JP3509924B2 - NBR support type glove and method of manufacturing the same - Google Patents
NBR support type glove and method of manufacturing the sameInfo
- Publication number
- JP3509924B2 JP3509924B2 JP07131094A JP7131094A JP3509924B2 JP 3509924 B2 JP3509924 B2 JP 3509924B2 JP 07131094 A JP07131094 A JP 07131094A JP 7131094 A JP7131094 A JP 7131094A JP 3509924 B2 JP3509924 B2 JP 3509924B2
- Authority
- JP
- Japan
- Prior art keywords
- nbr
- glove
- gloves
- latex
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ニトリル−ブタジエン
ゴム（ＮＢＲ）のサポート型手袋およびその製造法に関
し、更に詳細には、ＮＢＲを用いながら柔軟性に富み、
使用感のよいＮＢＲサポート型手袋に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a nitrile-butadiene rubber (NBR) support type glove and a method for producing the same, and more specifically, it is highly flexible while using NBR.
The present invention relates to a NBR support type glove that is easy to use.
【０００２】[0002]
【従来の技術】各種ゴムや塩化ビニル等を利用して形成
される家庭用あるいは作業用手袋には、サポート型のも
のと、ノンサポート型のものがある。このうち、サポー
ト型の手袋は、メリヤス等で編成した手袋の表面をゴム
や高分子物質で処理したものであり、ノンサポート型の
手袋に比べ強度が強いので特に作業用に広く使用されて
いる。2. Description of the Related Art There are support type and non-support type gloves for household or work made of various kinds of rubber or vinyl chloride. Among them, the support type gloves are knitted with knitted fabric, etc., the surface of which is treated with rubber or a polymer substance. Since they have stronger strength than non-support type gloves, they are widely used especially for work. .
【０００３】このサポート型手袋としては、シームレス
メリヤス手袋に塩化ビニルを塗布したものが提供され、
市販されている。 しかし、塩化ビニルを利用した手袋
で石油類を扱う作業を行うと、塩化ビニル中から可塑剤
が溶出してしまい、硬化するため長時間の使用には耐え
られないという問題があった。As the support type gloves, seamless knit gloves coated with vinyl chloride are provided.
It is commercially available. However, when working on petroleum with gloves using vinyl chloride, there is a problem that the plasticizer is eluted from the vinyl chloride and hardens so that it cannot be used for a long time.
【０００４】これに対し、ＮＢＲを使用したサポート型
手袋（以下、「ＮＢＲ手袋」という）は、耐油性が優れ
ている他、突き刺し強度に優れ、かつ軽量であるため作
業用手袋として適しているとされていた。On the other hand, the support type gloves using NBR (hereinafter referred to as "NBR gloves") are excellent in oil resistance, excellent in puncture strength, and light in weight, and thus are suitable as work gloves. Was said.
【０００５】[0005]
【発明が解決しようとする課題】しかし、従来のＮＢＲ
手袋は、繊維中にＮＢＲが浸透しやすく、場合によって
は裏面（内側）までＮＢＲ層が形成される場合があり、
塩化ビニルを用いたものに比べ柔軟性が落ち、指先感覚
が悪く、違和感があるという欠点があった。従って、耐
油性や強度を保ちながら、柔軟性を有するＮＢＲ手袋の
提供が求められていた。However, the conventional NBR
In gloves, NBR easily penetrates into the fiber, and in some cases, an NBR layer may be formed on the back surface (inside),
Compared with the one using vinyl chloride, it had the drawbacks of lower flexibility, poor fingertip feel, and discomfort. Therefore, it has been demanded to provide NBR gloves having flexibility while maintaining oil resistance and strength.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、上記課題
に鑑み鋭意検討を行った結果、浸透性の低いＮＢＲラテ
ックスを用いてＮＢＲを適切に繊維層に浸漬させれば、
密着性と柔軟性を兼ね備えたＮＢＲ手袋が得られるこ
と、およびこのＮＢＲ手袋上に保護層を設ければ更に充
分な強度も有するＮＢＲ手袋が得られることを見出し、
本発明を完成した。Means for Solving the Problems As a result of intensive studies in view of the above problems, the present inventors have found that if NBR is appropriately dipped in a fiber layer using NBR latex having low permeability,
It was found that an NBR glove having both adhesion and flexibility can be obtained, and that if a protective layer is provided on the NBR glove, an NBR glove having sufficient strength can be obtained.
The present invention has been completed.
【０００７】すなわち本発明の第一の目的は、表面張力
が３５dyne／cm以上であるＮＢＲラテックスにより形成
されるＮＢＲ層を設けたＮＢＲ手袋およびその製造法を
提供することである。また、本発明の第二の目的は、上
記ＮＢＲ手袋上に更に保護層を設けたＮＢＲ手袋および
その製造方法を提供するものである。That is, a first object of the present invention is to provide an NBR glove provided with an NBR layer formed of NBR latex having a surface tension of 35 dyne / cm or more, and a method for producing the same. A second object of the present invention is to provide an NBR glove in which a protective layer is further provided on the NBR glove, and a method for producing the NBR glove.
【０００８】本発明のＮＢＲ手袋は、金型に装着された
編み上げ手袋を表面張力が３５dyne／cm程度以上に調製
されたＮＢＲラテックス液（以下、「ラテックス液」と
いうことがある）で処理し、乾燥させることにより調製
される。In the NBR glove of the present invention, the knitted glove attached to the mold is treated with an NBR latex liquid (hereinafter, sometimes referred to as "latex liquid") having a surface tension of about 35 dyne / cm or more, It is prepared by drying.
【０００９】本発明のＮＢＲ手袋の基体として使用され
る編み上げ手袋としては、木綿等を利用した縫製タイプ
の手袋を利用することもできるが、シームレスタイプの
メリヤス手袋を利用する方が手袋内部の縫代がなくなる
ため使用感が良いため好ましく、特に、繊維が１３ゲー
ジ程度のメリヤス手袋を用いることが好ましい。As the braided glove used as the base of the NBR glove of the present invention, a sewn type glove using cotton or the like can be used, but a seamless type knitted glove is sewn inside the glove. This is preferable because it gives a good feeling in use because there is no cost, and it is particularly preferable to use knitted gloves having fibers of about 13 gauge.
【００１０】この手袋基体を処理するラテックス液は、
表面張力が３５dyne／cm程度以上であることが必要であ
り、好ましくは４０dyne／cm以上である。表面張力が、
３５dyne／cm以下の場合は、ラテックス液が手袋基体の
繊維層に浸透し、固まるため、ＮＢＲ手袋の柔軟性が失
われ、本発明の目的を十分に達成できないことがある。
また、あまり表面張力が高い場合、例えば５５dyne／c
m程度以上の場合は繊維層とＮＢＲ層の接着性が低下す
るので好ましくない。The latex liquid for treating this glove substrate is
The surface tension needs to be about 35 dyne / cm or more, preferably 40 dyne / cm or more. Surface tension
When it is 35 dyne / cm or less, the latex liquid penetrates into the fiber layer of the glove substrate and is hardened, so that the flexibility of the NBR glove is lost and the object of the present invention may not be sufficiently achieved.
If the surface tension is too high, for example, 55 dyne / c
When it is about m or more, the adhesiveness between the fiber layer and the NBR layer is deteriorated, which is not preferable.
【００１１】ラテックス液の表面張力を上記の範囲にす
るためには、ラテックス液中に加える界面活性剤の種類
や量を調製する必要がある。このラテックス液の表面張
力を前記範囲に調製するための界面活性剤には特に制限
はなく、例えば、脂肪酸系等の界面活性剤を利用するこ
とができる。In order to bring the surface tension of the latex liquid into the above range, it is necessary to adjust the kind and amount of the surfactant added to the latex liquid. The surfactant for adjusting the surface tension of the latex liquid to the above range is not particularly limited and, for example, a fatty acid-based surfactant can be used.
【００１２】例えば、界面活性剤としてオレイン酸カリ
ウムを用いた場合は、ソープカバー率が７０〜９０％程
度となるようにラテックス中に添加すれば良い。 ま
た、市販の高表面張力のラテックス液、例えばニッポー
ル１５６２（日本ゼオン(株)製）等を利用しても良い。For example, when potassium oleate is used as the surfactant, it may be added to the latex so that the soap cover ratio is about 70 to 90%. Alternatively, a commercially available high surface tension latex liquid, for example, Nipol 1562 (manufactured by Nippon Zeon Co., Ltd.) or the like may be used.
【００１３】手袋基体をラテックス液で処理する方法と
しては、基体にラテックス液を滴下する方法、スプレー
する方法、浸漬する方法等が挙げられるが、滴下あるい
はスプレーする方法が好ましい。Examples of the method of treating the glove substrate with the latex liquid include a method of dropping the latex liquid on the substrate, a method of spraying the substrate, a method of immersing the latex liquid, and the method of dropping or spraying is preferable.
【００１４】このラテックス液で処理された手袋基体
は、必要により余分なラテックス液を除去した後、６０
〜１２０℃程度の熱風で１０〜６０分間程度乾燥し、Ｎ
ＢＲ手袋とされる。The glove substrate treated with this latex solution was prepared by removing excess latex solution as needed, and then 60
Dry with hot air at ~ 120 ° C for about 10-60 minutes,
BR gloves.
【００１５】上記のようにしてＮＢＲ手袋を得ることが
できるが、この手袋に抗菌性や防臭性を付与するため、
ラテックス液中に抗菌剤や消臭剤を添加することもでき
る。添加することのできる抗菌剤の例としては、ネオシ
ントール（神東塗料(株)製）、プリベントールＢＣＭ
（バイエル(株)製）等を挙げることができ、また消臭剤
としては、ミズカナイト（水澤化学(株)製）等を挙げる
ことができる。NBR gloves can be obtained as described above, but in order to impart antibacterial and deodorant properties to these gloves,
An antibacterial agent and a deodorant may be added to the latex liquid. Examples of antibacterial agents that can be added are neocintol (manufactured by Shinto Paint Co., Ltd.) and Preventol BCM.
(Manufactured by Bayer Co., Ltd.) and the like, and examples of the deodorant include Mizukanite (manufactured by Mizusawa Chemical Co., Ltd.).
【００１６】また、本発明のＮＢＲ手袋には、その表面
の強度を挙げる目的で保護層を設けることもでき、更
に、ＮＢＲ手袋に直接あるいは上記保護層上に滑り止め
層を設けることもできる。Further, the NBR glove of the present invention may be provided with a protective layer for the purpose of increasing the strength of the surface thereof, and further, the NBR glove may be provided with a non-slip layer directly or on the protective layer.
【００１７】ＮＢＲ手袋上の保護層としては、ＮＢＲラ
テックスにより形成されるＮＢＲ層や塩化ビニルゾルに
より形成される塩化ビニル層が利用できる。例えば、保
護層としてＮＢＲ層を利用する場合、このＮＢＲを形成
させるためのラテックス液としては、従来のＮＢＲ層形
成のために利用されていたＮＢＲラテックス液を用いる
ことができる。 すなわち、保護層形成のためのラテッ
クス液には、特に表面張力についての制限はなく、例え
ば一般に利用されている表面張力が２５〜３５dyne／cm
程度のものを使用することができる。同様に、塩化ビニ
ルゾルを用いて保護層を形成する場合も使用する塩化ビ
ニルゾルの表面張力についても制約はない。As the protective layer on the NBR glove, an NBR layer formed of NBR latex or a vinyl chloride layer formed of vinyl chloride sol can be used. For example, when the NBR layer is used as the protective layer, the latex liquid for forming the NBR may be the conventional NBR latex liquid used for forming the NBR layer. That is, there is no particular limitation on the surface tension of the latex liquid for forming the protective layer. For example, the commonly used surface tension is 25 to 35 dyne / cm.
Something can be used. Similarly, there is no restriction on the surface tension of the vinyl chloride sol used when the protective layer is formed using the vinyl chloride sol.
【００１８】上記のＮＢＲラテックスあるいは塩化ビニ
ルゾル（以下、「保護層形成液」ということがある）を
用いて、ＮＢＲ手袋上に保護層を形成せしめるには、前
記の如くして製造されたＮＢＲ手袋を常法に従って保護
層形成液に浸漬し、乾燥させれば良い。 保護層形成液
中へのＮＢＲ手袋の浸漬は、例えば垂直浸漬等により、
３０〜６０秒間程度行えば良く、その後の乾燥は、１０
０〜２００℃程度の温風により、１０〜６０分程度行え
ば良い。In order to form a protective layer on an NBR glove using the above NBR latex or vinyl chloride sol (hereinafter sometimes referred to as "protective layer forming liquid"), the NBR glove manufactured as described above is used. It may be soaked in a protective layer forming liquid and dried according to a conventional method. Immersion of the NBR glove in the protective layer forming liquid is performed by, for example, vertical immersion.
It may be performed for about 30 to 60 seconds, and the subsequent drying is 10
It may be performed for about 10 to 60 minutes with warm air of about 0 to 200 ° C.
【００１９】更に、本発明のＮＢＲ手袋には、無機粉体
あるいは有機固形物を含有するバインダー液で処理する
ことにより、直接あるいは保護層の上から滑り止め層を
形、成せしめることもでき、また、加硫等を行うことも
できる。 これらも従来公知の方法で行うことができ
る。Furthermore, the NBR glove of the present invention can be treated with a binder solution containing an inorganic powder or an organic solid to form a non-slip layer directly or on the protective layer. It is also possible to carry out vulcanization and the like. These can also be performed by a conventionally known method.
【００２０】[0020]
【作用】本発明のＮＢＲ手袋は、相対的に高い表面張力
を有するラテックス液により手袋基体の繊維層と適当な
強度で接着したＮＢＲ層を形成させることにより製造さ
れるものである。そして、このようにして形成された手
袋は、繊維中へのＮＢＲの浸漬が適度に抑えられるの
で、耐油性と柔軟性を有するものとなるのである。ま
た、保護層形成液で保護層を形成せしめたＮＢＲ手袋
は、上記の特性の他、優れた機械的強度をも有するもの
である。The NBR glove of the present invention is manufactured by forming an NBR layer which is bonded to the fiber layer of the glove substrate with an appropriate strength by using a latex liquid having a relatively high surface tension. The glove formed in this way has oil resistance and flexibility because the immersion of NBR in the fibers can be appropriately suppressed. Further, the NBR gloves having the protective layer formed with the protective layer forming liquid have not only the above-mentioned characteristics but also excellent mechanical strength.
【００２１】[0021]
【実施例】次に、実施例および試験例を挙げ本発明を更
に詳しく説明する。EXAMPLES Next, the present invention will be described in more detail with reference to Examples and Test Examples.
【００２２】実 施 例 １
下記方法により、ＮＢＲ手袋を製造した。すなわち、ま
ず、温度が２０℃〜５０℃程度の金型に１３ゲージのメ
リヤス手袋をしわにならないように装着する。 このメ
リヤス手袋に下記表１の組成のＮＢＲ配合液を斜め浸漬
およびシャワーで均一になるよう塗布した後、指先下向
きで３分間放置する。 放置により余剰液が全てたれた
後、この手袋を７０〜１００℃の熱風で１０分間乾燥す
る。Example 1 NBR gloves were manufactured by the following method. That is, first, a 13 gauge knitted glove is attached to a mold having a temperature of about 20 ° C. to 50 ° C. so as not to wrinkle. The knitted gloves are coated with the NBR compounded liquid having the composition shown in Table 1 below so as to be evenly dipped and showered, and left for 3 minutes with the fingertips facing downward. After all the excess liquid has been dropped by leaving it, this glove is dried with hot air at 70 to 100 ° C. for 10 minutes.
【００２３】次いで常温で３〜１０分間冷却し、表２の
組成の滑り止め液に浸漬し、２〜１０秒で引き上げ、更
に７０〜１００℃の熱風で３０〜１００分乾燥を行う。
最後に、１２０〜１３０℃で１０〜２０分間加硫を行な
い、金型から離型した後、１２０℃で１０〜１５分間乾
燥を行ない、ＮＢＲ手袋（本発明品１）を得た。Then, it is cooled at room temperature for 3 to 10 minutes, immersed in a non-slip solution having the composition shown in Table 2, pulled up in 2 to 10 seconds, and dried with hot air at 70 to 100 ° C. for 30 to 100 minutes.
Finally, vulcanization was performed at 120 to 130 ° C. for 10 to 20 minutes, the mold was released, and then drying was performed at 120 ° C. for 10 to 15 minutes to obtain NBR gloves (product 1 of the present invention).
【００２４】 [0024]
【００２５】* ディスパージョンの組成は次の通りであ
る。
（ Ａ 部 ）
カゼイン ５ｇ
２５％ ＮＨ3ＯＨ ２ｇ
水 ４０ｇ
（ Ｂ 部 ）
コロイド硫黄特Ｍ ２０ｇ
１号亜鉛華 ４０ｇ
ノクセラ−ＢＺ １０ｇ
デモールＥＰ ５０ｇ
（顔料）ＬＮ-６４３Ａ ５０ｇ
水 １００ｇ* The composition of the dispersion is as follows. (Part A) Casein 5g 25% NH 3 OH 2g Water 40g (Part B) Colloidal Sulfur M 20g No. 1 Zinc Flower 40g Noxella-BZ 10g Demol EP 50g (Pigment) LN-643A 50g Water 100g
【００２６】（ 調 製 法 ）Ａ部を先に溶かしてからＢ
部と混ぜ、ボールミル中で４８時間撹拌し分散させる。(Preparation method) Melt part A first and then B
Parts and stir in a ball mill for 48 hours to disperse.
【００２７】なお、表１の組成物は、ＮＢＲラテックス
を計量後、これを撹拌しながら他の成分を添加し、添加
終了後更に３０分間撹拌を続けて調製した。The compositions shown in Table 1 were prepared by weighing NBR latex, adding other components while stirring the NBR latex, and continuing stirring for 30 minutes after the addition was completed.
【００２８】 [0028]
【００２９】* 表２の組成物の製法：バインダー以外の
成分を計量後、混合し、１２時間以上撹拌する。 次い
で、これに撹拌しながらバインダーを添加し、配合を終
了する。* Preparation method of the composition of Table 2: Components other than the binder are weighed, mixed, and stirred for 12 hours or more. Next, a binder is added to this while stirring, and the compounding is completed.
【００３０】実 施 例 ２
下記方法により、保護層付ＮＢＲ手袋を製造した。すな
わち、まず、温度が２０℃〜５０℃程度の金型に１３ゲ
ージのメリヤス手袋をしわにならないように装着する。
このメリヤス手袋に下記表３の組成のＮＢＲ配合液を
斜め浸漬し、均一になるよう塗布した後、指先下向きで
３分間放置する。 放置により余剰液が全てたれた後、
この手袋を７０〜１００℃の熱風で４０分間乾燥する。Example 2 NBR gloves with a protective layer were manufactured by the following method. That is, first, a 13 gauge knitted glove is attached to a mold having a temperature of about 20 ° C. to 50 ° C. so as not to wrinkle.
The knitted gloves are dipped in an NBR compounding solution having the composition shown in Table 3 below so as to be evenly coated, and then left for 3 minutes with the fingertip facing downward. After leaving all excess liquid by leaving it
The gloves are dried with hot air at 70 to 100 ° C for 40 minutes.
【００３１】次いで常温で３〜１０分間冷却し、表４の
組成のＮＢＲ配合液に垂直浸漬し、７０〜１００℃の熱
風で４０分間乾燥する。 なお、垂直浸漬時の引き上げ
速度は、１０秒〜６０秒／３０ｃｍとする。乾燥後、更
に前記表２の組成の滑り止め液に浸漬し、２〜１０秒で
引き上げ、更に７０〜１００℃の熱風で３０〜１００分
乾燥を行う。最後に、１２０〜１３０℃で１０〜２０分
間加硫を行ない、金型から離型した後、１２０℃で１０
〜１５分間乾燥を行ない、ＮＢＲ手袋（本発明品２）を
得た。Then, the mixture is cooled at room temperature for 3 to 10 minutes, vertically immersed in the NBR compounding liquid having the composition shown in Table 4, and dried with hot air at 70 to 100 ° C. for 40 minutes. The pulling rate during vertical immersion is 10 seconds to 60 seconds / 30 cm. After drying, it is further immersed in the non-slip solution having the composition shown in Table 2 above, pulled up in 2 to 10 seconds, and further dried with hot air at 70 to 100 ° C. for 30 to 100 minutes. Finally, after vulcanizing at 120 to 130 ° C. for 10 to 20 minutes and releasing from the mold, 10 at 120 ° C.
After drying for 15 minutes, NBR gloves (invention product 2) were obtained.
【００３２】 [0032]
【００３３】* ディスパージョンの組成および調製法は
表１と同じである。* Dispersion composition and preparation method are the same as in Table 1.
【００３４】なお、表３の組成物は、ＮＢＲラテックス
を計量後、これを撹拌しながら他の成分を添加し、添加
終了後更に３０分間撹拌を続けて調製した。The compositions shown in Table 3 were prepared by measuring NBR latex, adding other components while stirring the NBR latex, and continuing stirring for 30 minutes after the addition was completed.
【００３５】
* ディスパージョンの組成、調製法は表１と同じであ
る。
** 表４の組成物の調製法は、表１の組成物と同じ。[0035] * The composition and preparation method of the dispersion are the same as in Table 1. ** The preparation method of the composition of Table 4 is the same as the composition of Table 1.
【００３６】実 施 例 ３
メリヤス手袋の表３のＮＢＲ配合液の斜め浸漬をシャワ
ーに代える以外は実施例１と同様にしてＮＢＲ手袋（本
発明品３）を得た。Example 3 NBR gloves (product 3 of the present invention) were obtained in the same manner as in Example 1 except that shower was used instead of oblique immersion of the NBR compounding liquid shown in Table 3 of the knitted gloves.
【００３７】試 験 例
実施例１〜３で得られた本発明のＮＢＲ手袋について、
３０名のパネルにより、その柔軟性および指先感覚を調
べた。 なお、比較対照としては、表面張力が３０dyne
／cmのＮＢＲラテックス液を用い、１回浸漬法で調製さ
れたＮＢＲ手袋を用いた。この結果を表５に示す。Test Example Regarding the NBR gloves of the present invention obtained in Examples 1 to 3,
A panel of 30 people examined its flexibility and fingertip sensation. For comparison, the surface tension was 30 dyne.
The NBR gloves prepared by the single dipping method were used with the NBR latex solution of / cm. The results are shown in Table 5.
【００３８】 [0038]
【００３９】* 評価基準は次の通りである。 ＋＋： 試験項目が従来品より極めて良い。 ＋ ： 試験項目が従来品より良い。 ± ： 試験項目が従来品よりやや良い。 − ： 試験項目が従来品と同程度である。* The evaluation criteria are as follows. ++: Test items are significantly better than conventional products. +: The test items are better than conventional products. ±: Test items are slightly better than conventional products. -: Test items are similar to conventional products.
【００４０】この試験結果から、本発明手袋は柔軟性が
あり、指先感覚が良いものであることが明らかになっ
た。From the results of this test, it was revealed that the gloves of the present invention are flexible and have a good feeling on the fingertips.
【００４１】[0041]
【発明の効果】本発明の手袋は、耐油性があり、機械的
強度の高く、しかも柔軟性と指先感覚の良いものであ
る。従って、本発明によれば、作業用として極めて好適
なＮＢＲ手袋およびその製造方法が提供される。
以 上The glove of the present invention is oil resistant, has high mechanical strength, and is excellent in flexibility and fingertip feel. Therefore, according to the present invention, an NBR glove which is extremely suitable for work and a method for manufacturing the same are provided. that's all
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) A41D 19/00,19/04 ─────────────────────────────────────────────────── ─── Continuation of front page (58) Fields surveyed (Int.Cl. 7 , DB name) A41D 19/00, 19/04
Claims (3)
ne／cm以上であるＮＢＲラテックスに浸漬後、乾燥する
ことを特徴とするＮＢＲ手袋の製造方法。1. A knitted glove base material having a surface tension of 35 dy.
A method for manufacturing NBR gloves, which comprises drying in NBR latex having ne / cm or more and then drying.
たは消臭剤が添加されている請求項１記載のＮＢＲ手袋
の製造方法。 2. An antibacterial agent and / or in NBR latex.
The NBR glove according to claim 1, wherein a deodorant is added.
Manufacturing method.
ne／cm以上であるＮＢＲラテックスに浸漬後、乾燥し、
更にＮＢＲラテックスまたは塩化ビニルラテックスに浸
漬し、乾燥することを特徴とするＮＢＲ手袋の製造方
法。3. A knitted glove base material having a surface tension of 35 dy.
After soaking in NBR latex with ne / cm or more, dry,
A method for producing NBR gloves, further comprising immersing in NBR latex or vinyl chloride latex and drying.