JP5298543B2

JP5298543B2 - Converter operation method

Info

Publication number: JP5298543B2
Application number: JP2008015766A
Authority: JP
Inventors: 健史鈴木; 誠司鍋島; 雄太日野
Original assignee: JFE Steel Corp
Current assignee: JFE Steel Corp
Priority date: 2008-01-28
Filing date: 2008-01-28
Publication date: 2013-09-25
Anticipated expiration: 2028-01-28
Also published as: JP2009174029A

Abstract

<P>PROBLEM TO BE SOLVED: To restrain the formation of stuck bare metal while avoiding any trouble caused by the stuck bare metal in the opening part of a converter and the lowering of a productivity, accompanied with the prevention of this trouble. <P>SOLUTION: When molten iron 13 is blown in the converter 3, according to the distributing state of the stuck bare metal in the converter, any one of two kinds of top-blowing lances 8, 9 of the following (a) and (b), is selected and blown. (a) The top-blowing lance 8 is the one, in which one or more oxygen gas spouting nozzles for blowing are arranged at the lower end part, and at least one of the oxygen gas spouting nozzles has a gas supplying hole for controlling on the wall surface of the fan-state part, and the direction and/or the flowing speed of the jet spouted from the oxygen gas spouting nozzle for blowing can be controlled by supplying the gas for controlling from the supplying hole for controlling. (b) The top-blowing lance 9 is the one, in which the one or more of oxygen gas spouting nozzles for blowing, are arranged at the lower end part, and further, on the outer circumferential part, a gas spouting nozzle for melting the stuck bare metal, is arranged. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、転炉内の溶銑に上吹きランスから酸素ガスを吹き付けて、溶銑に対して酸化精錬を行う転炉操業方法に関し、詳しくは、スピッティングなどによる転炉炉口や側壁への地金の付着を抑制し、安定した転炉精錬を行うための操業方法に関するものである。 The present invention relates to a converter operating method in which oxygen gas is blown from an upper blowing lance to hot metal in a converter and oxidative refining is performed on the hot metal, and more specifically, to the converter furnace mouth and side wall by spitting or the like. The present invention relates to an operation method for suppressing the adhesion of gold and performing stable converter refining.

上吹きランスを介して酸素ガスを上吹きする転炉精錬においては、酸素吹錬中に発生するスピッティング及びスロッピングにより飛散した溶銑、溶鋼及びスラグの一部は、転炉の炉口や炉内側壁に地金として付着する。付着した地金は操業を続けるにつれて成長し、その大きさが或る限度以上になると、溶銑及びスクラップの炉内への装入の障害になるばかりでなく、吹錬中に地金が浴内へ落下したり或いは溶融流下したりすることで、浴の成分組成や温度の変動を来たし、操業に大きな支障をもたらす。このような付着地金は適切に除去しないと、その付着地金の下側の耐火物まで損傷する危険性もある。従って、スピッティング及びスロッピングの発生を軽減して、地金の付着・成長が生じにくい操業方法を指向するとともに、一旦付着した地金は操業に支障を来す大きさになる前に除去する必要がある。 In converter refining, in which oxygen gas is blown up through an upper blowing lance, molten iron, molten steel, and part of the slag scattered during spitting and slopping generated during oxygen blowing are part of the converter mouth and furnace. It adheres to the inner wall as a bullion. Adhered bullion grows as it continues to operate, and when its size exceeds a certain limit, it not only hinders the introduction of hot metal and scrap into the furnace, but the bullion is bathed in the bath during blowing. Dropping into the melt or flowing down causes fluctuations in the composition and temperature of the bath, causing a significant hindrance to the operation. There is also a risk of damaging the refractory underneath the attached bullion if it is not properly removed. Therefore, while reducing the occurrence of spitting and slopping and aiming for an operation method in which adhesion and growth of bullion is less likely to occur, the bullion once adhered is removed before it becomes large enough to interfere with operation. There is a need.

スピッティングの発生を軽減するために、従来から上吹きランスの改善が行われており、吹錬用酸素ガス噴射ノズルの多孔化や傾斜角度の増大といった方法が採られている。例えば特許文献１には、吹錬用酸素ガス噴射ノズルとして、傾斜角度の異なる２種類のラバールノズルを円周方向に交互に配置し、それにより、これらの各ノズルから噴射されるガス噴流の重なりを抑制し、スピッティングを低減する技術が開示されている。しかしながら、特許文献１を含めて従来報告されている方法では、特に酸素ガス供給流量（「送酸速度」ともいう）を増加させて吹錬時間の短縮を図ろうとした場合には、スピッティングの発生や地金付着を抑制するには至らず、依然、炉口付着地金の除去作業が必要となっている。 In order to reduce the occurrence of spitting, the top blowing lance has been improved conventionally, and methods such as making the blowing oxygen gas injection nozzle porous and increasing the inclination angle have been adopted. For example, in Patent Document 1, two types of Laval nozzles having different inclination angles are alternately arranged in the circumferential direction as oxygen gas injection nozzles for blowing, thereby overlapping the gas jets injected from these nozzles. Techniques for suppressing and reducing spitting are disclosed. However, in the methods that have been reported in the past including Patent Document 1, especially when the oxygen gas supply flow rate (also referred to as “acid feed rate”) is increased to shorten the blowing time, Neither generation nor adhesion of bullion has been suppressed, and it is still necessary to remove bullion attached to the furnace port.

炉口付着地金を除去する方法としては、スクラップシュートを炉口付着地金に衝突させ、物理的に除去するという伝統的な方法がある。しかしながら、この方法は、スクラップシュートを炉口付着地金部に直接ぶつけるので、その衝撃で炉口煉瓦の脱落を起こす危険性がある。 As a method for removing the furnace-hole-attached metal, there is a traditional method in which a scrap chute is collided with the furnace-hole-attached metal and physically removed. However, since this method directly hits the scrap chute against the furnace-portion metal part, there is a risk of dropping the furnace-port brick due to the impact.

また、特許文献２には、非操業中に専用の地金溶解用上吹きランスを炉口から炉内に挿入し、炉口に付着した地金を溶解・除去する方法が開示されている。しかしながら、この方法は、付着地金の除去には優れるが、転炉の非吹錬時に実施しなければならないので、非製鋼時間の増大を招き、転炉生産性を著しく阻害する。そこで、転炉の生産性を阻害することがないように、吹錬中に炉内で発生する排ガスを二次燃焼させ、その熱で炉口や炉内側壁に付着した地金を溶解除去する方法が提案されている。 Further, Patent Document 2 discloses a method of melting and removing a bare metal adhering to the furnace port by inserting a dedicated top blowing lance for melting a bare metal from the furnace port into the furnace during non-operation. However, this method is excellent in removing the adhering metal, but it must be carried out at the time of non-blowing of the converter, leading to an increase in non-steel time and significantly impairing converter productivity. Therefore, in order not to hinder the productivity of the converter, the exhaust gas generated in the furnace during secondary blowing is subjected to secondary combustion, and the heat is used to dissolve and remove the metal that has adhered to the furnace mouth and the inner wall of the furnace. A method has been proposed.

例えば、特許文献３には、上吹きランス先端に設けた吹錬用酸素ガス噴射ノズルから吹錬用酸素ガスを溶銑に吹き付けつつ、前記吹錬用酸素ガス噴射ノズルから所定の間隔を隔てた上吹きランスの側面に設置した地金溶解用ガス噴射ノズルから、炉内側壁に向けて酸素ガスを噴射し、炉内付着地金を溶解・除去する方法が開示されている。しかしながら、炉内での二次燃焼を利用する方法は、二次燃焼率を制御することが困難であり、特に付着地金が少なくなった場合には、二次燃焼熱によって耐火物が損傷されやすいという難点がある。尚、本発明においては、吹錬用酸素ガスと同時に、地金溶解用ガスを噴射できる上吹きランスを「吹錬・地金溶解用上吹きランス」と称し、地金溶解用ガスのみを噴射できる上吹きランスを「地金溶解用上吹きランス」と称し、吹錬用酸素ガスのみを供給可能な上吹きランスを「吹錬用上吹きランス」と称する。 For example, Patent Document 3 discloses a method in which a blowing oxygen gas is sprayed from a blowing oxygen gas injection nozzle provided at the tip of an upper blowing lance to a hot metal while being spaced apart from the blowing oxygen gas injection nozzle by a predetermined interval. A method is disclosed in which oxygen gas is injected toward the inner wall of the furnace from a metal injection gas injection nozzle installed on the side surface of the blowing lance to dissolve and remove the ingot in the furnace. However, in the method using secondary combustion in the furnace, it is difficult to control the secondary combustion rate. In particular, when the amount of attached metal is reduced, the refractory is damaged by the secondary combustion heat. There is a difficulty that it is easy. In the present invention, an upper blowing lance capable of injecting a bullion melting gas simultaneously with an oxygen gas for smelting is referred to as an “upper lance for blowing and bullion melting”, and only the bullion melting gas is injected. An upper blowing lance that can be supplied is called an “upper blowing lance for melting metal”, and an upper blowing lance that can supply only the oxygen gas for blowing is called an “upper blowing lance for blowing”.

更に、特許文献４には、吹錬用酸素ガスのみを供給可能な吹錬用上吹きランスと、吹錬用酸素ガスの供給と同時に、この吹錬用酸素ガスとは独立して流量制御が可能な地金溶解用酸素ガスを供給できる吹錬・地金溶解用上吹きランスとの２種類の上吹きランスを、適宜使い分けることにより、転炉炉口や炉内側壁の耐火物を損傷させることなく、付着地金の形成を抑制する技術が開示されている。しかしながら、この方法では、吹錬・地金溶解用上吹きランス使用時での耐火物の異常損傷のリスクは低減できるものの、付着地金の原因となるスピッティングの発生を低減する対策は採られていないため、比較的短期間で上吹きランスの切り替えをしながら操業することが必要となる。また、吹錬・地金溶解用上吹きランスの外周部に設けた地金溶解用ガス噴射ノズルの位置や噴射角度は、一旦設置したら変更はできないため、地金が付着しやすい位置と、地金を溶解しやすい位置とが一致していない場合には、付着地金の溶解能率が上がらず、吹錬・地金溶解用上吹きランスの連続使用頻度が増加し、結局、耐火物の異常損傷を招くというケースも生じる。 Furthermore, Patent Document 4 discloses a top lance for blowing that can supply only the oxygen gas for blowing, and simultaneously with the supply of the oxygen gas for blowing, the flow rate control is independent of the oxygen gas for blowing. Damage to the refractory at the converter furnace mouth and the inner wall of the furnace by properly using two types of top blowing lances, the blowing blast and blast metal melting top blowing lance that can supply oxygen gas for melting ingots The technique which suppresses formation of adhesion metal is disclosed. However, this method can reduce the risk of abnormal damage to the refractory when using an upper blowing lance for blowing and melting metal, but measures are taken to reduce the occurrence of spitting that causes adhesion metal. Therefore, it is necessary to operate while switching the upper blowing lance in a relatively short period of time. In addition, since the position and injection angle of the metal injection gas injection nozzle provided on the outer periphery of the upper blowing lance for blowing and metal dissolution cannot be changed once installed, If the position where the gold is easy to melt does not match, the dissolution efficiency of the ingot metal does not increase, and the frequency of continuous use of the top blowing lance for blowing and melting metal increases, resulting in abnormal refractories. In some cases, damage may occur.

ところで、本発明者等は、特許文献５において、転炉を用いて溶銑の脱炭精錬または溶銑の脱燐精錬を行う際に、吹錬用酸素ガス噴射ノズルの形状、ランス高さ、酸素ガス供給流量を変更することなく、１本の上吹きランスであっても酸素ガス噴流の制御が可能で、それにより、炉内付着地金の溶解、二次燃焼増大による溶鋼着熱、並びに高速吹錬を達成することのできる上吹きランスとして、「入口部にスロート部を有し且つ前記スロート部の下流側に末広がり部を有するガス噴射ノズルを１個以上配置した上吹きランスであって、前記ガス噴射ノズルのうちの少なくとも１個は、当該ノズルの前記末広がり部の壁面に配置された少なくとも１箇所の制御用ガス供給孔を有し、該制御用ガス供給孔から制御用ガスを供給することにより、前記ガス噴射ノズルから噴射される噴流の方向及び／または流速が制御されることを特徴とする上吹きランス」を提案している。特許文献５によれば、制御用ガス供給孔から供給される制御用ガスにより、ガス噴射ノズルから噴射されるガス噴流の方向及び／または流速が制御されるので、このガス噴射ノズルを吹錬用酸素ガス噴射ノズルとして使用することにより、ソフトブロー及びハードブローを任意に調節できるという作用・効果が発現される。但し、特許文献５に開示される上吹きランスのみでは、付着地金を溶解することは困難である。
特開平６−５７３２０号公報特開平４−３５４８１４号公報特開平８−１２７８１２号公報特開２０００−９６１２２号公報特開２００７−７７４８９号公報 By the way, in the patent document 5, the present inventors, when performing decarburization refining of hot metal or dephosphorization of hot metal using a converter, the shape of the oxygen gas injection nozzle for blowing, the lance height, oxygen gas Without changing the supply flow rate, it is possible to control the oxygen gas jet even with one top blowing lance, so that melting of the metal adhering to the furnace, molten heat deposition due to increased secondary combustion, and high-speed blowing are possible. As an upper blowing lance capable of achieving smelting, “an upper blowing lance having at least one gas injection nozzle having a throat portion at an inlet portion and a divergent portion downstream of the throat portion, At least one of the gas injection nozzles has at least one control gas supply hole arranged on the wall surface of the divergent portion of the nozzle, and supplies the control gas from the control gas supply hole. Before Direction and / or flow rate of the jet to be injected from the gas injection nozzle is proposed lance "over to being controlled. According to Patent Document 5, since the direction and / or flow velocity of the gas jet injected from the gas injection nozzle is controlled by the control gas supplied from the control gas supply hole, the gas injection nozzle is used for blowing. By using it as an oxygen gas injection nozzle, the effect of being able to arbitrarily adjust soft blow and hard blow is exhibited. However, it is difficult to dissolve the adhered metal using only the top blowing lance disclosed in Patent Document 5.
JP-A-6-57320 JP-A-4-354814 JP-A-8-127812 JP 2000-96122 A JP 2007-77489 A

上述したように、従来の技術では、上吹きランスや操業方法の改善によって地金付着を完全に防止することは困難であり、一方、付着した地金を除去する技術についても問題が残っている。 As described above, in the conventional technology, it is difficult to completely prevent the adhesion of the bullion by improving the top blowing lance and the operation method, while the technique for removing the adhered bullion remains a problem. .

本発明は上記事情に鑑みてなされたもので、その目的とするところは、転炉内の溶銑に上吹きランスを介して酸素ガスを上吹きして溶銑の酸化精錬を行うに当たり、転炉炉口の付着地金などに起因したトラブルや、これを防ぐための処置に伴う生産性の低下を回避しつつ、付着地金の形成を高度に抑制し、しかも炉口や炉内側壁の耐火物を損傷させることもない転炉操業方法を提供することである。 The present invention has been made in view of the above circumstances, and the object of the present invention is to convert oxygen in the molten iron in the converter through an upper blowing lance to perform the oxygen refining of the molten iron in the converter furnace. While avoiding troubles caused by the metal sticking to the mouth and the decrease in productivity due to measures to prevent it, the formation of the stick metal is highly suppressed, and the refractories on the furnace mouth and the inner wall of the furnace It is to provide a converter operation method that does not damage the furnace.

本発明者等は、上記課題を解決するべく、鋭意研究を重ねた結果、下記の知見を得るに至った。 As a result of intensive studies to solve the above problems, the present inventors have obtained the following knowledge.

即ち、転炉の炉口及び内壁での付着地金の溶解に際し、広範囲の付着地金を、下地の耐火物を損傷することなく溶解・除去して、炉口及び炉内側壁のプロフィールを良好に保つためには、吹錬用酸素ガスのみを供給する上吹きランス（吹錬用上吹きランス）と、吹錬用酸素ガスの供給と同時に、この吹錬用酸素ガスとは独立して流量制御が可能な地金溶解用ガスを供給できる上吹きランス（吹錬・地金溶解用上吹きランス）の２種類の上吹きランスを適宜使い分け、しかも、吹錬用上吹きランスを使用した吹錬で地金が付着しやすい位置と、吹錬・地金溶解用上吹きランスを使用した吹錬で地金を溶解しやすい位置とが一致するように、２種類の上吹きランスを構成し、そして組み合わせることが、極めて効果的であることを見出した。 That is, when melting the adherent metal at the furnace mouth and inner wall of the converter, a wide range of adhered metal is melted and removed without damaging the base refractory, so that the profile of the furnace mouth and the inner wall of the furnace is good. In order to maintain the flow rate, the upper blowing lance that supplies only the oxygen gas for blowing (the upper blowing lance for blowing) and the flow of the blowing oxygen gas at the same time as the blowing oxygen gas are supplied. Two types of top blowing lances (top blowing lances for blowing and bullion melting) that can supply controllable metal melting gas are properly used and blown using top blowing lances for blowing. Two types of top blowing lances are configured so that the position where bullion easily adheres to the position where bullion using the top lance for blowing and melting metal matches the position where bullion tends to melt. And found that combining is extremely effective.

吹錬用酸素ガスによる炉口及び炉内側壁への地金付着量や付着位置は、吹錬用酸素ガス噴射ノズルの傾斜角度に大きく影響される。一般的には、吹錬用酸素ガス噴射ノズルの傾斜角度を小さくする（鉛直下向きに近くする）と、スピッティング粒は鉛直上向きに跳ね上がりやすくなり、炉口近傍の地金付着が増加する。一方、吹錬用酸素ガス噴射ノズルの傾斜角度を大きくする（水平方向に近くする）と、側壁炉腹に近い位置の地金が成長しやすくなる。但し、転炉の使用回数が増加するにつれて炉内耐火物が損耗して、炉内形状が変化するなどの影響により、必ずしも決まった位置の地金が成長するとは限らない。従って、炉内形状の変化などを反映しつつ、操業状況に応じて吹錬用酸素ガス噴射ノズルの傾斜角度を微調整し、地金が付着しやすい位置と溶解しやすい位置とを一致させる技術が必要となる。 The amount and position of adhesion of the bullion to the furnace port and the inner wall of the furnace with the oxygen gas for blowing are greatly affected by the inclination angle of the oxygen gas injection nozzle for blowing. Generally, when the inclination angle of the oxygen gas injection nozzle for blow smelting is made small (close to the vertical downward direction), the spitting grains are likely to jump upward in the vertical direction, and the adhesion of the metal near the furnace mouth increases. On the other hand, if the inclination angle of the oxygen gas injection nozzle for blowing is increased (closer to the horizontal direction), the metal near the side of the side wall furnace tends to grow. However, as the number of times the converter is used increases, the refractory in the furnace wears out, and the shape of the ingot in the furnace does not always grow due to the change in the shape of the furnace. Therefore, a technology that finely adjusts the tilt angle of the oxygen gas injection nozzle for blowing according to the operation status while reflecting changes in the furnace shape, etc. Is required.

前述したように、本発明者等は、特許文献５において、流体素子の応用によりガス噴射ノズルの傾斜角度を実質的に変化させる方法を開示している。即ち、入口部にスロート部を有し、且つ前記スロート部の下流側に末広がり部を有する、所謂ラバールノズル型のガス噴射ノズルにおいて、末広がり部の壁面に制御用ガス供給孔を配置し、この制御用ガス供給孔に供給する制御用ガスの流量を変化させることにより、前記ガス噴射ノズルから噴出される噴流の噴出方向を自在に変更するという技術である。この構成のガス噴射ノズルを、吹錬用酸素ガスのみを供給する吹錬用酸素ガス噴射ノズルに適用し、制御用ガスの流量を調整することによって吹錬用酸素ガス噴射ノズルの傾斜角度を実質的に微調整すれば、地金が付着しやすい位置と溶解しやすい位置とを、一致させることができるとの知見を得た。 As described above, the present inventors have disclosed a method of substantially changing the inclination angle of the gas injection nozzle by applying a fluid element in Patent Document 5. That is, in a so-called Laval nozzle type gas injection nozzle having a throat portion at the inlet portion and a divergent portion downstream of the throat portion, a control gas supply hole is arranged on the wall surface of the divergent portion, and this control This is a technique for freely changing the jet direction of the jet jetted from the gas jet nozzle by changing the flow rate of the control gas supplied to the gas supply hole. The gas injection nozzle of this configuration is applied to the blowing oxygen gas injection nozzle that supplies only the blowing oxygen gas, and the tilt angle of the blowing oxygen gas injection nozzle is substantially adjusted by adjusting the flow rate of the control gas. As a result, it was found that the position where the metal is easily attached and the position where the metal is easily dissolved can be matched by fine adjustment.

本発明は、上記知見に基づいてなされたものであり、本発明に係る転炉操業方法は、上吹きランスから酸素ガスを供給して転炉で溶銑を吹錬するに際し、前記転炉内に付着した地金の分布状態に応じて、下記（イ）及び（ロ）の２種類の上吹きランスのうちの何れか一方を選定し、選定した上吹きランスを用いて吹錬することを特徴とするものである。
（イ）下端部に吹錬用酸素ガスを噴射する吹錬用酸素ガス噴射ノズルが１個以上設けられた上吹きランスであって、前記吹錬用酸素ガス噴射ノズルは、その入口部にスロート部を有するともに、該スロート部の下流側に末広がり部を有し、且つ、前記吹錬用酸素ガス噴射ノズルのうちの少なくとも１個は、前記末広がり部の壁面に少なくとも１個の制御用ガス供給孔を有しており、該制御用ガス供給孔から前記吹錬用酸素ガスとは独立して流量制御の可能な制御用ガスが供給されることにより、前記吹錬用酸素ガス噴射ノズルから噴射される噴流の方向及び／または流速を制御することが可能な吹錬用上吹きランス。
（ロ）下端部に吹錬用酸素ガスを噴射する吹錬用酸素ガス噴射ノズルが１個以上設けられ、且つ、外周部に前記吹錬用酸素ガスとは独立して流量制御の可能な地金溶解用酸素含有ガス及び／またはパージガスを供給する地金溶解用ガス噴射ノズルが設けられている吹錬・地金溶解用上吹きランス。 The present invention has been made on the basis of the above knowledge, and the converter operating method according to the present invention includes supplying oxygen gas from an upper blowing lance and blowing hot metal in the converter, According to the distribution state of the attached bullion, select one of the two types of top blowing lances (b) and (b) below, and perform blowing using the selected top blowing lance. It is what.
(A) An upper blowing lance provided with one or more blowing oxygen gas injection nozzles for injecting blowing oxygen gas at the lower end, the blowing oxygen gas injection nozzle having a throat at the inlet And at least one of the blown oxygen gas injection nozzles supplies at least one control gas to the wall surface of the divergent portion. The control gas supply hole is supplied with a control gas whose flow rate can be controlled independently from the blowing oxygen gas, and is injected from the blowing oxygen gas injection nozzle. A blown top lance capable of controlling the direction and / or flow rate of the generated jet.
(B) One or more blown oxygen gas injection nozzles for injecting blown oxygen gas at the lower end, and an outer periphery where flow rate can be controlled independently of the blown oxygen gas An upper blowing lance for melting and melting a bullion provided with a gas injection nozzle for melting a bullion supplying oxygen-containing gas and / or purge gas for dissolving gold.

本発明によれば、吹錬用上吹きランスの吹錬用酸素ガス噴射ノズルから噴射される酸素ガス噴流の方向を制御することができるので、転炉炉口及び転炉内壁への地金の付着を軽減することができるとともに、地金の付着位置を、吹錬・地金溶解用上吹きランスでの溶解しやすい位置に調整することができる。従って、吹錬用上吹きランスによる操業を長期間に亘って続けることができるとともに、或る程度付着地金が成長してきたならば、吹錬・地金溶解用上吹きランスに切り替えることで、付着地金を効率的に除去することができ、安定した転炉操業並びに転炉生産性の向上が可能になる。 According to the present invention, the direction of the oxygen gas jet injected from the blowing oxygen gas injection nozzle of the upper blowing lance for blowing can be controlled. Adhesion can be reduced, and the adhesion position of the metal can be adjusted to a position where it can be easily dissolved by the upper blowing lance for blowing and metal melting. Therefore, the operation with the upper blowing lance for blowing can be continued for a long period of time, and if the adhering metal has grown to some extent, switching to the upper blowing lance for blowing and melting the metal, Adhesive metal can be removed efficiently, and stable converter operation and converter productivity can be improved.

以下、添付図面を参照して本発明を具体的に説明する。図１は、本発明を実施するために用いる転炉設備の１例の概略図である。 Hereinafter, the present invention will be described in detail with reference to the accompanying drawings. FIG. 1 is a schematic diagram of an example of a converter facility used for carrying out the present invention.

図１において、外殻を鉄皮３とし、その内側を耐火物４とする転炉本体２に対して、吹錬用上吹きランス８及び吹錬・地金溶解用上吹きランス９の２種類の上吹きランスが、それぞれ炉口５を介して転炉本体２の内部に挿入可能に構成されている。吹錬用上吹きランス８は、その下端部から吹錬用酸素ガスを供給するための上吹きランスであり、一方、吹錬・地金溶解用上吹きランス９は、その下端部から吹錬用酸素ガスを供給するとともに、その外周部から、地金溶解用の酸素含有ガス或いは窒素ガスなどのパージガスを供給するための上吹きランスである。酸素含有ガスには酸素ガスが含まれる。 In FIG. 1, two types of an upper blowing lance 8 for blowing and an upper blowing lance 9 for blowing and bullion melting are applied to a converter body 2 having an iron shell 3 as an outer shell and a refractory 4 inside thereof. The top blowing lances can be inserted into the converter main body 2 through the furnace port 5. The upper blowing lance 8 for blowing is an upper blowing lance for supplying oxygen gas for blowing from the lower end thereof, while the upper blowing lance 9 for melting and melting metal is blown from the lower end thereof. This is an upper blowing lance for supplying a working oxygen gas and supplying a purge gas such as an oxygen-containing gas or a nitrogen gas for dissolving a metal from the outer peripheral portion thereof. The oxygen-containing gas includes oxygen gas.

また、転炉本体２には、側壁上部に出湯口６が設けられ、底部に複数の底吹き羽口７が設置されている。出湯口６は、酸素吹錬により得られた溶鋼や脱燐処理された溶銑を出湯するための排出孔であり、底吹き羽口７は、溶銑１３にＡｒガス、窒素ガスなどの攪拌用ガスを吹き込むための装置である。このようにして転炉設備１が構成されている。尚、転炉操業において、上吹きランスは厳しい熱負荷を受けるため、一般的に、補修、取替えの頻度は比較的高い。このために、現在稼動しているほとんどの転炉設備では、転炉本体一基に対して上吹きランス及びその昇降装置が二式並列で設置され、上吹きランスの交換を迅速に行えるような設備構成となっている。この観点から見ると、本発明で使用する転炉設備１の基本的な構成は特別な設備とはいえず、従って、本発明を実施する上で特別の設備改造は必要としない。 Further, the converter main body 2 is provided with a hot water outlet 6 at the upper part of the side wall and a plurality of bottom blowing tuyere 7 at the bottom. The tap 6 is a discharge hole for pouring molten steel obtained by oxygen blowing or hot metal that has been dephosphorized, and the bottom blow tuyere 7 is a stirring gas such as Ar gas or nitrogen gas. It is a device for blowing in. In this way, the converter equipment 1 is configured. In the converter operation, the top blow lance is subjected to a severe heat load, so that the frequency of repair and replacement is generally relatively high. For this reason, in most converter facilities currently in operation, an upper blowing lance and its lifting device are installed in parallel for one converter main body so that the upper blowing lance can be replaced quickly. The equipment configuration. From this point of view, the basic configuration of the converter equipment 1 used in the present invention is not a special equipment, and therefore, no special equipment modification is required to implement the present invention.

ここで先ず、本発明で使用する吹錬・地金溶解用上吹きランス９を、図面に基づき詳細に説明する。図２は、図１に示す吹錬・地金溶解用上吹きランス９の拡大図である。 First, the top blowing lance 9 for melting and melting metal used in the present invention will be described in detail with reference to the drawings. FIG. 2 is an enlarged view of the top blowing lance 9 for blowing and melting metal shown in FIG.

図２に示すように、吹錬・地金溶解用上吹きランス９は、円筒状のランス本体９ａと、このランス本体９ａの下端に溶接などにより接続されたランスチップ９ｂとで構成されており、ランス本体９ａは、途中まで、外管２４、仕切管２３、内管２２、最内管２１からなる同心円状の４種の鋼管、即ち四重管で構成され、先端部は、外管２４、仕切管２３、内管２２からなる同心円状の３種の鋼管、即ち三重管で構成されており、先端部の銅製のランスチップ９ｂには、鉛直斜め下向き方向を向いた複数個の吹錬用酸素ガス噴射ノズル１０が設置されている。それぞれの吹錬用酸素ガス噴射ノズル１０の中心線は、鉛直方向に対して傾斜しており、この鉛直方向に対する角度を傾斜角度と呼んでいる。また、吹錬・地金溶解用上吹きランス９の先端から所定の間隔を隔てた上方の、ランス本体９ａの外周部には、斜め下向き方向に向いた地金溶解用ガス噴射ノズル１１が設けられている。この地金溶解用ガス噴射ノズル１１からは、地金溶解用酸素含有ガス或いはパージガスが噴射される。 As shown in FIG. 2, the upper blow lance 9 for smelting and melting metal is composed of a cylindrical lance body 9a and a lance tip 9b connected to the lower end of the lance body 9a by welding or the like. The lance body 9a is composed of four types of concentric steel pipes, that is, a quadruple pipe, consisting of an outer tube 24, a partition tube 23, an inner tube 22 and an innermost tube 21, up to the middle. Are formed of three kinds of concentric steel pipes consisting of a partition pipe 23 and an inner pipe 22, that is, a triple pipe, and a copper lance tip 9b at the tip portion has a plurality of blow squeezings directed vertically downward. A working oxygen gas injection nozzle 10 is installed. The center line of each blowing oxygen gas injection nozzle 10 is inclined with respect to the vertical direction, and an angle with respect to the vertical direction is called an inclination angle. In addition, a gas injection nozzle 11 for dissolving a metal bar is provided on the outer peripheral portion of the lance body 9a, which is spaced apart from the tip of the upper blowing lance 9 for blowing and melting a metal bar, in a diagonally downward direction. It has been. From this metal injection gas-discharging nozzle 11, a metal-containing oxygen-containing gas or purge gas is injected.

外管２４と仕切管２３との間隙、及び、仕切管２３と内管２２との間隙は、吹錬・地金溶解用上吹きランス９を冷却するための冷却水の流路となっており、吹錬・地金溶解用上吹きランス９の上部に設けられた給水継手（図示せず）から供給された冷却水は、仕切管２３と内管２２との間隙を通ってランスチップ９ｂの部位まで至り、ランスチップ９ｂの部位で反転して外管２４と仕切管２３との間隙を通って吹錬・地金溶解用上吹きランス９の上部に設けられた排水継手（図示せず）から排出される。この場合に給排水の径路を逆としてもよい。 The gap between the outer pipe 24 and the partition pipe 23 and the gap between the partition pipe 23 and the inner pipe 22 serve as cooling water flow paths for cooling the upper blowing lance 9 for melting and melting metal. The cooling water supplied from a water supply joint (not shown) provided at the upper part of the upper blowing lance 9 for melting and melting metal is passed through the gap between the partition pipe 23 and the inner pipe 22 and flows into the lance tip 9b. A drainage joint (not shown) provided at the upper portion of the upper blowing lance 9 for blowing and smelting metal through the gap between the outer pipe 24 and the partition pipe 23 by reversing at the portion of the lance tip 9b. Discharged from. In this case, the water supply / drainage path may be reversed.

内管２２と最内管２１との間隙は、地金溶解用ガス噴射ノズル１１への酸素含有ガス及び／またはパージガスの供給流路となっており、吹錬・地金溶解用上吹きランス９の上端部から内管２２と最内管２１との間隙に供給された酸素含有ガス及び／またはパージガスは、内管２２と最内管２１との間隙を通り、地金溶解用ガス噴射ノズル１１から転炉本体内に噴出される。内管２２と最内管２１とは、最下段の地金溶解用ガス噴射ノズル１１の設置位置の直下で連結され、最内管２１はその位置で途絶えている。尚、ここでは、最内管２１が地金溶解用ガス噴射ノズル１１の直下で途絶えている例を示したが、下端が閉止されていればその位置は更に下方でもよく、設備配置上で構成が容易な構造にすればよい。また、パージガスは地金溶解操作をしない時に地金溶解用ガス噴射ノズル１１が目詰まりしないように保持するためのガスであり、パージガスとしては、窒素ガス、Ａｒガスなどを使用することができる。 The gap between the inner tube 22 and the innermost tube 21 serves as a supply flow path for oxygen-containing gas and / or purge gas to the metal injection gas injection nozzle 11, and an upper blow lance 9 for blowing and metal dissolution. The oxygen-containing gas and / or the purge gas supplied to the gap between the inner pipe 22 and the innermost pipe 21 from the upper end of the gas passes through the gap between the inner pipe 22 and the innermost pipe 21, and the gas injection nozzle 11 for dissolving the metal bar 11. Is ejected into the converter body. The inner tube 22 and the innermost tube 21 are connected directly below the installation position of the lowermost-stage metal melting gas injection nozzle 11, and the innermost tube 21 is disconnected at that position. Here, an example in which the innermost pipe 21 is cut off immediately below the metal injection gas injection nozzle 11 has been shown. However, if the lower end is closed, the position may be further lower, and it is configured on the equipment layout. It is sufficient to make the structure easy. In addition, the purge gas is a gas for holding the metal injection gas injection nozzle 11 so as not to be clogged when the metal dissolution operation is not performed, and nitrogen gas, Ar gas, or the like can be used as the purge gas.

また、最内管２１の内部は、吹錬用酸素ガス噴射ノズル１０への酸素ガスの供給流路となっており、吹錬・地金溶解用上吹きランス９の上端部から最内管２１の内部に供給された酸素ガスは、最内管２１の内部を通り、先端部では内管２２の内部を通り、吹錬用酸素ガス噴射ノズル１０から転炉本体内に噴出される。このように、地金溶解用酸素含有ガスの供給経路を、吹錬用酸素ガスの供給経路から独立させて制御できるようにしてある。 Further, the inside of the innermost pipe 21 serves as a supply flow path for oxygen gas to the oxygen gas injection nozzle 10 for blowing, and the innermost pipe 21 extends from the upper end portion of the upper blowing lance 9 for blowing and metal melting. The oxygen gas supplied to the inside passes through the inside of the innermost pipe 21, passes through the inside of the inner pipe 22 at the tip, and is jetted from the blowing oxygen gas injection nozzle 10 into the converter main body. In this way, the supply path of the oxygen-containing gas for melting the metal can be controlled independently of the supply path of the oxygen gas for blowing.

この吹錬用酸素ガス噴射ノズル１０の拡大図を図３に示す。図３に示すように、吹錬用酸素ガス噴射ノズル１０は、その断面が縮小する部分と拡大する部分の２つの円錐体で構成された所謂ラバールノズル形式のノズルであり、縮小部分は絞り部２５、拡大部分は末広がり部２７、絞り部２５から末広がり部２７に遷移する部位である、最も狭くなった部位はスロート２６と呼ばれている。ランス本体９ａの内部を通ってきた酸素ガスは、絞り部２５、スロート２６、末広がり部２７を順に通って、吹錬用酸素ガス噴射ノズル１０の先端から噴射される。噴射されたガスは、その流量により亜音速から超音速のジェットとなる。図３中のｄｔはスロート径、ｄｅは出口径であり、末広がり部２７の広がり角度θoは通常１０度以下である。 An enlarged view of this blowing oxygen gas injection nozzle 10 is shown in FIG. As shown in FIG. 3, the oxygen gas injection nozzle 10 for blowing is a so-called Laval nozzle type nozzle composed of two cones, a portion whose cross section is reduced and a portion where the cross section is enlarged. The enlarged portion is a divergent portion 27, and the narrowest portion, which is a portion that transitions from the narrowed portion 25 to the divergent portion 27, is called a throat 26. The oxygen gas that has passed through the inside of the lance main body 9 a passes through the throttle portion 25, the throat 26, and the divergent portion 27 in this order, and is injected from the tip of the blowing oxygen gas injection nozzle 10. The injected gas becomes a subsonic to supersonic jet depending on its flow rate. D t in FIG. 3 throat diameter, d e is the exit diameter, divergence angle θo of the flared portion 27 is less than the normal 10 degrees.

尚、図３に示すラバールノズル形状の吹錬用酸素ガス噴射ノズル１０では、絞り部２５及び末広がり部２７が円錐体であるが、ラバールノズルとしては絞り部２５及び末広がり部２７は円錐体である必要はなく、内径が曲線的に変化する曲面で構成してもよく、また、絞り部２５はスロート２６と同一の内径であるストレート状の円筒形としてもよい。絞り部２５及び末広がり部２７を、内径が曲線的に変化する曲面で構成する場合には、ラバールノズルとして理想的な流速分布が得られるが、ノズルの加工が極めて困難であり、一方、絞り部２５をストレート状の円筒形とした場合には、理想的な流速分布とは若干乖離するが、転炉吹錬での使用には全く問題とならず、且つ、ノズルの加工が極めて容易となる。本発明ではこれら全ての末広がりのノズルをラバールノズルと称する。 In addition, in the oxygen gas injection nozzle 10 for the blowing of a Laval nozzle shown in FIG. 3, the throttle portion 25 and the divergent portion 27 are conical bodies. Instead, the inner diameter may be configured by a curved surface, and the throttle portion 25 may be a straight cylindrical shape having the same inner diameter as the throat 26. When the throttle portion 25 and the divergent portion 27 are configured with curved surfaces whose inner diameter changes in a curved manner, an ideal flow velocity distribution as a Laval nozzle can be obtained, but the processing of the nozzle is extremely difficult. In the case of a straight cylindrical shape, there is a slight deviation from the ideal flow velocity distribution, but there is no problem for use in converter blowing, and nozzle processing becomes extremely easy. In the present invention, all these divergent nozzles are called Laval nozzles.

また、地金溶解用ガス噴射ノズル１１は、図１に示すように、ランス先端からの距離を３段階に分けて設置（３段構成）しているが、任意の段数を採ることができ、１段であろうと複数段であろうと、各々の転炉本体２の形状に沿った設計を行っていれば、本発明の効果を充分に発揮することができる。また更に、図２に示す地金溶解用ガス噴射ノズル１１はストレート型ノズルであるが、使用条件に応じてラバールノズル形状としても構わない。また更に、使用条件によっては、吹錬用酸素ガス噴射ノズル１０を鉛直下向き方向としても構わず、地金溶解用ガス噴射ノズル１１を水平方向或いは上向としても構わない。 In addition, as shown in FIG. 1, the gas injection nozzle 11 for dissolving a metal bar is installed in a three-stage distance from the tip of the lance (3-stage configuration), but can take any number of stages, Regardless of whether it is a single stage or a plurality of stages, the effect of the present invention can be fully exerted if the design is performed according to the shape of each converter body 2. Furthermore, although the metal injection gas injection nozzle 11 shown in FIG. 2 is a straight type nozzle, it may have a Laval nozzle shape depending on use conditions. Furthermore, depending on use conditions, the blowing gas oxygen injection nozzle 10 may be vertically downward, and the metal melting gas injection nozzle 11 may be horizontal or upward.

次ぎに、本発明で使用する吹錬用上吹きランス８を、図面に基づき詳細に説明する。図４は、図１に示す吹錬用上吹きランス８の拡大図である。尚、吹錬用上吹きランス８は、吹錬・地金溶解用上吹きランス９と類似しており、重複することもあるが説明する。 Next, the top blowing lance 8 for blowing used in the present invention will be described in detail with reference to the drawings. FIG. 4 is an enlarged view of the upper blowing lance 8 for blowing shown in FIG. The blowing lance 8 for blow smelting is similar to the blowing lance 9 for blowing and bullion melting and will be described in some cases.

図４に示すように、吹錬用上吹きランス８は、円筒状のランス本体８ａと、このランス本体８ａの下端に溶接などにより接続されたランスチップ８ｂとで構成されており、ランス本体８ａは、外管２０、仕切管１９、内管１８、最内管１７からなる同心円状の４種の鋼管、即ち四重管で構成され、先端部の銅製のランスチップ８ｂには、鉛直斜め下向き方向を向いた複数個の吹錬用酸素ガス噴射ノズル１０が設置されている。この吹錬用酸素ガス噴射ノズル１０は、前述した図３に示すラバール形状のノズルであり、それぞれの吹錬用酸素ガス噴射ノズル１０の中心線は、鉛直方向に対して傾斜している。また、吹錬用酸素ガス噴射ノズル１０のうちの少なくとも１つの吹錬用酸素ガス噴射ノズル１０には、その末広がり部２７の壁面に少なくとも１個の制御用ガス供給孔１２が設けられている。制御用ガス供給孔１２からは、当該吹錬用酸素ガス噴射ノズル１０から噴射される噴流の方向及び／または流速を制御するための制御用ガスが噴射される。この制御用ガスとしては、窒素ガスであろうと、空気であろうと、またＡｒガスであろうと、どのような種類のガスであっても使用可能であるが、制御用ガスは、最終的には吹錬用酸素ガス噴射ノズル１０で吹錬用酸素ガスと混合されて噴射されることから、酸素ガスを使用すれば精錬にも利用できるので望ましい。以下、制御用ガスとして酸素ガスを使用した例を説明する。 As shown in FIG. 4, the upper blow lance 8 for blowing is composed of a cylindrical lance body 8a and a lance tip 8b connected to the lower end of the lance body 8a by welding or the like. Is composed of four types of concentric steel pipes consisting of an outer pipe 20, a partition pipe 19, an inner pipe 18, and an innermost pipe 17, that is, a quadruple pipe. The copper lance tip 8b at the tip is vertically inclined downward. A plurality of blowing oxygen gas injection nozzles 10 facing in the direction are installed. This blowing oxygen gas injection nozzle 10 is a Laval nozzle as shown in FIG. 3 described above, and the center line of each blowing oxygen gas injection nozzle 10 is inclined with respect to the vertical direction. Further, at least one of the blowing oxygen gas injection nozzles 10 is provided with at least one control gas supply hole 12 on the wall surface of the divergent portion 27 thereof. From the control gas supply hole 12, a control gas for controlling the direction and / or flow velocity of the jet injected from the blowing oxygen gas injection nozzle 10 is injected. The control gas can be any type of gas, whether nitrogen gas, air, or Ar gas, but the control gas is ultimately Since it is mixed with the blowing oxygen gas by the blowing oxygen gas injection nozzle 10 and injected, it is desirable that oxygen gas can be used for refining. Hereinafter, an example in which oxygen gas is used as the control gas will be described.

外管２０と仕切管１９との間隙、及び、仕切管１９と内管１８との間隙は、吹錬用上吹きランス８を冷却するための冷却水の流路となっており、吹錬用上吹きランス８の上部に設けられた給水継手（図示せず）から供給された冷却水は、仕切管１９と内管１８との間隙を通ってランスチップ８ｂの部位まで至り、ランスチップ８ｂの部位で反転して外管２０と仕切管１９との間隙を通って吹錬用上吹きランス８の上部に設けられた排水継手（図示せず）から排出される。この場合に給排水の径路を逆としてもよい。 The gap between the outer pipe 20 and the partition pipe 19 and the gap between the partition pipe 19 and the inner pipe 18 serve as a flow path for cooling water for cooling the upper blowing lance 8 for blowing. Cooling water supplied from a water supply joint (not shown) provided on the upper portion of the upper blowing lance 8 passes through the gap between the partition pipe 19 and the inner pipe 18 to reach the portion of the lance tip 8b. It reverses at the site, passes through the gap between the outer pipe 20 and the partition pipe 19 and is discharged from a drainage joint (not shown) provided at the upper part of the upper blowing lance 8 for blowing. In this case, the water supply / drainage path may be reversed.

内管１８と最内管１７との間隙は、吹錬用酸素ガス噴射ノズル１０への酸素ガスの供給流路となっており、吹錬用上吹きランス８の上端部から内管１８と最内管１７との間隙に供給された酸素ガスは、内管１８と最内管１７との間隙を通り、吹錬用酸素ガス噴射ノズル１０から転炉本体内に噴出される。噴射されたガスは、その流量により亜音速から超音速のジェットとなる。 The gap between the inner pipe 18 and the innermost pipe 17 serves as a supply flow path for oxygen gas to the blowing oxygen gas injection nozzle 10, and from the upper end of the upper blowing lance 8 for blowing to the inner pipe 18 and the innermost pipe 18. The oxygen gas supplied to the gap with the inner pipe 17 passes through the gap between the inner pipe 18 and the innermost pipe 17 and is jetted from the blowing oxygen gas injection nozzle 10 into the converter main body. The injected gas becomes a subsonic to supersonic jet depending on its flow rate.

また、最内管１７の内部は、制御用ガス供給孔１２への制御用ガス（ここでは酸素ガス）の供給流路となっており、吹錬用上吹きランス８の上端部から最内管１７の内部に供給された制御用ガスとしての酸素ガス（以下、「制御用酸素ガス」と記す）は、最内管１７の内部を通り、制御用ガス供給孔１２から噴射される。このように、制御用酸素ガスの供給経路を、吹錬用酸素ガスの供給経路から独立させて制御できるようにしてある。 Further, the inside of the innermost pipe 17 is a supply flow path for the control gas (in this case, oxygen gas) to the control gas supply hole 12, and the innermost pipe extends from the upper end of the upper blowing lance 8 for blowing. An oxygen gas (hereinafter referred to as “control oxygen gas”) supplied to the inside of the control gas 17 passes through the innermost pipe 17 and is injected from the control gas supply hole 12. Thus, the control oxygen gas supply path can be controlled independently of the blowing oxygen gas supply path.

制御用ガス供給孔１２は、吹錬用酸素ガス噴射ノズル１０から噴射される噴流の方向及び／または流速を制御するための装置であり、図４に示すように、制御用ガス供給孔１２からの噴射方向が、吹錬用上吹きランス８の中心から外面側に向いている場合には、吹錬用酸素ガスの流量に対する制御用酸素ガスの流量を増加させると、吹錬用酸素ガス噴射ノズル１０から噴射される噴流は、より一層、吹錬用上吹きランス８の外周側へ偏向し、吹錬用酸素ガス噴射ノズル１０の傾斜角度を増加させた場合（水平方向に近くする）と同じ効果を発現する。逆に、吹錬用酸素ガスの流量に対する制御用酸素ガスの流量を減少させると、吹錬用酸素ガス噴射ノズル１０から噴射される噴流は偏向しにくくなり、吹錬用酸素ガス噴射ノズル１０の傾斜角度を減少させた場合（鉛直下向きに近くする）と同じ効果を発現する。ここで、図４に示す吹錬用酸素ガス噴射ノズル１０は、斜め下向き方向を向いており、このように斜め下向き方向を向くものが一般的であるが、鉛直下向き方向としても構わない。 The control gas supply hole 12 is a device for controlling the direction and / or flow velocity of the jet injected from the blowing oxygen gas injection nozzle 10, and as shown in FIG. Is directed to the outer surface side from the center of the upper blowing lance 8 for blowing, if the flow rate of the control oxygen gas is increased with respect to the flow rate of the blowing oxygen gas, the blowing oxygen gas injection The jet flow injected from the nozzle 10 is further deflected toward the outer peripheral side of the upper blowing lance 8 for blowing and when the inclination angle of the blowing oxygen gas injection nozzle 10 is increased (close to the horizontal direction). Has the same effect. On the contrary, if the flow rate of the control oxygen gas is decreased with respect to the flow rate of the blowing oxygen gas, the jet flow injected from the blowing oxygen gas injection nozzle 10 becomes difficult to be deflected. The same effect as when the inclination angle is decreased (approaching vertically downward) is exhibited. Here, the blown oxygen gas injection nozzle 10 shown in FIG. 4 is oriented obliquely downward, and is generally oriented obliquely downward in this manner, but may be a vertically downward direction.

更に、本発明で使用する吹錬用上吹きランス８の別の形態例について、図面に基づき説明する。図５は、本発明で使用する吹錬用上吹きランスの、図４とは別の形態例の拡大図である。ここでは、上記で説明した吹錬用上吹きランス８と区別するために、別の形態例の吹錬用上吹きランスを、「吹錬用上吹きランス８Ａ」と表示している。 Furthermore, another embodiment of the upper blowing lance 8 for blowing used in the present invention will be described with reference to the drawings. FIG. 5 is an enlarged view of an embodiment different from FIG. 4 of the top blowing lance for blowing used in the present invention. Here, in order to distinguish from the upper blowing lance 8 for blowing described above, the blowing upper blow lance of another embodiment is indicated as “upper blowing lance 8A for blowing”.

図５に示すように、吹錬用上吹きランス８Ａは、円筒状のランス本体８ｃと、このランス本体８ｃの下端に溶接などにより接続されたランスチップ８ｄとで構成されており、ランス本体８ｃは、外管２０、仕切管１９ａ、仕切管１９ｂ、内管１８からなる同心円状の４種の鋼管、即ち四重管で構成され、先端部の銅製のランスチップ８ｄには、鉛直斜め下向き方向を向いた複数個の吹錬用酸素ガス噴射ノズル１０が設置されている。この吹錬用酸素ガス噴射ノズル１０は、前述した図３に示すラバール形状のノズルであり、それぞれの吹錬用酸素ガス噴射ノズル１０の中心線は、鉛直方向に対して傾斜している。 As shown in FIG. 5, the upper blow lance 8A for blowing is composed of a cylindrical lance body 8c and a lance tip 8d connected to the lower end of the lance body 8c by welding or the like. Is composed of four types of concentric steel pipes consisting of an outer tube 20, a partition tube 19a, a partition tube 19b, and an inner tube 18, that is, a quadruple tube, and a copper lance tip 8d at the tip is vertically inclined downward. A plurality of blown oxygen gas injection nozzles 10 facing the direction are installed. This blowing oxygen gas injection nozzle 10 is a Laval nozzle as shown in FIG. 3 described above, and the center line of each blowing oxygen gas injection nozzle 10 is inclined with respect to the vertical direction.

また、吹錬用酸素ガス噴射ノズル１０のうちの少なくとも１つの吹錬用酸素ガス噴射ノズル１０には、その末広がり部２７の壁面に、少なくとも１個の制御用ガス供給孔１２が設けられている。制御用ガス供給孔１２からは、当該吹錬用酸素ガス噴射ノズル１０から噴射される噴流の方向及び／または流速を制御するための制御用ガスが噴射される。この制御用ガスの種類としては、図４の場合と同様に、窒素ガスであろうと、空気であろうと、またＡｒガスであろうと、どのような種類のガスであっても使用可能であるが、制御用ガスは、最終的には吹錬用酸素ガス噴射ノズル１０で吹錬用酸素ガスと混合され、噴射されることから、酸素ガスを使用すれば精錬にも利用できるので望ましい。以下、制御用ガスとして酸素ガスを使用した例を説明する。 Further, at least one of the blowing oxygen gas injection nozzles 10 is provided with at least one control gas supply hole 12 on the wall surface of the divergent portion 27 thereof. . From the control gas supply hole 12, a control gas for controlling the direction and / or flow velocity of the jet injected from the blowing oxygen gas injection nozzle 10 is injected. As the type of the control gas, any type of gas can be used, whether it is nitrogen gas, air, or Ar gas, as in the case of FIG. Since the control gas is finally mixed with the blowing oxygen gas by the blowing oxygen gas injection nozzle 10 and injected, it is desirable that oxygen gas can be used for refining. Hereinafter, an example in which oxygen gas is used as the control gas will be described.

外管２０と仕切管１９ａとの間隙、及び、仕切管１９ｂと内管１８との間隙は、吹錬用上吹きランス８Ａを冷却するための冷却水の流路となっており、吹錬用上吹きランス８Ａの上部に設けられた給水継手（図示せず）から供給された冷却水は、仕切管１９ｂと内管１８との間隙を通ってランスチップ８ｄの部位まで至り、ランスチップ８ｄの部位で反転して外管２０と仕切管１９ａとの間隙を通って吹錬用上吹きランス８Ａの上部に設けられた排水継手（図示せず）から排出される。この場合に給排水の径路を逆としてもよい。 The gap between the outer pipe 20 and the partition pipe 19a and the gap between the partition pipe 19b and the inner pipe 18 serve as a cooling water flow path for cooling the upper blowing lance 8A for blowing. Cooling water supplied from a water supply joint (not shown) provided at the upper part of the upper blow lance 8A passes through the gap between the partition pipe 19b and the inner pipe 18 to reach the site of the lance tip 8d. It reverses at the site, passes through the gap between the outer pipe 20 and the partition pipe 19a, and is discharged from a drainage joint (not shown) provided at the upper part of the upper blowing lance 8A. In this case, the water supply / drainage path may be reversed.

内管１８の内部は、吹錬用酸素ガス噴射ノズル１０への酸素ガスの供給流路となっており、吹錬用上吹きランス８Ａの上端部から内管１８の内部に供給された酸素ガスは、吹錬用酸素ガス噴射ノズル１０から転炉本体内に噴射される。また、仕切管１９ａと仕切管１９ｂの間隙は、制御用ガス供給孔１２への制御用酸素ガスの供給流路となっており、吹錬用上吹きランス８Ａの上端部から仕切管１９ａと仕切管１９ｂの間隙に供給された制御用酸素ガスは、制御用ガス供給孔１２から噴射される。このように、制御用酸素ガスの供給経路を、吹錬用酸素ガスの供給経路から独立させて制御できるようにしてある。 The inside of the inner pipe 18 serves as a supply flow path for oxygen gas to the blowing oxygen gas injection nozzle 10, and oxygen gas supplied from the upper end of the blowing upper blowing lance 8 </ b> A to the inside of the inner pipe 18. Is injected into the converter body from the oxygen gas injection nozzle 10 for blowing. Further, the gap between the partition pipe 19a and the partition pipe 19b serves as a supply flow path for the control oxygen gas to the control gas supply hole 12, and the partition pipe 19a and the partition pipe are separated from the upper end of the upper blowing lance 8A for blowing. The control oxygen gas supplied to the gap between the pipes 19b is injected from the control gas supply hole 12. Thus, the control oxygen gas supply path can be controlled independently of the blowing oxygen gas supply path.

制御用ガス供給孔１２は、吹錬用酸素ガス噴射ノズル１０から噴射される噴流の方向及び／または流速を制御するための装置であり、図５に示すように、制御用ガス供給孔１２からの噴射方向が、吹錬用上吹きランス８Ａの外面側から中心に向いている場合には、吹錬用酸素ガスの流量に対する制御用酸素ガスの流量を増加させると、吹錬用酸素ガス噴射ノズル１０から噴射される噴流は、より一層、吹錬用上吹きランス８Ａの中心軸側へ偏向し、吹錬用酸素ガス噴射ノズル１０の傾斜角度を減少させた場合（鉛直下向きに近くする）と同じ効果を発現する。逆に、吹錬用酸素ガスの流量に対する制御用酸素ガスの流量を減少させると、吹錬用酸素ガス噴射ノズル１０から噴射される噴流は偏向しにくくなり、吹錬用酸素ガス噴射ノズル１０の傾斜角度を増加させた場合（水平方向に近くする）と同じ効果を発現する。ここで、図５に示す吹錬用酸素ガス噴射ノズル１０は、斜め下向き方向を向いており、このように斜め下向き方向を向くものが一般的であるが、鉛直下向き方向としても構わない。 The control gas supply hole 12 is a device for controlling the direction and / or flow velocity of the jet injected from the blowing oxygen gas injection nozzle 10, and as shown in FIG. Is directed to the center from the outer surface side of the upper blowing lance 8A for blowing, if the flow rate of the control oxygen gas is increased relative to the flow rate of the blowing oxygen gas, the blowing oxygen gas injection When the jet flow injected from the nozzle 10 is further deflected toward the center axis side of the upper blowing lance 8A for blowing, and the inclination angle of the blowing oxygen gas injection nozzle 10 is reduced (approached vertically downward) Has the same effect as On the contrary, if the flow rate of the control oxygen gas is decreased with respect to the flow rate of the blowing oxygen gas, the jet flow injected from the blowing oxygen gas injection nozzle 10 becomes difficult to be deflected. The same effect as when the tilt angle is increased (close to the horizontal direction) is exhibited. Here, the blown oxygen gas injection nozzle 10 shown in FIG. 5 is directed obliquely downward, and generally is directed obliquely downward as described above, but may be a vertically downward direction.

尚、上記２種類の吹錬用上吹きランス８，８Ａ及び吹錬・地金溶解用上吹きランス９にガスを供給するバルブスタンドなどの設備は、双方の上吹きランスに共通の仕様となっている。即ち、バルブスタンドには、高流量系のラインと低流量系のラインとの２種類のラインを設けておき、吹錬用上吹きランス８，８Ａへの吹錬用酸素ガス及び吹錬・地金溶解用上吹きランス９への吹錬用酸素ガスは、高流量系のラインから供給され、吹錬用上吹きランス８，８Ａへの制御用酸素ガス及び吹錬・地金溶解用上吹きランス９への地金溶解用酸素含有ガスは、低流量系のラインから供給される。 The above-mentioned two types of top blowing lances 8 and 8A and equipment for supplying gas to the top blowing lances 9 for blowing and metal melting have specifications common to both top blowing lances. ing. That is, the valve stand is provided with two types of lines, a high flow rate line and a low flow rate line, and the oxygen gas for blowing to the upper blowing lances 8 and 8A for blowing and blowing The oxygen gas for blowing to the upper blowing lance 9 for melting gold is supplied from a high flow rate line, and the oxygen gas for control and the upper blowing for melting and blowing molten metal are supplied to the upper blowing lances 8 and 8A for blowing. The oxygen-containing gas for dissolving the metal to the lance 9 is supplied from a low flow rate line.

上記２種類の吹錬用上吹きランス８，８Ａ、及び、吹錬・地金溶解用上吹きランス９を用いた操業の形態について、以下にその概要を説明する。 The outline | summary is demonstrated below about the form of the operation using the above-mentioned 2 types of top blowing lances 8 and 8A for blowing, and the top blowing lance 9 for blowing and metal melting | dissolving.

転炉本体２の炉修後の立ち上げ時には、炉内及び炉口５に付着地金は存在しないので、吹錬用上吹きランス８または吹錬用上吹きランス８Ａを使用して、地金溶解操作を意図しない吹錬を１チャージ以上実施する。この際、制御用酸素ガスの流量は、予め定めた基準条件で吹錬を行う。この吹錬中に発生するスピッティング、スロッピングによって飛散した溶銑１３及びスラグ１４の一部は、転炉本体２の炉口５や炉内側壁に地金として付着する。 When the converter main body 2 is started up after repairing the furnace, there is no metal in the furnace and at the furnace port 5, so the upper blow lance 8 for blowing or the upper blow lance 8 A for blowing is used to Blowing that is not intended for melting operation is performed for one charge or more. At this time, the flow rate of the control oxygen gas is blown under a predetermined reference condition. Part of the hot metal 13 and the slag 14 scattered by spitting and slopping generated during the blowing process adheres to the furnace port 5 and the furnace inner wall of the converter body 2 as a bare metal.

当該チャージの吹錬終了後、吹錬操作者は、転炉本体２の炉口５及び炉内側壁部に付着している地金の状況を目視観察する。図１では、炉口５に付着した地金（以下、「炉口付着地金」と記す）を符号１５で表示し、炉内側壁部に付着した地金（以下、「側壁付着地金」と記す）を符号１６で表示している。一方で、地金付着状況と、それに対する使用すべき上吹きランス種類の選定基準を予め定めておく。この選定基準は、付着地金の量的推定や付着形状などに基づくものとする。 After the completion of the charge blowing, the blowing operator visually observes the state of the metal attached to the furnace port 5 and the furnace inner wall of the converter body 2. In FIG. 1, the bullion attached to the furnace port 5 (hereinafter referred to as “furnace port attached bullion”) is denoted by reference numeral 15, and the bullion attached to the inner wall of the furnace (hereinafter referred to as “side wall attached bullion”). Is denoted by reference numeral 16. On the other hand, the selection standard of the bullion adhesion situation and the type of top blowing lance to be used for it is determined in advance. This selection criterion shall be based on quantitative estimation of attached metal and attached shape.

上記基準に沿って、「地金溶解操作を要する」とされた場合には、吹錬・地金溶解用上吹きランス９に切り替え、次のチャージ以降少なくとも１チャージは吹錬・地金溶解用上吹きランス９を用いて吹錬する。吹錬終了後、吹錬操作者は、転炉本体２に付着していた炉口付着地金１５及び側壁付着地金１６の溶解状況を目視観察し、上記選定基準に基づき、吹錬・地金溶解用上吹きランス９による吹錬を次チャージ以降も継続するか、吹錬用上吹きランス８または吹錬用上吹きランス８Ａに切り替えるかを決定する。 If it is determined that “requires bullion melting operation” in accordance with the above criteria, switch to the upper blow lance 9 for blowing and bullion melting, and at least one charge for blowing and bullion melting after the next charge Blow using the top blow lance 9. After completion of the blowing, the blowing operator visually observes the melting state of the furnace mouth adhering metal 15 and the side wall adhering metal 16 adhering to the converter main body 2, and based on the above selection criteria, It is determined whether to continue blowing with the upper melting lance 9 for melting gold after the next charge, or to switch to the upper blowing lance 8 for blowing or the upper blowing lance 8A for blowing.

このようにして、吹錬用上吹きランス８，８Ａと吹錬・地金溶解用上吹きランス９とを適宜切り替えて使用することにより、常に炉口５及び炉内側壁の付着地金を適正な範囲内に制御して操業を行うことができる。 In this manner, by appropriately switching between the blowing lances 8 and 8A for blowing and the blowing lance 9 for melting and melting metal, the attached metal on the furnace port 5 and the inner wall of the furnace is always appropriate. It is possible to operate within a limited range.

この間、吹錬用上吹きランス８または吹錬用上吹きランス８Ａを使用した際の地金付着傾向（付着しやすい位置、量）、及び、吹錬・地金溶解用上吹きランス９を使用した際の地金溶解傾向（溶解しやすい位置、量）を把握しながら、地金の付着位置を制御するために、吹錬用上吹きランス８または吹錬用上吹きランス８Ａを使用した際の制御用酸素ガスの流量を調整することができる。また、１チャージの吹錬内においても制御用酸素ガスの流量を変化・調整することも可能である。 During this time, the adhesion tendency (position, amount) of the bullion when using the top blowing lance 8 for blowing or the top blowing lance 9 for blowing, and the top blowing lance 9 for melting and melting metal are used. When the upper blow lance 8 for blowing or the upper blow lance 8A for blowing is used to control the adhesion position of the bare metal while grasping the melting tendency of the bare metal (position and amount easy to dissolve) The flow rate of the control oxygen gas can be adjusted. It is also possible to change and adjust the flow rate of the control oxygen gas even within one charge blowing.

図４に示した吹錬用上吹きランス８の場合には、一般的には、吹錬用酸素ガスの流量に対して制御用酸素ガスの流量を少なくすると、吹錬用酸素ガス噴射ノズル１０の傾斜角度を小さくした場合（鉛直下向きに近くする）と同じ効果が得られ、地金の付着・成長しやすい位置は、炉口５の近傍となりやすく、吹錬用酸素ガスの流量に対して制御用酸素ガスの流量を多くすると、吹錬用酸素ガス噴射ノズル１０の傾斜角度を大きくした場合（水平方向に近くする）と同じ効果が得られ、地金の付着・成長しやすい位置は、炉内下方の炉腹に近い位置へと変化する。一方、図５に示した吹錬用上吹きランス８Ａの場合には、吹錬用酸素ガスの流量に対して制御用酸素ガスの流量を少なくすると、吹錬用酸素ガス噴射ノズル１０の傾斜角度を大きくした場合と同じ効果が得られ、地金の付着・成長しやすい位置は、炉内下方の炉腹に近い位置となりやすく、吹錬用酸素ガスの流量に対して制御用酸素ガスの流量を多くすると、吹錬用酸素ガス噴射ノズル１０の傾斜角度を小さくした場合と同じ効果が得られ、地金の付着・成長しやすい位置は、炉口５の近傍へと変化する。 In the case of the top blowing lance 8 shown in FIG. 4, generally, when the flow rate of the control oxygen gas is reduced with respect to the flow rate of the blowing oxygen gas, the blowing oxygen gas injection nozzle 10. The same effect as when the angle of inclination is reduced (nearly vertically downward), the position where the metal sticks and grows easily tends to be in the vicinity of the furnace port 5, and the flow rate of the oxygen gas for blowing When the flow rate of the control oxygen gas is increased, the same effect as when the inclination angle of the blowing oxygen gas injection nozzle 10 is increased (close to the horizontal direction) is obtained, and the position where the metal is easily attached and grown is It changes to a position close to the bottom of the furnace inside the furnace. On the other hand, in the case of the upper blowing lance 8A shown in FIG. 5, if the flow rate of the control oxygen gas is reduced with respect to the flow rate of the blowing oxygen gas, the inclination angle of the blowing oxygen gas injection nozzle 10 is reduced. The position where the same effect as that obtained by increasing the flow rate is obtained and the adhesion and growth of the metal is easy is close to the bottom of the furnace, and the flow rate of the control oxygen gas relative to the flow rate of the blowing oxygen gas Is increased, the same effect as when the inclination angle of the blowing oxygen gas injection nozzle 10 is reduced is obtained, and the position where the metal is easily attached and grown changes to the vicinity of the furnace port 5.

以上説明したように、本発明によれば、吹錬用上吹きランスに設けられた吹錬用酸素ガス噴射ノズルから噴射される酸素ガス噴流の方向を制御することができるので、転炉炉口及び転炉内壁への地金の付着を軽減することができるとともに、地金の付着位置を、吹錬・地金溶解用上吹きランスでの溶解しやすい位置に調整することができる。従って、吹錬用上吹きランスによる操業を長期間に亘って続けることができるとともに、或る程度付着地金が成長してきたならば、吹錬・地金溶解用上吹きランスに切り替えることで、付着地金を効率的に除去することができ、安定した転炉操業並びに転炉生産性の向上が可能になる。 As described above, according to the present invention, the direction of the oxygen gas jet injected from the blowing oxygen gas injection nozzle provided in the upper blowing lance for blowing can be controlled. In addition, the adhesion of the metal to the converter inner wall can be reduced, and the adhesion position of the metal can be adjusted to a position where it can be easily dissolved by the upper blowing lance for blowing and metal melting. Therefore, the operation with the upper blowing lance for blowing can be continued for a long period of time, and if the adhering metal has grown to some extent, switching to the upper blowing lance for blowing and melting the metal, Adhesive metal can be removed efficiently, and stable converter operation and converter productivity can be improved.

ここで、地金溶解用ガス噴射ノズルから噴射する地金溶解用ガスは、一般に酸素ガスであるが、酸素含有ガスであればよく、不活性ガスを混入させることも可能である。尚、吹錬用酸素ガスには、通常工業用純酸素ガスを使用する。 Here, the metal for dissolving the metal from the gas injection nozzle for dissolving the metal is generally oxygen gas, but may be any oxygen-containing gas and may be mixed with an inert gas. In addition, an industrial pure oxygen gas is normally used for the oxygen gas for blowing.

本発明を実施例により更に詳細に説明する。試験方法は、３００トン転炉に溶銑３１０トン及びスクラップ１０トン、並びに造滓剤を所定量装入し、図２に示す吹錬・地金溶解用上吹きランス及び図４に示す吹錬用上吹きランスの２種類の上吹きランスを用いて脱炭精錬した。吹錬・地金溶解用上吹きランスは、地金溶解用ガス噴射ノズルが、ランスの下端から２ｍの高さ位置と、ここから上方に１ｍ間隔で２ヶ所の計３段に設けられたものであり、地金溶解用ガス噴射ノズルは各段ともにランス外周の円周上に６孔づつ配置した。また、地金溶解用ガス噴射ノズルには、酸素ガスの他に、パージガスとして窒素ガス及びＡｒガスが供給されるように構成されている。用いた転炉設備は図１に示したものに準ずる。 The present invention will be described in more detail with reference to examples. The test method is that a 300 ton converter is charged with 310 tons of hot metal, 10 tons of scrap, and a predetermined amount of a slagging agent, and an upper blowing lance for melting and melting metal shown in FIG. Decarburization refining was performed using two types of top-blow lances. The top blowing lance for blowing and melting metal is a gas injection nozzle for melting metal that is provided in 3 steps, 2 meters above the bottom of the lance and 2 points above it at intervals of 1 meter. The gas injection nozzles for dissolving the metal bar were arranged in six holes on the circumference of the outer periphery of the lance at each stage. In addition to the oxygen gas, nitrogen gas and Ar gas are supplied to the metal injection gas injection nozzle as purge gas. The converter equipment used is similar to that shown in FIG.

吹錬用上吹きランスからの酸素ガス流量は４５０００〜６００００Nm³/hrであり、このうちの約５％を制御用酸素ガスとして制御用ガス供給孔から供給した。一方、吹錬・地金溶解用上吹きランスについては、吹錬用酸素ガス噴射ノズルからの酸素ガス流量は４５０００〜６００００Nm³/hr、地金溶解用ガス噴射ノズルからの酸素ガス流量は０〜３０００Nm³/hrの範囲内で調整した。地金溶解用ガス噴射ノズルからの酸素ガス流量が０Nm³/hrの場合にはパージガスを供給した。 The flow rate of oxygen gas from the top blowing lance for blowing was 45,000 to 60000 Nm ³ / hr, and about 5% of this was supplied from the control gas supply hole as control oxygen gas. On the other hand, for the top blowing lance for blowing and metal melting, the oxygen gas flow rate from the blowing oxygen gas injection nozzle is 45000 to 60000 Nm ³ / hr, and the oxygen gas flow rate from the metal melting gas injection nozzle is 0 to 0. Adjustment was made within the range of 3000 Nm ³ / hr. Purge gas was supplied when the flow rate of oxygen gas from the metal injection gas injection nozzle was 0 Nm ³ / hr.

吹錬用上吹きランスを２８チャージ連続使用したところで、炉口及び炉内側壁の付着地金が成長し、予め設定していた基準に達したので、２９チャージ目から吹錬・地金溶解用上吹きランスに切り替え、吹錬・地金溶解用上吹きランスを用いて３１チャージ目まで連続３チャージの吹錬を実施した。この間、付着地金は徐々に減少し、もはや溶解の必要のないレベルまで達した。また、炉内を点検したところ、炉内耐火物の損傷は見られなかった。 When the top blow lance for blow smelting was used continuously for 28 charges, the ingot metal on the furnace mouth and the inner wall of the furnace grew and reached the preset standard. Switching to the top blowing lance, three consecutive charges were blown up to the 31st charge using the top blowing lance for blowing and metal melting. During this time, the adhesion metal gradually decreased and reached a level that no longer required dissolution. Moreover, when the inside of the furnace was inspected, no damage was observed on the refractory inside the furnace.

それ以降、吹錬用上吹きランスを用いて２５〜３０チャージを連続して吹錬し、その後、吹錬・地金溶解用上吹きランスに切り替えて２〜５チャージを連続して吹錬するサイクルで操業した。その結果、付着地金が過度に成長したり、炉内耐火物を損傷したりすることなく、順調に操業することができた。 Thereafter, 25-30 charges are continuously blown using an upper blowing lance for blowing, and then 2-5 charges are blown continuously by switching to an upper blowing lance for blowing and melting metal. Operated in a cycle. As a result, it was possible to operate smoothly without excessively growing the attached metal and damaging the refractories in the furnace.

このように、本発明を適用することにより、転炉の生産性を阻害することなく、炉口及び炉内側壁耐火物の損傷を抑制しつつ、地金の付着を効率的に抑制できることが確認された。 Thus, by applying the present invention, it has been confirmed that adhesion of metal can be efficiently suppressed without inhibiting damage to the furnace mouth and the inner wall refractory without impairing the productivity of the converter. It was done.

本発明を実施するために用いる転炉設備の１例の概略図である。It is the schematic of one example of the converter equipment used in order to implement this invention. 図１に示す吹錬・地金溶解用上吹きランスの拡大図である。It is an enlarged view of the upper blowing lance for blowing and metal melting | dissolving shown in FIG. 図２に示す吹錬用酸素ガス噴射ノズルの拡大図である。It is an enlarged view of the oxygen gas injection nozzle for blowing shown in FIG. 図１に示す吹錬用上吹きランスの拡大図である。It is an enlarged view of the top blowing lance for blowing shown in FIG. 図１に示す吹錬用上吹きランスの別の形態例の拡大図である。It is an enlarged view of another example of the top blowing lance for blowing shown in FIG.

Explanation of symbols

１転炉設備
２転炉本体
３鉄皮
４耐火物
５炉口
６出湯口
７底吹き羽口
８吹錬用上吹きランス
８Ａ吹錬用上吹きランス
９吹錬・地金溶解用上吹きランス
１０吹錬用酸素ガス噴射ノズル
１１地金溶解用ガス噴射ノズル
１２制御用ガス供給孔
１３溶銑
１４スラグ
１５炉口付着地金
１６側壁付着地金
１７最内管
１８内管
１９仕切管
２０外管
２１最内管
２２内管
２３仕切管
２４外管
２５絞り部
２６スロート
２７末広がり部 DESCRIPTION OF SYMBOLS 1 Converter equipment 2 Converter body 3 Iron skin 4 Refractory 5 Furnace port 6 Outlet 7 Bottom blowing tuyere 8 Top blowing lance for blowing 8A Top blowing lance for blowing 9 Top blowing lance for blowing and metal melting DESCRIPTION OF SYMBOLS 10 Blowing oxygen gas injection nozzle 11 Metal injection gas injection nozzle 12 Control gas supply hole 13 Hot metal 14 Slag 15 Furnace adhesion metal 16 Side wall adhesion metal 17 Inner pipe 18 Inner pipe 19 Partition pipe 20 Outer pipe 21 innermost pipe 22 inner pipe 23 partition pipe 24 outer pipe 25 throttle part 26 throat 27 end spreading part

Claims

Following (a) and uses two top-blown one lance above the one of the lance following (b), upon which blowing the molten iron in a converter furnace by supplying oxygen gas from lance on the When blowing with the top blowing lance (b) below, the ground metal will be in a position where the adhesion metal in the converter is likely to melt when blowing with the top blowing lance (b) below. The hot metal is blown by controlling the flow rate of the control gas supplied from the control gas supply hole so that gold adheres, and this blow reaches the standard set in advance. The upper blowing lance to be used is switched from the upper blowing lance shown in (a) below to the upper blowing lance shown in (b) below, and hot metal is blown away, so that the adhesive metal in the converter does not need to be melted. After reaching the state, the upper blowing lance to be used is changed from the following (b) upper blowing lance to the following (b) Converter operation method characterized by blowing switch to lance.
(A) An upper blowing lance provided with one or more blowing oxygen gas injection nozzles for injecting blowing oxygen gas at the lower end, the blowing oxygen gas injection nozzle having a throat at the inlet And at least one of the blown oxygen gas injection nozzles supplies at least one control gas to the wall surface of the divergent portion. The control gas supply hole is supplied with a control gas whose flow rate can be controlled independently from the blowing oxygen gas, and is injected from the blowing oxygen gas injection nozzle. A top blowing lance capable of controlling the direction and / or flow velocity of the generated jet.
(B) One or more blown oxygen gas injection nozzles for injecting blown oxygen gas at the lower end, and an outer periphery where flow rate can be controlled independently of the blown oxygen gas An upper blowing lance provided with a gas injection nozzle for dissolving a metal in order to supply an oxygen-containing gas for dissolving gold and / or a purge gas.