JP4582386B2 - Laser marking material - Google Patents

Description

  The present invention relates to an inorganic material for marking by laser irradiation, and more particularly to a molybdenum-containing composite oxide that changes color to a black color tone by laser irradiation.

  Conventionally, marking of characters on electric / electronic parts, etc. has been carried out by applying ink in an arbitrary shape to the electronic parts main body by a method such as imprinting, transferring or printing, and then fixing by heating or ultraviolet irradiation. It was. However, the marking method using ink or the like may disappear due to friction or the like, and marking with fine characters or curved surfaces is difficult, and maintenance for maintaining the ink performance is troublesome. Therefore, a printing method that does not use ink is being adopted, and one of them is a printing method that uses a laser marker. The laser marker performs printing by irradiating a laser beam, and the printing mechanism includes a method of scattering the surface of the irradiated object and a method of printing using a chemical change on the surface of the irradiated object.

Several techniques have already been known for marking the surface of a resin composition molded article containing a filler that can be discolored by laser irradiation. For example, a composition (Patent Document 1) containing a copper hydroxide monophosphate, molybdenum oxide or titanium dioxide in a thermoplastic resin, copper phosphate, copper sulfate, basic cupric phosphate and A composition containing at least one selected from the group consisting of copper thiocyanate (Patent Document 2), a composition containing ABS resin containing at least two metal oxides (Patent Document 3), a molybdenum compound and a base Composition containing a porous filler (Patent Document 4), a composition containing an inorganic acid copper hydrate in an epoxy resin (Patent Document 5), and a composition containing a carbon black in a thermoplastic resin (Patent Document 5) 6) Laser marking using a composition containing iron oxide (Patent Document 7) is disclosed. However, with these conventional resin compositions, the blackness and quality of the marked characters and designs are not sufficient. For example, 1) the blackness of printing does not reach a satisfactory level, 2) the amount of filler in the resin is large, 3) the color of the filler is strong and the resin itself is colored, 4) foaming or filling of the resin Since the decomposition of the resin is utilized, there is a problem that the resin is damaged and fine printing cannot be performed.
JP-A-3-124161 JP-A-8-187951 Japanese Patent Laid-Open No. 9-20855 JP 11-29711 A JP-A-5-229256 JP-A-5-92657 JP-A-60-155493

  In marking by laser irradiation, a material that changes color to a color with high blackness is desired in terms of the visibility of the formed mark. It is an object of the present invention to provide a marking material that develops or changes color by laser irradiation and has a markedly high blackness of marked characters and designs.

  The marking material according to the present invention is a molybdenum-containing composite oxide represented by the following general formula (I). This composite oxide changes its color to a color with high blackness when irradiated with a laser.

MxMoyOz ……… (I)
Wherein, M is vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), cobalt (Co), Lee Ttoriumu (Y), zirconium (Zr), niobium (Nb), tin (Sn) And at least one selected from the group consisting of tungsten (W), x = 1, 1 ≦ y ≦ 9, when M is a divalent metal, 4 ≦ z ≦ 28, and when M is a trivalent metal, 4.5 ≤ z ≤ 28.5, when M is a tetravalent metal, 5 ≤ z ≤ 29, when M is a pentavalent metal, 5.5 ≤ z ≤ 29.5, when M is a hexavalent metal, 6 ≤ z ≤ 30 is there.

The laser marking material comprising the molybdenum-containing composite oxide according to the present invention is useful as a component constituting a resin composition that can be marked by laser irradiation.

The material for laser marking comprising the molybdenum-containing composite oxide according to the present invention can be any raw material such as metal carbonate, oxide, nitrate, phosphate, hydroxide, chloride, carboxylate (oxalate, etc.) ) Or the like. At the time of synthesis, a sintering inhibitor, a synthesis auxiliary agent or the like may be added.

  The synthesis method may be any of a solid phase method, a liquid phase method, and a gas phase method.

The laser marking material comprising a molybdenum-containing composite oxide according to the present invention is usually used in the form of fine particles having a particle size of 0.1 to 10 μm, preferably 0.5 to 5 μm.

  The synthetic resin for compounding the composite oxide is not particularly limited. For example, acrylic resin, polyacetal resin, polyamide resin, polyimide resin, polyester resin, polyvinyl chloride resin, polyolefin resin, polycarbonate resin, polystyrene resin, polysulfone resin. And thermosetting resins such as urethane resins, epoxy resins, diallyl phthalate resins, silicon resins, phenol resins, unsaturated polyester resins, melamine resins, urea resins, and copolymers thereof.

  In order to disperse the composite oxide in the resin, for example, an extruder, a roll mill, a mixer or a pulverizer is used by a known method. At this time, a surface treatment may be applied to improve the dispersibility of the composite oxide.

  The ratio of the molybdenum-containing composite oxide in the resin is 0.001 to 20% by weight, preferably 0.01 to 2% by weight. In dispersing the composite oxide in the resin, a dispersant, a surface treatment agent, a sensitizer for improving laser characteristics, and the like may be added. Moreover, according to each use, you may add the stabilizer, antioxidant, a flame retardant, glass fiber, and the additive currently used widely for plastic processing in resin.

When marking is performed by laser irradiation using a resin composition containing a molybdenum-containing composite oxide, the laser may be, for example, a YAG laser, a YVO ₄ laser, or a carbon dioxide gas laser, and the wavelength may be 532 to 10600 nm.

  ADVANTAGE OF THE INVENTION According to this invention, the complex oxide for laser markings which is excellent in the color-changing ability by laser irradiation, and has markedly high blackness of the marked character and design can be provided.

  Next, in order to describe the present invention specifically, some examples of the present invention and comparative examples for showing comparison with the examples will be given.

Synthesis Example of Molybdenum-Containing Composite Oxide First, a powder was prepared according to the following operation.

1. The required amounts of the two raw materials shown in Table 1 were taken so as to correspond to the compositions shown in Table 1, and these were dry-mixed with a small pulverizer (SK-M type, manufactured by Kyoritsu Riko Co., Ltd.).

2. 15 g of the mixed powder was taken in a collie and fired in an electric furnace (Advantech Toyo Co., Ltd., KS-1503) under the conditions shown in Table 1.

3. The fired powder was crushed with a mortar.

Powder evaluation The crushed powder was heaped in steel container (diameter 35 mm, depth 10 mm).

2. The whole container was pressed for 15 tf for 10 seconds with a press machine (TYPE M, manufactured by Maekawa Test Equipment Co., Ltd.) to produce a molded body.

3. The molded body was measured for color by a colorimeter (manufactured by Daiichi Seika Co., Ltd., COLORCOM C).

4). The molded body was irradiated with a YAG laser (manufactured by NEC Corporation, SL475K) to change the color of the molded body. Laser irradiation conditions were an input current of 11 A, a feed rate of 400 mm / second, and a Q-sw frequency of 7 kHz.

5. The discolored portion was measured with a colorimeter. The measurement results are shown in Table 1.

PET resin evaluation 3. in the polyethylene bag. 0.10 g of this powder was applied to 400 g of PET (Nihon Unipet, RT523C) particles.

2. The powder-coated PET was transferred to an aluminum container and dried at 140 ° C. for 4 hours with a forced circulation electric dryer (SPH-10, manufactured by Espec Corp.).

3. The dried sample was molded into a plate shape by an injection molding machine (manufactured by Nippon Steel Works, JSW, J50SAII).

4). The color of the PET molded body was measured with a colorimeter. The measurement results are shown in Table 1.

5. After the PET molded body was irradiated with a YAG laser, the irradiated portion was measured with a colorimeter.

  Table 1 shows the starting materials, blending composition, firing temperature, firing time, powder color after firing, powder printing ability, in-resin discoloration ability, resin coloring ability and foamability.

  Table 2 shows the measurement results of known copper marker additive copper carbonate and molybdenum compounds that are not complex oxides.

Powder printing ability: Printing performance when the powder itself is irradiated with laser x Printing is impossible, △ Printing is faint, ○ Printing is good, ◎ Clear printing Printing in resin: Printing when irradiated with a PET resin molding Performance x Not printable, △ print fading, ○ printing good, ◎ clear printing Resin coloring: coloring degree of resin when kneaded with PET resin × very dark coloring, △ dark coloring, ○ light coloring, ◎ almost coloring No Foaming property: surface of printed characters x foamed large, △ foamed large, ○ foamed small, ◎ no foamed Overall evaluation: The above evaluations were summed as x0 points, △ 1, ◯ 3 points, and ◎ 5 points. Overall evaluation is made with the total points obtained. × 1-5 points, Δ6-10 points, ○ 11-15 points, ◎ 16-20 points

Each product in Table 1 is represented by MxMoyOz as a molybdenum-containing composite oxide. When M is V, Cr, Mn, Fe, Co, Y , Zr, Nb, Sn, or W, the color of the powder after firing was light and the discoloration ability in the laser was excellent. In addition, when these composite oxides were dispersed in a resin, the ability to change color was excellent, and it was also superior to the known laser marker additive copper carbonate shown in Table 2. In addition, when copper carbonate is dispersed in the resin, this absorbs heat when the resin is melted, and discoloration of the resin itself increases, but in the case of these composite oxides, coloration to the resin is suppressed. . Moreover, foaming during laser irradiation was also suppressed.

  Regarding the use of the molybdenum-containing compound as an additive for a laser marker, there is a description in the above-mentioned Patent Document 4, but as shown in Table 2, these have insufficient discoloration ability, and when they are dispersed in a resin, the color becomes large, It is not good as overall evaluation.

Claims (1)

A laser marking material comprising a molybdenum-containing composite oxide represented by the following general formula (I).
MxMoyOz ……… (I)
Wherein, M is vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), cobalt (Co), Lee Ttoriumu (Y), zirconium (Zr), niobium (Nb), tin (Sn) And at least one selected from the group consisting of tungsten (W), x = 1, 1 ≦ y ≦ 9, when M is a divalent metal, 4 ≦ z ≦ 28, and when M is a trivalent metal, 4.5 ≤ z ≤ 28.5, when M is a tetravalent metal, 5 ≤ z ≤ 29, when M is a pentavalent metal, 5.5 ≤ z ≤ 29.5, when M is a hexavalent metal, 6 ≤ z ≤ 30 is there.