JP4525900B2 - Manufacturing method of optical element molding die and optical element molding die - Google Patents
Manufacturing method of optical element molding die and optical element molding die Download PDFInfo
- Publication number
- JP4525900B2 JP4525900B2 JP2004101937A JP2004101937A JP4525900B2 JP 4525900 B2 JP4525900 B2 JP 4525900B2 JP 2004101937 A JP2004101937 A JP 2004101937A JP 2004101937 A JP2004101937 A JP 2004101937A JP 4525900 B2 JP4525900 B2 JP 4525900B2
- Authority
- JP
- Japan
- Prior art keywords
- molding die
- optical
- amorphous alloy
- optical element
- supercooled liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、過冷却液体域を有する非晶質合金を用いて光学素子用成形金型を製造する製造方法、及びその製造方法により製造された光学素子用成形金型、並びにその光学素子用成型金型により成形された光学素子に関する。 The present invention relates to a manufacturing method for manufacturing a molding die for optical elements using an amorphous alloy having a supercooled liquid region, a molding die for optical elements manufactured by the manufacturing method, and molding for the optical elements. The present invention relates to an optical element molded by a mold.
従来から一般的に行われてきたプラスチック光学素子の成形用金型の製作手法によれば、例えば鋼材やステンレス鋼などでブランク(一次加工品)を作っておき、その上に無電解ニッケルメッキとよばれる化学メッキにより、アモルファス状のニッケルと燐の合金を100μmほどの厚みに鍍膜し、このメッキ層を超精密加工機によりダイアモンド工具で切削加工して、光学素子の光学面を成形するための高精度な光学面転写面を得ていた。 According to the conventional method of manufacturing a plastic optical element molding die, for example, a blank (primary processed product) is made of steel, stainless steel, etc., and electroless nickel plating is formed thereon. An amorphous nickel-phosphorus alloy is coated to a thickness of about 100 μm by chemical plating, and this plated layer is cut with a diamond tool by an ultra-precision machine to form the optical surface of the optical element. A highly accurate optical surface transfer surface was obtained.
かかる従来技術の手法によれば、基本的に機械加工により部品形状を創成するため、加工機の運動精度近くまで容易に部品精度が高められる反面、製作工程に機械加工と化学メッキ処理が混在し煩雑で納期がかかること、メッキ層の厚みを考慮してブランク(一次加工品)を作製する必要があること、必ずしもメッキ処理が安定している訳ではなく、ブランクの組成の偏りや汚れ具合によってメッキ層の付着強度がばらついたり、ピットと呼ばれるピンホール状の欠陥が生じたりすること、メッキ層の厚みの中で光学面転写面を創成しなければならないため、光学面転写面を再加工するときなどはメッキ厚みに余裕が無く加工不可能となる場合があること等々の不具合が生じていた。 According to such a conventional technique, the part shape is basically created by machining, so that the part accuracy can be easily increased to near the motion accuracy of the processing machine, but the machining process and the chemical plating process are mixed. It is complicated and takes delivery time, it is necessary to prepare a blank (primary processed product) in consideration of the thickness of the plating layer, the plating process is not necessarily stable, and it depends on the blank composition and the degree of dirt Rework the optical surface transfer surface because the adhesion strength of the plating layer varies, pinhole-like defects called pits occur, and the optical surface transfer surface must be created within the thickness of the plating layer. In some cases, there was a problem that the plating thickness could not be processed because it could not be processed.
更に、従来技術によれば、多量に光学面転写面をダイヤモンド切削加工する必要があるが、かかる場合、工具の切れ刃の状態や加工条件、加工環境温度の変化などの影響を受けて、切削加工し仕上げた光学面転写面の形状が微妙にバラツくという問題もあった。この光学面転写面の加工バラツキは、素材の被削性の悪さに起因するものであり、一般的には100nm程度の光学面形状誤差を発生し、非常に慎重に加工した場合でも50nm程度の形状誤差が残るが、これが多量に同一形状の光学面転写面を創成する際の加工精度限界となっている。 Furthermore, according to the prior art, it is necessary to perform a large amount of diamond cutting on the optical surface transfer surface. In such a case, the cutting is affected by the state of the cutting edge of the tool, processing conditions, changes in the processing environment temperature, etc. There was also a problem that the shape of the processed and finished optical surface transfer surface varied slightly. This variation in the processing of the optical surface transfer surface is due to the poor machinability of the material. Generally, an optical surface shape error of about 100 nm occurs, and even when processed very carefully, it is about 50 nm. Although a shape error remains, this is a processing accuracy limit when a large amount of the optical surface transfer surface having the same shape is created.
また、近年、光学面に輪帯状の回折溝(回折輪帯)を施して色収差を効率よく補正する光学素子が、光情報記録分野などで実用化され、大量に生産されている。その光学材料としては、プラスチックやガラスが使われているが、赤外光学系などではZnSeなどの結晶材料も用いられている。この様な光学素子は、成形により大量に且つ効率的に生産することができるが、その成形の際に、光学素子用成形金型で、光学素子の光学面における微細な回折溝をいかに高精度に効率よく製作するかが、極めて重要な課題となる。 In recent years, optical elements that provide an optical surface with an annular diffraction groove (diffraction annular zone) to efficiently correct chromatic aberration have been put to practical use in the optical information recording field and are produced in large quantities. As the optical material, plastic or glass is used, but in an infrared optical system or the like, a crystal material such as ZnSe is also used. Such optical elements can be produced in large quantities and efficiently by molding, but at the time of molding, how precise the fine diffraction grooves on the optical surface of the optical element can be with a molding die for optical elements. The most important issue is how to manufacture them efficiently.
例えば、ダイアモンド切削により、光学素子用成形金型の光学面転写面上に回折溝などの光学機能を有する微細なパターンを創成する揚合は、刃先の鋭さが回折溝形状の正確さを左右し、光学素子の光学面として転写された時に回折効率に大きな影響を与える。 For example, when creating a fine pattern with an optical function such as a diffraction groove on the optical surface transfer surface of a molding die for optical elements by diamond cutting, the sharpness of the blade edge affects the accuracy of the shape of the diffraction groove. When it is transferred as the optical surface of the optical element, the diffraction efficiency is greatly affected.
従って、回折輪帯の回折効率を低下させないためには、刃先の大きさを十分小さくせねばならず、そうすると、小さな刃先部分に切削抵抗が集中してかかるので切り込み量を小さくせねばならず、光学面全体を均一に切削除去するまでに加工回数が多くなる。また、刃先の小さなカッターマークによる光学面の表面粗さの劣化を防ぐためにも工具送り速度を遅くせねばならず、1回の光学面転写面加工時間も長くなる。その結果、回折溝を有する光学素子の成形用金型の切削加工においては、切削長が増大するので工具刃先の損耗が大きくなり、工具交換が頻繁となる。つまり、従来のダイアモンド切削により微細な形状を有する光学面転写面を加工する場合には、工具の寿命が極端に短くなり、しかも一つの光学面転写面を加工する時間も増大するので、頻繁に工具を交換せねばならないため加工効率が非常に低下し、光学素子用成形金型の生産性が低下してコストの急激な増大を招いていた。そのため、特にダイアモンド切削により微細な形状を表面に有する光学面転写面を仕上げる場合には、無電解ニッケルメッキ工程を含まない簡素で納期の短い金型製作手法が望まれる。 Therefore, in order not to reduce the diffraction efficiency of the diffraction ring zone, the size of the blade edge must be made sufficiently small, and then the cutting resistance is concentrated on the small blade edge part, so the cutting amount must be reduced, The number of machining operations increases until the entire optical surface is uniformly removed by cutting. Further, in order to prevent the surface roughness of the optical surface from being deteriorated due to the cutter mark having a small blade edge, the tool feed speed must be slowed down, and the processing time for one optical surface transfer surface is increased. As a result, in the cutting of the molding die for the optical element having the diffraction groove, the cutting length increases, so that the wear of the tool edge increases and the tool is frequently changed. In other words, when processing an optical surface transfer surface having a fine shape by conventional diamond cutting, the tool life is extremely shortened, and the time for processing one optical surface transfer surface also increases. Since the tool has to be changed, the processing efficiency is greatly reduced, the productivity of the optical element molding die is lowered, and the cost is rapidly increased. Therefore, in particular, when finishing an optical surface transfer surface having a fine shape on the surface by diamond cutting, a simple and short delivery method for manufacturing a die that does not include an electroless nickel plating process is desired.
加えて、近年、使用する光源の波長の数倍からそれよりも小さな微細構造を光学面に施して、新たな光学的機能を光学素子に付加することが試みられている。例えば、成形レンズの屈折による通常の集光機能とその時に副作用として発生する正の分散を、その非球面光学面の表面に回折溝を施すことで得られる回折による大きな負の分散を利用してうち消し、本来、屈折だけでは不可能な色消し機能を単玉光学素子に付加することが、DVD/CD互換の光ディスク用ピックアップ対物レンズで実用化されている。これは、光学素子を透過する光の波長の数10倍の大きさの回折溝による回折作用を利用したもので、このように波長より十分大きな構造による回折作用を扱う領域は、スカラー領域と呼ばれている。 In addition, in recent years, an attempt has been made to add a new optical function to an optical element by applying a fine structure smaller than several times the wavelength of a light source to be used to the optical surface. For example, the normal focusing function due to refraction of a molded lens and the positive dispersion that occurs as a side effect at that time are utilized by utilizing the large negative dispersion due to diffraction obtained by forming a diffraction groove on the surface of the aspheric optical surface. Of these, it has been put to practical use with a pickup objective lens for an optical disk compatible with DVD / CD to add an achromatic function, which is essentially impossible with refraction alone, to a single optical element. This utilizes the diffractive action of a diffraction groove having a size several tens of times the wavelength of light transmitted through the optical element, and the region that handles the diffractive action by a structure sufficiently larger than the wavelength is called a scalar region. It is.
一方、光学素子を透過する光の波長の数分の一という微細な間隔で、円錐形状の突起を光学面の表面に密集させて形成させることで、光の反射抑制機能を発揮できることが判っている。即ち、光波が光学素子に入射する際の空気との境界面での屈折率変化を、従来の光学素子のように1から媒体屈折率まで瞬間的に変化させるのではなく、微細な間隔で並んだ突起の円錐形状によって緩やかに変化させ、それにより光の反射を抑制することができるのである。このような突起を形成した光学面は、いわゆる蛾の眼(moth eye)と呼ばれる微細構造で、光の波長よりも微細な構造体が波長よりも短い周期で並ぶことにより、もはや個々の構造が回折せずに光波に対して平均的な屈折率として働くものである。このような領域を等価屈折率領域と一般に呼んでいる。このような等価屈折率領域に関しては、例えば電子情報通信学会論文誌C Vol.J83−C No.3 pp.173−181 2000年3月に述べられている。 On the other hand, it has been found that the light reflection suppressing function can be exhibited by forming the conical projections densely on the surface of the optical surface at a minute interval of a fraction of the wavelength of the light transmitted through the optical element. Yes. That is, the refractive index change at the interface with the air when the light wave enters the optical element is not instantaneously changed from 1 to the medium refractive index as in the conventional optical element, but is arranged at a fine interval. By changing the shape of the protrusions gradually, the reflection of light can be suppressed. The optical surface on which such protrusions are formed has a fine structure called a so-called “eyes”, and individual structures can no longer be obtained by arranging structures finer than the wavelength of light with a period shorter than the wavelength. It works as an average refractive index for light waves without being diffracted. Such a region is generally called an equivalent refractive index region. Regarding such an equivalent refractive index region, see, for example, IEICE Transactions C Vol. J83-C No. 3 pp. 173-181, described in March 2000.
等価屈折率領域の微細構造によれば、従来の反射防止コートに比べて反射防止効果の角度依存性や波長依存性を少なくしながら大きな反射防止効果を得られるが、プラスチック成形等によれば、光学面と微細構造を同時に創成できることから、レンズ機能と反射防止機能が同時に得られて、従来のように成形後に反射防止コート処理をするといった後加工が不要となる等の生産上のメリットも大きいと考えられ注目されている。さらに、このような等価屈折率領域の微細構造を光学面に対して方向性を持つように配すると、強い光学異方性を光学面に持たせることもでき、従来、水晶などの結晶を削りだして製作していた複屈折光学素子を成形によって得ることができ、また、屈折や反射光学素子と組み合わせて新たな光学的機能を付加することができる。この場合の光学異方性は、構造複屈折と呼ばれている。 According to the microstructure of the equivalent refractive index region, it is possible to obtain a large antireflection effect while reducing the angle dependency and wavelength dependency of the antireflection effect as compared with the conventional antireflection coating, but according to plastic molding or the like, Since the optical surface and fine structure can be created at the same time, the lens function and the antireflection function can be obtained at the same time, and there is also a great merit in production such that post-processing such as antireflection coating treatment after molding is unnecessary as in the past. It is considered and is attracting attention. Furthermore, if such a fine structure of the equivalent refractive index region is arranged so as to have directionality with respect to the optical surface, it is possible to give the optical surface strong optical anisotropy. Thus, the birefringent optical element produced can be obtained by molding, and a new optical function can be added in combination with a refractive or reflective optical element. The optical anisotropy in this case is called structural birefringence.
上述したスカラー領域と等価屈折率領域の間には、回折効率が入射条件のわずかな違いにより急激に変化する共鳴領域がある。例えば、回折輪帯の溝幅を狭くしていくと、波長の数倍程度で急激に回折効率が減少し、また増加するという現象(アノマリー)が発生する。この領域の性質を利用して、特定の波長のみを反射する導波モード共鳴格子フィルターを微細構造で実現して、通常の干渉フィルターと同等の効果をより角度依存性を少なくして実現できる。 Between the above-described scalar region and equivalent refractive index region, there is a resonance region in which the diffraction efficiency changes rapidly due to a slight difference in incident conditions. For example, when the groove width of the diffraction ring zone is narrowed, a phenomenon (anomaly) occurs in which the diffraction efficiency rapidly decreases and increases by several times the wavelength. By utilizing the characteristics of this region, a waveguide mode resonance grating filter that reflects only a specific wavelength can be realized with a fine structure, and the same effect as a normal interference filter can be realized with less angular dependence.
ところで、スカラー領域や、等価屈折率領域や、共鳴領或を利用して光学素子を形成しようとする場合、その光学面に微細な突起(又はくぼみ)を形成する必要がある。このような微細な突起(又はくぼみ)を備えた光学素子を大量生産するには、一般的にはプラスチックを素材として成形を行うことが適しているといえるが、かかる場合、微細な突起(又はくぼみ)に対応したくぼみ(又は突起)を備えた光学面転写面を、光学素子の成形用金型に設ける必要がある。 By the way, when an optical element is formed using a scalar region, an equivalent refractive index region, a resonance region, or the like, it is necessary to form fine protrusions (or depressions) on the optical surface. In order to mass-produce optical elements having such fine protrusions (or depressions), it can be said that it is generally suitable to perform molding using plastic as a raw material. It is necessary to provide an optical surface transfer surface provided with a recess (or protrusion) corresponding to the recess) in the molding die for the optical element.
しかるに、上述したような等価屈折領域や共鳴領域の突起(又はくぼみ)に関しては、数十乃至数百ナノメートルの間隔で突起(又はくぼみ)を形成しなくてはならず、切削加工を含む機械的加工では極めて困難である。 However, with respect to the protrusions (or depressions) in the equivalent refractive region and the resonance region as described above, protrusions (or depressions) must be formed at intervals of several tens to several hundreds of nanometers. It is extremely difficult to machine.
かかる問題に鑑みて、本出願人は、特許文献1において、基体に過冷却液体域を有する非晶質合金を付着させ、かかる非晶質合金を加工することで、光学素子の光学面を成形するための光学面転写面を形成する製造方法について開示している。かかる過冷却液体域を有する非晶質合金は、加工容易性に優れていることから、例えば光学面転写面に微細構造を形成する必要がある場合にも、これを容易に行うことができる。
しかるに、特許文献1においては、基体に対して過冷却液体域を有する非晶質合金を、どのようにして適切な膜厚で成膜させるかについて、具体的に言及されていない。即ち、通常は過冷却液体域を有する非晶質合金をバルク材から切り出して、基体に接合させた後、かかる過冷却液体域を有する非晶質合金を加工することになるが、過冷却液体域を有する非晶質合金は高価なものであるため、加工によって除去される部分が多いと収率が悪化し、光学素子用成形金型の製造コストを増大させる恐れがある。又、スパッタ等によって、過冷却液体域を有する非晶質合金の粒子を飛散させて、基体の平面上に膜層を形成できたとしても、光学素子の非球面形状分は、切削加工等によって過冷却液体域を有する非晶質合金を除去しなくてはならず、同様に製造コストが増大すると共に、加工の手間もかかる。
However,
本発明は、かかる従来技術の問題点に鑑みてなされたものであり、低コストであり取り扱いが容易であるにも関わらず、切削性に優れ、寸法精度を高めることができる光学素子用成形金型の製造方法、及びそれにより製造される光学素子用成型金型並びにそれにより成形される光学素子を提供することを目的とする。 The present invention has been made in view of the problems of the prior art, and is a mold for optical elements that is excellent in machinability and can improve dimensional accuracy despite its low cost and easy handling. An object of the present invention is to provide a mold manufacturing method, a molding die for optical elements manufactured thereby, and an optical element molded thereby.
請求項1に記載の光学素子用成形金型の製造方法は、光学素子の光学面を成形転写するための成形転写面を有する光学素子用成形金型の製造方法において、前記光学素子用成形金型の基体に、前記成形転写面が凹形状の場合には、前記成形転写面よりも曲率半径が大きい形状でベース面を形成し、前記成形転写面が凸形状の場合には、前記成形転写面よりも曲率半径が小さい形状でベース面を形成する工程と、前記ベース面に対し、隔置配置された素材から、その材料粒子を飛散させて、過冷却液体領域を有する非晶質合金を堆積させることで膜層を形成する工程と、前記膜層に所定の加工を施すことで前記成形転写面を得る工程と、を有し、前記所定の加工とは、光学素子の光学面に対応した母型を加熱して前記ベース面に形成された膜層に押しつける加熱プレス成形か、ダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工か、或いは、光学素子の光学面に対応した母型を加熱して前記ベース面に押しつける加熱プレス成形及びダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工であることを特徴とする。
The method for producing a molding die for an optical element according to
従来の製法では,無電解Niメッキを基体のベース面に付着させ、そこに成形転写面を形成していたが、必要なメッキ膜の厚さを得るためには、数週間という非常に長い時間が必要となり、1つの金型を形成するために相当に手間がかかっていた。 In the conventional manufacturing method, the electroless Ni plating is adhered to the base surface of the substrate and the molding transfer surface is formed thereon. However, in order to obtain the required plating film thickness, a very long time of several weeks is required. Is necessary, and it takes considerable time to form one mold.
これに対し、本発明のように,光学素子に光学面に対応した前記ベース面に対し、隔置配置された素材から、その材料粒子を飛散させて、過冷却液体領域を有する非晶質合金を堆積させる成膜工程(特にスパッタや蒸着法等)で膜層を形成した場合、非常に短時間で成膜できるため、メッキ製法に比較して、金型の製造時間を大幅に短縮できる。ところが、スパッタなどの成膜工程の場合、ターゲットより金属粒子が放射状に飛散するので、前記ベース面の形状によっては、過冷却液体領域を有する非晶質合金が堆積しやすい部位と、堆積しにくい部位とが生ずる。具体的には、金属粒子の飛散方向に対して、前記金型の面が傾いている部分には堆積しにくい傾向がある。従って堆積しやすい部位の膜厚は厚くなり、堆積しにくい部位の膜厚は薄くなるため、結果として前記ベース面上の膜厚が不均一となる。その膜層を、後工程で切削・研削等により削ることで成形転写面を得ようとした場合,膜厚が薄いと,加工可能な回数が減少することとなる。一般的に,光学素子用成形金型の成形転写面を加工するには,数回の加工を行って成形転写面を創成するため,加工可能な回数が少なくなると,1〜2回の加工で成形転写面を仕上げなければならず,加工自体の難易度があがるか、もしくは創成不可能となる。 On the other hand, as in the present invention, an amorphous alloy having a supercooled liquid region by scattering the material particles from a material spaced from the base surface corresponding to the optical surface of the optical element. When a film layer is formed in a film forming process (particularly sputtering, vapor deposition, etc.) for depositing metal, the film can be formed in a very short time, so that the manufacturing time of the mold can be greatly reduced as compared with the plating method. However, in the case of a film forming process such as sputtering, metal particles are scattered radially from the target. Therefore, depending on the shape of the base surface, an amorphous alloy having a supercooled liquid region is likely to be deposited, and is difficult to deposit. Part. Specifically, it tends to be difficult to deposit in a portion where the surface of the mold is inclined with respect to the scattering direction of the metal particles. Accordingly, the film thickness of the portion that is easy to deposit becomes thick, and the film thickness of the portion that is difficult to deposit becomes thin. As a result, the film thickness on the base surface becomes non-uniform. In the case where an attempt is made to obtain a molded transfer surface by cutting the film layer by cutting, grinding, or the like in a later step, if the film thickness is thin, the number of times that the film can be processed is reduced. Generally, in order to process a molding transfer surface of a molding die for optical elements, a molding transfer surface is created by performing several times of processing. The molding transfer surface must be finished, and the difficulty of processing itself increases or cannot be created.
かかる課題を解決するために、本発明においては、前記成形転写面が凹形状の場合には、前記成形転写面よりも曲率半径が大きい形状でベース面を予め形成し、前記成形転写面が凸形状の場合には、前記成形転写面よりも曲率半径が小さい形状でベース面を予め形成している。本発明の作用効果について、図1を参照して説明する。 In order to solve this problem, in the present invention, when the molding transfer surface is concave, the base surface is formed in advance with a shape having a larger radius of curvature than the molding transfer surface, and the molding transfer surface is convex. In the case of a shape, the base surface is formed in advance with a shape having a smaller radius of curvature than the molding transfer surface. The effects of the present invention will be described with reference to FIG.
図1(a)は、光学素子用成形金型の概略拡大断面図である。図1(a)において、金型Mの状面には、くぼんだ形状(凹形状)のベース面Bが形成されている。成膜時には、上方のターゲットTから、過冷却液体領域を有する非晶質合金粒子が放射状に飛散し、ベース面Bを含む金型Mの上面に付着し堆積する。本発明者の研究によれば、特にベース面Bの周辺(飛散方向に対して傾きが大きい位置)で、膜厚が薄くなるということが判明した。従って、ベース面Bの曲率半径R1を、最終的に形成される光学素子用成形金型の成形転写面Pの曲率半径R2よりも大きい形状で予め形成しておくことで、膜MGの表面形状が、成形転写面形状にほぼ一致する程度まで堆積が行われれば、膜厚の最も薄い部位でも、後加工において十分な膜厚が得られることとなる。 FIG. 1A is a schematic enlarged sectional view of a molding die for optical elements. In FIG. 1A, a concave surface (concave shape) base surface B is formed on the surface of the mold M. At the time of film formation, amorphous alloy particles having a supercooled liquid region radiate from the upper target T and adhere to and deposit on the upper surface of the mold M including the base surface B. According to the inventor's research, it has been found that the film thickness becomes thin particularly in the vicinity of the base surface B (a position where the inclination is large with respect to the scattering direction). Therefore, the surface shape of the film MG is formed in advance by forming the curvature radius R1 of the base surface B in a shape larger than the curvature radius R2 of the molding transfer surface P of the molding die for optical elements to be finally formed. However, if the deposition is performed to the extent that it substantially matches the shape of the molded transfer surface, a sufficient film thickness can be obtained in the post-processing even at the thinnest part.
図1(b)は、別な光学素子用成形金型の概略拡大断面図である。図1(b)において、金型Mの状面には、突出した形状(凸形状)のベース面Bが形成されている。成膜時には、上方のターゲットTから、過冷却液体領域を有する非晶質合金粒子が放射状に飛散し、ベース面Bを含む金型Mの上面に付着し堆積する。本発明者の研究によれば、特にベース面Bの周辺(飛散方向に対して傾きが大きい位置)で、膜厚が薄くなるということが判明した。従って、ベース面Bの曲率半径R1を、最終的に形成される光学素子用成形金型の成形転写面Pの曲率半径R2よりも小さい形状で予め形成しておくことで、膜MGの表面形状が、成形転写面形状にほぼ一致する程度まで堆積が行われれば、膜厚の最も薄い部位でも、後加工において十分な膜厚が得られることとなる。 FIG.1 (b) is a general | schematic expanded sectional view of another shaping | molding die for optical elements. In FIG. 1B, a protruding surface (convex shape) base surface B is formed on the surface of the mold M. At the time of film formation, amorphous alloy particles having a supercooled liquid region radiate from the upper target T and adhere to and deposit on the upper surface of the mold M including the base surface B. According to the inventor's research, it has been found that the film thickness becomes thin particularly in the vicinity of the base surface B (a position where the inclination is large with respect to the scattering direction). Therefore, the surface shape of the film MG is formed in advance by forming the curvature radius R1 of the base surface B in a shape smaller than the curvature radius R2 of the molding transfer surface P of the molding die for optical elements to be finally formed. However, if the deposition is performed to the extent that it substantially matches the shape of the molded transfer surface, a sufficient film thickness can be obtained in the post-processing even at the thinnest part.
更に、過冷却液体領域を有する非晶質合金のバルク材に関しての特許文献が数多く知られている。しかるに、バルク材の過冷却液体領域を有する非晶質合金金属の問題点の1つとしては,その大きな特徴である結晶構造のアモルファス(非晶質)状態を安定して製作するのが難しいということがある。非晶質状態を造り出すためには,まず,所望する組成通りに合金(母合金と呼ぶ)をアーク炉等で製造し、その母合金を高温に熱し液化させ,その後,104℃/secの冷却速度で急冷する。金属ガラスは非晶質な結晶状態であるのに比べて,母合金は炉で同じ組成比の金属を混ぜ合わせてだけものであり,結晶状態は多結晶体である。従って、バルク材の過冷却液体領域を有する非晶質合金を得るためには,この冷却工程が必要不可欠なため,工数が増えると共に,熱した合金を均一に急冷するため製法が限られる上に,冷却技術に熟練を要する。 In addition, many patent documents relating to bulk materials of amorphous alloys having a supercooled liquid region are known. However, one of the problems with amorphous alloy metals that have a supercooled liquid region in the bulk material is that it is difficult to stably produce the amorphous (amorphous) state of the crystal structure, which is a major feature thereof. Sometimes. In order to create an amorphous state, an alloy (called a master alloy) is first manufactured in an arc furnace or the like according to a desired composition, and the master alloy is heated to a high temperature and liquefied, and then 10 4 ° C / sec. Quench quickly at the cooling rate. Compared to the amorphous crystalline state of metallic glass, the master alloy is simply a mixture of metals with the same composition ratio in a furnace, and the crystalline state is polycrystalline. Therefore, in order to obtain an amorphous alloy having a supercooled liquid region of a bulk material, this cooling process is indispensable, so that the number of processes is increased and the manufacturing method is limited in order to rapidly cool the heated alloy uniformly. , Requires skill in cooling technology.
これに対し、本発明のように、所望の組成の金属の粒子を所定方向から飛散させて成膜を行えば、過冷却液体領域を有する非晶質合金を膜状に堆積させることができ、例えばターゲットに母合金さえ用意できれば,比較的容易に厚さ0.1〜500μm程度の薄膜状の過冷却液体領域を有する非晶質合金を得ることできるため、バルク材を用いる場合と比較し、製造時間が格段に短縮されることとなる。又、必要最低限の膜厚だけ成膜を行うことができるため、過冷却液体領域を有する非晶質合金の節約を図ることができ、製造コストを抑制できる。 On the other hand, if the film is formed by scattering metal particles having a desired composition from a predetermined direction as in the present invention, an amorphous alloy having a supercooled liquid region can be deposited in the form of a film, For example, if a mother alloy can be prepared for the target, an amorphous alloy having a thin supercooled liquid region with a thickness of about 0.1 to 500 μm can be obtained relatively easily. Compared with the case of using a bulk material, Manufacturing time will be significantly reduced. Further, since it is possible to form a film with the minimum necessary thickness, it is possible to save the amorphous alloy having the supercooled liquid region and to suppress the manufacturing cost.
更に、ターゲットの母合金としては、必ずしもアモルファス状態である必要はなく、所望の組成比を満たしていれば、飛散し堆積することで自然にアモルファス状態になるというメリットもある。即ち、所望とする過冷却液体領域を有する非晶質合金と同じ組成比の母合金ターゲットさえ用意してしまえば,バルク材等では安定して造ることが難しい材料・組成比の過冷却液体領域を有する非晶質合金,またバルク材ではアモルファス化しない材料・組成比についても,容易にアモルファス化して成膜できるのである。 Further, the target master alloy does not necessarily need to be in an amorphous state, and if the desired composition ratio is satisfied, there is an advantage that the amorphous state is naturally formed by scattering and depositing. In other words, if a master alloy target having the same composition ratio as that of an amorphous alloy having a desired supercooled liquid region is prepared, a supercooled liquid region of a material / composition ratio that is difficult to stably produce with bulk materials, etc. It is possible to easily form a film with an amorphous alloy having a material and a material / composition ratio that is not amorphized with a bulk material.
ここで、過冷却液体域を有するアモルファス状合金(非晶質合金)、いわゆる金属ガラスについて説明する。これは、加熱すると過冷却液体となるアモルファス状の合金材料で構成されるものであり、通常の金属が多結晶組織であるのに対して、組織がアモルファス状のため組成がミクロ的にも均一で機械強度や常温化学耐性に優れ、ガラス転移点を有し、過冷却液体域であるガラス転移点〜結晶化温度の範囲(通常、ガラス転移点+10〜50℃前後(最大で100℃)である)に加熱するとガラス状に軟化する(粘性流動体となる)ためプレス成形加工が出来るという、通常の金属には無い特徴を有する。また、切削加工においても、特にダイアモンド工具による超精密切削加工を行うと、高精度な鏡面が容易に得られることが発見されている。その理由は、この材料がアモルファス状であり結晶粒界を持たないので場所によらず被削性が均一であること、又、アモルファス状を保つために結晶化エネルギーを大きくして組成的に多晶体としているため、切削加工中のダイアモンドの拡散摩耗が少なく工具の刃先寿命を長く保てること等によると考えられる。超精密切削加工により実用的に光学面転写面の創成ができるバルク材としては、従来から知られているのは軟質金属だけであり、非常に微細な切込み量(100nm前後)による延性モード切削によってのみ、シリコンやガラスなどの硬度の高い材料を切削加工可能ではあったが、それは極めて低効率であった。従って、非晶質合金を金型材料として用いることは、金型を中心とした光学面創成加工に極めて大きな応用展開を示唆する発見であったといえる。同様の加工特性は、ダイアモンド砥石などを用いた研削加工についても、研削比が大きくとれる等の形で現れる。 Here, an amorphous alloy (amorphous alloy) having a supercooled liquid region, so-called metallic glass will be described. This is composed of an amorphous alloy material that becomes a supercooled liquid when heated, whereas ordinary metals have a polycrystalline structure, while the structure is amorphous, the composition is uniform even at a microscopic level. It has excellent mechanical strength and room temperature chemical resistance, has a glass transition point, and is in the range of the glass transition point to the crystallization temperature, which is a supercooled liquid region (usually around the glass transition point +10 to 50 ° C. (maximum 100 ° C.)) When heated to a certain level, it softens into a glassy state (becomes a viscous fluid), so that it can be press-molded. Also in cutting, it has been discovered that a highly accurate mirror surface can be easily obtained particularly when ultra-precision cutting is performed with a diamond tool. The reason for this is that this material is amorphous and has no grain boundaries, so that machinability is uniform regardless of location, and in order to maintain the amorphous state, the crystallization energy is increased to increase the composition. Since it is made of a crystal, it is considered that there is little diffusion wear of diamond during the cutting process, and the tool edge life of the tool can be kept long. As a bulk material that can be used to create an optical surface transfer surface practically by ultra-precision cutting, only soft metals have been known so far. By ductile mode cutting with a very fine depth of cut (around 100 nm). Only high hardness materials such as silicon and glass could be machined, but it was very inefficient. Therefore, it can be said that the use of an amorphous alloy as a mold material was a discovery that suggested an extremely large application development in optical surface creation processing centering on a mold. Similar processing characteristics appear in such a manner that the grinding ratio can be increased even when grinding using a diamond grindstone or the like.
本発明の光学素子用成形金型で用いることができる非晶質合金の種類は問わない。Pd系、Mg系、Ti系、Fe系、Zr系などの公知の金属ガラスが使えるが、過冷却液体域を有するアモルファス状である合金材料であることが、本発明に必要な要件であって、これらの組成や種類は問わない。ただし、プラスチック光学素子成形用の金型材料としては、樹脂温度が300℃近くであることから、Pd系、Ti系、Fe系などがガラス転移点が高いので有利であるが、より好ましくはPd系が空気中でほとんど酸化することなく、加熱プレスができるという点でも有利である。この場合、Pd(パラジウム)は貴金属で高価ではあるが、本発明の製造方法により得られる光学素子用成形金型は、必要に応じて、付着した前記非晶質合金を加熱することで異なるパターンを再形成することもできる。 The type of amorphous alloy that can be used in the molding die for optical elements of the present invention is not limited. Known metal glasses such as Pd-based, Mg-based, Ti-based, Fe-based, and Zr-based materials can be used, but an alloy material that is an amorphous material having a supercooled liquid region is a necessary requirement for the present invention. These compositions and types are not limited. However, as a mold material for molding a plastic optical element, since the resin temperature is close to 300 ° C., Pd-based, Ti-based, Fe-based, etc. are advantageous because of their high glass transition points, but more preferably Pd It is also advantageous in that the system can be hot pressed with little oxidation in air. In this case, although Pd (palladium) is a noble metal and expensive, the molding die for optical elements obtained by the production method of the present invention has different patterns by heating the attached amorphous alloy as necessary. Can also be reformed.
請求項2に記載の光学素子用成形金型の製造方法は、請求項1に記載の発明において、前記光学素子用成形金型により成形される光学素子の光学面に、光軸を中心とした輪帯構造が形成されることを特徴とするので、前記製造方法によって製造された光学素子用成形金型により成形された光学素子の機能をより高めることができる。 According to a second aspect of the present invention, there is provided a method for manufacturing an optical element molding die according to the first aspect, wherein the optical surface of the optical element molded by the optical element molding die is centered on the optical axis. Since the annular zone structure is formed, the function of the optical element molded by the optical element molding die manufactured by the manufacturing method can be further enhanced.
請求項3に記載の光学素子用成形金型の製造方法は、請求項2に記載の発明において、前記輪帯構造は、光路差付与構造であることを特徴とするので、前記製造方法によって製造された光学素子用成形金型により成形された光学素子の機能をより高めることができる。光路差付与構造としては、いわゆるNPS(Non−Periodic Surface)構造等が知られている。 According to a third aspect of the present invention, there is provided a method for manufacturing a molding die for an optical element according to the second aspect of the present invention, wherein the annular zone structure is an optical path difference providing structure. The function of the optical element molded by the molded optical element mold can be further enhanced. As the optical path difference providing structure, a so-called NPS (Non-Periodic Surface) structure or the like is known.
請求項4に記載の光学素子用成形金型の製造方法は、請求項2に記載の発明において、前記輪帯構造は、光軸方向断面が鋸歯状のブレーズ型回折構造であることを特徴とするので、前記製造方法によって製造された光学素子用成形金型により成形された光学素子の機能をより高めることができる。 According to a fourth aspect of the present invention, there is provided a method for manufacturing an optical element molding die according to the second aspect of the invention, wherein the annular zone structure is a blazed diffractive structure having a sawtooth cross section in the optical axis direction. Therefore, the function of the optical element molded by the optical element molding die manufactured by the manufacturing method can be further enhanced.
請求項5に記載の光学素子用成形金型の製造方法は、請求項2に記載の発明において、前記輪帯構造は、光軸方向断面が階段状の回折構造であることを特徴とするので、前記製造方法によって製造された光学素子用成形金型により成形された光学素子の機能をより高めることができる。階段状の回折構造としては、DOE等が知られている。 According to a fifth aspect of the present invention, there is provided the method for manufacturing a molding die for an optical element according to the second aspect of the invention, wherein the annular structure is a diffractive structure having a stepwise cross section in the optical axis direction. The function of the optical element molded by the optical element molding die manufactured by the manufacturing method can be further enhanced. A DOE or the like is known as a step-like diffraction structure.
請求項6に記載の光学素子用成形金型の製造方法は、請求項2〜5のいずれかに記載の発明において、前記輪帯構造は、前記光学素子に対して光を照射する光源の波長変化による前記光学素子の収差変化を補正する機能を有することを特徴とするので、例えば光ディスクに情報の記録及び/又は再生を行う光ピックアップ装置に好適な光学素子を提供できる。
The method for manufacturing a molding die for an optical element according to
請求項7に記載の光学素子用成形金型の製造方法は、請求項2〜6のいずれかに記載の発明において、前記輪帯構造は、前記光学素子の温度変化による収差変化を補正する機能を有することを特徴とするので、例えば光ディスクに情報の記録及び/又は再生を行う光ピックアップ装置に好適な光学素子を提供できる。
The method for manufacturing a molding die for an optical element according to claim 7 is the invention according to any one of
請求項8に記載の光学素子用成形金型の製造方法は、請求項1に記載の発明において、前記光学素子用成形金型により成形される光学素子の光学面に、複数の突起またはくぼみが転写成形されるように,前記光学素子用成形金型成形転写面には,対応したくぼみまたは突起が形成されていることを特徴とするので、前記製造方法によって製造された光学素子用成形金型により成形された光学素子の機能をより高めることができる。又、たとえ突起又はくぼみが数十乃至数百ナノメートルの間隔で配置しなくてはならないものであっても、機械加工を必要とすることなく、転写成形により容易に形成することができる。尚、くぼみまたは突起とは、くぼみと突起の双方が混在するものも含む。
The method for manufacturing an optical element molding die according to claim 8 is the invention according to
請求項9に記載の光学素子用成形金型の製造方法は、請求項8に記載の発明において、前記光学素子の光学面の突起またはくぼみは、等価屈折率領域の微細構造を形成することを特徴とする。尚、前記突起又はくぼみの間隔は、前記光学素子の光学面を透過する光の波長以下であると好ましい。 According to a ninth aspect of the present invention, there is provided the method for manufacturing a molding die for an optical element according to the eighth aspect of the invention, wherein the projection or depression of the optical surface of the optical element forms a fine structure of an equivalent refractive index region. Features. In addition, it is preferable that the space | interval of the said protrusion or a hollow is below the wavelength of the light which permeate | transmits the optical surface of the said optical element.
請求項10に記載の光学素子用成形金型の製造方法は、請求項8又は9に記載の発明において、前記光学素子の光学面の突起またはくぼみは、反射防止効果を発生する微細構造を形成することを特徴とする。尚、前記突起又はくぼみの間隔は、前記光学素子の光学面を透過する光の波長以下であると好ましい。
The method for producing a molding die for an optical element according to
請求項11に記載の光学素子用成形金型の製造方法は、請求項8〜10のいずれかに記載の発明において、前記光学素子の光学面の突起またはくぼみは、構造複屈折を発生する微細構造を形成することを特徴とする。尚、前記突起又はくぼみの間隔は、前記光学素子の光学面を透過する光の波長以下であると好ましい。
The method for producing a molding die for an optical element according to
請求項12に記載の光学素子用成形金型の製造方法は、請求項8〜11のいずれに記載の発明において、前記光学素子の光学面の突起またはくぼみは、共鳴領域の微細構造を形成することを特徴とする。尚、前記突起又はくぼみの間隔は、前記光学素子の光学面を透過する光の波長以下であると好ましい。 The method for producing a molding die for an optical element according to claim 12 is the invention according to any one of claims 8 to 11, wherein the projection or depression of the optical surface of the optical element forms a fine structure of the resonance region. It is characterized by that. In addition, it is preferable that the space | interval of the said protrusion or a hollow is below the wavelength of the light which permeate | transmits the optical surface of the said optical element.
請求項13に記載の光学素子用成形金型の製造方法は、請求項8〜12のいずれかに記載の発明において、前記光学素子の光学面の突起またはくぼみは、該光学面の一部に存在しており、その光学面を転写形成されるように、前記成形転写面の一部には、対応したくぼみまたは突起が存在していることを特徴とする。
The method for producing a molding die for an optical element according to
請求項14に記載の光学素子用成形金型の製造方法は、請求項8〜13のいずれかに記載の発明において、前記光学素子の光学面の一部に、少なくとも複数の形状または配置パターンを有する突起またはくぼみが存在しており、その光学面を転写形成されるように、前記光学面転写面の一部には、対応した少なくとも複数の形状または配置パターンのくぼみまたは突起が存在していることを特徴とする。前記光学素子の光学面に、微細構造の突起またはくぼみを、複数の形状や配置パターンを有するように形成し、それらを該光学面上に部分的に配置することにより、かかる光学面が、局部的にそれらの微細構造の光学機能を発揮することができる。これにより、光学面を通る光束に、微細構造の突起やくぼみの各形状や配置パターンによって生じる光学機能を部分的或いは選択的に施して、複数の光学機能を一つの光束に盛り込むことができる。この場合、光学素子の光学面上には、微細構造の突起やくぼみが必ず光学面の全面に存在している必要はない。すなわち、従来では、所定の光学機能を発揮するために複数の光学素子を組み合わせる必要があるところ、本発明の製造方法により製造された光学素子用成形金型により成形した光学素子を用いれば、単独で所定の光学機能を発揮することができ、光学系をより簡素化することができ、大幅なコストダウンが実現できる。又、本発明の製造方法によって製造された光学素子用成形金型によれば、かかる光学素子を容易に大量生産することができる。
The method for manufacturing a molding die for an optical element according to
請求項15に記載の光学素子用成形金型の製造方法は、請求項1に記載の発明において、前記光学素子用成形金型の成形転写面は、非球面形状のみからなることを特徴とする。即ち、微細構造を有しない光学面を成形することもできる。
The method for producing an optical element molding die according to claim 15 is characterized in that, in the invention according to
請求項16に記載の光学素子用成形金型の製造方法は、請求項1〜15のいずれかに記載の発明において、前記過冷却液体領域をもつ非晶質合金膜の膜層を、PVD(Physical Vapor Deposition)処理によって形成したことを特徴とする。
A method for producing a molding die for an optical element according to claim 16 is the invention according to any one of
請求項17に記載の光学素子用成形金型の製造方法は、請求項1〜15のいずれかに記載の発明において、前記過冷却液体領域をもつ非晶質合金膜の膜層を、スパッタ処理によって形成したことを特徴とするので、強固な薄膜を実現できる。
The method for manufacturing a molding die for an optical element according to claim 17 is the invention according to any one of
請求項18に記載の光学素子用成形金型の製造方法は、請求項1〜15のいずれかに記載の発明において、前記過冷却液体領域をもつ非晶質合金膜の膜層を、イオンプレーティング処理によって形成したことを特徴とするので、強固な薄膜を実現できる。
The method for producing a molding die for an optical element according to claim 18 is the invention according to any one of
請求項19に記載の光学素子用成形金型の製造方法は、請求項1〜15のいずれかに記載の発明において、前記過冷却液体領域をもつ非晶質合金膜の膜層を、蒸着法によって形成したことを特徴とするので、強固な薄膜を実現できる。
The method for producing a molding die for an optical element according to claim 19 is the method according to any one of
請求項20に記載の光学素子用成形金型の製造方法は、請求項1〜15のいずれかに記載の発明において、前記過冷却液体領域をもつ非晶質合金膜の膜層を、CVD(Chemical Vapor Deposition)処理によって形成したことを特徴とするので、強固な薄膜を実現できる。
The method for producing a molding die for optical elements according to
請求項21に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がFeを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Fe系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
The method for manufacturing a molding die for an optical element according to claim 21 is the invention according to any one of
請求項22に記載の光学素子用成形金型の製造方法は、請求項21に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Co,Ni,Cu,B,Al,Ga,C,Si,P,Zr,Nb,Ti,Wのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 The method for producing a molding die for optical elements according to claim 22 is the invention according to claim 21, wherein the amorphous alloy having the supercooled liquid region is Co, Ni, Cu, B, Al, Ga. , C, Si, P, Zr, Nb, Ti, and W are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項23に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がTiを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Ti系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
The method for producing a molding die for an optical element according to claim 23 is the invention according to any one of
請求項24に記載の光学素子用成形金型の製造方法は、請求項23に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Fe,Co,Ni,Cu,B,Al,Ga,C,Si,P,Zr,Nb,Wのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 The method for producing a molding die for optical elements according to claim 24 is the invention according to claim 23, wherein the amorphous alloy having the supercooled liquid region is Fe, Co, Ni, Cu, B, Al. , Ga, C, Si, P, Zr, Nb, and W are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項25に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がWを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Ti系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
The method for producing a molding die for an optical element according to claim 25 is the invention according to any one of
請求項26に記載の光学素子用成形金型の製造方法は、請求項25に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Ti,Fe,Co,Ni,Cu,B,Al,Ga,C,Si,P,Zr,Nbのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 A method for manufacturing a molding die for an optical element according to claim 26 is the invention according to claim 25, wherein the amorphous alloy having the supercooled liquid region is Ti, Fe, Co, Ni, Cu, B , Al, Ga, C, Si, P, Zr, and Nb are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項27に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がCoを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Co系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
A method for producing a molding die for an optical element according to claim 27 is the invention according to any one of
請求項28に記載の光学素子用成形金型の製造方法は、請求項27に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Ti,Fe,Ni,Cu,B,Al,Ga,C,Si,P,Zr,Nb,Wのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 A method for manufacturing a molding die for optical elements according to claim 28 is the invention according to claim 27, wherein the amorphous alloy having the supercooled liquid region is Ti, Fe, Ni, Cu, B, Al. , Ga, C, Si, P, Zr, Nb, and W are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項29に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がNiを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Ni系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
The method for producing a molding die for an optical element according to claim 29 is the invention according to any one of
請求項30に記載の光学素子用成形金型の製造方法は、請求項29に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Ti,Fe,Co,Cu,B,Al,Ga,C,Si,P,Zr,Nb,Wのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 The method for producing a molding die for an optical element according to claim 30 is the invention according to claim 29, wherein the amorphous alloy having the supercooled liquid region is Ti, Fe, Co, Cu, B, Al. , Ga, C, Si, P, Zr, Nb, and W are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項31に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がCuを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とするので、前記過冷却液体領域を有する非晶質合金の膜層を、スパッタ法などの成膜方法を用いることで,必要な箇所に必要な厚みだけ膜層を形成して,得ることができる。また、Cu系の金属ガラスを用いた光学素子用成形金型を製作する上で,金属ガラスのバルク材の場合に必要となる制御が難しい急冷工程を省くことで,その分の製作工程を少なくすることができる。
The method for producing a molding die for an optical element according to claim 31 is the invention according to any one of
請求項32に記載の光学素子用成形金型の製造方法は、請求項31に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Ti,Fe,Co,Ni,B,Al,Ga,C,Si,P,Zr,Nb,Wのいずれか1つ以上を、少なくとも1mol%の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 A method for producing a molding die for optical elements according to claim 32 is the invention according to claim 31, wherein the amorphous alloy having the supercooled liquid region is Ti, Fe, Co, Ni, B, Al. , Ga, C, Si, P, Zr, Nb, and W are contained at a ratio of at least 1 mol%, so that the supercooled liquid region of the amorphous alloy is 1 Can be expanded by ~ 50 ° C.
請求項33に記載の光学素子用成形金型の製造方法は、請求項1〜20のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金の膜層は、厚さ0.1〜500μmであり、前記過冷却液体領域を有する非晶質合金の組成がMoを20〜80mol%の割合で含み、前記過冷却液体領域を有する非晶質合金のガラス転移温度Tgが300〜800℃の範囲内にあることを特徴とする。
A manufacturing method of a molding die for optical elements according to claim 33 is the invention according to any one of
請求項34に記載の光学素子用成形金型の製造方法は、請求項33に記載の発明において、前記過冷却液体領域を有する非晶質合金は、Fe、Co,Ni、Cu、Hf,Zr,Ti,W,Sn,Al,Si,P,B、Pdのいずれか1つ以上を、少なくとも1mol%以上の割合で含有することを特徴とする。 The method for producing a molding die for an optical element according to claim 34 is the invention according to claim 33, wherein the amorphous alloy having the supercooled liquid region is Fe, Co, Ni, Cu, Hf, Zr. , Ti, W, Sn, Al, Si, P, B, and Pd are contained at a ratio of at least 1 mol% or more.
請求項35に記載の光学素子用成形金型の製造方法は、請求項21〜34のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金は、Pt,Ir,Au,Ag,Pd,Ru,Rh,Osの元素をいずれか1つ以上を、少なくとも1mol%以上の割合で含有してなることを特徴とするので、前記過冷却液体領域を有する非晶質合金の耐酸化性能を向上させることができる。 The method for producing a molding die for optical elements according to claim 35 is the invention according to any one of claims 21 to 34, wherein the amorphous alloy having the supercooled liquid region is Pt, Ir, Au, Since any one or more elements of Ag, Pd, Ru, Rh, and Os are contained in a ratio of at least 1 mol%, the acid resistance of the amorphous alloy having the supercooled liquid region Performance can be improved.
請求項36に記載の光学素子用成形金型の製造方法は、請求項21〜35のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金は、Zn,Al,Sn,Mg,Be,Sの元素をいずれか1つ以上を、少なくとも1mol%以上の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 The method for producing a molding die for optical elements according to claim 36 is the invention according to any one of claims 21 to 35, wherein the amorphous alloy having the supercooled liquid region is Zn, Al, Sn, Since any one or more elements of Mg, Be, and S are contained at a ratio of at least 1 mol%, the supercooled liquid region of the amorphous alloy is expanded by 1 to 50 ° C. Can do.
請求項37に記載の光学素子用成形金型の製造方法は、請求項21〜36のいずれかに記載の発明において、前記過冷却液体領域を有する非晶質合金は、Mo,Mn,V,Ge,Ru,Rh,N,S,Na,Be,K,Ca,Sの元素をいずれか1つ以上を、少なくとも1mol%以上の割合で含有してなることを特徴とするので、非晶質合金の過冷却液体領域を1〜50℃拡大させることができる。 The method for producing a molding die for optical elements according to claim 37 is the invention according to any one of claims 21 to 36, wherein the amorphous alloy having the supercooled liquid region is Mo, Mn, V, Since it contains at least 1 mol% of any one or more elements of Ge, Ru, Rh, N, S, Na, Be, K, Ca, and S, it is amorphous. The supercooled liquid region of the alloy can be expanded by 1-50 ° C.
更に、前記所定の加工とは、光学素子の光学面に対応した母型を加熱して前記ベース面に形成された膜層に押しつける加熱プレス成形であると好ましい。 Further, the predetermined processing is preferably hot press molding in which a matrix corresponding to the optical surface of the optical element is heated and pressed against the film layer formed on the base surface.
成形転写面上に微細な突起(又はくぼみ)を有する光学素子用成形金型の母型を予め形成しておき、前記過冷却液体領域を有する非晶質合金のガラス転移点温度以上に加熱してから、前記ベース面に成膜された前記過冷却液体領域を有する非晶質合金にプレスすると、微細な突起(又はくぼみ)を精度良く前記過冷却液体領域を有する非晶質合金の膜層に転写でき、成形転写面を精度良く形成できる。即ち、形状精度の良い母型が一つ存在すれば、光学素子用成形金型を、容易に大量に製作することができるのである。しかるに、このような母型の形成としては、例えば、光学素子の光学面に対応した面(母光学面)にレジストをスピンコート法などで塗布し、電子ビームやレーザービームによって微細パターンを露光した後、現像によって母光学面上の微細パターンを形状化する手法が考えられる。この方法によれば、通常の機械加工での創成では極めて困難である微細な突起(又はくぼみ)を形成することができる。 A preform for an optical element molding die having fine protrusions (or depressions) on the molding transfer surface is formed in advance, and heated to a temperature higher than the glass transition temperature of the amorphous alloy having the supercooled liquid region. After that, when the amorphous alloy having the supercooled liquid region formed on the base surface is pressed, a film layer of the amorphous alloy having the supercooled liquid region with fine protrusions (or depressions) is accurately obtained. The molding transfer surface can be accurately formed. That is, if there is one master mold with good shape accuracy, a large number of optical element molding dies can be easily manufactured. However, in order to form such a matrix, for example, a resist is applied to the surface corresponding to the optical surface of the optical element (mother optical surface) by a spin coat method or the like, and a fine pattern is exposed by an electron beam or a laser beam. Thereafter, a method of forming a fine pattern on the mother optical surface by development can be considered. According to this method, it is possible to form fine protrusions (or depressions) that are extremely difficult to create by ordinary machining.
更に、前記所定の加工とは、ダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工であると、前記非晶質合金の被削性を利用し、簡単な工程で高精度な光学素子用成形金型を大量生産できる。 Moreover, the the predetermined processing, if it is cutting the film layer formed on the base surface performed using a diamond tool, using the amorphous alloy machinability, high accuracy a simple process It is possible to mass-produce a mold for optical elements.
更に、前記所定の加工とは、光学素子の光学面に対応した母型を加熱して前記ベース面に押しつける加熱プレス成形と、ダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工であると、効率的な加工が可能となる。 Furthermore, the predetermined processing includes heating press molding that heats a base corresponding to the optical surface of the optical element and presses it against the base surface, and cutting of the film layer formed on the base surface using a diamond tool. If it is processing , efficient processing becomes possible.
請求項41に記載の光学素子用成形金型は、請求項1〜40のいずれかに記載の光学素子用成形金型の製造方法によって製造された光学素子用成形金型であって、200〜800℃の金型温度で光学素子の成形を1,000回行ったときに、金型表面粗度がRa0.05μm未満であることを特徴とするので、上述した製造方法で形成することにより、長寿命な光学素子用成形金型を提供できる。
The molding die for optical elements according to claim 41 is a molding die for optical elements manufactured by the method for producing a molding die for optical elements according to any one of
請求項42に記載の光学素子は、請求項第1〜40のいずれか記載の光学素子用成形金型の製造方法により製造された光学素子用成形金型、又は請求項41に記載の光学素子用成形金型を用いて成形されたことを特徴とするので、高精度を有しながらも低コストで製造できる。
An optical element according to claim 42 is an optical element molding die produced by the method for producing an optical element molding die according to any one of
請求項43に記載の光学素子は,請求項42に記載の発明において、プラスチック材料を素材とすることを特徴とするので、安価に容易に製造できる。 The optical element according to a 43rd aspect is characterized in that, in the invention according to the 42nd aspect, a plastic material is used as a raw material, so that the optical element can be easily manufactured at a low cost.
請求項44に記載の光学素子は,請求項42に記載の発明において、前記光学素子は,ガラス材料を素材とすることを特徴とするので、収差特性等に優れたものとなり,またプラスチック材料と比較すると高温高湿等の環境に対して製品の性能が安定し,耐久力に優れる。 The optical element according to claim 44 is characterized in that, in the invention according to claim 42, the optical element is made of a glass material, so that it has excellent aberration characteristics, etc. In comparison, the product performance is stable and highly durable against high temperature and high humidity environments.
請求項45に記載の光学素子は,請求項42〜44のいずれかに記載の発明において、前記光学素子は,例えば光ピックアップ装置に使用されるレンズであることを特徴とする。 According to a 45th aspect of the present invention, in the invention according to any one of the 42nd to 44th aspects, the optical element is a lens used in, for example, an optical pickup device.
本明細書中で用いる回折構造(回折輪帯)とは、光学素子(例えばレンズ)の光学面表面に、光軸を中心とする略同心状の輪帯として形成されたレリーフを設けて、回折によって光束を集光あるいは発散させる作用を持たせた回折面のことをいう。例えば、光軸を含む平面でその断面をみれば各輪帯は鋸歯のような形状が知られているが、そのような形状を含むものである。回折輪帯を回折溝ともいう。 The diffractive structure (diffraction ring zone) used in this specification is a diffraction pattern in which a relief formed as a substantially concentric ring zone centered on the optical axis is provided on the optical surface of an optical element (for example, a lens). This means a diffractive surface having a function of condensing or diverging a light beam. For example, when the cross section is viewed on a plane including the optical axis, each annular zone is known to have a sawtooth shape, but such a shape is included. The diffraction zone is also called a diffraction groove.
本発明が適用されるに当たり、輪帯構造や突起(又はくぼみ)の並びなど、個々の微細構造の形状や配列周期などは関係ない。どのような微細な構造であっても、光学素子に新たな機能を付加する目的で作られたものであれば、その光学素子用成形金型又はそれにより成形された光学素子は、本発明の範疇に含まれる。また、新たに付加する機能としては、収差を低減するものに限らない。光学系の特性に応じて収差を故意に増加させる場合も、最終的に理想とする収差に近づける目的で行う限り、本発明の範疇に含まれる。 When the present invention is applied, the shape and arrangement period of individual microstructures, such as the annular structure and the arrangement of protrusions (or depressions), are not relevant. Whatever the fine structure, if it is made for the purpose of adding a new function to the optical element, the molding die for the optical element or the optical element molded by the optical element can be used in the present invention. Included in the category. Further, the function to be newly added is not limited to the function for reducing aberration. The case where the aberration is intentionally increased according to the characteristics of the optical system is also included in the scope of the present invention as long as it is performed for the purpose of finally bringing it closer to the ideal aberration.
本発明によれば、低コストであり取り扱いが容易であるにも関わらず、切削性に優れ、寸法精度を高めることができる光学素子用成形金型の製造方法、及びそれにより製造される光学素子用成型金型並びにそれにより成形される光学素子を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, although it is low-cost and easy to handle, it is excellent in machinability and can improve a dimensional accuracy, The manufacturing method of the molding die for optical elements, and an optical element manufactured by it Molding molds and optical elements molded thereby can be provided.
以下、図面を参照して、本発明の実施の形態について説明する。図2は、光学素子用成形金型を製作するための母型の製作工程の例を示す図である。尚、母型の製作は、以下の方法に限らず、例えば後述する実施例で示すように、切削加工により形成しても良い。まず、図2(a)に示すように、母型材1に母光学面1aを形成する。かかる母光学面1aは、光学素子用成形金型により形成したいレンズ(光学素子の一例)の設計光学面形状に一致する。母光学面1aの周囲は、ティルト基準平面に対応する母幾何寸法基準面1bとなっている。
Embodiments of the present invention will be described below with reference to the drawings. FIG. 2 is a diagram illustrating an example of a manufacturing process of a mother die for manufacturing a molding die for optical elements. The production of the mother die is not limited to the following method, and may be formed by cutting as shown in the examples described later. First, as shown in FIG. 2A, the mother
続いて、図2(b)に示すように、不図示の駆動体によって母型材1を光軸回りに回転させながら、母光学面1a及び母幾何寸法基準面1bにレジストRを塗布する(スピンコート)。レジストRは、母光学面1a及び母幾何寸法基準面1bを含む母型材1の上面に、等しい膜厚でコーティングされる。
Subsequently, as shown in FIG. 2B, a resist R is applied to the mother
更に、レジストRがコーティングされた母光学面1aに対し、不図示の露光機により電子ビームLBを照射して、微細パターンを露光形成する。続いて、図2(c)に示すように、母型材1を溶液中に浸し、母光学面1a上において、露光形成された微細パターンに応じてレジストRを除去する。ここで、電子ビームLBのビーム径は極めて小さいので、数十乃至数百ナノメートルの間隔で露光を行えるため、それに応じてレジストRを除去することができる。
Further, the mother
その後、図2(d)に示すように、部分的にレジストRが除去された母型材1の上面を、イオンシャワーIS(加速されたアルゴンイオン等)の雰囲気中に曝し(ドライエッチング)、レジストRのパターンに応じて、母型材1の表面を除去する。このとき、レジストRの残っている部分は、表面が除去されない或いは除去されにくくなるため、露光時に厚く円形のレジストRを残すことで、それに対応して母型材1の光学転写面1a’の表面に、小さな円筒形状の突起が多数形成されることとなる。
Thereafter, as shown in FIG. 2D, the upper surface of the
このようにして形成された母型材1は、円管状のシリンダ2の一端を閉止するような形でボルト3で固定されて、母型4が形成されることとなる(図2(e))。シリンダ2と母型材1との間に、エアベントが形成されるように、シリンダ2の端面には、溝2aが形成されている。尚、母型材1の加工は、大規模な設備が必要であって、その製作コストも高いが、一つあれば、後述するようにして光学素子用成形金型を大量に製作できるので、特に問題はない。
The
図3は、光学素子用成形金型の製作工程を示す図である。まず、ステンレス鋼材等から基体10を形成する。基材10の材料は、特に限定されるものではないが、鋼やステンレス鋼などの一般的に用いられる金型材料であることが好ましく、その場合には供給も安定しており価格も安いという利点がある。ブランクとしての基体10は、一端(図で上端)に、光学素子の光学面(例えば非球面)に対応しているが、曲率半径がそれより大きいか等しい凹部(ベース面)10aと、その周囲の周囲面10bとを形成する(ベース面を形成する工程)ことで、金型の近似形状を有するようになっている。凹部10aと周囲面10b、基体10の端部周囲面10cの形状精度は、表面に施す過冷却液体域を有する非晶質合金(以下、単に非晶質合金ともいう)MGの膜厚によるが100μm程度の非晶質合金MGを成膜する場合であれば、10〜20μm程度の精度であれば十分なので、ブランク加工そのものはNC旋盤などを使用して数10分でできる程度のものである。この凹部10aと周囲面10b、さらに基体10の端部周囲面10cに、過冷却液体域を有する非晶質合金MGを、以下のようにして付着させる。
FIG. 3 is a diagram showing a manufacturing process of a molding die for optical elements. First, the
非晶質合金MGを、凹部10aと周囲面10b、基体10の端部周囲面10cの表面に対して、詳細は実施例で後述するようにして、スパッタや蒸着などのPVD処理やCVD処理により成膜する(膜層を形成する工程)。尚、本実施の形態では、凹部10a以外に、周囲面10b、端部周囲面10cにも非晶質合金MGを成膜させているが、成膜は凹部10aだけでもよい。
The amorphous alloy MG is applied to the surface of the
尚、以上の実施の形態では、基体10のベース面が凹形状を有している例を示しており、かかる場合には、最終的に形成される成形転写面よりもベース面の曲率半径が大きいか、あるいは等しい曲率半径の形状となっているが、基体10のベース面を凸形状とした例の場合には、最終的に形成される成形転写面よりもベース面の曲率半径が小さいか、あるいは等しい曲率半径の形状とすることで、同様の効果を得ることができる。
In the above embodiment, an example in which the base surface of the
非晶質合金MGの成膜は、CVD処理では、基材10が高温となり過冷却液体状態とする非晶質合金の性質上不利ではあるが、本発明は成膜をCVD処理やPVD処理のどちらかに限ったものではない。非晶質合金MGを比較的容易に成膜しやすいPVD処理では、スパッタやイオンプレーティング、蒸着などの処理があるが、ここではどれを用いても良い。ちなみに、スパッタ法ではターゲット材料は必ずしもアモルファス状態でなくとも良く、基材10に所望の組成比で構成原子を付着させれば、スパッタの原理上、付着時に急冷を伴うため、アモルファス状態で容易に成膜できる。成膜速度は0.2〜数μm/h程度で、スパッタ装置の出力をあげれば容易に短縮できるが、基材10の温度が上昇してアモルファス状にならなくなるため、水冷などによる基材10の冷却が必要となる。あまり膜厚が厚くても、この後のダイアモンド切削加工や加熱プレス成形などで取り代がたくさん残り効率が悪いので、通常は100μm程度がより好ましい。しかし、複雑な形状では数mmの膜厚が必要なこともあり、大凡10nmから1mm程度の範囲が、実用的な膜厚範囲である。
The film formation of the amorphous alloy MG is disadvantageous due to the nature of the amorphous alloy in which the
特に膜厚が厚い場合は、凹部10aと周囲面10b、基体10の端部周囲面10c以外の部分にはみ出した非晶質合金により、光学素子用成形金型の設計形状が損なわれることがある。そのために、成膜部分以外をマスキングしたり、成膜後にダイアモンド切削や研削加工によってはみ出し部を除去することも必要な場合がある。しかし、非晶質合金MGは、被削性が良くしかも除去量が少ないため、加工工数やコストの負担にはほとんどならない。
In particular, when the film thickness is thick, the design shape of the optical element molding die may be impaired by the amorphous alloy protruding beyond the
本実施の形態のごとく、非晶質合金MGを、このように光学素子用成形金型の極限られた部位だけに少量用いることによって、従来、優れた物性的な特徴をもちながらバルク形状の製作が難しかった種類の非晶質合金についても、光学素子用成形金型に適用することが可能となった。例えば、ニッケル系や銅系などの高硬度の非晶質合金は、金型材料として高耐久性が期待できるが、バルク状にしにくいため、先の出願の手法では光学素子用成形金型ヘの適用が難しかったが、本実施の形態のごとく成膜化することで、その適用が可能となった。さらに、バルク材料では冶金時に水素などのガスが地金中に存在するので、「す」と呼ばれる微小孔が存在し、ダイアモンド切削したり加熱プレス成形したときに、加工創成した光学面に現れて表面不良を生じさせることがあったが、本実施の形態のようなCVD処理やPVD処理によって気相から成膜する場合では、「す」が発生することはほぼ無いため、光学素子用成形金型の製作収率が高く維持できて、例えば不良対応のスペアを製作する必要がなくなるので、先の出願に開示した光学素子用成形金型に比べ、大幅に低コストになる。 As in the present embodiment, by using a small amount of the amorphous alloy MG only in a limited part of the molding die for optical elements as described above, it has been conventionally produced in a bulk shape with excellent physical properties. It has become possible to apply the amorphous alloy of a type that is difficult to apply to a molding die for optical elements. For example, high hardness amorphous alloys such as nickel-based and copper-based materials can be expected to have high durability as a mold material, but they are difficult to be bulked. Although it was difficult to apply, application was possible by forming a film as in this embodiment. Furthermore, in bulk materials, hydrogen and other gases exist in the metal during metallurgy, so there are micro holes called “su” that appear on the created optical surface when diamond cutting or hot press molding is performed. In some cases, surface defects may occur. However, in the case of forming a film from the vapor phase by CVD processing or PVD processing as in the present embodiment, there is almost no occurrence of “so”. Since the production yield of the mold can be maintained high, for example, it is not necessary to produce a spare for dealing with defects, so that the cost is significantly lower than that of the optical element molding die disclosed in the previous application.
続いて、この非晶質合金MGの成膜に対し、ダイアモンド切削加工や加熱プレス成形もしくはこれらの組み合わせを施すことで、非晶質合金MGの表面を所望の光学面転写面MGa(基体10の凹部10aに対応)及び幾何的寸法基準面転写面MGb(基体10の周囲面10bに対応)に仕上げる(成形転写面を得る工程)。本実施の形態によれば、基体10のベース面である凹部10aの曲率半径を、最終的に形成される光学素子用成形金型の成形転写面の曲率半径よりも大きいか、あるいは等しい形状で予め形成しておくことで、膜MGの表面形状が、成形転写面形状にほぼ一致する程度まで堆積が行われれば、膜厚の最も薄い部位でも、後加工において十分な膜厚が得られ、ダイアモンド切削加工や加熱プレス成形を適切に行えるというメリットがある。
Subsequently, the amorphous alloy MG is subjected to diamond cutting, hot press molding, or a combination thereof to form a film of the amorphous alloy MG, so that the surface of the amorphous alloy MG is transferred to a desired optical surface transfer surface MGa (of the substrate 10). (Corresponding to the
ダイアモンド切削は、図3に点線で示す単結晶ダイアモンド工具Tを用いて、超精密旋盤(不図示)などにより一つ―つ切削加工するものであるため、従来の無電解ニッケルメッキによる金型製作手法と基本的に同じ加工工程を経るが、従来に比べて、光学面転写面MGa及び幾何寸法基準面転写面MGbは、PVD処理又はCVD処理で迅速に緻密に形成され、化学メッキ処理をしないためピンホールなどの欠陥が無く処理納期が早いことと、被削性が非常に良いので工具摩耗が少なく切削加工による形状創成が容易であること等が、より優れた特徴といえる。 Diamond cutting uses a single crystal diamond tool T shown by the dotted line in FIG. 3 to cut one piece with an ultra-precision lathe (not shown). Although the processing steps are basically the same as the method, the optical surface transfer surface MGa and the geometric dimension reference surface transfer surface MGb are rapidly and densely formed by PVD processing or CVD processing and are not subjected to chemical plating processing compared to the conventional method. Therefore, it can be said that the excellent features are that there are no defects such as pinholes and that the process delivery time is fast and that the machinability is very good, so that tool wear is small and shape creation by cutting is easy.
図4は、加熱プレス成形による光学面素子成形用金型の光学面転写面及び幾何的寸法基準面転写面の形成工程を示す図である。まず、図2に示す工程で作製した母型4に、図4(a)に示すように支柱5を取り付ける。続いて、図4(b)に示すように、母型材1の周囲に配置されたヒーターHにより、母光学面1aと母幾何寸法基準面1bの周辺を予備加熱しておき、図3に示す工程で作製した基体10及び成膜した非晶質合金MG(機械加工されていてもよい)を、シリンダ2内に挿入し、プランジャー6で加圧する。このときシリンダ2内の空気は、エアベント(溝2a)を介して外部へと流出する。加熱された非晶質合金MGは、溶融した樹脂と同様に柔軟性があるため、わずかな加圧であっても、母型材1の母光学面1aと母幾何寸法基準面1bとの形状に一致するように変形する。
FIG. 4 is a diagram showing a process of forming an optical surface transfer surface and a geometric dimension reference surface transfer surface of an optical surface element molding die by hot press molding. First, as shown in FIG. 4A, the support column 5 is attached to the mother die 4 manufactured in the process shown in FIG. Subsequently, as shown in FIG. 4 (b), the periphery of the mother
更に、図4(c)に示すように、母型4とプランジャー6とを一体で、冷却水が満たされた容器7内に沈下させることで、非晶質合金MGを急冷させる。尚、かかる冷却は自然放冷であっても良い。その後、容器7から取り出した母型4とプランジャー6とを分離させることで、母光学面1aと母幾何寸法基準面1bに対応した光学面転写面MGaと幾何寸法基準面転写面MGbとを形成した光学素子用成形金型10’(図5)を取り出すことができる。深い光学面形状や複雑な光学面形状や酸化しやすい非晶質合金を加熱プレス成形する場合は、加熱、成形、冷却の工程を真空中で行うのが好ましい。
Furthermore, as shown in FIG. 4 (c), the
図5は、光学素子の一例であるレンズを形成するための光学素子用成形金型を含むダイセットの断面図である。上述のようにして非晶質合金MGを成膜した光学素子用成形金型10’と、同様にして非晶質合金MG’を成膜した光学素子用成形金型11’とを、光学面転写面MGa、MGa’同士及び幾何寸法基準面転写面MGb、MGb’同士を対向させるようにして、ダイセット金型13,14に挿入し、溶融したプラスチック材料PLを、不図示のゲートから通常の射出成形と同様に光学素子用成形金型10’,11’間に射出して、更に冷却することで、所望の形状のレンズを得ることができる。尚、ダイセット取り付け用のネジ孔10d’、11dを加工する場合も、非晶質合金MGと異なり、靱性に優れた基体10、11に対して穿孔しタップ切りを行えばよいので、加工時の破損を抑えることができ、また成形時の外力に対しても基体10、11がたわんで応力集中を緩和させる機能を有するため破損が抑制される。
FIG. 5 is a cross-sectional view of a die set including an optical element molding die for forming a lens which is an example of an optical element. The optical element molding die 10 ′ formed with the amorphous alloy MG as described above and the optical element molding die 11 ′ formed with the amorphous alloy MG ′ in the same manner as described above are optical surfaces. The transfer material MGa and MGa ′ and the geometric dimension reference surface transfer surfaces MGb and MGb ′ are opposed to each other so that they are inserted into the die set dies 13 and 14 and the molten plastic material PL is usually fed from a gate (not shown). Similarly to the injection molding, a lens having a desired shape can be obtained by injecting between the optical element molding dies 10 'and 11' and further cooling. In addition, when processing the screw holes 10d ′ and 11d for attaching the die set, unlike the amorphous alloy MG, the
このように本実施の形態では、加熱プレス成形によって光学面転写面MGaや幾何寸法基準面転写面MGbを創成する場合、非晶質合金MGが成膜された部分を重点的に加熱して軟化させ、加熱した母型1に押圧すれば足りる。重要なことは、本実施の形態では、非晶質合金MGは光学素子用成形金型10’全体に用いず、光学面転写面MGaや幾何寸法基準面転写面MGbを形成する層及びその周辺のみに限られており、基体10全体を均一に加熱する必要がないことである。従って、バルク材料の非晶質合金全体を加熱プレス成形する場合に比べて、熱容量が小さく加熱が容易なため温度制御も精度良くでき、プレス変形量も少ないのでプレス時間を大幅に短くできる。これらの特徴は、単に成形プロセスが制御しやすいというだけでなく、加熱中の非晶質合金の結晶化を避けるには非常に都合の良い条件であり、その結果、結晶化を気にすることなく加熱プレス成形を何度もやり直すことができ、それにより鋳潰さなくとも光学面転写面MGa等の形状修正やリサイクルが可能となり、又、優れた物性的特徴を有しながら結晶化しやすいため加熱プレス成形ができなかったような、ある種の非晶質合金についても、光学素子用成形金型ヘの適用が可能となる。
As described above, in the present embodiment, when the optical surface transfer surface MGa and the geometric dimension reference surface transfer surface MGb are created by hot press molding, the portion where the amorphous alloy MG is formed is preferentially heated and softened. It is sufficient to press the heated mother die 1. Importantly, in the present embodiment, the amorphous alloy MG is not used for the entire optical element molding die 10 ′, but the layer forming the optical surface transfer surface MGa and the geometric dimension reference surface transfer surface MGb and its periphery. However, it is not necessary to uniformly heat the
さらに加熱方法を簡便化すると、非晶質合金に光学面転写面や幾何寸法基準面転写面を成形するための母型のみを、成形温度に加熱しておき、これに基体に成膜した非晶質合金を押しつければ(加熱プレス)、非晶質合金が母型との接触表面から成形温度になるに従って軟化し転写成形が進行し、最終的には非晶質合金の全表面が母型に密着したところで成形が完了することになる。このように、加圧力も一定でほとんど制御しなくても成形が可能となるため、極めて簡素な加熱プレス成形装置で高精度に高効率に光学素子用成形金型の光学面転写面や幾何寸法基準面転写面を創成加工できる。また、母型のみを過熱する際は熱容量がさらに小さくなるので、非常に高精度に温度制御が可能となり、オーバーシュートやハンチングなどによる過熱を防ぎ、加熱プレス成形中の非晶質合金の結晶化や融着を効果的に防ぐことができる。 Furthermore, when the heating method is simplified, only the mother die for forming the optical surface transfer surface and the geometric dimension reference surface transfer surface on the amorphous alloy is heated to the forming temperature, and this is formed on the substrate. When the amorphous alloy is pressed (heated press), the amorphous alloy softens as the molding temperature rises from the contact surface with the master mold, and transfer molding proceeds. Molding is completed when it is in close contact with the mold. In this way, molding is possible with constant pressure and almost no control, so the optical surface transfer surface and geometric dimensions of the molding die for optical elements can be produced with high accuracy and high efficiency with an extremely simple hot press molding device. The reference surface transfer surface can be created. In addition, since the heat capacity is further reduced when heating only the matrix, it is possible to control the temperature with extremely high accuracy, preventing overheating due to overshoot and hunting, and crystallization of amorphous alloy during hot press forming And fusion can be effectively prevented.
加熱プレス成形の雰囲気は、通常は非晶質合金の酸化やそれに基づく結晶化を防ぐために真空中で行うことが好ましく、パラジウム系の非晶質合金は大気中で加熱してもほとんど酸化しないため、大気中で加熱プレス成形することができる。この場合、加熱プレス成形装置は、真空雰囲気を維持する必要もなくなるのでさらに簡素なものとすることができ、大気中で直接目視観察しながら加熱プレス成形ができるという利点がある。パラジウム系の非晶質合金としては、Pd40Cu30Ni10P20やPd76Cu6Si18、Pd61Pt15Cu6Si18などがあるが、パラジウムの含有量が少なくとも20mol%以上含有しないと、他の構成原子が酸化したり結晶化しやすくなって、大気中での加熱プレス成形は難しくなる。一方、パラジウムの含有量が80mol%以上では、一般的には、ガラス転移点が存在しなくなり非晶質合金とならない。そのため、大気中で加熱プレス成形を安定して行う非晶質合金の材料としては、パラジウム含有量が20mol%以上かつ80mol%以下であることが好ましい。また、最多含有原子であるパラジウム以外の構成原子から見ると、銅、ニッケル、アルミニウム、シリコン、燐、ボロンのいずれか1つ以上を、少なくとも3mol%以上含有していることが、アモルファス状の非晶質合金とするために必要である。これは、パラジウム系の非晶質合金に限らず、例えば、Zr55Al10Cu30Ni5、Zr57Ti3Al10Ni10Cu20、La65Al15Ni20、La55Al15Ni10Cu20、Co51Fe21Zr8B20、Fe56Cu7Ni7Zr10B20、Mg75Cu15Y10、Mg70Ni20La10等々、ほとんどの系の非晶質合金について言えることである。また、大気雰囲気中での加熱プレス成形では、母型と非晶質合金の成形面とに閉じた空間ができると、空気溜まりとなって加熱プレス成形の転写性を劣化させる場合がある。この場合はパラジウム系の非晶質合金であっても真空中で加熱プレス成形を行うとよい。回折輪帯などの微細構造を光学面に有する光学素子の成形用金型では、特に微細構造部で微小空気溜まりができやすく、その転写性を大きく損ねるので、真空中で加熱プレス成形する方が良い。
The atmosphere for hot press molding is usually preferably performed in vacuum to prevent oxidation of the amorphous alloy and crystallization based on it, since palladium-based amorphous alloy hardly oxidizes even when heated in air. It can be hot press molded in the atmosphere. In this case, the hot press molding apparatus does not need to maintain a vacuum atmosphere and can be further simplified, and there is an advantage that the hot press molding can be performed while directly observing in the air. Examples of the palladium-based amorphous alloy include Pd 40 Cu 30 Ni 10 P 20 , Pd 76 Cu 6 Si 18 , and Pd 61 Pt 15 Cu 6 Si 18 , but do not contain a palladium content of at least 20 mol% or more. Then, other constituent atoms are easily oxidized or crystallized, and hot press molding in the air becomes difficult. On the other hand, when the content of palladium is 80 mol% or more, generally, the glass transition point does not exist and an amorphous alloy is not formed. Therefore, it is preferable that the content of palladium is 20 mol% or more and 80 mol% or less as an amorphous alloy material that stably performs hot press molding in the atmosphere. Further, when viewed from the constituent atoms other than palladium, which is the most abundant atom, it is possible to contain at least 3 mol% of any one or more of copper, nickel, aluminum, silicon, phosphorus, and boron. Necessary to make a crystalline alloy. This is not limited to the amorphous alloy of palladium, for example, Zr 55 Al 10 Cu 30 Ni 5, Zr 57
パラジウム系などの貴金属の非晶質合金を光学素子用成形金型に用いる場合は、バルク材料では金型一つで高価な地金価値があるため、光学素子の成形生産工程でこのように高価で小さな部品を多量に扱うには、保管管理を厳重にするなどのセキュリティ上の問題が避けられなかった。しかし、本実施の形態のごとき光学素子用成形金型では、非晶質合金の膜厚を100μm程度とすることができるため、地金価値はわずかコンマ数パーセントにすぎず、その保管管理は従来と同様で良いという、先の出願の技術に対して、非常に重要な実用上の特徴がある。 When an amorphous alloy of noble metal such as palladium is used for a molding die for an optical element, the bulk material has an expensive bullion value with a single die, and thus is expensive in the optical element molding production process. In order to handle a large amount of small parts, security problems such as strict storage management were inevitable. However, in the molding die for optical elements as in the present embodiment, since the film thickness of the amorphous alloy can be about 100 μm, the bullion value is only a few percent, and the storage management has been conventional There is a very important practical feature to the technology of the earlier application that it may be the same.
本実施の形態の製造方法によって形成された光学素子用成形金型は、従来の金型のような化学メッキ処理が全く不要であり、高精度かつ高効率に光学面転写面の創成ができ、従って高精度な光学素子の光学面を転写成形できるにも関わらず、低コストで短納期かつ従来と同様の生産形態で取り扱えるという優れた特徴がある。さらに、微細構造を有する光学素子の成形用金型も容易に創成可能である。 The optical element molding die formed by the manufacturing method of the present embodiment does not require any chemical plating treatment as in the conventional die, and can create an optical surface transfer surface with high accuracy and high efficiency. Therefore, although the optical surface of the high-precision optical element can be transferred and molded, it has an excellent feature that it can be handled at a low cost, a short delivery time, and a production form similar to the conventional one. Furthermore, a mold for molding an optical element having a fine structure can be easily created.
図6は、このような光学素子用成形金型により形成されるレンズの光学面の例を拡大して示す斜視図である。図6(a)においては、レンズの光学面に、複数の突起の例として微細な円筒Cをマトリクス状に多数形成した構成(等価屈折率領域の微細構造の例)となっている。例えばかかる対物レンズをDVD記録/再生用光ピックアップ装置の対物レンズとして用いた場合、レンズを透過する光は650nm近傍である。そこで、微細な円筒Cの間隔Δを160nmとすると、かかる対物レンズに入射する光は殆ど反射せず、極めて光透過率の高い対物レンズを提供することができる。 FIG. 6 is an enlarged perspective view showing an example of an optical surface of a lens formed by such a molding die for optical elements. 6A shows a configuration in which a large number of fine cylinders C are formed in a matrix on the optical surface of the lens as an example of a plurality of protrusions (an example of a fine structure of an equivalent refractive index region). For example, when such an objective lens is used as an objective lens of a DVD recording / reproducing optical pickup device, the light transmitted through the lens is in the vicinity of 650 nm. Accordingly, when the interval Δ between the minute cylinders C is set to 160 nm, the light incident on the objective lens is hardly reflected, and an objective lens having an extremely high light transmittance can be provided.
図6(b)においては、レンズの光学面に、複数の突起の例として間隔Δで離隔した多数の微細な三角錐Tを形成しており、図6(a)と同様な顕著な効果を有する。この間隔Δとしては、0.1〜0.2μm以下であると散乱を低下させるので好ましい。図6(c)においては、レンズの光学面に、複数の突起の例として間隔Δで離隔した多数のフィンF(構造複屈折の微細構造の例)を形成している。フィンFの長さは、透過する光の波長より長く(上述の例では650nm以上)なっている。かかる構成を備えたレンズは、フィンFに沿った方向に振動面を有する光を透過させるが、フィンFに交差する方向の光は透過させないという、いわゆる偏光効果を奏する。図6(d)においては、レンズの光学面に、光軸を中心とした輪帯構造の例として、光軸方向断面が鋸歯状のブレーズ型回折輪帯Dを形成している。回折輪帯Dに関しては、例えば特開2001−195769号公報に、その形状に応じた効果である色収差補正及び温度補正について詳細に述べられているので、以下の説明を省略する。これ以外の輪帯構造として、NPS、DOE等も形成できる。また、図6(a)〜(c)においては、簡単のために平面上に、それら突起を設けた例を示したが、その底面を球面や非球面等の適宜の曲率半径を持った曲面とし、その曲面上に設けるようにしてもよい。 In FIG. 6B, a large number of fine triangular pyramids T separated by an interval Δ are formed on the optical surface of the lens as an example of a plurality of protrusions, and the same remarkable effect as in FIG. Have. As this space | interval (DELTA), since scattering is reduced as it is 0.1-0.2 micrometer or less, it is preferable. In FIG. 6C, a large number of fins F (example of fine structure of structural birefringence) separated by a distance Δ are formed on the optical surface of the lens as an example of a plurality of protrusions. The length of the fin F is longer than the wavelength of transmitted light (650 nm or more in the above example). A lens having such a configuration has a so-called polarization effect in which light having a vibration surface is transmitted in a direction along the fin F, but light in a direction intersecting the fin F is not transmitted. In FIG. 6D, a blazed diffractive ring zone D having a sawtooth cross section in the optical axis direction is formed on the optical surface of the lens as an example of the ring zone structure centered on the optical axis. Regarding the diffraction zone D, for example, Japanese Patent Laid-Open No. 2001-195769 describes in detail chromatic aberration correction and temperature correction, which are effects according to the shape thereof, and thus the following description is omitted. Other ring zones such as NPS and DOE can be formed. 6A to 6C show an example in which these protrusions are provided on a plane for the sake of simplicity, but the bottom surface is a curved surface having an appropriate curvature radius such as a spherical surface or an aspherical surface. And may be provided on the curved surface.
(金属ガラスの成膜方法)
図7は、金属ガラスの成膜装置を示す概略図である。図7において、筐体200で覆われた処理室Pには、ターゲットTを支持するターゲット支持台201が載置され、それにベース面を対応させるようにして、金型の基体10を保持する試料ホルダ202が配置されている。ターゲット支持台201の内部には冷却配管が形成され、かかる冷却配管には、外部の制御装置203を介して、温度調整用の冷却水を循環させることができるようになっている。
(Metal glass deposition method)
FIG. 7 is a schematic view showing a metal glass film forming apparatus. In FIG. 7, in a processing chamber P covered with a
又、処理室Pは、バルブV1を介してターボ分子ポンプ204に連結され、ターボ分子ポンプ204は、バルブV2を介してロータリーポンプ205に連結されている。処理室P内は、2つのポンプ204,205により吸引されて、10−1〜数Pa程度の圧力にされ、且つAr分子を含んでいる。
The processing chamber P is connected to a turbo
本実施の形態における大きな特徴としては,ターゲットTはアモルファス構造の金属ガラスである必要はなく,膜層を形成しようとする金属ガラスと同じ組成比を有していれば良い。 As a major feature of the present embodiment, the target T does not have to be an amorphous metal glass, and it is sufficient if it has the same composition ratio as the metal glass on which the film layer is to be formed.
次に、金属ガラスの成膜方法について説明する。まず,膜層を形成しようとする金属ガラスと同じ組成比のターゲットTを用意する。ここでは、必要とする組成比の母材を用意し,アーク放電により溶融(アーク炉)して銅鋳型に流し込む方法や,ホットプレスによる焼結法などで,母材を溶融し,図7の成膜装置のターゲットTに適合した型にすると良い。その際,ターゲットTの組成比が、所望する金属ガラスと同じ組成比になるように注意する。例えば,Feを主成分に含む金属ガラスで例をあげれば,Fe56Co7Ni7Zr8Nb2B20系金属ガラスのターゲットをホットプレスによる焼結法にて製作する。この場合は、まずFe,Co,Ni,Zr,Nbの元素を組成比通り用意し,アーク炉で入念に溶解し,混ぜ合わせる。これを溶かした後,十分冷やし,裏表反転させて,再度溶解し混ぜ合わせる。かかる工程を数回繰り返し,溶かしムラがないように,よく溶け合わせる。その後冷却してとりだしあと,粉砕し粉状にする。そののち,組成比通りのB(ホウ素)とあわせて,ホットプレスによって溶融し任意のターゲット形状に焼き固める。その他,Pd76Cu6Si18系金属ガラス等では,Pd,Cu,Siをアーク炉で入念に溶かすだけでターゲットを得ることが出来る。 Next, a method for forming a metal glass will be described. First, a target T having the same composition ratio as that of the metal glass on which the film layer is to be formed is prepared. Here, a base material having the required composition ratio is prepared, melted by arc discharge (arc furnace), poured into a copper mold, or sintered by hot press, etc., and the base material is melted. A mold suitable for the target T of the film forming apparatus may be used. At that time, care is taken that the composition ratio of the target T is the same as that of the desired metallic glass. For example, in the case of a metallic glass containing Fe as a main component, a target of Fe 56 Co 7 Ni 7 Zr 8 Nb 2 B 20 series metallic glass is manufactured by a sintering method using hot pressing. In this case, first, elements of Fe, Co, Ni, Zr, and Nb are prepared according to the composition ratio, and are carefully dissolved and mixed in an arc furnace. After melting this, cool well, invert the inside and outside, dissolve again and mix. Repeat this process several times and melt well to avoid melting unevenness. Then cool it down and grind it into a powder. After that, together with B (boron) according to the composition ratio, it is melted by hot pressing and baked into an arbitrary target shape. In addition, in the case of Pd 76 Cu 6 Si 18- based metallic glass or the like, a target can be obtained only by carefully melting Pd, Cu, Si in an arc furnace.
ここで例をあげた両者に共通なことは,アーク炉やホットプレスで製作したターゲットは多結晶合金で,必ずしもアモルファス構造(金属ガラス)である必要はないということである。もちろん,金属ガラスをそのままターゲットとしても問題ない。Pd40Cu30Ni10P20系金属ガラスでは,非常にアモルファス構造になりやすいため,ターゲットそのものを金属ガラスとすることもある。 What is common to both examples is that the target manufactured by an arc furnace or hot press is a polycrystalline alloy and does not necessarily have an amorphous structure (metallic glass). Of course, there is no problem even if the metallic glass is used as it is. Since Pd 40 Cu 30 Ni 10 P 20- based metallic glass tends to be very amorphous, the target itself may be a metallic glass.
以上のような方法にて製作したターゲットを図7の成膜装置に取り付け,スパッタ成膜を行う。成膜条件は,膜厚等の成膜する条件及び,装置によっても異なるが,1例をあげると,0.5PaのAr雰囲気中で,RF電極(不図示)間に500Wの高周波電圧を印加し,ターゲットTから成膜したい試料(ここでは,金型の基体10のベース面)までの距離を90mmにセットする。ターゲットT上に発生したプラズマのAr粒子が、高速でターゲットTに衝突することにより、その金属粒子が(所定の方向に)はじき飛ばされて、対向した基体10のベース面に付着し堆積して膜層となる。
The target manufactured by the above method is attached to the film forming apparatus shown in FIG. 7, and sputter film formation is performed. The film forming conditions vary depending on the film forming conditions such as the film thickness and the apparatus. For example, a high frequency voltage of 500 W is applied between RF electrodes (not shown) in an Ar atmosphere of 0.5 Pa. Then, the distance from the target T to the sample to be deposited (here, the base surface of the mold base 10) is set to 90 mm. The Ar particles of the plasma generated on the target T collide with the target T at a high speed, so that the metal particles are repelled (in a predetermined direction) and adhere to and deposit on the base surface of the
成膜装置によるが,距離により成膜速度が大体1μm/h〜20μm/hに変化するため適宜調整を行う。試料が近づけば近づくほど成膜速度は上がるが,成膜した膜の粒子が粗くなる等の問題が生ずるため,調整が必要である。又、付着する面が傾いていると、成膜速度が変わる。例をあげると,スパッタ法による成膜では,成膜面の傾き角度θに応じて,膜厚が平面の膜厚をAとすると,A×cosBθという依存式を満たす(ただし,B=0.5〜1の任意値であり、θ=90°以上の角度を除く)。よって,この依存式に応じて膜厚が,角度が大きくなるにつれて薄くなってゆく。前述したように成形転写面の加工時に,金属ガラスの膜厚が十分確保されていないと,成形転写面創成加工の難易度が上昇,あるいは不可能になる。よって,この依存式に応じて,基体10の成形転写面形状は,最終的に求めようとする,金型成形転写面より曲率半径を大きくして製作するか,あるいは,最終的に求めようとする金型成形転写面形状と同じ形状に製作する。それにより、適切な後加工が可能となる。
Although it depends on the film forming apparatus, the film forming speed changes from about 1 μm / h to 20 μm / h depending on the distance, so that adjustment is appropriately made. The closer the sample is, the higher the film forming speed is. However, problems such as coarse particles of the formed film occur, and adjustment is necessary. Further, when the surface to be attached is inclined, the film forming speed changes. For example, in the case of film formation by sputtering, depending on the inclination angle θ of the film formation surface, if the film thickness is A, the dependency formula A × cos Bθ is satisfied (where B = 0. An arbitrary value of 5 to 1, excluding an angle of θ = 90 ° or more). Therefore, the film thickness decreases as the angle increases according to this dependency formula. As described above, if the film thickness of the metal glass is not sufficiently secured during the processing of the molding transfer surface, the difficulty of forming the molding transfer surface increases or becomes impossible. Therefore, according to this dependency formula, the shape and shape of the molding transfer surface of the
この方式で成膜した試料のアモルファス状態の確認は,DSC(熱流束示差走査熱量測定装置)を用いて,アモルファス状態が過冷却液体領域に相転移する際に生ずる吸熱反応を観察するか,あるいはX線回折装置による観察で,アモルファス状態特有の結晶構造によるピークが全く見られないパターンを得ることで,確認することができる。以上のようにして,従来のバルク金属ガラスを製作する方法に比べて遙かに容易に,金属ガラスの膜を金型の基体10におけるベース面に成膜することができる。
Confirmation of the amorphous state of a sample formed by this method can be done by observing the endothermic reaction that occurs when the amorphous state undergoes a phase transition to the supercooled liquid region using a DSC (heat flux differential scanning calorimeter), or This can be confirmed by obtaining a pattern in which no peak due to the crystal structure peculiar to the amorphous state is observed by observation with an X-ray diffractometer. As described above, the metal glass film can be formed on the base surface of the
1 母型材
2 シリンダ
4 母型
5 支柱
6 プランジャー
7 容器
10 基体
10’ 光学素子用成形金型
MG 非晶質合金
DESCRIPTION OF
Claims (37)
前記光学素子用成形金型の基体に、前記成形転写面が凹形状の場合には、前記成形転写面よりも曲率半径が大きい形状でベース面を形成し、前記成形転写面が凸形状の場合には、前記成形転写面よりも曲率半径が小さい形状でベース面を形成する工程と、
前記ベース面に対し、隔置配置された素材から、その材料粒子を飛散させて、過冷却液体領域を有する非晶質合金を堆積させることで膜層を形成する工程と、
前記膜層に所定の加工を施すことで前記成形転写面を得る工程と、を有し、
前記所定の加工とは、光学素子の光学面に対応した母型を加熱して前記ベース面に形成された膜層に押しつける加熱プレス成形か、ダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工か、或いは、光学素子の光学面に対応した母型を加熱して前記ベース面に押しつける加熱プレス成形及びダイヤモンド工具を用いて行う前記ベース面に形成された膜層の切削加工であることを特徴とする光学素子用成形金型の製造方法。 In the manufacturing method of a molding die for optical elements having a molding transfer surface for molding and transferring the optical surface of the optical element,
When the molding transfer surface is concave on the base of the optical element molding die, the base surface is formed with a shape having a larger radius of curvature than the molding transfer surface, and the molding transfer surface is convex. The step of forming the base surface in a shape having a smaller radius of curvature than the molding transfer surface,
A step of forming a film layer by scattering the material particles from a material spaced from the base surface and depositing an amorphous alloy having a supercooled liquid region;
Obtaining the molding transfer surface by applying predetermined processing to the film layer,
The predetermined processing is heating press molding that heats a matrix corresponding to the optical surface of the optical element and presses it against the film layer formed on the base surface, or is formed on the base surface performed using a diamond tool. Cutting of the film layer, or cutting of the film layer formed on the base surface by using a hot press molding that presses the base corresponding to the optical surface of the optical element and pressing it against the base surface and using a diamond tool A method for producing a molding die for optical elements, wherein