JP4710173B2 - Release sheet, adhesive tape and tape adhesive - Google Patents

Release sheet, adhesive tape and tape adhesive Download PDF

Info

Publication number
JP4710173B2
JP4710173B2 JP2001176117A JP2001176117A JP4710173B2 JP 4710173 B2 JP4710173 B2 JP 4710173B2 JP 2001176117 A JP2001176117 A JP 2001176117A JP 2001176117 A JP2001176117 A JP 2001176117A JP 4710173 B2 JP4710173 B2 JP 4710173B2
Authority
JP
Japan
Prior art keywords
release agent
release
agent layer
release sheet
ink
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP2001176117A
Other languages
Japanese (ja)
Other versions
JP2002363515A (en
Inventor
伸久 小林
員義 若田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
New Oji Paper Co Ltd
Oji Holdings Corp
Original Assignee
Oji Holdings Corp
Oji Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oji Holdings Corp, Oji Paper Co Ltd filed Critical Oji Holdings Corp
Priority to JP2001176117A priority Critical patent/JP4710173B2/en
Publication of JP2002363515A publication Critical patent/JP2002363515A/en
Application granted granted Critical
Publication of JP4710173B2 publication Critical patent/JP4710173B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は、剥離シートおよび粘着テープに関するものである。さらに詳しくは、剥離剤層面に情報等の印刷を施した剥離シートおよび粘着テープに関するものである。
【0002】
【従来の技術】
一般に、剥離シートは、基材の少なくとも片面に剥離剤層を設けた構成で、ラベル等の粘着剤層面を使用時まで保護するために使われる。一方、粘着テープは、基材の片面に粘着剤層を設け、他方の面に剥離剤層を設け、巻き取り状にされ、使用時に巻き戻して使われる。
使用される剥離剤としては、長鎖アルキル基含有化合物、シリコーン変成樹脂系剥離剤、シリコーン系剥離剤などが主に用いられているが、特にシリコーン系剥離剤は、粘着剤に対して優れた剥離性を発揮するため、現在最も多く使用されている。
【0003】
しかし、通常、上記シリコーン系剥離剤は、剥離剤層面の臨界表面張力が小さく、その剥離剤層面にマジックなどで筆記することや、インクリボンを用いて熱転写印刷を施したり、印字することは不可能である。また、通常の印刷用インキを用いて剥離剤層面に印刷することは、インキメーカーにとっても、剥離剤メーカーにとっても不可能な技術とされており、剥離剤層上に情報を備えたシリコーン系剥離シートは存在しなかった。
【0004】
一方、剥離剤として、長鎖アルキル基含有化合物を塗工したものがある。この長鎖アルキル基含有化合物を設けた剥離剤層は、油性マジック等で字が書けるという特徴がある。しかしながら、長鎖アルキル基含有化合物は、シリコーン系の剥離剤と比較した場合に剥離力が高すぎることや、耐熱性が悪く、粘着剤層と貼り合わせたまま高温下に曝すと重剥離化して剥離異常を起こしてしまう等の問題があった。
【0005】
一般的なラベルは、表面基材に粘着剤層を介して剥離シートが積層された構成のものが、現在多く使用されている。表面基材には情報等を印刷・印字されるが、剥離シートは、粘着剤を保護する役割として使用されているに過ぎず、それ以外の機能を果たすことなく廃棄されるという問題があった。
【0006】
これらの欠点を解決するためには、予め基材の片面もしくは両面に通常のインキで印刷し、さらに印刷層の上に剥離剤層を設けることによって情報等を有する剥離シートを製造することが行われている。
しかしながら、印刷してから剥離剤を塗布、場合によっては裏面への粘着剤塗布を行うため、製造時の歩留まり等を考慮すると、最終製品の数量よりも多くの数量を印刷することになり、生産性が悪かった。また、一旦剥離剤まで加工し、あるいは粘着加工まで行った製品に印刷することができないため、何らかのトラブル、欠陥等があった場合、印刷加工を含めてすべてロスになってしまう等の問題があった。
【0007】
一方、特開平7−150092号公報では、シート基材に一層の剥離面で着色が行えるようにすることを課題とし、剥離性インキにより剥離面を設けた剥離シートが提案されている。しかし、剥離性インキを基材に直接印刷することは可能でも、剥離シートの剥離剤層面に印刷はできない。また、得られる剥離シートも剥離力の安定しないものであった。
【0008】
【発明が解決しようとする課題】
本発明は、粘着剤層と剥離剤層表面との剥離性および印刷インキによる印刷・印字記録適性に優れ、さらには環境への負荷が少ない剥離シートおよび粘着テープを提供することを目的とする。
【0009】
【課題を解決するための手段】
以下の発明を包含する。
(1)基材の少なくとも一面に剥離剤層を有し、該剥離剤層表面上の少なくとも一部分に印刷層を有する剥離シートであって、前記剥離剤層が、硬化性ポリシロキサン含有剥離剤を硬化して形成され、且つ前記印刷層を形成するインキが、剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキである剥離シート。
(2)前記剥離性放射線硬化型ポリシロキサンが、剥離性放射線硬化型ポリジメチルシロキサンである(1)記載の剥離シート。
(3)前記剥離性放射線硬化型インキが、剥離性放射線硬化型ポリシロキサンを少なくとも5質量%含有する(1)又は(2)記載の剥離シート。
(4)前記剥離性放射線硬化型インキが、剥離性紫外線硬化型インキである(1)〜(3)記載の剥離シート。
(5)前記硬化性ポリシロキサンが、硬化性ポリジメチルシロキサンである(1)〜(4)記載の剥離シート。
(6)前記剥離剤層中に、エラストマーおよび/又はセルロース誘導体をさらに含有する(1)〜(5)記載の剥離シート。
(7)前記剥離剤層中に、前記エラストマーを少なくとも50質量%含有し、且つ剥離剤層が、溶融熱転写記録適性を有する(6)記載の剥離シート。
(8)前記剥離剤層が、エラストマー80〜98質量%および硬化性ポリジメチルシロキサン2〜20質量%を含有する(6)又は(7)記載の剥離シート。
(9)前記剥離剤層中に、セルロース誘導体を少なくとも10質量%含有する(6)記載の剥離シート。
(10)前記剥離剤層が、セルロース誘導体10〜50質量%および硬化性ポリジメチルシロキサン50〜90質量%を含む(6)又は(9)記載の剥離シート。
(11)前記剥離剤層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)が45〜65度であり、且つ印刷層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)が45度以上である(1)〜(10)記載の剥離シート。
【0010】
本発明はさらに以下の発明を包含する。
(12)前記(1)〜(11)のいずれかに記載され、一面に剥離剤層を有する剥離シートを用い、その剥離剤層を設けた面とは反対面にアクリル系粘着剤層を設けて巻き取り状にしたことを特徴とする粘着テープ。
(13)前記剥離シートの、剥離剤層と前記印刷層との接着力をα、前記印刷層と前記粘着剤層との接着力βとした場合に、接着力α>接着力βの関係にある前記(12)に記載の粘着テープ。
(14)前記(12)又は(13)に記載の粘着テープを、被着体に貼着したテープ貼着物。
【0011】
【発明の実施の形態】
基材としては、公知の粘着テープ用の基材あるいは剥離シート用の基材が使用できる。例えば、クラフト紙、グラシン紙、上質紙、コート紙、キャストコート紙、クレープ紙、含浸紙等の紙基材や、ポリプロピレン、ポリエチレン、ポリエステル、ポリ塩化ビニル、ポリスチレン等の高分子フィルム、不織布、合成紙あるいは金属箔などが挙げられ、これらを適宜組み合わせて積層したものでもよい。紙基材に有機溶剤によって調整された剥離剤やエマルジョン型剥離剤等を塗布する場合等は、剥離剤塗布液の基材へのしみ込みを抑えるために、基材に目止め処理を施すことが好ましい。
【0012】
目止め処理としては、例えば、接着剤および/又は顔料を主成分とするものを予め塗布する、基材にポリエチレン等の熱可塑性樹脂をラミネートする(以下、ポリラミともいう)、基材に高分子フィルムを積層する等の方法がある。
【0013】
目止め処理に使用する接着剤としては、ポリビニルアルコール、ポリビニルピロリドン、ポリエチレンイミン、ポリアクリル酸塩、澱粉類、セルロース誘導体、ウレタン樹脂、アクリル樹脂、ポリエステル樹脂、アルキッド樹脂、メラミン樹脂、スチレン−ブタジエン共重合体ラテックス、スチレン−アクリル共重合体ラテックスおよびアクリル酸エステル樹脂系等を単独、もしくは併用して使用することができる。顔料としては、カオリン、水酸化アルミニウム、重質炭酸カルシウム、軽質炭酸カルシウム、酸化チタン、タルク、サチンホワイト、硫酸カルシウム、硫酸バリウム、酸化亜鉛、シリカ等の無機顔料、ポリプロピレン樹脂、ポリエチレン樹脂、スチレン樹脂、アクリル−スチレン樹脂、尿素−ホルマリン樹脂、メラミン−ホルマリン樹脂、ベンゾグアナミン樹脂等の有機顔料を単独、もしくは併用して使用することができる。
【0014】
本発明の剥離剤層に使用する剥離剤としては、硬化性ポリシロキサンを含有する必要がある。硬化性ポリシロキサンとしては、ポリジメチルシロキサン、ポリメチルフェニルシロキサン、ポリジフェニルシロキサンなどが例示でき、これらポリシロキサンを1種又は2種以上を用いて形成するとよい。中でも、剥離性および印刷性の両方の特性を持たせるには、硬化性ポリジメチルシロキサンを含有するものが好ましい。なお、剥離剤層中には、硬化性ポリシロキサンの他に、レジン系剥離コントロール剤等を適宜含有することもできる。
【0015】
剥離剤層中の硬化性ポリシロキサンの含有量は、剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキで形成される印刷層との密着性付与のために、剥離剤層全体の2質量%以上であることが好ましい。また、粘着剤層と剥離剤層との剥離性をより容易にするために、上記硬化性ポリシロキサンの含有量が5質量%以上であることがさらに好ましい。中でも、アクリル系粘着剤を用いる場合、硬化性ポリシロキサンの含有量は、10〜45質量%程度が特に好ましく、ゴム系粘着剤を用いる場合、硬化性ポリシロキサンの含有量は、15〜45質量%程度が特に好ましい。
【0016】
上記硬化性ポリシロキサン(以下、シリコーンとも言う)の形態としては、特に限定されないが、熱によって反応するタイプとして付加反応型、縮合反応型があり、放射線(例えば、紫外線、電子線)によって反応するタイプとしてラジカル付加型、ラジカル重合型、カチオン重合型等がある。また、それらには溶剤系、無溶剤系、エマルジョン系があり、各々の特徴によって使い分けて使用される。例えば、安価であり、汎用性の高い溶剤系又は無溶剤系の熱硬化型の付加反応シリコーンが好ましく用いられる。
また、フィルム基材等に塗工する場合などは、フィルムの熱収縮性等を考慮して無溶剤系の紫外線硬化型のラジカル付加反応シリコーン、カチオン重合型シリコーン等が好ましく用いられる。これらのシリコーンには基材との密着性を向上させるためにシランカップリング剤、あるいは粘着剤層に対する剥離力を制御するために、レジン系剥離コントロール剤、シリコーンオイル、シリカ等の助剤を適宜添加しても良い。
【0017】
上記剥離剤層中には、剥離剤層との剥離性に加え、インキ密着性向上、マジックインキでの筆記性、インクリボンの熱による溶融転写性、高摩擦係数等を単独もしくは複合的に付与させる目的として、エラストマーおよび/又はセルロース誘導体を含有することが好ましい。中でも、剥離剤層面に熱転写方式によってインクリボンを溶融転写させる剥離剤層として用いる場合、剥離剤層が、熱によって軟化し、インキとの親和性(すなわち、転写性および定着性)を向上させる目的として、エラストマーを少なくとも50質量%含有することが好ましい。さらに、インキとの親和性と粘着剤との剥離性を両立させるためには、エラストマー80〜98質量%および付加反応型ポリシロキサン2〜20質量%を含むことが好ましい。
【0018】
また、マジックインキでの筆記性を有する剥離剤層として用いる場合、上記剥離剤が、マジックインキ密着性を高め、マジックインキ吸油性を発揮させるためにセルロース誘導体を少なくとも10質量%含有することが好ましく、さらに、マジックインキでの筆記性と粘着剤との剥離性を両立させるためには、セルロース誘導体10〜50質量%および付加反応型ポリシロキサン50〜90質量%を含むことが好ましい。
【0019】
剥離剤層に使用するエラストマーとしては、エチレン−プロピレンゴム(EPM)、エチレン−プロピレンターポリマー(EPDM)、ポリイソブチレン(PIB)、ポリウレタン、ポリスチレン、ポリエステル等が挙げられる。中でも、剥離剤層を形成させた時の剥離剤層表面のべたつき等が少なく、硬化性ポリジメチルシロキサンとの相溶性が良いエチレン−プロピレンゴム、エチレン−プロピレンターポリマーが好ましい。さらに、耐熱性、耐候性、又は耐薬品性の向上、あるいは粘度調整などを目的としてスチレン−ブタジエンゴム、ブチルゴム、ニトリルゴム、ポリブタジエンゴム、塩化ビニル、ポリイソプレン、エチレン−酢酸ビニルコポリマー、あるいはこれら2種以上からなるポリマーアロイなどを本来の性能を損なわない程度に、適宜添加することもできる。
【0020】
剥離剤層に使用するセルロース誘導体としては、例えば、メチルセルロース、エチルセルロース、エチルヒドロキシエチルセルロース、ベンジルセルロース、アミノエチルセルロース、カルボキシメチルセルロース、カルボキシエチルセルロース等が挙げられる。単独もしくは2種以上を混合して用いても良い。
【0021】
剥離剤層の形成方法に特に限定はないが、例えばグラビアダイレクト法、グラビアリバース法、バーコート法、ロッド塗工法等が挙げられる。剥離剤層を硬化させる方法は、熱硬化型では70〜140℃程度で硬化させるとよく、紫外線もしくは電子線硬化型では専用の照射装置を用いて硬化させるとよい。上記剥離剤層の固形分塗布量は、特に限定されないが、剥離剤の硬化性、コストなどを考慮すると、0.05〜2g/m程度であることが好ましい。
【0022】
本発明の印刷層を形成するインキは、剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキを使用する。因みに、酸化重合型インキ、熱硬化型インキでは、剥離剤層との密着性が不良となる。
【0023】
剥離性放射線硬化型ポリシロキサンの官能基としては、放射線による反応に寄与するものを主体として、さらには反応性を高めたり、他の材料との親和性等を付与させるものであり、その種類は特に限定されないが、例えば、メルカプト基、ビニル基、ヘキセニル基、エポキシ基、アセトキシ基、メトキシ基、エトキシ基、フェニル基、アミノ基等が挙げられる。中でも、ビニル基を持った剥離性放射線硬化型ポリジメチルシロキサンを含有する剥離性放射線硬化型インキが好ましい。
本発明に使用される放射線とは、紫外線、電子線、α線、β線、γ線、中性子線、X線等が挙げられるが、操作性に優れる紫外線、電子線が好ましく、比較的コンパクトで安価な設備によって使用できる紫外線が特に好ましい。上記剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキは、剥離性紫外線硬化型インキであることが好ましい。さらに、粘着剤層と印刷層との剥離性を容易にするため、剥離性放射線硬化型ポリジメチルシロキサンを5質量%以上含有することが好ましい。
【0024】
印刷を施していない剥離剤層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)が35度以下であることが好ましい。上記接触角を調整することによって、剥離剤層表面に対する剥離性放射線硬化型インキの密着性をいっそう高めることが可能となる。中でも、剥離剤層に対して、上記剥離性放射線硬化型インキのハジキを抑制し、均一で印刷ムラのない印刷層を設けるため、印刷を施していない剥離剤層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)は0〜25度であることが好ましい。
【0025】
上記剥離性放射線硬化型ポリシロキサンを含有する特定の剥離性放射線硬化型インキを用いることによって、硬化性ポリシロキサンを含有する剥離剤層表面に対する親和性(以下、インキ定着性ともいう)が高まって、インキ密着性の良い印刷を施した剥離シートを形成できる。
さらに、剥離性放射線硬化型ポリジメチルシロキサンを含有する特定の剥離性紫外線硬化型インキを用いることによって、簡単かつ簡素な機械設備で容易に印刷することが可能となり、また剥離剤層とインキとの密着性に優れたものとなる。その他、熱硬化型ポリジメチルシロキサンを含有する熱硬化型インキを用いて印刷することが考えられるが、熱乾燥するための設備として、長いオーブンを必要としたり、基材としてフィルム等を用いた場合、基材が収縮するという欠点があり、また剥離性放射線硬化型インキほどの密着性が得られないため好ましくない。
【0026】
本発明の剥離性紫外線硬化型インキは、アクリル酸系樹脂、光重合開始剤、剥離性放射線硬化型ポリシロキサンおよび着色剤を主成分とするものである。その他に、硬化性を阻害しない範囲で、重合禁止剤、ワックス、溶剤、活性化合物やその他の助剤等を適宜添加してもよい。
【0027】
上記剥離性放射線硬化型ポリシロキサンとしては、例えば、メルカプト基とビニル基との反応によって硬化するラジカル付加型シリコーン、ヒドロシリル化反応型シリコーン、アクリル系ラジカル重合型シリコーン、エポキシ基含有のカチオン重合型シリコーン等が挙げられる。これらに限定されるものではない。
【0028】
上記アクリル酸系樹脂としては、例えば、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ジペンタエリスリトールヘキサアクリレート等の多価アルコールのアクリル酸エステル、エポキシアクリレート、ウレタンアクリレート、ポリエステルアクリレート、ポリエーテルアクリレート、アクリレートアルキッド、メラミンアクリレート等のプレポリマー、ヒドロキシブチルアクリレート、1,6−ヘキサンジオールジアクリレート、トリメチロールプロパントリアクリレート、ビスフェノールA型エポキシフェニルアクリレート等のモノマーが挙げられる。これらに限定されるものではない。
【0029】
上記光重合開始剤としては、例えば、アントラキノン、アセトフェノン、2,2−ジエトキシアセトフェノン、2−ヒドロキシ−2−メチルプロピオフェノン、2,2−ジメトキシ−2−フェニルアセトフェノン、p−ジメチルアセトフェノン、p−ジメチルアミノプロピイフェノン、ベンゾフェノン、2−クロロベンゾフェノン、4,4‘−ジクロロベンゾフェノン、4,4’−ビスジエチルアミノベンゾフェノン、ミヒラーケトン、ベンジル、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、メチルベンゾイルフォメート、ジブチルフェニルホスフィン、ヒドロキシアルキルフェノン、アルキルアミノフェノン、チオキサントン等が挙げられる。これらの光重合開始剤は単独で使用しても良いし、2種以上組み合わせて用いても良い。
【0030】
光重合開始剤の使用量は、剥離性放射線硬化型ポリシロキサン100重量部に対して、0.01〜10重量部が好ましい。電子線又はγ線などの硬化手段とする場合には、必ずしも重合開始剤を添加する必要はない。
【0031】
上記着色剤としては、例えば、有機系又は無機系の顔料や染料、カーボン、金属粉末などを適宜用いることができる。因みに、有機系顔料としては、例えば、アゾ系顔料、フタロシアニン系顔料、トリフェニルメタン系顔料、金属錯塩系顔料、バット染料系顔料、キナクリドン系顔料、イソインドリノン系顔料などが挙げられる。また、無機系顔料としては、例えば、シリカ、チタン、アルミナ、亜鉛華、ジルコニア、酸化カルシウム、マイカのような白色顔料、酸化マンガン・アルミナ、酸化クロム・酸化鉛、酸化鉄、硫化カドミウム・硫化セレンのような赤色顔料、酸化コバルト、ジルコニア・酸化バナジウム、酸化クロム・五酸化二バナジウムのような青色顔料、酸化クロム・酸化コバルト・酸化鉄・酸化マンガン、クロム酸塩、過マンガン酸塩のような黒色顔料、ジルコニウム・珪素・プラセオジム、バナジウム・鉛、クロム・チタン・アンチモンのような黄色顔料、酸化クロム、コバルト・クロム、アルミナ・クロムのような緑色顔料、アルミニウム・マンガン、鉄・珪素・ジルコニウムのような桃色顔料、等がその代表例として挙げられる。
【0032】
上記剥離性放射線硬化型インキを用い、印刷層を剥離剤層表面上に形成する方法としては、公知の印刷方法であれば、特に限定されないが、例えば、フレキソ印刷、凸版印刷、オフセット印刷、グラビア印刷、スクリーン印刷等によって印刷し、放射線を照射することによって形成することが可能である。
【0033】
上記印刷層の硬化後の厚みは、10μm以下、好ましくは 5μm以下になるように印刷することが好ましい。印刷層の厚みが10μmより厚くなると、印刷層の凝集力が低下する場合や、印刷していない部分との段差を生じたり、インキのコストや放射線量を多く必要とするなどコスト的に不利であるため好ましくない。さらに好ましい厚みは、0.1〜3μmである。0.1μmより薄いと、剥離剤層表面の凹凸によって印刷されない部分が出来てしまう。
【0034】
また、剥離剤層に対する印刷層の面積は、部分印刷でも全面印刷であっても差し支えない。印刷層が剥離剤層を全て覆っても、印刷層と粘着剤層との剥離性等に問題はない。さらに、上記剥離剤層には段階的に異なる印刷を印刷部分が重ならないように、あるいは重なるように施してもよい。
【0035】
本発明の剥離剤層は、剥離剤層面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)を45度以上にすることが好ましい。特に、剥離剤層面の接触角は、インキ密着性を配慮すると、上記接触角は45〜65度であることがより好ましい。因みに、剥離剤層面の接触角が45度より低くなると、インキとの密着性は向上するが、粘着剤層との剥離性が低下(以下、重剥離化ともいう)する傾向がある。一方、接触角が65度より高くなると、粘着剤層との剥離性が向上(以下、軽剥離化ともいう)するが、インキとの密着性は低下する傾向がある。また、印刷層面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)を45度以上にすることが、粘着剤層との剥離性に優れるので好ましい。
【0036】
上記剥離剤層表面および印刷層表面の接触角は、印刷層を形成するインキ中に含有する剥離性放射線硬化型ポリシロキサンの配合量や、剥離剤層に使用される表面エネルギーの異なる材料の添加によって調整することが可能である。例えば、剥離剤層で接触角を制御する場合、硬化性ポリシロキサンの配合量を増やすか、あるいはエチレン−プロピレンターポリマー等の表面エネルギーの低い材料を用いることによって接触角は高くなる。また、ポリシロキサンの配合量を減らすか、あるいはセルロース誘導体などの表面エネルギーの高い材料を用いることによって、剥離剤層面の接触角を低くすることが可能である。
一方、剥離性放射線硬化型インキで接触角を制御する場合、印刷層を形成するインキ中に含有する剥離性放射線硬化性ポリシロキサンの配合量を変えることによって、調整することが可能である。例えば、剥離性放射線硬化型ポリシロキサンの配合量を増やすと接触角は高くなる。また、剥離性放射線硬化型ポリシロキサンの配合量を減らすと接触角は低下する。
【0037】
このようにして得られた剥離シートは、剥離剤層上に印刷がなされているので、剥離剤を塗工する前に印刷をする必要がなく、印刷インキを調整することによって部分的に剥離力が異なる剥離シートを作製したり、 全面印刷することによって剥離剤層の有する剥離性やインキ密着性等の特性を全く変えた剥離シートや粘着テープ等の様々な用途、仕様に適う形態をとり得る剥離シートであるという点で有用である。
【0038】
本発明の印刷層を形成した剥離シートは、裏面に粘着剤層を形成した後、そのまま巻取り状にして粘着テープとすることができ、またこの形態が好ましい。
上記粘着テープに使用される粘着剤としては、アクリル系粘着剤、天然ゴム系粘着剤、合成ゴム系粘着剤、ウレタン系粘着剤が例示でき、中でも、モノマー組成、界面活性剤等の変更によって比較的粘着力、剥離力を調整することが容易であり、耐候性に優れたアクリル系粘着剤が好ましい。上記アクリル系粘着剤として、特に限定されることはないが、例えば、主モノマーとしてエチルアクリレート(EA)、ブチルアクリレート(BA)、2−エチルヘキシルアクリレート(2−EHA)、コモノマーとして酢酸ビニル(VAc)、アクリロニトリル(AN)、スチレン(St)、メチルメタクリレート(MMA)、アクリル酸(AA)、イタコン酸(IA)、ヒドロキシエチルメタクリレート(HEMA)、ヒドロキシプロピルメタクリレート(HPMA)、ジメチルアミノエチルメタクリレート(DM)、アクリルアマイド(AM)、メチロールアクリルアマイド(N−MAN)、グリシジルメタクリレート(GMA)、無水マレイン酸等を主成分(好ましくは80質量%以上)とするものが挙げられる。なお、剥離剤層にエラストマーを含有する場合、粘着剤に天然ゴム系粘着剤、合成ゴム系粘着剤などを用いると、極端に剥離力が高くなってしまうおそれがある。その理由としては、剥離剤層が熱可塑性エラストマーを含むブレンド組成物であり、天然ゴム系粘着剤や合成ゴム系粘着剤のエラストマー成分に近い性質があり、SP値が近いためではないかと推察される。したがって、ゴム系粘着剤を用いる場合、剥離剤層成分とSP値の差が大きいものを選ぶと良い。好ましいSP値の差としては、1.0以上である。また、粘着剤には、必要に応じて適宜、タッキファイヤー、紫外線吸収剤、架橋剤、軟化剤、顔料、老化防止剤等の各種添加物を配合することができる。本発明の粘着テープに用いる粘着剤は、上記原料を用いて常法に従って調整することができる。
【0039】
粘着剤の塗布量は、粘着剤の種類、粘着テープの用途等によって異なるが、10〜70g/m2である。中でも、20〜50g/m2がより好ましい。塗布量が10g/m2未満の場合には、段ボールなどの封かん性が悪くなることがあり、また70g/m2を超えると、テープ端面からの粘着剤のはみ出しが起こったり作業性が悪化する場合がある。
【0040】
粘着剤の塗工方式は、特に限定されないが、例えば、コンマコート法、リバースコート法、グラビアコート法、リバースグラビア法、キスコート法、ナイフコート法、バーコート法および工程紙にこれらの方式で塗布したものを転写させる転写法等が挙げられる。
【0041】
本発明の剥離シートの剥離剤層面と上記印刷層との接着力をα、上記印刷層と上記粘着剤層との接着力βとした場合に、接着力α>接着力βの関係を満足することは、剥離剤層上に印刷層を形成したインキが粘着剤層側に付着することなく印刷ができ、かつ粘着剤層が剥離性を有するために重要な品質要件となる。そのためには、上記した特定の剥離剤層および特定の印刷層を形成することが必要である。
【0042】
本発明の粘着剤層を設けた構成のものを印刷する方法は、特に限定されないが、例えば、粘着テープ給紙部及び巻取り部を有し、粘着テープの粘着剤層面が接触するロールにはシリコーンロール、テフロンロール等の粘着剤との極めて高い剥離性を有するロールが装着された印刷機によって印刷(例えば、フレキソ印刷、凸版印刷、オフセット印刷、グラビア印刷、スクリーン印刷、転写印刷等)し、印刷後に紫外線照射機等の放射線照射装置を備えた印刷機によって印刷することが好ましい。
【0043】
さらに具体的な用途について例示する。
▲1▼ 感熱記録層上に剥離剤層を形成させた剥離シート又は粘着テープに感熱方式で印字を施した後、感熱印字を施した剥離シート又は粘着テープの剥離剤層の全面或いは一部に剥離性放射線硬化型インキで印刷を施すことができる。
▲2▼ 剥離シート又は粘着テープの剥離剤層の全面或いは一部に剥離性放射線硬化型インキで印刷を施した後、感熱方式で印字を施すことができる。
▲3▼ 剥離剤層中にエラストマー成分を含有する剥離シート又は粘着テープに、市販の熱転写リボンを用いて熱転写方式により印字を施した後、熱転写印字を施した剥離シート又は粘着テープの全面或いは一部に剥離性放射線硬化型インキで印刷を施すことができる。
▲4▼ 剥離シート又は粘着テープの全面或いは一部に剥離性放射線硬化型インキで印刷を施した後、市販の熱転写リボンを用いて熱転写方式により印字を施すことができる。
これらは、固定情報を印刷で行い、個別情報をプリンター印字により行うことができる。
また、剥離シート又は粘着テープの剥離剤層の全面或いは一部に、剥離性放射線硬化型インキで印刷を施した後、剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキを含有したインクリボンを用いて、熱転写方式によって印字を施すこともできる。この場合、剥離剤層と印刷層との熱転写インクの定着性や粘着剤との剥離性に優れた品質を得ることができる。
【0044】
例えば、図1、図2、図3のような構成とすることができ、それぞれの構成によって様々な用途として利用する事が可能である。例えば、図2、3の構成とすることによって、籤などの隠し印刷が施された剥離シートや、図4のような粘着テープとすることによって、販売会社のロゴマークを入れた製品、またはバーコード印字した面の印字部/印字無し部に絵柄印刷した粘着テープ、あるいは絵柄印刷した粘着テープの絵柄印刷部以外の部分にバーコード印字を施した製品とすることもできる。
【0045】
【実施例】
以下に、実施例を挙げて本発明を具体的に説明するが、本発明はこれによって制限されるものではない。尚、実施例および比較例中の「部」および「%」は、特に断りのない限り固形分あるいは有効成分の「質量部」および「質量%」を示す。
【0046】
実施例1
(剥離シートの作製)
基材として64g/m2の上質紙(商品名:OK上質紙、王子製紙社製)の片面上にSBR(商品名:L−1571、旭化成社製)50部、カオリン(商品名:HTクレー、エンゲルハード社製)50部、消泡剤(商品名:ノプコ1407K、サンノプコ社製)0.5部、潤滑剤(商品名:ノプコートC104、サンノプコ社製)0.9部からなる目止め層を塗布量が7g/m2になるように目止め層を設けた基材(A)を作製した。
次いで、ムーニー粘度(ML1+4、at100℃)85、エチレン含有量62重量%、比重0.86のエチレン−プロピレンターポリマー(商品名:EP75F、JSR社製)90部、および架橋剤を含む付加反応型ポリジメチルシロキサン(商品名:LTC300B、東レダウコーニング社製)10部をトルエン溶液に溶解し、さらに白金系触媒(商品名:SRX212、東レダウコーニング社製)を上記ポリジメチルシロキサン(商品名:LTC300B、東レダウコーニング社製)100部に対して1.5重量部加え、良く攪拌した混合溶液を調製した。
この混合溶液を上記基材(A)の目止め層を設けた面に、メイヤバーを用いて固形分1.5g/mとなるよう塗工し、乾燥(オーブン温度130℃、乾燥時間30秒)させて剥離剤層を設けた。得られた剥離剤層面に下記配合の剥離性紫外線硬化型インキを、恩田製作所シール印刷機を用いて剥離剤層上に塗布した。その後、光量20mW/cm2で紫外線照射を行い、凸版UV印刷を行い、印刷を施した剥離シートを作製した。なお、得られた剥離シートの熱転写印字適性および油性インキでの筆記性においても良好であった。
【0047】
「剥離性紫外線硬化型インキ」
着色剤(商品名:オイルレッド、純正化学社製) 18部
ビスフェノールA型エポキシフェニルアクリレート 38部
1,6−ヘキサンジオールアクリレート 5部
トリメチロールプロパントリアクリレート 20部
2−ヒドロキシ−2−メチルプロピオフェノン(光重合開始剤) 5部
2,2−ジメトキシ−2−フェニルアセトフェノン(光重合開始剤) 3部
剥離性紫外線硬化型ポリジメチルシロキサン 8部
(商品名:BY24−551A、東レ・ダウコーニング・シリコーン社製)
剥離性紫外線硬化型ポリジメチルシロキサン 2部
(商品名:BY24−551B、東レ・ダウコーニング・シリコーン社製)
シランカップリング剤 0.2部
(商品名:BY24−848、東レ・ダウコーニング・シリコーン社製)
IPA 0.8部
【0048】
実施例2
剥離剤として付加反応型のシリコーン系剥離剤(商品名:BY24−312、東レダウコーニング社製、固形分濃度30%、)60部に、エチルセルロース(東京化成工業社製の粉末試薬)を40部加えた混合物をトルエンで溶解し、さらに白金系硬化触媒(商品名:SRX−212、東レダウコーニング社製)2部を添加した混合溶液を調製して、剥離剤塗工液として用いた以外は、実施例1と同様にして印刷を施した剥離シートを得た。なお、得られた剥離シートの熱転写印字適性および油性インキでの筆記性においても良好であった。
【0049】
実施例3
剥離性放射線硬化型インキとして下記組成のものに代えた以外は、実施例1と同様にして印刷を施した剥離シートを得た。なお、得られた剥離シートの熱転写印字適性および油性インキでの筆記性においても良好であった。
【0050】
「剥離性紫外線硬化型インキ」
着色剤(商品名:オイルレッド、純正化学社製) 25部
ビスフェノールA型エポキシフェニルアクリレート 20部
1,6−ヘキサンジオールアクリレート 2部
トリメチロールプロパントリアクリレート 10部
2−ヒドロキシ−2−メチルプロピオフェノン(光重合開始剤) 3部
2,2−ジメトキシ−2−フェニルアセトフェノン(光重合開始剤) 1部
剥離性紫外線硬化型ポリジメチルシロキサン 28部
(商品名:BY24−551A、東レ・ダウコーニング・シリコーン社製)
剥離性紫外線硬化型ポリジメチルシロキサン 9部
(商品名:BY24−551B、東レ・ダウコーニング・シリコーン社製)
シランカップリング剤 1.2部
(商品名:BY24−848、東レ・ダウコーニング・シリコーン社製)
IPA 0.8部
【0051】
実施例4
剥離性放射線硬化型インキとして下記組成のものに代えた以外は、実施例1と同様にして印刷を施した剥離シートを得た。なお、得られた剥離シートの熱転写印字適性および油性インキでの筆記性においても良好であった。
「剥離性紫外線硬化型インキ」
着色剤(商品名:オイルレッド、純正化学社製) 17部
剥離性紫外線硬化型ポリジメチルシロキサン 60部
(商品名:BY24−551A、東レ・ダウコーニング・シリコーン社製)
剥離性紫外線硬化型ポリジメチルシロキサン 18部
(商品名:BY24−551B、東レ・ダウコーニング・シリコーン社製)
シランカップリング剤 5部
(商品名:BY24−848、東レ・ダウコーニング・シリコーン社製)
【0052】
比較例1
実施例1に記載した目止め層を設けた基材(A)に、剥離剤として長鎖アルキルペンダント型ポリマー(商品名:ピーロイル1010、一方社油脂工業社製)をトルエンに溶解し、メイヤーバーを用いて基材の目止め層面上に固形分0.1g/m2となるよう塗工し、乾燥(乾燥温度100℃、乾燥時間30秒)した後、実施例1と同じ条件のインキ、印刷機で印刷を行い、印刷を施した剥離シートを得た。なお、得られた剥離シートの熱転写印字適性および油性インキでの筆記性は得られなかった。
【0053】
比較例2
剥離性放射線硬化型インキとして市販のUVインキ(商品名:フレキソAF藍、T&K TOKA社製)を用いた以外は実施例1と同様にして印刷を施した剥離シートを作製したが、インキの剥離面に対するハジキを生じ、印刷を施した剥離シートを得ることができなかった。
【0054】
上記実施例および比較例で得た剥離シートについて、それぞれ下記の方法により評価を行い、その結果を表1に示した。
【0055】
<印刷インキのハジキ>
恩田製作所シール印刷機を用いてUV印刷を行った際、剥離シートの剥離面に対する印刷インキのハジキを下記の基準で評価した。
○:剥離剤層面に対するインキのハジキがなく、奇麗な印刷面が形成される。
△:若干剥離剤層面に対するインキのハジキがあるが、ほぼ奇麗な印刷面が形成される
×:剥離剤層面に対してインキのハジキがあり、目的とする印刷面が形成されない。
【0056】
<印刷インキの密着性>
印刷を施した剥離シートの印刷面を指の腹で擦って下記の基準で評価した。
○:強く擦っても全くインキかすれ、インキ汚れ、インキ落ちがない。
△:強く擦ると若干インキかすれまたはインキ汚れを生じるが、インキ落ちはない。
×:強く擦るとインキかすれ、インキ汚れ、インキ落ちのいずれかが判別できるほど発生する。
【0057】
<印刷インキの耐擦過性>
染色堅牢度試験機(スガ試験機社製、FR−2)を用いて、印刷を施した剥離シートの印刷面に消しゴムを当て、500gf(一定)で最大100回往復させた時に記録された部分のインキかすれ、インキ汚れ、インキ落ち等の変化が現れるまでの回数を記録し、下記の基準で評価した。
(目視評価)
◎:50回往復してもインキかすれ、インキ汚れ、インキ落ちがない。
○:40回以上往復してもインキかすれ、インキ汚れ、インキ落ちがない。
△:30回以上(40回未満)往復してもインキかすれ、インキ汚れ、インキ落ちがない(実用上使用可能限界)。
×:30回未満でインキかすれ、インキ汚れ、インキ落ちのいずれかが発生する。
【0058】
<剥離剤層および印刷層の接触角>
23℃環境下、水とエタノールの質量比が1:1である溶液をマイクロシリンジを用いて、剥離剤層面または印刷層面に5μl滴下し、60秒後の接触角をJIS K 3211に準じて測定した。
【0059】
【表1】

Figure 0004710173
【0060】
実施例5
実施例1の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。なお、得られた粘着テープの熱転写印字適性および油性インキでの筆記性においても良好であった。また、印刷層表面が、粘着剤により剥がれることがなく良好なものであった。
【0061】
実施例6
実施例2の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。なお、得られた粘着テープの熱転写印字適性および油性インキでの筆記性においても良好であった。また、印刷層表面が、粘着剤により剥がれることがなく良好なものであった。
【0062】
実施例7
実施例3の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。なお、得られた粘着テープの熱転写印字適性および油性インキでの筆記性においても良好であった。また、印刷層表面が、粘着剤により剥がれることがなく良好なものであった。
【0063】
実施例8
実施例4の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。なお、得られた粘着テープの熱転写印字適性および油性インキでの筆記性においても良好であった。また、印刷層表面が、粘着剤により剥がれることがなく良好なものであった。
【0064】
比較例3
比較例1の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。なお、得られた粘着テープの熱転写印字適性および油性インキでの筆記性は得られなかった。
【0065】
比較例4
比較例2の剥離シートの剥離剤層面と反対面に、アクリル系粘着剤(商品名:L−145K、日本カーバイド社製)を固形分塗布量が30g/m2となるように塗布し、乾燥させた後、巻き取って剥離剤層面に印刷を施した粘着テープを作製した。
【0066】
<粘着剤層と剥離剤層との剥離性>
剥離シートの剥離剤層と粘着剤層との剥離性は、23℃、50%RH環境下、実施例5〜8で作製した粘着テープを巻き戻し、上記印刷を施した剥離シートの剥離剤層面上の印刷面に、粘着剤層が貼り合わされるように貼り付け、2Kgの圧着ロールで1往復させた後、JIS Z 0237に準じて、該粘着シートを引張り試験機で300mm/分の剥離速度で180°剥離した時の剥離力(N/m)を測定した。
【0067】
上記実施例で得た粘着テープについて、上記の方法により評価を行い、その結果を表2に示した。
【0068】
【表2】
Figure 0004710173
【0069】
表1から明らかなように、実施例1〜4のような印刷を施した剥離シートは、印刷部および非印刷部ともに粘着剤と剥離剤層との剥離性に優れ、かつ情報や意図を記録した剥離シートを得る事ができた。また、表2から明らかなように、実施例5〜8は、印刷層と粘着剤層との剥離性に問題がなく、印刷を施した粘着テープを提供することができた。
【0070】
表1における比較例1の剥離シートは、粘着剤の剥離力が高く、印刷部のインキ密着性が劣るため実用には適さない。比較例2では、インキのハジキを生じたため、印刷を施した剥離シートを得る事ができなかった。
【0071】
【発明の効果】
本発明の剥離剤層に硬化性ポリシロキサンを含有し、印刷層に剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキを用いることにより、剥離剤層とインキの密着性に優れた印刷を施した剥離シートが得られた。また、剥離性放射線硬化型ポリシロキサンの中でも、剥離性放射線硬化型ポリジメチルシロキサンがインキと粘着剤層との剥離性に優れる。さらに剥離性放射線硬化型インキの中でも、作業性の低下や基材等の劣化を起こさない剥離性紫外線硬化型インキが好ましく、剥離シートの印刷部、非印刷部の剥離剤層面と粘着剤との剥離性に優れ、情報や意図を備えた剥離シートを提供することが可能となった。
また、上記印刷部の剥離力を調整することによって、部分的に剥離力を変えた剥離シートや、上記印刷を施した剥離シートの印刷面に粘着シートを重ねることによって籤等とすることも可能である。
さらに、上記剥離シートの剥離剤層面に容易に印刷することが可能なため、販売会社等のロゴマークを付与した安価な粘着テープを提供することが可能である。
また、感熱記録層を形成させた剥離シート又は粘着テープに剥離性放射線硬化型インキで印刷を施す前或いは印刷を施した後、感熱方式で印字を施したり、エラストマーを含有する剥離シート又は粘着テープに剥離性放射線硬化型インキで印刷を施す前或いは印刷を施した後、市販の熱転写リボンを用いて熱転写方式により印字を施すことにより、実用上適した態様となる。
【図面の簡単な説明】
【図1】本発明の印刷を施した剥離シートの断面を示す模式図。
【図2】本発明の印刷を施した剥離シートの使用一例図。
【図3】本発明の印刷を施した剥離シートの平面を示す模式図。
【図4】本発明の印刷を施した剥離シートの剥離剤面とは他面に粘着剤を設けて粘着テープとした応用例の斜視を示す模式図。
【図5】従来の印刷を施した剥離シートの断面を示す模式図。
【符号の説明】
a:基材(剥離シート用又は粘着テープ用)
b:剥離剤層
c:印刷部
d:印刷を施した剥離シート
e:粘着剤層
f:表面基材
g:粘着シート
h:粘着ラベル
i:印刷を施した粘着テープ[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a release sheet and an adhesive tape. More specifically, the present invention relates to a release sheet and a pressure-sensitive adhesive tape in which information or the like is printed on the release agent layer surface.
[0002]
[Prior art]
In general, a release sheet has a configuration in which a release agent layer is provided on at least one surface of a substrate, and is used to protect the adhesive layer surface of a label or the like until use. On the other hand, the pressure-sensitive adhesive tape is provided with a pressure-sensitive adhesive layer on one side of the substrate and a release agent layer on the other side.
As the release agent used, long-chain alkyl group-containing compounds, silicone modified resin release agents, silicone release agents, etc. are mainly used, but silicone release agents are particularly superior to adhesives. Currently, it is most frequently used to exert its peelability.
[0003]
However, the silicone-based release agent usually has a small critical surface tension on the release agent layer surface, and writing on the release agent layer surface with a magic, etc., thermal transfer printing using an ink ribbon, or printing is not possible. Is possible. In addition, printing on the surface of the release agent layer using normal printing ink is considered an impossible technology for both the ink manufacturer and the release agent manufacturer. Silicone release with information on the release agent layer There was no sheet.
[0004]
On the other hand, there is a release agent coated with a long-chain alkyl group-containing compound. The release agent layer provided with this long-chain alkyl group-containing compound is characterized in that it can be written with oily magic or the like. However, long-chain alkyl group-containing compounds have too high peel strength when compared to silicone-based release agents, and heat resistance is poor. There were problems such as causing abnormal peeling.
[0005]
As a general label, a label having a structure in which a release sheet is laminated on a surface base material via an adhesive layer is often used. Although information etc. are printed / printed on the surface base material, the release sheet is only used to protect the adhesive, and has a problem of being discarded without performing other functions. .
[0006]
In order to solve these drawbacks, a release sheet having information or the like is manufactured by printing with normal ink on one side or both sides of the substrate in advance and further providing a release agent layer on the print layer. It has been broken.
However, since the release agent is applied after printing and, in some cases, the adhesive is applied to the back surface, considering the yield at the time of manufacture, the quantity will be printed more than the quantity of the final product. The nature was bad. In addition, since it is impossible to print on products once processed to release agent or adhesive processing, if there are any troubles, defects, etc., there is a problem that all including printing processing will be lost. It was.
[0007]
On the other hand, Japanese Patent Application Laid-Open No. 7-150092 proposes a release sheet provided with a release surface with a releasable ink, with the object of allowing the sheet base material to be colored with a single release surface. However, although it is possible to print the peelable ink directly on the substrate, it is not possible to print on the release agent layer surface of the release sheet. Further, the obtained release sheet was also unstable in peeling force.
[0008]
[Problems to be solved by the invention]
An object of this invention is to provide the peeling sheet and adhesive tape which are excellent in the peelability of an adhesive layer and the surface of a release agent layer, and the printing / printing recordability by a printing ink, and also with little load to an environment.
[0009]
[Means for Solving the Problems]
The following invention is included.
(1) A release sheet having a release agent layer on at least one surface of a substrate, and having a printing layer on at least a part of the surface of the release agent layer, wherein the release agent layer comprises a curable polysiloxane-containing release agent. A release sheet, wherein the ink which is formed by curing and forms the printing layer is a peelable radiation curable ink containing a peelable radiation curable polysiloxane.
(2) The release sheet according to (1), wherein the peelable radiation curable polysiloxane is a peelable radiation curable polydimethylsiloxane.
(3) The release sheet according to (1) or (2), wherein the peelable radiation curable ink contains at least 5% by mass of peelable radiation curable polysiloxane.
(4) The release sheet according to (1) to (3), wherein the peelable radiation curable ink is a peelable ultraviolet curable ink.
(5) The release sheet according to (1) to (4), wherein the curable polysiloxane is a curable polydimethylsiloxane.
(6) The release sheet according to any one of (1) to (5), wherein the release agent layer further contains an elastomer and / or a cellulose derivative.
(7) The release sheet according to (6), wherein the release agent layer contains at least 50% by mass of the elastomer, and the release agent layer has melt heat transfer recording suitability.
(8) The release sheet according to (6) or (7), wherein the release agent layer contains 80 to 98% by mass of an elastomer and 2 to 20% by mass of curable polydimethylsiloxane.
(9) The release sheet according to (6), wherein the release agent layer contains at least 10% by mass of a cellulose derivative.
(10) The release sheet according to (6) or (9), wherein the release agent layer contains 10 to 50% by mass of a cellulose derivative and 50 to 90% by mass of curable polydimethylsiloxane.
(11) The contact angle of the surface of the release agent layer with respect to a solution having a mass ratio of water to ethanol of 1: 1 (measured after 60 seconds in a drop amount of 5 μl in a 23 ° C. environment) is 45 to 65 degrees, and (1) to (10) in which the contact angle (measured after 60 seconds with a drop amount of 5 μl in a 23 ° C. environment) is 45 degrees or more with respect to a solution having a mass ratio of water and ethanol of 1: 1 on the surface of the printing layer Release sheet.
[0010]
The present invention further includes the following inventions.
(12) A release sheet described in any one of (1) to (11) above, having a release agent layer on one surface, and an acrylic pressure-sensitive adhesive layer provided on the surface opposite to the surface provided with the release agent layer Adhesive tape characterized by being rolled up.
(13) When the adhesive force between the release agent layer and the print layer of the release sheet is α and the adhesive force β between the print layer and the pressure-sensitive adhesive layer, the relationship of adhesive force α> adhesive force β The adhesive tape according to (12).
(14) A tape adhesive product in which the adhesive tape according to (12) or (13) is attached to an adherend.
[0011]
DETAILED DESCRIPTION OF THE INVENTION
As the substrate, a known adhesive tape substrate or release sheet substrate can be used. For example, kraft paper, glassine paper, high-quality paper, coated paper, cast coated paper, crepe paper, impregnated paper and other paper base materials, polypropylene, polyethylene, polyester, polyvinyl chloride, polystyrene and other polymer films, non-woven fabric, synthetic Paper, metal foil, etc. are mentioned, What laminated | stacked combining these suitably may be used. When applying a release agent or an emulsion type release agent adjusted with an organic solvent to a paper substrate, apply a sealing treatment to the substrate to prevent penetration of the release agent coating solution into the substrate. Is preferred.
[0012]
As the sealing treatment, for example, a material mainly composed of an adhesive and / or a pigment is applied in advance, a thermoplastic resin such as polyethylene is laminated on the substrate (hereinafter also referred to as polylamination), and a polymer is formed on the substrate. There are methods such as laminating films.
[0013]
Adhesives used for the sealing treatment include polyvinyl alcohol, polyvinylpyrrolidone, polyethyleneimine, polyacrylate, starch, cellulose derivative, urethane resin, acrylic resin, polyester resin, alkyd resin, melamine resin, and styrene-butadiene. Polymer latex, styrene-acrylic copolymer latex, acrylic ester resin system and the like can be used alone or in combination. Examples of pigments include kaolin, aluminum hydroxide, heavy calcium carbonate, light calcium carbonate, titanium oxide, talc, satin white, calcium sulfate, barium sulfate, zinc oxide, silica, and other inorganic pigments, polypropylene resin, polyethylene resin, and styrene resin. Organic pigments such as acrylic-styrene resin, urea-formalin resin, melamine-formalin resin, and benzoguanamine resin can be used alone or in combination.
[0014]
The release agent used for the release agent layer of the present invention needs to contain a curable polysiloxane. Examples of the curable polysiloxane include polydimethylsiloxane, polymethylphenylsiloxane, polydiphenylsiloxane, and the like, and these polysiloxanes may be formed using one kind or two or more kinds. Among them, those containing curable polydimethylsiloxane are preferable in order to have both peelability and printability. In the release agent layer, in addition to the curable polysiloxane, a resin-based release control agent and the like can be appropriately contained.
[0015]
The content of the curable polysiloxane in the release agent layer is the same as that of the entire release agent layer in order to provide adhesion with the print layer formed of the release radiation curable ink containing the release radiation curable polysiloxane. It is preferable that it is 2 mass% or more. Moreover, in order to make the peelability between the pressure-sensitive adhesive layer and the release agent layer easier, the content of the curable polysiloxane is more preferably 5% by mass or more. Among these, when an acrylic pressure-sensitive adhesive is used, the content of the curable polysiloxane is particularly preferably about 10 to 45% by mass. When a rubber-based pressure-sensitive adhesive is used, the content of the curable polysiloxane is 15 to 45% by mass. % Is particularly preferable.
[0016]
The form of the curable polysiloxane (hereinafter also referred to as silicone) is not particularly limited, but there are an addition reaction type and a condensation reaction type as a type that reacts with heat, and a reaction with radiation (for example, ultraviolet rays, electron beams). Types include radical addition type, radical polymerization type, and cationic polymerization type. In addition, there are a solvent system, a solvent-free system, and an emulsion system, and they are used separately depending on their characteristics. For example, a solvent-based or solvent-free thermosetting addition reaction silicone that is inexpensive and highly versatile is preferably used.
In the case of coating on a film substrate or the like, solvent-free ultraviolet curable radical addition reaction silicone, cationic polymerization type silicone or the like is preferably used in consideration of heat shrinkability of the film. In order to improve the adhesion to the base material for these silicones, a silane coupling agent or an auxiliary agent such as a resin-based release control agent, silicone oil, silica, etc. is appropriately used to control the release force to the adhesive layer. It may be added.
[0017]
In the above release agent layer, in addition to release properties from the release agent layer, improved ink adhesion, writing performance with magic ink, melt transferability by ink ribbon heat, high friction coefficient, etc. For the purpose, it is preferable to contain an elastomer and / or a cellulose derivative. In particular, when used as a release agent layer that melts and transfers an ink ribbon to the release agent layer surface by a thermal transfer method, the release agent layer is softened by heat to improve the affinity (that is, transferability and fixability) with ink. It is preferable to contain at least 50% by mass of an elastomer. Furthermore, in order to achieve both the affinity with the ink and the peelability of the pressure-sensitive adhesive, it is preferable to contain 80 to 98% by mass of an elastomer and 2 to 20% by mass of an addition reaction type polysiloxane.
[0018]
Further, when used as a release agent layer having a writing property with magic ink, the release agent preferably contains at least 10% by mass of a cellulose derivative in order to enhance the adhesion of the magic ink and exhibit the magic ink oil absorption. Furthermore, in order to achieve both the writing property with the magic ink and the peelability of the pressure-sensitive adhesive, it is preferable to contain 10 to 50% by mass of a cellulose derivative and 50 to 90% by mass of an addition reaction type polysiloxane.
[0019]
Examples of the elastomer used for the release agent layer include ethylene-propylene rubber (EPM), ethylene-propylene terpolymer (EPDM), polyisobutylene (PIB), polyurethane, polystyrene, polyester, and the like. Of these, ethylene-propylene rubbers and ethylene-propylene terpolymers, which have little stickiness on the surface of the release agent layer when the release agent layer is formed and have good compatibility with the curable polydimethylsiloxane, are preferable. Furthermore, styrene-butadiene rubber, butyl rubber, nitrile rubber, polybutadiene rubber, vinyl chloride, polyisoprene, ethylene-vinyl acetate copolymer, or these 2 for the purpose of improving heat resistance, weather resistance or chemical resistance, or adjusting viscosity. A polymer alloy composed of at least seeds can be appropriately added to such an extent that the original performance is not impaired.
[0020]
Examples of the cellulose derivative used in the release agent layer include methyl cellulose, ethyl cellulose, ethyl hydroxyethyl cellulose, benzyl cellulose, aminoethyl cellulose, carboxymethyl cellulose, carboxyethyl cellulose and the like. You may use individually or in mixture of 2 or more types.
[0021]
The method for forming the release agent layer is not particularly limited, and examples thereof include a gravure direct method, a gravure reverse method, a bar coating method, and a rod coating method. As a method for curing the release agent layer, the thermosetting type may be cured at about 70 to 140 ° C., and the ultraviolet ray or electron beam curing type may be cured using a dedicated irradiation device. The solid content coating amount of the release agent layer is not particularly limited, but it is 0.05 to 2 g / m in view of curability of the release agent, cost, and the like. 2 It is preferable that
[0022]
As the ink for forming the printing layer of the present invention, a releasable radiation curable ink containing a releasable radiation curable polysiloxane is used. Incidentally, the adhesion to the release agent layer becomes poor in the oxidation polymerization type ink and the thermosetting ink.
[0023]
The functional group of the peelable radiation curable polysiloxane is mainly composed of those that contribute to the reaction by radiation, and further increases the reactivity or imparts affinity with other materials. Although it does not specifically limit, For example, a mercapto group, a vinyl group, a hexenyl group, an epoxy group, an acetoxy group, a methoxy group, an ethoxy group, a phenyl group, an amino group etc. are mentioned. Among these, a releasable radiation curable ink containing a releasable radiation curable polydimethylsiloxane having a vinyl group is preferable.
Examples of the radiation used in the present invention include ultraviolet rays, electron beams, α rays, β rays, γ rays, neutron rays, X rays, etc., but ultraviolet rays and electron beams excellent in operability are preferable and relatively compact. Ultraviolet light that can be used with inexpensive equipment is particularly preferred. The peelable radiation curable ink containing the peelable radiation curable polysiloxane is preferably a peelable ultraviolet curable ink. Furthermore, in order to facilitate the peelability between the pressure-sensitive adhesive layer and the printed layer, it is preferable to contain 5% by mass or more of a peelable radiation-curable polydimethylsiloxane.
[0024]
The contact angle (measured after 60 seconds with a drop amount of 5 μl in a 23 ° C. environment) of the surface of the release agent layer not printed on a solution having a mass ratio of water to ethanol of 1: 1 is 35 degrees or less. preferable. By adjusting the contact angle, it becomes possible to further enhance the adhesion of the peelable radiation curable ink to the surface of the release agent layer. Above all, the mass of water and ethanol on the surface of the release agent layer that has not been printed, in order to suppress the repellency of the release radiation curable ink and to provide a print layer that is uniform and has no printing unevenness. The contact angle with respect to a solution having a ratio of 1: 1 (measured after 60 seconds at a drop volume of 5 μl in a 23 ° C. environment) is preferably 0 to 25 degrees.
[0025]
By using a specific releasable radiation curable ink containing the releasable radiation curable polysiloxane, the affinity (hereinafter also referred to as ink fixability) to the surface of the release agent layer containing the curable polysiloxane is increased. A release sheet subjected to printing with good ink adhesion can be formed.
Furthermore, by using a specific releasable ultraviolet curable ink containing a releasable radiation curable polydimethylsiloxane, it is possible to easily print with simple and simple mechanical equipment, and between the release agent layer and the ink. Excellent adhesion. In addition, it is conceivable to print using thermosetting ink containing thermosetting polydimethylsiloxane, but when equipment for heat drying requires a long oven or when a film is used as the substrate In addition, there is a disadvantage that the base material shrinks, and the adhesiveness as the peelable radiation curable ink cannot be obtained.
[0026]
The peelable ultraviolet curable ink of the present invention comprises an acrylic acid resin, a photopolymerization initiator, a peelable radiation curable polysiloxane, and a colorant as main components. In addition, a polymerization inhibitor, a wax, a solvent, an active compound, other auxiliary agents, and the like may be appropriately added as long as the curability is not impaired.
[0027]
Examples of the release radiation curable polysiloxane include radical addition type silicones that are cured by reaction of mercapto groups and vinyl groups, hydrosilylation reaction type silicones, acrylic radical polymerization type silicones, and epoxy group-containing cationic polymerization type silicones. Etc. It is not limited to these.
[0028]
Examples of the acrylic resin include acrylic acid esters of polyhydric alcohols such as pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol hexaacrylate, epoxy acrylate, urethane acrylate, polyester acrylate, polyether acrylate, and acrylate alkyd. And monomers such as prepolymers such as melamine acrylate, hydroxybutyl acrylate, 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, and bisphenol A type epoxyphenyl acrylate. It is not limited to these.
[0029]
Examples of the photopolymerization initiator include anthraquinone, acetophenone, 2,2-diethoxyacetophenone, 2-hydroxy-2-methylpropiophenone, 2,2-dimethoxy-2-phenylacetophenone, p-dimethylacetophenone, p -Dimethylaminopropiphenone, benzophenone, 2-chlorobenzophenone, 4,4'-dichlorobenzophenone, 4,4'-bisdiethylaminobenzophenone, Michler's ketone, benzyl, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, methyl Examples include benzoylfomate, dibutylphenylphosphine, hydroxyalkylphenone, alkylaminophenone, and thioxanthone. These photopolymerization initiators may be used alone or in combination of two or more.
[0030]
The amount of the photopolymerization initiator used is preferably 0.01 to 10 parts by weight with respect to 100 parts by weight of the peelable radiation curable polysiloxane. When a curing means such as electron beam or γ ray is used, it is not always necessary to add a polymerization initiator.
[0031]
As the colorant, for example, organic or inorganic pigments and dyes, carbon, metal powder, and the like can be used as appropriate. Incidentally, examples of organic pigments include azo pigments, phthalocyanine pigments, triphenylmethane pigments, metal complex pigments, vat dye pigments, quinacridone pigments, and isoindolinone pigments. Examples of inorganic pigments include white pigments such as silica, titanium, alumina, zinc white, zirconia, calcium oxide and mica, manganese oxide / alumina, chromium oxide / lead oxide, iron oxide, cadmium sulfide / selenium sulfide. Red pigments such as cobalt oxide, blue pigments such as zirconia / vanadium oxide, chromium oxide / divanadium pentoxide, chromium oxide / cobalt oxide / iron oxide / manganese oxide, chromate, permanganate Black pigment, yellow pigment such as zirconium, silicon, praseodymium, vanadium, lead, chromium, titanium, antimony, green pigment such as chromium oxide, cobalt, chromium, alumina, chromium, aluminum, manganese, iron, silicon, zirconium Such a pink pigment is a typical example.
[0032]
The method for forming the printing layer on the surface of the release agent layer using the above-described peelable radiation curable ink is not particularly limited as long as it is a known printing method. For example, flexographic printing, letterpress printing, offset printing, gravure It can be formed by printing, screen printing, or the like, and irradiation with radiation.
[0033]
The printed layer is preferably printed so that the thickness after curing is 10 μm or less, preferably 5 μm or less. If the thickness of the printed layer is greater than 10 μm, it may be disadvantageous in terms of cost, such as when the cohesive force of the printed layer is reduced, a difference from the unprinted part occurs, or the cost of the ink and the amount of radiation are increased. This is not preferable. A more preferable thickness is 0.1 to 3 μm. When it is thinner than 0.1 μm, a portion that is not printed is formed due to the unevenness of the surface of the release agent layer.
[0034]
Further, the area of the printing layer relative to the release agent layer may be partial printing or full surface printing. Even if the print layer covers the entire release agent layer, there is no problem in the peelability between the print layer and the pressure-sensitive adhesive layer. Further, the release agent layer may be printed in stages so that the printed portions do not overlap or overlap.
[0035]
In the release agent layer of the present invention, the contact angle of the release agent layer surface with respect to a solution having a mass ratio of water to ethanol of 1: 1 (measured after 60 seconds in a drop amount of 5 μl in a 23 ° C. environment) is 45 ° or more. It is preferable. In particular, the contact angle of the release agent layer surface is more preferably 45 to 65 degrees in consideration of ink adhesion. Incidentally, when the contact angle of the release agent layer surface is lower than 45 degrees, the adhesion with the ink is improved, but the release property with the pressure-sensitive adhesive layer tends to be lowered (hereinafter also referred to as heavy release). On the other hand, when the contact angle is higher than 65 degrees, the peelability from the pressure-sensitive adhesive layer is improved (hereinafter also referred to as “light peeling”), but the adhesiveness to the ink tends to be lowered. Further, the contact angle of the printed layer surface with respect to a solution having a mass ratio of water and ethanol of 1: 1 (measured after 60 seconds at 23 ° C. in a dropping amount of 5 μl) is 45 degrees or more. It is preferable because of its excellent peelability.
[0036]
The contact angle between the surface of the release agent layer and the surface of the print layer depends on the amount of release radiation curable polysiloxane contained in the ink forming the print layer and the addition of materials with different surface energies used in the release agent layer. It is possible to adjust by. For example, when the contact angle is controlled by the release agent layer, the contact angle is increased by increasing the blending amount of the curable polysiloxane or by using a material having a low surface energy such as an ethylene-propylene terpolymer. Moreover, it is possible to reduce the contact angle of the release agent layer surface by reducing the amount of polysiloxane blended or using a material having a high surface energy such as a cellulose derivative.
On the other hand, when the contact angle is controlled by the peelable radiation curable ink, it can be adjusted by changing the blending amount of the peelable radiation curable polysiloxane contained in the ink forming the printing layer. For example, increasing the blending amount of the peelable radiation curable polysiloxane increases the contact angle. Further, when the blending amount of the peelable radiation curable polysiloxane is reduced, the contact angle is lowered.
[0037]
Since the release sheet thus obtained is printed on the release agent layer, it is not necessary to print before applying the release agent, and the release force can be partially adjusted by adjusting the printing ink. It can take various forms, such as release sheets and adhesive tapes that have completely changed the properties of the release agent layer, such as the peelability and ink adhesion, by producing release sheets with different sizes or printing on the entire surface. This is useful in that it is a release sheet.
[0038]
The release sheet on which the printing layer of the present invention is formed can be wound into a pressure-sensitive adhesive tape as it is after forming the pressure-sensitive adhesive layer on the back surface, and this form is preferred.
Examples of the pressure-sensitive adhesive used in the pressure-sensitive adhesive tape include acrylic pressure-sensitive adhesives, natural rubber-based pressure-sensitive adhesives, synthetic rubber-based pressure-sensitive adhesives, and urethane-based pressure-sensitive adhesives. It is easy to adjust the mechanical adhesive force and the peel strength, and an acrylic pressure-sensitive adhesive having excellent weather resistance is preferable. Although it does not specifically limit as said acrylic adhesive, For example, ethyl acrylate (EA), butyl acrylate (BA), 2-ethylhexyl acrylate (2-EHA) as a main monomer, and vinyl acetate (VAc) as a comonomer , Acrylonitrile (AN), styrene (St), methyl methacrylate (MMA), acrylic acid (AA), itaconic acid (IA), hydroxyethyl methacrylate (HEMA), hydroxypropyl methacrylate (HPMA), dimethylaminoethyl methacrylate (DM) , Acryl amide (AM), methylol acryl amide (N-MAN), glycidyl methacrylate (GMA), maleic anhydride and the like as main components (preferably 80% by mass or more). In addition, when the release agent layer contains an elastomer, if a natural rubber-based adhesive, a synthetic rubber-based adhesive, or the like is used as the pressure-sensitive adhesive, the peeling force may be extremely increased. The reason is presumably because the release agent layer is a blend composition containing a thermoplastic elastomer and has properties close to the elastomer component of a natural rubber-based adhesive or a synthetic rubber-based adhesive, and the SP value is close. The Therefore, when a rubber-based adhesive is used, it is preferable to select one having a large difference between the release agent layer component and the SP value. A preferred SP value difference is 1.0 or more. Moreover, various additives, such as a tackifier, a ultraviolet absorber, a crosslinking agent, a softening agent, a pigment, and an anti-aging agent, can be appropriately blended in the pressure-sensitive adhesive. The pressure-sensitive adhesive used in the pressure-sensitive adhesive tape of the present invention can be adjusted according to a conventional method using the above raw materials.
[0039]
The amount of adhesive applied varies depending on the type of adhesive, the application of the adhesive tape, etc., but is 10 to 70 g / m. 2 It is. Above all, 20-50 g / m 2 Is more preferable. Application amount is 10g / m 2 If the amount is less than 70 g / m, sealing performance of cardboard or the like may be deteriorated. 2 Exceeding may cause sticking of the adhesive from the end face of the tape or workability.
[0040]
The application method of the adhesive is not particularly limited, but for example, it is applied to the comma coating method, reverse coating method, gravure coating method, reverse gravure method, kiss coating method, knife coating method, bar coating method and process paper by these methods. The transfer method etc. which transfer what was done are mentioned.
[0041]
When the adhesive force between the release agent layer surface of the release sheet of the present invention and the printed layer is α, and the adhesive force β between the printed layer and the pressure-sensitive adhesive layer is satisfied, the relationship of adhesive force α> adhesive force β is satisfied. This is an important quality requirement because the ink in which the printing layer is formed on the release agent layer can be printed without adhering to the adhesive layer side and the adhesive layer has releasability. For that purpose, it is necessary to form the above-mentioned specific release agent layer and specific print layer.
[0042]
Although the method of printing the thing of the structure which provided the adhesive layer of this invention is not specifically limited, For example, in the roll which has an adhesive tape paper feed part and a winding-up part, and the adhesive layer surface of an adhesive tape contacts Printing (for example, flexographic printing, letterpress printing, offset printing, gravure printing, screen printing, transfer printing, etc.) by a printing machine equipped with a roll having extremely high releasability from an adhesive such as a silicone roll and a Teflon roll, It is preferable to perform printing by a printing machine equipped with a radiation irradiation device such as an ultraviolet irradiation machine after printing.
[0043]
Furthermore, it demonstrates about a specific use.
(1) After printing on a release sheet or pressure-sensitive adhesive tape having a release agent layer formed on the heat-sensitive recording layer in a heat-sensitive manner, on the entire surface or a part of the release sheet layer of the release sheet or pressure-sensitive adhesive tape subjected to thermal printing. Printing can be performed with a peelable radiation curable ink.
{Circle around (2)} After printing on the entire surface or a part of the release agent layer of the release sheet or pressure-sensitive adhesive tape with the peelable radiation curable ink, printing can be carried out by a thermal method.
(3) After printing on a release sheet or adhesive tape containing an elastomer component in the release agent layer by a thermal transfer method using a commercially available thermal transfer ribbon, the entire surface or one side of the release sheet or adhesive tape subjected to thermal transfer printing The part can be printed with a peelable radiation curable ink.
(4) After printing on the entire surface or part of the release sheet or pressure-sensitive adhesive tape with a peelable radiation curable ink, printing can be performed by a thermal transfer method using a commercially available thermal transfer ribbon.
These can perform fixed information by printing and individual information by printer printing.
In addition, the entire surface or part of the release agent layer of the release sheet or pressure-sensitive adhesive tape was printed with a release radiation curable ink, and then contained a release radiation curable ink containing a release radiation curable polysiloxane. Printing can also be performed by a thermal transfer method using an ink ribbon. In this case, the quality excellent in the fixing property of the thermal transfer ink between the release agent layer and the printing layer and the release property from the adhesive can be obtained.
[0044]
For example, it can be configured as shown in FIGS. 1, 2, and 3 and can be used for various purposes depending on the configuration. For example, by using the configuration shown in FIGS. 2 and 3, a release sheet on which concealed printing such as wrinkles is applied, or an adhesive tape as shown in FIG. It can also be set as the product which gave barcode printing to the part other than the pattern printing part of the adhesive tape which carried out the pattern printing on the printing part / non-printing part of the code-printed surface, or the printed part.
[0045]
【Example】
EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited thereto. In the examples and comparative examples, “parts” and “%” indicate “parts by mass” and “% by mass” of the solid content or active ingredient unless otherwise specified.
[0046]
Example 1
(Preparation of release sheet)
64g / m as substrate 2 50 parts of SBR (trade name: L-1571, manufactured by Asahi Kasei Co., Ltd.) and kaolin (trade name: HT clay, manufactured by Engelhard) 50 on one side of high-quality paper (trade name: OK fine paper, manufactured by Oji Paper Co., Ltd.) Part of the antifoaming agent (trade name: Nopco 1407K, manufactured by San Nopco) and 0.9 part of a lubricant (trade name: Nopcoat C104, manufactured by San Nopco) with a coating amount of 7 g / m. 2 A base material (A) provided with a sealing layer was prepared.
Next, Mooney viscosity (ML 1 + 4 , At 100 ° C.) 85, an ethylene content of 62% by weight, an ethylene-propylene terpolymer having a specific gravity of 0.86 (trade name: EP75F, manufactured by JSR) and 90 parts of an addition reaction type polydimethylsiloxane (trade name) : LTC300B, manufactured by Toray Dow Corning Co., Ltd.) is dissolved in a toluene solution, and a platinum catalyst (trade name: SRX212, manufactured by Toray Dow Corning Co., Ltd.) is dissolved in the polydimethylsiloxane (trade name: LTC300B, manufactured by Toray Dow Corning Co., Ltd.). ) 1.5 parts by weight with respect to 100 parts, and a well-stirred mixed solution was prepared.
The mixed solution was added to the surface of the base material (A) provided with a sealing layer using a Mayer bar and the solid content was 1.5 g / m. 2 The release agent layer was provided by drying (oven temperature 130 ° C., drying time 30 seconds). A release UV curable ink having the following composition was applied onto the release agent layer using an Onda Seisakusho seal printer. After that, the amount of light 20mW / cm 2 Were subjected to UV irradiation, letterpress UV printing was performed, and a printed release sheet was prepared. In addition, the thermal transfer printing suitability of the obtained release sheet and the writing property with oil-based ink were also good.
[0047]
"Releasable UV curable ink"
18 parts of colorant (trade name: Oil Red, manufactured by Pure Chemical Co., Ltd.)
38 parts of bisphenol A type epoxyphenyl acrylate
1,6-hexanediol acrylate 5 parts
20 parts of trimethylolpropane triacrylate
2-hydroxy-2-methylpropiophenone (photopolymerization initiator) 5 parts
2,2-dimethoxy-2-phenylacetophenone (photopolymerization initiator) 3 parts
Peelable UV curable polydimethylsiloxane 8 parts
(Product name: BY24-551A, manufactured by Toray Dow Corning Silicone)
Peelable UV curable polydimethylsiloxane 2 parts
(Product name: BY24-551B, manufactured by Toray Dow Corning Silicone)
Silane coupling agent 0.2 parts
(Product name: BY24-848, manufactured by Toray Dow Corning Silicone)
IPA 0.8 part
[0048]
Example 2
Addition reaction type silicone release agent (trade name: BY24-312, manufactured by Toray Dow Corning Co., Ltd., solid content concentration 30%) as a release agent, 60 parts ethyl cellulose (powder reagent manufactured by Tokyo Chemical Industry Co., Ltd.) 40 parts Except that the added mixture was dissolved in toluene, and a mixed solution containing 2 parts of a platinum-based curing catalyst (trade name: SRX-212, manufactured by Toray Dow Corning Co., Ltd.) was prepared and used as a release agent coating solution. A release sheet printed in the same manner as in Example 1 was obtained. In addition, the thermal transfer printing suitability of the obtained release sheet and the writing property with oil-based ink were also good.
[0049]
Example 3
A release sheet printed in the same manner as in Example 1 was obtained except that the peelable radiation curable ink was replaced with one having the following composition. In addition, the thermal transfer printing suitability of the obtained release sheet and the writing property with oil-based ink were also good.
[0050]
"Releasable UV curable ink"
25 parts of colorant (trade name: Oil Red, manufactured by Junsei Kagaku)
Bisphenol A type epoxy phenyl acrylate 20 parts
1,6-hexanediol acrylate 2 parts
10 parts of trimethylolpropane triacrylate
2-hydroxy-2-methylpropiophenone (photopolymerization initiator) 3 parts
1,2-dimethoxy-2-phenylacetophenone (photopolymerization initiator) 1 part
Releaseable UV-curable polydimethylsiloxane 28 parts
(Product name: BY24-551A, manufactured by Toray Dow Corning Silicone)
Peelable UV curable polydimethylsiloxane 9 parts
(Product name: BY24-551B, manufactured by Toray Dow Corning Silicone)
Silane coupling agent 1.2 parts
(Product name: BY24-848, manufactured by Toray Dow Corning Silicone)
IPA 0.8 part
[0051]
Example 4
A release sheet printed in the same manner as in Example 1 was obtained except that the peelable radiation curable ink was replaced with one having the following composition. In addition, the thermal transfer printing suitability of the obtained release sheet and the writing property with oil-based ink were also good.
"Releasable UV curable ink"
17 parts of colorant (trade name: Oil Red, manufactured by Junsei Kagaku)
60 parts of peelable UV curable polydimethylsiloxane
(Product name: BY24-551A, manufactured by Toray Dow Corning Silicone)
18 parts of peelable UV curable polydimethylsiloxane
(Product name: BY24-551B, manufactured by Toray Dow Corning Silicone)
Silane coupling agent 5 parts
(Product name: BY24-848, manufactured by Toray Dow Corning Silicone)
[0052]
Comparative Example 1
A base chain (A) provided with a sealing layer described in Example 1 was dissolved in toluene with a long-chain alkyl pendant polymer (trade name: Pyroyl 1010, manufactured by Yushi Kogyo Co., Ltd.) as a release agent. 0.1 g / m of solid content on the sealing layer surface of the substrate 2 After being coated and dried (drying temperature 100 ° C., drying time 30 seconds), printing was performed with an ink and a printing machine under the same conditions as in Example 1 to obtain a printed release sheet. In addition, the thermal transfer printing suitability of the obtained release sheet and the writing property with oil-based ink were not obtained.
[0053]
Comparative Example 2
A release sheet was prepared in the same manner as in Example 1 except that a commercially available UV ink (trade name: Flexo AF Indigo, manufactured by T & K TOKA) was used as the peelable radiation curable ink. The peeling sheet with respect to the surface was generated, and a release sheet on which printing was performed could not be obtained.
[0054]
The release sheets obtained in the above Examples and Comparative Examples were evaluated by the following methods, respectively, and the results are shown in Table 1.
[0055]
<Repelling printing ink>
When UV printing was performed using an Onda Seisakusho printing press, the repellency of the printing ink on the release surface of the release sheet was evaluated according to the following criteria.
◯: There is no ink repellency on the release agent layer surface, and a beautiful printed surface is formed.
Δ: There is a slight repellency of the ink on the surface of the release agent layer, but an almost beautiful printed surface is formed.
X: Ink repelling occurs on the surface of the release agent layer, and the intended printing surface is not formed.
[0056]
<Adhesion of printing ink>
The printed surface of the release sheet that had been printed was rubbed with the finger pad and evaluated according to the following criteria.
○: There is no ink fading, ink smear, or ink drop even when rubbed strongly.
Δ: When rubbed strongly, slight ink fading or ink smearing occurs, but there is no ink drop.
X: When rubbed strongly, the ink appears to be discriminated as ink fading, ink smearing, or ink dropping.
[0057]
<Abrasion resistance of printing ink>
Using a dyeing fastness tester (manufactured by Suga Test Instruments Co., Ltd., FR-2), an eraser was applied to the printed surface of the release sheet that had been printed, and the portion recorded when reciprocating at a maximum of 100 times at 500 gf (constant) The number of times until changes such as ink fading, ink smearing, and ink dropping appeared was recorded and evaluated according to the following criteria.
(Visual evaluation)
A: No ink fading, ink smear, or ink drop even after 50 reciprocations.
○: No ink fading, ink smear, or ink drop even after 40 or more reciprocations.
Δ: No ink fading, ink smear, or ink drop even after 30 or more (less than 40) reciprocations (practical use limit).
X: In less than 30 times, ink fading, ink smearing, or ink dropping occurs.
[0058]
<Contact angle of release agent layer and print layer>
In a 23 ° C. environment, 5 μl of a solution having a mass ratio of water and ethanol of 1: 1 is dropped onto the release agent layer surface or the print layer surface using a microsyringe, and the contact angle after 60 seconds is measured according to JIS K 3211. did.
[0059]
[Table 1]
Figure 0004710173
[0060]
Example 5
On the surface opposite to the release agent layer surface of the release sheet of Example 1, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) was applied in a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced. In addition, the thermal transfer printing suitability of the obtained adhesive tape and the writing property with oil-based ink were also good. Further, the surface of the printing layer was good without being peeled off by the adhesive.
[0061]
Example 6
On the surface opposite to the release agent layer surface of the release sheet of Example 2, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) was applied in a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced. In addition, the thermal transfer printing suitability of the obtained adhesive tape and the writing property with oil-based ink were also good. Further, the surface of the printing layer was good without being peeled off by the adhesive.
[0062]
Example 7
On the surface opposite to the release agent layer surface of the release sheet of Example 3, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) was applied in a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced. In addition, the thermal transfer printing suitability of the obtained adhesive tape and the writing property with oil-based ink were also good. Further, the surface of the printing layer was good without being peeled off by the adhesive.
[0063]
Example 8
On the surface opposite to the release agent layer surface of the release sheet of Example 4, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) was applied at a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced. In addition, the thermal transfer printing suitability of the obtained adhesive tape and the writing property with oil-based ink were also good. Further, the surface of the printing layer was good without being peeled off by the adhesive.
[0064]
Comparative Example 3
On the surface opposite to the release agent layer surface of the release sheet of Comparative Example 1, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) was applied at a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced. In addition, the heat transfer printing suitability of the obtained adhesive tape and the writing property with oil-based ink were not obtained.
[0065]
Comparative Example 4
On the surface opposite to the release agent layer surface of the release sheet of Comparative Example 2, an acrylic pressure-sensitive adhesive (trade name: L-145K, manufactured by Nippon Carbide) is applied in a solid content of 30 g / m. 2 After being applied and dried, an adhesive tape that was wound up and printed on the surface of the release agent layer was produced.
[0066]
<Peelability between adhesive layer and release agent layer>
The peelability between the release agent layer and the pressure-sensitive adhesive layer of the release sheet was determined by unwinding the pressure-sensitive adhesive tape prepared in Examples 5 to 8 in an environment of 23 ° C. and 50% RH, and the release agent layer surface of the release sheet subjected to the above printing. After sticking on the upper printing surface so that the pressure-sensitive adhesive layer is stuck, it was reciprocated once with a 2 Kg pressure-bonding roll, and then the pressure-sensitive adhesive sheet was peeled off at 300 mm / min with a tensile tester according to JIS Z 0237. The peel force (N / m) when peeled at 180 ° was measured.
[0067]
About the adhesive tape obtained in the said Example, it evaluated by said method and the result was shown in Table 2.
[0068]
[Table 2]
Figure 0004710173
[0069]
As is clear from Table 1, the release sheets subjected to printing as in Examples 1 to 4 are excellent in the peelability of the pressure-sensitive adhesive and the release agent layer in both the printed part and the non-printed part, and record information and intentions. The obtained release sheet could be obtained. Further, as apparent from Table 2, Examples 5 to 8 had no problem in the peelability between the printed layer and the pressure-sensitive adhesive layer, and could provide a printed pressure-sensitive adhesive tape.
[0070]
The release sheet of Comparative Example 1 in Table 1 is not suitable for practical use because the peel strength of the pressure-sensitive adhesive is high and the ink adhesion of the printed part is poor. In Comparative Example 2, since the ink repellency occurred, it was not possible to obtain a printed release sheet.
[0071]
【The invention's effect】
The release agent layer of the present invention contains a curable polysiloxane, and the print layer is made of a release radiation curable ink containing a release radiation curable polysiloxane, thereby providing excellent adhesion between the release agent layer and the ink. A release sheet printed was obtained. Of the releasable radiation curable polysiloxane, the releasable radiation curable polydimethylsiloxane is excellent in releasability between the ink and the pressure-sensitive adhesive layer. Furthermore, among the detachable radiation curable inks, a detachable ultraviolet curable ink that does not cause deterioration in workability and deterioration of the substrate is preferable, and the release sheet layer surface of the release sheet and the non-printing part and the adhesive. It has become possible to provide a release sheet with excellent peelability and information and intent.
In addition, it is possible to make a crease by adjusting the peeling force of the printing part and peeling the adhesive sheet partially on the printing surface of the peeling sheet that has changed the peeling force or the printed sheet. It is.
Furthermore, since it can be easily printed on the release agent layer surface of the release sheet, it is possible to provide an inexpensive adhesive tape with a logo mark from a sales company or the like.
Also, before or after printing with a release radiation curable ink on a release sheet or adhesive tape on which a heat-sensitive recording layer is formed, printing is performed by a thermal method, or a release sheet or adhesive tape containing an elastomer. Before or after printing with a releasable radiation curable ink, printing is performed by a thermal transfer method using a commercially available thermal transfer ribbon, so that a practically suitable aspect is obtained.
[Brief description of the drawings]
FIG. 1 is a schematic view showing a cross section of a release sheet on which printing of the present invention has been performed.
FIG. 2 is a diagram illustrating an example of use of a release sheet that has been printed according to the present invention.
FIG. 3 is a schematic view showing a plane of a release sheet on which printing of the present invention has been performed.
FIG. 4 is a schematic view showing a perspective view of an application example in which an adhesive is provided on the other side of the release sheet of the release sheet subjected to printing of the present invention to provide an adhesive tape.
FIG. 5 is a schematic view showing a cross section of a release sheet subjected to conventional printing.
[Explanation of symbols]
a: Base material (for release sheet or adhesive tape)
b: Release agent layer
c: Printing section
d: Printed release sheet
e: Adhesive layer
f: Surface base material
g: Adhesive sheet
h: Adhesive label
i: Printed adhesive tape

Claims (14)

基材の少なくとも一面に剥離剤層を有し、該剥離剤層表面上の少なくとも一部分に印刷層を有する剥離シートであって、前記剥離剤層が、硬化性ポリシロキサン含有剥離剤を硬化して形成され、且つ前記印刷層を形成するインキが、剥離性放射線硬化型ポリシロキサンを含有する剥離性放射線硬化型インキであることを特徴とする剥離シート。  A release sheet having a release agent layer on at least one surface of a substrate, and having a printing layer on at least a part of the surface of the release agent layer, wherein the release agent layer cures the curable polysiloxane-containing release agent. A release sheet, wherein the ink that is formed and forms the print layer is a peelable radiation curable ink containing a peelable radiation curable polysiloxane. 前記剥離性放射線硬化型ポリシロキサンが、剥離性放射線硬化型ポリジメチルシロキサンである請求項1記載の剥離シート。  The release sheet according to claim 1, wherein the peelable radiation curable polysiloxane is a peelable radiation curable polydimethylsiloxane. 前記剥離性放射線硬化型インキが、剥離性放射線硬化型ポリシロキサンを少なくとも5質量%含有する請求項1又は2記載の剥離シート。  The release sheet according to claim 1 or 2, wherein the peelable radiation curable ink contains at least 5% by mass of a peelable radiation curable polysiloxane. 前記剥離性放射線硬化型インキが、剥離性紫外線硬化型インキである請求項1〜3記載の剥離シート。  The release sheet according to claim 1, wherein the peelable radiation curable ink is a peelable ultraviolet curable ink. 前記硬化性ポリシロキサンが、硬化性ポリメチルシロキサンである請求項1〜4記載の剥離シート。  The release sheet according to claim 1, wherein the curable polysiloxane is a curable polymethylsiloxane. 前記剥離剤層中に、エラストマーおよび/又はセルロース誘導体をさらに含有する請求項1〜5記載の剥離シート。  The release sheet according to claim 1, further comprising an elastomer and / or a cellulose derivative in the release agent layer. 前記剥離剤層中に、前記エラストマーを少なくとも50質量%含有し、且つ剥離剤層が、溶融熱転写記録適性を有する請求項6記載の剥離シート。  The release sheet according to claim 6, wherein the release agent layer contains at least 50% by mass of the elastomer, and the release agent layer has melt heat transfer recording suitability. 前記剥離剤層が、エラストマー80〜98質量%および硬化性ポリジメチルシロキサン2〜20質量%を含有する請求項6又は7記載の剥離シート。  The release sheet according to claim 6 or 7, wherein the release agent layer contains 80 to 98% by mass of an elastomer and 2 to 20% by mass of a curable polydimethylsiloxane. 前記剥離剤層中に、セルロース誘導体を少なくとも10質量%含有する請求項6記載の剥離シート。  The release sheet according to claim 6, wherein the release agent layer contains at least 10% by mass of a cellulose derivative. 前記剥離剤層が、セルロース誘導体10〜50質量%および硬化性ポリジメチルシロキサン50〜90質量%を含む請求項6又は9記載の剥離シート。  The release sheet according to claim 6 or 9, wherein the release agent layer contains 10 to 50% by mass of a cellulose derivative and 50 to 90% by mass of curable polydimethylsiloxane. 前記剥離剤層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)が45〜65度であり、且つ印刷層表面の、水とエタノールの質量比が1:1である溶液に対する接触角(23℃環境下、滴下量5μlで60秒後に測定)が45度以上である請求項1〜10記載の剥離シート。  The contact angle of the release agent layer surface with respect to a solution having a mass ratio of water and ethanol of 1: 1 (measured after 60 seconds at 23 ° C. in a dropping amount of 5 μl) is 45 to 65 degrees, and the surface of the printing layer The release sheet according to claim 1, wherein a contact angle (measured after 60 seconds at a drop amount of 5 μl in a 23 ° C. environment) is 45 degrees or more with respect to a solution having a mass ratio of water to ethanol of 1: 1. 請求項1〜11のいずれかに記載され、一面に剥離剤層を有する剥離シートを用い、その剥離剤層を設けた面とは反対面にアクリル系粘着剤層を設けて巻き取り状にしたことを特徴とする粘着テープ。  A release sheet according to any one of claims 1 to 11, wherein a release sheet having a release agent layer on one surface is used, and an acrylic pressure-sensitive adhesive layer is provided on the surface opposite to the surface on which the release agent layer is provided to form a wound shape. An adhesive tape characterized by that. 前記剥離シートの、剥離剤層と前記印刷層との接着力をα、前記印刷層と前記粘着剤層との接着力βとした場合に、接着力α>接着力βの関係にある請求項12に記載の粘着テープ。  The adhesive force α> adhesive force β when the adhesive force between the release agent layer and the print layer of the release sheet is α and the adhesive force β between the print layer and the pressure-sensitive adhesive layer. 12. The adhesive tape according to 12. 請求項12又は13に記載の粘着テープを、被着体に貼着したことを特徴とするテープ貼着物。  A tape adhesive product, wherein the adhesive tape according to claim 12 or 13 is adhered to an adherend.
JP2001176117A 2001-06-11 2001-06-11 Release sheet, adhesive tape and tape adhesive Expired - Lifetime JP4710173B2 (en)