JP4536405B2 - Resin sheet laminated metal plate - Google Patents
Resin sheet laminated metal plate Download PDFInfo
- Publication number
- JP4536405B2 JP4536405B2 JP2004086829A JP2004086829A JP4536405B2 JP 4536405 B2 JP4536405 B2 JP 4536405B2 JP 2004086829 A JP2004086829 A JP 2004086829A JP 2004086829 A JP2004086829 A JP 2004086829A JP 4536405 B2 JP4536405 B2 JP 4536405B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- metal plate
- resin sheet
- laminated metal
- sheet laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、金属板と樹脂シートが強固に接着されて、接着界面の密着性が良好で、耐水性(熱水試験後密着性)、加工性(加工後密着性)に優れた樹脂シート積層金属板に関する。 The present invention is a resin sheet laminate in which the metal plate and the resin sheet are firmly bonded, the adhesion at the bonding interface is good, and the water resistance (adhesion after hot water test) and workability (adhesion after processing) are excellent. It relates to a metal plate .
従来、樹脂積層鋼板、樹脂積層アルミニウム板などの樹脂シート(薄膜またはフィルム。以下、樹脂シートと略称する)積層金属板は、その樹脂シートによる意匠性や複合材としての機能性を生かして種々の分野に使用されている。この樹脂シート積層金属板において、樹脂シートと金属板との積層には、一般に、接着剤を使用した積層法や、熱融着による積層法が採用されている。中でも接着剤を使用した積層法が、利便性や廉価性などの観点から広く採用されている。 Conventionally, resin sheet (thin film or film; hereinafter abbreviated as resin sheet) laminated metal plates such as resin-laminated steel plates and resin-laminated aluminum plates have various designs utilizing the design properties and composite material functionality of the resin sheets. Used in the field. In this resin sheet laminated metal plate, generally, a lamination method using an adhesive or a lamination method by heat fusion is employed for laminating the resin sheet and the metal plate. Among them, the laminating method using an adhesive is widely used from the viewpoints of convenience and low cost.
接着剤によって樹脂シートと金属板とを積層するに際しては、接着剤を溶剤によって希釈した状態で、コーターなどにより金属板にコートするのが一般的である。しかしながら、近年、作業環境の汚染や作業員の健康上の問題などから、溶剤の使用を規制する動きがあり、溶剤を使用しないエマルジョン化した接着剤が種々提案されている(例えば、特許文献1および特許文献2参照)。樹脂シート積層金属板は、その意匠性を生かして意匠性が重視される用途に使用されることが多く、特にユニットバスなど、いわゆる水周りの部品製造用に使用される樹脂シート積層金属板は、耐水性が要求されるが、従来提案されているエマルジョン接着剤では、耐水性および加工性が不十分であるという問題があった。
本発明者らは、上記問題を解決し、耐水性、加工性に優れた樹脂シート積層金属板を提供すべく鋭意検討した結果、本発明に到達した。本発明の目的は、金属板と樹脂シートが強固に接着されて、接着界面の密着性が良好で、耐水性(熱水試験後密着性)、加工性(加工後密着性)に優れた樹脂シート積層金属板を提供することにある。 The inventors of the present invention have arrived at the present invention as a result of intensive studies to solve the above-mentioned problems and provide a resin sheet laminated metal plate having excellent water resistance and workability . The object of the present invention is a resin in which the metal plate and the resin sheet are firmly bonded, the adhesion at the bonding interface is good, and the water resistance (adhesion after hot water test) and workability (adhesion after processing) are excellent. The object is to provide a sheet metal sheet .
上記課題を解決するため、カルボキシル基を有するウレタン系樹脂エマルジョン(A)、および、イソシアネート基を有する架橋剤(B)からなる樹脂成分に、シランカップリング剤(C)が、カルボキシル基を有するウレタン系樹脂エマルジョン(A)の固形分100重量部に対し0.1〜5重量部配合されてなる樹脂組成物を主成分とする積層用接着剤を介して、金属板とポリ塩化ビニルを主成分とする樹脂シートが積層されてなることを特徴とする、樹脂シート積層金属板を提供する。 In order to solve the above problems, a urethane component resin emulsion (A) having a carboxyl group and a resin component comprising a crosslinking agent (B) having an isocyanate group, the silane coupling agent (C) is a urethane having a carboxyl group. The main component is a metal plate and polyvinyl chloride through a laminating adhesive composed mainly of a resin composition composed of 0.1 to 5 parts by weight per 100 parts by weight of the solid content of the resin-based resin emulsion (A). A resin sheet-laminated metal plate is provided, wherein the resin sheet is laminated.
本発明は、次のような特別に有利な効果を奏し、その産業上の利用価値は極めて大である。
1.本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物は、エマルジョン状態を呈し、塗料、接着剤などの主成分として使用され、このエマルジョンから形成される皮膜(薄膜)は、基体金属板との密着性、耐水性および耐薬品性に優れている。
2.本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物は、無溶剤型または少量の溶剤を含む程度であるので、塗料または接着剤の用途に使用する場合、作業環境の汚染や作業員の健康上の問題が生じない。
3.本発明に係る金属板と樹脂シートとの積層用接着剤は、エマルジョンの状態を呈しているので、塗布性に優れている。
4.本発明に係る樹脂シート積層金属板は、金属板と樹脂シートが強固に接着されており、耐水性(熱水試験後密着性)、加工性(加工後密着性)に優れているので、樹脂シート積層金属板の各種の用途、特に意匠性を有する樹脂積層金属板、または水周りの部品製造用に好適である。
The present invention has the following particularly advantageous effects, and its industrial utility value is extremely great.
1. The resin composition used for the production of the resin sheet laminated metal plate according to the present invention exhibits an emulsion state and is used as a main component of a paint, an adhesive, etc., and a film (thin film) formed from this emulsion is a substrate. Excellent adhesion to metal plates , water resistance and chemical resistance.
2. Since the resin composition used for the production of the resin sheet laminated metal plate according to the present invention is a solvent-free type or contains a small amount of a solvent, when used for a paint or an adhesive, There are no health problems for workers.
3. Since the adhesive for laminating the metal plate and the resin sheet according to the present invention is in an emulsion state, it is excellent in applicability.
4). In the resin sheet laminated metal plate according to the present invention , the metal plate and the resin sheet are firmly bonded , and are excellent in water resistance (adhesion after hot water test) and workability (adhesion after processing). It is suitable for various uses of sheet-laminated metal plates, particularly for resin-laminated metal plates having design properties, or for manufacturing parts around water.
以下、本発明を詳細に説明する。
本発明において、カルボキシル基を有するウレタン系樹脂エマルジョン(A){以下、成分(A)と略称することがある}は、例えば、高分子ポリオール(a)、水酸基2個以上とカルボキシル基1個以上を有する化合物(b)、有機ポリイソシアネート(c)、および、必要により鎖伸長剤(d)、および/または、重合停止剤(e)から合成されるウレタン系樹脂を、さらに、塩形成剤(f)によって水中に乳化させてなるアニオン性自己乳化型ウレタン系樹脂エマルジョンを意味する。なお、本発明において自己乳化型エマルジョンとは、分子内に親水性のカルボキシル基を有し、それ自体が単独で水溶性または水分散性を発揮するエマルジョンを言う。
Hereinafter, the present invention will be described in detail.
In the present invention, the urethane resin emulsion (A) having a carboxyl group (hereinafter sometimes abbreviated as component (A)) is, for example, a polymer polyol (a) having two or more hydroxyl groups and one or more carboxyl groups. A urethane-based resin synthesized from the compound (b) having an organic polyisocyanate (c) and, if necessary, the chain extender (d) and / or the polymerization terminator (e), It means an anionic self-emulsifying urethane resin emulsion emulsified in water by f). In the present invention, the self-emulsifying emulsion means an emulsion having a hydrophilic carboxyl group in the molecule and exhibiting water solubility or water dispersibility by itself.
高分子ポリオール(a)としては、例えば、ポリエーテルポリオール(a1)、ポリエステルポリオール(a2)、ポリラクトンポリオール(a3)、ポリカーボネートポリオール(a4)およびポリオレフィンポリオール(a5)などが挙げられる。ポリエーテルポリオール(a1)の具体例としては、エチレンオキシド、プロピレンオキシド、1,2−ブチレンオキシド、テトラヒドロフランなどのアルキレンオキシドを重合、または共重合させて得られたものが挙げられる。その具体例として、ポリエチレングリコール、ポリプロピレングリコール、ポリオキシエチレン−ポリオキシプロピレン(ブロック共重合またはランダム共重合)グリコール、ポリオキシエチレン−ポリテトラメチレンエーテルグリコール(ブロック共重合またはランダム共重合)、ポリテトラメチレンエーテルグリコールなどが挙げられる。 Examples of the polymer polyol (a) include polyether polyol (a1), polyester polyol (a2), polylactone polyol (a3), polycarbonate polyol (a4), and polyolefin polyol (a5). Specific examples of the polyether polyol (a1) include those obtained by polymerizing or copolymerizing alkylene oxides such as ethylene oxide, propylene oxide, 1,2-butylene oxide, and tetrahydrofuran. Specific examples include polyethylene glycol, polypropylene glycol, polyoxyethylene-polyoxypropylene (block copolymer or random copolymer) glycol, polyoxyethylene-polytetramethylene ether glycol (block copolymer or random copolymer), polytetra And methylene ether glycol.
ポリエステルポリオール(a2)の具体例としては、コハク酸、アジピン酸、セバチン酸、グルタル酸、アゼライン酸などの脂肪族ジカルボン酸、および/または、イソフタル酸、テレフタル酸などの芳香族ジカルボン酸と、エチレングリコール、プロピレングリコール、1,4−ブタンジオール、1,6−ヘキサンジオール、3−メチル−1,5−ペンタジオール、ネオペンチルグリコール、1,4−ジヒドロキシメチルシクロヘキサンなどの2価アルコールとを、重縮合させたものが挙げられる。その具体例として、ポリエチレンアジペートジオール、ポリブチレンアジペートジオール、ポヘキサメチレンアジペートジオール、ポリネオペンチルアジペートジオール、ポリエチレン/ブチレンアジペートジオール、ポリ−3−メチルペンタンアジペートジオール、ポリブチレンイソフタレートジオールなどが挙げられる。 Specific examples of the polyester polyol (a2) include aliphatic dicarboxylic acids such as succinic acid, adipic acid, sebacic acid, glutaric acid, and azelaic acid, and / or aromatic dicarboxylic acids such as isophthalic acid and terephthalic acid, and ethylene. A dihydric alcohol such as glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, 3-methyl-1,5-pentadiol, neopentyl glycol, 1,4-dihydroxymethylcyclohexane, A condensed product may be mentioned. Specific examples thereof include polyethylene adipate diol, polybutylene adipate diol, pohexamethylene adipate diol, polyneopentyl adipate diol, polyethylene / butylene adipate diol, poly-3-methylpentane adipate diol, polybutylene isophthalate diol, and the like. .
ポリラクトンポリオール(a3)の具体例としては、ポリカプロラクトンジオール、ポリカプロラクトントリオール、ポリ−3−メチルバレロラクトンジオール等が挙げられる。ポリカーボネートポリオール(a4)の具体例としては、ポリヘキサメチレンカーボネートジオールなどが挙げられる。ポリオレフィンポリオール(a5)の具体例として、ポリブタジエングリコール、ポリイソブチレングリコール、これらの水素化物などが挙げられる。これら例示した高分子ポリオール(a)は、単独でも2種以上の併用であってもよい。これら高分子ポリオール(a)のうち好ましいものは、ポリエーテルポリオール(a1)、ポリエステルポリオール(a2)、ポリラクトンポリオール(a3)およびポリカーボネートポリオール(a4)である。高分子ポリオール(a)の数平均分量は、好ましくは300〜5000であり、より好ましくは500〜3000である。 Specific examples of the polylactone polyol (a3) include polycaprolactone diol, polycaprolactone triol, and poly-3-methylvalerolactone diol. Specific examples of the polycarbonate polyol (a4) include polyhexamethylene carbonate diol. Specific examples of the polyolefin polyol (a5) include polybutadiene glycol, polyisobutylene glycol, and hydrides thereof. These exemplified polymer polyols (a) may be used alone or in combination of two or more. Among these polymer polyols (a), polyether polyol (a1), polyester polyol (a2), polylactone polyol (a3) and polycarbonate polyol (a4) are preferred. The number average amount of the polymer polyol (a) is preferably 300 to 5,000, more preferably 500 to 3,000.
水酸基2個以上とカルボキシル基1個以上を有する化合物(b){以下、単に化合物(b)と略称することがある}としては、例えば、ジメチロール酢酸、ジメチロールプロピオン酸、ジメチロール酪酸などのジメチロールアルカン酸が挙げられる。中でも好ましいのは、ジメチロールプロピオン酸である。化合物(b)の量は、高分子ポリオール(a)に対し5重量%以下、より好ましくは0.1〜4重量%である。化合物(b)の量が0.1重量%未満では、樹脂成分の安定なウレタン系樹脂エマルジョン(A)が得難く、5重量%を超えると、樹脂成分中の親水性が高くなるため、ウレタン系樹脂エマルジョンの粘度が著しく高くなり、またこのウレタン系樹脂エマルジョン(A)から得られる皮膜(薄膜またはシート)の耐水性が低下するので、いずれも好ましくない。 Examples of the compound (b) having two or more hydroxyl groups and one or more carboxyl groups (hereinafter sometimes simply referred to as the compound (b)) include dimethylol such as dimethylolacetic acid, dimethylolpropionic acid, and dimethylolbutyric acid. An alkanoic acid is mentioned. Of these, dimethylolpropionic acid is preferred. The amount of the compound (b) is 5% by weight or less, more preferably 0.1 to 4% by weight with respect to the polymer polyol (a). If the amount of the compound (b) is less than 0.1% by weight, it is difficult to obtain a stable urethane-based resin emulsion (A) of the resin component, and if it exceeds 5% by weight, the hydrophilicity in the resin component becomes high. Since the viscosity of the resin emulsion is remarkably increased, and the water resistance of the film (thin film or sheet) obtained from the urethane resin emulsion (A) is lowered, both are not preferable.
有機ポリイソシアネート(c)は、分子中にNCO基を有する有機化合物であって、炭素数(NCO基中の炭素を除く、以下同じ)が2〜12の脂肪族ジイソシアネート(c1)、炭素数4〜15の脂環式ジイソシアネート(c2)、炭素数8〜12の芳香脂肪族ジイソシアネート(c3)、および、炭素数6〜20の芳香族ジイソシアネート、脂肪族ジイソシアネート、または、脂環式ジイソシアネートから誘導されるイソシアヌレートおよびピーレット変性ポリイシシアネートなどをいう。 The organic polyisocyanate (c) is an organic compound having an NCO group in the molecule, the aliphatic diisocyanate (c1) having 2 to 12 carbon atoms (excluding carbon in the NCO group, the same shall apply hereinafter), and 4 carbon atoms. Derived from -15 cycloaliphatic diisocyanate (c2), araliphatic diisocyanate (c3) having 8 to 12 carbon atoms, and aromatic diisocyanate, aliphatic diisocyanate or alicyclic diisocyanate having 6 to 20 carbon atoms. Isocyanurate and pyret-modified polyisocyanate.
脂肪族ジイソシアネート(c1)の具体例としては、ヘキサメチレンジイソシアネート、リジンジイソシアネートなどが挙げられる。脂環式ジイソシアネート(c2)の具体例としては、シクロヘキシルメタンジイソシアネート、イソホロンジイソシアネート、シクロヘキサンジイソシアネート、水素化トリレンジイソシアネート、水素化キシリレンジイソシアネートなどが挙げられる。芳香族ジイソシアネート(c3)の具体例としては、トリレンジイソシアネート、α,α,α',α'−テトラメチルキシリレンジイソシアネート、ジフェニルメタンジイソシアネート、ナフチレンジイソシアネート、キシリレンジイソシアネートなどが挙げられる。これら例示した有機ポリイソシアネート(c)は、単独でも2種以上の併用であってもよい。 Specific examples of the aliphatic diisocyanate (c1) include hexamethylene diisocyanate and lysine diisocyanate. Specific examples of the alicyclic diisocyanate (c2) include cyclohexylmethane diisocyanate, isophorone diisocyanate, cyclohexane diisocyanate, hydrogenated tolylene diisocyanate, hydrogenated xylylene diisocyanate, and the like. Specific examples of the aromatic diisocyanate (c3) include tolylene diisocyanate, α, α, α ′, α′-tetramethylxylylene diisocyanate, diphenylmethane diisocyanate, naphthylene diisocyanate, xylylene diisocyanate, and the like. These exemplified organic polyisocyanates (c) may be used alone or in combination of two or more.
これら有機ポリイソシアネート(c)のうち好ましいものは、脂肪族ジイソシアネート(c1)および脂環式ジイソシアネート(c2)であり、特に好ましいものは、ヘキサメチレンジイソシアネート、シクロヘキシルメタンジイソシアネートおよびイソホロンジイソシアネートである。脂肪族ジイソシアネート(c1)または脂環式ジイソシアネート(c2)から誘導されるイソシアヌレートおよびピーレット変性ポリイソシアネートも、同様に好ましい。有機ポリイソシアネート(c)の量は、高分子ポリオール(a)に対して好ましくは60重量%以下、より好ましくは1〜50重量%である。 Among these organic polyisocyanates (c), preferred are aliphatic diisocyanate (c1) and alicyclic diisocyanate (c2), and particularly preferred are hexamethylene diisocyanate, cyclohexylmethane diisocyanate and isophorone diisocyanate. Preference is likewise given to isocyanurates and pyret-modified polyisocyanates derived from aliphatic diisocyanates (c1) or alicyclic diisocyanates (c2). The amount of the organic polyisocyanate (c) is preferably 60% by weight or less, more preferably 1 to 50% by weight, based on the polymer polyol (a).
必要により樹脂成分中に含ませる鎖伸長剤(d)の具体例としては、低分子ポリオール(d1)およびポリアミン(d2)が挙げられる。低分子ポリオール(d1)としては、例えば、前記ポリエステルポリオール(a2)の原料として挙げた2価アルコール、およびそのアルキレンオキシド低モル付加物(数平均分子量500未満)、ビスフェノールのアルキレンオキシド低モル付加物(数平均分子量500未満)、グリセリン、トリメチロールエタン、トリメチロールプロパンなどの3価アルコール、およびそのアルキレンオキシド低モル付加物(数平均分子量500未満)などが挙げられる。 Specific examples of the chain extender (d) to be included in the resin component as necessary include a low molecular polyol (d1) and a polyamine (d2). As the low molecular polyol (d1), for example, the dihydric alcohol mentioned as the raw material of the polyester polyol (a2), and its alkylene oxide low molar adduct (number average molecular weight less than 500), bisphenol alkylene oxide low molar adduct (Number average molecular weight less than 500), trihydric alcohols such as glycerin, trimethylolethane, trimethylolpropane, and alkylene oxide low molar adducts thereof (number average molecular weight less than 500).
ポリアミン(d2)の具体例としては、エチレンジアミン、N−ヒドロキシエチルエチレンジアミン、テトラメチレンジアミン、ヘキサメチレンジアミン、ジエチレントリアミンなどの脂肪族ポリアミン類、4,4’−ジアミノジシクロヘキシルメタン、1,4−ジアミノシクロヘキサン、イソホロンジアミンなどの脂環式ポリアミン類、キシリレンジアミン、α,α,α',α'−テトラメチルキシリレンジアミンなどの芳香環を有する脂肪族ポリアミン類、4,4’−ジアミノジフェニルメタン、トリレンジアミン、ベンヂジン、フェニレンジアミンなどの芳香族ポリアミン類が挙げられる。これらは単独でも2種以上の併用であってもよい。鎖伸長剤(d)の配合量は、使用する高分子ポリオール(a)に対して好ましくは30重量%以下、より好ましくは0.5〜20重量%である。 Specific examples of the polyamine (d2) include aliphatic polyamines such as ethylenediamine, N-hydroxyethylethylenediamine, tetramethylenediamine, hexamethylenediamine, and diethylenetriamine, 4,4′-diaminodicyclohexylmethane, 1,4-diaminocyclohexane, Alicyclic polyamines such as isophoronediamine, aliphatic polyamines having an aromatic ring such as xylylenediamine, α, α, α ′, α′-tetramethylxylylenediamine, 4,4′-diaminodiphenylmethane, tolylene Aromatic polyamines such as amine, benzidine, and phenylenediamine are listed. These may be used alone or in combination of two or more. The amount of the chain extender (d) is preferably 30% by weight or less, more preferably 0.5 to 20% by weight, based on the polymer polyol (a) used.
また、必要により樹脂成分中に含ませる重合停止剤(e)としては、メタノール、ブタノール、シクロヘキサノールなどの低分子モノアルコール類、モノ−およびジ−エチルアミン、モノ−およびジ−ブチルアミンなどのアルカノールアミン類が挙げられる。重合停止剤(e)の配合量は、使用する高分子ポリオール(a)に対して20重量%以下であり、より好ましくは0.1〜10重量%である。 Further, as necessary, the polymerization terminator (e) contained in the resin component includes low-molecular monoalcohols such as methanol, butanol and cyclohexanol, and alkanolamines such as mono- and di-ethylamine, mono- and di-butylamine. Kind. The compounding quantity of a polymerization terminator (e) is 20 weight% or less with respect to the high molecular polyol (a) to be used, More preferably, it is 0.1 to 10 weight%.
塩形成剤(f)の具体例としては、トリメチルアミン、トリエチルアミン、トリイソプロピルアミン、トリ−n−プロピルアミン、トリ−n−ブチルアミンなどのトリアルキルアミン類、N−メチルモルホリン、N−エチルモルホリンなどのN−アルキルモルホリン類、N−ジメチルエタノールアミン、N−ジエチルエタノールアミンなどのN−ジアルキルアルカノールアミン類が挙げられる。これらは単独で使用できるし、2種以上併用することもできる。これらのうち好ましいものは、トリアルキルアミン類であり、特に好ましいものは、トリエチルアミンである。塩形成剤(f)の量は、使用する化合物(b)のカルボキシル基1当量に対して好ましくは0.3〜1当量、より好ましくは0.4〜0.8当量である。 Specific examples of the salt forming agent (f) include trialkylamines such as trimethylamine, triethylamine, triisopropylamine, tri-n-propylamine, tri-n-butylamine, N-methylmorpholine, N-ethylmorpholine, and the like. N-dialkylalkanolamines such as N-alkylmorpholines, N-dimethylethanolamine, N-diethylethanolamine and the like can be mentioned. These can be used alone or in combination of two or more. Of these, preferred are trialkylamines, and particularly preferred is triethylamine. The amount of the salt forming agent (f) is preferably 0.3 to 1 equivalent, more preferably 0.4 to 0.8 equivalent, relative to 1 equivalent of the carboxyl group of the compound (b) used.
ウレタン系樹脂エマルジョンを製造する際には、まず、有機溶剤の存在下または不存在下で、高分子ポリオール(a)、水酸基2個以上とカルボキシル基1個以上を有する化合物(b)、有機ポリイソシアネート(c)、必要により鎖伸長剤(d)および/または重合停止剤(e)を、一段法または多段法によって反応させて、カルボキシル基含有ウレタン系樹脂を形成する。ついで、得られたカルボキシル基含有ウレタン系樹脂を、塩形成剤(f)によって中和した後、または、中和しながら水と混合して分散体(エマルジョン)とする。この後、必要に応じて溶剤を除去し、平均粒子径0.001〜1μm程度のウレタン系樹脂粒子が分散した、自己乳化型のウレタン系樹脂エマルジョン(A)が得られる。ウレタン系樹脂の形成反応は、通常20〜150℃の温度、好ましくは50〜120℃の温度で行うが、アミンを使用する場合は80℃以下、好ましくは60〜0℃の温度で行う。 In producing a urethane resin emulsion, first, in the presence or absence of an organic solvent, a polymer polyol (a), a compound (b) having two or more hydroxyl groups and one or more carboxyl groups, an organic polymer, The carboxyl group-containing urethane resin is formed by reacting the isocyanate (c), if necessary, the chain extender (d) and / or the polymerization terminator (e) by a one-stage method or a multistage method. Next, the obtained carboxyl group-containing urethane resin is neutralized with the salt forming agent (f) or mixed with water while neutralizing to obtain a dispersion (emulsion). Thereafter, the solvent is removed as necessary, and a self-emulsifying urethane resin emulsion (A) in which urethane resin particles having an average particle diameter of about 0.001 to 1 μm are dispersed is obtained. The formation reaction of the urethane-based resin is usually performed at a temperature of 20 to 150 ° C., preferably 50 to 120 ° C., but when an amine is used, it is performed at a temperature of 80 ° C. or less, preferably 60 to 0 ° C.
また、反応を促進させるため、通常のウレタン系樹脂形成反応に使用されるアミン系触媒、または、ジオクチル錫ジマレート、ジブチル錫ジラウレート、オクチル酸第一錫、ジブチル錫オキシド、ビス(トリ−n−ブチル錫オキシド)などの錫系触媒を使用することができる。また、有機溶剤を使用する場合の溶剤としては、水溶性で水と同程度ないしそれ以下の沸点を有するものが好ましく、具体的には、アセトン、メチルエチルケトン、テトラヒドロフラン、ジオキサンなどが挙げられる。 In order to accelerate the reaction, an amine catalyst used in a usual urethane resin forming reaction, or dioctyltin dimaleate, dibutyltin dilaurate, stannous octylate, dibutyltin oxide, bis (tri-n-butyl) Tin-based catalysts such as tin oxide) can be used. In the case of using an organic solvent, a solvent that is water-soluble and has a boiling point comparable to or lower than that of water is preferable. Specific examples include acetone, methyl ethyl ketone, tetrahydrofuran, and dioxane.
ウレタン系樹脂エマルジョン(A)は、その製造方法に特に制限はない。ウレタン系樹脂エマルジョン(A)は、上記の特性を具備しているものであれば、市販されているものであってもよい。市販されているウレタン樹脂エマルジョン(A)として、例えば、三洋化成工業社製のユーコート、パーマリン(いずれも商品名)、第一工業製薬社製のスーパーフレックス(商品名)、大日本インキ社製のボンディック(商品名)などが挙げられる。 The production method of the urethane resin emulsion (A) is not particularly limited. The urethane resin emulsion (A) may be a commercially available product as long as it has the above-mentioned characteristics. Examples of commercially available urethane resin emulsions (A) include Sanyo Kasei Kogyo Co., Ltd., Permarin (all trade names), Dai-ichi Kogyo Seiyaku Superflex (trade names), Dainippon Ink Co., Ltd. Bondic (trade name) and the like are listed.
本発明において、イソシアネート基を有する架橋剤(B){以下、単に成分(B)と略称することがある}は、分子中に1個以上のイソシアネート基を有し、水分散可能なものをいう。このような特性を有するものであれば特に制限はないが、ウレタン系樹脂エマルジョン(A)との架橋反応の進行や相溶性、作業性などを勘案すると、水と容易に混和するようなものが好ましく、ポリエチレンオキシド、カルボキシル基、スルホン酸基などの1種以上を有し、親水性成分で変性された自己乳化型ポリイソシアネート(B1)、または水性ブロックポリイソシアネート(B2)が好ましい。 In the present invention, the crosslinking agent (B) having an isocyanate group (hereinafter sometimes simply referred to as component (B)) means one having at least one isocyanate group in the molecule and capable of being dispersed in water. . There is no particular limitation as long as it has such characteristics, but considering the progress of the crosslinking reaction with the urethane-based resin emulsion (A), compatibility, workability, etc., it is easy to mix with water. Preferably, self-emulsifying polyisocyanate (B1) or aqueous block polyisocyanate (B2) having one or more of polyethylene oxide, carboxyl group, sulfonic acid group and the like and modified with a hydrophilic component is preferable.
自己乳化型ポリイソシアネート(B1)は、例えば、ポリイソシアネート分子鎖中に、イソシアネート基と反応し得る活性水素基を1個以上有する親水性基、および疎水性基を導入することにより製造することができる。親水性基と同時に疎水性基を導入するのは、ポリイソシアネートを水中に分散させたときに、その周りに存在している水分子と、付近に存在する未反応のイソシアネート基との反応を、立体障害的またはその親油性に基づいて、界面化学的に抑制する効果を得るためである。疎水性基としては、例えば、活性水素基を1個以上有する高級アルコールや、水酸基含有脂肪酸エステルなど挙げられる。 The self-emulsifying polyisocyanate (B1) can be produced, for example, by introducing a hydrophilic group having at least one active hydrogen group capable of reacting with an isocyanate group and a hydrophobic group into the polyisocyanate molecular chain. it can. The introduction of the hydrophobic group simultaneously with the hydrophilic group is because when the polyisocyanate is dispersed in water, the reaction between the water molecules present around the polyisocyanate and the unreacted isocyanate group present in the vicinity is performed. This is because the effect of suppressing surface chemistry is obtained based on steric hindrance or its lipophilicity. Examples of the hydrophobic group include higher alcohols having one or more active hydrogen groups, and hydroxyl group-containing fatty acid esters.
自己乳化型ポリイソシアネート(B1)を得るのに用いられるポリイソシアネートとしては、例えば、フェニレンジイソシアネート、トリレンジイソシアネート、キシリレンジイソシアネート、テトラメチルキシリレンジイソシアネート、ナフチレンジイソシアネート、ジフェニルメタンジイソシアネートなど、およびこれら異性体からなる芳香族ジイソシアネート類、1,6−ヘキサメチレンジイソシアネート、1,12−ドデカンジイソシアネートなどの脂肪族ジイソシアネート類、シクロヘキサンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、イソホロンジイソシアネート、ノルボルナンジイソシアネートなどの脂環式ジイソシアネート類、2,4,6−トリイソシアネートトルエン、2,4,4’−トリイソシアネートジフェニルエーテル、トリ(イソシアネートフェニル)メタンなどのトリイソシアネート類などが挙げられる。 Examples of the polyisocyanate used to obtain the self-emulsifying polyisocyanate (B1) include phenylene diisocyanate, tolylene diisocyanate, xylylene diisocyanate, tetramethylxylylene diisocyanate, naphthylene diisocyanate, diphenylmethane diisocyanate, and the isomers thereof. Aromatic diisocyanates consisting of, aliphatic diisocyanates such as 1,6-hexamethylene diisocyanate, 1,12-dodecane diisocyanate, cycloaliphatic diisocyanates such as cyclohexane diisocyanate, dicyclohexylmethane diisocyanate, isophorone diisocyanate, norbornane diisocyanate, 2, 4,6-triisocyanatotoluene, 2,4,4'-triisocyanate DOO diphenylether, birds and the like triisocyanates such as (isocyanate phenyl) methane.
また、ポリイソシアネートと活性水素基含有化合物との反応によるイソシアネート基末端化合物、またはこれら化合物の反応、例えば、アダクト型ポリイソシアネートやウレトジオン化反応、イソシアヌレート化反応、カルボジイミド化反応、ウレトンイミン化反応、ビュレット化反応などによるイソシアネート変性体、およびこれらの混合物なども挙げられる。これらポリイソシアネートのうち、水分散安定性、水分散後のイソシアネート基の安定性、無黄変性などの観点から、脂肪族ポリイソシアネート、脂環式ポリイシシアネートが好ましく、中でも耐熱性、架橋性の観点から、平均イソシアネート基数が2以上のイソシアヌレート環含有ポリイソシアネートがより好ましい。 In addition, isocyanate group-terminated compounds by reaction of polyisocyanates with active hydrogen group-containing compounds, or reactions of these compounds, such as adduct type polyisocyanates, uretdioneation reactions, isocyanurate reactions, carbodiimidization reactions, ureton iminization reactions, burettes. Examples thereof include isocyanate-modified products obtained by chemical reaction and mixtures thereof. Of these polyisocyanates, aliphatic polyisocyanates and alicyclic polyisocyanates are preferred from the viewpoints of water dispersion stability, stability of isocyanate groups after water dispersion, non-yellowing, and the like. From the viewpoint, an isocyanurate ring-containing polyisocyanate having an average number of isocyanate groups of 2 or more is more preferable.
このイソシアヌレート環含有ポリイソシアネートは、例えば、原料のポリイソシアネートを第3級アミン類、アルキル置換エチレンイミン類、第3級アルキルフォスフィン類、アセチルアセン金属塩類、各種有機酸の金属塩類などのウレトジオン化触媒、および/または、イソシアヌレート化触媒、さらに必要に応じ、助触媒を用いて、溶剤の存在下または不存在下、0〜90℃の温度範囲で、液状のポリオールまたはジオクチルフタレート(DOP)などの可塑剤中で、反応させて得られる。 This isocyanurate ring-containing polyisocyanate includes, for example, raw diisocyanates such as tertiary amines, alkyl-substituted ethyleneimines, tertiary alkylphosphines, acetylacene metal salts, and metal salts of various organic acids. Liquid polyol or dioctyl phthalate (DOP) in the temperature range of 0 to 90 ° C. in the presence or absence of a solvent using a catalyst and / or an isocyanurate catalyst and, if necessary, a cocatalyst. It can be obtained by reacting in a plasticizer.
上の反応で使用される助触媒としては、例えば、フェノール性ヒドロキシル基含有化合物、アルコール性ヒドロキシル基含有化合物などが挙げられる。上の反応で使用される溶剤としては、例えば、トルエン、キシレンなどの芳香族類、メチルエチルケトン、メチルイソブチルケトンなどのケトン類、酢酸エチル、酢酸ブチルなどのエステル類、プロピレングリコールメチルエーテルアセテート、エチル−3−エトキシプロピオネートなどのグリコールエーテルエステル類など、イソシアネート基に対して不活性な溶剤が挙げられる。また、反応停止剤により触媒を不活性化し上記反応を停止させることができる。反応停止剤としては、例えば、リン酸、パラトルエンスルホン酸メチル、硫黄などが挙げられる。 Examples of the cocatalyst used in the above reaction include phenolic hydroxyl group-containing compounds and alcoholic hydroxyl group-containing compounds. Examples of the solvent used in the above reaction include aromatics such as toluene and xylene, ketones such as methyl ethyl ketone and methyl isobutyl ketone, esters such as ethyl acetate and butyl acetate, propylene glycol methyl ether acetate, ethyl- Examples thereof include solvents inert to isocyanate groups, such as glycol ether esters such as 3-ethoxypropionate. Further, the reaction can be stopped by inactivating the catalyst with a reaction terminator. Examples of the reaction terminator include phosphoric acid, methyl paratoluenesulfonate, sulfur and the like.
自己乳化型ポリイソシアネート(B1)を得る際に使用されるポリイソシアネートに、親水性基を導入するための親水性化合物としては、脂肪酸塩、スルホン酸塩、リン酸エステル、硫酸エステル塩などのアニオン性化合物、第一級アミン塩、第二級アミン塩、第三級アミン塩、第四級アンモニウム塩、ピリジニウム塩などのカチオン性化合物、アニオン性化合物、ノニオン性化合物、スルホベタインなどの両性化合物が挙げられる。 Examples of the hydrophilic compound for introducing a hydrophilic group into the polyisocyanate used in obtaining the self-emulsifying polyisocyanate (B1) include anions such as fatty acid salts, sulfonates, phosphate esters, and sulfate ester salts. Active compounds, primary amine salts, secondary amine salts, tertiary amine salts, quaternary ammonium salts, pyridinium salts and other cationic compounds, anionic compounds, nonionic compounds, amphoteric compounds such as sulfobetaines Can be mentioned.
自己乳化型ポリイソシアネート(B1)を得る際に使用されるポリイソシアネートに、ノニオン性基を導入するためのノニオン性化合物としては、ポリアルキレンエーテルアルコール、ポリアルキレン脂肪酸エステルなどが挙げられる。ポリアルキレンエーテルアルコールを得る際に、開始剤として使用される活性水素含有化合物としては、メタノール、n−ブタノール、シクロヘキサノール、フェノール、エチレングリコール、プロピレングリコール、アニリン、トリメチロールプロパン、グリセリンなどが挙げられる。これらのうち、水分散安定性の観点から、低級アルコールが好ましい。また、ポリアルキレン脂肪酸エステルを得る際に開始剤として使用される脂肪酸としては、酢酸、プロピオン酸、酪酸などが挙げられ、これらのうち、水分散安定性の観点から、低級脂肪酸が好ましい。 Examples of the nonionic compound for introducing a nonionic group into the polyisocyanate used for obtaining the self-emulsifying polyisocyanate (B1) include polyalkylene ether alcohols and polyalkylene fatty acid esters. Examples of the active hydrogen-containing compound used as an initiator when obtaining a polyalkylene ether alcohol include methanol, n-butanol, cyclohexanol, phenol, ethylene glycol, propylene glycol, aniline, trimethylolpropane, and glycerin. . Of these, lower alcohols are preferred from the viewpoint of water dispersion stability. Examples of the fatty acid used as an initiator when obtaining a polyalkylene fatty acid ester include acetic acid, propionic acid, butyric acid and the like, and among these, a lower fatty acid is preferable from the viewpoint of water dispersion stability.
ポリアルキレンエーテルアルコール、ポリアルキレン脂肪酸エステルなどに存在するアルキレンオキサイド鎖は、3〜90個、好ましくは5〜50個である。また、アルキレンオキシド鎖は、すべてエチレンオキシド鎖で構成されていてもよいが、全アルキレンオキシド鎖中に、エチレンオキシドユニットとプロピレンオキシドユニットなどの、他のアルキレンオキシドユニットとで構成されていてもよい。この場合、ポリイソシアネートの水分散性を考慮すると、エチレンオキシドユニットを70重量%以上含むことが好ましい。 The number of alkylene oxide chains present in polyalkylene ether alcohol, polyalkylene fatty acid ester and the like is 3 to 90, preferably 5 to 50. Moreover, all the alkylene oxide chains may be composed of ethylene oxide chains, but may be composed of other alkylene oxide units such as ethylene oxide units and propylene oxide units in the entire alkylene oxide chains. In this case, considering the water dispersibility of the polyisocyanate, it is preferable to contain 70% by weight or more of ethylene oxide units.
自己乳化型ポリイソシアネート(B1)を得る際に使用されるポリイソシアネートに、疎水性基を導入するための高級アルコールとしては、例えば、オクチルアルコール、カプリルアルコール、ノニルアルコール、デシルアルコール、ウンデシルアルコール、ラウリルアルコール、トリデシルアルコール、ミスチリルアルコール、ペンタデシルアルコール、セチルアルコール、シンナミルアルコールなどが挙げられる。 Examples of the higher alcohol for introducing a hydrophobic group into the polyisocyanate used for obtaining the self-emulsifying polyisocyanate (B1) include octyl alcohol, capryl alcohol, nonyl alcohol, decyl alcohol, undecyl alcohol, Examples include lauryl alcohol, tridecyl alcohol, mystyryl alcohol, pentadecyl alcohol, cetyl alcohol, and cinnamyl alcohol.
さらに、自己乳化型ポリイソシアネート(B1)を得る際に使用されるポリイソシアネートに、疎水性基を導入するための水酸基含有エステルの原料としての脂肪酸としては、例えばα−オキシプロピオン酸、オキシコハク酸、ジオキシコハク酸、ε−オキシプロパン−1,2,3−トリカルボン酸、ヒドロキシ酢酸、α−ヒドロキシ酪酸、ヒドロキシステアリン酸、リシノール酸、リシノエライジン酸、リシノステアロール酸、サリチル酸、マンデル酸などが挙げられる。原料としての水酸基含有化合物としては、例えば、メチルアルコール、エチルアルコール、プロピルアルコール、イソプロピルアルコール、ブチルアルコール、ドデシルアルコール、ラウリルアルコールなどが挙げられる。 Furthermore, as the fatty acid as a raw material of the hydroxyl group-containing ester for introducing a hydrophobic group into the polyisocyanate used when obtaining the self-emulsifying polyisocyanate (B1), for example, α-oxypropionic acid, oxysuccinic acid, Dioxysuccinic acid, ε-oxypropane-1,2,3-tricarboxylic acid, hydroxyacetic acid, α-hydroxybutyric acid, hydroxystearic acid, ricinoleic acid, ricinoelaidic acid, ricinostearolic acid, salicylic acid, mandelic acid, etc. It is done. Examples of the hydroxyl group-containing compound as a raw material include methyl alcohol, ethyl alcohol, propyl alcohol, isopropyl alcohol, butyl alcohol, dodecyl alcohol, and lauryl alcohol.
自己乳化型ポリイソシアネート(B1)は、一般には溶剤の不存在下で、50〜130℃の温度範囲で製造されるが、必要に応じて不活性の溶剤、触媒などを使用することもできる。自己乳化型ポリイソシアネートは、分子鎖中に親水性基を導入することにより水分散安定性を向上させることができる。さらに適度な長さの親油性基を親水性基とのバランスを考慮して導入することにより、水中でのイソシアネート基と水との反応を、界面化学的に抑制することができる。また、自己乳化型ポリイソシアネート(B1)には、必要に応じて他の各種樹脂添加物を配合することができる。配合できる樹脂添加物としては、例えば、酸化防止剤、紫外線吸収剤、耐熱性向上剤、着色剤、無機または有機充填剤、可塑剤、滑剤、帯電防止剤、補強材、触媒などが挙げられる。 The self-emulsifying polyisocyanate (B1) is generally produced in the temperature range of 50 to 130 ° C. in the absence of a solvent, but an inert solvent, a catalyst or the like can also be used as necessary. Self-emulsifying polyisocyanates can improve water dispersion stability by introducing hydrophilic groups into the molecular chain. Furthermore, by introducing a lipophilic group having an appropriate length in consideration of the balance with the hydrophilic group, the reaction between the isocyanate group and water in water can be suppressed interfacially. Moreover, other various resin additives can be mix | blended with self-emulsification type polyisocyanate (B1) as needed. Examples of resin additives that can be blended include antioxidants, ultraviolet absorbers, heat resistance improvers, colorants, inorganic or organic fillers, plasticizers, lubricants, antistatic agents, reinforcing materials, and catalysts.
親水性基が導入された自己乳化型ポリイソシアネート(B1)は、水と混合することにより容易に水分散液とすることができる。得られた水分散液は、水に分散した後も比較的安定に存在しているイソシアネート基が、基材表面に存在する活性水素と反応するので、基体との密着性が極めて優れ、耐水性にも優れた塗料、接着剤を得ることができる。また、自己乳化型ポリイソシアネート(B1)を水に分散させた後、かなりの時間が経過しイソシアネート基が消滅した後も、粒径が0.1〜0.3μm程度のポリイソシアネート粒子がエマルジョン状態で安定に存在しているため、このエマルジョンを塗布し常温乾燥、または加熱乾燥して得られる皮膜は、硬く強靱となる。しかし、基材との密着性が重視される場合は、イソシアネート基が消滅しない期間内に使用するのが望ましい。 The self-emulsifying polyisocyanate (B1) introduced with a hydrophilic group can be easily made into an aqueous dispersion by mixing with water. In the resulting aqueous dispersion, the isocyanate groups that exist relatively stably after being dispersed in water react with the active hydrogen present on the surface of the substrate, so that the adhesion to the substrate is extremely excellent, and the water resistance In addition, excellent paints and adhesives can be obtained. Further, after the self-emulsifying type polyisocyanate (B1) is dispersed in water, the polyisocyanate particles having a particle size of about 0.1 to 0.3 μm are in an emulsion state even after a considerable time has passed and the isocyanate group has disappeared. Therefore, the film obtained by applying this emulsion and drying at room temperature or drying by heating becomes hard and tough. However, when importance is attached to the adhesion to the substrate, it is desirable to use it within a period in which the isocyanate group does not disappear.
上記自己乳化型ポリイソシアネート(B1)は、市販品の中から本発明の目的に合ったものを入手することができる。市販されている自己乳化型ポリイソシアネート(B1)であって、本発明において使用し得るものとして、日本ポリウレタン工業社製のアクアネート(商品名)100、110、200、210が挙げられる。 As the self-emulsifying polyisocyanate (B1), a commercially available product that meets the object of the present invention can be obtained. Examples of commercially available self-emulsifying polyisocyanates (B1) that can be used in the present invention include Aquanate (trade names) 100, 110, 200, and 210 manufactured by Nippon Polyurethane Industry Co., Ltd.
イソシアネート基を有する架橋剤(B)としては、自己乳化型ポリイソシアネート(B1)と同様、水性ブロックイソシアネート(B2)も使用できる。水性ブロックイソシアネート(B2)を得る方法としては、(1)ブロックイソシアネートを水中に分散するため、例えば、亜硫酸水素ナトリウムのように親水性の強いブロック剤を用いてブロックイソシアネートを水中に分散する方法、(2)ポリイソシアネートの一部を、親水性基を有する化合物で変性し、水中に分散する方法、など挙げられる。上記(1)のポリイソシアネートの親水性基による変性は、ポリイソシアネートに、例えば、ジメチロールプロピオン酸、ジメチロールブタン酸などのカルボン酸のような親水性基を有するグリコール類や、ポリエチレングリコールのような、親水性ポリオール類を反応させる方法により可能であり、この反応は必要により触媒の存在下に遂行される。 As the crosslinking agent (B) having an isocyanate group, an aqueous blocked isocyanate (B2) can also be used as in the self-emulsifying polyisocyanate (B1). As a method for obtaining the aqueous blocked isocyanate (B2), (1) in order to disperse the blocked isocyanate in water, for example, a method in which the blocked isocyanate is dispersed in water using a highly hydrophilic blocking agent such as sodium bisulfite, (2) A method in which a part of polyisocyanate is modified with a compound having a hydrophilic group and dispersed in water. The modification of the polyisocyanate of the above (1) with a hydrophilic group is carried out by using, for example, glycols having a hydrophilic group such as carboxylic acid such as dimethylolpropionic acid and dimethylolbutanoic acid, and polyethylene glycol. It is possible by a method of reacting hydrophilic polyols, and this reaction is carried out in the presence of a catalyst if necessary.
ブロックイソシアネートの水分散体に用いられるポリイソシアネート類としては、前述の自己乳化型ポリイソシアネートに用いられるものと同様のものが挙げられる。これらのポリイソシアネートは、イソシアネート基がブロック剤でブロックされブロックイソシアネートとなる。ブロック剤としては、例えばマロン酸ジメチル、マロン酸ジエチル、アセト酢酸メチル、アセト酢酸エチル、アセチルアセトンなどの活性メチレン系化合物、ホルムアルデヒド、アセトアルドオキシム、アセトンオキシム、メチルエチルケトオキシム、シクロヘキサノンオキシムなどのオキシム系化合物が挙げられ、これらは単独でも2種以上の併用であってもよい。 Examples of the polyisocyanate used in the aqueous dispersion of blocked isocyanate include the same as those used in the above self-emulsifying polyisocyanate. In these polyisocyanates, isocyanate groups are blocked with a blocking agent to become blocked isocyanates. Examples of the blocking agent include active methylene compounds such as dimethyl malonate, diethyl malonate, methyl acetoacetate, ethyl acetoacetate, and acetylacetone, and oxime compounds such as formaldehyde, acetoaldoxime, acetone oxime, methylethylketoxime, and cyclohexanone oxime. These may be used alone or in combination of two or more.
ブロック化反応は、溶剤の存在下または不存在下で行うことができる。溶剤を使用する場合は、イソシアネート基に対して不活性な溶剤を使用することが必要である。溶剤としては、一般のウレタン化反応に用いられるものが使用できる。また溶剤を使用した場合は、ブロックイソシアネートを水中に分散した後、必要により公知の方法で脱溶剤してもよい。ブロック化反応の際は、触媒として、錫、亜鉛、鉛などの有機金属塩、3級アミンなどを使用することができる。ブロック化反応は、−20〜150℃の温度範囲で行う。イソシアネート基はブロック化されないと、保存中に水や活性水素含有化合物と反応し、架橋に関与することができなくなるので、ポリイソシアネートの全てのイソシアネート基がブロック化されたものが望ましい。 The blocking reaction can be performed in the presence or absence of a solvent. When using a solvent, it is necessary to use a solvent inert to the isocyanate group. As the solvent, those used in general urethanization reactions can be used. Moreover, when using a solvent, after dispersing blocked isocyanate in water, you may remove a solvent by a well-known method if necessary. In the blocking reaction, an organic metal salt such as tin, zinc, or lead, a tertiary amine, or the like can be used as a catalyst. The blocking reaction is performed in the temperature range of -20 to 150 ° C. If the isocyanate group is not blocked, it reacts with water or an active hydrogen-containing compound during storage and cannot participate in crosslinking, so that all isocyanate groups of the polyisocyanate are preferably blocked.
得られたブロックイソシアネートは、必要により乳化剤やポリビニルアルコールなどの保護コロイドを使用して水中に分散させ、水性ブロックイソシアネート(B2)とされる。ブロックイソシアネートの水中への分散の際には、ホモミキサー、ホモジナイザーなどの乳化装置を使用することができる。 The obtained blocked isocyanate is dispersed in water as necessary using a protective colloid such as an emulsifier and polyvinyl alcohol to obtain an aqueous blocked isocyanate (B2). When dispersing the blocked isocyanate in water, an emulsifier such as a homomixer or a homogenizer can be used.
この水性ブロックイソシアネート(B2)は、市販品の中から本発明の目的に合ったものを容易に入手することができる。目的に合った市販品としては、第一工業製薬社製、エラストロン(商品名)H−3、E−37、C−9、F−29、H−38、W−11、MF−25、BN−08、BN−11などが挙げられる。また、水性ブロックイソシアネート(B2)の使用に際しては、反応を促進させるための触媒を使用してもよく、触媒としては、例えば、前記市販品を使用する場合には、第一工業製薬社製、エラストロンキャタリスト(商品名)64を使用できる。 This aqueous blocked isocyanate (B2) can be easily obtained from commercially available products that meet the purpose of the present invention. Commercially available products suitable for the purpose include those manufactured by Daiichi Kogyo Seiyaku Co., Ltd., Elastron (trade names) H-3, E-37, C-9, F-29, H-38, W-11, MF-25, and BN. -08, BN-11 and the like. Further, when using the aqueous blocked isocyanate (B2), a catalyst for promoting the reaction may be used. As the catalyst, for example, when using the commercially available product, Daiichi Kogyo Seiyaku Co., Ltd. Elastron catalyst (trade name) 64 can be used.
前記カルボキシル基を有するウレタン系樹脂エマルジョン(A)に、水性ブロックイソシアネート(B2)を配合した場合には、樹脂成分は水性硬化型樹脂組成物となる。この水性硬化型樹脂組成物は、使用時に加熱することにより、潜在性の水性ブロックイソシアネート(B2)からブロック剤が解離し、イソシアネート基とウレタン系樹脂エマルジョン(A)中のウレタン樹脂のカルボキシル基とで架橋反応が生じ、基体との密着性、耐水性、耐溶剤性などが優れた皮膜(樹脂シートまたは薄膜)を形成する。 When the water-based blocked isocyanate (B2) is blended with the urethane-based resin emulsion (A) having a carboxyl group, the resin component becomes an aqueous curable resin composition. When this aqueous curable resin composition is heated during use, the blocking agent is dissociated from the latent aqueous blocked isocyanate (B2), and the isocyanate group and the carboxyl group of the urethane resin in the urethane resin emulsion (A) A cross-linking reaction occurs to form a film (resin sheet or thin film) having excellent adhesion to the substrate, water resistance, solvent resistance and the like.
本発明に係る樹脂組成物では、前記カルボキシル基を有するウレタン系樹脂エマルジョン(A)に、イソシアネート基を有する架橋剤(B)として、自己乳化型ポリイソシアネート(B1)、または、水性ブロックイソシアネート(B2)を配合することにより、皮膜(樹脂シートまたは薄膜)形成時に、ウレタン系樹脂エマルジョン(A)粒子内または粒子間において、機能的な結合が発現し、皮膜の性能を著しく向上させることができる。架橋剤(B)として、自己乳化型ポリイソシアネート(B1)を使用する場合、使用直前にウレタン系樹脂エマルジョン(A)と混合することにより、自己乳化型ポリイソシアネート(B1)のイソシアネート基が、ウレタン系樹脂エマルジョン(A)の粒子の樹脂中のカルボキシル基と反応するため、皮膜と基材との密着性、耐水性、耐溶剤性などが向上するので、塗料や接着剤の用途に好適である。また、架橋剤(B)として水性ブロックイソシアネート(B2)を使用する場合、使用時に加熱することにより、解離されたイソシアネート基が、ウレタン系樹脂エマルジョン(A)の樹脂粒子中のカルボキシル基と速やかに反応する。 In the resin composition according to the present invention, self-emulsifying polyisocyanate (B1) or aqueous blocked isocyanate (B2) is used as the crosslinking agent (B) having an isocyanate group in the urethane resin emulsion (A) having a carboxyl group. ), When the film (resin sheet or thin film) is formed, functional bonds are expressed in or between the urethane resin emulsion (A) particles, and the performance of the film can be remarkably improved. When the self-emulsifying polyisocyanate (B1) is used as the cross-linking agent (B), the isocyanate group of the self-emulsifying polyisocyanate (B1) is mixed with the urethane resin emulsion (A) immediately before use so that the urethane group Since it reacts with the carboxyl group in the resin of the particles of the resin-based resin emulsion (A), the adhesion between the film and the substrate, water resistance, solvent resistance, etc. are improved, which is suitable for use in paints and adhesives. . Moreover, when using aqueous | water-based blocked isocyanate (B2) as a crosslinking agent (B), the dissociated isocyanate group is rapidly and the carboxyl group in the resin particle of a urethane type resin emulsion (A) by heating at the time of use. react.
ウレタン系樹脂エマルジョン(A)と架橋剤(B)との配合割合は、ウレタン系樹脂エマルジョン(A)の固形分100重量部に対して、架橋剤(B)の配合量を1〜50重量部とするのが好ましい。架橋剤(B)の配合量が1重量部未満では、皮膜の耐水性が悪くなり、50重量部を超えても耐水性の向上効果がなくなり、いずれも好ましくない。 The blending ratio of the urethane resin emulsion (A) and the crosslinking agent (B) is 1 to 50 parts by weight of the crosslinking agent (B) based on 100 parts by weight of the solid content of the urethane resin emulsion (A). Is preferable. When the blending amount of the crosslinking agent (B) is less than 1 part by weight, the water resistance of the film is deteriorated, and even when it exceeds 50 parts by weight, the effect of improving the water resistance is lost.
本発明に係る樹脂組成物において、必須の構成成分であるシランカップリング剤(C){以下、単に成分(C)と略称することがある}は、その分子中に二個以上の異なった反応基を有する有機ケイ素化合物を言う。シランカップリング剤(C)の少なくとも二個の反応基のうち、一個はガラス、金属などの無機質と化学結合する反応基とし、残りの一個は、ウレタン系樹脂エマルジョン(A)の樹脂粒子と結合する反応基とするのが好ましい。無機質である金属表面と結合する反応基は、特に限定されないが、例えば、メトキシ基、エトキシ基などであり、また、有機材料であるウレタン系樹脂エマルジョンの樹脂粒子と結合する反応基には、例えば、グリシド基、アミノ基、アクリル基などである。 In the resin composition according to the present invention, the silane coupling agent (C), which is an essential constituent component (hereinafter sometimes simply referred to as component (C)), has two or more different reactions in the molecule. An organosilicon compound having a group. Of the at least two reactive groups of the silane coupling agent (C), one is a reactive group that chemically bonds to inorganic substances such as glass and metal, and the other is bonded to the resin particles of the urethane resin emulsion (A). It is preferable to make it a reactive group. The reactive group bonded to the inorganic metal surface is not particularly limited. For example, the reactive group bonded to the resin particles of the urethane resin emulsion, which is an organic material, is, for example, a methoxy group or an ethoxy group. A glycid group, an amino group, an acrylic group, and the like.
シランカップリング剤(C)としては、例えば、ビニルトリメトキシシラン、ビニルトリエトキシシラン、N−(2−アミノエチル)−3−アミノプロピルメチルジメトキシシラン、N−(2−アミノエチル)−3−アミノプロピルメチルメトキシシラン、3−アミノプリピルトリエトキシシラン、3−トリエトキシシリル−N−(1,3−ジメチル−ブチリデン)プロピルアミン、N−フェニル−3−アミノプロピルトリメトキシシラン、3−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルメチルジメトキシシラン、γ−グリシドキシプロピルペンタメチルジシロキサン、γ−グリシドキシプロピルメチルジエトキシシラン、γ−グリシドキシプロピルジメチルエトキシシラン、(γ−グリシドキシプロピル)−ビス−(トリメチルシロキシ)メチルシラン、3−−メタクリロキシプロピルトリメトキシシラン、3−メルカプトプロピルトリメトキシシランなどが挙げられる。これらのうち、反応基としてグリシジル基またはアミノ基を有するシラン化合物が好ましい。これらシランカップリング剤は、多数市販されており、容易に入手可能である。 Examples of the silane coupling agent (C) include vinyltrimethoxysilane, vinyltriethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, and N- (2-aminoethyl) -3- Aminopropylmethylmethoxysilane, 3-aminopropyltriethoxysilane, 3-triethoxysilyl-N- (1,3-dimethyl-butylidene) propylamine, N-phenyl-3-aminopropyltrimethoxysilane, 3-glycyl Sidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldimethoxysilane, γ-glycidoxypropylpentamethyldisiloxane, γ-glycidoxypropylmethyldiethoxysilane, γ-glycidoxypropyldimethylethoxysilane, ( γ-glycidoxypropyl) -bis- (Trimethylsiloxy) methylsilane, 3-methacryloxypropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane and the like. Of these, silane compounds having a glycidyl group or an amino group as a reactive group are preferred. Many of these silane coupling agents are commercially available and are readily available.
シランカップリング剤(C)の配合量は、ウレタン系樹脂エマルジョン(A)の固形分100重量部に対し、0.1〜5重量部の範囲で選ぶものとする。配合量が0.1重量部未満では、皮膜(樹脂シートまたは薄膜)密着性、耐水性などの改良効果がなく、5重量部を超えると、コート性が劣り、また皮膜の耐水性の著しい向上効果がないので、いずれも好ましくない。 The compounding quantity of a silane coupling agent (C) shall be chosen in the range of 0.1-5 weight part with respect to 100 weight part of solid content of a urethane type resin emulsion (A). When the blending amount is less than 0.1 parts by weight, there is no improvement effect such as adhesion to the film (resin sheet or thin film) and water resistance, and when it exceeds 5 parts by weight, the coatability is inferior and the water resistance of the film is remarkably improved. Since there is no effect, neither is preferable.
本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物は、塗料、接着剤などの主成分として使用され、特に接着剤としての用途が有用である。本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物を接着剤として使用する場合は、樹脂組成物をそのまま使用できるし、用途・目的によっては各種の添加剤を配合して使用できる。配合できる添加剤としては、顔料、充填剤、骨材、分散剤、分散安定剤、湿潤剤、増粘剤、レベリング剤、レオロジーコントロール剤、消泡剤、可塑剤、造膜助剤、有機溶剤、防腐剤、pH調整剤、防錆剤、酸化防止剤、紫外線吸収剤などが挙げられる。これら添加剤は、単独でも2種以上を併用してもよい。 The resin composition used for the production of the resin sheet laminated metal plate according to the present invention is used as a main component such as a paint or an adhesive, and is particularly useful as an adhesive. When the resin composition used for the production of the resin sheet laminated metal plate according to the present invention is used as an adhesive, the resin composition can be used as it is, and depending on the use and purpose, various additives may be blended and used. it can. Additives that can be blended include pigments, fillers, aggregates, dispersants, dispersion stabilizers, wetting agents, thickeners, leveling agents, rheology control agents, antifoaming agents, plasticizers, film-forming aids, organic solvents , Antiseptics, pH adjusters, rust inhibitors, antioxidants, ultraviolet absorbers and the like. These additives may be used alone or in combination of two or more.
本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物からなる接着剤は、鋼板、メッキ鋼板などの金属板表面へのコート性に優れ、金属板表面との接着性に優れ、皮膜は密着性、耐水性に優れ、さらにポリ塩化ビニル樹脂フィルムなどの有機基材との接着性にも優れることから、樹脂積層鋼板のような樹脂シート積層金属板を製造する際の接着剤としても使用されるものである。 The adhesive comprising the resin composition used for the production of the resin sheet laminated metal plate according to the present invention is excellent in coatability on the surface of a metal plate such as a steel plate or plated steel plate, and excellent in adhesion to the surface of the metal plate, The film has excellent adhesion and water resistance, and also has excellent adhesion to organic substrates such as polyvinyl chloride resin film, so it can be used as an adhesive when producing resin sheet laminated metal plates such as resin laminated steel sheets. Are also used .
本発明が適用できる金属板としては、例えば、鉄板、鋼板、ブリキ板、ティンフリースチール板、黄銅板、アルミニウム板、ステンレススチール板、またはこれらを一成分とする合金製板が挙げられる。これらの金属板の表面には、例えば、クロム酸処理、リン酸処理、クロム酸/リン酸処理、電解クロム酸処理、クロメート処理などの化学処理、または、電気化学的処理、物理的処理などが施されていてもよい。金属板の厚さは、用途により異なるので特に限定されるものではないが、好ましくは0.02〜1mm、より好ましくは0.1〜0.6mmである。 Examples of the metal plate to which the present invention can be applied include an iron plate, a steel plate, a tin plate, a tin-free steel plate, a brass plate, an aluminum plate, a stainless steel plate, or an alloy plate containing these as one component. The surface of these metal plates is subjected to chemical treatment such as chromic acid treatment, phosphoric acid treatment, chromic acid / phosphoric acid treatment, electrolytic chromic acid treatment, chromate treatment, or electrochemical treatment or physical treatment. It may be given. Although the thickness of a metal plate changes with uses, it is not specifically limited, Preferably it is 0.02-1 mm, More preferably, it is 0.1-0.6 mm.
金属板の表面に接着剤を塗布する方式は、特に制限はなく、エアーレス法、スプレイ法、浸漬法、ロールコート法、刷毛塗り法などのいずれであってもよい。金属板に塗布する接着剤の厚さは、1〜10μmの範囲が好適であり、塗布後は80〜120℃の温度で数十秒間の乾燥処理を行う。 The method for applying the adhesive to the surface of the metal plate is not particularly limited, and any of an airless method, a spray method, a dipping method, a roll coating method, a brush coating method, and the like may be used. The thickness of the adhesive applied to the metal plate is preferably in the range of 1 to 10 μm, and after the application, drying treatment is performed at a temperature of 80 to 120 ° C. for several tens of seconds.
樹脂積層鋼板を調整する際に上記金属板に積層される樹脂シートは、特に限定されるものではなく、例えば、ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、ポリブテン、環状ポリオレフィンなどの非晶質ポリオレフィン樹脂、ポリスチレン、ABS樹脂、SBS、SEBSなどのスチレン系樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリメチルメタクリレート、ポリメチルアクリレート、共重合アクリル等の(メタ)アクリレート系樹脂、ポリウレタンなどのウレタン系樹脂、エポキシ樹脂、ポリエチレンテレフタレート、ポリエチレン−2,6−ナフタレートなどのポリエステル系樹脂、ポリアミド6、ポリアミド12、共重合ポリアミドなどのポリアミド系樹脂、ポリビニルアルコール、エチレン−ビニルアルコール共重合体などのポリビニルアルコール系樹脂、ポリイミド樹脂、ポリエーテルイミド樹脂、ポリサルホン樹脂、ポリエーテルサルホン樹脂、ポリアミドイミド樹脂、ポリエーテルエーテルケトン樹脂、ポリカーボネート樹脂、ポリビニルブチラール樹脂、ポリアリレート樹脂、エチレン−四フッ化エチレン共重合体、三フッ化塩化エチレン重合体、四フッ化エチレン−六フッ化プロピレン共重合体、四フッ化エチレン−パーフルオロアルコキシエチレン共重合体、ポリフッ化ビニル、ポリフッ化ビニリデン、パーフルオロエチレン−パーフルオロプロピレン−パーフロロビニルエーテル三元共重合体などのフッ素系樹脂の単独、または、ブレンド物が挙げられる。 The resin sheet laminated on the metal plate when adjusting the resin-laminated steel sheet is not particularly limited. For example, amorphous polyolefin such as polyethylene, polypropylene, ethylene-propylene copolymer, polybutene, and cyclic polyolefin Resin, polystyrene, ABS resin, styrene resin such as SBS, SEBS, polyvinyl chloride resin, polyvinylidene chloride resin, polymethyl methacrylate, polymethyl acrylate, copolymerized acrylic (meth) acrylate resin, polyurethane and other urethanes Resin, epoxy resin, polyester resin such as polyethylene terephthalate, polyethylene-2,6-naphthalate, polyamide resin such as polyamide 6, polyamide 12, copolymer polyamide, polyvinyl alcohol, ethylene-vinyl Polyvinyl alcohol resins such as alcohol copolymers, polyimide resins, polyetherimide resins, polysulfone resins, polyethersulfone resins, polyamideimide resins, polyetheretherketone resins, polycarbonate resins, polyvinyl butyral resins, polyarylate resins, ethylene -Tetrafluoroethylene copolymer, Trifluoroethylene chloride polymer, Tetrafluoroethylene- Hexafluoropropylene copolymer, Tetrafluoroethylene-Perfluoroalkoxyethylene copolymer, Polyvinyl fluoride, Polyvinylidene fluoride , A fluororesin such as perfluoroethylene-perfluoropropylene-perfluorovinyl ether terpolymer, or a blend thereof.
また、上記原料樹脂には、樹脂シートの用途、目的に応じて各種の添加剤を配合することができる。添加剤としては、顔料、充填剤、可塑剤、酸化防止剤、紫外線吸収剤、帯電防止剤、滑剤等が挙げられ、適宜単独或いは組み合わせて使用する。樹脂シートは、一層または二層以上の積層シートが挙げられる。これらの樹脂シートは、未延伸のものでもよいし、一軸方向または軸方向に延伸したものでもよい。樹脂シートの厚さは、5〜500μmの範囲のものが好ましい。さらに、樹脂シートは、公知の表面処理、例えば、コロナ放電処理、プラズマ処理、火炎処理、薬液処理を施したものであってもよく、さらには極性ポリマーコーティング処理、色模様の印刷やエンボス加工等を施したものであってもよい。 Moreover, various additives can be mix | blended with the said raw material resin according to the use and the objective of a resin sheet. Examples of the additive include pigments, fillers, plasticizers, antioxidants, ultraviolet absorbers, antistatic agents, lubricants, and the like, and they are used alone or in combination as appropriate. Examples of the resin sheet include a single layer or a laminated sheet of two or more layers. These resin sheets may be unstretched or may be stretched uniaxially or axially. The resin sheet preferably has a thickness in the range of 5 to 500 μm. Further, the resin sheet may be subjected to a known surface treatment such as corona discharge treatment, plasma treatment, flame treatment, chemical treatment, and further polar polymer coating treatment, color pattern printing, embossing, etc. It may be given.
金属板に樹脂シートを積層する方法は、特に限定されず、従来から知られている方法によって製造できる。従来から知られている方法としては、例えば、(1)押出機先端に、コートハンガーダイ、Tダイ、Iダイなどのダイを装備し、押出機で原料樹脂を溶融させ、ダイからシート(薄膜)状に押出しながら金属板の表面を被覆する、いわゆる押出ラミネート法や、(2)予めシートを調製し、このシートを加熱された金属板上にニップロールなどで圧着する方法、などが挙げられる。 The method for laminating the resin sheet on the metal plate is not particularly limited, and can be produced by a conventionally known method. As a conventionally known method, for example, (1) A die such as a coat hanger die, a T die, or an I die is provided at the tip of the extruder, a raw material resin is melted by the extruder, and a sheet (thin film) A so-called extrusion laminating method in which the surface of the metal plate is coated while being extruded into a shape, and (2) a method in which a sheet is prepared in advance and this sheet is pressure-bonded onto a heated metal plate with a nip roll or the like.
以下、本発明を実施例に基づいて、より詳細に説明するが、本発明は以下に記載した例に限定されるものではない。また、実施例中に「部」とあるのは、重量部の意味である。 EXAMPLES Hereinafter, although this invention is demonstrated in detail based on an Example, this invention is not limited to the example described below. In the examples, “parts” means parts by weight.
[実施例1]
<樹脂組成物エマルジョンの調製>
カルボキシル基を親水性基として有するウレタン系樹脂エマルジョン{成分(A)、三洋化成工業社製、商品名:ユーコートUWS145}100部に対し、架橋剤として自己乳化型ポリイソシアネート{成分(B1)、日本ポリウレタン工業社製、商品名:アクアネート100}15部、および、シランカップリング剤(成分C)として3−グリシドキシプロピルトリメトキシシラン(日本ユニカー社製、A187)0.5部を配合し、樹脂組成物エマルジョンを調製した。
[Example 1]
<Preparation of resin composition emulsion>
Urethane resin emulsion having a carboxyl group as a hydrophilic group {component (A), manufactured by Sanyo Kasei Kogyo Co., Ltd., trade name: U-coat UWS145}, 100 parts of self-emulsifying polyisocyanate {component (B1), Japan Made by Polyurethane Industry Co., Ltd., trade name: Aquanate 100} 15 parts, and 0.5 part of 3-glycidoxypropyltrimethoxysilane (Nihon Unicar Co., A187) as a silane coupling agent (component C) A resin composition emulsion was prepared.
<樹脂積層鋼板の調製>
得られた樹脂組成の液エマルジョンを水で希釈し、固形分濃度を10重量%とし、ロールコート法により厚さ0.45mmの溶融亜鉛メッキ鋼板上に、乾燥後の膜厚みが3μmとなるように塗布した。別途、重合度が1000のポリ塩化ビニル(PVC)100部に対して、DOP換算で可塑剤30部、安定剤、顔料を添加してフィルム化した、厚さが150μmの軟質PVCフィルムを調製した。上記鋼板の塗布を220℃に加熱し、この片面に上記軟質PVCフィルムに、ニップロールで圧着し、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板につき、以下に記載の方法で特性の評価試験を行い、その結果を表―1に示した。
<Preparation of resin laminated steel sheet>
The liquid emulsion of the obtained resin composition is diluted with water to a solid content concentration of 10% by weight, and the film thickness after drying is 3 μm on a hot-dip galvanized steel sheet having a thickness of 0.45 mm by roll coating. It was applied to. Separately, a soft PVC film having a thickness of 150 μm was prepared by adding 30 parts of a plasticizer, a stabilizer, and a pigment in terms of DOP to 100 parts of polyvinyl chloride (PVC) having a polymerization degree of 1000. . The application of the steel sheet was heated to 220 ° C., and the soft PVC film was pressure-bonded to one side of the steel sheet with a nip roll to prepare a PVC resin laminated steel sheet. The obtained PVC resin laminated steel sheet was subjected to a property evaluation test by the method described below, and the results are shown in Table-1.
<樹脂積層鋼板の特性評価方法>
樹脂積層鋼板の各種特性の評価項目と評価方法は、以下のとおりである。
(1)コート性:上記方法で調製した樹脂組成物エマルジョンを、金属板表面にロールコート法により、固形分の厚さが3μmになるように塗布したとき、金属板表面に塗布液のはじきなど目視観察した。外観に異常が認められないものを○、外観に異常が認められるものを×、と判定した。
(2)初期密着性:PVC樹脂積層鋼板から、30mm×120mmの大きさの試験片を切取り、この試験片のPVCフィルム部を20mm幅で、剥離速度50mm/分の条件下で、鋼板表面から180度方向に剥離した。剥離した際の最大荷重を剥離強度とし、剥離強度が40N/20mm幅以上で材料破断するものを○、30N/20mm幅以上で40N/20mm幅に満たないものを△、30N/20mm幅に満たないものを×、と判定した。
<Method for evaluating characteristics of resin-laminated steel sheet>
Evaluation items and evaluation methods for various properties of the resin-laminated steel sheet are as follows.
(1) Coatability: When the resin composition emulsion prepared by the above method is applied on the surface of the metal plate by the roll coating method so that the thickness of the solid content is 3 μm, the coating solution is repelled on the surface of the metal plate. Visual observation was performed. The case where no abnormality was observed in the appearance was judged as “◯”, and the case where abnormality was found in the appearance was judged as “X”.
(2) Initial adhesion: From a PVC resin-laminated steel sheet, a test piece having a size of 30 mm × 120 mm was cut out, and the PVC film part of this test piece was 20 mm wide and peeled at 50 mm / min from the steel sheet surface. Peeled in the direction of 180 degrees. The maximum load at the time of peeling is taken as the peel strength. The peel strength is 40N / 20mm width or more when the material breaks, ○, 30N / 20mm width or more and less than 40N / 20mm width, Δ, 30N / 20mm width Those not present were judged as x.
(3)熱水試験後密着性:上記方法で調製したPVC樹脂積層鋼板から、30mm×120mmの大きさの試験片を切取り、この試験片を沸騰水中に5時間浸漬して引き上げ、この試験片につき上記(2)におけると同様の方法で、PVCフィルムの密着性を評価した。剥離強度が30N/20mm幅以上のものを○、25N/20mm幅以上で30N/20mm幅に満たないものを△、25N/20mm幅に満たないものを×、と判定とした。この熱水試験後密着性に優れていることは、同時に耐水性も優れていることを意味する。
(4)加工後密着性:上記(2)におけると同様の方法で調製したPVC樹脂積層鋼鈑を、30mm×120mmの大きさ試験片に切り取り、この試験片に50mmの間隔で二本の横線を描き、横線の間隔が60mmになるまで一軸方向に延伸した。これを試料とし、上記(2)と同様の方法で、金属板とPVCフィルムとの密着性を評価した。剥離強度が30N/20mm幅以上のものを○、30N/20mm幅に満たないものを×、と判定した。この試験では、PVC樹脂積層鋼鈑を延伸することにより、鋼板とPVCフィルムとの密着性が低下するので、絞り加工時の密着性(剥離性)を評価できる。
(5)総合評価:上記評価項目(1)〜(4)の結果を総合的に勘案して、評価したもの。
(3) Adhesiveness after hot water test: A test piece having a size of 30 mm × 120 mm was cut out from the PVC resin laminated steel sheet prepared by the above method, and this test piece was dipped in boiling water for 5 hours and pulled up. The adhesion of the PVC film was evaluated in the same manner as in (2) above. Peel strength ○ more than a 30 N / 20 mm width, which is less than 30 N / 20 mm width 25 N / 20 mm width or more △, and × those less than 25 N / 20 mm width, and determination. The excellent adhesion after the hot water test means that the water resistance is also excellent.
(4) Adhesion after processing: A PVC resin laminated steel sheet prepared in the same manner as in (2) above was cut into a 30 mm × 120 mm size test piece, and two horizontal lines were cut into this test piece at intervals of 50 mm. Was drawn and uniaxially stretched until the distance between the horizontal lines reached 60 mm. Using this as a sample, the adhesion between the metal plate and the PVC film was evaluated by the same method as in (2) above. Those having a peel strength of 30 N / 20 mm width or more were evaluated as “◯”, and those having a peel strength of less than 30 N / 20 mm width as “X”. In this test, since the adhesiveness between the steel sheet and the PVC film is lowered by stretching the PVC resin laminated steel sheet, the adhesiveness (peelability) at the time of drawing can be evaluated.
(5) Comprehensive evaluation: evaluated by comprehensively considering the results of the evaluation items (1) to (4).
[実施例2]
実施例1に記載の例において、架橋剤{成分(B)}を、水性ブロックイソシアネート(B2)(第一工業製薬社製、商品名:エラストロンBN−08)30部、およびブロックイソシアネート用触媒(第一工業製薬社製、商品名:エラストロンキャタリスト64)0.5部の組合せに代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―1に示した。
[Example 2]
In the example described in Example 1, the crosslinking agent {component (B)} was mixed with 30 parts of an aqueous blocked isocyanate (B2) (manufactured by Daiichi Kogyo Seiyaku Co., Ltd., trade name: Elastron BN-08), and a catalyst for blocked isocyanate ( Daiichi Kogyo Seiyaku Co., Ltd., trade name: Elastron Catalyst 64) A PVC resin laminated steel sheet was prepared in the same procedure as in the same example except that the combination was changed to 0.5 part. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-1.
[比較例1]
実施例1に記載の例において、架橋剤{成分(B)}をメラミン樹脂(住友化学工業社製、商品名:スミマール40WT)5部に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―1に示した。
[Comparative Example 1]
In the example described in Example 1, except that the cross-linking agent {component (B)} was replaced with 5 parts of melamine resin (manufactured by Sumitomo Chemical Co., Ltd., trade name: Sumimar 40WT), the same procedure as in the same example, A PVC resin laminated steel sheet was prepared. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-1.
[比較例2]
実施例1に記載の例において、ウレタン系樹脂エマルジョン{成分(A)}を、カルボキシル基を有するポリエステル樹脂エマルジョン(東洋紡績社製、商品名:バイロナールMD1250)に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―1に示した。
[Comparative Example 2]
In the example described in Example 1, except that the urethane resin emulsion {component (A)} is replaced with a polyester resin emulsion having a carboxyl group (manufactured by Toyobo Co., Ltd., trade name: Vylonal MD1250), A PVC resin laminated steel sheet was created in the same procedure. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-1.
[比較例3]
実施例1に記載の例において、ウレタン系樹脂エマルジョン{成分(A)}を、ポリエチレンオキシドを有するウレタン樹脂エマルジョン(第一工業製薬社製、商品名:スーパーフレックス500)に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―1に示した。
[Comparative Example 3]
In the example described in Example 1, except that the urethane resin emulsion {component (A)} is replaced with a urethane resin emulsion having a polyethylene oxide (trade name: Superflex 500, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.), A PVC resin laminated steel sheet was prepared in the same procedure as in the example. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-1.
[比較例4]
実施例1に記載の例において、シランカップリング剤{成分(C)}を添加しなかった外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―1に示した。
[Comparative Example 4]
In the example described in Example 1, a PVC resin laminated steel sheet was prepared in the same procedure as in the same example except that the silane coupling agent {component (C)} was not added. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-1.
[実施例3]
実施例1に記載の例において、シランカップリング剤{成分(C)}を、γ−アミノプロピルトリエトキシシラン(日本ユニカー社製、銘柄名:A1100)に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―2に示した。
[Example 3]
In the example described in Example 1, except that the silane coupling agent {component (C)} was replaced with γ-aminopropyltriethoxysilane (manufactured by Nihon Unicar Co., Ltd., brand name: A1100), the same as in the example A PVC resin laminated steel sheet was prepared by the procedure described above. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-2.
[実施例4]
実施例1に記載の例において、シランカップリング剤{成分(C)}を、3−メタクリロキシプロピルトリメトキシシラン(信越化学工業社製、銘柄名:KBM503)に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―2に示した。
[Example 4]
In the example described in Example 1, except that the silane coupling agent {component (C)} was replaced with 3-methacryloxypropyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd., brand name: KBM503) A PVC resin laminated steel sheet was prepared in the same procedure as above. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-2.
[実施例5]
実施例1に記載の例において、シランカップリング剤{成分(C)}を、3−メルカプトプロピルトリメトキシシラン(信越化学工業社製、銘柄名:KBM803)に代えた外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―2に示した。
[Example 5]
In the example described in Example 1, except that the silane coupling agent {component (C)} is replaced with 3-mercaptopropyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd., brand name: KBM803) A PVC resin laminated steel sheet was created in the same procedure. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-2.
[実施例6]
実施例1に記載の例において、シランカップリング剤{成分(C)}の添加量を、0.1部に変更した外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―2に示した。
[Example 6]
In the example described in Example 1, a PVC resin laminated steel sheet was prepared in the same procedure as in the same example except that the addition amount of the silane coupling agent {component (C)} was changed to 0.1 part. . The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-2.
[実施例7]
実施例1に記載の例において、シランカップリング剤{成分(C)}の添加量を、1部に変更した外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表―2に示した。
[Example 7]
In the example described in Example 1, a PVC resin laminated steel sheet was prepared in the same procedure as in the same example except that the addition amount of the silane coupling agent {component (C)} was changed to 1 part. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table-2.
[比較例5]
実施例1に記載の例において、シランカップリング剤{成分(C)}の添加量の0.5部を8部に変更した外は、同例におけると同様の手順で、PVC樹脂積層鋼板を作成した。得られたPVC樹脂積層鋼板を上記方法で評価し、その結果を表2に示した。
[Comparative Example 5]
In the example described in Example 1, except that 0.5 part of the addition amount of the silane coupling agent {component (C)} was changed to 8 parts, the PVC resin laminated steel sheet was prepared in the same procedure as in the example. Created. The obtained PVC resin laminated steel sheet was evaluated by the above method, and the results are shown in Table 2.
表―1および表―2より、次のことが明らかである。
(1)カルボキシル基を有するウレタン系樹脂エマルジョン(A)に自己乳化型ポリイソシアネート(B1)または水性ブロックイソシアネート(B2)を加え、シランカップリング剤(C)として3−グリシドキシプロピルトリメトキシシランを、請求項1で規定する範囲で配合して樹脂組成物を接着剤とし、軟質PVCフィルムと鋼板との接着に使用したときは、得られるPVC積層鋼板は、初期密着性、熱水試験後密着性(耐水性)、加工後密着性などに優れている(実施例1、実施例2参照)。
(2)それに対し、成分(C)を請求項1に規定していないメラミン系化合物に変えた場合は、PVC樹脂積層鋼板は、初期密着性が低く、熱水試験後密着性(耐水性)、加工後密着性に劣る(比較例1参照)。
(3)カルボキシル基を有する樹脂エマルジョンであっても、ウレタン系樹脂エマルジョンでないカルボキシル基を有するポリエステル樹脂エマルジョンであると、PVC樹脂積層鋼板は、初期密着性は良いもの、熱水試験後密着性(耐水性)、加工後密着性に劣る(比較例2参照)。
(4)ウレタン系樹脂エマルジョンであっても、カルボキシル基でないポリエチレンオキシドを有するウレタン系樹脂エマルジョンであると、PVC樹脂積層鋼板は、初期密着性が低く、熱水試験後密着性(耐水性)、加工後密着性に劣る(比較例3参照)。
From Table-1 and Table-2, the following is clear.
(1) Self-emulsifying polyisocyanate (B1) or aqueous blocked isocyanate (B2) is added to urethane resin emulsion (A) having a carboxyl group, and 3-glycidoxypropyltrimethoxysilane is used as silane coupling agent (C). When the resin composition is used as an adhesive by adhering within the range specified in claim 1 and is used for adhesion between the soft PVC film and the steel sheet, the obtained PVC laminated steel sheet is subjected to initial adhesion and hot water test. Excellent adhesion (water resistance), adhesion after processing, etc. (see Examples 1 and 2).
(2) On the other hand, when the component (C) is changed to a melamine compound not specified in claim 1, the PVC resin laminated steel sheet has low initial adhesion and adhesion after a hot water test (water resistance). Inferior in adhesion after processing (see Comparative Example 1).
(3) Even if it is a resin emulsion having a carboxyl group, if it is a polyester resin emulsion having a carboxyl group that is not a urethane resin emulsion, the PVC resin-laminated steel sheet has good initial adhesion, and adhesion after a hot water test ( Water resistance) and poor adhesion after processing (see Comparative Example 2).
(4) Even if it is a urethane-based resin emulsion, if it is a urethane-based resin emulsion having a polyethylene oxide that is not a carboxyl group, the PVC resin-laminated steel sheet has low initial adhesion, and adhesion after hot water testing (water resistance), Poor adhesion after processing (see Comparative Example 3).
(5)カルボキシル基を有するウレタン系樹脂エマルジョン(A)と自己乳化型ポリイソシアネート(B1)を使用しても、シランカップリング剤(C)を添加しないときには、PVC樹脂積層鋼板は、初期密着性、加工後密着性に優れるものの、熱水試験後密着性(耐水性)に劣る(比較例4参照)。
(6)実施例1におけるシランカップリング剤(C)として、アミノ基を有するシランカップリング剤を使用しても、PVC樹脂積層鋼板は、実施例1におけるものと同様に、初期密着性、熱水試験後密着性(耐水性)、加工後密着性に優れたものとなる(実施例3参照)。
(7)シランカップリング剤(C)であっても、官能基がメタクリロキシ、メルカプト基であるものは、グリシジル基を有するシランカップリング剤を使用した実施例1、アミノ基を有するシランカップリング剤を使用した実施例3ものに比較し、熱水試験後密着性、耐水性にやや劣るが、シランカップリング剤を添加しない比較例4のものと比較すると、熱水試験後密着性は改良される(実施例4、実施例5参照)。
(8)カルボキシル基を有するウレタン系樹脂エマルジョン(A)と、自己乳化型ポリイソシアネート(B1)とを含む樹脂成分に、シランカップリング剤(C)を請求項1で規定する範囲内で配合すると、PVC樹脂積層鋼板は、初期密着性、熱水試験後密着性、加工後密着性、耐水性に優れる(実施例6、実施例7参照)。
(9)しかしながら、シランカップリング剤(C)を請求項1で規定する範囲を超えて配合すると、PVC樹脂積層鋼板を作成するときのコート性が著しく劣るものとなり、またPVC樹脂積層鋼板は、剥離強度が高くなるにも拘わらず、コート性が不良で、熱水試験後密着性が劣る(比較例5参照)。
(5) Even when the urethane-based resin emulsion (A) having a carboxyl group and the self-emulsifying type polyisocyanate (B1) are used, when the silane coupling agent (C) is not added, the PVC resin laminated steel sheet has an initial adhesiveness. Although excellent in adhesion after processing, it is inferior in adhesion (water resistance) after a hot water test (see Comparative Example 4).
(6) Even if a silane coupling agent having an amino group is used as the silane coupling agent (C) in Example 1, the PVC resin laminated steel sheet has the same initial adhesiveness and heat as in Example 1. The adhesion after water test (water resistance) and the adhesion after processing are excellent (see Example 3).
(7) Even if it is a silane coupling agent (C), those in which the functional groups are methacryloxy and mercapto groups are those in Example 1 using a silane coupling agent having a glycidyl group, and a silane coupling agent having an amino group Compared with the one in Example 3 using the same, the adhesion after the hot water test and water resistance are slightly inferior, but the adhesion after the hot water test is improved as compared with the one in Comparative Example 4 in which no silane coupling agent is added. (See Example 4 and Example 5).
(8) When the silane coupling agent (C) is blended within the range specified in claim 1 to the resin component containing the urethane-based resin emulsion (A) having a carboxyl group and the self-emulsifying polyisocyanate (B1). The PVC resin laminated steel sheet is excellent in initial adhesion, adhesion after a hot water test, adhesion after processing, and water resistance (see Examples 6 and 7).
(9) However, when the silane coupling agent (C) is blended beyond the range specified in claim 1, the coatability when creating a PVC resin laminated steel sheet is remarkably inferior. Despite the high peel strength, the coatability is poor and the adhesion after the hot water test is poor (see Comparative Example 5).
本発明に係る樹脂シート積層金属板製造用に使用される樹脂組成物からなる接着剤は、コート性に優れ、金属板との密着性、耐水性および耐薬品性に優れた皮膜を形成し得ることから、無溶剤型の塗料、接着剤としての用途に好適である。本発明に係る樹脂シート積層金属板は、金属板と樹脂シートが強固に接着されており、耐水性(熱水試験後密着性)、加工性(加工後密着性)に優れているので、樹脂シート積層金属板の各種の用途、特に意匠性を有する樹脂積層金属板、または水周りの部品製造用に好適である。 The adhesive comprising the resin composition used for producing the resin sheet laminated metal plate according to the present invention is excellent in coatability and can form a film excellent in adhesion to the metal plate , water resistance and chemical resistance. Therefore, it is suitable for use as a solventless paint or adhesive. In the resin sheet laminated metal plate according to the present invention, the metal plate and the resin sheet are firmly bonded, and are excellent in water resistance (adhesion after hot water test) and workability (adhesion after processing). It is suitable for various uses of sheet-laminated metal plates, particularly for resin-laminated metal plates having design properties, or for manufacturing parts around water.
Claims (8)
熱水試験後密着性:樹脂シート積層金属板を30mm×120mmの大きさの試験片を切取り、この試験片を沸騰水中に5時間浸漬して引き上げ、この試験片の樹脂シート部を20mm幅で、剥離速度50mm/分の条件下で、鋼板表面から180度方向に剥離した際の最大荷重を剥離強度とする。 2. The resin sheet laminated metal plate according to claim 1, wherein the resin sheet laminated metal plate has a peel strength of 25 N / 20 mm width or more according to evaluation of adhesion after a hot water test described below.
Adhesion after hot water test: A test piece of 30 mm × 120 mm in size was cut out from the resin sheet laminated metal plate, and this test piece was immersed in boiling water for 5 hours and pulled up. The resin sheet portion of this test piece was 20 mm wide. The maximum load when peeling from the steel sheet surface in the direction of 180 degrees under the peeling speed of 50 mm / min is defined as peeling strength.
加工後密着性:樹脂シート積層金属板を30mm×120mmの大きさ試験片に切り取り、この試験片に50mmの間隔で二本の横線を描き、横線の間隔が60mmになるまで一軸方向に延伸し、この試験片の樹脂シート部を20mm幅で、剥離速度50mm/分の条件下で、鋼板表面から180度方向に剥離した際の最大荷重を剥離強度とする。 The resin sheet laminated metal plate according to claim 1 or 2, wherein the resin sheet laminated metal plate has a peeling strength of 30 N / 20 mm width or more according to the following post-processing adhesion evaluation.
Adhesion after processing: Cut the resin sheet laminated metal plate into a 30 mm x 120 mm test piece, draw two horizontal lines at an interval of 50 mm on this test piece, and stretch it uniaxially until the distance between the horizontal lines reaches 60 mm The maximum load when the resin sheet portion of the test piece is 20 mm wide and peeled from the steel sheet surface in the direction of 180 degrees under the condition of a peeling speed of 50 mm / min is defined as the peel strength.
初期密着性:樹脂シート積層金属板を30mm×120mmの大きさ試験片に切り取り、この試験片の樹脂シート部を20mm幅で、剥離速度50mm/分の条件下で、鋼板表面から180度方向に剥離した際の最大荷重を剥離強度とする。 The resin sheet laminated metal plate according to any one of claims 1 to 3, wherein the resin sheet laminated metal plate has a peel strength of 40 N / 20 mm width or more according to the following evaluation of initial adhesion.
Initial adhesion: The resin sheet laminated metal plate was cut into a 30 mm × 120 mm size test piece, and the resin sheet portion of the test piece was 20 mm wide and peeled at a peel rate of 50 mm / min. The maximum load at the time of peeling is defined as peeling strength.