JP4916399B2 - Cool carpet - Google Patents
Cool carpet Download PDFInfo
- Publication number
- JP4916399B2 JP4916399B2 JP2007213522A JP2007213522A JP4916399B2 JP 4916399 B2 JP4916399 B2 JP 4916399B2 JP 2007213522 A JP2007213522 A JP 2007213522A JP 2007213522 A JP2007213522 A JP 2007213522A JP 4916399 B2 JP4916399 B2 JP 4916399B2
- Authority
- JP
- Japan
- Prior art keywords
- carpet
- base fabric
- phase change
- pile yarn
- change material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明は、清涼感のあるカーペットに関するものであり、人がカーペットの表面に触れたときに冷やりとした涼しさを感じるようにした、夏用のカーペットに関するものである。 The present invention relates to a refreshing carpet, and more particularly to a summer carpet that allows a person to feel a cool coolness when touching the surface of the carpet.
日本の住宅において、カーペットは１年を通じて多く使われるようになり、カーペットの上に座ったり、横になったりして寛ぐ家庭は多い。カーペットは、冬季には暖かさを求められ、夏季においては涼しく爽やかな感覚の得られるようなものが好まれる。この相反する性質を兼ね備えたカーペットは未だ存在していないが、冬季と夏季で、それぞれ異なる性質のカーペットを敷きかえるようにしているのが一般的である。特に夏季においては、夏用のカーペットとして、汗等の吸水性のよい綿カーペットや、イグサや籐の敷物を敷いて夏の暑さを凌ぐようにしていることが多い。 In Japanese homes, carpets are used frequently throughout the year, and many families relax by sitting or lying on the carpet. Carpets are required to be warm in the winter and cool and refreshing in the summer. Although carpets having these contradictory properties have not yet existed, it is common to replace carpets having different properties in winter and summer. In summer, in particular, as a carpet for summer, a cotton carpet with good water absorption such as sweat, rush and rattan rugs are often laid to surpass the heat of summer.
特許文献１においては、さらさらとした清涼感のあるカーペットを得るべく、単繊維断面の扁平率が３〜８で、該単繊維の繊度が５〜２５ｄｔｅｘのポリ乳酸繊維で構成されるポリ乳酸扁平捲縮糸を用いたカーペットが提案されている。 In Patent Document 1, in order to obtain a carpet with a refreshing and refreshing feeling, a flatness of polylactic acid composed of polylactic acid fibers having a flatness of 3 to 8 and a fineness of the single fiber of 5 to 25 dtex is obtained. Carpets using crimped yarn have been proposed.
また、特許文献２においては、水和熱が負である物質と特定の無機化合物との複合体を布帛に担持させたものは清涼性に優れ、夏用の衣服やタオルなどに有用な技術として提案されている。 Moreover, in patent document 2, what supported the composite of the substance with a negative heat of hydration and a specific inorganic compound on the cloth is excellent in coolness, and is useful technology for summer clothes, towels, etc. Proposed.
また、特許文献３においては、繊維製品に優れた接触冷感を付与すべく、融点が２５〜３７℃であり、潜熱の放出・吸収を伴って可逆的に固液相転移する潜熱蓄熱材を封入してなるマイクロカプセルを固着することによって、皮膚との接触時に心地よい冷感を与え、暑さによる不快感を低減する技術を開示している。しかしながら、これらの技術は、繊維形態を特殊な扁平形態にしてさらさら感を付与するカーペットの技術であったり、潜熱蓄熱材を利用して衣料用等の薄物の繊維表面に清涼感を与える技術ではあるが、厚みがあって空気を多く含み、断熱効果が大きな繊維集合体であるカーペットにおいては、保温効果が大きいことから、カーペットとしての清涼感、冷感を得られるような技術には到ってはいない。
本発明は、かかる技術的背景に鑑みてなされたものであって、人がカーペットの表面に触れたときに、確実に冷やりとした涼しさを感じられるようにした、夏用のカーペットを提供することを目的とする。 The present invention has been made in view of such a technical background, and provides a summer carpet that can surely feel a cool coolness when a person touches the surface of the carpet. The purpose is to do.
本発明者らは、このような課題を解決するために鋭意検討の結果、基布の表面側と、基布から上のパイル糸全体に相転移材料を封入したマイクロカプセルを固着させることにより、人がカーペットの表面に触れたときに、確実に冷やりとした涼しさを感じられるようにした夏用のカーペットが得られることを見出し本発明に到達した。前記目的を達成するために、本発明は以下の手段を提供する。 As a result of intensive studies to solve such problems, the inventors fixed the microcapsules encapsulating the phase change material on the surface side of the base fabric and the entire pile yarn above the base fabric, The present inventors have found that a summer carpet is obtained that is sure to feel cool when a person touches the surface of the carpet. In order to achieve the above object, the present invention provides the following means.
［１］パイル糸と基布からなる表皮層と、バッキング層とを含むカ−ペットにおいて、基布から上のパイル糸に相転移材料を封入したマイクロカプセルが固着されていることに特徴のある涼感カ−ペット。 [1] In a carpet including a skin layer composed of a pile yarn and a base fabric, and a backing layer, a microcapsule in which a phase change material is sealed is fixed to the pile yarn above the base fabric. Cool carpet.
［２］パイル糸と基布からなる表皮層と、バッキング層とを含むカ−ペットにおいて、基布表面と基布から上のパイル糸に相転移材料を封入したマイクロカプセルが固着されていることに特徴のある涼感カ−ペット。 [2] In a carpet including a skin layer composed of a pile yarn and a base fabric, and a backing layer, a microcapsule in which a phase change material is sealed is fixed to the surface of the base fabric and the pile yarn above the base fabric. A cool carpet with a distinctive character.
［３］前記相転移材料は、融点が２０〜３５℃で、マイクロカプセルに封入されている相転移材料であることに特徴のある前項１または２に記載の涼感カ−ペット。 [3] The cool-feeling carpet according to item 1 or 2, wherein the phase change material is a phase change material having a melting point of 20 to 35 ° C. and encapsulated in microcapsules.
［４］前記相転移材料は、融点が２０〜３５℃で、マイクロカプセルに封入されている相転移材料で、二種類以上の融点をもつ相転移材料であることに特徴のある前項１または２に記載の涼感カ−ペット。 [4] The phase change material according to item 1 or 2, wherein the phase change material is a phase change material having a melting point of 20 to 35 ° C. and encapsulated in a microcapsule and having two or more melting points. Cool feeling carpet described in 1.
［５］前記相転移材料が０．５０〜５０．０ｇ／ｍ２バインダー樹脂によってカ−ペットに固着していることに特徴のある前項１乃至４のいずれかに記載の涼感カ−ペット。 [5] The cool carpet according to any one of items 1 to 4 above, wherein the phase change material is fixed to the carpet with a binder resin of 0.50 to 50.0 g / m 2 .
［６］前記涼感カ−ペットにおいて、パイル糸が少なくとも綿を含んでいるパイル糸によって構成されることに特徴のある前項１乃至５のいずれかに記載の涼感カ−ペット。 [6] The cool feeling carpet according to any one of the above items 1 to 5, wherein the cool feeling carpet is constituted by a pile yarn including at least cotton.
［７］前記涼感カ−ペットにおいて、ＱＭＡＸ（接触温冷感値）が０．０８５ｊ／ｃｍ２・ｓｅｃより大きいことに特徴のある前項１乃至６のいずれかに記載の涼感カ−ペット。 [7] The cool feeling carpet according to any one of the above items 1 to 6, wherein the cool feeling carpet has a QMAX (contact thermal cooling value) larger than 0.085 j / cm 2 · sec.
［１］の発明では、パイル糸と基布からなる表皮層と、バッキング層とを含むカ−ペットにおいて、基布から上のパイル糸に相転移材料を封入したマイクロカプセルが固着されているので、人がカーペット表面のパイル糸に触れたとき、冷やりとした涼しさを感じることができる。 In the invention of [1], in a carpet including a skin layer composed of a pile yarn and a base fabric, and a backing layer, a microcapsule in which a phase change material is sealed is fixed to the pile yarn above the base fabric. When people touch the pile yarn on the carpet surface, they can feel the coolness.
［２］の発明では、パイル糸と基布からなる表皮層と、バッキング層とを含むカ−ペットにおいて、基布表面と基布から上のパイル糸に相転移材料を封入したマイクロカプセルが固着されているので、人がカーペット表面のどの部分に触れたとしても、冷やりとした涼しさを感じることができる。 In the invention of [2], in a carpet including a skin layer composed of a pile yarn and a base fabric, and a backing layer, a microcapsule in which a phase change material is sealed is fixed to the surface of the base fabric and the pile yarn above the base fabric. So, no matter where you touch the carpet surface, you can feel cool and cool.
［３］の発明では、融点が２０〜３５℃の相転移材料が、マイクロカプセルに封入されてカ−ペットに固着しているので、人体がカ−ペットに接触したときに相転移材料が融解し、そのとき人体から融解熱の移動がおこり、人は、カ−ペットを冷たく感じることができる。 In the invention of [3], since the phase transition material having a melting point of 20 to 35 ° C. is sealed in the microcapsule and fixed to the carpet, the phase transition material is melted when the human body comes into contact with the carpet. At that time, the heat of fusion moves from the human body, and the person can feel the carpet cold.
［４］の発明では、融点が２０〜３５℃で、マイクロカプセルに封入されている相転移材料において、二種類以上の融点をもつ相転移材料がマイクロカプセルに封入されてカ−ペットに固着しているので、気温が一つの相転移材料の融点に達していたとしても、他の融点をもつ相転移材料が溶融しないで残っており、人体がカ−ペットに接触したときに残っている相転移材料が融解し、そのとき人体から融解熱の移動がおこり、人は、カ−ペットを冷たく感じることができる。 In the invention of [4], in the phase change material encapsulated in the microcapsule having a melting point of 20 to 35 ° C., the phase change material having two or more melting points is encapsulated in the microcapsule and fixed to the carpet. Therefore, even if the temperature reaches the melting point of one phase change material, the phase change material having the other melting point remains unmelted and remains when the human body comes into contact with the carpet. The transition material melts, at which time the heat of fusion occurs from the human body and the person can feel the carpet cold.
［５］の発明では、相転移材料が０．５０〜５０．０ｇ／ｍ２バインダー樹脂によって固着しているので、十分な涼感能力を持ったカーペットとすることができる。 In the invention of [5], since the phase change material is fixed by 0.50 to 50.0 g / m 2 binder resin, the carpet can have a sufficient cool feeling ability.
［６］の発明では、パイル糸が少なくとも綿を含んでいるパイル糸によって構成されるので、吸湿性のよい綿繊維が、人体の汗等の水分をとることからサラッとした涼感のあるカーペットとすることができる。 In the invention of [6], since the pile yarn is composed of a pile yarn containing at least cotton, the hygroscopic cotton fiber absorbs moisture such as sweat of the human body, and thus has a smooth and cool carpet. can do.
［７］の発明では、ＱＭＡＸ（接触温冷感値）が０．０８５ｊ／ｃｍ２・ｓｅｃより大きいので、カーペットに肌が接触したとき冷感を確実に感じることができる。 In the invention of [7], since QMAX (contact thermal cooling value) is larger than 0.085 j / cm 2 · sec, it is possible to surely feel the cooling feeling when the skin comes into contact with the carpet.
次に、この発明に係る涼感カーペットの一実施形態を図面に基づいて説明する。この実施形態の涼感カーペット１は、パイル糸２と基布３とバッキング層４を含み、パイル糸２の全体と基布３のパイル糸側表面に相転移材料を封入したマイクロカプセル６がバインダー樹脂（図示せず）により固着されている。（図１参照）夏用のカーペットは、冬用のものに比べてパイル長が低く、ステッチが粗く目付の軽い傾向があるので、人がカーペット上に乗って手をついたとき、パイル糸だけでなく基布にも皮膚が接することがあるので、図１においては、基布表面と基布から上のパイル糸に相転移材料を封入したマイクロカプセル６を固着させている。また図１では、バッキング層４の保護やクッション性を付与するために不織布からなるセカンド基布５を積層している。 Next, an embodiment of a cool carpet according to the present invention will be described with reference to the drawings. The cool carpet 1 of this embodiment includes a pile yarn 2, a base fabric 3, and a backing layer 4, and a microcapsule 6 in which a phase change material is sealed on the entire pile yarn 2 and the pile yarn side surface of the base fabric 3 is a binder resin. (Not shown). (See Figure 1) Summer carpets have a lower pile length than those for winter, and the stitches are rough and tend to be lighter, so when people get on the carpet and touch their hands, only the pile yarn In addition, since the skin may also come into contact with the base fabric, in FIG. 1, the microcapsules 6 enclosing the phase change material are fixed to the surface of the base fabric and the pile yarn above the base fabric. Moreover, in FIG. 1, in order to provide protection and cushioning properties for the backing layer 4, a second base fabric 5 made of a nonwoven fabric is laminated.
相転移材料（ＰＣＭ）は、固相と液相との間で反復転換する材料で、融解、凝固するときに発現する熱を利用して、熱を蓄積、あるいは放出させて、相転移材料周辺の温度を制御するものである。相転移材料としては、パラフィンやワックス等の炭化水素化合物が好適に使用されるが特に限定しない。該相転移材料を封入したマイクロカプセルは市販されており、大和化学工業株式会社製プレサーモ、三木理研工業株式会社製蓄熱蓄冷マイクロカプセル等を挙げることができ、マイクロカプセルの組成としても、特に限定されなくて、一般に市販されているものでよい。 A phase change material (PCM) is a material that is repeatedly converted between a solid phase and a liquid phase, and uses heat generated when melting and solidifying to accumulate or release the heat, thereby surrounding the phase change material. The temperature is controlled. As the phase change material, hydrocarbon compounds such as paraffin and wax are preferably used, but are not particularly limited. Microcapsules encapsulating the phase change material are commercially available, and examples include prethermo manufactured by Daiwa Chemical Industry Co., Ltd., heat storage cold storage microcapsules manufactured by Miki Riken Kogyo Co., Ltd., and the composition of the microcapsules is also particularly limited. It is not necessary to use a commercially available product.
本発明で使用する相転移材料を封入したマイクロカプセルは、熱吸収のピーク温度（融点ともいう）または熱放散のピーク温度（凝固点ともいう）が２０〜３５℃の範囲内であるものが好ましい。人の体温は、３６〜３７℃であるが、手や足の表面温度はこれよりも低く３２〜３４℃といわれているので、２０〜３５℃で熱吸収のピーク温度（融点）となる相転移材料が好ましい。より好ましいピーク温度（融点）は、２５〜３２℃である。 The microcapsules encapsulating the phase change material used in the present invention preferably have a heat absorption peak temperature (also referred to as melting point) or a heat dissipation peak temperature (also referred to as freezing point) in the range of 20 to 35 ° C. Although the human body temperature is 36-37 ° C, the surface temperature of the hands and feet is said to be lower than this, 32-34 ° C, so the phase that becomes the peak temperature (melting point) of heat absorption at 20-35 ° C. Transition materials are preferred. A more preferable peak temperature (melting point) is 25 to 32 ° C.
熱吸収のピーク温度が低すぎる場合では、人体が接触する前に既に相転移材料が溶けてしまっており、人体が接触しても涼感効果を得ることはできない。また、熱吸収のピーク温度が高すぎる場合には、人体が接触しても、相転移材料が溶けないため、涼感効果を得ることはできない。 When the peak temperature of heat absorption is too low, the phase transition material has already melted before the human body comes into contact, and even if the human body comes into contact, a cool feeling effect cannot be obtained. In addition, when the peak temperature of heat absorption is too high, even if a human body comes into contact, the phase change material does not melt, so that a cool feeling effect cannot be obtained.
室温の高い部屋で本発明のカーペットを使用する場合は、二種類以上の融点をもつ相転移材料が有効である。例えば、融点が２５℃と３２℃の二種類の融点をもつ相転移材料を封入したマイクロカプセルを５０対５０の割合でパイル糸と基布に固着させた場合、夏の日の朝の室温が２０℃のときは、融点２５℃の相転移材料が有効に働き涼感効果を得ることができる。午後になって室温が上昇し、３０℃となった場合は、融点の低い相転移材料は、既に溶けてしまっており、３２℃の融点をもつ相転移材料の効果しか得ることができない。２５℃の融点をもつ相転移材料で全てを構成した場合、午前中は、涼感を感じられるが、午後は全く感じられない状況となる。また、３２℃の融点をもつ相転移材料で全てを構成した場合は、室温と融点の温度差が大きく、ほとんど涼感効果が得られないが、室温と融点の温度差が小さくなる午後には涼感を感じられるようになる。 When the carpet of the present invention is used in a room having a high room temperature, a phase change material having two or more melting points is effective. For example, when a microcapsule enclosing a phase change material having two melting points of 25 ° C. and 32 ° C. is fixed to a pile yarn and a base fabric at a ratio of 50:50, the room temperature in the morning of summer day is When the temperature is 20 ° C., a phase transition material having a melting point of 25 ° C. works effectively and a cool feeling effect can be obtained. When the room temperature rises to 30 ° C. in the afternoon, the phase transition material having a low melting point has already melted, and only the effect of the phase transition material having a melting point of 32 ° C. can be obtained. When all are composed of a phase change material having a melting point of 25 ° C., a cool feeling can be felt in the morning, but not in the afternoon at all. In addition, when all of the phase change materials having a melting point of 32 ° C. are used, the temperature difference between the room temperature and the melting point is large, and a cooling effect is hardly obtained. You will be able to feel
相転移材料を封入したマイクロカプセルは、０．５０〜５０．０ｇ／ｍ２バインダー樹脂によってカーペットの基布表面と基布から上のパイル糸に固着されるのが好ましい。０．５０ｇ／ｍ２を下回ると涼感効果を感じられない。また、５０．０ｇ／ｍ２を超えて固着しても、カーペットの風合が硬くなり、コストが上昇するだけで効果が伴わず好ましくない。より好ましくは、１〜２０．０ｇ／ｍ２の固着量がよい。 The microcapsules enclosing the phase change material are preferably fixed to the carpet base fabric surface and the pile yarn above the base fabric with 0.50 to 50.0 g / m 2 binder resin. If it is less than 0.50 g / m 2 , a cool feeling effect cannot be felt. Moreover, even if it exceeds 50.0 g / m < 2 >, the feel of a carpet will become hard and it will only increase cost, and it is not preferable. More preferably, a fixed amount of 1 to 20.0 g / m 2 is good.
また相転移材料を封入したマイクロカプセルの粒径は１〜５０μｍが好ましい。５０μｍを超えると、ザラツキ感や硬さが発現しカーペットの好ましい風合にならない。更に好ましい粒径は、５〜２５μｍである。 The particle size of the microcapsules enclosing the phase change material is preferably 1 to 50 μm. If it exceeds 50 μm, the feeling of roughness and hardness will be manifested, and the preferred texture of the carpet will not be achieved. A more preferable particle size is 5 to 25 μm.
バインダー樹脂としては、パイル糸２と基布表面に相転移材料を封入したマイクロカプセル６を強固に固着することが出来ればよいが、一般的には、例えばウレタン樹脂、自己架橋型アクリル樹脂、メタアクリル樹脂、シリコン樹脂、グリオキザール樹脂、ポリエステル樹脂、酢酸ビニル樹脂、塩化ビニリデン樹脂、ブタジエン樹脂、メラミン樹脂、エポキシ樹脂、アクリル−シリコン共重合体樹脂、スチレン−ブタジエン共重合体樹脂（ＳＢＲ）、エチレン−酢酸ビニル共重合体樹脂（ＥＶＡ）、イソブチレン無水マレイン酸共重合体樹脂、エチレン−スチレン−アクリレート−メタアクリレート共重合体樹脂等を挙げることができる。 As the binder resin, it is sufficient if the pile capsule 2 and the microcapsule 6 enclosing the phase change material can be firmly fixed to the surface of the base fabric. Generally, for example, urethane resin, self-crosslinking acrylic resin, Acrylic resin, silicone resin, glyoxal resin, polyester resin, vinyl acetate resin, vinylidene chloride resin, butadiene resin, melamine resin, epoxy resin, acrylic-silicone copolymer resin, styrene-butadiene copolymer resin (SBR), ethylene- Examples thereof include vinyl acetate copolymer resin (EVA), isobutylene maleic anhydride copolymer resin, and ethylene-styrene-acrylate-methacrylate copolymer resin.
パイル糸２と基布表面に相転移材料を封入したマイクロカプセル６を固着する方法は、バインダー樹脂溶液に浸透剤、相転移材料を封入したマイクロカプセル等を均一に分散させ、スプレー法やコーティング法など従来からある方法でカーペットのパイル糸側にパイル糸の上側から十分塗布し、乾燥処理してパイル糸と基布の表面に固着する。この時、浸透剤を混入しないとパイル表面に処理液が留まり、パイルの根元付近まで処理液が届かないことから、浸透剤を適度に使用することが好ましい。バインダー樹脂の乾燥手段は、加熱処理により乾燥させる方が望ましく、バッキング層の乾燥工程と同時に行うと効率的である。この時の加熱処理温度は、パイル糸と基布とバッキング層の素材や規格にもよるが、１００〜１８０℃とするのが好ましい。この温度での加熱処理によりパイル糸への固着性がより高まり、耐久性が一段と向上する。 The method of fixing the microcapsules 6 encapsulating the phase change material on the pile yarn 2 and the surface of the base fabric is to uniformly disperse the microcapsules encapsulating the penetrant and the phase change material in the binder resin solution. A conventional method such as application to the pile yarn side of the carpet from the upper side of the pile yarn is sufficiently applied, followed by drying treatment to adhere to the surface of the pile yarn and the base fabric. At this time, if the penetrant is not mixed, the treatment liquid remains on the surface of the pile, and the treatment liquid does not reach the vicinity of the pile root. Therefore, it is preferable to use the penetrant appropriately. The drying means for the binder resin is preferably dried by heat treatment, and is efficient when performed simultaneously with the drying process of the backing layer. The heat treatment temperature at this time is preferably 100 to 180 ° C., although it depends on the material and specifications of the pile yarn, the base fabric, and the backing layer. By heat treatment at this temperature, the adhesion to the pile yarn is further increased, and the durability is further improved.
また、前記相転移材料を封入したマイクロカプセルと浸透剤とバインダー樹脂とは、水に分散した水分散液として使用することができる。バインダー樹脂については水との間でエマルジョン状態を形成させるのがより好ましい。なお、分散媒としては、水以外にアルコール等も使用し得るが、水が好適である。水に分散させる順序としては、相転移材料を封入したマイクロカプセルを水に分散させておいてから、浸透剤、バインダー樹脂を分散せしめるのが、マイクロカプセルとバインダー樹脂をより均一に分散させる観点から好ましい。また、この水分散液に、分散剤、増粘剤などの各種添加剤を配合してもよい。 Moreover, the microcapsules, penetrant, and binder resin encapsulating the phase change material can be used as an aqueous dispersion dispersed in water. The binder resin is more preferably formed into an emulsion state with water. As the dispersion medium, alcohol or the like can be used in addition to water, but water is preferred. In order to disperse in water, the microcapsules encapsulating the phase change material are dispersed in water, and then the penetrant and binder resin are dispersed from the viewpoint of more evenly dispersing the microcapsules and binder resin. preferable. Moreover, you may mix | blend various additives, such as a dispersing agent and a thickener, with this aqueous dispersion.
本発明において、パイル糸２の素材としては特に限定されず、ポリエステル繊維、ポリアミド繊維、ポリプロピレン繊維、アクリル繊維、レ−ヨン繊維等の合成繊維からなるもの等を好適に使用でき、その他麻、綿、羊毛等の天然繊維からなるもの等も使用できる。中でも、綿は吸水性に優れていることから夏用のカーペットに多く使われており、本発明においても吸湿性のよい綿繊維が相転移材料を封入したマイクロカプセルの効果と相俟って、サラッとした涼感のあるカーペットとすることができる。パイルの形態としてもカットパイルであっても、ル−プパイルであってもよいが、ル−プパイルのほうが涼感は感じやすい。パイル糸２の目付についても、特に限定されないで、カーペットの形態をなすものであればよい。 In this invention, it does not specifically limit as a raw material of the pile thread | yarn 2, What consists of synthetic fibers, such as a polyester fiber, a polyamide fiber, a polypropylene fiber, an acrylic fiber, rayon fiber, etc. can be used conveniently, Other hemp, cotton Also, those made of natural fibers such as wool can be used. Among them, cotton is often used in summer carpets because of its excellent water absorption, combined with the effect of microcapsules in which cotton fibers with good hygroscopicity encapsulate a phase change material in the present invention, It can be a smooth and cool carpet. The pile may be a cut pile or a loop pile, but the loop pile has a cooler feeling. The basis weight of the pile yarn 2 is not particularly limited as long as it forms a carpet.
また、基布３としても、特に限定されるものではなく、ポリエステル繊維やポリプロピレン繊維、麻、綿等の天然繊維からなる織、編基布、不織布等通常使用される基布でよいが、中でも、綿基布は吸水性に優れていることから夏用のカーペット基布に多く使われており、本発明においても好ましい素材である。 Further, the base fabric 3 is not particularly limited, and may be a commonly used base fabric such as a woven fabric, a knitted base fabric, and a nonwoven fabric made of natural fibers such as polyester fiber, polypropylene fiber, hemp, and cotton. Cotton base fabrics are often used in carpet base fabrics for summer because of their excellent water absorption, and are also preferred materials in the present invention.
ＱＭＡＸは、一定面積、一定質量の純銅板（熱容量０．４１８５５ｊ／℃）に熱を蓄え、これが試料表面に接触した直後に、蓄えられた熱量が低温側の試料物体に移動する熱量のピーク値を測定した値をいうもので、ＱＭＡＸが大きいほど接触したときに冷たく感じ、小さいほど温かく感じる。 QMAX stores heat in a pure copper plate (heat capacity 0.41855j / ° C) with a constant area and a constant mass, and immediately after it contacts the sample surface, the stored heat amount moves to the low-temperature sample object. The larger the QMAX, the colder it feels when touched, and the smaller the QMAX, the warmer it feels.
次に、バッキング層５としては、パイル糸２と基布３とを固定できる樹脂組成物やゴム組成物であれば特に限定されず、例えば樹脂組成物の樹脂成分としてはアクリル系、ウレタン系、ポリ塩化ビニル、ポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体（ＥＶＡ）等の樹脂が挙げられる。ゴム組成物のゴム成分としてはＳＢＲ（スチレン−ブタジエン）、ＮＢＲ（アクリロニトリル−ブタジエンゴム）ＭＢＲ（メチルメタクリレート−ブタジエンゴム）あるいは天然ゴム等が挙げられる。また、充填剤として炭酸カルシウム、水酸化アルミニウム、水酸化マグネシウム、フライアッシュ等を添加してバッキング層として使用するのが一般的である。 Next, the backing layer 5 is not particularly limited as long as it is a resin composition or a rubber composition that can fix the pile yarn 2 and the base fabric 3. For example, the resin component of the resin composition may be acrylic, urethane, Examples thereof include resins such as polyvinyl chloride, polyethylene, polypropylene, and ethylene-vinyl acetate copolymer (EVA). Examples of the rubber component of the rubber composition include SBR (styrene-butadiene), NBR (acrylonitrile-butadiene rubber) MBR (methyl methacrylate-butadiene rubber), and natural rubber. In general, calcium carbonate, aluminum hydroxide, magnesium hydroxide, fly ash or the like is added as a filler and used as a backing layer.
また、図１に示すようにバッキング層４の下側にクッション性能とバッキング層の保護性能を付与すべく、不織布からなるセカンド基布５を設けてもよい。セカンド基布５としては、特に限定されず、ニ−ドルパンチ不織布、スパンボント不織布等を例示できる。セカンド基布５の目付は５０〜１０００ｇ／ｍ２、その厚さを０．５〜１５ｍｍ、構成繊維の繊度を０．１〜３０デシテックスの範囲に設定するのが好ましい。セカンド基布５の目付が、５０ｇ／ｍ２未満ではカ−ペットとしての機能や品位の劣ったものとなり、好ましくない。１０００ｇ／ｍ２を超えると徒にコスト増大となるだけで好ましくない。素材としては、パイル糸、基布と同様に特に限定されない。また、セカンド基布５の最下部表面に、樹脂組成物やゴム組成物で滑り止め層を形成してもよい。 Further, as shown in FIG. 1, a second base fabric 5 made of a non-woven fabric may be provided below the backing layer 4 in order to provide cushion performance and backing layer protection performance. It does not specifically limit as the second base fabric 5, A needle punch nonwoven fabric, a spunbond nonwoven fabric, etc. can be illustrated. The basis weight of the second base fabric 5 is preferably 50 to 1000 g / m 2 , the thickness is set to 0.5 to 15 mm, and the fineness of the constituent fibers is preferably set to a range of 0.1 to 30 dtex. If the basis weight of the second base fabric 5 is less than 50 g / m 2 , the function and quality of the carpet are inferior, which is not preferable. If it exceeds 1000 g / m 2 , the cost will increase unnecessarily. The material is not particularly limited as in the case of pile yarn and base fabric. Further, an anti-slip layer may be formed on the lowermost surface of the second base fabric 5 with a resin composition or a rubber composition.
次に、この発明の実施例として使用したカーペットの材質、構造、相転移材料を封入したマイクロカプセルの種類、加工方法、涼感性能測定試験および判定方法は次の通りである。 Next, the material and structure of the carpet used as an embodiment of the present invention, the type of microcapsules encapsulating the phase change material, the processing method, the cool feeling performance measurement test and the determination method are as follows.
＜使用材料＞
基布・・・目付１００ｇ／ｍ２ポリプロピレンテープヤーン織布（１４×１３）
パイル糸・・・ポリエステル繊維からなるパイル糸をループ状にタフティング機（１／８Ｇ）で基布に植え込む（パイル長５．０ｍｍ、目付５００ｇ／ｍ２）
バッキング層・・・ＳＢＲラテックス（充填剤として炭酸カルシウム）
セカンド基布・・・５デシテックスのポリエステル繊維からなるニードルパンチ不織布（目付３００ｇ／ｍ２、厚さ６ｍｍ）
相転移材料を封入したマイクロカプセル・・・プレサーモ（大和化学工業株式会社製）融点２５℃と融点３１℃の二種類
バインダー樹脂・・・アクリル−シリコン共重合体樹脂「ライトエポック」（共栄社株式会社製）
浸透剤・・・「ペレックスＯＴ−Ｐ」（花王株式会社製）
<Materials used>
Base fabric: basis weight 100g / m 2 polypropylene tape yarn woven fabric (14 x 13)
Pile yarn: pile yarn made of polyester fiber is planted in a loop with a tufting machine (1 / 8G) (pile length 5.0 mm, basis weight 500 g / m 2 )
Backing layer: SBR latex (calcium carbonate as filler)
Second base fabric: Needle punched nonwoven fabric made of 5 dtex polyester fiber (300 g / m 2 basis weight, thickness 6 mm)
Microcapsules encapsulating phase change material: Prethermo (manufactured by Daiwa Chemical Industry Co., Ltd.) Two types of melting point: 25 ° C and 31 ° C Binder resin: Acrylic-silicone copolymer resin “Light Epoch” (Kyoeisha Co., Ltd.) Made)
Penetration agent "Perex OT-P" (manufactured by Kao Corporation)
＜涼感性能測定試験＞
ＱＭＡＸ・・・カトーテック株式会社製ＴＨＥＲＭＯ ＬＡＢＯ ＩＩ ＴＹＰＥを用い、純銅板の初期温度３０℃、カーペット温度２０℃、接触圧０．９８ｋＰａで測定した。０．０８５ｊ／ｃｍ２・ｓｅｃより大きいものを合格とした。
官能評価・・・相転移材料を封入したマイクロカプセルを固着していないカーペットを基準に冷たいと感じるかどうかを一対比較法で評価し、被験者数を１０人とし、８０％以上の人が冷たいと感じたものを合格とした。（気温２０℃湿度６５％の標準室内にて評価）
<Cool feeling performance measurement test>
QMAX: Measured at an initial temperature of 30 ° C. of a pure copper plate, a carpet temperature of 20 ° C., and a contact pressure of 0.98 kPa, using THERMO LABO II TYPE manufactured by Kato Tech Co., Ltd. A thing larger than 0.085 j / cm 2 · sec was regarded as acceptable.
Sensory evaluation: Evaluate whether or not it feels cold based on the carpet not fixed with the microcapsules enclosing the phase change material by a paired comparison method, the number of subjects is 10, and 80% or more people are cold What I felt was accepted. (Evaluated in a standard room with temperature 20 ° C and humidity 65%)
＜実施例１＞
水１００重量部に相転移材料を封入したマイクロカプセル分散液（パラフィン封入、融点２５℃、固形分４０％）６重量部を分散させておいてから、浸透剤０．５重量部、バインダー樹脂を６重量部分散した水溶液をスプレーにてカーペット表面に２５０ｇ／ｍ２塗布し、１２０℃、１０分間乾燥処理して、カーペット上に相転移材料を封入したマイクロカプセルを６ｇ／ｍ２固着した涼感カーペットを得た。カーペット断面を実態顕微鏡で観察したところ、パイル糸に相転移材料を封入したマイクロカプセルが固着しているのを確認できた。(図２参照)
涼感性能測定試験でＱＭＡＸは０．１００ｊ／ｃｍ２・ｓｅｃで、比較例１との官能評価においては９人の人が冷たいと感じていた。
<Example 1>
After dispersing 6 parts by weight of a microcapsule dispersion liquid (sealed with paraffin, melting point 25 ° C., solid content 40%) in which 100 parts by weight of water is encapsulated in a phase change material, 0.5 parts by weight of a penetrant and a binder resin are dispersed. Cooling carpet in which 6 g parts by weight of an aqueous solution dispersed is applied to the carpet surface by spraying at 250 g / m 2, dried at 120 ° C. for 10 minutes, and 6 g / m 2 of microcapsules enclosing the phase change material are fixed on the carpet. Got. When the cross section of the carpet was observed with an actual microscope, it was confirmed that the microcapsules in which the phase change material was sealed in the pile yarn were fixed. (See Figure 2)
In the cool feeling performance measurement test, QMAX was 0.100 j / cm 2 · sec, and in sensory evaluation with Comparative Example 1, nine people felt cold.
＜比較例１＞
実施例１において、相転移材料を封入したマイクロカプセル分散液を０とした以外は実施例１と同様にしてカーペットを得た。涼感性能測定試験でＱＭＡＸは０．０８０ｊ／ｃｍ２・ｓｅｃで、官能評価において基準となるカーペットとした。
<Comparative Example 1>
A carpet was obtained in the same manner as in Example 1 except that the microcapsule dispersion in which the phase change material was encapsulated was changed to 0. In the cool feeling performance measurement test, QMAX was 0.080 j / cm 2 · sec, and it was used as a reference carpet in sensory evaluation.
＜実施例２＞
実施例１において、相転移材料の融点が３１℃のものを使用した以外は実施例１と同様にしてカーペットを得た。涼感性能測定試験でＱＭＡＸは０．０９０ｊ／ｃｍ２・ｓｅｃで、比較例１との官能評価において８人の人が冷たいと感じていた。
<Example 2>
A carpet was obtained in the same manner as in Example 1 except that a phase change material having a melting point of 31 ° C. was used. In the cool feeling performance measurement test, QMAX was 0.090 j / cm 2 · sec, and eight people felt cold in sensory evaluation with Comparative Example 1.
＜実施例３＞
実施例１において、パイル糸を綿１００％の４．２番手双糸とした以外は実施例１と同様にしてカーペットを得た。涼感性能測定試験でＱＭＡＸは０．１１０ｊ／ｃｍ２・ｓｅｃで、官能評価において全員の人が冷たいと感じていた。
<Example 3>
A carpet was obtained in the same manner as in Example 1 except that, in Example 1, the pile yarn was changed to 4.2% double yarn of 100% cotton. In the cool feeling performance measurement test, QMAX was 0.110 j / cm 2 · sec, and everyone felt cold in the sensory evaluation.
＜比較例２＞
実施例１において、相転移材料を封入したマイクロカプセル分散液（パラフィン封入、融点２５℃、固形分４０％）を０．３重量部とした以外は実施例１と同様にしてカーペットを得た。カーペット上に相転移材料を封入したマイクロカプセルを０．３ｇ／ｍ２固着したカーペットであった。涼感性能測定試験でＱＭＡＸは０．０８３ｊ／ｃｍ２・ｓｅｃで、比較例１との官能評価において５人の人が冷たいと感じただけであった。
<Comparative example 2>
A carpet was obtained in the same manner as in Example 1 except that 0.3 parts by weight of the microcapsule dispersion (sealed with paraffin, melting point 25 ° C., solid content 40%) encapsulating the phase change material was used. The carpet was obtained by fixing 0.3 g / m 2 of microcapsules enclosing a phase change material on the carpet. In the cool feeling performance measurement test, QMAX was 0.083 j / cm 2 · sec, and in the sensory evaluation with Comparative Example 1, only five people felt cold.
＜実施例４＞
実施例１において、浸透剤を０とした以外は実施例１と同様にしてカーペットを得た。涼感性能測定試験でＱＭＡＸは０．１０５ｊ／ｃｍ２・ｓｅｃで合格で、官能評価において１０人の人全員が冷たいと感じた。マイクロカプセルは、パイル糸の上部に多く固着し、パイル糸の下部や基布の上面には殆んど固着していない状態が観察された。
<Example 4>
A carpet was obtained in the same manner as in Example 1 except that the penetrant was changed to 0. In the cool feeling performance measurement test, QMAX passed 0.105 j / cm 2 · sec, and all 10 people felt cold in sensory evaluation. It was observed that a lot of microcapsules adhered to the upper part of the pile yarn and hardly adhered to the lower part of the pile yarn and the upper surface of the base fabric.
＜参考例１＞
実施例１において、マイクロカプセル分散液（パラフィン封入、融点２５℃と３０℃を半々、固形分４０％）６重量部としとした以外は実施例１と同様にしてカーペットを得た。実施例１と共に気温２８℃湿度７０％の室内にて官能評価したところ、実施例１は全員涼感を感じられなかったが、参考例１は８人の人が冷たいと感じていた。
<Reference Example 1>
A carpet was obtained in the same manner as in Example 1 except that 6 parts by weight of the microcapsule dispersion (paraffin encapsulated, melting points of 25 ° C. and 30 ° C., solid content of 40%) was changed to 6 parts by weight. When sensory evaluation was performed together with Example 1 in a room with an air temperature of 28 ° C. and a humidity of 70%, Example 1 did not all feel cool, but Reference Example 1 felt that 8 people were cold.
上述のように、相転移材料を封入したマイクロカプセルを少なくともパイル糸に固着しているものについては、未加工のものと比較して、明らかに涼しさの感じられるカーペットとすることができた。 As described above, at least the microcapsules encapsulating the phase change material fixed to the pile yarn could be a carpet that clearly felt cooler than the unprocessed ones.
１・・・涼感カーペット
２・・・パイル糸
３・・・基布
４・・・バッキング層
５・・・セカンド基布
６・・・相転移材料を封入したマイクロカプセル
DESCRIPTION OF SYMBOLS 1 ... Cool feeling carpet 2 ... Pile yarn 3 ... Base fabric 4 ... Backing layer 5 ... Second base fabric 6 ... Microcapsule enclosing phase change material
Claims (4)