JP4806252B2 - Toner, developer, toner container, process cartridge, image forming apparatus, and image forming method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a toner excellent in various properties such as charging property and transferability, giving high image quality and having excellent cleaning property, a developer using the toner and capable of enhancing image quality, a container containing such a toner, a process cartridge, an image forming apparatus and an image forming method. <P>SOLUTION: With respect to a root mean square (RMS) of surface roughness of the toner calculated by numerical expression 1 at the time of measuring a range two &mu;m square including at least a toner vertex on a surface of one toner particle in measurement of one place with an atomic force microscope (AFM), difference (&Delta;RMS) between the two extreme values of the above root mean square (RMS) in measurement of 50 places is 100-600. In the expression, (x<SB>i</SB>-x) represents difference between mean value and measured value of surface roughness, and N represents the number of measurements per one place and is 256&le;N&le;262,144. <P>COPYRIGHT: (C)2006,JPO&amp;NCIPI

Description

  The present invention relates to a toner for developing an electrostatic image in electrophotography, electrostatic recording, electrostatic printing, and the like, a developer using the toner, a container containing the toner, a process cartridge, an image forming apparatus, and an image forming method. .

  Image formation by electrophotography generally forms an electrostatic charge image on a photoreceptor (hereinafter sometimes referred to as “electrophotographic photoreceptor”, “electrostatic latent image carrier”, or “image carrier”). The electrostatic image is developed with a developer to form a visible image (toner image), and then the visible image is transferred to a recording medium such as paper and fixed to form a fixed image. (See Patent Document 1).

  As the developer, a one-component developer using a magnetic toner or a non-magnetic toner alone and a two-component developer composed of a toner and a carrier are known. Further, as the toner, a toner produced by a kneading and pulverizing method is generally used in which a thermoplastic resin is melt-kneaded with a release agent such as a pigment and wax, a charge control agent, etc., and then finely pulverized and further classified. Yes. If necessary, inorganic fine particles or organic fine particles may be added to the surface of the toner particles for the purpose of improving fluidity and cleaning properties.

  However, in the kneading and pulverizing method, the toner shape and surface structure obtained are indeterminate, and the toner shape and surface structure are arbitrary although there are some changes depending on the pulverization properties of the materials used and various conditions of the pulverization process. It is difficult to control. In addition, in order to obtain a high-resolution and high-gradation image, it is necessary to further narrow the toner particle size distribution. However, there are problems such as limit of classification ability, reduction in yield and productivity, and cost increase. In addition, it is extremely difficult to produce a toner having a small particle size, particularly a particle size of 6 μm or less.

The irregular toner obtained by the pulverization and kneading method has a different adhesion area to the developing roll for a one-component developer and an adhesion area to a carrier for a two-component developer. In addition, the adhesion force to the carrier is different, and there is a problem that a difference occurs in chargeability, that is, ease of development. Even when the particle diameters of the toners are different, the charge amounts of the individual toner particles are different, so that the development is different.
As described above, when each toner particle is easily developed, easily developable toner is selectively developed, while hard-to-develop toner remains in the developing device, and developability changes with time. There is a problem. Similarly, in transfer to a recording medium, toner that is easily transferred and toner that is difficult to transfer are mixed, and image quality deterioration such as toner scattering tends to occur.

  In the pulverization and kneading method, when a toner is produced by internally adding a release agent such as wax, the release agent may be exposed on the surface of the toner particles depending on the combination with a thermoplastic resin. In particular, in a combination of a resin that is imparted with elasticity by a high molecular weight component and hardly pulverized, and a brittle wax such as polypropylene, exposure of the wax on the toner particle surface is often observed. Such exposure of the release agent is effective for releasability during fixing and cleaning of the toner remaining on the photoreceptor after transfer, but the fluidizing agent on the toner particle surface is easily moved by mechanical force. Therefore, there is a problem that the developing roll, the photoconductor, the carrier and the like are likely to be contaminated with wax, leading to a decrease in the reliability of the image forming apparatus.

  The toner image formed on such a photoconductor is transferred to a recording medium, but the transfer residual toner remaining on the photoconductor is cleaned by, for example, blade cleaning, fur brush cleaning, roller cleaning, or the like. However, if these cleaning devices are provided, the size of the image forming apparatus inevitably increases, which is against the demand for downsizing the apparatus. In addition, from the viewpoint of nature conservation ecology, a system with a small amount of waste toner to be discarded is desired, and there is a great interest in a toner having excellent chargeability.

In addition, in order to form a high-quality image, it is important to improve the adaptability with members used in the development process, in particular, electrostatic latent image carriers, intermediate transfer members, charging members, etc. Therefore, a toner having a good balance between the image density and the image fog in the development and having a good transfer efficiency is required. Therefore, for example, spherical toners (see Patent Document 2) that define the shape factors SF-1 and SF-2 and magnetic toners that are made spherical by mechanical impact force (see Patent Document 3) have been proposed.
However, the toner described in Patent Document 2 does not describe any transferability, and when an image is formed using the toner, it is recognized that the transfer efficiency is low. In addition, the toner described in Patent Document 3 is still insufficient in transfer efficiency and needs further improvement.

  Therefore, the toners that are excellent in various characteristics such as chargeability and transferability, obtain high image quality, have excellent cleaning properties, and related technologies using the toners have not yet been sufficiently satisfactory. It is.

US Pat. No. 2,297,691 JP-A 61-279864 Japanese Patent Laid-Open No. 63-235953

  An object of the present invention is to solve various problems in the prior art and achieve the following objects. That is, the present invention is excellent in various properties such as chargeability and transferability, provides high image quality, has excellent cleaning properties, and can be improved in image quality by using the toner. It is an object to provide a container, a process cartridge, an image forming apparatus, and an image forming method.

Means for solving the problems are as follows. That is,
<1> Using the atomic force microscope (AFM), the following formula 1 of the surface roughness measured in a range of 2 μm in length and 2 μm in width including at least the toner apex portion on the surface of one toner for one measurement. Regarding the calculated root mean square (RMS), the difference between the maximum value and the minimum value (ΔRMS) of the root mean square (RMS) in 50 measurements is 100 to 600.
<2> The toner according to <1>, wherein a difference (ΔRMS) between a maximum value and a minimum value of root mean square (RMS) is 200 to 600.
<3> The toner according to any one of <1> and <2>, wherein the root mean square (RMS) has a maximum value of 200 to 650.
<4> The toner according to any one of <1> to <3>, wherein a root mean square (RMS) minimum value is 10 to 150.
<5> The toner according to any one of <1> to <4>, wherein the average circularity is 0.93 to 0.97.
<6> The toner according to <5>, including a toner having an average circularity of 0.98 or more and 40% by mass or less, and a toner having an average circularity of 0.95 or less and 35% by mass or less.
<7> The toner according to any one of <1> to <6>, wherein the toner is granulated by emulsifying or dispersing a solution or dispersion of the toner material in an aqueous medium.
<8> The toner according to <7>, wherein the solution or dispersion of the toner material contains an organic solvent, and the organic solvent is removed during or after granulation.
<9> The toner material includes at least an active hydrogen group-containing compound and a polymer capable of reacting with the active hydrogen group-containing compound,
By granulating, by reacting the active hydrogen group-containing compound and a polymer capable of reacting with the active hydrogen group-containing compound to produce an adhesive base material, particles containing at least the adhesive base material are obtained. The toner according to any one of <7> to <8>, which is performed.
<10> The toner according to any one of <1> to <9>, wherein the toner has a volume average particle diameter (Dv) of 3 to 8 μm.
<11> The toner according to any one of <1> to <10>, wherein the toner has a volume average particle diameter (Dv) / number average particle diameter (Dn) of 1.00 to 1.15.
<12> A developer comprising the toner according to any one of <1> to <11>.
<13> A toner-containing container filled with the toner according to any one of <1> to <11>.
<14> An electrostatic latent image carrier and an electrostatic latent image formed on the electrostatic latent image carrier are developed using the toner according to any one of <1> to <11> to be a visible image And a developing means for forming the process cartridge.
<15> An electrostatic latent image carrier, an electrostatic latent image forming unit for forming an electrostatic latent image on the electrostatic latent image carrier, and the electrostatic latent image according to <1> to <11> Development means for forming a visible image by developing using any of the toners, transfer means for transferring the visible image to a recording medium, and fixing means for fixing the transferred image transferred to the recording medium The image forming apparatus is characterized by having at least.
<16> An electrostatic latent image forming step of forming an electrostatic latent image on the electrostatic latent image carrier, and the electrostatic latent image using the toner according to any one of <1> to <11> An image comprising at least a developing step for developing to form a visible image, a transferring step for transferring the visible image to a recording medium, and a fixing step for fixing the transferred image transferred to the recording medium It is a forming method.

The toner of the present invention has the following surface roughness measured using an atomic force microscope (AFM) in a range of 2 μm in length × 2 μm in width including at least the toner apex portion on the surface of one toner for one measurement. About the root mean square (RMS) calculated from Formula 1, the difference (ΔRMS) between the maximum value and the minimum value of the root mean square (RMS) in 50 measurements is 100 to 600. As a result, it is possible to provide a toner having excellent cleaning properties while maintaining the same image quality and chargeability as spherical toners.

  The developer of the present invention contains the toner of the present invention. Therefore, when an image is formed by electrophotography using the developer, it is excellent in various properties such as chargeability and transferability, high image quality is obtained, excellent cleaning properties, and a large number of sheets over a long period of time. Even when used repeatedly, high image quality capable of forming a stable image with good reproducibility can be obtained.

  The toner-containing container of the present invention contains the toner of the present invention in a container. For this reason, when an image is formed by electrophotography using the toner contained in the toner-containing container, as a result, it has excellent cleaning properties, excellent characteristics such as chargeability and transferability, and high image quality. Is obtained.

  The process cartridge of the present invention comprises an electrostatic latent image carrier and developing means for developing a latent image formed on the electrostatic latent image carrier using the toner of the present invention to form a visible image. At least. The process cartridge is detachable from the image forming apparatus, is excellent in convenience, and uses the toner of the present invention. As a result, the process cartridge has excellent cleaning properties and various characteristics such as chargeability and transferability. Excellent image quality.

  The image forming apparatus of the present invention includes an electrostatic latent image carrier, an electrostatic latent image forming unit that forms an electrostatic latent image on the electrostatic latent image carrier, and the electrostatic latent image of the present invention. The image forming apparatus includes at least a developing unit that forms a visible image by developing with toner, a transfer unit that transfers the visible image to a recording medium, and a fixing unit that fixes the transferred image transferred to the recording medium. In the image forming apparatus, the electrostatic latent image forming unit forms an electrostatic latent image on the electrostatic latent image carrier. The transfer means transfers the visible image to a recording medium. The fixing unit fixes the transferred image transferred to the recording medium. As a result, it has excellent cleaning properties, is excellent in various characteristics such as chargeability and transferability, and can form a high-quality electrophotographic image.

  The image forming method of the present invention includes an electrostatic latent image forming step of forming an electrostatic latent image on an electrostatic latent image carrier, and the electrostatic latent image is developed using the toner of the present invention to be visible. It includes at least a developing step for forming an image, a transfer step for transferring the visible image to a recording medium, and a fixing step for fixing the transferred image transferred to the recording medium. In the image forming method, an electrostatic latent image is formed on the electrostatic latent image carrier in the electrostatic latent image forming step. In the transfer step, the visible image is transferred to a recording medium. In the fixing step, the transferred image transferred to the recording medium is fixed. As a result, it has excellent cleaning properties, is excellent in various characteristics such as chargeability and transferability, and can form a high-quality electrophotographic image.

  According to the present invention, the conventional problems can be solved, and by controlling the difference between the maximum value and the minimum value (ΔRMS) of the root mean square (RMS) of the toner, the charging stability equivalent to that of the spherical toner can be improved. Provided are a toner having excellent cleaning properties while maintaining image quality, and a developer, a container containing toner, a process cartridge, an image forming apparatus, and an image forming method capable of improving image quality using the toner. .

(toner)
The toner of the present invention has the following surface roughness measured using an atomic force microscope (AFM) in a range of 2 μm in length × 2 μm in width including at least the toner apex portion on the surface of one toner for one measurement. About the root mean square (RMS) calculated from Formula 1, the difference (ΔRMS) between the maximum value and the minimum value of the root mean square (RMS) in 50 measurements is 100 to 600, preferably 200 to 600. 250 to 550 are more preferable.
When ΔRMS is less than 100, cleaning failure may occur. When it exceeds 600, chargeability and transferability are deteriorated, and image deterioration may occur.
In Equation 1, N represents the number of measurements per measurement (one toner), and 256 (= 16 × 16) ≦ N ≦ 262144 (= 512 × 512).

The maximum value of the root mean square (RMS) is preferably 200 to 650, more preferably 300 to 550.
10-150 are preferable and, as for the minimum value of the said root mean square (RMS), 10-80 are more preferable.

  Here, in the measurement of the AFM (AFM: Atomic Force Microscope), the toner particles are searched for with an optical microscope, an AFM cantilever (corresponding to a sensor) is lowered on each of the toner particles, and the length is 4 μm × A range of 4 μm (4 μm square) is measured. A toner apex portion is searched from the 4 μm square, a range of 2 μm in length × 2 μm in width (2 μm square) is measured so that the toner apex portion is in the center, and an RMS value is calculated from the above Equation 1. Similarly, the RMS value is measured for 50 toner particles (measurement at 50 locations), and the difference (ΔRMS) between the maximum value and the minimum value of the RMS value is calculated.

Specifically, the root mean square (RMS) of the toner using the AFM can be measured as follows.
An AFM (AFM: Atomic Force Microscope) (NANOStation II, manufactured by SURFACE IMAGEING SYSTEMS) was used under the following measurement conditions.
・ Measurement mode: Tapping mode-AFM
Measurement range: X-Range: 2000.0 nm
: Y-Range: 2000.0 nm
Measurement resolution: 128 × 128 pixels (number of measurements N = 16384)
Scan speed: 0.3 Lines / s
Cantilever: manufactured by Nanosensors, AR5-NCLR-20
・ Resonance frequency: 161.005 kHz
・ Amplitude: 90.0 nm

  The toner of the present invention is not particularly limited as long as the production method and material satisfy the above conditions, and can be appropriately selected from known ones according to the purpose. For example, a high-quality and high-definition image can be obtained. In order to output, it is preferable that the toner has a small particle diameter. As a method for producing such a toner, there are a pulverization classification method, a suspension polymerization method, an emulsion polymerization method, a polymer suspension method, etc. in which an oil phase is emulsified, suspended or aggregated in an aqueous medium to form toner base particles. is there.

  The pulverization method is, for example, a method of obtaining the toner base particles by melting and kneading the toner material, pulverizing, classifying and the like. In the case of the pulverization method, for the purpose of setting the average circularity of the toner in the range of 0.97 to 1.0, the shape is controlled by applying a mechanical impact force to the obtained toner base particles. May be. In this case, the mechanical impact force can be applied to the toner base particles using a device such as a hybridizer or mechanofusion.

The suspension polymerization method is an oil-soluble polymerization initiator, emulsification described later in an aqueous medium in which a colorant, a release agent, and the like are dispersed in a polymerizable monomer and a surfactant and other solid dispersant are contained. Emulsified and dispersed by the method. Thereafter, a polymerization reaction is performed to form particles, and then wet processing for attaching inorganic fine particles to the toner particle surfaces in the present invention may be performed. At that time, it is preferable to treat the toner particles from which excess surfactant and the like are removed by washing.
Examples of the polymerizable monomer include acrylic acids, methacrylic acid, α-cyanoacrylic acid, α-cyanomethacrylic acid, itaconic acid, crotonic acid, fumaric acid, maleic acid, maleic anhydride, and other acids, acrylamide, By using a part of acrylate or methacrylate having amino group such as methacrylamide, diacetone acrylamide or their methylol compounds, vinyl pyridine, vinyl pyrrolidone, vinyl imidazole, ethyleneimine, dimethylaminoethyl methacrylate, etc. Functional groups can be introduced.
Further, by selecting a dispersant having an acid group or a basic group as a dispersant to be used, the dispersant can be adsorbed and left on the particle surface to introduce a functional group.

  As the emulsion polymerization method, a water-soluble polymerization initiator and a polymerizable monomer are emulsified in water using a surfactant, and a latex is synthesized by a usual emulsion polymerization method. Separately, a dispersion in which a colorant, a release agent and the like are dispersed in an aqueous medium is prepared, and after mixing, the toner is aggregated to a toner size and heat-fused to obtain a toner. Thereafter, wet processing of inorganic fine particles described later may be performed. A functional group can be introduced on the surface of the toner particles by using a latex similar to the monomer that can be used in the suspension polymerization method.

  In the present invention, among these, since the selectivity of the resin is high, the low-temperature fixability is high, the granulation property is excellent, and the particle size, the particle size distribution, and the shape can be easily controlled. The toner is preferably obtained by emulsifying or dispersing a toner material dissolved or dispersed in an aqueous medium and granulating the toner.

The toner material solution is obtained by dissolving the toner material in a solvent, and the toner material dispersion liquid is obtained by dispersing the toner material in a solvent.
Examples of the toner material include an adhesive base obtained by reacting an active hydrogen group-containing compound, a polymer capable of reacting with the active hydrogen group-containing compound, a binder resin, a release agent, and a colorant. And, if necessary, other components such as resin fine particles and a charge control agent.

-Adhesive substrate-
The adhesive substrate exhibits adhesiveness to a recording medium such as paper, and is formed by reacting the active hydrogen group-containing compound and a polymer capable of reacting with the active hydrogen group-containing compound in the aqueous medium. It may contain at least a polymer and may further contain a binder resin appropriately selected from known binder resins.

There is no restriction | limiting in particular as a weight average molecular weight of the said adhesive base material, Although it can select suitably according to the objective, For example, 1,000 or more are preferable and 2,000-10,000,000 are more preferable. 3,000 to 1,000,000 are particularly preferred.
When the weight average molecular weight is less than 1,000, the hot offset resistance may be deteriorated.

The storage elastic modulus of the adhesive substrate is not particularly limited and may be appropriately selected depending on the intended purpose. For example, the temperature (TG ′) at which the measurement frequency is 20 Hz is 10,000 dyne / cm ² , Usually, it is 100 ° C. or higher, and preferably 110 to 200 ° C. When the (TG ′) is less than 100 ° C., the hot offset resistance may be deteriorated.
The viscosity of the adhesive substrate is not particularly limited and may be appropriately selected depending on the intended purpose. For example, the temperature (Tη) at which a poise of 1,000 at a measurement frequency of 20 Hz is usually 180 ° C. or less. Yes, 90-160 degreeC is preferable. When the (Tη) exceeds 180 ° C., the low-temperature fixability may be deteriorated.
Therefore, from the viewpoint of achieving both hot offset resistance and low-temperature fixability, the (TG ′) is preferably higher than the (Tη). That is, the difference (TG′−Tη) between (TG ′) and (Tη) is preferably 0 ° C. or higher, more preferably 10 ° C. or higher, and further preferably 20 ° C. or higher. The larger the difference, the better.
Further, from the viewpoint of achieving both low-temperature fixability and heat-resistant storage stability, (TG′−Tη) is preferably 0 to 100 ° C., more preferably 10 to 90 ° C., and still more preferably 20 to 80 ° C.

Specific examples of the adhesive substrate are not particularly limited and may be appropriately selected depending on the intended purpose. Particularly preferred examples include polyester resins.
There is no restriction | limiting in particular as said polyester-type resin, Although it can select suitably according to the objective, For example, a urea modified polyester-type resin etc. are mentioned especially suitably.
The urea-modified polyester resin comprises an amine (B) as the active hydrogen group-containing compound and an isocyanate group-containing polyester prepolymer (A) as a polymer that can react with the active hydrogen group-containing compound. It is obtained by reacting in a medium.
The urea-modified polyester resin may contain a urethane bond in addition to the urea bond, and in this case, the molar ratio of the urea bond to the urethane bond (urea bond / urethane bond) is particularly limited. However, 100/0 to 10/90 is preferable, 80/20 to 20/80 is more preferable, and 60/40 to 30/70 is particularly preferable.
When the urea bond is less than 10, the hot offset resistance may be deteriorated.

  Preferable specific examples of the urea-modified polyester resin include the following (1) to (10), that is, (1) a polyester pre-reacted polycondensate of bisphenol A ethylene oxide 2 mol adduct and isophthalic acid with isophorone diisocyanate. A mixture of a polymer urealated with isophorone diamine and a polycondensate of bisphenol A ethylene oxide 2 mol adduct and isophthalic acid, and (2) a polycondensate of bisphenol A ethylene oxide 2 mol adduct and isophthalic acid A mixture of a polyester prepolymer reacted with diisocyanate and uread with isophoronediamine, a bicondensate of bisphenol A ethylene oxide 2 mol adduct and terephthalic acid, (3) bisphenol A ethylene oxide 2 mol A polyester prepolymer obtained by reacting an adduct / bisphenol A propylene oxide 2 mol adduct and a polycondensate of terephthalic acid with isophorone diisocyanate, and urethanized with isophorone diamine, and bisphenol A ethylene oxide 2 mol adduct / bisphenol A propylene. Mixture of oxide 2 mol adduct and polycondensate of terephthalic acid, (4) Bisphenol A ethylene oxide 2 mol adduct / bisphenol A propylene oxide 2 mol adduct and terephthalic acid polycondensate were reacted with isophorone diisocyanate. A mixture of a polyester prepolymer uread with isophoronediamine, a bisphenol A propylene oxide 2-mole adduct and a polycondensate of terephthalic acid, (5) bisphenol A A polyester prepolymer obtained by reacting a polycondensate of tylene oxide 2 mol adduct and terephthalic acid with isophorone diisocyanate and uread with hexamethylenediamine, and a polycondensate of bisphenol A ethylene oxide 2 mol adduct and terephthalic acid (6) Polyester prepolymer obtained by reacting a polycondensate of bisphenol A ethylene oxide with 2 mol of bisphenol A and isophorone diisocyanate with urea and hexamethylenediamine and 2 mol of bisphenol A ethylene oxide. Product / bisphenol A propylene oxide 2 mol adduct and terephthalic acid polycondensate, (7) bisphenol A ethylene oxide 2 mol adduct and terephthalic acid polycondensate A mixture of a polyester prepolymer reacted with socyanate with urethanized with ethylenediamine and a polycondensate of bisphenol A ethylene oxide 2 mol adduct and terephthalic acid, (8) bisphenol A ethylene oxide 2 mol adduct and isophthalic acid (9) Bisphenol A ethylene, a mixture of a polyester prepolymer obtained by reacting a polycondensate of bisphenol with diphenylmethane diisocyanate and uread with hexamethylene diamine, a bicondensate of bisphenol A ethylene oxide and a polycondensate of isophthalic acid, Polyester prepolymer obtained by reacting polycondensate of oxide 2 mol adduct / bisphenol A propylene oxide 2 mol adduct and terephthalic acid / dodecenyl succinic anhydride with diphenylmethane diisocyanate Mixture of uremer with hexamethylenediamine and bisphenol A ethylene oxide 2-mole adduct / bisphenol A propylene oxide 2-mole adduct and terephthalic acid polycondensate, (10) bisphenol A ethylene oxide 2-mole addition And a mixture of a polyester prepolymer obtained by reacting a polycondensate of isophthalic acid and toluene diisocyanate with urea diisocyanate with hexamethylenediamine, a bicondensate of bisphenol A ethylene oxide and a polycondensate of isophthalic acid, etc. Preferably mentioned.

-Active hydrogen group-containing compound-
The active hydrogen group-containing compound acts as an elongation agent, a crosslinking agent, or the like when a polymer capable of reacting with the active hydrogen group-containing compound undergoes an elongation reaction, a crosslinking reaction, or the like in the aqueous medium.
The active hydrogen group-containing compound is not particularly limited as long as it has an active hydrogen group, and can be appropriately selected depending on the purpose. For example, the polymer capable of reacting with the active hydrogen group-containing compound is In the case of the isocyanate group-containing polyester prepolymer (A), the amines (B) can be increased in molecular weight by a reaction such as an elongation reaction or a crosslinking reaction with the isocyanate group-containing polyester prepolymer (A). Is preferred.
There is no restriction | limiting in particular as said active hydrogen group, According to the objective, it can select suitably, For example, a hydroxyl group (alcoholic hydroxyl group or phenolic hydroxyl group), an amino group, a carboxyl group, a mercapto group etc. are mentioned. These may be used individually by 1 type and may use 2 or more types together. Among these, an alcoholic hydroxyl group is particularly preferable.

The amines (B) are not particularly limited and may be appropriately selected depending on the intended purpose. Examples thereof include diamine (B1), trivalent or higher polyamine (B2), amino alcohol (B3), and amino mercaptan. (B4), amino acid (B5), and those obtained by blocking the amino groups of B1 to B5 (B6).
These may be used individually by 1 type and may use 2 or more types together. Among these, diamine (B1), a mixture of diamine (B1) and a small amount of a trivalent or higher polyamine (B2) are particularly preferable.

Examples of the diamine (B1) include aromatic diamines, alicyclic diamines, and aliphatic diamines. Examples of the aromatic diamine include phenylenediamine, diethyltoluenediamine, 4,4′diaminodiphenylmethane, and the like. Examples of the alicyclic diamine include 4,4′-diamino-3,3′dimethyldicyclohexylmethane, diaminecyclohexane, and isophoronediamine. Examples of the aliphatic diamine include ethylene diamine, tetramethylene diamine, and hexamethylene diamine.
Examples of the trivalent or higher polyamine (B2) include diethylenetriamine and triethylenetetramine.
Examples of the amino alcohol (B3) include ethanolamine and hydroxyethylaniline.
Examples of the amino mercaptan (B4) include aminoethyl mercaptan and aminopropyl mercaptan.
Examples of the amino acid (B5) include aminopropionic acid and aminocaproic acid.
Examples of the block (B6) in which the amino group of B1 to B5 is blocked include, for example, a ketimine obtained from any of the amines (B1) to (B5) and ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, etc.) Compounds, oxazolyzone compounds, and the like.

  In addition, a reaction terminator can be used to stop the elongation reaction, the crosslinking reaction, etc. between the active hydrogen group-containing compound and the polymer capable of reacting with the active hydrogen group-containing compound. Use of the reaction terminator is preferable in that the molecular weight and the like of the adhesive substrate can be controlled within a desired range. Examples of the reaction terminator include monoamines (diethylamine, dibutylamine, butylamine, laurylamine, etc.) or those blocked (ketimine compounds).

As a mixing ratio of the amines (B) and the isocyanate group-containing polyester prepolymer (A), the isocyanate group [NCO] in the isocyanate group-containing prepolymer (A) and the amines (B) The mixing equivalent ratio ([NCO] / [NHx]) of the amino group [NHx] is preferably 1/3 to 3/1, more preferably 1/2 to 2/1, It is particularly preferably 1.5 to 1.5 / 1.
If the mixing equivalent ratio ([NCO] / [NHx]) is less than 1/3, the low-temperature fixability may decrease. If it exceeds 3/1, the molecular weight of the urea-modified polyester resin will be low. The hot offset resistance may be deteriorated.

--Polymer capable of reacting with active hydrogen group-containing compound--
The polymer capable of reacting with the active hydrogen group-containing compound (hereinafter sometimes referred to as “prepolymer”) is not particularly limited as long as it has at least a site capable of reacting with the active hydrogen group-containing compound. However, it can be appropriately selected from known resins, and examples thereof include polyol resins, polyacrylic resins, polyester resins, epoxy resins, and derivative resins thereof.
These may be used individually by 1 type and may use 2 or more types together. Among these, a polyester resin is particularly preferable in terms of high fluidity and transparency during melting.

The site capable of reacting with the active hydrogen group-containing compound in the prepolymer is not particularly limited and may be appropriately selected from known substituents. For example, an isocyanate group, an epoxy group, a carboxylic acid, An acid chloride group, and the like.
These may be contained singly or in combination of two or more. Among these, an isocyanate group is particularly preferable.

Among the prepolymers, it is easy to adjust the molecular weight of the polymer component, and oil-less low-temperature fixing characteristics in dry toners, in particular, good releasability and fixability even in the absence of a release oil application mechanism to a fixing heating medium. It is particularly preferable that it is a urea bond-forming group-containing polyester resin (RMPE) in that it can be secured.
As said urea bond production | generation group, an isocyanate group etc. are mentioned, for example. When the urea bond generating group in the urea bond generating group-containing polyester resin (RMPE) is the isocyanate group, the isocyanate group-containing polyester prepolymer (A) and the like are particularly preferable as the polyester resin (RMPE). It is done.

  The isocyanate group-containing polyester prepolymer (A) is not particularly limited and may be appropriately selected depending on the intended purpose. For example, it is a polycondensate of a polyol (PO) and a polycarboxylic acid (PC), And what made the said active hydrogen group containing polyester resin react with polyisocyanate (PIC), etc. are mentioned.

  There is no restriction | limiting in particular as said polyol (PO), According to the objective, it can select suitably, For example, diol (DIO), trihydric or more polyol (TO), diol (DIO), and trihydric or more polyol A mixture with (TO), etc. are mentioned. These may be used individually by 1 type and may use 2 or more types together. Among these, the diol (DIO) alone or a mixture of the diol (DIO) and a small amount of the trivalent or higher polyol (TO) is preferable.

Examples of the diol (DIO) include alkylene glycols, alkylene ether glycols, alicyclic diols, alkylene oxide adducts of alicyclic diols, bisphenols, alkylene oxide adducts of bisphenols, and the like.
The alkylene glycol is preferably one having 2 to 12 carbon atoms, such as ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,4-butanediol, 1,6-hexanediol, and the like. Can be mentioned. Examples of the alkylene ether glycol include diethylene glycol, triethylene glycol, dipropylene glycol, polyethylene glycol, polypropylene glycol, polytetramethylene ether glycol, and the like. Examples of the alicyclic diol include 1,4-cyclohexanedimethanol and hydrogenated bisphenol A. Examples of the alkylene oxide adduct of the alicyclic diol include those obtained by adding an alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide to the alicyclic diol. Examples of the bisphenols include bisphenol A, bisphenol F, and bisphenol S. Examples of the alkylene oxide adduct of the bisphenol include those obtained by adding an alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide to the bisphenol.
Among these, alkylene glycols having 2 to 12 carbon atoms, alkylene oxide adducts of bisphenols and the like are preferable, and alkylene oxide adducts of bisphenols, alkylene oxide adducts of bisphenols and alkylene glycols having 2 to 12 carbon atoms. Mixtures are particularly preferred.

The trivalent or higher polyol (TO) is preferably 3 to 8 or higher, for example, a trivalent or higher polyhydric aliphatic alcohol, a trivalent or higher polyphenol, a trivalent or higher polyphenol. And alkylene oxide adducts.
Examples of the trihydric or higher polyhydric aliphatic alcohol include glycerin, trimethylolethane, trimethylolpropane, pentaerythritol, sorbitol and the like. Examples of the trihydric or higher polyphenols include trisphenol PA, phenol novolak, cresol novolak, and the like. Examples of the trivalent or higher polyphenols alkylene oxide adducts include those obtained by adding an alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide to the trivalent or higher polyphenols.

  The mixture mass ratio (DIO: TO) of the diol (DIO) and the trivalent or higher polyol (TO) in the mixture of the diol (DIO) and the trivalent or higher polyol (TO) is 100: 0.01-100: 10 are preferable and 100: 0.01-100: 1 are more preferable.

There is no restriction | limiting in particular as said polycarboxylic acid (PC), Although it can select suitably according to the objective, For example, dicarboxylic acid (DIC), trivalent or more polycarboxylic acid (TC), dicarboxylic acid (DIC) ) And a tri- or higher valent polycarboxylic acid.
These may be used individually by 1 type and may use 2 or more types together. Among these, dicarboxylic acid (DIC) alone or a mixture of DIC and a small amount of trivalent or higher polycarboxylic acid (TC) is preferable.
Examples of the dicarboxylic acid include alkylene dicarboxylic acid, alkenylene dicarboxylic acid, aromatic dicarboxylic acid, and the like.
Examples of the alkylene dicarboxylic acid include succinic acid, adipic acid, and sebacic acid. As said alkenylene dicarboxylic acid, a C4-C20 thing is preferable, For example, a maleic acid, a fumaric acid, etc. are mentioned. As said aromatic dicarboxylic acid, a C8-C20 thing is preferable, For example, a phthalic acid, an isophthalic acid, a terephthalic acid, naphthalene dicarboxylic acid etc. are mentioned.
Among these, alkenylene dicarboxylic acid having 4 to 20 carbon atoms and aromatic dicarboxylic acid having 8 to 20 carbon atoms are preferable.

The trivalent or higher polycarboxylic acid (TO) is preferably a trivalent to octavalent or higher one, and examples thereof include aromatic polycarboxylic acids.
The aromatic polycarboxylic acid preferably has 9 to 20 carbon atoms, and examples thereof include trimellitic acid and pyromellitic acid.

  As the polycarboxylic acid (PC), the dicarboxylic acid (DIC), the trivalent or higher polycarboxylic acid (TC), and a mixture of the dicarboxylic acid (DIC) and the trivalent or higher polycarboxylic acid, Any acid anhydride or lower alkyl ester selected from can also be used. Examples of the lower alkyl ester include methyl ester, ethyl ester, isopropyl ester and the like.

  Mixing mass ratio (DIC: TC) of the dicarboxylic acid (DIC) and the trivalent or higher polycarboxylic acid (TC) in the mixture of the dicarboxylic acid (DIC) and the trivalent or higher polycarboxylic acid (TC) There is no restriction | limiting in particular, According to the objective, it can select suitably, For example, 100: 0.01-100: 10 are preferable and 100: 0.01-100: 1 are more preferable.

  The mixing ratio for the polycondensation reaction between the polyol (PO) and the polycarboxylic acid (PC) is not particularly limited and may be appropriately selected depending on the intended purpose. For example, in the polyol (PO) The equivalent ratio ([OH] / [COOH]) of the hydroxyl group [OH] to the carboxyl group [COOH] in the polycarboxylic acid (PC) is usually preferably 2/1 to 1/1. More preferably, it is 0.5 / 1 to 1/1, and particularly preferably 1.3 / 1 to 1.02 / 1.

There is no restriction | limiting in particular as content in the said isocyanate group containing polyester prepolymer (A) of the said polyol (PO), Although it can select suitably according to the objective, For example, 0.5-40 mass% is preferable. 1-30 mass% is more preferable, and 2-20 mass% is especially preferable.
When the content is less than 0.5% by mass, the hot offset resistance deteriorates, and it may be difficult to achieve both the heat-resistant storage stability and the low-temperature fixability of the toner, and exceeds 40% by mass. In some cases, the low-temperature fixability may deteriorate.

There is no restriction | limiting in particular as said polyisocyanate (PIC), Although it can select suitably according to the objective, For example, aliphatic polyisocyanate, alicyclic polyisocyanate, aromatic diisocyanate, araliphatic diisocyanate, isocyanurate And those blocked with phenol derivatives, oximes, caprolactams, and the like.
Examples of the aliphatic polyisocyanate include tetramethylene diisocyanate, hexamethylene diisocyanate, 2,6-diisocyanatomethylcaproate, octamethylene diisocyanate, decamethylene diisocyanate, dodecamethylene diisocyanate, tetradecamethylene diisocyanate, trimethylhexane diisocyanate, Examples include tetramethylhexane diisocyanate. Examples of the alicyclic polyisocyanate include isophorone diisocyanate and cyclohexylmethane diisocyanate. Examples of the aromatic diisocyanate include tolylene diisocyanate, diphenylmethane diisocyanate, 1,5-naphthylene diisocyanate, diphenylene-4,4′-diisocyanate, 4,4′-diisocyanato-3,3′-dimethyldiphenyl, 3- Examples thereof include methyldiphenylmethane-4,4′-diisocyanate, diphenyl ether-4,4′-diisocyanate and the like. Examples of the araliphatic diisocyanate include α, α, α ′, α′-tetramethylxylylene diisocyanate. Examples of the isocyanurates include tris-isocyanatoalkyl-isocyanurate and triisocyanatocycloalkyl-isocyanurate.
These can be used alone or in combination of two or more.

As a mixing ratio when the polyisocyanate (PIC) and the active hydrogen group-containing polyester resin (for example, a hydroxyl group-containing polyester resin) are reacted, the isocyanate group [NCO] in the polyisocyanate (PIC) and the hydroxyl group-containing group are used. The mixing equivalent ratio ([NCO] / [OH]) with the hydroxyl group [OH] in the polyester resin is usually preferably 5/1 to 1/1, and 4/1 to 1.2 / 1. Is more preferable, and 3/1 to 1.5 / 1 is particularly preferable.
When the isocyanate group [NCO] exceeds 5, the low-temperature fixability may be deteriorated, and when it is less than 1, the offset resistance may be deteriorated.

There is no restriction | limiting in particular as content in the said isocyanate group containing polyester prepolymer (A) of the said polyisocyanate (PIC), Although it can select suitably according to the objective, For example, 0.5-40 mass% is Preferably, 1-30 mass% is more preferable, and 2-20 mass% is still more preferable.
When the content is less than 0.5% by mass, the hot offset resistance is deteriorated, and it may be difficult to achieve both heat resistant storage stability and low-temperature fixability. When the content exceeds 40% by mass, Low temperature fixability may deteriorate.

As an average number of the isocyanate groups contained per molecule of the isocyanate group-containing polyester prepolymer (A), 1 or more is preferable, 1.2 to 5 is more preferable, and 1.5 to 4 is more preferable.
When the average number of the isocyanate groups is less than 1, the molecular weight of the polyester resin (RMPE) modified with the urea bond-forming group is lowered, and the hot offset resistance may be deteriorated.

  The weight average molecular weight (Mw) of the polymer capable of reacting with the active hydrogen group-containing compound is 1,000 to 30,000 in terms of molecular weight distribution by GPC (gel permeation chromatography) soluble in tetrahydrofuran (THF). Preferably, 1,500-15,000 are more preferable. When the weight average molecular weight (Mw) is less than 1,000, the heat resistant storage stability may be deteriorated, and when it exceeds 30,000, the low temperature fixability may be deteriorated.

The measurement of the molecular weight distribution by the gel permeation chromatography (GPC) can be performed, for example, as follows.
That is, first, the column is stabilized in a 40 ° C. heat chamber. At this temperature, tetrahydrofuran (THF) as a column solvent is allowed to flow at a flow rate of 1 ml per minute, and 50 to 200 μl of a tetrahydrofuran sample solution of a resin whose sample concentration is adjusted to 0.05 to 0.6 mass% is injected and measured. In measuring the molecular weight of the sample, the molecular weight distribution of the sample is calculated from the relationship between the logarithmic value of the calibration curve created by several monodisperse polystyrene standard samples and the count number. Examples of standard polystyrene samples for preparing the calibration curve include Pressure Chemical Co. Or the molecular weights made by Toyo Soda Industry Co., Ltd. are 6 × 10 ² , 2.1 × 10 ² , 4 × 10 ² , 1.75 × 10 ⁴ , 1.1 × 10 ⁵ , 3.9 × 10 ⁵ , 8. It is preferable to use 6 × 10 ⁵ , 2 × 10 ⁶ , and 4.48 × 10 ⁶ , and use at least about 10 standard polystyrene samples. As the detector, an RI (refractive index) detector can be used.

--Binder resin--
There is no restriction | limiting in particular as said binder resin, According to the objective, it can select suitably, For example, although a polyester resin etc. are mentioned, Unmodified polyester resin (unmodified polyester resin) is especially preferable.
When the unmodified polyester resin is contained in the toner, low-temperature fixability and glossiness can be improved.
Examples of the unmodified polyester resin include those similar to the urea bond-forming group-containing polyester resin, that is, a polycondensate of a polyol (PO) and a polycarboxylic acid (PC). The unmodified polyester resin is partially compatible with the urea bond-forming group-containing polyester resin (RMPE), that is, has a similar structure that is compatible with each other. It is preferable in terms of resistance to hot offset.

  The weight average molecular weight (Mw) of the unmodified polyester resin is preferably 1,000 to 30,000, preferably 1,500 to 15, in terms of molecular weight distribution by GPC (gel permeation chromatography) soluble in tetrahydrofuran (THF). 1,000 is more preferable. When the weight average molecular weight (Mw) is less than 1,000, the heat resistant storage stability may be deteriorated. Therefore, the content of the component having the weight average molecular weight (Mw) of less than 1,000 as described above Needs to be 8 to 28% by mass. On the other hand, when the weight average molecular weight (Mw) exceeds 30,000, the low-temperature fixability may be deteriorated.

Here, the measurement of the said weight average molecular weight can be performed as follows.
Gel permeation chromatography (GPC) measuring device: GPC-8220 GPC (manufactured by Tosoh Corporation)
Column: TSK gel SuperHZM-H 15cm triple (made by Tosoh Corporation)
Temperature: 40 ° C
Solvent: tetrahydrofuran (THF)
Flow rate: 0.35 ml / min
Sample: 0.4 ml of 0.15 mass% sample was injected Sample pretreatment: Sample was dissolved in tetrahydrofuran THF (stabilized Wako Pure Chemical Industries, Ltd.) at 0.15 mass% and filtered through a 0.2 μm filter. The filtrate is used as a sample. 100 μl of the THF sample solution is injected and measured. In measuring the molecular weight of a sample, the molecular weight distribution of the sample is calculated from the relationship between the logarithmic value of a calibration curve prepared from several types of monodisperse polystyrene standard samples and the number of counts. As a standard polystyrene sample for preparing a calibration curve, Showd STANDARD Std. No. S-7300, S-210, S-390, S-875, S-1980, S-10.9, S-629, S-3.0, S-0.580, and toluene were used. An RI (refractive index) detector was used as the detector.

The glass transition temperature of the unmodified polyester resin is usually 30 to 70 ° C, more preferably 35 to 70 ° C, still more preferably 35 to 50 ° C, and particularly preferably 35 to 45 ° C. When the glass transition temperature is less than 30 ° C., the heat-resistant storage stability of the toner may be deteriorated, and when it exceeds 70 ° C., the low-temperature fixability may be insufficient.
The hydroxyl value of the unmodified polyester resin is preferably 5 mgKOH / g, more preferably 10 to 120 mgKOH / g, and still more preferably 20 to 80 mgKOH / g. When the hydroxyl value is less than 5 mgKOH / g, it may be difficult to achieve both heat-resistant storage stability and low-temperature fixability.
The acid value of the unmodified polyester resin is preferably 1.0 to 50.0 mgKOH / g, more preferably 1.0 to 45.0 mgKOH / g, and still more preferably 15.0 to 45.0 mgKOH / g. Generally, it becomes easy to be negatively charged by giving the toner an acid value.

Here, the acid value (AV) and the hydroxyl value (OHV) are specifically determined by the following procedure.
・ Measuring device: potentiometric automatic titrator DL-53 Titrator (Metler Toledo)
-Electrode used: DG113-SC (manufactured by METTLER TOLEDO)
・ Analysis software: LabX Light Version1.00.000
-Calibration of apparatus: Use a mixed solvent of 120 ml of toluene and 30 ml of ethanol.
・ Measurement temperature: 23 ℃
The measurement conditions are as follows.
Stir
Speed [%] 25
Time [s] 15
EQP titration
Titrant / Sensor
Titrant CH ₃ ONa
Concentration [mol / L] 0.1
Sensor DG115
Unit of measurement mV
Predispensing to volume
Volume [mL] 1.0
Wait time [s] 0
Titrant addition Dynamic
dE (set) [mV] 8.0
dV (min) [mL] 0.03
dV (max) [mL] 0.5
Measure mode Equilibrium controlled
dE [mV] 0.5
dt [s] 1.0
t (min) [s] 2.0
t (max) [s] 20.0
Recognition
Threshold 100.0
Steepest jump only No
Range No
Tendency None
Termination
At maximum volume [mL] 10.0
At potential No
At slope No
After number EQPs Yes
n = 1
comb. Termination conditions No
Evaluation
Procedure Standard
Potential 1 No
Potential 2 No
Stop for reevaluation No

-Method of measuring acid value-
The acid value is measured under the following conditions based on the measurement method described in JIS K0070-1992.
Sample preparation: 0.5 g of toner (0.3 g for ethyl acetate-soluble component) is added to 120 ml of toluene and dissolved by stirring for about 10 hours at room temperature (23 ° C.). Furthermore, 30 ml of ethanol is added to prepare a sample solution.
The measurement can be calculated by the apparatus described above, but specifically, the calculation is performed as follows.
Titrate with a pre-standardized N / 10 caustic potassium to alcohol solution, and determine the acid value from the consumption of the alcohol potassium solution by the following formula.
Acid value = KOH (ml) x N x 56.1 / sample mass (where N is a factor of N / 10 KOH)

-Measurement method of hydroxyl value-
Weigh accurately 0.5 g of sample into a 100 ml volumetric flask and add 5 ml of acetylating reagent correctly. Then, it is immersed in a bath at 100 ° C. ± 5 ° C. and heated. After 1-2 hours, the flask is removed from the bath, allowed to cool, water is added and shaken to decompose acetic anhydride. Next, in order to complete the decomposition, the flask is again heated in a bath for 10 minutes or more and allowed to cool, and then the wall of the flask is thoroughly washed with an organic solvent. This solution is subjected to potentiometric titration with an N / 2 potassium hydroxide ethyl alcohol solution using the electrode to determine the OH value (according to JIS K0070-1966).

When the unmodified polyester resin is contained in the toner, the mixing mass ratio (RMPE / PE) of the urea bond-forming group-containing polyester resin (RMPE) and the unmodified polyester resin (PE) is 5/95. -25/75 is preferable, and 10 / 90-25 / 75 is more preferable.
When the mixing mass ratio of the unmodified polyester resin (PE) exceeds 95, the hot offset resistance is deteriorated, and it may be difficult to achieve both heat-resistant storage stability and low-temperature fixability. Glossiness may deteriorate.
As content of the said non-modified polyester resin in the said binder resin, 50-100 mass% is preferable, for example, 70-95 mass% is more preferable, 80-90 mass% is still more preferable. When the content is less than 50% by mass, the low-temperature fixability and the glossiness of the image may be deteriorated.

-Other ingredients-
There is no restriction | limiting in particular as said other component, According to the objective, it can select suitably, For example, a coloring agent, a mold release agent, a charge control agent, an inorganic fine particle, a fluid improvement agent, a cleaning property improvement agent, magnetic Materials, metal soaps, and the like.

The colorant is not particularly limited and may be appropriately selected from known dyes and pigments according to the purpose. For example, carbon black, nigrosine dye, iron black, naphthol yellow S, Hansa yellow (10G, 5G, G), cadmium yellow, yellow iron oxide, ocher, yellow lead, titanium yellow, polyazo yellow, oil yellow, Hansa yellow (GR, A, RN, R), pigment yellow L, benzidine yellow (G, GR), Permanent Yellow (NCG), Vulcan Fast Yellow (5G, R), Tartrazine Lake, Quinoline Yellow Lake, Anthrazan Yellow BGL, Isoindolinone Yellow, Bengala, Lead Red, Lead Red, Cadmium Red, Cad Muum Mercury Red, Antimon Zhu, Permanent Red 4R, PA Red, Faise Red, Parachlor Ortho Nitroaniline Red, Resol Fast Scarlet G, Brilliant Fast Scarlet, Brilliant Carmine BS, Permanent Red (F2R, F4R, FRL, FRLL, F4RH), Fast Scarlet VD, Belkan Fast Rubin B, Brilliant Scarlet G, Risor Rubin GX, Permanent Red F5R, Brilliant Carmine 6B, Pogment Scarlet 3B, Bordeaux 5B, Toluidine Maroon, Permanent Bordeaux F2K, Helio Bordeaux BL, Bordeaux 10B, Bon Maroon Light, Bon Maroon Medium, Eosin Lake, Rhodamine Lake B, Rhodamine Lake Y, Alizarin Lake, Thioindigo Red B, Thioindigo Maroon, Oh Lured, Quinacridone Red, Pyrazolone Red, Polyazo Red, Chrome Vermilion, Benzidine Orange, Perinone Orange, Oil Orange, Cobalt Blue, Cerulean Blue, Alkaline Blue Lake, Peacock Blue Lake, Victoria Blue Lake, Metal Free Phthalocyanine Blue, Phthalocyanine Blue, Fast Sky Blue, Indanthrene Blue (RS, BC), Indigo, Ultramarine Blue, Bitumen, Anthraquinone Blue, Fast Violet B, Methyl Violet Lake, Cobalt Purple, Manganese Purple, Dioxane Violet, Anthraquinone Violet, Chrome Green, Zinc Green, Oxidation Chrome, Pyridian, Emerald Green, Pigment Green B, Naphthol Green B, Green Gold, Ash Examples include green lake, malachite green lake, phthalocyanine green, anthraquinone green, titanium oxide, zinc white, and lithobon.
These may be used individually by 1 type and may use 2 or more types together.

The content of the colorant in the toner is not particularly limited and may be appropriately selected depending on the intended purpose, but is preferably 1 to 15% by mass, and more preferably 3 to 10% by mass.
When the content is less than 1% by mass, a reduction in the coloring power of the toner is observed. When the content exceeds 15% by mass, poor pigment dispersion in the toner occurs, the coloring power decreases, The characteristics may be degraded.

  The colorant may be used as a master batch combined with a resin. The resin is not particularly limited and may be appropriately selected from known ones according to the purpose. For example, styrene or a substituted polymer thereof, a styrene copolymer, polymethyl methacrylate, polybutyl methacrylate , Polyvinyl chloride, polyvinyl acetate, polyethylene, polypropylene, polyester, epoxy resin, epoxy polyol resin, polyurethane, polyamide, polyvinyl butyral, polyacrylic acid resin, rosin, modified rosin, terpene resin, aliphatic hydrocarbon resin, alicyclic ring Aromatic hydrocarbon resin, aromatic petroleum resin, chlorinated paraffin, paraffin, and the like. These may be used individually by 1 type and may use 2 or more types together.

  Examples of the polymer of styrene or a substituted product thereof include polyester resin, polystyrene, poly p-chlorostyrene, polyvinyl toluene, and the like. Examples of the styrene copolymer include a styrene-p-chlorostyrene copolymer, a styrene-propylene copolymer, a styrene-vinyltoluene copolymer, a styrene-vinylnaphthalene copolymer, and a styrene-methyl acrylate copolymer. Polymer, styrene-ethyl acrylate copolymer, styrene-butyl acrylate copolymer, styrene-octyl acrylate copolymer, styrene-methyl methacrylate copolymer, styrene-ethyl methacrylate copolymer, styrene- Butyl methacrylate copolymer, styrene-α-chloromethyl methacrylate copolymer, styrene-acrylonitrile copolymer, styrene-vinyl methyl ketone copolymer, styrene-butadiene copolymer, styrene-isoprene copolymer, styrene An acrylonitrile-indene copolymer, Styrene - maleic acid copolymer, styrene - maleic acid ester copolymer, and the like.

  The masterbatch can be produced by mixing or kneading the masterbatch resin and the colorant under high shear. At this time, it is preferable to add an organic solvent in order to enhance the interaction between the colorant and the resin. Also, the so-called flushing method is preferable in that the wet cake of the colorant can be used as it is, and there is no need to dry it. This flushing method is a method of mixing or kneading an aqueous paste containing water of a colorant together with a resin and an organic solvent, and transferring the colorant to the resin side to remove moisture and organic solvent components. For the mixing or kneading, for example, a high shear dispersion device such as a three-roll mill is preferably used.

There is no restriction | limiting in particular as said mold release agent, According to the objective, it can select suitably from well-known things, For example, waxes etc. are mentioned suitably.
Examples of the waxes include carbonyl group-containing waxes, polyolefin waxes, long chain hydrocarbons, and the like. These may be used individually by 1 type and may use 2 or more types together. Among these, a carbonyl group-containing wax is preferable.
Examples of the carbonyl group-containing wax include polyalkanoic acid esters, polyalkanol esters, polyalkanoic acid amides, polyalkylamides, dialkyl ketones, and the like. Examples of the polyalkanoic acid ester include carnauba wax, montan wax, trimethylolpropane tribehenate, pentaerythritol tetrabehenate, pentaerythritol diacetate dibehenate, glycerin tribehenate, and 1,18-octadecane. Examples thereof include diol distearate. Examples of the polyalkanol ester include tristearyl trimellitic acid and distearyl maleate. Examples of the polyalkanoic acid amide include dibehenyl amide. Examples of the polyalkylamide include trimellitic acid tristearylamide. Examples of the dialkyl ketone include distearyl ketone. Of these carbonyl group-containing waxes, polyalkanoic acid esters are particularly preferred.
Examples of the polyolefin wax include polyethylene wax and polypropylene wax.
Examples of the long chain hydrocarbon include paraffin wax and sazol wax.

There is no restriction | limiting in particular as melting | fusing point of the said mold release agent, Although it can select suitably according to the objective, 40-160 degreeC is preferable, 50-120 degreeC is more preferable, 60-90 degreeC is especially preferable.
When the melting point is less than 40 ° C., the wax may adversely affect the heat-resistant storage stability, and when it exceeds 160 ° C., cold offset may easily occur during fixing at a low temperature.
The melt viscosity of the release agent is preferably 5 to 1000 cps, more preferably 10 to 100 cps, as a measured value at a temperature 20 ° C. higher than the melting point of the wax.
If the melt viscosity is less than 5 cps, the releasability may be lowered, and if it exceeds 1000 cps, the effect of improving hot offset resistance and low-temperature fixability may not be obtained.

There is no restriction | limiting in particular as content in the said toner of the said mold release agent, Although it can select suitably according to the objective, 0-40 mass% is preferable and 3-30 mass% is more preferable.
When the content exceeds 40% by mass, the fluidity of the toner may be deteriorated.

The charge control agent is not particularly limited and may be appropriately selected from known ones according to the purpose. However, since a color tone may change when a colored material is used, a colorless or nearly white material may be used. Preferably, for example, triphenylmethane dyes, molybdate chelate pigments, rhodamine dyes, alkoxyamines, quaternary ammonium salts (including fluorine-modified quaternary ammonium salts), alkylamides, phosphorus alone or compounds thereof, tungsten Examples thereof include a single substance or a compound thereof, a fluorine-based activator, a metal salt of salicylic acid, and a metal salt of a salicylic acid derivative. These may be used individually by 1 type and may use 2 or more types together.
Commercially available products may be used as the charge control agent. Examples of the commercially available products include quaternary ammonium salt Bontron P-51, oxynaphthoic acid metal complex E-82, and salicylic acid metal complex. E-84, E-89 of a phenol-based condensate (above, manufactured by Orient Chemical Industries), TP-302, TP-415 of a quaternary ammonium salt molybdenum complex (above, manufactured by Hodogaya Chemical Co., Ltd.), Fourth Copy charge PSY VP2038 of quaternary ammonium salt, copy blue PR of triphenylmethane derivative, copy charge of quaternary ammonium salt NEG VP2036, copy charge NX VP434 (manufactured by Hoechst), LRA-901, LR which is a boron complex -147 (manufactured by Nippon Carlit), quinacridone, azo pigment, other sulfonic acid groups, carbo Sill group, polymer compounds having a functional group such as quaternary ammonium salts, and the like.
The charge control agent may be melted and kneaded with the master batch and then dissolved or dispersed, or may be added together with the toner components when directly dissolving or dispersing in the organic solvent, or The toner particles may be fixed on the toner surface after production.

  The content of the charge control agent in the toner varies depending on the type of the binder resin, the presence / absence of an additive, a dispersion method, and the like, and cannot be generally specified. On the other hand, 0.1-10 mass parts is preferable, and 0.2-5 mass parts is more preferable. When the content is less than 0.1 parts by mass, the charge controllability may not be obtained. When the content exceeds 10 parts by mass, the chargeability of the toner becomes too large, and the effect of the main charge control agent is reduced. As a result, the electrostatic attractive force with the developing roller increases, which may lead to a decrease in developer fluidity and a decrease in image density.

-Resin fine particles-
The resin fine particle is not particularly limited as long as it is a resin that can form an aqueous dispersion in an aqueous medium, and can be appropriately selected from known resins according to the purpose, and may be a thermoplastic resin. It may be a thermosetting resin, for example, vinyl resin, polyurethane resin, epoxy resin, polyester resin, polyamide resin, polyimide resin, silicon resin, phenol resin, melamine resin, urea resin, aniline resin, ionomer resin, polycarbonate. Examples of the resin include vinyl resins. Of these, vinyl resins are particularly preferable.
These may be used individually by 1 type and may use 2 or more types together. Among these, at least one selected from a vinyl resin, a polyurethane resin, an epoxy resin, and a polyester resin is preferable because an aqueous dispersion of fine spherical resin fine particles can be easily obtained.
The vinyl resin is a polymer obtained by homopolymerizing or copolymerizing a vinyl monomer. For example, a styrene- (meth) acrylic acid ester resin, a styrene-butadiene copolymer, a (meth) acrylic acid-acrylic acid ester polymer. Styrene-acrylonitrile copolymer, styrene-maleic anhydride copolymer, styrene- (meth) acrylic acid copolymer, and the like.
Moreover, as the resin fine particles, a copolymer comprising a monomer having at least two unsaturated groups can be used.
The monomer having at least two unsaturated groups is not particularly limited and may be appropriately selected depending on the intended purpose. For example, a sodium salt of ethylene oxide methacrylate adduct sulfate (“Eleminol RS-30”). ", Sanyo Chemical Industries, Ltd.), divinylbenzene, 1,6-hexanediol acrylate, and the like.

  The resin fine particles can be obtained by polymerization according to a known method appropriately selected according to the purpose, but is preferably obtained as an aqueous dispersion of the resin fine particles. The method for preparing the aqueous dispersion of the resin fine particles is, for example, (1) In the case of the vinyl resin, a vinyl monomer is used as a starting material and is selected from suspension polymerization, emulsion polymerization, seed polymerization, and dispersion polymerization. (2) In the case of polyaddition or condensation resin such as polyester resin, polyurethane resin, epoxy resin, etc., a precursor (monomer, oligomer). Or the like, or a solvent solution thereof is dispersed in an aqueous medium in the presence of an appropriate dispersant, and then heated or added with a curing agent to be cured to produce an aqueous dispersion of resin fine particles (3) ) In the case of polyaddition or condensation resin such as polyester resin, polyurethane resin, epoxy resin, etc., it may be a precursor (monomer, oligomer, etc.) or a solvent solution thereof (liquid). (4) Preliminary polymerization reaction (addition polymerization, ring-opening polymerization, polyaddition, addition) After the resin prepared by any polymerization reaction mode such as condensation and condensation polymerization is pulverized using a mechanical pulverizer or jet type pulverizer and then classified to obtain resin fine particles , A method of dispersing in water in the presence of an appropriate dispersant, (5) prepared in advance by a polymerization reaction (any polymerization reaction mode such as addition polymerization, ring-opening polymerization, polyaddition, addition condensation, condensation polymerization, etc.) (6) A polymerization reaction (addition polymerization) in advance, in which resin fine particles are obtained by spraying a resin solution in which the resin is dissolved in a solvent to obtain resin fine particles and then dispersing the resin fine particles in water in the presence of an appropriate dispersant. , Ring-opening polymerization, polyaddition, addition condensation The resin fine particles can be obtained by adding a poor solvent to a resin solution obtained by dissolving a resin prepared in a solvent by a polymerization reaction method such as condensation polymerization or by cooling a resin solution previously dissolved in a solvent by heating. And then removing the solvent to obtain resin particles, and then dispersing the resin particles in water in the presence of a suitable dispersant. (7) Polymerization reaction (addition polymerization, ring-opening polymerization, heavy polymerization) in advance (Any polymerization reaction mode such as addition, addition condensation, and condensation polymerization may be used.) A resin solution prepared by dissolving a resin prepared in a solvent in a solvent is dispersed in an aqueous medium and then heated or heated. (8) A resin prepared in advance by a polymerization reaction (which may be any polymerization reaction mode such as addition polymerization, ring-opening polymerization, polyaddition, addition condensation or condensation polymerization) is used as a solvent. In the dissolved resin solution A method of dissolving a suitable emulsifier and then adding water to carry out phase inversion emulsification is preferable.

  Examples of the toner include toners produced by a known suspension polymerization method, emulsion aggregation method, emulsion dispersion method, etc., and can react with an active hydrogen group-containing compound and the active hydrogen group-containing compound. The toner material containing the polymer is dissolved in an organic solvent to prepare a toner solution, and then the toner solution is dispersed in an aqueous medium to prepare a dispersion, and the active hydrogen group-containing solution is prepared in the aqueous medium. A toner obtained by reacting a compound with a polymer capable of reacting with the active hydrogen group-containing compound to form an adhesive substrate in the form of particles and removing the organic solvent is preferred.

-Toner solution-
The toner solution can be prepared by dissolving the toner material in the organic solvent.

-Organic solvent-
The organic solvent is not particularly limited as long as it is a solvent that can dissolve or disperse the toner material, and can be appropriately selected according to the purpose. For example, the boiling point is less than 150 ° C. in terms of ease of removal. Volatile ones are preferred, for example, toluene, xylene, benzene, carbon tetrachloride, methylene chloride, 1,2-dichloroethane, 1,1,2-trichloroethane, trichloroethylene, chloroform, monochlorobenzene, dichloroethylidene, methyl acetate, acetic acid Examples include ethyl, methyl ethyl ketone, and methyl isobutyl ketone. Among these, toluene, xylene, benzene, methylene chloride, 1,2-dichloroethane, chloroform, carbon tetrachloride and the like are preferable, and ethyl acetate is particularly preferable. These may be used individually by 1 type and may use 2 or more types together.
There is no restriction | limiting in particular as the usage-amount of the said organic solvent, According to the objective, it can select suitably, For example, 40-300 mass parts is preferable with respect to 100 mass parts of said toner materials, and 60-140 mass parts is preferable. More preferably, 80-120 mass parts is still more preferable.

-Dispersion-
The dispersion is prepared by dispersing the toner solution in an aqueous medium.
When the toner solution is dispersed in the aqueous medium, a dispersion (oil droplets) made of the toner solution is formed in the aqueous medium.

--- Aqueous medium--
The aqueous medium is not particularly limited and may be appropriately selected from known ones. Examples thereof include water, solvents miscible with water, and mixtures thereof. Among these, Is particularly preferred.
The solvent miscible with water is not particularly limited as long as it is miscible with water, and examples thereof include alcohol, dimethylformamide, tetrahydrofuran, cellosolves, and lower ketones.
Examples of the alcohol include methanol, isopropanol, ethylene glycol and the like. Examples of the lower ketones include acetone and methyl ethyl ketone.
These may be used individually by 1 type and may use 2 or more types together.

The toner solution is preferably dispersed in the aqueous medium with stirring.
The dispersion method is not particularly limited and can be appropriately selected using a known disperser. Examples of the disperser include a low-speed shear disperser, a high-speed shear disperser, and a friction disperser. High pressure jet disperser, ultrasonic disperser, and the like. Among these, a high-speed shearing disperser is preferable in that the particle size of the dispersion (oil droplets) can be controlled to 2 to 20 μm.
When the high-speed shearing disperser is used, conditions such as the rotation speed, dispersion time, and dispersion temperature are not particularly limited and can be appropriately selected according to the purpose. For example, the rotation speed is 1 3,000 to 30,000 rpm is preferable, 5,000 to 20,000 rpm is more preferable, and the dispersion time is preferably 0.1 to 5 minutes in the case of a batch method, and the dispersion temperature is under pressure. 0-150 degreeC is preferable and 40-98 degreeC is more preferable. The dispersion temperature is generally easier when the temperature is higher.

As an example of the method for producing the toner, a method for producing the toner by forming the adhesive base material in the form of particles will be described below.
In the method of granulating the toner by forming the adhesive substrate into particles, for example, preparation of an aqueous medium phase, preparation of the toner solution, preparation of the dispersion, addition of the aqueous medium, etc. Synthesis of a polymer (prepolymer) capable of reacting with an active hydrogen group-containing compound, synthesis of the active hydrogen group-containing compound, etc.).

The aqueous medium phase can be prepared, for example, by dispersing the resin fine particles in the aqueous medium. There is no restriction | limiting in particular as the addition amount in this aqueous medium of this resin fine particle, According to the objective, it can select suitably, For example, 0.5-10 mass% is preferable.
The toner solution is prepared by adding, in the organic solvent, the active hydrogen group-containing compound, a polymer capable of reacting with the active hydrogen group-containing compound, the colorant, the release agent, the charge control agent, and the unmodified. A toner material such as a polyester resin can be dissolved or dispersed.
In the toner material, components other than the polymer (prepolymer) capable of reacting with the active hydrogen group-containing compound are added when the resin fine particles are dispersed in the aqueous medium in the aqueous medium phase preparation. It may be added and mixed in the aqueous medium, or when the toner solution is added to the aqueous medium phase, it may be added to the aqueous medium phase together with the toner solution.

The dispersion can be prepared by emulsifying and dispersing the previously prepared toner solution in the previously prepared aqueous medium phase. In the emulsification / dispersion, when the active hydrogen group-containing compound and the polymer capable of reacting with the active hydrogen group-containing compound are subjected to an extension reaction or a crosslinking reaction, the adhesive base material is generated.
The adhesive substrate (for example, the urea-modified polyester resin) includes, for example, (1) a polymer that can react with the active hydrogen group-containing compound (for example, the isocyanate group-containing polyester prepolymer (A)). A toner solution is emulsified or dispersed in the aqueous medium phase together with the active hydrogen group-containing compound (for example, the amines (B)) to form a dispersion, and both are subjected to an extension reaction or the like in the aqueous medium phase. (2) The toner solution is emulsified or dispersed in the aqueous medium to which the active hydrogen group-containing compound has been added in advance, to form a dispersion, and in the aqueous medium phase Or (3) the active hydrogen group after the toner solution is added and mixed in the aqueous medium. The organic compound is added to form a dispersion, it may be generated by elongation reaction or crosslinking reaction from particle interfaces in the aqueous medium phase. In the case of (3), a modified polyester resin is preferentially produced on the surface of the toner to be produced, and a concentration gradient can be provided in the toner particles.

  The reaction conditions for producing the adhesive base material by the emulsification or dispersion are not particularly limited, depending on the combination of the polymer capable of reacting with the active hydrogen group-containing compound and the active hydrogen group-containing compound. The reaction time is preferably 10 minutes to 40 hours, more preferably 2 hours to 24 hours, and the reaction temperature is preferably 0 to 150 ° C, more preferably 40 to 98 ° C.

  In the aqueous medium phase, as a method for stably forming the dispersion containing a polymer capable of reacting with the active hydrogen group-containing compound (for example, the isocyanate group-containing polyester prepolymer (A)), for example, In an aqueous medium phase, a polymer capable of reacting with the active hydrogen group-containing compound (for example, the isocyanate group-containing polyester prepolymer (A)), the colorant, the release agent, the charge control agent, the unmodified Examples thereof include a method in which the toner solution prepared by dissolving or dispersing the toner material such as polyester resin in the organic solvent is added and dispersed by shearing force. The details of the dispersion method are as described above.

In the preparation of the dispersion, if necessary, a dispersant is used from the viewpoint of stabilizing the dispersion (oil droplets composed of the toner solution) and sharpening the particle size distribution while obtaining a desired shape. Is preferred.
There is no restriction | limiting in particular as said dispersing agent, According to the objective, it can select suitably, For example, surfactant, a slightly water-soluble inorganic compound dispersing agent, a polymeric protective colloid, etc. are mentioned. These may be used individually by 1 type and may use 2 or more types together. Among these, surfactants are preferable.

Examples of the surfactant include an anionic surfactant, a cationic surfactant, a nonionic surfactant, and an amphoteric surfactant.
Examples of the anionic surfactant include alkylbenzene sulfonates, α-olefin sulfonates, phosphate esters and the like, and those having a fluoroalkyl group are preferable. Examples of the anionic surfactant having a fluoroalkyl group include a fluoroalkylcarboxylic acid having 2 to 10 carbon atoms or a metal salt thereof, disodium perfluorooctanesulfonylglutamate, 3- [omega-fluoroalkyl (6 carbon atoms). -11) Oxy] -1-alkyl (carbon number 3-4) sodium sulfonate, 3- [omega-fluoroalkanoyl (carbon number 6-8) -N-ethylamino] -1-propanesulfonic acid sodium, fluoroalkyl (Carbon number 11-20) carboxylic acid or its metal salt, perfluoroalkyl carboxylic acid (carbon number 7-13) or its metal salt, perfluoroalkyl (carbon number 4-12) sulfonic acid or its metal salt, perfluoro Octanesulfonic acid diethanolamide, N-propyl-N- (2-hydroxy Ethyl) perfluorooctanesulfonamide, perfluoroalkyl (carbon number 6-10) sulfonamidopropyltrimethylammonium salt, perfluoroalkyl (carbon number 6-10) -N-ethylsulfonylglycine salt, monoperfluoroalkyl (carbon number) 6-16) Ethyl phosphate and the like. Examples of commercially available surfactants having a fluoroalkyl group include Surflon S-111, S-112, S-113 (Asahi Glass Co., Ltd.); Florad FC-93, FC-95, FC-98, FC -129 (Sumitomo 3M Co., Ltd.); Unidyne DS-101, DS-102 (Daikin Industries, Ltd.); 833 (manufactured by Dainippon Ink & Chemicals, Inc.); Xtop EF-102, 103, 104, 105, 112, 123A, 123B, 306A, 501, 201, 204 (manufactured by Tochem Products); 100, F150 (manufactured by Neos) and the like.

  Examples of the cationic surfactant include amine salt type surfactants and quaternary ammonium salt type cationic surfactants. Examples of the amine salt type surfactant include alkylamine salts, aminoalcohol fatty acid derivatives, polyamine fatty acid derivatives, imidazolines, and the like. Examples of the quaternary ammonium salt type cationic surfactant include alkyltrimethylammonium salt, dialkyldimethylammonium salt, alkyldimethylbenzylammonium salt, pyridinium salt, alkylisoquinolinium salt, benzethonium chloride and the like. . Among the cationic surfactants, aliphatic quaternary ammonium salts such as aliphatic primary, secondary or tertiary amine acids having a fluoroalkyl group, and perfluoroalkyl (carbon number 6 to 10) sulfonamidopropyltrimethylammonium salts. Benzalkonium salt, benzethonium chloride, pyridinium salt, imidazolinium salt, and the like. Commercially available products of the cationic surfactant include, for example, Surflon S-121 (Asahi Glass Co., Ltd.); Florad FC-135 (Sumitomo 3M Co., Ltd.); Unidyne DS-202 (Daikin Industries Co., Ltd.), Megafuck F-150, F-824 (manufactured by Dainippon Ink & Chemicals, Inc.); Xtop EF-132 (manufactured by Tochem Products);

Examples of the nonionic surfactant include fatty acid amide derivatives and polyhydric alcohol derivatives.
Examples of the amphoteric surfactant include alanine, dodecyldi (aminoethyl) glycine, di (octylaminoethyl) glycine, N-alkyl-N, N-dimethylammonium betaine and the like.

Examples of the poorly water-soluble inorganic compound dispersant include tricalcium phosphate, calcium carbonate, titanium oxide, colloidal silica, and hydroxyapatite.
Examples of the polymeric protective colloid include acids, (meth) acrylic monomers containing a hydroxyl group, vinyl alcohol or ethers of vinyl alcohol, esters of vinyl alcohol and a compound containing a carboxyl group, amides Examples thereof include homopolymers or copolymers of compounds or their methylol compounds, chlorides, those having a nitrogen atom or a heterocyclic ring thereof, polyoxyethylenes, celluloses, and the like.
Examples of the acids include acrylic acid, methacrylic acid, α-cyanoacrylic acid, α-cyanomethacrylic acid, itaconic acid, crotonic acid, fumaric acid, maleic acid, maleic anhydride, and the like. Examples of the (meth) acrylic monomer containing a hydroxyl group include β-hydroxyethyl acrylate, β-hydroxyethyl methacrylate, β-hydroxypropyl acrylate, β-hydroxypropyl methacrylate, and γ-acrylate. -Hydroxypropyl, γ-hydroxypropyl methacrylate, 3-chloro-2-hydroxypropyl acrylate, 3-chloro-2-hydroxypropyl methacrylate, diethylene glycol monoacrylate, diethylene glycol monomethacrylate, glycerol monoacrylate Glycerin monomethacrylate, N-methylol acrylamide, N-methylol methacrylamide and the like. Examples of the vinyl alcohol or ethers with vinyl alcohol include vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, and the like. Examples of the esters of vinyl alcohol and a compound containing a carboxyl group include vinyl acetate, vinyl propionate, and vinyl butyrate. Examples of the amide compound or these methylol compounds include acrylamide, methacrylamide, diacetone acrylamide acid, or these methylol compounds. Examples of the chlorides include acrylic acid chloride and methacrylic acid chloride. Examples of the homopolymer or copolymer such as those having a nitrogen atom or a heterocyclic ring thereof include vinyl pyridine, vinyl pyrrolidone, vinyl imidazole, and ethylene imine. Examples of the polyoxyethylene are polyoxyethylene, polyoxypropylene, polyoxyethylene alkylamine, polyoxypropylene alkylamine, polyoxyethylene alkylamide, polyoxypropylene alkylamide, polyoxyethylene nonylphenyl ether, polyoxyethylene Examples thereof include oxyethylene lauryl phenyl ether, polyoxyethylene stearyl phenyl ester, and polyoxyethylene nonyl phenyl ester. Examples of the celluloses include methyl cellulose, hydroxyethyl cellulose, and hydroxypropyl cellulose.

In the preparation of the dispersion, a dispersion stabilizer can be used as necessary.
Examples of the dispersion stabilizer include acids that are soluble in acids and alkalis such as calcium phosphate salts.
When the dispersion stabilizer is used, the calcium phosphate salt can be removed from the fine particles by a method of dissolving the calcium phosphate salt with an acid such as hydrochloric acid and then washing with water, or a method of decomposing with an enzyme.

  In the preparation of the dispersion, a catalyst for the extension reaction or the crosslinking reaction can be used. Examples of the catalyst include dibutyltin laurate and dioctyltin laurate.

  The organic solvent is removed from the obtained dispersion (emulsified slurry). The organic solvent is removed by (1) a method of gradually raising the temperature of the entire reaction system to completely evaporate and remove the organic solvent in the oil droplets, and (2) spraying the emulsified dispersion in a dry atmosphere. And a method of completely removing the water-insoluble organic solvent in the oil droplets to form toner fine particles and evaporating and removing the aqueous dispersant together.

  When the organic solvent is removed, toner particles are formed. The toner particles can be washed, dried, etc., and then classified as desired. Classification can be performed, for example, by removing fine particle portions in a liquid by a cyclone, a decanter, centrifugation, or the like, and the classification operation may be performed after obtaining a powder after drying.

Thus, the obtained toner particles are mixed with particles of the colorant, release agent, charge control agent, etc., and further, a mechanical impact force is applied to the release agent from the surface of the toner particles. And the like can be prevented from being detached.
As the method for applying the mechanical impact force, for example, a method in which an impact force is applied to the mixture by blades rotating at a high speed, a mixture is introduced into a high-speed air stream and accelerated to appropriately collide particles or composite particles. The method of making it collide with a board, etc. are mentioned. As an apparatus used in this method, for example, an ong mill (manufactured by Hosokawa Micron), an I-type mill (manufactured by Nippon Pneumatic Co., Ltd.), and a pulverization air pressure are lowered, a hybridization system (manufactured by Nara Machinery Co., Ltd.) ), Kryptron system (manufactured by Kawasaki Heavy Industries, Ltd.), automatic mortar, and the like.

  The toner preferably has the following volume average particle diameter (Dv), volume average particle diameter (Dv) / number average particle diameter (Dn), average circularity, and the like.

The volume average particle diameter (Dv) of the toner is, for example, preferably 3 to 8 μm, more preferably 4 to 7 μm, and still more preferably 5 to 6 μm. Here, the volume average particle diameter is defined as Dv = [(Σ (nD ³ ) / Σn) ^1/3 (where n is the number of particles and D is the particle diameter).
When the volume average particle size is less than 3 μm, in the case of a two-component developer, the toner may be fused to the surface of the carrier during a long period of stirring in the developing device, and the charging ability of the carrier may be reduced. In the developer, toner filming on the developing roller and toner fusion to a member such as a blade are likely to occur because the toner is thinned. When the thickness exceeds 8 μm, the resolution is high and high. It becomes difficult to obtain an image of an image quality, and when the balance of the toner in the developer is performed, the variation in the particle diameter of the toner may increase.

The ratio (Dv / Dn) of the volume average particle diameter (Dv) to the number average particle diameter (Dn) in the toner is preferably 1.00 to 1.15.
When the ratio of the volume average particle diameter to the number average particle diameter (Dv / Dn) is 1.15 or less, the particle size distribution of the toner is relatively sharp and the fixability is improved. If it is less than the above, in the case of a two-component developer, the toner may be fused to the surface of the carrier during long-term agitation in the developing device, and the charging ability of the carrier may be deteriorated or the cleaning property may be deteriorated. In the case of the agent, toner filming on the developing roller and toner thinning are likely to cause toner fusion to a member such as a blade.

  The volume average particle diameter and the ratio (Dv / Dn) between the volume average particle diameter and the number average particle diameter can be measured using, for example, a particle size measuring device “Multisizer III” manufactured by Beckman Coulter, Inc. it can.

The average circularity is a value obtained by dividing the circumference of an equivalent circle having the same projected area as the shape of the toner by the circumference of the actual particles, and is preferably 0.93 to 0.97, for example.
When the average circularity is less than 0.93, the toner is in an irregular shape separated from the spherical shape, and a satisfactory transfer property and a high-quality image free from dust may not be obtained. In an image forming system that employs blade cleaning or the like, defective cleaning occurs on the photosensitive member and the transfer belt, and in the case of image formation with high image area ratio such as dirt on the image, for example, a photographic image. The toner on which an untransferred image is formed due to a paper feed failure or the like may become a transfer residual toner on the photosensitive member, resulting in background smearing of the image, or the charging roller for contact charging the photosensitive member Etc., and the original charging ability may not be exhibited.
Further, it is preferable that 40% by mass or less of toner having an average circularity of 0.98 or more and 35% by mass or less of toner having an average circularity of 0.95 or less.
The average circularity is measured by, for example, an optical detection band method in which a suspension containing toner is passed through an imaging unit detection band on a flat plate, and a particle image is optically detected and analyzed by a CCD camera. For example, it can be measured using a flow type particle image analyzer FPIA-2100 (manufactured by Sysmex Corporation).

  The coloration of the toner is not particularly limited and may be appropriately selected according to the purpose, and may be at least one selected from black toner, cyan toner, magenta toner, and yellow toner. Can be obtained by appropriately selecting the type of the colorant, and is preferably a color toner.

(Developer)
The developer of the present invention contains at least the toner of the present invention, and other components such as a carrier selected appropriately. The developer may be a one-component developer or a two-component developer. However, when it is used for a high-speed printer or the like corresponding to the recent improvement in information processing speed, the life is improved. In view of the above, the two-component developer is preferable.
In the case of the one-component developer using the toner of the present invention, even if the balance of the toner is performed, there is little fluctuation in the particle diameter of the toner, and the filming of the toner on the developing roller or the toner is made thin. Therefore, the toner is not fused to a member such as a blade, and good and stable developability and images can be obtained even when the developing device is used (stirred) for a long time. Further, in the case of the two-component developer using the toner of the present invention, even if the balance of the toner over a long period of time is performed, the fluctuation of the toner particle diameter in the developer is small, and even in the long-term stirring in the developer, Good and stable developability can be obtained.

  There is no restriction | limiting in particular as said carrier, Although it can select suitably according to the objective, What has a core material and the resin layer which coat | covers this core material is preferable.

  There is no restriction | limiting in particular as a material of the said core material, It can select suitably from well-known things, For example, 50-90 emu / g manganese-strontium (Mn-Sr) type material, manganese-magnesium (Mn-) Mg) -based materials and the like are preferable, and highly magnetized materials such as iron powder (100 emu / g or more) and magnetite (75 to 120 emu / g) are preferable in terms of securing image density. In addition, a weakly magnetized material such as a copper-zinc (Cu—Zn) -based (30 to 80 emu / g) is advantageous in that it can weaken the contact with the photoconductor in which the toner is in a spiked state and is advantageous in improving the image quality. Is preferred. These may be used alone or in combination of two or more.

The particle diameter of the core material is preferably an average particle diameter (volume average particle diameter (D ₅₀ )) of 10 to 200 μm, and more preferably 40 to 100 μm.
When the average particle diameter (volume average particle diameter (D ₅₀ )) is less than 10 μm, the distribution of carrier particles may increase the number of fine powders, lower the magnetization per particle, and cause carrier scattering. If the thickness exceeds 150 μm, the specific surface area may decrease and toner scattering may occur. In the case of a full color having a large solid portion, the reproduction of the solid portion may be deteriorated.

  The material of the resin layer is not particularly limited and can be appropriately selected from known resins according to the purpose. For example, amino resins, polyvinyl resins, polystyrene resins, halogenated olefin resins, Polyester resin, polycarbonate resin, polyethylene resin, polyvinyl fluoride resin, polyvinylidene fluoride resin, polytrifluoroethylene resin, polyhexafluoropropylene resin, copolymer of vinylidene fluoride and acrylic monomer, fluorine And a copolymer of vinylidene fluoride and vinyl fluoride, a fluoroterpolymer such as a terpolymer of tetrafluoroethylene, vinylidene fluoride and a non-fluorinated monomer, and a silicone resin. These may be used individually by 1 type and may use 2 or more types together.

  Examples of the amino resin include urea-formaldehyde resin, melamine resin, benzoguanamine resin, urea resin, polyamide resin, and epoxy resin. Examples of the polyvinyl resin include acrylic resin, polymethyl methacrylate resin, polyacrylonitrile resin, polyvinyl acetate resin, polyvinyl alcohol resin, and polyvinyl butyral resin. Examples of the polystyrene resin include polystyrene resin and styrene-acrylic copolymer resin. Examples of the halogenated olefin resin include polyvinyl chloride. Examples of the polyester resin include polyethylene terephthalate resin and polybutylene terephthalate resin.

  The resin layer may contain conductive powder or the like as necessary. Examples of the conductive powder include metal powder, carbon black, titanium oxide, tin oxide, and zinc oxide. The average particle diameter of these conductive powders is preferably 1 μm or less. When the average particle diameter exceeds 1 μm, it may be difficult to control electric resistance.

For example, the resin layer is prepared by dissolving the silicone resin or the like in a solvent to prepare a coating solution, and then uniformly coating the coating solution on the surface of the core material by a known coating method, drying, and baking. It can be formed by doing. Examples of the application method include an immersion method, a spray method, and a brush coating method.
There is no restriction | limiting in particular as said solvent, Although it can select suitably according to the objective, For example, toluene, xylene, methyl ethyl ketone, methyl isobutyl ketone, cersol butyl acetate, etc. are mentioned.
The baking is not particularly limited, and may be an external heating method or an internal heating method. For example, a stationary electric furnace, a fluid electric furnace, a rotary electric furnace, a burner furnace, etc. The method of using, the method of using a microwave, etc. are mentioned.

The amount of the resin layer in the carrier is preferably 0.01 to 5.0% by mass.
When the amount is less than 0.01% by mass, the uniform resin layer may not be formed on the surface of the core material. When the amount exceeds 5.0% by mass, the resin layer becomes thick. In some cases, granulation of carriers occurs, and uniform carrier particles may not be obtained.

When the developer is the two-component developer, the content of the carrier in the two-component developer is not particularly limited and may be appropriately selected depending on the intended purpose. For example, 90 to 98% by mass Is preferable, and 93-97 mass% is more preferable.
The mixing ratio of the toner and the carrier of the two-component developer is generally 1 to 10.0 parts by mass of the toner with respect to 100 parts by mass of the carrier.

Since the developer of the present invention contains the toner of the present invention, the developer of the present invention is excellent in offset resistance and heat-resistant storage stability and can stably form a clear and high-quality image.
The developer of the present invention can be suitably used for image formation by various known electrophotographic methods such as a magnetic one-component development method, a non-magnetic one-component development method, and a two-component development method. It can be particularly suitably used for containers, process cartridges, image forming apparatuses and image forming methods.

(Toner container)
The toner-containing container of the present invention comprises the toner or the developer of the present invention contained in a container.
There is no restriction | limiting in particular as said container, It can select suitably from well-known things, For example, what has a toner container main body and a cap etc. are mentioned suitably.
The size, shape, structure, material and the like of the toner container body are not particularly limited and can be appropriately selected according to the purpose. For example, the shape is preferably a cylindrical shape, A spiral unevenness is formed on the surface, the toner as the contents can be transferred to the discharge port side by rotating, and a part or all of the spiral part has a bellows function, etc. Particularly preferred.
The material of the toner container main body is not particularly limited, and those having good dimensional accuracy are preferable. For example, a resin is preferable. Among them, for example, polyester resin, polyethylene resin, polypropylene resin, polystyrene resin, polychlorinated resin Preferred examples include vinyl resin, polyacrylic acid, polycarbonate resin, ABS resin, polyacetal resin, and the like.
The toner-containing container of the present invention is easy to store and transport, has excellent handleability, and is preferably used for replenishing toner by being detachably attached to the process cartridge and image forming apparatus of the present invention described later. Can do.

(Process cartridge)
The process cartridge of the present invention develops an electrostatic latent image carrier carrying an electrostatic latent image and the electrostatic latent image carried on the electrostatic latent image carrier using a developer to form a visible image. A developing unit for forming the image forming apparatus, and further including other means such as a charger, an exposure unit, a developing unit, a transfer unit, a cleaning unit, and a discharging unit, which are appropriately selected as necessary. .
The developing means includes a developer container that contains the toner or developer of the present invention, and a developer carrier that carries and transports the toner or developer contained in the developer container. And a layer thickness regulating member for regulating the thickness of the toner layer to be carried.
The process cartridge of the present invention can be detachably provided in various electrophotographic apparatuses, facsimiles, and printers, and is preferably detachably provided in the image forming apparatus of the present invention described later.

Here, for example, as shown in FIG. 1, the process cartridge includes a photosensitive member 101, and further includes a charger 102, a developing unit 104, a cleaning unit 107, and a transfer unit 108, and further, if necessary. It has other members. In FIG. 1, reference numeral 103 denotes exposure light from the exposure device, and 105 denotes a recording medium.
As the photoreceptor 101, the same one as an image forming apparatus described later can be used. An arbitrary charging member is used as the charger 102.
Next, the image forming process using the process cartridge shown in FIG. 1 will be described. The photoconductor 101 is charged on the surface by charging by the charging means 102 and exposure 103 by the exposure means (not shown) while rotating in the direction of the arrow. An electrostatic latent image corresponding to the exposure image is formed. The electrostatic latent image is developed with toner by the developing unit 104, and the toner development is transferred to the recording medium 105 by the transfer unit 108 and printed out. Next, the surface of the photoconductor after the image transfer is cleaned by the cleaning unit 107 and further neutralized by a neutralizing unit (not shown), and the above operation is repeated again.

  The image forming apparatus of the present invention is constructed by integrally combining the electrostatic latent image carrier and the components such as a developing device and a cleaning device as a process cartridge, and this unit can be attached to and detached from the apparatus main body. It may be configured. In addition, at least one of a charger, an image exposure device, a developing device, a transfer or separation device, and a cleaning device is integrally supported together with an electrostatic latent image carrier to form a process cartridge, and is detachably attached to the apparatus main body. One unit may be detachable using guide means such as a rail of the apparatus main body.

(Image forming apparatus and image forming method)
The image forming apparatus of the present invention includes an electrostatic latent image carrier, an electrostatic latent image forming unit, a developing unit, a transfer unit, and a fixing unit, and further appropriately selected as necessary. For example, a neutralizing means, a cleaning means, a recycling means, a control means, and the like.
The image forming method of the present invention includes an electrostatic latent image forming step, a developing step, a transfer step, and a fixing step, and other steps appropriately selected as necessary, for example, a static elimination step, a cleaning step, It includes a recycling process and a control process.

  The image forming method of the present invention can be preferably carried out by the image forming apparatus of the present invention, the electrostatic latent image forming step can be performed by the electrostatic latent image forming means, and the developing step is the developing The transfer step can be performed by the transfer unit, the fixing step can be performed by the fixing unit, and the other steps can be performed by the other unit.

-Electrostatic latent image forming step and electrostatic latent image forming means-
The electrostatic latent image forming step is a step of forming an electrostatic latent image on the electrostatic latent image carrier.
The material, shape, structure, size, etc. of the electrostatic latent image carrier (photosensitive member) are not particularly limited, and can be appropriately selected from known ones. Examples of the material include inorganic photoreceptors such as amorphous silicon and selenium, and organic photoreceptors such as polysilane and phthalopolymethine. Among these, amorphous silicon or the like is preferable in terms of long life.

  The formation of the electrostatic latent image can be performed, for example, by uniformly charging the surface of the electrostatic latent image carrier and then performing imagewise exposure, and is performed by the electrostatic latent image forming unit. be able to. The electrostatic latent image forming means includes, for example, at least a charger that uniformly charges the surface of the electrostatic latent image carrier and an exposure device that exposes the surface of the electrostatic latent image carrier imagewise. Prepare.

The charging can be performed, for example, by applying a voltage to the surface of the electrostatic latent image carrier using the charger.
The charger is not particularly limited and may be appropriately selected depending on the purpose. For example, a known contact charging device including a conductive or semiconductive roll, brush, film, rubber blade, etc. And non-contact chargers using corona discharge such as corotrons and corotrons.

The exposure can be performed, for example, by exposing the surface of the latent electrostatic image bearing member imagewise using the exposure device.
The exposure device is not particularly limited as long as it can expose the surface of the electrostatic latent image carrier charged by the charger so as to form an image to be formed, and is appropriately selected according to the purpose. For example, various exposure devices such as a copying optical system, a rod lens array system, a laser optical system, and a liquid crystal shutter optical system can be used.
In the present invention, a back light system in which imagewise exposure is performed from the back side of the electrostatic latent image carrier may be employed.

-Development process and development means-
The developing step is a step of developing the electrostatic latent image using the toner or the developer of the present invention to form a visible image.
The visible image can be formed, for example, by developing the electrostatic latent image using the toner or the developer of the present invention, and can be performed by the developing unit.
The developing unit is not particularly limited as long as it can be developed using, for example, the toner or the developer of the present invention, and can be appropriately selected from known ones. For example, the toner of the present invention Preferred examples include a developer containing at least a developer, and at least a developing device capable of contacting or non-contacting the toner or the developer with the electrostatic latent image. More preferred is a developing device.

  The developing unit may be a dry developing type, a wet developing type, a single color developing unit, or a multi-color developing unit. For example, a toner having a stirrer for charging the toner or the developer by frictional stirring and a rotatable magnet roller is preferable.

  In the developing device, for example, the toner and the carrier are mixed and agitated, and the toner is charged by friction at that time, and held on the surface of the rotating magnet roller in a raised state to form a magnetic brush. . Since the magnet roller is disposed in the vicinity of the electrostatic latent image carrier (photoconductor), a part of the toner constituting the magnetic brush formed on the surface of the magnet roller is electrically attracted. It moves to the surface of the electrostatic latent image carrier (photoconductor) by force. As a result, the electrostatic latent image is developed with the toner, and a visible image is formed with the toner on the surface of the electrostatic latent image carrier (photoconductor).

  The developer accommodated in the developing device is a developer containing the toner of the present invention, but the developer may be a one-component developer or a two-component developer. The toner contained in the developer is the toner of the present invention.

-Transfer process and transfer means-
The transfer step is a step of transferring the visible image onto a recording medium. After the primary transfer of the visible image onto the intermediate transfer member using an intermediate transfer member, the visible image is transferred onto the recording medium. A primary transfer step of forming a composite transfer image by transferring a visible image onto an intermediate transfer body using two or more colors, preferably full color toner as the toner, and a composite transfer image; A mode including a secondary transfer step of transferring the transfer image onto the recording medium is more preferable.
The transfer can be performed, for example, by charging the latent electrostatic image bearing member (photoconductor) of the visible image using a transfer charger, and can be performed by the transfer unit. The transfer means includes a primary transfer means for transferring a visible image onto an intermediate transfer member to form a composite transfer image, and a secondary transfer means for transferring the composite transfer image onto a recording medium. Embodiments are preferred.
The intermediate transfer member is not particularly limited and may be appropriately selected from known transfer members according to the purpose. For example, a transfer belt and the like are preferable.

The transfer means (the primary transfer means and the secondary transfer means) is a transfer for peeling and charging the visible image formed on the electrostatic latent image carrier (photoconductor) to the recording medium side. It is preferable to have at least a vessel. There may be one transfer means or two or more transfer means.
Examples of the transfer device include a corona transfer device using corona discharge, a transfer belt, a transfer roller, a pressure transfer roller, and an adhesive transfer device.
The recording medium is typically plain paper, but is not particularly limited as long as it can transfer an unfixed image after development, and can be appropriately selected according to the purpose. PET for OHP A base or the like can also be used.

The fixing step is a step of fixing the visible image transferred to the recording medium using a fixing device, and may be performed each time the toner of each color is transferred to the recording medium, or for the toner of each color. You may perform this simultaneously in the state which laminated | stacked this.
There is no restriction | limiting in particular as said fixing device, Although it can select suitably according to the objective, A well-known heating-pressing means is suitable. Examples of the heating and pressing means include a combination of a heating roller and a pressure roller, a combination of a heating roller, a pressure roller, and an endless belt.
The heating in the heating and pressing means is usually preferably 80 to 200 ° C.
In the present invention, for example, a known optical fixing device may be used together with or in place of the fixing step and the fixing unit depending on the purpose.

The neutralization step is a step of performing neutralization by applying a neutralization bias to the electrostatic latent image carrier, and can be suitably performed by a neutralization unit.
The neutralization means is not particularly limited, and may be appropriately selected from known neutralizers as long as it can apply a neutralization bias to the electrostatic latent image carrier. Preferably mentioned.

The cleaning step is a step of removing the toner remaining on the electrostatic latent image carrier and can be suitably performed by a cleaning unit.
The cleaning means is not particularly limited as long as it can remove the electrophotographic toner remaining on the electrostatic latent image carrier, and can be appropriately selected from known cleaners. Suitable examples include brush cleaners, electrostatic brush cleaners, magnetic roller cleaners, blade cleaners, brush cleaners, web cleaners, and the like.

The recycling step is a step of recycling the electrophotographic toner removed by the cleaning step to the developing unit, and can be suitably performed by the recycling unit.
There is no restriction | limiting in particular as said recycling means, A well-known conveyance means etc. are mentioned.

The control step is a step of controlling each of the steps, and can be suitably performed by a control unit.
The control means is not particularly limited as long as the movement of each means can be controlled, and can be appropriately selected according to the purpose. Examples thereof include devices such as a sequencer and a computer.

  One mode for carrying out the image forming method of the present invention by the image forming apparatus of the present invention will be described with reference to FIG. The image forming apparatus 100 shown in FIG. 2 includes a photosensitive drum 10 (hereinafter referred to as “photosensitive member 10”) as the electrostatic latent image carrier, a charging roller 20 as the charger, and exposure as the exposure device. The apparatus 30 includes a developing device 40 as the developing means, an intermediate transfer member 50, a cleaning device 60 as the cleaning means having a cleaning blade, and a static elimination lamp 70 as the static elimination means.

  The intermediate transfer member 50 is an endless belt, and is designed to be movable in the direction of an arrow by three rollers 51 that are arranged inside and stretched. Part of the three rollers 51 also functions as a transfer bias roller that can apply a predetermined transfer bias (primary transfer bias) to the intermediate transfer member 50. The intermediate transfer body 50 is provided with a cleaning device 90 having a cleaning blade in the vicinity thereof, and for transferring (secondary transfer) a developed image (toner image) to a transfer sheet 95 as a final transfer material. A transfer roller 80 serving as a transfer unit to which a transfer bias can be applied is disposed to face the transfer roller 80. Around the intermediate transfer member 50, a corona charger 58 for applying a charge to the toner image on the intermediate transfer member 50 is arranged between the photosensitive member 10 and the intermediate transfer member 50 in the rotation direction of the intermediate transfer member 50. It is disposed between the contact portion and the contact portion between the intermediate transfer member 50 and the transfer paper 95.

  The developing device 40 includes a developing belt 41 as the developer carrying member, and a black developing unit 45K, a yellow developing unit 45Y, a magenta developing unit 45M, and a cyan developing unit 45C provided around the developing belt 41. . The black developing unit 45K includes a developer accommodating portion 42K, a developer supplying roller 43K, and a developing roller 44K. The yellow developing unit 45Y includes a developer accommodating portion 42Y, a developer supplying roller 43Y, and a developing roller 44Y. The magenta developing unit 45M includes a developer accommodating portion 42M, a developer supplying roller 43M, and a developing roller 44M, and the cyan developing unit 45C includes a developer accommodating portion 42C and a developer supplying roller 43C. And a developing roller 44C. The developing belt 41 is an endless belt, is rotatably stretched around a plurality of belt rollers, and a part thereof is in contact with the photoconductor 10.

  In the image forming apparatus 100 shown in FIG. 2, for example, the charging roller 20 charges the photosensitive drum 10 uniformly. The exposure device 30 performs imagewise exposure on the photosensitive drum 10 to form an electrostatic latent image. The electrostatic latent image formed on the photosensitive drum 10 is developed by supplying toner from the developing device 40 to form a visible image (toner image). The visible image (toner image) is transferred (primary transfer) onto the intermediate transfer member 50 by the voltage applied from the roller 51, and further transferred (secondary transfer) onto the transfer paper 95. As a result, a transfer image is formed on the transfer paper 95. The residual toner on the photoconductor 10 is removed by the cleaning device 60, and the charge on the photoconductor 10 is temporarily removed by the charge eliminating lamp 70.

  Another mode for carrying out the image forming method of the present invention by the image forming apparatus of the present invention will be described with reference to FIG. The image forming apparatus 100 shown in FIG. 3 does not include the developing belt 41 in the image forming apparatus 100 shown in FIG. 2, and a black developing unit 45K, a yellow developing unit 45Y, a magenta developing unit 45M, and Except for the fact that the cyan developing unit 45C is arranged directly opposite, it has the same configuration as the image forming apparatus 100 shown in FIG. In FIG. 3, the same components as those in FIG. 2 are denoted by the same reference numerals.

Another mode for carrying out the image forming method of the present invention by the image forming apparatus of the present invention will be described with reference to FIG. The tandem image forming apparatus shown in FIG. 4 is a tandem type color image forming apparatus. The tandem image forming apparatus includes a copying apparatus main body 150, a paper feed table 200, a scanner 300, and an automatic document feeder (ADF) 400.
The copying apparatus main body 150 is provided with an endless belt-like intermediate transfer member 50 at the center. The intermediate transfer member 50 is stretched around the support rollers 14, 15 and 16, and can be rotated clockwise in FIG. 4. An intermediate transfer member cleaning device 17 for removing residual toner on the intermediate transfer member 50 is disposed in the vicinity of the support roller 15. The intermediate transfer member 50 stretched between the support roller 14 and the support roller 15 is a tandem type in which four image forming units 18 of yellow, cyan, magenta, and black are arranged to face each other along the conveyance direction. A developing device 120 is disposed. An exposure device 21 is disposed in the vicinity of the tandem developing device 120. A secondary transfer device 22 is disposed on the side of the intermediate transfer member 50 opposite to the side on which the tandem developing device 120 is disposed. In the secondary transfer device 22, a secondary transfer belt 24, which is an endless belt, is stretched around a pair of rollers 23, and the transfer paper conveyed on the secondary transfer belt 24 and the intermediate transfer body 50 are in contact with each other. Is possible. A fixing device 25 is disposed in the vicinity of the secondary transfer device 22. The fixing device 25 includes a fixing belt 26 that is an endless belt, and a pressure roller 27 that is pressed against the fixing belt 26.
In the tandem image forming apparatus, a sheet reversing device 28 for reversing the transfer paper for image formation on both sides of the transfer paper is disposed in the vicinity of the secondary transfer device 22 and the fixing device 25. Yes.

  Next, formation of a full color image (color copy) using the tandem image forming apparatus will be described. That is, first, a document is set on the document table 130 of the automatic document feeder (ADF) 400, or the automatic document feeder 400 is opened and the document is set on the contact glass 32 of the scanner 300. 400 is closed.

  When a start switch (not shown) is pressed, when the document is set on the automatic document feeder 400, the document is transported and moved onto the contact glass 32, and then the document is set on the contact glass 32. Immediately after that, the scanner 300 is driven, and the first traveling body 33 and the second traveling body 34 travel. At this time, light from the light source is irradiated by the first traveling body 33 and reflected light from the document surface is reflected by the mirror in the second traveling body 34 and is received by the reading sensor 36 through the imaging lens 35 to be color. An original (color image) is read and used as black, yellow, magenta, and cyan image information.

  Each image information of black, yellow, magenta and cyan is stored in each image forming means 18 (black image forming means, yellow image forming means, magenta image forming means and cyan image forming means in the tandem image forming apparatus. ) And black, yellow, magenta and cyan toner images are formed in the respective image forming means. That is, each image forming means 18 (black image forming means, yellow image forming means, magenta image forming means, and cyan image forming means) in the tandem image forming apparatus is respectively photosensitive as shown in FIG. On the basis of the body 10 (the black photoreceptor 10K, the yellow photoreceptor 10Y, the magenta photoreceptor 10M, and the cyan photoreceptor 10C), the charger 60 that uniformly charges the photoreceptor, and each color image information. The photosensitive member is exposed to each color image-corresponding image (L in FIG. 5), and an electrostatic latent image corresponding to each color image is formed on the photosensitive member. A developing device 61 that develops using color toner (black toner, yellow toner, magenta toner, and cyan toner) to form a toner image with each color toner, and the toner image is an intermediate transfer member. The image forming apparatus includes a transfer charger 62 for transferring the image onto 0, a photoconductor cleaning device 63, and a static eliminator 64, and each monochrome image (black image, yellow image, magenta) based on the image information of each color. Image and cyan image) can be formed. The black image, the yellow image, the magenta image, and the cyan image formed in this way are formed on the black photoconductor 10K on the intermediate transfer member 50 that is rotated by the support rollers 14, 15, and 16, respectively. The black image, the yellow image formed on the yellow photoconductor 10Y, the magenta image formed on the magenta photoconductor 10M, and the cyan image formed on the cyan photoconductor 10C are sequentially transferred (primary transfer). Is done. Then, the black image, the yellow image, the magenta image, and the cyan image are superimposed on the intermediate transfer member 50 to form a composite color image (color transfer image).

  On the other hand, in the paper feed table 200, one of the paper feed rollers 142 is selectively rotated to feed out a sheet (recording paper) from one of the paper feed cassettes 144 provided in multiple stages in the paper bank 143. Each sheet is separated and sent to the paper feed path 146, transported by the transport roller 147, guided to the paper feed path 148 in the copying machine main body 150, and abutted against the registration roller 49 and stopped. Alternatively, the sheet feed roller 142 is rotated to feed out sheets (recording paper) on the manual feed tray 54, separated one by one by the separation roller 52, put into the manual feed path 53, and abutted against the registration roller 49 and stopped. . The registration roller 49 is generally used while being grounded, but may be used in a state where a bias is applied to remove paper dust from the sheet. Then, the registration roller 49 is rotated in synchronization with the synthesized color image (color transfer image) synthesized on the intermediate transfer member 50, and a sheet (recording paper) is interposed between the intermediate transfer member 50 and the secondary transfer device 22. The secondary color transfer device 22 transfers the composite color image (color transfer image) onto the sheet (recording paper), thereby transferring the color image onto the sheet (recording paper). Is formed. The residual toner on the intermediate transfer member 50 after image transfer is cleaned by the intermediate transfer member cleaning device 17.

  The sheet (recording paper) on which the color image has been transferred is conveyed by the secondary transfer device 22 and sent to the fixing device 25, where the combined color image (color) is generated by heat and pressure. (Transfer image) is fixed on the sheet (recording paper). Thereafter, the sheet (recording paper) is switched by the switching claw 55 and discharged by the discharge roller 56 and stacked on the discharge tray 57, or switched by the switching claw 55 and reversed by the sheet reversing device 28 and transferred again. After being guided to the position and recording an image on the back surface, the image is discharged by the discharge roller 56 and stacked on the discharge tray 57.

  In the image forming apparatus and the image forming method of the present invention, the toner of the present invention having excellent characteristics such as chargeability and transferability, high image quality, and excellent cleaning properties is used. An image can be formed.

Examples of the present invention will be described below, but the present invention is not limited to the following examples.

Example 1
<Adhesive substrate production process>
First, a yellow toner was manufactured as follows.
-Preparation of toner solution-
--- Synthesis of unmodified polyester (low molecular weight polyester)-
In a reaction vessel equipped with a cooling tube, a stirrer and a nitrogen introduction tube, 220 parts by mass of bisphenol A ethylene oxide 2 mol adduct, 561 parts by mass of bisphenol A propion oxide 3 mol adduct, 218 parts by mass of terephthalic acid, 48 masses of adipic acid And 2 parts by mass of dibutyltin oxide were added and reacted at 230 ° C. for 8 hours under normal pressure. Next, after reacting the reaction solution under a reduced pressure of 10 to 15 mmHg for 5 hours, 45 parts by mass of trimellitic anhydride was added to the reaction vessel, and the reaction was performed at 180 ° C. for 2 hours under normal pressure. A modified polyester was synthesized.
The obtained unmodified polyester had a number average molecular weight (Mn) of 2,500, a weight average molecular weight (Mw) of 6,700, a glass transition temperature (Tg) of 43 ° C., and an acid value of 25.

-Preparation of master batch (MB)-
Bisacetoacetolide pigment (CI Pigment Yellow) (“Novoperm Yellow 4G”; Clariant, average particle size = 90 nm), 50 parts by mass, polyester resin (“RS801”, Sanyo Chemical Industries) Made by company, acid value = 10, weight average molecular weight (Mw) = 20,000, glass transition temperature (Tg) = 64 ° C.) 50 parts by mass and water 30 parts by mass were mixed with a Henschel mixer (Mitsui Mining Co., Ltd.). . The mixture was kneaded for 45 minutes at 130 ° C. with two rolls, rolled and cooled, and pulverized to a size of 1 mm in diameter with a pulverizer (manufactured by Hosokawa Micron) to prepare a master batch.

-Preparation of organic solvent phase-
In a reaction vessel in which a stir bar and a thermometer were set, 378 parts by mass of the unmodified polyester, 110 parts by mass of carnauba wax, 22 parts by mass of CCA (“salicylic acid metal complex E-84”, manufactured by Orient Chemical Industry Co., Ltd.), and 947 parts by mass of ethyl acetate was added, the temperature was raised to 80 ° C. with stirring, the temperature was maintained at 80 ° C. for 5 hours, and then cooled to 30 ° C. over 1 hour. Next, 500 parts by mass of the master batch (content of 11% by mass of the bisacetoacetalilide pigment in the toner) and 500 parts by mass of ethyl acetate are charged in a reaction vessel and mixed for 1 hour to obtain a raw material solution. It was.
1324 parts by mass of the obtained raw material solution was transferred to a reaction vessel, and using a bead mill (“Ultra Visco Mill”; manufactured by Imex Co., Ltd.), the liquid feeding speed was 1 kg / hr, the disk peripheral speed was 6 m / sec, and 0.5 mm zirconia. The bisacetoacetalilide pigment and carnauba wax were dispersed in 3 passes under the condition of 80% by volume of beads. Next, 630 parts by mass of a 65% by mass ethyl acetate solution of the unmodified polyester was added to the wax dispersion. One pass was performed in a bead mill under the same conditions as described above, and the mixture was dispersed to prepare an organic solvent phase.
The solid content concentration (130 ° C., 30 minutes) of the obtained organic solvent phase was 50% by mass.

--Synthesis of prepolymer--
In a reaction vessel equipped with a cooling tube, a stirrer and a nitrogen introduction tube, 682 parts by mass of bisphenol A ethylene oxide 2 mol adduct, 81 parts by mass of bisphenol A propylene oxide 2 mol adduct, 283 parts by mass of terephthalic acid, trimellitic anhydride 22 parts by mass of acid and 2 parts by mass of dibutyltin oxide were charged and reacted at 230 ° C. for 8 hours under normal pressure. Subsequently, it was made to react under reduced pressure of 10-15mHg for 5 hours, and the intermediate polyester was synthesize | combined.
The resulting intermediate polyester has a number average molecular weight (Mn) of 2,100, a weight average molecular weight (Mw) of 9,500, a glass transition temperature (Tg) of 55 ° C., an acid value of 0.5, and a hydroxyl value of 51.
Next, 410 parts by mass of the intermediate polyester, 89 parts by mass of isophorone diisocyanate, and 500 parts by mass of ethyl acetate are charged in a reaction vessel equipped with a cooling pipe, a stirrer, and a nitrogen introduction pipe, and reacted at 100 ° C. for 5 hours. Thus, a prepolymer (polymer capable of reacting with the active hydrogen group-containing compound) was synthesized.
The free isocyanate content of the obtained prepolymer was 1.53% by mass.

--Synthesis of ketimine (the active hydrogen group-containing compound)-
In a reaction vessel equipped with a stir bar and a thermometer, 170 parts by mass of isophoronediamine and 75 parts by mass of methyl ethyl ketone were charged and reacted at 50 ° C. for 5 hours to synthesize a ketimine compound (the active hydrogen group-containing compound).
The amine value of the obtained ketimine compound (the active hydrogen machine-containing compound) was 418.
In a reaction vessel, 648 parts by mass of the organic solvent phase, 44 parts by mass of the prepolymer, 0.05 part by mass (0.01% by mass) of organosilica as the deforming agent, and 6.6 parts by mass of the ketimine compound. The toner solution was prepared by mixing for 1 minute at 5,000 rpm using a TK type homomixer (manufactured by Tokushu Kika Co., Ltd.).

-Preparation of dispersion-
--Preparation of fine particle dispersion--
In a reaction vessel in which a stir bar and a thermometer are set, 683 parts by mass of water, 11 parts by mass of sodium salt of ethylene oxide methacrylate adduct sulfate ("Eleminol RS-30", manufactured by Sanyo Chemical Industries, Ltd.), styrene 83 Part by weight, 83 parts by weight of methacrylic acid, 110 parts by weight of butyl acrylate, and 1 part by weight of ammonium persulfate were charged and stirred at 400 rpm for 15 minutes to obtain a white emulsion. The emulsion was heated to raise the system temperature to 75 ° C. and reacted for 5 hours. Next, 30 parts by mass of a 1% by mass ammonium persulfate aqueous solution was added, and the mixture was aged at 75 ° C. for 5 hours, so that vinyl resin particles (copolymer of sodium salt of styrene-methacrylic acid-butyl acrylate-methacrylic acid ethylene oxide adduct sulfate) An aqueous dispersion of polymer) (fine particle dispersion) was prepared.
The volume average particle size of the fine particles contained in the obtained fine particle dispersion was measured with a particle size distribution measuring apparatus (“LA-920”, manufactured by Horiba, Ltd.) using a laser light scattering method, and found to be 105 nm. Further, when a part of the fine particle dispersion was dried to isolate the resin, and the glass transition temperature (Tg) of the resin was measured, it was 59 ° C. and the weight average molecular weight (Mw) was measured. 000.

-Preparation of aqueous medium-
990 parts by weight of water, 83 parts by weight of the fine particle dispersion, 37 parts by weight of a 48.5% by weight aqueous solution of sodium dodecyl diphenyl ether disulfonate (“Eleminol MON-7” manufactured by Sanyo Chemical Industries, Ltd.), and 90 parts by weight of ethyl acetate Were mixed and stirred to obtain a milky white liquid (aqueous medium).

--Emulsification and dispersion--
809 parts by mass of the toner solution was added to 1200 parts by mass of the aqueous medium, and the mixture was mixed with the TK homomixer at a rotational speed of 13,000 rpm for 20 minutes to prepare a dispersion (emulsion slurry).
Next, the emulsified slurry was charged into a reaction vessel equipped with a stirrer and a thermometer, and after removing the solvent at 30 ° C. for 8 hours, aging was carried out at 45 ° C. for 4 hours to obtain a dispersed slurry.
The obtained dispersion slurry had a volume average particle size of 5.7 μm and a number average particle size of 5.0 μm as measured by Multisizer III (manufactured by Beckman Coulter, Inc.).

-Cleaning and drying-
After filtering 100 parts by mass of the dispersion slurry under reduced pressure, adding 300 parts by mass of ion exchange water to the filter cake, mixing with a TK homomixer (at 12,000 rpm for 10 minutes), and then filtering three times. And a final filter cake was obtained.
Here, the obtained final filter cake was dried with a circulating dryer at 45 ° C. for 48 hours, and sieved with a mesh of 75 μm to obtain yellow toner base particles of Example 1.

(Example 2)
The same as Example 1 except that 0.05 parts by mass (0.01% by mass) of organosilica added in the toner solution preparation step of Example 1 was changed to 0.01 parts by mass (0.002% by mass). Thus, toner base particles were prepared.

(Example 3)
The same as Example 1 except that 0.05 parts by mass (0.01% by mass) of organosilica added in the toner solution preparation step of Example 1 was changed to 0.10 parts by mass (0.02% by mass). Thus, toner base particles were prepared.

(Comparative Example 1)
“Mixing step” in Example 1 The following components in Table 1 were stirred and mixed at a peripheral speed of 20 m / s using a TK auto homomixer (manufactured by Tokushu Kika Kogyo Co., Ltd.). A mixture of body compositions was prepared.

  Next, in the “dispersion suspension step”, the components shown in Table 2 below were mixed and dispersed to obtain an aqueous medium.

Next, while stirring 165 parts by mass of the obtained aqueous medium with an auto homomixer at a peripheral speed of 20 m / s, 105 parts by mass of the mixed solution of the polymerizable monomer composition was added and stirred for 3 minutes. And then stopped to obtain a suspension.
The obtained suspension was heated to 70 ° C. under a nitrogen atmosphere and stirred for 24 hours to prepare a toner composition. Hydrochloric acid was added thereto, the pH value was adjusted to 1, and the mixture was stirred for 1 hour to completely dissolve calcium phosphate, washed with water and dehydrated repeatedly, and dried to obtain toner base particles of Comparative Example 1.

  For the obtained toner base particles of Examples 1 to 3 and Comparative Example 1, the root mean square (RMS), the average circularity, the volume average particle diameter (Dv), and the number average particle diameter (Dn) are as follows. And particle size distribution (volume average particle diameter (Dv) / number average particle diameter (Dn)) were measured. The results are shown in Table 3.

<Root mean square (RMS)>
The root mean square (RMS) of the toner is measured by using NANO Station II (manufactured by SURFACE IMAGEING SYSTEMS) 50 times (50 toners). The difference between the value and the minimum value (ΔRMS) was determined. The measurement conditions are shown below.
〔Measurement condition〕
・ Measurement mode: Tapping mode-AFM
Measurement range: X-Range: 2000.0 nm
: Y-Range: 2000.0 nm
Measurement resolution: 128 × 128 pixels (number of measurements N = 16384)
Scan speed: 0.3 Lines / s
Cantilever: manufactured by Nanosensors, AR5-NCLR-20
・ Resonance frequency: 161.005 kHz
・ Amplitude: 90.0 nm

<Average circularity>
Measurement was performed using a flow type particle image analyzer (“FPIA-2100”, manufactured by Sysmex Corporation) for measurement with an average circularity of 0.98 or more and 0.95 or less based on the number of toners, and analysis software (FPIA− 2100 Data Processing Program for FPIA version 00-10). Specifically, 0.1% to 0.5 ml of 10% by weight surfactant (alkylbenzene sulfonate Neogen SC-A, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) is added to a glass 100 ml beaker, and each toner is treated with 0.1. 1-0.5 g was added and stirred with a micropartel, and then 80 ml of ion-exchanged water was added. The obtained dispersion was subjected to a dispersion treatment for 3 minutes with an ultrasonic disperser (manufactured by Honda Electronics Co., Ltd.). Using the FPIA-2100, the shape and distribution of the toner were measured until a dispersion concentration of 5,000 to 15,000 / μl was obtained. In this measurement method, it is important that the concentration of the dispersion is 5,000 to 15,000 / μl from the viewpoint of measurement reproducibility of average circularity. In order to obtain the concentration of the dispersion, it is necessary to change the conditions of the dispersion, that is, the amount of surfactant to be added and the amount of toner. The amount of the surfactant varies depending on the hydrophobicity of the toner as in the measurement of the toner particle diameter described above. If it is added in a large amount, noise due to bubbles is generated. It will be enough. Further, the toner addition amount is different from the particle size, and decreases when the particle size is small. Further, when the particle size is large, it is necessary to increase it. When the toner particle size is 3 to 7 μm, the dispersion concentration is adjusted to 5000 to 15000 / μl by adding 0.1 to 0.5 g of the toner amount. It becomes possible.

<Toner particle size>
The volume average particle diameter (Dv) and the number average particle diameter (Dn) of the toner are measured with a particle size measuring device (“Multisizer III”, manufactured by Beckman Coulter, Inc.) with an aperture diameter of 100 μm, and analysis software (Beckman Coulter Multisizer) is used. 3 Version 3.51). Specifically, 0.5 ml of 10% by weight surfactant (alkylbenzene sulfonate Neogen SC-A, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) is added to a 100 ml beaker made of glass, and 0.5 g of each toner is added. The mixture was stirred with a spatula, and then 80 ml of ion exchange water was added. The obtained dispersion was subjected to a dispersion treatment for 10 minutes with an ultrasonic disperser (W-113MK-II, manufactured by Honda Electronics Co., Ltd.). The dispersion was measured using the Multisizer III and Isoton III (manufactured by Beckman Coulter, Inc.) as the measurement solution. In the measurement, the toner sample dispersion was dropped so that the concentration indicated by the apparatus was 8 ± 2%. In this measurement method, it is important that the concentration is 8 ± 2% from the viewpoint of the reproducibility of the particle size. Within this concentration range, no error occurs in the particle size.

  Next, Examples 1 to 3 and Comparative Example were prepared in a conventional manner from 5% by mass of each of the toners of Examples 1 to 3 and Comparative Example and 95% by mass of a copper-zinc ferrite carrier having an average particle diameter of 40 μm coated with a silicone resin. 1 developer was produced.

  Using the obtained developers, the cleaning property, charging stability, image graininess and sharpness were evaluated as follows. The results are shown in Table 4.

<Evaluation of cleaning properties>
The transfer residual toner on the photosensitive member that passed through the cleaning process was transferred to white paper with a scotch tape (manufactured by Sumitomo 3M Limited), and measured with a Macbeth reflection densitometer RD514.
The difference from the blank is 0 to 0.01, ◎ (good), 0.02 to 0.05, ○, 0.06 to 0.1, Δ, ).

<Charging stability>
Using an evaluation machine that was tuned by modifying the image forming apparatus (Ricoh Co., Ltd., IPSiO Color 8100) to an oil-less fixing system, each toner used an image area ratio 5% chart Continuous 100,000 sheet output durability test And the change in the charge amount at that time was evaluated. 1 g of developer was weighed and the change in charge amount was determined by the blow-off method.
When the change in the charge amount was 5 μc / g or less, it was evaluated as ◯, when it was 10 μc / g or less, Δ when it exceeded 10 μc / g.

<Image graininess and sharpness>
Using an evaluation machine that has been tuned by modifying the image forming apparatus (Ricoh Co., Ltd., IPSiO Color 8100) to an oil-less fixing system, a photographic image is output in a single color, and the degree of graininess and sharpness is visually evaluated. did.
Evaluations were made from GOOD, ◎, ○, Δ, and ×.並 is equivalent to offset printing, ◯ is slightly worse than offset printing, Δ is much worse than offset printing, and × is very bad compared to conventional electrophotographic images.

<Durability>
The developer is set in an evaluation machine that has been tuned by remodeling the image forming apparatus (Ricoh Co., Ltd., IPSiO Color 8100) to an oil-less fixing system, and is capable of producing 1,000,000 sheets in a single color under normal temperature / humidity environment. Continuous image output was performed, and the image graininess and sharpness were evaluated.

From the results of Table 4, since Examples 1 to 3 all have ΔRMS in the range of 100 to 600, compared to Comparative Example 1 in which ΔRMS is out of range, the chargeability, graininess, and sharpness are Are equivalent, but are found to have excellent cleaning properties.
In Comparative Example 1, in the durability evaluation, the image deterioration is remarkable due to poor cleaning, and it is recognized that the graininess after the durability test and the sharpness are remarkably inferior as compared with Examples 1 to 3.

  The toner of the present invention is excellent in various properties such as chargeability and transferability, provides high image quality, has excellent cleaning properties, and is suitably used for high quality image formation. The developer, toner-containing container, process cartridge, image forming apparatus and image forming method of the present invention using the toner of the present invention are suitably used for high-quality image formation.

FIG. 1 is a schematic explanatory view showing an example of the process cartridge of the present invention. FIG. 2 is a schematic explanatory view showing an example in which the image forming method of the present invention is carried out by the image forming apparatus of the present invention. FIG. 3 is a schematic explanatory view showing another example in which the image forming method of the present invention is carried out by the image forming apparatus of the present invention. FIG. 4 is a schematic explanatory view showing an example of carrying out the image forming method of the present invention by the image forming apparatus (tandem color image forming apparatus) of the present invention. FIG. 5 is a partially enlarged schematic explanatory view of the image forming apparatus shown in FIG.

Explanation of symbols

10 Photoconductor (Photoconductor drum)
10K black photoconductor 10Y yellow photoconductor 10M magenta photoconductor 10C cyan photoconductor 14 support roller 15 support roller 16 support roller 17 intermediate transfer cleaning device 18 image forming means 20 charging roller 21 exposure device 22 secondary transfer device 23 Roller 24 Secondary transfer belt 25 Fixing device 26 Fixing belt 27 Pressure belt 28 Sheet reversing device 30 Exposure device 32 Contact glass 33 First traveling member 34 Second traveling member 35 Imaging lens 36 Reading sensor 40 Developing device 41 Developing belt 42K Developer container 42Y Developer container 42M Developer container 42C Developer container 43K Developer supply roller 43Y Developer supply roller 43M Developer supply roller 43C Developer supply roller 44K Developer roller 44Y Developer roller 44M Developer Roller 44C Developing roller 45K Black developing unit 45Y Yellow developing unit 45M Magenta developing unit 45C Cyan developing unit 49 Registration roller 50 Intermediate transfer member 51 Roller 52 Separating roller 53 Manual feed path 54 Manual feed tray 55 Switching claw 56 Discharge roller 57 discharge tray 58 corona charger 60 cleaning device 61 developing device 62 transfer charger 63 photoconductor cleaning device 64 static eliminator 70 static elimination lamp 71 cleaning blade 72 support member 80 transfer roller 90 cleaning device 95 transfer paper 100 image forming apparatus 101 photoconductor DESCRIPTION OF SYMBOLS 102 Charging device 103 Exposure 104 Developing means 105 Recording medium 107 Cleaning means 108 Transfer means 120 Tandem type developing device 130 Document table 142 Feed roller 143 Paper bank 14 Paper feed cassette 145 separating roller 146 feed path 147 transport rollers 148 feed path 150 copier main body 200 feeder table 300 Scanner 400 automatic document feeder (ADF)

Claims (13)

Using an atomic force microscope (AFM), a surface roughness obtained by measuring a range of 2 μm in length × 2 μm in width including at least the toner apex portion on the surface of one toner for one measurement is calculated from the following formula 1. About the root mean square (RMS), the difference (ΔRMS) between the maximum value and the minimum value of the root mean square (RMS) in 50 measurements is 115 nm to 566 nm ,
The toner is granulated by emulsifying or dispersing a solution or dispersion obtained by dissolving or dispersing a toner material in an organic solvent in an aqueous medium,
The toner material includes at least an active hydrogen group-containing compound, a polymer capable of reacting with the active hydrogen group-containing compound, a binder resin, a release agent, a colorant, and a deforming agent,
The deforming agent is 0.002% by mass to 0.02% by mass of organosilica based on the total amount of the binder resin, the release agent, and the colorant,
The granulation produces particles containing at least the adhesive base material while producing the adhesive base material by reacting the active hydrogen group-containing compound with a polymer capable of reacting with the active hydrogen group-containing compound. Made by
A toner, wherein the organic solvent is removed during or after granulation.
The toner according to claim 1, wherein a difference (ΔRMS) between a maximum value and a minimum value of root mean square (RMS) is 250 nm to 550 nm . The toner according to claim 1, wherein the root mean square (RMS) has a maximum value of 200 nm to 650 nm . The toner according to claim 1, wherein the minimum value of root mean square (RMS) is 10 nm to 150 nm .   The toner according to claim 1, having an average circularity of 0.93 to 0.97.   The toner according to claim 5, wherein the toner contains 40% by mass or less of toner having an average circularity of 0.98 or more and 35% by mass or less of toner having an average circularity of 0.95 or less. The toner according to claim 1, wherein the toner has a volume average particle diameter (Dv) of 3 μm to 8 μm .   The toner according to claim 1, wherein the volume average particle diameter (Dv) / number average particle diameter (Dn) of the toner is 1.00 to 1.15.   A developer comprising the toner according to claim 1. Toner container to the toner according to any one of claims 1 8, characterized by comprising filled. A latent electrostatic image bearing member, a developing means for forming the developed visible image using a toner according to the electrostatic latent image formed on the latent electrostatic image bearing member to any one of claims 1 to 8 A process cartridge having at least 9. The electrostatic latent image carrier, an electrostatic latent image forming unit that forms an electrostatic latent image on the electrostatic latent image carrier, and the toner according to any one of claims 1 to 8. At least developing means for forming a visible image by developing the toner, transfer means for transferring the visible image to a recording medium, and fixing means for fixing the transferred image transferred to the recording medium. An image forming apparatus. An electrostatic latent image forming step of forming an electrostatic latent image on an electrostatic latent image bearing member, a visible image by developing with a toner according to the electrostatic latent image to any of claims 1 to 8 An image forming method comprising: a developing step for forming the image; a transfer step for transferring the visible image to a recording medium; and a fixing step for fixing the transferred image transferred to the recording medium.