JP3509247B2 - Resin composition for porous material, porous material and method for producing the same - Google Patents

Description

Detailed Description of the Invention

[0001]

FIELD OF THE INVENTION The present invention relates to a resin composition for a porous material containing an unsaturated polyester having a metal sulfonate group, a polymerizable monomer and water, and a porous material containing a filler therein. TECHNICAL FIELD The present invention relates to a resin composition, a porous material and a method for producing the same, and more particularly to a porous material suitable for civil engineering and building materials such as flooring materials used in places that are easily wet with water.

[0002]

2. Description of the Related Art Generally, a porous floor material is used for bathrooms, poolsides, etc., which are easily wet with water. As a floor material made of such a porous material, for example, Japanese Patent Laid-Open No. 03-14864
The one described in Japanese Patent Publication is known. This conventional porous material is manufactured by mixing an unsaturated polyester resin with a hydrophilic powder and improving the dispersibility with water to heat-cure an aqueous dispersion produced. I was trying.

[0003]

However, if the method of incorporating the hydrophilic powdery particles is adopted, the time required for the incorporation increases, the physical properties of the resin deteriorate due to the incorporation, the influence on the curing characteristics of the resin, etc. However, there is a drawback that the resin composition is different from the conventional resin composition.

[0004]

The present inventors have completed the present invention as a result of intensive research to solve the above problems.

That is, the present invention provides a resin composition for a porous material comprising (A) (a) an unsaturated polyester having a metal sulfonate group, (b) a polymerizable monomer, and (c) water, and further ( B) A resin composition containing a filler, preferably 1 of an unsaturated polyester resin containing a metal sulfonate group.
It is a dispersion of 0.05 to 0.80 parts by weight of water with respect to parts by weight, preferably the resin composition according to claim 1 or 2 is used as a surface layer, preferably 1
To 3) a method for producing a porous material, preferably pouring, wherein the resin composition is cast or applied onto a mold, a release paper, or a substrate, and then water is removed by heating to make the material porous. The agent is calcium carbonate powder, clay, alumina powder, silica powder, talc, barium sulfate, silica powder, glass powder, glass beads, mica, aluminum hydroxide, cellulose thread, silica sand, river sand, cold water stone, marble scrap,
It is intended to provide a resin composition for a porous material, which is one or more kinds selected from crushed stone, and a porous material.

Next, the present invention will be described in detail.

(Structure) The unsaturated polyester (a) used in the present invention is obtained by a condensation reaction of a dibasic acid containing an α, β-unsaturated dibasic acid and a polyhydric alcohol, and is preferably Has a number average molecular weight of 500 to 5,000. Further, it may be a mixture of an unsaturated polyester resin containing a metal sulfonate base as an essential component and a general unsaturated polyester resin, a vinyl ester resin, an acrylated polyester resin, etc., usually at room temperature dissolved in a monomer. It is liquid.

Examples of the α, β-unsaturated dibasic acid used for preparing the unsaturated polyester (a) include maleic acid, maleic anhydride, fumaric acid and halogenated maleic anhydride. As the saturated dibasic acid, phthalic acid, phthalic anhydride, halogenated phthalic anhydride, isophthalic acid, terephthalic acid, tetrahydrophthalic acid, tetrahydrophthalic anhydride, hexahydrophthalic acid, hexahydrophthalic anhydride, hexahydroterephthalic acid, Hexahydroisophthalic acid, succinic acid, malonic acid, glutaric acid, adipic acid, sebacic acid, 1,12-
Dodecane diacid, 2,6-naphthalenedicarboxylic acid, 2,
7-naphthalenedicarboxylic acid, 2,3-naphthalenedicarboxylic acid, 2,3-naphthalenedicarboxylic anhydride,
4,4'-biphenyldicarboxylic acid, dialkyl esters thereof and the like can be mentioned.

Examples of polyhydric alcohols include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, 2 -Methyl-1,3-propanediol, 1,3
-Butanediol, neopentyl glycol, hydrogenated bisphenol A, 1,4-butanediol, an adduct of bisphenol A and propylene oxide or ethylene oxide, 1,2,3,4-tetrahydroxybutane , Glycerin, trimethylolpropane, 1,3-propanediol, 1,2-cyclohexane glycol, 1,3
-Cyclohexane glycol, 1,4-cyclohexane glycol, 1,4-cyclohexane dimethanol, paraxylene glycol, bicyclohexyl-4,4'-
Examples thereof include diol, 2,6-decalin glycol and 2,7-decalin glycol.

Further, the raw material for introducing the metal sulfonate group into the unsaturated polyester is a dibasic acid or a polyhydric alcohol (in the case of a dibasic acid, a condensable derivative thereof may be used), for example, sulfoisophthalic acid or sulfo. Terephthalic acid, sulfophthalic acid, 4-sulfonaphthalene-2,
A sodium salt of 7-dicarboxylic acid (or a derivative thereof) and one of the following structural formulas (formula 1 and formula 2):

[0011]

[Chemical 1]

[0012]

[Chemical 2]

And the like.

The raw material for introducing the sulfonate group into the unsaturated polyester of the present invention is 0.5 to 20% by weight in the unsaturated polyester solid component, preferably 3.
0 wt% to 5 wt% is used. If it exceeds 20% by weight, it becomes difficult to produce the unsaturated polyester, and the heat resistance of the resin is significantly lowered. On the other hand, if it is less than 0.1% by weight, sufficient dispersibility of water cannot be obtained, which is not preferable.

Examples of the polymerizable monomer (b) used in the present invention include styrene, t-butylstyrene, divinylbenzene, chlorostyrene, vinyltoluene, vinyl acetate, α-methylstyrene, diallyl phthalate, Examples thereof include alkyl esters of acrylic acid and alkyl esters of methacrylic acid, and one or more of these monomers can be effectively used. These may be used alone or in combination, and may be unsaturated polyesters 10 to 70.
Parts by weight, preferably 30 to 50 parts by weight, are dissolved in 90 to 30 parts by weight, preferably 70 to 50 parts by weight of the copolymerizable monomer to form the composition.

The resin composition may also contain a polymerization inhibitor, preferably tolhydroquinone, hydroquinone, benzoquinone, hydroquinone monomethyl ether, p-tert-butylcatechol, 2,6-t.
It is possible to add a polymerization inhibitor such as ert-butyl-4-methylphenol to the mixture, preferably 10 to 2000 ppm.

Further, the thermosetting resin composition containing the unsaturated polyester (a) and the polymerizable monomer (b) contains a curing agent to accelerate its curing. Organic peroxides are particularly preferable. Specifically, known materials such as diacyl peroxide-based, peroxy ester-based, hydroperoxide-based, dialkyl peroxide-based, ketone peroxide-based, peroxyketal-based, alkyl perester-based, percarbonate-based are used, It can be appropriately selected depending on molding conditions, curing temperature and the like.

The amount of the curing agent added is unsaturated polyester.
With respect to 100 parts by weight of the total amount of (a) and the polymerizable monomer (b),
It is 0.1 to 4 parts by weight. You may use the said hardening | curing agent in combination of 2 or more types.

Unsaturated polyester (a) and polymerizable monomer (b)
The thermosetting resin composition containing and preferably contains a curing accelerator. Preferably, metal soaps such as cobalt naphthenate, cobalt octenoate, vanadyl octenoate, copper naphthenate, barium naphthenate, and the like, as the metal chelate compound, vanadyl acetyl acetate, cobalt acetyl acetate, iron acetyl acetonate. is there. The amines include dimethylaniline, Nn-diethylaniline, Nn-dimethylparatoluidine, N-ethyl-metatoluidine, triethanolamine, metatoluidine, diethylenetriamine,
Examples include pyridine, phenylmorpholine, piperidine, diethanolaniline and the like.

The amount of the curing accelerator added is preferably 0.1 to 3 parts by weight based on 100 parts by weight of the total amount of the unsaturated polyester (a) and the polymerizable monomer (b). In the present invention, amine-based accelerators are preferred. The curing accelerator may be added to the resin in advance, or may be added at the time of use.

The filler (B) used in the present invention is preferably, for example, calcium carbonate powder, clay, alumina powder, silica powder, talc, barium sulfate, silica powder, glass powder, glass beads, mica, water. Examples thereof include aluminum oxide, cellulose yarn, silica sand, river sand, cold water stone, and marble chips. Particularly preferred is calcium carbonate powder.

The proportion of each component in the composition of the present invention is 0.05 to 0.80 part by weight of water (c), preferably 1 part by weight of the thermosetting resin composition (A). 0.0
5 to 0.50 parts by weight, 0 to 5 parts by weight of the filler (B), preferably 0 to 2 parts by weight. If the amount of water is more than the above range, the water is likely to separate and a uniform composition is not obtained, resulting in poor curing.

In the composition of the present invention, a thermosetting resin composition containing a curing initiator, a curing accelerator and the like added as necessary is mixed with a filler and water is added, or conversely, water is added first. In addition to the above, the filler may be added after mixing. From the viewpoint of workability, thermosetting resin composition, water (c) and inorganic filler (B)
It is preferable to prepare the mixture and the mixture separately and then mix the both.

The method for producing a porous material according to the present invention is a method in which the above resin composition is used as a mold, a release paper, or a substrate (for example, concrete, metal, wood, tile, plastic, FRP).
Etc.) is cast or applied, and then heated, preferably at 60 to 130 ° C., more preferably at 70 to 110 ° C., to remove water and cure, whereby a porous material can be obtained.

[0025]

EXAMPLES The present invention will be described in more detail with reference to examples below, but the present invention is not limited to these examples. In addition, "part" in the text means part by weight.

First, the thermosetting resin compositions A, B, C, D
Was manufactured as follows. (1) Thermosetting resin composition A In a 3 liter four-necked flask equipped with a thermometer, a stirrer, an inert gas inlet, and a reflux condenser, 749 parts of diethylene glycol, 365 parts of terephthalic acid, and 5-sodium sulfo were prepared. 54 parts of isophthalic acid was charged, the temperature was raised to 210 ° C., and when the solid acid value became 1 or less, 146 parts of adipic acid, 237 parts of phthalic anhydride, and 1 part of maleic anhydride.
96 parts were charged, the temperature was raised to 210 ° C., and after reacting for 16 hours, 960 parts of styrene monomer, 0.10 part of tolhydroquinone, 0.04 part of 5% copper naphthenate were added, and the nonvolatile content was 61.4% and the acid value was 18. 3. An unsaturated polyester resin having a Gardner viscosity R was obtained.

(2) Thermosetting resin composition B In a three-liter four-necked flask equipped with a thermometer, a stirrer, an inert gas inlet, and a reflux condenser, 551 parts of neopentyl glycol and 378 parts of isophthalic acid, Charge 50 parts of 5-sodium sulfoisophthalic acid, raise the temperature to 210 ° C., and when the solid acid value becomes 1 or less, charge 201 parts of propylene glycol and 580 parts of fumaric acid.
After heating to 10 ° C and reacting for 9 hours, styrene monomer 1
301 parts, hydroquinone 0.12 parts, 4-tert-butyl catechol 0.17 parts, copper naphthenate 0.12
Parts were added to obtain an unsaturated polyester resin having a nonvolatile content of 54.8%, an acid value of 7.2 and a Gardner viscosity QR.

(3) Thermosetting resin composition C 100 parts by weight of calcium carbonate was added to 50 parts by weight of the resin composition A and sufficiently stirred by a high speed disperser to obtain a resin composition.

(4) Thermosetting resin composition D To 50 parts by weight of resin composition B, 100 parts by weight of calcium carbonate was added and sufficiently stirred with a high speed disperser to obtain a resin composition.

Example 1-4 0.2 parts by weight of water was added to 1 part by weight of each of the compositions A, B, C and D obtained above, and each resin composition was prepared by mixing with a high-speed stirrer. With respect to parts by weight, benzoyl peroxide of 0.
Add 01 parts by weight, cast, heat cure (80 ° C),
A molded body was obtained.

When the weight of each molded product was measured, it was almost the same as the total amount of water scattered, and it was confirmed that the molded product was porous due to the water scattering. .

Molds were formed on the molded products by the method specified in JIS-Z2911, and the mold-generated parts were wiped off after 4 weeks. All the molded products could be completely removed.

Example 5-8 To 1 part by weight of each of the compositions A, B, C and D obtained above, 0.2 parts by weight of water was added and mixed with a high-speed stirrer to prepare 1 of each resin composition. 2 parts by weight of No. 7 silica sand,
Add 0.01 parts by weight of benzoyl peroxide to give a diameter of about 6.
It was poured into a petri dish of 5 cm and cured by heating (120 ° C.) to obtain a molded body of porous material.

When 10 cc of water was dropped onto the upper surface of this molded product by a spoid, all the porous molding materials of the A, B, C and D resin compositions were completely passed to the lower surface in about 30 seconds.

[0035]

EFFECTS OF THE INVENTION The composition of the present invention can be easily cured by heating in a state where water is dispersed, to obtain a molded product which becomes a porous material. The molded product is resistant to stains such as mold. It has excellent properties. Therefore, it is useful as a civil engineering and building material such as a floor material around the water in bathrooms, washrooms, etc., which requires mold resistance and porosity.

─────────────────────────────────────────────────── ─── Continuation of front page (58) Fields surveyed (Int.Cl. ⁷ , DB name) C08F 283/01 C08L 67/06 C08K 3/00 C08J 9/00

Claims (6)

(57) [Claims] 1. A resin composition for a porous material comprising (A) (a) an unsaturated polyester having a metal sulfonate group (b) a polymerizable monomer (c) water. 2. A porous material comprising (A) a thermosetting resin composition containing (a) an unsaturated polyester having a metal sulfonate group (b) a polymerizable monomer (c) water and (B) a filler. Resin composition for flexible materials. 3. From 1 part by weight of the unsaturated polyester resin containing a metal sulfonate group, water is added in an amount of 0.05 to.
The resin composition according to claim 1, wherein 0.80 parts by weight is dispersed. 4. A porous material comprising the resin composition according to claim 1 or 2 as a surface layer. 5. After casting or coating the resin composition according to any one of claims 1 to 3 onto a mold, a release paper or a substrate,
A method for producing a porous material, which comprises heating to remove water to make the material porous. 6. The filler (B) is calcium carbonate powder, clay, alumina powder, silica powder, talc, barium sulfate, silica powder, glass powder, glass beads, mica, aluminum hydroxide, cellulose thread, silica sand, river sand. , Cold water stone,
The resin composition according to claim 2, which is one or more kinds selected from marble scraps.