JP5531446B2 - ORGANIC ELECTROLUMINESCENT ELEMENT, ORGANIC ELECTROLUMINESCENT ELEMENT MATERIAL, DISPLAY DEVICE AND LIGHTING DEVICE - Google Patents

ORGANIC ELECTROLUMINESCENT ELEMENT, ORGANIC ELECTROLUMINESCENT ELEMENT MATERIAL, DISPLAY DEVICE AND LIGHTING DEVICE Download PDF

Info

Publication number
JP5531446B2
JP5531446B2 JP2009101736A JP2009101736A JP5531446B2 JP 5531446 B2 JP5531446 B2 JP 5531446B2 JP 2009101736 A JP2009101736 A JP 2009101736A JP 2009101736 A JP2009101736 A JP 2009101736A JP 5531446 B2 JP5531446 B2 JP 5531446B2
Authority
JP
Japan
Prior art keywords
group
general formula
ring
organic
atom
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2009101736A
Other languages
Japanese (ja)
Other versions
JP2010248429A (en
Inventor
信也 大津
大 池水
智寛 押山
雅人 西関
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Inc
Original Assignee
Konica Minolta Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Inc filed Critical Konica Minolta Inc
Priority to JP2009101736A priority Critical patent/JP5531446B2/en
Publication of JP2010248429A publication Critical patent/JP2010248429A/en
Application granted granted Critical
Publication of JP5531446B2 publication Critical patent/JP5531446B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、有機エレクトロルミネッセンス素子、有機エレクトロルミネッセンス素子材料、表示装置および照明装置に関する。   The present invention relates to an organic electroluminescence element, an organic electroluminescence element material, a display device, and a lighting device.

従来、発光型の電子ディスプレイデバイスとして、エレクトロルミネッセンスディスプレイ(以下、ELDという)がある。ELDの構成要素としては、無機エレクトロルミネッセンス素子や有機エレクトロルミネッセンス素子(以下、有機EL素子ともいう)が挙げられる。   Conventionally, as a light-emitting electronic display device, there is an electroluminescence display (hereinafter referred to as ELD). Examples of the constituent elements of ELD include inorganic electroluminescent elements and organic electroluminescent elements (hereinafter also referred to as organic EL elements).

無機エレクトロルミネッセンス素子は平面型光源として使用されてきたが、発光素子を駆動させるためには交流の高電圧が必要である。   Inorganic electroluminescent elements have been used as planar light sources, but an alternating high voltage is required to drive the light emitting elements.

一方、有機EL素子は発光する化合物を含有する発光層を陰極と陽極で挟んだ構成を有し、発光層に電子及び正孔を注入して、再結合させることにより励起子(エキシトン)を生成させ、このエキシトンが失活する際の光の放出(蛍光・リン光)を利用して発光する素子であり、数V〜数十V程度の電圧で発光が可能であり、更に自己発光型であるために視野角に富み、視認性が高く、薄膜型の完全固体素子であるために省スペース、携帯性等の観点から注目されている。   On the other hand, an organic EL device has a structure in which a light-emitting layer containing a light-emitting compound is sandwiched between a cathode and an anode, and excitons (excitons) are generated by injecting electrons and holes into the light-emitting layer and recombining them. The device emits light by utilizing the emission of light (fluorescence / phosphorescence) when the exciton is deactivated, and can emit light at a voltage of several volts to several tens of volts. Therefore, it has a wide viewing angle, high visibility, and since it is a thin-film type completely solid element, it has attracted attention from the viewpoints of space saving and portability.

しかしながら、今後の実用化に向けた有機EL素子においては、更に低消費電力で効率よく高輝度に発光する有機EL素子の開発が望まれている。   However, in organic EL elements for practical use in the future, development of organic EL elements that emit light efficiently and with high luminance with lower power consumption is desired.

特許第3093796号公報では、スチルベン誘導体、ジスチリルアリーレン誘導体またはトリススチリルアリーレン誘導体に微量の蛍光体をドープし、発光輝度の向上、素子の長寿命化を達成している。   In Japanese Patent No. 3093796, a small amount of a phosphor is doped into a stilbene derivative, a distyrylarylene derivative or a tristyrylarylene derivative to achieve an improvement in light emission luminance and a longer device lifetime.

また、8−ヒドロキシキノリンアルミニウム錯体をホスト化合物として、これに微量の蛍光体をドープした有機発光層を有する素子(例えば、特開昭63−264692号公報)、8−ヒドロキシキノリンアルミニウム錯体をホスト化合物として、これにキナクリドン系色素をドープした有機発光層を有する素子(例えば、特開平3−255190号公報)等が知られている。   Further, an element having an organic light-emitting layer in which an 8-hydroxyquinoline aluminum complex is used as a host compound and a small amount of phosphor is doped thereto (for example, JP-A 63-264692), and an 8-hydroxyquinoline aluminum complex is used as a host compound. For example, an element having an organic light emitting layer doped with a quinacridone dye (for example, JP-A-3-255190) is known.

以上のように、励起一重項からの発光を用いる場合、一重項励起子と三重項励起子の生成比が1:3であるため発光性励起種の生成確率が25%であり、光の取り出し効率が約20%であるため、外部取り出し量子効率(η)の限界は5%とされている。   As described above, when light emission from excited singlet is used, the generation ratio of singlet excitons and triplet excitons is 1: 3, and thus the generation probability of luminescent excited species is 25%. Since the efficiency is about 20%, the limit of the external extraction quantum efficiency (η) is set to 5%.

ところが、プリンストン大より励起三重項からのリン光発光を用いる有機EL素子の報告(M.A.Baldo et al.,Nature、395巻、151〜154頁(1998年))がされて以来、室温でリン光を示す材料の研究が活発になってきている。   However, since Princeton University reported on an organic EL device using phosphorescence emission from an excited triplet (MA Baldo et al., Nature, 395, 151-154 (1998)), Research on materials that exhibit phosphorescence has become active.

例えば、M.A.Baldo et al.,Nature、403巻、17号、750〜753頁(2000年)、また米国特許第6,097,147号明細書等にも開示されている。   For example, M.M. A. Baldo et al. , Nature, 403, 17, 750-753 (2000), US Pat. No. 6,097,147, and the like.

励起三重項を使用すると、内部量子効率の上限が100%となるため励起一重項の場合に比べて原理的に発光効率が4倍となり、冷陰極管とほぼ同等の性能が得られる可能性があることから照明用途としても注目されている。   When the excited triplet is used, the upper limit of the internal quantum efficiency is 100%. In principle, the luminous efficiency is four times that of the excited singlet, and there is a possibility that almost the same performance as a cold cathode tube can be obtained. Therefore, it is attracting attention as a lighting application.

例えば、S.Lamansky et al.,J.Am.Chem.Soc.,123巻、4304頁(2001年)等においては、多くの化合物がイリジウム錯体系等重金属錯体を中心に合成検討されている。   For example, S.M. Lamansky et al. , J .; Am. Chem. Soc. , 123, 4304 (2001), etc., many compounds are being studied for synthesis centering on heavy metal complexes such as iridium complexes.

また、前述のM.A.Baldo et al.,Nature、403巻、17号、750〜753頁(2000年)においては、ドーパントとしてトリス(2−フェニルピリジン)イリジウムを用いた検討がされている。   In addition, the aforementioned M.I. A. Baldo et al. , Nature, 403, 17, 750-753 (2000), studies have been made using tris (2-phenylpyridine) iridium as a dopant.

その他、M.E.Tompson等は、The 10th International Workshop on Inorganic and Organic Electroluminescence(EL’00、浜松)において、ドーパントとしてLIr(acac)、例えば、(ppy)Ir(acac)を、またMoon−Jae Youn.0g、Tetsuo Tsutsui等は、やはりThe 10th International Workshop on Inorganic and Organic Electroluminescence(EL’00、浜松)において、ドーパントとしてトリス(2−(p−トリル)ピリジン)イリジウム(Ir(ptpy)),トリス(ベンゾ[h]キノリン)イリジウム(Ir(bzq))等を用いた検討を行っている(なおこれらの金属錯体は一般にオルトメタル化イリジウム錯体と呼ばれている。)。 In addition, M.M. E. Thompson et al. In The 10th International Works on Inorganic and Organic Electroluminescence (EL'00, Hamamatsu) used L 2 Ir (acac), for example, (ppy) 2 Ir (acac), e 0 g, Tetsuo Tsutsui, etc., again The 10th International Workshop on Inorganic and Organic Electroluminescence (EL'00, Hamamatsu), the dopant as tris (2-(p-tolyl) pyridine) iridium (Ir (ptpy) 3), tris ( Studies using benzo [h] quinoline) iridium (Ir (bzq) 3 ) and the like are being conducted (note that these metal complexes are generally called ortho-metalated iridium complexes).

また、前記S.Lamansky et al.,J.Am.Chem.Soc.,123巻、4304頁(2001年)や特開2001−247859号公報等においても、各種イリジウム錯体を用いて素子化する試みがされている。   In addition, the S. Lamansky et al. , J .; Am. Chem. Soc. , 123, 4304 (2001) and Japanese Patent Application Laid-Open No. 2001-247859, etc., attempts have been made to form devices using various iridium complexes.

また、高い発光効率を得るためにThe 10th International Workshop on Inorganic and Organic Electroluminescence(EL’00、浜松)では、Ikai等はホール輸送性の化合物をリン光性化合物のホストとして用いている。また、M.E.Tompson等は各種電子輸送性材料をリン光性化合物のホストとして、これらに新規なイリジウム錯体をドープして用いている。   In order to obtain high luminous efficiency, in the 10th International Workshop on Inorganic and Organic Electroluminescence (EL'00, Hamamatsu), Ikai et al. Uses a hole transporting compound as a host of a phosphorescent compound. In addition, M.M. E. Thompson et al. Use various electron transporting materials as a host of phosphorescent compounds, doped with a novel iridium complex.

リン光性の高効率の発光材料は、発光波長の短波化と素子の発光寿命の改善が難しく、実用に耐えうる性能を十分に達成できていないのが現状である。   A phosphorescent high-efficiency light-emitting material is difficult to shorten the emission wavelength and improve the light-emission lifetime of the device, and has not been able to achieve sufficient performance for practical use.

また、波長の短波化に関してはこれまでフェニルピリジンにフッ素原子、トリフルオロメチル基、シアノ基等の電子吸引基を置換基として導入すること、配位子としてピコリン酸やピラザボール系の配位子を導入することが知られている。   In addition, regarding wavelength shortening, introduction of an electron withdrawing group such as a fluorine atom, a trifluoromethyl group, a cyano group or the like into phenylpyridine as a substituent, and picolinic acid or a pyrazabole-based ligand as a ligand. It is known to introduce.

しかしながら、これらの配位子では発光材料の発光波長が短波化して青色を達成し、高効率の素子を達成できる一方、素子の発光寿命は大幅に劣化するため、そのトレードオフの改善が求められていた。   However, with these ligands, the emission wavelength of the light-emitting material is shortened to achieve blue, and a high-efficiency device can be achieved. On the other hand, the light-emitting lifetime of the device is greatly deteriorated, so an improvement in the trade-off is required. It was.

近年、より短波で長寿命なフェナンスリジン骨格を有する金属錯体についての開示がある。(例えば、特許文献1,2,3参照。)。   In recent years, there has been disclosed a metal complex having a phenanthridine skeleton having a shorter wavelength and a longer lifetime. (For example, see Patent Documents 1, 2, and 3.)

これらの化合物は、465nm付近にリン光発光極大ピークを有しており、有機エレクトロルミネッセンス素子用の青色ドーパントとして期待されている。   These compounds have a phosphorescence maximum peak in the vicinity of 465 nm, and are expected as blue dopants for organic electroluminescence devices.

しかしながら、上記の有機EL素子の発光寿命と発光効率は、いまだ実用的に満足できるものではなく改善が求められている。   However, the light emission lifetime and the light emission efficiency of the organic EL element are not yet satisfactory practically, and improvements are required.

米国特許出願公開第2007/0190359号明細書US Patent Application Publication No. 2007/0190359 国際公開第07/095118号パンフレットInternational Publication No. 07/095118 Pamphlet 米国特許出願公開第2008/0297033号明細書US Patent Application Publication No. 2008/0297033

本発明は、上記課題に鑑みなされたものであり、本発明の目的は、高い発光効率を示し、高い外部取り出し量子効率を示し、且つ、駆動寿命が長い(発光寿命が長い)有機EL素子、該有機EL素子を備えた照明装置及び表示装置、更には、前記有機EL素子に用いられる有機EL素子材料を提供することにある。   The present invention has been made in view of the above problems, and an object of the present invention is to provide an organic EL element that exhibits high light emission efficiency, exhibits high external extraction quantum efficiency, and has a long driving life (long light emission life). Another object is to provide an illumination device and a display device including the organic EL element, and further provide an organic EL element material used for the organic EL element.

本発明者等は、上記フェナンスリジン骨格を有する金属錯体について、鋭意検討した。具体的には、末端に嵩高いアミノ置換基を有する事で金属錯体同士の相互作用を抑える。更には、ホール輸送性ユニットであるアミノ基の導入により、発光層内でのキャリアバランスを向上させることができた。これらの効果により素子効率と素子寿命の向上を達成できた。   The present inventors diligently studied the metal complex having the phenanthridine skeleton. Specifically, the interaction between metal complexes is suppressed by having a bulky amino substituent at the terminal. Furthermore, the carrier balance in the light emitting layer could be improved by introducing an amino group which is a hole transporting unit. With these effects, the device efficiency and the device life can be improved.

本発明の上記目的は、下記の構成により達成される。   The above object of the present invention can be achieved by the following constitution.

1.陽極と陰極により挟まれた少なくとも1層の発光層を有する有機エレクトロルミネッセンス素子において、
該発光層が、下記一般式(1)または一般式(3)で表される部分構造を含む化合物を少なくとも1つ含有する有機層を有することを特徴とする有機エレクトロルミネッセンス素子。
1. In an organic electroluminescence device having at least one light emitting layer sandwiched between an anode and a cathode,
The light emitting layer has an organic layer containing at least one compound containing a partial structure represented by the following general formula (1) or general formula (3 ) .

Figure 0005531446
Figure 0005531446

〔〔式中、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1a〜E1qで構成される骨格は合計で18π電子を有する。E1aとE1pは各々異なり、炭素原子または窒素原子を表す。 1a 〜E 1e により形成される環はイミダゾール環またはピラゾール環を表す。1a〜R1iは各々、水素原子または置換基を表すが、R1a〜R1iのうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、一般式(1)中、置換基R1bが下記一般式(X)で表される場合を除く。〕 [In the formula, E 1a to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, and the skeleton composed of E 1a to E 1q has a total of 18π electrons. E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom. The ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring. R 1a to R 1i each represents a hydrogen atom or a substituent, and at least one of R 1a to R 1i represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the general formula (1), the case where the substituent R 1b is represented by the following general formula (X) is excluded. ]

Figure 0005531446
Figure 0005531446

〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または、芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕

Figure 0005531446
(式中、RおよびRは、水素、アルキル、およびアリールからなる群から独立に選択され;
およびRの少なくとも1つは、4個以上の原子を有するアルキルであり;
は、モノ-、ジ-、トリ-、またはテトラ置換基を表し;かつ、
は、水素、アルキル、およびアリールからなる群から独立に選択
される。
.前記一般式(A)におけるRNa及びRNbが、共にアルキル基を表すことを特徴とする前記1に記載の有機エレクトロルミネッセンス素子。
.前記一般式(A)におけるRNa及びRNbが、共に芳香族炭化水素環基を表すことを特徴とする前記1または2に記載の有機エレクトロルミネッセンス素子
.前記一般式(1)または一般式(3)で表される部分構造が、下記一般式(5)または一般式(7)で表されることを特徴とする前記1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。 [Wherein L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb form a ring. Not . n is 1. ]]
Figure 0005531446
Wherein R 1 and R 2 are independently selected from the group consisting of hydrogen, alkyl, and aryl;
At least one of R 1 and R 2 is an alkyl having 4 or more atoms;
R 3 represents a mono-, di-, tri-, or tetra substituent; and
R 3 is independently selected from the group consisting of hydrogen, alkyl, and aryl. )
2 . 2. The organic electroluminescence device according to 1 above, wherein RNa and RNb in the general formula (A) both represent an alkyl group.
3 . 3. The organic electroluminescence device as described in 1 or 2 above, wherein RNa and RNb in the general formula (A) both represent an aromatic hydrocarbon ring group .
4 . Partial structure represented by the general formula (1) or the general formula (3) is represented by the following general formula (5) or the 1 any one of 3, characterized by being represented by the general formula (7) The organic electroluminescent element of description.

Figure 0005531446
Figure 0005531446

〔〔式中、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1a〜E1eにより形成される環はイミダゾール環またはピラゾール環を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。E1aとE1pは各々異なり、炭素原子または窒素原子を表す。R1a〜R1i、R51〜R54及びR61〜R63は各々、水素原子または置換基を表すが、R1a〜R1i、R51〜R54、R61〜R63のうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、一般式(5)中、置換基R1bが前記一般式(X)で表される場合を除く。〕 [In the formula, E 1a to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring , and E 1f to E The ring formed by 1k represents a 5-membered aromatic heterocyclic ring, and the ring formed by E 11 to E 1q represents a 6-membered aromatic hydrocarbon ring or a 6-membered aromatic heterocyclic ring. E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom. R 1a to R 1i , R 51 to R 54 and R 61 to R 63 each represent a hydrogen atom or a substituent, and at least one of R 1a to R 1i , R 51 to R 54 , and R 61 to R 63 Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the general formula (5), the case where the substituent R 1b is represented by the general formula (X) is excluded. ]

Figure 0005531446
Figure 0005531446

〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕 [Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ] ]

.前記一般式(5)または一般式(7)で表される部分構造が、下記一般式(8)または一般式(10)で表されることを特徴とする前記に記載の有機エレクトロルミネッセンス素子。 5 . 5. The organic electroluminescence device according to 4 above, wherein the partial structure represented by the general formula (5) or the general formula (7) is represented by the following general formula (8) or the general formula (10) .

Figure 0005531446
Figure 0005531446

〔〔式中、E1f〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。R1c〜R1i、R51〜R56 及び61 65 各々、水素原子または置換基を表すが、R1c〜R1i、R51〜R56、R61 65 うち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、式中、置換基R 55 が前記一般式(X)で表される場合を除く。[In the formula, E 1f to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1f to E 1k represents a 5-membered aromatic heterocycle, and E 1l ring formed by to E 1q represents an aromatic hydrocarbon ring or 6-membered 6-membered aromatic heterocyclic ring. Each R 1c ~R 1i, R 51 ~R 56 and R 61 ~ R 65 represents a hydrogen atom or a substituent, R 1c to R 1i, among R 51 ~R 56, R 61 ~ R 65 at least Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the formula, the case where the substituent R 55 is represented by the general formula (X) is excluded. ]

Figure 0005531446
Figure 0005531446

〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
.前記一般式(5)または一般式(7)で表される部分構造が、下記一般式(11)または一般式(13)で表されることを特徴とする前記に記載の有機エレクトロルミネッセンス素子。
[Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ]]
6 . 5. The organic electroluminescence device according to 4 above, wherein the partial structure represented by the general formula (5) or the general formula (7) is represented by the following general formula (11) or the general formula (13). .

Figure 0005531446
Figure 0005531446

〔〔式中、E1f〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。R1c〜R1i、R51〜R56 及び61 65 各々、水素原子または置換基を表すが、R1c〜R1i、R51〜R56、R61 65 うち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、式中、置換基R 55 が前記一般式(X)で表される場合を除く。[In the formula, E 1f to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1f to E 1k represents a 5-membered aromatic heterocycle, and E 1l ring formed by to E 1q represents an aromatic hydrocarbon ring or 6-membered 6-membered aromatic heterocyclic ring. Each R 1c ~R 1i, R 51 ~R 56 and R 61 ~ R 65 represents a hydrogen atom or a substituent, R 1c to R 1i, among R 51 ~R 56, R 61 ~ R 65 at least Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the formula, the case where the substituent R 55 is represented by the general formula (X) is excluded. ]

Figure 0005531446
Figure 0005531446

〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
.前記一般式(A)におけるLが、「アルキル基、芳香族炭化水素環基または複素環基から導かれる2価以上の基」、−O−、−S−または−NRz−、或いは、これらの基を組み合わせてなる連結基(但し、−NRz−中、Rzは水素原子、アルキル基、芳香族炭化水素環基、複素環基を表す。)を表すことを特徴とする前記1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。
[Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ]]
7 . L 1 in the general formula (A) is “a divalent or higher valent group derived from an alkyl group, an aromatic hydrocarbon ring group or a heterocyclic group”, —O—, —S— or —NRz—, or these 1 to 6 above, which represents a linking group formed by combining these groups (wherein RZ represents a hydrogen atom, an alkyl group, an aromatic hydrocarbon ring group, or a heterocyclic group in -NRz-). The organic electroluminescent element as described in any one.

.前記一般式(A)におけるLが、アルキル基または芳香族炭化水素環基、または、これらの基を組み合わせてなる連結基を表すことを特徴とする前記に記載の有機エレクトロルミネッセンス素子。 8 . 8. The organic electroluminescence device as described in 7 above, wherein L 1 in the general formula (A) represents an alkyl group, an aromatic hydrocarbon ring group, or a linking group formed by combining these groups.

.前記一般式(A)におけるLが、アルキル基を表すことを特徴とする前記に記載の有機エレクトロルミネッセンス素子。 9 . 9. The organic electroluminescence device as described in 8 above, wherein L 1 in the general formula (A) represents an alkyl group.

10.前記有機層が前記一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれか1つで表される部分構造を含む化合物を少なくとも1種含有し、該有機層がウェットプロセスを用いて形成されたことを特徴とする前記1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。 10 . The organic layer has a partial structure represented by any one of the general formulas (1), (3), (5), (7), (8), (10), (11) or (13). 10. The organic electroluminescence device as described in any one of 1 to 9 above, which contains at least one compound containing the organic layer and is formed using a wet process.

11.前記Mが白金またはイリジウムであることを特徴とする前記1〜10のいずれか一項に記載の有機エレクトロルミネッセンス素子。 11 . Said M is platinum or iridium, The organic electroluminescent element as described in any one of said 1-10 characterized by the above-mentioned.

12.前記1に記載の一般式(1)または(3)で表される部分構造を含む化合物、前記に記載の一般式(5)または(7)で表される部分構造を含む化合物、前記に記載の一般式(8)または(10)で表される部分構造を含む化合物、若しくは、前記に記載の一般式(11)または(13)で表される部分構造を含む化合物、を含有することを特徴とする有機エレクトロルミネッセンス素子材料。 12 . Formula (1) or the compound containing the partial structure represented by (3) according to 1, general formula (5) or the compound containing the partial structure represented by (7) according to the 4, the 5 A compound containing the partial structure represented by the general formula (8) or (10) described in the above, or a compound containing the partial structure represented by the general formula (11) or (13) described in the above 6. An organic electroluminescent element material characterized by comprising:

13.前記1に記載の一般式(1)または(3)で表される部分構造を含む化合物、前記に記載の一般式(5)または(7)で表される部分構造を含む化合物、前記に記載の一般式(8)または(10)で表される部分構造を含む化合物、あるいは、前記に記載の一般式(11)または(13)で表される部分構造を含む化合物、において、Mが、白金またはイリジウムであることを特徴とする前記12に記載の有機エレクトロルミネッセンス素子材料。 13 . Formula (1) or the compound containing the partial structure represented by (3) according to 1, general formula (5) or the compound containing the partial structure represented by (7) according to the 4, the 5 In the compound containing the partial structure represented by the general formula (8) or (10) described in the above, or the compound containing the partial structure represented by the general formula (11) or (13) described in the above 6 , 13. The organic electroluminescent element material as described in 12 above, wherein M is platinum or iridium.

14.前記1〜11のいずれか一項に記載の有機エレクトロルミネッセンス素子を備えたことを特徴とする表示装置。 14 . A display device comprising the organic electroluminescence element according to any one of 1 to 11 above.

15.前記1〜11のいずれか一項に記載の有機エレクトロルミネッセンス素子を備えたことを特徴とする照明装置。 15 . A lighting device comprising the organic electroluminescence element according to any one of 1 to 11 above.

本発明によれば、高い発光効率を示し、高い外部取り出し量子効率を示し、且つ、駆動寿命が長い(発光寿命が長い)有機EL素子、該有機EL素子を備えた照明装置及び表示装置、更には、前記有機EL素子に用いられる有機EL素子材料を提供することができる。   According to the present invention, an organic EL element that exhibits high light emission efficiency, high external extraction quantum efficiency, and a long driving life (long light emission life), an illumination device and a display device including the organic EL element, and Can provide an organic EL element material used for the organic EL element.

有機EL素子から構成される表示装置の一例を示した模式図である。It is the schematic diagram which showed an example of the display apparatus comprised from an organic EL element. 表示部の模式図である。It is a schematic diagram of a display part. 照明装置の概略図である。It is the schematic of an illuminating device. 照明装置の断面図である。It is sectional drawing of an illuminating device.

本発明の有機エレクトロルミネッセンス素子においては、請求項1〜11のいずれか一項に規定される構成により、高い発光効率を示し、高い外部取り出し量子効率を示し、且つ、駆動寿命が長い(発光寿命が長い)有機EL素子、該有機EL素子を備えた照明装置及び表示装置を提供することができた。 In the organic electroluminescence device of the present invention, the structure defined in any one of claims 1 to 11 exhibits high light emission efficiency, high external extraction quantum efficiency, and long drive life (light emission life). However, it was possible to provide an organic EL element, and a lighting device and a display device including the organic EL element.

また、該素子の構成層の形成に有用な有機EL素子材料を分子設計することができた。   Moreover, the organic EL element material useful for formation of the component layer of the element could be molecularly designed.

以下、本発明に係る各構成要素の詳細について、順次説明する。   Hereinafter, details of each component according to the present invention will be sequentially described.

《金属錯体(金属錯体化合物ともいう)》
本発明に係る金属錯体(金属錯体化合物ともいう)について説明する。
《Metal complex (also called metal complex compound)》
The metal complex (also referred to as a metal complex compound) according to the present invention will be described.

本発明者等は、有機EL素子の発光層に用いる有機EL素子材料に着目、特に発光ドーパントとして用いる金属錯体化合物について種々検討した。   The present inventors paid attention to the organic EL element material used for the light emitting layer of the organic EL element, and examined various metal complex compounds used as a light emitting dopant.

その中で、従来公知の金属錯体化合物の配位子においては、金属錯体の基本骨格に電子吸引性の置換基を導入して得られた発光材料は、素子の発光寿命が大幅に劣化しやすくなるという問題点があることがわかったが、一方において、発光材料の発光波長が短波化して青色が達成され、且つ、高効率の素子を達成できるという効果が得られることがわかってきた。   Among them, in the ligands of conventionally known metal complex compounds, the light emitting material obtained by introducing an electron-withdrawing substituent into the basic skeleton of the metal complex tends to greatly deteriorate the light emission lifetime of the device. However, on the other hand, it has been found that the emission wavelength of the light emitting material is shortened to achieve blue, and that an effect of achieving a highly efficient device can be obtained.

そこで、本発明者らは、金属錯体の基本骨格に置換基を導入することで、波長のコントロールや寿命の改善を図るという、従来公知のアプローチではなく、置換基の導入と同様の効果が期待できる縮合環に着目した。   Therefore, the present inventors are expected to achieve the same effect as the introduction of substituents, rather than a conventionally known approach of introducing a substituent into the basic skeleton of the metal complex to control the wavelength and improve the lifetime. We focused on the fused ring that can be formed.

その結果、幾つかの構造で寿命の改善傾向が見出された。しかしながら、これまで知られているような縮合環を導入した場合には、発光波長のレッドシフトが著しく、緑、赤色発光となってしまっていた。   As a result, the improvement tendency of lifetime was found in several structures. However, when a fused ring as known so far is introduced, the red shift of the emission wavelength is remarkable, resulting in green and red emission.

本発明者等は更に検討を進め、本発明に係る一般式(1)または(3)で表される部分構造を含む化合物(金属錯体、金属錯体化合物等ともいう)に示されているような縮合環を導入した場合、発光材料の発光波長シフトが小さく、且つ、所望の発光波長で、長寿命化を実現した発光ドーパントの開発に成功した。 The present inventors have further studied and as shown in the compounds (also referred to as metal complexes, metal complex compounds, etc.) containing the partial structure represented by the general formula (1) or (3) according to the present invention. When a condensed ring is introduced, the light emitting wavelength shift of the light emitting material is small, and a light emitting dopant that achieves a long lifetime at a desired light emitting wavelength has been successfully developed.

更に、これらの一般式(1)または(3)で表される部分構造を含む化合物(金属錯体)に置換している原子の大きさと電子効果を組み合わせることを考慮するにより、波長を変化させることなく、長寿命化と高効率化の両立を共に可能にする効果を見出した。 Furthermore, the wavelength can be changed in consideration of combining the size of atoms substituted with the compound (metal complex) containing the partial structure represented by the general formula (1) or (3) and the electronic effect. In addition, we found an effect that makes it possible to achieve both long life and high efficiency.

すなわち、一般式(1)または(3)で表される部分構造を有する化合物に上記一般式(A)で表される置換基を特定位置に置換させることで、化合物自体の凝集性を抑制すると共に、ホール輸送性ユニットであるアミノ基の導入により、発光層内でのキャリアバランスを向上させ、発光効率も大幅に向上するというものである。 That is, the compound having the partial structure represented by the general formula (1) or (3) is substituted with the substituent represented by the general formula (A) at a specific position, thereby suppressing aggregation of the compound itself. At the same time, the introduction of an amino group which is a hole transporting unit improves the carrier balance in the light emitting layer and greatly improves the light emission efficiency.

更に、分子の見かけの嵩高さが向上したことで分子の振動が抑えられるため、励起状態からの熱失活などの非発光成分が減少し、発光効率も大幅に向上するというものである。   Furthermore, since the apparent bulkiness of the molecules is improved, the vibration of the molecules can be suppressed, so that non-luminescent components such as heat deactivation from the excited state are reduced, and the luminous efficiency is greatly improved.

また、本発明に係る一般式(1)または(3)で示される部分構造に係る配位子であっても、その他組み合わせる補助配位子や置換基自身が長波なものを置換基として導入することにより、金属錯体の発光波長を所望の領域に制御できる。 Moreover, even if it is a ligand which concerns on the partial structure shown by General formula (1) or (3) which concerns on this invention, the auxiliary | assistant ligand combined or the substituent itself introduces a long wave thing as a substituent. Thus, the emission wavelength of the metal complex can be controlled in a desired region.

従って、金属錯体の発光波長を長波な領域(緑〜赤)に制御する機能を付与するための分子設計は、本発明に係る一般式(1)または(3)で表される部分構造を金属錯体の基本骨格設計の出発点とすることにより可能である。 Therefore, the molecular design for imparting the function of controlling the emission wavelength of the metal complex to a long wave region (green to red) is a metal of the partial structure represented by the general formula (1) or (3) according to the present invention. This is possible by setting the starting point for the basic skeleton design of the complex.

本発明に係る一般式(1)または(3)で示される部分構造を有する化合物(金属錯体)は、各々Mで表される遷移金属元素の価数により、複数の配位子を有することができるが、前記配位子は全て同一でもよく、また、各々異なる構造を有する配位子を有していてもよい。 The compound (metal complex) having a partial structure represented by the general formula (1) or (3) according to the present invention may have a plurality of ligands depending on the valence of the transition metal element represented by M. However, the ligands may all be the same, or may have ligands having different structures.

しかしながら、本発明に記載の効果を好ましく得る観点から、錯体中の配位子の種類は、好ましくは1〜2種類から構成されることが好ましく、更に好ましくは1種類である。   However, from the viewpoint of preferably obtaining the effects described in the present invention, the type of ligand in the complex is preferably composed of 1 to 2 types, and more preferably 1 type.

本発明に係る金属錯体を形成する配位子としては、本発明に係る一般式(1)または(3)で示される部分構造から遷移金属元素Mを除いた部分(配位子)のみから構成された化合物が最も好ましく用いられる。 As a ligand which forms the metal complex which concerns on this invention, it is comprised only from the part (ligand) remove | excluding the transition metal element M from the partial structure shown by General formula (1) or (3) which concerns on this invention. The compound obtained is most preferably used.

ここで、配位子とは、本発明に係る一般式(1)または(3)で示される部分構造から遷移金属元素Mを除いた部分が、各々配位子である。 Here, the ligand is a ligand obtained by removing the transition metal element M from the partial structure represented by the general formula (1) or (3) according to the present invention.

また、本発明に係る金属錯体の形成に用いることのできる、従来公知の配位子については、後に詳細に説明する。   Further, conventionally known ligands that can be used for forming the metal complex according to the present invention will be described in detail later.

《Mで表される元素周期表における8族〜10族の遷移金属元素》
また、本発明に係る一般式(1)または(3)で表される部分構造を有する金属錯体の形成に用いられる金属としては、元素周期表の8〜10族の遷移金属元素(単に遷移金属ともいう)が用いられるが、中でも、イリジウム、白金が好ましい遷移金属元素として挙げられる。
<< Group 8-10 transition metal element in the periodic table of elements represented by M >>
In addition, as a metal used for forming a metal complex having a partial structure represented by the general formula (1) or (3) according to the present invention, a transition metal element of group 8 to 10 of the periodic table (simply a transition metal) Among them, iridium and platinum are preferable as transition metal elements.

以下、本発明に係る一般式(1)または(3)で表される部分構造を有する化合物(金属錯体)の配位子が有する部分構造について説明する。 Hereinafter, the partial structure which the ligand of the compound (metal complex) which has the partial structure represented by General formula (1) or (3) based on this invention has is demonstrated.

《一般式(1)または(3)で表される部分構造》
一般式(1)または(3)において、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1a〜E1qで構成される骨格は合計で18π電子を有する。E1aとE1pは各々異なり、炭素原子または窒素原子を表す。 1a 〜E 1e により形成される環はイミダゾール環またはピラゾール環を表す。
<< Partial structure represented by general formula (1) or (3) >>
In General Formula (1) or (3), E 1a to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom, or a sulfur atom, and the skeleton composed of E 1a to E 1q has a total of 18π electrons. . E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom. The ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring.

一般式(1)または(3)において、R1a〜R1iは各々、水素原子または置換基を表すが、R1a〜R1iのうち少なくとも1つは前記一般式(A)で表される置換基を表す。 In the general formula (1) or (3) , R 1a to R 1i each represents a hydrogen atom or a substituent, and at least one of R 1a to R 1i is a substitution represented by the general formula (A). Represents a group.

1a〜R1iで表される置換基(以下、「R1a〜R1iで各々表される置換基」または、単に「前述の置換基」ともいう。)としては、アルキル基(例えば、メチル基、エチル基、プロピル基、イソプロピル基、tert−ブチル基、ペンチル基、ヘキシル基、オクチル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基等)、シクロアルキル基(例えば、シクロペンチル基、シクロヘキシル基等)、アルケニル基(例えば、ビニル基、アリル基等)、アルキニル基(例えば、エチニル基、プロパルギル基等)、芳香族炭化水素基(芳香族炭素環基、アリール基等ともいい、例えば、フェニル基、p−クロロフェニル基、メシチル基、トリル基、キシリル基、ナフチル基、アントリル基、アズレニル基、アセナフテニル基、フルオレニル基、フェナントリル基、インデニル基、ピレニル基、ビフェニリル基等)、芳香族複素環基(例えば、ピリジル基、ピリミジニル基、フリル基、ピロリル基、イミダゾリル基、ベンゾイミダゾリル基、ピラゾリル基、ピラジニル基、トリアゾリル基(例えば、1,2,4−トリアゾール−1−イル基、1,2,3−トリアゾール−1−イル基等)、オキサゾリル基、ベンゾオキサゾリル基、チアゾリル基、イソオキサゾリル基、イソチアゾリル基、フラザニル基、チエニル基、キノリル基、ベンゾフリル基、ジベンゾフリル基、ベンゾチエニル基、ジベンゾチエニル基、インドリル基、カルバゾリル基、カルボリニル基、ジアザカルバゾリル基(前記カルボリニル基のカルボリン環を構成する炭素原子の一つが窒素原子で置き換わったものを示す)、キノキサリニル基、ピリダジニル基、トリアジニル基、キナゾリニル基、フタラジニル基等)、複素環基(例えば、ピロリジル基、イミダゾリジル基、モルホリル基、オキサゾリジル基等)、アルコキシ基(例えば、メトキシ基、エトキシ基、プロピルオキシ基、ペンチルオキシ基、ヘキシルオキシ基、オクチルオキシ基、ドデシルオキシ基等)、シクロアルコキシ基(例えば、シクロペンチルオキシ基、シクロヘキシルオキシ基等)、アリールオキシ基(例えば、フェノキシ基、ナフチルオキシ基等)、アルキルチオ基(例えば、メチルチオ基、エチルチオ基、プロピルチオ基、ペンチルチオ基、ヘキシルチオ基、オクチルチオ基、ドデシルチオ基等)、シクロアルキルチオ基(例えば、シクロペンチルチオ基、シクロヘキシルチオ基等)、アリールチオ基(例えば、フェニルチオ基、ナフチルチオ基等)、アルコキシカルボニル基(例えば、メチルオキシカルボニル基、エチルオキシカルボニル基、ブチルオキシカルボニル基、オクチルオキシカルボニル基、ドデシルオキシカルボニル基等)、アリールオキシカルボニル基(例えば、フェニルオキシカルボニル基、ナフチルオキシカルボニル基等)、スルファモイル基(例えば、アミノスルホニル基、メチルアミノスルホニル基、ジメチルアミノスルホニル基、ブチルアミノスルホニル基、ヘキシルアミノスルホニル基、シクロヘキシルアミノスルホニル基、オクチルアミノスルホニル基、ドデシルアミノスルホニル基、フェニルアミノスルホニル基、ナフチルアミノスルホニル基、2−ピリジルアミノスルホニル基等)、アシル基(例えば、アセチル基、エチルカルボニル基、プロピルカルボニル基、ペンチルカルボニル基、シクロヘキシルカルボニル基、オクチルカルボニル基、2−エチルヘキシルカルボニル基、ドデシルカルボニル基、フェニルカルボニル基、ナフチルカルボニル基、ピリジルカルボニル基等)、アシルオキシ基(例えば、アセチルオキシ基、エチルカルボニルオキシ基、ブチルカルボニルオキシ基、オクチルカルボニルオキシ基、ドデシルカルボニルオキシ基、フェニルカルボニルオキシ基等)、アミド基(例えば、メチルカルボニルアミノ基、エチルカルボニルアミノ基、ジメチルカルボニルアミノ基、プロピルカルボニルアミノ基、ペンチルカルボニルアミノ基、シクロヘキシルカルボニルアミノ基、2−エチルヘキシルカルボニルアミノ基、オクチルカルボニルアミノ基、ドデシルカルボニルアミノ基、フェニルカルボニルアミノ基、ナフチルカルボニルアミノ基等)、カルバモイル基(例えば、アミノカルボニル基、メチルアミノカルボニル基、ジメチルアミノカルボニル基、プロピルアミノカルボニル基、ペンチルアミノカルボニル基、シクロヘキシルアミノカルボニル基、オクチルアミノカルボニル基、2−エチルヘキシルアミノカルボニル基、ドデシルアミノカルボニル基、フェニルアミノカルボニル基、ナフチルアミノカルボニル基、2−ピリジルアミノカルボニル基等)、ウレイド基(例えば、メチルウレイド基、エチルウレイド基、ペンチルウレイド基、シクロヘキシルウレイド基、オクチルウレイド基、ドデシルウレイド基、フェニルウレイド基、ナフチルウレイド基、2−ピリジルアミノウレイド基等)、スルフィニル基(例えば、メチルスルフィニル基、エチルスルフィニル基、ブチルスルフィニル基、シクロヘキシルスルフィニル基、2−エチルヘキシルスルフィニル基、ドデシルスルフィニル基、フェニルスルフィニル基、ナフチルスルフィニル基、2−ピリジルスルフィニル基等)、アルキルスルホニル基(例えば、メチルスルホニル基、エチルスルホニル基、ブチルスルホニル基、シクロヘキシルスルホニル基、2−エチルヘキシルスルホニル基、ドデシルスルホニル基等)、アリールスルホニル基またはヘテロアリールスルホニル基(例えば、フェニルスルホニル基、ナフチルスルホニル基、2−ピリジルスルホニル基等)、ハロゲン原子(例えば、フッ素原子、塩素原子、臭素原子等)、フッ化炭化水素基(例えば、フルオロメチル基、トリフルオロメチル基、ペンタフルオロエチル基、ペンタフルオロフェニル基等)、シアノ基、ニトロ基、ヒドロキシ基、メルカプト基、シリル基(例えば、トリメチルシリル基、トリイソプロピルシリル基、トリフェニルシリル基、フェニルジエチルシリル基等)等が挙げられる。これらの置換基は上記の置換基によって更に置換されていてもよい。これらの置換基は複数が互いに結合して環を形成していてもよい。 Examples of the substituent represented by R 1a to R 1i (hereinafter, also referred to as “substituents represented by R 1a to R 1i ” or simply “the aforementioned substituent”) include an alkyl group (for example, methyl Group, ethyl group, propyl group, isopropyl group, tert-butyl group, pentyl group, hexyl group, octyl group, dodecyl group, tridecyl group, tetradecyl group, pentadecyl group, etc.), cycloalkyl group (for example, cyclopentyl group, cyclohexyl group) Etc.), alkenyl groups (eg, vinyl groups, allyl groups, etc.), alkynyl groups (eg, ethynyl groups, propargyl groups, etc.), aromatic hydrocarbon groups (aromatic carbocyclic groups, aryl groups, etc.), such as phenyl Group, p-chlorophenyl group, mesityl group, tolyl group, xylyl group, naphthyl group, anthryl group, azulenyl group, acenaphthenyl Group, fluorenyl group, phenanthryl group, indenyl group, pyrenyl group, biphenylyl group, etc.), aromatic heterocyclic group (for example, pyridyl group, pyrimidinyl group, furyl group, pyrrolyl group, imidazolyl group, benzimidazolyl group, pyrazolyl group, pyrazinyl group) , Triazolyl group (for example, 1,2,4-triazol-1-yl group, 1,2,3-triazol-1-yl group, etc.), oxazolyl group, benzoxazolyl group, thiazolyl group, isoxazolyl group, isothiazolyl Group, furazanyl group, thienyl group, quinolyl group, benzofuryl group, dibenzofuryl group, benzothienyl group, dibenzothienyl group, indolyl group, carbazolyl group, carbolinyl group, diazacarbazolyl group (which constitutes the carboline ring of the carbolinyl group) One of the carbon atoms Quinoxalinyl group, pyridazinyl group, triazinyl group, quinazolinyl group, phthalazinyl group, etc.), heterocyclic group (for example, pyrrolidyl group, imidazolidyl group, morpholyl group, oxazolidyl group, etc.), alkoxy group (for example, Methoxy group, ethoxy group, propyloxy group, pentyloxy group, hexyloxy group, octyloxy group, dodecyloxy group, etc.), cycloalkoxy group (for example, cyclopentyloxy group, cyclohexyloxy group, etc.), aryloxy group (for example, Phenoxy group, naphthyloxy group, etc.), alkylthio group (eg, methylthio group, ethylthio group, propylthio group, pentylthio group, hexylthio group, octylthio group, dodecylthio group, etc.), cycloalkylthio group (eg, cyclopentylthio group, Cyclohexylthio group etc.), arylthio group (eg phenylthio group, naphthylthio group etc.), alkoxycarbonyl group (eg methyloxycarbonyl group, ethyloxycarbonyl group, butyloxycarbonyl group, octyloxycarbonyl group, dodecyloxycarbonyl group etc.) ), Aryloxycarbonyl group (for example, phenyloxycarbonyl group, naphthyloxycarbonyl group, etc.), sulfamoyl group (for example, aminosulfonyl group, methylaminosulfonyl group, dimethylaminosulfonyl group, butylaminosulfonyl group, hexylaminosulfonyl group, Cyclohexylaminosulfonyl group, octylaminosulfonyl group, dodecylaminosulfonyl group, phenylaminosulfonyl group, naphthylaminosulfonyl group, 2-pyridyla Nosulfonyl group, etc.), acyl groups (for example, acetyl group, ethylcarbonyl group, propylcarbonyl group, pentylcarbonyl group, cyclohexylcarbonyl group, octylcarbonyl group, 2-ethylhexylcarbonyl group, dodecylcarbonyl group, phenylcarbonyl group, naphthylcarbonyl) Group, pyridylcarbonyl group, etc.), acyloxy group (eg, acetyloxy group, ethylcarbonyloxy group, butylcarbonyloxy group, octylcarbonyloxy group, dodecylcarbonyloxy group, phenylcarbonyloxy group, etc.), amide group (eg, methyl Carbonylamino group, ethylcarbonylamino group, dimethylcarbonylamino group, propylcarbonylamino group, pentylcarbonylamino group, cyclohexylcarbonylamino group, 2-ethyl Ruhexylcarbonylamino group, octylcarbonylamino group, dodecylcarbonylamino group, phenylcarbonylamino group, naphthylcarbonylamino group, etc.), carbamoyl group (for example, aminocarbonyl group, methylaminocarbonyl group, dimethylaminocarbonyl group, propylaminocarbonyl group) Pentylaminocarbonyl group, cyclohexylaminocarbonyl group, octylaminocarbonyl group, 2-ethylhexylaminocarbonyl group, dodecylaminocarbonyl group, phenylaminocarbonyl group, naphthylaminocarbonyl group, 2-pyridylaminocarbonyl group, etc.), ureido group (for example, Methylureido group, ethylureido group, pentylureido group, cyclohexylureido group, octylureido group, dodecylureido group, Nylureido group, naphthylureido group, 2-pyridylaminoureido group, etc.), sulfinyl group (for example, methylsulfinyl group, ethylsulfinyl group, butylsulfinyl group, cyclohexylsulfinyl group, 2-ethylhexylsulfinyl group, dodecylsulfinyl group, phenylsulfinyl group, Naphthylsulfinyl group, 2-pyridylsulfinyl group, etc.), alkylsulfonyl group (eg, methylsulfonyl group, ethylsulfonyl group, butylsulfonyl group, cyclohexylsulfonyl group, 2-ethylhexylsulfonyl group, dodecylsulfonyl group, etc.), arylsulfonyl group or A heteroarylsulfonyl group (eg, phenylsulfonyl group, naphthylsulfonyl group, 2-pyridylsulfonyl group, etc.), halogen atom (eg, fluorine Atom, chlorine atom, bromine atom, etc.), fluorinated hydrocarbon group (eg, fluoromethyl group, trifluoromethyl group, pentafluoroethyl group, pentafluorophenyl group, etc.), cyano group, nitro group, hydroxy group, mercapto group And silyl groups (for example, trimethylsilyl group, triisopropylsilyl group, triphenylsilyl group, phenyldiethylsilyl group, etc.). These substituents may be further substituted with the above substituents. A plurality of these substituents may be bonded to each other to form a ring.

但し、一般式(1)中、置換基R 1b が前記一般式(X)で表される場合を除く。
一般式(1)または(3)において、R1a〜R1iは各々、水素原子または置換基を表すが、R1a〜R1iのうち少なくとも1つは前記一般式(A)で表される置換基を表す。
However, in the general formula (1), the case where the substituent R 1b is represented by the general formula (X) is excluded.
In the general formula (1) or (3) , R 1a to R 1i each represents a hydrogen atom or a substituent, and at least one of R 1a to R 1i is a substitution represented by the general formula (A). Represents a group.

以下、一般式(A)で表される置換基について説明する。   Hereinafter, the substituent represented by the general formula (A) will be described.

(一般式(A)で表される置換基)
一般式(1)または(3)におけるR1a〜R1iのうち少なくとも1つで表される一般式(A)において、Lは連結基を表し、RNa、RNbは各々、水素原子、アルキル基、芳香族炭化水素基または、芳香族複素環基を表し、RNa、RNbが環を形成することはない。nは1である。
(Substituent represented by formula (A))
In general formula (A) represented by at least one of R 1a to R 1i in general formula (1) or (3), L 1 represents a linking group, and RNa and RNb each represent a hydrogen atom or an alkyl group. Represents an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. n is 1.

で表される連結基としては、「アルキル基、芳香族炭化水素環基または複素環基から導かれる2価以上の基、好ましくは2〜4価の基」、−O−、−S−または−NRz−、或いは、これらの基を組み合わせてなる連結基(但し、−NRz−中、Rzは水素原子、アルキル基、芳香族炭化水素環基、複素環基を表す。)であることが好ましく、連結基Lが、「アルキル基または芳香族炭化水素環基から導かれる2価以上の基、好ましくは2〜4価の基」、或いは、これらの基を組み合わせてなる連結基、であることがより好ましく、連結基Lが、アルキル基から導かれる2価以上の基、好ましくは2〜4価の基、であることが特に好ましい。 Examples of the linking group represented by L 1 include “a divalent or higher valent group derived from an alkyl group, aromatic hydrocarbon ring group or heterocyclic group, preferably a divalent to tetravalent group”, —O—, —S. -Or -NRz- or a linking group formed by combining these groups (wherein RZ represents a hydrogen atom, an alkyl group, an aromatic hydrocarbon ring group or a heterocyclic group in -NRz-). The linking group L 1 is “a divalent or higher valent group derived from an alkyl group or an aromatic hydrocarbon ring group, preferably a 2 to 4 valent group”, or a linking group formed by combining these groups, It is more preferable that the linking group L 1 is a divalent or higher valent group derived from an alkyl group, preferably a 2 to 4 valent group.

で表される連結基が導かれる該アルキル基としては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、tert−ブチル基、ペンチル基、ヘキシル基、オクチル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、シクロペンチル基、シクロヘキシル基、ビニル基、アリル基、エチニル基、プロパルギル基等が挙げられる。 Examples of the alkyl group from which the linking group represented by L 1 is derived include a methyl group, an ethyl group, a propyl group, an isopropyl group, a tert-butyl group, a pentyl group, a hexyl group, an octyl group, a dodecyl group, and a tridecyl group. Tetradecyl group, pentadecyl group, cyclopentyl group, cyclohexyl group, vinyl group, allyl group, ethynyl group, propargyl group and the like.

で表される連結基が導かれる該芳香族炭化水素環基としては、例えば、フェニル基、p−クロロフェニル基、メシチル基、トリル基、キシリル基、ナフチル基、アントリル基、アズレニル基、アセナフテニル基、フルオレニル基、フェナントリル基、インデニル基、ピレニル基、ビフェニリル基等が挙げられる。 Examples of the aromatic hydrocarbon ring group from which the linking group represented by L 1 is derived include a phenyl group, a p-chlorophenyl group, a mesityl group, a tolyl group, a xylyl group, a naphthyl group, an anthryl group, an azulenyl group, and an acenaphthenyl group. Group, fluorenyl group, phenanthryl group, indenyl group, pyrenyl group, biphenylyl group and the like.

で表される連結基が導かれる該複素環基としては、芳香族複素環基(例えば、ピリジル基、ピリミジニル基、フリル基、ピロリル基、イミダゾリル基、ベンゾイミダゾリル基、ピラゾリル基、ピラジニル基、トリアゾリル基(例えば、1,2,4−トリアゾール−1−イル基、1,2,3−トリアゾール−1−イル基等)、オキサゾリル基、ベンゾオキサゾリル基、チアゾリル基、イソオキサゾリル基、イソチアゾリル基、フラザニル基、チエニル基、キノリル基、ベンゾフリル基、ジベンゾフリル基、ベンゾチエニル基、ジベンゾチエニル基、インドリル基、カルバゾリル基、カルボリニル基、ジアザカルバゾリル基(前記カルボリニル基のカルボリン環を構成する炭素原子の一つが窒素原子で置き換わったものを示す)、キノキサリニル基、ピリダジニル基、トリアジニル基、キナゾリニル基、フタラジニル基等)、複素環基(例えば、ピロリジル基、イミダゾリジル基、モルホリル基、オキサゾリジル基等)が挙げられる。 Examples of the heterocyclic group from which the linking group represented by L 1 is derived include an aromatic heterocyclic group (for example, pyridyl group, pyrimidinyl group, furyl group, pyrrolyl group, imidazolyl group, benzoimidazolyl group, pyrazolyl group, pyrazinyl group, Triazolyl group (for example, 1,2,4-triazol-1-yl group, 1,2,3-triazol-1-yl group, etc.), oxazolyl group, benzoxazolyl group, thiazolyl group, isoxazolyl group, isothiazolyl group , Furazanyl group, thienyl group, quinolyl group, benzofuryl group, dibenzofuryl group, benzothienyl group, dibenzothienyl group, indolyl group, carbazolyl group, carbolinyl group, diazacarbazolyl group (which constitutes the carboline ring of the carbolinyl group) (Indicates one of the carbon atoms replaced by a nitrogen atom) Nyl group, pyridazinyl group, triazinyl group, quinazolinyl group, phthalazinyl group and the like) and heterocyclic groups (for example, pyrrolidyl group, imidazolidyl group, morpholyl group, oxazolidyl group and the like).

で表される連結基として、好ましくは、例えば、メチレン基、エチレン基、1−メチルエチレン基、1−イソプロピルエチレン基、ペンチレン基、−CHO−基、−CHOCH−基、−CHSCH−基、フェニレン基、−((C)(−CH)−基、−(C)−CH−基、−(C)−O−基、−S−基、−CO−基、−CONH−基、−SONH−基、−SO−基、ナフチレン基、フェニル基から導かれる3価の基、チエニレン基、ピリジレン基、ピリミヂニレン基、キノリニレン基、等が挙げられる。 The linking group represented by L 1 is preferably, for example, a methylene group, an ethylene group, a 1-methylethylene group, a 1-isopropylethylene group, a pentylene group, a —CH 2 O— group, a —CH 2 OCH 2 — group. , —CH 2 SCH 2 — group, phenylene group, — ((C 6 H 2 ) (— CH 3 ) 2 ) — group, — (C 6 H 4 ) —CH 2 — group, — (C 6 H 4 ) —O— group, —S— group, —CO— group, —CONH— group, —SO 2 NH— group, —SO 2 — group, naphthylene group, trivalent group derived from phenyl group, thienylene group, pyridylene Group, pyrimidinylene group, quinolinylene group, and the like.

一般式(A)において、RNa、RNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表す。   In the general formula (A), RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group, or an aromatic heterocyclic group.

一般式(A)におけるRNa、RNbが、共にアルキル基であることが好ましい。また、RNa、RNbが、共に芳香族炭化水素環基であることが好ましい。   It is preferable that RNa and RNb in the general formula (A) are both alkyl groups. Moreover, it is preferable that both RNa and RNb are aromatic hydrocarbon ring groups.

RNa、RNbで表されるアルキル基としては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、tert−ブチル基、ペンチル基、ヘキシル基、オクチル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基シクロペンチル基、シクロヘキシル基等が挙げられる。   Examples of the alkyl group represented by RNa and RNb include methyl group, ethyl group, propyl group, isopropyl group, tert-butyl group, pentyl group, hexyl group, octyl group, dodecyl group, tridecyl group, tetradecyl group, pentadecyl group. Group cyclopentyl group, cyclohexyl group and the like.

好ましくは、メチル基、エチル基、i−プロピル基、シクロヘキシル基、等が挙げられる。   Preferably, a methyl group, an ethyl group, i-propyl group, a cyclohexyl group, etc. are mentioned.

RNa、RNbで表される芳香族炭化水素基としては、芳香族炭素環基、アリール基等ともいい、例えば、フェニル基、p−クロロフェニル基、メシチル基、トリル基、キシリル基、ナフチル基、アントリル基、アズレニル基、アセナフテニル基、フルオレニル基、フェナントリル基、インデニル基、ピレニル基、ビフェニリル基等が挙げられる。好ましくは、フェニル基等が挙げられる。   The aromatic hydrocarbon group represented by RNa or RNb is also called an aromatic carbocyclic group or an aryl group. For example, phenyl group, p-chlorophenyl group, mesityl group, tolyl group, xylyl group, naphthyl group, anthryl group. Group, azulenyl group, acenaphthenyl group, fluorenyl group, phenanthryl group, indenyl group, pyrenyl group, biphenylyl group and the like. Preferably, a phenyl group etc. are mentioned.

RNa、RNbで表される芳香族複素環基としては、例えば、ピリジル基、ピリミジニル基、フリル基、ピロリル基、イミダゾリル基、ベンゾイミダゾリル基、ピラゾリル基、ピラジニル基、トリアゾリル基(例えば、1,2,4−トリアゾール−1−イル基、1,2,3−トリアゾール−1−イル基等)、オキサゾリル基、ベンゾオキサゾリル基、チアゾリル基、イソオキサゾリル基、イソチアゾリル基、フラザニル基、チエニル基、キノリル基、ベンゾフリル基、ジベンゾフリル基、ベンゾチエニル基、ジベンゾチエニル基、インドリル基、カルバゾリル基、カルボリニル基、ジアザカルバゾリル基(前記カルボリニル基のカルボリン環を構成する炭素原子の一つが窒素原子で置き換わったものを示す)、キノキサリニル基、ピリダジニル基、トリアジニル基、キナゾリニル基、フタラジニル基等が挙げられる。   Examples of the aromatic heterocyclic group represented by RNa and RNb include a pyridyl group, a pyrimidinyl group, a furyl group, a pyrrolyl group, an imidazolyl group, a benzoimidazolyl group, a pyrazolyl group, a pyrazinyl group, and a triazolyl group (for example, 1,2, 4-triazol-1-yl group, 1,2,3-triazol-1-yl group, etc.), oxazolyl group, benzoxazolyl group, thiazolyl group, isoxazolyl group, isothiazolyl group, furazanyl group, thienyl group, quinolyl group , Benzofuryl group, dibenzofuryl group, benzothienyl group, dibenzothienyl group, indolyl group, carbazolyl group, carbolinyl group, diazacarbazolyl group (one of the carbon atoms constituting the carboline ring of the carbolinyl group is replaced by a nitrogen atom) Quinoxalinyl group, pyridazini Group, triazinyl group, quinazolinyl group, and phthalazinyl group.

また、上記一般式(1)または(3)で表される部分構造の好ましい態様として、前記一般式(5)または(7)で表される部分構造が挙げられる。 Moreover, the partial structure represented by the said General formula (5) or (7) is mentioned as a preferable aspect of the partial structure represented by the said General formula (1) or (3) .

《一般式(5)または(7)で表される部分構造》
一般式(5)または(7)において、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し(E1a〜E1qで構成される骨格は合計で18π電子を有する。)、E1aとE1pは各々異なり、炭素原子または窒素原子を表す。
<< Partial structure represented by general formula (5) or (7) >>
The general formula (5) or in (7), E 1a to E 1q are each a carbon atom, a nitrogen atom, 18Pai electrons represents an oxygen atom or a sulfur atom (backbone comprised of E 1a to E 1q in total E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom.

一般式(5)または(7)において、E1a〜E1eにより形成される環はイミダゾール環またはピラゾール環を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表す。 In General Formula (5) or (7), the ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring, and the ring formed from E 1f to E 1k represents a 5-membered aromatic heterocyclic ring. .

これらの各環は各々更に、前述の置換基を有していても良い。   Each of these rings may further have the aforementioned substituent.

一般式(5)または(7)において、E1f〜E1kにより形成される5員の芳香族複素環としては、例えば、オキサゾール環、チアゾール環、オキサジアゾール環、オキサトリアゾール環、イソオキサゾール環、テトラゾール環、チアジアゾール環、チアトリアゾール環、イソチアゾール環、チオフェン環、フラン環、ピロール環、イミダゾール環、ピラゾール環、トリアゾール環等が挙げられる。 The general formula (5) or (7), as the aromatic heterocyclic 5-membered formed by E 1f to E 1k, for example, an oxazole ring, a thiazole ring, an oxadiazole ring, oxatriazole ring, iso Examples thereof include an oxazole ring, a tetrazole ring, a thiadiazole ring, a thiatriazole ring, an isothiazole ring, a thiophene ring, a furan ring, a pyrrole ring, an imidazole ring, a pyrazole ring, and a triazole ring.

上記の中でも、チオフェン環、フラン環、ピロール環、イミダゾール環、ピラゾール環等が好ましく、特に好ましくは、チオフェン環、フラン環、ピロール環が挙げられる。   Among these, a thiophene ring, a furan ring, a pyrrole ring, an imidazole ring, a pyrazole ring and the like are preferable, and a thiophene ring, a furan ring, and a pyrrole ring are particularly preferable.

これらの各環は各々更に、前述の置換基を有していても良い。   Each of these rings may further have the aforementioned substituent.

一般式(5)または(7)において、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。 The general formula (5) or (7), the ring formed by E 1l to E 1q represents an aromatic hydrocarbon ring or 6-membered 6-membered aromatic heterocyclic ring.

1l〜E1qにより形成される6員の芳香族炭化水素環としては、ベンゼン環が挙げられる。該ベンゼン環は更に前述の置換基を有していても良い。 Examples of the 6-membered aromatic hydrocarbon ring formed by E 11 to E 1q include a benzene ring. The benzene ring may further have the aforementioned substituent.

1l〜E1qにより形成される6員の芳香族複素環としては、例えば、ピリジン環、ピリダジン環、ピリミジン環、ピラジン環、トリアジン環等が挙げられる。これらの環は、更に前述の置換基を有していても良い。 Examples of the 6-membered aromatic heterocycle formed by E 11 to E 1q include a pyridine ring, a pyridazine ring, a pyrimidine ring, a pyrazine ring, and a triazine ring. These rings may further have the aforementioned substituent.

一般式(5)または(7)において、R1a〜R1i、R51〜R54、R61 63 各々、水素原子または置換基を表すが、R1a〜R1i、R51〜R54、R61 63 うち少なくとも1つは下記一般式(A)で表される置換基を表す。
但し、一般式(5)中、置換基R 1b が前記一般式(X)で表される場合を除く。
The general formula (5) or in (7), R 1a ~R 1i , R 51 ~R54, each R 61 ~ R 63, represents a hydrogen atom or a substituent, R 1a ~R 1i, R 51 ~ at least one of R 54, R 61 ~ R 63 represents a substituent represented by the following general formula (a).
However, in the general formula (5), the case where the substituent R 1b is represented by the general formula (X) is excluded.

1a〜R1i、R51〜R54、R61 63 表される置換基としては、前記の置換基と同義である。 R 1a to R 1i, examples of the substituent represented by R 51 ~R 54, R 61 ~ R 63 are the same as defined above substituents.

1a〜R1iのうち少なくとも1つで表される一般式(A)は、一般式(1)または(3)における一般式(A)で表される置換基と同義である。 General formula (A) represented by at least one of R 1a to R 1i has the same meaning as the substituent represented by general formula (A) in general formula (1) or (3) .

また、一般式(5)または(7)で表される部分構造の更に好ましい態様として、前記一般式(8)または(10)、若しくは、一般式(11)または(13)、で表される部分構造が挙げられる。 Moreover, a further preferred embodiment of the partial structure represented by the general formula (5) or (7), before following general formula (8) or (10) or the general formula (11) or (13), in expressed A partial structure.

《一般式(8)または(10)、若しくは、一般式(11)または(13)、のいずれかで表される部分構造》
前記一般式(8)または(10)、若しくは、一般式(11)または(13)において、E1f〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。
<< Partial structure represented by either general formula (8) or (10) or general formula (11) or (13) >>
In the general formula (8) or (10) or the general formula (11) or (13), E 1f to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom, or a sulfur atom, and E 1f to E The ring formed by 1k represents a 5-membered aromatic heterocyclic ring, and the ring formed by E 11 to E 1q represents a 6-membered aromatic hydrocarbon ring or a 6-membered aromatic heterocyclic ring .

1f〜E1kにより形成される環で表される5員の芳香族複素環としては、一般式(5)または(7)におけるE1f〜E1kにより形成される環で表される5員の芳香族複素環と同義である。 The aromatic heterocyclic 5-membered represented by the ring formed by E 1f to E 1k, the general formula (5) or 5-membered represented by the ring formed by E 1f to E 1k in (7) It is synonymous with the aromatic heterocyclic ring.

1l〜E1qにより形成される環で表される6員の芳香族炭化水素環としては、一般式(5)または(7)におけるE1l〜E1qにより形成される環で表される6員の芳香族炭化水素環と同義である。 The 6-membered aromatic hydrocarbon ring represented by the ring formed by E 1l to E 1q, represented by the ring formed by E 1l to E 1q in the general formula (5) or (7) 6 It is synonymous with a member aromatic hydrocarbon ring.

1l〜E1qにより形成される環で表される6員の芳香族複素環としては、一般式(5)または(7)におけるE1l〜E1qにより形成される環で表される6員の芳香族複素環と同義である。 E 1l aromatic heterocyclic 6-membered represented by the ring formed by to E 1q, general formula (5) or 6 membered represented by the ring formed by E 1l to E 1q in (7) It is synonymous with the aromatic heterocyclic ring.

前記一般式(8)または(10)、若しくは、一般式(11)または(13)において、R1c〜R1i、R51〜R56、R61 65 各々、水素原子または置換基を表すが、R1c〜R1i、R51〜R56、R61 65 うち少なくとも1つは下記一般式(A)で表される置換基を表す。 Formula (8) or (10), or, in the general formula (11) or (13), R 1c to R 1i, each R 51 ~R 56, R 61 ~ R 65 is a hydrogen atom or a substituent It represents but, R 1c ~R 1i, at least one of R 51 ~R 56, R 61 ~ R 65 represents a substituent represented by the following general formula (a).

該R1c〜R1i、R51〜R56、R61 65 表される置換基としては、前記の置換基と同義である。
但し、式中、置換基R 55 が前記一般式(X)で表される場合を除く。
The R 1c to R 1i, The substituents represented by R 51 ~R 56, R 61 ~ R 65, have the same meanings as defined above substituents.
However, in the formula, the case where the substituent R 55 is represented by the general formula (X) is excluded.

1a〜R1i、R51〜R56、R61 65 うち少なくとも1つで表される一般式(A)は、一般式(1)または(3)、一般式(5)または(7)、における一般式(A)で表される置換基と同義である。 R 1a ~R 1i, R 51 ~R 56, R 61 ~ general formula represented by at least one of R 65 (A) of the general formula (1) or (3), the general formula (5) or ( 7), which is synonymous with the substituent represented by Formula (A).

(本発明に係る金属錯体の形成に適用可能な配位子)
本発明に係る一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれかで表される部分構造を含む化合物(金属錯体、金属錯体化合物ともいう)の形成には、従来公知の配位子を必要に応じて併用することが可能である。
(Ligand applicable to formation of metal complex according to the present invention)
A compound comprising a partial structure represented by any one of the general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention ( In forming a metal complex or metal complex compound), a conventionally known ligand can be used in combination as necessary.

また、所謂配位子としては、当該業者が周知の配位子(配位化合物ともいう)を必要に応じて配位子として併用することができる。   Moreover, as what is called a ligand, the said trader can use together a well-known ligand (it is also called a coordination compound) as a ligand as needed.

従来公知の金属錯体に用いられる配位子としては、種々の公知の配位子があるが、例えば、「Photochemistry and Photophysics of Coordination Compounds」Springer−Verlag社 H.Yersin著 1987年発行、「有機金属化学−基礎と応用−」 裳華房社 山本明夫著 1982年発行 等に記載の配位子(例えば、ハロゲン配位子(好ましくは塩素配位子)、含窒素ヘテロ環配位子(例えば、ビピリジル、フェナントロリンなど)、ジケトン配位子なと)が挙げられる。   There are various known ligands used in conventionally known metal complexes. For example, “Photochemistry and Photophysics of Coordination Compounds” Springer-Verlag H. Published by Yersin in 1987, “Organometallic Chemistry-Fundamentals and Applications-” Liu Huabo Company, Akio Yamamoto, published in 1982, etc. (for example, halogen ligands (preferably chlorine ligands), Nitrogen heterocyclic ligands (for example, bipyridyl, phenanthroline, etc.) and diketone ligands).

以下、本発明に係る一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれかで表される部分構造を含む(有するともいう)化合物(金属錯体、金属錯体化合物ともいう)の具体例および参考とされる化合物を示すが、本発明はこれらに限定されない。 Hereinafter, the general formula of the present invention (1), (3), (5), (7), the partial structure represented by any of (8), (10), (11) or (13) Specific examples of the compound to be included (also referred to as having) (also referred to as a metal complex or a metal complex compound) and a compound to be referred to are shown, but the present invention is not limited thereto.

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

これらの金属錯体は、例えば、Organic Letter誌、Vol.3、No.16、2579〜2581頁(2001)、Inorganic Chemistry,第30巻、第8号、1685〜1687頁(1991年)、J.Am.Chem.Soc.,123巻、4304頁(2001年)、Inorganic Chemistry,第40巻、第7号、1704〜1711頁(2001年)、Inorganic Chemistry,第41巻、第12号、3055〜3066頁(2002年)、New Journal of Chemistry.,第26巻、1171頁(2002年)、Organic Letter誌、Vol.8、No.3、415〜418頁(2006)、更にこれらの文献中に記載の参考文献等の方法を適用することにより合成できる。   These metal complexes are described in, for example, Organic Letter, Vol. 3, no. 16, 2579-2581 (2001), Inorganic Chemistry, Vol. 30, No. 8, 1685-1687 (1991), J. Am. Am. Chem. Soc. , 123, 4304 (2001), Inorganic Chemistry, Vol. 40, No. 7, 1704-1711 (2001), Inorganic Chemistry, Vol. 41, No. 12, 3055-3066 (2002) , New Journal of Chemistry. 26, 1171 (2002), Organic Letter, Vol. 8, no. 3, pages 415 to 418 (2006), and further by applying methods such as references described in these documents.

本発明に係る一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれかで表される部分構造を含む化合物(金属錯体、金属錯体化合物ともいう)の合成例を以下に示す。 A compound comprising a partial structure represented by any one of the general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention ( Synthesis examples of metal complexes and metal complex compounds) are shown below.

《合成例1:例示化合物D−1の合成》:本発明の有機EL素子材料
本発明の有機EL素子材料である例示化合物D−1を下記に示す工程により合成した。
<< Synthesis Example 1: Synthesis of Exemplified Compound D-1 >>: Organic EL Element Material of the Present Invention Exemplified Compound D-1 which is an organic EL element material of the present invention was synthesized by the following steps.

Figure 0005531446
Figure 0005531446

(μ錯体の合成)
100ml四つ口フラスコに化合物(1)0.5g、2−エトキシエタノール7.5ml、水2.5mlを入れ、窒素吹き込み管、温度計、コンデンサーをつけて油浴スターラー上にセットした。
(Synthesis of μ complex)
A 100 ml four-necked flask was charged with 0.5 g of compound (1), 7.5 ml of 2-ethoxyethanol, and 2.5 ml of water, and set on an oil bath stirrer with a nitrogen blowing tube, a thermometer and a condenser.

これに、0.3gのIrCl・3HOを添加し、内温100℃付近で3時間煮沸還流して反応終了とした。 To this, 0.3 g of IrCl 3 .3H 2 O was added, and the reaction was completed by boiling and refluxing at an internal temperature of about 100 ° C. for 3 hours.

反応終了後室温まで冷却して濾過し、メタノールで良く洗浄して乾燥して、μ錯体(2)0.55gを得た。   After completion of the reaction, the reaction mixture was cooled to room temperature, filtered, washed thoroughly with methanol and dried to obtain 0.55 g of μ complex (2).

(acac錯体(3)の合成)
50ml四つ口フラスコに、0.55gのμ錯体(2)、0.18gのアセチルアセトン、0.5gの炭酸ナトリウム、2−エトキシエタノール12mlを入れ、窒素吹き込み管、温度計、コンデンサーをつけて油浴スターラー上にセットした。
(Synthesis of acac complex (3))
In a 50 ml four-necked flask, put 0.55 g of μ complex (2), 0.18 g of acetylacetone, 0.5 g of sodium carbonate, 12 ml of 2-ethoxyethanol, oil with nitrogen blowing tube, thermometer and condenser Set on bath stirrer.

窒素気流化内温122℃付近で2時間反応した。   The reaction was performed for 2 hours at an internal temperature of 122 ° C. under nitrogen flow.

反応終了後室温まで冷却し、結晶を濾過した。この結晶を水30ml、MeOH10mlで洗浄して乾燥し、0.45gのacac錯体(3)を得た。   After completion of the reaction, the reaction mixture was cooled to room temperature and the crystals were filtered. The crystals were washed with 30 ml of water and 10 ml of MeOH and dried to obtain 0.45 g of acac complex (3).

(D−1の合成)
50ml四つ口フラスコに、0.45gのacac錯体(3)、0.23gの化合物(1)、エチレングリコール10mlを入れ、窒素吹き込み管、温度計、空冷管をつけて油浴スターラー上にセットした。窒素気流化内温180℃付近で10時間加熱攪拌して反応終了とした。
(Synthesis of D-1)
Place 0.45 g of acac complex (3), 0.23 g of compound (1), and 10 ml of ethylene glycol in a 50 ml four-necked flask, and set on an oil bath stirrer with a nitrogen blowing tube, thermometer, and air cooling tube. did. The reaction was terminated by heating and stirring for 10 hours at a nitrogen gas flow inside temperature of about 180 ° C.

反応終了後、室温まで冷却し、結晶を濾過した。   After completion of the reaction, the reaction mixture was cooled to room temperature and the crystals were filtered.

結晶をカラムクロマトグラフィーで精製して、D−1を0.2g得た。   The crystal was purified by column chromatography to obtain 0.2 g of D-1.

得られた例示化合物D−1の構造はH−NMR(核磁気共鳴スペクトル)、マススペクトルを用いて構造を確認した。 The structure of the obtained exemplary compound D-1 was confirmed using 1 H-NMR (nuclear magnetic resonance spectrum) and mass spectrum.

本発明に係る一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれかの部分構造を有する化合物(金属錯体)を有機EL素子材料として用いることにより、高い発光効率を示し、発光寿命が長く、初期劣化が抑制され、且つ、ダークスポットのない有機エレクトロルミネッセンス素子(有機EL素子)、照明装置及び表示装置を提供することができた。 Compound (metal complex) having a partial structure of any one of general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention Is used as an organic EL element material to provide an organic electroluminescence element (organic EL element), a lighting device, and a display device that exhibit high light emission efficiency, have a long light emission lifetime, suppress initial deterioration, and have no dark spots We were able to.

本発明に係る一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれかで示される部分構造を含む化合物(金属錯体)は、本発明の有機EL素子の少なくとも1層の発光層に含有されるが、該発光層以外の構成層に含まれていてもよい。 Compound (metal) containing a partial structure represented by any of the general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention The complex) is contained in at least one light emitting layer of the organic EL device of the present invention, but may be contained in a constituent layer other than the light emitting layer.

尚、本発明の有機EL素子の構成層については後に詳細に説明する。   The constituent layers of the organic EL element of the present invention will be described in detail later.

《有機EL素子の構成層》
本発明の有機EL素子の構成層について説明する。本発明において、有機EL素子の層構成の好ましい具体例を以下に示すが、本発明はこれらに限定されない。
<< Constituent layers of organic EL elements >>
The constituent layers of the organic EL element of the present invention will be described. In this invention, although the preferable specific example of the layer structure of an organic EL element is shown below, this invention is not limited to these.

(i)陽極/発光層/電子輸送層/陰極
(ii)陽極/正孔輸送層/発光層/電子輸送層/陰極
(iii)陽極/正孔輸送層/発光層/正孔阻止層/電子輸送層/陰極
(iv)陽極/正孔輸送層/発光層/正孔阻止層/電子輸送層/陰極バッファー層/陰極
(v)陽極/陽極バッファー層/正孔輸送層/発光層/正孔阻止層/電子輸送層/陰極バッファー層/陰極
(vi)陽極/正孔輸送層/電子阻止層/発光層/正孔阻止層/電子輸送層/陰極
本発明の有機EL素子においては、青色発光層の発光極大波長は430nm〜480nmにあるものが好ましく、緑色発光層は発光極大波長が510nm〜550nm、赤色発光層は発光極大波長が600nm〜640nmの範囲にある単色発光層であることが好ましく、これらを用いた表示装置であることが好ましい。また、これらの少なくとも3層の発光層を積層して白色発光層としたものであってもよい。更に、発光層間には非発光性の中間層を有していてもよい。本発明の有機EL素子としては白色発光層であることが好ましく、これらを用いた照明装置であることが好ましい。
(I) Anode / light emitting layer / electron transport layer / cathode (ii) Anode / hole transport layer / light emitting layer / electron transport layer / cathode (iii) Anode / hole transport layer / light emitting layer / hole blocking layer / electron Transport layer / cathode (iv) Anode / hole transport layer / light emitting layer / hole blocking layer / electron transport layer / cathode buffer layer / cathode (v) Anode / anode buffer layer / hole transport layer / light emitting layer / hole Blocking layer / electron transport layer / cathode buffer layer / cathode (vi) Anode / hole transport layer / electron block layer / light emitting layer / hole block layer / electron transport layer / cathode In the organic EL device of the present invention, blue light emission The light emission maximum wavelength of the layer is preferably in the range of 430 nm to 480 nm, the green light emission layer is preferably a monochromatic light emitting layer having a light emission maximum wavelength in the range of 510 nm to 550 nm, and the red light emission layer is in the range of the light emission maximum wavelength of 600 nm to 640 nm. This is a display device using these. It is preferred. Alternatively, a white light emitting layer may be formed by laminating at least three light emitting layers. Further, a non-light emitting intermediate layer may be provided between the light emitting layers. The organic EL element of the present invention is preferably a white light emitting layer, and is preferably a lighting device using these.

本発明の有機EL素子を構成する各層について説明する。   Each layer which comprises the organic EL element of this invention is demonstrated.

《発光層》
本発明に係る発光層は、電極または電子輸送層、正孔輸送層から注入されてくる電子及び正孔が再結合して発光する層であり、発光する部分は発光層の層内であっても発光層と隣接層との界面であってもよい。
<Light emitting layer>
The light emitting layer according to the present invention is a layer that emits light by recombination of electrons and holes injected from the electrode, the electron transport layer, or the hole transport layer, and the light emitting portion is in the layer of the light emitting layer. May be the interface between the light emitting layer and the adjacent layer.

発光層の膜厚の総和は特に制限はないが、膜の均質性や、発光時に不必要な高電圧を印加するのを防止し、かつ、駆動電流に対する発光色の安定性向上の観点から、2nm〜5μmの範囲に調整することが好ましく、更に好ましくは2nm〜200nmの範囲に調整され、特に好ましくは、10nm〜20nmの範囲である。   The total film thickness of the light emitting layer is not particularly limited, but from the viewpoint of improving the uniformity of the film, preventing unnecessary application of high voltage during light emission, and improving the stability of the emission color with respect to the drive current. It is preferable to adjust in the range of 2 nm to 5 μm, more preferably in the range of 2 nm to 200 nm, and particularly preferably in the range of 10 nm to 20 nm.

発光層の作製には、後述する発光ドーパントやホスト化合物を、例えば、真空蒸着法、スピンコート法、キャスト法、LB法、インクジェット法等の公知の薄膜化法により成膜して形成することができる。   For the production of the light-emitting layer, a light-emitting dopant or a host compound, which will be described later, is formed by a known thinning method such as a vacuum deposition method, a spin coating method, a casting method, an LB method, or an ink-jet method. it can.

本発明の有機EL素子の発光層には、発光ホスト化合物と、発光ドーパント(リン光ドーパント(リン光発光性ドーパントともいう)や蛍光ドーパント等)の少なくとも1種類とを含有することが好ましい。   The light emitting layer of the organic EL device of the present invention preferably contains a light emitting host compound and at least one kind of light emitting dopant (such as a phosphorescent dopant (also referred to as a phosphorescent dopant) or a fluorescent dopant).

(ホスト化合物(発光ホスト等ともいう))
本発明に用いられるホスト化合物について説明する。
(Host compound (also called luminescent host))
The host compound used in the present invention will be described.

ここで、本発明においてホスト化合物とは、発光層に含有される化合物の内でその層中での質量比が20%以上であり、且つ室温(25℃)においてリン光発光のリン光量子収率が、0.1未満の化合物と定義される。好ましくはリン光量子収率が0.01未満である。また、発光層に含有される化合物の中で、その層中での質量比が20%以上であることが好ましい。   Here, the host compound in the present invention is a phosphorescent quantum yield of phosphorescence emission at a room temperature (25 ° C.) having a mass ratio of 20% or more in the compound contained in the light emitting layer. Is defined as a compound of less than 0.1. The phosphorescence quantum yield is preferably less than 0.01. Moreover, it is preferable that the mass ratio in the layer is 20% or more among the compounds contained in a light emitting layer.

ホスト化合物としては、公知のホスト化合物を単独で用いてもよく、または複数種併用して用いてもよい。ホスト化合物を複数種用いることで、電荷の移動を調整することが可能であり、有機EL素子を高効率化することができる。また、後述する発光ドーパントを複数種用いることで、異なる発光を混ぜることが可能となり、これにより任意の発光色を得ることができる。   As the host compound, known host compounds may be used alone or in combination of two or more. By using a plurality of types of host compounds, it is possible to adjust the movement of charges, and the organic EL element can be made highly efficient. Moreover, it becomes possible to mix different light emission by using multiple types of light emission dopants mentioned later, and, thereby, arbitrary luminescent colors can be obtained.

また、本発明に用いられる発光ホストとしては、従来公知の低分子化合物でも、繰り返し単位をもつ高分子化合物でもよく、ビニル基やエポキシ基のような重合性基を有する低分子化合物(蒸着重合性発光ホスト)でもよく、前記材料Cのような化合物を1種または複数種用いても良い。   The light emitting host used in the present invention may be a conventionally known low molecular compound or a high molecular compound having a repeating unit, and a low molecular compound having a polymerizable group such as a vinyl group or an epoxy group (deposition polymerization property). A light emitting host), or one or more compounds such as the material C may be used.

以下に、本発明に好ましく用いられるホスト化合物の具体例を示すが、本発明はこれらに限定されない。   Although the specific example of the host compound preferably used for this invention below is shown, this invention is not limited to these.

Figure 0005531446
Figure 0005531446

併用してもよい公知のホスト化合物としては、正孔輸送能、電子輸送能を有しつつ、且つ発光の長波長化を防ぎ、なお且つ高Tg(ガラス転移温度)である化合物が好ましい。   As a known host compound that may be used in combination, a compound that has a hole transporting ability and an electron transporting ability, prevents the emission of light from being increased in wavelength, and has a high Tg (glass transition temperature) is preferable.

公知のホスト化合物の具体例としては、以下の文献に記載されている化合物が挙げられる。   Specific examples of known host compounds include compounds described in the following documents.

特開2001−257076号公報、同2002−308855号公報、同2001−313179号公報、同2002−319491号公報、同2001−357977号公報、同2002−334786号公報、同2002−8860号公報、同2002−334787号公報、同2002−15871号公報、同2002−334788号公報、同2002−43056号公報、同2002−334789号公報、同2002−75645号公報、同2002−338579号公報、同2002−105445号公報、同2002−343568号公報、同2002−141173号公報、同2002−352957号公報、同2002−203683号公報、同2002−363227号公報、同2002−231453号公報、同2003−3165号公報、同2002−234888号公報、同2003−27048号公報、同2002−255934号公報、同2002−260861号公報、同2002−280183号公報、同2002−299060号公報、同2002−302516号公報、同2002−305083号公報、同2002−305084号公報、同2002−308837号公報等。   JP-A-2001-257076, 2002-308855, 2001-313179, 2002-319491, 2001-357777, 2002-334786, 2002-8860, 2002-334787, 2002-15871, 2002-334788, 2002-43056, 2002-334789, 2002-75645, 2002-338579, 2002-105445 gazette, 2002-343568 gazette, 2002-141173 gazette, 2002-352957 gazette, 2002-203683 gazette, 2002-363227 gazette, 2002-231453 gazette, No. 003-3165, No. 2002-234888, No. 2003-27048, No. 2002-255934, No. 2002-286061, No. 2002-280183, No. 2002-299060, No. 2002. -302516, 2002-305083, 2002-305084, 2002-308837, and the like.

(発光ドーパント)
本発明に係る発光ドーパントについて説明する。
(Luminescent dopant)
The light emitting dopant according to the present invention will be described.

本発明に係る発光ドーパントとしては、蛍光ドーパント(蛍光性化合物ともいう)、リン光ドーパント(リン光発光体、リン光性化合物、リン光発光性化合物等ともいう)を用いることができるが、より発光効率の高い有機EL素子を得る観点からは、本発明の有機EL素子の発光層や発光ユニットに使用される発光ドーパント(単に、発光材料ということもある)としては、上記のホスト化合物を含有すると同時に、リン光ドーパントを含有することが好ましい。   As the light-emitting dopant according to the present invention, a fluorescent dopant (also referred to as a fluorescent compound) or a phosphorescent dopant (also referred to as a phosphorescent emitter, a phosphorescent compound, a phosphorescent compound, or the like) can be used. From the viewpoint of obtaining an organic EL device with high luminous efficiency, the light emitting dopant used in the light emitting layer or the light emitting unit of the organic EL device of the present invention (sometimes simply referred to as a light emitting material) contains the above host compound. At the same time, it is preferable to contain a phosphorescent dopant.

尚、本発明に係る一般式(1)〜(13)のいずれかで表される部分構造を含む(有するともいう)化合物(金属錯体、金属錯体化合物ともいう)は、本発明の有機EL素子の構成層において、発光層で用いられるが、好ましく、該発光層においては、発光ドーパントとして用いられることが好ましく、更に好ましくは、リン光ドーパントとして用いられることである。   In addition, the compound (also referred to as a metal complex or metal complex compound) containing (also referred to as) a partial structure represented by any one of the general formulas (1) to (13) according to the present invention is the organic EL of the present invention. Although it is used in the light emitting layer in the component layer of the element, it is preferably used as a light emitting dopant in the light emitting layer, and more preferably used as a phosphorescent dopant.

(リン光ドーパント)
本発明に係るリン光ドーパントについて説明する。
(Phosphorescent dopant)
The phosphorescent dopant according to the present invention will be described.

本発明に係るリン光ドーパントは、励起三重項からの発光が観測される化合物であり、具体的には、室温(25℃)にてリン光発光する化合物であり、リン光量子収率が、25℃において0.01以上の化合物であると定義されるが、好ましいリン光量子収率は0.1以上である。   The phosphorescent dopant according to the present invention is a compound in which light emission from an excited triplet is observed. Specifically, the phosphorescent dopant is a compound that emits phosphorescence at room temperature (25 ° C.) and has a phosphorescence quantum yield of 25. Although it is defined as a compound of 0.01 or more at ° C., a preferable phosphorescence quantum yield is 0.1 or more.

上記リン光量子収率は、第4版実験化学講座7の分光IIの398頁(1992年版、丸善)に記載の方法により測定できる。溶液中でのリン光量子収率は種々の溶媒を用いて測定できるが、本発明に係るリン光ドーパントは、任意の溶媒のいずれかにおいて上記リン光量子収率(0.01以上)が達成されればよい。   The phosphorescence quantum yield can be measured by the method described in Spectroscopic II, page 398 (1992 edition, Maruzen) of Experimental Chemistry Course 4 of the 4th edition. Although the phosphorescence quantum yield in a solution can be measured using various solvents, the phosphorescence dopant according to the present invention achieves the phosphorescence quantum yield (0.01 or more) in any solvent. That's fine.

リン光ドーパントの発光は原理としては2種挙げられ、一つはキャリアが輸送されるホスト化合物上でキャリアの再結合が起こってホスト化合物の励起状態が生成し、このエネルギーをリン光ドーパントに移動させることでリン光ドーパントからの発光を得るというエネルギー移動型、もう一つはリン光ドーパントがキャリアトラップとなり、リン光ドーパント上でキャリアの再結合が起こりリン光ドーパントからの発光が得られるというキャリアトラップ型であるが、いずれの場合においても、リン光ドーパントの励起状態のエネルギーはホスト化合物の励起状態のエネルギーよりも低いことが条件である。   There are two types of light emission of phosphorescent dopants in principle. One is the recombination of carriers on the host compound to which carriers are transported to generate an excited state of the host compound, and this energy is transferred to the phosphorescent dopant. The energy transfer type that obtains light emission from the phosphorescent dopant, and the other is that the phosphorescent dopant becomes a carrier trap, carrier recombination occurs on the phosphorescent dopant, and light emission from the phosphorescent dopant is obtained. Although it is a trap type, in any case, the excited state energy of the phosphorescent dopant is required to be lower than the excited state energy of the host compound.

リン光ドーパントは、有機EL素子の発光層に使用される公知のものの中から適宜選択して用いることができる。   The phosphorescent dopant can be appropriately selected from known materials used for the light emitting layer of the organic EL device.

リン光ドーパントは、好ましくは元素周期表で8族〜10族の遷移金属元素を中心金属として有する錯体系化合物であり、更に好ましくはイリジウム化合物、オスミウム化合物、または白金化合物(白金錯体系化合物)、希土類錯体であり、中でも最も好ましいのはイリジウム化合物である。   The phosphorescent dopant is preferably a complex compound having a transition metal element of group 8 to group 10 as the central metal in the periodic table, more preferably an iridium compound, an osmium compound, or a platinum compound (platinum complex compound), Rare earth complexes, most preferably iridium compounds.

また、本発明に係る前記一般式(1)〜(13)のいずれかで表される部分構造を含む(有するともいう)化合物(金属錯体、金属錯体化合物ともいう)と併用することができる化合物としては、以下の特許公報に記載されている化合物が挙げられる。   Further, it can be used in combination with a compound (also referred to as having a partial structure) represented by any one of the general formulas (1) to (13) according to the present invention (also referred to as a metal complex or a metal complex compound). Examples of the compound include compounds described in the following patent publications.

国際公開第00/70655号パンフレット、特開2002−280178号公報、特開2001−181616号公報、特開2002−280179号公報、特開2001−181617号公報、特開2002−280180号公報、特開2001−247859号公報、特開2002−299060号公報、特開2001−313178号公報、特開2002−302671号公報、特開2001−345183号公報、特開2002−324679号公報、国際公開第02/15645号パンフレット、特開2002−332291号公報、特開2002−50484号公報、特開2002−332292号公報、特開2002−83684号公報、特表2002−540572号公報、特開2002−117978号公報、特開2002−338588号公報、特開2002−170684号公報、特開2002−352960号公報、国際公開第01/93642号パンフレット、特開2002−50483号公報、特開2002−100476号公報、特開2002−173674号公報、特開2002−359082号公報、特開2002−175884号公報、特開2002−363552号公報、特開2002−184582号公報、特開2003−7469号公報、特表2002−525808号公報、特開2003−7471号公報、特表2002−525833号公報、特開2003−31366号公報、特開2002−226495号公報、特開2002−234894号公報、特開2002−235076号公報、特開2002−241751号公報、特開2001−319779号公報、特開2001−319780号公報、特開2002−62824号公報、特開2002−100474号公報、特開2002−203679号公報、特開2002−343572号公報、特開2002−203678号公報等。   WO 00/70655 pamphlet, JP 2002-280178, JP 2001-181616, JP 2002-280179, JP 2001-181617, JP 2002-280180, JP 2001-247859, JP 2002-299060, JP 2001-313178, JP 2002-302671, JP 2001-345183, JP 2002-324679, International Publication No. 02/15645 pamphlet, JP 2002-332291 A, JP 2002-50484 A, JP 2002-332292 A, JP 2002-83684 A, JP 2002-540572 A, JP 2002-2002 A. No. 117978, JP 20 JP-A-2-338588, JP-A-2002-170684, JP-A-2002-352960, WO01 / 93642, JP-A-2002-50483, JP-A-2002-1000047, JP-A-2002. No. -173744, JP-A No. 2002-359082, JP-A No. 2002-17584, JP-A No. 2002-363552, JP-A No. 2002-184582, JP-A No. 2003-7469, JP-T-2002-525808. Gazette, JP2003-7471, JP2002-525833, JP2003-31366, JP2002-226495, JP2002-234894, JP2002-2335076 JP 2002-241751 A JP 2001-319779, JP 2001-319780, JP 2002-62824, JP 2002-1000047, JP 2002-203679, JP 2002-343572, JP 2002-203678 gazette etc.

以下に、具体例の一部を示す。   Some specific examples are shown below.

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

(蛍光ドーパント(蛍光性化合物ともいう))
蛍光ドーパント(蛍光性化合物)としては、クマリン系色素、ピラン系色素、シアニン系色素、クロコニウム系色素、スクアリウム系色素、オキソベンツアントラセン系色素、フルオレセイン系色素、ローダミン系色素、ピリリウム系色素、ペリレン系色素、スチルベン系色素、ポリチオフェン系色素、または希土類錯体系蛍光体等が挙げられる。
(Fluorescent dopant (also called fluorescent compound))
Fluorescent dopants (fluorescent compounds) include coumarin dyes, pyran dyes, cyanine dyes, croconium dyes, squalium dyes, oxobenzanthracene dyes, fluorescein dyes, rhodamine dyes, pyrylium dyes, perylene dyes Examples thereof include dyes, stilbene dyes, polythiophene dyes, and rare earth complex phosphors.

次に、本発明の有機EL素子の構成層として用いられる電荷輸送層、すなわち、注入層、阻止層、電子輸送層等について説明する。   Next, a charge transport layer used as a constituent layer of the organic EL device of the present invention, that is, an injection layer, a blocking layer, an electron transport layer, and the like will be described.

《注入層:電子注入層、正孔注入層》
注入層は必要に応じて設け、電子注入層と正孔注入層があり、上記の如く陽極と発光層または正孔輸送層の間、及び陰極と発光層または電子輸送層との間に存在させてもよい。
<< Injection layer: electron injection layer, hole injection layer >>
The injection layer is provided as necessary, and there are an electron injection layer and a hole injection layer, and as described above, it exists between the anode and the light emitting layer or the hole transport layer and between the cathode and the light emitting layer or the electron transport layer. May be.

注入層とは、駆動電圧低下や発光輝度向上のために電極と有機層間に設けられる層のことで、「有機EL素子とその工業化最前線(1998年11月30日エヌ・ティー・エス社発行)」の第2編第2章「電極材料」(123〜166頁)に詳細に記載されており、正孔注入層(陽極バッファー層)と電子注入層(陰極バッファー層)とがある。   An injection layer is a layer provided between an electrode and an organic layer in order to reduce drive voltage and improve light emission luminance. “Organic EL element and its forefront of industrialization (issued by NTT Corporation on November 30, 1998) 2), Chapter 2, “Electrode Materials” (pages 123 to 166) in detail, and includes a hole injection layer (anode buffer layer) and an electron injection layer (cathode buffer layer).

陽極バッファー層(正孔注入層)は、特開平9−45479号公報、同9−260062号公報、同8−288069号公報等にもその詳細が記載されており、具体例として、銅フタロシアニンに代表されるフタロシアニンバッファー層、酸化バナジウムに代表される酸化物バッファー層、アモルファスカーボンバッファー層、ポリアニリン(エメラルディン)やポリチオフェン等の導電性高分子を用いた高分子バッファー層等が挙げられる。   The details of the anode buffer layer (hole injection layer) are described in JP-A-9-45479, JP-A-9-260062, JP-A-8-288069 and the like. As a specific example, copper phthalocyanine is used. Examples thereof include a phthalocyanine buffer layer represented by an oxide, an oxide buffer layer represented by vanadium oxide, an amorphous carbon buffer layer, and a polymer buffer layer using a conductive polymer such as polyaniline (emeraldine) or polythiophene.

陰極バッファー層(電子注入層)は、特開平6−325871号公報、同9−17574号公報、同10−74586号公報等にもその詳細が記載されており、具体的にはストロンチウムやアルミニウム等に代表される金属バッファー層、フッ化リチウムに代表されるアルカリ金属化合物バッファー層、フッ化マグネシウムに代表されるアルカリ土類金属化合物バッファー層、酸化アルミニウムに代表される酸化物バッファー層等が挙げられる。上記バッファー層(注入層)はごく薄い膜であることが望ましく、素材にもよるがその膜厚は0.1nm〜5μmの範囲が好ましい。   The details of the cathode buffer layer (electron injection layer) are described in JP-A-6-325871, JP-A-9-17574, JP-A-10-74586, and the like. Specifically, strontium, aluminum, etc. Metal buffer layer typified by lithium, alkali metal compound buffer layer typified by lithium fluoride, alkaline earth metal compound buffer layer typified by magnesium fluoride, oxide buffer layer typified by aluminum oxide, etc. . The buffer layer (injection layer) is preferably a very thin film, and the film thickness is preferably in the range of 0.1 nm to 5 μm although it depends on the material.

《阻止層:正孔阻止層、電子阻止層》
阻止層は、上記の如く有機化合物薄膜の基本構成層の他に必要に応じて設けられるものである。例えば、特開平11−204258号公報、同11−204359号公報、及び「有機EL素子とその工業化最前線(1998年11月30日エヌ・ティー・エス社発行)」の237頁等に記載されている正孔阻止(ホールブロック)層がある。
<Blocking layer: hole blocking layer, electron blocking layer>
The blocking layer is provided as necessary in addition to the basic constituent layer of the organic compound thin film as described above. For example, it is described in JP-A Nos. 11-204258, 11-204359, and “Organic EL elements and their forefront of industrialization” (issued by NTT, Inc. on November 30, 1998). There is a hole blocking (hole blocking) layer.

正孔阻止層とは広い意味では電子輸送層の機能を有し、電子を輸送する機能を有しつつ正孔を輸送する能力が著しく小さい正孔阻止材料からなり、電子を輸送しつつ正孔を阻止することで電子と正孔の再結合確率を向上させることができる。   The hole blocking layer has a function of an electron transport layer in a broad sense, and is made of a hole blocking material that has a function of transporting electrons and has a remarkably small ability to transport holes. The probability of recombination of electrons and holes can be improved by blocking.

また、後述する電子輸送層の構成を必要に応じて、本発明に係わる正孔阻止層として用いることができる。   Moreover, the structure of the electron carrying layer mentioned later can be used as a hole-blocking layer concerning this invention as needed.

本発明の有機EL素子の正孔阻止層は、発光層に隣接して設けられていることが好ましい。   The hole blocking layer of the organic EL device of the present invention is preferably provided adjacent to the light emitting layer.

正孔阻止層には、前述のホスト化合物として挙げたカルバゾール誘導体、カルボリン誘導体、ジアザカルバゾール誘導体(カルボリン誘導体のカルボリン環を構成する炭素原子の一つが窒素原子で置き換わったものを示す。)を含有することが好ましい。   The hole blocking layer contains the carbazole derivative, carboline derivative, or diazacarbazole derivative (showed by replacing one of the carbon atoms constituting the carboline ring of the carboline derivative with a nitrogen atom) as the host compound. It is preferable to do.

また、本発明においては、複数の発光色の異なる複数の発光層を有する場合、その発光極大波長が最も短波にある発光層が、全発光層中、最も陽極に近いことが好ましいが、このような場合、該最短波層と該層の次に陽極に近い発光層との間に正孔阻止層を追加して設けることが好ましい。更には、該位置に設けられる正孔阻止層に含有される化合物の50質量%以上が、前記最短波発光層のホスト化合物に対しそのイオン化ポテンシャルが0.3eV以上大きいことが好ましい。   In the present invention, when a plurality of light emitting layers having different light emission colors are provided, the light emitting layer having the shortest wavelength of light emission is preferably closest to the anode among all the light emitting layers. In this case, it is preferable to additionally provide a hole blocking layer between the shortest wave layer and the light emitting layer next to the anode next to the anode. Furthermore, it is preferable that 50% by mass or more of the compound contained in the hole blocking layer provided at the position has an ionization potential of 0.3 eV or more larger than the host compound of the shortest wave emitting layer.

イオン化ポテンシャルは化合物のHOMO(最高被占分子軌道)レベルにある電子を真空準位に放出するのに必要なエネルギーで定義され、例えば下記に示すような方法により求めることができる。   The ionization potential is defined by the energy required to emit an electron at the HOMO (highest occupied molecular orbital) level of the compound to the vacuum level, and can be obtained by the following method, for example.

(1)米国Gaussian社製の分子軌道計算用ソフトウェアであるGaussian98(Gaussian98、Revision A.11.4,M.J.Frisch,et al,Gaussian,Inc.,Pittsburgh PA,2002.)を用い、キーワードとしてB3LYP/6−31G*を用いて構造最適化を行うことにより算出した値(eV単位換算値)の小数点第2位を四捨五入した値としてイオン化ポテンシャルを求めることができる。この計算値が有効な背景には、この手法で求めた計算値と実験値の相関が高いためである。   (1) Using Gaussian 98 (Gaussian 98, Revision A.11.4, MJ Frisch, et al, Gaussian, Inc., Pittsburgh PA, 2002.), a molecular orbital calculation software manufactured by Gaussian, USA The ionization potential can be obtained as a value obtained by rounding off the second decimal place of the value (eV unit converted value) calculated by performing structural optimization using B3LYP / 6-31G *. This calculation value is effective because the correlation between the calculation value obtained by this method and the experimental value is high.

(2)イオン化ポテンシャルは光電子分光法で直接測定する方法により求めることもできる。例えば、理研計器社製の低エネルギー電子分光装置「Model AC−1」を用いて、あるいは紫外光電子分光として知られている方法を好適に用いることができる。   (2) The ionization potential can also be obtained by a method of directly measuring by photoelectron spectroscopy. For example, a method known as ultraviolet photoelectron spectroscopy can be suitably used by using a low energy electron spectrometer “Model AC-1” manufactured by Riken Keiki Co., Ltd.

尚、本発明に係る前記一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれか一つで表される部分構造を含む(有するともいう)化合物を正孔阻止層に含有することも可能である。 The portion represented by any one of the general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention. It is also possible to contain a compound including (or having) a structure in the hole blocking layer.

一方、電子阻止層とは広い意味では正孔輸送層の機能を有し、正孔を輸送する機能を有しつつ電子を輸送する能力が著しく小さい材料からなり、正孔を輸送しつつ電子を阻止することで電子と正孔の再結合確率を向上させることができる。   On the other hand, the electron blocking layer has a function of a hole transport layer in a broad sense, and is made of a material that has a function of transporting holes and has an extremely small ability to transport electrons, and transports electrons while transporting holes. By blocking, the recombination probability of electrons and holes can be improved.

また、後述する正孔輸送層の構成を必要に応じて電子阻止層として用いることができる。本発明に係る正孔阻止層、電子輸送層の膜厚としては、好ましくは3nm〜100nmであり、更に好ましくは5nm〜30nmである。   Moreover, the structure of the positive hole transport layer mentioned later can be used as an electron blocking layer as needed. The film thickness of the hole blocking layer and the electron transport layer according to the present invention is preferably 3 nm to 100 nm, and more preferably 5 nm to 30 nm.

尚、本発明に係る前記一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれか一つで表される部分構造を含む(有するともいう)化合物を電子阻止層に含有することも可能である。 The portion represented by any one of the general formulas (1) , (3), (5), (7), (8), (10), (11) or (13) according to the present invention. It is also possible to contain a compound including (or having) a structure in the electron blocking layer.

《正孔輸送層》
正孔輸送層とは正孔を輸送する機能を有する正孔輸送材料からなり、広い意味で正孔注入層、電子阻止層も正孔輸送層に含まれる。正孔輸送層は単層または複数層設けることができる。
《Hole transport layer》
The hole transport layer is made of a hole transport material having a function of transporting holes, and in a broad sense, a hole injection layer and an electron blocking layer are also included in the hole transport layer. The hole transport layer can be provided as a single layer or a plurality of layers.

正孔輸送材料としては、正孔の注入または輸送、電子の障壁性のいずれかを有するものであり、有機物、無機物のいずれであってもよい。例えば、トリアゾール誘導体、オキサジアゾール誘導体、イミダゾール誘導体、ポリアリールアルカン誘導体、ピラゾリン誘導体及びピラゾロン誘導体、フェニレンジアミン誘導体、アリールアミン誘導体、アミノ置換カルコン誘導体、オキサゾール誘導体、スチリルアントラセン誘導体、フルオレノン誘導体、ヒドラゾン誘導体、スチルベン誘導体、シラザン誘導体、アニリン系共重合体、また導電性高分子オリゴマー、特にチオフェンオリゴマー等が挙げられる。   The hole transport material has any one of hole injection or transport and electron barrier properties, and may be either organic or inorganic. For example, triazole derivatives, oxadiazole derivatives, imidazole derivatives, polyarylalkane derivatives, pyrazoline derivatives and pyrazolone derivatives, phenylenediamine derivatives, arylamine derivatives, amino-substituted chalcone derivatives, oxazole derivatives, styrylanthracene derivatives, fluorenone derivatives, hydrazone derivatives, Examples thereof include stilbene derivatives, silazane derivatives, aniline copolymers, and conductive polymer oligomers, particularly thiophene oligomers.

正孔輸送材料としては上記のものを使用することができるが、ポルフィリン化合物、芳香族第3級アミン化合物及びスチリルアミン化合物、特に芳香族第3級アミン化合物を用いることが好ましい。   The above-mentioned materials can be used as the hole transport material, but it is preferable to use a porphyrin compound, an aromatic tertiary amine compound and a styrylamine compound, particularly an aromatic tertiary amine compound.

芳香族第3級アミン化合物及びスチリルアミン化合物の代表例としては、N,N,N′,N′−テトラフェニル−4,4′−ジアミノフェニル;N,N′−ジフェニル−N,N′−ビス(3−メチルフェニル)−〔1,1′−ビフェニル〕−4,4′−ジアミン(TPD);2,2−ビス(4−ジ−p−トリルアミノフェニル)プロパン;1,1−ビス(4−ジ−p−トリルアミノフェニル)シクロヘキサン;N,N,N′,N′−テトラ−p−トリル−4,4′−ジアミノビフェニル;1,1−ビス(4−ジ−p−トリルアミノフェニル)−4−フェニルシクロヘキサン;ビス(4−ジメチルアミノ−2−メチルフェニル)フェニルメタン;ビス(4−ジ−p−トリルアミノフェニル)フェニルメタン;N,N′−ジフェニル−N,N′−ジ(4−メトキシフェニル)−4,4′−ジアミノビフェニル;N,N,N′,N′−テトラフェニル−4,4′−ジアミノジフェニルエーテル;4,4′−ビス(ジフェニルアミノ)クオードリフェニル;N,N,N−トリ(p−トリル)アミン;4−(ジ−p−トリルアミノ)−4′−〔4−(ジ−p−トリルアミノ)スチリル〕スチルベン;4−N,N−ジフェニルアミノ−(2−ジフェニルビニル)ベンゼン;3−メトキシ−4′−N,N−ジフェニルアミノスチルベンゼン;N−フェニルカルバゾール、更には米国特許第5,061,569号明細書に記載されている2個の縮合芳香族環を分子内に有するもの、例えば、4,4′−ビス〔N−(1−ナフチル)−N−フェニルアミノ〕ビフェニル(NPD)、特開平4−308688号公報に記載されているトリフェニルアミンユニットが3つスターバースト型に連結された4,4′,4″−トリス〔N−(3−メチルフェニル)−N−フェニルアミノ〕トリフェニルアミン(MTDATA)等が挙げられる。   Representative examples of aromatic tertiary amine compounds and styrylamine compounds include N, N, N ', N'-tetraphenyl-4,4'-diaminophenyl; N, N'-diphenyl-N, N'- Bis (3-methylphenyl)-[1,1′-biphenyl] -4,4′-diamine (TPD); 2,2-bis (4-di-p-tolylaminophenyl) propane; 1,1-bis (4-di-p-tolylaminophenyl) cyclohexane; N, N, N ′, N′-tetra-p-tolyl-4,4′-diaminobiphenyl; 1,1-bis (4-di-p-tolyl) Aminophenyl) -4-phenylcyclohexane; bis (4-dimethylamino-2-methylphenyl) phenylmethane; bis (4-di-p-tolylaminophenyl) phenylmethane; N, N'-diphenyl-N, N ' − (4-methoxyphenyl) -4,4'-diaminobiphenyl; N, N, N ', N'-tetraphenyl-4,4'-diaminodiphenyl ether; 4,4'-bis (diphenylamino) quadriphenyl; N, N, N-tri (p-tolyl) amine; 4- (di-p-tolylamino) -4 '-[4- (di-p-tolylamino) styryl] stilbene; 4-N, N-diphenylamino- (2-diphenylvinyl) benzene; 3-methoxy-4′-N, N-diphenylaminostilbenzene; N-phenylcarbazole, and also two of those described in US Pat. No. 5,061,569. Having a condensed aromatic ring in the molecule, for example, 4,4'-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (NPD), JP-A-4-3086 4,4 ', 4 "-tris [N- (3-methylphenyl) -N-phenylamino] triphenylamine in which three triphenylamine units described in Japanese Patent No. 8 are linked in a starburst type ( MTDATA) and the like.

更にこれらの材料を高分子鎖に導入した、またはこれらの材料を高分子の主鎖とした高分子材料を用いることもできる。また、p型−Si、p型−SiC等の無機化合物も正孔注入材料、正孔輸送材料として使用することができる。   Furthermore, a polymer material in which these materials are introduced into a polymer chain or these materials are used as a polymer main chain can also be used. In addition, inorganic compounds such as p-type-Si and p-type-SiC can also be used as the hole injection material and the hole transport material.

また、特開平11−251067号公報、J.Huang et.al.著文献(Applied Physics Letters 80(2002),p.139)に記載されているような、所謂p型正孔輸送材料を用いることもできる。   JP-A-11-251067, J. Org. Huang et. al. A so-called p-type hole transport material as described in a book (Applied Physics Letters 80 (2002), p. 139) can also be used.

本発明においては、より高効率の発光素子が得られることからこれらの材料を用いることが好ましい。   In the present invention, these materials are preferably used because a light-emitting element with higher efficiency can be obtained.

正孔輸送層は上記正孔輸送材料を、例えば、真空蒸着法、スピンコート法、キャスト法、インクジェット法を含む印刷法、LB法等の公知の方法により、薄膜化することにより形成することができる。正孔輸送層の膜厚については特に制限はないが、通常は5nm〜5μm程度、好ましくは5nm〜200nmである。この正孔輸送層は上記材料の1種または2種以上からなる一層構造であってもよい。   The hole transport layer can be formed by thinning the hole transport material by a known method such as a vacuum deposition method, a spin coating method, a casting method, a printing method including an ink jet method, or an LB method. it can. Although there is no restriction | limiting in particular about the film thickness of a positive hole transport layer, Usually, 5 nm-about 5 micrometers, Preferably it is 5 nm-200 nm. The hole transport layer may have a single layer structure composed of one or more of the above materials.

また、不純物をドープしたp性の高い正孔輸送層を用いることもできる。その例としては、特開平4−297076号公報、特開2000−196140号公報、同2001−102175号公報の各公報、J.Appl.Phys.,95,5773(2004)等に記載されたものが挙げられる。   Alternatively, a hole transport layer having a high p property doped with impurities can be used. Examples thereof include JP-A-4-297076, JP-A-2000-196140, 2001-102175, J. Pat. Appl. Phys. 95, 5773 (2004), and the like.

本発明においては、このようなp性の高い正孔輸送層を用いることが、より低消費電力の素子を作製することができるため好ましい。   In the present invention, it is preferable to use a hole transport layer having such a high p property because a device with lower power consumption can be produced.

《電子輸送層》
電子輸送層とは電子を輸送する機能を有する材料からなり、広い意味で電子注入層、正孔阻止層も電子輸送層に含まれる。電子輸送層は単層または複数層設けることができる。
《Electron transport layer》
The electron transport layer is made of a material having a function of transporting electrons, and in a broad sense, an electron injection layer and a hole blocking layer are also included in the electron transport layer. The electron transport layer can be provided as a single layer or a plurality of layers.

従来、単層の電子輸送層、及び複数層とする場合は発光層に対して陰極側に隣接する電子輸送層に用いられる電子輸送材料(正孔阻止材料を兼ねる)としては、陰極より注入された電子を発光層に伝達する機能を有していればよく、その材料としては従来公知の化合物の中から任意のものを選択して用いることができ、例えば、ニトロ置換フルオレン誘導体、ジフェニルキノン誘導体、チオピランジオキシド誘導体、カルボジイミド、フレオレニリデンメタン誘導体、アントラキノジメタン及びアントロン誘導体、オキサジアゾール誘導体等が挙げられる。   Conventionally, in the case of a single electron transport layer and a plurality of layers, an electron transport material (also serving as a hole blocking material) used for an electron transport layer adjacent to the light emitting layer on the cathode side is injected from the cathode. As long as it has a function of transferring electrons to the light-emitting layer, any material can be selected and used from among conventionally known compounds. For example, nitro-substituted fluorene derivatives, diphenylquinone derivatives Thiopyrandioxide derivatives, carbodiimides, fluorenylidenemethane derivatives, anthraquinodimethane and anthrone derivatives, oxadiazole derivatives and the like.

更に、上記オキサジアゾール誘導体において、オキサジアゾール環の酸素原子を硫黄原子に置換したチアジアゾール誘導体、電子吸引基として知られているキノキサリン環を有するキノキサリン誘導体も、電子輸送材料として用いることができる。更にこれらの材料を高分子鎖に導入した、またはこれらの材料を高分子の主鎖とした高分子材料を用いることもできる。   Furthermore, in the above oxadiazole derivative, a thiadiazole derivative in which the oxygen atom of the oxadiazole ring is substituted with a sulfur atom, and a quinoxaline derivative having a quinoxaline ring known as an electron withdrawing group can also be used as an electron transport material. Furthermore, a polymer material in which these materials are introduced into a polymer chain or these materials are used as a polymer main chain can also be used.

また、8−キノリノール誘導体の金属錯体、例えば、トリス(8−キノリノール)アルミニウム(Alq)、トリス(5,7−ジクロロ−8−キノリノール)アルミニウム、トリス(5,7−ジブロモ−8−キノリノール)アルミニウム、トリス(2−メチル−8−キノリノール)アルミニウム、トリス(5−メチル−8−キノリノール)アルミニウム、ビス(8−キノリノール)亜鉛(Znq)等、及びこれらの金属錯体の中心金属がIn、Mg、Cu、Ca、Sn、GaまたはPbに置き替わった金属錯体も、電子輸送材料として用いることができる。   In addition, metal complexes of 8-quinolinol derivatives such as tris (8-quinolinol) aluminum (Alq), tris (5,7-dichloro-8-quinolinol) aluminum, tris (5,7-dibromo-8-quinolinol) aluminum Tris (2-methyl-8-quinolinol) aluminum, tris (5-methyl-8-quinolinol) aluminum, bis (8-quinolinol) zinc (Znq), and the like, and the central metals of these metal complexes are In, Mg, Metal complexes replaced with Cu, Ca, Sn, Ga or Pb can also be used as the electron transport material.

その他、メタルフリーもしくはメタルフタロシアニン、またはそれらの末端がアルキル基やスルホン酸基等で置換されているものも、電子輸送材料として好ましく用いることができる。また、発光層の材料として例示したジスチリルピラジン誘導体も、電子輸送材料として用いることができるし、正孔注入層、正孔輸送層と同様にn型−Si、n型−SiC等の無機半導体も電子輸送材料として用いることができる。   In addition, metal-free or metal phthalocyanine, or those having terminal ends substituted with an alkyl group or a sulfonic acid group can be preferably used as the electron transporting material. In addition, the distyrylpyrazine derivative exemplified as the material of the light emitting layer can also be used as an electron transport material, and an inorganic semiconductor such as n-type-Si, n-type-SiC, etc. as in the case of the hole injection layer and hole transport layer Can also be used as an electron transporting material.

電子輸送層は上記電子輸送材料を、例えば、真空蒸着法、スピンコート法、キャスト法、インクジェット法を含む印刷法、LB法等の公知の方法により、薄膜化することにより形成することができる。電子輸送層の膜厚については特に制限はないが、通常は5nm〜5μm程度、好ましくは5nm〜200nmである。電子輸送層は上記材料の1種または2種以上からなる一層構造であってもよい。   The electron transport layer can be formed by thinning the electron transport material by a known method such as a vacuum deposition method, a spin coating method, a casting method, a printing method including an ink jet method, or an LB method. Although there is no restriction | limiting in particular about the film thickness of an electron carrying layer, Usually, 5 nm-about 5 micrometers, Preferably it is 5 nm-200 nm. The electron transport layer may have a single layer structure composed of one or more of the above materials.

また、不純物をドープしたn性の高い電子輸送層を用いることもできる。その例としては、特開平4−297076号公報、同10−270172号公報、特開2000−196140号公報、同2001−102175号公報、J.Appl.Phys.,95,5773(2004)等に記載されたものが挙げられる。   Further, an electron transport layer having a high n property doped with impurities can also be used. Examples thereof include JP-A-4-297076, JP-A-10-270172, JP-A-2000-196140, 2001-102175, J.A. Appl. Phys. 95, 5773 (2004), and the like.

本発明においては、このようなn性の高い電子輸送層を用いることがより低消費電力の素子を作製することができるため好ましい。   In the present invention, it is preferable to use an electron transport layer having such a high n property because an element with lower power consumption can be manufactured.

《陽極》
有機EL素子における陽極としては、仕事関数の大きい(4eV以上)金属、合金、電気伝導性化合物及びこれらの混合物を電極物質とするものが好ましく用いられる。このような電極物質の具体例としては、Au等の金属、CuI、インジウムチンオキシド(ITO)、SnO、ZnO等の導電性透明材料が挙げられる。
"anode"
As the anode in the organic EL element, an electrode material made of a metal, an alloy, an electrically conductive compound, or a mixture thereof having a high work function (4 eV or more) is preferably used. Specific examples of such electrode materials include metals such as Au, and conductive transparent materials such as CuI, indium tin oxide (ITO), SnO 2 , and ZnO.

また、IDIXO(In−ZnO)等非晶質で透明導電膜を作製可能な材料を用いてもよい。陽極はこれらの電極物質を蒸着やスパッタリング等の方法により薄膜を形成させ、フォトリソグラフィー法で所望の形状のパターンを形成してもよく、あるいはパターン精度をあまり必要としない場合は(100μm以上程度)、上記電極物質の蒸着やスパッタリング時に所望の形状のマスクを介してパターンを形成してもよい。 Alternatively, an amorphous material such as IDIXO (In 2 O 3 —ZnO) capable of forming a transparent conductive film may be used. For the anode, these electrode materials may be formed into a thin film by a method such as vapor deposition or sputtering, and a pattern having a desired shape may be formed by a photolithography method, or when pattern accuracy is not so high (about 100 μm or more) A pattern may be formed through a mask having a desired shape at the time of vapor deposition or sputtering of the electrode material.

あるいは、有機導電性化合物のように塗布可能な物質を用いる場合には、印刷方式、コーティング方式等湿式成膜法を用いることもできる。この陽極より発光を取り出す場合には、透過率を10%より大きくすることが望ましく、また陽極としてのシート抵抗は数百Ω/□以下が好ましい。更に膜厚は材料にもよるが、通常10nm〜1000nm、好ましくは10nm〜200nmの範囲で選ばれる。   Or when using the substance which can be apply | coated like an organic electroconductivity compound, wet film-forming methods, such as a printing system and a coating system, can also be used. When light emission is extracted from the anode, it is desirable that the transmittance be greater than 10%, and the sheet resistance as the anode is preferably several hundred Ω / □ or less. Further, although the film thickness depends on the material, it is usually selected in the range of 10 nm to 1000 nm, preferably 10 nm to 200 nm.

《陰極》
一方、陰極としては仕事関数の小さい(4eV以下)金属(電子注入性金属と称する)、合金、電気伝導性化合物及びこれらの混合物を電極物質とするものが用いられる。このような電極物質の具体例としては、ナトリウム、ナトリウム−カリウム合金、マグネシウム、リチウム、マグネシウム/銅混合物、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al)混合物、インジウム、リチウム/アルミニウム混合物、希土類金属等が挙げられる。これらの中で、電子注入性及び酸化等に対する耐久性の点から、電子注入性金属とこれより仕事関数の値が大きく安定な金属である第二金属との混合物、例えば、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al)混合物、リチウム/アルミニウム混合物、アルミニウム等が好適である。
"cathode"
On the other hand, as the cathode, a material having a low work function (4 eV or less) metal (referred to as an electron injecting metal), an alloy, an electrically conductive compound, and a mixture thereof as an electrode material is used. Specific examples of such electrode materials include sodium, sodium-potassium alloy, magnesium, lithium, magnesium / copper mixture, magnesium / silver mixture, magnesium / aluminum mixture, magnesium / indium mixture, aluminum / aluminum oxide (Al 2 O 3 ) Mixtures, indium, lithium / aluminum mixtures, rare earth metals and the like. Among these, from the point of durability against electron injection and oxidation, etc., a mixture of an electron injecting metal and a second metal which is a stable metal having a larger work function than this, for example, a magnesium / silver mixture, Magnesium / aluminum mixtures, magnesium / indium mixtures, aluminum / aluminum oxide (Al 2 O 3 ) mixtures, lithium / aluminum mixtures, aluminum and the like are preferred.

陰極はこれらの電極物質を蒸着やスパッタリング等の方法により薄膜を形成させることにより、作製することができる。また、陰極としてのシート抵抗は数百Ω/□以下が好ましく、膜厚は通常10nm〜5μm、好ましくは50nm〜200nmの範囲で選ばれる。尚、発光した光を透過させるため、有機EL素子の陽極または陰極のいずれか一方が透明または半透明であれば発光輝度が向上し好都合である。   The cathode can be produced by forming a thin film of these electrode materials by a method such as vapor deposition or sputtering. The sheet resistance as a cathode is preferably several hundred Ω / □ or less, and the film thickness is usually selected in the range of 10 nm to 5 μm, preferably 50 nm to 200 nm. In order to transmit the emitted light, if either one of the anode or the cathode of the organic EL element is transparent or translucent, the light emission luminance is improved, which is convenient.

また、陰極に上記金属を1nm〜20nmの膜厚で作製した後に、陽極の説明で挙げた導電性透明材料をその上に作製することで、透明または半透明の陰極を作製することができ、これを応用することで陽極と陰極の両方が透過性を有する素子を作製することができる。   Moreover, after producing the said metal by the film thickness of 1 nm-20 nm to a cathode, the transparent or semi-transparent cathode can be produced by producing the electroconductive transparent material quoted by description of the anode on it, By applying this, an element in which both the anode and the cathode are transmissive can be manufactured.

《支持基板》
本発明の有機EL素子に用いることのできる支持基板(以下、基体、基板、基材、支持体等とも言う)としては、ガラス、プラスチック等の種類には特に限定はなく、また透明であっても不透明であってもよい。支持基板側から光を取り出す場合には、支持基板は透明であることが好ましい。好ましく用いられる透明な支持基板としては、ガラス、石英、透明樹脂フィルムを挙げることができる。特に好ましい支持基板は、有機EL素子にフレキシブル性を与えることが可能な樹脂フィルムである。
《Support substrate》
As a support substrate (hereinafter also referred to as a substrate, substrate, substrate, support, etc.) that can be used in the organic EL device of the present invention, there is no particular limitation on the type of glass, plastic, etc., and it is transparent. May be opaque. When extracting light from the support substrate side, the support substrate is preferably transparent. Examples of the transparent support substrate preferably used include glass, quartz, and a transparent resin film. A particularly preferable support substrate is a resin film capable of giving flexibility to the organic EL element.

樹脂フィルムとしては、例えば、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)等のポリエステル、ポリエチレン、ポリプロピレン、セロファン、セルロースジアセテート、セルローストリアセテート、セルロースアセテートブチレート、セルロースアセテートプロピオネート(CAP)、セルロースアセテートフタレート(TAC)、セルロースナイトレート等のセルロースエステル類またはそれらの誘導体、ポリ塩化ビニリデン、ポリビニルアルコール、ポリエチレンビニルアルコール、シンジオタクティックポリスチレン、ポリカーボネート、ノルボルネン樹脂、ポリメチルペンテン、ポリエーテルケトン、ポリイミド、ポリエーテルスルホン(PES)、ポリフェニレンスルフィド、ポリスルホン類、ポリエーテルイミド、ポリエーテルケトンイミド、ポリアミド、フッ素樹脂、ナイロン、ポリメチルメタクリレート、アクリルあるいはポリアリレート類、アートン(商品名JSR社製)あるいはアペル(商品名三井化学社製)といったシクロオレフィン系樹脂等を挙げられる。   Examples of the resin film include polyesters such as polyethylene terephthalate (PET) and polyethylene naphthalate (PEN), polyethylene, polypropylene, cellophane, cellulose diacetate, cellulose triacetate, cellulose acetate butyrate, cellulose acetate propionate (CAP), Cellulose esters such as cellulose acetate phthalate (TAC) and cellulose nitrate or derivatives thereof, polyvinylidene chloride, polyvinyl alcohol, polyethylene vinyl alcohol, syndiotactic polystyrene, polycarbonate, norbornene resin, polymethylpentene, polyether ketone, polyimide , Polyethersulfone (PES), polyphenylene sulfide, polysulfones Cycloolefin resins such as polyetherimide, polyetherketoneimide, polyamide, fluororesin, nylon, polymethylmethacrylate, acrylic or polyarylate, Arton (trade name, manufactured by JSR) or Appel (trade name, manufactured by Mitsui Chemicals) Can be mentioned.

樹脂フィルムの表面には、無機物、有機物の被膜またはその両者のハイブリッド被膜が形成されていてもよく、JIS K 7129−1992に準拠した方法で測定された、水蒸気透過度(25±0.5℃、相対湿度(90±2)%RH)が0.01g/(m・24h)以下のバリア性フィルムであることが好ましく、更には、JIS K 7126−1987に準拠した方法で測定された酸素透過度が、10−3ml/(m・24h・atm)以下、水蒸気透過度が、10−5g/(m・24h)以下の高バリア性フィルムであることが好ましい。 On the surface of the resin film, an inorganic film, an organic film, or a hybrid film of both may be formed. Water vapor permeability (25 ± 0.5 ° C.) measured by a method according to JIS K 7129-1992. , Relative humidity (90 ± 2)% RH) is preferably 0.01 g / (m 2 · 24 h) or less, and further, oxygen measured by a method according to JIS K 7126-1987. A high barrier film having a permeability of 10 −3 ml / (m 2 · 24 h · atm) or less and a water vapor permeability of 10 −5 g / (m 2 · 24 h) or less is preferable.

バリア膜を形成する材料としては、水分や酸素等素子の劣化をもたらすものの浸入を抑制する機能を有する材料であればよく、例えば、酸化珪素、二酸化珪素、窒化珪素等を用いることができる。更に該膜の脆弱性を改良するために、これら無機層と有機材料からなる層の積層構造を持たせることがより好ましい。無機層と有機層の積層順については特に制限はないが、両者を交互に複数回積層させることが好ましい。   As a material for forming the barrier film, any material may be used as long as it has a function of suppressing entry of elements that cause deterioration of elements such as moisture and oxygen. For example, silicon oxide, silicon dioxide, silicon nitride, or the like can be used. Further, in order to improve the brittleness of the film, it is more preferable to have a laminated structure of these inorganic layers and organic material layers. Although there is no restriction | limiting in particular about the lamination | stacking order of an inorganic layer and an organic layer, It is preferable to laminate | stack both alternately several times.

バリア膜の形成方法については特に限定はなく、例えば、真空蒸着法、スパッタリング法、反応性スパッタリング法、分子線エピタキシー法、クラスタ−イオンビーム法、イオンプレーティング法、プラズマ重合法、大気圧プラズマ重合法、プラズマCVD法、レーザーCVD法、熱CVD法、コーティング法等を用いることができるが、特開2004−68143号公報に記載されているような大気圧プラズマ重合法によるものが特に好ましい。   The method for forming the barrier film is not particularly limited. For example, the vacuum deposition method, sputtering method, reactive sputtering method, molecular beam epitaxy method, cluster ion beam method, ion plating method, plasma polymerization method, atmospheric pressure plasma weight A combination method, a plasma CVD method, a laser CVD method, a thermal CVD method, a coating method, and the like can be used, but an atmospheric pressure plasma polymerization method as described in JP-A-2004-68143 is particularly preferable.

不透明な支持基板としては、例えば、アルミ、ステンレス等の金属板、フィルムや不透明樹脂基板、セラミック製の基板等が挙げられる。   Examples of the opaque support substrate include metal plates such as aluminum and stainless steel, films, opaque resin substrates, and ceramic substrates.

本発明の有機EL素子の発光の室温における外部取り出し効率は、1%以上であることが好ましく、より好ましくは5%以上である。   The external extraction efficiency at room temperature of light emission of the organic EL device of the present invention is preferably 1% or more, more preferably 5% or more.

ここに、外部取り出し量子効率(%)=有機EL素子外部に発光した光子数/有機EL素子に流した電子数×100である。   Here, the external extraction quantum efficiency (%) = the number of photons emitted to the outside of the organic EL element / the number of electrons sent to the organic EL element × 100.

また、カラーフィルター等の色相改良フィルター等を併用しても、有機EL素子からの発光色を蛍光体を用いて多色へ変換する色変換フィルターを併用してもよい。色変換フィルターを用いる場合においては、有機EL素子の発光のλmaxは480nm以下が好ましい。   In addition, a hue improvement filter such as a color filter may be used in combination, or a color conversion filter that converts the emission color from the organic EL element into multiple colors using a phosphor. In the case of using a color conversion filter, the λmax of light emission of the organic EL element is preferably 480 nm or less.

《封止》
本発明に用いられる封止手段としては、例えば、封止部材と電極、支持基板とを接着剤で接着する方法を挙げることができる。
<Sealing>
As a sealing means used for this invention, the method of adhere | attaching a sealing member, an electrode, and a support substrate with an adhesive agent can be mentioned, for example.

封止部材としては、有機EL素子の表示領域を覆うように配置されておればよく、凹板状でも平板状でもよい。また透明性、電気絶縁性は特に問わない。   As a sealing member, it should just be arrange | positioned so that the display area | region of an organic EL element may be covered, and concave plate shape or flat plate shape may be sufficient. Further, transparency and electrical insulation are not particularly limited.

具体的には、ガラス板、ポリマー板・フィルム、金属板・フィルム等が挙げられる。ガラス板としては、特にソーダ石灰ガラス、バリウム・ストロンチウム含有ガラス、鉛ガラス、アルミノケイ酸ガラス、ホウケイ酸ガラス、バリウムホウケイ酸ガラス、石英等を挙げることができる。また、ポリマー板としては、ポリカーボネート、アクリル、ポリエチレンテレフタレート、ポリエーテルサルファイド、ポリサルフォン等を挙げることができる。金属板としては、ステンレス、鉄、銅、アルミニウム、マグネシウム、ニッケル、亜鉛、クロム、チタン、モリブテン、シリコン、ゲルマニウム及びタンタルからなる群から選ばれる一種以上の金属または合金からなるものが挙げられる。   Specific examples include a glass plate, a polymer plate / film, and a metal plate / film. Examples of the glass plate include soda-lime glass, barium / strontium-containing glass, lead glass, aluminosilicate glass, borosilicate glass, barium borosilicate glass, and quartz. Examples of the polymer plate include polycarbonate, acrylic, polyethylene terephthalate, polyether sulfide, and polysulfone. Examples of the metal plate include those made of one or more metals or alloys selected from the group consisting of stainless steel, iron, copper, aluminum, magnesium, nickel, zinc, chromium, titanium, molybdenum, silicon, germanium, and tantalum.

本発明においては、素子を薄膜化できるということからポリマーフィルム、金属フィルムを好ましく使用することができる。   In the present invention, a polymer film and a metal film can be preferably used because the element can be thinned.

更には、ポリマーフィルムは、JIS K 7126−1987に準拠した方法で測定された酸素透過度が1×10−3ml/(m・24h・atm)以下、JIS K 7129−1992に準拠した方法で測定された、水蒸気透過度(25±0.5℃、相対湿度(90±2)%RH)が、1×10−6g/(m・24h)以下のものであることが好ましい。 Furthermore, the polymer film has an oxygen permeability of 1 × 10 −3 ml / (m 2 · 24 h · atm) or less measured by a method according to JIS K 7126-1987, and a method according to JIS K 7129-1992. It is preferable that the water vapor permeability (25 ± 0.5 ° C., relative humidity (90 ± 2)% RH) measured in (1) is 1 × 10 −6 g / (m 2 · 24 h) or less.

封止部材を凹状に加工するのは、サンドブラスト加工、化学エッチング加工等が使われる。   For processing the sealing member into a concave shape, sandblasting, chemical etching, or the like is used.

接着剤として具体的には、アクリル酸系オリゴマー、メタクリル酸系オリゴマーの反応性ビニル基を有する光硬化及び熱硬化型接着剤、2−シアノアクリル酸エステル等の湿気硬化型等の接着剤を挙げることができる。また、エポキシ系等の熱及び化学硬化型(二液混合)を挙げることができる。また、ホットメルト型のポリアミド、ポリエステル、ポリオレフィンを挙げることができる。また、カチオン硬化タイプの紫外線硬化型エポキシ樹脂接着剤を挙げることができる。   Specific examples of the adhesive include photocuring and thermosetting adhesives having reactive vinyl groups such as acrylic acid oligomers and methacrylic acid oligomers, and moisture curing adhesives such as 2-cyanoacrylates. be able to. Moreover, heat | fever and chemical curing types (two-component mixing), such as an epoxy type, can be mentioned. Moreover, hot-melt type polyamide, polyester, and polyolefin can be mentioned. Moreover, a cationic curing type ultraviolet curing epoxy resin adhesive can be mentioned.

尚、有機EL素子が熱処理により劣化する場合があるので、室温から80℃までに接着硬化できるものが好ましい。また、前記接着剤中に乾燥剤を分散させておいてもよい。封止部分への接着剤の塗布は市販のディスペンサーを使ってもよいし、スクリーン印刷のように印刷してもよい。   In addition, since an organic EL element may deteriorate by heat processing, what can be adhesive-hardened from room temperature to 80 degreeC is preferable. A desiccant may be dispersed in the adhesive. Application | coating of the adhesive agent to a sealing part may use commercially available dispenser, and may print like screen printing.

また、有機層を挟み支持基板と対向する側の電極の外側に該電極と有機層を被覆し、支持基板と接する形で無機物、有機物の層を形成し封止膜とすることも好適にできる。   In addition, it is also preferable that the electrode and the organic layer are coated on the outside of the electrode facing the support substrate with the organic layer interposed therebetween, and an inorganic or organic layer is formed in contact with the support substrate to form a sealing film. .

この場合、該膜を形成する材料としては、水分や酸素等素子の劣化をもたらすものの浸入を抑制する機能を有する材料であればよく、例えば、酸化珪素、二酸化珪素、窒化珪素等を用いることができる。   In this case, the material for forming the film may be any material that has a function of suppressing intrusion of elements that cause deterioration of elements such as moisture and oxygen. For example, silicon oxide, silicon dioxide, silicon nitride, or the like may be used. it can.

更に該膜の脆弱性を改良するために、これら無機層と有機材料からなる層の積層構造を持たせることが好ましい。これらの膜の形成方法については、特に限定はなく、例えば真空蒸着法、スパッタリング法、反応性スパッタリング法、分子線エピタキシー法、クラスタ−イオンビーム法、イオンプレーティング法、プラズマ重合法、大気圧プラズマ重合法、プラズマCVD法、レーザーCVD法、熱CVD法、コーティング法等を用いることができる。   Further, in order to improve the brittleness of the film, it is preferable to have a laminated structure of these inorganic layers and layers made of organic materials. The method for forming these films is not particularly limited. For example, vacuum deposition, sputtering, reactive sputtering, molecular beam epitaxy, cluster-ion beam method, ion plating method, plasma polymerization method, atmospheric pressure plasma A polymerization method, a plasma CVD method, a laser CVD method, a thermal CVD method, a coating method, or the like can be used.

封止部材と有機EL素子の表示領域との間隙には、気相及び液相では、窒素、アルゴン等の不活性気体やフッ化炭化水素、シリコンオイルのような不活性液体を注入することが好ましい。また真空とすることも可能である。また、内部に吸湿性化合物を封入することもできる。   In the gap between the sealing member and the display area of the organic EL element, an inert gas such as nitrogen or argon, or an inert liquid such as fluorinated hydrocarbon or silicon oil can be injected in the gas phase and liquid phase. preferable. A vacuum is also possible. Moreover, a hygroscopic compound can also be enclosed inside.

吸湿性化合物としては、例えば、金属酸化物(例えば、酸化ナトリウム、酸化カリウム、酸化カルシウム、酸化バリウム、酸化マグネシウム、酸化アルミニウム等)、硫酸塩(例えば、硫酸ナトリウム、硫酸カルシウム、硫酸マグネシウム、硫酸コバルト等)、金属ハロゲン化物(例えば、塩化カルシウム、塩化マグネシウム、フッ化セシウム、フッ化タンタル、臭化セリウム、臭化マグネシウム、沃化バリウム、沃化マグネシウム等)、過塩素酸類(例えば、過塩素酸バリウム、過塩素酸マグネシウム等)等が挙げられ、硫酸塩、金属ハロゲン化物及び過塩素酸類においては無水塩が好適に用いられる。   Examples of the hygroscopic compound include metal oxides (for example, sodium oxide, potassium oxide, calcium oxide, barium oxide, magnesium oxide, aluminum oxide) and sulfates (for example, sodium sulfate, calcium sulfate, magnesium sulfate, cobalt sulfate). Etc.), metal halides (eg calcium chloride, magnesium chloride, cesium fluoride, tantalum fluoride, cerium bromide, magnesium bromide, barium iodide, magnesium iodide etc.), perchloric acids (eg perchloric acid) Barium, magnesium perchlorate, and the like), and anhydrous salts are preferably used in sulfates, metal halides, and perchloric acids.

《保護膜、保護板》
有機層を挟み支持基板と対向する側の前記封止膜、あるいは前記封止用フィルムの外側に、素子の機械的強度を高めるために保護膜、あるいは保護板を設けてもよい。特に封止が前記封止膜により行われている場合には、その機械的強度は必ずしも高くないため、このような保護膜、保護板を設けることが好ましい。
《Protective film, protective plate》
In order to increase the mechanical strength of the element, a protective film or a protective plate may be provided on the outer side of the sealing film on the side facing the support substrate with the organic layer interposed therebetween or on the sealing film. In particular, when the sealing is performed by the sealing film, the mechanical strength is not necessarily high, and thus it is preferable to provide such a protective film and a protective plate.

これに使用することができる材料としては、前記封止に用いたのと同様なガラス板、ポリマー板・フィルム、金属板・フィルム等を用いることができるが、軽量且つ薄膜化ということからポリマーフィルムを用いることが好ましい。   As a material that can be used for this, the same glass plate, polymer plate / film, metal plate / film, and the like used for the sealing can be used, but the polymer film is light and thin. Is preferably used.

《光取り出し》
有機EL素子は空気よりも屈折率の高い(屈折率が1.7〜2.1程度)層の内部で発光し、発光層で発生した光のうち15%から20%程度の光しか取り出せないことが一般的に言われている。これは、臨界角以上の角度θで界面(透明基板と空気との界面)に入射する光は、全反射を起こし素子外部に取り出すことができないことや、透明電極ないし発光層と透明基板との間で光が全反射を起こし、光が透明電極ないし発光層を導波し、結果として光が素子側面方向に逃げるためである。
《Light extraction》
The organic EL element emits light inside a layer having a refractive index higher than that of air (refractive index is about 1.7 to 2.1) and can extract only about 15% to 20% of the light generated in the light emitting layer. It is generally said. This is because light incident on the interface (interface between the transparent substrate and air) at an angle θ greater than the critical angle causes total reflection and cannot be taken out of the device, or between the transparent electrode or light emitting layer and the transparent substrate. This is because the light is totally reflected between the light and the light is guided through the transparent electrode or the light emitting layer, and as a result, the light escapes in the direction of the element side surface.

この光の取り出しの効率を向上させる手法としては、例えば、透明基板表面に凹凸を形成し、透明基板と空気界面での全反射を防ぐ方法(米国特許第4,774,435号明細書)、基板に集光性を持たせることにより効率を向上させる方法(特開昭63−314795号公報)、素子の側面等に反射面を形成する方法(特開平1−220394号公報)、基板と発光体の間に中間の屈折率を持つ平坦層を導入し、反射防止膜を形成する方法(特開昭62−172691号公報)、基板と発光体の間に基板よりも低屈折率を持つ平坦層を導入する方法(特開2001−202827号公報)、基板、透明電極層や発光層のいずれかの層間(含む、基板と外界間)に回折格子を形成する方法(特開平11−283751号公報)等がある。   As a method for improving the light extraction efficiency, for example, a method of forming irregularities on the surface of the transparent substrate to prevent total reflection at the interface between the transparent substrate and the air (US Pat. No. 4,774,435), A method of improving efficiency by providing a light collecting property to a substrate (Japanese Patent Laid-Open No. 63-314795), a method of forming a reflective surface on a side surface of an element (Japanese Patent Laid-Open No. 1-220394), and light emission from a substrate A method of forming an antireflection film by introducing a flat layer having an intermediate refractive index between the bodies (Japanese Patent Laid-Open No. 62-172691), a flat having a lower refractive index between the substrate and the light emitter than the substrate A method of introducing a layer (Japanese Patent Laid-Open No. 2001-202827), a method of forming a diffraction grating between any one of a substrate, a transparent electrode layer and a light emitting layer (including between the substrate and the outside) (Japanese Patent Laid-Open No. 11-283951) Gazette).

本発明においては、これらの方法を本発明の有機EL素子と組み合わせて用いることができるが、基板と発光体の間に基板よりも低屈折率を持つ平坦層を導入する方法、あるいは基板、透明電極層や発光層のいずれかの層間(含む、基板と外界間)に回折格子を形成する方法を好適に用いることができる。   In the present invention, these methods can be used in combination with the organic EL device of the present invention. However, a method of introducing a flat layer having a lower refractive index than the substrate between the substrate and the light emitter, or a substrate, transparent A method of forming a diffraction grating between any layers of the electrode layer and the light emitting layer (including between the substrate and the outside) can be suitably used.

本発明はこれらの手段を組み合わせることにより、更に高輝度あるいは耐久性に優れた素子を得ることができる。   In the present invention, by combining these means, it is possible to obtain an element having higher luminance or durability.

透明電極と透明基板の間に低屈折率の媒質を光の波長よりも長い厚みで形成すると、透明電極から出てきた光は、媒質の屈折率が低いほど外部への取り出し効率が高くなる。   When a medium having a low refractive index is formed between the transparent electrode and the transparent substrate with a thickness longer than the wavelength of light, the light extracted from the transparent electrode has a higher extraction efficiency to the outside as the refractive index of the medium is lower.

低屈折率層としては、例えば、エアロゲル、多孔質シリカ、フッ化マグネシウム、フッ素系ポリマー等が挙げられる。透明基板の屈折率は一般に1.5〜1.7程度であるので、低屈折率層は屈折率がおよそ1.5以下であることが好ましい。また、更に1.35以下であることが好ましい。   Examples of the low refractive index layer include aerogel, porous silica, magnesium fluoride, and a fluorine-based polymer. Since the refractive index of the transparent substrate is generally about 1.5 to 1.7, the low refractive index layer preferably has a refractive index of about 1.5 or less. Further, it is preferably 1.35 or less.

また、低屈折率媒質の厚みは媒質中の波長の2倍以上となるのが望ましい。これは低屈折率媒質の厚みが、光の波長程度になってエバネッセントで染み出した電磁波が基板内に入り込む膜厚になると、低屈折率層の効果が薄れるからである。   The thickness of the low refractive index medium is preferably at least twice the wavelength in the medium. This is because the effect of the low refractive index layer is diminished when the thickness of the low refractive index medium is about the wavelength of light and the electromagnetic wave that has exuded by evanescent enters the substrate.

全反射を起こす界面もしくはいずれかの媒質中に回折格子を導入する方法は、光取り出し効率の向上効果が高いという特徴がある。   The method of introducing a diffraction grating into an interface or any medium that causes total reflection is characterized by a high effect of improving light extraction efficiency.

この方法は回折格子が1次の回折や2次の回折といった所謂ブラッグ回折により、光の向きを屈折とは異なる特定の向きに変えることができる性質を利用して、発光層から発生した光のうち層間での全反射等により外に出ることができない光を、いずれかの層間もしくは、媒質中(透明基板内や透明電極内)に回折格子を導入することで光を回折させ、光を外に取り出そうとするものである。   This method uses the property that the diffraction grating can change the direction of light to a specific direction different from refraction by so-called Bragg diffraction such as first-order diffraction and second-order diffraction. Light that cannot be emitted due to total internal reflection between layers is diffracted by introducing a diffraction grating in any layer or medium (in a transparent substrate or transparent electrode), and the light is removed. I want to take it out.

導入する回折格子は、二次元的な周期屈折率を持っていることが望ましい。これは発光層で発光する光はあらゆる方向にランダムに発生するので、ある方向にのみ周期的な屈折率分布を持っている一般的な1次元回折格子では、特定の方向に進む光しか回折されず、光の取り出し効率がさほど上がらない。   The introduced diffraction grating desirably has a two-dimensional periodic refractive index. This is because light emitted from the light-emitting layer is randomly generated in all directions, so in a general one-dimensional diffraction grating having a periodic refractive index distribution only in a certain direction, only light traveling in a specific direction is diffracted. Therefore, the light extraction efficiency does not increase so much.

しかしながら、屈折率分布を二次元的な分布にすることにより、あらゆる方向に進む光が回折され、光の取り出し効率が上がる。回折格子を導入する位置としては前述の通り、いずれかの層間もしくは媒質中(透明基板内や透明電極内)でもよいが、光が発生する場所である有機発光層の近傍が望ましい。   However, by making the refractive index distribution a two-dimensional distribution, light traveling in all directions is diffracted, and light extraction efficiency is increased. As described above, the position where the diffraction grating is introduced may be in any of the layers or in the medium (in the transparent substrate or in the transparent electrode), but is preferably in the vicinity of the organic light emitting layer where light is generated.

このとき、回折格子の周期は媒質中の光の波長の約1/2〜3倍程度が好ましい。   At this time, the period of the diffraction grating is preferably about 1/2 to 3 times the wavelength of light in the medium.

回折格子の配列は正方形のラチス状、三角形のラチス状、ハニカムラチス状等、2次元的に配列が繰り返されることが好ましい。   The arrangement of the diffraction grating is preferably two-dimensionally repeated such as a square lattice, a triangular lattice, or a honeycomb lattice.

《集光シート》
本発明の有機EL素子は基板の光取り出し側に、例えば、マイクロレンズアレイ状の構造を設けるように加工し、あるいは所謂集光シートと組み合わせることにより、特定方向、例えば、素子発光面に対し正面方向に集光することにより、特定方向上の輝度を高めることができる。
<Condenser sheet>
The organic EL device of the present invention is processed to provide, for example, a microlens array-like structure on the light extraction side of the substrate, or in combination with a so-called condensing sheet, so that the organic EL device is in front of a specific direction, for example, the device light emitting surface. By condensing in the direction, the luminance in a specific direction can be increased.

マイクロレンズアレイの例としては、基板の光取り出し側に一辺が30μmでその頂角が90度となるような四角錐を2次元に配列する。一辺は10μm〜100μmが好ましい。これより小さくなると回折の効果が発生して色付く、大きすぎると厚みが厚くなり好ましくない。   As an example of the microlens array, quadrangular pyramids having a side of 30 μm and an apex angle of 90 degrees are two-dimensionally arranged on the light extraction side of the substrate. One side is preferably 10 μm to 100 μm. If it becomes smaller than this, the effect of diffraction will generate | occur | produce and color, and if too large, thickness will become thick and is not preferable.

集光シートとしては、例えば、液晶表示装置のLEDバックライトで実用化されているものを用いることが可能である。このようなシートとして、例えば、住友スリーエム社製輝度上昇フィルム(BEF)等を用いることができる。プリズムシートの形状としては、例えば、基材に頂角90度、ピッチ50μmの△状のストライプが形成されたものであってもよいし、頂角が丸みを帯びた形状、ピッチをランダムに変化させた形状、その他の形状であってもよい。   As the condensing sheet, for example, a sheet that is put into practical use in an LED backlight of a liquid crystal display device can be used. As such a sheet, for example, a brightness enhancement film (BEF) manufactured by Sumitomo 3M Limited can be used. As the shape of the prism sheet, for example, the base material may be formed by forming a △ -shaped stripe having a vertex angle of 90 degrees and a pitch of 50 μm, or the vertex angle is rounded and the pitch is changed randomly. Other shapes may be used.

また、発光素子からの光放射角を制御するために、光拡散板・フィルムを集光シートと併用してもよい。例えば、(株)きもと製拡散フィルム(ライトアップ)等を用いることができる。   Moreover, in order to control the light emission angle from a light emitting element, you may use together a light diffusing plate and a film with a condensing sheet. For example, a diffusion film (light-up) manufactured by Kimoto Co., Ltd. can be used.

《有機EL素子の作製方法》
本発明の有機EL素子の作製方法の一例として、陽極/正孔注入層/正孔輸送層/発光層/正孔阻止層/電子輸送層/陰極からなる有機EL素子の作製法を説明する。
<< Method for producing organic EL element >>
As an example of the method for producing the organic EL device of the present invention, a method for producing an organic EL device comprising an anode / hole injection layer / hole transport layer / light emitting layer / hole blocking layer / electron transport layer / cathode will be described.

まず適当な基体上に所望の電極物質、例えば、陽極用物質からなる薄膜を1μm以下、好ましくは10nm〜200nmの膜厚になるように、蒸着やスパッタリング等の方法により形成させ陽極を作製する。   First, a desired electrode material, for example, a thin film made of an anode material is formed on a suitable substrate so as to have a film thickness of 1 μm or less, preferably 10 nm to 200 nm, to form an anode.

次に、この上に有機EL素子材料である正孔注入層、正孔輸送層、発光層、正孔阻止層、電子輸送層等の有機化合物薄膜を形成させる。   Next, organic compound thin films such as a hole injection layer, a hole transport layer, a light emitting layer, a hole blocking layer, and an electron transport layer, which are organic EL element materials, are formed thereon.

これら各層の形成方法としては、前記の如く蒸着法、ウェットプロセス(スピンコート法、キャスト法、インクジェット法、印刷法)等があるが、均質な膜が得られやすく、且つピンホールが生成しにくい等の点から、本発明においてはスピンコート法、インクジェット法、印刷法等の塗布法による成膜が好ましい。   As a method for forming each of these layers, there are a vapor deposition method, a wet process (spin coating method, casting method, ink jet method, printing method) and the like as described above, but it is easy to obtain a homogeneous film and it is difficult to generate pinholes. In view of the above, film formation by a coating method such as a spin coating method, an ink jet method, or a printing method is preferable in the present invention.

有機EL材料を溶解または分散する液媒体としては、例えば、メチルエチルケトン、シクロヘキサノン等のケトン類、酢酸エチル等の脂肪酸エステル類、ジクロロベンゼン等のハロゲン化炭化水素類、トルエン、キシレン、メシチレン、シクロヘキシルベンゼン等の芳香族炭化水素類、シクロヘキサン、デカリン、ドデカン等の脂肪族炭化水素類、DMF、DMSO等の有機溶媒を用いることができる。また分散方法としては、超音波、高剪断力分散やメディア分散等の分散方法により分散することができる。   Examples of the liquid medium for dissolving or dispersing the organic EL material include ketones such as methyl ethyl ketone and cyclohexanone, fatty acid esters such as ethyl acetate, halogenated hydrocarbons such as dichlorobenzene, toluene, xylene, mesitylene, cyclohexylbenzene and the like. Aromatic hydrocarbons, aliphatic hydrocarbons such as cyclohexane, decalin, and dodecane, and organic solvents such as DMF and DMSO can be used. Moreover, as a dispersion method, it can disperse | distribute by dispersion methods, such as an ultrasonic wave, high shear force dispersion | distribution, and media dispersion | distribution.

これらの層を形成後、その上に陰極用物質からなる薄膜を1μm以下、好ましくは、50nm〜200nmの範囲の膜厚になるように、例えば、蒸着やスパッタリング等の方法により形成させ、陰極を設けることにより所望の有機EL素子が得られる。   After these layers are formed, a thin film made of a cathode material is formed thereon by 1 μm or less, preferably by a method such as vapor deposition or sputtering so that the film thickness is in the range of 50 nm to 200 nm. By providing, a desired organic EL element can be obtained.

また、作製順序を逆にして、陰極、電子注入層、電子輸送層、発光層、正孔輸送層、正孔注入層、陽極の順に作製することも可能である。このようにして得られた多色の表示装置に、直流電圧を印加する場合には陽極を+、陰極を−の極性として電圧2V〜40V程度を印加すると発光が観測できる。また交流電圧を印加してもよい。尚、印加する交流の波形は任意でよい。   In addition, it is also possible to reverse the production order and produce the cathode, the electron injection layer, the electron transport layer, the light emitting layer, the hole transport layer, the hole injection layer, and the anode in this order. When a DC voltage is applied to the multicolor display device thus obtained, light emission can be observed by applying a voltage of about 2 V to 40 V with the anode as + and the cathode as-. An alternating voltage may be applied. The alternating current waveform to be applied may be arbitrary.

《用途》
本発明の有機EL素子は、表示デバイス、ディスプレイ、各種発光光源として用いることができる。発光光源として、例えば、照明装置(家庭用照明、車内照明)、時計や液晶用バックライト、看板広告、信号機、光記憶媒体の光源、電子写真複写機の光源、光通信処理機の光源、光センサーの光源等が挙げられるがこれに限定するものではないが、特に液晶表示装置のバックライト、照明用光源としての用途に有効に用いることができる。
<Application>
The organic EL element of the present invention can be used as a display device, a display, and various light emission sources. For example, lighting devices (home lighting, interior lighting), clock and liquid crystal backlights, billboard advertisements, traffic lights, light sources of optical storage media, light sources of electrophotographic copying machines, light sources of optical communication processors, light Although the light source of a sensor etc. are mentioned, It is not limited to this, Especially, it can use effectively for the use as a backlight of a liquid crystal display device, and a light source for illumination.

本発明の有機EL素子においては、必要に応じ成膜時にメタルマスクやインクジェットプリンティング法等でパターニングを施してもよい。   In the organic EL element of the present invention, patterning may be performed by a metal mask, an ink jet printing method, or the like as needed during film formation.

パターニングする場合は、電極のみをパターニングしてもよいし、電極と発光層をパターニングしてもよいし、素子全層をパターニングしてもよく、素子の作製においては、従来公知の方法を用いることができる。   In the case of patterning, only the electrode may be patterned, the electrode and the light emitting layer may be patterned, or the entire layer of the device may be patterned. Can do.

本発明の有機EL素子や本発明に係る化合物の発光する色は、「新編色彩科学ハンドブック」(日本色彩学会編、東京大学出版会、1985)の108頁の図4.16において、分光放射輝度計CS−1000(コニカミノルタセンシング社製)で測定した結果をCIE色度座標に当てはめたときの色で決定される。   The light emission color of the organic EL device of the present invention and the compound according to the present invention is shown in FIG. 4.16 on page 108 of “New Color Science Handbook” (edited by the Japan Color Society, University of Tokyo Press, 1985). It is determined by the color when the result measured with the total CS-1000 (manufactured by Konica Minolta Sensing) is applied to the CIE chromaticity coordinates.

また、本発明の有機EL素子が白色素子の場合には、白色とは、2度視野角正面輝度を上記方法により測定した際に、1000cd/mでのCIE1931表色系における色度がX=0.33±0.07、Y=0.33±0.1の領域内にあることを言う。 When the organic EL element of the present invention is a white element, white means that the chromaticity in the CIE1931 color system at 1000 cd / m 2 is X when the 2 ° viewing angle front luminance is measured by the above method. = 0.33 ± 0.07 and Y = 0.33 ± 0.1.

以下、実施例により本発明を詳細に説明するが、本発明はこれらに限定されない。また、以下の実施例において用いられる化合物の構造を下記に示す。   EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these. The structures of the compounds used in the following examples are shown below.

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

Figure 0005531446
Figure 0005531446

実施例1
《有機EL素子1−1の作製》
陽極として100mm×100mm×1.1mmのガラス基板上にITO(インジウムチンオキシド)を100nm成膜した基板(NHテクノグラス社製NA45)にパターニングを行った後、このITO透明電極を設けた透明支持基板をイソプロピルアルコールで超音波洗浄し、乾燥窒素ガスで乾燥し、UVオゾン洗浄を5分間行った。
Example 1
<< Production of Organic EL Element 1-1 >>
Transparent support provided with this ITO transparent electrode after patterning on a substrate (NH45 manufactured by NH Techno Glass Co., Ltd.) formed by depositing 100 nm of ITO (indium tin oxide) on a glass substrate of 100 mm × 100 mm × 1.1 mm as an anode The substrate was ultrasonically cleaned with isopropyl alcohol, dried with dry nitrogen gas, and subjected to UV ozone cleaning for 5 minutes.

この透明支持基板を市販の真空蒸着装置の基板ホルダーに固定し、一方、モリブデン製抵抗加熱ボートにα−NPDを200mg入れ、別のモリブデン製抵抗加熱ボートにホスト化合物としてH−1を200mg入れ、別のモリブデン製抵抗加熱ボートにBAlqを200mg入れ、別のモリブデン製抵抗加熱ボートに発光ドーパント化合物としてFIr(pic)を100mg入れ、更に別のモリブデン製抵抗加熱ボートにAlqを200mg入れ、真空蒸着装置に取り付けた。 This transparent support substrate was fixed to a substrate holder of a commercially available vacuum deposition apparatus, while 200 mg of α-NPD was put in a molybdenum resistance heating boat, and 200 mg of H-1 as a host compound was put in another molybdenum resistance heating boat, 200 mg of BAlq was put into another resistance heating boat made of molybdenum, 100 mg of FIr (pic) as a luminescent dopant compound was put into another resistance heating boat made of molybdenum, and 200 mg of Alq 3 was put into another resistance heating boat made of molybdenum, and vacuum deposition was performed. Attached to the device.

次いで、真空槽を4×10−4Paまで減圧した後、α−NPDの入った前記加熱ボートに通電して加熱し、蒸着速度0.1nm/秒で透明支持基板に蒸着し、膜厚40nmの正孔輸送層を設けた。 Next, after reducing the vacuum chamber to 4 × 10 −4 Pa, the heating boat containing α-NPD was heated by heating, and deposited on the transparent support substrate at a deposition rate of 0.1 nm / sec. The hole transport layer was provided.

更に、H−1とFIr(pic)の入った前記加熱ボートに通電して加熱し、それぞれ蒸着速度0.2nm/秒、0.012nm/秒で前記正孔輸送層上に共蒸着して、膜厚40nmの発光層を設けた。なお、蒸着時の基板温度は室温であった。   Further, the heating boat containing H-1 and FIr (pic) was energized and heated, and co-deposited on the hole transport layer at a deposition rate of 0.2 nm / second and 0.012 nm / second, respectively. A light emitting layer having a thickness of 40 nm was provided. In addition, the substrate temperature at the time of vapor deposition was room temperature.

更に、BAlqの入った前記加熱ボートに通電して加熱し、蒸着速度0.1nm/秒で前記発光層の上に蒸着して膜厚10nmの正孔阻止層を設けた。   Further, the heating boat containing BAlq was energized and heated, and was deposited on the light emitting layer at a deposition rate of 0.1 nm / second to provide a 10 nm thick hole blocking layer.

その上に、更に、Alqの入った前記加熱ボートに通電して加熱し、蒸着速度0.1nm/秒で前記正孔阻止層の上に蒸着して更に膜厚40nmの電子輸送層を設けた。尚、蒸着時の基板温度は室温であった。 In addition, the heating boat containing Alq 3 is further energized and heated, and deposited on the hole blocking layer at a deposition rate of 0.1 nm / second to further provide an electron transport layer having a thickness of 40 nm. It was. In addition, the substrate temperature at the time of vapor deposition was room temperature.

引き続きフッ化リチウム0.5nm及びアルミニウム110nmを蒸着して陰極を形成し、有機EL素子1−1を作製した。   Then, 0.5 nm of lithium fluoride and 110 nm of aluminum were vapor-deposited, the cathode was formed, and the organic EL element 1-1 was produced.

作製後の各有機EL素子の非発光面をガラスケースで覆い、厚み300μmのガラス基板を封止用基板として用いて、周囲にシール材として、エポキシ系光硬化型接着剤(東亞合成社製ラックストラックLC0629B)を適用し、これを上記陰極上に重ねて前記透明支持基板と密着させ、ガラス基板側からUV光を照射して、硬化させて、封止して、図3、図4に示すような照明装置を形成して評価した。   The non-light-emitting surface of each organic EL element after fabrication is covered with a glass case, a 300 μm thick glass substrate is used as a sealing substrate, and an epoxy photo-curing adhesive (LUX Track LC0629B) is applied, stacked on the cathode and brought into close contact with the transparent support substrate, irradiated with UV light from the glass substrate side, cured and sealed, as shown in FIGS. Such a lighting device was formed and evaluated.

図3は、照明装置の概略図を示し、有機EL素子101は、ガラスカバー102で覆われている(尚、ガラスカバーでの封止作業は、有機EL素子101を大気に接触させることなく窒素雰囲気下のグローブボックス(純度99.999%以上の高純度窒素ガスの雰囲気下)で行った)。   FIG. 3 shows a schematic diagram of the lighting device, in which the organic EL element 101 is covered with a glass cover 102 (note that the sealing operation with the glass cover is performed without bringing the organic EL element 101 into contact with the atmosphere. (It was performed in a glove box under an atmosphere (under an atmosphere of high-purity nitrogen gas having a purity of 99.999% or more)).

図4は、照明装置の断面図を示し、図2において、105は陰極、106は有機EL層、107は透明電極付きガラス基板を示す。尚、ガラスカバー102内には窒素ガス108が充填され、捕水剤109が設けられている。   4 shows a cross-sectional view of the lighting device. In FIG. 2, 105 denotes a cathode, 106 denotes an organic EL layer, and 107 denotes a glass substrate with a transparent electrode. The glass cover 102 is filled with nitrogen gas 108 and a water catching agent 109 is provided.

《有機EL素子1−2〜1−28の作製》
有機EL素子1−1の作製において、表1に記載のように発光ホスト、発光ドーパント材料を変更した以外は同様にして、有機EL素子1−2〜1−28を作製した。
<< Production of Organic EL Elements 1-2 to 1-28 >>
In the production of the organic EL element 1-1, organic EL elements 1-2 to 1-28 were produced in the same manner except that the light emitting host and the light emitting dopant material were changed as shown in Table 1.

《有機EL素子1−2〜1−28の評価》
以下のようにして、作製した有機EL素子1−1〜1−28の評価を行い、その結果を表1に示す。
<< Evaluation of Organic EL Elements 1-2 to 1-28 >>
The produced organic EL elements 1-1 to 1-28 were evaluated as follows, and the results are shown in Table 1.

(外部取りだし量子効率)
作製した有機EL素子について、23℃、乾燥窒素ガス雰囲気下で2.5mA/cm定電流を印加した時の外部取り出し量子効率(%)を測定した。なお測定には同様に分光放射輝度計CS−1000(コニカミノルタセンシング社製)を用いた。
(External extraction quantum efficiency)
About the produced organic EL element, external extraction quantum efficiency (%) when 2.5 mA / cm 2 constant current was applied in a dry nitrogen gas atmosphere at 23 ° C. was measured. For the measurement, a spectral radiance meter CS-1000 (manufactured by Konica Minolta Sensing) was used in the same manner.

表1の外部取りだし量子効率の測定結果は、有機EL素子1−1の測定値を100とした時の相対値で表した。   The measurement results of the external extraction quantum efficiency in Table 1 are expressed as relative values when the measured value of the organic EL element 1-1 is 100.

(半減寿命)
下記に示す測定法に従って、半減寿命の評価を行った。
(Half life)
The half-life was evaluated according to the measurement method shown below.

各有機EL素子を初期輝度1000cd/mを与える電流で定電流駆動して、初期輝度の1/2(500cd/m)になる時間を求め、これを半減寿命の尺度とした。なお、半減寿命は比較の有機EL素子1−1を100とした時の相対値で表示した。 Each organic EL device driven with a constant current at a current giving an initial luminance 1000 cd / m 2, obtains the time to be 1/2 (500cd / m 2) of the initial luminance, which was used as a measure of the half-life. The half life was expressed as a relative value when the comparative organic EL element 1-1 was set to 100.

(初期劣化)
下記に示す測定法に従って、初期劣化の評価を行った。前記半減寿命の測定時に、輝度が90%に到達する時間を測定し、これを初期劣化の尺度とした。
(Initial deterioration)
The initial deterioration was evaluated according to the measurement method shown below. When the half-life was measured, the time required for the luminance to reach 90% was measured and used as a measure of initial deterioration.

なお、初期劣化は比較の有機EL素子1−1を100とした。   The initial deterioration was 100 for the comparative organic EL element 1-1.

初期劣化は以下の計算式を基に計算した。   The initial deterioration was calculated based on the following formula.

初期劣化=(有機EL素子1−1の輝度90%到達時間)/(各素子の輝度90%到達時間)×100
すなわち、初期劣化の値は、小さいほど初期の劣化が小さいことを示す。
Initial deterioration = (luminance 90% arrival time of organic EL element 1-1) / (luminance 90% arrival time of each element) × 100
That is, the smaller the initial deterioration value is, the smaller the initial deterioration is.

(ダークスポット)
各有機EL素子を室温下、2.5mA/cmの定電流条件下による連続点灯を行った際の発光面を目視で下記のようにランク評価した。
(Dark spot)
The ranks of the light emitting surfaces when each organic EL element was continuously lit under a constant current condition of 2.5 mA / cm 2 at room temperature were visually evaluated as follows.

連続点灯時間10時間経過後の各素子を、無作為に抽出した10人による目視評価を行い、
×:ダークスポットを確認した人数が5人以上の場合
△:ダークスポットを確認した人数が1〜4人の場合
○:ダークスポットを確認した人数が0人の場合
とした。
Each element after 10 hours of continuous lighting time has been visually evaluated by 10 people randomly selected,
×: When the number of people who confirmed dark spots was 5 or more Δ: When the number of people confirmed dark spots was 1 to 4 ○: The number of people who confirmed dark spots was 0.

評価結果を表1に示す。   The evaluation results are shown in Table 1.

Figure 0005531446
Figure 0005531446

表1から、比較の素子に比べて、本発明の有機EL素子は、外部取り出し量子効率が高く、且つ、寿命が長く、更には初期劣化を抑えられていることが明らかである。これらは、末端に嵩高いアミノ置換基を有する事で金属錯体同士の相互作用を抑えており、更には、ホール輸送性ユニットであるアミノ基の導入により、発光層内でのキャリアバランスを向上させた効果である。   From Table 1, it is clear that the organic EL device of the present invention has a high external extraction quantum efficiency, a long lifetime, and further suppresses initial deterioration as compared with the comparative device. These have a bulky amino substituent at the end to suppress the interaction between metal complexes, and further, by introducing an amino group which is a hole transporting unit, the carrier balance in the light emitting layer is improved. Effect.

実施例2
《フルカラー表示装置の作製》
(青色発光素子の作製)
実施例1の有機EL素子1−5を青色発光素子として用いた。
Example 2
<Production of full-color display device>
(Production of blue light emitting element)
The organic EL element 1-5 of Example 1 was used as a blue light emitting element.

(緑色発光素子の作製)
実施例1の有機EL素子1−1において、FIr(pic)をIr−1に変更した以外は同様にして、緑色発光素子を作製し、これを緑色発光素子として用いた。
(Production of green light emitting element)
A green light emitting device was produced in the same manner as in the organic EL device 1-1 of Example 1 except that FIr (pic) was changed to Ir-1, and this was used as a green light emitting device.

(赤色発光素子の作製)
実施例1の有機EL素子1−1において、FIr(pic)をIr−9に変更した以外は同様にして、赤色発光素子を作製し、これを赤色発光素子として用いた。
(Production of red light emitting element)
A red light emitting device was produced in the same manner as in the organic EL device 1-1 of Example 1 except that FIr (pic) was changed to Ir-9, and this was used as a red light emitting device.

上記で作製した赤色、緑色、青色発光有機EL素子を同一基板上に並置し、図1に記載のような形態を有するアクティブマトリクス方式フルカラー表示装置を作製した。図2には、作製した前記表示装置の表示部Aの模式図のみを示した。   The red, green, and blue light-emitting organic EL elements produced above were juxtaposed on the same substrate to produce an active matrix type full-color display device having a configuration as shown in FIG. In FIG. 2, only the schematic diagram of the display part A of the produced display device is shown.

即ち、同一基板上に複数の走査線5及びデータ線6を含む配線部と並置した複数の画素3(発光の色が赤領域の画素、緑領域の画素、青領域の画素等)とを有し、配線部の走査線5及び複数のデータ線6はそれぞれ導電材料からなり、走査線5とデータ線6は格子状に直交して、直交する位置で画素3に接続している(詳細は図示せず)。   That is, a plurality of pixels 3 (light emission color is a red region pixel, a green region pixel, a blue region pixel, etc.) juxtaposed with a wiring portion including a plurality of scanning lines 5 and data lines 6 on the same substrate. The scanning lines 5 and the plurality of data lines 6 in the wiring portion are each made of a conductive material, and the scanning lines 5 and the data lines 6 are orthogonal to each other in a lattice shape and are connected to the pixels 3 at the orthogonal positions (for details, see FIG. Not shown).

前記複数画素3は、それぞれの発光色に対応した有機EL素子、アクティブ素子であるスイッチングトランジスタと駆動トランジスタそれぞれが設けられたアクティブマトリクス方式で駆動されており、走査線5から走査信号が印加されるとデータ線6から画像データ信号を受け取り、受け取った画像データに応じて発光する。このように赤、緑、青の画素を適宜、並置することによって、フルカラー表示装置を作製した。   The plurality of pixels 3 are driven by an active matrix system provided with an organic EL element corresponding to each emission color, a switching transistor as an active element, and a driving transistor, and a scanning signal is applied from a scanning line 5. The image data signal is received from the data line 6 and light is emitted according to the received image data. In this way, a full color display device was produced by appropriately juxtaposing red, green, and blue pixels.

このフルカラー表示装置は駆動することにより、輝度が高く、高耐久性を有し、且つ鮮明なフルカラー動画表示が得られることが分かった。   It has been found that when this full-color display device is driven, a high-brightness, high durability, and clear full-color moving image display can be obtained.

実施例3
《白色発光素子及び白色照明装置の作製》
実施例1の透明電極基板の電極を20mm×20mmにパターニングし、その上に実施例1と同様に正孔注入/輸送層としてα−NPDを25nmの厚さで成膜し、更に、H−1の入った前記加熱ボートと例示化合物D−15の入ったボート及びIr−9の入ったボートをそれぞれ独立に通電して、発光ホストであるH−1と発光ドーパントとして例示化合物D−15、及びIr−9の蒸着速度が100:5:0.6になるように調節し、膜厚30nmの厚さになるように蒸着し、発光層を設けた。
Example 3
<< Preparation of white light emitting element and white lighting device >>
The electrode of the transparent electrode substrate of Example 1 was patterned to 20 mm × 20 mm, and α-NPD was formed thereon with a thickness of 25 nm as a hole injection / transport layer in the same manner as in Example 1; The heated boat containing 1 and the boat containing Exemplified Compound D-15 and the boat containing Ir-9 were energized independently, and H-1 as a luminescent host and Exemplified Compound D-15 as a luminescent dopant, In addition, the evaporation rate of Ir-9 was adjusted to be 100: 5: 0.6, vapor deposition was performed so as to have a thickness of 30 nm, and a light emitting layer was provided.

次いで、BAlqを10nm成膜して正孔阻止層を設けた。更に、Alqを40nmで成膜し電子輸送層を設けた。 Next, 10 nm of BAlq was deposited to provide a hole blocking layer. Furthermore, it was deposited Alq 3 at 40nm an electron transporting layer.

次に、実施例1と同様に電子注入層の上にステンレス鋼製の透明電極とほぼ同じ形状の正方形穴あきマスクを設置し、陰極バッファー層としてフッ化リチウム0.5nm及び陰極としてアルミニウム150nmを蒸着、成膜した。   Next, as in Example 1, a square perforated mask having the same shape as the transparent electrode made of stainless steel was placed on the electron injection layer, and lithium fluoride 0.5 nm was used as the cathode buffer layer and aluminum 150 nm was used as the cathode. Vapor deposition and film formation were performed.

この素子を実施例1と同様な方法及び同様な構造の封止缶を具備させ、図3、図4に示すような平面ランプを作製した。この平面ランプに通電したところほぼ白色の光が得られ、照明装置として使用できることが分かった。   This element was provided with a sealing can having the same method and the same structure as in Example 1, and a flat lamp as shown in FIGS. 3 and 4 was produced. When this flat lamp was energized, almost white light was obtained, and it was found that it could be used as a lighting device.

実施例4
《白色発光素子及び白色照明装置の作製−2》
陽極として100mm×100mm×1.1mmのガラス基板上にITO(インジウムチンオキシド)を100nm成膜した基板(NHテクノグラス社製NA−45)にパターニングを行った後、このITO透明電極を設けた透明支持基板をイソプロピルアルコールで超音波洗浄し、乾燥窒素ガスで乾燥し、UVオゾン洗浄を5分間行った。
Example 4
<< Production of White Light Emitting Element and White Lighting Device-2 >>
After patterning on a substrate (NH-Techno Glass NA-45) formed by depositing 100 nm of ITO (indium tin oxide) on a 100 mm × 100 mm × 1.1 mm glass substrate as an anode, this ITO transparent electrode was provided. The transparent support substrate was ultrasonically cleaned with isopropyl alcohol, dried with dry nitrogen gas, and subjected to UV ozone cleaning for 5 minutes.

この透明支持基板上に、ポリ(3,4−エチレンジオキシチオフェン)−ポリスチレンスルホネート(PEDOT/PSS、Bayer社製、Baytron P Al 4083)を純水で70%に希釈した溶液を3000rpm、30秒でスピンコート法により成膜した後、200℃にて1時間乾燥し、膜厚30nmの第1正孔輸送層を設けた。   On this transparent support substrate, a solution obtained by diluting poly (3,4-ethylenedioxythiophene) -polystyrene sulfonate (PEDOT / PSS, Bayer, Baytron P Al 4083) to 70% with pure water at 3000 rpm for 30 seconds. Then, the film was formed by spin coating and then dried at 200 ° C. for 1 hour to provide a first hole transport layer having a thickness of 30 nm.

この基板を窒素雰囲気下に移し、第1正孔輸送層上に、50mgの化合物Dを10mlのトルエンに溶解した溶液を1000rpm、30秒の条件下、スピンコート法により成膜した。180秒間紫外光を照射し、光重合・架橋を行った後、60℃で1時間真空乾燥し第2正孔輸送層(電子阻止層)とした。   This substrate was transferred to a nitrogen atmosphere, and a solution of 50 mg of compound D dissolved in 10 ml of toluene was formed on the first hole transport layer by spin coating at 1000 rpm for 30 seconds. After irradiating with ultraviolet light for 180 seconds to perform photopolymerization / crosslinking, vacuum drying was performed at 60 ° C. for 1 hour to obtain a second hole transport layer (electron blocking layer).

次に、H−5(60mg)、例示化合物D−15(3.0mg)、Ir−9(3.0mg)をトルエン6mlに溶解した溶液を用い、1000rpm、30秒の条件下、スピンコート法により成膜し、発光層を形成した。   Next, using a solution of H-5 (60 mg), Exemplified Compound D-15 (3.0 mg), Ir-9 (3.0 mg) dissolved in 6 ml of toluene, spin coating method under conditions of 1000 rpm and 30 seconds To form a light emitting layer.

続いて、この基板を真空蒸着装置の基板ホルダーに固定し、モリブデン製抵抗加熱ボートにBAlqを200mg入れ、真空蒸着装置に取り付けた。   Subsequently, this substrate was fixed to a substrate holder of a vacuum deposition apparatus, 200 mg of BAlq was put into a molybdenum resistance heating boat, and attached to the vacuum deposition apparatus.

真空槽を4×10−4Paまで減圧した後、BAlqの入った前記加熱ボートに通電して加熱し、蒸着速度0.1nm/秒で前記発光層の上に蒸着して、更に膜厚40nmの電子輸送層を設けた。 The vacuum chamber was depressurized to 4 × 10 −4 Pa, and then heated by energizing the heating boat containing BAlq, and deposited on the light emitting layer at a deposition rate of 0.1 nm / sec. The electron transport layer was provided.

なお、蒸着時の基板温度は室温であった。   In addition, the substrate temperature at the time of vapor deposition was room temperature.

引き続き、フッ化リチウム0.5nm及びアルミニウム110nmを蒸着して陰極を形成し、白色発光有機EL素子を作製した。   Then, 0.5 nm of lithium fluoride and 110 nm of aluminum were vapor-deposited, the cathode was formed, and the white light emitting organic EL element was produced.

この素子に通電したところほぼ白色の光が得られ、照明装置として使用出来ることが判った。   When this element was energized, almost white light was obtained, and it was found that it could be used as a lighting device.

さらに、例示化合物D−15のかわりに例示化合物D−1、D−4、D−9を用い、同様の素子を作成した。   Furthermore, the same element was created using the exemplary compounds D-1, D-4, and D-9 instead of the exemplary compound D-15.

発光材料が重合性基を有している場合は、180秒間紫外光を照射し、光重合・架橋を行った後、60℃で1時間真空乾燥し発光層とした。   In the case where the light emitting material has a polymerizable group, ultraviolet light was irradiated for 180 seconds to perform photopolymerization / crosslinking, and then vacuum dried at 60 ° C. for 1 hour to obtain a light emitting layer.

これらの素子に通電したところほぼ白色の光が得られ、照明装置として使用出来ることが判った。   When these elements were energized, almost white light was obtained, and it was found that they could be used as a lighting device.

実施例5
《白色発光素子及び白色照明装置の作製−3》
陽極として100mm×100mm×1.1mmのガラス基板上にITO(インジウムチンオキシド)を100nm製膜した基板(NHテクノグラス社製NA−45)にパターニングを行った後、このITO透明電極を設けた透明支持基板をイソプロピルアルコールで超音波洗浄し、乾燥窒素ガスで乾燥し、UVオゾン洗浄を5分間行った。
Example 5
<< Preparation of white light emitting element and white illumination device-3 >>
After patterning on a substrate (NA-45 manufactured by NH Techno Glass Co., Ltd.) formed by depositing 100 nm of ITO (indium tin oxide) on a 100 mm × 100 mm × 1.1 mm glass substrate as an anode, this ITO transparent electrode was provided. The transparent support substrate was ultrasonically cleaned with isopropyl alcohol, dried with dry nitrogen gas, and subjected to UV ozone cleaning for 5 minutes.

この透明支持基板上に、ポリ(3,4−エチレンジオキシチオフェン)−ポリスチレンスルホネート(PEDOT/PSS、Bayer社製、Baytron P Al 4083)を純水で70%に希釈した溶液を3000rpm、30秒でスピンコート法により製膜した後、200℃にて1時間乾燥し、膜厚30nmの第1正孔輸送層を設けた。   On this transparent support substrate, a solution obtained by diluting poly (3,4-ethylenedioxythiophene) -polystyrene sulfonate (PEDOT / PSS, Bayer, Baytron P Al 4083) to 70% with pure water at 3000 rpm for 30 seconds. After the film formation by spin coating, the film was dried at 200 ° C. for 1 hour to provide a first hole transport layer having a thickness of 30 nm.

この基板を窒素雰囲気下に移し、第1正孔輸送層上に、50mgの化合物Dを10mlのトルエンに溶解した溶液を1000rpm、30秒の条件下、スピンコート法により製膜した。180秒間紫外光を照射し、光重合・架橋を行った後、60℃で1時間真空乾燥し第2正孔輸送層とした。   This substrate was transferred to a nitrogen atmosphere, and a solution of 50 mg of compound D dissolved in 10 ml of toluene was formed on the first hole transport layer by spin coating at 1000 rpm for 30 seconds. After irradiating with ultraviolet light for 180 seconds to carry out photopolymerization / crosslinking, vacuum drying was performed at 60 ° C. for 1 hour to form a second hole transport layer.

次に、化合物E(60mg)、Ir−14(3.0mg)、例示化合物D−35(3.0mg)をトルエン6mlに溶解した溶液を用い、1000rpm、30秒の条件下、スピンコート法により製膜した。15秒間紫外光を照射し、光重合・架橋を行わせ、さらに真空中150℃で1時間加熱を行い、発光層とした。   Next, a solution obtained by dissolving Compound E (60 mg), Ir-14 (3.0 mg), and Exemplified Compound D-35 (3.0 mg) in 6 ml of toluene was spin-coated under a condition of 1000 rpm and 30 seconds. A film was formed. Irradiated with ultraviolet light for 15 seconds to cause photopolymerization / crosslinking, and further heated in vacuum at 150 ° C. for 1 hour to obtain a light emitting layer.

更に、化合物F(20mg)をトルエン6mlに溶解した溶液を用い、1000rpm、30秒の条件下、スピンコート法により製膜した。15秒間紫外光を照射し、光重合・架橋を行わせ、さらに真空中80℃で1時間加熱を行い、正孔阻止層とした。   Furthermore, a film in which compound F (20 mg) was dissolved in 6 ml of toluene was used to form a film by spin coating under conditions of 1000 rpm and 30 seconds. Ultraviolet light was irradiated for 15 seconds, photopolymerization / crosslinking was performed, and further heating was performed in vacuum at 80 ° C. for 1 hour to form a hole blocking layer.

続いて、この基板を真空蒸着装置の基板ホルダーに固定し、モリブデン製抵抗加熱ボートにAlqを200mg入れ、真空蒸着装置に取り付けた。真空槽を4×10−4Paまで減圧した後、Alqの入った前記加熱ボートに通電して加熱し、蒸着速度0.1nm/秒で前記正孔阻止層の上に蒸着して、更に膜厚40nmの電子輸送層を設けた。 Subsequently, this substrate was fixed to a substrate holder of a vacuum vapor deposition apparatus, and 200 mg of Alq 3 was put into a molybdenum resistance heating boat and attached to the vacuum vapor deposition apparatus. After depressurizing the vacuum chamber to 4 × 10 −4 Pa, energizing and heating the heating boat containing Alq 3 , depositing on the hole blocking layer at a deposition rate of 0.1 nm / second, An electron transport layer having a thickness of 40 nm was provided.

なお、蒸着時の基板温度は室温であった。   In addition, the substrate temperature at the time of vapor deposition was room temperature.

引き続き、フッ化リチウム0.5nm及びアルミニウム110nmを蒸着して陰極を形成し、白色発光有機EL素子を作製した。   Then, 0.5 nm of lithium fluoride and 110 nm of aluminum were vapor-deposited, the cathode was formed, and the white light emitting organic EL element was produced.

この素子に通電したところほぼ白色の光が得られ、照明装置として使用出来ることが判った。   When this element was energized, almost white light was obtained, and it was found that it could be used as a lighting device.

1 ディスプレイ
3 画素
5 走査線
6 データ線
A 表示部
B 制御部
107 透明電極付きガラス基板
106 有機EL層
105 陰極
102 ガラスカバー
108 窒素ガス
109 捕水剤
DESCRIPTION OF SYMBOLS 1 Display 3 Pixel 5 Scanning line 6 Data line A Display part B Control part 107 Glass substrate with a transparent electrode 106 Organic EL layer 105 Cathode 102 Glass cover 108 Nitrogen gas 109 Water catching agent

Claims (15)

陽極と陰極により挟まれた少なくとも1層の発光層を有する有機エレクトロルミネッセンス素子において、
該発光層が、下記一般式(1)または一般式(3)で表される部分構造を含む化合物を少なくとも1つ含有する有機層を有することを特徴とする有機エレクトロルミネッセンス素子。
Figure 0005531446
〔〔式中、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1a〜E1qで構成される骨格は合計で18π電子を有する。E1aとE1pは各々異なり、炭素原子または窒素原子を表す。 1a 〜E 1e により形成される環はイミダゾール環またはピラゾール環を表す。1a〜R1iは各々、水素原子または置換基を表すが、R1a〜R1iのうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、一般式(1)中、置換基R1bが下記一般式(X)で表される場合を除く。〕
Figure 0005531446
〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または、芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
Figure 0005531446
(式中、RおよびRは、水素、アルキル、およびアリールからなる群から独立に選択され;
およびRの少なくとも1つは、4個以上の原子を有するアルキルであり;
は、モノ-、ジ-、トリ-、またはテトラ置換基を表し;かつ、
は、水素、アルキル、およびアリールからなる群から独立に選択される。)
In an organic electroluminescence device having at least one light emitting layer sandwiched between an anode and a cathode,
The light emitting layer has an organic layer containing at least one compound containing a partial structure represented by the following general formula (1) or general formula (3).
Figure 0005531446
[In the formula, E 1a to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, and the skeleton composed of E 1a to E 1q has a total of 18π electrons. E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom. The ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring. R 1a to R 1i each represents a hydrogen atom or a substituent, and at least one of R 1a to R 1i represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the general formula (1), the case where the substituent R 1b is represented by the following general formula (X) is excluded. ]
Figure 0005531446
[Wherein L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb form a ring. Not . n is 1. ]]
Figure 0005531446
Wherein R 1 and R 2 are independently selected from the group consisting of hydrogen, alkyl, and aryl;
At least one of R 1 and R 2 is an alkyl having 4 or more atoms;
R 3 represents a mono-, di-, tri-, or tetra substituent; and
R 3 is independently selected from the group consisting of hydrogen, alkyl, and aryl. )
前記一般式(A)におけるRNa及びRNbが、共にアルキル基を表すことを特徴とする請求項1に記載の有機エレクトロルミネッセンス素子。 2. The organic electroluminescence device according to claim 1, wherein RNa and RNb in the general formula (A) both represent an alkyl group. 前記一般式(A)におけるRNa及びRNbが、共に芳香族炭化水素環基を表すことを特徴とする請求項1または2に記載の有機エレクトロルミネッセンス素子。 RNa and RNb in Formula (A) The organic electroluminescent device according to claim 1 or 2, characterized in that both represent aromatic hydrocarbon ring group. 前記一般式(1)または一般式(3)で表される部分構造が、下記一般式(5)または一般式(7)で表されることを特徴とする請求項1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。
Figure 0005531446
〔〔式中、E1a〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1a〜E1eにより形成される環はイミダゾール環またはピラゾール環を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。E1aとE1pは各々異なり、炭素原子または窒素原子を表す。R1a〜R1i、R51〜R54及びR61〜R63は各々、水素原子または置換基を表すが、R1a〜R1i、R51〜R54、R61〜R63のうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、一般式(5)中、置換基R1bが前記一般式(X)で表される場合を除く。〕
Figure 0005531446
〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
Partial structure represented by the general formula (1) or the general formula (3) is any one of claims 1-3, characterized by being represented by the following general formula (5) or the general formula (7) The organic electroluminescent element of the item.
Figure 0005531446
[In the formula, E 1a to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1a to E 1e represents an imidazole ring or a pyrazole ring , and E 1f to E The ring formed by 1k represents a 5-membered aromatic heterocyclic ring, and the ring formed by E 11 to E 1q represents a 6-membered aromatic hydrocarbon ring or a 6-membered aromatic heterocyclic ring. E 1a and E 1p are different from each other and represent a carbon atom or a nitrogen atom. R 1a to R 1i , R 51 to R 54 and R 61 to R 63 each represent a hydrogen atom or a substituent, and at least one of R 1a to R 1i , R 51 to R 54 , and R 61 to R 63 Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the general formula (5), the case where the substituent R 1b is represented by the general formula (X) is excluded. ]
Figure 0005531446
[Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ]]
前記一般式(5)または一般式(7)で表される部分構造が、下記一般式(8)または一般式(10)で表されることを特徴とする請求項に記載の有機エレクトロルミネッセンス素子。
Figure 0005531446
〔〔式中、E1f〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。R1c〜R1i、R51〜R56及びR61〜R65は各々、水素原子または置換基を表すが、R1c〜R1i、R51〜R56、R61〜R65のうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、式中、置換基R55が前記一般式(X)で表される場合を除く。〕
Figure 0005531446
〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
The organic electroluminescence according to claim 4 , wherein the partial structure represented by the general formula (5) or the general formula (7) is represented by the following general formula (8) or the general formula (10). element.
Figure 0005531446
[In the formula, E 1f to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1f to E 1k represents a 5-membered aromatic heterocycle, and E 1l The ring formed by -E1q represents a 6-membered aromatic hydrocarbon ring or a 6-membered aromatic heterocycle. R 1c to R 1i , R 51 to R 56 and R 61 to R 65 each represent a hydrogen atom or a substituent, and at least one of R 1c to R 1i , R 51 to R 56 , and R 61 to R 65 Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the formula, the case where the substituent R 55 is represented by the general formula (X) is excluded. ]
Figure 0005531446
[Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ]]
前記一般式(5)または一般式(7)で表される部分構造が、下記一般式(11)または一般式(13)で表されることを特徴とする請求項に記載の有機エレクトロルミネッセンス素子。
Figure 0005531446
〔〔式中、E1f〜E1qは各々、炭素原子、窒素原子、酸素原子または硫黄原子を表し、E1f〜E1kにより形成される環は5員の芳香族複素環を表し、E1l〜E1qにより形成される環は、6員の芳香族炭化水素環または6員の芳香族複素環を表す。R1c〜R1i、R51〜R56及びR61〜R65は各々、水素原子または置換基を表すが、R1c〜R1i、R51〜R56、R61〜R65のうち少なくとも1つは下記一般式(A)で表される置換基を表す。Mは元素周期表における8族〜10族の遷移金属原子を表す。但し、式中、置換基R55が前記一般式(X)で表される場合を除く。〕
Figure 0005531446
〔式中、Lは連結基を表し、RNa及びRNbは各々、水素原子、アルキル基、芳香族炭化水素基または芳香族複素環基を表し、RNaとRNbとが環を形成することはない。nは1である。〕〕
The organic electroluminescence according to claim 4 , wherein the partial structure represented by the general formula (5) or the general formula (7) is represented by the following general formula (11) or the general formula (13). element.
Figure 0005531446
[In the formula, E 1f to E 1q each represent a carbon atom, a nitrogen atom, an oxygen atom or a sulfur atom, the ring formed by E 1f to E 1k represents a 5-membered aromatic heterocycle, and E 1l The ring formed by -E1q represents a 6-membered aromatic hydrocarbon ring or a 6-membered aromatic heterocycle. R 1c to R 1i , R 51 to R 56 and R 61 to R 65 each represent a hydrogen atom or a substituent, and at least one of R 1c to R 1i , R 51 to R 56 , and R 61 to R 65 Represents a substituent represented by the following general formula (A). M represents a group 8-10 transition metal atom in the periodic table. However, in the formula, the case where the substituent R 55 is represented by the general formula (X) is excluded. ]
Figure 0005531446
[Wherein, L 1 represents a linking group, RNa and RNb each represent a hydrogen atom, an alkyl group, an aromatic hydrocarbon group or an aromatic heterocyclic group, and RNa and RNb do not form a ring. . n is 1. ]]
前記一般式(A)におけるLが、「アルキル基、芳香族炭化水素環基または複素環基から導かれる2価以上の基」、−O−、−S−または−NRz−、或いは、これらの基を組み合わせてなる連結基(但し、−NRz−中、Rzは水素原子、アルキル基、芳香族炭化水素環基、複素環基を表す。)を表すことを特徴とする請求項1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。 L 1 in the general formula (A) is “a divalent or higher valent group derived from an alkyl group, an aromatic hydrocarbon ring group or a heterocyclic group”, —O—, —S— or —NRz—, or these comprising a combination of group linking group (provided that, -NRz- in, Rz represents. hydrogen atom, an alkyl group, an aromatic hydrocarbon ring group, a heterocyclic group) 1 to claim, characterized in that representing the 6 Organic electroluminescent element as described in any one of these. 前記一般式(A)におけるLが、アルキル基または芳香族炭化水素環基、または、これらの基を組み合わせてなる連結基を表すことを特徴とする請求項に記載の有機エレクトロルミネッセンス素子。 The organic electroluminescence device according to claim 7 , wherein L 1 in the general formula (A) represents an alkyl group, an aromatic hydrocarbon ring group, or a linking group obtained by combining these groups. 前記一般式(A)におけるLが、アルキル基を表すことを特徴とする請求項に記載の有機エレクトロルミネッセンス素子。 Wherein L 1 in the general formula (A) An organic electroluminescence device according to claim 8, characterized in that an alkyl group. 前記有機層が前記一般式(1)、(3)、(5)、(7)、(8)、(10)、(11)または(13)のいずれか1つで表される部分構造を含む化合物を少なくとも1種含有し、該有機層がウェットプロセスを用いて形成されたことを特徴とする請求項1〜のいずれか一項に記載の有機エレクトロルミネッセンス素子。 The organic layer has a partial structure represented by any one of the general formulas (1), (3), (5), (7), (8), (10), (11) or (13). The organic electroluminescence device according to any one of claims 1 to 9 , wherein the organic layer contains at least one kind of compound, and the organic layer is formed using a wet process. 前記Mが白金またはイリジウムであることを特徴とする請求項1〜10のいずれか一項に記載の有機エレクトロルミネッセンス素子。 The organic electroluminescent device according to any one of claims 1 to 10, wherein M is platinum or iridium. 請求項1に記載の一般式(1)または(3)で表される部分構造を含む化合物、請求項に記載の一般式(5)または(7)で表される部分構造を含む化合物、請求項に記載の一般式(8)または(10)で表される部分構造を含む化合物、若しくは、請求項に記載の一般式(11)または(13)で表される部分構造を含む化合物、を含有することを特徴とする有機エレクトロルミネッセンス素子材料。 A compound comprising a partial structure represented by the general formula (1) or (3) according to claim 1, a compound comprising a partial structure represented by the general formula (5) or (7) according to claim 4 , The compound containing the partial structure represented by General formula (8) or (10) of Claim 5 or the partial structure represented by General formula (11) or (13) of Claim 6 is included. An organic electroluminescent element material comprising a compound. 請求項1に記載の一般式(1)または(3)で表される部分構造を含む化合物、請求項に記載の一般式(5)または(7)で表される部分構造を含む化合物、請求項に記載の一般式(8)または(10)で表される部分構造を含む化合物、あるいは、請求項に記載の一般式(11)または(13)で表される部分構造を含む化合物、において、Mが、白金またはイリジウムであることを特徴とする請求項12に記載の有機エレクトロルミネッセンス素子材料。 A compound comprising a partial structure represented by the general formula (1) or (3) according to claim 1, a compound comprising a partial structure represented by the general formula (5) or (7) according to claim 4 , The compound containing the partial structure represented by General formula (8) or (10) of Claim 5 or the partial structure represented by General formula (11) or (13) of Claim 6 is included. In the compound, M is platinum or iridium, The organic electroluminescent element material according to claim 12 , wherein M is platinum or iridium. 請求項1〜11のいずれか一項に記載の有機エレクトロルミネッセンス素子を備えたことを特徴とする表示装置。 A display device comprising the organic electroluminescence element according to any one of claims 1 to 11 . 請求項1〜11のいずれか一項に記載の有機エレクトロルミネッセンス素子を備えたことを特徴とする照明装置。 Lighting apparatus comprising the organic electroluminescent device according to any one of claims 1 to 11.
JP2009101736A 2009-04-20 2009-04-20 ORGANIC ELECTROLUMINESCENT ELEMENT, ORGANIC ELECTROLUMINESCENT ELEMENT MATERIAL, DISPLAY DEVICE AND LIGHTING DEVICE Active JP5531446B2 (en)