JP3468971B2 - Cosmetics - Google Patents

Cosmetics

Info

Publication number
JP3468971B2
JP3468971B2 JP05250896A JP5250896A JP3468971B2 JP 3468971 B2 JP3468971 B2 JP 3468971B2 JP 05250896 A JP05250896 A JP 05250896A JP 5250896 A JP5250896 A JP 5250896A JP 3468971 B2 JP3468971 B2 JP 3468971B2
Authority
JP
Japan
Prior art keywords
resin powder
silicone
primary particle
solution
silicone resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP05250896A
Other languages
Japanese (ja)
Other versions
JPH0971509A (en
Inventor
章裕 黒田
由希夫 阿川
Original Assignee
カネボウ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by カネボウ株式会社 filed Critical カネボウ株式会社
Priority to JP05250896A priority Critical patent/JP3468971B2/en
Publication of JPH0971509A publication Critical patent/JPH0971509A/en
Application granted granted Critical
Publication of JP3468971B2 publication Critical patent/JP3468971B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【発明の属する技術分野】本発明は、感触および化粧効
果持続性に優れ、かつ小じわの隠ぺい効果にも優れた化
粧料に関する。さらに詳しくは、シリコーン樹脂粉体を
事前に粉砕して得られる粉砕溶液を配合することで、感
触および化粧効果持続性に優れ、かつ小じわの隠ぺい効
果にも優れた化粧料に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cosmetic composition which is excellent in touch and long-lasting effect of cosmetics and also in the effect of hiding fine wrinkles. More specifically, the present invention relates to a cosmetic composition which is excellent in touch and long-lasting effect of cosmetics and also in the effect of hiding fine wrinkles by blending a grinding solution obtained by previously grinding a silicone resin powder.

【0002】[0002]

【従来の技術および発明が解決しようとする課題】従
来、特開平2−243612号公報、特開平7−533
33号公報、特公平4−66446号公報、特公平6−
51614号公報には、種々の珪素含有樹脂粉体をその
まま液体化粧料に配合することで、感触、保湿性などの
特性が向上することが知られている。
2. Description of the Related Art Conventionally, JP-A-2-243612 and JP-A-7-533 have been proposed.
Japanese Patent No. 33, Japanese Patent Publication No. 4-66446, Japanese Patent Publication No. 6-
It is known from Japanese Patent Publication No. 51614 that blending various silicon-containing resin powders into a liquid cosmetic composition as it is improves properties such as touch and moisture retention.

【0003】これらの珪素含有樹脂粉体は、ホモミキサ
ー等の様な、粉砕力の弱い装置を用いて製剤中で粉砕し
た状態では均一な分散状態とはならずに、ある程度の粉
体が集合した二次凝集体の形で存在している場合が多
い。
These silicon-containing resin powders are not uniformly dispersed when they are crushed in a preparation using a device having a weak crushing force such as a homomixer, but some powders are aggregated. Often present in the form of secondary aggregates.

【0004】これに対して、特公平6−55897号公
報には、低粘度シリコーン油とシリコーン樹脂をロール
ミルで混練りしたペースト状シリコーン組成物に関する
技術が述べられている。この場合、二次凝集体はおおよ
そほぐれており、増粘性が得られる特徴がある。しかし
ながら、この組成物は増粘性を目的としたため、組成物
からの低粘度シリコーン油のブリード性の有無を中心と
した技術であり、油剤内の樹脂の存在状態により、光学
コントロールが可能となる技術については開示されてい
ない。そして、ペースト内での樹脂が複合化されていな
いため、化粧料配合時の塗布感がぼそぼそとしたものに
なる問題があった。さらに、上記公報の実施例によれば
その平均粒子径は100〜500μmの不定型粒子で大
粒子のものを使用しており、粉砕した系の屈折率をコン
トロールするという光学コントロールには不適であっ
た。したがって、本発明者らは、シリコーン樹脂粉体の
粉砕方法と化粧効果について光学的検討を鋭意行い、小
じわの隠ぺい効果と化粧効果持続性に優れる化粧料を得
ることを目的とするものである。
On the other hand, Japanese Patent Publication No. 6-55897 discloses a technique relating to a paste-like silicone composition obtained by kneading a low-viscosity silicone oil and a silicone resin with a roll mill. In this case, the secondary agglomerates are roughly loosened, and the characteristic is that thickening is obtained. However, since this composition is intended for thickening, it is a technology that focuses on the presence or absence of bleeding properties of the low-viscosity silicone oil from the composition, and it is a technology that enables optical control depending on the presence state of the resin in the oil agent. Is not disclosed. In addition, since the resin in the paste is not composited, there is a problem that the application feeling when blending the cosmetic material becomes unclear. Further, according to the examples of the above publications, the amorphous particles having an average particle diameter of 100 to 500 μm and large particles are used, which is not suitable for optical control of controlling the refractive index of the pulverized system. It was Therefore, the present inventors have made an optical study on the pulverizing method of silicone resin powder and the cosmetic effect, and an object of the present invention is to obtain a cosmetic material having a fine wrinkle hiding effect and an excellent cosmetic effect sustainability.

【0005】[0005]

【課題を解決するための手段】上記の目的は、平均一次
粒子径0.1〜30μmの範囲にあるシリコーン樹脂粉
体をシリコーン油を含む油剤中で粉砕して得られる粉砕
溶液を事前に作製し、これを化粧料に配合することによ
って、本発明を達成できる。すなわち、シリコーン樹脂
粉体の有する感触を維持したまま、小じわの隠ぺい効果
と化粧効果持続性に優れる化粧料が得られることを見い
だした。
The above-mentioned object is to prepare in advance a pulverized solution obtained by pulverizing a silicone resin powder having an average primary particle diameter of 0.1 to 30 μm in an oil agent containing silicone oil. Then, the present invention can be achieved by blending this with a cosmetic. That is, silicone resin
It was found that a cosmetic having a fine wrinkle hiding effect and a long-lasting cosmetic effect can be obtained while maintaining the feel of the powder .

【0006】さらに詳しくは、粉砕溶液内で、シリコー
樹脂粉体由来の構造が密になっている部位では屈折率
が高く、逆に粗になっている部位では屈折率が低いこと
を利用し、この屈折率の変化を粉砕溶液内で連続的に発
生させることで、光の屈折を任意に変化させ、しわなど
の皮膚表面状態を光学的にぼやかすこと(以後、この状
態を「乱屈折」と定義する)が可能な化粧料が得られる
ことを見いだした。
[0006] More particularly, in a grinding solution, silicone
The refractive index is high in the area where the structure derived from the resin powder is dense, and conversely, the refractive index is low in the area where the structure is coarse. By causing it to occur, it is possible to obtain cosmetics that can arbitrarily change the refraction of light and optically obscure skin surface conditions such as wrinkles (hereinafter, this condition is defined as "random refraction"). I found a thing.

【0007】本発明の構成は、以下の通りである。すな
わち、本発明の請求項1は、粉砕する混合液100重量
部に対し、平均一次粒子径が0.1〜30μmのシリコ
ーン樹脂粉体(但し、ナイロン樹脂粉体をシリコーン化
合物で被覆した樹脂粉体は除く)5〜75重量部が、環
状シリコーン、揮発性直鎖状シリコーンから選ばれるシ
リコーン油を含む油剤中で粉砕して得られた粉砕溶液を
配合した化粧料である。
The structure of the present invention is as follows. That is, a first aspect of the present invention, with respect to mixture 100 parts by weight of pulverized, the average primary particle size of 0.1~30μm silico
Over emissions resin powder (however, siliconized nylon resin powder
Resin powder is excluded) 5 to 75 parts by weight coated with compound is blended with a cyclic silicone, pulverized solution obtained was triturated in oil comprising a silicone oil selected from volatile linear silicone cosmetic Is.

【0008】本発明の請求項2は、シリコーン樹脂粉体
の一次構造が崩れている状態に粉砕した粉砕溶液を配合
した請求項1に記載の化粧料である。
A second aspect of the present invention is the cosmetic material according to the first aspect, which contains a pulverized solution pulverized in a state in which the primary structure of the silicone resin powder is collapsed.

【0009】本発明の請求項3は、粉砕前のシリコーン
樹脂粉体の一次粒子形状が球状であり、かつその平均一
次粒子径(A)に対して、粉砕後の該シリコーン樹脂粉
体の平均一次粒子径(B)の割合(B)/(A)が、
0.3〜0.9である粉砕溶液を配合した請求項1また
は2に記載の化粧料である。
According to a third aspect of the present invention, the primary particle shape of the silicone resin powder before pulverization is spherical, and the average primary particle diameter (A) of the silicone resin powder after pulverization is the same. The ratio (B) / (A) of the average primary particle diameter (B) of the powder is
It is a cosmetics of Claim 1 or 2 which mix | blended the grinding | pulverization solution which is 0.3-0.9.

【0010】本発明の請求項4は、粉砕前のシリコーン
樹脂粉体の一次粒子形状が球状であり、その平均一次粒
子径(A)に対して、粉砕後の該シリコーン樹脂粉体の
平均一次粒子径(B)の割合(B)/(A)が、0〜
0.4である粉砕溶液を配合した請求項1または2に記
載の化粧料である。
According to a fourth aspect of the present invention, the primary particle shape of the silicone resin powder before pulverization is spherical, and the average primary particle diameter (A) of the silicone resin powder after pulverization is the same. The ratio (B) / (A) of the average primary particle size (B) of the body is 0 to
The cosmetic according to claim 1 or 2, which is blended with a pulverized solution of 0.4.

【0011】本発明の請求項5は、粉砕前のシリコーン
樹脂粉体の一次粒子形状が球状であり、かつその平均一
次粒子径(A)に対して、粉砕後のシリコーン樹脂粉体
の平均一次粒子径(B)の割合(B)/(A)が、0〜
0.4である粉砕溶液と、有機系または無機系の紫外線
防御成分を配合した請求項1または2に記載の化粧料で
ある。
According to a fifth aspect of the present invention, the primary particle shape of the silicone resin powder before pulverization is spherical, and the average particle diameter (A) of the silicone resin powder after pulverization is the same as that of the silicone resin powder after pulverization. The ratio (B) / (A) of the average primary particle size (B) of the body is 0 to
The cosmetic according to claim 1 or 2, wherein a pulverized solution of 0.4 and an organic or inorganic ultraviolet protection component are blended.

【0012】[0012]

【発明の実施の形態】以下、本発明の実施の形態につい
て詳述する。
BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in detail below.

【0013】 本発明で用いるシリコーン樹脂粉体とは、
電子顕微鏡を用いた観察による樹脂粉体の平均一次粒子
径が、0.1〜30μmの範囲にあり、ましくは0.
1〜20μmであって、珪素原子を含有していることが
特徴である。樹脂の粒度分布は狭くても広くても構わな
い。但し、50μm以上の粒度分布が大きい場合には、
小じわの隠ぺい性が弱くなる問題がある。また、その形
状は、球状、不定形状、塊状、板状、針状などが挙げら
れる。この内、本発明の目的から球状もしくは、球状の
集合体が最も好ましい。
The silicone resin powder used in the present invention is
The average primary particle diameter of the resin powder by observation using an electron microscope, in the range of 0.1 to 30 [mu] m, is good Mashiku 0.
The feature is that it is 1 to 20 μm and contains a silicon atom. The particle size distribution of the resin may be narrow or wide. However, when the particle size distribution of 50 μm or more is large,
There is a problem that the hiding power of fine wrinkles is weakened. The shape may be spherical, irregular, lumpy, plate-like, needle-like or the like. Of these, spherical or spherical aggregates are most preferable for the purpose of the present invention.

【0014】 シリコーン 樹脂粉体としては、内外のシ
リコーンメーカーより発売されているシリコーン樹脂粉
体が挙げられ、例えば東芝シリコーン製のトスパールシ
リーズや東レ・ダウコーニング・シリコーン製のトレフ
ィルシリーズなどが挙げられる。この内、特に本発明で
用いるシリコーン樹脂粉体としてはトレフィルシリーズ
ましい。
[0014] as a silicone resin powder, silicone resin powder and the like that have been released from countries inside and outside of the silicone manufacturers, for example, Toshiba made of silicone toss Pearl series and manufactured by Dow Corning Toray Silicone Co. DOO refill series And so on. Among them, preparative refill series good preferable particularly as the silicone resin powder used in the present invention.

【0015】 本発明では、シリコーン樹脂粉体の内、塑
性変形を受け易い、エラストマー(例えば、シリコーン
弾性パウダー:前記トレフィルシリーズなど)としての
特性を有するものが好ましい。
In the present invention, among the silicone resin powders, those having properties as an elastomer (for example, silicone elastic powder: the trefill series, etc.) which are easily subjected to plastic deformation are preferable.

【0016】 本発明で用いるシリコーン油としては、
状シリコーン、揮発性直鎖状シリコーンである。環状シ
リコーンの好ましい例としては、オクタメチルシクロテ
トラシロキサン(以後、D4と呼ぶ)、デカメチルシク
ロペンタシロキサン(以後、D5と呼ぶ)が挙げられ
る。
[0016] As the silicone oil used in the present invention, the ring <br/> like silicone, a volatile linear silicone. Preferred examples of the cyclic silicone include octamethylcyclotetrasiloxane (hereinafter referred to as D4) and decamethylcyclopentasiloxane (hereinafter referred to as D5).

【0017】 本発明で用いる油剤としては、化粧料に使
用可能な従来公知の物質を使用することができる。例え
ばステアリルアルコール、セチルアルコール、イソステ
アリルアルコール、ラウリルアルコール、ヘキサデシル
アルコール、オクチルドデカノール等の高級アルコー
ル、グリセリン、ポリエチレングリコール、1,3−ブ
タンジオール、プロピレングリコール、マルビトール等
の多価アルコール、イソステアリン酸、ステアリン酸、
ウンデシレン酸、オレイン酸等の脂肪酸、ミリスチン酸
ミリスチル、ラウリン酸ヘキシル、オレイン酸デシル、
ミリスチン酸イソプロピル、パルミチン酸イソプロピ
ル、ジメチルオクタン酸ヘキシルデシル、モノステアリ
ン酸グリセリン、フタル酸ジエチル、モノステアリン酸
エチレングリコール、オキシステアリン酸オクチル等の
エステル類、流動パラフィン、ワセリン、スクワラン等
の炭化水素、ラノリン、還元ラノリン、カルナバロウ等
のロウ、ミンク油、カカオ脂、ヤシ油、パーム核油、ツ
バキ油、ゴマ油、ヒマシ油、オリーブ油等の油脂、エチ
レン・α−オレフィン・コオリゴマー、流動イソパラフ
ィン、軽質流動イソパラフィン、パラフィン、有機系紫
外線吸収剤等が挙げられる。この内、従来の化粧料への
配合割合が多く、粉砕溶液配合時にもとの処方系に影響
が少ない油剤である、常温で液体のエステル油、多価ア
ルコール、パラフィン類、有機系紫外線吸収剤が好まし
い。さらに、本発明では、油剤としてシリコーン油のみ
を油剤として用いることも可能である。
As the oil agent used in the present invention, conventionally known substances that can be used in cosmetics can be used. For example, higher alcohols such as stearyl alcohol, cetyl alcohol, isostearyl alcohol, lauryl alcohol, hexadecyl alcohol and octyldodecanol, polyhydric alcohols such as glycerin, polyethylene glycol, 1,3-butanediol, propylene glycol and malbitol, isostearic acid. ,stearic acid,
Undecylenic acid, fatty acids such as oleic acid, myristyl myristate, hexyl laurate, decyl oleate,
Isopropyl myristate, isopropyl palmitate, hexyldecyl dimethyloctanoate, glyceryl monostearate, diethyl phthalate, ethylene glycol monostearate, esters of octyl oxystearate, hydrocarbons such as liquid paraffin, petrolatum and squalane, lanolin , Reduced lanolin, waxes such as carnauba wax, mink oil, cacao butter, coconut oil, palm kernel oil, camellia oil, sesame oil, castor oil, oils and fats such as olive oil, ethylene / α-olefin / co-oligomer, liquid isoparaffin, light liquid isoparaffin , Paraffin, organic UV absorbers and the like. Of these, an oil agent that has a large blending ratio with conventional cosmetics and has little effect on the original formulation system when blending a pulverized solution.Ester oil, polyhydric alcohol, paraffins, organic UV absorbers that are liquid at room temperature. Is preferred. Further, in the present invention, it is possible to use only silicone oil as an oil agent.

【0018】 本発明では、シリコーン樹脂粉体をシリコ
ーン油を含む油剤中で粉砕または摩砕して粉砕溶液を得
る。粉砕の方法としては、湿式粉砕機を用いることが好
ましい。湿式粉砕機に粉砕媒体が必要な場合には、その
種類は問わないが、安全性の見地からセラミックス、ア
ルミナ、ポリアセタール樹脂等の樹脂が好ましい。湿式
粉砕機の例としては、マイクロス、ダイノミル、オング
ミル、ペイントコンディショナー、サンドミル、ボール
ミル等が挙げられるがこれに限定されるものではない。
また、一般的には、生産性とコストに優れたサンドミ
ル、ダイノミル、マイクロス等の媒体ミルを用いること
が好ましい。
In the present invention, the silicone resin powder is pulverized or ground in an oil agent containing silicone oil to obtain a pulverized solution. A wet pulverizer is preferably used as the pulverizing method. When a pulverizing medium is required for the wet pulverizer, the type is not limited, but from the viewpoint of safety, resins such as ceramics, alumina and polyacetal resin are preferable. Examples of wet pulverizers include, but are not limited to, Micros, Dynomill, Ongmill, paint conditioner, sand mill, ball mill and the like.
Further, in general, it is preferable to use a media mill such as a sand mill, a dyno mill, or a micros, which is excellent in productivity and cost.

【0019】 本発明では、粉砕溶液100重量部中に
リコーン樹脂粉体が5〜75重量部含まれている5重
量部未満では、製品系内でのシリコーン樹脂粉体の配合
量が少ないために、シリコーン樹脂粉体の特徴が得られ
にくくなり、また、75重量部を超えると、粉砕溶液の
粘性が上昇するため、製品系への配合および再分散が行
いにくくなる傾向がある。
In the present invention, sheet during the milling solution 100 parts by weight
The silicone resin powder is contained in an amount of 5 to 75 parts by weight . If the amount is less than 5 parts by weight, it is difficult to obtain the characteristics of the silicone resin powder because the amount of the silicone resin powder in the product system is small, and if it exceeds 75 parts by weight, the viscosity of the pulverized solution increases. Therefore, it tends to be difficult to mix and redisperse the product in the product system.

【0020】 また、粉砕溶液中のシリコーン樹脂粉体の
濃度が30重量部を超えた場合では、一般に粘性が増加
するため、粉砕効率の低下が発生する。この場合、ポリ
エーテル変性シリコーンやアクリルシリコーンなどの界
面活性効果を有する成分もしくは界面活性剤を使用する
ことで粘度上昇を抑制することができる。
Further, when the concentration of the silicone resin powder in the grinding solution exceeds 30 parts by weight, the viscosity generally increases, so that the grinding efficiency decreases. In this case, an increase in viscosity can be suppressed by using a component or a surfactant having a surfactant effect such as polyether modified silicone or acrylic silicone.

【0021】 本発明で用いる粉砕の条件は、粉砕機の粉
砕効率や粉砕能力によって異なるが、もとのシリコーン
樹脂粉体の一次構造が崩れている状態が好ましい。この
「一次構造が崩れている状態」の評価方法としては、例
えば以下に示す方法が挙げられる。
The crushing conditions used in the present invention vary depending on the crushing efficiency and crushing ability of the crusher, but it is preferable that the original primary structure of the silicone resin powder is collapsed. Examples of the method for evaluating the “state in which the primary structure is broken” include the following methods.

【0022】 シリコーン 樹脂粉体を含み、強い力で粉砕
していない状態の溶液を走査型電子顕微鏡の試料台に塗
布し1000倍程度の倍率にて観察した時の、シリコー
樹脂粉体の平均一次粒子径を測定し、これを数視野に
て行い平均値を得る。この平均値をAとする。次に、
リコーン樹脂粉体が粉砕されている状態の溶液を同様に
して観察する。この時の平均一次粒子径をBとする。こ
の時、B/Aの値が0〜0.9の範囲に入っている場合
を、一次構造が崩れている状態とする。すなわち、この
状態では、シリコーン樹脂粉体が機械的に変形を受け、
構造が変化していることを示している。なお、B/Aの
値が0の状態とは、一次粒子が完全に変形を受けて、本
来の構造を失ってしまったこと、すなわち、粒子構造が
認められない状態を示す。
[0022] comprises a silicone resin powder, a strong state which is not crushed by the force solution when observed by a scanning electron microscope sample stage applied 1000 times the magnification of a silicone
The average primary particle size of the emission resin powder was measured to obtain an average value performed by several viewing it. Let this average value be A. Then,
Similarly, the solution in which the ricone resin powder is crushed is observed. The average primary particle diameter at this time is defined as B. At this time, when the value of B / A is in the range of 0 to 0.9, the primary structure is broken. That is, in this state, the silicone resin powder is mechanically deformed,
It shows that the structure is changing. The B / A value of 0 means that the primary particles have been completely deformed and lost their original structure, that is, the particle structure is not recognized.

【0023】 ここで、小じわの隠ぺいを目的とする場合
には、B/Aの値は、0.3〜0.9の範囲にあること
が好ましい。この範囲であれば、小じわの隠ぺい性が高
い効果がある。B/Aの値が0〜0.3の範囲では、粉
砕溶液内での局所的な屈折率の変化が少なく、光の乱屈
折が生じにくいため、小じわの隠ぺい性は低下する。ま
た、B/Aの値が0.9を超えると、ただの樹脂分散溶
液となってしまい、本発明でいう構造の変化が認められ
ない。
[0023] Here, for the purpose of hiding the fine lines, the value of B / A is preferably in the range of 0.3 to 0.9. Within this range, the effect of hiding fine wrinkles is high. When the value of B / A is in the range of 0 to 0.3, the local change in the refractive index in the pulverized solution is small, and light irregular refraction hardly occurs, so the hiding property of fine wrinkles decreases. Further, if the value of B / A exceeds 0.9, the resin dispersion becomes a mere resin dispersion solution, and the change in the structure referred to in the present invention is not recognized.

【0024】 本発明で、粉砕溶液の小じわの隠ぺい性を
評価する方法としては、製品を実際に使用してもらい目
視判定する方法が最も好ましいが、簡易的には、粉砕溶
液をシャーレ等の透明容器に約1〜2mm厚に一定に塗布
し、これに可視領域の波長を有するレーザー光を照射
し、レーザー光の直進性の妨害状態より、乱屈折の状態
を評価することができる。例えば、B/Aの値が0.8
の外観透明の粉砕溶液を用いた場合、レーザー光は粉砕
溶液により乱屈折され、明瞭な像を結ばなくなるのに対
し、B/Aの値が0の場合では、粉砕溶液を透過した後
も、明瞭な像を結ぶ。この状態を指標として評価する
と、実際の使用時に近い結果が得られる。
In the present invention, the method for evaluating the hiding property of fine wrinkles in the crushed solution is most preferably a method in which the product is actually used and visually judged. A container is coated with a uniform thickness of about 1 to 2 mm, and a laser beam having a wavelength in the visible region is irradiated on the container, and the state of irregular refraction can be evaluated from the state of obstruction of the straightness of the laser beam. For example, the value of B / A is 0.8
When a transparent pulverizing solution is used, the laser light is irregularly refracted by the pulverizing solution and does not form a clear image. On the other hand, when the B / A value is 0, even after passing through the pulverizing solution, Form a clear image. When this state is evaluated as an index, a result close to that in actual use can be obtained.

【0025】 一方、本発明の粉砕溶液をサンスクリーン
剤等の紫外線防御を目的とした化粧料に使用する場合で
は、B/Aの値としては、0〜0.4の範囲にあること
が好ましい。シリコーン樹脂粉体は一般に紫外線に対し
て透明である(紫外線を透過する)ため、この樹脂構造
の内部へ紫外線が透過し、高SPF値や高PA値を目的
とする化粧料の場合には、その性能が低下してしまうこ
とが多い。これに対して、樹脂構造が完全に崩れている
場合では、微粒子酸化チタンや有機系紫外線吸収剤等の
紫外線防御成分が充分な効果を発揮できる。
On the other hand, in case of using the cosmetic for the purpose of ultraviolet protective such as sunscreens pulverized solution of the present invention, as the value of B / A, it is preferably in the range of 0-0.4 . Since silicone resin powder is generally transparent to ultraviolet rays (transmits ultraviolet rays), ultraviolet rays penetrate into the inside of this resin structure, and in the case of cosmetics aiming for high SPF value and high PA value, Its performance often deteriorates. On the other hand, when the resin structure is completely broken, the ultraviolet protection components such as fine particle titanium oxide and organic ultraviolet absorber can exert a sufficient effect.

【0026】 本発明の化粧料では、上記の粉砕溶液を化
粧料100重量部中に0.5〜99重量部配合すること
が好ましく、さらに好ましくは1〜30重量部である。
この範囲内では、粉砕により良分散されたシリコーン
脂粉体の各種特性を充分に発揮することが可能である。
In the cosmetic of the present invention, it is preferable to add 0.5 to 99 parts by weight of the above pulverized solution to 100 parts by weight of the cosmetic, and more preferably 1 to 30 parts by weight.
Within this range, it is possible to sufficiently exhibit various characteristics of the silicone resin powder that is well dispersed by pulverization.

【0027】 本発明の化粧料では、上記の各成分以外
に、通常化粧料に用いられる粉体類、油剤、樹脂、界面
活性剤、紫外線吸収剤、香料、防腐剤、殺菌剤、保湿
剤、粘剤、生理活性成分、溶剤、塩類、水、酸化防止
剤、キレート剤、中和剤、pH調整剤等を同時に配合する
ことができる。
In the cosmetic of the present invention, in addition to the above-mentioned components, powders, oils, resins, surfactants, ultraviolet absorbers, fragrances, preservatives, bactericides, moisturizers, which are usually used in cosmetics, A viscous agent, a physiologically active ingredient, a solvent, salts, water, an antioxidant, a chelating agent, a neutralizing agent, a pH adjusting agent and the like can be added at the same time.

【0028】 粉体の例としては、赤色104号、赤色2
01号、黄色4号、青色1号、黒色401号等の色素、
黄色4号Alレーキ、黄色203号Baレーキ等のレー
キ色素、ナイロンパウダー、シルクパウダー、ウレタン
パウダー、テフロンパウダー、シリコーンパウダー、セ
ルロースパウダー等の高分子、黄酸化鉄、赤色酸化鉄、
黒酸化鉄、酸化クロム、カーボンブラック、群青、紺青
等の有色顔料、酸化亜鉛、酸化チタン、酸化セリウム等
の白色顔料、タルク、マイカ、セリサイト、カオリン等
の体質顔料、雲母チタン等のパール顔料、硫酸バリウ
ム、炭酸カルシウム、炭酸マグネシウム、珪酸アルミニ
ウム、珪酸マグネシウム等の金属塩、シリカ、アルミナ
等の無機粉体、微粒子酸化チタン、微粒子酸化亜鉛、微
粒子酸化鉄、チタニアゾル、アルミナ処理微粒子酸化チ
タン、シリカ処理微粒子酸化チタン、ベントナイト、ス
メクタイト、炭化珪素等が挙げられる。これらの粉体の
形状(板状、球状、針状、棒状、不定形状等)、凝集状
態および一次粒子径の大きさ(1nm〜100μmの範
囲が好ましい)に特に制限はない。
[0028] Examples of powder, 104 Red No. red 2
No. 01, yellow No. 4, blue No. 1, black No. 401, etc.
Rake pigments such as yellow No. 4 Al lake and yellow No. 203 Ba lake, polymers such as nylon powder, silk powder, urethane powder, Teflon powder, silicone powder, cellulose powder, yellow iron oxide, red iron oxide,
Colored pigments such as black iron oxide, chromium oxide, carbon black, ultramarine blue and dark blue, white pigments such as zinc oxide, titanium oxide and cerium oxide, body pigments such as talc, mica, sericite and kaolin, and pearl pigments such as titanium mica. , Barium sulfate, calcium carbonate, magnesium carbonate, aluminum silicate, magnesium silicate and other metal salts, silica, alumina and other inorganic powders, fine particles of titanium oxide, fine particles of zinc oxide, fine particles of iron oxide, titania sol, fine particles of alumina treated titanium oxide, silica Examples include treated fine particles of titanium oxide, bentonite, smectite, silicon carbide and the like. There is no particular limitation on the shape of these powders (plate-like, spherical, needle-like, rod-like, irregular shape, etc.), the agglomerated state and the size of the primary particle diameter (preferably in the range of 1 nm to 100 μm).

【0029】 これらの粉体は、従来公知の表面処理、例
えばフッ素化合物処理、シリコーン処理、ペンダント処
理、シランカップリング剤処理、チタンカップリング剤
処理、油剤処理、N−アシル化リジン処理、ポリアクリ
ル酸処理、金属石鹸処理、アミノ酸処理、無機化合物処
理、プラズマ処理、メカノケミカル処理、アミノ酸処理
等によって事前に表面処理されていてもいなくても構わ
ない。
[0029] These powders are conventionally known surface treatment such as fluorine compound treatment, silicone treatment, pendant treatment, silane coupling agent treatment, titanium coupling agent treatment, oil treatment, N- acylated lysine treatment, polyacrylic It may or may not be surface-treated in advance by acid treatment, metal soap treatment, amino acid treatment, inorganic compound treatment, plasma treatment, mechanochemical treatment, amino acid treatment and the like.

【0030】 フッ素化合物処理の例としては、パーフル
オロアルキルリン酸エステルやその塩、パーフルオロア
ルキルシラン、テフロン、パーフルオロアルキルカルボ
ン酸を用いた表面処理や金属石鹸処理、プラズマによる
表面フッ素化処理、テフロンとのメカノケミカル複合化
処理等が挙げられる。
[0030] Examples of the fluorine compound treatment, perfluoroalkyl phosphoric acid esters and salts thereof, perfluoroalkyl silanes, Teflon, perfluoroalkyl carboxylic acid surface treatment, metal soap treatment using the surface fluorination treatment by plasma, Examples include mechanochemical composite treatment with Teflon.

【0031】 油剤の例としては、前記油剤と同様のもの
が挙げられる。また、シリコーン系油剤としても前記と
同様のものが使用可能である。さらに、パーフルオロポ
リエーテル、フッ化ピッチ、フルオロカーボン、フルオ
ロアルコール、フルオロアルキル・ポリエーテル共変性
シリコーン等のフッ素化合物、トリメチルシロキシケイ
酸、フルオロアルキル基含有シリコーン樹脂、シリコー
ンゲル、シリコーンRTVゴムなどのシリコーン化合物
も使用可能である。
[0031] Examples of oil include those similar to the aforementioned oil. Further, the same silicone-based oil agent as described above can be used. Further, fluorine compounds such as perfluoropolyether, fluorinated pitch, fluorocarbon, fluoroalcohol, fluoroalkyl / polyether co-modified silicone, trimethylsiloxysilicic acid, fluoroalkyl group-containing silicone resin, silicone gel, silicone RTV rubber and other silicones. Compounds can also be used.

【0032】 界面活性剤としては、例えばアニオン界面
活性剤、カチオン界面活性剤、ノニオン界面活性剤、両
性界面活性剤を用いることができる。
As the surface active agent, for example, an anionic surface active agent, a cationic surface active agent, a nonionic surface active agent, or an amphoteric surface active agent can be used.

【0033】 有機系紫外線防御剤としては、例えばパラ
メトキシケイ皮酸2−エチルヘキシル、パラジメチルア
ミノ安息香酸2−エチルヘキシル、2−ヒドロキシ−4
−メトキシベンゾフェノン、2−ヒドロキシ−4−メト
キシベンゾフェノン−5−硫酸、2,2’−ジヒドロキ
シ−4−メトキシベンゾフェノン、p−メトキシハイド
ロケイ皮酸 ジエタノールアミン塩、パラアミノ安息香
酸(以下、PABAと略す)、エチルジヒドロキシプロ
ピルPABA、グリセリルPABA、サリチル酸ホモメ
ンチル、メチル−O−アミノベンゾエート、2−エチル
ヘキシル−2−シアノ−3,3−ジフェニルアクリレー
ト、オクチルジメチルPABA、メトキシケイ皮酸オク
チル、サリチル酸オクチル、2−フェニル−ベンズイミ
ダゾール−5−硫酸、サリチル酸トリエタノールアミ
ン、3−(4−メチルベンジリデン)カンフル、2,4
−ジヒドロキシベンゾフェニン、2,2’,4,4’−
テトラヒドロキシベンゾフェノン、2,2’−ジヒドロ
キシ−4,4’−ジメトキシベンゾフェノン、2−ヒド
ロキシ−4−N−オクトキシベンゾフェノン、4−イソ
プロピル ジベンゾイルメタン、ブチルメトキシジベン
ゾイルメタン、4−(3,4−ジメトキシフェニルメチ
レン)−2,5−ジオキソ−1−イミダゾリジンプロピ
オン酸−2−エチルヘキシル等が挙げられる。また、無
機系紫外線防御剤としては、例えば微粒子酸化チタン、
微粒子酸化亜鉛、微粒子酸化鉄、微粒子酸化セリウム、
鉄ドーピング酸化チタンやこれらを複合化したもの等が
ある。
Examples of the organic ultraviolet protective agent, for example 2-ethylhexyl p-methoxycinnamate, p-dimethylaminobenzoic acid 2-ethylhexyl, 2-hydroxy-4
-Methoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfuric acid, 2,2'-dihydroxy-4-methoxybenzophenone, p-methoxyhydrocinnamic acid diethanolamine salt, para-aminobenzoic acid (hereinafter abbreviated as PABA), Ethyldihydroxypropyl PABA, glyceryl PABA, homomenthyl salicylate, methyl-O-aminobenzoate, 2-ethylhexyl-2-cyano-3,3-diphenylacrylate, octyldimethyl PABA, octyl methoxycinnamate, octyl salicylate, 2-phenyl-. Benzimidazole-5-sulfuric acid, triethanolamine salicylate, 3- (4-methylbenzylidene) camphor, 2,4
-Dihydroxybenzophenine, 2,2 ', 4,4'-
Tetrahydroxybenzophenone, 2,2'-dihydroxy-4,4'-dimethoxybenzophenone, 2-hydroxy-4-N-octoxybenzophenone, 4-isopropyldibenzoylmethane, butylmethoxydibenzoylmethane, 4- (3,4 -Dimethoxyphenylmethylene) -2,5-dioxo-1-imidazolidine-2-ethylhexyl propionate and the like. Further, as the inorganic ultraviolet protective agent, for example, fine particle titanium oxide,
Fine particle zinc oxide, fine particle iron oxide, fine particle cerium oxide,
There are iron-doped titanium oxide and composites of these.

【0034】 粘剤の例としては、ジェランガム、ポリカ
ルボン酸、ポリアクリル酸、ポリビニルアルコール、寒
天、ジェランガム、アラビアガム、トラガントガム、カ
ラヤガム、キサンタンガム、タマリンドガム、グアーガ
ム、アルギン酸、カルボキシビニルポリマー等が挙げら
れる。
[0034] Examples of Nebazai is gellan gum, polycarboxylic acid, polyacrylic acid, polyvinyl alcohol, agar, gellan gum, gum arabic, tragacanth gum, karaya gum, xanthan gum, tamarind gum, guar gum, alginic acid, carboxyvinyl polymers and the like .

【0035】 生理活性成分の例としては、抗炎症剤、チ
ロシナーゼ活性阻害剤、植物抽出エキス、ビタミン類、
硫黄、尿素、血行促進剤等が挙げられる。
[0035] Examples of the physiologically active ingredient, an anti-inflammatory agent, tyrosinase activity inhibitor, plant extracts, vitamins,
Examples include sulfur, urea, blood circulation promoters, and the like.

【0036】 塩類の例としては、塩化ナトリウム、塩化
カリウム、塩化カルシウム、乳酸カルシウム、塩化アル
ミニウム、各種リン酸塩等が挙げられる。
[0036] Examples of salts are sodium chloride, potassium chloride, calcium chloride, calcium lactate, aluminum chloride, various phosphates and the like.

【0037】 溶剤の例としては、エタノール、メタノー
ル、イソプロピルアルコール、LPG、エーテル、ヘキ
サン、N−メチルピロリドン、イソプレングリコール、
環状シリコーン、低分子直鎖状シリコーン、軽質流動イ
ソパラフィン等が挙げられる。
[0037] Examples of the solvent include ethanol, methanol, isopropyl alcohol, LPG, ether, hexane, N- methylpyrrolidone, isoprene glycol,
Cyclic silicones, low molecular weight linear silicones, light liquid isoparaffins and the like can be mentioned.

【0038】本発明の化粧料の例としては、例えば油性
ファンデーション、乳化ファンデーション、水使用ファ
ンデーション、両用ファンデーション、白粉、頬紅、プ
レストパウダー、チークカラー、アンダーカバー、口
紅、リップコート、アイシャドウ、アイライナー、ネイ
ルカラー、化粧下地、乳液、ローション、クリーム、エ
ッセンス、サンスクリーン剤、ハンドローション、コン
ディショナー、シャンプー、ドライシャンプー、リン
ス、ヘアリキッド、ヘアトリートメント、キューティク
ルコート剤、セット剤、香水、デオドラント剤、クレン
ジング料、洗顔ソープ、石鹸等が挙げられる。
Examples of the cosmetics of the present invention include oily foundations, emulsified foundations, water-use foundations, dual-use foundations, white powder, blushers, pressed powders, cheek colors, undercovers, lipsticks, lip coats, eye shadows, eye liners. , Nail color, makeup base, emulsion, lotion, cream, essence, sunscreen, hand lotion, conditioner, shampoo, dry shampoo, conditioner, hair liquid, hair treatment, cuticle coat agent, setting agent, perfume, deodorant agent, cleansing agent And soap, face wash, and the like.

【0039】[0039]

【実施例】以下、実施例および比較例によって本発明を
詳細に説明する。なお、配合量は重量%である。
The present invention will be described in detail below with reference to Examples and Comparative Examples. The blending amount is% by weight.

【0040】 また、実施例および比較例で用いた化粧料
の各種特性に対する評価方法を以下に示す。
The evaluation methods for various properties of the cosmetics used in the examples and comparative examples are shown below.

【0041】 (1)官能特性試験 塗布時の感触(なめらかさ)、塗布後の仕上がり(しっ
とり感)を専門検査員10名によって調べ、表1の基準
で評価した。
[0041] (1) organoleptic properties test applied at the time of the feeling (smoothness), examined by professional inspectors ten finish (moist feeling) after application, was evaluated by the criteria in Table 1.

【0042】 (2)化粧効果(メイクのノリ) 専門検査員10名が洗顔後、本発明の化粧料を右半顔だ
けに塗布し、ついで顔全体にメイクアップ料を施し左右
の化粧効果を比較し、表1の基準で評価した。
[0042] (2) cosmetic effect after the (make-up of nori) professional inspector 10 people washing the face, the cosmetic was applied only to the right half face of the present invention, then the cosmetic effect of the left and right subjected to make-up fee to the entire face The results were compared and evaluated according to the criteria shown in Table 1.

【0043】 (3)化粧効果持続性 上記化粧料の評価後、2時間経過した時点での左右の顔
の化粧効果を比較し、表1の基準で評価した。
[0043] (3) After evaluation of the cosmetic effect lasting the cosmetics, to compare the cosmetic effect of the left and right of the face at the time of the lapse of 2 hours, was assessed by criteria in Table 1.

【0044】 (4)小じわ隠し効果 化粧料塗布後の小じわの隠ぺい性を専門検査員10名に
よって調べ、表1の基準で評価した。
[0044] (4) fine lines Hidden effect cosmetic after application of the concealment of the fine lines examined by a professional inspector 10 people, was evaluated by the criteria in Table 1.

【0045】 (5)粉砕溶液のレーザー直進性 粉砕溶液をアプリケーターにより、ガラス板上に2mm厚
に塗布し、塗布面に垂直に赤色レーザーを照射し、ガラ
ス板を突き抜けた光の状態を紙にあてて観察した。像が
明瞭でない場合を乱屈折あり、像が明瞭な場合を乱屈折
なしと評価した。
The [0045] (5) applicator laser straightness grinding solution pulverized solution was applied to a 2mm thick on a glass plate, a red laser was irradiated perpendicularly to the coating surface, the state of the light penetrates the glass plate on paper I observed it. When the image was not clear, it was evaluated as irregular refraction, and when the image was clear, it was evaluated as no irregular refraction.

【0046】 前記各種特性(1〜4)の評価基準を、表
1に示す。
[0046] The evaluation criteria for the various characteristics (1-4), shown in Table 1.

【0047】[0047]

【表1】 [Table 1]

【0048】実施例1〜4、比較例1〜4(乳液) 表2および3に示す処方にて乳液を調製した。シリコー
樹脂粉体としては、東レ・ダウコーニング・シリコー
ン製の「トレフィル505C」タイプ(一次粒子形状:
球状)を使用し、また粉砕溶液としては、下記の粉砕方
法により得られた試料(粉体25重量%配合)を使用し
た。
[0048] Examples 1-4 were prepared emulsion at formulations shown in Comparative Examples 1 to 4 (emulsion) Table 2 and 3. Silicone
As the resin powder, Toray Dow Corning Silicone "Trefil 505C" type (primary particle shape:
The sample obtained by the following pulverization method (containing 25% by weight of powder) was used as the pulverization solution.

【0049】 (調製方法:実施例) 表2中の成分1〜7を約80℃にて均一に混合し(溶液
1)、また表中の成分8〜12および14を約80℃に
て均一に溶解した(溶液2)。次に、溶液2をホモミキ
サーで撹拌しながら、溶液1を添加して乳化し、その冷
却過程の70℃で成分13を添加した後、室温まで冷却
し撹拌を停止した。
[0049] (Preparation method: Example) Table Components 1 to 7 in 2 were uniformly mixed at about 80 ° C. (solution 1), also uniform components 8-12 and 14 of Table at about 80 ° C. (Solution 2). Next, while stirring Solution 2 with a homomixer, Solution 1 was added to emulsify, Component 13 was added at 70 ° C. during the cooling process, and then the mixture was cooled to room temperature and stirring was stopped.

【0050】[0050]

【表2】 [Table 2]

【0051】(粉砕方法) トレフィル505Cタイプ12.5重量部に75重量部
の環状シリコーン(D5)を加え、粗撹拌した後、奈良
機械工業製湿式超微粉砕装置「マイクロス」にて粉砕
(900rpm,10分間)を行った。次いで、この溶
液にトレフィル505Cタイプ12.5重量部を加え、
粗撹拌した後、同様に粉砕を行い、粉砕溶液を得た(B
/A=0.8)。なお、レーザー光の直進性評価より、
この粉砕溶液は乱屈折を起こしていることが判った。
[0051] (grinding method) Trefil 505C type 12.5 parts by weight of cyclic silicone (D5) 75 parts by weight was added and after coarse stirred, pulverized by Nara Machinery Industry Co. wet micronization device "microspheres" ( 900 rpm, 10 minutes). Next, 12.5 parts by weight of trefil 505C type was added to this solution,
After roughly stirring, pulverization was performed in the same manner to obtain a pulverized solution (B
/A=0.8). In addition, from the evaluation of the straightness of the laser light,
It was found that this pulverized solution had irregular refraction.

【0052】 (調製方法:比較例) 表3中の成分1〜8を約80℃にて均一に混合溶解し
(溶液1)、また表中の成分9〜13および15を約8
0℃にて均一に溶解した(溶液2)。次に、上記溶液2
をホモミキサーで撹拌しながら、溶液1を添加して乳化
し、その冷却過程の70℃で成分14を添加した後、室
温まで冷却し撹拌を停止した。
[0052] (Preparation method: Comparative Example) Table components in 3 1-8 were uniformly mixed and dissolved at about 80 ° C. (solution 1), also the components 9 to 13 and 15 in Table about 8
It dissolved uniformly at 0 ° C. (solution 2). Next, the above solution 2
While stirring with a homomixer, Solution 1 was added to emulsify, component 14 was added at 70 ° C. during the cooling process, and then the mixture was cooled to room temperature and stirring was stopped.

【0053】[0053]

【表3】 [Table 3]

【0054】得られた乳液の特性を表2および表3に併
せて示す。この表に示されるように、実施例1〜4の官
能特性試験、化粧効果および化粧効果持続性、そして小
じわの隠ぺい性はいずれも良好であったが、粉砕溶液を
用いていない比較例1〜4は官能特性試験、化粧効果お
よび化粧効果持続性、小じわの隠ぺい性はいずれも不良
であった。
[0054] The characteristics of the obtained emulsion are shown together in Table 2 and Table 3. As shown in this table, the sensory property test of Examples 1 to 4, the cosmetic effect and the durability of the cosmetic effect, and the hiding property of fine wrinkles were all good, but Comparative Examples 1 to 1 in which the grinding solution was not used. No. 4 was poor in the organoleptic property test, the cosmetic effect, the durability of the cosmetic effect, and the hiding property of fine wrinkles.

【0055】 かかる実施例より明かなように、本発明の
化粧料は官能特性試験、化粧効果および化粧効果持続
性、そして小じわの隠ぺい性に優れていた。
As is clear from the above examples, the cosmetics of the present invention were excellent in sensory property test, cosmetic effect and cosmetic effect lasting property, and hiding property of fine wrinkles.

【0056】 実施例5〜8、比較例5〜8(クリーム) 表4、5に示す処方にて、クリームを調製した。シリコ
ーン樹脂粉体としては、東芝シリコーン製「トスパール
145A」タイプ(一次粒子形状:真球状)を使用し、
また粉砕溶液としては、下記の粉砕方法により得られた
試料(粉体25重量%配合)を使用した。
[0056] Examples 5-8, in the formulations shown in Comparative Examples 5 to 8 (cream) Table 4,5, was prepared cream. Silico
As the resin powder, Toshiba Silicone "Tospearl 145A" type (primary particle shape: spherical) is used.
A sample (compounded with 25% by weight of powder) obtained by the following pulverizing method was used as the pulverizing solution.

【0057】 (粉砕方法) トスパール145Aタイプ25重量部に75重量部の環
状シリコーン(D5)を加え、粗撹拌した後、湿式超微
粉砕装置「マイクロス」にて粉砕(1500rpm,1
0分間)を行い、粉砕溶液を得た(B/A=0.8)。
なお、レーザー光の直進性評価より、この粉砕溶液は乱
屈折を起こしていることが判った。
[0057] The (grinding method) Tospearl 145A type 25 parts by weight 75 parts by weight of the cyclic silicone (D5) was added and after coarse stirred, milled wet micronization device by "microspheres" (1500 rpm, 1
It was carried out for 0 minutes) to obtain a ground solution (B / A = 0.8).
From the evaluation of the straightness of the laser beam, it was found that this pulverized solution had irregular refraction.

【0058】 (調製方法:実施例) 表4中の成分1〜8を約80℃にて均一に混合し(溶液
1)、また表中の成分9〜12および14を約80℃に
て均一に溶解した(溶液2)。次に、溶液2をホモミキ
サーで撹拌しながら、溶液1を添加して乳化し、その冷
却過程の70℃で成分13を添加した後、室温まで冷却
し撹拌を停止した。
[0058] (Preparation method: Example) Table components 1-8 in 4 were uniformly mixed at about 80 ° C. (solution 1), also uniform components 9 to 12 and 14 in the table at about 80 ° C. (Solution 2). Next, while stirring Solution 2 with a homomixer, Solution 1 was added to emulsify, Component 13 was added at 70 ° C. during the cooling process, and then the mixture was cooled to room temperature and stirring was stopped.

【0059】[0059]

【表4】 [Table 4]

【0060】(調製方法:比較例) 表5中の成分1〜8を約80℃にて均一に混合し(溶液
1)、また表中の成分9〜12および14を約80℃に
て均一に溶解した(溶液2)。次に、溶液2をホモミキ
サーで撹拌しながら、溶液1を添加して乳化し、その冷
却過程の70℃で成分13を添加した後、室温まで冷却
し撹拌を停止した。
[0060] (Preparation method: Comparative Example) Table components 1-8 in 5 were uniformly mixed at about 80 ° C. (solution 1), also uniform components 9 to 12 and 14 in the table at about 80 ° C. (Solution 2). Next, while stirring Solution 2 with a homomixer, Solution 1 was added to emulsify, Component 13 was added at 70 ° C. during the cooling process, and then the mixture was cooled to room temperature and stirring was stopped.

【0061】[0061]

【表5】 [Table 5]

【0062】得られたクリームの特性を表4、5に併せ
て示す。この表に示されるように、実施例5〜8の官能
特性試験、化粧効果および化粧効果持続性、小じわの隠
ぺい性はいずれも良好であったが、粉砕溶液を用いてい
ない比較例5〜8は官能特性試験、化粧効果、化粧効果
持続性および小じわの隠ぺい性のいずれもやや不良であ
った。
[0062] The properties of the resulting cream are also shown in Tables 4 and 5. As shown in this table, the sensory property test of Examples 5 to 8, the cosmetic effect and the durability of the cosmetic effect, and the hiding property of fine wrinkles were all good, but Comparative Examples 5 to 8 using no grinding solution. The sensory characteristics test, the cosmetic effect, the lasting effect of the cosmetic effect and the hiding property of fine wrinkles were all poor.

【0063】 かかる実施例より明かなように、本発明の
化粧料は官能特性試験、化粧効果、化粧効果持続性およ
び小じわの隠ぺい性に優れていた。
As is clear from the above examples, the cosmetics of the present invention were excellent in the sensory property test, the cosmetic effect, the durability of the cosmetic effect and the hiding property of fine wrinkles.

【0064】 実施例9(美容液) 表6に示す処方にて、白濁様の美容液を調製した。シリ
コーン粉体としては、東レ・ダウコーニング・シリコー
ン製「トレフィル506C」(一次粒子形状:球状)を
使用し、また粉砕溶液としては、下記の粉砕方法により
得られた試料(粉体25重量%配合)を使用した。
[0064] in Example 9 (Essence) formulation shown in Table 6, to prepare a cloudy-like essence. Siri
As the corn powder, "Trefil 506C" (primary particle shape: spherical) made by Toray Dow Corning Silicone was used, and as the crushing solution, a sample obtained by the following crushing method (25% by weight powder was blended) )It was used.

【0065】 (粉砕方法) トレフィル506C25重量部に75重量部の環状シリ
コーン(D5)を加え、粗撹拌した後、湿式超微粉砕装
置「マイクロス」にて粉砕(2600rpm,30分)
を行い、粉砕溶液を得た(B/A=0.1)。また、レ
ーザー光の直進性評価より、この粉砕溶液は乱屈折を起
こしていないことが判った。
[0065] (grinding method) Trefil 506C25 parts by weight of cyclic silicone (D5) 75 parts by weight was added and after coarse stirred, pulverized by a wet micronization device "microspheres" (2600 rpm, 30 minutes)
Then, a pulverized solution was obtained (B / A = 0.1). Moreover, it was found from the evaluation of the straightness of the laser beam that this pulverized solution did not cause irregular refraction.

【0066】 (調整方法) 表6中の油性成分1〜4を室温にて均一に混合溶解し
(溶液1)、また水性成分5〜9を室温にて均一に混合
溶解した(溶液2)。次に、溶液2をホモミキサーにて
撹拌しながら溶液1を添加した後、引き続いて5分間撹
拌して実施例9の美容液を得た。
[0066] The oily components 1-4 in (adjustment method) Table 6 were uniformly mixed and dissolved at room temperature (solution 1), also were uniformly mixed and dissolved aqueous component 5-9 at room temperature (solution 2). Next, Solution 1 was added while stirring Solution 2 with a homomixer, and subsequently stirred for 5 minutes to obtain a beauty essence of Example 9.

【0067】[0067]

【表6】 [Table 6]

【0068】この様にして得られた実施例9の美容液
は、官能特性試験、化粧効果、化粧効果持続性のいずれ
も良好であった。
[0068] Essence of Example 9 obtained in this way, the functional characteristics test, cosmetic effect, were any of the cosmetic effect lasting good.

【0069】 実施例10(リップクリーム) 実施例1〜4にて使用した方法と同様にして、湿式超微
粉砕装置「マイクロス」を用いて粉砕(2600rp
m,40分間)した粉砕溶液(B/A=0)を用い、表
7に示す処方にてリップクリームを調製した。下記に官
能特性の評価結果を示す。なお、レーザー光の直進性評
価より、この粉砕溶液は乱屈折を起こしていないことが
判った。
[0069] In a manner similar to that used in Example 10 (Lip Cream) Examples 1-4, ground using a wet micronization device "microspheres" (2600Rp
A lip balm was prepared according to the formulation shown in Table 7 using the pulverized solution (B / A = 0) that was subjected to m, 40 minutes). The evaluation results of sensory characteristics are shown below. From the evaluation of the straightness of the laser beam, it was found that this pulverized solution did not cause irregular refraction.

【0070】[0070]

【表7】 [Table 7]

【0071】その結果、本実施例のリップクリームは、
塗布時に非常になめらかな感触であり、また塗布後は唇
にしっとりした感触を与える、きわめて良好な官能特性
を有していた。
[0071] As a result, lip cream of the present embodiment,
It had a very smooth organoleptic feel at the time of application and had a very good organoleptic property to give a moist feel to the lips after application.

【0072】 実施例11(ファンデーション) 表8に示す処方にて、ファンデーションを調製した。
リコーン樹脂粉体としては、「トレフィル505C」タ
イプを使用し、また粉砕溶液としては、下記の粉砕方法
により得られた試料(粉体45重量%配合)を使用し
た。
[0072] At formulation shown in Example 11 (Foundation) Table 8 were prepared foundation. Shi
As the silicone resin powder, "Trefil 505C" type was used, and as the grinding solution, a sample (powder 45% by weight powder) obtained by the following grinding method was used.

【0073】 (粉砕方法) トレフィル505Cタイプ45重量部に53重量部のジ
メチルポリシロキサン(6cSt)およびポリエーテル
変性シリコーン2重量部を加え、粗撹拌した後、湿式超
微粉砕装置「マイクロス」にて粉砕(1000rpm,
10分)を行い、粉砕溶液を得た(B/A=0.8)。
なお、レーザー光の直進性評価より、この粉砕溶液は乱
屈折を起こしていることが判った。
[0073] (grinding method) Trefil 505C type 45 parts by weight of dimethyl polysiloxane (6 cSt) and polyether-modified silicone 2 parts by weight of 53 parts by weight was added and after crude stirred, wet micronization device to "microspheres" And crush (1000 rpm,
After 10 minutes), a pulverized solution was obtained (B / A = 0.8).
From the evaluation of the straightness of the laser beam, it was found that this pulverized solution had irregular refraction.

【0074】 (調製方法) 各成分をミキサーを用いて混合した後、アトマイザーに
て粉砕した。次いで、金型を用いて金皿に打型して製品
を得た。
[0074] (Preparation method) After mixing the components using a mixer, and pulverized with an atomizer. Then, the product was obtained by stamping on a metal plate using a mold.

【0075】[0075]

【表8】 [Table 8]

【0076】本実施例のファンデーションを専門パネラ
ー10名により実際に評価したところ、感触、化粧効果
持続性および小じわの隠ぺい性は表9に示す結果となっ
た。
When the foundation of this example was actually evaluated by 10 expert panelists, the results shown in Table 9 were the feeling, the durability of the cosmetic effect and the hiding property of fine wrinkles.

【0077】[0077]

【表9】 [Table 9]

【0078】表9の結果より、本実施例のファンデーシ
ョンは、感触、化粧効果持続性および小じわの隠ぺい性
に優れていることが判った。
From the results shown in Table 9, it was found that the foundation of this example was excellent in touch, durability of cosmetic effect and hiding of fine wrinkles.

【0079】 実施例11(サンスクリーン剤) 表10に示す処方にて、サンスクリーン剤を調製した。
シリコーン樹脂粉体としては、「トレフィル505C」
タイプを使用し、また粉砕溶液としては、下記の粉砕方
法により得られた試料を使用した。
[0079] At formulation shown in Example 11 (sunscreens) Table 10 were prepared sunscreens.
As a silicone resin powder, "Trefyl 505C"
As the grinding solution, the sample obtained by the following grinding method was used.

【0080】 (粉砕方法) トレフィル505Cタイプ30重量部とアルキルアルコ
キシシラン処理超微粒子酸化チタン(平均一次粒子径3
0nm)10重量部に環状シリコーン(D4,D5の
1:1重量比混合溶液)55重量部およびポリエーテル
変性シリコーン5重量部を加え、粗撹拌した後、湿式超
微粉砕装置「マイクロス」にて粉砕(1800rpm,
60分)を行い、粉砕溶液を得た(B/A=0)。
[0080] (grinding method) Trefil 505C type 30 parts by weight and the alkyl alkoxy silane treated ultrafine titanium oxide (average primary particle diameter of 3
(0 nm) 10 parts by weight, 55 parts by weight of cyclic silicone (mixed solution of D4 and D5 in a 1: 1 ratio by weight) and 5 parts by weight of polyether-modified silicone were added, and after coarse stirring, they were added to a wet ultrafine pulverizer "Micros". And crush (1800 rpm,
After 60 minutes), a pulverized solution was obtained (B / A = 0).

【0081】[0081]

【表10】 [Table 10]

【0082】(調製方法) 各成分を粗混合した後、ダイノミルを用いて粉砕を行
い、得られた溶液をステンレスボールと共にボトルに充
填して製品とした。
[0082] (Preparation method) After coarse mixing the ingredients, and milling by using a Dyno-mill, and the resulting solution was a product filled into the bottle with a stainless ball.

【0083】 本実施例のサンスクリーン剤を専門パネラ
ー10名により実際に評価したところ、感触、化粧効果
持続性および紫外線防御効果は表11に示す結果となっ
た。なお、紫外線防御効果は日本化粧品工業連合会通達
(平成4年1月1日付)のSPF測定法に基づき、ソー
ラーシュミレーター(ソーラーライト社製、3D−60
0型)を用いて実施した。実験条件は、パネラーの背部
皮膚10×10cm面に、試料2mg/cm2を塗布した。
When the sunscreen agent of this example was actually evaluated by 10 expert panelists, the feel, the durability of the cosmetic effect and the ultraviolet protection effect were as shown in Table 11. The ultraviolet protection effect is based on the SPF measurement method of the Japan Cosmetic Industry Federation Notification (January 1, 1992), based on the solar simulator (3D-60, manufactured by Solar Light Co., Ltd.).
0 type). As the experimental conditions, the sample 2 mg / cm 2 was applied to the back skin of the panelist 10 × 10 cm.

【0084】[0084]

【表11】 [Table 11]

【0085】表11の結果より、本実施例のサンスクリ
ーン剤は、感触、化粧効果持続性および紫外線防御効果
に優れていることが判った。
From the results shown in Table 11, it was found that the sunscreen agent of this example was excellent in touch, durability of cosmetic effect and ultraviolet protection effect.

【0086】 比較例9 トレフィル506Cタイプ80重量部に環状シリコーン
(D5)20重量部を加え、マイクロスを用いて粉砕を
行ったが、液化しないため、試験を中止した。
[0086] Comparative Example 9 Trefil 506C type 80 parts by weight cyclic silicone (D5) 20 parts by weight were added, were subjected to grinding with microspheres, because it does not liquefied, the test was stopped.

【0087】[0087]

【発明の効果】以上のことから、本発明は、感触、化粧
効果持続性および小じわの隠ぺい性に優れた化粧料を提
供することは明かである。
From the above, it is clear that the present invention provides a cosmetic composition which is excellent in touch, durability of cosmetic effect and hiding of fine wrinkles.

Claims (5)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 粉砕する混合液100重量部に対し、平
均一次粒子径が0.1〜30μmのシリコーン樹脂粉体
(但し、ナイロン樹脂粉体をシリコーン化合物で被覆し
た樹脂粉体は除く)5〜75重量部が、環状シリコー
ン、揮発性直鎖状シリコーンから選ばれるシリコーン油
を含む油剤中で粉砕して得られた粉砕溶液を配合した化
粧料。
1. A silicone resin powder having an average primary particle diameter of 0.1 to 30 μm with respect to 100 parts by weight of a mixed liquid to be ground.
(However, if nylon resin powder is coated with a silicone compound,
Were excluded resin powder) 5 to 75 parts by weight, cyclic silicones, cosmetics containing the pulverized solution obtained by trituration with oil containing a silicone oil selected from volatile linear silicone.
【請求項2】 シリコーン樹脂粉体の一次構造が崩れて
いる状態に粉砕した粉砕溶液を配合した請求項1に記載
の化粧料。
2. The cosmetic material according to claim 1, wherein a pulverized solution pulverized in a state where the primary structure of the silicone resin powder is broken is blended.
【請求項3】 粉砕前のシリコーン樹脂粉体の一次粒子
形状が球状であり、かつその平均一次粒子径(A)に対
して、粉砕後の該シリコーン樹脂粉体の平均一次粒子径
(B)の割合(B)/(A)が、0.3〜0.9である
粉砕溶液を配合した請求項1または2に記載の化粧料。
3. The primary particle shape of the silicone resin powder before pulverization is spherical, and the average primary particle diameter (B) of the silicone resin powder after pulverization is relative to the average primary particle diameter (A) thereof. The cosmetic according to claim 1 or 2, wherein a pulverized solution having a ratio (B) / (A) of 0.3 to 0.9 is blended.
【請求項4】 粉砕前のシリコーン樹脂粉体の一次粒子
形状が球状であり、その平均一次粒子径(A)に対し
て、粉砕後の該シリコーン樹脂粉体の平均一次粒子径
(B)の割合(B)/(A)が、0〜0.4である粉砕
溶液を配合した請求項1または2に記載の化粧料。
4. The primary particle shape of the silicone resin powder before pulverization is spherical, and the average primary particle diameter (A) of the average primary particle diameter (B) of the silicone resin powder after pulverization is The cosmetic according to claim 1 or 2, wherein a pulverized solution having a ratio (B) / (A) of 0 to 0.4 is blended.
【請求項5】 粉砕前のシリコーン樹脂粉体の一次粒子
形状が球状であり、かつその平均一次粒子径(A)に対
して、粉砕後のシリコーン樹脂粉体の平均一次粒子径
(B)の割合(B)/(A)が、0〜0.4である粉砕
溶液と、有機系または無機系の紫外線防御成分を配合し
た請求項1または2に記載の化粧料。
5. The primary particle shape of the silicone resin powder before pulverization is spherical, and the average primary particle diameter (B) of the silicone resin powder after pulverization is smaller than that of the average primary particle diameter (A). The cosmetic composition according to claim 1 or 2, wherein a pulverized solution having a ratio (B) / (A) of 0 to 0.4 and an organic or inorganic ultraviolet protection component are blended.
JP05250896A 1995-07-05 1996-02-14 Cosmetics Expired - Lifetime JP3468971B2 (en)