JP4335634B2 - Shading solution - Google Patents
Shading solution Download PDFInfo
- Publication number
- JP4335634B2 JP4335634B2 JP2003347892A JP2003347892A JP4335634B2 JP 4335634 B2 JP4335634 B2 JP 4335634B2 JP 2003347892 A JP2003347892 A JP 2003347892A JP 2003347892 A JP2003347892 A JP 2003347892A JP 4335634 B2 JP4335634 B2 JP 4335634B2
- Authority
- JP
- Japan
- Prior art keywords
- light
- film
- shielding
- resin
- shielding coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は、ハウス栽培あるいはトンネル栽培に使用する農業用フィルムに適用する遮光塗布液に関する。 The present invention relates to a light-shielding coating solution applied to an agricultural film used for house cultivation or tunnel cultivation.
ハウス栽培あるいはトンネル栽培に関し、農業用フィルムハウス内で栽培される作物にとって、透過する太陽光線が強すぎ、作物に焼けなどの悪影響を与える場合がある。特に夏場の作物の焼けを防止するため、石灰などの無機物を水に分散させ、農業用ハウスフィルム吹きかけて石灰などの無機物の皮膜を形成させ、遮光するという手段が採用されてきている。しかしながら、この方法では、フィルム上に均一に塗布することが困難であり、また、石灰などの無機物の皮膜が脆いため、長時間維持できず、雨が降ると簡単に流れ落ちてしまう等の欠点があった。 Regarding house cultivation or tunnel cultivation, the transmitted sunlight is too strong for crops cultivated in an agricultural film house, which may adversely affect the crops such as burning. In particular, in order to prevent burning of crops in summer, a method of dispersing inorganic substances such as lime in water and spraying an agricultural house film to form a film of inorganic substances such as lime has been adopted. However, in this method, it is difficult to uniformly apply on the film, and since the inorganic film such as lime is brittle, it cannot be maintained for a long time, and it easily flows down when it rains. there were.
そこで、最近になって、顔料含有の遮光用ペイント（遮光塗料）を農業用フィルムにスプレーで散布・塗布し、フィルム上に遮光塗膜を形成させ、遮光を行う方法が提案されている（特許文献１）。この農業用フィルムに遮光ペイントを散布・塗布する方法にあっては、特定の粘度に調整した顔料含有の白色水性エマルジョン塗料を使用するものであり、フィルム上への遮光塗膜の形成は優れたものである。 Therefore, recently, a method has been proposed in which a pigment-containing light-shielding paint (light-shielding paint) is sprayed and applied to an agricultural film by spraying to form a light-shielding coating film on the film, thereby shielding light (Patent) Reference 1). In the method of spraying and applying the shading paint to this agricultural film, a pigment-containing white aqueous emulsion paint adjusted to a specific viscosity is used, and the formation of the shading coating film on the film is excellent. Is.
しかしながら、この遮光塗布膜が不要になった場合、塗布した遮光塗料を除去しなければならないが、これら塗布膜を形成するエマルジョン塗料自体は、不要時の除去を可能とする処方で配合されているものではない。したがって、例えば、冬場においてハウス内に太陽光線の透過を必要とする場合には、界面活性剤を含有する強力な除去液あるいは有機溶媒等で遮光塗膜を除去するか、新たな農業用フィルムを展張する必要があった。 However, when this light-shielding coating film becomes unnecessary, the applied light-shielding paint must be removed, but the emulsion paint itself that forms these coating films is formulated with a formulation that enables removal when not needed. It is not a thing. Therefore, for example, when it is necessary to transmit sunlight into the house in winter, remove the light-shielding coating with a strong removing liquid containing a surfactant or an organic solvent, or install a new agricultural film. There was a need to expand.
このような点を改良するものとして、最近除去可能な保護コーティングが提案されている（特許文献２）。この除去可能な保護コーティングは、強塩基および錯体形成剤を含む除去液により除去可能な保護コーティングであって、顔料とバインダーとしてビニルポリマー系の高分子化合物を使用したものであり、除去液として強塩基および錯体形成剤としてニトリロ３酢酸の３ナトリウム塩を使用したものである。 In order to improve such points, a protective coating that can be removed recently has been proposed (Patent Document 2). This removable protective coating is a protective coating that can be removed by a remover containing a strong base and a complexing agent, and uses a vinyl polymer polymer as a pigment and a binder. A trisodium salt of nitrilotriacetic acid is used as a base and a complex forming agent.
当該保護コーティング液にあっては、バインダーとして４０〜２５０の酸価を有するビニルポリマー系の高分子化合物を使用している。この酸価は、ポリマー系バインダーについて、１連鎖あたりのフリーカルボン酸基の平均数と関係するものであり、酸価が大きなものであればあるほど、耐水性が無くなり水に溶けやすくなる。また、酸価が小さなものであれば、水に溶けにくい性質を有するものである。この特許文献２で提案されている保護コーティングは、酸価が４０〜２５０と比較的低いものであり、したがって耐水性があり、保護コーティングを除去するためには、除去液中に強塩基化合物ならびに界面活性剤を添加しなくてはならず、そのため液が泡立ち、液の調製がしづらいという問題点があった。 In the protective coating solution, a vinyl polymer polymer compound having an acid value of 40 to 250 is used as a binder. This acid value is related to the average number of free carboxylic acid groups per chain in the polymer-based binder, and the higher the acid value, the less water resistance and the easier it is to dissolve in water. Moreover, if an acid value is small, it has a property which is hard to melt | dissolve in water. The protective coating proposed in this Patent Document 2 has a relatively low acid value of 40 to 250, and is therefore water resistant. In order to remove the protective coating, a strong base compound and There was a problem that the surfactant had to be added, so that the liquid foamed and it was difficult to prepare the liquid.
この点を改良するべく、本発明者は酸価の値について鋭意検討した結果、酸価が４０未満の樹脂を使用した場合であっても、その耐水性が完全に確保されたものではなく、また当該樹脂の特性として、エマルジョンとは異なる分散状態の樹脂ディスパージョンとしてフィルム上に分散・散布され、形成された遮光塗膜は、雨などの水により徐々に流れ落ちるものであることが判明した。したがって、その樹脂ディスパージョン中の樹脂の添加量を適宜調整することにより、フィルム上に形成させる遮光塗膜の持続性の持続時間を調整することができ、特別に除去液を必要としないものであることを確認し、本発明を完成させるに至った。 In order to improve this point, as a result of intensive studies on the value of the acid value, the present inventor has not completely ensured its water resistance even when a resin having an acid value of less than 40 is used. Further, as a characteristic of the resin, it was found that the light-shielding coating film formed by being dispersed and dispersed on the film as a resin dispersion in a dispersed state different from the emulsion gradually flows down due to water such as rain. Therefore, by appropriately adjusting the amount of resin added in the resin dispersion, the duration of the durability of the light-shielding coating film formed on the film can be adjusted, and no special removing liquid is required. It has been confirmed that the present invention has been completed.
したがって本発明は、上記問題点に鑑み、農業用フィルムへ塗布する遮光塗布液として、塗料中に均一に遮光剤を含有させることができ、したがってフィルム上に均一に遮光剤を分散・塗布することにより、簡便に遮光効果が得られ、かつ、フィルム上に形成させる遮光塗膜の耐水性の持続時間を調整することができ、その遮光塗布膜を特別な除去液で除去する必要のない遮光塗布液を提供することを課題とする。 Therefore, in view of the above problems, the present invention can uniformly contain a light-shielding agent in a paint as a light-shielding coating solution to be applied to an agricultural film, and therefore uniformly disperse and apply the light-shielding agent on the film. The light-shielding effect can be easily obtained, and the water-resistant duration of the light-shielding coating film formed on the film can be adjusted, and the light-shielding coating film does not need to be removed with a special removing liquid. It is an object to provide a liquid.
かかる課題を解決するための本発明は、そのひとつの基本的態様として、白色顔料、４０未満の酸価を有する樹脂ディスパージョン、水性溶媒として水からなることを特徴とする遮光塗布液である。 The present invention for solving this problem is a light-shielding coating solution comprising, as one basic aspect thereof, a white pigment, a resin dispersion having an acid value of less than 40, and water as an aqueous solvent.
より具体的な本発明は、水１００重量部に対して白色顔料１〜６０重量部、４０未満の酸価を有する樹脂ディスパージョンを固形分として０．５〜１０重量部添加してなることを特徴とする遮光塗布液である。
この場合、白色顔料としては、チタン白、酸化チタン、炭酸カルシウム、タルク、クレー、シリカ、マイカ、硫酸バリウム等をあげることができるが、なかでも炭酸カルシウムが好結果を与えた。
More specifically, the present invention comprises adding 1 to 60 parts by weight of a white pigment to 100 parts by weight of water and adding 0.5 to 10 parts by weight of a resin dispersion having an acid value of less than 40 as a solid content. This is a characteristic light-shielding coating solution.
In this case, examples of the white pigment include titanium white, titanium oxide, calcium carbonate, talc, clay, silica, mica, barium sulfate, etc. Among them, calcium carbonate gave good results.
また本発明は、別の態様として、農業用フィルム表面に塗布した後、所望のフィルム展張期間が経過すれば、特別な除去液を使用することなく、雨などの水により除去し得るよう持続性を調整した遮光塗布膜に関する。具体的には、農業用フィルムの表面に遮光塗布液を塗布して得られる遮光塗膜において、遮光塗布液が、白色顔料、４０未満の酸価を有する樹脂ディスパージョン、水性溶媒として水からなり、遮光塗布膜の持続性を、遮光塗布液の樹脂ディスパージョンの樹脂固形分を０．５〜１０重量部部の範囲で添加量を調整することを特徴とする遮光塗布膜である。 Further, the present invention, as another aspect, can be removed so that it can be removed by water such as rain without using a special removing liquid after a desired film stretching period has elapsed after being applied to the agricultural film surface. The present invention relates to a light-shielding coating film in which Specifically, in a light-shielding coating film obtained by applying a light-shielding coating solution to the surface of an agricultural film, the light-shielding coating solution comprises a white pigment, a resin dispersion having an acid value of less than 40, and water as an aqueous solvent. The light-shielding coating film is characterized by adjusting the addition amount of the resin solid content of the resin dispersion of the light-shielding coating liquid in the range of 0.5 to 10 parts by weight.
本発明は、特に、遮光塗布液成分中に塗膜形成用の樹脂として、酸価が４０未満である樹脂を使用し、その樹脂がエマルジョンとは異なる樹脂ディスパージョンの形態で使用したこと、さらに樹脂の添加量を調整することにより、その塗膜が不要となった場合には、特別の除去液を使用することなく、雨などにより簡便に除去し得るものであり、したがって、除去液の調製をする必要がない。 In particular, the present invention uses a resin having an acid value of less than 40 as a resin for forming a coating film in the light-shielding coating liquid component, and the resin is used in the form of a resin dispersion different from the emulsion. By adjusting the amount of resin added, when the coating is no longer necessary, it can be easily removed by rain without using a special removal liquid. There is no need to do.
除去液中に含まれる界面活性剤や、有機溶媒は、その種類によっては土壌中に残留し、作物の生育に悪影響を与える。さらに、生育した作物中における残留有機溶媒が問題となり、また、基材となる農業用フィルム自体の物性低下となる場合もある。本発明はこのような悪影響を与える点を回避し得る点に大きな特徴を有するものである。 Depending on the type of the surfactant and organic solvent contained in the removal liquid, they may remain in the soil and adversely affect the growth of the crop. Furthermore, the residual organic solvent in the grown crop becomes a problem, and the physical properties of the agricultural film itself serving as a base material may be lowered. The present invention is greatly characterized in that it can avoid such adverse effects.
また、ディスパージョンタイプの樹脂を使用し、エマルジョンタイプの非水溶性樹脂を使用しない点で、遮光塗布液の泡立ちが少なくなり、液の調製、ならびフィルム上への塗布が容易なものである特徴を有している。特にディスパージョンタイプの樹脂を使用したことより、エマルジョンタイプの非水溶性樹脂を用いた遮光塗布液にみられるフィルム上へ塗布した場合の遮光塗布液の泡たれが無い点で、特に優れたものである特徴を有する。 In addition, it uses dispersion type resin and does not use emulsion type water-insoluble resin, so that foaming of light-shielding coating liquid is reduced, and preparation of liquid and application on film are easy. have. Especially excellent in that there is no foaming of the light-shielding coating solution when it is applied on a film found in a light-shielding coating solution using an emulsion-type water-insoluble resin, since a dispersion type resin is used. It has the characteristic which is.
また本発明により、フィルム上に形成させる遮光塗膜の耐水性の持続時間を調整することができ、その除去にあたっては特別な除去液を必要としない。このような点は、従来の遮光塗布液にはみられない特異的効果である。 In addition, according to the present invention, the water resistance duration of the light-shielding coating film formed on the film can be adjusted, and no special removing liquid is required for the removal. Such a point is a specific effect not found in the conventional light-shielding coating solution.
本発明が提供する遮光塗布液中に含有される、遮光性を確保するために添加される白色顔料としては、チタン白、酸化チタン、炭酸カルシウム、タルク、クレー、シリカ、マイカ、硫酸バリウム等をあげることができる。これらの白色顔料はその１種でも、また複数種を選択し、組合せて使用することができる。 The white pigment contained in the light-shielding coating solution provided by the present invention and added to ensure light-shielding properties includes titanium white, titanium oxide, calcium carbonate, talc, clay, silica, mica, barium sulfate and the like. I can give you. These white pigments can be used alone or in combination.
これらの白色顔料の中でも、炭酸カルシウムを使用するのがよいことが判明した。炭酸カルシウムは、本発明の遮光塗布液中に樹脂とともに含有され、農業フィルムに塗布された場合には、遮光被膜を形成させるものである。この場合の炭酸カルシウムの粒子径は一概には限定できないが、微細な平均粒子径を有する微粉末としての炭酸カルシウムを用いるのがよい。すなわち、当該炭酸カルシウムは、本発明の遮光塗布液中に均一に分散され、遮光性被膜を形成させるものであり、その粒径は微細なものであることが好ましい。なお、粒子径が大きな場合には、遮光塗布液中に炭酸カルシウムが沈降してしまい、塗布することが困難となり、またスプレー塗布を意図した場合には、かかるスプレー塗布ができず、したがって遮光性を確保することが困難となる。このような微細な炭酸カルシウムの中でも、特にコロイド状の炭酸カルシウムを使用するのがよい。 Of these white pigments, it has been found that calcium carbonate should be used. Calcium carbonate is contained together with the resin in the light-shielding coating solution of the present invention, and forms a light-shielding film when applied to an agricultural film. In this case, the particle diameter of calcium carbonate cannot be generally limited, but it is preferable to use calcium carbonate as a fine powder having a fine average particle diameter. That is, the calcium carbonate is uniformly dispersed in the light-shielding coating solution of the present invention to form a light-shielding film, and the particle diameter is preferably fine. When the particle size is large, calcium carbonate settles in the light-shielding coating solution, making it difficult to apply, and when spray coating is intended, such spray coating cannot be performed, and thus the light-shielding property. It becomes difficult to ensure. Among such fine calcium carbonates, it is particularly preferable to use colloidal calcium carbonate.
かかる微細な炭酸カルシウムの含有量としては、遮光剤として所望の遮光効果を発揮し得る量であればよく、水１００重量部に対して１〜６０重量部添加するのがよい。１量部未満であると所望の遮光効果を得ることが困難となり、また６０重量部を超えて添加してもそれ以上の遮光効果が得られず、かえって不経済であり、さらに遮光塗布液をスプレー塗布する際に目詰まりを生じ易く、好ましいものではない。 The content of such fine calcium carbonate may be an amount that can exhibit a desired light-shielding effect as a light-shielding agent, and is preferably added in an amount of 1 to 60 parts by weight with respect to 100 parts by weight of water. If it is less than 1 part by weight, it is difficult to obtain a desired light-shielding effect, and even if added in excess of 60 parts by weight, no further light-shielding effect can be obtained, which is uneconomical. Clogging is likely to occur during spray application, which is not preferable.
また、本発明が提供する農業用フィルムに適用する遮光塗布液においては、遮光塗布液中に含有される樹脂としては、フィルム上に塗布された遮光塗布液が乾燥し、無機遮光材である炭酸カルシウムを均一に保持した樹脂膜を形成するものである樹脂が使用される。 Further, in the light-shielding coating solution applied to the agricultural film provided by the present invention, as the resin contained in the light-shielding coating solution, the light-shielding coating solution applied on the film is dried and carbonic acid which is an inorganic light-shielding material. A resin that forms a resin film in which calcium is uniformly held is used.
当該樹脂としては、その酸価が４０未満であり、数平均分子量が１０，０００〜１００，０００である水分散性の樹脂を使用する。そのような水分散性の樹脂としては、アクリル系樹脂、ウレタン系樹脂、ビニル系樹脂、ポリエステル系樹脂、エポキシ系樹脂等をあげることができるが、なかでも特に酸価が４０未満を有する水分散性アクリル系樹脂、水分散性ウレタン系樹脂が好ましく使用される。 As the resin, a water dispersible resin having an acid value of less than 40 and a number average molecular weight of 10,000 to 100,000 is used. Examples of such water-dispersible resins include acrylic resins, urethane resins, vinyl resins, polyester resins, epoxy resins, and the like, and in particular, water dispersion having an acid value of less than 40. An acrylic resin and a water-dispersible urethane resin are preferably used.
これらの水分散性アクリル系樹脂あるいは水分散性ウレタン系樹脂にあっては、その酸価が４０を超える場合には、形成される樹脂塗膜の持続性が十分ではなく、必要とされる遮光塗布膜の保持期間を満たすことができない。 In these water-dispersible acrylic resins or water-dispersible urethane resins, if the acid value exceeds 40, the formed resin coating film is not sufficiently durable and required light shielding. The retention period of the coating film cannot be satisfied.
本発明が提供する遮光塗布液においては、上記の水分散性アクリル系樹脂あるいは水分散性ウレタン系樹脂は樹脂ディスパージョンタイプの樹脂として使用される。なお、本発明にいうディスパージョンタイプの樹脂とは、水溶性樹脂そのものと樹脂エマルジョンのいずれにも属さない、分散性の樹脂であり、その酸価が４０未満の値を有していることから、持続性がある程度確保されたものであり、遮光塗布液への添加量を調整することにより、塗膜自体の持続性を調整することが可能となる特徴を有している。 In the light-shielding coating solution provided by the present invention, the water-dispersible acrylic resin or the water-dispersible urethane resin is used as a resin dispersion type resin. The dispersion type resin referred to in the present invention is a dispersible resin that does not belong to either the water-soluble resin itself or the resin emulsion, and has an acid value of less than 40. The durability is ensured to some extent, and the durability of the coating film itself can be adjusted by adjusting the amount added to the light-shielding coating solution.
本発明が提供する遮光塗布液中における当該水分散性アクリル系樹脂あるいはウレタン樹脂の含有量は、水１００重量部に対して、樹脂固形分として０．１〜１０重量部添加するのがよい。０．１重量部未満であるとフィルム上への塗膜の形成が不十分なものとなり、また１０重量部を超える場合には、塗布作業性が低下するとともに、塗布後の乾燥に時間がかかり、それに反して塗膜の持続性はそれほど向上せず経済的ではない。 The content of the water-dispersible acrylic resin or urethane resin in the light-shielding coating solution provided by the present invention is preferably 0.1 to 10 parts by weight as a resin solid content with respect to 100 parts by weight of water. If the amount is less than 0.1 parts by weight, the formation of the coating film on the film becomes insufficient. If the amount exceeds 10 parts by weight, the coating workability is lowered and it takes time to dry after coating. On the other hand, the durability of the coating film is not so economical and not economical.
本発明の遮光塗布液には、上記した白色顔料、特に炭酸カルシウムの他に、必要に応じて、さらに硬化剤、防腐剤、増粘剤、減粘剤、分散剤、界面活性剤、酸化防止剤、紫外線吸収剤、アルコール類等を添加することができる。 In addition to the above-mentioned white pigment, particularly calcium carbonate, the light-shielding coating solution of the present invention may further include a curing agent, preservative, thickener, thickener, dispersant, surfactant, and antioxidant as necessary. An agent, an ultraviolet absorber, alcohols and the like can be added.
なお、本発明が提供する遮光塗布液が適用し得る農業フィルムとしては、従来から農業用フィルムとして用いられているものを、いずれも使用することができる。そのようなフィルムの材質としては、例えば、ポリ塩化ビニルフィルム、ポリエステルフィルム、アクリル樹脂系フィルム、ポリエチレン系フィルム、ポリプロピレンフィルム、ポリウレタンフィルム、ガラス、酢酸ビニル系フィルム等を挙げることができる。 In addition, as an agricultural film which can apply the light-shielding coating liquid provided by the present invention, any film conventionally used as an agricultural film can be used. Examples of such a film material include a polyvinyl chloride film, a polyester film, an acrylic resin film, a polyethylene film, a polypropylene film, a polyurethane film, glass, and a vinyl acetate film.
かかる農業用フィルムに対する本発明の遮光塗布液の塗布量は、固形分として０．１〜５０ｇ／ｍ２程度が好ましい。０．１ｇ／ｍ２未満であると、充分な遮光効果を得ることができない。また５０ｇ／ｍ２を超える場合には、塗工作業中に農業用フィルムから樹脂の落滴が生じ、好ましいものではない。 The coating amount of the light-shielding coating solution of the present invention on such an agricultural film is preferably about 0.1 to 50 g / m 2 as a solid content. If it is less than 0.1 g / m 2 , a sufficient light shielding effect cannot be obtained. On the other hand, if it exceeds 50 g / m 2 , the resin drops from the agricultural film during the coating operation, which is not preferable.
かくして、本発明の微細粒子径を有する白色顔料、特に微細炭酸カルシウム、４０未満の酸価を有する樹脂ディスパージョンおよび水性溶媒として水を含有する遮光塗布液は、農業用フィルム上にスプレー散布あるいは塗布されて塗膜を形成し、遮光塗布液中に均一に分散、含有される白色顔料により簡便にその遮光効果を得ることができる。 Thus, the white pigment having a fine particle diameter of the present invention, particularly fine calcium carbonate, a resin dispersion having an acid value of less than 40, and a light-shielding coating solution containing water as an aqueous solvent are sprayed or applied onto an agricultural film. Thus, a coating film is formed, and the light shielding effect can be easily obtained by the white pigment uniformly dispersed and contained in the light shielding coating solution.
また、その遮光性塗膜は、添加する樹脂の酸価の値、ならびにその添加量によりその持続性が調整されている。したがって、遮光塗布液の塗布にあたっては、ハウス内で生育させる作物の種類、使用時期を勘案して、その樹脂の添加量を調整し、塗膜を形成させることにより、その後は雨など、あるいは水の散布により、容易に遮光塗膜を除去し得るのである。 In addition, the durability of the light-shielding coating film is adjusted by the acid value of the resin to be added and the amount of the resin added. Therefore, when applying the light-shielding coating solution, the amount of resin added is adjusted in consideration of the type of crops grown in the house and the period of use, and a coating film is formed. The light-shielding coating film can be easily removed by spraying.
以下に本発明を実施例および比較例により、より詳細に説明するが、本発明はこれらの実施例に限定されるものではない。 EXAMPLES The present invention will be described in more detail with reference to examples and comparative examples below, but the present invention is not limited to these examples.
実施例１〜３：
下記表１に記載の処方（重量部）により、本発明の遮光塗布液を得た。得られた遮光塗布液を農業用ビニルハウスフィルムにスプレー塗工し、その遮光性、塗布性および持続性を一定の基準により評価し、その結果をあわせて表１中に示した。
Examples 1-3 :
The light-shielding coating solution of the present invention was obtained according to the formulation (parts by weight) shown in Table 1 below. The obtained light-shielding coating solution was spray-coated on an agricultural vinyl house film, and its light-shielding properties, coating properties and sustainability were evaluated according to certain criteria. The results are shown in Table 1.
＊１：炭酸カルシウムスラリー：ハイドロカーブ９０（平均粒子径：１．１μｍ、固形分７５％：添加量は固形分量で表示）備北粉化社製
＊２：界面活性剤：Ｌ−７７ 日本ユニカー社製
＊３：アクリル系樹脂Ａ：ＳＰ−５０ＴＦ（水分散性アクリル樹脂：酸価４０未満、固形分３０％：添加量は固形分量で表示）日本純薬社製
* 1: Calcium carbonate slurry: Hydro curve 90 (average particle size: 1.1 μm, solid content: 75%: added amount is indicated by solid content) manufactured by Bihoku Flour & Chemical Co., Ltd. * 2: surfactant: L-77 Nippon Unicar Company * 3: Acrylic resin A: SP-50TF (water-dispersible acrylic resin: acid value less than 40, solid content 30%: added amount is expressed in solid content) manufactured by Nippon Pure Chemical Co., Ltd.
＊５：遮光性については、以下の測定により評価した。
遮光塗布液を塗布した後、室温で乾燥させたフィルムの透明性を、目視により以下の基準で判定した。
◎：均一に白くなり透明感がない。
○：若干不均一であるが、透明感がない。
□：不均一であり、少し透明感がない。
△：かなり不均一であり、透明感がある。
×：全く透明である。
* 5: The light shielding property was evaluated by the following measurement.
After applying the light-shielding coating solution, the transparency of the film dried at room temperature was visually judged according to the following criteria.
A: Uniformly white and not transparent.
○: Slightly non-uniform but not transparent.
□: non-uniform and slightly transparent
Δ: Uneven and transparent.
X: It is completely transparent.
＊６：塗布性は、遮光塗布液をフィルム上に塗布液を塗布した状態を、目視により以下の基準で判定した。
◎：液垂れせず、均一に塗布できる。
○：やや液垂れするが、均一に塗布できる。
□：やや液垂れし、少し不均一になる。
△：液垂れし、不均一になる。
×：液垂れが激しく、不均一になる。
* 6: The applicability was determined visually by the following criteria when the light-shielding coating solution was applied on the film.
(Double-circle): It can apply | coat uniformly, without dripping.
○: Slightly dripping but can be applied uniformly.
□: Slightly dripping and slightly uneven.
Δ: Liquid dripping and non-uniformity.
X: The dripping is severe and non-uniform.
＊７：持続性については、以下の測定により評価した。
遮光塗布液を塗布した後、室温で乾燥させたフィルムを野外に暴露し、塗膜の状態を目視により以下の基準で判定した。
◎：塗布後約６０日間塗膜を保持し、その後流れ落ちる。
○：塗布後約４０日間塗膜を保持し、その後流れ落ちる。
□：塗布後約２０日間塗膜を保持し、その後流れ落ちる。
△：塗布後約１０日間塗膜を保持し、その後流れ落ちる。
×：塗布後塗膜が全て流れ落ちた。
注８：塗布後約６０日間塗膜を保持するが、その後除去には除去液が必要であった。
* 7: Sustainability was evaluated by the following measurement.
After the light-shielding coating solution was applied, the film dried at room temperature was exposed to the outdoors, and the state of the coating film was visually determined according to the following criteria.
(Double-circle): A coating film is hold | maintained for about 60 days after application | coating, and it flows down after that.
○: The coating film is retained for about 40 days after application, and then flows down.
□: The coating film is retained for about 20 days after application, and then flows down.
(Triangle | delta): A coating film is hold | maintained for about 10 days after application | coating, and it flows down after that.
X: All the coating films flowed down after application.
Note 8: The coating film was retained for about 60 days after coating, but a removal liquid was required for removal thereafter.
比較例１〜５：
上記実施例と同様に、下記表２に記載の処方（重量部）により、比較例の遮光塗布液を得た。得られた遮光塗布液を農業用ビニルハウスフィルムにスプレー塗工し、その遮光性、塗布性および持続性を一定の基準により評価し、その結果をあわせて表中に示した。
Comparative Examples 1-5:
In the same manner as in the above Examples, a light-shielding coating solution of Comparative Example was obtained by the formulation (parts by weight) shown in Table 2 below. The obtained light-shielding coating solution was spray-coated on an agricultural vinyl house film, and its light-shielding properties, coating properties and sustainability were evaluated according to certain criteria, and the results are also shown in the table.
表中の＊１〜＊８は表１と同様である。
＊９：アクリル系樹脂Ｂ：ＡＴ−５１５（水分散性アクリル樹脂：酸価約１１０、固形分３０％：添加量は固形分量で表示）日本純薬社製
＊１０：Ａ−６１２（アクリル系エマルジョン樹脂）楠本化成社製
注１１：吹付けができないため評価不能
注１２：吹付けができない。
* 1 to * 8 in the table are the same as in Table 1.
* 9: Acrylic resin B: AT-515 (water-dispersible acrylic resin: acid value about 110, solid content 30%: added amount is indicated by solid content) manufactured by Nippon Pure Chemical Co., Ltd. * 10: A-612 (acrylic type) Emulsion resin) manufactured by Enomoto Kasei Co., Ltd. Note 11: Cannot be sprayed and cannot be evaluated Note 12: Cannot be sprayed.
以上の実施例１〜３および比較例１〜５の結果からも明らかなように、本発明の遮光塗布液は、農業用フィルムへの塗布することで、良好な遮光性が得られ、吹付け塗工性も優れ、フィルム上に形成される塗膜の持続性が調整されており、除去液を使用することなく塗膜が除去し得るものであることが理解される。
これに対して比較例の遮光塗布液は、炭酸カルシウムを含有しないと全く遮光性を確保することができず、また、炭酸カルシウムの含有量が多い場合には、吹付けの際に目詰まりが生じ、吹付け自体が困難なものである。さらに、炭酸カルシウムの平均粒子径が大きい場合には、沈降して塗布できないものであることが理解される。
また、酸価が約１１０である水分散性アクリル系樹脂を使用する本発明の遮光塗布液は、持続性が劣るものであった。
また、水分散性アクリル形樹脂と異なりエマルジョンタイプのアクリル樹脂を使用した場合には、形成された塗膜は、その除去には除去液の使用が必要であった。
As is clear from the results of Examples 1 to 3 and Comparative Examples 1 to 5 described above, the light-shielding coating solution of the present invention can be applied to agricultural films to obtain good light-shielding properties and sprayed. It is understood that the coating property is excellent, the durability of the coating film formed on the film is adjusted, and the coating film can be removed without using a removing liquid.
On the other hand, the light-shielding coating solution of the comparative example cannot ensure light-shielding properties at all unless it contains calcium carbonate, and when the calcium carbonate content is high, clogging occurs during spraying. The spraying itself is difficult. Furthermore, it is understood that when the average particle size of calcium carbonate is large, it cannot settle and cannot be applied.
Moreover, the light-shielding coating solution of the present invention using a water-dispersible acrylic resin having an acid value of about 110 was inferior in sustainability.
In addition, when an emulsion type acrylic resin is used, unlike the water-dispersible acrylic resin, it is necessary to use a removing liquid for removing the formed coating film.
以上記載したように、本発明のハウス栽培あるいはトンネル栽培に使用する農業用フィルムに適用する遮光塗布液は、白色顔料、特に炭酸カルシウム、酸価が４０未満である樹脂ディスパージョン、および水性溶媒として水を含有するものであり、遮光塗布液液中へ炭酸カルシウムを均一に分散させることが可能となり、遮光塗布液液の垂れを防止することができるものである。 As described above, the light-shielding coating solution applied to the agricultural film used for house cultivation or tunnel cultivation of the present invention is a white pigment, particularly calcium carbonate, a resin dispersion having an acid value of less than 40, and an aqueous solvent. It contains water, enables calcium carbonate to be uniformly dispersed in the light-shielding coating solution, and prevents dripping of the light-shielding coating solution.
また、樹脂の酸価が４０未満であるうえに、樹脂をディスパージョンタイプとして使用し、さらにその添加量を調整することにより、形成される遮光塗膜の持続性を調整し得るものであり、遮光性塗膜が不要となった場合においても、特別の除去液を使用することなく、雨などにより簡便に塗膜を除去し得るものであり、有機溶媒、あるいは界面活性剤を含有しなければ除去できない塗膜と異なり、土壌環境へ与える影響が少なく、加えて、ハウス、トンネル等の被覆材を廃棄、交換する必要が無くなり、農業従事者に対して、多大な経費節減をもたらす利点を有している。
In addition, the acid value of the resin is less than 40, the resin is used as a dispersion type, and by adjusting the addition amount, the durability of the light-shielding coating film to be formed can be adjusted. Even when a light-shielding coating film is no longer needed, the coating film can be easily removed by rain, etc. without using a special removing solution, and it must contain no organic solvent or surfactant. Unlike coatings that cannot be removed, it has little impact on the soil environment. In addition, it eliminates the need to dispose of and replace coverings such as houses and tunnels, and has the advantage of greatly reducing costs for farmers. is doing.
Claims (2)