JP4876436B2 - 防護材料及び防護衣服 - Google Patents
防護材料及び防護衣服 Download PDFInfo
- Publication number
- JP4876436B2 JP4876436B2 JP2005153724A JP2005153724A JP4876436B2 JP 4876436 B2 JP4876436 B2 JP 4876436B2 JP 2005153724 A JP2005153724 A JP 2005153724A JP 2005153724 A JP2005153724 A JP 2005153724A JP 4876436 B2 JP4876436 B2 JP 4876436B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- protective
- gas
- less
- protective material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
選択透過層の素材としてはポリアクリレート、ポリアクリロニトリル、ポリアミド、ポリアミドイミド、ポリウレタン、ポリエステル、共重合ポリエステル、ポリオレフィン、エチレン−ビニルアルコール系共重合体、ポリビニルアルコール、セルロース、セルロース誘導体等の皮膜形成性能を有するポリマーで皮膜形成後に透湿性とガス状有機化学物質に対して選択透過能を有する材料であればよい。これらの材料を単独、混合、あるいは順次積層して皮膜を形成しても構わない。
シート状繊維集合体としては綿、麻、毛、絹等の天然繊維、レーヨン、ポリノジック、キュプラ、リヨセル等の再生繊維、アセテート、トリアセテート等の半合成繊維、ナイロン、アラミド、ビニロン、ビニリデン、ポリ塩化ビニル、ポリエステル、アクリル、アクリル系、ポリエチレン、ポリプロピレン、ポリウレタン、ポリクラール、ポリアリレート、ポリベンザゾール、ポリイミド、ポリフェニレンスルフィド等の合成繊維からなる織物、編物、不織布等が挙げられる。これら繊維は単独あるいは混紡、交織、交編等により組み合わせてシート状繊維集合体としても良い。
透湿性のある微多孔あるいは無孔質のフィルム又は膜としてはポリエチレン、ポリプロピレン、ポリテトラフルオロエチレン、共重合ポリエステル、ポリウレタン、ポリエーテルポリウレタン、アクリレート等のシート状物が挙げられる。
外層付加層としては、JIS L 1092に記載の5.2スプレー試験を実施した場合の撥水度が4以上、AATCC Test Method 118による撥油度が4級以上である織物、編物、または不織布などが好適に用いることができるが、柔軟性を考慮したものの使用が推奨される。
選択透過層とガス吸着層からなる積層材料と外層付加層とは、あらかじめ接着剤により接着されている形態でもよいし、柔軟性を考慮し、接着せずに重ね合わせた状態で縫製加工し、衣服を作製してもよい。
内層付加層の目的としては、外部から与えられる機械的な力からガス吸着性物質及び選択透過層を保護する役割と、防護衣着用者の汗によるべたつき感を抑制する役割である。
が好ましく、さらに好ましくは350 g/m2以下である。400g/m2を超えると防護衣服の質量が大きくなり熱ストレスの原因となる。
透湿性:JIS L 1099 塩化カルシウム法に準拠した。
比表面積:窒素の吸着等温線を求め、これを基にしてBET法により算出する。
質量:JIS L 1018 8.4及びJIS L 1096 8.4による。
厚さ:JIS L 1018 8.5及びJIS L 1096 8.5による。
メルトインデックス:JIS K 7210による。
通気性:JIS L 1018 8.33及びJIS L 1096 8.4による。
剛軟度:JIS L 1096 8.27による。
着用感:ワンピース型の防護衣服を着用し、32℃、70%RHの恒温恒湿室において、10 分間、速度5km/hrでトレッドミル上で歩行した後の心拍数、血圧、皮膚温、直腸温、衣 服内温湿度の測定およびアンケート調査からの総合評価。
選択透過層を以下の方法で作製した。酢化度55%、6%粘度70×10-3Pa・Sの酢酸セルロース(ダイセル化学工業(株)L-30)を使用し、溶媒はメチルエチルケトンとN、Nジメチルホルムアミドの1:1混合溶液を使用し、固形分濃度が10wt%となるように室温で混合撹拌することにより酢酸セルロース溶液を作製した。この溶液を離型紙(リンテック(株)製)上に流延し、コーティングナイフにより膜厚を調節しながら塗工し、オーブン中で乾燥を行った。70℃で1分間乾燥させた後、120℃で2分間乾燥を行った。得られた選択透過層の厚さは20μm、質量20g/m2、透湿度175g/m2・hであった。
前記ガス吸着層と選択透過膜層を、質量20g/m2、メルトインデックス60g/10minの通気
性不織布状ホットメルト接着剤により接着後、外層付加層と内層付加層をホットメルトタイプのウレタン接着剤を使用し点接着により積層した。得られた防護材料は、質量284g/m2、厚さ1.00mm、透湿度143g/m2・hであった。この防護材料を用いたガス透過性試験結果を表1に示す。
実施例1においてガス吸着層を除いた防護材料を作製した。得られた防護材料は質量214g/m2、厚さ0.70mm、透湿度145g/m2・hであった。この防護材料を用いたガス透過性試験結果を表1に示す。
実施例1における選択透過膜層とガス吸着層の接着を、メルトインデックス120g/10minの透湿型ウレタン樹脂により点接着した。質量304g/m2、厚さ1.03mm、透湿度168g/m2・hであった。この防護材料を用いたガス透過性試験結果を表1に示す。
2:選択透過層
3:ガス吸着性物質層
4:内層付加層
5:上方セル(150cc)
6:サンプリング口
7:試験液
8:試験品
9:パラフィンシーリング
10:下方セル(150cc)
Claims (5)
- BET比表面積700m2/g以上3000m2/g以下の繊維状活性炭からなる層(ガス吸着層)を含むガス吸着層と、ガス状有機化学物質に対して透過抑制能があり、透湿度が60g/m 2 ・h以上850g/m 2 ・h以下である選択透過層との積層が、メルトインデックスが100g/10min以下の接着剤により積層されている防護材料。
- 接着剤が不織布状であることを特徴とする請求項1記載の防護材料。
- 接着剤がウレタン系、ビニルアルコール系、エステル系の何れかであることを特徴とする請求項1又は2に記載の防護材料。
- 前記選択透過層を少なくとも1層以上有し、かつ衣服の内側から見てガス吸着層の外側に少なくとも1層以上の該選択透過層が配置されている請求項1〜3いずれかに記載の防護材料。
- 請求項1〜4いずれかに記載の防護材料を用いることを特徴とする防護衣料。