JP3930980B2 - Kneaded rubber composition - Google Patents

Kneaded rubber composition Download PDF

Info

Publication number
JP3930980B2
JP3930980B2 JP24499998A JP24499998A JP3930980B2 JP 3930980 B2 JP3930980 B2 JP 3930980B2 JP 24499998 A JP24499998 A JP 24499998A JP 24499998 A JP24499998 A JP 24499998A JP 3930980 B2 JP3930980 B2 JP 3930980B2
Authority
JP
Japan
Prior art keywords
color
rubber
component
kneading
kneaded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP24499998A
Other languages
Japanese (ja)
Other versions
JP2000072919A (en
Inventor
隆造 山本
Original Assignee
ラビット株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ラビット株式会社 filed Critical ラビット株式会社
Priority to JP24499998A priority Critical patent/JP3930980B2/en
Publication of JP2000072919A publication Critical patent/JP2000072919A/en
Application granted granted Critical
Publication of JP3930980B2 publication Critical patent/JP3930980B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は、揉練又は延伸によりそれ自体が変色する粘弾性体および練り消しゴムに関する。
【0002】
【従来技術】
従来、練り消しゴムとしては、芳香性を呈するもの、揉練時に煙が発生するものなど種々の練り消しゴムが広く利用されている。
【0003】
【発明が解決しようとする課題】
しかし、練り消しゴム自体が利用されている時に変色する練り消しゴムは得られていなかった。また、練り消しゴムなどの粘弾性体が、温度によって変色するものは得られていない。
【0004】
従って、本発明の目的は、揉練又は延伸により変色する粘弾性体を提供することにある。
本発明の他の目的は、揉練又は延伸による熱によって、それ自身が変色する粘弾性体を提供することにある。
本発明のさらに他の目的は、揉練や延伸によって変色する練り消しゴムを提供することにある。
【0005】
【課題を解決するための手段】
本発明者は、鋭意検討の結果、特定の色素成分を含有している練り消しゴムを用いると、揉練又は延伸によりそれ自体が変色することを見出し本発明を完成させた。すなわち、本発明は、揉練又は延伸により変色する変色性色素成分を含有する粘弾性体である。
【0006】
本発明の粘弾性体は、揉練又は延伸により変色する変色性色素成分を含有しているため、揉練又は延伸により粘弾性自体が変色する。従って、当該粘弾性体は、それ自体において、揉練又は延伸前の色と、揉練又は延伸後の色とが異なるという面白さを有している。すなわち、当該粘弾性体を揉んだり、練ったり、又は引き伸ばしたりすると、変色性色素成分が発色又は消色するため、揉練又は延伸前後で異なった色となり、粘弾性体を利用するときの面白さを発現することができる。
【0007】
本発明では、前記変色性色素成分としては、揉練又は延伸による熱によって変色する感熱性色素を用いることができる。粘弾性体を揉んだり、練ったり、引っ張って延ばしたりすると、粘弾性体には熱が発生する。この熱を利用して粘弾性体を変色させることができる。なお、このような揉練又は延伸による熱とは、揉練又は延伸によって、粘弾性体に応力がかかることにより発生する熱であると思われる。
【0008】
変色性色素成分としては、揉練力又は延伸力によって潰れない感熱性マイクロカプセルで構成されており、かつ該感熱性マイクロカプセル内部には、揉練又は延伸による熱によって変色する感熱性着色成分が含有されている変色性色素成分(「感熱変色性色素成分」と称する場合がある)を好適に用いることができる。すなわち、変色性色素成分は、揉練力又は延伸力によって潰れず、かつカプセル内部には揉練又は延伸による熱によって変色する感熱性着色成分が含有された感熱性マイクロカプセルで構成されているので、揉練又は延伸による応力により生じる熱によって、感熱性着色成分が着色又は消色等により変色し、粘弾性体の色が揉練又は延伸の前後で変化する。
【0009】
従って、このような感熱性マイクロカプセルを用いる方法では、容易に、揉練又は延伸前後において、粘弾性体の色を異なる色に調整することができる。また、粘弾性体の変色前後の色として種々の色を選択することができ、粘弾性体の色を多様化することもできる。
【0010】
このような粘弾性体は、練り消しゴムとして好適に用いることができる。すなわち、練り消しゴムの色を使用時に変化させることができるため、練り消しゴムの利用者は、本来の揉む或いは練る、又は引き伸ばすという遊びの面白さに加えて、練り消しゴム自体が変色するという面白さを味わうことができる。なお、揉練とは、揉んだり、練ったりすることをいう。
【0011】
【発明の実施の形態】
本発明の粘弾性体、特に練り消しゴムの特色は、揉練又は延伸により変色する変色性色素成分を含有していることにある。このような変色性色素成分としては、感熱変色性色素成分を好適に用いることができる。また、熱により変色する変色性色素成分として、例えば、縮合芳香環置換エチレン誘導体などを用いることができる。
【0012】
(感熱変色性色素成分)
感熱変色性色素成分は、揉練力又は延伸力によって潰れない感熱性マイクロカプセルで構成されており、かつ該感熱性マイクロカプセル内部には、揉練又は延伸による熱によって変色する感熱性着色成分が含有されている変色性色素成分で構成されている。感熱性着色成分としては、例えば、染料、顕色剤、及び感熱温度で溶融する減感剤の組み合わせを用いることができる。すなわち、当該粘弾性体では、感熱性マイクロカプセル内で、感熱温度以下において、染料と顕色剤とが互いに接触して両者が反応することにより発色しており、感熱温度以下では固体の減感剤が染料及び顕色剤と組み合わされてカプセル内に含有されており、揉練又は延伸時などにおいて、粘弾性体内の温度が感熱温度以上になると、減感剤が溶融することにより、染料と顕色剤とが分離されて消色し、粘弾性体の色が変化する。なお、染料と顕色剤とが反応することにより消色し、感熱温度以上になると、染料と顕色剤との反応が消失することにより発色するメカニズムなどであってもよい。
【0013】
このような粘弾性体は感熱温度以上になると変色することができるため、感熱温度が体温より低い場合、触っただけでも変色する場合がある。
【0014】
また、揉練又は延伸時に発生する熱による粘弾性体の温度上昇がおさまり、粘弾性体の温度が感熱温度以下に低下すると、粘弾性体の色が変化する可逆的な変色を有していてもよい。このような可逆的な変色では、感熱温度以下になると、通常、粘弾性体の色は元の粘弾性体の色にもどる。すなわち、本発明では、感熱変色性色素成分としては、例えば、揉練又は延伸時に発生する熱により有色から無色に変色し、該変色温度の温度を下回ると無色から有色に変色する可逆的な変色性色素成分を採用することができる。もちろん、揉練又は延伸時に発生する熱により有色から他の有色に変色し、変色温度以下に温度が低下すると、元の有色に変色する可逆的な変色性色素成分も採用することができる。
【0015】
もちろん、本発明では、感熱変色性色素成分を含有する粘弾性体において、粘弾性体の変色は、前述のような可逆的な変色であってもよく、不可逆的な変色であってもよい。
【0016】
(感熱変色性色素成分の染料)
感熱変色性色素成分において、好ましい態様では、感熱性着色成分は、染料、顕色剤、及び感熱温度で溶融する減感剤を含有している。なお、このような組成で感熱性着色成分が構成されていると、前述の可逆的な変色を達成することができる。
【0017】
感熱性着色成分の染料としては、例えば、ロイコ染料を好適に用いることができる。より具体的には、染料としては、例えば、トリフェニルメタンフタリド類(例えば、クリスタルバイオレットラクトン、マラカイトグリーンラクトンなど)、フルオラン類、ロイコオーラミン類(例えば、ベンゾイルロイコメチレンブルーなど)、ローダミンラクタム類(例えば、2−{3,6−ビス(ジエチルアミノ)−9−(o−クロロアニリノ)キサンチル安息香酸ラクタムなど)、スピロピラン類(例えば、6´−クロロ−8´−メトキシ−ベンゾインドリノ−スピロピラン、6´−ブロモ−3´−メトキシ−ベンゾインドリノ−スピロピランなど)、ポリアリールカルビノール類(例えば、クリスタルバイオレットカルビノール、マラカイトグリーンカルビノールなど)、インドリン類(例えば、2−(フェニルイミノエチリデン)−3,3−ジメチルインドリンなど)などを用いることができる。染料は単独で又は二種以上組み合わせて使用することができる。本発明では、染料の種類により色を調整することができる。もちろん、染料の使用量により発色の濃度を調整することができる。
【0018】
染料としては、トリフェニルメタンフタリド類、フルオラン類、ロイコオーラミン類を好適に用いることができる。
【0019】
より具体的には、前記トリフェニルメタンフタリド類としては、例えば、3,3−ビス(p−ジメチルアミノフェニル)フタリド、3,3−ビス(p−ジメチルアミノフェニル)−6−ジメチルアミノフタリド、3,3−ビス(p−ジメチルアミノフェニル)−6−クロロフタリド、3−(2´−ヒドロキシ−4´−ジメチルアミノフェニル)−3−(2´−メトキシ−5´−クロロフェニル)フタリド、3−(2´−ヒドロキシ−4´−ジメチルアミノフェニル)−3−(2´−メトキシ−5´−ニトロフェニル)フタリド、3−(2´−ヒドロキシ−4´−ジエチルアミノフェニル)−3−(2´−メトキシ−5´−メチルフェニル)フタリド、3−(2´−メトキシ−4´−ジメチルアミノフェニル)−3−(2´−ヒドロキシ−4´−クロロ−5´−メチルフェニル)フタリドなどが例示できる。
【0020】
フルオラン類には、例えば、3−シクロヘキシルアミノ−6−クロロフルオラン、3−ジメチルアミノ−5,7−ジメチルフルオラン、3−ジエチルアミノ−7−クロロフルオラン、3−ジエチルアミノ−7−メチルフルオラン、3−ジエチルアミノ−6−メチル−7−クロロフルオラン、2−(N−フェニル−N−メチルアミノ)−6−(N−P−トリル−N−エチルアミノ)フルオラン、3−(N−p−トリル−N−エチルアミノ)−6−メチル−7−アニリノフルオラン、3−ピロリジノ−6−メチル−7−アニリノフルオラン、3−ジエチルアミノ−7,8−ベンズフルオラン、2−{N−(3−トリフルオロメチルフェニル)アミノ}−ジエチルアミノフルオラン、3−ジエチルアミノ−7−(o−クロロアニリノ)フルオラン、3−ジブチルアミノ−7−(o−クロロアニリノ)フルオラン、3−(N−メチル−N−アミルアミノ)−6−メチル−7−アニリノフルオラン、3−(N−メチル−N−シクロヘキシルアミノ)−6−メチル−7−アニリノフルオラン、3−ジエチルアミノ−6−メチル−7−アニリノフルオラン、3−(N,N−ジエチルアミノ)−5−メチル−7−(N,N−ジベンジルアミノ)フルオラン、3−ジエチルアミノ−5−クロロ−7−(N−トリフルオロメチルアニリノ)フルオラン、3−ジエチル−5−クロロ−7−(α−フェニルエチルアミノ)フルオラン、3−(N−エチル−p−トルイジノ)7−(α−フェニルエチルアミノ)フルオラン、3−ジエチルアミノ−7−(o−メトキシカルボニルフェニルアミノ)フルオラン、3−ジエチルアミノ−5−メチル−7−(α−フェニルエチルアミノ)フルオラン、3−ジエチルアミノ−7−ピペリジノフルオラン、2−クロロ−3−(N−メチルトルイジノ)−7−(p−n−ブチルアニリノ)フルオラン、3−(N−メチル−N−イソプロピルアミノ)−6−メチル−7−アニリノフルオラン、3−ジブチルアミノ−6−メチル−7−アニリノフルオラン、3−{N−エチル−N−(2−エトキシプロピル)アミノ}−6−メチル−7−アニリノフルオラン、3−(N−ベンジル−N−シクロヘキシルアミノ)−5,6−ベンゾ−7−α−ナフチルアミノ−4´−ブロモフルオラン、3−ジエチルアミノ−6−クロロ−7−アニリノフルオラン、3−ジエチルアミノ−6−メチル−メシチジノ−4´,5´−ベンゾフルオラン、3−N−メチル−N−イソブチル−6−メチル−7−アニリノフルオラン、3−N−メチル−N−イソアミル−6−メチル−7−アニリノフルオラン、3−ジエチルアミノ−6−メチル−7−(2´,5´−ジメチルアニリノ)フルオランなどが含まれる。
【0021】
(感熱変色性色素成分の顕色剤)
感熱変色性色素成分において、顕色剤としては、電子受容性化合物、例えば、固体酸や、フェノール系の化合物を好適に用いることができる。顕色剤としては、固体又は液体のものを用いることができる。なお、固体酸とは、「常温で固体の電子受容性化合物」のことを意味している。顕色剤は単独で又は二種以上組み合わせて使用することができる。なお、感熱変色性色素成分の顕色剤として、公知の顕色剤も使用することは可能である。
【0022】
固体酸には、例えば、無機系固体酸(金属の酸化物、金属の硫化物、金属の硫酸塩、金属のリン酸塩などの金属化合物、活性粘土などの粘土鉱質、ゼオライトなど)、有機系固体酸(例えば、フェノール系樹脂、サリチル酸又はその誘導体並びにこれらの塩など)などが含まれる。前記活性粘土としては、例えば、活性白土、酸性白土、モンモリロナイトなどが例示できる。フェノール系樹脂としては、慣用のフェノール系樹脂を用いることができる。フェノール系樹脂の分子量としては特に制限されない。
【0023】
本発明では、顕色剤としてはフェノール系化合物を好適に用いることができる。特に、本発明では、感熱変色性色素成分の顕色剤としては、フェノール性水酸基を1又は2以上有する化合物、例えば、モノフェノール類、ジフェノール類、トリフェノール類などを好適に使用できる。
【0024】
モノフェノール類には、例えば、モノヒドロキシフェニル系化合物(例えば、4−ヒドロキシベンゾフェノン、p−ヒドロキシジフェニル、4−ヒドロキシジフェニルアミン、p−クミルフェノール、p−フェノールスルホンアミド、4−ヒドロキシベンゼンスルホン酸メチル、4−ヒドロキシフェニルメチルケトンなど)、フェニルカルボン酸系化合物(例えば、p−ヒドロキシ安息香酸ベンジルなどのオキシ安息香酸エステル、2−ヒドロキシフタル酸ジメチルエステル、2−ヒドロキシフタル酸ジフェニルエステルなどのオキシフタル酸エステル、4´−ヒドロキシサリチル酸アニリド、5−ベンジルサリチル酸アニリドなど)、モノヒドロキシナフタレン系化合物(例えば、α−ナフトール、β−ナフトール、2−メチル−1−ナフトール、8−アミノ−2−ナフトールなどのオキシナフタレン、1−オキシ−2−ナフトエ酸、2−オキシ−3−ナフトエ酸などのオキシナフトエ酸、2−アセトナフトン、ヒドロキシナフタレンスルホン酸など)などが含まれる。
【0025】
ジフェノール類としては、例えば、ビスフェノール系化合物、ジヒドロキシナフタレン系化合物(例えば、1,3−ジオキシナフタレン、1,4−ジオキシナフタレンなどのジオキシナフタレン、1,4−ジヒドロキシナフタレンモノプロピルエーテルなどのジオキシナフタレンアルキルエーテル、1,4−ジヒドロキシナフタレンモノベンジルエーテルなどのジオキシナフタレンアリールエーテルなど)などが挙げられる。
【0026】
ビスフェノール系化合物には、例えば、式(1a)〜(1f)で表される化合物などが含まれる。
【0027】
【化1】

Figure 0003930980
【化2】
Figure 0003930980
【化3】
Figure 0003930980
【化4】
Figure 0003930980
【化5】
Figure 0003930980
【化6】
Figure 0003930980
【化7】
Figure 0003930980
(式1a〜1fにおいて、R、Rは同一又は異なって、アルキル基を示す。Rはアルキレン基、シクロアルキレン基、アリーレン基であり、Rはアルキレン基である。nは1〜10の整数である)
【0028】
式(1a)〜(1f)において、アルキル基には、例えば、メチル、エチル、プロピル、イソプロピル、ブチル基などの炭素数1〜10程度の直鎖状又は分岐鎖状のアルキル基(好ましくは炭素数1〜6のアルキル基)が含まれる。アルキレン基としては、例えば、メチレン、エチレン、プロピレン基などの炭素数1〜10程度のアルキレン基が例示できる。シクロアルキレン基には、例えば、シクロヘキシレン基などが含まれ、アリーレン基には、例えば、フェニレン基などが含まれる。また、nは1〜10の整数である。
【0029】
より具体的には、ビスフェノール系化合物としては、例えば、メチレンビスフェノール、4,4´−エチリデンビスフェノール、4,4´−(2−エチルヘキシリデン)ビスフェノールなどが例示できる。
【0030】
トリフェノール類としては、例えば、3,4,5−トリヒドロキシ安息香酸−C1−18アルキルエステル化合物などを使用できる。
【0031】
顕色剤としては、フェノール系化合物の中でもジフェノール類、特にビスフェノール系化合物が好適に使用される。顕色剤の使用量は、特に制限されず、例えば、感熱変色性色素成分の染料1重量部に対して0.1〜5重量部、好ましくは0.5〜3重量部程度である。本発明では、顕色剤の種類や使用量により発色の濃度を調整することができる。
【0032】
(感熱変色性色素成分の減感剤)
減感剤としては、感熱温度で溶融する又は融解する化合物を用いることができる。なお、感熱温度とは、「揉練又は延伸によって発生する熱による特定の温度」のことをいう。
【0033】
減感剤としては、室温から、揉練又は延伸によって発生する熱による温度が最大である温度(例えば、50℃程度)までの間で溶融又は融解する化合物を用いることができる。本発明では、粘弾性体を手によって揉んだり、練ったり、引き伸ばしたりすることを考慮すると、融点が、例えば、26〜50℃である減感剤を好適に用いることができる。特に、減感剤の融点が26〜37℃であると、当該粘弾性体は、揉練又は延伸時に発生する熱により粘弾性体が変色するとともに、手で触ったところも体温により変色する。一方、減感剤の融点が38℃以上(例えば、38〜50℃)であると、当該粘弾性体は、手で触ったところは体温によっては変色せず、揉練や延伸により粘弾性体の温度が38℃以上になると、粘弾性体自体が変色する。
【0034】
減感剤としては、例えば、脂肪族系高級アルコール類、芳香族系アルコール(例えば、フェノール、o−クレゾール、p−クレゾールなど)、脂肪族系高級脂肪酸類、脂肪族系高級脂肪酸エステル類(例えば、オクタデカン酸メチルなどの脂肪族系高級脂肪酸アルキルエステル類など)などが挙げられる。減感剤としては、高級アルコール類、高級脂肪酸類を好適に用いることができる。高級アルコール類としては、例えば、1−ドデカノール、1−テトラデカノール、1−ヘキサデカノール、1−オクタデカノールなどの炭素数12〜18程度(好ましくは14〜18)の直鎖飽和脂肪族系アルコールが挙げられる。高級脂肪酸類としては、例えば、デカン酸、ドデカン酸、テトラデカン酸などの炭素数10〜16程度の直鎖飽和脂肪族系脂肪酸などが挙げられる。減感剤は単独で又は二種以上組み合わせて使用することができる。
【0035】
減感剤の使用量は、特に制限されない。減感剤の使用量は、感熱性マイクロカプセル内において、感熱温度以下では染料及び顕色剤を接触させ、かつ感熱温度以上では染料及び顕色剤を接触させないような量であればよい。本発明では、減感剤の種類により変色の温度を調整することができる。
【0036】
(感熱変色性色素成分の感熱性マイクロカプセル)
本発明では、前記感熱性着色成分(例えば、染料、顕色剤及び減感剤)は感熱性マイクロカプセル内に含有させて用いることができる。このような感熱性マイクロカプセルの壁材としては、例えば、アクリル系樹脂、アミド系樹脂、ウレタン系樹脂、エポキシ系樹脂、メラミン系樹脂(例えば、メラミン−ホルムアルデヒド樹脂など)、尿素系樹脂(例えば、尿素−メラミン−ホルムアルデヒド樹脂など)などの種々の樹脂を用いることができる。壁材としての樹脂は単独で又は二種以上組み合わせて使用することができる。感熱性マイクロカプセルとしては、揉練又は延伸時の力により潰れない又は壊れないことが必要であるので、感熱性マイクロカプセルの壁材としては、メラミン系樹脂、尿素系樹脂を、特にメラミン系樹脂を好適に使用することができる。また、容易には潰れないようにするために、特に、感熱性マイクロカプセルとしては二重壁を構成していることが好ましい。なお、感熱性マイクロカプセルとしては粉体状又はペースト状の形態を有していることが好ましい。感熱性マイクロカプセルの大きさは、例えば、直径が0.5〜200μm、好ましくは1〜30μmである。
【0037】
感熱性着色成分(例えば、染料、顕色剤及び減感剤)を感熱性マイクロカプセルに内包する方法としては、慣用的に使用されている方法(例えば、in situ重合方法、界面重合方法、コンセルベーション方法など)を採用して行うことができる。これらの重合方法では公知の重合条件を適用することができ、例えば、特開昭53−84883号公報、特開平7−324178号公報などに記載されている条件を適用することができる。また、特開平5−7767号公報に記載されている方法を採用することにより、二重壁を有している感熱性マイクロカプセルを調製することができる。なお、重合に際しては、例えば、染料及び顕色剤を減感剤に分散させたものを芯材として用いることができる。
【0038】
感熱性着色成分は単独で又は二種以上組み合わせて使用することができる。例えば、可逆的に変色することができ、かつ変色温度が異なる複数の(例えば、2種類の)感熱性着色成分を用いると、粘弾性体は段階的に変色する。このような段階的に変色する場合では、特に粘弾性体の温度が感熱温度以上から室温に低下する場合に段階的に変色しやすく、粘弾性体が時間とともに段階的に元の色に戻ることを視認できるため、極めて面白い。
【0039】
なお、本発明では、感熱変色性色素成分としては、商品名:TCパウダー(株式会社サクラクレパス社製)を用いることができる。より具体的には、感熱変色性色素成分としては、例えば、商品名:TCパウダーローズ、商品名:TCパウダーオレンジ、商品名:TCパウダーイエロー、商品名:TCパウダーブルー、商品名:TCパウダーグリーン(以上、株式会社サクラクレパス製)などが挙げられる。
【0040】
(粘弾性体)
変色性色素成分(例えば、感熱変色性色素成分)は単独で又は二種以上組み合わせて使用することができる。本発明では、変色性色素成分としては種々の組み合わせで用いることが可能であり、当該組み合わせが多数あるため、種々の面白さを有している粘弾性体、特に練り消しゴムを調製することができる。
【0041】
本発明の粘弾性体、特に練り消しゴムは、前記変色性色素成分と、粘弾性材料とを少なくとも含んでいる。粘弾性材料としては、特に制限されず、例えば、ゴム成分、樹脂成分、エラストマー成分などを用いることができる。
【0042】
(ゴム成分含有粘弾性体)
本発明では、ゴム成分含有粘弾性体としては、変色性色素成分と、公知のゴム成分とで構成することができ、必要に応じて各種添加剤などを用いることができる。すなわち、ゴム成分含有粘弾性体には、変色性色素成分の他、ゴム成分、軟化剤、充填剤、老化防止剤、着色剤などが含有されていてもよい。
【0043】
ゴム成分としては、特に制限されず、例えば、天然ゴム(例えば、いわゆる生ゴムなど)、合成ゴム(例えば、ブタジエンゴム、スチレン−ブタジエンゴム、イソブチレン−イソプレンゴム、アクリロニトリル−ブタジエンゴム、ブチルゴムなど)を用いることができる。
【0044】
軟化剤としては、特に制限されず、例えば、鉱物油(例えば、エキステンダー油、プロセスオイル、流動パラフィン、モーター油、タービン油、マシン油など)、植物系油脂(例えば、菜種油、綿実油、大豆油など)、脂肪酸、ワックス類、フタル酸系可塑剤、シリコン系オイル、フッ素系オイルなどが挙げられる。
【0045】
シリコン系オイルとしては、例えば、商品名「KF69」(信越化学株式会社製)、商品名「KF352」(信越化学株式会社製)などのシリコーンオイルを用いることができる。
【0046】
特に、軟化剤としてシリコン系オイルを用いると、引っ張っても切れにくく、切れずに延ばし続けることができる粘弾性体、すなわち延性が高い粘弾性体(練り消しゴムなど)を調製することができる。
【0047】
充填剤としては、公知の充填剤、例えば、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウム、シリカ、タルク、クレー、珪藻土、石英粉、アルミナ、アルミナシリケート、マイカ、ファクティス(例えば、菜種油、綿実油、大豆油などに塩化硫黄を反応させたもの)などを用いることができる。
【0048】
老化防止剤としては、例えば、アルデヒドアミン類、第2級アミン類、フェニレンジアミン類、フェノール類などが挙げられる。
【0049】
さらに、着色剤としては、有機顔料、無機顔料、蛍光顔料などの種々の公知の顔料や、染料などを用いることができる。
【0050】
ゴム成分含有粘弾性体において、変色性色素成分の割合は特に制限されず、他の含有されている成分の種類などに応じて選択することができる。
【0051】
ゴム成分含有粘弾性体が、例えば、変色性色素成分、ゴム成分、軟化剤、充填剤、老化防止剤及び着色剤で構成されている場合、変色性色素成分の割合は、例えば、粘弾性体全量に対して0.2〜30重量%、好ましくは0.5〜10重量%の範囲から選択することができる。変色性色素成分の含有量が粘弾性体全量に対して0.2重量%より少ないと変色の効果が低い。一方、30重量%より多いと粉っぽくなり、また延性が低下して引き伸ばしたときに切れやすくなる。
【0052】
また、ゴム成分の割合は、例えば、粘弾性体全量に対して5〜65重量%、好ましくは10〜55重量%の範囲から選択することができる。ゴム成分の含有量が粘弾性体全量に対して5重量%より少ないと粘弾性が低下する。一方、65重量%より多いと粘弾性体は硬くなり引っ張ることが困難になり、また揉んだり練ったりすることも困難になる。
【0053】
軟化剤の割合は、例えば、粘弾性体全量に対して3〜55重量%、好ましくは10〜45重量%の範囲から選択することができる。軟化剤の含有量が粘弾性体全量に対して3重量%より少ないと粘弾性体の粘度が高くなって脆くなり、延伸や揉練を行うことが困難になる。一方、55重量%より多いと粘弾性体の粘度が低くなりすぎたり、粘弾性体の表面がべたついたりするようになり、また、揉練や延伸による発熱が抑えられ、熱が発生しにくくなる。
【0054】
充填剤の割合は、例えば、粘弾性体全量に対して1〜70重量%、好ましくは5〜60重量%の範囲から選択することができる。充填剤の含有量が粘弾性体全量に対して70重量%より多いと粘弾性体は粉っぽくなり、ちぎれ易くなる。
【0055】
老化防止剤の割合は、例えば、粘弾性体全量に対して0〜5重量%、好ましくは0.1〜2重量%の範囲から選択することができる。着色剤の割合は、例えば、粘弾性体全量に対して0〜30重量%、好ましくは0〜10重量%の範囲から選択することができる。
【0056】
なお、粘弾性材料として樹脂成分を用いる場合、熱可塑性樹脂と、可塑剤、充填剤、安定剤、着色剤などとを組み合わせて用いる場合が多い。また、粘弾性材料としてエラストマー成分を用いる場合は、熱可塑性エラストマーと、軟化剤、充填剤、安定剤、着色剤などとを組み合わせて用いる場合が多い。
【0057】
本発明の粘弾性体は、紫外線吸収剤、光安定剤などの安定剤や、他の慣用的に使用されている添加剤、香料、ポリオレフィン系樹脂などの熱可塑性樹脂などを含んでいてもよい。
【0058】
(粘弾性体の調製方法)
本発明の粘弾性体又は練り消しゴムは、前記成分(例えば、変色性色素成分や、粘弾性材料など)を混合して調製することができる。粘弾性体の調製に際しては、ニーダーやバンバリミキサーなどの混合機、押し出し成形機の他、インジェクション成形機、プレス成形機などを用いることができる。
【0059】
なお、ゴム成分含有粘弾性体の調製に際しては、加硫を行ってもよいが、加硫を行う必要はない。本発明では、通常、加硫操作は行われない。
【0060】
特に、ゴム成分含有粘弾性体において、延伸により変色する変色性色素成分を含有する場合は、軟化剤としてシリコン系オイルを含んでいる場合が多い。一方、揉練により変色する変色性色素成分を含有する場合は、軟化剤としてシリコン系オイルを用いてもよく、用いなくてもよい。
【0061】
本発明の粘弾性体は揉練や延伸によって変色するため、練り消しゴム、粘土おもちゃなどの粘弾性を利用したおもちゃ又は玩具、特に練り消しゴムとして有用である。特に練り消しゴムにおいては、揉んだり、練ったり、引っ張ったりしているうちに、練り消しゴムが変色するので、揉んだり、練ったり、引っ張ったりするという練り消しゴム本来の遊びである揉練や延伸に加えて、練り消しゴムが揉練や延伸の程度に応じて変色するという面白さがある。
【0062】
本発明の粘弾性体の変色する温度、特に練り消しゴムの変色する温度は、特に制限されない。例えば、粘弾性体、特に練り消しゴムは26〜50℃程度で変色するように調整することができる。従って、粘弾性体、特に練り消しゴムは、揉練や延伸によって容易に変色する。なお、粘弾性体又は練り消しゴムにおいて、前記感熱変色性色素成分を用い、減感剤が含まれている場合、染料と顕色剤との組み合わせ、および減感剤の種類によって、感熱温度がコントロールされる。
【0063】
本発明の粘弾性体又は練り消しゴムでは、変色性色素成分と、着色剤とを組み合わせて用いると、粘弾性体又は練り消しゴムの色を種々の色に調整することができ、粘弾性体の色を多様化することができるので、さらに、面白さや綺麗さを付与することができる。従って、本発明では、変色性色素成分と着色剤とを組み合わせて用いることは極めて好ましい。
【0064】
本発明の粘弾性体、特に練り消しゴムは、それ自体が揉練や延伸によって変色するという面白さを有しているので、揉練や延伸させるという動作にも面白さを消費者に提供することができるため、粘弾性体、特に練り消しゴムは産業上極めて有用である。
【0065】
【実施例】
以下、本発明を実施例によって詳細に説明する。なお、本発明はこれらの実施例に限定されるものではない。
【0066】
(実施例1)
感熱性マイクロカプセル(商品名:TCパウダー38℃ローズ、サクラクレパス社製):2重量部、ゴム成分(アクリロニトリル−ブタジエンゴム、商品名:JSR N230SL、日本合成ゴム社製):50重量部、軟化剤(商品名:スピンドル油#60、シェル石油社製):26重量部、軟化剤(シリコーンオイル、商品名:KF69、信越化学社製):10重量部、充填剤(シリカ、商品名:カープレックス#1120、塩野義製薬社製):10重量部、着色剤(酸化チタン、商品名:TITANIX JR−805、TAYCA社製):0.6重量部、着色剤(フタロシアニングリーン):0.4重量部、香料:1重量部の割合で、バンバリミキサーを用いて慣用の方法により混合し、練り消しゴムを調製した。当該練り消しゴムは柔らかく、揉練、延伸を行うことができ、練り消しゴムとして好適に用いることができる粘度を有している。特に、延性が優れており、有限ではあるが、かなり引き延ばし続けることができる。
【0067】
(実施例2)
感熱性マイクロカプセル(商品名:TCパウダー45℃グリーン、サクラクレパス社製):2重量部、ゴム成分(スチレン−ブタジエンゴム、商品名:JSR1500、日本合成ゴム社製):26重量部、軟化剤(ペトロラタム、商品名:ペトロラタムNo.5、山文油化社製):7重量部、軟化剤(商品名:スピンドル油#60、シェル石油社製):15重量部、充填剤(ファクティス、商品名:白サブ1、天満サブ化学工業社製):26重量部、充填剤(炭酸カルシウム、商品名:白艶華0、白石工業社製):20重量部、着色剤(酸化チタン、商品名:TITANIX JR−805、TAYCA社製):3.5重量部、着色剤(ナフトールレッド):0.5重量部の割合であること以外、実施例1と同様にして練り消しゴムを調製した。当該練り消しゴムは柔らかく、揉練、延伸を行うことができ、練り消しゴムとして好適に用いることができる粘度を有している。
【0068】
(実施例3)
感熱性マイクロカプセル(商品名:TCパウダー32℃ブルー、サクラクレパス社製):3重量部、ゴム成分(ブタジエンゴム、商品名:ニポールBR1220、日本ゼオン社製):13重量部、軟化剤(流動パラフィン):15重量部、充填剤(ファクティス、商品名:白サブ1、天満サブ化学工業社製):47重量部、充填剤(炭酸カルシウム、商品名:白艶華0、白石工業社製):10重量部、充填剤(硫酸バリウム、商品名:硫酸バリウムBA、堺化学社製):7重量部、着色剤(酸化チタン、商品名:TITANIX JR−805、TAYCA社製):5重量部の割合であること以外、実施例1と同様にして練り消しゴムを調製した。当該練り消しゴムは柔らかく、揉練、延伸を行うことができ、練り消しゴムとして好適に用いることができる粘度を有している。
【0069】
(実施例4)
感熱性マイクロカプセル(商品名:TCパウダー32℃オレンジ、サクラクレパス社製):1.5重量部、ゴム成分(スチレン−ブタジエンゴム、商品名:JSR0202、日本合成ゴム社製):8重量部、ゴム成分(ブタジエンゴム、商品名:ニポールBR1220、日本ゼオン社製):5重量部、軟化剤(商品名:スピンドル油#60、シェル石油社製):10重量部、軟化剤(綿実油):14重量部、充填剤(ファクティス、商品名:白サブ1、天満サブ化学工業社製):40重量部、充填剤(ファクティス、商品名:あめサブ、天満サブ化学工業社製):10重量部、充填剤(シリカ、商品名:カープレックス#1120、塩野義製薬社製):6重量部、着色剤(酸化チタン、商品名:TITANIX JR−805、TAYCA社製):1重量部、着色剤(群青):3重量部、老化防止剤(第二級アミン類、老化防止剤D、住友化学社製):0.5重量部、香料:1重量部の割合であること以外、実施例1と同様にして練り消しゴムを調製した。当該練り消しゴムは柔らかく、揉練、延伸を行うことができ、練り消しゴムとして好適に用いることができる粘度を有している。
【0070】
(実施例5)
感熱性マイクロカプセル(商品名:TCパウダー29℃イエロー、サクラクレパス社製):2重量部、感熱性マイクロカプセル(商品名:TCパウダー38℃ローズ、サクラクレパス社製):2重量部、ゴム成分(アクリロニトリル−ブタジエンゴム、商品名:JSR N230SL、日本合成ゴム社製):43重量部、ゴム成分(天然ゴム、RSS 2号):5重量部、軟化剤(流動パラフィン):13重量部、軟化剤(シリコーンオイル、商品名:KF352、信越化学社製):13重量部、充填剤(炭酸カルシウム、商品名:白艶華0、白石工業社製):17重量部、着色剤(酸化チタン、商品名:TITANIX JR−805、TAYCA社製):1.4重量部、着色剤(群青):2重量部、香料:1重量部、紫外線吸収剤(商品名:TINUVIN 384 MP、チバガイギー社製):0.4重量部、光安定剤(商品名:TINUVIN 123、チバガイギー社製):0.2重量部の割合であること以外、実施例1と同様にして練り消しゴムを調製した。当該練り消しゴムは柔らかく、揉練、延伸を行うことができ、練り消しゴムとして好適に用いることができる粘度を有している。特に、延性が優れており、有限ではあるが、かなり引き延ばし続けることができる。
【0071】
実施例1〜5で得られた練り消しゴムを、揉んだり、練ったり、引き伸ばしたりして、練り消しゴムの変色を視認により調べた。
【0072】
実施例1に係る練り消しゴムは、揉んだり練ったりしただけでは変色しなかったが、引き伸ばすと、特に急激に引き伸ばしたり又は複数回引き伸ばしたりすると、練り消しゴムの色が紫色から緑色に変化した。
【0073】
実施例2に係る練り消しゴムは、揉んだり練ったりしただけでは変色しなかったが、引き伸ばすと、特に急激に引き伸ばしたり又は複数回引き伸ばしたりすると、練り消しゴムの色が灰色から赤色に変化した。
【0074】
実施例3に係る練り消しゴムは、揉んだり練ったりすると、練り消しゴムの色が青色から白色に変化した。また、引き伸ばして引っ張っても、練り消しゴムの色が青色から白色に変化した。
【0075】
実施例4に係る練り消しゴムは、揉んだり練ったりすると、練り消しゴムの色がオリーブ色から青色に変化した。また、引き伸ばして引っ張っても、練り消しゴムの色がオリーブ色から青色に変化した。
【0076】
実施例5に係る練り消しゴムは、揉んだり練ったりすると、練り消しゴムの色が灰色から紫色に変化した。また、急激に引き伸ばすと、練り消しゴムの色が灰色から青色に変化した。さらに、急激ではなく、複数回引き伸ばしたりすると、練り消しゴムの色が灰色から紫色に変わり、さらに青色に変化した。また、青色に変色している練り消しゴムを放置すると、青色から紫色に変化し、さらに灰色に変化した。すなわち、実施例5に係る練り消しゴムは温度の上昇又は下降と共に、2段階の色変化を起こすことができる。
【0077】
従って、本発明では、揉んだり、練ったり、引っ張ったりするうちに色が変化する練り消しゴムが作製された。
【0078】
【発明の効果】
本発明の粘弾性体は、揉練又は延伸により変色する。特に、揉練又は延伸による熱によって変色する。本発明の粘弾性体は練り消しゴムとして有用である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a viscoelastic body and a kneading rubber that change color by kneading or stretching.
[0002]
[Prior art]
Conventionally, as a kneading rubber, various kneading rubbers such as those exhibiting aromaticity and those generating smoke during kneading have been widely used.
[0003]
[Problems to be solved by the invention]
However, no kneading rubber has been obtained that changes color when the kneading rubber itself is used. In addition, a viscoelastic body such as a kneaded eraser has not been obtained that changes color with temperature.
[0004]
Accordingly, an object of the present invention is to provide a viscoelastic body that changes color by kneading or stretching.
Another object of the present invention is to provide a viscoelastic body that itself changes color by heat generated by kneading or stretching.
Still another object of the present invention is to provide a kneaded rubber that changes color by kneading or stretching.
[0005]
[Means for Solving the Problems]
As a result of intensive studies, the present inventor has found that when a kneaded rubber containing a specific pigment component is used, the color itself is changed by kneading or stretching, and the present invention has been completed. That is, the present invention is a viscoelastic body containing a color-changing dye component that changes color by kneading or stretching.
[0006]
Since the viscoelastic body of the present invention contains a color-changing dye component that changes color by kneading or stretching, the viscoelasticity itself changes color by kneading or stretching. Therefore, the viscoelastic body itself has an interest that the color before kneading or stretching differs from the color after kneading or stretching. That is, when the viscoelastic body is kneaded, kneaded, or stretched, the color-changing dye component develops or loses color, so that it becomes a different color before and after kneading or stretching, which is interesting when using a viscoelastic body. Can be expressed.
[0007]
In the present invention, as the color-changing dye component, a heat-sensitive dye that changes color by heat generated by kneading or stretching can be used. When a viscoelastic body is kneaded, kneaded, or pulled and stretched, heat is generated in the viscoelastic body. This heat can be used to change the color of the viscoelastic body. In addition, it is thought that the heat | fever by such a kneading or extending | stretching is the heat | fever generate | occur | produced when stress is applied to a viscoelastic body by kneading | pulling or extending | stretching.
[0008]
The color-changing dye component is composed of heat-sensitive microcapsules that are not crushed by kneading force or stretching force, and inside the heat-sensitive microcapsules, there is a heat-sensitive coloring component that changes color due to heat by kneading or stretching. The contained color-changing dye component (sometimes referred to as “heat-sensitive color-changing dye component”) can be preferably used. That is, the color-changing dye component is composed of heat-sensitive microcapsules that are not crushed by the kneading force or stretching force, and the capsule contains a heat-sensitive coloring component that changes color by heat due to kneading or stretching. The heat-sensitive coloring component is discolored by coloring or decoloring due to heat generated by stress due to kneading or stretching, and the color of the viscoelastic body changes before and after kneading or stretching.
[0009]
Therefore, in the method using such heat-sensitive microcapsules, the color of the viscoelastic body can be easily adjusted to a different color before and after kneading or stretching. Moreover, various colors can be selected as colors before and after the color change of the viscoelastic body, and the colors of the viscoelastic body can be diversified.
[0010]
Such a viscoelastic body can be suitably used as a kneading rubber. That is, since the color of the kneading rubber can be changed at the time of use, the kneading rubber user has the fun that the kneading rubber itself changes in color in addition to the fun of kneading, kneading, or stretching. You can taste it. In addition, training refers to kneading and training.
[0011]
DETAILED DESCRIPTION OF THE INVENTION
The special feature of the viscoelastic body of the present invention, particularly the kneaded rubber, is that it contains a color-changing dye component that changes color by kneading or stretching. As such a color-changing dye component, a heat-sensitive color-changing dye component can be suitably used. Further, for example, a condensed aromatic ring-substituted ethylene derivative can be used as the color-changing dye component that changes color by heat.
[0012]
(Thermochromic dye component)
The thermochromic dye component is composed of heat-sensitive microcapsules that are not crushed by kneading force or stretching force, and inside the thermosensitive microcapsules there is a heat-sensitive coloring component that changes color by heat due to kneading or stretching. It is composed of a discoloring dye component that is contained. As the heat-sensitive coloring component, for example, a combination of a dye, a developer, and a desensitizer that melts at a heat-sensitive temperature can be used. That is, in the viscoelastic body, the color develops when the dye and the developer come into contact with each other and react with each other at a temperature lower than the heat sensitive temperature within the heat sensitive microcapsule. The agent is contained in the capsule in combination with the dye and the developer, and when the temperature in the viscoelastic body becomes higher than the heat sensitive temperature at the time of kneading or stretching, the desensitizer melts, The developer is separated and decolored, and the color of the viscoelastic body changes. In addition, the mechanism etc. which decolorize by reaction of dye and a color developer, and when it becomes more than heat sensitive temperature, a color develops by the reaction of a dye and color developer lose | disappears may be sufficient.
[0013]
Such a viscoelastic body can change color when the temperature is higher than the heat sensitive temperature. Therefore, when the heat sensitive temperature is lower than the body temperature, the color may change even just by touching.
[0014]
In addition, the temperature rise of the viscoelastic body due to heat generated during kneading or stretching is suppressed, and when the temperature of the viscoelastic body falls below the heat sensitive temperature, it has a reversible discoloration that changes the color of the viscoelastic body. Also good. In such a reversible color change, the color of the viscoelastic body usually returns to the color of the original viscoelastic body when the temperature is lower than the heat sensitive temperature. That is, in the present invention, as the thermochromic dye component, for example, reversible color change that changes from colored to colorless by heat generated during kneading or stretching, and changes from colorless to colored when the temperature is lower than the color change temperature. Sex pigment components can be employed. Of course, a reversible color-changing dye component that changes color from one color to another due to heat generated during kneading or stretching and changes to the original color when the temperature falls below the color change temperature can also be employed.
[0015]
Of course, in the present invention, in the viscoelastic body containing the thermochromic dye component, the color change of the viscoelastic body may be a reversible color change as described above or an irreversible color change.
[0016]
(Dye of thermochromic pigment component)
In the heat-sensitive color-changing pigment component, in a preferred embodiment, the heat-sensitive coloring component contains a dye, a developer, and a desensitizer that melts at a heat-sensitive temperature. In addition, when the thermosensitive coloring component is comprised by such a composition, the above-mentioned reversible discoloration can be achieved.
[0017]
As the dye of the thermosensitive coloring component, for example, a leuco dye can be suitably used. More specifically, examples of the dye include triphenylmethanephthalides (for example, crystal violet lactone and malachite green lactone), fluorans, leucooramines (for example, benzoylleucomethylene blue), and rhodamine lactams. (E.g., 2- {3,6-bis (diethylamino) -9- (o-chloroanilino) xanthylbenzoate lactam), spiropyrans (e.g., 6'-chloro-8'-methoxy-benzoindolino-spiropyran, 6'-bromo-3'-methoxy-benzoindolino-spiropyran, etc.), polyarylcarbinols (eg, crystal violet carbinol, malachite green carbinol, etc.), indolines (eg, 2- (phenyliminoethylidene)) 3,3-dimethyl-indoline, etc.) or the like can be used. The dyes can be used alone or in combination of two or more. In the present invention, the color can be adjusted according to the type of dye. Of course, the color density can be adjusted by the amount of dye used.
[0018]
As the dye, triphenylmethane phthalides, fluorans, and leucooramines can be preferably used.
[0019]
More specifically, examples of the triphenylmethane phthalides include 3,3-bis (p-dimethylaminophenyl) phthalide and 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide. 3,3-bis (p-dimethylaminophenyl) -6-chlorophthalide, 3- (2′-hydroxy-4′-dimethylaminophenyl) -3- (2′-methoxy-5′-chlorophenyl) phthalide, 3- (2'-hydroxy-4'-dimethylaminophenyl) -3- (2'-methoxy-5'-nitrophenyl) phthalide, 3- (2'-hydroxy-4'-diethylaminophenyl) -3- ( 2'-methoxy-5'-methylphenyl) phthalide, 3- (2'-methoxy-4'-dimethylaminophenyl) -3- (2'-hydroxy-4'-chloro-) '- etc. methylphenyl) phthalide can be exemplified.
[0020]
Examples of the fluorans include 3-cyclohexylamino-6-chlorofluorane, 3-dimethylamino-5,7-dimethylfluorane, 3-diethylamino-7-chlorofluorane, 3-diethylamino-7-methylfluorane. 3-diethylamino-6-methyl-7-chlorofluorane, 2- (N-phenyl-N-methylamino) -6- (NP-tolyl-N-ethylamino) fluorane, 3- (Np -Tolyl-N-ethylamino) -6-methyl-7-anilinofluorane, 3-pyrrolidino-6-methyl-7-anilinofluorane, 3-diethylamino-7,8-benzfluorane, 2- { N- (3-trifluoromethylphenyl) amino} -diethylaminofluorane, 3-diethylamino-7- (o-chloroanilino) fluorane, -Dibutylamino-7- (o-chloroanilino) fluorane, 3- (N-methyl-N-amylamino) -6-methyl-7-anilinofluorane, 3- (N-methyl-N-cyclohexylamino) -6 -Methyl-7-anilinofluorane, 3-diethylamino-6-methyl-7-anilinofluorane, 3- (N, N-diethylamino) -5-methyl-7- (N, N-dibenzylamino) Fluorane, 3-diethylamino-5-chloro-7- (N-trifluoromethylanilino) fluorane, 3-diethyl-5-chloro-7- (α-phenylethylamino) fluorane, 3- (N-ethyl-p) -Toluidino) 7- (α-phenylethylamino) fluorane, 3-diethylamino-7- (o-methoxycarbonylphenylamino) fluorane, 3- Ethylamino-5-methyl-7- (α-phenylethylamino) fluorane, 3-diethylamino-7-piperidinofluorane, 2-chloro-3- (N-methyltoluidino) -7- (pn-butylanilino) ) Fluorane, 3- (N-methyl-N-isopropylamino) -6-methyl-7-anilinofluorane, 3-dibutylamino-6-methyl-7-anilinofluorane, 3- {N-ethyl- N- (2-ethoxypropyl) amino} -6-methyl-7-anilinofluorane, 3- (N-benzyl-N-cyclohexylamino) -5,6-benzo-7-α-naphthylamino-4 ′ -Bromofluorane, 3-diethylamino-6-chloro-7-anilinofluorane, 3-diethylamino-6-methyl-mesitidino-4 ', 5'-benzofluorane 3-N-methyl-N-isobutyl-6-methyl-7-anilinofluorane, 3-N-methyl-N-isoamyl-6-methyl-7-anilinofluorane, 3-diethylamino-6-methyl- 7- (2 ′, 5′-dimethylanilino) fluorane and the like are included.
[0021]
(Developer of thermochromic dye component)
In the thermochromic dye component, as the developer, an electron accepting compound such as a solid acid or a phenolic compound can be suitably used. As the developer, a solid or liquid developer can be used. The solid acid means “an electron-accepting compound that is solid at room temperature”. Developers can be used alone or in combination of two or more. In addition, it is also possible to use a well-known developer as a developer of a thermochromic pigment component.
[0022]
Examples of solid acids include inorganic solid acids (metal oxides, metal sulfides, metal sulfates, metal phosphates such as metal phosphates, clay minerals such as active clay, zeolites, etc.), organic Based solid acids (for example, phenolic resins, salicylic acid or derivatives thereof, and salts thereof). Examples of the activated clay include activated clay, acidic clay, and montmorillonite. As the phenolic resin, a conventional phenolic resin can be used. The molecular weight of the phenolic resin is not particularly limited.
[0023]
In the present invention, a phenol compound can be suitably used as the developer. In particular, in the present invention, compounds having one or more phenolic hydroxyl groups, such as monophenols, diphenols, and triphenols, can be suitably used as the color developer for the thermochromic dye component.
[0024]
Examples of monophenols include monohydroxyphenyl compounds (for example, 4-hydroxybenzophenone, p-hydroxydiphenyl, 4-hydroxydiphenylamine, p-cumylphenol, p-phenolsulfonamide, methyl 4-hydroxybenzenesulfonate). 4-hydroxyphenyl methyl ketone, etc.), phenylcarboxylic acid compounds (for example, oxybenzoic acid esters such as p-hydroxybenzoic acid benzyl, oxyphthalic acid such as 2-hydroxyphthalic acid dimethyl ester, 2-hydroxyphthalic acid diphenyl ester) Esters, 4′-hydroxysalicylic acid anilide, 5-benzylsalicylic acid anilide, etc.), monohydroxynaphthalene compounds (eg, α-naphthol, β-naphthol, 2-methyl-1-naphtho) Oxynaphthalene such as 8-amino-2-naphthol, oxynaphthoic acid such as 1-oxy-2-naphthoic acid, 2-oxy-3-naphthoic acid, 2-acetonaphthone, hydroxynaphthalenesulfonic acid, etc.) It is.
[0025]
Examples of diphenols include bisphenol compounds and dihydroxynaphthalene compounds (for example, dioxynaphthalene such as 1,3-dioxynaphthalene and 1,4-dioxynaphthalene, 1,4-dihydroxynaphthalene monopropyl ether, etc. And dioxynaphthalene aryl ethers such as 1,4-dihydroxynaphthalene monobenzyl ether).
[0026]
Examples of the bisphenol compound include compounds represented by formulas (1a) to (1f).
[0027]
[Chemical 1]
Figure 0003930980
[Chemical 2]
Figure 0003930980
[Chemical 3]
Figure 0003930980
[Formula 4]
Figure 0003930980
[Chemical formula 5]
Figure 0003930980
[Chemical 6]
Figure 0003930980
[Chemical 7]
Figure 0003930980
(In the formulas 1a to 1f, R 1 , R 2 Are the same or different and each represents an alkyl group. R 3 Is an alkylene group, a cycloalkylene group, or an arylene group, and R 4 Is an alkylene group. n is an integer of 1 to 10)
[0028]
In the formulas (1a) to (1f), the alkyl group includes, for example, a linear or branched alkyl group having about 1 to 10 carbon atoms such as methyl, ethyl, propyl, isopropyl and butyl groups (preferably carbon 1-6 alkyl groups) are included. As an alkylene group, C1-C10 alkylene groups, such as a methylene, ethylene, a propylene group, can be illustrated, for example. The cycloalkylene group includes, for example, a cyclohexylene group, and the arylene group includes, for example, a phenylene group. Moreover, n is an integer of 1-10.
[0029]
More specifically, examples of the bisphenol compound include methylene bisphenol, 4,4′-ethylidene bisphenol, 4,4 ′-(2-ethylhexylidene) bisphenol, and the like.
[0030]
Examples of triphenols include 3,4,5-trihydroxybenzoic acid-C 1-18 Alkyl ester compounds and the like can be used.
[0031]
As the developer, diphenols, particularly bisphenol compounds, are preferably used among the phenol compounds. The amount of the developer to be used is not particularly limited, and is, for example, about 0.1 to 5 parts by weight, preferably about 0.5 to 3 parts by weight with respect to 1 part by weight of the thermochromic dye component. In the present invention, the color density can be adjusted by the type and amount of the developer.
[0032]
(Desensitizer for thermochromic dye component)
As the desensitizer, a compound that melts or melts at a heat sensitive temperature can be used. The heat sensitive temperature means “a specific temperature due to heat generated by kneading or stretching”.
[0033]
As the desensitizer, a compound that melts or melts from room temperature to a temperature at which the temperature due to heat generated by kneading or stretching is maximum (for example, about 50 ° C.) can be used. In the present invention, considering that the viscoelastic body is kneaded, kneaded, or stretched by hand, a desensitizer having a melting point of, for example, 26 to 50 ° C. can be suitably used. In particular, when the melting point of the desensitizer is 26 to 37 ° C., the viscoelastic body is discolored by heat generated during kneading or stretching, and the part touched by the hand is also discolored by body temperature. On the other hand, when the melting point of the desensitizer is 38 ° C. or higher (for example, 38 to 50 ° C.), the viscoelastic body does not change color depending on body temperature when touched by hand, and the viscoelastic body does not change depending on body temperature. When the temperature becomes 38 ° C. or higher, the viscoelastic body itself changes color.
[0034]
Examples of the desensitizer include aliphatic higher alcohols, aromatic alcohols (eg, phenol, o-cresol, p-cresol, etc.), aliphatic higher fatty acids, aliphatic higher fatty acid esters (for example, And aliphatic higher fatty acid alkyl esters such as methyl octadecanoate). As the desensitizer, higher alcohols and higher fatty acids can be suitably used. Examples of higher alcohols include linear saturated aliphatics having about 12 to 18 carbon atoms (preferably 14 to 18) such as 1-dodecanol, 1-tetradecanol, 1-hexadecanol, 1-octadecanol and the like. Based alcohols. Examples of higher fatty acids include linear saturated aliphatic fatty acids having about 10 to 16 carbon atoms such as decanoic acid, dodecanoic acid, and tetradecanoic acid. A desensitizer can be used individually or in combination of 2 or more types.
[0035]
The amount of the desensitizer used is not particularly limited. The amount of the desensitizer used in the heat-sensitive microcapsules may be an amount such that the dye and the developer are brought into contact with each other at a temperature lower than the heat sensitive temperature and that the dye and the developer are not brought into contact with each other at a temperature higher than the heat sensitive temperature. In the present invention, the temperature of discoloration can be adjusted by the type of desensitizer.
[0036]
(Thermosensitive microcapsules of thermochromic dye components)
In the present invention, the heat-sensitive coloring component (for example, a dye, a developer and a desensitizer) can be used by being contained in a heat-sensitive microcapsule. Examples of the wall material of such heat-sensitive microcapsules include acrylic resins, amide resins, urethane resins, epoxy resins, melamine resins (for example, melamine-formaldehyde resins), urea resins (for example, Various resins such as urea-melamine-formaldehyde resin can be used. The resin as the wall material can be used alone or in combination of two or more. As the heat-sensitive microcapsule, it is necessary that the heat-sensitive microcapsule is not crushed or broken by force during kneading or stretching. Therefore, as the wall material of the heat-sensitive microcapsule, melamine resin, urea resin, particularly melamine resin is used. Can be preferably used. Moreover, in order not to be easily crushed, it is particularly preferable that the heat-sensitive microcapsule has a double wall. The heat-sensitive microcapsules preferably have a powdery or pasty form. The size of the thermosensitive microcapsule is, for example, 0.5 to 200 μm in diameter, and preferably 1 to 30 μm.
[0037]
As a method for encapsulating a heat-sensitive coloring component (for example, a dye, a developer, and a desensitizer) in a heat-sensitive microcapsule, a conventionally used method (for example, an in situ polymerization method, an interfacial polymerization method, a concert) A basation method). In these polymerization methods, known polymerization conditions can be applied. For example, the conditions described in JP-A-53-84883, JP-A-7-324178 and the like can be applied. Further, by adopting the method described in JP-A-5-7767, a thermosensitive microcapsule having a double wall can be prepared. In the polymerization, for example, a material in which a dye and a developer are dispersed in a desensitizer can be used as a core material.
[0038]
The thermosensitive coloring components can be used alone or in combination of two or more. For example, when a plurality of (for example, two types) thermosensitive coloring components that can change color reversibly and have different color changing temperatures are used, the viscoelastic body changes color stepwise. In such a stepwise color change, especially when the temperature of the viscoelastic body is lowered from the heat-sensitive temperature to room temperature, the color changes easily in a stepwise manner, and the viscoelastic body returns to its original color step by step. Is very interesting.
[0039]
In the present invention, as the thermochromic dye component, trade name: TC powder (manufactured by Sakura Crepas Co., Ltd.) can be used. More specifically, examples of the thermochromic dye component include trade name: TC powder rose, trade name: TC powder orange, trade name: TC powder yellow, trade name: TC powder blue, trade name: TC powder green. (The above is made by Sakura Crepas Co., Ltd.).
[0040]
(Viscoelastic body)
The color-changing dye component (for example, heat-sensitive color-changing dye component) can be used alone or in combination of two or more. In the present invention, the color-changing dye component can be used in various combinations, and since there are many such combinations, viscoelastic bodies having various funs, particularly kneaded rubbers can be prepared. .
[0041]
The viscoelastic body of the present invention, particularly the kneaded rubber, contains at least the color-changing pigment component and a viscoelastic material. The viscoelastic material is not particularly limited, and for example, a rubber component, a resin component, an elastomer component, or the like can be used.
[0042]
(Rubber component-containing viscoelastic body)
In the present invention, the rubber component-containing viscoelastic body can be composed of a color-changing dye component and a known rubber component, and various additives can be used as necessary. That is, the rubber component-containing viscoelastic body may contain a rubber component, a softening agent, a filler, an anti-aging agent, a colorant and the like in addition to the color-changing pigment component.
[0043]
The rubber component is not particularly limited, and for example, natural rubber (for example, so-called raw rubber), synthetic rubber (for example, butadiene rubber, styrene-butadiene rubber, isobutylene-isoprene rubber, acrylonitrile-butadiene rubber, butyl rubber, etc.) is used. be able to.
[0044]
The softening agent is not particularly limited, and for example, mineral oil (for example, extender oil, process oil, liquid paraffin, motor oil, turbine oil, machine oil, etc.), vegetable oil (for example, rapeseed oil, cottonseed oil, soybean oil) Etc.), fatty acids, waxes, phthalic acid plasticizers, silicone oils, fluorine oils and the like.
[0045]
As the silicone-based oil, for example, silicone oils such as a trade name “KF69” (manufactured by Shin-Etsu Chemical Co., Ltd.) and a trade name “KF352” (manufactured by Shin-Etsu Chemical Co., Ltd.) can be used.
[0046]
In particular, when silicone oil is used as a softening agent, it is possible to prepare a viscoelastic body (such as a kneaded rubber) that is difficult to cut even when pulled and can continue to be stretched without breaking, that is, a highly ductile body (such as kneaded rubber).
[0047]
Examples of the filler include known fillers such as calcium carbonate, magnesium carbonate, magnesium oxide, silica, talc, clay, diatomaceous earth, quartz powder, alumina, alumina silicate, mica, factis (for example, rapeseed oil, cottonseed oil, soybean oil, etc. In which sulfur chloride is reacted).
[0048]
Examples of the antiaging agent include aldehyde amines, secondary amines, phenylenediamines, phenols and the like.
[0049]
Furthermore, as the colorant, various known pigments such as organic pigments, inorganic pigments, fluorescent pigments, dyes, and the like can be used.
[0050]
In the rubber component-containing viscoelastic body, the ratio of the color-changing pigment component is not particularly limited, and can be selected according to the type of other contained components.
[0051]
When the rubber component-containing viscoelastic body is composed of, for example, a color-changing dye component, a rubber component, a softener, a filler, an anti-aging agent, and a colorant, the ratio of the color-changing dye component is, for example, a viscoelastic body It can be selected from the range of 0.2 to 30% by weight, preferably 0.5 to 10% by weight with respect to the total amount. If the content of the color-changing dye component is less than 0.2% by weight based on the total amount of the viscoelastic body, the effect of color change is low. On the other hand, if it is more than 30% by weight, it becomes powdery, and it becomes easy to cut when stretched due to reduced ductility.
[0052]
Moreover, the ratio of a rubber component can be selected from the range of 5-65 weight% with respect to a viscoelastic body whole quantity, Preferably it is 10-55 weight%. When the content of the rubber component is less than 5% by weight with respect to the total amount of the viscoelastic body, the viscoelasticity is lowered. On the other hand, if it is more than 65% by weight, the viscoelastic body becomes hard and difficult to pull, and it is difficult to knead and knead.
[0053]
The proportion of the softening agent can be selected, for example, from the range of 3 to 55% by weight, preferably 10 to 45% by weight, based on the total amount of the viscoelastic body. When the content of the softening agent is less than 3% by weight based on the total amount of the viscoelastic body, the viscosity of the viscoelastic body becomes high and becomes brittle, and it becomes difficult to perform stretching and kneading. On the other hand, if it exceeds 55% by weight, the viscosity of the viscoelastic body becomes too low, or the surface of the viscoelastic body becomes sticky, and heat generation due to kneading and stretching is suppressed, making it difficult to generate heat. .
[0054]
The proportion of the filler can be selected, for example, from the range of 1 to 70% by weight, preferably 5 to 60% by weight, based on the total amount of the viscoelastic body. When the content of the filler is more than 70% by weight with respect to the total amount of the viscoelastic body, the viscoelastic body becomes powdery and easily broken.
[0055]
The proportion of the anti-aging agent can be selected, for example, from the range of 0 to 5% by weight, preferably 0.1 to 2% by weight, based on the total amount of the viscoelastic body. The proportion of the colorant can be selected, for example, from the range of 0 to 30% by weight, preferably 0 to 10% by weight, based on the total amount of the viscoelastic body.
[0056]
In the case where a resin component is used as the viscoelastic material, a thermoplastic resin and a plasticizer, a filler, a stabilizer, a colorant and the like are often used in combination. When an elastomer component is used as the viscoelastic material, a thermoplastic elastomer is often used in combination with a softener, a filler, a stabilizer, a colorant, and the like.
[0057]
The viscoelastic body of the present invention may contain stabilizers such as ultraviolet absorbers and light stabilizers, other conventionally used additives, fragrances, thermoplastic resins such as polyolefin resins, and the like. .
[0058]
(Method for preparing viscoelastic body)
The viscoelastic body or kneaded rubber of the present invention can be prepared by mixing the above-described components (for example, a color-changing pigment component, a viscoelastic material, etc.). In preparing the viscoelastic body, an injection molding machine, a press molding machine, and the like can be used in addition to a mixer such as a kneader or a Banbury mixer, and an extrusion molding machine.
[0059]
In preparing the rubber component-containing viscoelastic body, vulcanization may be performed, but vulcanization is not necessary. In the present invention, the vulcanization operation is usually not performed.
[0060]
In particular, when the rubber component-containing viscoelastic body contains a color-changing dye component that changes color by stretching, it often contains silicone oil as a softening agent. On the other hand, when a color-changing pigment component that changes color by kneading is contained, silicon-based oil may or may not be used as a softening agent.
[0061]
Since the viscoelastic body of the present invention is discolored by kneading or stretching, it is useful as a toy or toy using viscoelasticity such as a kneaded eraser or clay toy, particularly as a kneaded eraser. Especially with kneaded rubber, the kneaded rubber changes color while kneading, kneading, and pulling, so in addition to kneading and stretching, which is the natural play of kneading rubber, kneading, kneading, and pulling. Thus, the kneaded rubber has an interesting effect that the color changes depending on the degree of kneading and stretching.
[0062]
The temperature at which the viscoelastic body of the present invention changes color, particularly the temperature at which the kneaded rubber changes color is not particularly limited. For example, a viscoelastic body, particularly a kneaded rubber can be adjusted so as to change color at about 26 to 50 ° C. Accordingly, the viscoelastic body, particularly the kneaded rubber, is easily discolored by kneading or stretching. When the thermochromic pigment component is used in the viscoelastic body or kneaded rubber and a desensitizer is included, the thermosensitive temperature is controlled by the combination of the dye and developer and the type of desensitizer. Is done.
[0063]
In the viscoelastic body or kneaded rubber of the present invention, when the color-changing pigment component and the colorant are used in combination, the color of the viscoelastic body or the kneaded rubber can be adjusted to various colors. Since it is possible to diversify, it is possible to further provide fun and beauty. Therefore, in the present invention, it is extremely preferable to use a combination of a color-changing dye component and a colorant.
[0064]
Since the viscoelastic body of the present invention, particularly the kneaded rubber, has the fun of being discolored by kneading and stretching itself, it also provides the consumer with the fun of kneading and stretching. Therefore, viscoelastic bodies, especially kneaded rubbers are very useful in industry.
[0065]
【Example】
Hereinafter, the present invention will be described in detail by way of examples. The present invention is not limited to these examples.
[0066]
Example 1
Heat-sensitive microcapsules (trade name: TC powder 38 ° C. Rose, manufactured by Sakura Crepas): 2 parts by weight, rubber component (acrylonitrile-butadiene rubber, trade name: JSR N230SL, manufactured by Nippon Synthetic Rubber): 50 parts by weight, softening Agent (trade name: spindle oil # 60, manufactured by Shell Sekiyu KK): 26 parts by weight, softener (silicone oil, product name: KF69, manufactured by Shin-Etsu Chemical Co., Ltd.): 10 parts by weight, filler (silica, product name: car Plex # 1120, manufactured by Shionogi & Co., Ltd.): 10 parts by weight, colorant (titanium oxide, trade name: TITANIX JR-805, manufactured by TAYCA): 0.6 part by weight, colorant (phthalocyanine green): 0.4 Weight parts and fragrances were mixed at a ratio of 1 part by weight by a conventional method using a Banbury mixer to prepare a kneaded rubber. The kneaded rubber is soft and can be kneaded and stretched, and has a viscosity that can be suitably used as a kneaded rubber. In particular, the ductility is excellent, and although it is finite, it can continue to be stretched considerably.
[0067]
(Example 2)
Thermosensitive microcapsules (trade name: TC powder 45 ° C. green, manufactured by Sakura Crepas): 2 parts by weight, rubber component (styrene-butadiene rubber, product name: JSR 1500, manufactured by Nippon Synthetic Rubber): 26 parts by weight, softener (Petrolatum, trade name: Petrolatum No. 5, manufactured by Yamabun Oil Chemical Co., Ltd.): 7 parts by weight, softener (trade name: Spindle oil # 60, manufactured by Shell Sekiyu Co., Ltd.): 15 parts by weight, filler (Factis, product) Name: White Sub 1, manufactured by Tenma Sub Chemical Industry Co., Ltd.): 26 parts by weight, filler (calcium carbonate, trade name: Shiraka Hana 0, manufactured by Shiroishi Kogyo Co., Ltd.): 20 parts by weight, colorant (titanium oxide, trade name: TITANIX JR-805, manufactured by TAYCA): 3.5 parts by weight, colorant (naphthol red): 0.5 parts by weight Except that the ratio was 0.5 parts by weight, a kneaded rubber was prepared in the same manner as in Example 1. . The kneaded rubber is soft and can be kneaded and stretched, and has a viscosity that can be suitably used as a kneaded rubber.
[0068]
(Example 3)
Thermosensitive microcapsules (trade name: TC powder 32 ° C blue, made by Sakura Crepas): 3 parts by weight, rubber component (butadiene rubber, trade name: Nipol BR1220, made by Nippon Zeon): 13 parts by weight, softener (flow) Paraffin): 15 parts by weight, filler (Factis, trade name: white sub 1, manufactured by Tenma Sub Chemical Industry): 47 parts by weight, filler (calcium carbonate, trade name: white white flower, manufactured by Shiroishi Industrial Co., Ltd.): 10 Part by weight, filler (barium sulfate, trade name: barium sulfate BA, manufactured by Sakai Chemical Co., Ltd.): 7 parts by weight, colorant (titanium oxide, trade name: TITANIX JR-805, manufactured by TAYCA): 5 parts by weight Except that, a kneaded rubber was prepared in the same manner as in Example 1. The kneaded rubber is soft and can be kneaded and stretched, and has a viscosity that can be suitably used as a kneaded rubber.
[0069]
Example 4
Thermosensitive microcapsules (trade name: TC powder 32 ° C orange, manufactured by Sakura Crepas): 1.5 parts by weight, rubber component (styrene-butadiene rubber, trade name: JSR0202, manufactured by Nippon Synthetic Rubber Co.): 8 parts by weight, Rubber component (butadiene rubber, trade name: Nipol BR1220, manufactured by Nippon Zeon Co., Ltd.): 5 parts by weight, softener (trade name: spindle oil # 60, manufactured by Shell Sekiyu Co., Ltd.): 10 parts by weight, softener (cotton seed oil): 14 Part by weight, filler (Factis, trade name: White Sub 1, manufactured by Tenma Sub Chemical Industries): 40 parts by weight, Filler (Factis, trade name: Ame Sub, manufactured by Tenma Sub Chemical Industries): 10 parts by weight, Filler (silica, trade name: Carplex # 1120, manufactured by Shionogi Pharmaceutical Co., Ltd.): 6 parts by weight, colorant (titanium oxide, trade name: TITANIX JR-805, manufactured by TAYCA) ): 1 part by weight, colorant (ultraviolet): 3 parts by weight, anti-aging agent (secondary amines, anti-aging agent D, manufactured by Sumitomo Chemical Co., Ltd.): 0.5 part by weight, perfume: 1 part by weight Except that, a kneaded rubber was prepared in the same manner as in Example 1. The kneaded rubber is soft and can be kneaded and stretched, and has a viscosity that can be suitably used as a kneaded rubber.
[0070]
(Example 5)
Heat-sensitive microcapsules (trade name: TC powder 29 ° C yellow, made by Sakura Crepas): 2 parts by weight, heat-sensitive microcapsules (trade name: TC powder 38 ° C rose, made by Sakura Crepas): 2 parts by weight, rubber component (Acrylonitrile-butadiene rubber, trade name: JSR N230SL, manufactured by Nippon Synthetic Rubber): 43 parts by weight, rubber component (natural rubber, RSS No. 2): 5 parts by weight, softener (liquid paraffin): 13 parts by weight, softening Agent (silicone oil, trade name: KF352, manufactured by Shin-Etsu Chemical Co., Ltd.): 13 parts by weight, filler (calcium carbonate, trade name: white white flower, manufactured by Shiraishi Kogyo Co., Ltd.): 17 parts by weight, colorant (titanium oxide, trade name) : TITANIX JR-805, manufactured by TAYCA): 1.4 parts by weight, colorant (ultraviolet): 2 parts by weight, fragrance: 1 part by weight, ultraviolet absorber (trade name: INUVIN 384 MP, manufactured by Ciba Geigy): 0.4 parts by weight, light stabilizer (trade name: TINUVIN 123, manufactured by Ciba Geigy): kneaded in the same manner as in Example 1 except that the ratio was 0.2 parts by weight. An eraser was prepared. The kneaded rubber is soft and can be kneaded and stretched, and has a viscosity that can be suitably used as a kneaded rubber. In particular, the ductility is excellent, and although it is finite, it can continue to be stretched considerably.
[0071]
The kneaded rubber obtained in Examples 1 to 5 was kneaded, kneaded, or stretched, and the discoloration of the kneaded rubber was visually examined.
[0072]
The kneaded rubber according to Example 1 did not change color just by kneading or kneading, but when stretched, particularly when stretched rapidly or stretched a plurality of times, the color of the kneaded rubber changed from purple to green.
[0073]
The kneaded rubber according to Example 2 did not change color just by kneading or kneading, but when stretched, particularly when stretched rapidly or stretched a plurality of times, the color of the kneaded rubber changed from gray to red.
[0074]
When the kneading rubber according to Example 3 was kneaded or kneaded, the color of the kneading rubber changed from blue to white. Also, even when stretched and pulled, the color of the kneaded rubber changed from blue to white.
[0075]
When the kneading rubber according to Example 4 was kneaded or kneaded, the color of the kneading rubber changed from olive to blue. Also, even when stretched and pulled, the color of the kneaded rubber changed from olive to blue.
[0076]
When the kneaded rubber according to Example 5 was kneaded or kneaded, the color of the kneaded rubber changed from gray to purple. In addition, when stretched rapidly, the color of the kneaded rubber changed from gray to blue. Furthermore, when it was stretched several times rather than suddenly, the color of the kneading rubber changed from gray to purple and further to blue. Also, when the kneaded rubber that had turned blue was left, it changed from blue to purple and further to gray. That is, the kneaded rubber according to Example 5 can cause a two-stage color change as the temperature rises or falls.
[0077]
Therefore, in the present invention, a kneaded eraser was produced in which the color changes while kneading, kneading, or pulling.
[0078]
【The invention's effect】
The viscoelastic body of the present invention changes color by kneading or stretching. In particular, the color changes due to heat generated by kneading or stretching. The viscoelastic body of the present invention is useful as a kneading rubber.

Claims (4)

スチレン−ブタジエンゴム、ブタジエンゴム、
アクリロニトリル−ブタジエンゴム、天然ゴムのいずれかから選ばれたゴム成分を含む粘弾性材料と、感熱変色性色素成分と、着色剤とを含有し、
前記感熱変色性色素成分は、練り消しゴムの揉練又は延伸による応力により生じる発熱によって、練り消しゴム組成物の色が揉練又は延伸の前後で変化する感熱変色性色素成分であって、
感熱変色性色素成分は感熱性マイクロカプセルで構成されており、かつ該感熱性マイクロカプセル内部には感熱性着色成分が含有しており、
感熱性マイクロカプセルの壁材はメラミン系樹脂で構成されており、
感熱性着色成分がロイコ染料、顕色剤、及び感熱温度で溶融する減感剤を含有し、
上記減感剤が26〜50℃の融点を有しており、
練り消しゴム全量に対して0.2〜30重量%感熱変色性色素成分を含有し、練り消しゴム全量に対して5〜65重量%ゴム成分を含有する練り消しゴム組成物。
Styrene-butadiene rubber, butadiene rubber,
A viscoelastic material containing a rubber component selected from acrylonitrile-butadiene rubber and natural rubber, a thermochromic dye component, and a colorant ;
The thermochromic dye component is a thermochromic dye component in which the color of the kneaded rubber composition changes before and after kneading or stretching due to heat generated by stress due to kneading or stretching of the kneaded rubber,
The thermochromic dye component is composed of thermosensitive microcapsules, and a thermosensitive coloring component is contained inside the thermosensitive microcapsules,
The wall material of the thermosensitive microcapsule is composed of melamine resin,
The heat-sensitive coloring component contains a leuco dye, a developer, and a desensitizer that melts at a heat-sensitive temperature,
The desensitizer has a melting point of 26-50 ° C.,
A kneaded rubber composition containing 0.2 to 30% by weight of a thermochromic pigment component based on the total amount of the kneaded rubber and 5 to 65% by weight of the rubber component based on the total amount of the kneaded rubber.
減感剤の融点が38℃以上である請求項1記載の練り消しゴム組成物。The kneaded rubber composition according to claim 1, wherein the desensitizer has a melting point of 38 ° C or higher. 減感剤の融点が26〜37℃である請求項1記載の練り消しゴム組成物。The kneaded rubber composition according to claim 1, wherein the desensitizer has a melting point of 26 to 37 ° C. 請求項1乃至3いずれかに記載の変色性色素成分は、揉練又は延伸による熱により有色から無色に変色し、該変色温度の温度を下回ると無色から有色に変色する可逆的な変色性色素成分である請求項1乃至3のいずれかに記載の練り消しゴム組成物。The reversible color-changing dye component according to any one of claims 1 to 3, wherein the color-changing dye component changes from colored to colorless by heat due to kneading or stretching, and changes from colorless to colored when the temperature is lower than the temperature of the color change. The kneaded rubber composition according to any one of claims 1 to 3, which is a component.
JP24499998A 1998-08-31 1998-08-31 Kneaded rubber composition Expired - Fee Related JP3930980B2 (en)