JP3681160B2 - Agricultural curtain material and its manufacturing method - Google Patents

Agricultural curtain material and its manufacturing method Download PDF

Info

Publication number
JP3681160B2
JP3681160B2 JP2001113899A JP2001113899A JP3681160B2 JP 3681160 B2 JP3681160 B2 JP 3681160B2 JP 2001113899 A JP2001113899 A JP 2001113899A JP 2001113899 A JP2001113899 A JP 2001113899A JP 3681160 B2 JP3681160 B2 JP 3681160B2
Authority
JP
Japan
Prior art keywords
polyester
woven fabric
yarn
curtain material
agricultural
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2001113899A
Other languages
Japanese (ja)
Other versions
JP2002305989A (en
Inventor
一良 中川
永世 大廣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Aion Co Ltd
Original Assignee
Aion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Aion Co Ltd filed Critical Aion Co Ltd
Priority to JP2001113899A priority Critical patent/JP3681160B2/en
Publication of JP2002305989A publication Critical patent/JP2002305989A/en
Application granted granted Critical
Publication of JP3681160B2 publication Critical patent/JP3681160B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は、遮光性,通気性,保温性等に優れた農業用カーテン資材およびその製法に関するものである。
【0002】
【従来の技術】
従来から、農作物を、できるだけ天候に左右されない人工的な環境下で栽培することを目的として、ビニールハウスやガラスハウス内でのハウス栽培や、ビニールトンネルを用いたトンネル栽培が、広く行われている。そして、上記ハウス内やトンネル内には、日中の強い日差しを遮光し、夜間、地面からの輻射熱の拡散を防止して保温するために、例えば図4(a)に示すように、農業用カーテン1を張設することが多い。
【0003】
しかし、上記のように、ハウス内に上記農業用カーテン1を張設しても、季節によっては、日中の温度が30℃近くまで上昇する場合があるため、適温が18℃前後であるレタス等を栽培する場合には、日差しの強い日中は上記農業用カーテン1の裾を上げて換気し、外気温の下がる夕方以降はこれを下ろす作業を毎日繰り返す必要があり、多大な労力がかかるという問題がある。
【0004】
そこで、最近、図4(b)に示すように、上記農業用カーテン1の裾を、アーチ状のパイプ製枠体2に沿って、天井側に巻き上げたり引き下ろしたりする動作を自動的に行うことのできる巻き上げ式カーテンが提案され、広く普及しつつある。
【0005】
このような農業用カーテン1としては、ポリ塩化ビニル、ポリエチレン、エチレン−酢酸ビニル共重合体等の樹脂フィルムや、ポリエステル,ポリエチレン,ナイロン,ポリプロピレン等の繊維からなる不織布シートが汎用されている。
【0006】
【発明が解決しようとする課題】
しかしながら、上記樹脂フィルムを用いたものは、保温性には優れているものの、通気性や透湿性に乏しいため、ハウスやトンネルの外張材の内側に結露した水が滴下してフィルム表面に溜まって水溜まりができ、その重みによって、巻き上げ・引き下ろしによる開閉作業を行うことができにくくなるという問題がある。また、日中、フィルムを巻き上げた状態で数時間放置しておくと、互いに接したフィルム同士が熱によって貼り付き、下に降ろす動作がしにくくなり、注意しないとその部分が破損してしまうという問題がある。
【0007】
一方、不織布シートを用いたものは、通気性、透湿性が樹脂フィルムよりも優れており、結露水の水溜まりを生じる等のトラブルは生じにくいが、繊維集合体であることから、表面が毛羽立ちやすく、巻き上げ・引き下ろし作業を繰り返すと、不織布シートと、これを張設しているパイプ製枠体2とが擦れ合って損傷しやすいという問題がある。
【0008】
本発明は、このような事情に鑑みなされたもので、遮光性、通気性、保温性等に優れるだけでなく、寸法安定性にも優れ、長期にわたって良好に使用することのできる農業用カーテン資材およびその製法の提供をその目的とする。
【0009】
【課題を解決するための手段】
上記の目的を達成するため、本発明は、ポリエステル系織物からなる農業用カーテン資材であって、上記ポリエステル系織物が、主として、チタン化合物を0.001〜0.40重量%含有するポリエステル異形断面糸によって構成されており、上記織物の乾熱収縮率が経方向・緯方向とも1.5%以下に設定され、耐候処理が施されている農業用カーテン資材を第1の要旨とし、そのなかでも、特に、上記ポリエステル異形断面糸が、多葉形状の断面を有し、上記断面形状の外接円の直径と内接円の直径の比である異形度が1.5〜4に設定されている農業用カーテン資材を第2の要旨とする。
【0010】
また、本発明は、それらのなかでも、特に、上記織物を構成するカバーファクタが800〜2200に設定されている農業用カーテン資材を第3の要旨とし、農作物栽培用ハウス内に、ハウス天井面とハウス側面に沿って張設され、少なくともその側面に沿う部分が、ハウス内の状況に応じて巻き上げたり引き下ろしたりすることができるよう設定された巻き上げ式カーテンとして用いられる農業用カーテン資材を第4の要旨とする。
【0011】
さらに、本発明は、主として、チタン化合物0.001〜0.40重量%と耐候剤とを含有するポリエステル異形断面糸によって構成されたポリエステル系織物の生機を準備し、この生機を精練乾燥後、195〜220℃で15〜90秒間加熱することにより寸法安定化処理を行うようにした農業用カーテン資材の製法を第5の要旨とする。
【0012】
また、本発明は、主として、チタン化合物を0.001〜0.40重量%含有するポリエステル異形断面糸によって構成されたポリエステル系織物の生機を準備し、この生機を精練乾燥後、耐候剤の分散液に浸漬して織物を構成する糸の繊維表面に耐候剤を付着させた後、脱液・乾燥後、195〜220℃で15〜90秒間加熱することにより上記耐候剤の付着固定と寸法安定化処理を同時に行うようにした農業用カーテン資材の製法を第6の要旨とし、そのなかでも、特に、上記耐候剤の付着固定量が、0.010〜0.600%owfとなるようにした農業用カーテン資材の製法を第8の要旨とする。
【0013】
【発明の実施の形態】
つぎに、本発明の実施の形態について説明する。
【0014】
本発明の農業用カーテン資材は、ポリエステル系織物からなり、このポリエステル系織物は、主として、チタン化合物を0.001〜0.40重量%(以下「%」と略す)含有するポリエステル異形断面糸によって構成されている。
【0015】
上記ポリエステル系織物において、主として用いられるポリエステル異形断面糸は、ポリエチレンテレフタレートを常法により紡糸・延伸し、必要に応じて適宜の撚りを与えることによって得られる。なお、紡糸時の口金として、開口が真円のものではなく、異形断面形成用の特殊形状のものが用いられる。また、紡糸される糸には、0.001〜0.40%の範囲内で、チタン化合物が含有されるようになっている。
【0016】
上記チタン化合物は、従来から、紡糸時の曳糸性を向上させるとともに、糸を白濁させてダル調にするという役割を果たすものであるが、本発明では、特に、上記チタン化合物の含有割合を、できるだけ低く抑えることにより糸が艶やかなブライト糸となるようにして、光の反射率を高めるようにしている。このため、上記範囲内のなかでも、0.001〜0.30%に設定することが好ましく、0.001〜0.10%に設定することがさらに好ましい。なお、チタン化合物が0.001%未満では、紡糸効率が低下しやすくなり、逆に、0.40%を超えると、糸が濁ってダル糸となり得られる織物の光反射率が低下し、ひいては遮熱性が低下する。そして、このようなチタン化合物としては、二酸化チタンの他、これにアルミニウム、亜鉛、シリカ、硫酸バリウム、カルシウム等を適宜含有する各種のものがあげられ、その種類は特に限定されない。
【0017】
また、上記ポリエステル異形断面糸の断面形状は、どのようなものであっても差し支えないが、なかでも、複数の突出部を有する多葉形状のものが好適である。その一例として、図1に、3葉形状のものを示す。このような、多葉形状断面の糸を用いて得られる農業用カーテン資材は、糸が、前述のように、チタン化合物の含有割合を低く抑えたブライト糸であることと相俟って、日光を効果的に反射し、遮熱性に優れるだけでなく、織り目の間から弱い光が分散して漏れるため、農業用カーテン資材で被覆されたハウス内やトンネル内が比較的明るいという利点を有している。
【0018】
そして、上記多葉形状の異形断面糸のなかでも、特に、その外接円の直径Dとその内接円の直径dの比(D/d、図1参照)である異形度が、1.5〜4となるよう設定されているものが、上記効果に優れており、好適である。
【0019】
なお、多葉形状の他の例として、図2(a)に示す4葉形状のもの、図2(b)に示す6葉形状のもの等をあげることができる。また、その突出部の形状も、円弧状ではなく、より角張った形状のもの、細長い棒状のもの等、適宜の形に設定することができる。あるいは、図2(c)に示すように、円形の一部が欠損したような形状であってもよい。
【0020】
そして、本発明に用いられる織物は、上記異形断面糸を100%用いたものであっても、その一部を、種類の異なる他の糸に置き換えたものであってもよい。上記異形断面糸と併用できる他の糸としては、異形断面を有しないポリエステル糸の他、プロピレン糸、ポリエチレン糸、ポリアミド糸等があげられる。これらの糸は異形断面糸であってもそうでなくてもよい。また、同じ異形断面糸であっても、0.40%を超えるチタン化合物含有量の糸を部分的に用いるようにしてもよい。さらに、織物に、より保湿性を与えるために、ポリビニルアルコール等の吸水性繊維からなる糸を併用するようにしてもよい。そして、これらの糸を、上記ポリエステル異形断面糸と混ぜて使用する場合は、織物全体に対し50%を超えない範囲内で用いることが好適である。すなわち、50%より多く配合すると、前述の、ポリエステル異形断面糸を用いることによって得られる効果が低下するからである。なお、これらの糸は、混紡してもよいし、製織の段階で、経糸や緯糸に混ぜて織り込むようにしてもよい。
【0021】
また、本発明において、織物の織り方は、特に限定するものではないが、通常、平織り、からみ織り等が用いられる。
【0022】
そして、本発明に用いられる上記ポリエステル系織物は、ハウス内への張設、巻き上げ・引き下ろし等の繰り返し作業に耐え得る充分な物理的強度を備えていることが要求されるのであり、例えば、JIS L 1096のラベルストリップ法(引張速度:20cm/分、つかみ間隔:20cm、試験片幅:5cm)に従って測定される引張強さが、経方向、緯方向とも、100N以上となるよう設定することが好適である。ただし、ポリエステル系織物を農業用カーテン資材として用いた場合、経時的劣化により引張強さが低下することを考慮すれば、その耐用年数との兼ね合いから、未使用状態では、400N以上の引張強さを備えていることが望ましい。また、同様の方法で測定される伸び率が、未使用の状態で20〜50%であることが好適である。すなわち、この範囲内において、張設された農業用カーテン資材がたるまないからである。
【0023】
そして、同様の考え方から、上記ポリエステル系織物の、JIS L 1096のペンジュラム法による引裂強さは、未使用の状態で800cN以上、経時的にも200cN以上の値が維持されるよう設定することが好適である。
【0024】
さらに、上記ポリエステル系織物の通気性は、JIS L 1096のフラジール法に従って測定される値が、5〜100cm3 /cm2 /秒となるよう設定されることが好適である。すなわち、通気性が上記の範囲内であれば、この織物の特徴である遮光効果と相俟って、ハウス内の温度と湿度が、適正な状態に保持されるからである。
【0025】
また、上記ポリエステル系織物には、優れた寸法安定性を付与させることができるのであり、これが、本発明の大きな特徴である。これにより、本発明の農業用カーテン資材は、ハウス内で60〜80℃、あるいはそれ以上の高温状態におかれても、寸法が大きく変化することがなく、従来の樹脂フィルムを用いたもののように、高温によって資材が収縮してハウスとの連結部や枠体等の構造体(パイプ等)を歪めることがなく、長期にわたって良好に使用することができる。
【0026】
すなわち、本発明に用いられるポリエステル系織物は、乾熱収縮率が1.5%以下という優れた寸法安定性を備えている。なかでも、乾熱収縮率1%以下に設定することが好適である。なお、上記「乾熱収縮率」は、JIS L 1057A−1法(140℃)によるアイロン収縮率を示す。
【0027】
このように優れた寸法安定性を付与するには、上記ポリエステル系織物を製造する際、つぎのような処理を行うことが必要である。すなわち、すでに述べたように、チタン化合物を所定割合で含有するポリエステル異形断面糸を、主として用いたポリエステル系織物の生機を精練乾燥後、195〜220℃で15〜90秒間加熱することにより寸法安定化処理をする。このようにして、目的とする高寸法安定性の織物を得ることができる。また、場合によっては、糸の段階で上記と同様の高温加熱を予め行うことにより、寸法安定化処理を施すようにしてもよい。
【0028】
なお、ポリエステル系織物における仕上げ加工は、通常、190℃以下で行われるが、その場合、本発明が目的とする寸法安定性を得ることができないため、本発明では、上記のように、処理温度を195〜220℃に上げて、寸法安定化を兼ねた仕上げ処理を行う。したがって、本発明では、この仕上げ処理を「寸法安定化処理」という。
【0029】
また、上記ポリエステル系織物には、耐候性の向上を目的として、耐候剤が付与される。付与方法としては、ポリエステル異形断面糸の紡糸工程において、耐候剤を原料樹脂に練込む方法と、ポリエステル系織物に耐候剤を付着固定する方法の2つがあげられる。
【0030】
上記原料樹脂に耐候剤を練込む方法では、原料樹脂組成物全体に対する耐候剤の含有割合を、0.010〜0.600%に設定することが、効果の点で好適である。
【0031】
また、上記ポリエステル系織物に耐候剤を付着固定する方法は、具体的には、例えばつぎのようにして行われる。すなわち、耐候剤が適宜の媒体に分散された分散液に織物を浸漬し、耐候剤を織物を構成する糸の繊維表面に付着させたのち、これを脱液・乾燥し、その後、ベーキングすることにより、上記耐候剤を付着固定することができる。そして、上記ベーキングは、195〜220℃で15〜90秒間加熱する寸法安定化処理で兼ねることができる。この方法によれば、耐候剤の付着固定と寸法安定化処理を同時に達成することができる。なお、上記ベーキング兼寸法安定化処理に先立って、通常の条件にしたがって、プレセットを行うことができる。
【0032】
なお、上記耐候剤としては、ベンゾフェノン系,ベンゾトリアゾール系等の紫外線吸収剤や、フェノール系,リン酸系等の紫外線安定剤(酸化防止剤)、ヒンダードアミン系光安定剤(HALS)等があげられる。なかでも、ベンゾトリアゾール系紫外線吸収剤(市販品:日華化学社製のサンライフ LPS−950等)が好適に用いられる。
【0033】
さらに、上記ポリエステル系織物のカバーファクタは、800〜2200に設定することが好適である。ただし、上記カバーファクタ(CF)は、下記の式で示される値である。
【0034】
【数1】

Figure 0003681160
【0035】
すなわち、上記カバーファクタが800未満では、織密度が低すぎて充分な遮熱性が得られにくくなり、逆にカバーファクタが2200を超えると、通気度が低くなり、透水性が損なわれるおそれがある。
【0036】
そして、上記ポリエステル系織物の厚みは、0.05〜0.5mm、なかでも0.09〜0.20mmに設定することが好適である。すなわち、厚みが薄すぎると、強度的な問題が生じ、逆に厚すぎると、やはり通気度が低くなり、透水性が損なわれるおそれがある。
【0037】
上記ポリエステル系織物からなる本発明の農業用カーテン資材は、光反射率が高く、遮熱性に優れるだけでなく、通気性、保温性にも優れ、ハウスやトンネル内での農産物栽培において、優れた栽培促進効果を奏する。また、引張強さ、伸び率、引裂強さ等の物理的物性にも優れており、取り扱いやすい。しかも、寸法安定性にも優れているため、長期使用によっても、その連結部等において裂傷が生じたりすることがなく、長期にわたって良好に使用することができる。したがって、このものは、巻き上げたり引き下ろしたりする作業が自動的に行われるよう設定された巻き上げ式カーテン(図4〔b〕参照)に適用するのに最適である。そして、光反射率が高い半面、カーテンで覆われた内側空間が比較的明るいため、これを張設したハウス内やトンネル内での作業がしやすいという利点を有する。
【0038】
つぎに、実施例について比較例とともに説明する。
【0039】
【実施例1】
下記の表1に示す特性を備えたポリエステル異形断面糸(断面3葉形状、図1参照)を準備した。そして、この糸を経糸および緯糸として用い、後記の表2に示す条件で織成し、平織りの生機を得た。
【0040】
【表1】
Figure 0003681160
【0041】
【表2】
Figure 0003681160
【0042】
つぎに、上記生機を、常法により精練乾燥し、ついで、紫外線吸収剤(日華化学社製、サンライフ LPS−950)の0.2%水系分散液に、上記生機を浸漬した。そして、200℃×30秒間のベーキング兼寸法安定化処理を行うことにより、目的とする織物を得た。この織物は、厚み0.11mm、カバーファクタ1567、目付70g/m2 であった。
【0043】
【実施例2】
緯糸の二酸化チタン含有量を、0.5%にした。それ以外は、上記実施例1と同様にして、目的とする織物を得た。この織物は、厚み0.10mm、カバーファクタ1558、目付70g/m2 であった。
【0044】
【比較例1】
経糸および緯糸の二酸化チタン含有量を、ともに0.5%にした。そして、200℃×30秒間のベーキング兼寸法安定化処理に代えて、180℃×30秒間の仕上げ処理を行った。それ以外は実施例1と同様にして織物を得た。この織物は、厚み0.10mm、カバーファクタ1548、目付69g/m2 であった。
【0045】
【比較例2,3】
比較例2品として、従来から農業用カーテン資材として用いられているポリエステル製スパンボンド不織布(厚み0.16mm、目付50g/m2 )を用意した。また、比較例3品として、同じく従来から農業用カーテン資材として用いられている軟質塩化ビニルフィルム(厚み0.075mm、目付95g/m2 )を用意した。
【0046】
そして、これらの実施例1,2品、比較例1〜3品について、下記の表3に示す各項目について測定を行い、その結果を、下記の表3に併せて示した。なお、各測定方法は、前述のとおりである。また、実際に、図4(b)に示す巻き上げ式の農業用カーテン1としてそれぞれを用いて12カ月使用し、その開閉作業性と、耐久性と、保温性・遮熱性を評価した。良好なものを「○」とし、やや劣るものを「△」とし、使用に支障が生じるものを「×」とした。なお、比較例2,3品については、経緯の区別がないが、それぞれの長手方向を経方向とし、幅方向を緯方向とした。
【0047】
【表3】
Figure 0003681160
【0048】
上記の結果から、実施例1,2品は、全ての項目において、優れた性能を有していることがわかる。
【0049】
さらに、実施例1,2品と比較例1品の遮熱性について、図3に示す装置を用いて測定した。この装置は、治具3によって、裏面に黒い画用紙4を取り付けた試料5を垂直に保持し、上記試料5から30cm離れた位置に光源(レフランプ:岩崎電気社製、アイランプ<スポット>PRS100V500W)6を設置して、試料5を10分間照射し、裏面側に設置したサーモカメラ7により、画用紙4の温度を経時的に測定して、昇温曲線を記録するようにした装置である。なお、室温は22℃±2℃であった。測定の結果を図5に示す。
【0050】
上記の結果から、実施例1,2品は、比較例1品よりも優れた遮熱性を備えており、特に、経糸、緯糸とも二酸化チタン含有割合を0.05%に制限した実施例1品が、より優れた遮熱性を備えていることがわかる。
【0051】
【発明の効果】
以上のように、本発明の農業用カーテン資材は、チタン化合物の含有割合を低く抑えた特殊なポリエステル異形断面糸を主として用い、しかも耐候処理を施した特殊なポリエステル系織物で構成されているため、光反射率が高く、遮熱性に優れている。そして、通気性、保温性にも優れ、ハウスやトンネル内での農産物栽培において、優れた栽培促進効果を奏する。また、引張強さ、伸び率、引裂強さ等の物理的物性にも優れており、取り扱いやすい。しかも、寸法安定性にも優れているため、長期使用によっても、その連結部等において裂傷が生じたりすることがなく、長期にわたって良好に使用することができる。したがって、このものは、巻き上げたり引き下ろしたりする作業が自動的に行われるよう設定された巻き上げ式カーテン等に適用するのに最適である。
【図面の簡単な説明】
【図1】本発明の一実施例に用いるポリエステル異形断面糸の説明図である。
【図2】(a),(b),(c)はいずれも上記ポリエステル異形断面糸の変形例を示す説明図である。
【図3】遮熱性を測定する装置の説明図である。
【図4】(a)は農業用カーテン資材の一般的な使用態様の一例を示す説明図、(b)は他の例を示す説明図である。
【図5】実施例品と比較例品の遮熱性を示す温度−照射時間の特性曲線図である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to an agricultural curtain material excellent in light-shielding property, air permeability, heat retention and the like, and a method for producing the same.
[0002]
[Prior art]
Conventionally, in order to cultivate crops in an artificial environment that is not affected by the weather as much as possible, greenhouse cultivation in greenhouses and glass houses and tunnel cultivation using vinyl tunnels have been widely performed. . Then, in the house or tunnel, in order to shield the strong sunlight during the daytime and prevent the radiation heat from diffusing from the ground at night, for example, as shown in FIG. The curtain 1 is often stretched.
[0003]
However, even if the agricultural curtain 1 is stretched in the house as described above, the daytime temperature may rise to nearly 30 ° C depending on the season, so lettuce has an appropriate temperature of around 18 ° C. When cultivating etc., it is necessary to raise the hem of the curtain 1 for ventilation during the daytime when the sunlight is strong, and to lower it every day after the evening when the outside temperature falls, which takes a lot of labor. There is a problem.
[0004]
Therefore, recently, as shown in FIG. 4 (b), the skirt of the agricultural curtain 1 is automatically moved up and down to the ceiling side along the arched pipe frame 2. Roll-up curtains that can be used are proposed and are becoming widespread.
[0005]
As such an agricultural curtain 1, resin films such as polyvinyl chloride, polyethylene, and ethylene-vinyl acetate copolymer, and nonwoven fabric sheets made of fibers such as polyester, polyethylene, nylon, and polypropylene are widely used.
[0006]
[Problems to be solved by the invention]
However, the one using the above resin film is excellent in heat retention, but lacks air permeability and moisture permeability, so water condensed on the inside of the outer material of the house or tunnel drops and accumulates on the film surface. Thus, there is a problem that the water pool is formed, and the weight makes it difficult to perform the opening / closing operation by winding and pulling down. Also, if the film is left for several hours in the daytime with the film rolled up, the films that are in contact with each other will stick together by heat, making it difficult to move down, and if not careful, that part will be damaged. There's a problem.
[0007]
On the other hand, the non-woven fabric sheet has better breathability and moisture permeability than the resin film, and is less likely to cause trouble such as the accumulation of condensed water. When the winding and pulling-down operations are repeated, there is a problem that the nonwoven fabric sheet and the pipe frame 2 on which the non-woven sheet is stretched are rubbed and easily damaged.
[0008]
The present invention has been made in view of such circumstances, and is not only excellent in light shielding properties, air permeability, heat retention properties, etc., but also excellent in dimensional stability and can be used satisfactorily for a long time. And the purpose is to provide its manufacturing method.
[0009]
[Means for Solving the Problems]
In order to achieve the above object, the present invention provides an agricultural curtain material comprising a polyester woven fabric, wherein the polyester woven fabric mainly contains 0.001 to 0.40% by weight of a titanium compound. The first gist is an agricultural curtain material that is made of yarn and has a dry heat shrinkage rate of 1.5% or less in both the warp direction and the weft direction, and is subjected to weathering treatment. However, in particular, the polyester deformed cross-section yarn has a multilobal cross section, and the degree of deformity, which is the ratio of the diameter of the circumscribed circle and the diameter of the inscribed circle of the cross section, is set to 1.5-4. Agricultural curtain material that is present is the second gist.
[0010]
In addition, the present invention has, in particular, an agricultural curtain material in which the cover factor constituting the woven fabric is set to 800 to 2200, and the ceiling surface of the house in the crop cultivation house. A fourth agricultural curtain material used as a roll-up curtain that is stretched along the side of the house and at least a portion along the side can be rolled up or down according to the situation in the house. The gist of
[0011]
Furthermore, the present invention mainly prepares a woven fabric of a polyester woven fabric composed of a polyester modified cross-section yarn containing 0.001 to 0.40% by weight of a titanium compound and a weathering agent. A fifth gist is a method for producing an agricultural curtain material in which a dimension stabilization treatment is performed by heating at 195 to 220 ° C. for 15 to 90 seconds.
[0012]
In addition, the present invention mainly prepares a living machine of a polyester woven fabric composed of a polyester modified cross-sectional yarn containing 0.001 to 0.40% by weight of a titanium compound. After attaching the weathering agent to the fiber surface of the yarn constituting the fabric by dipping in the liquid, removing the liquid and drying, and then heating at 195 to 220 ° C. for 15 to 90 seconds, the fixing and dimensional stability of the above weathering agent The sixth gist is a method for producing an agricultural curtain material that is simultaneously subjected to a chemical conversion treatment, and in particular, the adhesion fixing amount of the weathering agent is set to 0.010 to 0.600% owf. The manufacturing method of the curtain material for agriculture is the eighth gist.
[0013]
DETAILED DESCRIPTION OF THE INVENTION
Next, an embodiment of the present invention will be described.
[0014]
The agricultural curtain material of the present invention is composed of a polyester woven fabric, and this polyester woven fabric is mainly composed of a polyester modified cross-section yarn containing 0.001 to 0.40 wt% (hereinafter abbreviated as “%”) of a titanium compound. It is configured.
[0015]
In the polyester-based woven fabric, the polyester deformed cross-sectional yarn mainly used is obtained by spinning and stretching polyethylene terephthalate by a conventional method, and applying an appropriate twist as necessary. In addition, as a base at the time of spinning, an opening having a special shape for forming a modified cross section is used instead of a perfect circle. The spun yarn contains a titanium compound in the range of 0.001 to 0.40%.
[0016]
Conventionally, the titanium compound plays a role of improving the spinnability at the time of spinning and making the yarn cloudy to make a dull tone. In the present invention, in particular, the content ratio of the titanium compound is increased. By keeping it as low as possible, the yarn becomes a bright bright yarn, so that the reflectance of light is increased. For this reason, in the said range, it is preferable to set to 0.001 to 0.30%, and it is more preferable to set to 0.001 to 0.10%. If the titanium compound is less than 0.001%, the spinning efficiency tends to decrease. Conversely, if the titanium compound exceeds 0.40%, the light reflectance of the woven fabric that can be formed into a dull yarn by turbidity of the yarn decreases, and as a result Heat shielding properties are reduced. Examples of such a titanium compound include titanium dioxide, and various compounds that appropriately contain aluminum, zinc, silica, barium sulfate, calcium, and the like. The type of the titanium compound is not particularly limited.
[0017]
Moreover, the cross-sectional shape of the polyester modified cross-section yarn may be any shape, but among them, a multi-leaf shape having a plurality of protrusions is preferable. As an example, FIG. 1 shows a three-leaf type. Agricultural curtain material obtained using such a multi-leaf shaped cross-section yarn is combined with the fact that the yarn is a bright yarn with a low content of titanium compound, as described above. In addition to being excellent in heat insulation, it also has the advantage of being relatively bright in houses and tunnels covered with agricultural curtain materials because weak light is scattered and leaks between the weaves. ing.
[0018]
Among the multi-leaf shaped irregular cross-section yarns, in particular, the degree of irregularity, which is the ratio of the diameter D of the circumscribed circle to the diameter d of the inscribed circle (D / d, see FIG. 1) is 1.5. Those set to ˜4 are excellent in the above effects and are suitable.
[0019]
Other examples of the multi-leaf shape include a four-leaf shape shown in FIG. 2A and a six-leaf shape shown in FIG. 2B. Also, the shape of the protruding portion is not an arc shape but can be set to an appropriate shape such as a more angular shape or an elongated rod shape. Or as shown in FIG.2 (c), the shape which a part of circular shape lacked may be sufficient.
[0020]
The woven fabric used in the present invention may be one using 100% of the modified cross-section yarn, or a part thereof replaced with another type of yarn. Examples of other yarns that can be used in combination with the modified cross-section yarn include propylene yarn, polyethylene yarn, polyamide yarn and the like, in addition to polyester yarn having no modified cross-section. These yarns may or may not be profile cross-sectional yarns. Further, even with the same modified cross-section yarn, a yarn having a titanium compound content exceeding 0.40% may be partially used. Furthermore, in order to give the fabric more moisture retention, a yarn made of water-absorbing fibers such as polyvinyl alcohol may be used in combination. And when these yarns are used by mixing with the above-mentioned polyester modified cross-section yarn, it is preferable to use them within a range not exceeding 50% with respect to the entire fabric. That is, when the blending amount is more than 50%, the effect obtained by using the above-described polyester modified cross-section yarn is lowered. Note that these yarns may be blended, or may be woven and mixed with warps and wefts at the stage of weaving.
[0021]
In the present invention, the weaving method of the woven fabric is not particularly limited, but plain weaving, leash weaving and the like are usually used.
[0022]
The polyester-based woven fabric used in the present invention is required to have sufficient physical strength to withstand repeated operations such as tensioning in a house, winding and pulling down, for example, JIS. The tensile strength measured according to the L 1096 label strip method (tensile speed: 20 cm / min, gripping interval: 20 cm, test piece width: 5 cm) may be set to be 100 N or more in both the longitudinal direction and the weft direction. Is preferred. However, when polyester fabric is used as an agricultural curtain material, considering that the tensile strength decreases due to deterioration over time, the tensile strength of 400 N or more is used in an unused state in consideration of its service life. It is desirable to have. Moreover, it is suitable that the elongation measured by the same method is 20 to 50% in an unused state. That is, within this range, the stretched agricultural curtain material does not sag.
[0023]
From the same concept, the tear strength of the polyester woven fabric according to the JIS L 1096 pendulum method can be set to maintain a value of 800 cN or more in an unused state and 200 cN or more over time. Is preferred.
[0024]
Further, the breathability of the polyester-based fabric is preferably set so that the value measured according to the JIS L 1096 Frazier method is 5 to 100 cm 3 / cm 2 / sec. That is, if the air permeability is within the above range, the temperature and humidity in the house are maintained in an appropriate state in combination with the light shielding effect that is characteristic of the fabric.
[0025]
In addition, the polyester-based woven fabric can be provided with excellent dimensional stability, which is a major feature of the present invention. As a result, the agricultural curtain material of the present invention does not change greatly in dimensions even when placed in a house at a high temperature of 60 to 80 ° C. or higher, and seems to use a conventional resin film. In addition, the material shrinks due to the high temperature and does not distort the structure (pipe or the like) such as the connecting portion with the house or the frame, and can be used well for a long period of time.
[0026]
That is, the polyester fabric used in the present invention has excellent dimensional stability with a dry heat shrinkage of 1.5% or less. In particular, it is preferable to set the dry heat shrinkage rate to 1% or less. The “dry heat shrinkage rate” indicates the iron shrinkage rate according to the JIS L 1057A-1 method (140 ° C.).
[0027]
In order to impart such excellent dimensional stability, it is necessary to perform the following treatment when the polyester-based fabric is produced. That is, as described above, the polyester deformed cross-section yarn containing a titanium compound in a predetermined ratio is dimensionally stabilized by scouring and drying a polyester woven fabric machine mainly used at 195 to 220 ° C. for 15 to 90 seconds. Process. In this way, the intended high dimensional stability fabric can be obtained. In some cases, the dimensional stabilization process may be performed by preliminarily performing high-temperature heating similar to the above at the yarn stage.
[0028]
The finishing process in the polyester-based woven fabric is usually performed at 190 ° C. or lower. In that case, the dimensional stability intended by the present invention cannot be obtained. Is raised to 195 to 220 ° C., and a finishing process is performed which also serves to stabilize dimensions. Therefore, in the present invention, this finishing process is referred to as “dimension stabilization process”.
[0029]
In addition, a weathering agent is added to the polyester woven fabric for the purpose of improving the weather resistance. Examples of the application method include two methods: a method of kneading a weathering agent into a raw material resin in a spinning process of a polyester modified cross-section yarn, and a method of adhering and fixing a weathering agent to a polyester fabric.
[0030]
In the method of kneading a weathering agent into the raw material resin, it is preferable in terms of effects that the content ratio of the weathering agent with respect to the entire raw material resin composition is set to 0.010 to 0.600%.
[0031]
The method for attaching and fixing the weathering agent to the polyester fabric is specifically performed as follows, for example. That is, immersing a woven fabric in a dispersion in which a weathering agent is dispersed in an appropriate medium, attaching the weathering agent to the fiber surface of the yarn constituting the woven fabric, and then draining and drying it, followed by baking. Thus, the weathering agent can be adhered and fixed. And the said baking can serve as the dimension stabilization process heated at 195-220 degreeC for 15 to 90 second. According to this method, it is possible to achieve adhesion fixing of the weathering agent and dimensional stabilization treatment at the same time. Prior to the baking and dimensional stabilization treatment, presetting can be performed according to normal conditions.
[0032]
Examples of the weathering agent include UV absorbers such as benzophenone and benzotriazole, UV stabilizers (antioxidants) such as phenols and phosphates, and hindered amine light stabilizers (HALS). . Among these, a benzotriazole ultraviolet absorber (commercially available product: Sun Life LPS-950 manufactured by Nikka Chemical Co., Ltd.) is preferably used.
[0033]
Furthermore, the cover factor of the polyester-based fabric is preferably set to 800-2200. However, the cover factor (CF) is a value represented by the following equation.
[0034]
[Expression 1]
Figure 0003681160
[0035]
That is, if the cover factor is less than 800, the woven density is too low to obtain sufficient heat shielding properties. Conversely, if the cover factor exceeds 2200, the air permeability may be lowered and the water permeability may be impaired. .
[0036]
The thickness of the polyester woven fabric is preferably set to 0.05 to 0.5 mm, particularly 0.09 to 0.20 mm. That is, if the thickness is too thin, there is a problem in strength. On the other hand, if the thickness is too thick, the air permeability may be lowered and water permeability may be impaired.
[0037]
The agricultural curtain material of the present invention comprising the polyester-based woven fabric has high light reflectance and excellent heat shielding properties, as well as excellent breathability and heat retention, and is excellent in agricultural production in houses and tunnels. There is a cultivation promotion effect. In addition, it has excellent physical properties such as tensile strength, elongation rate, and tear strength, and is easy to handle. In addition, since it is excellent in dimensional stability, it can be used satisfactorily for a long period of time without causing laceration in the connecting portion or the like even after long-term use. Therefore, this is optimal for application to a hoisting curtain (see FIG. 4B) that is set so that the hoisting and lowering operations are automatically performed. On the other hand, since the inner space covered with the curtain is relatively bright while having a high light reflectivity, there is an advantage that it is easy to work in a house or tunnel in which this is stretched.
[0038]
Next, examples will be described together with comparative examples.
[0039]
[Example 1]
Polyester deformed cross-section yarns having the characteristics shown in Table 1 below (3-section cross-section, see FIG. 1) were prepared. This yarn was used as warp and weft and woven under the conditions shown in Table 2 below to obtain a plain weave machine.
[0040]
[Table 1]
Figure 0003681160
[0041]
[Table 2]
Figure 0003681160
[0042]
Next, the raw machine was scoured and dried by a conventional method, and then the raw machine was immersed in a 0.2% aqueous dispersion of a UV absorber (manufactured by Nikka Chemical Co., Ltd., Sun Life LPS-950). And the target textile fabric was obtained by performing the baking and dimension stabilization process of 200 degreeC x 30 second (s). This fabric had a thickness of 0.11 mm, a cover factor of 1567, and a basis weight of 70 g / m 2 .
[0043]
[Example 2]
The titanium dioxide content of the weft was 0.5%. Other than that was carried out similarly to the said Example 1, and obtained the target textile fabric. This fabric had a thickness of 0.10 mm, a cover factor of 1558, and a basis weight of 70 g / m 2 .
[0044]
[Comparative Example 1]
Both the warp and weft titanium dioxide contents were 0.5%. Then, instead of baking and dimensional stabilization treatment at 200 ° C. for 30 seconds, a finishing treatment at 180 ° C. for 30 seconds was performed. Otherwise, a woven fabric was obtained in the same manner as in Example 1. This fabric had a thickness of 0.10 mm, a cover factor of 1548, and a basis weight of 69 g / m 2 .
[0045]
[Comparative Examples 2 and 3]
A polyester spunbond nonwoven fabric (thickness 0.16 mm, basis weight 50 g / m 2 ) conventionally used as an agricultural curtain material was prepared as two comparative examples. Moreover, the soft vinyl-chloride film (thickness 0.075mm, weight per unit area 95g / m < 2 >) conventionally used as a curtain material for agriculture as a comparative example 3 goods was prepared.
[0046]
And about these Examples 1 and 2 goods and Comparative Examples 1-3 goods, it measured about each item shown in following Table 3, and the result was combined with following Table 3, and was shown. Each measuring method is as described above. In actuality, each roll-up type agricultural curtain 1 shown in FIG. 4 (b) was used for 12 months, and its opening and closing workability, durability, heat retention and heat insulation were evaluated. Good ones were rated as “◯”, slightly inferior ones as “Δ”, and those that caused trouble in use as “X”. In addition, although there is no distinction between the backgrounds of Comparative Examples 2 and 3, the longitudinal direction is the warp direction and the width direction is the weft direction.
[0047]
[Table 3]
Figure 0003681160
[0048]
From the above results, it can be seen that Examples 1 and 2 have excellent performance in all items.
[0049]
Further, the heat shielding properties of the products of Examples 1 and 2 and the product of Comparative Example 1 were measured using the apparatus shown in FIG. This apparatus uses a jig 3 to vertically hold a sample 5 with a black drawing paper 4 attached to the back side, and a light source (ref lamp: manufactured by Iwasaki Electric Co., Ltd., Eyelamp <Spot> PRS100V500W) at a position 30 cm away from the sample 5. 6, the sample 5 is irradiated for 10 minutes, the temperature of the drawing paper 4 is measured over time by the thermo camera 7 installed on the back side, and the temperature rise curve is recorded. The room temperature was 22 ° C. ± 2 ° C. The measurement results are shown in FIG.
[0050]
From the above results, the products of Examples 1 and 2 have better heat shielding properties than the products of Comparative Example 1, and in particular, the products of Example 1 in which the content of titanium dioxide is limited to 0.05% for both warp and weft. However, it turns out that it has the more excellent heat-shielding property.
[0051]
【The invention's effect】
As described above, the agricultural curtain material according to the present invention is composed of a special polyester-based woven fabric mainly using a special polyester deformed cross-sectional yarn with a low content of titanium compound and subjected to a weather resistance treatment. High light reflectivity and excellent heat insulation. And it is excellent also in air permeability and heat retention, and has an excellent cultivation promotion effect in agricultural product cultivation in a house or tunnel. In addition, it has excellent physical properties such as tensile strength, elongation rate, and tear strength, and is easy to handle. In addition, since it has excellent dimensional stability, it can be used satisfactorily for a long period of time without causing laceration in the connecting portion or the like even when used for a long period of time. Therefore, this is optimal for application to a roll-up curtain or the like that is set so that the work of winding up and down is automatically performed.
[Brief description of the drawings]
BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is an explanatory diagram of a polyester modified cross-sectional yarn used in one embodiment of the present invention.
FIGS. 2A, 2B, and 2C are explanatory views showing modified examples of the polyester modified cross-sectional yarn.
FIG. 3 is an explanatory diagram of an apparatus for measuring heat shielding properties.
4A is an explanatory view showing an example of a general usage mode of an agricultural curtain material, and FIG. 4B is an explanatory view showing another example.
FIG. 5 is a characteristic curve of temperature-irradiation time showing heat shielding properties of an example product and a comparative example product.

Claims (7)

ポリエステル系織物からなる農業用カーテン資材であって、上記ポリエステル系織物が、主として、チタン化合物を0.001〜0.40重量%含有するポリエステル異形断面糸によって構成されており、上記織物の乾熱収縮率が経方向・緯方向とも1.5%以下に設定され、耐候処理が施されていることを特徴とする農業用カーテン資材。A curtain material for agriculture made of polyester woven fabric, wherein the polyester woven fabric is mainly composed of polyester deformed cross-section yarn containing 0.001 to 0.40% by weight of a titanium compound, and the dry heat of the woven fabric. An agricultural curtain material characterized in that the shrinkage rate is set to 1.5% or less in both the warp direction and the weft direction and is subjected to weathering treatment. 上記ポリエステル異形断面糸が、多葉形状の断面を有し、上記断面形状の外接円の直径と内接円の直径の比である異形度が1.5〜4に設定されている請求項1記載の農業用カーテン資材。The said polyester irregular cross-section thread | yarn has a cross-section of a multileaf shape, and the deformity degree which is a ratio of the diameter of the circumscribed circle of the said cross-sectional shape and the diameter of an inscribed circle is set to 1.5-4. Agricultural curtain material as described. 上記織物を構成するカバーファクタが800〜2200に設定されている請求項1または2記載の農業用カーテン資材。The agricultural curtain material according to claim 1 or 2, wherein a cover factor constituting the woven fabric is set to 800 to 2200. 農作物栽培用ハウス内に、ハウス天井面とハウス側面に沿って張設され、少なくともその側面に沿う部分が、ハウス内の状況に応じて巻き上げたり引き下ろしたりすることができるよう設定された巻き上げ式カーテンとして用いられる請求項1〜3のいずれか一項に記載の農業用カーテン資材。A roll-up curtain that is stretched along the ceiling and side of the house in the crop cultivation house, and at least the part along the side can be rolled up or down according to the conditions in the house. The agricultural curtain material as described in any one of Claims 1-3 used as. 主として、チタン化合物0.001〜0.40重量%と耐候剤とを含有するポリエステル異形断面糸によって構成されたポリエステル系織物の生機を準備し、この生機を精練乾燥後、195〜220℃で15〜90秒間加熱することにより寸法安定化処理を行うようにしたことを特徴とする農業用カーテン資材の製法。A production machine for a polyester-based woven fabric mainly composed of a polyester modified cross-section yarn containing 0.001 to 0.40% by weight of a titanium compound and a weathering agent was prepared. A method for producing an agricultural curtain material, characterized in that dimension stabilization treatment is performed by heating for ~ 90 seconds. 主として、チタン化合物を0.001〜0.40重量%含有するポリエステル異形断面糸によって構成されたポリエステル系織物の生機を準備し、この生機を精練乾燥後、耐候剤の分散液に浸漬して織物を構成する糸の繊維表面に耐候剤を付着させた後、脱液・乾燥後、195〜220℃で15〜90秒間加熱することにより上記耐候剤の付着固定と寸法安定化処理を同時に行うようにしたことを特徴とする農業用カーテン資材の製法。A textile machine of a polyester woven fabric mainly composed of a polyester deformed cross-section yarn containing 0.001 to 0.40% by weight of a titanium compound is prepared. After adhering the weathering agent to the fiber surface of the yarn that constitutes the yarn, after removing the liquid and drying, heating and fixing at 195 to 220 ° C. for 15 to 90 seconds simultaneously perform the fixing and dimensional stabilization treatment of the weathering agent. A method for producing agricultural curtain materials characterized by 上記耐候剤の付着固定量が、0.010〜0.600%owfとなるようにした請求項6記載の農業用カーテン資材の製法。The method for producing an agricultural curtain material according to claim 6, wherein an adhesion fixing amount of the weathering agent is 0.010 to 0.600% owf.
JP2001113899A 2001-04-12 2001-04-12 Agricultural curtain material and its manufacturing method Expired - Fee Related JP3681160B2 (en)