in which two or more hydrogen atoms are removed is used.
When Y ² is an alkylene group, it is preferably 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, particularly preferably 1 to 4 carbon atoms, and 1 to 3 carbon atoms. Most preferably it is.
When Y ² is a divalent aliphatic cyclic group, a group in which two or more hydrogen atoms have been removed from cyclopentane, cyclohexane, norbornane, isobornane, adamantane, tricyclodecane, or tetracyclododecane is particularly preferable. .
When Y ² is a divalent linking group containing a hetero atom, examples of the divalent linking group containing a hetero atom include —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O—, —C (═O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group or an acyl group), —S—. , —S (═O) ₂ —, —S (═O) ₂ —O—, “—AO (oxygen atom) —B— (wherein A and B each independently have a substituent) And a combination of an alkylene group and a divalent linking group containing a hetero atom.

When Y ² is —NH—, the substituent (alkyl group, acyl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and more preferably 1 to 5 carbon atoms. It is particularly preferred that
When Y ² is “A—O—B”, A and B are each independently a divalent hydrocarbon group which may have a substituent.
The hydrocarbon group having “substituent” means that part or all of the hydrogen atoms in the hydrocarbon group are substituted with groups or atoms other than hydrogen atoms.

  The hydrocarbon group in A may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity.

The aliphatic hydrocarbon group for A may be saturated or unsaturated, and is usually preferably saturated.
Specific examples of the aliphatic hydrocarbon group for A include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in the structure.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 8, still more preferably 2 to 5, and most preferably 2.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group, an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [— (CH ₂ ) ₃ -], tetramethylene group _{[- (CH 2) 4 -} ], a pentamethylene group _{[- (CH 2) 5 -} ] , and the like.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - Alkylethylene groups such as CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH ₃ ) CH ₂ —; Alkyl trimethylene groups such as —CH (CH ₃ ) CH ₂ CH ₂ —, —CH ₂ CH (CH ₃ ) CH ₂ —; —CH (CH ₃ ) CH ₂ CH ₂ CH ₂ —, —CH ₂ CH (CH _{3) CH} 2 CH ₂ - alkyl, such as alkyl tetramethylene group such as Such as an alkylene group, and the like. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.
The chain-like aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated lower alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, an oxygen atom (═O), and the like.

Examples of the aliphatic hydrocarbon group containing a ring include a cyclic aliphatic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and the cyclic aliphatic hydrocarbon group described above as a chain-like aliphatic group. And a group bonded to the terminal of the aromatic hydrocarbon group or interposed in the middle of the chain-like aliphatic hydrocarbon group.
The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The cyclic aliphatic hydrocarbon group may be a polycyclic group or a monocyclic group. As the monocyclic group, a group in which two hydrogen atoms have been removed from a monocycloalkane having 3 to 6 carbon atoms is preferable, and examples of the monocycloalkane include cyclopentane and cyclohexane.
As the polycyclic group, a group in which two hydrogen atoms are removed from a polycycloalkane having 7 to 12 carbon atoms is preferable. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, tetra And cyclododecane.
The cyclic aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a lower alkyl group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated lower alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, an oxygen atom (= O), and the like.

  A is preferably a linear aliphatic hydrocarbon group, more preferably a linear alkylene group, still more preferably a linear alkylene group having 2 to 5 carbon atoms, and most preferably an ethylene group.

Examples of the hydrocarbon group for B include the same divalent hydrocarbon groups as those described above for A.
B is preferably a linear or branched aliphatic hydrocarbon group, particularly preferably a methylene group or an alkylmethylene group.
The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group.

  More specifically, examples of the structural unit (a1) include structural units represented by the following general formulas (a1-1) to (a1-4).

［式中、Ｘ’は第３級アルキルエステル型酸解離性溶解抑制基を表し、Ｙは炭素数１〜５の低級アルキル基、または脂肪族環式基を表し；ｎは０〜３の整数を表し；Ｙ^２は２価の連結基を表し；Ｒは前記と同じであり、Ｒ^１’、Ｒ^２’はそれぞれ独立して水素原子または炭素数１〜５の低級アルキル基を表す。］

[Wherein, X ′ represents a tertiary alkyl ester type acid dissociable, dissolution inhibiting group, Y represents a lower alkyl group having 1 to 5 carbon atoms, or an aliphatic cyclic group; n represents an integer of 0 to 3] Y ² represents a divalent linking group; R is the same as defined above; R ¹ ′ and R ² ′ each independently represent a hydrogen atom or a lower alkyl group having 1 to 5 carbon atoms. ]

In the formula, X 'include the same tertiary alkyl ester-type acid dissociable, dissolution inhibiting groups as those described above for X ^{1.
R 1 ', R 2',} n, as the Y, respectively, ^{R 1} in the general formula listed in the description of "acetal-type acid dissociable, dissolution inhibiting group" described above ^{(p1) ', R 2'} , n, Y The same thing is mentioned.
The Y ^2, the same groups as those described above for ^{Y 2} in the general formula (a1-0-2).

Specific examples of the structural units represented by the general formulas (a1-1) to (a1-4) are shown below.
In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a1), one type may be used alone, or two or more types may be used in combination.
Among these, the structural unit represented by general formula (a1-1), (a1-2) or (a1-3) is preferable, and specifically, (a1-1-1) to (a1-1-4). , (A1-1-20) to (a1-1-23), (a1-2-1) to (a1-2-24) and (a1-3-25) to (a1-3-28) It is more preferable to use at least one selected from the group.
Furthermore, as the structural unit (a1), those represented by the following general formula (a1-1-01) that include structural units of the formula (a1-1-1) to the formula (a1-1-3), In the following general formula (a1-1-02) including the structural units of formulas (a1-1-16) to (a1-1-17) and formulas (a1-1-20) to (a1-1-23) What is represented, what is represented by the following general formula (a1-3-01) including the structural units of formulas (a1-3-25) to (a1-3-26), and formula (a1-3-27) ) To (a1-3-28) and those represented by the following general formula (a1-3-02) or the formulas (a1-3-29) to (a1-3-30) The following general formula (a1-3-03) including units is also preferable.

[式中、Ｒはそれぞれ独立に水素原子、低級アルキル基またはハロゲン化低級アルキル基を示し、Ｒ^１１は低級アルキル基を示す。Ｒ^１２は低級アルキル基を示す。ｈは１〜６の整数を表す。]

[Wherein, R independently represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group, and R ¹¹ represents a lower alkyl group. R ¹² represents a lower alkyl group. h represents an integer of 1 to 6. ]

In general formula (a1-1-01), R is the same as defined above. The lower alkyl group for R ^{11 is the same as} the lower alkyl group for R, and is preferably a methyl group, an ethyl group, or an isopropyl group.

In general formula (a1-1-02), R is the same as defined above. The lower alkyl group for R ^{12 is the same as} the lower alkyl group for R, and is preferably a methyl group, an ethyl group, or an isopropyl group. h is preferably 1 or 2, and most preferably 2.

[式中、Ｒは水素原子、低級アルキル基またはハロゲン化低級アルキル基を示し；Ｒ^１４は低級アルキル基であり、Ｒ^１３は水素原子またはメチル基であり、ａは１〜１０の整数である。]

[Wherein, R represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group; R ¹⁴ represents a lower alkyl group, R ¹³ represents a hydrogen atom or a methyl group, and a represents an integer of 1 to 10. . ]

[式中、Ｒは水素原子、低級アルキル基またはハロゲン化低級アルキル基を示し；Ｒ^１４は低級アルキル基であり、Ｒ^１３は水素原子またはメチル基であり、ａは１〜１０の整数であり、ｎ’は１〜６の整数である。]

[Wherein, R represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group; R ¹⁴ represents a lower alkyl group, R ¹³ represents a hydrogen atom or a methyl group, and a represents an integer of 1 to 10. , N ′ is an integer of 1-6. ]

［式中、Ｒは前記と同じであり、Ｙ^２’およびＹ^２”はそれぞれ独立して２価の連結基であり、Ｘ’は酸解離性溶解抑制基であり、ｎは０〜３の整数である。］

[Wherein, R is the same as defined above, Y ² ′ and Y ² ″ each independently represent a divalent linking group, X ′ represents an acid dissociable, dissolution inhibiting group, and n represents 0 to 3] It is an integer.]

In the general formulas (a1-3-01) to (a1-3-03), R is the same as described above.
R ¹³ is preferably a hydrogen atom.
The lower alkyl group for R ^{14 is the same as} the lower alkyl group for R, and is preferably a methyl group or an ethyl group.
n ′ is preferably 1 or 2, and most preferably 2.
a is preferably an integer of 1 to 8, more preferably an integer of 2 to 5, and most preferably 2.
As the divalent linking group for Y ² ′ and Y ² ″, the same groups as those described above for Y ² in formula (a1-3) can be given.
Y ² ′ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and even more preferably a linear alkylene group. Among these, a linear alkylene group having 1 to 5 carbon atoms is preferable, and a methylene group and an ethylene group are most preferable.
Y ² ″ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and still more preferably a linear alkylene group. A linear alkylene group of 1 to 5 is preferable, and a methylene group and an ethylene group are most preferable.
Examples of the acid dissociable, dissolution inhibiting group in X ′ include the same groups as described above, and are preferably tertiary alkyl ester type acid dissociable, dissolution inhibiting groups, and (i) the monovalent aliphatic cyclic group described above. A group having a tertiary carbon atom on the ring skeleton of the group is more preferable, and among them, the group represented by the general formula (1-1) is preferable.
n is an integer of 0 to 3, and n is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 1.

  In the component (A1), the proportion of the structural unit (a1) is preferably 10 to 80 mol%, more preferably 20 to 70 mol%, more preferably 25 to 50 mol%, based on all structural units constituting the component (A1). Is more preferable. By setting it to the lower limit value or more, a pattern can be easily obtained when the resist composition is used, and by setting it to the upper limit value or less, it is possible to balance with other structural units.

(Structural unit (a2))
The structural unit (a2) is a structural unit derived from an acrylate ester containing a lactone-containing cyclic group.
Here, the lactone-containing cyclic group refers to a cyclic group containing one ring (lactone ring) containing an —O—C (O) — structure. The lactone ring is counted as the first ring, and when it is only the lactone ring, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure.
When the component (A1) is used for forming a resist film, the lactone cyclic group of the structural unit (a2) increases the adhesion of the resist film to the substrate or has an affinity for a developer containing water. It is effective in raising.

As the structural unit (a2), any unit can be used without any particular limitation.
Specifically, the lactone-containing monocyclic group is a group in which one hydrogen atom is removed from a 4- to 6-membered ring lactone, such as a group in which one hydrogen atom is removed from β-propiolactone, or γ-butyrolactone. Examples thereof include a group in which one hydrogen atom has been removed, and a group in which one hydrogen atom has been removed from δ-valerolactone. Examples of the lactone-containing polycyclic group include groups in which one hydrogen atom has been removed from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring.

  More specifically, examples of the structural unit (a2) include structural units represented by general formulas (a2-1) to (a2-5) shown below.

［式中、Ｒは水素原子、低級アルキル基またはハロゲン化低級アルキル基であり；Ｒ’はそれぞれ独立に水素原子、炭素数１〜５のアルキル基、炭素数１〜５のアルコキシ基または−ＣＯＯＲ”であり、Ｒ”は水素原子またはアルキル基であり；Ｒ^２９は単結合または２価の連結基であり、ｓ”は０または１〜２の整数であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり；ｍは０または１の整数である。］

[Wherein, R represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group; R ′ each independently represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or —COOR; R "is a hydrogen atom or an alkyl group; R ²⁹ is a single bond or a divalent linking group; s" is 0 or an integer of 1 to 2; A "is an oxygen atom or a sulfur atom. An alkylene group having 1 to 5 carbon atoms, an oxygen atom or a sulfur atom, and m is an integer of 0 or 1. ]

R in the general formulas (a2-1) to (a2-5) is the same as R in the structural unit (a1).
Examples of the alkyl group having 1 to 5 carbon atoms of R ′ include a methyl group, an ethyl group, a propyl group, an n-butyl group, and a tert-butyl group.
Examples of the alkoxy group having 1 to 5 carbon atoms of R ′ include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, and a tert-butoxy group.
R ′ is preferably a hydrogen atom in view of industrial availability.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, and more preferably 1 to 5 carbon atoms.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Or a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorinated alkyl group Specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane, or a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Etc.
A ″ is preferably an alkylene group having 1 to 5 carbon atoms or —O—, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group.
R ²⁹ is a single bond or a divalent linking group. The divalent linking group is the same as the divalent linking group described for Y ² in the general formula (a1-0-2), and among them, an alkylene group and an ester bond (—C (═O ) -O-) or a combination thereof. The alkylene group as the divalent linking group for R ²⁹ is more preferably a linear or branched alkylene group. Specifically, the same as the linear alkylene group and the branched alkylene group mentioned as the aliphatic hydrocarbon group for A in Y ² can be used.
s ″ is preferably an integer of 1 to 2.
Specific examples of the structural units represented by the general formulas (a2-1) to (a2-5) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

In the component (A1), as the structural unit (a2), one type of structural unit may be used, or two or more types may be used in combination.
As the structural unit (a2), at least one selected from the group consisting of structural units represented by the general formulas (a2-1) to (a2-5) is preferable, and the general formulas (a2-1) to (a2) -3) At least 1 sort (s) selected from the group which consists of a structural unit represented by 3) is more preferable. Among these, from structural units represented by chemical formulas (a2-1-1), (a2-2-1), (a2-2-7), (a2-3-1) and (a2-3-5) It is preferable to use at least one selected from the group consisting of

  The proportion of the structural unit (a2) in the component (A1) is preferably 5 to 60 mol%, more preferably 10 to 50 mol%, with respect to the total of all structural units constituting the component (A1). 50 mol% is more preferable. By making it the lower limit value or more, the effect of containing the structural unit (a2) can be sufficiently obtained, and by making it the upper limit value or less, it is possible to balance with other structural units.

(Structural unit (a3))
The structural unit (a3) is a structural unit derived from an acrylate ester containing a polar group-containing aliphatic hydrocarbon group.
When the component (A1) has the structural unit (a3), the hydrophilicity of the component (A) is increased, the affinity with the developer is increased, the alkali solubility in the exposed area is improved, and the resolution is improved. Contributes to improvement.
Examples of the polar group include a hydroxyl group, a cyano group, a carboxy group, and a hydroxyalkyl group in which part of hydrogen atoms of an alkyl group is substituted with a fluorine atom, and a hydroxyl group is particularly preferable.
Examples of the aliphatic hydrocarbon group include a linear or branched hydrocarbon group having 1 to 10 carbon atoms (preferably an alkylene group) and a polycyclic aliphatic hydrocarbon group (polycyclic group). It is done.
As the polycyclic group, for example, a resin for a resist composition for ArF excimer laser can be appropriately selected from among many proposed ones. The polycyclic group preferably has 7 to 30 carbon atoms.
Among them, a structural unit derived from an acrylate ester containing an aliphatic polycyclic group containing a hydroxyalkyl group in which a part of hydrogen atoms of a hydroxyl group, a cyano group, a carboxy group, or an alkyl group is substituted with a fluorine atom Is more preferable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from bicycloalkane, tricycloalkane, tetracycloalkane and the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among these polycyclic groups, there are groups in which two or more hydrogen atoms have been removed from adamantane, groups in which two or more hydrogen atoms have been removed from norbornane, and groups in which two or more hydrogen atoms have been removed from tetracyclododecane. Industrially preferable.

  The structural unit (a3) is derived from a hydroxyethyl ester of acrylic acid when the hydrocarbon group in the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group having 1 to 10 carbon atoms. When the hydrocarbon group is a polycyclic group, the structural unit represented by the following formula (a3-1), the structural unit represented by the following formula (a3-2), and the following formula The structural unit represented by (a3-3) is preferable.

[式中、Ｒは前記と同じであり、ｊは１〜３の整数であり、ｋは１〜３の整数であり、ｔ’は１〜３の整数であり、ｌは１〜５の整数であり、ｓは１〜３の整数である。]

[Wherein, R is the same as above, j is an integer of 1 to 3, k is an integer of 1 to 3, t ′ is an integer of 1 to 3, and l is an integer of 1 to 5] And s is an integer of 1 to 3. ]

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl group is bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group is bonded to the 3-position of the adamantyl group.
j is preferably 1, and a hydroxyl group bonded to the 3-position of the adamantyl group is particularly preferred.

  In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.

  In formula (a3-3), t ′ is preferably 1. l is preferably 1. s is preferably 1. In these, a 2-norbornyl group or a 3-norbornyl group is preferably bonded to the terminal of the carboxy group of acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

As the structural unit (a3), one type may be used alone, or two or more types may be used in combination.
In the component (A1), the proportion of the structural unit (a3) is preferably 5 to 50 mol%, more preferably 5 to 40 mol%, based on all structural units constituting the component (A1). More preferred is ˜25 mol%. By setting it to the lower limit value or more, the effect of containing the structural unit (a3) can be sufficiently obtained, and by setting it to the upper limit value or less, it is possible to balance with other structural units.

(Structural unit (a5))
The structural unit (a5) is a structural unit having a polymerizable group, an aromatic hydrocarbon group, and a hydroxyl group.
The polymerizable group is a group having an ethylenic double bond (vinyl group, (meth) acryloyl group, cyclic olefin). Examples of the aromatic hydrocarbon group include an aromatic hydrocarbon group for R ⁵⁸ described later, and benzene, naphthalene, anthracene and the like are preferable.
When the structural unit (a5) is a resist composition, moderate alkali solubility can be obtained. In addition, lithography properties such as resolution and sensitivity are improved. Further, when KrF, electron beam, or EUV is used as the exposure wavelength, it is preferable to have the structural unit (a5) because lithography properties such as sensitivity and resolution are improved.
Examples of the structural unit (a5) include structural units represented by the following general formula (a5-1) or (a5-2).

［式中、Ｒは前記と同様であり、Ｒ^５５〜Ｒ^５６はそれぞれ独立して、ハロゲン原子、炭素数１〜５のアルキル基、炭素数１〜５のアルコキシ基、または炭素数１〜５のハロゲン化アルキル基であり、ｐは１〜３の整数であり、ｑは０〜４の整数であり、ｐ＋ｑは１〜５であり；Ｙ^３は単結合または−Ｃ（＝Ｏ）−Ｏ−Ｒ^５８−（Ｒ^５８は単結合または２価の連結基である。）であり；Ｒ^５７は単結合またはアルキレン基であり、ｘは１〜３の整数であり、ｙは０〜６の整数であり、ｘ＋ｙは１〜７である。］

[Wherein, R is the same as defined above, and R ^{55 to} R ⁵⁶ each independently represent a halogen atom, an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or 1 to 5 carbon atoms. Wherein p is an integer of 1 to 3, q is an integer of 0 to 4, p + q is 1 to 5; Y ³ is a single bond or —C (═O) —O. -R ⁵⁸ - ^{(. R 58} represents a single bond or a divalent linking group) ^{be; R 57} is a single bond or an alkylene group, x is an integer of 1 to 3, y is 0 to 6 It is an integer and x + y is 1-7. ]

In formula (a5-1), R is the same as defined above, and is preferably a hydrogen atom or a methyl group.
p is an integer of 1 to 3, q is an integer of 0 to 4, and p + q is 1 to 5. However, p + q is 1-5.
p is most preferably 1.
q is preferably an integer of 0 to 2, more preferably 0 or 1, and industrially particularly preferably 0.

In formula (a5-1), the bonding position of the hydroxyl group in the phenyl group is not particularly limited. When p is 1, any of the o-position, m-position and p-position may be used, and the p-position is preferred because it is readily available and inexpensive. When p is 2 or 3, any bonding position can be combined.
Further, the bonding position of R ^{55 in} the phenyl group is not particularly limited. When q is 1, any of the o-position, m-position and p-position may be used. When q is an integer greater than or equal to 2, arbitrary bond positions can be combined.
When q is an integer greater than or equal to 2, several ^R55 may be the same respectively, and may differ.

R ⁵⁵ is a halogen atom, an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms.
Examples of the halogen atom for R ⁵⁵ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
As the alkyl group for R ⁵⁵ , an alkyl group having 1 to 5 carbon atoms is preferable. The alkyl group is preferably a linear or branched alkyl group, and specifically includes a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, and pentyl. Group, isopentyl group, neopentyl group and the like.
The alkoxy group of R ^55, preferably an alkoxy group having 1 to 5 carbon atoms. The alkoxy group is preferably a linear or branched alkoxy group, and specific examples include a methoxy group, an ethoxy group, an n-propoxy group, an i-propoxy group, and an n-butoxy group.
The halogenated alkyl group for R ⁵⁵ is preferably a fluorinated alkyl group. In the fluorinated alkyl group, the alkyl groups include alkyl groups of 1 to 5 carbon atoms for R ^55.

  In formula (a5-2), R is the same as defined above.

Y ³ is a single bond or —C (═O) —O—R ⁵⁸ — (R ⁵⁸ is a single bond or a divalent linking group).
Preferred examples of the divalent linking group for R ⁵⁸ include a divalent hydrocarbon group which may have a substituent, a divalent linking group containing a hetero atom, and the like.
In the “divalent hydrocarbon group optionally having substituent (s)” in R ^58, the hydrocarbon group has “substituent” means that part or all of the hydrogen atoms in the hydrocarbon group are It means substituted with a group or atom other than a hydrogen atom.
The hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity.
The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated.
More specifically, examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 8, still more preferably 1 to 5, and most preferably 1 to 2.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.
The chain-like aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, an oxygen atom (= O), and the like.

Examples of the aliphatic hydrocarbon group containing a ring in the structure include a cyclic aliphatic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and the cyclic aliphatic hydrocarbon group described above. Examples thereof include a group bonded to the terminal of the chain aliphatic hydrocarbon group or interposed in the middle of the chain aliphatic hydrocarbon group.
The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The cyclic aliphatic hydrocarbon group may be a polycyclic group or a monocyclic group. As the monocyclic group, a group in which two hydrogen atoms have been removed from a monocycloalkane having 3 to 6 carbon atoms is preferable, and examples of the monocycloalkane include cyclopentane and cyclohexane.
As the polycyclic group, a group in which two hydrogen atoms are removed from a polycycloalkane having 7 to 12 carbon atoms is preferable. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, tetra And cyclododecane.
The cyclic aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (= O).

Examples of the aromatic hydrocarbon group include aromatics of monovalent aromatic hydrocarbon groups such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, and a phenanthryl group. A divalent aromatic hydrocarbon group obtained by removing one hydrogen atom from the nucleus of the aromatic hydrocarbon;
An aromatic hydrocarbon group in which a part of carbon atoms constituting the ring of the divalent aromatic hydrocarbon group is substituted with a heteroatom such as an oxygen atom, a sulfur atom or a nitrogen atom;
An arylalkyl group such as benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc., and a hydrogen atom from the nucleus of the aromatic hydrocarbon In addition, an aromatic hydrocarbon group or the like from which one is removed may be mentioned.
The aromatic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (= O).

In the “divalent linking group containing a heteroatom” in R ^58, the heteroatom in the “divalent linking group containing a heteroatom” is an atom other than a carbon atom and a hydrogen atom, such as an oxygen atom, a nitrogen atom, A sulfur atom, a halogen atom, etc. are mentioned.
Specific examples of the divalent linking group containing a hetero atom include —O—, —C (═O) —, —C (═O) —O—, and a carbonate bond (—O—C (═O) —. O-), -NH-, ^-NR04 ( ^R04 is an alkyl group)-, -NH-C (= O)-, = N- and the like. Moreover, the combination etc. of these "divalent coupling groups containing a hetero atom" and a bivalent hydrocarbon group are mentioned. Examples of the divalent hydrocarbon group include the same hydrocarbon groups that may have a substituent as described above, and a linear or branched aliphatic hydrocarbon group is preferable.

The divalent linking group for R ⁵⁸ is preferably an alkylene group, an ester bond (—C (═O) —O—), or a combination thereof.
The alkylene group for R ⁵⁸ is more preferably a linear or branched alkylene group. Specifically, the same as the linear alkylene group and branched alkylene group mentioned as the aliphatic hydrocarbon group for R ²⁰ can be used.
As the linear alkylene group for R ⁵⁸ , a methylene group or an ethylene group is preferable, and a methylene group is particularly preferable.
As the branched alkylene group for R ⁵⁸ , an alkylmethylene group or an alkylethylene group is preferable, and —CH (CH ₃ ) —, —C (CH ₃ ) ₂ —, or —C (CH ₃ ) ₂ CH ₂ — is Particularly preferred.
Examples of the combination of an alkylene group and an ester bond (-C (= O) -O-) , ^{e.g., -R 58 '-C (= O} ) -O -, - R 58' -C (= O) -O- R ⁵⁸ ″ — and the like. In the formula, R ⁵⁸ ′ and R ⁵⁸ ″ are each independently an alkylene group. As the alkylene group for R ⁵⁸ ′ and R ⁵⁸ ″, the same alkylene groups as those described above for R ⁵⁸ can be used.

R ⁵⁸ may be a single bond or a divalent linking group. A single bond or an alkylene group is preferred, and a single bond is most preferred.

In the present invention, Y ³ is a single bond, —C (═O) —O— or —C (═O) —O—R ⁵⁸ ′ — (R ⁵⁸ ′ is as defined above). Preferably, a single bond or —C (═O) —O— is more preferable, and a single bond is most preferable.

R ⁵⁷ is a single bond or an alkylene group.
The alkylene group for R ⁵⁷ may be linear, branched or cyclic, and is preferably linear or branched. The alkylene group preferably has 1 to 12 carbon atoms, and specific examples thereof include a group in which one hydrogen atom has been removed from the alkyl group described above for R ¹ .
R ⁵⁷ is preferably a single bond or a methylene group, and most preferably a single bond.
When x is an integer of 2 or more, the plurality of R ⁵⁷ may be the same or different. For example, if x is 2, the two ^-R 57 -OH, one of ^{R 57} is a hydrogen atom, the other of ^{R 57} may be an alkylene group.

R ⁵⁶ is a halogen atom, an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, and is the same as described for R ⁵⁵ .
When y is an integer of 2 or more, the plurality of R ⁵⁶ may be the same or different.

x is an integer of 1 to 3, and y is an integer of 0 to 6. However, x + y is 1-7.
x is most preferably 1.
y is preferably an integer of 0 to 2, preferably 0 or 1, and particularly preferably 0.

In formula (a5-2), Y ³ (the carbon atom to which R is bonded when Y ³ is a single bond) may be bonded to the 1-position of the naphthalene ring or bonded to the 2-position. Also good.
The bonding position of —R ⁵⁷ —OH in the naphthalene ring is not particularly limited. When Y ³ (the carbon atom to which R is bonded when Y ³ is a single bond) is bonded to the 1- or 2-position of the naphthalene ring, any one of the 5-8th positions of the naphthalene ring is preferable. In particular, when x is 1, any one of 5 to 7 positions of the naphthalene ring is preferable, and 5 or 6 positions are preferable. When x is an integer greater than or equal to 2, arbitrary bond positions can be combined.

  As the structural unit (a5-2), structural units represented by general formulas (a5-8) to (a5-16) shown below are particularly desirable.

［式中、ＲおよびＹ^３はそれぞれ前記と同じである。］

[Wherein, R and Y ³ are the same as defined above. ]

  The proportion of the structural unit (a5) in the component (A1) is preferably 5 to 85 mol%, more preferably 30 to 80 mol%, based on the total of all structural units constituting the component (A). 60 to 75 mol% is most preferable. Within this range, moderate alkali solubility is obtained when a resist composition is obtained. In addition, lithography properties such as resolution and sensitivity are improved.

(Structural unit (a4))
The component (A1) may contain other structural units (a4) other than the structural units (a1) to (a3) and (a5) as long as the effects of the present invention are not impaired.
The structural unit (a4) is not particularly limited as long as it is another structural unit that is not classified into the structural units (a1) to (a3) and (a5) described above. For ArF excimer laser and KrF excimer laser A number of hitherto known materials can be used as resist resins such as (preferably for ArF excimer laser).
As the structural unit (a4), for example, a structural unit derived from an acrylate ester containing an acid non-dissociable aliphatic polycyclic group, a structural unit derived from a styrene monomer, a vinyl naphthalene monomer, or the like. Is preferred. Examples of the polycyclic group include those exemplified in the case of the structural unit (a1), and for ArF excimer laser and KrF excimer laser (preferably for ArF excimer laser). A number of hitherto known materials can be used as the resin component of the resist composition.
In particular, at least one selected from a tricyclodecanyl group, an adamantyl group, a tetracyclododecanyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include those represented by the following general formulas (a4-1) to (a4-5).

［式中、Ｒは前記と同じである。］

[Wherein, R is the same as defined above. ]

  When the structural unit (a4) is contained in the component (A1), the structural unit (a4) is preferably contained in an amount of 1 to 30 mol% based on the total of all the structural units constituting the component (A1). 5 to 30 mol% is more preferable.

In the present invention, the component (A1) is preferably a polymer having the structural unit (a1).
Examples of such a polymer include a copolymer having the structural units (a1) and (a2), a copolymer having the structural units (a1) and (a3), and the structural units (a1), (a2), and (a3). ), Copolymers having structural units (a1) and (a5), and the like. More specifically, for example, a copolymer composed of the structural units (a1), (a2) and (a3), a copolymer composed of the structural units (a1) and (a5), and the like are preferable.

In the component (A), as the component (A1), one type may be used alone, or two or more types may be used in combination.
In the present invention, as the component (A1), those containing the following combinations of structural units are particularly preferable.

［式中、Ｒ、Ｒ’は前記と同じであり、複数のＲはそれぞれ同じであっても異なっていてもよい。Ｒ^１０は低級アルキル基であり、ｎ１５は０又は１である。］

[Wherein, R and R ′ are the same as described above, and a plurality of R may be the same or different. R ¹⁰ is a lower alkyl group, and n15 is 0 or 1. ]

In formula (A1-11), the lower alkyl group for R ^{10 is the same as} the lower alkyl group for R, preferably a methyl group or an ethyl group, and most preferably a methyl group.
In formula (A1-12), R ′ is preferably a hydrogen atom or a methyl group, and particularly preferably a hydrogen atom. R is preferably a hydrogen atom or a methyl group, and particularly preferably a methyl group. n15 is particularly preferably 0.
In formula (A1-12), the bonding position between adamantane and —CH ₂ —O— (CH ₂ ) _n15 — is preferably the 1st or 2nd position of adamantane, and more preferably the 2nd position.

The component (A1) can be obtained by polymerizing a monomer for deriving each structural unit by a known radical polymerization using a radical polymerization initiator such as azobisisobutyronitrile (AIBN).
Further, for the component (A1), in the polymerization, a chain transfer agent such as HS—CH ₂ —CH ₂ —CH ₂ —C (CF ₃ ) ₂ —OH is used in combination, so that the terminal A —C (CF ₃ ) ₂ —OH group may be introduced into the. As described above, a copolymer introduced with a hydroxyalkyl group in which a part of hydrogen atoms of an alkyl group is substituted with a fluorine atom reduces development defects and LER (line edge roughness: uneven unevenness of line side walls). It is effective in reducing
A commercially available monomer may be used as the monomer for deriving each structural unit, or the monomer may be synthesized using a known method.

The mass average molecular weight (Mw) of the component (A1) (polystyrene conversion standard by gel permeation chromatography) is not particularly limited, preferably 2000 to 50000, more preferably 3000 to 30000, most preferably 5000 to 20000. preferable. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
Further, the dispersity (Mw / Mn) of the component (A1) is not particularly limited, and is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and 1.2 to 2 .5 is most preferred.
In addition, Mn shows a number average molecular weight.

  The proportion of the component (A1) in the component (A) is preferably 25% by mass or more, more preferably 50% by mass, further preferably 75% by mass, and 100% by mass with respect to the total mass of the component (A). May be. When the proportion is 25% by mass or more, a resist pattern having a good shape can be easily obtained, and lithography properties are improved.

[(A2) component]
The component (A2) is preferably a low molecular compound having a molecular weight of 500 or more and less than 2500 and having an acid dissociable, dissolution inhibiting group and a hydrophilic group as exemplified in the description of the component (A1). Specifically, a compound in which a part of hydrogen atoms of a hydroxyl group of a compound having a plurality of phenol skeletons is substituted with the acid dissociable, dissolution inhibiting group can be mentioned.
The component (A2) is, for example, a part of the hydrogen atom of the hydroxyl group of a low molecular weight phenol compound known as a sensitizer in a non-chemically amplified g-line or i-line resist or a heat resistance improver. Those substituted with a soluble dissolution inhibiting group are preferred and can be arbitrarily used.
Examples of such low molecular weight phenol compounds include bis (4-hydroxyphenyl) methane, bis (2,3,4-trihydroxyphenyl) methane, 2- (4-hydroxyphenyl) -2- (4′-hydroxyphenyl). ) Propane, 2- (2,3,4-trihydroxyphenyl) -2- (2 ′, 3 ′, 4′-trihydroxyphenyl) propane, tris (4-hydroxyphenyl) methane, bis (4-hydroxy-) 3,5-dimethylphenyl) -2-hydroxyphenylmethane, bis (4-hydroxy-2,5-dimethylphenyl) -2-hydroxyphenylmethane, bis (4-hydroxy-3,5-dimethylphenyl) -3, 4-dihydroxyphenylmethane, bis (4-hydroxy-2,5-dimethylphenyl) -3,4-dihydroxyph Phenylmethane, bis (4-hydroxy-3-methylphenyl) -3,4-dihydroxyphenylmethane, bis (3-cyclohexyl-4-hydroxy-6-methylphenyl) -4-hydroxyphenylmethane, bis (3-cyclohexyl- 4-hydroxy-6-methylphenyl) -3,4-dihydroxyphenylmethane, 1- [1- (4-hydroxyphenyl) isopropyl] -4- [1,1-bis (4-hydroxyphenyl) ethyl] benzene, Examples include 2 to 6 nuclei of formalin condensates of phenols such as phenol, m-cresol, p-cresol and xylenol. Of course, it is not limited to these. In particular, a phenol compound having 2 to 6 triphenylmethane skeletons is preferable because of excellent resolution and LWR.
The acid dissociable, dissolution inhibiting group is not particularly limited, and examples thereof include those described above.
(A2) A component may be used individually by 1 type and may be used in combination of 2 or more type.

In the resist composition of the present invention, as the component (A), one type may be used alone, or two or more types may be used in combination.
Among the above, the component (A) preferably contains the component (A1).
In the resist composition of the present invention, the content of the component (A) may be adjusted according to the resist film thickness to be formed.

<(B) component>
[(B1) component]
The resist composition of the present invention contains an acid generating component (B) that generates an acid upon exposure, and the component (B) is an acid generator comprising a compound represented by the following general formula (b1-1) ( B1) (hereinafter referred to as “component (B1)”).

［式中、Ｒ^１はアリーレン基またはアルキレン基であり、Ｒ^２、Ｒ^３はそれぞれ独立にアリール基またはアルキル基であり、Ｒ^２、Ｒ^３は相互に結合して式中のイオウ原子と共に環を形成していてもよく、Ｒ^１〜Ｒ^３のうち少なくとも１つは、アリーレン基またはアリール基であり、Ｙ^１はｎ価の連結基であり、ｎは２または３であり、Ｘ⁻はアニオンである。］

[Wherein R ¹ is an arylene group or an alkylene group, R ² and R ³ each independently represents an aryl group or an alkyl group, and R ² and R ³ are bonded to each other to form a ring together with a sulfur atom in the formula In which at least one of R ^{1 to} R ³ is an arylene group or an aryl group, Y ¹ is an n-valent linking group, n is 2 or 3, and X ⁻ is Anion. ]

((B1) component cation part)
In General Formula (b1-1), Y ¹ is an n-valent linking group, and n is 2 or 3.
Examples of the divalent linking group for Y ¹ include an alkylene group, an alkenylene group, an arylene group, a carbonyl group, a carbonyloxy group, a sulfonyl group, a carbonylamino group, a sulfonylamide group, an ether group, a thioether group, an amino group, a disulfide group, And an acyl group, an alkylsulfonyl group, —CH═CH—, —C≡C—, an aminocarbonylamino group, an aminosulfonylamino group, and a combination of two or more of these.
The divalent linking group for Y ¹ may be linear, branched or cyclic, and is preferably cyclic.
The divalent linking group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and particularly preferably 1 to 10 carbon atoms.
Alkylene group for Y ^1, The alkenylene group preferably has 1 to 20 carbon atoms, more preferably 1 to 10 carbon atoms, still more preferably 1 to 8 carbon atoms, 1 to 6 carbon atoms are particularly preferred, 1 to carbon atoms 4 is most preferred. As the alkylene group and alkenylene group, a partially or completely halogenated alkylene group or alkenylene group (hereinafter sometimes referred to as a halogenated alkylene group or a halogenated alkenylene group) is particularly preferable. The partially halogenated alkylene group or alkenylene group means an alkylene group or alkenylene group in which a part of the hydrogen atoms are substituted with a halogen atom, and a completely halogenated alkylene group or alkenylene group. Means an alkylene group or alkenylene group in which all of the hydrogen atoms are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. That is, the halogenated alkylene group and the halogenated alkenylene group are preferably a fluorinated alkylene group and a fluorinated alkenylene group.
The arylene group for Y ¹ preferably has 4 to 20 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms. As the arylene group, a partially or completely halogenated arylene group is particularly preferable. The partially halogenated arylene group means an arylene group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated arylene group means that all of the hydrogen atoms are halogen atoms. An arylene group substituted with
The divalent linking group may have a substituent. The phrase “having a substituent” for the linking group means that part or all of the hydrogen atoms in the linking group having a hydrogen atom are substituted with an atom or group other than a hydrogen atom.
Examples of the substituent that the divalent linking group may have include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
In such a substituent, examples of the alkoxy group include an alkoxy group having 1 to 5 carbon atoms, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, and a tert-butoxy group are preferable. .
As said halogen atom, a fluorine atom, a chlorine atom, a bromine atom, an iodine atom, etc. are mentioned, A fluorine atom is preferable.
As the halogenated alkyl group, a part or all of hydrogen atoms of an alkyl group having 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, a tert-butyl group, etc. And a group substituted with a halogen atom.
Among these, the divalent linking group for Y ¹ is preferably a group in which two carbonyl groups are combined at both ends of the arylene group.
The trivalent linking group for Y ¹ is preferably a group in which three carbonyl groups are combined with an arylene group.
Preferred specific examples of Y ¹ are listed below.

In general formula (b1-1), R ¹ represents an arylene group or an alkylene group.
The arylene group of R ^1, is not particularly limited, for example, an arylene group having 6 to 20 carbon atoms, said arylene groups, part or all of the hydrogen atoms may be substituted. For example, it may or may not be substituted with an alkyl group, alkoxy group, halogen atom, hydroxyl group or the like.
Such an arylene group is preferably an arylene group having 6 to 10 carbon atoms because it can be synthesized at a low cost. Specific examples include a phenylene group and a naphthylene group.
The alkyl group that may be substituted with a hydrogen atom of the arylene group is preferably an alkyl group having 1 to 5 carbon atoms, and is a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. Are more preferable, and a methyl group is particularly preferable.
As the alkoxy group that may be substituted for the hydrogen atom of the arylene group, an alkoxy group having 1 to 5 carbon atoms is preferable, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, A tert-butoxy group is more preferable.
The halogen atom that may be substituted for the hydrogen atom of the arylene group is preferably a fluorine atom.

The alkylene group of R ^1, is not particularly limited, for example, linear C1-10, branched or cyclic alkylene group, and the like. It is preferable that it is C1-C5 from the point which is excellent in resolution. Specifically, a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C (CH ₃ ) (CH ₂ ) an ethylene group _{[-CH 2 CH 2 -];} ; CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - - C (CH 2 CH 3) 2 alkyl groups such as - CH _{(CH 3) CH 2 -,} - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - CH (CH 2 CH - ₃₎ CH ₂ alkyl groups such as, trimethylene group (n- propylene _{group) [- CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) An alkyl trimethylene group such as CH ₂ —; a tetramethylene group [—CH ₂ CH; ₂ CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ CH ₂ CH ₂ —, —CH ₂ CH (CH ₃ ) CH ₂ CH ₂ — and the like alkyltetramethylene group; pentamethylene group [—CH ₂ CH ₂ CH ₂ CH ₂ CH ₂ —] and the like. Among these, a methylene group is preferable because it is more excellent in resolution and can be synthesized at a low cost.

In the general formula (b1-1), R ² and R ³ are each independently an aryl group or an alkyl group.
The aryl group for R ² and R ³ is not particularly limited, and may be, for example, an aryl group having 6 to 20 carbon atoms, and the aryl group may have a part or all of its hydrogen atoms substituted. Good. For example, it may or may not be substituted with an alkyl group, alkoxy group, halogen atom, hydroxyl group or the like.
Such an aryl group is preferably an aryl group having 6 to 10 carbon atoms because it can be synthesized at a low cost. Specific examples include a phenyl group and a naphthyl group.
Examples of the alkyl group, alkoxy group and halogen atom in which the hydrogen atom of the aryl group may be substituted are the same as the alkyl group, alkoxy group and halogen atom in which the arylene group of R ¹ may be substituted. Can be mentioned.

There is no restriction | limiting in particular as an alkyl group of R < ² >, R < ³ >, For example, a C1-C10 linear, branched or cyclic alkyl group etc. are mentioned. It is preferable that it is C1-C5 from the point which is excellent in resolution. Specific examples include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, an n-pentyl group, a cyclopentyl group, a hexyl group, a cyclohexyl group, a nonyl group, and a decanyl group. . Among these, a methyl group is preferable because it is more excellent in resolution and can be synthesized at a low cost.

In the formula (b1-1), R ² and R ³ may be bonded to each other to form a ring together with the sulfur atom in the formula.
In such a case, it is preferable to form a 3- to 10-membered ring including a sulfur atom, and it is particularly preferable to form a 5- to 7-membered ring.
The ring structure formed with the sulfur atom may contain a hetero atom such as a sulfur atom or an oxygen atom (—O—, ═O).
Specific examples of the ring formed include, for example, a benzene ring, naphthalene ring, anthracene ring, phenanthrene ring, fluorene ring, triphenylene ring, naphthacene ring, biphenyl ring, pyrrole ring, furan ring, thiophene ring, imidazole ring, oxazole ring, Thiazole ring, pyridine ring, pyrazine ring, pyrimidine ring, pyridazine ring, indolizine ring, indole ring, benzofuran ring, benzothiophene ring, isobenzofuran ring, quinolidine ring, quinoline ring, phthalazine ring, naphthyridine ring, quinoxaline ring, quinoxazoline ring , Isoquinoline ring, carbazole ring, phenanthridine ring, acridine ring, phenanthroline ring, thianthrene ring, chromene ring, xanthene ring, phenoxathiin ring, phenothiazine ring, phenazine ring and the like.

In formula (b1-1), at least one of R ^{1 to} R ³ is an arylene group or an aryl group.

  Preferred specific examples of the cation moiety of the component (B1) are listed below.

((B1) component anion part)
In the general formula (b1-1), X ⁻ represents an anion, and n is the same as described above.
The anion of X ⁻ is not particularly limited, and for example, what is known as an anion portion of an onium salt acid generator can be used as appropriate.
X ^- is, for example, the general formula "R ^{14 SO} 3 _- ^{(R 14} is substituted or linear also, branched or cyclic alkyl group, a halogenated alkyl group, an aryl group, Or an alkenyl group)) ”.

In the general formula “R ¹⁴ SO ₃ ⁻ ”, R ¹⁴ represents a linear, branched or cyclic alkyl group, halogenated alkyl group, aryl group, or alkenyl group which may have a substituent. Represent.

The linear or branched alkyl group as R ¹⁴ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms. preferable.
The cyclic alkyl group as R ¹⁴ preferably has 4 to 15 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms.

The halogenated alkyl group as R ¹⁴ is one in which part or all of the hydrogen atoms in the alkyl group are substituted with halogen atoms, and the alkyl group is preferably a lower alkyl group having 1 to 5 carbon atoms, Among them, a linear or branched alkyl group is more preferable, and it is a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, a tert-butyl group, a tert-pentyl group, or an isopentyl group. Further preferred. And the halogen atom by which a hydrogen atom is substituted includes a fluorine atom, a chlorine atom, an iodine atom, a bromine atom and the like. In the halogenated alkyl group, it is preferable that 50 to 100% of the total number of hydrogen atoms in the alkyl group (alkyl group before halogenation) is substituted with a halogen atom, and all the hydrogen atoms are substituted with a halogen atom. More preferably.
Here, the halogenated alkyl group is preferably a fluorinated alkyl group. The fluorinated alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
Further, the fluorination rate of the fluorinated alkyl group is preferably 10 to 100%, more preferably 50 to 100%. Particularly, when all the hydrogen atoms are substituted with fluorine atoms, the strength of the acid is increased. preferable.
Specific examples of such a preferred fluorinated alkyl group include a trifluoromethyl group, a heptafluoro-n-propyl group, and a nonafluoro-n-butyl group.

The aryl group as R ¹⁴ is preferably an aryl group having 6 to 20 carbon atoms.
The alkenyl group as R ¹⁴ is preferably an alkenyl group having 2 to 10 carbon atoms.

In R ¹⁴ , “may have a substituent” means a part of hydrogen atoms in the linear, branched or cyclic alkyl group, halogenated alkyl group, aryl group, or alkenyl group. Or it means that all may be substituted with a substituent (an atom or group other than a hydrogen atom).
The number of substituents in R ¹⁴ may be one, or two or more.

Examples of the substituent include a halogen atom, a hetero atom, an alkyl group, a formula: X ¹ -Q ^1- [where Q ¹ is a divalent linking group containing an oxygen atom, and X ¹ represents a substituent. It is a C3-C30 hydrocarbon group which may have. ] Etc. which are represented by these.
Examples of the halogen atom and alkyl group include the same groups as those described above for R ¹⁴ as the halogen atom and alkyl group in the halogenated alkyl group.
Examples of the hetero atom include an oxygen atom, a nitrogen atom, and a sulfur atom.

In the group represented by X ¹ -Q ^1- , Q ¹ is a divalent linking group containing an oxygen atom.
Q ¹ may contain an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, oxygen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group containing an oxygen atom include an oxygen atom (ether bond: —O—), an ester bond (—C (═O) —O—), and an amide bond (—C (═O) —NH. -), A carbonyl group (-C (= O)-), a non-hydrocarbon oxygen atom-containing linking group such as a carbonate bond (-O-C (= O) -O-); the non-hydrocarbon oxygen atom Examples include a combination of a containing linking group and an alkylene group.
Examples of the combination include —R ⁹¹ —O—, —R ⁹² —O—C (═O) —, —C (═O) —O—R ⁹³ —O—C (═O) — , R ^{91 to} R ⁹³ are each independently an alkylene group.) And the like.
The alkylene group for R ^{91 to} R ⁹³ is preferably a linear or branched alkylene group, and the alkylene group preferably has 1 to 12 carbon atoms, more preferably 1 to 5 carbon atoms, and particularly preferably 1 to 3 carbon atoms. preferable.
Specific examples of the alkylene group include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C ( _{CH 3) (CH 2 CH 3} ) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene group _[-CH 2 CH _2— ]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH ₃ ) CH ₂ —, Alkylethylene groups such as —CH (CH ₂ CH 3) CH ₂ —; trimethylene group (n-propylene group) [—CH ₂ CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ CH ₂ —, —CH ₂ CH _(CH 3) CH ₂ - such as an alkyl trimethylene group; Te Ramechiren group _{[-CH 2 CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; penta And methylene group [—CH ₂ CH ₂ CH ₂ CH ₂ CH ₂ —] and the like.
Q ¹ is preferably a divalent linking group containing an ester bond or an ether bond, and in particular, —R ⁹¹ —O—, —R ⁹² —O—C (═O) — or —C (═O) — O—R ⁹³ —O—C (═O) — is preferred.

In the group represented by X ¹ -Q ^1- , the hydrocarbon group of X ¹ may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group.
The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30, more preferably 5 to 20, still more preferably 6 to 15, and most preferably 6 to 12. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic hydrocarbon group include a hydrogen atom from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, and a phenanthryl group. Aryl groups such as aryl group, benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc., from which one is removed. The number of carbon atoms in the alkyl chain in the arylalkyl group is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.
The aromatic hydrocarbon group may have a substituent. For example, a part of carbon atoms constituting the aromatic ring of the aromatic hydrocarbon group may be substituted with a hetero atom, and the hydrogen atom bonded to the aromatic ring of the aromatic hydrocarbon group is substituted with the substituent. May be.
Examples of the former include heteroaryl groups in which some of the carbon atoms constituting the ring of the aryl group are substituted with heteroatoms such as oxygen atoms, sulfur atoms, nitrogen atoms, and aromatic hydrocarbons in the arylalkyl groups. Examples include heteroarylalkyl groups in which some of the carbon atoms constituting the ring are substituted with the above heteroatoms.
Examples of the substituent of the aromatic hydrocarbon group in the latter example include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as a substituent of the aromatic hydrocarbon group is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. preferable.
The alkoxy group as a substituent of the aromatic hydrocarbon group is preferably an alkoxy group having 1 to 5 carbon atoms, and is a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group, tert- A butoxy group is preferable, and a methoxy group and an ethoxy group are most preferable.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent of the aromatic hydrocarbon group include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

The aliphatic hydrocarbon group for X ¹ may be a saturated aliphatic hydrocarbon group or an unsaturated aliphatic hydrocarbon group. The aliphatic hydrocarbon group may be linear, branched or cyclic.
In X ¹ , the aliphatic hydrocarbon group may be a group in which a part of carbon atoms constituting the aliphatic hydrocarbon group may be substituted with a substituent containing a hetero atom, and hydrogen constituting the aliphatic hydrocarbon group A part or all of the atoms may be substituted with a substituent containing a hetero atom.
The “heteroatom” in X ¹ is not particularly limited as long as it is an atom other than a carbon atom and a hydrogen atom, and examples thereof include a halogen atom, an oxygen atom, a sulfur atom, and a nitrogen atom.
Examples of the halogen atom include a fluorine atom, a chlorine atom, an iodine atom, and a bromine atom.
The substituent containing a hetero atom may be composed of only the hetero atom, or may be a group containing a group or atom other than the hetero atom.
Specific examples of the substituent for substituting a part of the carbon atom include —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O. —, —C (═O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group, an acyl group, etc.), —S—, —S (═O) ₂ —, — S (= O) ₂ —O— and the like can be mentioned. When the aliphatic hydrocarbon group is cyclic, these substituents may be included in the ring structure.
Specific examples of the substituent for substituting part or all of the hydrogen atoms include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), and a cyano group.
The alkoxy group is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group, and a methoxy group or an ethoxy group. Is most preferred.
As said halogen atom, a fluorine atom, a chlorine atom, a bromine atom, an iodine atom, etc. are mentioned, A fluorine atom is preferable.
As the halogenated alkyl group, a part or all of hydrogen atoms of an alkyl group having 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, a tert-butyl group, etc. And a group substituted with a halogen atom.

Examples of the aliphatic hydrocarbon group include a linear or branched saturated hydrocarbon group, a linear or branched monovalent unsaturated hydrocarbon group, or a cyclic aliphatic hydrocarbon group (aliphatic ring). Formula group) is preferred.
The linear saturated hydrocarbon group (alkyl group) preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. Specifically, for example, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decanyl group, undecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group Group, pentadecyl group, hexadecyl group, isohexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group, heicosyl group, docosyl group and the like.
The branched saturated hydrocarbon group (alkyl group) preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specifically, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, Examples include 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like.

As an unsaturated hydrocarbon group, it is preferable that carbon number is 2-10, 2-5 are preferable, 2-4 are preferable, and 3 is especially preferable. Examples of the linear monovalent unsaturated hydrocarbon group include a vinyl group, a propenyl group (allyl group), and a butynyl group. Examples of the branched monovalent unsaturated hydrocarbon group include a 1-methylpropenyl group and a 2-methylpropenyl group.
Among the above, the unsaturated hydrocarbon group is particularly preferably a propenyl group.

The aliphatic cyclic group may be a monocyclic group or a polycyclic group. The number of carbon atoms is preferably 3 to 30, more preferably 5 to 30, further preferably 5 to 20, particularly preferably 6 to 15, and most preferably 6 to 12.
Specifically, for example, a group in which one or more hydrogen atoms are removed from a monocycloalkane; a group in which one or more hydrogen atoms are removed from a polycycloalkane such as bicycloalkane, tricycloalkane, tetracycloalkane, etc. Can be mentioned. More specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; one or more polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Examples include a group excluding a hydrogen atom.
When the aliphatic cyclic group does not contain a substituent containing a hetero atom in the ring structure, the aliphatic cyclic group is preferably a polycyclic group, and has one or more hydrogen atoms from the polycycloalkane. Excluded groups are preferred, and most preferred are groups in which one or more hydrogen atoms have been removed from adamantane.
When the aliphatic cyclic group includes a substituent containing a hetero atom in the ring structure, examples of the substituent containing a hetero atom include —O—, —C (═O) —O—, —S—. , —S (═O) ₂ — and —S (═O) ₂ —O— are preferable. Specific examples of the aliphatic cyclic group include the following formulas (L1) to (L5), (S1) to (S4), and the like.

［式中、Ｑ”は炭素数１〜５のアルキレン基、−Ｏ−、−Ｓ−、−Ｏ−Ｒ^９４−または−Ｓ−Ｒ^９５−であり、Ｒ^９４およびＲ^９５はそれぞれ独立に炭素数１〜５のアルキレン基であり、ｍは０または１の整数である。］

[Wherein, Q ″ is an alkylene group having 1 to 5 carbon atoms, —O—, —S—, —O—R ⁹⁴ — or —S—R ⁹⁵ —, and R ⁹⁴ and R ⁹⁵ are each independently carbon. An alkylene group of 1 to 5 and m is an integer of 0 or 1.]

In the formula, examples of the alkylene group for Q ″, R ⁹⁴ and R ⁹⁵ include the same alkylene groups as those described above for R ^{91 to} R ⁹³ .
In these aliphatic cyclic groups, a part of hydrogen atoms bonded to carbon atoms constituting the ring structure may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
As said alkyl group, a C1-C5 alkyl group is preferable, and it is especially preferable that they are a methyl group, an ethyl group, a propyl group, n-butyl group, and a tert- butyl group.
Examples of the alkoxy group and the halogen atom are the same as those exemplified as the substituent for substituting part or all of the hydrogen atoms.

In the present invention, X ¹ is preferably a cyclic group which may have a substituent. The cyclic group may be an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a substituent. It is preferably an aliphatic cyclic group that may be used.
The aromatic hydrocarbon group is preferably a naphthyl group which may have a substituent or a phenyl group which may have a substituent.
As the aliphatic cyclic group which may have a substituent, a polycyclic aliphatic cyclic group which may have a substituent is preferable. The polycyclic aliphatic cyclic group is preferably a group obtained by removing one or more hydrogen atoms from the polycycloalkane, the above (L2) to (L5), (S3) to (S4), and the like.

Among the above, R ¹⁴ preferably has a halogenated alkyl group or X ¹ -Q ^1- as a substituent.
In the case of having X ¹ -Q ^1- as a substituent, R ¹⁴ is X ¹ -Q ¹ -Y ^3- [wherein Q ¹ and X ¹ are the same as above, and Y ³ has a substituent. Or an optionally substituted alkylene group having 1 to 4 carbon atoms or an optionally substituted fluorinated alkylene group having 1 to 4 carbon atoms. ] Is preferable.
In the group represented by X ¹ -Q ¹ -Y ^3- , examples of the alkylene group for Y ³ include the same alkylene groups as those described above for Q ¹ having 1 to 4 carbon atoms.
Examples of the fluorinated alkylene group include groups in which part or all of the hydrogen atoms of the alkylene group have been substituted with fluorine atoms.
As Y ^3, _{specifically, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF (CF 2 CF 3) -, _{^{-C (CF 3) 2 -,}} - CF 2 CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF ₃ ) —, —C (CF ₃ ) ₂ CF ₂ —, —CF (CF ₂ CF ₃ ) CF ₂ —, —CF (CF ₂ CF ₂ CF ₃ ) —, —C (CF ₃ ) (CF _{2 CF 3) -; - CHF} -, - CH 2 CF 2 -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -, - CH (CF 3) CH 2 -, - CH (CF 2 _{CF 3) -, - C (} CH 3) (CF 3) -, - CH 2 CH 2 CH 2 CF 2 -, - C H ₂ CH ₂ CF ₂ CF ₂ —, —CH (CF ₃ ) CH ₂ CH ₂ —, —CH ₂ CH (CF ₃ ) CH ₂ —, —CH (CF ₃ ) CH (CF ₃ ) —, —C ( _{CF 3) 2 CH 2 -;} - CH 2 -, - CH 2 CH 2 -, - CH 2 CH 2 CH 2 -, - CH (CH 3) CH 2 -, - CH (CH 2 CH 3) -, - _{C (CH 3) 2 -,} - CH 2 CH 2 CH 2 CH 2 -, - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 -, - CH (CH 3) CH _{(CH 3) -, - C} (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - CH (CH 2 CH 2 CH 3) -, - C (CH 3) (CH 2 CH ₃ ) — and the like.

Y ³ is preferably a fluorinated alkylene group, and particularly preferably a fluorinated alkylene group in which the carbon atom bonded to the adjacent sulfur atom is fluorinated. Examples of such fluorinated alkylene _{group, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF 2 CF 2 CF 2 CF 2 _{-, - CF (CF 3)} CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF 3) -, - C (CF 3) 2 CF 2 -, _{-CF (CF 2 CF 3) CF} 2 -; - CH 2 CF 2 -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -; - CH 2 CH 2 CH 2 CF 2 -, - CH ₂ CH ₂ CF ₂ CF ₂ —, —CH ₂ CF ₂ CF ₂ CF ₂ — and the like can be mentioned.
Of _{these, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, or _CH 2 _CF 2 CF ₂ - is _{preferable, -CF 2 -, - CF 2} CF 2 - or -CF ₂ CF ₂ CF ₂ - is more preferable, -CF ₂ - is particularly preferred.

The alkylene group or fluorinated alkylene group may have a substituent. An alkylene group or a fluorinated alkylene group has a “substituent” means that part or all of the hydrogen atom or fluorine atom in the alkylene group or fluorinated alkylene group is substituted with an atom or group other than a hydrogen atom and a fluorine atom. Means that
Examples of the substituent that the alkylene group or fluorinated alkylene group may have include an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, and a hydroxyl group.

R ¹⁴ is ^X 1 ^-Q 1 -Y ³ - is a group represented by ^R 14 -SO ₃ - Examples of the anions, for example represented by the following formula (b1) ~ (b8).

［式中、ｐは１〜３の整数であり、ｑ１〜ｑ２はそれぞれ独立に１〜５の整数であり、ｒ１〜ｒ２は０〜３の整数であり、ｇ”は１〜２０の整数であり、Ｒ^７は置換基であり、ｍ６〜ｍ１０はそれぞれ独立に０または１であり、ｖ１〜ｖ６はそれぞれ独立に０〜３の整数であり、ｗ１〜ｗ５はそれぞれ独立に０〜３の整数であり、Ｑ”は前記と同じである。］

[In the formula, p is an integer of 1 to 3, q1 to q2 are each independently an integer of 1 to 5, r1 to r2 are integers of 0 to 3, and g ″ is an integer of 1 to 20. Yes, R ⁷ is a substituent, m6 to m10 are each independently 0 or 1, v1 to v6 are each independently an integer of 0 to 3, and w1 to w5 are each independently an integer of 0 to 3. And Q ″ is the same as described above. ]

As the substituent for R ^7, the same as those described above as the substituent that the aliphatic hydrocarbon group may have and the substituent that the aromatic hydrocarbon group may have in X ¹ above. Is mentioned.
Code (r1 and r2, w1 to w5) attached to R ⁷ when is an integer of 2 or more, a plurality of the ^{R 7} groups may be the same, respectively, may be different.

In addition, in the general formula (b1-1), X ⁻ includes, for example, an anion represented by the following general formula (b-3) and an anion represented by the following general formula (b-4).

［式中、Ｘ”は、少なくとも１つの水素原子がフッ素原子で置換された炭素数２〜６のアルキレン基を表し；Ｙ”、Ｚ”は、それぞれ独立に、少なくとも１つの水素原子がフッ素原子で置換された炭素数１〜１０のアルキル基を表す。］

[Wherein X ″ represents an alkylene group having 2 to 6 carbon atoms in which at least one hydrogen atom is substituted with a fluorine atom; Y ″ and Z ″ each independently represent at least one hydrogen atom as a fluorine atom; Represents an alkyl group having 1 to 10 carbon atoms and substituted with

In the general formula (b-3), X ″ is a linear or branched alkylene group in which at least one hydrogen atom is substituted with a fluorine atom, and the alkylene group preferably has 2 carbon atoms. -6, more preferably 3-5 carbon atoms, most preferably 3 carbon atoms.
In the general formula (b-4), Y ″ and Z ″ are each independently a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom. Carbon number becomes like this. Preferably it is 1-10, More preferably, it is C1-C7, Most preferably, it is C1-C3.
The number of carbon atoms of the X ″ alkylene group or the number of carbon atoms of the Y ″ and Z ″ alkyl groups is preferably as small as possible because the solubility in a resist solvent is good within the above-mentioned range of carbon numbers.
In addition, in the alkylene group of X ″ or the alkyl group of Y ″ and Z ″, the strength of the acid increases as the number of hydrogen atoms substituted with fluorine atoms increases, and high-energy light or electron beam of 200 nm or less This is preferable because the transparency to the surface is improved.
The fluorination rate of the alkylene group or alkyl group is preferably 70 to 100%, more preferably 90 to 100%, and most preferably a perfluoroalkylene group or a perfluoroalkylene group in which all hydrogen atoms are substituted with fluorine atoms. A fluoroalkyl group;

In the general formula (b1-1), X ⁻ may be a halogen anion.
Here, examples of the halogen anion include fluoride ion, chloride ion, bromide ion, and iodide ion.

Among the above, X ⁻ in the general formula (b1-1) is preferably an anion represented by the general formula “R ¹⁴ SO ₃ ⁻ ”, and R ¹⁴ is represented by X ¹ -Q ¹ -Y ³ —. And those represented by the above formulas (b1) to (b8), those in which R ¹⁴ is a halogenated alkyl group, more preferably those in which R ¹⁴ is a halogenated alkyl group.

As the component (B1), one type may be used alone, or two or more types may be used in combination.
The content ratio of the component (B1) is preferably in the range of 5 to 70 parts by weight, more preferably in the range of 10 to 70 parts by weight with respect to 100 parts by weight of the component (A). It is particularly preferable that the amount be in the range of -70 parts by mass. The sensitivity with respect to the exposure light source at the time of setting it as a resist composition as the content rate of (B1) component is more than the lower limit of the said range increases more. It is preferable for it to be not more than the upper limit of the above range, since a uniform solution can be obtained and the storage stability becomes good.

  In the resist composition of the present invention, the content ratio of the component (B1) in the component (B) is preferably 40% by mass or more, more preferably 70% by mass or more, and even 100% by mass. Good. Most preferably, it is 100 mass%. When the content ratio of the component (B1) is not less than the lower limit of the above range, the sensitivity to the exposure light source when using the resist composition is further increased.

[(B2) component]
The resist composition of the present invention may contain, as the component (B), an acid generator component (hereinafter referred to as “component (B2)”) that does not correspond to the component (B1).
The component (B2) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used. Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, bisalkyl or bisarylsulfonyldiazomethanes, poly (bissulfonyl) diazomethanes, and the like. There are various known diazomethane acid generators, nitrobenzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators, and the like.
As the onium salt acid generator, for example, a compound represented by the following general formula (b-1) or (b-2) can be used.

[Wherein, R ¹ ″ to R ³ ″ and R ⁵ ″ to R ⁶ ″ each independently represents an aryl group or an alkyl group; among R ¹ ″ to R ³ ″ in formula (b-1), Any two of them may be bonded to each other to form a ring together with the sulfur atom in the formula; at least one of R ¹ ″ to R ³ ″ represents an aryl group, and of R ⁵ ″ to R ⁶ ″ At least one represents an aryl group; R ⁴ ″ is as defined above.]

In formula (b-1), R ¹ ″ to R ³ ″ each independently represents an aryl group or an alkyl group. In addition, any two of R ¹ ″ to R ³ ″ in formula (b-1) may be bonded to each other to form a ring together with the sulfur atom in the formula.
Further, at least one of R ¹ ″ to R ³ ″ represents an aryl group. Of R ¹ ″ to R ³ ″, two or more are preferably aryl groups, and most preferably all R ¹ ″ to R ³ ″ are aryl groups.
The aryl group for R ¹ ″ to R ³ ″ is not particularly limited, and is, for example, an aryl group having 6 to 20 carbon atoms, in which part or all of the hydrogen atoms are alkyl groups, alkoxy groups It may or may not be substituted with a group, ether group, halogen atom, halogenated alkyl group, hydroxyl group or the like. The aryl group is preferably an aryl group having 6 to 10 carbon atoms because it can be synthesized at a low cost. Specific examples include a phenyl group and a naphthyl group.
As the alkyl group, ether group, halogen atom and halogenated alkyl group in which the hydrogen atom of the aryl group may be substituted, the aryl group in R ⁷ ″ to R ⁹ ″ may have a substituent. Examples are the same as the alkyl group, ether group, halogen atom, and halogenated alkyl group mentioned as the group.
The alkyl group for R 1 ^{"~R 3",} is not particularly limited, for example, linear C1-10, branched or cyclic alkyl group, and the like. It is preferable that it is C1-C5 from the point which is excellent in resolution. Specific examples include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, an n-pentyl group, a cyclopentyl group, a hexyl group, a cyclohexyl group, a nonyl group, and a decanyl group. A methyl group is preferable because it is excellent in resolution and can be synthesized at low cost.
Among these, R ¹ ″ to R ³ ″ are most preferably a phenyl group or a naphthyl group, respectively.

When any two of R ¹ ″ to R ³ ″ in the formula (b-1) are bonded to each other to form a ring together with the sulfur atom in the formula, a 3 to 10 membered ring including the sulfur atom is formed. It is preferable that a 5- to 7-membered ring is formed.
When any two of R ¹ ″ to R ³ ″ in formula (b-1) are bonded to each other to form a ring together with the sulfur atom in the formula, the remaining one may be an aryl group preferable. Examples of the aryl group include the same aryl groups as those described above for R ¹ ″ to R ³ ″.

In addition, R ¹ ″ to R ³ ″ in the formula (b-1) may have a substituent represented by the following formula (b).

［式（ｂ）中、Ｒ^５２は鎖状又は環状の炭化水素基を表し、ｆは０又は１を表し、ｇは０又は１を表す。］

[In the formula (b), R ⁵² represents a chain or cyclic hydrocarbon group, f represents 0 or 1, and g represents 0 or 1. ]

In the formula (b), R ⁵² represents a chain or cyclic hydrocarbon group.
In R ⁵² , the hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group.

Examples of the aliphatic hydrocarbon group represented by R ⁵² include a linear, branched or cyclic saturated hydrocarbon group having 1 to 15 carbon atoms, or a linear or branched non-carbon group having 2 to 5 carbon atoms. A saturated hydrocarbon group is mentioned.
The aliphatic hydrocarbon group for R ⁵² may be an acid dissociable group. Examples of the acid dissociable group include those conventionally proposed as acid dissociable, dissolution inhibiting groups for base resins for chemically amplified resists, such as tertiary alkyl ester type acid dissociable, dissolution inhibiting groups, And acetal type acid dissociable, dissolution inhibiting groups.

In R ⁵² , the linear or branched saturated hydrocarbon group may have a substituent. Examples of the substituent include an alkoxy group, a halogen atom, a hydroxyl group, an oxygen atom (═O), a cyano group, and a carboxy group.

As the cyclic saturated hydrocarbon group, the cyclic saturated hydrocarbon group may be either a polycyclic group or a monocyclic group, and examples thereof include a cyclic saturated hydrocarbon group having 3 to 20 carbon atoms. Examples include groups in which one hydrogen atom has been removed from a monocycloalkane or polycycloalkane (bicycloalkane, tricycloalkane, tetracycloalkane, etc.). More specifically, one or more hydrogen atoms are removed from monocycloalkanes such as cyclopentane, cyclohexane, cycloheptane, and cyclooctane, and polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Group.
The cyclic saturated hydrocarbon group may have a substituent. As the one having the substituent, for example, one in which a part of carbon atoms constituting the ring in the cyclic saturated hydrocarbon group is substituted with a hetero atom (the former) may be used, and the ring in the cyclic saturated hydrocarbon group may be substituted. The hydrogen atom bonded to may be substituted with a substituent (the latter).
Examples of the former include one or more hydrogen atoms from a heterocycloalkane in which a part of the carbon atoms constituting the ring of the monocycloalkane or polycycloalkane is substituted with a heteroatom such as an oxygen atom, a sulfur atom, or a nitrogen atom. Examples include groups other than atoms. The ring structure may have an ester bond (—C (═O) —O—). Specifically, a lactone-containing monocyclic group such as a group obtained by removing one hydrogen atom from γ-butyrolactone, or a group obtained by removing one hydrogen atom from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring. And other lactone-containing polycyclic groups.
Examples of the substituent in the latter example are the same as those described above as the substituent that the linear or branched saturated hydrocarbon group may have, and an alkyl group. The alkyl group as the substituent is preferably a lower alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group or an ethyl group. The carbon atom constituting the ring to which the alkyl group is bonded is bonded to the terminal of -C (= O)-(O) g- in the substituent represented by the general formula (b1-0). Is preferred.

In R ⁵² , examples of the linear unsaturated hydrocarbon group include a vinyl group, a propenyl group (allyl group), and a butynyl group.
Examples of the branched unsaturated hydrocarbon group include a 1-methylpropenyl group and a 2-methylpropenyl group.
The linear or branched unsaturated hydrocarbon group may have a substituent. Examples of the substituent include the same as those mentioned as the substituent that the linear or branched saturated hydrocarbon group may have.

As the aromatic hydrocarbon group for R ^52, the same aromatic hydrocarbon groups as those described above for X ¹ can be mentioned.

Among the above, R ⁵² is preferably a cyclic hydrocarbon group, more preferably a cyclic aliphatic hydrocarbon group, and further preferably a cyclic saturated hydrocarbon group.

R ⁴ ″ represents a linear, branched or cyclic alkyl group or a fluorinated alkyl group.
The linear or branched alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
The cyclic alkyl group is a cyclic group as indicated by R ¹ ″ and preferably has 4 to 15 carbon atoms, more preferably 4 to 10 carbon atoms, and more preferably 6 carbon atoms. Most preferably, it is -10.
The fluorinated alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
The fluorination rate of the fluorinated alkyl group (ratio of fluorine atoms in the alkyl group) is preferably 10 to 100%, more preferably 50 to 100%. Particularly, all the hydrogen atoms are substituted with fluorine atoms. A fluorinated alkyl group (perfluoroalkyl group) is preferable because the strength of the acid is increased.
R ⁴ ″ is most preferably a linear or cyclic alkyl group or a fluorinated alkyl group.
R ⁴ ″ may have a substituent, and examples of the substituent include the same substituents as exemplified in the description of R ¹⁴ above.

In formula (b-2), R ⁵ ″ to R ⁶ ″ each independently represents an aryl group or an alkyl group. At least one of R ⁵ ″ to R ⁶ ″ represents an aryl group. It is preferable that all of R ⁵ ″ to R ⁶ ″ are aryl groups.
As the aryl group for R ⁵ ″ to R ⁶ ″, the same as the aryl groups for R ¹ ″ to R ³ ″ can be used.
Examples of the alkyl group for R ⁵ ″ to R ⁶ ″ include the same as the alkyl group for R ¹ ″ to R ³ ″.
Among these, it is most preferable that R ⁵ ″ to R ⁶ ″ are all phenyl groups.
"The, ^{R 4} in the formula (b-1)" ^{R 4} in the In the formula (b-2) include the same as.

Specific examples of the onium salt acid generators represented by formulas (b-1) and (b-2) include diphenyliodonium trifluoromethanesulfonate or nonafluorobutanesulfonate, bis (4-tert-butylphenyl) iodonium. Trifluoromethane sulfonate or nonafluorobutane sulfonate, triphenylsulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, tri (4-methylphenyl) sulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its Nonafluorobutanesulfonate, dimethyl (4-hydroxynaphthyl) sulfonium trifluoromethanesulfonate, its heptaful Lopropanesulfonate or its nonafluorobutanesulfonate, trifluoromethanesulfonate of monophenyldimethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; trifluoromethanesulfonate of diphenylmonomethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate (4-methylphenyl) diphenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, (4-methoxyphenyl) diphenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate , Trifluoromethanesulfonate of tri (4-tert-butyl) phenylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate, trifluoromethanesulfonate of diphenyl (1- (4-methoxy) naphthyl) sulfonium, its heptafluoropropane Sulfonate or its nonafluorobutane sulfonate, di (1-naphthyl) phenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1-phenyltetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate Or nonafluorobutanesulfonate thereof; 1- (4-methylphenyl) ) Tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate 1- (4-methoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; 1- (4-ethoxynaphthalene-1- Yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonaflu 1- (4-n-butoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; 1-phenyltetrahydrothiopyranium trifluoromethanesulfonate , Its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (4-hydroxyphenyl) tetrahydrothiopyranium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5-dimethyl -4-Hydroxyphenyl) tetrahydrothiopyranium trifluoromethanesulfonate, its heptafluoropropanes Honeto or nonafluorobutanesulfonate; 1- (4-methylphenyl) trifluoromethanesulfonate tetrahydrothiophenium Pila chloride, heptafluoropropane sulfonate or its nonafluorobutane sulfonate, and the like.
In addition, onium salts in which the anion portion of these onium salts is replaced with methanesulfonate, n-propanesulfonate, n-butanesulfonate, n-octanesulfonate, or anions represented by the above formulas (b1) to (b8) are also used. Can do.

  Moreover, the onium salt type acid generator which replaced the anion part by the anion represented by the said general formula (b-3) or (b-4) in the said general formula (b-1) or (b-2). (The cation moiety is the same as the cation moiety in (b-1) or (b-2)).

  Moreover, the sulfonium salt which has the cation represented by the following general formula (b-5) or (b-6) in a cation part can also be used as an onium salt type | system | group acid generator.

［式中、Ｒ^４１〜Ｒ^４６はそれぞれ独立してアルキル基、アセチル基、アルコキシ基、カルボキシ基、水酸基またはヒドロキシアルキル基であり；ｎ_１〜ｎ_５はそれぞれ独立して０〜３の整数であり、ｎ_６は０〜２の整数である。］

[Wherein R ^{41 to} R ⁴⁶ are each independently an alkyl group, acetyl group, alkoxy group, carboxy group, hydroxyl group or hydroxyalkyl group; n _{1 to} n ₅ are each independently an integer of 0 to 3; There, _{n 6} is an integer of 0-2. ]

In R ^{41 to} R ⁴⁶ , the alkyl group is preferably an alkyl group having 1 to 5 carbon atoms, more preferably a linear or branched alkyl group, and a methyl group, an ethyl group, a propyl group, an isopropyl group, n A butyl group or a tert-butyl group is particularly preferable.
The alkoxy group is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a linear or branched alkoxy group, and particularly preferably a methoxy group or an ethoxy group.
The hydroxyalkyl group is preferably a group in which one or more hydrogen atoms in the alkyl group are substituted with a hydroxy group, and examples thereof include a hydroxymethyl group, a hydroxyethyl group, and a hydroxypropyl group.
When the symbols n _{1 to} n ₆ attached to R ^{41 to} R ⁴⁶ are integers of 2 or more, the plurality of R ^{41 to} R ⁴⁶ may be the same or different.
n ₁ is preferably 0 to 2, more preferably 0 or 1, and still more preferably 0.
n ₂ and n ₃ are preferably each independently 0 or 1, more preferably 0.
n ₄ is preferably 0 to 2, more preferably 0 or 1.
n ₅ is preferably 0 or 1, more preferably 0.
n ₆ is preferably 0 or 1, more preferably 1.

The anion part of the sulfonium salt having a cation represented by the formula (b-5) or (b-6) in the cation part is not particularly limited, and the anion part of the onium salt acid generators proposed so far It may be similar.
Examples of the anion moiety include fluorinated alkyl sulfonate ions such as the anion moiety (R ⁴ ″ SO ₃ —) of the onium salt acid generator represented by the general formula (b-1) or (b-2). An anion represented by the above general formula (b-3) or (b-4), etc. Among them, a fluorinated alkyl sulfonate ion is preferable, and a fluorinated alkyl sulfonate ion having 1 to 4 carbon atoms. Are more preferable, and linear perfluoroalkylsulfonic acid ions having 1 to 4 carbon atoms are particularly preferable, and specific examples thereof include trifluoromethylsulfonic acid ions, heptafluoro-n-propylsulfonic acid ions, and nonafluoro-n-. A butyl sulfonate ion etc. are mentioned.

  In this specification, the oxime sulfonate acid generator is a compound having at least one group represented by the following general formula (B-1), and has a property of generating an acid upon irradiation with radiation. is there. Such oxime sulfonate-based acid generators are frequently used for chemically amplified resist compositions, and can be arbitrarily selected and used.

［式（Ｂ−１）中、Ｒ^３１、Ｒ^３２はそれぞれ独立に有機基を表す。］

[In formula (B-1), R ³¹ and R ³² each independently represents an organic group. ]

The organic groups of R ³¹ and R ³² are groups containing carbon atoms, and atoms other than carbon atoms (for example, hydrogen atoms, oxygen atoms, nitrogen atoms, sulfur atoms, halogen atoms (fluorine atoms, chlorine atoms, etc.), etc.) You may have.
As the organic group for R ^31, a linear, branched, or cyclic alkyl group or aryl group is preferable. These alkyl groups and aryl groups may have a substituent. There is no restriction | limiting in particular as this substituent, For example, a fluorine atom, a C1-C6 linear, branched or cyclic alkyl group etc. are mentioned. Here, “having a substituent” means that part or all of the hydrogen atoms of the alkyl group or aryl group are substituted with a substituent.
As an alkyl group, C1-C20 is preferable, C1-C10 is more preferable, C1-C8 is more preferable, C1-C6 is especially preferable, and C1-C4 is the most preferable. As the alkyl group, a partially or completely halogenated alkyl group (hereinafter sometimes referred to as a halogenated alkyl group) is particularly preferable. The partially halogenated alkyl group means an alkyl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated alkyl group means that all of the hydrogen atoms are halogen atoms. Means an alkyl group substituted with Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. That is, the halogenated alkyl group is preferably a fluorinated alkyl group.
The aryl group preferably has 4 to 20 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms. As the aryl group, a partially or completely halogenated aryl group is particularly preferable. The partially halogenated aryl group means an aryl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated aryl group means that all of the hydrogen atoms are halogen atoms. Means an aryl group substituted with.
R ³¹ is particularly preferably an alkyl group having 1 to 4 carbon atoms having no substituent or a fluorinated alkyl group having 1 to 4 carbon atoms.

As the organic group for R ^32, a linear, branched, or cyclic alkyl group, aryl group, or cyano group is preferable. As the alkyl group and aryl group for R ^32, the same alkyl groups and aryl groups as those described above for R ³¹ can be used.
R ³² is particularly preferably a cyano group, an alkyl group having 1 to 8 carbon atoms having no substituent, or a fluorinated alkyl group having 1 to 8 carbon atoms.

  More preferable examples of the oxime sulfonate-based acid generator include compounds represented by the following general formula (B-2) or (B-3).

［式（Ｂ−２）中、Ｒ^３３は、シアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３４はアリール基である。Ｒ^３５は置換基を有さないアルキル基またはハロゲン化アルキル基である。］

[In Formula (B-2), R ³³ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁴ is an aryl group. R ³⁵ represents an alkyl group having no substituent or a halogenated alkyl group. ]

［式（Ｂ−３）中、Ｒ^３６はシアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３７は２または３価の芳香族炭化水素基である。Ｒ^３８は置換基を有さないアルキル基またはハロゲン化アルキル基である。ｐ”は２または３である。］

[In Formula (B-3), R ³⁶ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁷ is a divalent or trivalent aromatic hydrocarbon group. ^R38 is an alkyl group having no substituent or a halogenated alkyl group. p ″ is 2 or 3.]

In the general formula (B-2), the alkyl group or halogenated alkyl group having no substituent of R ³³ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and carbon atoms. Numbers 1 to 6 are most preferable.
R ³³ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³³ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred.

As the aryl group of R ³⁴ , one hydrogen atom is removed from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, or a phenanthryl group. And heteroaryl groups in which some of the carbon atoms constituting the ring of these groups are substituted with heteroatoms such as oxygen, sulfur and nitrogen atoms. Among these, a fluorenyl group is preferable.
The aryl group of R ³⁴ may have a substituent such as an alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or an alkoxy group. The alkyl group or halogenated alkyl group in the substituent preferably has 1 to 8 carbon atoms, and more preferably 1 to 4 carbon atoms. The halogenated alkyl group is preferably a fluorinated alkyl group.

The alkyl group or halogenated alkyl group having no substituent of R ³⁵ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 6 carbon atoms.
R ³⁵ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³⁵ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred is the strength of the acid generated. Most preferably, it is a fully fluorinated alkyl group in which a hydrogen atom is 100% fluorine-substituted.

In the general formula (B-3), the alkyl group or halogenated alkyl group having no substituent for R ³⁶ is the same as the alkyl group or halogenated alkyl group having no substituent for R ^33. Is mentioned.
Examples of the divalent or trivalent aromatic hydrocarbon group for R ³⁷ include groups obtained by further removing one or two hydrogen atoms from the aryl group for R ³⁴ .
Examples of the alkyl group or halogenated alkyl group having no substituent of R ³⁸ include the same alkyl groups or halogenated alkyl groups as those having no substituent of R ³⁵ .
p ″ is preferably 2.

Specific examples of the oxime sulfonate acid generator include α- (p-toluenesulfonyloxyimino) -benzyl cyanide, α- (p-chlorobenzenesulfonyloxyimino) -benzyl cyanide, α- (4-nitrobenzenesulfonyloxy). Imino) -benzylcyanide, α- (4-nitro-2-trifluoromethylbenzenesulfonyloxyimino) -benzylcyanide, α- (benzenesulfonyloxyimino) -4-chlorobenzylcyanide, α- (benzenesulfonyl) Oxyimino) -2,4-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -2,6-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -4-methoxybenzyl cyanide, α- ( 2-Chlorobenzenesulfonyloxyimino) 4-methoxybenzylcyanide, α- (benzenesulfonyloxyimino) -thien-2-ylacetonitrile, α- (4-dodecylbenzenesulfonyloxyimino) -benzylcyanide, α-[(p-toluenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α-[(dodecylbenzenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α- (tosyloxyimino) -4-thienyl cyanide, α- (methylsulfonyloxyimino) -1-cyclo Pentenyl acetonitrile, α- (methylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -1-cycloheptenylacetonitrile, α- (methylsulfonyloxyimino) -1-cyclooctene Acetonitrile, α- (trifluoromethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -cyclohexylacetonitrile, α- (ethylsulfonyloxyimino) -ethylacetonitrile, α- (propyl Sulfonyloxyimino) -propylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclopentylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclohexylacetonitrile, α- (cyclohexylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- ( Ethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclope Nthenyl acetonitrile, α- (n-butylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (ethylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclohexenylacetonitrile , Α- (n-butylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -phenylacetonitrile, α- (methylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (trifluoro Methylsulfonyloxyimino) -phenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (ethylsulfonyloxyimino) -p- Butoxy phenylacetonitrile, alpha-(propylsulfonyl oxyimino)-p-methylphenyl acetonitrile, alpha-like (methylsulfonyloxyimino)-p-bromophenyl acetonitrile.
Further, an oxime sulfonate-based acid generator disclosed in JP-A-9-208554 (paragraphs [0012] to [0014] [Chemical 18] to [Chemical 19]), pamphlet of International Publication No. 04/074242, An oxime sulfonate-based acid generator disclosed in Examples 1 to 40) on pages 65 to 85 can also be suitably used.
Moreover, the following can be illustrated as a suitable thing.

Among diazomethane acid generators, specific examples of bisalkyl or bisarylsulfonyldiazomethanes include bis (isopropylsulfonyl) diazomethane, bis (p-toluenesulfonyl) diazomethane, bis (1,1-dimethylethylsulfonyl) diazomethane, Examples include bis (cyclohexylsulfonyl) diazomethane, bis (2,4-dimethylphenylsulfonyl) diazomethane, and the like.
Further, diazomethane acid generators disclosed in JP-A-11-035551, JP-A-11-035552, and JP-A-11-035573 can also be suitably used.
Examples of poly (bissulfonyl) diazomethanes include 1,3-bis (phenylsulfonyldiazomethylsulfonyl) propane and 1,4-bis (phenylsulfonyldiazo) disclosed in JP-A-11-322707. Methylsulfonyl) butane, 1,6-bis (phenylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (phenylsulfonyldiazomethylsulfonyl) decane, 1,2-bis (cyclohexylsulfonyldiazomethylsulfonyl) ethane, 1,3 -Bis (cyclohexylsulfonyldiazomethylsulfonyl) propane, 1,6-bis (cyclohexylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (cyclohexylsulfonyldiazomethylsulfonyl) decane, etc. Door can be.

  As the component (B2), one type of acid generator may be used alone, or two or more types may be used in combination.

  1-70 mass parts is preferable with respect to 100 mass parts of (A) component, as for the total content of the (B) component in the resist composition of this invention, 5-70 mass parts is more preferable, 8-70 mass parts. Is most preferred. By setting it within the above range, pattern formation is sufficiently performed. Moreover, since a uniform solution is obtained and storage stability becomes favorable, it is preferable.

<Optional component>
[(D) component]
The resist composition of the present invention preferably further contains a nitrogen-containing organic compound component (D) (hereinafter referred to as “component (D)”) as an optional component.
The component (D) is not particularly limited as long as it acts as an acid diffusion control agent, that is, a quencher that traps the acid generated from the component (B) by exposure, and a wide variety of components have already been proposed. Therefore, it may be used arbitrarily from known ones, and among them, aliphatic amines, particularly secondary aliphatic amines and tertiary aliphatic amines are preferred. Here, the aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 20 carbon atoms.

Examples of the aliphatic amine include an amine (alkylamine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 20 or less carbon atoms. .
Specific examples of alkylamines and alkyl alcohol amines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di- -Dialkylamines such as n-heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine , Tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decanylamine, tri-n-dodecylamine, etc .; diethanolamine, triethanolamine, diisopropanolamine Triisopropanolamine, di -n- octanol amine, tri -n- octanol amine, stearyl diethanolamine, alkyl alcohol amines such as lauryl diethanolamine. Among these, trialkylamine and / or alkyl alcohol amine are preferable.

Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.
Examples of the aromatic amine include aniline, pyridine, 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, diphenylamine, triphenylamine, and tribenzylamine.
Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2 -(1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxy Ethoxy) ethoxy} ethylamine and the like.

These may be used alone or in combination of two or more.
In the present invention, it is particularly preferable to use a trialkylamine as the component (D).
(D) component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component. By setting the content in the above range, the resist pattern shape, the stability over time, and the like are improved.

[(E) component]
The resist composition of the present invention includes, as optional components, organic carboxylic acids, and phosphorus oxo acids and derivatives thereof for the purpose of preventing sensitivity deterioration, improving the resist pattern shape, stability with time, and the like. You may contain the at least 1 sort (s) of compound (E) (henceforth "(E) component") selected.
As the organic carboxylic acid, for example, acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid and the like are suitable.
Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid, and phosphinic acid. Among these, phosphonic acid is particularly preferable.
Examples of the oxo acid derivative of phosphorus include esters in which the hydrogen atom of the oxo acid is substituted with a hydrocarbon group, and the hydrocarbon group includes an alkyl group having 1 to 5 carbon atoms and 6 to 6 carbon atoms. 15 aryl groups and the like.
Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.
Examples of phosphonic acid derivatives include phosphonic acid esters such as phosphonic acid dimethyl ester, phosphonic acid-di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester.
Examples of the phosphinic acid derivatives include phosphinic acid esters such as phenylphosphinic acid.
(E) A component may be used individually by 1 type and may use 2 or more types together.
As the component (E), an organic carboxylic acid is preferable, and salicylic acid is particularly preferable.
(E) A component is normally used in the ratio of 0.01-5.0 mass parts with respect to 100 mass parts of (A) component.

  The resist composition of the present invention further contains miscible additives as desired, for example, an additional resin for improving the performance of the resist film, a surfactant, a dissolution inhibitor, and a plasticizer for improving coatability. Stabilizers, colorants, antihalation agents, dyes, and the like can be added as appropriate.

[(S) component]
The resist composition of the present invention can be produced by dissolving the material in an organic solvent (hereinafter referred to as “(S) component”).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution, and any one of conventionally known solvents for chemically amplified resists can be used. Two or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cycloheptanone, cycloheptanone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, 2-heptanone; ethylene glycol, diethylene glycol, propylene Polyhydric alcohols such as glycol and dipropylene glycol; compounds having an ester bond such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, or dipropylene glycol monoacetate, the polyhydric alcohols or the ester bond Monoalkyl ethers such as monomethyl ether, monoethyl ether, monopropyl ether, monobutyl ether, etc. Derivatives of polyhydric alcohols such as compounds having an ether bond such as monophenyl ether [In these, propylene glycol monomethyl ether acetate (PGMEA) and propylene glycol monomethyl ether (PGME) are preferred]; cyclic such as dioxane Ethers and esters such as methyl lactate, ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, Cresyl methyl ether, diphenyl ether, dibenzyl ether, phenetole, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene , Aromatic organic solvents such as cymene and mesitylene, dimethyl sulfoxide (DMSO), and the like.
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Among the above, propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), EL, and γ-butyrolactone are preferable.
Moreover, the mixed solvent which mixed PGMEA or PGME, and the polar solvent is preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA or PGME and a polar solvent, and is preferably 1: 9 to 9: 1, more preferably 2: 8 to The range is 8: 2.
More specifically, when EL is blended as a polar solvent, the mass ratio of PGMEA: EL is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3.
In addition, as the component (S), a mixed solvent of at least one selected from PGMEA and EL and γ-butyrolactone is also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
Furthermore, a mixed solvent of PGME and dimethyl sulfoxide is also preferable. In this case, the mixing ratio of the former and the latter is preferably 9: 1 to 1: 9, more preferably 8: 2 to 2: 8, and most preferably 7: 3 to 5: 5. It is.
The amount of the component (S) used is not particularly limited and is a concentration that can be applied to the support, and is appropriately set according to the coating film thickness. The concentration is 0.5 to 20% by mass, preferably 1 to 15% by mass.

  The dissolution of the material in the component (S) can be carried out, for example, by simply mixing and stirring each of the above components by a normal method. If necessary, a disperser such as a dissolver, a homogenizer, or a three roll mill You may use and disperse and mix. Moreover, after mixing, you may further filter using a mesh, a membrane filter, etc.

The resist composition of the present invention described above is a novel one that has not been known so far.
According to the resist composition of the present invention, lithography properties such as sensitivity, depth of focus (DOF), exposure margin (EL) and the like are good when using an exposure light source such as ArF excimer laser. Further, a resist pattern can be formed with excellent mask reproducibility (for example, mask error factor (MEF)), and the formed resist pattern shape (for example, the roundness of the hole when the hole pattern is formed), CDU ( In-plane uniformity of pattern dimensions), LWR (line width roughness), etc. are also good. EL is a range of exposure that can form a resist pattern with a dimension within which the deviation from the target dimension is within a predetermined range when the exposure is changed, that is, an exposure that provides a resist pattern that is faithful to the mask pattern. The larger the EL margin value, the smaller the change amount of the pattern size accompanying the change in the exposure amount, and the better the process margin. DOF is a range of depth of focus in which a resist pattern can be formed with a dimension in which a deviation from a target dimension is within a predetermined range when exposure is performed with the same exposure amount shifted up and down, that is, a resist faithful to a mask pattern. This is the range where the pattern can be obtained, and the larger the value, the better. LWR is a phenomenon in which the line width of a line pattern becomes non-uniform when a resist pattern is formed using a resist composition, and the improvement becomes more important as the pattern becomes finer. Yes.
Moreover, according to the resist composition of the present invention, the resist pattern shape is good when an exposure light source such as EUV (extreme ultraviolet) is used. Therefore, the resist composition of the present invention is particularly suitable as a resist composition used in the step of exposing a resist film using EUV as an exposure light source.
The reason why the above effect is obtained is not clear, but as a factor, the resist composition of the present invention includes an acid generator (B1) comprising the compound represented by the general formula (b1-1). Contains component (B). The component (B1) has two or three cations in the structure. This is presumed to improve resolution and lithography characteristics.

≪Resist pattern formation method≫
The resist pattern forming method according to the second aspect of the present invention comprises a step of forming a resist film on a support using the resist composition of the present invention, a step of exposing the resist film, and the resist film. A step of forming a resist pattern by alkali development.
The resist pattern forming method of the present invention can be performed, for example, as follows.
That is, first, the resist composition of the present invention is applied onto a support with a spinner or the like, and prebaked (post-apply bake (PAB)) for 40 to 120 seconds, preferably 60 to 150 ° C. under a temperature condition of 80 to 150 ° C. This is applied for 90 seconds, and this is selected by using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus, for example, by exposure through a mask pattern or by direct irradiation of an electron beam without using a mask pattern. After the exposure, PEB (post-exposure heating) is applied for 40 to 120 seconds, preferably 60 to 90 seconds, at a temperature of 80 to 150 ° C. Next, this is developed with an alkali developer, for example, an aqueous solution of 0.1 to 10% by mass of tetramethylammonium hydroxide (TMAH), preferably rinsed with pure water and dried. In some cases, a baking process (post-bake) may be performed after the development process. In this way, a resist pattern faithful to the mask pattern can be obtained.

The support is not particularly limited, and a conventionally known one can be used, and examples thereof include a substrate for electronic components and a substrate on which a predetermined wiring pattern is formed. More specifically, a silicon substrate, a metal substrate such as copper, chromium, iron, and aluminum, a glass substrate, and the like can be given. As a material for the wiring pattern, for example, copper, aluminum, nickel, gold or the like can be used.
Further, the support may be a substrate in which an inorganic and / or organic film is provided on the above-described substrate. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include an organic antireflection film (organic BARC).
The wavelength used for the exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The resist composition is effective for KrF excimer laser, ArF excimer laser, EB or EUV, and more effective for ArF excimer laser, EB or EUV.

The exposure method of the resist film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the resist film and the lens at the lowest position of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure (immersion exposure) is performed in that state. It is an exposure method.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film to be exposed is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent.
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point: 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

  The resist pattern forming method of the present invention can also be used for a double exposure method and a double patterning method.

≪Compound≫
The compound according to the third aspect of the present invention is a compound represented by the following general formula (b1-1) (hereinafter referred to as “compound (b1-1)”), and the first aspect of the present invention described above. It is the same as the component (B1) contained in the component (B) of the resist composition.

［式中、Ｒ^１はアリーレン基またはアルキレン基であり、Ｒ^２、Ｒ^３はそれぞれ独立にアリール基またはアルキル基であり、Ｒ^２、Ｒ^３は相互に結合して式中のイオウ原子と共に環を形成していてもよく、Ｒ^１〜Ｒ^３のうち少なくとも１つは、アリーレン基またはアリール基であり、Ｙ^１はｎ価の連結基であり、ｎは２または３であり、Ｘ⁻はアニオンである。］

[Wherein R ¹ is an arylene group or an alkylene group, R ² and R ³ each independently represents an aryl group or an alkyl group, and R ² and R ³ are bonded to each other to form a ring together with a sulfur atom in the formula In which at least one of R ^{1 to} R ³ is an arylene group or an aryl group, Y ¹ is an n-valent linking group, n is 2 or 3, and X ⁻ is Anion. ]

  The description about the compound of this invention is the same as the description about the said (B1) component.

≪Acid generator≫
The acid generator which is the 4th aspect of this invention consists of a compound represented by the said general formula (b1-1).
The acid generator is useful as an acid generator for a chemically amplified resist composition, for example, the acid generator component (B) of the resist composition according to the first aspect of the present invention.

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited by these examples.
In this example, the compound represented by the chemical formula (1) is referred to as “compound (1)”, and the same applies to compounds represented by other formulas.

[Compound Synthesis Example 1 (Synthesis of Compound (B2-A))]
In this example, the compounds used as the acid generator component (B) were synthesized according to the synthesis examples shown below.
Under a nitrogen atmosphere, compound (B1) (16.1 g), terephthalic acid chloride (4.1 g) and dichloromethane (350 g) were added to the reaction vessel and cooled to 10 ° C. or lower. A solution of triethylamine (4.5 g) in dichloromethane was slowly added dropwise thereto, and after completion of the addition, the mixture was warmed to room temperature and stirred for 10 minutes. Thereafter, dilute hydrochloric acid was added to the reaction solution to wash the organic layer, followed by washing with pure water. Hexane (1050 g) was dropped into the dichloromethane solution and crystallized to obtain 13 g of compound (B2-A). As a result of IC measurement, the counter anion molar ratio was CH ₃ SO ₃ ⁻ / Cl ⁻ = 45.9 / 54.1.

The compound (B2-A) was analyzed by NMR.
¹ H-NMR (400 MHz, Acetone-d ₆ + D ₂ O): δ (ppm) = 8.56 (s, 4H, ArH in ArC═O), 7.88-8.02 (m, 20H, ArH) , 7.84 (s, 4H, ArH ), 2.76 (s, 2.8H, CH 3 SO 3), 2.36 (s, 12H, CH 3).
From the results shown above, it was confirmed that the compound (B2-A) had a structure shown below.

[Compound Synthesis Example 2 (Synthesis of Compound (B3-A))]
Compound (B2-A) (1.5 g), dichloromethane (23 g), pure water (12 g) and potassium perfluorobutanesulfonate (0.7 g) were added, and the mixture was stirred at room temperature for 12 hours, followed by liquid separation. The organic layer was recovered. Thereafter, the organic layer was repeatedly washed with dilute hydrochloric acid and washed with water until neutral, and concentrated under reduced pressure to obtain 1.5 g of compound (B3-A) as a white powder.

The compound (B3-A) was analyzed by NMR.
¹ H-NMR (400 MHz, DMSO-d ₆ ): δ (ppm) = 8.44 (s, 4H, ArH in ArC═O), 7.78-7.90 (m, 24H, ArH), 2. _{23 (s, 12H, CH 3} ).
¹⁹ F-NMR (376 MHz, DMSO-d ₆ ): δ (ppm) = − 77.8, −112.0, −118.5, −122.9.
From the results shown above, it was confirmed that the compound (B3-A) had a structure shown below.

[Compound Synthesis Examples 3 to 24]
In the above compound synthesis example 2, the same operation was performed except that the compound (M ⁺ -X ⁻ ) was synthesized by changing it to those shown in the following Tables 1 to 6 (equal molar amount). Thereby, products (compounds (B4-A) to (B25-A)) composed of anions (monovalent) and cations (divalent) shown in Tables 1 to 6 were obtained.
Each compound was analyzed by NMR, and the results are shown in Tables 1-6. In Tables 1 to 6, “↑” indicates that the cation of the product is the same as the cation in the cation part of the compound (B4-A).

[Compound Synthesis Example 25 (Synthesis of Compound (B2-B))]
In this example, the compounds used as the acid generator component (B) were synthesized according to the synthesis examples shown below.
Under a nitrogen atmosphere, compound (B1) (16.1 g), isophthalic acid chloride (4.1 g) and dichloromethane (187 g) were added to the reaction vessel and cooled to 10 ° C. or lower. A solution of triethylamine (4.5 g) in dichloromethane was slowly added dropwise thereto, and after completion of the addition, the mixture was warmed to room temperature and stirred for 10 minutes. Thereafter, dilute hydrochloric acid was added to the reaction solution to wash the organic layer, followed by washing with pure water. Hexane (1050 g) was dropped into the dichloromethane solution and crystallized to obtain 14 g of compound (B2-B). As a result of IC measurement, the counter anion molar ratio was CH ₃ SO ₃ ⁻ / Cl ⁻ = 43.4 / 56.6.

The compound (B2-B) was analyzed by NMR.
¹ H-NMR (400 MHz, DMSO-d ₆ ): δ (ppm) = 8.82 (s, 1H, ArH in ArC═O), 8.57 (dd, 2H, ArH in ArC═O), 7. 74-7.94 (m, 25H, ArH in cation + ArH in ArC = O), 2.24 (s, 2.6H, CH 3 SO 3), 2.19 (s, 12H, CH 3).
From the results shown above, it was confirmed that the compound (B2-B) had a structure shown below.

[Compound Synthesis Example 26 (Synthesis of Compound (B3-B))]
Compound (B2-B) (8.68 g), dichloromethane (134 g), pure water (67 g) and potassium perfluorobutanesulfonate (8 g) were added, and the mixture was stirred at room temperature for 12 hours. The layer was collected. Thereafter, the organic layer was repeatedly washed with dilute hydrochloric acid and washed with water until neutral, and concentrated under reduced pressure to obtain 12.2 g of compound (B3-B) as a white powder.

The compound (B3-B) was analyzed by NMR.
¹ H-NMR (400 MHz, DMSO-d ₆ ): δ (ppm) = 8.90 (s, 1H, ArH in ArC═O), 8.60 (dd, 2H, ArH in ArC═O), 7. 77-7.96 (m, 25H, ArH in cation + ArH in ArC = O), 2.24 (s, 12H, CH 3).
¹⁹ F-NMR (376 MHz, DMSO-d ₆ ): δ (ppm) = − 77.9, −112.0, −118.6, −123.0.
From the results shown above, it was confirmed that the compound (B3-B) had a structure shown below.

[Compound Synthesis Examples 27 to 49]
The same operation as in Compound Synthesis Example 26 was performed except that the compound (M ⁺ -X ⁻ ) was synthesized by changing it to those shown in the following Tables 7 to 12 (equal molar amount). Thereby, products (compounds (B4-B) to (B26-B)) composed of anions (monovalent) and cations (divalent) shown in Tables 1 to 6 were obtained.
Each compound was analyzed by NMR, and the results are shown in Tables 7-12. In Tables 7 to 12, “↑” indicates that the cation of the product is the same as the cation in the cation part of the compound (B4-B).

[Example 1-3, Comparative Example 1] <Preparation of resist composition>
Each component shown in Table 13 was mixed and dissolved to prepare a positive resist composition.

In Table 13, the numerical value in [] shows a compounding quantity (part by mass). Moreover, the symbol in Table 13 shows the following, respectively.
(A) -1: a polymer compound (Mw7000, Mw / Mn1.7) represented by the following chemical formula (A) -1.
(B) -1: Compound (B3-A).
(B) -2: the compound (B3-B).
(B) -3: A compound represented by the following chemical formula (B) -3.
(D) -1: tri-n-pentylamine.
(E) -1: Salicylic acid (S) -1: Mixed solvent of PGMEA / PGME = 6/4 (mass ratio).
(S) -2: γ-butyrolactone

<Evaluation of lithography properties>
Using the obtained resist composition, a resist pattern was formed by the following procedure, and the lithography characteristics were evaluated.
[Resist pattern formation]
An organic antireflection film composition “ARC29A” (trade name, manufactured by Brewer Science Co., Ltd.) is applied onto an 8-inch silicon wafer using a spinner, and baked at 205 ° C. for 60 seconds on a hot plate and dried. Thus, an organic antireflection film having a film thickness of 82 nm was formed. Then, each of the obtained resist compositions is applied onto the antireflection film using a spinner, pre-baked (PAB) treatment is performed at 110 ° C. for 60 seconds on a hot plate, and the film is dried. A resist film having a thickness of 150 nm was formed.
Next, an ArF exposure apparatus NSR-S302 (manufactured by Nikon; NA (numerical aperture) = 0.60, 2/3 annular illumination) is applied to the resist film through a mask (6% halftone) pattern. The resist film was selectively irradiated with an ArF excimer laser (193 nm).
Subsequently, a post-exposure heating (PEB) treatment was performed at 110 ° C. for 60 seconds, and a 2.38 mass% tetramethylammonium hydroxide (TMAH) aqueous solution “NMD-3” (trade name, Tokyo Ohka Kogyo Co., Ltd.) at 23 ° C. Manufactured for 30 seconds, and then rinsed with pure water for 30 seconds and shaken off and dried.
As a result, in each example, a line-and-space resist pattern (hereinafter referred to as “LS pattern”) having a line width of 120 nm and a pitch of 240 nm was formed on the resist film.

[sensitivity]
In the above resist pattern formation, the optimum exposure dose Eop (mJ / cm ² ; sensitivity) for forming an LS pattern with a line width of 120 nm and a pitch of 240 nm was determined. The results are shown in Table 14.

[Mask error factor (MEF) evaluation]
In the above Eop, an LS pattern is formed using a mask pattern that targets an LS pattern with a line width of 130 nm and a pitch of 260 nm, and a mask pattern that targets an LS pattern with a line width of 120 nm and a pitch of 260 nm. The MEF value was determined. The results are shown in Table 14.
MEF = | CD130-CD120 | / | MD130-MD120 |
In the above formula, CD130 and CD120 are the actual line widths (nm) of the LS pattern formed using the mask patterns targeting the line widths 130 nm and 120 nm, respectively. MD130 and MD120 are line widths (nm) targeted by the mask pattern, respectively, and MD130 = 130 and MD120 = 120.
The closer this MEF value is to 1, the more the resist pattern faithful to the mask pattern is formed.

[EL margin evaluation]
The exposure amount when the line of the LS pattern was formed within a range of ± 5% (114 nm to 126 nm) of the target dimension (line width 120 nm) was determined, and the EL margin (unit:%) was determined by the following formula. The results are shown in Table 14.
EL margin (%) = (| E1-E2 | / Eop) × 100
E1 represents an exposure amount (mJ / cm ² ) when an LS pattern having a line width of 114 nm is formed, and E2 represents an exposure amount (mJ / cm ² ) when an LS pattern having a line width of 126 nm is formed. Show.

  From the results of Table 14, it was confirmed that the resist compositions of Examples 1 to 3 according to the present invention were superior in lithography properties when using an ArF excimer laser as compared with the resist composition of Comparative Example 1. did it.

  From the results of this evaluation, among the compounds (B3-A) to (B25-A) and (B3-B) to (B26-B), the compounds used as acid generators in Examples 1 to 3 By using other compounds as acid generators, a similar effect that “a resist pattern having excellent lithography properties can be formed” can be expected when an ArF excimer laser is used.

[Example 4-7, Comparative Example 2] <Preparation of resist composition>
Each component shown in Table 15 was mixed and dissolved to prepare a positive resist composition.

In Table 15, the values in [] indicate the amount (parts by mass). Of the symbols in Table 15, (B) -1, (B) -2, (E) -1, (S) -1, and (S) -2 are the same as above, and the others are each The following are shown.
(A) -2: a polymer compound (Mw10000, Mw / Mn2.0) represented by the following chemical formula (A) -2.
(B) -4: A compound represented by the following chemical formula (B) -4.
(D) -2: tri-n-octylamine.

<Evaluation of lithography properties>
Using the obtained resist composition, a resist pattern was formed by the following procedure, and the lithography characteristics were evaluated.
[Resist pattern formation]
The positive resist composition of each example was uniformly applied on an 8-inch silicon substrate subjected to hexamethyldisilazane (HMDS) treatment at 90 ° C. for 36 seconds, using a spinner, and then at 110 ° C. for 60 seconds. PAB treatment was performed to form a resist film (film thickness 60 nm).
The resist film is drawn (exposure) at an accelerating voltage of 70 keV using an electron beam lithography machine HL-800D (VSB) (manufactured by Hitachi), PEB treatment is performed at 100 ° C. for 60 seconds, and further 23 ° C. After developing for 30 seconds using a 2.38 mass% aqueous solution of TMAH “NMD-3: manufactured by Tokyo Ohka Kogyo Co., Ltd.”, rinsing with pure water for 15 seconds, and post-processing at 100 ° C. for 60 seconds. Bake (PDB) treatment was performed to form an L / S pattern.

[sensitivity]
In the above resist pattern formation, the optimum exposure dose Eop (mJ / cm ² ; sensitivity) for forming an LS pattern with a line width of 100 nm and a pitch of 200 nm was determined. The results are shown in Table 16.

[Dissolution rate of unexposed area]
The resist composition solutions of Examples 4 to 7 and Comparative Example 2 were uniformly applied on an 8-inch silicon substrate using a spinner, and pre-baked (PAB) treatment at 110 ° C. for 60 seconds on a hot plate. And a resist film having a film thickness of 60 nm was formed. Next, the resist film was immersed in a 2.38 mass% tetramethylammonium hydroxide (TMAH) aqueous solution at 23 ° C. for 30 seconds, and the dissolution rate (film reduction amount / immersion time, unit: Å / s) was measured.
The lower the dissolution rate of the unexposed portion, the more the resist film can be reduced, and the contrast difference with the exposed portion can be increased.

[Shape evaluation]
The cross-sectional shape of the S / L pattern having a space width of 100 nm and a pitch of 200 nm formed by Eop was observed using a scanning electron microscope (trade name: S-9220, manufactured by Hitachi, Ltd.). Evaluated by criteria. The results are shown in Table 16.
A: The side wall of the line is perpendicular to the substrate surface at the interface with the substrate and has a high rectangularity.
(Triangle | delta): Although the side wall of a line is perpendicular | vertical with respect to the substrate surface in the interface part with a board | substrate, the top part is a little round.

  From the results of Table 16, it was confirmed that the resist compositions of Examples 4 to 7 according to the present invention can form a resist pattern having a better shape than the resist composition of Comparative Example 2.

Claims (7)

A resist composition containing a base material component (A) whose solubility in an alkaline developer is changed by the action of an acid, and an acid generator component (B) that generates an acid upon exposure,
The said acid generator component (B) contains the acid generator (B1) which consists of a compound represented by the following general formula (b1-1), The resist composition characterized by the above-mentioned.

[Wherein R ¹ is an arylene group or an alkylene group, R ² and R ³ each independently represents an aryl group or an alkyl group, and R ² and R ³ are bonded to each other to form a ring together with a sulfur atom in the formula And at least one of R ^{1 to} R ³ is an arylene group or an aryl group, Y ¹ is an n-valent linking group containing a carbonyl group, and n is 2 or 3. , X ⁻ is an anion. ]   The resist composition according to claim 1, wherein the base component (A) is a base component whose solubility in an alkali developer is increased by the action of an acid.   The resist composition according to claim 2, wherein the substrate component (A) is a resin component (A1) and has a structural unit (a1) derived from an acrylate ester containing an acid dissociable, dissolution inhibiting group.   The resist composition according to claim 1, wherein the base material component (A) further has a structural unit (a2) derived from an acrylate ester containing a lactone-containing cyclic group.   The resist composition according to claim 1, wherein the base material component (A) further has a structural unit (a3) derived from an acrylate ester containing a polar group-containing aliphatic hydrocarbon group. object.   Furthermore, the resist composition as described in any one of Claims 1-5 containing a nitrogen-containing organic compound component (D).   A step of forming a resist film on a support using the resist composition according to any one of claims 1 to 6, a step of exposing the resist film, and an alkali development of the resist film to form a resist pattern A resist pattern forming method including a forming step.