JP5051437B2 - Printed matter, ink set for verification, and manufacturing method thereof - Google Patents
Printed matter, ink set for verification, and manufacturing method thereof Download PDFInfo
- Publication number
- JP5051437B2 JP5051437B2 JP2007168282A JP2007168282A JP5051437B2 JP 5051437 B2 JP5051437 B2 JP 5051437B2 JP 2007168282 A JP2007168282 A JP 2007168282A JP 2007168282 A JP2007168282 A JP 2007168282A JP 5051437 B2 JP5051437 B2 JP 5051437B2
- Authority
- JP
- Japan
- Prior art keywords
- infrared
- pigment
- ink
- infrared absorbing
- reflecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、印刷物及び照合用インキセット並びにその製造方法に関する。さらに詳しくは、赤外線で照合できる明度の高い赤外線吸収インキと赤外線反射インキとからなる照合用インキセットを用いた印刷物及び照合用インキセット並びにその製造方法に関する。 The present invention relates to a printed matter, a collation ink set, and a method for producing the same. More specifically, the present invention relates to a printed matter using a collation ink set composed of an infrared absorbing ink having a high brightness that can be collated with infrared rays and an infrared reflection ink, a collation ink set, and a method for manufacturing the same.
赤外線吸収インキと赤外線反射インキとからなる照合用インキセットを用いた印刷技術は、偽造防止を目的として利用されてきた。これは、インキの赤外線反射性及び赤外線吸収性の違いを利用して、目視では判別できず、赤外線カメラでのみ隠されている秘密情報を読み取ることができるように印刷する技術である。例えば、白色のインキ及び黒色のインキの赤外線反射性及び赤外線吸収性を利用し、赤外線カメラ等の機械で読み取り可能な情報をバーコード等のパターン状のマークとして印刷し、さらにこの印刷パターンを赤外領域の光を吸収しないインキで塗りつぶして隠蔽し、これに赤外線を照射してマークを走査し、その反射赤外光の強度を二極化することにより記録された情報を読み取る技術(特許文献1参照)が知られている。 A printing technique using a collating ink set composed of an infrared absorbing ink and an infrared reflecting ink has been used for the purpose of preventing forgery. This is a technique for printing so that secret information that cannot be visually determined and is hidden only by an infrared camera can be read using the difference between the infrared reflectivity and the infrared absorptivity of ink. For example, by utilizing the infrared reflectivity and infrared absorptivity of white ink and black ink, information readable by a machine such as an infrared camera is printed as a pattern mark such as a barcode, and this print pattern is printed in red. Technology that reads recorded information by painting the outer region with ink that does not absorb light, concealing it, irradiating it with infrared rays, scanning the mark, and dipolarizing the intensity of the reflected infrared light (Patent Literature) 1) is known.
また、赤外線の反射能を有する基材に赤外線の透過率または反射率の異なる少なくとも2種類以上の同色調のインキ層を併設または積層する技術(特許文献2参照)が知られている。 In addition, a technique is known in which a base material having infrared reflectivity is provided with or laminated with at least two or more ink layers having the same color tone having different infrared transmittance or reflectance (see Patent Document 2).
これまで、赤外線吸収インキには、赤外線吸収の大きいカーボンブラックのような顔料が一般的に用いられ、したがって、赤外線吸収インキの色は可視光域で黒に近い色を呈するものであった。
一方、赤外線反射インキは、赤外線吸収インキのダミーとするためには、可視光域では赤外線吸収インキと同色の黒に近い色を示すが、赤外線領域では吸収のないインキでなければならない。このような赤外線領域で吸収のない黒色インキの成分としてシアン、イエロー、マゼンタのインキの三原色を混合した3原色混合ブラックや黒色インキ組成物の主成分を硫化ビスマスとしたもの(特許文献3参照)が知られている。
In the past, pigments such as carbon black having high infrared absorption have been generally used for infrared absorbing ink, and therefore the color of infrared absorbing ink has a color close to black in the visible light range.
On the other hand, in order to use infrared reflection ink as a dummy of infrared absorption ink, the infrared reflection ink has a color close to black, which is the same color as the infrared absorption ink in the visible light region, but must be an ink that does not absorb in the infrared region. As a component of a black ink that does not absorb in the infrared region, a mixture of three primary colors of cyan, yellow, and magenta inks and a black ink composition containing bismuth sulfide as a main component (see Patent Document 3) It has been known.
従来は、赤外線吸収インキに顔料としてカーボンブラックを使用することから、ダミーインキとして使用される赤外線反射インキには黒を基調とする色を用いるしかなかった。そのため、偽造防止印刷部分には明度の低い色が使用され、明るくカラフルな色は用いることができず、デザイン性の高い印刷を施すことができなかった。 Conventionally, since carbon black is used as a pigment in the infrared absorbing ink, the infrared reflective ink used as the dummy ink has to use a color based on black. For this reason, a color with low lightness is used for the forgery-preventing printing portion, and bright and colorful colors cannot be used, and printing with high designability cannot be performed.
そこで、本発明者等は、赤外線を吸収または反射するインキの材料として、白色度の高い材料を用いることに着想し、カーボンブラックに代えて薄い灰色を呈するアンチモン錫(SnO2,Sb2O3)を赤外線吸収インキの顔料として用いる技術を開発した。この技術により、明度が高く、カラフルな色調の赤外線吸収インキを使用することができるようになり、明るくカラフルでデザイン性のある偽造防止印刷が可能となってきた。 Accordingly, the present inventors have conceived of using a material with high whiteness as an ink material that absorbs or reflects infrared rays, and antimony tin (SnO 2 , Sb 2 O 3) that exhibits light gray instead of carbon black. ) Was developed as a pigment for infrared absorbing ink. With this technology, it has become possible to use infrared absorbing ink with high brightness and colorful colors, and it has become possible to perform anti-counterfeit printing that is bright, colorful, and has a design.
明度の高い赤外線吸収インキを用いて偽造防止印刷を形成するためには、赤外線吸収インキで印刷した部分と赤外線反射インキ(ダミーインキ)で印刷した部分を、可視光線下で同色に見える印刷パターンにしておかなければならない。そのため、可視光下で印刷パターンの両インキ間に色差が生じないよう、赤外線吸収インキと赤外線反射インキを調肉しておくことが必要である。従来の黒色を基調とした照合用インキセットの場合には色合わせは困難ではなかったが、明度の高い照合用インキセットの場合には、色合わせにおいて微妙な調整が必要となる。 In order to form anti-counterfeit printing using infrared light absorbing ink with high brightness, the printed pattern that looks the same color under visible light on the part printed with infrared light absorbing ink and the part printed with infrared reflective ink (dummy ink). I have to keep it. Therefore, it is necessary to prepare the infrared absorbing ink and the infrared reflecting ink so as not to cause a color difference between the two inks of the print pattern under visible light. In the case of a conventional matching ink set based on black, color matching has not been difficult, but in the case of a matching ink set with high brightness, fine adjustment is required in color matching.
ところが、長時間を費やして微妙な調肉作業により色合わせを行い、赤外線吸収インキと赤外線反射インキが同じ色を呈する照合用インキセットを開発しても、印刷基材にパターンを印刷した場合に両インキ間で色差が生ずることが多々あった。これは、上記照合用インキセットの各インキが同じ色であっても、各インキに含まれた顔料は異なるので、印刷パターンを形成するインキ被膜の透過度がそれぞれ異なり、印刷基材の背景色や材質の影響を受けることに起因している。さらに、印刷方式の違いにより異なる色合いを有するビヒクルを使用するために、このビヒクル自体の色にも影響を受ける。
したがって、背景色や材質の異なる印刷基材に偽造防止印刷をするために、印刷基材毎に得られたインキを印刷して色合いを確認し、可視光下で印刷パターンの色差の生じない赤外線吸収インキと赤外線反射インキの組み合わせを調肉する必要があった。このため、インキの製造と色合せ作業に膨大な時間と煩雑な労力を要していた。
However, when a pattern is printed on a printing substrate even if a long time is spent, color matching is performed by delicate meat preparation, and a matching ink set is developed in which infrared absorbing ink and infrared reflecting ink exhibit the same color. There were often color differences between the two inks. This is because, even if each ink of the above-mentioned matching ink set is the same color, the pigment contained in each ink is different, so the transparency of the ink film forming the printing pattern is different, and the background color of the printing substrate This is due to the influence of the material. Further, since a vehicle having a different hue due to a difference in printing method is used, the color of the vehicle itself is also affected.
Therefore, in order to perform anti-counterfeit printing on printing substrates with different background colors and materials, the ink obtained for each printing substrate is printed to check the hue, and infrared that does not cause a color difference in the printed pattern under visible light It was necessary to prepare a combination of absorbing ink and infrared reflecting ink. For this reason, enormous time and complicated labor are required for the production and color matching of ink.
本発明は、上記課題に鑑み、印刷基材の種類や材質等に関わらず赤外線で照合でき、かつ、明度の高い、印刷物及び照合用インキセット並びにその製造方法を提供することを目的とする。 In view of the above problems, an object of the present invention is to provide a printed matter and a collating ink set that can be collated with infrared rays regardless of the type and material of the printing base material and have high brightness, and a method for producing the same.
本発明者等は赤外線吸収インキと赤外線反射インキで印刷した印刷物について鋭意研究した結果、赤外線吸収インキに含まれる顔料と赤外線反射インキに含まれる顔料の粒径分布が可視光下で生じる色差に関係していることを見出し、本発明を完成するに至った。 As a result of intensive studies on printed matter printed with infrared absorbing ink and infrared reflecting ink, the present inventors have found that the particle size distribution of the pigment contained in the infrared absorbing ink and the pigment contained in the infrared reflecting ink is related to the color difference generated under visible light. As a result, the present invention has been completed.
上記目的を達成するために、本発明に係る印刷物は、赤外線領域で光吸収率が高い赤外線吸収顔料を含む赤外線吸収インキ層と、赤外線領域で反射率が高いかまたは光吸収率が低い赤外線反射顔料を含む赤外線反射インキ層と、が基材上に印刷されていて、赤外線吸収顔料と赤外線反射顔料との何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキには、基本色と色を同色とするための染料が含有されており、赤外線吸収インキと赤外線反射インキとに含まれる赤外線を吸収及び反射する顔料の粒径分布が同等であることを特徴とする。 In order to achieve the above object, a printed matter according to the present invention includes an infrared absorbing ink layer containing an infrared absorbing pigment having a high light absorption rate in the infrared region, and an infrared reflection having a high reflectance or a low light absorption rate in the infrared region. An infrared reflective ink layer containing a pigment and an infrared reflective ink or infrared reflective ink which is printed on a substrate and has either one of an infrared absorbing pigment or an infrared reflecting pigment as a basic color and the other pigment. Contains a dye for making the same color as the basic color, and the particle size distribution of the pigment that absorbs and reflects the infrared rays contained in the infrared absorbing ink and the infrared reflecting ink is equal. To do.
上記構成において、好ましくは、赤外線吸収顔料と赤外線反射顔料との粒径分布は、最小粒径の対比率が0.9以上であり、最大粒径の対比率が0.9以上であって、かつ個数平均粒子径の対比率が0.9以上である。
赤外線吸収インキ及び赤外線反射インキには、好ましくは、基本色と異なる色にするための着色剤が添加されている。
赤外線吸収顔料は、好ましくは、アンチモン錫からなり、また、赤外線反射顔料は、好ましくは、酸化チタンからなる。
In the above configuration, preferably, the particle size distribution of the infrared absorbing pigment and the infrared reflective pigment has a minimum particle size ratio of 0.9 or more and a maximum particle size ratio of 0.9 or more, The ratio of the number average particle diameter is 0.9 or more.
The infrared absorbing ink and the infrared reflecting ink are preferably added with a colorant for making the color different from the basic color.
The infrared absorbing pigment is preferably made of antimony tin, and the infrared reflecting pigment is preferably made of titanium oxide.
上記構成によれば、赤外線で照合でき、かつ、明度の高い赤外線吸収インキ及び赤外線反射インキからなる照合用インキセットを用いることで、意匠性が向上した印刷が得られる。 According to the said structure, the printing which improved the designability is obtained by using the ink set for collation which can collate with infrared rays and consists of infrared absorption ink and infrared reflection ink with high brightness.
本発明に係る照合用インキセットは、赤外線領域で光吸収率が高い赤外線吸収顔料を含む赤外線吸収インキと赤外線領域で反射率が高いかまたは光吸収率が低い赤外線反射顔料を含む赤外線反射インキとからなり、赤外線吸収顔料と赤外線反射顔料との何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキには、基本色と色を同色とするための染料が含有されており、赤外線吸収インキと赤外線反射インキに含まれる赤外線を吸収及び反射する顔料の粒径分布が同等であることを特徴とする。 The ink set for verification according to the present invention includes an infrared absorbing ink containing an infrared absorbing pigment having a high light absorption rate in the infrared region, an infrared reflecting ink containing an infrared reflecting pigment having a high reflectance or a low light absorption rate in the infrared region, and The infrared absorbing ink or the infrared reflecting ink containing either one of the infrared absorbing pigment and the infrared reflecting pigment as a basic color and the other pigment contains a dye for making the basic color the same color. The particle size distribution of the pigment that absorbs and reflects the infrared rays contained in the infrared absorbing ink and the infrared reflecting ink is equal.
上記構成において、好ましくは、赤外線吸収顔料と赤外線反射顔料との粒径分布は、最小粒径の対比率が0.9以上であり、最大粒径の対比率が0.9以上であって、かつ個数平均粒子径の対比率が0.9以上である。
赤外線吸収インキ及び赤外線反射インキには、好ましくは、基本色と異なる色にするための着色剤が添加されている。
赤外線吸収顔料は、好ましくはアンチモン錫からなり、また、赤外線反射顔料は、好ましくは酸化チタンからなる。
In the above configuration, preferably, the particle size distribution of the infrared absorbing pigment and the infrared reflective pigment has a minimum particle size ratio of 0.9 or more and a maximum particle size ratio of 0.9 or more, The ratio of the number average particle diameter is 0.9 or more.
The infrared absorbing ink and the infrared reflecting ink are preferably added with a colorant for making the color different from the basic color.
The infrared absorbing pigment is preferably made of antimony tin, and the infrared reflecting pigment is preferably made of titanium oxide.
上記構成によれば、赤外線で照合でき、明度の高い照合用インキを実現できる。赤外線を吸収する顔料及び反射する顔料の粒径分布を同等としたことにより、インキ被膜の透過度もほぼ同率になり、その色が印刷基材等の外的要因による影響を受けない照合用インキセットが得られる。 According to the said structure, it can collate with infrared rays and can implement | achieve the collation ink with high brightness. By making the particle size distribution of the pigment that absorbs infrared rays and the pigment that reflects it equal, the transparency of the ink coating will be almost the same, and the color will not be affected by external factors such as the printing substrate. A set is obtained.
本発明の赤外線吸収インキ及び赤外線反射インキからなる照合用インキセットの製造方法は、
(1)赤外線領域で光吸収率が高い赤外線吸収顔料と赤外線領域で反射率が高いかまたは光吸収率が低い赤外線反射顔料との粒径分布を同等のものとする工程、
(2)工程(1)で得た赤外線吸収顔料を含む赤外線吸収インキを製造する工程、
(3)工程(1)で得た赤外線反射顔料を含む赤外線反射インキを製造する工程、を含み、
赤外線吸収顔料または赤外線反射顔料の何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキを製造する工程(2)または(3)において、染料を添加して基本色と同色とすることを特徴とする。
The method for producing a collating ink set comprising the infrared absorbing ink and infrared reflecting ink of the present invention,
(1) A step of making the particle size distributions of an infrared absorbing pigment having a high light absorption rate in the infrared region and an infrared reflecting pigment having a high reflectance or a low light absorption rate in the infrared region equivalent.
(2) a step of producing an infrared absorbing ink containing the infrared absorbing pigment obtained in step (1),
(3) a step of producing an infrared reflective ink containing the infrared reflective pigment obtained in step (1),
In the step (2) or (3) for producing an infrared absorbing ink or an infrared reflecting ink containing either one of the infrared absorbing pigment or the infrared reflecting pigment as a basic color and adding the other pigment, a basic color is added. It is characterized by having the same color.
本発明の赤外線吸収インキ及び赤外線反射インキからなる照合用インキセットの別の製造方法は、
(1)赤外線領域で光吸収率が高い赤外線吸収顔料を準備する工程、
(2)赤外線領域で反射率が高いかまたは光吸収率が低く、工程(1)で準備した赤外線吸収顔料と同等の粒径分布を有する赤外線反射顔料を準備する工程、
(3)工程(1)で準備した赤外線吸収顔料を含む赤外線吸収インキを製造する工程、
(4)工程(2)で準備した赤外線反射顔料を含む赤外線反射インキを製造する工程、を含み、
赤外線吸収顔料または赤外線反射顔料の何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキを製造する工程(3)または(4)において、染料を添加して基本色と同色とすることを特徴とする。
Another method for producing a collating ink set comprising the infrared absorbing ink and infrared reflecting ink of the present invention is as follows:
(1) preparing an infrared absorbing pigment having a high light absorption rate in the infrared region;
(2) a step of preparing an infrared reflective pigment having a particle size distribution equivalent to that of the infrared absorbing pigment prepared in step (1), having a high reflectance in the infrared region or a low light absorption rate;
(3) A step of producing an infrared absorbing ink containing the infrared absorbing pigment prepared in step (1),
(4) producing an infrared reflecting ink containing the infrared reflecting pigment prepared in step (2),
In the step (3) or (4) for producing an infrared absorbing ink or an infrared reflecting ink containing either of the infrared absorbing pigment or the infrared reflecting pigment as a basic color and the other pigment, a basic color by adding a dye It is characterized by having the same color.
上記構成において、好ましくは、赤外線吸収顔料と赤外線反射顔料との粒径分布は、最小粒径の対比率が0.9以上であり、最大粒径の対比率が0.9以上であって、かつ個数平均粒子径の対比率が0.9以上である。
赤外線吸収インキ及び赤外線反射インキには、好ましくは、基本色と異なる色にするための着色剤が添加されている。
赤外線吸収顔料は、好ましくはアンチモン錫からなり、また、赤外線反射顔料は、好ましくは酸化チタンからなる。
In the above configuration, preferably, the particle size distribution of the infrared absorbing pigment and the infrared reflective pigment has a minimum particle size ratio of 0.9 or more and a maximum particle size ratio of 0.9 or more, The ratio of the number average particle diameter is 0.9 or more.
The infrared absorbing ink and the infrared reflecting ink are preferably added with a colorant for making the color different from the basic color.
The infrared absorbing pigment is preferably made of antimony tin, and the infrared reflecting pigment is preferably made of titanium oxide.
上記構成によれば、基本色とは異なる色を呈するように、同じ種類で、同じ量の着色剤で着色して、基本色とは異なる同色の赤外線吸収インキ及び赤外線反射インキを調肉することができる。つまり、基本色インキセットの色合わせさえ行えば、印刷物に必要な色合わせは、同じ種類の着色剤であれば、赤外線吸収インキ及び赤外線反射インキに対する組成割合(重量%)が同じようにすればよい。したがって、従来の赤外線インキとは異なり、基材毎に赤外線吸収インキと赤外線反射インキの着色剤を調製する必要がなくなる。これにより、本発明の照合用インキセットの製造方法によれば、赤外線で照合でき、かつ、明度の高い照合用インキセットを製造する場合に、基材毎に色合わせをする必要がなくなり、明度が高く赤外線で照合することができる照合用インキセットを低コストで製造することができる。 According to the said structure, it colors with the same kind and the same quantity of coloring agent so that a color different from a basic color may be exhibited, and it prepares infrared absorbing ink and infrared reflective ink of the same color different from a basic color Can do. In other words, as long as the color matching of the basic color ink set is performed, the color matching required for the printed material is the same kind of colorant, as long as the composition ratio (% by weight) to the infrared absorbing ink and the infrared reflecting ink is the same. Good. Therefore, unlike conventional infrared inks, it is not necessary to prepare colorants for infrared absorbing ink and infrared reflecting ink for each substrate. Thereby, according to the manufacturing method of the collation ink set of the present invention, when producing a collation ink set that can be collated with infrared rays and has high brightness, it is not necessary to perform color matching for each substrate. Therefore, it is possible to produce a collating ink set that can be collated with infrared rays at a low cost.
本発明の赤外線吸収インキと赤外線反射インキとからなる照合用インキセットに含まれる顔料の粒径分布を同等とし、この照合用インキセットを印刷物に用いることで、印刷基材やビヒクルに応じて調肉する必要がなくなる。また、赤外線吸収インキ及び赤外線反射インキからなる照合用インキセットの製造においても、インキを印刷して色合せするという作業を行わなくても印刷した状態で同じ色を呈するインキを得ることができるので、作業効率を飛躍的に向上させることができる。 By making the particle size distribution of the pigments contained in the collating ink set comprising the infrared absorbing ink and the infrared reflecting ink of the present invention equal, and using this collating ink set for the printed matter, it is adjusted according to the printing substrate and vehicle. No need to meat. Also, in the production of a collating ink set consisting of infrared absorbing ink and infrared reflecting ink, it is possible to obtain an ink that exhibits the same color in the printed state without having to perform the operation of printing and color matching the ink. , Work efficiency can be dramatically improved.
以下に、図面を参照して本発明の実施の態様について詳細に説明する。
図1は、本発明の印刷物の構造を模式的に示す断面図である。図1に示すように、本発明の印刷物1は、被印刷物となる基材2上に、赤外線吸収インキ層3と、赤外線吸収インキと同じ色の赤外線反射インキ層4とからなる印刷パターンを有している。赤外線吸収インキ及び赤外線反射インキからなる組み合わせを照合用インキセットと呼ぶ。
Embodiments of the present invention will be described below in detail with reference to the drawings.
FIG. 1 is a cross-sectional view schematically showing the structure of the printed matter of the present invention. As shown in FIG. 1, the printed
基材1は、赤外線吸収インキ及び赤外線反射インキで印刷できる素材であれば何でもよく、例えば、紙、プラスチックシート、プラスチックフィルム、布、合成紙、セラミック板、木材、ガラスなどの種々の素材を用いることができる。
The
照合用インキセットにおいて、赤外線吸収インキは赤外線領域で光吸収の高い顔料(以下、適宜に赤外線吸収顔料と呼ぶ)を含み、赤外線反射インキは赤外線領域で反射率が高いかまたは光吸収率の低い顔料(以下、適宜に赤外線反射顔料と呼ぶ)を含んでいる。これらの赤外線吸収顔料及び赤外線反射顔料は、それぞれ明度が高い顔料を用い、何れか一方の顔料の色を基本色とする。 In the reference ink set, the infrared absorbing ink contains a pigment having high light absorption in the infrared region (hereinafter referred to as an infrared absorbing pigment as appropriate), and the infrared reflecting ink has high reflectance or low light absorption in the infrared region. It contains a pigment (hereinafter referred to as an infrared reflective pigment as appropriate). Each of these infrared absorbing pigments and infrared reflecting pigments is a pigment having high brightness, and the color of one of the pigments is a basic color.
他方の顔料を含む赤外線吸収インキまたは赤外線反射インキには、基本色と色を同色とするための染料が添加される。つまり、赤外線を吸収する顔料と赤外線を反射する顔料の基本色を合わせておく。この場合、顔料よりも粒子が極めて小さく、粒径を無視できる染料を好適に用いることができる。
なお、以下の説明においては、赤外線を吸収する顔料の色を基本色とし、赤外線を反射する顔料に染料を添加するものとする。
A dye for making the basic color the same color is added to the infrared absorbing ink or the infrared reflecting ink containing the other pigment. That is, the basic colors of the pigment that absorbs infrared rays and the pigment that reflects infrared rays are matched. In this case, it is possible to suitably use a dye that has extremely smaller particles than the pigment and can ignore the particle size.
In the following description, it is assumed that the color of a pigment that absorbs infrared rays is a basic color, and a dye is added to the pigment that reflects infrared rays.
赤外線吸収インキ層3に用いる赤外線吸収インキは、赤外線領域で光吸収率が高い顔料と、媒質(以下、適宜にビヒクルと呼ぶ)と、必要に応じて添加される補助剤と、から構成されており、さらに赤外線吸収インキ層3を可視光で視認できる基本色と異なる色とするための着色剤が、添加されている。
The infrared absorbing ink used for the infrared absorbing
赤外線吸収インキを明度の高い色とするための顔料としては、SnO2とSbO3とからなるアンチモン錫やITO(インジウムティンオキサイド)などを用いることができる。アンチモン錫と発明者等が入手した他の赤外線吸収顔料との赤外線反射スペクトルを比較すると、アンチモン錫の赤外線吸収率が最も高かった。したがって、赤外線吸収インキ用の顔料としては、アンチモン錫を好適に用いることができる。 Antimony tin or ITO (indium tin oxide) composed of SnO 2 and SbO 3 can be used as a pigment for making the infrared absorbing ink have a high brightness color. When comparing the infrared reflection spectra of antimony tin and other infrared absorbing pigments obtained by the inventors, the infrared absorption rate of antimony tin was the highest. Therefore, antimony tin can be suitably used as a pigment for infrared absorbing ink.
赤外線反射インキ層4に用いる赤外線反射インキは、赤外線領域で反射率が高いかまたは光吸収率が低い顔料と上記基本色に合わせるための染料などからなる着色剤と、媒質と、必要に応じて添加する補助剤と、から構成されており、さらに赤外線反射インキ層4が可視光で視認できる基本色と異なる色とするための着色剤が、添加されている。この着色剤は、赤外線吸収インキで用いるのと同じ種類で、同じ量の着色剤を使用することができる。
The infrared reflective ink used for the infrared
赤外線領域で反射率が高い顔料は、赤外線を反射する明度の高い顔料であれば何でもよく、具体的例を示すと、TiO2(酸化チタン)、酸化亜鉛、硫化亜鉛、酸化ジルコニウム等が挙げられ、特に好ましくは酸化チタンである。酸化チタンは工業材料として広く普及しており、様々な粒度を有する酸化チタンが容易に入手でき、扱い易いという利点がある。 The pigment having a high reflectance in the infrared region may be any pigment having a high brightness that reflects infrared rays. Specific examples include TiO 2 (titanium oxide), zinc oxide, zinc sulfide, and zirconium oxide. Particularly preferred is titanium oxide. Titanium oxide is widely used as an industrial material, and has the advantage that titanium oxide having various particle sizes is easily available and easy to handle.
赤外線吸収インキ用の顔料としてアンチモン錫を用い、赤外線反射インキ用の顔料として酸化チタンを用いた場合の基本色の色合わせの例について説明する。アンチモン錫は薄い灰色を呈する。一方、酸化チタンは白色を呈する。このため、赤外線反射インキの顔料となる酸化チタンに染料を添加して、アンチモン錫と同色にすることができる。 An example of basic color matching when antimony tin is used as a pigment for infrared absorbing ink and titanium oxide is used as a pigment for infrared reflecting ink will be described. Antimony tin is light gray. On the other hand, titanium oxide exhibits a white color. For this reason, a dye can be added to the titanium oxide used as a pigment of infrared reflective ink, and it can be made the same color as antimony tin.
上記着色剤は、赤外線吸収インキ及び赤外線反射インキの色を基本色以外の色にするために添加され、顔料や染料を用いることができる。この顔料や染料は、印刷用であれば何を用いてもよく、特に制限はない。ただし、赤外線吸収インキに添加する着色剤は、赤外線を吸収する材料が好ましい。逆に、赤外線反射インキに添加する着色剤は、赤外線を反射する材料が好ましい。 The colorant is added to change the color of the infrared absorbing ink and the infrared reflecting ink to a color other than the basic color, and a pigment or a dye can be used. Any pigment or dye may be used as long as it is for printing, and is not particularly limited. However, the colorant added to the infrared absorbing ink is preferably a material that absorbs infrared rays. Conversely, the colorant added to the infrared reflecting ink is preferably a material that reflects infrared rays.
ビヒクルは、特に制限はなく、用いる印刷法、印刷版、印刷機、被印刷物、インキ成分及び状態、インキの乾燥に応じて、植物油、加工油、鉱油のような油類、天然樹脂、加工樹脂、合成樹脂等の樹脂類、脂肪族炭化水素系溶剤、芳香族炭化水素系溶剤、アルコール系溶剤、エステル系溶剤、ケトン系溶剤、グリコール系溶剤等を用いることできる。 The vehicle is not particularly limited, and depending on the printing method used, printing plate, printing press, printing material, ink components and state, drying of the ink, oils such as vegetable oil, processing oil, mineral oil, natural resin, processing resin Resins such as synthetic resins, aliphatic hydrocarbon solvents, aromatic hydrocarbon solvents, alcohol solvents, ester solvents, ketone solvents, glycol solvents and the like can be used.
補助剤は、乾燥度調整剤、粘稠度調節剤、その他の調製剤として裏移り防止剤、防かび剤、消泡剤、可塑剤、グロスワニス、安定剤、皮張防止剤などを必要に応じて添加してもよい。 Adjuvants include dryness adjusters, consistency adjusters, and other preparations such as anti-set-off agents, fungicides, antifoaming agents, plasticizers, gloss varnishes, stabilizers, and anti-skinning agents as needed. It may be added.
印刷物1の特徴は、赤外線吸収インキ層3及び赤外線反射インキ層4を目視したときに、基材の材質やビヒクルの色によらず、同じ色を呈するように、赤外線吸収インキ層3及び赤外線反射インキ層にそれぞれ含有される赤外線吸収顔料と赤外線反射顔料の粒径分布を同等とすることにある。本発明において、「顔料の粒径分布が同等である」とは、赤外線吸収インキに含まれる赤外線吸収顔料の粒径分布と赤外線反射インキに含まれる赤外線反射顔料の粒径分布が、それぞれ近似していることを意味している。
具体的には、
(1)粒径の最小粒径の対比率が0.9以上であり、
(2)最大粒径の対比率が0.9以上であって、かつ、
(3)個数平均粒子径の対比率が0.9以上であることを必要とする。
The feature of the printed
In particular,
(1) The ratio of the minimum particle size to the particle size is 0.9 or more,
(2) The ratio of maximum particle size is 0.9 or more, and
(3) The ratio of the number average particle diameter needs to be 0.9 or more.
顔料の粒径分布は、例えば、レーザ光を粒子に照射し、その散乱光強度から粒子径や粒度分布を測定するレーザ回折・散乱法により求めることができる。
図2は、赤外線吸収インキ層3及び赤外線反射インキ層4に用いる顔料の粒度分布を示す模式図である。図2の横軸は粒径(任意目盛)であり、縦軸は粒子数(任意目盛)である。顔料Aは赤外線吸収インキの顔料、顔料Bは赤外線反射吸収インキの顔料である。例えば、定容積の2つの顔料A,Bの粒度が図2に示すような分布をしている場合、対比率は以下のようにして求めることができる。
The particle size distribution of the pigment can be determined, for example, by a laser diffraction / scattering method in which particles are irradiated with laser light and the particle size and particle size distribution are measured from the intensity of the scattered light.
FIG. 2 is a schematic diagram showing the particle size distribution of pigments used in the infrared absorbing
(顔料Aの最小、最大又は個数平均粒子径)<(顔料Bの最小、最大又は個数平均粒子径)の場合
最小粒径の対比率=(顔料Aの最小粒径)/(顔料Bの最小粒径)≧0.9
最大粒径の対比率=(顔料Aの最大粒径)/(顔料Bの最大粒径)≧0.9
個数平均粒子径の対比率=(顔料Aの個数平均粒子径)/(顔料Bの個数平均粒子径)≧0.9
(Minimum, maximum or number average particle diameter of pigment A) <(Minimum, maximum or number average particle diameter of pigment B) Contrast of minimum particle diameter = (minimum particle diameter of pigment A) / (minimum of pigment B) Particle size) ≧ 0.9
Ratio of maximum particle diameter = (maximum particle diameter of pigment A) / (maximum particle diameter of pigment B) ≧ 0.9
Ratio of number average particle diameter = (number average particle diameter of pigment A) / (number average particle diameter of pigment B) ≧ 0.9
(顔料Aの最小、最大又は個数平均粒子径)>(顔料Bの最小、最大又は個数平均粒子径)の場合
最小粒径の対比率=(顔料Bの最小粒径)/(顔料Aの最小粒径)≧0.9
最大粒径の対比率=(顔料Bの最大粒径)/(顔料Aの最大粒径)≧0.9
個数平均粒子径の対比率=(顔料Bの個数平均粒子径)/(顔料Aの個数平均粒子径)≧0.9
When (minimum, maximum or number average particle diameter of pigment A)> (minimum, maximum or number average particle diameter of pigment B) contrast of minimum particle diameter = (minimum particle diameter of pigment B) / (minimum of pigment A) Particle size) ≧ 0.9
Ratio of maximum particle diameter = (maximum particle diameter of pigment B) / (maximum particle diameter of pigment A) ≧ 0.9
Ratio of number average particle diameter = (number average particle diameter of pigment B) / (number average particle diameter of pigment A) ≧ 0.9
すなわち、最小粒径と最大粒径の差が10%以内であって、個数平均粒子径の対比率が0.9以上であれば、顔料Aと顔料Bは、粒径分布が同等であると定義する。 That is, if the difference between the minimum particle size and the maximum particle size is within 10% and the ratio of the number average particle size is 0.9 or more, the pigment A and the pigment B have the same particle size distribution. Define.
図3は、図1の印刷物1のパターンを模式的に示す平面図である。図では、赤外線吸収インキ層3と赤外線反射インキ層4の目視できない境界5を点線で示している。本発明の印刷物1は、赤外線吸収インキ層3及び赤外線反射インキ層4に用いる顔料の粒度分布を上記のように設定した場合には、基材2の材質によらず目視ではその境界5が識別できない。
FIG. 3 is a plan view schematically showing the pattern of the printed
上記の印刷パターンの色は、赤外線吸収インキ層3と赤外線反射インキ層4に添加された着色剤で決まるが、印刷物1の用途や意匠(デザイン)に応じて、その色合わせの程度は調整してもよい。同じ色ではあっても、隣接する印刷パターンの場合と、印刷物1の中の離れた位置の印刷パターンとの場合には、要求される色合わせの厳密さは変わる可能性がある。つまり、前者の場合には色合わせを極めて厳密に行う必要がある。後者の場合にはほぼ同じ色に視認できるという程度の色合わせで済むかもしれない。この後者の場合には、同じ色を配置する印刷パターンの位置が異なるので、隣接して印刷パターンを配置する場合に比較すると多少の色の違いは目立たなくすることができる。
The color of the printing pattern is determined by the colorant added to the infrared absorbing
赤外線吸収インキ層3及び赤外線反射インキ層4に用いる顔料の粒度分布が上記(1)〜(3)の条件外の場合には、基材2の材質により赤外線吸収インキ層3及び赤外線反射インキ層4との境界が目視で識別できる場合がある。
図4は、印刷物10及び10Aの赤外線吸収インキ層及び赤外線反射インキ層に用いる顔料の粒度分布を上記の条件外に設定した場合の印刷パターンを模式的に示す平面図であり、(A)及び(B)は、それぞれ、基材が異なる場合を示している。
図4(A)は、図3に示した基材2に、顔料の粒度分布を上記の条件外に設定したときに、赤外線吸収インキ層13及び赤外線反射インキ層14が同色となるように顔料を調製した場合の印刷パターンである。この場合には、赤外線吸収インキ層13及び赤外線反射インキ層14との境界5は、目視では判別できない。
When the particle size distribution of the pigment used in the infrared absorbing
FIG. 4 is a plan view schematically showing a printing pattern when the particle size distribution of the pigment used in the infrared absorbing ink layer and the infrared reflecting ink layer of the printed
FIG. 4 (A) shows the pigment so that the infrared absorbing
一方、図4(B)の印刷物10Aは、図4(A)の基材12を変えた以外は同じように印刷したときの印刷パターンである。赤外線吸収インキ層13及び赤外線反射インキ層14との境界6は目視で判別でき、この場合、境界6を実線で示している。したがって、この場合には、図4(A)に示した基材2の場合と同じ赤外線吸収インキ層13及び赤外線反射インキ層14の組成を使用できない。つまり、基材12に合わせて赤外線吸収インキ層13及び赤外線反射インキ層14の着色剤の組成を新たに調製する必要が生じる。
On the other hand, 10A of printed matter of FIG. 4 (B) is a printing pattern when it prints similarly except having changed the
本発明によれば、上記のような顔料及び着色剤の条件とすることにより、材質の異なる基材2上に印刷した場合に赤外線吸収インキ層3と赤外線反射インキ層4の境目5で色差が生じない印刷物1を提供することができる。このため、基材2を代える度に赤外線吸収インキ3と赤外線反射インキ4の色を調製する作業が不要となる。
According to the present invention, by using the above-described conditions for the pigment and the colorant, there is a color difference at the
次に、本発明の実施形態による赤外線吸収インキ3と赤外線反射インキ4とからなる照合用インキセットの製造方法について説明する。
本発明の赤外線吸収インキ及び赤外線反射インキからなる照合用インキセットの製造方法の一つは、
(1)赤外線領域での光吸収率が高い赤外線吸収顔料と赤外線領域での反射率が高いかまたは光吸収率が低い赤外線反射顔料との粒径分布を同等のものとする工程、
(2)工程(1)で得た赤外線吸収顔料と媒質と着色剤と必要に応じて添加する補助剤と、を含む赤外線吸収インキを製造する工程、
(3)工程(1)で得た赤外線反射顔料と、媒質と着色剤と必要に応じて添加する補助剤と、を含む赤外線反射インキを製造する工程、
を含む製造方法である。
Next, the manufacturing method of the collation ink set which consists of the infrared
One of the methods for producing a collating ink set comprising the infrared absorbing ink and the infrared reflecting ink of the present invention is:
(1) A step of making the particle size distributions of an infrared absorbing pigment having a high light absorption rate in the infrared region and an infrared reflecting pigment having a high reflectance in the infrared region or a low light absorption rate equal.
(2) A step of producing an infrared absorbing ink comprising the infrared absorbing pigment obtained in step (1), a medium, a colorant, and an auxiliary agent added as necessary.
(3) A step of producing an infrared reflective ink comprising the infrared reflective pigment obtained in the step (1), a medium, a colorant, and an auxiliary agent added as necessary.
It is a manufacturing method containing.
さらに、別の製造方法は、
(1)赤外線領域での光吸収率が高い赤外線吸収顔料を準備する工程、
(2)赤外線領域での反射率が高いかまたは光吸収率が低く、上記工程(1)で準備した赤外線吸収顔料と同等の粒径分布を有する赤外線反射顔料を準備する工程、
(3)工程(1)で準備した赤外線吸収顔料と、媒質と着色剤と必要に応じて添加する補助剤と、を含む赤外線吸収インキを製造する工程、
(4)工程(2)で準備した赤外線反射顔料と、媒質と着色剤と必要に応じて添加する補助剤と、を含む赤外線反射インキを製造する工程、
を含む製造方法である。
Furthermore, another manufacturing method is:
(1) preparing an infrared absorbing pigment having a high light absorption rate in the infrared region;
(2) a step of preparing an infrared reflective pigment having a particle size distribution equivalent to that of the infrared absorbing pigment prepared in the step (1), having a high reflectance in the infrared region or a low light absorption rate;
(3) A step of producing an infrared absorbing ink comprising the infrared absorbing pigment prepared in step (1), a medium, a colorant, and an auxiliary agent added as necessary.
(4) A step of producing an infrared reflective ink comprising the infrared reflective pigment prepared in the step (2), a medium, a colorant, and an auxiliary agent added as necessary.
It is a manufacturing method containing.
ここで、赤外線吸収インキ3と赤外線反射インキ4の顔料の種類とその粒径分布は、前述したとおりである。なお、顔料の粒度が上記の範囲にない場合には、顔料の粉砕・解砕手段としてビーズ(ボール)ミルを使用することで、最小粒径、最大粒径を調節することができる。
Here, the types of pigments and the particle size distribution of the infrared absorbing
上記製造方法においては、赤外線吸収インキ及び赤外線反射インキは、基本色を同じにするために、何れか一方の顔料には、染料が添加される。この工程は、着色剤を添加する前の工程で行うことが望ましい。この基本色となる赤外線反射顔料及び赤外線反射顔料に何れかに添加する染料の量が調肉されたインキを照合用インキセットの基本色インキセットと呼ぶ。 In the above production method, a dye is added to one of the pigments so that the infrared absorbing ink and the infrared reflecting ink have the same basic color. This step is desirably performed before the colorant is added. The infrared reflective pigment that is the basic color and the ink in which the amount of the dye added to the infrared reflective pigment is adjusted are referred to as a basic color ink set of the reference ink set.
上記工程で製造した基本色インキセットには、さらに、基本色とは異なる色を呈するように、同じ種類で、同じ量の着色剤で着色して、基本色とは異なる同色の赤外線吸収インキ及び赤外線反射インキを調肉することができる。つまり、基本色インキセットの色合わせさえ行えば、印刷物に必要な色合わせは、同じ種類の着色剤であれば、赤外線吸収インキ及び赤外線反射インキに対する組成割合(重量%)を同じようにすればよい。したがって、従来の赤外線インキとは異なり、基材毎に赤外線吸収インキと赤外線反射インキの着色剤を調製する必要がなくなる。 The basic color ink set manufactured in the above process is further colored with the same type and the same amount of colorant so as to exhibit a color different from the basic color, and the infrared absorbing ink of the same color different from the basic color and Infrared reflective ink can be prepared. In other words, as long as color matching of the basic color ink set is performed, the color matching required for the printed material is the same type of colorant, and the composition ratio (% by weight) with respect to the infrared absorbing ink and the infrared reflecting ink should be the same. Good. Therefore, unlike conventional infrared inks, it is not necessary to prepare colorants for infrared absorbing ink and infrared reflecting ink for each substrate.
以下、実施例によって、本発明をさらに詳細に説明する。
実施例1として、水色インキを調肉した。赤外線吸収インキの基本色インキは、アンチモン錫(SnO2:Sb2O3=99:1)を3gと、ビヒクルとして樹脂30g及び溶媒15gとの組成とした。樹脂は、塩酢ビ樹脂及びポリエステル樹脂を用い、その重量割合を1:1とした。塩酢ビ樹脂は、塩化ビニルと酢酸ビニルとの共重合物である。溶媒は、メチルエチルケトン(MEK)及びトルエンを用い、その重量割合を1:1とした。
Hereinafter, the present invention will be described in more detail by way of examples.
As Example 1, light blue ink was prepared. The basic color ink of the infrared absorbing ink was composed of 3 g of antimony tin (SnO 2 : Sb 2 O 3 = 99: 1), 30 g of resin as a vehicle, and 15 g of solvent. As the resin, vinyl acetate resin and polyester resin were used, and the weight ratio was 1: 1. The vinyl chloride resin is a copolymer of vinyl chloride and vinyl acetate. The solvent used was methyl ethyl ketone (MEK) and toluene, and the weight ratio was 1: 1.
赤外線反射インキの基本色インキは、酸化チタン(TiO2)を3gと、染料(桜宮化学社製、マイクロリス(登録商標、以下同じ))と、ビヒクルとして樹脂30g及び溶媒15gとの組成とした。樹脂及び溶媒の組成は、赤外線吸収インキと同じ組成とした。赤外線反射吸収インキの基本色と同じ色とするための染料は、マイクロリスレッド(1/100希釈)0.39gとマイクロリスブルー(1/100希釈)0.16gと、マイクロリスイエロー(1/100希釈)0.76gの組成とした。 The basic color ink of the infrared reflective ink has a composition of 3 g of titanium oxide (TiO 2 ), a dye (manufactured by Sakuramiya Chemical Co., Ltd., Microlith (registered trademark, hereinafter the same)), and 30 g of a resin as a vehicle and 15 g of a solvent. . The composition of the resin and the solvent was the same as that of the infrared absorbing ink. Dyes for making the same color as the basic color of the infrared reflection-absorbing ink are 0.39 g of microrethread (1/100 dilution), 0.16 g of microlith blue (1/100 dilution), microlith yellow (1 / The composition was 0.76 g.
上記組成とすることで、赤外線吸収インキ及び赤外線反射インキの基本色が同じ色となった。さらに、この基本色インキセットを水色とするために、マイクロリスブルー(1/100希釈)からなる着色剤を、インキ重量に対して5〜15%混入し、赤外線吸収インキ及び赤外線反射インキを調肉した。 By setting it as the said composition, the basic color of infrared rays absorption ink and infrared rays reflection ink became the same color. Furthermore, in order to make this basic color ink set light blue, a colorant consisting of microlith blue (1/100 dilution) is mixed in an amount of 5 to 15% with respect to the ink weight to prepare infrared absorbing ink and infrared reflecting ink. I got meat.
図5及び表1は、赤外線吸収インキに用いた顔料のアンチモン錫の粒度分布を示している。図5の横軸は粒径(μm)であり、左縦軸は頻度(%)であり、右縦軸は累積(%)である。測定にはレーザ回折・散乱法を用い、日機装株式会社製マイクロトラック粒度分析装置を使用した。
図5及び表1から明らかなように、アンチモン錫の粒径は、0.223μm〜3.27μmであり、個数平均粒子径は0.403μmであった。
As apparent from FIG. 5 and Table 1, the particle diameter of antimony tin was 0.223 μm to 3.27 μm, and the number average particle diameter was 0.403 μm.
図6及び表2は、赤外線反射インキに用いた顔料の酸化チタンの粒度分布を示している。図6の横軸は粒径(μm)、左縦軸は頻度(%)であり、右縦軸は累積(%)である。測定装置は図5の場合に用いた装置と同じである。
図6及び表2から明らかなように、酸化チタンの粒径は、0.223μm〜3.270μmであり、個数平均粒子径は0.422μmであった。
As is clear from FIG. 6 and Table 2, the particle diameter of titanium oxide was 0.223 μm to 3.270 μm, and the number average particle diameter was 0.422 μm.
上記測定結果から、アンチモン錫及び酸化チタンの最小及び最大粒径の対比率は1であり、個数平均粒子径の対比率は0.955となり、アンチモン錫及び酸化チタンの粒径は、上記した顔料の条件を満たしていることが分かる。 From the above measurement results, the ratio of the minimum and maximum particle diameters of antimony tin and titanium oxide is 1, the ratio of the number average particle diameter is 0.955, and the particle diameters of antimony tin and titanium oxide are the above pigments. It can be seen that this condition is satisfied.
実施例2として、緑色インキを調肉した。赤外線の吸収用及び反射用インキの基本色を得るために用いた顔料や染料の組成は実施例1と同じとした。 As Example 2, green ink was prepared. The composition of the pigments and dyes used to obtain the basic colors of the infrared absorbing and reflecting inks was the same as in Example 1.
さらに、この基本色インキセットを緑色とするために、マイクロリスグリーン(1/100希釈)からなる着色剤をインキ重量に対して5〜15%混入し、実施例2の赤外線吸収インキ及び赤外線反射インキを調肉した。 Furthermore, in order to make this basic color ink set green, a colorant composed of microlith green (1/100 dilution) is mixed in an amount of 5 to 15% with respect to the ink weight, and the infrared absorbing ink and infrared reflection of Example 2 are mixed. The ink was prepared.
次に、実施例1及び2に対する比較例を説明する。
(比較例1)
比較例1で用いた赤外線吸収顔料は、実施例1の赤外線吸収顔料と同じアンチモン錫である。さらに、水色に着色するための着色剤として3種類の顔料を添加し、比較例1の水色の赤外線吸収インキを調肉した。表3は、比較例1の赤外線吸収インキに用いた顔料の組成及び添加比率を示している。顔料dは赤外線吸収顔料として用いたアンチモン錫であり、顔料a,b,cは着色用顔料である。
顔料a(TiO2、40.30%)
顔料b(Co2SiO4、13.4%)
顔料c((Zr,V)SiO4、9.40%)
顔料d(SnO2,Sb2O3、36.90%)
ここで、括弧内の最初の化学式は顔料成分を示し、数字は赤外線吸収インキ中の顔料の添加比率(重量%)を示している。
(Comparative Example 1)
The infrared absorbing pigment used in Comparative Example 1 is the same antimony tin as the infrared absorbing pigment of Example 1. Further, three kinds of pigments were added as colorants for coloring in light blue, and the light blue infrared absorbing ink of Comparative Example 1 was prepared. Table 3 shows the composition and addition ratio of the pigment used in the infrared absorbing ink of Comparative Example 1. Pigment d is antimony tin used as an infrared absorbing pigment, and pigments a, b, and c are coloring pigments.
Pigment a (TiO 2 , 40.30%)
Pigment b (Co 2 SiO 4 , 13.4%)
Pigment c ((Zr, V) SiO 4 , 9.40%)
Here, the first chemical formula in parentheses indicates the pigment component, and the numbers indicate the addition ratio (% by weight) of the pigment in the infrared absorbing ink.
比較例1で用いた赤外線反射顔料は、実施例1の赤外線反射顔料と同じ酸化チタンである。さらに、水色に着色するための着色剤として4種類の顔料を添加し、比較例1の水色の赤外線反射インキを調肉した。表3は、比較例1の赤外線反射インキに用いた顔料の組成及び添加比率を示している。顔料aは赤外線反射顔料として用いた酸化チタンであり、顔料b,c,d,eは着色用顔料である。顔料eは4種類の顔料から構成されている。
顔料a(TiO2、58.7%)
顔料b(Co2SiO4、21.40%)
顔料c((Zr,V)SiO4、15.00%)
顔料d(SnO2,Sb2O3、2.20%)
顔料e((Ni,Co,Fe)(Fe,Cr)2O4,(Co,Fe,Mn)(Fe,Cr,Mn)2O4,(Zn,Fe)(Fe,Cr)2O4,(Co,Fe)(Fe,Cr)2O4、2.70%)
ここで、括弧内の最初の化学式は顔料成分を示し、数字は赤外線反射インキ中の顔料の添加比率(重量%)を示している。
The infrared reflective pigment used in Comparative Example 1 is the same titanium oxide as the infrared reflective pigment of Example 1. Further, four types of pigments were added as colorants for coloring in light blue, and the light blue infrared reflective ink of Comparative Example 1 was prepared. Table 3 shows the composition and addition ratio of the pigment used in the infrared reflective ink of Comparative Example 1. Pigment a is titanium oxide used as an infrared reflecting pigment, and pigments b, c, d, and e are coloring pigments. The pigment e is composed of four types of pigments.
Pigment a (TiO 2 , 58.7%)
Pigment b (Co 2 SiO 4 , 21.40%)
Pigment c ((Zr, V) SiO 4 , 15.00%)
Pigment e ((Ni, Co, Fe) (Fe, Cr) 2 O 4 , (Co, Fe, Mn) (Fe, Cr, Mn) 2 O 4 , (Zn, Fe) (Fe, Cr) 2 O 4 , (Co, Fe) (Fe, Cr) 2 O 4 , 2.70%)
Here, the first chemical formula in the parentheses indicates the pigment component, and the numbers indicate the addition ratio (% by weight) of the pigment in the infrared reflective ink.
図7及び表4は、比較例1の赤外線吸収インキで用いた顔料、つまり、表3で示した組成の顔料全体の粒度分布を示している。図7の横軸は粒径(μm)であり、左縦軸は頻度(%)であり、右縦軸は累積(%)である。測定装置は図5の場合に用いた装置と同じである。
図7及び表4から明らかなように、比較例1の赤外線吸収インキで用いた顔料の粒径は0.375μm〜3.889μmであり、個数平均粒子径は0.602μmであった。
As is apparent from FIG. 7 and Table 4, the particle size of the pigment used in the infrared absorbing ink of Comparative Example 1 was 0.375 μm to 3.889 μm, and the number average particle size was 0.602 μm.
図8及び表5は、比較例1の赤外線反射インキで用いた顔料、つまり、表3で示した組成の顔料全体の粒度分布を示している。図8の横軸は粒径(μm)であり、左縦軸は頻度(%)であり、右縦軸は累積(%)である。測定装置は図5の場合に用いた装置と同じである。
図8及び表5から明らかなように、酸化チタンの粒径は、0.315μm〜2.313μmであり、個数平均粒子径は0.535μmであった。
As apparent from FIG. 8 and Table 5, the particle diameter of titanium oxide was 0.315 μm to 2.313 μm, and the number average particle diameter was 0.535 μm.
上記測定結果から、比較例1の赤外線吸収インキで用いた顔料と赤外線反射インキで用いた顔料との最小粒径の対比率は0.84であり、最大粒径の対比率は0.595であり、個数平均粒子径の対比率は0.89であった。したがって、比較例1の赤外線吸収インキで用いた顔料と赤外線反射インキで用いた顔料との粒径は、上記した本発明の顔料の条件を満たしていないことが分かる。 From the above measurement results, the minimum particle size ratio of the pigment used in the infrared absorbing ink of Comparative Example 1 and the pigment used in the infrared reflective ink is 0.84, and the maximum particle size ratio is 0.595. Yes, the ratio of the number average particle diameter was 0.89. Therefore, it can be seen that the particle diameters of the pigment used in the infrared absorbing ink of Comparative Example 1 and the pigment used in the infrared reflective ink do not satisfy the above-described conditions of the pigment of the present invention.
(比較例2)
比較例2で用いた赤外線吸収顔料は、実施例1の赤外線吸収顔料と同じアンチモン錫である。さらに、緑色に着色するための着色剤として3種類の顔料を添加し、比較例2の緑色の赤外線吸収インキを調肉した。表6は、比較例2の赤外線吸収インキに用いた顔料の組成及び添加比率を示している。顔料dは赤外線吸収顔料として用いたアンチモン錫であり、顔料a,f,gは着色用顔料である。顔料gは2種類の顔料から構成されている。
顔料a(TiO2、10.00%)
顔料d(SnO2,Sb2O3、33.90%)
顔料f((Zr,Pr)SiO4、53.20%)
顔料g((Zr,Pr)SiO4,(Co,Zn)(Cr,Al)2O4、2.90%)
ここで、括弧内の最初の化学式は顔料成分を示し、数字は赤外線吸収インキ中の顔料の添加比率(重量%)を示している。
The infrared absorbing pigment used in Comparative Example 2 is the same antimony tin as the infrared absorbing pigment of Example 1. Further, three kinds of pigments were added as colorants for coloring in green, and the green infrared absorbing ink of Comparative Example 2 was prepared. Table 6 shows the composition and addition ratio of the pigment used in the infrared absorbing ink of Comparative Example 2. Pigment d is antimony tin used as an infrared absorbing pigment, and pigments a, f, and g are coloring pigments. The pigment g is composed of two types of pigments.
Pigment a (TiO 2 , 10.00%)
Pigment f ((Zr, Pr) SiO 4 , 53.20%)
Pigment g ((Zr, Pr) SiO 4 , (Co, Zn) (Cr, Al) 2 O 4 , 2.90%)
Here, the first chemical formula in parentheses indicates the pigment component, and the numbers indicate the addition ratio (% by weight) of the pigment in the infrared absorbing ink.
比較例2で用いた赤外線反射顔料は、実施例1の赤外線反射顔料と同じ酸化チタンである。さらに、緑色に着色するための着色剤として4種類の顔料を添加し、比較例2の水色の赤外線反射インキを調肉した。表6は、比較例2の赤外線反射インキに用いた顔料の組成及び添加比率を示している。顔料aは赤外線反射顔料として用いた酸化チタンであり、顔料c,e,f,gは着色用顔料である。顔料eは4種類の顔料から、顔料gは2種類の顔料から構成されている。
顔料a(TiO2、16.60%)
顔料c((Zr,V)SiO4、2.20%)
顔料e((Ni,Co,Fe)(Fe,Cr)2O4,(Co,Fe,Mn)(Fe,Cr,Mn)2O4,(Zn,Fe)(Fe,Cr)2O4,(Co,Fe)(Fe,Cr)2O4、2.20%)
顔料f((Zr,Pr)SiO4、74.60%)
顔料g((Zr,Pr)SiO4,(Co,Zn)(Cr,Al)2O4、4.40%)
ここで、括弧内の最初の化学式は顔料成分を示し、数字は赤外線反射インキ中の顔料の添加比率(重量%)を示している。
The infrared reflective pigment used in Comparative Example 2 is the same titanium oxide as the infrared reflective pigment of Example 1. Further, four kinds of pigments were added as colorants for coloring in green, and the light blue infrared reflective ink of Comparative Example 2 was prepared. Table 6 shows the composition and addition ratio of the pigment used in the infrared reflective ink of Comparative Example 2. Pigment a is titanium oxide used as an infrared reflecting pigment, and pigments c, e, f, and g are coloring pigments. The pigment e is composed of four types of pigments, and the pigment g is composed of two types of pigments.
Pigment a (TiO 2 , 16.60%)
Pigment c ((Zr, V) SiO 4 , 2.20%)
Pigment e ((Ni, Co, Fe) (Fe, Cr) 2 O 4 , (Co, Fe, Mn) (Fe, Cr, Mn) 2 O 4 , (Zn, Fe) (Fe, Cr) 2 O 4 , (Co, Fe) (Fe, Cr) 2 O 4 , 2.20%)
Pigment f ((Zr, Pr) SiO 4 , 74.60%)
Pigment g ((Zr, Pr) SiO 4 , (Co, Zn) (Cr, Al) 2 O 4 , 4.40%)
Here, the first chemical formula in the parentheses indicates the pigment component, and the numbers indicate the addition ratio (% by weight) of the pigment in the infrared reflective ink.
比較例1と同様に、比較例2の赤外線吸収インキ及び赤外線反射インキで用いたそれぞれの顔料の粒度分布を測定した。その結果、比較例2の赤外線吸収インキで用いた顔料及び赤外線反射インキで用いた顔料の粒径は、上記した本発明の顔料の条件を満たしていないことが分かった。 Similar to Comparative Example 1, the particle size distribution of each pigment used in the infrared absorbing ink and the infrared reflecting ink of Comparative Example 2 was measured. As a result, it was found that the particle diameters of the pigment used in the infrared absorbing ink of Comparative Example 2 and the pigment used in the infrared reflecting ink did not satisfy the above-described conditions of the pigment of the present invention.
上記の調肉したインキは、印刷方式に応じて、樹脂の重量に対する上記インキ顔料の重量比率及びビヒクルの樹脂組成を変えた。 The above prepared ink changed the weight ratio of the ink pigment to the weight of the resin and the resin composition of the vehicle according to the printing method.
表7は、比較例1及び2の各インキにおいて、各印刷方式に対する赤外線吸収インキ及び赤外線反射インキの顔料の重量比率を示す表である。この場合、顔料の重量比率は樹脂に対する比率である。例えば、樹脂が100g、溶剤50g、顔料15gの場合に、顔料の重量比率を15重量%として示している。比較例1の場合、フレキソ用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ15重量%、10重量%とし、樹脂はアクリル系オリゴマーを用い、その色は黄色である。グラビア用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ32重量%、21重量%とし、樹脂はポリエステル又は塩酢ビを用い、その色は透明である。シルクUV用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ14重量%、8重量%とし、樹脂はロジン変性フェノールを用い、その色は白色である。シルク酸化重合用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ14重量%、9重量%とし、樹脂はロジン変性フェノールを用い、その色は透明である。
比較例2のインキの場合、各印刷方式で用いた樹脂は比較例1と同じである。
表7に示すように、フレキソ用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ14重量%、10重量%とした。グラビア用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ30重量%、23重量%とした。シルクUV用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ14重量%、8重量%とした。シルク酸化重合用には、赤外線吸収インキ及び赤外線反射インキの顔料の重量比率はそれぞれ14重量%、10重量%とした。
In the case of the ink of Comparative Example 2, the resin used in each printing method is the same as that of Comparative Example 1.
As shown in Table 7, for flexo, the weight ratios of the pigments of infrared absorbing ink and infrared reflecting ink were 14 wt% and 10 wt%, respectively. For gravure, the weight ratios of the pigments of the infrared absorbing ink and infrared reflecting ink were 30% by weight and 23% by weight, respectively. For silk UV, the weight ratios of the pigments of infrared absorbing ink and infrared reflecting ink were 14% by weight and 8% by weight, respectively. For silk oxidative polymerization, the pigment weight ratios of the infrared absorbing ink and infrared reflecting ink were 14 wt% and 10 wt%, respectively.
実施例1及び比較例1で調肉した水色の赤外線吸収インキ及び赤外線反射インキと実施例2及び比較例2で調肉した緑色の赤外線吸収インキ及び赤外線反射インキと、を基材2として上質紙やPETフィルム等のフィルムに、図1のようなパターンとなるようにバーコーターで展色し、色相差を目視で調べた。
High-quality paper using as a
実施例1及び2の赤外線吸収インキと赤外線反射インキの場合には、何れの基材でも色相差がなかった。
一方、比較例1及び比較例2のインキの場合には、紙や色のついたフィルムからなる基材の場合には、基材自体の色やその材質により色相差が生じた。さらに、透明なフィルムからなる基材の場合には、基材の下にある下地の色、つまり、基材の背景色と基材の材質により色相差が生じた。そのため、比較例1及び2の赤外線吸収インキ及び赤外線反射インキは、各基材毎に色相を同じにする調肉作業が必要であった。
In the case of the infrared absorbing ink and the infrared reflecting ink of Examples 1 and 2, there was no hue difference in any of the substrates.
On the other hand, in the case of the inks of Comparative Example 1 and Comparative Example 2, in the case of a base material made of paper or a colored film, a hue difference occurred depending on the color of the base material itself and its material. Further, in the case of a substrate made of a transparent film, a hue difference is caused by the color of the underlying layer under the substrate, that is, the background color of the substrate and the material of the substrate. For this reason, the infrared absorbing ink and the infrared reflecting ink of Comparative Examples 1 and 2 have to be prepared for the same hue for each substrate.
本発明は、上記実施の形態に限定されるものではなく、特許請求の範囲に記載した発明の範囲内で種々の変形が可能であり、例えば、赤外線吸収インキ及び赤外線反射インキの顔料組成や用いるビヒクルや着色剤などの添加剤は印刷物の目的に応じて設定することができ、それらも本発明の範囲内に含まれることはいうまでもない。 The present invention is not limited to the above-described embodiment, and various modifications are possible within the scope of the invention described in the claims. For example, the pigment composition and use of infrared absorbing ink and infrared reflecting ink Needless to say, additives such as a vehicle and a colorant can be set in accordance with the purpose of the printed matter, and these are also included in the scope of the present invention.
1:印刷物
2,12:基材
3,13:赤外線吸収インキ層
4,14:赤外線反射インキ層
5:赤外線吸収インキ層及び赤外線反射インキ層との目視できない境界
6:赤外線吸収インキ層及び赤外線反射インキとの目視できる境界
10,10A:顔料の粒度分布を本発明の条件外に設定した赤外線吸収インキ層及び赤外線反射インキ層を用いた印刷物
1: Printed
Claims (13)
上記赤外線吸収顔料と上記赤外線反射顔料との何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキには、上記基本色と色を同色とするための染料が含有されており、
上記赤外線吸収顔料の粒径分布と上記赤外線反射顔料の粒径分布とにおいて、最小粒径の対比率が0.9以上、最大粒径の対比率が0.9以上、かつ個数平均粒子径の対比率が0.9以上であることを特徴とする、印刷物。 An infrared-absorbing ink layer containing an infrared-absorbing pigment having a high light absorption rate in the infrared region, and an infrared-reflecting ink layer containing an infrared-reflecting pigment having a high reflectance or a low light absorption rate in the infrared region are formed on the substrate. Printed material,
One of the infrared absorbing pigment and the infrared reflecting pigment is used as a basic color, and the infrared absorbing ink or infrared reflecting ink containing the other pigment contains a dye for making the same color as the basic color. Has been
In the particle size distribution of the infrared absorbing pigment and the particle size distribution of the infrared reflective pigment, the ratio of the minimum particle diameter is 0.9 or more, the ratio of the maximum particle diameter is 0.9 or more, and the number average particle diameter is A printed matter having a contrast ratio of 0.9 or more .
上記赤外線吸収顔料と上記赤外線反射顔料との何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキには、上記基本色と色を同色とするための染料が含有されており、
上記赤外線吸収顔料の粒径分布と上記赤外線反射顔料の粒径分布とにおいて、最小粒径の対比率が0.9以上、最大粒径の対比率が0.9以上、かつ個数平均粒子径の対比率が0.9以上であることを特徴とする、照合用インキセット。 An infrared absorbing ink containing an infrared absorbing pigment having a high light absorption rate in the infrared region, and an infrared reflecting ink containing an infrared reflecting pigment having a high reflectance or a low light absorption rate in the infrared region,
One of the infrared absorbing pigment and the infrared reflecting pigment is used as a basic color, and the infrared absorbing ink or infrared reflecting ink containing the other pigment contains a dye for making the same color as the basic color. Has been
In the particle size distribution of the infrared absorbing pigment and the particle size distribution of the infrared reflective pigment, the ratio of the minimum particle diameter is 0.9 or more, the ratio of the maximum particle diameter is 0.9 or more, and the number average particle diameter is A matching ink set, wherein the contrast ratio is 0.9 or more .
(1)赤外線領域で光吸収率が高い赤外線吸収顔料の粒径分布と、赤外線領域で反射率が高いかまたは光吸収率が低い赤外線反射顔料との粒径分布とにおいて、最小粒径の対比率を0.9以上、最大粒径の対比率を0.9以上、かつ個数平均粒子径の対比率を0.9以上とする工程、
(2)上記工程(1)で得た赤外線吸収顔料を含む赤外線吸収インキを製造する工程、
(3)上記工程(1)で得た赤外線反射顔料を含む赤外線反射インキを製造する工程、を含み、
上記赤外線吸収顔料または上記赤外線反射顔料の何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキを製造する上記工程(2)または(3)において、染料を添加して上記基本色と同色とすることを特徴とする、照合用インキセットの製造方法。 A method for producing a collating ink set comprising an infrared absorbing ink and an infrared reflecting ink,
(1) A pair of minimum particle diameters in a particle size distribution of an infrared absorbing pigment having a high light absorption rate in the infrared region and a particle size distribution of an infrared reflecting pigment having a high reflectance or a low light absorption rate in the infrared region. A step in which the ratio is 0.9 or more, the maximum particle size is 0.9 or more, and the number average particle size is 0.9 or more ,
(2) A step of producing an infrared absorbing ink containing the infrared absorbing pigment obtained in the step (1),
(3) a step of producing an infrared reflective ink containing the infrared reflective pigment obtained in the step (1),
In step (2) or (3) above, a dye is added in the above step (2) or (3) for producing an infrared absorbing ink or an infrared reflecting ink containing either of the infrared absorbing pigment or the infrared reflecting pigment as a basic color and the other pigment. A method for producing a collating ink set, wherein the same color as the basic color is used.
(1)赤外線領域で光吸収率が高い赤外線吸収顔料を準備する工程、
(2)上記赤外線領域で反射率が高いかまたは光吸収率が低い赤外線反射顔料の粒径分布が、上記工程(1)で準備した赤外線吸収顔料の粒径分布に関し、最小粒径の対比率が0.9以上、最大粒径の対比率が0.9以上、かつ個数平均粒子径の対比率が0.9以上である赤外線反射顔料を準備する工程、
(3)上記工程(1)で準備した赤外線吸収顔料を含む赤外線吸収インキを製造する工程、
(4)上記工程(2)で準備した赤外線反射顔料を含む赤外線反射インキを製造する工程、を含み、
上記赤外線吸収顔料または上記赤外線反射顔料の何れか一方の色を基本色とし、他方の顔料を含む赤外線吸収インキまたは赤外線反射インキを製造する上記工程(3)または(4)において、染料を添加して上記基本色と同色とすることを特徴とする、照合用インキセットの製造方法。 A method for producing a collating ink set comprising an infrared absorbing ink and an infrared reflecting ink,
(1) preparing an infrared absorbing pigment having a high light absorption rate in the infrared region;
(2) particle size distribution of the infrared reflective pigment the infrared region is high reflectivity or light absorptivity is not low, relates the particle size distribution of the infrared absorbing pigment prepared in the above step (1), a pair of minimum particle size A step of preparing an infrared reflecting pigment having a ratio of 0.9 or more, a maximum particle size ratio of 0.9 or more, and a number average particle diameter ratio of 0.9 or more ;
(3) A step of producing an infrared absorbing ink containing the infrared absorbing pigment prepared in the step (1),
(4) producing an infrared reflective ink containing the infrared reflective pigment prepared in the step (2),
In step (3) or (4) above, a dye is added in the above step (3) or (4) for producing an infrared absorbing ink or an infrared reflecting ink containing either one of the infrared absorbing pigment or the infrared reflecting pigment as a basic color and the other pigment. A method for producing a collating ink set, wherein the same color as the basic color is used.
The method for producing a matching ink set according to any one of claims 9 to 11 , wherein the infrared reflective pigment is made of titanium oxide.