JP3466388B2 - Copolyester and its molded product - Google Patents

Description

Detailed Description of the Invention

[0001]

TECHNICAL FIELD The present invention relates to a copolyester, a method for producing the same, a method for producing a molded article using the copolymer polyester, and a molded article obtained thereby. More specifically, the present invention has a high melt viscosity, yet exhibits a non-Newtonian property that is a low viscosity at a high shear rate and a high viscosity at a low shear rate, and causes melt fracture such as sharkskin flow during molding. The present invention relates to a copolyester having excellent properties that a crystallization rate is suppressed and a gelled product does not occur, a method for producing the copolyester, and a molded article made of the copolyester. Therefore, when a molded product is manufactured by extrusion blow molding or other melt molding methods, it has excellent transparency, appearance, touch, etc., and mechanical properties such as impact resistance, mechanical properties, heat resistance, and moisture resistance. It is possible to smoothly produce a high-quality molded product having excellent properties and chemical resistance. The copolyester of the invention is particularly suitable for extrusion blow molding.

[0002]

2. Description of the Related Art Polyester resins such as polyethylene terephthalate are excellent in various properties such as transparency, mechanical properties, gas barrier property and flavor barrier property, and also residual monomers and harmful additions when formed into molded products. Since there is little worry about the agent and it has excellent hygiene and safety, juice, soft drink,
It has become widely used in recent years as a hollow container for filling seasonings, oils, cosmetics, detergents and other products.

As a typical molding method for manufacturing a hollow molded article such as a container from plastic, (1) a melted plasticized resin is extruded as a cylindrical parison through a die orifice, and the parison is in a softened state. An extrusion blow molding method in which a fluid such as air is blown inside by sandwiching it with a mold; and (2) a molten resin is injected into the mold to once mold a sealed parison (preform), and then There are two methods, an injection blow molding method, in which is injected into a blow mold and a fluid such as air is blown to perform molding.

Of the above-mentioned molding methods, the former extrusion blow molding method is simpler in process than the latter injection blow molding method, and does not require a high-level technique for producing and molding a mold. In addition, the equipment cost and die manufacturing cost are low, making it suitable for high-mix low-volume production. Moreover, the extrusion blow molding method has an advantage that it is possible to manufacture a molded product having a complicated shape including a fine product, a deep product, a large product, a handle, and the like.

From this point of view, various attempts have been made in the past to perform extrusion blow molding using a general-purpose polyester resin such as polyethylene terephthalate or polybutylene terephthalate. However, a general-purpose polyester resin generally has a low melt viscosity, Therefore, when extrusion blow molding is attempted, it is difficult for the parison after extrusion to drastically draw down and be shaped. Moreover, there is a problem that crystallization is likely to occur at the time of blowing after extrusion, transparency is impaired, and improper shaping occurs. And the above-mentioned inconvenience resulting from such low melt viscosity and easy crystallization in a general-purpose polyester resin such as polyethylene terephthalate is usually 30 cm or more in length required for manufacturing a large hollow molded article. It is particularly remarkable in extrusion blow molding for extruding a long parison. Therefore, it is practically extremely difficult to obtain a molded product having a uniform shape and size by extrusion blow molding and having excellent transparency, particularly a large hollow molded product, using a general-purpose polyester resin such as polyethylene terephthalate. is there.

Therefore, for the above reasons, vinyl chloride resins and polyolefins have conventionally been mainly used in extrusion blow molding because they have a high melt viscosity and do not cause remarkable drawdown of the parison extruded in the molten state. Came. However, extrusion blow-molded products manufactured using vinyl chloride resin have problems in hygiene and safety due to the elution of harmful additives such as plasticizers and metal stabilizers. There is a problem that it produces toxic gas when incinerated, and its use tends to decrease mainly in Europe. In addition, when extrusion blow molding is performed using a polyolefin such as polyethylene, there is a drawback in that white turbidity due to crystals is generated in the molded product and the transparency and appearance of the molded product are likely to be poor.

Therefore, various proposals have been made so far regarding a polyester resin suitable for extrusion blow molding. As such a conventional technique, a dicarboxylic acid or its ester-forming component and a diol component are reacted to produce a polyester. , A method for producing a copolyester for use in extrusion blow molding using a diol component containing an ethylene oxide adduct of bisphenol A (JP-A-4-59822, JP-A-5-65338, and JP-A-5-33522). 125
165 and JP-A-5-186579); When a polyester is produced by reacting a dicarboxylic acid or its ester-forming component with a diol component, cyclohexanedimethanol or the like is used as a diol component to form a copolymerized polyester. Manufacturing method (Comparative example of JP-A-5-65338 and JP-A-7-20
No. 7003); A method for producing a branched polyester using terephthalic acid, ethylene glycol, 1,4-cyclohexanedimethanol and a small amount of a polyfunctional branching compound (see US Defense Publication No. T954,005); Along with dicarboxylic acid components such as acids and their ester-forming derivatives and diol components such as ethylene glycol, general-purpose polyfunctional components such as trimethylolpropane, pentaerythritol and trimellitic acid, and chain terminators such as benzoic acid and stearic acid. A method for producing a copolyester for extrusion blow molding using the same (see JP-A-54-137095); by reacting a dicarboxylic acid component such as terephthalic acid or an ester-forming derivative thereof with a diol component such as ethylene glycol. Esterification reaction or After a low polymer is produced by a stell exchange reaction, it is reacted with a general-purpose crosslinking agent such as trimethylolpropane, pentaerythritol, and trimellitic acid to carry out a polymerization reaction to form a prepolymer, and the prepolymer is solidified. A method for producing a copolyester for extrusion blow molding by phase polymerization (JP-A-54-163962 and JP-A-55-927).
No. 30); a method for producing a copolyester for extrusion blow molding by using a branching agent such as terephthalic acid, isophthalic acid, pentaerythritol and an end capping agent such as m-anisic acid (JP-A-61-1). No. 181823); and the like are known.

In the above-mentioned and conventional methods, the melting point of the copolyester is lowered by the copolymerization of the ethylene oxide adduct of bisphenol A and cyclohexanedimethanol, whereby the melt extrusion temperature becomes lower than the conventional temperature. To be able to set
The melt viscosity during extrusion blow molding can be increased. However, even in that case, the melt viscosity is not high enough to perform extrusion blow molding, so that a remarkable drawdown occurs in the parison after extrusion, making it difficult to shape, and the extrusion blow molding is performed smoothly. I can't do it. Further, as an adverse effect of molding at low temperature, minute surface roughness occurs in an extrusion blow-molded product such as a bottle, and the appearance and feel of the molded product are likely to be impaired. In addition, the copolyester obtained by the above-mentioned and conventional methods are often unable to perform solid-phase polymerization due to its low melting point, and even when solid-state polymerization can be performed, the solid-state polymerization rate is extremely slow. Since the degree of polymerization does not increase sufficiently, it is difficult to increase the melt viscosity, and molded articles obtained from the copolyester have poor transparency and uneven thickness.

Further, in the above-mentioned conventional method, 1,4-cyclohexanedimethanol is used in an amount of 1 relative to all diol units.
Since a high proportion of 0 to 40 mol% is used for copolymerization, low temperature molding is possible due to amorphization or a decrease in melting point as in the conventional method, and a conventional method due to a branched structure of a polyfunctional branching agent compound. The melt viscosity of the polyester tends to be higher than that of the copolyester obtained in and. However, the conventional method does not mention solid-state polymerization at all. And, the copolyester obtained by the conventional method is a so-called "amorphous" polymer, or even if it is crystalline, its melting point is too low, so that solid-phase polymerization is impossible or solid-phase polymerization is possible. Even if the polymerization is possible, the melting point is too low when solid phase polymerization is carried out, sticking between chips and pellets occurs, or the polymerization rate is too low,
The molecular weight cannot be made high enough. Therefore, the melt viscosity of the copolyester obtained there is not high enough to perform extrusion blow molding, and as a result, remarkable drawdown of the parison after extrusion occurs and shaping becomes difficult, and extrusion blow molding is performed smoothly. I can't do it. Further, also in the conventional method, as in the above-mentioned and the prior arts, as an adverse effect of molding at a low temperature, minute surface roughness occurs in an extrusion blow-molded product such as a bottle, and the appearance and feel of the molded product are easily impaired. In addition, if the copolyester is dried at a high temperature before molding, it will have to stick at a low temperature because the sticking between chips and pellets will occur, so it is necessary to dry for a long time with a large-scale device such as a vacuum drying facility. , Productivity is reduced. Further, in the case of an amorphous polymer, sticking between chips and pellets is likely to occur in the lower portion of the hopper of the extruder, which causes a problem that extrusion cannot be performed.

Further, the polyester obtained by the above-mentioned conventional method in which a cross-linking agent composed of a polyfunctional compound and a chain stopper such as benzoic acid or stearic acid are used in combination has a melt viscosity higher than that of an ethylene terephthalate homopolymer. Although the melt strength is increased, the crystallization rate is higher than that of the ethylene terephthalate homopolymer, so spherulites are generated during parison extrusion, and the resulting extruded blow-molded product shows significant whitening and transparency. Will be lacking. When a large parison of 30 cm or more is extruded to produce a large hollow molded product by extrusion blow molding, the lower part of the parison is solidified by crystallization, and the pinch-off part at the bottom of the container such as a bottle causes poor adhesion. Become.
In addition, as in the cases of the above-mentioned conventional methods, minute surface roughness is generated in the molded product, and the appearance and feel of the molded product are likely to be remarkably poor. Further, in terms of the productivity of the copolyester, since the crystallinity rapidly increases during solid phase polymerization, the diffusion of ethylene glycol in the polymer necessary for increasing the polymerization rate is hindered, It is difficult to smoothly produce the desired copolyester. Further, the copolyester obtained by this conventional method has an extremely high degree of crystallinity, so that unmelted spots frequently occur in the extrusion step in extrusion blow molding, and it is difficult to produce a good molded product. Then, the above-mentioned various drawbacks are particularly remarkable in a state where the resin extrusion speed is high as in the case of manufacturing a large-sized hollow molded article.

Further, the copolymerized polyester obtained by the above-mentioned conventional method has a higher crystallization rate than the ethylene terephthalate homopolymer, like the copolymerized polyester obtained by the above-mentioned conventional method, and therefore the parison extrusion is performed. Occasionally, spherulites are formed, and the resulting extrusion blow-molded product or the like becomes significantly whitened or lacks transparency. Further, in the production of a large hollow molded product accompanied by the extrusion of a long parison having a length of 30 cm or more, the lower part of the parison is solidified by crystallization, and the pinch-off portion at the bottom of the hollow molded product such as a bottle causes poor adhesion. . Furthermore, since the cross-linking degree of the copolyester cannot be properly controlled by not using the end-capping agent composed of a monofunctional compound, a gel-like substance derived from the over-crosslinked structure is generated because of the over-crosslinked state. As a result, spots such as spots appear on the molded product and the appearance of the molded product is impaired. further,
Also in the case of this conventional method, as in the case of the above-mentioned conventional methods, the surface roughness of the molded product is slightly generated, and the appearance and feel of the molded product are apt to be remarkably poor. And, the above-mentioned Japanese Patent Laid-Open No. 54-54 cited as the prior art.
-163962 and JP-A-55-92730 describe that a small amount of isophthalic acid, neopentyl glycol or the like can be copolymerized, in which case the crystallization rate of the copolymerized polyester is suppressed. Although the early solidification of the bottom part of the parison and the whitening of the hollow molded article during the production of the hollow molded article are reduced to some extent, the occurrence of gel-like substances derived from the overcrosslinked structure and the surface roughness of the molded article are still present. It remains unsolved.

Further, in the above-mentioned conventional method, the melt viscosity and the shear sensitivity of the melt viscosity are increased by copolymerizing a branching agent such as pentaerythritol and an end capping agent such as m-anisic acid and further performing solid phase polymerization. It is said that a copolyester with a small amount of gels derived from the over-crosslinked structure can be obtained, and the copolymerization of isophthalic acid as a bifunctional component suppresses the crystallization rate of the copolyester to produce a hollow molded article. The crystallization rate of the copolyester at the bottom of the parison is suppressed at this time, and the solidification of the bottom of the parison and the whitening of the hollow molded product during the production of the hollow molded article tend to be reduced to some extent. However, when producing a large hollow molded product with extrusion of a long parison of 30 cm or more using a conventional polyester copolymer,
There is a drawback in that the bottom of the hollow molded article is whitened due to crystallization at the bottom of the previously extruded parison. And
Also in the case of this conventional method, as in the case of the above-mentioned conventional methods, minute surface roughness occurs in the molded product, and its appearance and touch are likely to be remarkably poor. Especially 3
When the extrusion amount per unit time is 20 kg or more, such as when manufacturing a large hollow molded product accompanied by extrusion of a long parison of 0 cm or more, minute surface roughness of the molded product becomes remarkable, and In addition, unmelted seeds are likely to occur in the molded product due to the difficulty of melting the crystal.

Moreover, none of the copolyesters obtained by the above-mentioned conventional methods and the molded articles made from them have sufficiently high mechanical properties such as drop impact strength. In the case of a hollow molded product such as a bottle, its drop impact strength needs to be 1 m or more, but the bottle was manufactured by extrusion blow molding using the copolymerized polyester obtained by the above-mentioned conventional methods. However, in both cases, the drop impact strength was less than 1 m, which caused a problem in practical use. In particular, a bottle having an internal volume of 1 liter or more has a large breaking energy and is easily broken. Bottles obtained by the conventional method of copolyester are particularly inferior in drop impact strength, and it is speculated that this is because the mechanical properties and mechanical properties of the copolyester are reduced by copolymerizing isophthalic acid. .
In addition to the above-mentioned prior arts, the present inventors have tried to produce polyethylene terephthalate having a high degree of polymerization by solid phase polymerization, but the solid phase polymerization rate is extremely slow, and extrusion blow molding is performed. It has been found that polyethylene terephthalate having a sufficiently high degree of polymerization and melt viscosity, which is suitable for, for example, cannot be efficiently obtained in a short time, and is not practical in terms of productivity.

[0014]

SUMMARY OF THE INVENTION Therefore, the object of the present invention is to solve the above-mentioned various problems, and (1) when the melt viscosity is sufficiently high, the composition is extruded when used for extrusion blow molding. It is possible to shape the hollow molded product smoothly without drawdown of the parison; (2) Slow crystallization speed, no formation of spherulites during extrusion of the parison, and molding of the obtained extrusion blow molded product. (3) In the production of large hollow molded products that extrude long parisons of 30 cm or more, solidification does not occur due to crystallization of the lower part of the parison and molding of bottles etc. Adhesion failure at the pinch-off part at the bottom of the product does not occur; (4) Various types of molded products with no microscopic surface roughness and excellent appearance and feel can be obtained; Also Ku has less occurrence of gels, spots such as fish eyes does not occur in the molded product,
A molded product having excellent transparency and good appearance can be obtained; (6) the resulting molded product has excellent impact resistance; and (7) high solid-state polymerization rate and excellent productivity. , Which are excellent in melt moldability, especially extrusion blow moldability, and have excellent shape stability, dimensional accuracy, appearance, touch, transparency, etc. It is to provide a polyester that can be manufactured. And an object of the present invention is to provide a method capable of producing a polyester having the above-mentioned various excellent properties in a short time with high productivity. Further, an object of the present invention is to provide a method for producing a molded product by performing melt molding, particularly extrusion blow molding, using the polyester having the above-mentioned various properties, and a molded product by the method.

[0015]

[Means for Solving the Problems] Under the above-mentioned circumstances, the above-mentioned high functionality of polyester resin is used in the more and more developing applications, especially in the extrusion blow molding application for producing large hollow moldings. Focusing attention, various studies have been conducted on a copolyester based on a polyethylene terephthalate polymer, and as a result, a dicarboxylic acid component consisting of terephthalic acid and a diol component consisting of ethylene glycol and a small amount of an ethylene oxide adduct of bisphenol A. After the esterification reaction, to produce a prepolymer by performing a polymerization reaction in a molten state, by solid-phase polymerization of the prepolymer, it becomes possible to increase the degree of polymerization of polyester in a short time, The melt viscosity of polyester during extrusion blow molding can be increased and Sex, hollow molded articles excellent in such has been found to give the appearance (see JP-A-6-99476 and JP-A No. 7-258396).

The inventors of the present invention further conducted research based on the above findings, and found that in a polyester mainly composed of a terephthalic acid unit and an ethylene glycol unit, a polyester other than a terephthalic acid unit and an ethylene glycol unit was added to the polyester. Containing a specific diol unit having a benzene nucleus in a specific ratio, and containing a polyfunctional compound unit composed of a polyfunctional compound having three or more functional groups and a monofunctional compound unit derived from a monofunctional compound in specific ratios. When the polymerization degree is increased by solid-state polymerization, the copolyester obtained thereby is disclosed in the above-mentioned JP-A-6-99476 and JP-A-7-2.
Similar to the invention according to Japanese Patent No. 58396, a high degree of polymerization can be achieved in a short time, and a low viscosity at a high shear rate and a high viscosity at a low shear rate are exhibited. It can be carried out more smoothly than the inventions described in JP-A-6-99476 and JP-A-7-258396, and in particular, a large hollow molded article accompanied by extrusion of a long parison of 30 cm or more is produced by extrusion blow molding. Has good moldability suitable for
It has been found that the melt viscosity is sufficiently high, the drawdown of the extruded parison does not occur, and a hollow molded article excellent in transparency, color tone, appearance and touch can be smoothly shaped.

Moreover, the above-mentioned copolyesters developed by the present inventors have a slow crystallization rate, and do not form spherulites during extrusion of the parison during extrusion blow molding.
The obtained blow-molded product has no whitening and is excellent in transparency, and further, when producing a large hollow-molded product involving extrusion of a parison having a length of 30 cm or more, solidification due to crystallization of the lower part of the parison does not occur. It was also found that the pinch-off portion at the bottom of molded articles such as bottles did not cause defective adhesion. Further, the above-mentioned copolyester developed by the present inventors, shows appropriate shear stress at the time of melt molding, therefore the molded product obtained by the melt molding has a good appearance and texture without surface roughness, Further, they have found that the degree of cross-linking is well adjusted, no gel is generated due to over-crosslinking, the transparency is excellent, and the mechanical strength is excellent. Further, the present inventors have found that the copolyester has a high solid phase polymerization rate and can be economically produced with good productivity, and completed the invention based on these various findings.

That is, the present invention provides (1) a copolyester mainly composed of a dicarboxylic acid unit composed of a terephthalic acid unit and a diol unit composed of an ethylene glycol unit, and having another copolymerized unit; The copolymerized polyester of, as another copolymerized unit, (i) (a) represented by the following general formula (I);

[0019]

[Chemical 5]

[Wherein A is a group represented by the formula: --CH ₂ CH ₂ --or formula: --CH (CH ₃ ) CH _2- , B is a divalent hydrocarbon group, a carbonyl group, a sulfonyl group, oxygen Atom or direct bond (-), R ¹ and R ² are each an inert substituent, j and k are each independently an integer of 0 to 8, and s and t are each independently an integer of 0 to 4. ] The diol unit (I) shown by these; and (b) The following general formula (II);

[0021]

[Chemical 6]

[Wherein A is a group represented by the formula: --CH ₂ CH ₂ --or formula: --CH (CH ₃ ) CH _2- , R ³ is an inert substituent, and m and n are each independently. An integer of 0 to 8 and u represents an integer of 0 to 4] at least one bifunctional compound unit selected from the diol units (II); Based on at least one of polyfunctional compounds having 3 or more of carboxyl groups, hydroxyl groups and / or their ester-forming groups. Having functional compound units (III) in a proportion of 0.005 to 1 mol% based on the total number of moles of all structural units of the copolyester; and (iii) monocarboxylic acids, monoalcohols and their ester forming properties. Derivative Without even one monofunctional monofunctional compound units derived from the compound (IV) based on the total moles of all the structural units of the copolyester formula (alpha);

[0023]

[Equation 3]

[In the formula, [III] is the proportion (mol%) of the polyfunctional compound unit (III) in the copolyester, [I]
V] is a monofunctional compound unit (I
V) (mole%), p represents the average number of functional groups of the polyfunctional compound that induces the polyfunctional compound unit (III)}. is there. The present invention also provides a method for producing a copolyester mainly comprising a dicarboxylic acid unit composed of a terephthalic acid unit and a diol unit composed of an ethylene glycol unit, and having another copolymerized unit; [1] terephthalic acid or the It mainly comprises a dicarboxylic acid component consisting of an ester-forming derivative and a diol component consisting of ethylene glycol, and in addition to the above-mentioned main dicarboxylic acid component and diol component, (a) the following general formula (V);

[0025]

[Chemical 7]

[Wherein A is a group represented by the formula: --CH ₂ CH ₂ --or formula: --CH (CH ₃ ) CH _2- , B is a divalent hydrocarbon group, a carbonyl group, a sulfonyl group, oxygen Atom or direct bond (-), R ¹ and R ² are each an inert substituent, j and k are each independently an integer of 0 to 8, and s and t are each independently an integer of 0 to 4. ] A diol (V) represented by the following general formula (VI);

[0027]

[Chemical 8]

[In the formula, A is a group represented by the formula: --CH ₂ CH ₂ --or formula: --CH (CH ₃ ) CH _2- , R ³ is an inert substituent, and m and n are each independently. An integer of 0 to 8 and u represents an integer of 0 to 4] and at least one bifunctional compound selected from the following: a diol (VI); and an ester-forming derivative thereof; (b) a carboxyl group, At least one polyfunctional compound having three or more hydroxyl groups and / or their ester-forming groups; and (c) at least one monofunctional compound of a monocarboxylic acid, a monoalcohol and their ester-forming derivatives; And (d) the content of the bifunctional compound in the reaction raw material is diol unit (I) derived from the bifunctional compound and / or dio The amount of the unit (II) is 0.5 to 7 mol% based on the total number of moles of all structural units of the copolyester; (e) the content of the polyfunctional compound in the reaction raw material. The amount of the polyfunctional compound unit (III) derived from the polyfunctional compound is 0.005 to 1 mol% based on the total number of moles of all structural units of the copolyester; (F) The content of the monofunctional compound in the reaction raw material is such that the proportion of the monofunctional compound unit (IV) derived from the monofunctional compound is based on the total number of moles of all structural units of the copolyester, Formula (α) below;

[0029]

[Equation 4]

[In the formula, [III] is the ratio (mol%) of the polyfunctional compound unit (III) in the copolyester, [I]
V] is a monofunctional compound unit (I
V) ratio (mol%), p represents the average number of functional groups of the polyfunctional compound that induces the polyfunctional compound unit (III)}, and the reaction raw materials are esterified or esterified. After an exchange reaction, it is melt-polymerized to form a polyester prepolymer; and then [2] the polyester prepolymer obtained in the above step [1] is solid-phase polymerized; The present invention relates to a method for producing polyester.

Further, the present invention is a molded article made of the above-mentioned copolymerized polyester, particularly an extrusion blow molded article. Then, the present invention is a method for producing a molded article by performing extrusion blow molding using the above-mentioned copolymerized polyester.

[0032]

BEST MODE FOR CARRYING OUT THE INVENTION The present invention described above will be described in detail. As described above, the copolyester of the present invention needs to be a copolyester mainly composed of a terephthalic acid unit and an ethylene glycol unit and having another copolymer unit. In the copolymerized polyester of the present invention, the total proportion (mol%) of the terephthalic acid unit and the ethylene glycol unit is calculated from the total number of moles of all structural units constituting the copolymerized polyester (that is, 100 mol%), and the diol unit described below is obtained. (I) and / or diol unit (II), and polyfunctional compound unit (III)
And the value of the monofunctional compound unit (IV). Generally, the total proportion (mol%) of terephthalic acid units and ethylene glycol units in the copolymerized polyester of the present invention is about 70 to 98 mol% based on the total number of moles of all structural units constituting the copolymerized polyester. Is preferred, and more preferably about 90-98 mol%. If the total proportion of terephthalic acid units and ethylene glycol units in the copolyester is less than 70 mol%, the copolyester becomes amorphous and it becomes difficult to achieve a high degree of polymerization by solid phase polymerization, while 98 mol% When it exceeds the above range, the crystals of the copolyester become difficult to melt, and unmelted spots are likely to occur frequently in the molded product, which is not preferable.

The copolyester of the present invention is
In addition to the terephthalic acid unit and the ethylene glycol unit, at least one bifunctional compound selected from the diol unit (I) represented by the general formula (I) and the diol unit (II) represented by the general formula (II). The compound unit is adjusted to 0 ..% based on the total number of moles of all structural units of the copolyester.
It is necessary to have the ratio of 5 to 7 mol%. When the bifunctional compound unit is, for example, an isophthalic acid unit, a hydroxybenzoic acid unit, or the like, minute surface roughness occurs in an extrusion blow-molded product such as a bottle, and the appearance and feel of the molded product are significantly impaired. Particularly, in the production of a molded product such as a large bottle having an extrusion rate of 20 kg / hour or more, the surface roughness becomes remarkable, and the impact resistance of the molded product becomes poor.

In the copolymerized polyester of the present invention, in the diol unit (I) and / or the diol unit (II), the group A is a group (ethylene group) represented by the formula: --CH ₂ CH _2- , or a formula:- a group represented by (1,2-propylene _{group) - CH (CH 3) CH} 2. In the copolyester of the present invention, in the diol unit (I) and / or the diol unit (II) contained therein, even if all the groups A are ethylene groups, all the groups A are 1,2-
Even if it is a propylene group, a part of the group A may be an ethylene group and the remaining group A may be a 1,2-propylene group. Among them, the diol unit (I) in the copolyester is
It is preferable that the group A in the diol unit (II) and / or ethylene group is an ethylene group from the viewpoint of easiness of production of the copolyester and production cost.

The group B in the diol unit (I)
Is a divalent hydrocarbon group, a carbonyl group, a sulfonyl group,
It is an oxygen atom or a direct bond (-). When the group B is a divalent hydrocarbon group, an alkylene group having 1 to 8 carbon atoms,
It is preferably an alkylidene group or a divalent aromatic group, and specific examples thereof include methylene group, dichloromethylene group, ethylene group, ethylidene group, propylene group, propylidene group, trimethylene group, isopropylidene group, butylidene group. , Ethylethylene group, tetramethylene group, 1
-Methylpropylidene group, 1,2-dimethylethylene group, pentylidene group, 1-methylbutylidene group, pentamethylene group, 1-ethyl-2-methylethylene group, 1,
3-dimethyltrimethylene group, 1-ethylpropylidene group, trimethylethylene group, isopropylmethylene group,
1-methylbutylidene group, 2,2-dimethylpropylidene group, hexamethylene group, 1-ethylbutylidene group,
1,2-diethylethylene group, 1,3-dimethylbutylidene group, ethyltrimethylethylene group, heptamethylene group, octamethylene group, 1,1-cyclopentylidene group, 1,1-cyclohexylidene group, 1, Examples thereof include a 1-cycloheptylidene group, a 1,1-cyclooctylidene group, a benzylidene group, and a 1-phenylethylidene group.

In the copolyester of the present invention, all the groups B in the diol unit (I) present in the copolyester may be the same or different. Among them, in the copolyester of the present invention,
It is preferable that the group B in the diol unit (I) is an isopropylidene group, a sulfonyl group and / or a 1,1-cyclohexylidene group, because the thermal stability of the copolymerized polyester when melted is good.

In the copolyester of the present invention, j, k, m and n in the diol unit (I) and / or the diol unit (II) are each independently an integer of 0-8, and therefore j, k, m and n may be the same number or different numbers. Of which
J, k, m and n are independent of each other from the viewpoint of easy production of the copolyester, thermal stability of the copolyester at the time of melting, and good color tone of the molded product using the copolyester. It is preferably 1 or 2, and more preferably j, k, m and n are each 1.

In the diol unit (I) and / or diol unit (II) of the copolyester of the present invention,
The benzene nucleus may be substituted with an inert substituent (R ^{1 to} R ³ ), in which case the inert substituents R ¹ , R ² and R
³ is preferably a lower alkyl group such as a methyl group, an ethyl group and a propyl group; and a halogen atom such as chlorine, bromine and iodine. Further, s, t and u representing the number of inactive substituents in the diol unit (I) and / or the diol unit (II) are each preferably 0 to 2, and more preferably 0.

The diol unit (I) constituting the copolyester of the present invention may be any of the above-mentioned diol units, but a preferable example of the diol unit (I) is 2,2-bis [4]. -(2-hydroxyethoxy) phenyl] propane, 2- {4- [2- (2-hydroxyethoxy) ethoxy] phenyl} -2- [4 '
-(2-hydroxyethoxy) phenyl] propane,
2,2-bis {4- [2- (2-hydroxyethoxy)]
Ethoxy] phenyl} propane, bis [4- (2-hydroxyethoxy) phenyl] sulfone, {4- [2-
(2-Hydroxyethoxy) ethoxy] phenyl}-
[4 ′-(2-hydroxyethoxy) phenyl] sulfone, bis {4- [2- (2-hydroxyethoxy) ethoxy] phenyl} sulfone, 1,1-bis [4- (2-
Hydroxyethoxy) phenyl] cyclohexane, 1-
{4- [2- (2-Hydroxyethoxy) ethoxy] phenyl} -1- [4 '-(2-hydroxyethoxy) phenyl] cyclohexane, 1,1-bis {4- [2-
Named are diol units derived from (2-hydroxyethoxy) ethoxy] phenyl} cyclohexane, 2,2-bis [4- (2-hydroxyethoxy) -2,3,5,6-tetrabromophenyl] propane and the like. You can Among the diol units derived from the above compounds, the diol unit (I) is 2,2-bis [4- (2
-Hydroxyethoxy) phenyl] propane unit or bis [4- (2-hydroxyethoxy) phenyl] sulfone unit facilitates the production of the copolyester and further enhances the melt stability of the copolyester. It is also possible to improve the color tone of the molded product produced using the copolyester.

Further, the diol unit (II) constituting the copolyester of the present invention may be any of the above-mentioned diol units, but a preferable example of the diol unit (II) is 1,4-bis. (2-hydroxyethoxy) benzene, 1- (2-hydroxyethoxy) -4
Examples thereof include diol units derived from-[2- (2-hydroxyethoxy) ethoxy] benzene and 1,4-bis [2- (2-hydroxyethoxy) ethoxy] benzene. Among the diol units derived from the above compounds, when the diol unit (II) is a 1,4-bis (2-hydroxyethoxy) benzene unit, the production of the copolyester becomes easy and the copolymerization The melt stability of polyester can be increased,
Further, it is possible to improve the color tone of the molded product manufactured using the copolyester.

The copolyester of the present invention has, as the diol unit (I) and / or the diol unit (II),
You may have only 1 type of the above-mentioned diol unit, or may have 2 or more types.

In the copolymerized polyester of the present invention, the ratio of diol units (I) and / or diol units (II) [two or more kinds of diol units (I) and / or
Or, when it has a diol unit (II), its total proportion] is required to be 0.5 to 7 mol% based on the total number of moles of all structural units of the copolyester, as described above. Is. If the proportion of the diol unit (I) and / or the diol unit (II) is less than 0.5 mol%, the crystallization rate of the copolyester becomes too fast, and whitening due to the formation of spherulites during melt molding occurs. In the production of a large hollow molded product that occurs due to crystallization, the transparency of the molded product is lost, and in addition, the lower part of the parison solidifies early due to crystallization, such as bottles. The pinch-off portion at the bottom of the molded product causes poor adhesion. Moreover, if the crystallinity is too high, unmelted spots are generated in the molded product during melt molding, resulting in a poor appearance.

On the other hand, when the proportion of the diol unit (I) and / or the diol unit (II) exceeds 7 mol%, the crystallinity and melting point of the copolyester become too low,
Even if solid-phase polymerization cannot be carried out, or even if solid-phase polymerization can be carried out, the solid-phase polymerization rate becomes extremely slow and the degree of polymerization does not increase sufficiently. Has poor mechanical strength.

The proportion of the diol unit (I) and / or the diol unit (II) in the copolyester can increase the productivity of the copolyester itself,
Moreover, the melt viscosity of the copolyester is sufficiently high to enable better melt molding such as extrusion blow molding, and there is no whitening, which is more excellent in transparency and mechanical strength. It is preferable that the amount is in the range of 1.5 to 5 mol% based on the total number of moles of all the structural units of the copolyester, from the viewpoint that it can be obtained.

By the way, a small amount of diethylene glycol units is contained in the copolymerized polyester produced as a by-product of diethylene glycol which is a dimer of ethylene glycol during the production of the copolymerized polyester of the present invention. When a large amount of diethylene glycol units is contained in the copolymer, the glass transition temperature of the copolyester is lowered, causing problems such as deterioration of heat resistance and coloring,
Molded articles such as bottles obtained from the copolyester have poor heat resistance, strength, color tone and the like, so it is preferable to reduce the proportion of diethylene glycol units in the copolyester as much as possible. For the reasons described above, it is preferable that the proportion of diethylene glycol units in the copolyester is less than 1.5 mol% based on the total number of moles of all structural units of the copolyester.
It is more preferable to keep it to 1.4 mol% or less, and 1.3
It is more preferable to keep it to be mol% or less.

The copolyester of the present invention contains a polyfunctional compound unit (III) derived from at least one polyfunctional compound having three or more carboxyl groups, hydroxyl groups and / or ester forming groups thereof. Based on the total number of moles of all structural units of the polymerized polyester, 0.
It is necessary to have a proportion of 005 to 1 mol% [the total proportion of two or more kinds of polyfunctional compound units (III)]. If the proportion of the polyfunctional compound unit (III) is less than 0.005 mol%, the melt viscosity will not be sufficiently high, and the appropriate melt viscosity, that is, non-Newtonian property will not occur, and the melt molding such as extrusion blow moldability will occur. Moldability becomes poor. In particular, when extrusion blow molding is performed, drawdown of the parison becomes severe and the parison is clogged or crushed, making it impossible to manufacture a hollow molded article having a good shape.
Moreover, the ratio of the polyfunctional compound unit (III) is 0.005.
If it is less than mol%, the solid-phase polymerization rate at the time of producing the copolyester becomes slow and the productivity of the copolyester decreases. On the other hand, when the proportion of the polyfunctional compound unit (III) exceeds 1 mol%, the cross-linked structure in the copolyester becomes too much and gel derived from the over-cross-linked structure is produced. Problems such as spots and whitening occur, and the transparency, appearance, and touch are impaired. Then, if the degree of polymerization of the copolyester is lowered so as not to cause gelation, the entanglement between molecules is reduced, and sufficient mechanical strength cannot be obtained. Moreover,
If the proportion of the polyfunctional compound unit (III) exceeds 1 mol%, the crystallization rate will be too high during the production of the molded product, spherulites will be formed and the molded product will be whitened and the transparency will be reduced. In addition, shaping is likely to be poor, and in extrusion blow molding, blow moldability due to crystallization of parison becomes poor.

The proportion of the polyfunctional compound unit (III) in the copolyester is such that the melt viscosity is sufficiently high and the melt molding such as extrusion blow molding can be more favorably carried out, and the whitening and poor shaping of the molded product. Can be smoothly prevented, a molded product having more excellent mechanical strength can be obtained, and the productivity of the copolyester itself can be further improved. It is preferably in the range of 0.01 to 0.5 mol% based on the total number of moles.

The polyfunctional compound unit (III) is derived from a polyfunctional compound having three or more one or more groups selected from a carboxyl group, a hydroxyl group and / or their ester-forming groups. It is not particularly limited as long as it is a unit, and the polyfunctional compound for deriving the polyfunctional compound unit (III) has three or more hydroxyl groups even if it is a polyfunctional compound having only three or more carboxyl groups. It may be a polyfunctional compound or a polyfunctional compound having a total of three or more carboxyl groups and hydroxyl groups.

Preferred examples of the polyfunctional compound unit (III) include trimesic acid, trimellitic acid, 1,2,3-
Benzenetricarboxylic acid, pyromellitic acid, 1,4
Aromatic polycarboxylic acids such as 5,8-naphthalene tetracarboxylic acid; Aromatic polyalcohols such as 1,3,5-trihydroxybenzene; Trimethylolpropane, pentaerythritol, glycerin, 1,3,5-Cyclohexanetriol An aliphatic or alicyclic polyalcohol; 4-hydroxyisophthalic acid, 3-hydroxyisophthalic acid, 2,3-dihydroxybenzoic acid, 2,4-dihydroxybenzoic acid, 2,5-dihydroxybenzoic acid,
Aromatic hydroxycarboxylic acids such as 2,6-dihydroxybenzoic acid, protocatechuic acid, gallic acid, and 2,4-dihydroxyphenylacetic acid; Aliphatic hydroxycarboxylic acids such as tartaric acid and malic acid; Derived from their ester-forming derivatives The polyfunctional compound unit can be mentioned. The copolyester of the present invention may have, as the polyfunctional compound unit (III), only one kind of the above-mentioned polyfunctional compound units or two or more kinds thereof.

Among the above, the copolymerized polyester of the present invention is a polyfunctional compound unit (III) which is a polyfunctional compound unit derived from trimellitic acid, pyromellitic acid, trimesic acid, trimethylolpropane and pentaerythritol. It is preferable to have one kind or two or more kinds of them from the viewpoint of easiness of manufacturing the copolyester and the manufacturing cost, and from the viewpoint of suppressing gelation,
A trimellitic acid unit and a trimesic acid unit are more preferable.

Further, the copolyester of the present invention is
Derived from at least one monofunctional compound of a monocarboxylic acid, a monoalcohol and their ester-forming derivatives together with the above-mentioned diol unit (I) and / or diol unit (II) and polyfunctional compound unit (III). It is necessary to have a monofunctional compound unit (IV). In the copolyester of the present invention, the monofunctional compound unit (IV) functions as a terminal capping compound unit, and caps a molecular chain end group and / or a branched chain end group in the copolyester to form a copolyester. To prevent excessive crosslinking and gel formation. The monofunctional compound unit (IV) is not particularly limited as long as it is a unit derived from at least one of a monocarboxylic acid, a monoalcohol and an ester-forming derivative thereof.

Preferred examples of the monofunctional compound unit (IV) include benzoic acid, o-methoxybenzoic acid, m-methoxybenzoic acid, p-methoxybenzoic acid, o-methylbenzoic acid, m-methylbenzoic acid, p. -Methylbenzoic acid, 2,3
-Dimethylbenzoic acid, 2,4-dimethylbenzoic acid, 2,
5-dimethylbenzoic acid, 2,6-dimethylbenzoic acid,
3,4-Dimethylbenzoic acid, 3,5-Dimethylbenzoic acid, 2,4,6-Trimethylbenzoic acid, 2,4,6-Trimethoxybenzoic acid, 3,4,5-Trimethoxybenzoic acid, 1-Naphthoic acid , 2-naphthoic acid, 2-biphenylcarboxylic acid, 1-naphthaleneacetic acid, 2-naphthaleneacetic acid and other aromatic monocarboxylic acids; n-octanoic acid, n-nonanoic acid, myristic acid, pentadecanoic acid, stearic acid,
Aliphatic monocarboxylic acids such as oleic acid, linoleic acid and linoleic acid; ester-forming derivatives of the above monocarboxylic acids; benzyl alcohol, 2,5-dimethylbenzyl alcohol, 2-phenethyl alcohol, phenol,
Aromatic monoalcohols such as 1-naphthol and 2-naphthol; pentadecyl alcohol, stearyl alcohol, polyethylene glycol monoalkyl ether, polypropylene glycol monoalkyl ether, polytetramethylene glycol monoalkyl ether, oleyl alcohol, cyclododecanol and other fats Mention may be made of units derived from monofunctional compounds such as group or alicyclic monoalcohols. The copolyester of the present invention may have, as the monofunctional compound unit (IV), only one type of the above-mentioned monofunctional compound units or two or more types thereof.

Among them, the copolyester of the present invention is a monofunctional compound unit (IV) containing benzoic acid, 2,
It has a unit derived from one or more monofunctional compounds selected from 4,6-trimethoxybenzoic acid, 2-naphthoic acid, stearic acid and stearyl alcohol in the production of a copolyester. It is preferable in terms of easiness and manufacturing cost.

The copolyester of the present invention is
Based on the total number of moles of all structural units of the copolyester, the monofunctional compound unit (IV) is represented by the following formula (α);

[0055]

[Equation 5]

[In the formula, [III] is the ratio (mol%) of the polyfunctional compound unit (III) in the copolyester, [I]
V] is a monofunctional compound unit (I
V) ratio (mol%), p represents the average number of functional groups of the polyfunctional compound that induces the polyfunctional compound unit (III)} [when having two or more monofunctional compound units (IV)] Must have the total ratio].

In the above formula (α), the average number of functional groups p of the polyfunctional compound that induces the polyfunctional compound unit (III) is p.
Means an average value of the functional groups of all polyfunctional compounds used for forming the copolyester, for example, p = 3 when only trifunctional compounds are used as polyfunctional compounds,
As a polyfunctional compound, a trifunctional compound and a tetrafunctional compound are used.
When used in a molar ratio of 0:50, p = 3 × 0.5 + 4 ×
0.5 = 3.5, and when a trifunctional compound and a tetrafunctional compound are used as a polyfunctional compound in a molar ratio of 20:80, p = 3 × 0.2 + 4 × 0.8 = 3.8. Therefore, although not limited, for example, the polyfunctional compound unit (III) is a trifunctional compound unit derived from a trifunctional compound, and the content ratio of the polyfunctional compound unit (III) in the copolyester is In the case of 0.1 mol%, in the above formula (α), p = 3 and [III]
= 0.1 (mol%), so 2 (mol%) ≧ [IV]
≧ 0.01 (mol%), monofunctional compound unit (IV)
The preferred range of the content ratio of is 0.01 to 2 mol% based on the total number of moles of all structural units of the copolyester.

The proportion of the monofunctional compound unit (IV) in the copolyester is lower than the lower limit value of the above-mentioned formula (α), that is, {0.1 × (p-2) × [III]} (mol%). If the amount is too small, a gel will be formed due to over-crosslinking,
When a molded product is manufactured, problems such as spots and whitening may occur, resulting in poor appearance and loss of transparency. On the other hand, when the proportion of the monofunctional compound unit (IV) in the copolyester is larger than the upper limit value of the above formula (α), that is, {20 × (p−2) × [III]} (mol%), In some cases, the solid-phase polymerization rate at the time of producing the copolyester becomes slow and the productivity of the copolyester decreases. From the viewpoints of easiness of production of the copolyester, production cost, appearance of the molded article and transparency, the monofunctional compound unit (I
The ratio of V) is {10 × (p−2) × [III]} ≧ [IV]
The range of ≧ {0.5 × (p−2) × [III]} is preferable.

The copolymerized polyester of the present invention may contain a copolymerized unit other than the above-mentioned structural units as long as it is in a small amount (usually 3 mol% or less based on all the structural units) so as not to impair its physical properties. . Examples of the copolymerization unit include aromatic dicarboxylic acids such as isophthalic acid, phthalic acid, biphenyldicarboxylic acid, diphenyletherdicarboxylic acid, diphenylsulfonedicarboxylic acid, diphenylketonedicarboxylic acid, sodium sulfoisophthalate, and 2,6-naphthalenedicarboxylic acid. Acids; aliphatic dicarboxylic acids such as malonic acid, succinic acid, adipic acid, azelaic acid, sebacic acid; alicyclic dicarboxylic acids such as decalin dicarboxylic acid and cyclohexanedicarboxylic acid; trimethylene glycol,
Tetramethylene glycol, hexamethylene glycol, aliphatic diols, such as neopentyl glycol; more glycolic acid, hydroxy acrylic acid, hydroxypropionic acid, asiatic acid, Kinoba acid, hydroxybenzoic acid, mandelic acid, hydroxy etc. A Toro Rakuchin acid Carboxylic acid; structural units derived from aliphatic lactones such as ε-caprolactone can be mentioned.

The intrinsic viscosity of the copolyester of the present invention may vary depending on the type of melt-molding method of the copolyester, but when used in melt molding accompanied by melt extrusion, particularly in extrusion blow molding, It is preferably within the range of 1.0 to 1.5 dl / g, and particularly from the viewpoints of mechanical strength, appearance, moldability and productivity at the time of manufacturing a molded product, etc. of the obtained extrusion blow molded product. More preferably, it is within the range of 4 dl / g. In particular, in the case of extrusion blow molding, when the intrinsic viscosity of the copolyester is less than 0.8 dl / g, drawdown of the parison becomes large at the time of extrusion blow molding, and molding failure is likely to occur, and further Mechanical strength tends to decrease. On the other hand, in the case of performing molding accompanied by melt extrusion, particularly extrusion blow molding, when the intrinsic viscosity of the copolyester is larger than 1.5 dl / g, the melt viscosity becomes too high, and during melt extrusion, especially extrusion blow molding. Weld lines are likely to occur in the molded product during molding, the appearance of the resulting molded product is likely to be poor, and moreover, the torque is high during extrusion, which tends to cause unevenness in the extrusion amount and other molding problems. Become. Further, when the intrinsic viscosity of the copolyester is larger than 1.5 dl / g, the time required to extrude a predetermined amount of the copolyester becomes long and the productivity of the molded product tends to be lowered. The above-mentioned relationship between the intrinsic viscosity of the copolymerized polyester, the moldability of the copolymerized polyester, and the physical properties of the molded product obtained from the copolymerized polyester is particularly remarkable in extrusion blow molding, but not limited to extrusion blow molding, extrusion molding, Almost the same tendency occurs in melt molding involving melt extrusion such as injection / extrusion blow molding.

Further, the copolyester of the present invention is 2
The melt viscosity (η1) at a shear rate of 0.1 rad / sec at a temperature of 70 ° C. is preferably 5 × 10 ^{4 to} 5 × 10 ⁶ poises. When the melt viscosity (η1) of the copolyester satisfies the above conditions, curl back is particularly unlikely to occur during melt molding such as extrusion blow molding, and molding defects are almost completely eliminated. Can be prevented, and in addition, melt fracture (melt fracture) and die swell during melt extrusion can be prevented.
The phenomenon of 1) is remarkably suppressed, and a molded product having particularly excellent appearance and uniformity can be obtained.

Further, the copolyester of the present invention is 2
The melt viscosity (η2) at a shear rate of 100 rad / sec at a temperature of 70 ° C. is preferably 5 × 10 ^{3 to} 5 × 10 ⁵ poises, and the melt viscosity (η2) of the copolyester satisfies the above conditions. In the case of melt-molding such as extrusion blow molding, it is possible to smoothly prevent drawdown or sagging of the extruded product in the softened state such as parison, resulting in high productivity and copolymerization. It is possible to smoothly prevent the thermal decomposition of polyester, unevenness of extrusion at the time of extrusion, and generation of weld lines.

The copolyester of the present invention is
Shear rate 0.1 rad at the temperature of 270 ° C.
/ Viscosity (η1) requirements and melt viscosity at a shear rate of 100 rad / sec at a temperature of 270 ° C. (η
In addition to the requirement of 2), the melt viscosity (η1) and the melt viscosity (η2) are expressed by the following formula (β): −0.7 ≦ (1/3) log ₁₀ (η2 / η1) ≦ −0.2 (β It is more preferable that the following is satisfied. When the above formula (β) is satisfied, the copolyester exhibits moderate non-Newtonian properties and exhibits an appropriately low melt viscosity at a high shear rate and an appropriately high melt viscosity at a low shear rate. Therefore, especially when extrusion blow molding or injection / extrusion blow molding is performed, the formability of the parison becomes extremely good.

From the viewpoint of improving the parison forming property, (1/3) log in the above formula (β) is used.
More preferably, the value of ₁₀ (η2 / η1) is in the range of −0.60 to −0.25. In the above formula (β), (1/3) log ₁₀ (η2 / η1) is the melt viscosity (η1) and the melt viscosity in a natural logarithmic graph with the melt viscosity as the vertical axis and the shear rate as the horizontal axis. It is calculated as the slope of the straight line connecting the two points of viscosity (η2). The values of the melt viscosity (η1) and the melt viscosity (η2) referred to in the present specification refer to the values measured by the method described in the section of Examples below.

Further, the copolyester of the present invention is
The sharkskin critical shear stress (σss) at a temperature of 270 ° C. is 1 × 10 ⁶ dyne / cm ² or more, and the shear stress (σ100) at a shear rate of 100 / sec at a temperature of 270 ° C. is the sharkskin critical value. Shear stress (σs
It is preferably not more than the value of s). The present inventors have found that the shear stress of the copolyester during melt molding is also closely related to the above-mentioned surface roughness of the molded product obtained. The shark skin critical shear stress (σss) at 270 ° C. of the copolyester is 1 × 10 ⁶ dyne / c.
and m ² or more, and the shear stress at a shear rate of 100 / sec at a temperature of 270 ℃ (σ100) is less than the value of sharkskin critical shear stress (σss), when performing the melt molding such as extrusion blow molding In addition, it is possible to obtain a molded article in which the phenomenon of surface roughness is significantly suppressed and which is particularly excellent in appearance such as transparency and touch. It is presumed that this is because, in the case of the copolyester having the shear stress as described above, the remarkable release of the elastic normal stress between the copolyester melt and the extruder die is suppressed. . The sharkskin critical shear stress (σss) and the shear rate of the copolyester referred to here are 100 /
The shear stress in seconds (σ100) refers to the shear stress when extruded into a strand shape by using a capillary nozzle by a capillograph, and the details thereof are as described in the section of Examples below.

The copolymerized polyester of the present invention preferably has a glass transition temperature of 60 ° C. or higher, and from the viewpoint of preventing shrinkage of a molded article obtained by extrusion blow molding or other melt molding, Transition temperature is 70 ℃
The above is more preferable. When the glass transition temperature of the copolyester is less than 60 ° C., after the molded product, particularly the extrusion blow molded product, is taken out of the mold, the molded product is shrunk due to the relaxation of residual stress and the appearance of the molded product is impaired. Sometimes.

The copolyester of the present invention preferably has a terminal carboxyl group concentration of 30 μeq / g or less, which is effective in preventing melt stability of the polyester, prevention of coloration, and suppression of wall surface roughness of a hollow molded article in extrusion blow molding. From the viewpoint, the terminal carboxyl group concentration is more preferably 20 μeq / g or less. When the terminal carboxyl group concentration of the copolyester exceeds 30 μeq / g, molded products, particularly extrusion blow molded products, are markedly colored and the molecular weight is markedly lowered.

The copolyester of the present invention has a melt flow rate (temperature of 270 ° C.) from the viewpoints of moldability during melt molding such as extrusion blow molding, uniformity of the obtained molded product, and productivity during molding. Hereinafter, it may be abbreviated as "MFR"), preferably in the range of 0.3 to 7.5 g / 10 minutes, and more preferably in the range of 0.5 to 5 g / 10 minutes.

The copolyester of the present invention is
The crystallinity is preferably 20 to 40%. When the crystallinity of the copolyester is less than 20%, pellets or chips are likely to stick to each other during solid phase polymerization, which makes it difficult to carry out solid phase polymerization smoothly, resulting in lower productivity. Moreover, during molding, blocking occurs between pellets and chips of the copolyester, which makes it difficult to perform molding smoothly. On the other hand, the crystallinity of the copolyester is 4
If it exceeds 0%, the meltability of pellets and chips will be poor, resin squeal will occur during molding (sound is generated due to friction between pellets and chips), and a load on the molding machine due to torque increase will occur. Molding becomes difficult to be performed smoothly, and unmelted lumps are generated in a molded product, which easily causes defects such as transparency, appearance, and touch. In order to smoothly perform solid phase polymerization to enhance the productivity of the copolyester, and to smoothly perform melt molding to obtain a molded product of good quality, the crystallinity of the copolyester is 25 to More preferably, it is within the range of 35%.

The copolyester of the present invention preferably has a cold crystallization temperature of 150 ° C. or lower and a crystallization heat amount in the cold crystallization of 20 J / g or lower. When the cold crystallization temperature is higher than 150 ° C., or when the heat of crystallization during cold crystallization exceeds 20 J / g, the growth rate of spherulites is high, and whitening occurs in the obtained molded product. It tends to be inferior in transparency. Further, when extrusion blow molding is performed, solidification of the parison occurs at an early stage, which makes it difficult to shape. In order to sufficiently delay the rate of spherulite formation during melt-molding and obtain a molded article with excellent transparency with good shapeability, the cold crystallization temperature of the copolyester is 140 ° C or lower, and It is more preferable that the heat of crystallization in crystallization is 15 J / g or less. The cold crystallization temperature and the amount of heat of crystallization in the cold crystallization mentioned here are values measured by a differential thermal analysis (DSC), and the details thereof are as described in the section of Examples below.

As described above, the copolymerized polyester of the present invention comprises [1] (i) terephthalic acid or its ester-forming derivative; (ii) ethylene glycol; (iii) diol unit (I) and / or diol unit. At least one 2 selected from the above-mentioned diol (V), diol (VI) and their ester-forming derivatives for introducing (II) into the copolyester.
Functional compound; (iv) 3 or more of the above-mentioned carboxyl group, hydroxyl group and / or their ester-forming group for introducing the polyfunctional compound unit (III) into the copolyester.
And (v) at least one of the above-mentioned monocarboxylic acid, monoalcohol and ester-forming derivative thereof for introducing the monofunctional compound unit (IV) into the copolyester. A diol unit (I) derived from the bifunctional compound, wherein the content of the bifunctional compound in the reaction raw material is a monofunctional compound of a kind;
And / or the proportion of diol units (II) is from 0.5 to 0.5 based on the total number of moles of all structural units of the copolyester.
The content of the polyfunctional compound in the reaction raw material is such that the ratio of the polyfunctional compound unit (III) derived from the polyfunctional compound is all structural units of the copolyester. The amount of the monofunctional compound in the reaction raw material is 0.005 to 1 mol% based on the total number of moles of the monofunctional compound (IV). After a reaction raw material having an amount such that the ratio of) is such that the above mathematical formula (α) is satisfied based on the total number of moles of all structural units of the copolyester, an esterification reaction or a transesterification reaction is performed, By melt-polymerizing it to form a polyester prepolymer; [2] solid-phase polymerizing the polyester prepolymer obtained in the above step (1); You can

In the above method for producing a copolyester, the diol unit (I) and / or the diol unit (II) are introduced into the copolyester as a bifunctional compound, a polyfunctional compound and a monofunctional compound. The respective compounds described above can be used as the bifunctional compound, the polyfunctional compound for introducing the polyfunctional compound unit (III) and the monofunctional compound for introducing the monofunctional compound unit (IV).

In producing the copolyester,
The molar ratio of (total diol component) :( total dicarboxylic acid component) is 1.1: 1 to 1.5: 1, and the molar ratio of (polyfunctional compound component) :( total dicarboxylic acid component) is 0. .0
001: 1 to 0.02: 1 and the molar ratio of (monofunctional compound component) :( polyfunctional compound component) is {0.1 × (p−2)}: 1 to {20 × ( p-2)}:
It is preferable to mix the reaction components so as to be 1 (p is as defined above), and to carry out an esterification reaction or a transesterification reaction.

The above-mentioned esterification reaction or transesterification reaction is usually about 3 kg / cm ² under normal pressure or absolute pressure.
It is advisable to perform the treatment under the following pressure at a temperature of 230 to 300 ° C. while distilling off the produced water or alcohol. Then, subsequently, additives such as a polymerization catalyst and an anti-coloring agent are added if necessary, and a polyester prepolymer having a desired viscosity is obtained at a temperature of 200 to 300 ° C. under a reduced pressure of 5 mmHg or less. Melt polymerization to produce a polyester prepolymer. In that case, the intrinsic viscosity of the polyester prepolymer is 0.40 to 0.75 from the viewpoint of handling properties of the polyester prepolymer.
It is preferably in the range of dl / g and its MFR
Is preferably 15.0 g / 10 minutes or more.

When a polymerization catalyst is used in the above-mentioned melt polymerization reaction, those usually used in the production of polyester can be used. For example, antimony compounds such as antimony oxide; germanium compounds such as germanium oxide; Titanium compounds such as tetramethoxytitanium, tetraethoxytitanium, tetra-n-propoxytitanium, tetraisopropoxytitanium and tetrabutoxytitanium; di-n-butyltin dilaurate, di-n-butyltin oxide, dibutyltin diacetate and the like. Examples thereof include tin compounds, and these catalyst compounds may be used alone or in combination of two or more kinds. The amount of the polymerization catalyst used is 0.00 based on the weight of the dicarboxylic acid component.
It is preferably in the range of 2 to 0.8% by weight.

When a coloring preventing agent is used, for example, phosphorous acid, phosphoric acid, trimethyl phosphite, triphenyl phosphite, tridecyl phosphite, trimethyl phosphate, tridecyl phosphite, triphenyl phosphite. And the like, and these phosphorus compounds may be used alone or in combination of two or more kinds. It is preferable that the amount of the anti-coloring agent made of the above-mentioned phosphorus compound used is in the range of 0.001 to 0.5% by weight based on the weight of the dicarboxylic acid component. Further, in order to suppress coloring due to thermal decomposition of the copolyester, a cobalt compound such as cobalt acetate is added in an amount of 0.001 to 0.
It is preferable to add 5% by weight, and more preferably 0.05 to 0.3% by weight.

Furthermore, as described above, when a large amount of diethylene glycol units are contained in the copolyester, the glass transition temperature of the copolyester is lowered, and the heat resistance is lowered and the coloring is caused accordingly. Although the heat resistance, strength, color tone and the like of the molded product such as are poor, the above-mentioned esterification reaction, transesterification reaction and / or melt polymerization reaction is carried out by tetraalkylammonium hydroxide such as tetraethylammonium hydroxide; It is preferable to carry out the treatment in the presence of a diethylene glycol by-product inhibitor composed of an organic amine such as ethanolamine or triethylamine, because the proportion of diethylene glycol units in the copolyester can be reduced.

Next, the polyester prepolymer obtained by the above-mentioned melt polymerization reaction is made into chips or pellets having an arbitrary shape such as a die shape, a column shape, etc.
After pre-drying at a temperature below 0 ° C, its intrinsic viscosity, MF
Solid phase polymerization is carried out until R or the like reaches a desired value to form a desired copolyester. The solid phase polymerization is preferably carried out under vacuum, reduced pressure or in an inert gas such as nitrogen gas. Further, it is preferable to carry out solid phase polymerization while flowing the chips or pellets by an appropriate method such as a rolling method or a gas fluidized bed method so that the polyester prepolymer chips or pellets do not stick to each other. Solid phase polymerization is usually preferably carried out at a temperature within the range of 180 to 240 ° C.,
It is more preferable to carry out at a temperature within the range of 190 to 230 ° C. Further, the solid-phase polymerization temperature is within the above-mentioned range from the viewpoint of preventing sticking between chips and pellets, and the copolyester intended for production (copolymer polyester finally obtained). ) From the melting point of 1)
The temperature may be 5 ° C. or lower, preferably 20 ° C. or lower. From the viewpoint of productivity, it is preferable that the polymerization time is usually in the range of about 5 to 40 hours. Then, by performing the series of reactions described above, the copolyester of the present invention can be produced with good productivity in a short time.

Since the copolyester of the present invention is excellent in melt moldability, transparency, heat resistance, mechanical properties, etc., it is extrusion blow molding method, injection / extrusion blow molding method, extrusion molding method, injection molding method. It can be molded into various molded products by other melt molding methods. Among them, the copolyester of the present invention is suitable for use in molding involving a melt extrusion process, and particularly suitable for use in extrusion blow molding. And, melt molding using the copolymerized polyester of the present invention, especially extrusion blow molding with melt extrusion,
When injection / extrusion blow molding, extrusion molding, injection molding, etc. are performed, it is possible to manufacture with good productivity without causing deformation after extrusion, and the molded product obtained thereby has dimensional accuracy, Has excellent properties such as transparency, heat resistance, moisture resistance, and chemical resistance. In particular, when extrusion blow molding is performed using the copolymerized polyester of the present invention, the drawdown property of the extruded parison is good, and the drawdown time of the parison is maintained in an appropriate range. The diameter is uniform, blow moldability is good,
Hollow molded products with good shape and dimensional accuracy without distortion or deformation can be smoothly produced with good productivity without causing problems during molding, and the extrusion blow molded products obtained thereby are transparent. It has excellent properties such as impact resistance, heat resistance, moisture resistance, and chemical resistance.

In carrying out melt-molding using the copolymerized polyester of the present invention, each melt-molding method conventionally known for thermoplastic resins, for example, extrusion blow molding method, injection / extrusion blow molding method, It may be carried out according to the extrusion molding method and the injection molding method, and the specific molding contents are not particularly limited. In particular, when performing extrusion blow molding using the copolymerized polyester of the present invention, the type of the extrusion blow molding method is not particularly limited, and like the conventionally known extrusion blow molding method, for example, the copolymerized polyester of the present invention. Melt extrusion molding to form a cylindrical parison, insert this into the blow mold while the parison is in the softened state, blow a gas such as air to blow the parison into a predetermined shape along the shape of the mold cavity. It can be performed by a method of expanding into a hollow shape. When the extrusion blow molding is performed by the above-described method, the melt extrusion temperature is set to a temperature within the range of (melting point of copolyester + 10 ° C.) to (melting point of copolyester + 70 ° C.). It is preferable from the points such as.

The shape, structure, etc. of the molded product of the present invention are not particularly limited, and may be, for example, a hollow molded product, a tubular body, a plate, a sheet, a film, a rod-shaped body, a molded product, etc., depending on each application. Can have any shape and structure, and its dimensions are not limited. Of which
The invention is particularly suitable for hollow molded articles by extrusion blow molding.

Further, a molded article obtained from the copolyester of the present invention is a laminate with other materials such as other plastics, metals, fibers and cloth even if it is formed of the copolyester of the present invention alone. Or a molded article having a shape other than the laminated structure of the copolymerized polyester of the present invention and the above-mentioned other materials, and is not limited at all. In particular, when the molded product of the present invention is an extrusion blow molded product, for example, a single-layer hollow molded product (a hollow container or the like) consisting only of the copolyester of the present invention, the copolyester of the present invention and polyethylene, polypropylene,
It can be a multi-layer hollow molded article with other plastics such as ethylene-vinyl alcohol copolymer and polyethylene terephthalate (PET). Layer bottle, PET layer / Copolyester layer / PET
A five-layer bottle composed of layers / copolyester layer / PET layer may be mentioned. However, the molded article of the present invention is of course not limited to the above.

If desired, the copolyester of the present invention may contain various additives conventionally used for other thermoplastic resins and polyester resins, for example, colorants such as dyes and pigments. , Stabilizers such as UV absorbers,
You may mix | blend an antistatic agent, a flame retardant, a flame retardant auxiliary agent, a lubricant, a plasticizer, an inorganic filler, etc.

[0084]

EXAMPLES The present invention will be specifically described below with reference to Examples and the like, but the present invention is not limited thereto. In the following examples, the content of each structural unit of the polyester (copolymerized polyester or homopolymerized polyester) and the physical properties of the polyester were measured, and the drawdown property and blow moldability of the parison during extrusion blow molding of the polyester were evaluated, and extrusion was performed. The transparency of the molded product (bottle) obtained by blow molding, the evaluation of the gel generation rate and the spot generation rate, and the drop fracture height measurement and the drop strength evaluation of the molded product (bottle) were performed as follows. went.

(1) Content of each structural unit in polyester: The polyester is subjected to methanolysis, the constituent components are separated by high performance liquid chromatography, and the obtained components are UV / visible absorption spectrum, refractive index and infrared absorption. Quantitative analysis by spectrum (IR) was performed to determine the content rate of each structural unit. It was also confirmed by ¹ H-NMR spectrum of polyester using deuterated trifluoroacetic acid as a solvent.

(2) Intrinsic viscosity of polyester: In an equal weight mixed solvent of phenol and tetrachloroethane,
At 30 ℃, c base Rohde-type viscometer (Hayashi Seisakusho "HRK-
3 type ").

(3) Melt Flow Rate (MFR) of Prepolymer and Polyester: Melt Indexer L
244 (manufactured by Takara Industry Co., Ltd.). Specifically, prepolymer or polyester (final product)
After the chips of No. 1 were filled in a cylinder having an inner diameter of 9.55 mm and a length of 162 mm and melted at 270 ° C. (However, in Comparative Examples 6 and 8, since the copolyester was amorphous, at 210 ° C. (Molten), a prepolymer extruded from a 2.1 mm diameter orifice provided in the center of the cylinder by evenly applying a load of 2160 g and a 9.48 mm diameter plunger to the melted prepolymer or polyester. Alternatively, the outflow rate (g / 10 minutes) of the polyester was measured and this was used as the melt flow rate.

(4) Melt viscosity (η1 and η2) of polyester: Shear rate 0.1 rad of polyester at 270 ° C. using a parallel plate by a mechanical spectrometer (“RMS-800” manufactured by Rheometrics). Melt viscosity (η1) (poise) at 100 s / sec and melt viscosity (η2) (poise) at a shear rate of 100 rad / sec of polyester at a temperature of 270 ° C. were dynamically measured (however, Comparative Example 6 and In the case of Comparative Example 8, the copolymerized polyester was amorphous, so the measurement was performed at 210 ° C.).

(5) Shark skin critical shear stress (σss) and shear stress (σ100) of polyester: diameter 2 mm × length 10 m by a Capirograph (manufactured by Toyo Seiki)
The polyester was extruded into strands at a temperature of 270 ° C. with varying shear rate using a capillary nozzle of m. The shear stress at the time when the surface of the strand is roughened (at the time when the ten-point average surface roughness reaches 1.5 μmRz or more) is determined, and this is calculated as the critical shear stress (σss) (dyne / cm ² ) of sharkskin (shark skin). ). Also, using the same device, the shear stress (σ100) of polyester at a shear rate of 100 / sec at a temperature of 270 ° C.
(Dyne / cm ² ) was measured (however, in Comparative Examples 6 and 8, since the copolyester was amorphous, it was measured at 210 ° C.).

(6) Crystallinity of polyester (χc):
The density (d) of polyester (25 ° C.) was measured, and the density (d) of completely amorphous PET (polyethylene terephthalate) was measured.
a) is 1.335, the density (dc) of fully crystallized PET (polyethylene terephthalate) is 1.501, and the crystallinity (χc) of polyester is calculated from the following formula (γ).
I asked.

[0091]  χc (%) = {dc (d-da) / d (dc-da)} × 100 (γ)

(7) Glass transition temperature of polyester (T
g) and melting point (Tm): according to JIS K7121, by a differential thermal analysis method (DSC) using a thermal analysis system "METTLER TA3000" (manufactured by METTLER CORPORATION),
The measurement was performed under the condition that the temperature rising rate was 10 ° C./min.

(8) Cold crystallization temperature of polyester (Tc
c) and heat of cold crystallization (ΔHcc): JIS K71
According to No. 21, using a thermal analysis system "METTLER TA3000" (manufactured by METTLER CORPORATION) by a differential thermal analysis method (DSC), the temperature is kept at a melting point + 40 ° C for 5 minutes, and then the temperature lowering rate is 5 ° C / minute. It was measured at.

(9) Terminal carboxyl group concentration (CEG) of polyester: 0.2 g of polyester was dissolved in 10 ml of benzyl alcohol heated to 215 ° C., 10 ml of chloroform was added to the solution, and titrated with benzyl alcohol caustic soda. did.

(10) Drawdown property of the parison during extrusion blow molding: (i) Drawdown time of the parison (seconds) Extrusion blow molding device manufactured by Placo Co., Ltd. (hollow molding machine "BM-304 / J2 type machine") ) At an extrusion temperature of 270 ° C. at an extrusion rate of about 25 kg / hour to form a cylindrical parison (however, in the case of Comparative Example 6 and Comparative Example 8, the copolymerized polyester was amorphous. Since it was molded at an extrusion temperature of 210 ° C), the cylindrical parison was cut and bottom formed by sandwiching it with a blow mold while it was in a softened state, and this was blow molded to a set volume of 1800 ml and a set weight of 80 Gram soft drink bottles were produced. The extrusion blow molding device used here is designed such that when the parison draws down 35 cm, it is sandwiched by the mold and blown. Therefore, the time (second) required to draw down 35 cm is reduced by drawdown. Measured as time. In the case of the extrusion blow molding device used here, the moldability becomes good when the drawdown time is within the range of 15 to 25 seconds. If the drawdown time is less than 15 seconds, the drawdown is severe and the parison shape becomes non-uniform, resulting in defective products with large thickness unevenness after blow, inability to insert into the blow mold, blockage in the hollow part of the parison, etc. Occurs. Further, if the drawdown time exceeds 25 seconds, the productivity of the molded product (bottle) becomes low, and the melt viscosity of the polyester is too high to blow uniformly, and further non-adhesion at the pinch-off part of the bottle In addition, a weld line is easily generated, and the molding device is easily damaged due to an increase in torque.

(Ii) Difference between maximum diameter (outer diameter) and minimum diameter (outer diameter) of parison: Cylindrical parison was extruded at an extrusion temperature of 270 ° C. using the above extrusion blow molding apparatus (however,
In the case of Comparative Example 6 and Comparative Example 8, since the copolyester was amorphous, it was molded at an extrusion temperature of 210 ° C.), and when the parison reached 35 cm, the maximum diameter (outer diameter) and the minimum diameter of the parison were reached. (Outer diameter) was measured and the difference between them was obtained. The diameter of the annular die of the extrusion nozzle of the extrusion blow molding apparatus used here is 3.5 cm, but the extruded parison is a drawdown due to its own weight, and the diameter tends to become smaller as the distance from the die increases. If the difference between the maximum diameter and the minimum diameter of the parison is 1 cm or less, normal extrusion blow molding can be performed smoothly. On the other hand, when the difference between the maximum diameter and the minimum diameter of the parison exceeds 1 cm, uneven thickness occurs after blowing, resulting in defective products.

(Iii) Comprehensive evaluation of drawdown properties of the parison: Table 1 below shows the drawdown time of the parison, the difference between the maximum diameter and the minimum diameter of the parison, and the size of the bottle productivity. The drawdown property was comprehensively evaluated according to the evaluation criteria. At that time, regarding the productivity of the bottles, from the viewpoint of cost, 120 or more bottles could be produced per hour, and the case where the number of molding defects was less than 10 bottles per 100 bottles was considered to be good. In addition, the molding failure here means that the shape of the bottle cannot be inserted into the blow mold due to the drawdown of the extruded parison, the hollow part of the parison is blocked, the pinch-off portion is not adhered due to high viscosity, and the bottle shape is uneven. When at least one of the problems of deformation and destruction of occurs.

[0098]

[Table 1]

(11) Blow moldability during extrusion blow molding (i) Average wall thickness of bottle: The bottle body obtained by molding is divided into 5 parts at equal intervals from the upper part to the lower part of the bottle body, and each of them is divided into a circle The wall thickness was measured at 20 points in total by dividing the wall into four at equal intervals in the circumferential direction, and the average wall thickness was calculated.
The average wall thickness is 0.3 in terms of appearance, touch and bottle strength.
It is preferably in the range of mm or more and 0.7 mm or less. (Ii) Bottle thickness unevenness: The difference (mm) between the maximum thickness and the minimum thickness in the wall thickness of the bottle body obtained in the above measurement (i) was obtained and evaluated. The thickness unevenness is preferably less than 0.3 mm, and if it is more than 0.3 mm, an ultrathin portion and / or a damaged portion is generated, and the appearance and / or the touch becomes poor. (Iii) Comprehensive evaluation of blow moldability Comprehensive evaluation of blow moldability was performed according to the evaluation criteria shown in Table 2 below.

[0100]

[Table 2]

(12) Transparency of bottles: (i) Haze value (cloudiness value): ASTM D1003 was used for a total of 24 places in which the body of the bottle was divided into 6 parts over the upper part, the middle part and the lower part and further divided into 4 parts on the circumference. According to the Poic integrating sphere type light transmittance / total light reflectance meter (manufactured by Nippon Seimitsu Co., Ltd. “SEP-HS / 30D-R
The haze value at each location was measured using a mold, and the average value was taken as the haze value (cloudiness value) of the bottle. When the haze value exceeds 8, the transparency becomes poor due to whitening due to spherulite formation or light scattering due to gel-like lumps.
It is preferable that the haze value is 4 or less from the viewpoint of transparency. (Ii) The bottle body was shredded into 1 cm ² (1 cm x 1 cm square pieces), and a color difference meter ("SM" manufactured by Suga Test Instruments Co., Ltd.
-4 type "). When the b value exceeds 8, the yellow color of the bottle becomes strong and the appearance becomes poor. It is preferable in terms of color tone that the b value is 4 or less. (Iii) Comprehensive evaluation of transparency of bottles: Comprehensive evaluation of transparency of bottles was performed according to the evaluation criteria shown in Table 3 below.

[0102]

[Table 3]

(13) Gel generation rate of bottle: Polyester on the body of the bottle was cut out in a weight of 1 g and dissolved in 10 ml of hexafluoroisopropanol while keeping it at a temperature of 30 ° C. for 5 hours. It was filtered through a 4G glass filter. The gel product was heated at a temperature of 100 ° C. for 60 minutes to be dried, and then the weight thereof was measured to obtain a weight percentage with respect to the cut polyester sample (1 g), which was defined as a gel product generation rate, and the results are shown in Table 4 below. The gel generation rate of the bottle was evaluated according to the standard.

[0104]

[Table 4]

(14) Occurrence rate of bottle lumps: The center of the bottle body was cut out at 10 cm × 10 cm, and the number of lumps contained therein was visually measured. Therefore, the bottleneck occurrence rate was evaluated.

[0106]

[Table 5]

(15) Drop impact strength of bottles: Each of the 10 bottles obtained by molding was filled with water so as not to leave voids and capped. When the bottle is naturally dropped from a height of 50 cm and the bottle is not broken, the drop height is increased by 10 cm and the bottle is naturally dropped in the same manner, and the operation is sequentially repeated to obtain the height at which the bottle is broken. The average value of the heights of the bottles at the time of breaking was taken as the falling breaking height. The drop impact strength of the bottle was evaluated according to the evaluation criteria shown in Table 6 below.

[0108]

[Table 6]

Example 1 (1) 100.00 parts by weight of terephthalic acid, 48.73 parts by weight of ethylene glycol, 2,2-bis [4- (2-
Hydroxyethoxy) phenyl] propane 5.75 parts by weight, trimethylolpropane 0.081 parts by weight and benzoic acid 0.015 parts by weight were prepared into a slurry, and 0.020 parts by weight of germanium dioxide, 0.01
5 parts by weight of phosphorous acid, 0.015 parts by weight of cobalt acetate and 0.015 parts by weight of tetraethylammonium hydroxide were added. This slurry was heated to a temperature of 250 ° C. under pressure (absolute pressure 2.5 kg / cm ² ) and an esterification reaction was carried out until the esterification rate reached 95% to produce a low polymer. Then, under a reduced pressure of 1 mmHg,
The above-mentioned low polymer is melt-polymerized at a temperature of 270 ° C. to form a prepolymer of a copolyester having an intrinsic viscosity of 0.70 dl / g, which is extruded from a nozzle in a strand shape and cut into a cylindrical tip ( The diameter was about 2.5 mm and the length was about 3.5 mm). The melt flow rate of this prepolymer at 270 ° C. was 32 g / 10 minutes. (2) Then, the prepolymer chips of the copolyester obtained above are pre-dried at 150 ° C. for 5 hours, and then 210 ° C. under reduced pressure of 0.1 mmHg using a rolling vacuum solid-state polymerization apparatus. Solid phase polymerization was carried out for 27 hours to obtain a copolyester having a high molecular weight.

(3) The content of each structural unit of the copolyester obtained in (2) above was measured by the above-mentioned method. As a result, the terephthalic acid unit, the ethylene glycol unit, the 2,2-bis unit in the copolyester were measured. [4- (2
The contents of -hydroxyethoxy) phenyl] propane unit, trimethylolpropane unit, benzoic acid unit and diethylene glycol unit were as shown in Table 8 below. (4) The physical properties of the copolyester obtained in (2) above were measured by the methods described above, and the results are shown in Table 8 below.
As shown in, the intrinsic viscosity is 1.10 dl / g, 270 ° C.
MFR at the temperature of 2.0 g / 10 min, melt viscosity at the shear rate of 0.1 rad / sec (η1) at the temperature of 1.36 × 10 ⁵ poise, melt viscosity at the shear rate of 100 rad / sec (η2) Is 1.40 × 10 ⁴ poise, and therefore the value of (1/3) log ₁₀ (η2 / η1) is −0.
It was 33. Furthermore, the sharkskin critical shear stress (σss) at 270 ° C. of the copolyester obtained in (2) above is 5.0 × 10 ⁶ dyne / cm ² , and the shear stress (σ100) at a shear rate of 100 / sec is 2.6 × 10 ⁶ d
It was yne / cm ² . Further, when χc, Tg, Tm, Tcc and ΔHcc of the copolyester obtained in the above (2) were measured by the above method, the following Table 8 was obtained.
33%, 79 ° C, 243 ° C, 14
It was 3 ° C. and 15 J / g. Furthermore, the terminal carboxyl group concentration (CEG) of the copolymerized polyester obtained in (2) above was 12 μeq / g.

(5) The copolymerized polyester obtained in (2) above was extrusion blow molded by the above method using an extrusion blow molding device ("BM-304 J2 type" manufactured by Placo Co., Ltd.). A bottle with a set capacity of 1800 ml and a set weight of 80 g was manufactured. When measured or evaluated by the method,
It was as shown in 3.

Examples 2 to 4 Terephthalic acid and ethylene glycol were used in the proportions shown in Table 8 below, and a difunctional unit for the diol unit (I) and / or the diol unit (II) having a benzene nucleus was added thereto. 2,2- as a compound
Bis [4- (2-hydroxyethoxy) phenyl] propane is trimethylolpropane or trimellitic anhydride as a polyfunctional compound for the polyfunctional compound unit (III), and a monofunctional compound for the monofunctional compound unit (IV). As 2
-Using naphthoic acid, benzoic acid or 2,4,6-trimethoxybenzoic acid in the proportions shown in Table 8, esterification reaction and melt polymerization reaction were carried out in the same manner as in Example 1 to prepare a copolymerized polyester prepolymer. After producing the polymer chips, solid phase polymerization was carried out at the temperatures and the times shown in Table 8 below to produce copolymerized polyesters. The content of each structural unit in the obtained copolyester and the physical properties of the copolyester were examined in the same manner as in Example 1, and the results are shown in Table 8 below. Also,
Extrusion blow molding was carried out in the same manner as in Example 1 using the copolymerized polyesters obtained in Examples 2 to 4 to produce bottles, and the drawdown property of the parison at that time, blow moldability and the obtained The transparency, gel generation rate, spot generation rate, drop breaking height, and drop impact strength of the bottles were measured or evaluated by the methods described above, and the results are shown in Table 13 below.

Examples 5 to 8 Terephthalic acid and ethylene glycol were used in the proportions shown in Table 9 below, and a difunctional unit for diol unit (I) and / or diol unit (II) having a benzene nucleus was added thereto. Bis [4 as compound
-(2-hydroxyethoxy) phenyl] sulfone or 1,4-bis (2-hydroxyethoxy) benzene, pentaerythritol, trimellitic anhydride or trimesic acid as a polyfunctional compound for the polyfunctional compound unit (III), Using stearic acid, stearyl alcohol, m-anisic acid or benzoic acid in the proportions shown in Table 9 as the monofunctional compound for the monofunctional compound unit (IV), the esterification reaction and melting were carried out in the same manner as in Example 1. After the polymerization reaction was carried out to manufacture a prepolymer chip of the copolyester, solid phase polymerization was carried out at the temperature and time shown in Table 9 below to manufacture the copolyester. The content of each structural unit in the obtained copolyester and the physical properties of the copolyester were examined in the same manner as in Example 1. The results are shown in Table 9 below. Further, extrusion blow molding was carried out in the same manner as in Example 1 using the copolymerized polyesters obtained in Examples 5 to 8 to produce bottles, and the drawdown property of the parison, blow moldability and The transparency, gel generation rate, spot generation rate, drop breakage height and drop impact strength of the obtained bottle were measured or evaluated by the methods described above, and the results are shown in Table 13 below.

Comparative Examples 1 to 4 Terephthalic acid and ethylene glycol were used in the proportions shown in Table 10 below, to which neopentyl glycol was added or not as a bifunctional compound for the bifunctional compound unit. Alternatively, isophthalic acid was added as a bifunctional compound for the bifunctional compound unit, and trimethylolpropane, trimellitic anhydride or pentaerythritol was added as a polyfunctional compound for the polyfunctional compound unit (III) in the proportions shown in Table 10. In the same manner as in Example 1 with or without benzoic acid or m-anisic acid as the monofunctional compound for the monofunctional compound unit (IV) in the proportions shown in Table 10. And the temperature shown in Table 10 below after prepolymer chips of the copolyester are produced by carrying out a melt polymerization reaction. And performing solid phase polymerization with time, to produce a copolymerized polyester, respectively. The content of each structural unit in the obtained copolyester and the physical properties of the copolyester were examined in the same manner as in Example 1, and the results are shown in Table 10 below. Further, extrusion blow molding was carried out in the same manner as in Example 1 using the copolymerized polyesters obtained in Comparative Examples 1 to 4 to produce bottles, and the drawdown property of the parison at that time, the blow moldability and The transparency, gel generation rate, spot generation rate, drop breakage height and drop impact strength of the obtained bottle were measured or evaluated by the methods described above, and the results are shown in Table 13 below.
It was as shown in.

Comparative Examples 5 to 8 [0115] Terephthalic acid and ethylene glycol were used in Table 11 below.
2 for the diol unit (I) and / or the diol unit (II) having a benzene nucleus.
A diol unit (I) and / or a diol unit (II) having no functional compound or having a benzene nucleus
2,2-bis [4- (2-hydroxyethoxy) phenyl] propane is used as the bifunctional compound for the polyfunctional compound, and the polyfunctional compound for the polyfunctional compound unit (III) is not used or the polyfunctional compound unit (III) is used. ) Is used as a polyfunctional compound for trimethylolpropane in a ratio shown in Table 11,
Then, the monofunctional compound for the monofunctional compound unit (IV) was not used, or naphthoic acid was used as the monofunctional compound for the monofunctional compound unit (IV) in the proportions shown in Table 11 or not. In the same manner as in 1, the esterification reaction and the melt polymerization reaction were carried out to produce prepolymer chips of the copolyester, and then solid phase polymerization was carried out at the temperature and time shown in Table 11 below to obtain the copolyester. It was produced (however, in Comparative Example 6 and Comparative Example 8, since the prepolymer chips of the copolyester were amorphous, they were used as they were for the following extrusion blow molding without solid phase polymerization). The content of each structural unit in the obtained copolyester and the physical properties of the copolyester were examined in the same manner as in Example 1 and were as shown in Table 11 below (however, as compared with the above, comparison was made). For Example 6 and Comparative Example 8, the measurement was performed at 210 ° C). Further, using the copolymerized polyesters obtained in Comparative Examples 5 to 8, extrusion blow molding was performed in the same manner as in Example 1 to produce a bottle, and the drawdown property of the parison, the blow moldability and When the transparency, gel generation rate, spot generation rate, drop breakage height and drop impact strength of the obtained bottle were measured or evaluated by the above-mentioned methods, it was as shown in Table 13 below (however, As described above, in Comparative Example 6 and Comparative Example 8, extrusion blow molding was performed at 210 ° C).

Comparative Examples 9 to 11 Using terephthalic acid and ethylene glycol in the proportions shown in Table 12 below,
Further, 2,2-bis [4- (2-hydroxyethoxy) phenyl] propane is used as a bifunctional compound for the diol unit (I) and / or the diol unit (II) having a benzene nucleus, and a polyfunctional compound is also used. Unit (III)
Whether trimellitic acid is used as a polyfunctional compound for use in the proportions shown in Table 12 or not, and benzoic acid is used as a monofunctional compound for the monofunctional compound unit (IV) in proportions shown in Table 12. Alternatively, without using, after performing an esterification reaction and a melt polymerization reaction in the same manner as in Example 1 to produce a prepolymer chip of a copolyester,
Solid-state polymerization was carried out at the temperature and time shown in Table 12 below to produce copolymerized polyesters. When the content of each structural unit in the obtained copolyester and the physical properties of the copolyester were examined in the same manner as in Example 1, the results are shown in Table 12 below. Further, extrusion blow molding was carried out in the same manner as in Example 1 using the copolyesters obtained in Comparative Examples 9 to 11 to produce bottles, and the drawdown property of the parison, blow moldability and The transparency of the resulting bottle,
The gel generation rate, the spot generation rate, the drop fracture height, and the drop impact strength were measured or evaluated by the above-mentioned methods, and were as shown in Table 13 below.

The abbreviations used in Tables 8 to 12 below are as shown in Table 7 below.

[0118]

[Table 7]

[0119]

[Table 8]

[0120]

[Table 9]

[0121]

[Table 10]

[0122]

[Table 11]

[0123]

[Table 12]

[0124]

[Table 13]

From the results of Tables 8 to 9 and Table 13 above,
The diol unit (I) and / or the diol unit (II) having a benzene nucleus is added in an amount of 0.5 to 7 based on the total number of moles of all structural units of the copolyester, which is mainly composed of a terephthalic acid unit and an ethylene glycol unit.
In the range of mol%, and the polyfunctional compound unit (III) in the range of 0.005 to 1 mol%, and the monofunctional compound unit (IV) in the range satisfying the above formula (α). Examples 1-8 for making copolyesters having
In the case of, it can be seen that a copolymerized polyester having an intrinsic viscosity suitable for melt molding such as extrusion blow molding can be produced in a short solid-state polymerization time of 30 hours or less. Moreover, when the bottles were produced by extrusion blow molding using the copolymerized polyesters obtained in Examples 1 to 8, the drawdown time of the extruded parison was in the proper range of 16 to 23 seconds, which was the minimum of the parison. The difference between the maximum value and the maximum value is 0.7 cm
The production amount of the bottle is 120 or more per hour, and the proportion of poorly formed bottles is less than 10 out of 100 bottles, and the parison has excellent drawdown property. The average wall thickness of the bottle is 0.3
It is found that the thickness is in the range of mm or more and 0.7 mm or less, the thickness unevenness is less than 0.3 mm, and the blow moldability is excellent. In addition, the bottles obtained in Examples 1 to 8 have haze values of 4 or less and b values of 4 or less and are excellent in transparency, and the gel generation rate is 2.5% or less. The number of spots is extremely small, and the percentage of spots is 5 pieces / 100 cm ² or less.
It can be seen that it has a high drop impact strength at 00 cm or more.

In contrast, Tables 10 and 13 above
From the result, it is mainly composed of a terephthalic acid unit and an ethylene glycol unit, but does not have a diol unit (I) and / or a diol unit (II) having a benzene nucleus, and only a polyfunctional compound unit (III), or In the case of Comparative Examples 1 and 2 in which the copolyester having only the polyfunctional compound unit (III) and the monofunctional compound unit (IV) is produced, the solid phase polymerization time is 40 hours or more, which is long for the polymerization. It can be seen that it takes time and is inferior in productivity. Moreover, when a bottle is manufactured by extrusion blow molding using the copolyester obtained in these Comparative Examples, the thickness unevenness of the bottle is 0.30 mm or more and the blow moldability is poor, and The resulting bottle had a haze value of 10 or more and poor transparency, and the gel generation rate exceeded 5% (Comparative Example 2). Also, the seed generation rate exceeded 10/100 cm ² . It can be seen that the appearance and feel are poor, and that the drop breaking height is 50 cm and the drop impact strength is small.

From the results shown in Tables 10 and 13, the diol unit (I) and / or the diol unit (II) mainly composed of terephthalic acid units and ethylene glycol units and having a benzene nucleus were not contained. Instead, it has a neopentyl glycol unit as a bifunctional compound unit, a trimethylolpropane unit as a polyfunctional compound unit (III), and a monofunctional compound unit (I
In the case of Comparative Example 3 in which a copolyester having no V) is produced, the solid-phase polymerization time exceeds 30 hours, and it takes a long time to carry out the polymerization, which shows that the productivity is poor. Moreover, when a bottle was produced by extrusion blow molding using the copolymerized polyester obtained in Comparative Example 3,
The uneven thickness of the bottle is 0.30 mm or more and the blow moldability is inferior, and the obtained bottle has a haze value of more than 4 and is poor in transparency, and further, the gel generation rate is high. It was found to be over 5%, and the occurrence rate of seeds was over 10 pieces / 100 cm ² , and the appearance and feel were poor, and the drop fracture height was 80 cm, and the drop impact strength was small. .

Further, from the results of Tables 10 and 13 above, the diol unit (I) mainly composed of a terephthalic acid unit and an ethylene glycol unit and having a benzene nucleus.
And / or does not have a diol unit (II), instead has an isophthalic acid unit as a bifunctional compound unit, has a pentaerythritol unit as a polyfunctional compound unit (III), and is a monofunctional compound The copolymerized polyester of Comparative Example 4 having the m-anisic acid unit as the unit (IV) had a bottle thickness unevenness of 0.45 mm when the bottle was manufactured by extrusion blow molding, and was inferior in blow moldability. In addition, the obtained bottle had a remarkably small surface roughness and had a haze value of 8.5 and was inferior in transparency, and was also inferior in touch. In addition, it can be seen that the bottle obtained using the copolyester of Comparative Example 4 has a drop breakage height of 50 cm, a small drop impact strength, and low quality.

From the results of Table 11 and Table 13 above, a polyester produced by using only terephthalic acid and ethylene glycol, having a benzene nucleus having a diol unit (I) and / or a diol unit (II)
Comparative Example 5 containing no polyfunctional compound unit (III) and no monofunctional compound unit (IV)
(Wherein the polyester of Comparative Example 5 has 1.30 mol% of diethylene glycol units which are the above-mentioned undesirable copolymerization units), the drawdown time of the parison is 5 seconds, and The difference between the maximum diameter and the minimum diameter is 3.0 cm or more, and the drawdown property of the parison is extremely inferior, which means that extrusion blow molding is practically difficult. Further, in the case of Comparative Example 5, the solid phase polymerization takes 67 hours, and it can be seen that the productivity is extremely low.

From the results shown in Tables 11 and 13, the diol unit (I) and / or the diol unit (II) mainly consisting of a terephthalic acid unit and an ethylene glycol unit and having a benzene nucleus were obtained. The copolymerized polyesters of Comparative Examples 6 and 8 whose proportion exceeded 7 mol% based on the total number of moles of all structural units of the copolymerized polyester were amorphous, and thus the degree of polymerization was increased by solid phase polymerization. It was not possible to obtain a high melt viscosity at a temperature of 270 ° C. and extrusion blow molding could not be performed. Therefore, extrusion blow molding was performed at a temperature of 210 ° C., which was barely possible, but the parison It is inferior in draw-down property, and when the bottle is manufactured by extrusion blow molding, the thickness unevenness of the bottle is 0.45 mm and blow moldability It can be seen that the poor. In addition, the bottles obtained in Comparative Example 6 and Comparative Example 8 were remarkably surface-roughened by molding at low temperature,
Therefore, the haze value exceeds 8, which is inferior in transparency, and inferior in tactile sensation.
It can be seen that the impact strength is cm and the drop impact strength is small and the quality is low.

From the results shown in Tables 11 and 13, the diol unit (I) and / or diol unit (II) and the polyfunctional compound unit (which mainly consist of terephthalic acid unit and ethylene glycol unit and have a benzene nucleus) III) but with a benzene nucleus having a proportion of diol units (I) and / or diol units (II) below 0.5 mol% based on the total number of moles of all structural units of the copolyester. The copolymerized polyester of Comparative Example 7 was inferior in blow moldability because the bottle thickness unevenness was 0.3 mm when the bottle was manufactured by extrusion blow molding, and the obtained bottle had a high crystallization rate. The haze value is 8 or more, the transparency is poor, the drop breaking height is 80 cm, the drop impact strength is small, and the quality is low. I understand.

From the results shown in Tables 12 and 13, the diol unit (I) and / or the diol unit (II) mainly composed of the terephthalic acid unit and the ethylene glycol unit and having a benzene nucleus and the polyfunctional compound unit ( The copolymerized polyester of Comparative Example 9 having III) but not the monofunctional compound unit (IV) has a bottle thickness unevenness of 0.35 mm when the bottle is manufactured by extrusion blow molding, and is blown. Moldability is inferior, and the resulting bottle has minute roughness on the surface and has a haze value of 8 or more and is inferior in transparency, gels and unmelted lumps are remarkable, and the drop breaking height is 70 cm. It can be seen that the drop impact strength is low and the quality is low.

From the results shown in Tables 12 and 13, the diol unit (I) and / or the diol unit (II) mainly consisting of a terephthalic acid unit and an ethylene glycol unit and having a benzene nucleus were obtained. The copolymerized polyester of Comparative Example 10, which does not have the polyfunctional compound unit (III) and the monofunctional compound unit (IV), is inferior in drawdown property of the parison, and when the bottle is produced by extrusion blow molding. The average wall thickness of the bottle is 0.20m
m, the thickness unevenness is 0.50 mm and the blow moldability is poor, and the obtained bottle has an extremely thin center portion of the body and has a drop breaking height of 50 cm and a drop impact strength. It can be seen that it is small and of poor quality.

From the results shown in Tables 12 and 13, the diol unit (I) and / or diol unit (II) mainly composed of a terephthalic acid unit and an ethylene glycol unit and having a benzene nucleus, a polyfunctional compound unit ( III) and monofunctional compound unit (IV),
The copolymerized polyester of Comparative Example 11 in which the proportion of the monofunctional compound unit (IV) was more than the range of the above formula (α), the polymerization degree could not be sufficiently increased by melt polymerization and solid phase polymerization, and the viscosity was low. there were. For this reason, even if this copolymerized polyester was subjected to extrusion blow molding, a parison could not be formed and a molded product could not be obtained.

[0135]

EFFECT OF THE INVENTION The copolymerized polyester of the present invention has a high melt viscosity, a low viscosity at a high shear rate, and a high viscosity at a low shear rate, and exhibits non-Newtonian properties. Melt fracture does not occur, the crystallization rate is suppressed, and since it has excellent characteristics that it does not cause lumps, it has extremely excellent melt moldability, extrusion blow molding using the copolymerized polyester of the present invention, When melt molding such as injection / extrusion blow molding, extrusion molding, injection molding, etc., there is no whitening or spots,
High quality with excellent properties such as transparency, surface condition, appearance, touch, and mechanical properties such as impact resistance, mechanical properties, dimensional accuracy, heat resistance, moisture resistance, chemical resistance, etc. The molded product can be manufactured extremely smoothly. And the copolyester of the present invention has a high melt viscosity and good melt viscosity characteristics suitable for use in melt molding involving a melt extrusion step among the above-described melt molding methods, particularly extrusion blow molding, Therefore, when extrusion blow molding is performed using the copolymerized polyester of the present invention, the drawdown property of the extruded parison is good, and the drawdown time of the parison is kept in an appropriate range. To produce a hollow molded product with a uniform diameter, good blow moldability, no distortion and deformation, good shape and dimensional accuracy, without any troubles during molding, and with good productivity. And can be used very suitably for extrusion blow molding of a large hollow molded product accompanied by extrusion of a relatively long parison having a length of 30 cm or more. Further, in the case of the method for producing a copolyester of the present invention, a copolyester having the above-mentioned excellent properties can be produced economically with good productivity in a short time, particularly in a shortened solid phase polymerization time. You can

─────────────────────────────────────────────────── ─── Continuation of the front page (58) Fields surveyed (Int.Cl. ⁷ , DB name) C08G 63/00-63/91

Claims (8)

(57) [Claims] 1. A copolymerized polyester mainly comprising a dicarboxylic acid unit composed of a terephthalic acid unit and a diol unit composed of an ethylene glycol unit, and having another copolymerized unit; (2) The copolymerized polyester described above. As other copolymerized units, (i) (a) the following general formula (I); [In the formula, A formula: -CH ₂ CH ₂ - or formula: -CH (C
H ₃ ) CH ₂ — group, B is divalent hydrocarbon group, carbonyl group, sulfonyl group, oxygen atom or direct bond (−), R ¹ and R ² are respectively inert substituents, j and k Each independently represents an integer of 0 to 8 and s and t each independently represent an integer of 0 to 4]; and (b) the following general formula (I):
I); [In the formula, A formula: -CH ₂ CH ₂ - or formula: -CH (C
H ₃ ) CH ₂ —, R ³ is an inert substituent, m and n are each independently an integer of 0 to 8, and u is 0.
A diol unit (II) represented by the formula: ## STR3 ## at least one difunctional compound unit based on the total number of moles of all structural units of the copolyester.
And (ii) a polyfunctional compound unit derived from at least one polyfunctional compound having 3 or more carboxyl groups, hydroxyl groups and / or their ester-forming groups ((ii) III) in a proportion of 0.005-1 mol% based on the total moles of all structural units of the copolyester; and (iii) at least one of monocarboxylic acids, monoalcohols and their ester-forming derivatives. The monofunctional compound unit (IV) derived from one monofunctional compound is represented by the following formula (α) based on the total number of moles of all structural units of the copolyester; {In the formula, [III] is the proportion (mol%) of the polyfunctional compound unit (III) in the copolyester, [IV] is the proportion (mol%) of the monofunctional compound unit (IV) in the copolyester, and p is A copolymerized polyester having a ratio of satisfying the average number of functional groups of the polyfunctional compound that induces the polyfunctional compound unit (III)}. 2. The copolyester according to claim 1, which has an intrinsic viscosity of 0.8 to 1.5 dl / g. 3. A shear rate of 0.1 at a temperature of 270 ° C.
Melt viscosity (η1) in rad / sec is 5 × 10 ^{4 to} 5 × 10
⁶ poise and a shear rate of 10 at a temperature of 270 ° C
The melt viscosity (η2) at 0 rad / sec is 5 × 10 ^{3 to} 5 × 1.
0 is ⁵ poise, and the melt viscosity (.eta.1) and melt viscosity (.eta.2) is the following formula (β); -0.7 ≦ (1/3 ) log 10 (η2 / η1) ≦ -0.2 ( The copolymerized polyester according to claim 1 or 2, which satisfies β). 4. The sharkskin critical shear stress (σss) at a temperature of 270 ° C. is 1 × 10 ⁶ dyne / cm ² or more, and the shear stress (σ100) at a shear rate of 100 / sec at a temperature of 270 ° C. is shark. The copolymerized polyester according to any one of claims 1 to 3, which has a skin critical shear stress (? Ss) or less. 5. A molded article made of the copolyester according to claim 1. 6. The molded product according to claim 5, which is an extrusion blow molded product. 7. A method for producing a molded article by carrying out extrusion blow molding using the copolymerized polyester according to any one of claims 1 to 4. 8. A method for producing a copolyester mainly composed of a dicarboxylic acid unit composed of a terephthalic acid unit and a diol unit composed of an ethylene glycol unit and having another copolymerized unit; [1] terephthalic acid or an ester thereof. In addition to the above-mentioned main dicarboxylic acid component and diol component, in addition to the above-mentioned main dicarboxylic acid component and diol component, (a) the following general formula (V); [In the formula, A formula: -CH ₂ CH ₂ - or formula: -CH (C
H ₃ ) CH ₂ — group, B is divalent hydrocarbon group, carbonyl group, sulfonyl group, oxygen atom or direct bond (−), R ¹ and R ² are respectively inert substituents, j and k Each independently represent an integer of 0 to 8 and s and t each independently represent an integer of 0 to 4]; and a diol (V) represented by the following general formula (VI); [In the formula, A formula: -CH ₂ CH ₂ - or formula: -CH (C
H ₃ ) CH ₂ —, R ³ is an inert substituent, m and n are each independently an integer of 0 to 8, and u is 0.
Represents an integer of 4 to 4], and at least one bifunctional compound selected from the following: (b) a carboxyl group, a hydroxyl group and / or their ester forming properties; A reaction raw material containing at least one polyfunctional compound having three or more groups; and (c) at least one monofunctional compound of a monocarboxylic acid, a monoalcohol and an ester-forming derivative thereof, and ( d) The content of the bifunctional compound in the reaction raw material is such that the ratio of the diol unit (I) and / or the diol unit (II) derived from the bifunctional compound is the total moles of all structural units of the copolyester. The amount is 0.5 to 7 mol% based on the number; (e) the content of the polyfunctional compound in the reaction raw material is An amount such that the proportion of the polyfunctional compound unit (III) derived from the polyfunctional compound is 0.005 to 1 mol% based on the total number of moles of all structural units of the copolyester; (f) The content of the monofunctional compound in the reaction raw material, the proportion of the monofunctional compound unit (IV) derived from the monofunctional compound is based on the total number of moles of all structural units of the copolyester, the following formula (α ); [Equation 2] {In the formula, [III] is the proportion (mol%) of the polyfunctional compound unit (III) in the copolyester, [IV] is the proportion (mol%) of the monofunctional compound unit (IV) in the copolyester, and p is The amount of the reaction raw material is such that the average amount of functional groups of the polyfunctional compound that induces the polyfunctional compound unit (III) is satisfied}, and then the reaction raw material is subjected to an esterification reaction or a transesterification reaction and then melt-polymerized. Forming a polyester prepolymer; then [2] solid-phase polymerizing the polyester prepolymer obtained in the above step [1].
5. The method for producing the copolyester according to any one of 4 to 4.