JP3461202B2 - Liquid composition, ink set, and inkjet recording method - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a technique for obtaining a water-resistant image by reducing bleeding that occurs when forming a color image on plain paper, and is most preferably used for image formation using an ink jet recording system. liquid compositions, Inkuse' preparative及 beauty jet recording method using the liquid composition.

[0002]

2. Description of the Related Art An ink jet recording method is one in which a droplet of ink is ejected and the ink is adhered to a recording medium such as paper for recording. In particular, Japanese Patent Publication No. 61-59911, Japanese Patent Publication No. 61-59912, and Japanese Patent Publication No. 61-5.
According to the ink jet recording method of the type disclosed in Japanese Patent No. 9914, in which an electrothermal converter is used as the ejection energy supply means and thermal energy is applied to ink to generate bubbles, the droplets are ejected. High-density multi-orifice can be easily realized, and high-resolution and high-quality images can be recorded at high speed.

However, the ink used in the conventional ink jet recording method contains water as a main component and contains a water-soluble high-boiling point solvent such as glycol for the purpose of preventing drying and preventing nozzle clogging. Therefore, it is estimated that when recording on plain paper using such ink, sufficient fixability may not be obtained, or due to uneven distribution of fillers and sizing agents on the recording paper surface. This causes a problem such as the occurrence of a non-uniform image. or,
In particular, when trying to obtain a color image, the inks of a certain color are successively superposed before the ink of a certain color is fixed on the recording paper. There is a problem that they are not uniformly mixed (hereinafter, this phenomenon is called bleeding) and a satisfactory image cannot be obtained.

On the other hand, as a means for improving the fixing property, Japanese Patent Application Laid-Open No. 55-65269 discloses a method of adding a compound such as a surfactant which enhances the permeability to ink. Further, JP-A-55-66976 discloses the use of an ink mainly composed of a volatile solvent. However, although the former method of adding a surfactant or the like to the ink increases the permeability of the ink into the recording paper and improves the fixability and bleeding of the ink to some extent, the coloring material in the ink is Since it penetrates deeply, inconveniences such as a decrease in image density and saturation occur. In addition, the ink spreads in the horizontal direction, resulting in problems such as a decrease in edge sharpness and a decrease in resolution. On the other hand, in the case of the latter method using an ink mainly composed of a volatile solvent, in addition to the same inconvenience as in the former case, clogging occurs due to evaporation of the solvent in the nozzle portion of the recording head. It was easy to do and was not preferable.

Further, in order to improve the above-mentioned problems, there has been proposed a method of depositing a liquid for improving an image in advance on a recording medium before ejecting ink. For example, in JP-A-63-29971, an ink containing an anionic dye is prepared by depositing a liquid containing an organic compound having two or more cationic groups per molecule on a recording medium. The method of recording is disclosed in.
Further, JP-A-64-9279 discloses a method in which an acidic liquid containing succinic acid or the like is deposited on a recording medium and then recording is performed with an ink containing an anionic dye. Further, Japanese Patent Application Laid-Open No. 64-63185 discloses a method of applying a liquid insolubilizing a dye prior to ink recording.

However, in any of the above-mentioned methods, since the bleeding and water resistance of the image are improved by precipitating the dye itself, the effect of suppressing bleeding between the color inks described above is insufficient, and the precipitation Since the dyes are likely to be unevenly distributed on the recording paper, the coverage of the recording paper on the pulp fibers is poor and the uniformity of the image is deteriorated.

[0007]

SUMMARY OF THE INVENTION Therefore, the object of the present invention is to solve the following five problems in view of the above circumstances. That is, the following two points can be cited as problems in performing inkjet recording on plain paper. (1) The print quality is good while having a good fixing property. (2) Sufficient image density is obtained and the uniformity of a solid image is high. In addition, the following three points are raised as problems especially when forming a color image on plain paper. (3) Prevent bleeding. (4) Color reproducibility is good and a high-definition image can be obtained. (5) Make the recorded image completely waterproof.

[0008]

The above object can be achieved by the present invention described below. That is, the present invention is an anionic compound.
Ink-jet recording ink containing
Inkjet recording method used for jet recording
A liquid composition applied to a recording medium by
It is characterized by containing an amine and a cationic surfactant.
It is a liquid composition to be collected. Also, it is preferable to use such a liquid composition.
In a preferred form, the polyamine has the following general formula (I):
Those shown are listed. H ₂ N (CH ₂ CH ₂ NH) _n H (I) (where n = 3 to 30) The present invention also provides yellow, magenta, cyan and black.
Black, red, blue and green ink groups
One or more types of inkjet recording inks
Contains at least cationic substances and polyamines as essential ingredients
I a combination of the liquid composition that is contained in
In addition, each color ink contains at least an anionic group.
A water-soluble dye or at least an anio
Characterized by containing an organic compound and a pigment
It is an ink set. Such a preferred embodiment of the present invention is
The surface tension of the liquid composition is higher than the surface tension of each color ink.
A very low ink set is included. Further, the present invention is
The ink used for recording is used together with the ink containing the nonionic compound.
It contains Liamine and a cationic surfactant.
A liquid composition according to the above-mentioned aspect, and an anio.
Having a combination with an ink containing an ionic compound
It is an ink set characterized by the above. The present invention also provides
An ink jet that forms an inkjet image on a recording medium.
Inkjet recording method
(I) Recording with ink containing anionic compound
A liquid composition for use in polyamines and cations
Composition containing a surface active agent
The object is attached to the recording medium by the inkjet recording method.
And (ii) containing an anionic compound
Ink is attached on the recording medium by the inkjet recording method.
And the steps (i) and (ii) above.
The liquid composition and the ink contact each other on the recording medium.
The inkjet recording method is characterized in that
It In a preferred embodiment of the present invention, the above step (ii) is
An inkjet recording method performed after the step (i), or
Alternatively, the step (i) may be performed by applying the liquid composition to the entire surface of the recording medium.
The ink jet recording method having a step of attaching
Can be mentioned.

[0009]

The function of the liquid composition containing the cationic substance according to the present invention will be described with reference to the drawings. The liquid composition according to the present invention, when used with an ink containing an anionic compound, for example, a dye as a coloring material, when mixed with the ink on the recording paper or at a position penetrating the recording paper,
As shown in (c) of FIG. 9, as the first step of the reaction, a low molecular weight component of the cationic substance contained in the liquid composition, such as a cationic surfactant, and an anion in the ink. The ionic compound causes an association by an ionic interaction, and the dye in the ink instantaneously aggregates and separates from the solution phase.

Next, in the second step of the reaction, an aggregate of an anionic compound and a low molecular weight cationic substance is adsorbed by a high molecular weight component contained in the liquid composition, and thus the coagulation is generated. The size of the collection is even larger (d),
Difficult to enter the gap between fibers of recording paper. As a result, solid-liquid separation occurs, and only the liquid portion permeates into the recording paper (e), so that both improvement in printing quality and improvement in fixing property can be achieved. At the same time, the viscosity of the aggregate formed by the low molecular weight component of the cationic substance, the anionic compound, and the polyamine, which is the high molecular weight component of the cationic substance, generated by the mechanism as described above, increases, Since it does not move along with the movement of the medium, even when adjacent dots are formed with different color inks as in the conventional full-color image formation described above, they do not mix with each other and bleeding occurs. Absent. or,
Since the aggregates are essentially water-insoluble, the water resistance of the formed image is perfect. Further, it also has the effect of improving the light fastness of the image formed by the polymer shielding effect.

[0011]

BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail with reference to the preferred embodiments of the present invention. The liquid composition according to the present invention is a liquid composition containing at least a cationic substance and is characterized by containing polyamine as an essential component. In a more preferable embodiment, at least a cationic surfactant is used as the cationic substance. The ink set according to the present invention is characterized by using the liquid composition according to the present invention as described above,
Preferably, as the colored ink for recording used together with the liquid composition, an ink containing at least a dye containing an anionic group or an ink containing at least an anionic compound and a pigment is used.

The action and effect of the liquid composition according to the present invention are as described above, and a low molecular weight cationic substance contained in the liquid composition and a water-soluble dye containing at least an anionic group contained in the ink, or The anionic compound used with the pigment first forms an aggregate by ionic interaction. In addition, the formation reaction rate of this aggregate needs to be extremely high.

The constituent components of the liquid composition according to the present invention will be described below. Preferred specific examples of the polyamine which is an essential component of the liquid composition according to the present invention include ethyleneamines represented by the following general formula (I), polyethyleneimine represented by the general formula (II), spermidine and spermine. However, the present invention is not limited to these. _{H 2 N (CH 2 CH 2} NH) n H (I) ( where, n = 3 to 30) (However, n = 3 to 20)

Specific examples of the cationic surfactant which is particularly preferably used as the cationic substance constituting the liquid composition according to the present invention include the following. For example, primary, secondary and tertiary amine salt type compounds, specifically, hydrochlorides such as laurylamine, coconut amine, stearylamine, rosinamine and the like; acetates;
Primary ammonium salt type compounds, specifically lauryltrimethylammonium chloride, cetyltrimethylammonium chloride, lauryldimethylbenzylammonium chloride, benzyltributylammonium chloride, benzalkonium chloride, etc .; pyridinium salt type compounds, specifically cetylpyridinium Chloride,
Cetylpyridinium bromide and the like; imidazoline type cationic compounds, specifically 2-heptadecenyl-hydroxyethylimidazoline and the like; ethylene oxide adducts of higher alkylamines, specifically dihydroxyethylstearylamine and the like are preferable.

Further, in the present invention, other p
An amphoteric surfactant that exhibits a cationic property in the H region is also preferably used as the cationic substance. Specifically, for example, an amino acid type amphoteric surfactant; R-NH-CH ₂
Compound of -CH ₂ -COOH type; betaine compounds,
Specific examples include carboxylic acid salt type amphoteric surfactants such as stearyl dimethyl betaine and lauryl dihydroxyethyl betaine, as well as sulfate ester type, sulfonic acid type and phosphoric acid ester type amphoteric surfactants. Of course, when these amphoteric surfactants are used, the liquid composition according to the present invention is adjusted so as to have a pH below their isoelectric point, or this liquid composition is mixed with ink on the recording medium. In this case, it is necessary to adjust the pH so that the pH is below the isoelectric point. Although examples of low molecular weight cationic compounds have been given above as cationic substances, it goes without saying that the cationic substances that can be used in the present invention are not necessarily limited to these.

The amount of the above-mentioned cationic substance contained in the liquid composition according to the present invention is preferably 0.05 to 20% by weight on a weight basis, more preferably 0.5. Although it is in the range of 10% by weight, it is necessary to determine the optimum range depending on the combination of substances used. As the amount of the water-soluble cationic surfactant,
A range of 0.05 to 10% by weight is suitable.

Next, other components constituting the liquid composition according to the present invention will be specifically described. The colorless or light-colored liquid composition according to the present invention generally comprises water, a water-soluble organic solvent, and other appropriate additives in addition to the above-mentioned polyamine and the cationic substance. As the water-soluble organic solvent used at this time, dimethylformamide, amides such as dimethylacetamide, ketones such as acetone, tetrahydrofuran, ethers such as dioxane,
Polyalkylene glycols such as polyethylene glycol and polypropylene glycol, ethylene glycol,
Alkylene glycols such as propylene glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol, hexylene glycol, diethylene glycol, ethylene glycol methyl ether, diethylene glycol monomethyl ether, triethylene glycol monomethyl ether, etc. In addition to lower alkyl ethers of polyhydric alcohols, monohydric alcohols such as ethanol, isopropyl alcohol, n-butyl alcohol and isobutyl alcohol,
Glycerin, N-methyl-2-pyrrolidone, 1,3-dimethyl-imidazolidinone, triethanolamine, sulfolane, dimethylsulfoxide and the like are preferably used. The content of the water-soluble organic solvent is not particularly limited, but is preferably 5 to 60% by weight, more preferably 5 to 40% by weight based on the total weight of the liquid composition.

In addition to the above, the liquid composition according to the present invention may further contain a viscosity adjusting agent, a pH adjusting agent, an antiseptic agent, if necessary.
Additives such as various surfactants, antioxidants, and evaporation promoters may be appropriately mixed. The selection of the surfactant is particularly important in adjusting the permeability of the liquid into the recording medium. The liquid composition according to the present invention is more preferably colorless, but when mixed with ink on a recording medium,
It may be a light-colored ink that does not change the color tone of each color ink. Further, as a suitable range of various physical properties of the liquid composition as described above, at about 25 ° C., the pH is 3 to 12, preferably 3 to 8, more preferably 3 to 5, and the surface tension is 10.
-60 dyn / cm, more preferably 10-40 dyn
/ Cm and the viscosity is 1 to 30 cps. It is what As will be described later, the surface tension of the liquid composition according to the present invention is preferably lower than the surface tension of the ink used with the liquid composition.

Next, the ink constituting the ink set according to the present invention will be described. For the ink used in the present invention, a water-soluble dye containing an anionic group is used as a coloring material, or when a pigment is used as a coloring material, a combination of an anionic compound is used. In addition to the above-mentioned ink used in the present invention, water, a water-soluble organic solvent and other components such as a viscosity modifier, pH
A regulator, an antiseptic, a surfactant, an antioxidant and the like are contained as necessary.

The water-soluble dye containing an anionic group used in the present invention includes a color index (COLO).
There is no particular limitation as long as it is a water-soluble acid dye, direct dye or reactive dye described in UR INDEX).
Further, even those not described in the color index are not particularly limited as long as they have an anionic group such as a sulfone group and a carboxyl group. Of course, the water-soluble dyes referred to herein include those whose solubility is pH-dependent.

As the water-soluble organic solvent contained in the ink containing the water-soluble dye as the coloring material as described above,
The water-soluble organic solvent used in the liquid composition according to the present invention, which is colorless or light-colored as described above, can be similarly used.
The same applies to the preferable range of the content of these water-soluble organic solvents in the ink. Further, the preferable physical property range of the ink is exactly the same as that of the liquid composition. However, regarding the surface tension of the ink, it is preferable that the surface tension of the ink is higher than the surface tension of the liquid composition according to the present invention, because it may be effective in carrying out the image forming method according to the present invention. This is because if the surface tensions of the two are adjusted in this manner, for example, in the printing process, the liquid composition ejected first can have an even wettability of the ink ejected later on the recording medium. It is thought that it will be exerted, but the details are not clear.

When a pigment is used as a coloring material of the ink used in the present invention, the amount of the pigment is 1 to 20% by weight, preferably 2 to 12% by weight based on the total weight of the ink. Used in the range. Specific examples of the pigment used in the present invention include carbon black used as a black ink. For example, carbon black produced by a furnace method or a channel method may be used. Diameter is 15 to 40 mμ, specific surface area by BET method is 50 to 300 m ² / g, DBP oil absorption is 40 to 1
Those having characteristics such as 50 ml / 100 g, volatile content of 0.5 to 10%, and pH value of 2 to 9 are preferably used.
Examples of commercially available products having such characteristics include No.
2300, No. 900, MCF88, No. 33, N
o. 40, No. 45, No. 52, MA7, MA8,
No. 2200B (Made by Mitsubishi Kasei), RAVEN12
55 (Made in Colombia), REGAL400R, RE
GAL330R, REGAL660R, MOGUL L
(Above made by Cabot), Color Black FW
1, COLOR Black FW18, Color
Black S170, Color Black S1
50, Printex 35, Printex U (all manufactured by Degussa) and the like, and any of them can be preferably used.

As the pigment used for the yellow ink, for example, C.I. I. Pigment Yellow
w 1, C.I. I. Pigment Yellow 2,
C. I. Pigment Yellow 3, C.I. I.
Pigment Yellow 13, C.I. I. Pig
ment Yellow 16, C.I. I. Pigmen
Examples of pigments used in magenta ink include C.I. I. Pig
ment Red 5, C.I. I. Pigment Re
d 7, C.I. I. Pigment Red 12, C.I.
I. Pigment Red 48 (Ca), C.I. I.
Pigment Red 48 (Mn), C.I. I. Pi
gment Red 57 (Ca), C.I. I. Pigm
entRed 112, C.I. I. Pigment Re
d122 and the like. Examples of the pigment used for the cyan ink include C.I. I. Pigment Bl
ue 1, C.I. I. Pigment Blue 2,
C. I. Pigment Blue 3, C.I. I. Pig
ment Blue 15: 3, C.I. I. Pigmen
t Blue 16, C.I. I. Pigment Blu
e 22, C.I. I. Vat Blue 4, C.I. I. V
Examples thereof include at Blue 6 and the like, but the present invention is not limited thereto. In addition to the above, it is of course possible to use pigments newly produced for the present invention.

As the dispersant to be contained in the ink when a pigment is used, any water-soluble resin can be used, but the weight average molecular weight is 1,00.
The range of 0 to 30,000 is preferable, and the range of 3,000 to 15,000 is more preferably used. Specific examples of such dispersants include styrene, styrene derivatives, vinylnaphthalene, vinylnaphthalene derivatives, aliphatic alcohol esters of α, β-ethylenically unsaturated carboxylic acids, acrylic acid, acrylic acid derivatives, and maleic acid. , Maleic acid derivative, itaconic acid, itaconic acid derivative, fumaric acid, fumaric acid derivative, vinyl acetate, vinylpyrrolidone, acrylamide,
And a block copolymer composed of at least two or more monomers (at least one of which is a hydrophilic monomer) selected from derivatives thereof, a random copolymer, a graft copolymer, or a copolymer thereof. Salt etc. are mentioned. Alternatively,
Natural resins such as rosin, shellac and starch can also be preferably used. These resins are alkali-soluble resins that are soluble in an aqueous solution in which a base is dissolved.
The water-soluble resin used as the pigment dispersant is preferably contained in the range of 0.1 to 5% by weight based on the total weight of the ink.

Particularly, in the case of an ink containing the above-mentioned pigment, it is preferable that the entire ink is adjusted to be neutral or alkaline. This is preferable because the solubility of the water-soluble resin used as the pigment dispersant can be improved and the ink can be further excellent in long-term storage stability. However, in this case, it may cause corrosion of various members used in the inkjet recording apparatus. Therefore, it is preferable that the pH range is 7 to 10. Examples of the pH adjuster used in this case include various organic amines such as diethanolamine and triethanolamine, inorganic alkali agents such as sodium hydroxide, lithium hydroxide, and alkali metal hydroxides such as potassium hydroxide, Examples include organic acids and mineral acids. The water-soluble resin, which is a pigment and a dispersant as described above, is dispersed or dissolved in an aqueous liquid medium.

A suitable aqueous liquid medium in the ink containing the pigment used in the present invention is a mixed solvent of water and a water-soluble organic solvent, and water is not ordinary water containing various ions, It is preferable to use ion-exchanged water (deionized water).

Examples of the water-soluble organic solvent used by mixing with water include methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol and the like. Alkyl alcohols having 1 to 4 carbon atoms; amides such as dimethylformamide and dimethylacetamide; ketones or keto alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyalkylenes such as polyethylene glycol and polypropylene glycol Glycols; ethylene glycol, propylene glycol, butylene glycol, triethylene glycol,
1,2,6-hexanetriol, thiodiglycol,
Alkylene glycols in which the alkylene group such as hexylene glycol and diethylene glycol contains 2 to 6 carbon atoms; glycerin; ethylene glycol monomethyl (or ethyl) ether, diethylene glycol methyl (or ethyl) ether, triethylene glycol monomethyl (or ethyl) Lower alkyl ethers of polyhydric alcohols such as ethers; N-methyl-2-pyrrolidone,
2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone and the like can be mentioned. Among these many water-soluble organic solvents, polyhydric alcohols such as diethylene glycol and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl (or ethyl) ether are preferable.

The content of the water-soluble organic solvent as described above in the ink is generally 3 to 50% by weight, preferably 3 to 40% by weight based on the total weight of the ink.
Also, the content of water used is 1 of the total weight of the ink.
The range is 0 to 90% by weight, preferably 30 to 80% by weight.

Further, the ink containing the pigment used in the present invention contains, in addition to the above-mentioned components, a surfactant, a defoaming agent, a defoaming agent, in order to obtain an ink having desired physical properties, if necessary. Preservatives and the like can be added as appropriate. In addition to the above pigments, water-soluble dyes such as those described above can be added as appropriate as a coloring material. Further, similarly to the above, when using an ink containing a pigment, it is preferable that the surface tension of the ink is larger than the surface tension of the liquid composition according to the present invention. It is preferable to adjust the surface tension of the ink in such a manner as described above.

As a method for producing an ink containing a pigment as described above, first, the pigment is added to an aqueous medium containing at least a water-soluble resin as a dispersant and water,
After stirring, dispersion is carried out using a dispersion means described later, and if necessary, centrifugal separation is carried out to obtain a desired dispersion liquid. Next, a sizing agent and appropriately selected additive components such as those mentioned above are added to this dispersion, and the mixture is stirred to obtain the ink used in the present invention.

When the above-mentioned alkali-soluble type resin is used as the dispersant, it is necessary to add a base to dissolve the resin. Organic amines such as ethanolamine, diethanolamine, triethanolamine, amine methyl propanol and ammonia, or inorganic bases such as potassium hydroxide and sodium hydroxide are preferably used.

In addition, in the method for producing an ink containing a pigment, it is effective to carry out premixing for 30 minutes or more before stirring and dispersing the aqueous medium containing the pigment. That is, such premixing operation is preferable because it improves wettability of the pigment surface and promotes adsorption of the dispersant on the pigment surface.

The disperser used in the dispersion treatment of the above-mentioned pigment may be any disperser generally used, and examples thereof include a ball mill, a roll mill and a sand mill. Among them, a high speed type sand mill is preferably used, and as such a thing, for example, a super mill, a sand grinder, a bead mill,
Examples thereof include agitator mill, grain mill, dyno mill, pearl mill and cobol mill (all are trade names).

When an ink containing a pigment is used in an ink jet recording method, a pigment having an optimum particle size distribution is used because of the requirement of anti-clogging property and the like, but it has a desired particle size distribution. As a method of obtaining a pigment,
Decrease the size of the crushing media of the disperser, increase the filling rate of the crushing media, lengthen the processing time, slow the discharge speed, classify with a filter or centrifuge after crushing, and these Methods such as a combination of the above methods can be mentioned.

In the present invention, when an ink containing a pigment is used, in addition to the various components described above in the ink, an anionic compound such as an anionic surfactant or an anionic polymer substance is used. Is preferably added. Especially when an anionic compound is not used as a dispersant, it is essential to add such an anionic substance. The addition amount at this time is from 0.05 to
It is 10% by weight, preferably 0.2 to 5% by weight. or,
It is also a preferred embodiment that the amphoteric surfactant is adjusted to a pH below its isoelectric point and contained. As an example of the anionic surfactant used at this time, generally used ones such as carboxylate type, sulfate type, sulfonate type and phosphate type can be preferably used. . Examples of the anionic polymer include alkali-soluble resins, specifically, sodium polyacrylate, and those obtained by copolymerizing acrylic acid with a part of the polymer. Of course, it is not limited to these.

The image forming method according to the present invention will be described. In the image forming method according to the present invention, the liquid composition as described above is attached to the image forming area on the recording medium, or to the image forming area and its vicinity. And the step of ejecting ink containing a dye containing at least an anionic group, or ink containing at least an anionic compound and a pigment as droplets from an ejection orifice onto a recording medium according to a recording signal. (B) is included.

The recording medium used in the above-mentioned image forming method is not particularly limited, and conventionally used so-called plain paper such as copy paper and bond paper is preferably used. Of course, a coated paper specially prepared for ink jet recording and a transparent film for OHP are also suitably used. Further, it can be suitably used for general high-quality paper and glossy paper.

The image forming method according to the present invention may be any method as long as the above-mentioned liquid composition according to the present invention and the ink coexist on a recording medium, and therefore, the liquid composition and the ink. It does not matter which of the above is applied to the recording medium first. The image forming area in the present invention is an area to which ink dots are attached, and the vicinity of the image forming area is an area about 1 to 5 dots outside the area to which ink dots are attached. Refers to.

[0039] As method in which deposition of the liquid composition on a recording medium, for example, but is also considered method in which adhered to the entire surface of the recording medium by a spray or roller or the like, the onset
In the bright, the image forming area where the ink adheres, or intends row by an inkjet method that can only allowed to adhere selectively and uniformly liquid composition image forming area and the vicinity of the image formation region. At this time, various ink jet recording methods can be used, but a particularly preferable method is a method of ejecting droplets by using bubbles generated by thermal energy. The time from the application of the liquid composition to the recording medium to the application of the ink to the recording medium is not particularly limited, but preferably the ink is applied to the recording medium at about the same time or within a few seconds. Preferably.

Next, a recording apparatus preferably used in the image forming method according to the present invention will be described. In the present invention, an inkjet recording method is preferably used in which a recording signal is applied to the ink of the recording head and the generated thermal energy ejects droplets. The structure of the recording head, which is the main part of such an apparatus, is shown in FIGS. 1, 2 and 3.

The head 13 is a heating head 15 having a heating resistor used for heat-sensitive recording, such as glass, ceramic, or plastic in which ink is formed in a flow path (a head is shown in the drawing, but is not limited thereto. Not a thing)
It is obtained by bonding and. The heating head 15 includes a protective film 16 made of silicon oxide or the like, an aluminum electrode 17-
1, 17-2, heating resistor layer 1 formed of nichrome, etc.
8, a heat storage layer 19, and a substrate 20 having a good heat dissipation property such as alumina. The ink 21 reaches the ejection orifice 22, and the pressure P forms a meniscus 23.

Here, when an electric signal is applied to the electrodes 17-1 and 17-2, the area indicated by n of the heating head 15 rapidly generates heat, and air bubbles are generated in the ink 21 in contact therewith, The meniscus is ejected by the pressure, becomes a recording droplet 24 from the orifice 22, and flies toward the recording material 25. FIG. 3 shows a schematic view of a recording head in which a large number of nozzles shown in FIG. 1 are arranged. The recording head is made by closely adhering a glass plate or the like 27 having a large number of flow paths to a heating head 28 similar to that described in FIG. 1 is a sectional view of the head 13 along the ink flow path, and FIG. 2 is a sectional view taken along the line AB of FIG.

FIG. 4 shows an example of an ink jet recording apparatus incorporating the head. In FIG. 4, reference numeral 61 denotes a blade as a wiping member, one end of which is held by a blade holding member to be a fixed end, which is in the form of a wrench lever. The blade 61 is arranged at a position adjacent to the recording area of the recording head, and is configured to move in a direction perpendicular to the moving direction of the recording head to come into contact with the ejection port surface to perform capping. Further, 63 is an ink absorber provided adjacent to the blade 61, and like the blade 61, is held in a form protruding in the moving path of the recording head. The blade 61, the cap 62, and the absorber 63 constitute an ejection recovery unit 64, and the blade 61 and the absorber 63 remove water, dust, and the like from the ink ejection port surface.

Reference numeral 65 denotes a recording head having ejection energy generating means, which ejects ink onto a recording material facing the ejection port surface where ejection ports are arranged for recording, and 66 denotes a recording head in which the recording head 65 is mounted. A carriage for moving 65. The carriage 66 is movably engaged with the guide shaft 67, and a part of the carriage 66 is connected (not shown) to a belt 69 driven by a motor 68. As a result, the carriage 66 can move along the guide shaft 67, and the recording head 65 can move the recording area and its adjacent area. Reference numeral 51 is a paper feed section for inserting a recording material, and 52 is a paper feed roller driven by a motor (not shown). With these configurations, the recording material is fed to the position facing the ejection port surface of the recording head,
As the recording progresses, the paper is ejected to the paper ejecting section provided with the paper ejecting roller 53.

In the above structure, when the recording head 65 returns to the home position after recording is completed, the cap 62 of the head recovery section 64 is retracted from the movement path of the recording head 65, but the blade 61 is projected into the movement path. There is. As a result, the ejection port surface of the recording head 65 is wiped. When the cap 62 comes into contact with the ejection port surface of the recording head 65 to perform capping, the cap 62 moves so as to project into the movement path of the recording head.

When the recording head 65 moves from the home position to the recording start position, the cap 62 and the blade 61 are at the same positions as the above wiping positions. As a result, the ejection opening surface of the recording head 65 is wiped even during this movement. The above-mentioned movement of the recording head to the home position is performed not only at the end of recording and at the time of ejection recovery, but also at a predetermined interval to the home position adjacent to the recording area while the recording head moves in the recording area for recording. However, the wiping is performed along with this movement.

FIG. 5 is a diagram showing an example of an ink cartridge in which the ink is supplied to the head through an ink supply member, for example, a tube. Here, 40 is an ink containing portion containing the supply ink, for example, an ink bag, and a rubber stopper 42 is provided at the tip thereof. By inserting a needle (not shown) into this stopper 42, the ink in the ink bag 40 can be supplied to the head. Four
Reference numeral 4 is an absorber that receives waste ink. As the ink storage portion, it is preferable that the liquid contact surface with the ink is formed of polyolefin, particularly polyethylene. The ink jet recording apparatus used in the present invention is not limited to the above-described head and ink cartridge which are separate bodies, and those in which they are integrated as shown in FIG. 6 are also preferably used.

In FIG. 6, reference numeral 70 denotes a recording unit, in which an ink containing portion for containing ink, for example, an ink absorber is contained, and the ink in the ink absorber has a plurality of orifices. It is configured to be ejected as an ink droplet from the portion 71. As a material for the ink absorber, for example, polyurethane can be used. Reference numeral 72 denotes an atmosphere communication port for communicating the inside of the recording unit with the atmosphere. The recording unit 70 is used instead of the recording head shown in FIG. 4, and is detachable from the carriage 66. In the recording apparatus used in the present invention, an ink jet recording apparatus that applies thermal energy to ink to eject ink droplets has been described above as an example. However, in addition to this, a piezo type ink jet recording apparatus that uses a piezoelectric element may be used. You can use it as well.

When carrying out the recording method of the present invention, for example, a recording device in which five recording heads shown in FIG. 3 are arranged on a carriage is used. FIG. 7 shows an example thereof. Reference numerals 81, 82, 83, and 84 are recording heads for ejecting inks of yellow, magenta, cyan, and black colors, respectively. Reference numeral 85 is a head for ejecting a colorless liquid composition. The head is arranged in the above-mentioned recording device and ejects ink of each color according to a recording signal.
Further, prior to that, the liquid composition is preliminarily attached to a portion where the ink of each color is attached to the recording paper. Although FIG. 7 shows an example in which five recording heads are used,
The present invention is not limited to this, and it is also preferable to use one recording head for yellow, magenta, cyan, black, and colorless liquid as shown in FIG.
Of course, the heads may be arranged so that the recording order of the colorless liquid and the ink is opposite to the above order.

[0050]

[Examples] Examples , comparative examples and reference examples are shown below,
The present invention will be described more specifically. In the text, "part" and "%" are based on weight unless otherwise specified. The weight average molecular weight of the dispersant of the pigment ink was measured by the GPC method using styrene polymer as a standard, and the average particle diameter of the dispersion was measured by the dynamic light scattering method.

Reference Example 1 First, the following components were mixed and dissolved, and then pressure-filtered with a membrane filter (trade name: Fluoropore filter, manufactured by Sumitomo Electric Industries) having a pore size of 0.22 μm, and then N
The pH was adjusted to 5.0 with aOH to obtain A as a colorless liquid composition of this reference example. Ingredients of liquid composition A: pentaethylenehexamine 10 parts, thiodiglycol 10 parts, water 80 parts

(Preparation of Ink I) Next, the following components were mixed, and the pore size was 0.22.
Yellow, magenta, cyan, and black inks Y1, M1, and C1 containing a dye containing an anionic group, which are pressure-filtered with a μm membrane filter (trade name: Fluoropore filter, manufactured by Sumitomo Electric Industries, Ltd.) , B1 were obtained. This Y1, M1, C1 and B1 is used as the recording liquid I.

[0053]

[0054]

[0055]

[0056] constitute an ink set according to this reference example with reference to colorless liquid composition A and the ink I of the present reference example obtained as described above were recorded on PPC paper (manufactured by Canon Inc.). As the inkjet recording apparatus used, the same recording apparatus as shown in FIG.
A color image was formed using one recording head. At this time, the liquid composition A was first ejected and deposited on the recording paper, and then the ink I was deposited. The recording head used here had a recording density of 360 dpi, and the driving condition was a driving frequency of 5 kHz. Also, the ejection volume per dot is yellow, magenta and cyan ink,
For colorless liquid compositions, heads of 45 pl were used, and for black ink, 8 dots per dot were used.
A 0 pl head was used. The recording conditions are the same throughout the examples and comparative examples when the ink containing the dye described below is used. Further, the environmental conditions during the print test are unified to 25 ° C./55% RH.

Example 1 A colorless liquid composition B of the present example consisting of the following components,
Ink I using the same dye as the coloring material used in Reference Example 1
Was used to form an ink set according to the present invention, and recording was performed on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1. Also in this example, the colorless liquid composition B was first ejected and first adhered to the recording paper, and then the ink I was adhered to perform the printing and recording. Ingredients of liquid composition B: triethylenepentamine 10 parts, benzalkonium chloride 1 part, thiodiglycol 10 parts, water 79 parts

Example 2 A colorless liquid composition C of this example consisting of the following components:
Ink I using the same dye as the coloring material used in Reference Example 1
Was used to form an ink set according to the present invention, and recording was performed on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1. Also in this example, the colorless liquid composition C was first ejected and first applied on the recording paper, and then the ink I was applied to perform the printing and recording. Ingredients of liquid composition C -triethylenepentamine 10 parts-lauryltrimethylammonium ammonium chloride 1 part-thiodiglycol 10 parts-water 79 parts

Example 3 A colorless liquid composition D of this example comprising the following components:
Ink I using the same dye as the coloring material used in Reference Example 1
Was used to form an ink set according to the present invention, and recording was performed on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1. Also in this example, the colorless liquid composition D was first ejected to be first deposited on the recording paper, and then the ink I was deposited to perform print recording. Components of Liquid Composition D Hexaethyleneheptamine 5 parts Cetyltrimethylammonium chloride 1.5 parts Thiodiglycol 10 parts Water 83.5 parts

Reference Example 2 Yellow, magenta, cyan and black color inks Y2, M2, C2 and B2 respectively containing a pigment and an anionic compound were obtained as described below. This Y2, M
Ink II was used as Nos. 2, C2 and B2, and the ink set of this reference example was constructed with the colorless liquid composition A used in Reference example 1. Using this ink set, recording was performed on PPC paper (manufactured by Canon). In this reference example, the colorless liquid composition A was first ejected and first applied on the recording paper, and then the ink II was applied to perform printing and recording. The recording head used here had a recording density of 360 dpi, and the driving condition was a driving frequency of 5 kHz. The ejection volume per dot is 45 p for each of the yellow, magenta and cyan inks and the colorless liquid composition.
1 head was used, and for black ink, 60 pl head per dot was used. The recording conditions are the same throughout the examples when the ink containing the pigment described below is used. Further, the environmental conditions during the print test are unified to 25 ° C./55% RH.

(Preparation of Ink II) Black Ink B2 Anionic polymer P-1 (styrene-methacrylic acid-ethyl acrylate, acid value 400, weight average molecular weight 6,0)
00, an aqueous solution with a solid content of 20%, a neutralizing agent: potassium hydroxide) was used as a dispersant, and the following materials were charged into a batch type vertical sand mill (made by AIMEX) and 1 mm diameter glass beads were filled as a medium. The dispersion treatment was performed for 3 hours while cooling with water. The viscosity after dispersion was 9 cps and the pH was 10.0. This dispersion was centrifuged to remove coarse particles, to prepare a carbon black dispersion having a weight average particle diameter of 100 nm.

Composition of carbon black dispersion P-1 aqueous solution (solid content 20%) 40 parts carbon black Mogul L (manufactured by Cablack) 24 parts glycerin 15 parts ethylene glycol monobutyl ether 0.5 parts isopropyl alcohol 3 parts water 135 parts Next, the dispersion obtained above was thoroughly stirred to obtain a black ink B2 for ink jet containing a pigment. The solid content of the final preparation was about 10%.

Yellow ink Y2 anionic polymer P-2 (styrene-acrylic acid-methyl methacrylate, acid value 280, weight average molecular weight 1
1,000%, an aqueous solution with a solid content of 20%, a neutralizing agent: diethanolamine) was used as a dispersant, and the following materials were used to carry out a dispersion treatment in the same manner as in the production of the black ink B2 to obtain a weight average particle diameter. A 103 nm yellow color dispersion was prepared.

Composition of yellow dispersion -P-2 aqueous solution (solid content 20%) 35 parts -C. I. Pigment Yellow 180 (Nova Palm Yellow PH-G, made by Hoechst) 24 parts ・ Triethylene glycol 10 parts ・ Diethylene glycol 10 parts ・ Ethylene glycol monobutyl ether 1.0 part ・ Isopropyl alcohol 0.5 parts ・ Water 135 parts

The yellow dispersion obtained above was sufficiently stirred to obtain an inkjet yellow ink Y2 containing a pigment. The solid content of the final preparation was about 10%.

Cyan Ink C2 Using the anionic polymer P-1 used in the preparation of the black ink B2 as a dispersant, the following materials were used, and the same dispersion treatment as in the case of the above carbon black dispersion was performed. Then, a cyan color dispersion having a weight average particle diameter of 120 nm was produced. Cyan color dispersion composition P-1 aqueous solution (solid content 20%) 30 parts C.I. I. Pigment Blue 15: 3 (Fastgen Blue FGF, Dainippon Ink and Chemicals) 24 parts, glycerin 15 parts, diethylene glycol monobutyl ether 0.5 parts, isopropyl alcohol 3 parts, water 135 parts

The cyan color dispersion obtained above was sufficiently stirred to obtain a cyan ink C2 for ink jet containing a pigment. The solid content of the final preparation was about 9.6%.

Using the anionic polymer P-1 used in the preparation of the magenta ink M2 black ink B2 as a dispersant and the following materials, the same dispersion treatment as in the case of the carbon black dispersion described above. Then, a magenta color dispersion having a weight average particle diameter of 115 nm was produced.

The magenta color dispersion obtained above was sufficiently stirred to obtain a magenta ink M2 for ink jet containing a pigment. The solids content of the final preparation is about 9.2.
%Met.

Example 4 Ink II containing the pigment used in Reference Example 2 ,
The colorless liquid composition B used in Example 1 was used to form an ink set of this example, and this was used to perform recording on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1. In this example, the colorless liquid composition B was first ejected and first applied on the recording paper, and then the ink II was applied to perform printing and recording.

Example 5 Ink II containing the pigment used in Reference Example 2 ,
The colorless liquid composition C used in Example 2 was used to form the ink set of this example, and this was used to perform recording on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1. In this example, the colorless liquid composition C was first ejected and first adhered to the recording paper, and then the ink II was adhered to perform printing recording.

Example 6 Ink II containing the pigment used in Reference Example 2 ,
The ink set of this example was constituted with the colorless liquid composition D used in Example 3 , and recording was performed on PPC paper (manufactured by Canon Inc.) under the same conditions as in Reference Example 1 using this. In this example, the colorless liquid composition D was first ejected and first applied on the recording paper, and then the ink II was applied to perform printing and recording.

Reference Example 3 An ink set of this Reference Example was prepared by using Ink I containing a dye as a coloring material and the colorless liquid composition A used in Reference Example 1, and the ink I was first attached to a recording paper. Then, in the same manner as in Reference Example 1 except that the colorless liquid composition A is post-shot,
Print recording was performed.

Example 7 An ink set of this example was prepared by using the ink I containing a dye as a coloring material and the colorless liquid composition B used in Example 1 , and the ink I was first attached to a recording paper. Then, in the same manner as in Reference Example 1 except that the colorless liquid composition B is post-shot,
Print recording was performed.

Example 8 An ink set of this example was prepared by using the ink I containing a dye as a coloring material and the colorless liquid composition C used in Example 2 , and the ink I was first adhered to a recording paper. Then, in the same manner as in Example 3 except that the colorless liquid composition C is post-applied,
Print recording was performed.

Example 9 An ink set of this example was prepared by using the ink I containing a dye as a coloring material and the colorless liquid composition D used in Example 3 , and the ink I was first attached to a recording paper. Then, printing recording was performed under the same conditions as in Reference Example 1 except that the colorless liquid composition D was post-printed.

Reference Example 4 An ink set of this Reference Example was prepared by using Ink II using a pigment as a coloring material and the colorless liquid composition A used in Reference Example 2 , and ink II was first applied to a recording paper. Then, printing recording was performed under the same conditions as in Reference Example 1 except that the colorless liquid composition A was post-printed.

[0078] Using the colorless liquid composition B used in ink II as Example 4 using Example 1 0 pigment as a colorant, an ink set of the present embodiment, first, deposition of ink II to the recording paper Printing recording was performed under the same conditions as in Reference Example 1 except that the colorless liquid composition B was post-printed.

Example 1 1 Ink II using a pigment as a coloring material and the colorless liquid composition C used in Example 5 were used to prepare an ink set of this example. First, ink II was attached to a recording paper. Then, printing and recording were performed under the same conditions as in Reference Example 1 except that the colorless liquid composition C was post-printed.

Example 1 2 An ink set of this example was prepared by using Ink II using a pigment as a coloring material and the colorless liquid composition D used in Example 6 , and ink II was first attached to a recording paper. Then, printing and recording were performed under the same conditions as in Reference Example 1 except that the colorless liquid composition D was post-printed.

[0081] Except for not using the colorless liquid composition A used in Comparative Example 1 Reference Example 1, printing was performed recording in exactly the same conditions as in Reference Example 1.

[0082]

[Evaluation] Examples 1 to 12, Comparative Example 1 and Reference Example 1
-Each recorded image obtained in Reference Example 4 was evaluated by the following evaluation methods and evaluation criteria. 1. Image density A solid image was formed using a colorless liquid composition and black ink, and the reflection density after standing for 12 hours was measured with a reflection densitometer Macbeth RD915 (manufactured by Macbeth). The evaluation criteria are as follows. ⊚: reflection density of 1.30 or more ◯: reflection density of 1.25 or more and less than 1.30 Δ: reflection density of 1.15 or more and less than 1.25 ×; reflection density of less than 1.15

2. With a liquid composition of the fixability colorless and the yellow and magenta ink, after the formation of the solid image of red, superimposed on the recorded image with another blank in its own weight, transferring the image recorded in the back side of the paper The time until the stain disappears and the dirt does not occur,
The time at the end of recording was set as time zero, and measurement was performed based on this as a measure of fixing property. The evaluation criteria are as follows. ⊚: Fixability is less than 20 seconds ◯: Fixability is 20 seconds or more and less than 30 seconds Δ: Fixability is 30 seconds or more and less than 40 seconds ×; Fixability is 40 seconds or more

3. Character grade Black alphanumeric characters were printed using a colorless liquid composition and black ink, and evaluated visually. When the feathering was hardly noticeable, it was marked with ⊚, when the feathering was slightly conspicuous but there was no practical problem, it was marked with ◯, and when it was lower than that, it was marked with x.

4. Bleeding Canon Color Bubble Jet Printer BJC-8
In the same printing mode as 20J printing mode A (2Pass, one-way printing), a colorless liquid composition and solid portions of yellow, magenta, cyan, and black inks are printed adjacent to each other, and at the boundary portion of each color. The degree of bleeding was visually observed. The case where bleeding hardly occurred was marked with ⊚, the case where bleeding occurred slightly but it was at a level where there was practically no problem was marked with ◯, and the other levels were marked with x.

5. Solid images of water-resistant yellow, magenta, cyan, and black inks were printed, left for 1 hour, and then immersed in tap water at a water temperature of 20 ° C for 5 minutes. Then, remove it from the water, lightly press the filter paper to remove the water on the surface of the recorded image,
It was air dried as it was. Image density (OD value) before water resistance test
And the OD value after the water resistance test, the remaining OD after the water resistance test
The rate was expressed as a percentage and used as a measure of water resistance. yellow,
Among magenta, cyan and black, the one having the lowest water resistance was taken as the water resistance evaluation result. The water resistance evaluation criteria are as follows. ⊚: Residual OD ratio is 80% or more ◯: Residual OD ratio is 70% or more and less than 80% ×; Residual OD ratio is less than 70% Incidentally, the area where the colorless liquid composition adheres to the recording medium in the above evaluation Is the same area as the ink image forming area,
The printing duty is 100% for both the colorless liquid composition and the ink. Further, the printing direction is unidirectional.

[0087] Example for evaluation items described above 1 to Example 1 2, the evaluation results of the obtained image in Comparative Example 1 and Reference Examples 1 to Reference Example 4 are listed in Table 1. As is clear from Table 1, in Examples, fixability, character quality, image density,
An image with good bleeding and water resistance was obtained, whereas in Comparative Example 1, only an image with poor character quality at low density was obtained, and the water resistance of the image was also poor.

[0088]

[0089] Reference Example 5 and colorless liquid composition used in Reference Example 1, the yellow ink in I was used in Reference Example 1, 3 magenta and cyan
A solid image was recorded at 100% duty using colors to form a so-called process black. All printed conditions were the same as in Reference Example 1. Image density at this time,
The evaluation results of the fixability, character quality, water resistance, and bleeding at the boundary between the process black and other colors were all good, confirming the effects of the present invention.

[0090]

As described above, according to the present invention, particularly in the case of performing color ink jet recording on plain paper, it is possible to obtain a high print quality and a sufficient image density while having a high-speed fixing property. Moreover, the uniformity of the solid image is also high, and a high-definition image with good color reproducibility can be obtained with bridging.
Moreover, an excellent ink jet recorded image can be provided in which the excellent image as described above completely satisfies the water resistance.

[Brief description of drawings]

FIG. 1 is a vertical sectional view of a head portion of an inkjet recording apparatus.

FIG. 2 is a cross-sectional view of a head portion of an inkjet recording device.

FIG. 3 is an external perspective view of a head portion of the inkjet recording apparatus.

FIG. 4 is a perspective view showing an example of an inkjet recording apparatus.

FIG. 5 is a vertical sectional view of an ink cartridge.

FIG. 6 is a perspective view of a recording unit.

FIG. 7 is a perspective view showing a recording unit in which a plurality of recording heads used in an embodiment of the present invention are arranged.

FIG. 8 is a perspective view of another recording head used in the present invention.

FIG. 9 is a conceptual diagram showing an image forming method according to the present invention.

[Explanation of symbols]

13: Head 14: Ink grooves 15 and 28: Heating head 16: Protective film 17: Aluminum electrode 18: Heating resistor layer 19: Heat storage layer 20: Substrate 21: Ink 22: Ejection orifice (fine hole) 23: Meniscus 24: Ink droplet 25: Recording material 26: Multi-groove 27: Glass plate 40: Ink bag 42: Rubber stopper 44: Ink absorber 45: Ink cartridge 51: Paper feed section 52: Paper feed roller 52: Paper ejection roller 61: blade 62: cap 63: ink absorber 64: ejection recovery unit 65: recording head 66: carriage 67: guide shaft 68: motor 69: belt 70: recording unit 71: head unit 72: atmosphere communication port

Continuation of the front page (56) Reference JP-A-60-109894 (JP, A) JP-A-60-67190 (JP, A) JP-A-59-43065 (JP, A) JP-A-64-69381 (JP , A) JP 63-315284 (JP, A) JP 63-299970 (JP, A) JP 3-240557 (JP, A) JP 6-92009 (JP, A) (58) Fields investigated (Int.Cl. ⁷ , DB name) B41M 5/00 C09D 11/00

Claims (8)

(57) [Claims] 1. An ink jet containing an anionic compound.
It is applied to the recording medium by the inkjet recording method, which is used for inkjet recording with the inkjet recording ink.
A liquid composition comprising: a polyamine and a cationic surfactant. 2. The liquid composition according to claim 1 , wherein the polyamine is represented by the following general formula (I). _{H 2 N (CH 2 CH 2} NH) n H (I) ( where, n = 3 to 30) 3. A combination of at least one ink- jet recording ink selected from the group of inks of each color of yellow, magenta, cyan, black, red, blue and green, and the liquid composition according to claim 1, and An ink set characterized in that each color ink contains a water-soluble dye containing at least an anionic group, or at least contains an anionic compound and a pigment. 4. The ink set according to claim 3 , wherein the surface tension of the liquid composition is lower than the surface tension of each color ink. 5. A liquid composition according to claim 1 or 2 ,
An ink set comprising a combination with an ink containing an anionic compound. 6. An ink jet recording method for forming an ink jet image on a recording medium , comprising: ( i) applying the liquid composition according to claim 1 or 2.
Tsu DOO recording method by the process is deposited on the recording medium; and, Inkuji ink that contains (ii) an anionic compound
An inkjet recording method , wherein the steps (i) and (ii) are performed so that the liquid composition and the ink are in contact with each other on the recording medium. Method. 7. The ink jet recording method according to claim 6 , wherein step (ii) is performed after step (i). 8. In step (i), the ink jet recording method according to claim 6 or 7 on the entire surface of the recording medium allowed to adhere to the liquid composition.