JP4538825B1 - A chemical injection material and a chemical injection method using a water-absorbent resin whose surface is covered with a hydrophilic polymer compound as a coating material. - Google Patents

Abstract

A conventional chemical solution injection material has produced a hydrous gel of a chemical solution in the ground, and has filled the soil particle gap with the hydrous gel to increase the ground strength, reduce the hydraulic conductivity, and improve the ground. However, the water-containing gel of the conventional chemical solution lacks long-term stability in the ground, and has a serious defect that the ground improvement effect is reduced or lost in several months.
The A surface water-absorbent resin covered with a hydrophilic polymer was poured into in the injection chemical is dispersed in water in the ground as a coating material, a water-containing gel of the water-absorbent resin in the ground It is possible to form, exhibit water absorption performance, and demonstrate the ground improvement effect. The coating material exhibits the effect of temporarily preventing contact between the water-absorbent resin and water until the completion of the pouring operation. After the pouring is completed, the coating material is dissolved or discretely lost with water or the like used as a dispersion, The water absorbent resin and water can be brought into contact with each other, and the water absorbent performance of the water absorbent resin can be exhibited.

Description

INDUSTRIAL APPLICABILITY The present invention is suitable for the ground improvement field used for improving the ground strength or reducing the water permeability of the ground, in a state where a water- absorbing resin covered with a hydrophilic polymer compound with a surface as a coating material is dispersed in water. The present invention relates to a chemical solution injection material and a chemical solution injection method for injection into the ground as a dispersion .

In the conventional general chemical injection material and chemical injection method , various chemical injection materials are selected and used depending on the properties of the target ground. For example, hardening of aqueous solution using aqueous solution diluted with water glass, inorganic acid such as phosphoric acid or sulfuric acid, bicarbonate such as sodium bicarbonate, or water suspension such as cement or slag Using a Y-shaped tube or the like, the chemical solution is injected into the ground at the same time while combining the two chemical solutions, reacted with both chemical solutions, cured in units of seconds to several minutes, and water glass hydrogel in the ground. It has been produced to improve the ground strength and reduce the ground permeability, thereby exerting the ground improvement effect.

  However, the water glass hydrogel lacks long-term stability in the ground, and has a serious defect that the ground improvement effect is reduced or lost in several months, especially in the ground with stagnant or underground water. .

Moreover, once water was washed out from the water glass hydrogel, even if it encountered water again, it was not possible to take in the water and generate the water glass hydrogel having the same volume again. Therefore, the chemical injection method using water glass as the main agent is called “temporary construction method”, and it is considered that there is no sustainability, long-lasting, and permanent nature of the ground improvement effect, and it has been applied only to limited applications.

Furthermore, the conventional general chemical solution injection material determines the concentration of the main agent solution and the hardening agent solution as appropriate, and generates water glass hydrogel in the ground to improve the ground strength and reduce the ground permeability. It has been demonstrated. However, the concentration of both chemicals is diluted by the stagnant water or underground water in the ground, and the injection tip chemical (injection initial flow) becomes insufficient in concentration to produce a hydrous gel with insufficient strength or a completely hydrous gel. In some cases, it was discharged without being generated. These uncured spilled chemical injections cause pollution of the surrounding environment and have caused serious social problems in the past.

Therefore, a water- injecting gel that has good affinity with water, which is expected to have a sustained soil improvement effect, and a chemical-injected material that is difficult to inhibit the formation of water-containing gel by diluting with ground water or underground water in the ground And development of the construction method has been demanded.

  On the other hand, water-absorbing resin is expected from the viewpoint of good affinity with water, but water-absorbing resin could not be injected into the ground. That is, when injecting into the ground, it is no exaggeration to say that the only solvent or dispersion that can be used in consideration of environmental pollution is water alone. When water is used as the dispersion of the water-absorbent resin, an injectable chemical solution is created, and the injected chemical solution increases in viscosity within a few seconds to tens of seconds, resulting in a highly viscous liquid or gelled in a container and injected into the ground. I couldn't.

  JP 10-168452   JP 10-017866   Japanese justice 9-071775   JP 10-066964

  Water-absorbing resin covered with a hydrophilic polymer compound as a coating material on the surface is injected into the ground as a dispersion in a state of being dispersed in water, and the water-absorbing resin hydrogel is formed in the ground. It became possible to exhibit the ground improvement effect. That is, the coating material of the hydrophilic polymer compound that covers the surface of the water-absorbent resin exhibits the effect of temporarily preventing contact between the water-absorbent resin and water until the injection operation is completed, and after the injection is completed, the dispersion is performed. Water used as a liquid, water such as stagnant water or underground water in the ground, dissolved or dissociated from the surface of the water-absorbent resin and disappeared from the surface of the water-absorbent resin, the water-absorbent resin and water can be contacted, The water absorption performance of the water absorbent resin will be exhibited.

A water-absorbent resin that is expected to have long-term stability in the ground has an extremely strong affinity with water and has a performance of not easily releasing water even when pressure is applied. A water-absorbing resin covered with a hydrophilic polymer compound as a covering material is injected into the ground as a dispersion in a state of being dispersed in water, and the water-absorbing resin in the ground is water used as a dispersion, or By gradually coming into contact with water due to stagnant water or underground water in the ground, water-absorbing resin performance is exhibited and a water-containing gel of the water-absorbing resin is formed in the ground. The water-absorbing resin hydrated gel exhibits a ground improvement effect, and it is possible to provide a chemical injection material having a good affinity with water and a method for the same. Further, when the water-absorbing resin whose surface is covered with a hydrophilic polymer compound is used as an injectable drug solution in a state of being dispersed in water, the water-absorbing resin is temporarily prevented from directly contacting with water. The chemical solution for injection does not immediately thicken and can be injected into the ground as a dispersion in a state of being dispersed in water, and the water absorbing performance of the water absorbent resin can be exhibited in the ground. . Furthermore, since the above dispersion liquid is unlikely to inhibit the formation of hydrous gel due to stagnant water or underground water in the ground, it is possible to carry out ground improvement without causing environmental contamination around the ground improvement.

The inventors have completed the present invention in view of the above problems. That is, a water-absorbing resin whose surface is covered with a hydrophilic polymer compound is injected into the ground as a dispersion in a state of being dispersed in water, and the water-absorbing resin is used as a dispersion in the ground. Alternatively, due to stagnant water or underground water in the ground, the water absorbent resin performance is gradually exhibited, and a water-containing gel of the water absorbent resin is formed in the ground. The water-absorbing resin water-containing gel exerted a ground improvement effect, and it has become possible to provide a chemical injection material having a good affinity for water and a construction method thereof.

The surface of the water absorbent resin covered by a hydrophilic polymer compound as a covering material of, when creating a injection drug solution, since the water-absorbent resin is not in direct contact with the water, injectate thicken immediately There is nothing, and it is possible to inject into the ground as a dispersion in a state of being dispersed in water.

  Furthermore, since the above dispersion liquid is unlikely to inhibit the formation of the water-absorbent resin-containing gel due to stagnant water or underground water in the ground, the ground can be improved without causing environmental pollution around the ground.

The water-absorbing resin injected into the ground exhibits water-absorbing properties that the water-absorbing resin has as a water-absorbing resin performance, for example, while exhibiting characteristics such as a high water absorption ratio and excellent water absorption speed when in contact with water in the ground A water-absorbing resin hydrogel is formed and hardened, and the ground improvement effect is exhibited. It is also possible to provide a chemical injection material having a good affinity for water and a method for the same.

  By injecting the water-absorbing resin covered with the hydrophilic polymer compound with the above surface as a coating material into the ground as a dispersion in a state of being dispersed in water, and leaving it to stand, the coating material becomes a dispersion in the ground. Dissolved or dissociated from the surface of the water-absorbent resin and disappeared from the surface of the water-absorbent resin due to the water used, water stagnated in the ground or underground water, etc. The water absorption performance of the resin will be exhibited.

  In general, the water-absorbent resin can absorb water several tens to several hundred times as much as its own weight to generate a hydrogel. That is, the water absorption capacity of the water absorbent resin is several tens to several hundreds. Using this performance, it is possible to control the water in the ground, which the civil engineering and construction industry has been aiming for many years, by taking in the water in the ground and generating a water-containing resin hydrogel in the ground. became. That is, the water-absorbent resin whose surface is coated with a hydrophilic polymer compound as a coating material is prepared by injecting a dispersion liquid using water as a dispersion liquid at a magnification equal to or lower than the water absorption capacity of the water-absorbent resin used. As a result, the water-absorbent resin can take water in the ground up to the water absorption ratio and generate a water-absorbent resin-containing gel in the ground. This is because the water-absorbent resin-type injection solution whose surface is covered with a hydrophilic polymer compound is an extremely safe chemical solution against surrounding environmental problems, since it is difficult for water-containing gel to be generated or washed away in the ground. It can be said that there is.

Furthermore, even if water is lost from the water-absorbing resin hydrogel once in the ground and volume shrinkage occurs, when water is encountered again, the water is taken up in a very short time, and the water-absorbing water of the same volume is again obtained. A resin hydrogel can be produced. The water in the ground fluctuates depending on the dry season and the rainy season, but this property of generating a hydrous gel of almost the same volume again is extremely useful performance as the water stopping performance of the chemical solution injection material . In other words, when there is no water in the ground, it is not particularly necessary to demonstrate the water-stopping effect due to the water-containing gel.When the water is large, the water-containing gel does not release the water even when the water is taken in and the pressure is applied. Maintaining the water stop effect is extremely beneficial as a ground improvement effect. Moreover, even if this water discharge | release and re-uptake are repeatedly performed, a water-containing performance is not impaired significantly, and is a factor which shows the long-term stability of the ground improvement effect by a water-absorbing-resin water-containing gel.

  Further, by injecting a hydrophilic polymer compound covering the surface of the water-absorbent resin with an acid substance or alkali substance separately prepared while dissolving or accelerating the dissolution, the performance of the water-absorbent resin is improved in the ground. It is possible to make it appear rapidly, and the ground improvement effect can be freely expressed.

As a method of injecting a water- absorbing resin covered with a hydrophilic polymer compound with the surface as a coating material into the ground as a dispersion in a state of being dispersed in water , a so-called one-shot (one-shot) method, that is, the water-absorbing resin is used. By injecting only one liquid dispersion into the ground in a state dispersed in water and leaving it to stand, the water-absorbent resin comes into contact with water in the ground, exerts its water-absorbent resin performance, hardens, An improvement effect can be exhibited. It is very useful as a chemical solution injection method that injection work can be performed with only one liquid and that it can be hardened in the ground. That is, in comparison with the method using two liquids, in addition to the reduction in labor for preparing the injection liquid, work efficiency such as downsizing and weight reduction of the injection apparatus is significantly improved. In addition, the most basic mistakes such as the mixing of two liquids and the mixing ratio in order to exert the ground improvement effect can be completely improved.

  Also, prepare a dispersion in which a water-absorbing resin covered with a hydrophilic polymer compound with the surface as a coating material is dispersed in water, and an aqueous solution or suspension containing a separately prepared acidic or alkaline substance. It is also possible to inject both liquids into the ground by associating them using a Y-shaped tube or the like, that is, a so-called 1.5 shot method. In this method, the hydrophilic polymer compound covering the surface of the water-absorbent resin with an acidic substance or an alkali substance is injected while dissolving or accelerating the dissolution, thereby rapidly improving the performance of the water-absorbent resin in the ground. It can be demonstrated and the ground improvement effect can be expressed freely.

  Furthermore, after the water-absorbing resin whose surface is covered with the hydrophilic polymer compound is dispersed in water and injected into the ground as a one-component dispersion, an aqueous solution or dispersion further containing another acidic substance or alkaline substance It is also possible to inject the liquid into the ground by a method of injecting the liquid as one liquid, a so-called toe shot (2 shot) method. In this method, the hydrophilic polymer compound that covers the surface of the water-absorbing resin previously injected into the ground can be dissolved or promoted in the ground so that the water-absorbing resin performance can be exhibited from that point. It is. By appropriately selecting the toe shot method from the one-shot method described above, it is possible to freely exhibit effects that meet the purpose of ground improvement.

  Which method to select from the one-shot method to the toe-shot method should be selected according to the characteristics of each method, the soil quality of the improved ground, and the purpose of ground improvement.

Of course, this chemical injection material and chemical injection method can be used for conventional ground improvement purposes, such as waterproofing of soft ground, ground strength improvement, underground tunnel construction, sewer construction, and house protection construction. It is.

  In addition, the ability to take water in the ground and generate water-absorbing resin hydrogel in the ground will constrain the water in the ground and will not release water easily even if pressure is applied. Therefore, it is extremely effective in preventing the ground liquefaction phenomenon caused by earthquakes, which was impossible in the past. In particular, many domestic oil storage bases are located on landfills, and measures to prevent liquefaction during an earthquake have been sought for many years. Current liquefaction prevention techniques are known to reduce or remove water from the ground, but have not been sufficiently effective. In addition, the method of reducing or extracting water is limited in the places where it can be used because of the fear of land subsidence. In addition, similar problems are seen in national infrastructure industries such as landfill airports and nuclear power plants, and expectations for liquefaction prevention technology are extremely high.

  Moreover, when the water-absorbing resin takes in water in the ground, the swelling effect of the water-absorbing resin will exert the consolidation effect of the ground, the ground strength will increase, the ground hydraulic conductivity will decrease, It can contribute to the construction of levee collapse prevention and quay protection. This performance is also consistent with the liquefaction prevention technology.

The chemical solution injection material and the chemical solution injection method can make a great contribution as a water stop material and a water stop method for leaking water from a crack in a concrete structure.

  When water absorbent resin performance is exhibited in the ground, water is absorbed by several tens to several hundred times the weight of the water absorbent resin to produce a water absorbent resin hydrogel, so the influence on the surrounding ground must be considered. However, this point can be determined from the filling rate of the chemical solution, the loss factor, and the water absorption performance of the water absorbent resin to be used in consideration of the soil performance, particle size distribution, porosity and the like of the target ground.

As a result of intensive studies on a method for producing a water-absorbing resin chemical injection material that achieves the above object, at least when the water-absorbing resin surface is covered with a hydrophilic polymer compound as a coating material, the water-absorbing resin has a water-absorbing performance. the found that it is possible to sufficiently exhibit a liquid injection material and chemical grouting method, thereby completing the present invention.

As a method for producing a water-absorbing resin chemical injection material , a water-absorbing resin having a water absorption ratio of several tens to several hundred times is dispersed using a low-boiling organic solvent such as acetone, methyl alcohol, or ethyl alcohol as a dispersion, and hydrophilic. Water-absorbing resin chemical liquid injection material in which the surface of the water-absorbing resin is covered with a hydrophilic polymer compound by removing a dispersion such as a low-boiling organic solvent by adding and mixing a water-soluble polymer compound and reducing the pressure, etc. Can be manufactured.

  The weight ratio of the dispersion liquid such as the low-boiling organic solvent and the water-absorbing resin used in the above production method varies depending on the water-absorbing resin and low-boiling organic solvent used, but it is preferable to use the dispersion liquid several times as much as the water-absorbing resin. Further, the hydrophilic polymer compound to be used is preferably about 5% to 200% of the water absorbent resin. The weight ratio between the hydrophilic polymer compound and the water-absorbing resin means the coating thickness of the hydrophilic polymer compound as a coating material. The coating thickness is determined by dissolving the coating material from the surface of the water-absorbing resin. This means a discrete speed, and is also a factor that greatly affects the speed at which the water absorbent resin performance is exhibited in the ground. That is, this weight ratio should be determined by the speed at which the water absorption performance in the ground is exhibited.

The above water-absorbing resin chemical injection material is obtained by changing the weight ratio of the water-absorbing resin to be used and the hydrophilic polymer compound covering the surface of the water-absorbing resin, water as a dispersion at the time of injection, and the ground after the injection. The time until the water directly contacts the surface of the water-absorbent resin due to the water remaining in the water or the underground water will be different. That is, when the weight ratio of the hydrophilic polymer compound covering the surface with respect to the water absorbent resin is large, the time until the water absorbent resin and water come into direct contact with each other becomes longer, and the injection work time during injection is longer. It can be said that it will take longer and workability will be improved. Further, the water absorption performance of the water absorbent resin is gradually exhibited in the ground after injection.

The weight ratio of the water absorbent resin used and the hydrophilic polymer compound covering the surface of the water absorbent resin chemical injection material varies depending on factors such as the water absorption magnification, shape, average particle diameter or particle size distribution of the water absorbent resin used. However, there is no particular limitation as long as the weight ratio of the water-absorbent resin and the hydrophilic polymer compound covering the surface is in the range of 15/85 to 85/15 . When the water absorbent resin ratio is less than the above weight ratio, a sufficient ground improvement effect cannot be exhibited. Moreover, when there is much water absorbing resin ratio, there exists a possibility of gelatinizing in the container in injection | pouring operation. On the other hand, if the water-absorbing resin ratio is too large, the surface of the water-absorbing resin cannot be sufficiently covered with the hydrophilic polymer compound, which is not preferable. Two or more hydrophilic polymer compounds that cover the surface of the water absorbent resin may be used.

When the surface of the water absorbent resin is coated with a hydrophilic polymer compound as a coating material increases the particle size of the water absorbent resin liquid injection material, but injection into the ground is concerned, generally the current chemical grouting There is a construction method using cement particles or blast furnace slag as a construction method used in this method, and the particle size of the cement particles or blast furnace slag is a standard.

  Examples of the water-absorbing resin used in the present invention include polyacrylic acid and derivatives thereof, starch-acrylic acid copolymer and derivatives thereof, hydrolyzate of starch-acrylonitrile copolymer, vinyl acetate-acrylic ester copolymer Saponified product of polymer, crosslinked product of isobutylene-maleic anhydride copolymer, hydrolyzate of acrylonitrile copolymer or acrylamide copolymer, or a crosslinked product thereof, crosslinked product of acrylate-acrylamide copolymer, crosslinked product of polyvinyl alcohol, modified product Examples include crosslinked polyethylene oxide, crosslinked acrylamide-2-methylpropanesulfonate, crosslinked (meth) acryloylethanesulfonate copolymer, crosslinked carboxymethylcellulose salt, and crosslinked polymer of cationic monomers. Of these, polyacrylic acid and its derivatives, starch-acrylic acid copolymers, and mixtures thereof are preferred in terms of water absorption characteristics and safety. These water-absorbing resins may be used alone or in combination of two or more.

The purpose of the present invention is to target a chemical injection material with good durability. However, as with conventional ground improvement purposes, it does not necessarily require long-term durability or does not require long-term water-absorbing resin to remain in the ground. For example, a biodegradable water-absorbing resin typified by polylactic acid or a derivative thereof, and a crosslinked polyamino acid polymer can also be used.

  The covering material used in the present invention covers the surface of the water-absorbent resin and aims to prevent contact between the water-absorbent resin and water during the pouring operation, and after pouring the water-absorbent resin into the ground, The coating material dissolves or separates from the surface of the water-absorbent resin due to water used as a dispersion at the time of injection, water stagnant in the ground or underground water, etc., and does not hinder contact with the water-absorbent resin and water. It is essential to have. After contact with water, the water-absorbent resin exhibits its water-absorbing performance, and a water-absorbent resin-containing gel is produced and cured in the ground, thereby exhibiting a ground improvement effect.

  The covering material is not particularly limited as long as it has the above-described effects, but is preferably inexpensive and excellent in safety.

As the coating material, at the time of producing the water-absorbing resin chemical injection material , it is dispersed or dissolved in a low-boiling organic solvent used as a dispersion of the water-absorbing resin, and after removing the low-boiling organic solvent, It covers the surface and can temporarily prevent contact between the water-absorbent resin and water. After pouring into the ground, the water and the water-absorbent resin come into contact with each other, and the water-absorbing performance of the water-absorbent resin is reduced. Any material can be used as long as it can be exhibited, and examples thereof include hydrophilic compounds, but are not particularly limited. For example, water-soluble polyvinyl alcohol (PVA, poval), carboxymethylcellulose (CMC), methylcellulose, hydroxyethylcellulose (HEC), hydroxypropylcellulose, polyacrylic acid (salt), crosslinked polyacrylic acid (salt), alginic acid (salt), Examples include starch, various aqueous emulsions, polyacrylamide, gelatin, gum arabic, polyvinyl pyrrolidone, dextrin, and casein. These compounds may be used alone or in combination of two or more.

  EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention further in detail, this invention is not limited at all by these.

(Comparative Example 1) At present, the grout agent for the ground improvement method for urban civil engineering is prepared by adding 120 liters of water to 80 liters of commercially available JIS No. 3 water glass, and dissolving 20 kg of sodium bicarbonate in 180 liters of water. In many cases, a two-pack type curing agent liquid is used. When 100 ml of each of the main agent solution and the curing agent solution was weighed into a 500 ml beaker and stirred and mixed at room temperature, it was cured in about 60 seconds to produce a water glass hydrogel, and the entire beaker was cured.

(Comparative Example 2) When 200 ml of the cured product (water glass hydrogel) prepared in (Comparative Example 1) was left in the open state without covering the 500 ml beaker for 7 days at room temperature, the weight was It decreased by about 25%. The volume of the water glass hydrogel was also shrunk by approximately 25%.

(Comparative Example 3) 50 g of ion-exchanged water was added to 150 g of the water-glass hydrogel after standing in the air of (Comparative Example 2), and left at room temperature for 2 hours. The supernatant water remaining without being taken into the water glass hydrogel again was removed, and the result of weight measurement of the water was about 48 g. That is, the water-glass hydrated gel after standing in the air again takes in a little water again to form a water-glass hydrated gel again, but it takes a long time and produces an overall water-containing gel almost the same as the original volume. There wasn't.

(Comparative Example 4) In a 500 ml beaker, 2 g of acrylic acid polymer partial sodium salt crosslinked product (Aquaric CA-K4: Nippon Shokubai Co., Ltd.) as a water-absorbing resin was gradually added to 200 ml of ion-exchanged water and mixed. A liquid base liquid was prepared. This main agent solution starts to thicken rapidly during mixing at room temperature. After about 20 seconds, the fluidity is lost and a water-absorbent resin-containing gel is formed in a beaker, which is cured and cannot be used as a liquid injection solution. Met.

When 200 ml of the water-absorbent resin hydrogel prepared in (Comparative Example 4) was left in the open state without a lid in a 500 ml beaker for 7 days at room temperature, the weight decreased by about 35%. The volume of the water-absorbent resin-containing gel also contracted by about 35%. When 70 g of ion-exchanged water was added to 130 g of the water-absorbing resin water-containing gel after standing in the air, the water-absorbing resin water-containing gel was formed again after about 40 seconds, and the entire contents in the beaker were cured, and the appearance was almost uniform. It became a gel. The operation of this method of leaving in the air and adding the same amount of water to the water-absorbent resin after volume shrinkage to generate a water-absorbent resin-containing gel again was repeated five times. A water-containing resin hydrogel was produced, and the entire contents in the beaker were cured, and the gel became substantially uniform in appearance.

In a 500 ml beaker, 4 g of sodium polyacrylate (molecular weight: about 10,000; Reagent Wako Pure Chemicals) was dissolved as a hydrophilic polymer compound in 300 g of methanol. 2 g of the acrylic acid polymer partial sodium salt crosslinked product (AQUALIC CA-K4: Nippon Shokubai Co., Ltd.) as a water-absorbent resin was dispersed and mixed in this solution, and then the beaker was transferred into a desiccator. By removing methanol, a hydrophilic polymer compound-coated water absorbent resin was obtained. 6 g of the hydrophilic polymer compound-coated water-absorbing resin was gradually added to and mixed with 200 ml of ion-exchanged water to prepare a water-dispersed main agent solution. Even after 30 minutes, the main agent solution did not increase in viscosity and could be used as a chemical solution injection solution. As a result of leaving the main agent solution 200 ml as it was at room temperature, a water-absorbent resin-containing gel was formed after about 2 hours, and the entire beaker was cured.

(Comparative Example 5) The sand gel will be described in detail below. Prepared a steel frame container with a side of 10cm and a height of 15cm, filled with Toyoura standard sand in it, compacted with water, and left for 2 days to prepare a sandy soil model ground. . A grout injection tube was installed at the center of the model ground and at a position 5 cm above the bottom of the container. After preparing 250 ml each of the main agent liquid and the hardener liquid of Comparative Example 1 in a container and adjusting the liquid temperature to about 20 ° C., both liquids were mixed with the above-mentioned sandy soil model ground with a liquid feed pump at a volume ratio of 1: 1. Inside, it was press-fitted from a grout injection tube. While injecting in all directions around the grout injection tube at an injection pressure of 2 to 5 kgf / cm 2, the injection tube was pulled up little by little, and when it was pulled up 10 cm, all operations were stopped and the grout injection tube was pulled out and left standing. Water in the sandy soil model ground and a mixture of excess main agent solution and hardener solution leaked from the upper lid of the steel frame container. After 5 hours, the model ground construction container was disassembled, and tap water was vigorously sprayed onto the sandy soil model ground to wash away the non-consolidated portion. As a result, the center of the model ground construction container was fixed. A consolidated ground body appeared. The volume was about 40% of the model ground building container. Moreover, as a result of collecting three sand gel cores from the consolidated ground body and measuring the uniaxial compressive strength characteristics, the measured values varied from 3 to 6 kgf / cm 2. The total weight of the consolidated ground body was 1.5 kg.

In the steel frame container prepared in (Comparative Example 5), 15 g of the hydrophilic polymer compound-coated water absorbent resin prepared in Example 2 is dispersed in 500 ml of pure water, and one main liquid is prepared in the container. After the temperature was adjusted to about 20 ° C., it was press-fitted from the grout injection pipe into the sandy soil model ground with a liquid feed pump. The injection tube was pulled up little by little while injecting in all directions around the grout injection tube at an injection pressure of 2 to 3 kgf / cm 2, and all operations were stopped and the grout injection tube was pulled out and allowed to stand when it was pulled up 10 cm. Water and excess main liquid in the sandy soil model ground leaked from the upper lid of the steel frame container. After 5 hours elapsed, the model ground building container was disassembled, and tap water was vigorously sprayed onto the sandy soil model ground to wash away the non-consolidated parts, but the entire model ground building container was integrated. A solid ground body appeared. That is, the volume was about 100% of the model ground building container. As a result of collecting three sand gel cores from the consolidated ground body and measuring the uniaxial compressive strength characteristics, there is a variation in the measured value of 8 to 10 kgf / cm 2, but the value shows a sufficient improvement effect. It was. The total weight of the consolidated ground body was 3.9 Kg.

When the consolidated ground body prepared in (Example 5) was left in the air at room temperature for 7 days, the consolidated ground body was slightly contracted. The total weight of the left solid body was 3.75 kg. When this solidified solid body was put in a model ground construction container and filled with tap water around 0.3 kg, it was restored to the size before shrinkage after about 10 minutes, and the total weight was also restored to 3.9 kg. There was no particular change in appearance.

The invention's effect

The chemical injection material and the chemical injection method using the water-absorbent resin of the present invention are used for conventional ground improvement purposes, for example, waterproofing of soft ground, ground strength improvement, underground tunnel construction, sewer construction, and houses. Of course, it can be used for protective works, but the sustainability of the ground improvement effect, the generation of water-containing gel by taking in the water in the ground, and water retention that does not release water easily even when the water-absorbing resin applies pressure. It can contribute to the prevention of ground liquefaction due to earthquakes and the stabilization of river embankments. Furthermore, it can be said that it is an extremely safe chemical solution in which water-containing gel is not generated or washed away in the ground, and contamination is not easily caused to the surrounding environment problems. The property of being able to take in water in the ground other than the water used for dispersion is widely applicable to water-stopping materials, water leakage prevention agents, etc., and can contribute to further expansion of the use of chemical injection materials and chemical injection methods. is there.

Claims (3)

  A chemical injection material characterized in that a water-absorbing resin covered with a hydrophilic polymer compound with a surface as a coating material is dispersed in water and injected into the ground. The chemical injection material according to claim 1, wherein the water absorbent resin is an acrylic acid copolymer and a derivative thereof. A chemical injection method according to claim 1, wherein the chemical injection material according to claim 1 is injected into the ground as a single injection chemical.