JP5588049B2 - Multilayer laminate manufacturing method - Google Patents

Description

  The present invention relates to a method for manufacturing a multilayer laminate in which a plurality of sheet-like materials having similar shapes are overlapped to form a multilayer laminate, and the sheet materials are heated and bonded while preventing lateral displacement of the overlapped sheet materials.

  A typical example of a multilayer laminate is a printed circuit board. Generally, a printed circuit board has a basic configuration of a dielectric material called “prepreg” obtained by impregnating a synthetic resin into a base material such as a synthetic resin plate, a glass plate, a glass nonwoven fabric, or paper. Further, a sheet such as a copper foil having electrical conductivity is bonded to the side facing the prepreg. The laminate thus assembled is generally referred to as a two-layer CCL material.

In the manufacturing process of a four-layer board, a two-layer printed circuit board called a predetermined number of prepregs and then an inner core is formed on a metal plate having a structure (CAC) in which copper foil is bonded to the front and back of an aluminum plate. The assembly unit composed of a set of four-layer substrate materials is completed by overlapping the prepreg and the CAC in this order (see Patent Document 1).
Next, these units (commonly called “pages”) are repeated approximately 10 times to form a press assembly (commonly called “book”).
Then, after storing this book in a metal frame or metal container (commonly called “lunch box”) for preventing lateral misalignment, it is set in a hot press machine and press-molded at a predetermined temperature and pressure. A four-layer substrate is manufactured.
A substrate having four or more layers can also be produced in the same process by increasing the number of inner core layers.

In this molding process, the mold used is made of a metal container that is sturdy like a lunch box because a metal frame for preventing lateral displacement is required. For this reason, such a metal container is referred to as a “lunch box”.
This lunch box is made of an iron plate having a thickness of 5 to 50 mm. This lunch box has a problem that a large number of metal frames or metal containers (lunch boxes) are required because the size of the base material, that is, the sheet laminate, must be changed. . In addition, it is necessary to complete a storage for storing the lunch box.
For example, when manufacturing 30 types of substrates of different sizes in a factory having one 10-stage stacking facility (hot press machine), 10 stages × 30 types = 300 metal frames or metal containers are required. .
Furthermore, since a spare part is also required, 350 or more metal frames or metal containers and storages thereof are required.

In addition, storage of these metal frames or metal containers requires a clean environment and management from the standpoint of measures against foreign materials on the material to be laminated, and is generally strictly prohibited from being stacked, so a wide storage is required. And Thereby, the management cost of the metal frame or the metal container and the storage becomes high.
Further, these metal frames or metal containers are made of 5-50 mm thick iron plates, so that their weight is heavy, and there are some which have a weight of 20 kg or more per piece. Also, since heavy objects are handled in the work, the load on the worker is large, and the worker needs to be careful with dangerous work.

Japanese Patent No. 3100833

  The present invention relates to a method for producing a multilayer laminate in which sheet materials are heat-bonded, and more particularly to a method for producing a single-sided or double-sided multilayer laminate used for a printed wiring board. This method provides a method for preventing lateral slippage due to slipping, which eliminates the need for a large amount of metal frames or metal containers, and further simplifies the material assembling work at the time of stacking, thereby reducing costs and improving safety. It is to be an issue.

As a result of intensive research to solve the above problems, the present inventors have arranged an elastic block in contact with or close to the outer edge of the sheet-like material, and it is effective to prevent lateral displacement of the sheet material. The knowledge that it is.
Based on this knowledge, the present invention 1) superimposes a plurality of sheet-like materials having similar shapes, and superimposes the sheet-like material on a flat plate-shaped lower mold in a method for producing a multilayer laminate that is heated and pressurized. In addition, the heat-resistant elastic block thicker than the stacked sheet material is placed outside the outer edge of the placed sheet-like material, and a flat plate-shaped upper die is placed on these. Place and press the sheet material superimposed on the elastic block between the upper and lower flat plate molds while heating, and heat-join the sheet material while preventing lateral displacement of the sheet material due to the swelling of the elastic block A method for producing a multilayer laminate is provided.

The present invention also provides:
2) The multilayer body is a printed circuit board, and the method for producing a multilayer laminate according to 1) above, wherein the elastic block has a heat resistance of 200 ° C. or higher. The method for producing a multilayer laminate according to 1) or 2) 4) The production of a multilayer laminate according to any one of 1) to 3) above, wherein the sheet-like material is a rectangular sheet material. Method.
5) The method for producing a multilayer laminate according to any one of 1) to 4) above, wherein the elastic block is silicon rubber or fluororubber.
6) The elastic blocks to be arranged on the outside of the outer side of the placed sheet-like material are shorter than each side of the sheet-like material, and one or more elastic blocks are arranged for one side of the sheet-like material. The manufacturing method of the multilayer laminated body as described in any one of said 1) -5) characterized by the above-mentioned.

According to the present invention, the arrangement of the elastic block can be arbitrarily changed between the flat lower mold and the upper mold according to the size and shape of the sheet-like material. Does not require a unique metal frame or metal container.
Therefore, many kinds of metal frames or metal containers are not required, and accordingly, management costs such as mold storage can be reduced. Furthermore, since the metal mold | die (upper and lower) in this invention is a flat metal mold | die, such as a flat iron plate, it has the big effect that a storage volume can be saved significantly.
Further, the elastic block for preventing the lateral displacement is small and lighter than the metal mold, so that there is an advantage that the work load is reduced.
Furthermore, in the conventional method, the prepreg that has flowed out at the time of lamination adheres to the side wall of the metal frame or metal container for preventing lateral deviation, so this peeling work is necessary, but the elastic block in the present invention is soft, There is an effect that the attached prepreg can be easily cleaned.

By assembling the core, prepreg, and CAC in that order, a set of rectangular (rectangular) four-layer sheet material (A) was placed, and the rectangular sheet material and elastic block superimposed on the lower mold were placed. It is a figure which shows a state (B) and also the CAC construction method which has arrange | positioned the elastic body to these periphery (C). The upper die is placed on the upper side of the overlapped sheet material and elastic block shown in Fig. 1 (A), and the die assembly before pressing is prepared (A). The elastic block is deformed and the sheet material is pressed and fixed from the side. It is a figure which shows a mode (B) and (C) leading to. By assembling the core, prepreg, and SUS one after another, a set of rectangular (rectangular) four-layer sheet material (A) was placed on the lower mold, and the rectangular sheet material and elastic block placed on the lower mold were placed. It is a figure which shows a state (B) and also the CAC construction method which has arrange | positioned the elastic body to these periphery (C). The upper die is placed on the upper side of the overlapped sheet material and elastic block in Fig. 3 and the die assembly is prepared before pressing (A). The elastic block is deformed and the sheet material is pressed and fixed from the side. It is a figure which shows a mode (B) and (C) leading to.

The production process of a four-layer substrate using CAC (Cu—Al—Cu) having a structure in which copper foil is bonded to the front and back of an aluminum plate will be described. As shown in FIG. By assembling a predetermined number of prepregs, followed by a two-layer printed circuit board called an inner core, then a prepreg, and then a CAC, an assembly of a set of rectangular (rectangular) four-layer sheet materials is completed. .
Next, these units (commonly called “pages”) are repeated about 10 times to form a multilayered sheet material (commonly called “book”) for pressing.
Generally, AC (adhesive sheet of aluminum and copper) and CAC (copper-aluminum-copper adhesive sheet) are usually rectangular, and are made slightly larger in area than similar prepregs and inner cores, As shown in FIG. 1A, the CAC has a structure in which the end of the CAC protrudes slightly.

Next, as shown in FIG. 1B, the stacked sheet materials (books) having similar shapes are placed on a lower mold (for example, a flat iron plate). In general, a rectangular sheet material is often used as the sheet material, but a triangular, quadrangular or other polygonal sheet material can also be used. Any similar sheet material can be used without any particular problem. An elastic block (rubber block) is disposed on the lower mold near the center of each side (four sides) of the sheet material.
This elastic block (rubber block) is made of a material that is thicker than the thickness of the stacked sheet material placed on the lower mold, and has a shape that does not easily fall over. For example, a hexagon (dice shape) is preferable. Further, the elastic block is installed outside each side of the overlapped sheet material as shown in FIG. In this case, the elastic block may be brought into contact with the sheet material or may be arranged close to each other.
Since the end of the CAC protrudes slightly as described above, the elastic block is in a position in contact with the end of the CAC. Since CAC has higher strength than copper foil, as shown in FIG. 1B, CAC, core, and prepreg are in an aligned state.

Although one elastic block is provided on each side in FIGS. 1B and 1C, a plurality of elastic blocks may be provided. When a plurality of sheets are installed, it is desirable to place them on the lower mold by aligning them in parallel with the stacked sheet materials having similar shapes.
In general, the temperature when laminating and adhering sheet materials is about 180 ° C., so that the elastic block has a high heat resistance, such as silicon rubber (abbreviation VMQ: heat resistant limit temperature 230 ° C.) or fluorine rubber. (Abbreviation NR: heat-resistant limit temperature 230 ° C) is preferably used.

Next, as shown in FIG. 2A, an upper mold (flat iron plate) is placed on the upper side of the overlapped sheet material and the elastic block. This completes preparations for assembling the mold before press-in.
Next, the above-described material after the assembly of the mold is set in a hot press machine, and pressing is started. First, as pressure is applied, the elastic block is pressed between the upper and lower molds and fixed.

Thereafter, as shown in FIGS. 2 (B) and 2 (C), when pressure is further applied, the elastic block is deformed, and a force that bulges into a barrel shape acts, so that the sheet material on which the elastic block is overlapped is placed sideways. From pressing down to fixing. In this case, the CAC is deformed as shown in FIG. 2B by being compressed, but this deformation encloses the inner core and the prepreg, and can prevent a lateral shift between the core and the prepreg.
After that, by applying a predetermined heating temperature and pressure, the prepreg is cured and the copper foil and the prepreg are joined to complete the laminated substrate. As described above, the prepreg is melted during hot pressing, so that the inner layer core is liable to be laterally displaced. However, by using the elastic block of the present invention, this can be suppressed.
In order to prevent the inner core from slipping, a large force is not required, and as shown in FIGS. 1 and 2, it is sufficient to place only one on each side.

Next, the manufacturing process of the 4-layer board | substrate using a SUS board is demonstrated. As shown in FIG. 3 (A), a predetermined number of prepregs, then a two-layer printed circuit board called an inner core, then a prepreg, and then a SUS board are sequentially stacked on the SUS board. The assembly of a rectangular (rectangular) set of four-layer sheet material is completed.
Next, these units (commonly called “pages”) are repeated about 10 times to form a multilayered sheet material (commonly called “book”) for pressing.
In general, the SUS plate is manufactured to have a slightly smaller area than the copper foil, and has a structure in which the end of the copper foil slightly protrudes as shown in FIG. In general, the end of the copper foil is bent and set as shown in FIG.

Next, as shown in FIG. 3B, the stacked sheet materials (books) having similar shapes are placed on a lower mold (for example, a flat iron plate). An elastic block (rubber block) is disposed on the lower mold near the center of each side (four sides) of the sheet material.
This elastic block (rubber block) is made of a material that is thicker than the thickness of the stacked sheet material placed on the lower mold, and has a shape that does not easily fall over. Usually, it is good to use a hexagon (die shape). Moreover, the elastic block is installed outside each side of the overlapped sheet material, as shown in FIG.
As described above, the end of the copper foil has a structure that slightly protrudes, but since it is folded, the elastic block is in a position that contacts the end of all the laminated sheets.

In FIGS. 3B and 3C, one elastic block is installed on each side, but a plurality of elastic blocks may be installed. When a plurality of sheets are installed, it is desirable to place them on the lower mold by aligning them in parallel with the stacked sheet materials having similar shapes. This is the same as when the CAC is used.
In general, the temperature when laminating and adhering sheet materials is about 180 ° C., so that the elastic block has a high heat resistance, such as silicon rubber (abbreviation VMQ: heat resistant limit temperature 230 ° C.) or fluorine rubber. (Abbreviation NR: heat-resistant limit temperature 230 ° C) is preferably used.

Next, as shown in FIG. 4A, an upper mold (a flat iron plate) is placed on the upper side of the overlapped sheet material and the elastic block. This completes preparations for assembling the mold before press-in.
Next, the above-described material after the assembly of the mold is set in a hot press machine, and pressing is started. First, as pressure is applied, the elastic block is pressed between the upper and lower molds and fixed.

After that, as shown in FIGS. 4B and 4C, when pressure is further applied, the elastic block is deformed and a force that bulges into a barrel shape acts, and the sheet material on which the elastic block overlaps is laterally moved. From pressing down to fixing. In this case, the copper foil is already folded, but is further pressed to wrap the inner core and the prepreg, thereby preventing the core and the prepreg from being laterally displaced.
After that, by applying a predetermined heating temperature and pressure, the prepreg is cured and the copper foil and the prepreg are joined to complete the laminated substrate. As described above, the prepreg is melted during hot pressing, so that the inner layer core is liable to be laterally displaced. However, by using the elastic block of the present invention, this can be suppressed.
In order to prevent the inner core from laterally shifting, a large force is not necessary, and as shown in FIGS. 3 and 4, it is sufficient to place only one on each side.

  Next, specific examples of the present invention will be described. The following examples are intended to facilitate understanding of the present invention and are not limited thereto. That is, modifications, embodiments, and other examples based on the technical idea of the present invention are included in the present invention.

Example 1
As shown in FIGS. 1 (A), (B), and (C), a book is assembled on a lower laminated mold (a flat iron plate having a thickness of 10 mm), and a rubber-made material is placed near the center of the four sides. Arranged the blocks. Since the maximum temperature at the time of lamination is about 180 ° C., in this embodiment, silicon rubber (abbreviated as VMQ: heat resistant limit temperature 230 ° C.) having a heat resistance of 50% is used for the rubber block.
The shape of the silicon rubber was a 55 mm cube that was 5 mm higher than the height of the book (stacked sheet material).

Thereafter, as shown in FIG. 2 (A), by placing the upper laminated mold (a flat iron plate having a thickness of 10 mm), the preparation of the mold assembly before press-in is completed, and the press program shown in Table 1 Thus, hot pressing was performed.
When press work was started, first, pressure was applied and the rubber block was pressed between the upper and lower molds to fix the book.
Thereafter, as shown in Table 1, by further applying pressure, the rubber block was deformed, the book was pressed from the side, and the CAC and the prepreg were fixed.

Thereafter, when the pressure was further increased, the rubber block was further deformed, and the aluminum plate of CAC was pushed and bent as shown in FIG. As a result, slipping of the inner layer core was prevented. As described above, in general, AC (aluminum-copper adhesive sheet) and CAC (copper-aluminum-copper adhesive sheet) have a slightly larger area than the prepreg and the inner layer core. ) As shown in FIG.
For this reason, the CAC is pushed and bent as shown in FIG. Since such a deformation becomes a form in which the inner layer core existing between them is held, slipping of the inner layer core is more effectively suppressed.

As described above, the prepreg was cured by passing a predetermined temperature (maximum temperature 180 ° C.) and pressure (30 kg / cm ² ). After that, when the temperature dropped, the book was disassembled, and a multilayer laminate substrate could be completed.
As described above, the core material is liable to be laterally displaced by melting the prepreg during heating, but this can be suppressed by employing the rubber block of the present invention.

(Example 2)
Next, the specific example of the manufacturing method of the multilayer laminated body using a SUS board is demonstrated.
As shown in FIGS. 3 (A), (B), and (C), the book is assembled on the lower laminated mold (a flat iron plate having a thickness of 10 mm), and a rubber-made material is placed near the center of the four sides. Arranged the blocks. Since the maximum temperature at the time of lamination is about 180 ° C., in this example, fluororubber having high heat resistance was adopted for the rubber block.
The shape of the fluororubber was a 55 mm cube that was 5 mm higher than the height of the book (stacked sheet material).

Thereafter, as shown in FIG. 2A, by placing the upper laminated mold (a flat iron plate having a thickness of 10 mm), preparation of the mold assembly before press-in was completed, and the same as in Example 1 In addition, hot pressing was performed. Although copper foil has protruded from the lamination sheet, as shown to FIG. 2 (A), these are bent and set.
When press work was started, first, pressure was applied and the rubber block was pressed between the upper and lower molds to fix the book. Thereafter, by further applying pressure, the rubber block was deformed, and the book was pressed from the side to fix the SUS, core, and prepreg.

Thereafter, when the pressure was further increased, the rubber block was further deformed to press the four sides of the laminate, and the copper foil wrapped around the inner layer core, thereby preventing the inner layer core and the prepreg from slipping.
As described above, the prepreg was cured by passing a predetermined temperature (maximum temperature 180 ° C.) and pressure (30 kg / cm ² ). After that, when the temperature dropped, the book was disassembled, and a multilayer laminate substrate could be completed.
As described above, the core material is liable to be laterally displaced by melting the prepreg during heating, but this can be suppressed by employing the rubber block of the present invention.

According to the present invention, the arrangement of the elastic blocks can be arbitrarily changed between the flat lower mold and the upper mold in accordance with the size and shape of the sheet-like material. A metal container is no longer necessary, and the management cost for storing molds can be reduced accordingly. The molds (upper and lower) in the present invention are simply flat plate molds such as flat iron plates, so that the storage volume can be saved greatly, and the elastic block for preventing lateral displacement is small, and the metal mold Since it is lighter than the mold, it has the merit of reducing the work load.
Furthermore, in the conventional method, the prepreg that has flowed out at the time of lamination adheres to the side wall of the metal frame or metal container for preventing lateral deviation, so this peeling work is necessary, but the elastic block in the present invention is soft, There is an effect that the attached prepreg can be easily cleaned. From the above, the merit of the present invention is great, and is particularly useful for the production of printed circuit boards.

Claims (9)

In a method for producing a multilayer laminate in which a plurality of sheet-like materials having similar shapes are superposed and heated and pressurized,
Sheet material including AC (aluminum-copper adhesive sheet) or CAC (copper-aluminum-copper adhesive sheet), a prepreg, and a printed circuit board is used as the AC or the end of the CAC. It is placed on a flat plate-shaped lower mold so as to protrude from the end of the prepreg, and has a heat resistance that is thicker than the stacked sheet material on the outer side of the placed sheet-like material. An elastic block is disposed, and a flat upper mold is placed thereon, and the sheet material superimposed on the elastic block is pressed between the upper and lower flat molds while being heated, and the elastic block is expanded. A method for producing a multilayer laminate in which sheet material is heated and bonded while preventing lateral displacement of the sheet material. In a method for producing a multilayer laminate in which a plurality of sheet-like materials having similar shapes are superposed and heated and pressurized,
Sheet material including AC (aluminum-copper adhesive sheet) or CAC (copper-aluminum-copper adhesive sheet), a prepreg, and a printed circuit board is used as the AC or the end of the CAC. It is placed on a flat plate-shaped lower mold so as to protrude from the end of the prepreg, and has a heat resistance that is thicker than the stacked sheet material on the outer side of the placed sheet-like material. The elastic block is arranged so that the position can be changed, and a flat upper mold is placed on the elastic block, and the upper and lower flat molds are heated while the sheet material superimposed on the elastic block is heated. A method for manufacturing a multilayer laminate, in which a sheet material is heat-bonded while being pressed to prevent lateral displacement of the sheet material due to the swelling of the elastic block. In a method for producing a multilayer laminate in which a plurality of sheet-like materials having similar shapes are superposed and heated and pressurized,
Sheet material including AC (aluminum-copper adhesive sheet) or CAC (copper-aluminum-copper adhesive sheet), a prepreg, and a printed circuit board is used as the AC or the end of the CAC. It is placed on a flat plate-shaped lower mold so as to protrude from the end of the prepreg, and has a heat resistance that is thicker than the stacked sheet material on the outer side of the placed sheet-like material. An elastic block is disposed, and a flat upper mold is placed thereon, and the sheet material superimposed on the elastic block is pressed between the upper and lower flat molds while being heated, and the elastic block is expanded. A multilayer laminate manufacturing method in which sheet material is heated and bonded while preventing lateral displacement of the sheet material, and the elastic block is not fixed to the lower mold. Method of manufacturing a multi-layer laminate. In a method for producing a multilayer laminate in which a plurality of sheet-like materials having similar shapes are superposed and heated and pressurized,
Sheet material including AC (aluminum-copper adhesive sheet) or CAC (copper-aluminum-copper adhesive sheet), a prepreg, and a printed circuit board is used as the AC or the end of the CAC. It is placed on a flat plate-shaped lower mold so as to protrude from the end of the prepreg, and has a heat resistance that is thicker than the stacked sheet material on the outer side of the placed sheet-like material. An elastic block is disposed, and a flat upper mold is placed thereon, and the sheet material superimposed on the elastic block is pressed between the upper and lower flat molds while being heated, and the elastic block is expanded. The manufacturing method of the multilayer laminated body which heat-joins a sheet material, preventing the sheet material from slipping laterally (providing a groove for fixing the elastic block to the lower mold) Except for a method of manufacturing a multi-layer laminate that is). The laminate is, the printed circuit sandwiching board in the prepreg, further multilayer according to the prepreg to any one of claims 1 to 4, characterized in that said AC or laminate sandwiched by the CAC A manufacturing method of a layered product.   The method for producing a multilayer laminate according to any one of claims 1 to 5, wherein the elastic block has a heat resistance of 200 ° C or higher.   The method for producing a multilayer laminate according to any one of claims 1 to 6, wherein the sheet material is a rectangular sheet material.   The method for producing a multilayer laminate according to any one of claims 1 to 7, wherein the elastic block is silicon rubber or fluororubber.   The elastic blocks arranged outside the outer side of the placed sheet-like material are shorter than each side of the sheet-like material, and one or more elastic blocks are arranged for one side of the sheet-like material. The manufacturing method of the multilayer laminated body as described in any one of Claims 1-8.