JP5454350B2 - Pneumatic tire - Google Patents
Pneumatic tire Download PDFInfo
- Publication number
- JP5454350B2 JP5454350B2 JP2010110970A JP2010110970A JP5454350B2 JP 5454350 B2 JP5454350 B2 JP 5454350B2 JP 2010110970 A JP2010110970 A JP 2010110970A JP 2010110970 A JP2010110970 A JP 2010110970A JP 5454350 B2 JP5454350 B2 JP 5454350B2
- Authority
- JP
- Japan
- Prior art keywords
- bead core
- bead
- pneumatic tire
- rubber
- thermoplastic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、ビードワイヤを巻き重ねてビードコアを構成した空気入りタイヤにおいて、成形・加硫時のビードの層崩れを抑制することにより、ビードコアの成形精度(特にタイヤ回転軸方向に見たビードコアの真円度)を高めてユニフォーミティを改善し、また、ビードコアの耐久性(ワイヤなどの耐セパレーション性)に優れた空気入りタイヤに関する。 In a pneumatic tire in which a bead core is formed by winding bead wires, the present invention suppresses bead layer collapse during molding and vulcanization, thereby reducing the bead core molding accuracy (particularly the trueness of the bead core viewed in the tire rotation axis direction). The present invention relates to a pneumatic tire that improves uniformity by improving the circularity, and also has excellent bead core durability (separation resistance such as wires).
空気入りタイヤのビード部には、スチールワイヤを連続的に巻回して成形された環状のビードコアが形成されている。 An annular bead core formed by continuously winding a steel wire is formed on the bead portion of the pneumatic tire.
このビードコアは、通常、スチールワイヤを横一列に複数本並べたものをゴムで被覆し、これを連続的に円環状に巻き取って構成されるか(所謂「層巻き」方式)、あるいは1本のスチールワイヤをゴムで被覆し、これを連続的に円環状に巻き取って構成されている(所謂「1本巻き」方式)。 This bead core is usually configured by covering a plurality of steel wires arranged in a horizontal row with rubber and winding them continuously in an annular shape (so-called “layer winding” method), or one The steel wire is covered with rubber and continuously wound into an annular shape (so-called “one-winding” method).
このようなビードコアを有する空気入りタイヤの製造をする場合、いずれの方式であっても、成形・加硫時にワイヤ束中の個々のワイヤにはばらけようとする力が働く。すなわち、しっかりと全体にまとまって均斉にワイヤ束を形成しようとする力が働くことはほとんど無く、特にワイヤの端末付近では、始端、終端ともに束から浮き上がろうとする挙動を示す。 When a pneumatic tire having such a bead core is manufactured, a force is applied to the individual wires in the wire bundle during molding and vulcanization, regardless of which method is used. That is, there is almost no force for forming a wire bundle firmly and evenly on the whole, and in particular near the end of the wire, both the starting end and the terminal end show a behavior of floating from the bundle.
こうした状況により、成形・加硫時にビードコアを構成するワイヤに乱れやずれが生じると、空気入りタイヤ中でのビードコアの成形精度(ビードコアの真円度)が悪化することになり、それが製造されたタイヤのユニフォーミティにも影響を与え、さらに、操縦安定性、乗り心地やロードノイズ騒音などにも影響を及ぼす。 Under these circumstances, if the wire constituting the bead core is disturbed or displaced during molding and vulcanization, the bead core molding accuracy in the pneumatic tire (the roundness of the bead core) will deteriorate, and it will be manufactured. This also affects the uniformity of tires, and also affects driving stability, ride comfort and road noise.
このような点に鑑み、全体の軽量化を図りながら、ビードコアを構成するワイヤを強固に結束してユニフォーミティを向上することを目的として、ビードコアの周囲にヤング率が50MPa以上の熱可塑性樹脂または熱可塑性エラストマー組成物からなる被覆層を設けるという提案(特許文献1)、あるいは、ビードワイヤの変形を防止することを目的に、200℃以上の融点を有しかつ特定の伸びと伸張切断特性を有する熱可塑性材料で
ビードコアを被覆するという提案(特許文献2)がされている。
In view of these points, a thermoplastic resin having a Young's modulus of 50 MPa or more around the bead core for the purpose of improving the uniformity by firmly binding the wires constituting the bead core while reducing the overall weight. Proposal of providing a coating layer made of a thermoplastic elastomer composition (Patent Document 1), or having a melting point of 200 ° C. or more and specific elongation and stretch cutting properties for the purpose of preventing deformation of the bead wire There has been a proposal (Patent Document 2) that a bead core is coated with a thermoplastic material.
しかし、これらの提案のものはビードコアを硬く被覆することによってワイヤのばらけを抑制する作用はあっても、熱可塑性材料の被覆層とカーカス層との間で剛性の差が大きいものとなるので、以下のような問題を招くことがあった。 However, even though these proposals have the effect of suppressing the dispersion of the wire by covering the bead core hard, there is a large difference in rigidity between the coating layer of the thermoplastic material and the carcass layer. The following problems may be caused.
すなわち、タイヤ成形後にビードコアとカーカス層との間でのセパレーション(剥離)発生の問題が生じたり、あるいは、成形・加硫時においてビード部近くのカーカス層の部分がビードコアに対し不均斉かつランダムに滑るような挙動を局部的に示す場合があり、これが成形精度を損なう要因となり、所望通りのユニフォーミティを有するタイヤを成形することができない場合がある等の問題を招くことがあった。 That is, there is a problem of separation (peeling) between the bead core and the carcass layer after the molding of the tire, or the portion of the carcass layer near the bead portion is unevenly and randomly with respect to the bead core during molding and vulcanization. In some cases, the slipping behavior is locally shown, which is a factor that impairs the molding accuracy and may cause a problem that a tire having the desired uniformity may not be molded.
本発明の目的は、上述したような点に鑑み、ワイヤを巻き重ねてビードコアを構成した空気入りタイヤにおいて、成形・加硫時のビードの層崩れを抑制することにより、ビードコアの成形精度(特にタイヤ回転軸方向に見た、ビードコアの真円度)を高めて優れたユニフォーミティを有するとともに、ビードコアの耐久性(ワイヤなどの耐セパレーション性)に優れた空気入りタイヤを提供することにある。 In view of the above-described points, an object of the present invention is to reduce the bead layer collapse during molding and vulcanization in a pneumatic tire in which a bead core is formed by winding a wire. An object of the present invention is to provide a pneumatic tire that has an excellent uniformity by increasing the roundness of the bead core as viewed in the tire rotation axis direction, and is excellent in the durability of the bead core (separation resistance of a wire or the like).
上記した目的を達成する本発明の空気入りタイヤは、以下の(1)の構成を有する。 The pneumatic tire of the present invention that achieves the above object has the following configuration (1).
(1)ビードワイヤが巻き重ねられて形成されたビードコアと、左右の該ビードコアに装架されたカーカス層を有する空気入りタイヤにおいて、該ビードコアは前記ビードワイヤを融点が200℃以上の熱可塑性樹脂中に埋設して構成され、かつ該ビードコアと前記カーカス層の間に、熱可塑性樹脂中にゴムを分散混合させた熱可塑性エラストマーからなるビードコアカバー層を配設したことを特徴とする空気入りタイヤ。 (1) In a pneumatic tire having a bead core formed by winding bead wires and a carcass layer mounted on the left and right bead cores, the bead core is placed in a thermoplastic resin having a melting point of 200 ° C. or more. A pneumatic tire characterized in that a bead core cover layer made of a thermoplastic elastomer in which rubber is dispersed and mixed in a thermoplastic resin is disposed between the bead core and the carcass layer.
また、かかる本発明の空気入りタイヤにおいて、下記(2)〜(6)のいずれかの構成を有することが好ましい。 In addition, the pneumatic tire of the present invention preferably has any one of the following configurations (2) to (6).
(2)前記熱可塑性エラストマーを構成する熱可塑性樹脂が、前記ビードワイヤを埋設している融点が200℃以上の熱可塑性樹脂と同一のものであることを特徴とする上記(1)記載の空気入りタイヤ。
(3)前記熱可塑性エラストマーを構成するゴムが、硫黄架橋可能なジエン系ポリマーからなることを特徴とする請求項1または2記載の空気入りタイヤ。
(4)前記ビードコアが、1本のビードワイヤを螺旋状に巻き回して積層させて構成されたものであり、かつ、該ビードコアの横断面形状が略6角形のものであることを特徴とする上記(1)〜(3)のいずれかに記載の空気入りタイヤ。
(5)前記熱可塑性エラストマーからなるビードコアカバー層を、ビードコアの外周面のうち、カーカス層に面した面にだけ隣接させて設設したことを特徴とする上記(1)〜(4)のいずれかに記載の空気入りタイヤ。
(6)前記熱可塑性エラストマーからなるビードコアカバー層の厚さが0.5〜2mmであることを特徴とする上記(1)〜(5)のいずれかに記載の空気入りタイヤ。
(2) The pneumatic according to the above (1), wherein the thermoplastic resin constituting the thermoplastic elastomer is the same as the thermoplastic resin having a melting point in which the bead wire is embedded at 200 ° C. or higher. tire.
(3) The pneumatic tire according to claim 1 or 2, wherein the rubber constituting the thermoplastic elastomer comprises a diene polymer capable of sulfur crosslinking.
(4) The bead core is configured by laminating and laminating one bead wire in a spiral shape, and the bead core has a substantially hexagonal cross-sectional shape. The pneumatic tire according to any one of (1) to (3).
(5) Any of the above (1) to (4), wherein the bead core cover layer made of the thermoplastic elastomer is provided adjacent to only the surface facing the carcass layer among the outer peripheral surfaces of the bead core. The pneumatic tire according to Crab.
(6) The pneumatic tire according to any one of (1) to (5) above, wherein the bead core cover layer made of the thermoplastic elastomer has a thickness of 0.5 to 2 mm.
請求項1にかかる本発明によれば、ビードワイヤを、融点が200℃以上の熱可塑性樹脂、すなわち、加硫温度よりも高い融点である熱可塑性樹脂中に埋設することにより、成形・加硫時のワイヤの乱れが抑制されてユニフォーミティに優れた空気入りタイヤを製造することができ、さらに、ビードコアとカーカス層の間に、熱可塑性樹脂中にゴムを分散混合させた熱可塑性エラストマーからなるビードコアカバー層を配設したことにより、ビードワイヤ(ビードコア)とカーカスコード間の剛性の段差(傾斜)が緩やかに適正化されることにより、耐久性が改善されて耐セパレーション性にも優れたものととなり、また、加硫時にカーカス層付近のビード部が適度かつ均斉な滑りをすることができることとなり、不均斉な滑りの発生がなくなり、ビードコアの成形精度(特に真円度)が高くタイヤのユニフォーミティに優れたものとなる。 According to the first aspect of the present invention, the bead wire is embedded in a thermoplastic resin having a melting point of 200 ° C. or higher, that is, a thermoplastic resin having a melting point higher than the vulcanization temperature. The bead core is made of a thermoplastic elastomer in which rubber is dispersed and mixed in a thermoplastic resin between the bead core and the carcass layer. By arranging the cover layer, the rigidity step (inclination) between the bead wire (bead core) and the carcass cord is moderately optimized, and the durability is improved and the separation resistance is excellent. In addition, the bead portion in the vicinity of the carcass layer can slip moderately and evenly during vulcanization, and there is no occurrence of uneven slipping. Ri, and that the molding accuracy of the bead core (especially roundness) and excellent uniformity of the higher tire.
特に、請求項2にかかる本発明によれば、上述した請求項1の発明の効果を有するとともに、熱可塑性エラストマーのビードカバー層を構成する熱可塑性樹脂がビードワイヤを埋設している融点200℃以上の熱可塑性樹脂と同一のものであるので、ビードコアとビードカバー層の接着性が良好になり、耐久性の点でいっそう優れた空気入りタイヤを実現できる。 In particular, according to the present invention according to claim 2, while having the effect of the invention of claim 1 described above, the thermoplastic resin constituting the bead cover layer of the thermoplastic elastomer has a melting point of 200 ° C. or higher where the bead wire is embedded. Since this is the same as the above thermoplastic resin, the adhesiveness between the bead core and the bead cover layer is improved, and a pneumatic tire more excellent in terms of durability can be realized.
請求項3にかかる本発明によれば、上述した請求項1の発明の効果を有するとともに、前記熱可塑性エラストマーを構成するゴムが硫黄架橋可能なジエン系ポリマーからなるので、ビードコアとビードカバー層の接着性が良好になり、耐久性の点でいっそう優れた空気入りタイヤを実現できる。 According to the third aspect of the present invention, since the rubber constituting the thermoplastic elastomer is composed of a sulfur-crosslinkable diene polymer, the bead core and the bead cover layer have the effects of the first aspect. Adhesiveness is improved, and a pneumatic tire that is superior in terms of durability can be realized.
請求項4にかかる本発明によれば、特にバス・トラック用などで、ビードコアが6角形の断面形状を有していて、加硫時に、特に、ビード部近くのカーカス層の部分がビードコアに対し不均斉かつランダムに滑るような挙動を局部的に強くする傾向が強い場合でも、加硫時にカーカス層付近のビード部が適度かつ均斉な滑りをすることができることになるので、不均斉かつランダムな滑りの発生がなくなり、ビードコアの成形精度(特に真円度)が高くタイヤのユニフォーミティに優れた空気入りタイヤを実現することができる。 According to the fourth aspect of the present invention, particularly for buses and trucks, the bead core has a hexagonal cross-sectional shape, and at the time of vulcanization, the portion of the carcass layer particularly near the bead portion is in relation to the bead core. Even when there is a strong tendency to locally increase the behavior of uneven and random sliding, the bead portion near the carcass layer can be moderately and uniformly slipped during vulcanization, so that the uneven and random It is possible to realize a pneumatic tire with no slippage and high bead core molding accuracy (particularly roundness) and excellent tire uniformity.
請求項5にかかる本発明によれば、上述した請求項1の発明の効果を有するとともに、ビードコアカバー層を効果が高い箇所のみに設けたことによりコストの点で優れた空気入りタイヤを実現することができる。 According to the fifth aspect of the present invention, a pneumatic tire having the effects of the first aspect of the invention described above and having a bead core cover layer only in a highly effective portion is realized in terms of cost. be able to.
請求項6にかかる本発明によれば、上述した各請求項の効果をより明確に発揮する空気入りタイヤを実現することができる。 According to the sixth aspect of the present invention, it is possible to realize a pneumatic tire that more clearly exhibits the effects of the above-described claims.
以下、図面などを用いて、更に詳しく本発明の空気入りタイヤについて、説明する。 Hereinafter, the pneumatic tire of the present invention will be described in more detail with reference to the drawings.
本発明の空気入りタイヤは、ビードワイヤが巻き重ねられて形成されたビードコアと、左右の該ビードコアに装架されたカーカス層を有する空気入りタイヤにおいて、ビードコアは、ビードワイヤを融点200℃以上の熱可塑性樹脂中に埋設して構成されていて、かつ該ビードコアとカーカス層の間に、熱可塑性樹脂中にゴムを分散混合させた熱可塑性エラストマーからなるビードコアカバー層を配設したことを特徴とする。 The pneumatic tire of the present invention is a pneumatic tire having a bead core formed by winding bead wires and a carcass layer mounted on the left and right bead cores. The bead core is made of thermoplastic resin having a melting point of 200 ° C. or higher. A bead core cover layer made of a thermoplastic elastomer in which rubber is dispersed and mixed in a thermoplastic resin is disposed between the bead core and the carcass layer.
図1において、1はトレッド部、2はサイドウォール部、3はビード部である。左右一対のビード部3間にはカーカス層4が装架され、このカーカス層4の端部がビードコア5の廻りにタイヤ内側から外側に折り返されている。トレッド部1におけるカーカス層4の外周側にはベルト層6がタイヤ全周にわたって配置されている。
In FIG. 1, 1 is a tread portion, 2 is a sidewall portion, and 3 is a bead portion. A
図2は、図1の空気入りタイヤのビード部3付近を拡大して示した断面図であり、ビードコア5は、スチールワイヤ7と融点200℃以上の熱可塑性樹脂8とから構成され、該スチールワイヤ7は該融点200℃以上の熱可塑性樹脂6に埋設されているものである。該ビードコア5とカーカス層4の間には、熱可塑性樹脂中にゴムを分散混合させた熱可塑性エラストマーからなるビードコアカバー層9が配設されている。
2 is an enlarged cross-sectional view showing the vicinity of the
かかる構成としたことにより、ビードワイヤ7を加硫温度よりも高い温度の融点(200℃以上)を有する熱可塑性樹脂中に埋設していることにより、成形・加硫時においても、ビードワイヤ7の乱れは抑制されて、ユニフォーミティ上好ましい成形が可能となる。
By adopting such a configuration, the
一方で、それだけでは、ビードワイヤ7の埋設樹脂が、一般的な埋設材料であるインシュレーションゴム等と比較すると剛性が非常に高いものであるため、ビード部における「ビードワイヤ7/その埋設樹脂8/カーカスコートゴム10/カーカスコード11」という複合構造でみると、材料剛性の段差が大きくなって、これがビード部近くのカーカス層の部分がビードコアに対し不均斉かつランダムに滑るような挙動を局部的に示す要因となるおそれがある。
On the other hand, since the embedded resin of the
そこで、本発明では、図2に示したように、ビードコア5とカーカス層4の間に、熱可塑性樹脂中にゴムを分散混合させた熱可塑性エラストマーからなるビードコアカバー層9を配設したものである。すなわち、本発明では、「ビードワイヤ7/その埋設樹脂8/ビードコアカバー層9/カーカスコートゴム10/カーカスコード11」との複合構造が形成されている。
Therefore, in the present invention, as shown in FIG. 2, a bead
このビードコアカバー層9は、前述した熱可塑性樹脂8とカーカス層4(コートゴム)の間に介在して、それらの剛性差からくる問題をやわらげる緩衝層あるいはクッション層というべき役割を果たす。具体的には、成形・加硫時において、それらがスムーズな相対的動きをすることを可能にして、ビード部に大きな力が作用しても局部的なすべりやずれ等を生ずることなく、ビードコアの成形精度(特に真円度)が高くユニフォーミティに優れたタイヤの成形を実現させるものとなる。
The bead
上述した効果を良好に発揮させるために、ビードコアカバー層の厚さは好ましくは0.5〜2mmである。 In order to exhibit the above-described effects satisfactorily, the thickness of the bead core cover layer is preferably 0.5 to 2 mm.
本発明においてビードワイヤを埋設する樹脂として使用される融点200℃以上の熱可塑性樹脂としては、特に限定されるものではないが、ナイロン6(融点225℃)、ナイロン66(融点267℃)、ポリエチレンテレフタレート(融点260℃)などを使用することができる。 The thermoplastic resin having a melting point of 200 ° C. or higher used as a resin for embedding a bead wire in the present invention is not particularly limited, but nylon 6 (melting point 225 ° C.), nylon 66 (melting point 267 ° C.), polyethylene terephthalate (Melting point 260 ° C.) or the like can be used.
また、ビードコアカバー層をなす熱可塑性エラストマーを構成する熱可塑性樹脂は、ビードワイヤを埋設している融点200℃以上の熱可塑性樹脂と同一のものであることが好ましい。このように構成すると、カバー層とビードコアの接着性が改善されて、耐久性により優れたものとなる。 The thermoplastic resin constituting the thermoplastic elastomer constituting the bead core cover layer is preferably the same as the thermoplastic resin having a melting point of 200 ° C. or higher in which the bead wire is embedded. If comprised in this way, the adhesiveness of a cover layer and a bead core will be improved, and it will become the thing excellent by durability.
また、熱可塑性エラストマーを構成するゴムは、硫黄架橋可能なジエン系ポリマーからなることが好ましく、このように構成すると、ビードコアカバー層とビードコアの接着性がより強くなり、耐久性により優れたものとなる。 The rubber constituting the thermoplastic elastomer is preferably composed of a sulfur-crosslinkable diene-based polymer. When configured in this manner, the adhesion between the bead core cover layer and the bead core is stronger and the durability is more excellent. Become.
また、本発明において、ビードコアが、1本のビードワイヤを螺旋状に巻き回して積層させて構成されたものであり、かつ、ビードコアの横断面形状が略6角形のものであることが好ましい。本発明の空気入りタイヤは、製造する際にビード部の変形が大きい、トラック・バス用タイヤの製造にあたってより効果的だからであり、したがって、ビードコアの横断面形状が略6角形のものに効果が大きい。 Moreover, in this invention, it is preferable that a bead core is comprised by winding and laminating | stacking one bead wire spirally, and the cross-sectional shape of a bead core is a thing of a substantially hexagon. This is because the pneumatic tire of the present invention is more effective in manufacturing tires for trucks and buses in which the deformation of the bead portion is large in manufacturing, and therefore the effect is effective when the bead core has a substantially hexagonal cross-sectional shape. large.
また、ビードコアの外周面のうち、カーカス層に面した面にだけ該面に隣接させて熱可塑性エラストマーからなるビードコアカバー層を設設することが好ましい。ビードフィラーとビードコアの間に設けても、ユニフォーミティの改善に貢献する度合いが小さいからである。 Moreover, it is preferable to provide a bead core cover layer made of a thermoplastic elastomer adjacent to only the surface facing the carcass layer of the outer peripheral surface of the bead core. This is because even if it is provided between the bead filler and the bead core, the degree of contribution to improvement of uniformity is small.
本発明において、ビードコアカバー層を構成する熱可塑性エラストマーのマトリクスとなる熱可塑性樹脂としては、例えば、ポリアミド系樹脂〔例えば、ナイロン6(N6)、ナイロン66(N66)、ナイロン46(N46)、ナイロン11(N11)、ナイロン12(N12)、ナイロン610(N610)、ナイロン612(N612)、ナイロン6/66共重合体(N6/66)、ナイロン6/66/610共重合体(N6/66/610)、ナイロンMXD6(MXD6)、ナイロン6T、ナイロン6/6T共重合体、ナイロン66/PP共重合体、ナイロン66/PPS共重合体〕及びそれらのN−アルコキシアルキル化物、例えば、ナイロン6のメトキシメチル化物、ナイロン6/610共重合体のメトキシメチル化物、ナイロン612のメトキシメチル化物、ポリエステル系樹脂〔例えば、ポリブチレンテレフタレート(PBT)、ポリエチレンテレフタレート(PET)、ポリエチレンイソフタレート(PEI)、PET/PEI共重合体、ポリアリレート(PAR)、ポリブチレンナフタレート(PBN)、液晶ポリエステル、ポリオキシアルキレンジイミドジ酸/ポリブチレンテレフタレート共重合体などの芳香族ポリエステル〕、ポリニトリル系樹脂〔例えば、ポリアクリロニトリル(PAN)、ポリメタクリロニトリル、アクリロニトリル/スチレン共重合体(AS)、(メタ)アクリロニトリル/スチレン共重合体、(メタ)アクリロニトリル/スチレン/ブタジエン共重合体〕、ポリメタクリレート系樹脂〔例えば、ポリメタクリル酸メチル(PMMA)、ポリメタクリル酸エチル〕、ポリビニル系樹脂〔例えば、酢酸ビニル、ポリビニルアルコール(PVA)、ビニルアルコール/エチレン共重合体(EVOH)、ポリ塩化ビニリデン(PDVC)、ポリ塩化ビニル(PVC)、塩化ビニル/塩化ビニリデン共重合体、塩化ビニリデン/メチルアクリレート共重合体、塩化ビニリデン/アクリロニトリル共重合体(ETFE)〕、セルロース系樹脂〔例えば、酢酸セルロース、酢酸酪酸セルロース〕、フッ素系樹脂〔例えば、ポリフッ化ビニリデン(PVDF)、ポリフッ化ビニル(PVF)、ポリクロルフルオロエチレン(PCTFE)、テトラフロロエチレン/エチレン共重合体〕、イミド系樹脂〔例えば、芳香族ポリイミド(PI)〕等を好ましく用いることができる。 In the present invention, examples of the thermoplastic resin used as the matrix of the thermoplastic elastomer constituting the bead core cover layer include polyamide resins [eg, nylon 6 (N6), nylon 66 (N66), nylon 46 (N46), nylon 11 (N11), nylon 12 (N12), nylon 610 (N610), nylon 612 (N612), nylon 6/66 copolymer (N6 / 66), nylon 6/66/610 copolymer (N6 / 66 / 610), nylon MXD6 (MXD6), nylon 6T, nylon 6 / 6T copolymer, nylon 66 / PP copolymer, nylon 66 / PPS copolymer] and their N-alkoxyalkylated products such as nylon 6 Methoxymethylated product, nylon 6/610 copolymer methoxymethylated product, 612 methoxymethylated product, polyester resin [for example, polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polyethylene isophthalate (PEI), PET / PEI copolymer, polyarylate (PAR), polybutylene naphthalate (PBN), liquid crystal polyester, aromatic polyester such as polyoxyalkylene diimide diacid / polybutylene terephthalate copolymer], polynitrile resin [for example, polyacrylonitrile (PAN), polymethacrylonitrile, acrylonitrile / styrene copolymer (AS), (meth) acrylonitrile / styrene copolymer, (meth) acrylonitrile / styrene / butadiene copolymer], polymethacrylate resin [for example, polymethyl methacrylate (PM A), polyethyl methacrylate], polyvinyl resin [for example, vinyl acetate, polyvinyl alcohol (PVA), vinyl alcohol / ethylene copolymer (EVOH), polyvinylidene chloride (PDVC), polyvinyl chloride (PVC), chloride Vinyl / vinylidene chloride copolymer, vinylidene chloride / methyl acrylate copolymer, vinylidene chloride / acrylonitrile copolymer (ETFE)], cellulosic resin [eg, cellulose acetate, cellulose acetate butyrate], fluorine resin [eg, polyfluoride] Vinylidene fluoride (PVDF), polyvinyl fluoride (PVF), polychlorofluoroethylene (PCTFE), tetrafluoroethylene / ethylene copolymer], an imide-based resin [for example, aromatic polyimide (PI)] or the like is preferably used. it can.
また、熱可塑性エラストマーを構成するゴムとしては、例えば、ジエン系ゴム及びその水添物〔例えば、天然ゴム(NR)、イソプレンゴム(IR)、エポキシ化天然ゴム、スチレンブタジエンゴム(SBR)、ブタジエンゴム(BR、高シスBR及び低シスBR)、ニトリルゴム(NBR)、水素化NBR、水素化SBR〕、オレフィン系ゴム〔例えば、エチレンプロピレンゴム(EPDM、EPM)、マレイン酸変性エチレンプロピレンゴム(M−EPM)、ブチルゴム(IIR)、イソブチレンと芳香族ビニル又はジエン系モノマー共重合体、アクリルゴム(ACM)、アイオノマー〕、含ハロゲンゴム〔例えば、Br−IIR、CI−IIR、イソブチレンパラメチルスチレン共重合体の臭素化物(Br−IPMS)、クロロプレンゴム(CR)、ヒドリンゴム(CHR)、クロロスルホン化ポリエチレンゴム(CSM)、塩素化ポリエチレンゴム(CM)、マレイン酸変性塩素化ポリエチレンゴム(M−CM)〕、シリコンゴム〔例えば、メチルビニルシリコンゴム、ジメチルシリコンゴム、メチルフェニルビニルシリコンゴム〕、含イオウゴム〔例えば、ポリスルフィドゴム〕、フッ素ゴム〔例えば、ビニリデンフルオライド系ゴム、含フッ素ビニルエーテル系ゴム、テトラフルオロエチレン−プロピレン系ゴム、含フッ素シリコン系ゴム、含フッ素ホスファゼン系ゴム〕、熱可塑性エラストマー〔例えば、スチレン系エラストマー、オレフィン系エラストマー、エステル系エラストマー、ウレタン系エラストマー、ボリアミド系エラストマー〕等を好ましく使用することができる。 Examples of the rubber constituting the thermoplastic elastomer include diene rubbers and hydrogenated products thereof [for example, natural rubber (NR), isoprene rubber (IR), epoxidized natural rubber, styrene butadiene rubber (SBR), butadiene. Rubber (BR, high cis BR and low cis BR), nitrile rubber (NBR), hydrogenated NBR, hydrogenated SBR], olefin rubber [for example, ethylene propylene rubber (EPDM, EPM), maleic acid modified ethylene propylene rubber ( M-EPM), butyl rubber (IIR), isobutylene and aromatic vinyl or diene monomer copolymer, acrylic rubber (ACM), ionomer], halogen-containing rubber [eg, Br-IIR, CI-IIR, isobutylene paramethylstyrene Copolymer bromide (Br-IPMS), chloroprene (CR), hydrin rubber (CHR), chlorosulfonated polyethylene rubber (CSM), chlorinated polyethylene rubber (CM), maleic acid modified chlorinated polyethylene rubber (M-CM)], silicone rubber [eg methyl vinyl silicone rubber , Dimethyl silicone rubber, methyl phenyl vinyl silicone rubber], sulfur-containing rubber (for example, polysulfide rubber), fluorine rubber (for example, vinylidene fluoride rubber, fluorine-containing vinyl ether rubber, tetrafluoroethylene-propylene rubber, fluorine-containing silicon) Rubber, fluorine-containing phosphazene rubbers], thermoplastic elastomers (for example, styrene elastomers, olefin elastomers, ester elastomers, urethane elastomers, polyamide elastomers) and the like are preferably used. Door can be.
熱可塑性エラストマーにおいて、特定の熱可塑性樹脂とゴムとの組成比は、特に限定されるものではなく、熱可塑性樹脂のマトリクス中にゴムが不連続相として分散した構造をとるように適宜決めればよいが、好ましい範囲は重量比90/10〜30/70である。 In the thermoplastic elastomer, the composition ratio between the specific thermoplastic resin and the rubber is not particularly limited, and may be appropriately determined so as to have a structure in which the rubber is dispersed as a discontinuous phase in the thermoplastic resin matrix. However, the preferred range is 90/10 to 30/70 by weight.
以下、実施例により本発明の空気入りタイヤの具体的構成・効果について説明する。 Hereinafter, specific configurations and effects of the pneumatic tire of the present invention will be described with reference to examples.
なお、本発明において、以下の実施例で、耐久性試験(走行距離km)、タイヤのユニフォーミティ試験(ラジアルフォースバリエーション(RFV))については、それぞれ下記の方法で測定し、評価したものである。 In the present invention, in the following examples, a durability test (traveling distance km) and a tire uniformity test (radial force variation (RFV)) are measured and evaluated by the following methods, respectively. .
(1)耐久性(指数評価)
試験タイヤ(乗用車用タイヤ)に酸素を350kPaの圧力で充填し、そのままの状態で80℃の雰囲気下に3週間放置して、強制的に酸化劣化を生じさせる。その3週間を経過した後に、直ちに充填された酸素を抜き、通常の空気圧180kPaで空気を充填して走行試験用タイヤとする。
(1) Durability (index evaluation)
A test tire (passenger car tire) is filled with oxygen at a pressure of 350 kPa, and left as it is in an atmosphere of 80 ° C. for 3 weeks to forcibly cause oxidative degradation. After 3 weeks, the filled oxygen is immediately drained and filled with air at a normal air pressure of 180 kPa to obtain a running test tire.
走行試験は、直径1707mmの走行試験ドラムを使用して、荷重はJATMAに規定される最大荷重の80%とし、ドラム上でのスリップ角(首振り角)をプラス・マイナス2°とし、速度80km/hで連続走行させて、2000km走行ごとに、試験タイヤをシアログラフィ試験装置を用いた非破壊試験方式により、ビードコア付近の剥がれ・故障の発生有無をチェックした。 The running test uses a running test drum with a diameter of 1707 mm, the load is 80% of the maximum load specified by JATMA, the slip angle (swing angle) on the drum is plus or minus 2 °, and the speed is 80 km. The test tire was checked for occurrence of peeling / failure in the vicinity of the bead core by a nondestructive test method using a shearography test device every 2000 km.
それらの発生が認められれば、その試験タイヤの走行はそれ以上は行わずに、そのタイヤの走行距離データとした。発生が認められない場合は、そのタイヤを再び2000kmの走行試験に供して、その走行後、またビードコア付近の剥がれ・故障の発生有無をチェックすることを繰り返した。 If such occurrence was recognized, the test tire was not run any further, and the travel distance data of the tire was used. When no occurrence was observed, the tire was again subjected to a 2000 km running test, and after the running, the presence or absence of peeling / failure in the vicinity of the bead core was repeatedly checked.
この試験は、上記のように高圧で酸素を充填して過酷な条件で強制的な劣化をさせた後の耐久性試験であり、走行距離が10000kmを超えるレベルであれば実際の空気入りタイヤとして十分に優れた耐久性があると認められるものである。 This test is a durability test after filling with oxygen at a high pressure and forcibly degrading under severe conditions as described above. If the mileage exceeds 10,000 km, it is an actual pneumatic tire. It is recognized as having sufficiently excellent durability.
この試験では、3万mまでの距離の試験を行い、それでもビードコア付近の剥がれ・故障の発生が認められないものは、走行距離「30000m超」として評価し、それ以上は走行を行わなかった。 In this test, a distance test up to 30,000 m was conducted, and even if no peeling or failure was observed near the bead core, the travel distance was “over 30000 m”, and no further travel was performed.
(2)ユニフォーミティ(ラジアルフォースバリエーション(RFV))
JASO C607「自動車タイヤのユニフォーミティ試験方法」に準拠して、空気圧200kPa、縦荷重を空気圧200kPaでの負荷能力の0.85倍として、ラジアルフォースバリエーション(RFV)を測定し、ユニフォーミティの評価を行った。ラジアルフォースの単位は「N(ニュートン)」であり、その値が小さいほどラジアルフォースにばらつきがなく、タイヤの均斉さが優れていることを表している。
(2) Uniformity (Radial Force Variation (RFV))
In accordance with JASO C607 “Testing method for uniformity of automobile tires”, the radial force variation (RFV) was measured with an air pressure of 200 kPa and a longitudinal load of 0.85 times the load capacity at an air pressure of 200 kPa. went. The unit of radial force is “N (Newton)”, and the smaller the value, the more uniform the radial force and the better the tire uniformity.
実施例1〜4、従来例1〜2
表1に示したとおりのビードワイヤ埋設材料とビードコアカバー層、さらにカーカスゴム層の組合せを変えて、合計6種類のビードを製造した。ビードワイヤ埋設材料のナイロン66樹脂は融点が267℃のものである。
Examples 1-4, conventional examples 1-2
A total of six types of beads were manufactured by changing the combination of the bead wire embedding material, the bead core cover layer, and the carcass rubber layer as shown in Table 1. Nylon 66 resin as a bead wire embedding material has a melting point of 267 ° C.
ビードコアカバー層は、図2に示したようにビードコアの3面とカーカス層に接して配置させた。ビードコアカバー層の厚さは1.5mmとした。 The bead core cover layer was disposed in contact with the three surfaces of the bead core and the carcass layer as shown in FIG. The thickness of the bead core cover layer was 1.5 mm.
これらの各ビードを用いて、タイヤサイズ225/55R17の空気入りタイヤを試作して、耐久性およびユニフォーミティの評価を行った。 Using each of these beads, a pneumatic tire with a tire size of 225 / 55R17 was prototyped, and durability and uniformity were evaluated.
各実施例、比較例の評価結果を表1に示した。本発明によれば、耐久性とユニフォーミティに優れた空気入りタイヤが得られることがわかる。 The evaluation results of each example and comparative example are shown in Table 1. According to the present invention, it can be seen that a pneumatic tire excellent in durability and uniformity can be obtained.
1:トレッド部
2:サイドウォール部
3:ビード部
4:カーカス層
5:ビードコア
6:ベルト層
7:ビードワイヤ
8:ビードワイヤの埋設樹脂
9:ビードコアカバー層
10:カーカスコートゴム
11:カーカスコード
1: Tread part 2: Side wall part 3: Bead part 4: Carcass layer 5: Bead core 6: Belt layer 7: Bead wire 8: Bead wire embedded resin 9: Bead core cover layer 10: Carcass coat rubber 11: Carcass cord
Claims (6)
The pneumatic tire according to any one of claims 1 to 5, wherein a thickness of the bead core cover layer made of the thermoplastic elastomer is 0.5 to 2 mm.