JP3421258B2 - Coated pigment - Google Patents
Coated pigmentInfo
- Publication number
- JP3421258B2 JP3421258B2 JP31581998A JP31581998A JP3421258B2 JP 3421258 B2 JP3421258 B2 JP 3421258B2 JP 31581998 A JP31581998 A JP 31581998A JP 31581998 A JP31581998 A JP 31581998A JP 3421258 B2 JP3421258 B2 JP 3421258B2
- Authority
- JP
- Japan
- Prior art keywords
- coated
- pigment
- adhesion
- moist feeling
- pigments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】
【0001】
【発明の属する技術分野】本発明は、顔料の表面が2鎖
2親水基含有化合物で被覆処理された被覆顔料に関す
る。
【0002】
【従来の技術】被覆顔料として、従来、金属石鹸、N-
アシルアミノ酸、シリコーン等を被覆した顔料がケーキ
型ファンデーション等に用いられている。金属石鹸被覆
顔料は、耐水性や皮膚に対する付着性にすぐれるが、し
っとり感に欠ける。N-アシルアミノ酸被覆顔料は、し
っとり感をやや有するものの、付着性に劣る。シリコー
ン被覆顔料はすべりにすぐれるものの、しっとり感に欠
ける。
【0003】このように、被覆顔料として、皮膚に対す
る付着性、しっとり感で十分にすぐれるものはまだ開発
されていない。
【0004】
【発明が解決しようとする課題】本発明の目的は、皮膚
に対する付着性にすぐれるとともに、しっとり感、すべ
りにすぐれる被覆顔料を提供することである。
【0005】
【課題を解決するための手段】本発明の目的は、一般式
1
【0006】
【化2】
【0007】(但し、RCOは炭素原子数8から22の
脂肪酸残基であり、AはOHまたはカルボキシル基が置
換してもよいC1〜6のアルキレン鎖であり、nは2〜
6の整数であり、Yはカルボキシル基である。)で示さ
れる2鎖2親水基含有化合物のMg、Ca、Zn、C
o、Al、Ti、Fe、Zrから選択される多価金属塩
で被覆処理された被覆顔料によって達成される。
【0008】
【発明の実施の形態】本発明の被覆物質の遊離酸、およ
び水溶性塩は特開平8-311003号公報によって公
知である。また、本発明の被覆物質の多価金属塩は、こ
の水溶性塩(ナトリウム、カリウム、アンモニウム、ト
リエタノールアミンなど)と水溶性多価金属塩との組み
合わせによる複合塩として容易に得られる。水溶性多価
金属塩としては、MgCl2,MgSO4,CaCl2Z
nCl2,ZnSO4,AlCl3,TiCl4,FeCl
3,FeSO4,ZrOCl2,CoCl2が挙げられる。
【0009】本発明で適用される顔料は、タルク、カオ
リン、マイカ、セリサイト、硫酸バリウム、炭酸カルシ
ウム、炭酸マグネシウム、ケイ酸アルミ二ウム、ケイ酸
マグネシウム、酸化チタン等のよく知られている顔料す
べてである。粒径は問わない。
【0010】以上の被覆物質でこれらの顔料を被覆処理
する方法は、特許第2788085号公報に記載されて
いる公知のものである。尚、これらの被覆顔料は、基礎
化粧品、パウダーファンデーション、リクイドファンデ
ーション、アイシャドー、口紅、ネイルカラー等のメイ
クアップ化粧料、入浴剤に好適に配合される。
【0011】
【実施例】以下、実施例に記載の評価試験の方法は次の
通りである。
実用特性試験(皮膚に対する付着性、しっとり感)
専門検査員10人による実用テストで調べた。皮膚に対す
る付着性、しっとり感のスコアは極めてよい(5点)、
よい(4点)、普通(3点)、悪い(2点)、極めて悪
い(1点)の5段階に評価し、10名のスコアの平均値
を求め、次のように表示した。
−−−−−−−−−−−−−−−−−−−
スコアの平均値 付着性、しっとり感
3.8を超える ○
2.5〜3.8 △
2.5未満 ×
−−−−−−−−−−−−−−−−−−−
【0012】実施例1 エチレンジアミン−N,N−ジ
ステアロイル−N,N−ジコハク酸ジアルミニウムで被
覆処理したタルクエチレンジアミン−N,N−ジステア
ロイル−N,N−ジコハク酸ジナトリウム40gを60
℃の水10リットルに溶解し、これにタルク1kgを懸
濁した。この中に硫酸アルミニウムの5%水溶液100
ミリリットルを20分かけて送液ポンプにより加えた。
その後、20分間攪拌し、ろ過、水洗し、110℃にて
乾燥した。これを解砕し、エチレンジアミン−N,N−
ジコハク酸アルミニウム被覆処理タルクを得た。
【0013】比較例1 N−ステアロイル−L−アスパ
ラギン酸アルミニウムで被覆処理したタルク
エチレンジアミン−N,N−ジステアロイル−N,N−
ジコハク酸ジナトリウムの代わりにN−ステアロイル−
L−アスパラギン酸モノナトリウムを用いる他は実施例
1と同様にして処理顔料を製造した。
【0014】
【0015】表1に実施例1、比較例1で得た処理顔料
を評価した結果を示す。
【0016】
【表1】【0017】実施例1の処理顔料は、比較例1で得た処
理顔料よりも皮膚に対する付着性、しっとり感の点で顕
著に優れている。
【0018】応用例1 油性ファンデーション
酸化チタン100g,タルク10g、マイカ10g、ベン
ガラ10g、黄酸化鉄20g、黒酸化鉄3gを水1リッ
トルに懸濁させた。これに塩化マグネシウム1.4gを
溶解させた後、エチレンジアミン−N,N−ジステアロ
イル−N,N−ジコハク酸ジナトリウムの4.5%水溶
液200gを20分間で均一に添加した。さらに20分
間攪拌後、ろ過、水洗し、80℃にて噴霧乾燥した。次
いで,ヘンシェルミキサーにて3分間混合し、エチレン
ジアミン−N,N−ジステアロイル−N,N−ジコハク
酸マグネシウムで被覆処理混合顔料を得た。これを油性
ファンデーションに応用した。配合量は重量%である。
成分A:被覆処理混合顔料 40.0
成分B:流動パラフィン 25.8
パルミチン酸イソプロピル 15.0
ソルビタンモノオレート 3.0
マイクロクリスタンワックス 8.0
オゾケライト 7.0
キャンデリラロウ 1.0
防腐剤 0.2
成分C:香料 適量
成分Bを加熱・混合し、均一にした。これに成分Aを加
え、混合物をロールミルで練った。これを再融解し、攪
拌下に冷却し、60℃にて成分Cを加え、容器に流し込
み、放冷して固めた。この油性ファンデーションは皮膚
に対する付着性、しっとり感の点で顕著にすぐれてい
た。
【0019】
【発明の効果】以上記載の通り、本発明は皮膚に対する
付着性、しっとり感の点で顕著にすぐれる被覆処理顔料
を提供することが明らかである。Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coated pigment whose surface is coated with a compound having two chains and two hydrophilic groups. 2. Description of the Related Art Metallic soap, N-
Pigments coated with acylamino acids, silicones, and the like are used in cake-type foundations and the like. Metallic soap-coated pigments are excellent in water resistance and adhesion to skin, but lack moist feeling. N-acylamino acid-coated pigments have a slightly moist feeling but are poor in adhesion. Although silicone-coated pigments are excellent in slipperiness, they lack moist feeling. [0003] As described above, as a coating pigment, a pigment having sufficiently excellent adhesion to skin and moist feeling has not yet been developed. [0004] It is an object of the present invention to provide a coated pigment which is excellent in adhesion to the skin, and which has excellent moist feeling and slipperiness. SUMMARY OF THE INVENTION The object of the present invention is to provide a compound of the general formula 1 (Where RCO is a fatty acid residue having 8 to 22 carbon atoms, A is OH or a C1-6 alkylene chain which may be substituted by a carboxyl group, and n is 2 to 2)
6 is an integer, and Y is a carboxyl group . ), Mg, Ca, Zn, C
This is achieved by a coated pigment coated with a polyvalent metal salt selected from o, Al, Ti, Fe, and Zr. [0008] The free acid and the water-soluble salt of the coating substance of the present invention are known from JP-A-8-311003. Further, the polyvalent metal salt of the coating substance of the present invention can be easily obtained as a complex salt obtained by combining this water-soluble salt (eg, sodium, potassium, ammonium, triethanolamine) and a water-soluble polyvalent metal salt. Examples of the water-soluble polyvalent metal salt include MgCl 2 , MgSO 4 , and CaCl 2 Z.
nCl 2 , ZnSO 4 , AlCl 3 , TiCl 4 , FeCl
3 , FeSO 4 , ZrOCl 2 , CoCl 2 . The pigments used in the present invention include well-known pigments such as talc, kaolin, mica, sericite, barium sulfate, calcium carbonate, magnesium carbonate, aluminum silicate, magnesium silicate and titanium oxide. Is all. The particle size does not matter. The method of coating these pigments with the above coating materials is a known method described in Japanese Patent No. 2788085. These coated pigments are suitably blended in basic cosmetics, powder foundation, liquid foundation, eye shadow, lipstick, nail color, and other makeup cosmetics and bath additives. EXAMPLES The method of the evaluation test described in the examples is as follows. Practical property test (adhesion to skin, moist feeling) It was examined by a practical test by 10 professional inspectors. Very good adhesion (5 points)
Evaluation was made on a five-point scale of good (4 points), normal (3 points), bad (2 points), and extremely bad (1 point), and the average value of the scores of the ten people was calculated and displayed as follows. −−−−−−−−−−−−−−−−−−−− Average score value Adhesion, moist feeling exceeds 3.8 ○ 2.5 to 3.8 △ less than 2.5 × −−− EXAMPLE 1 Talcethylenediamine-N, N-coated with ethylenediamine-N, N-distearoyl-N, N-dialuminum disuccinate Disodium disodium-N, N-disuccinate disodium 40g 40 g
The resultant was dissolved in 10 liters of water at 10 ° C., and 1 kg of talc was suspended therein. 5% aqueous solution of aluminum sulfate 100
Milliliters were added over 20 minutes via the pump.
Thereafter, the mixture was stirred for 20 minutes, filtered, washed with water, and dried at 110 ° C. This is crushed and ethylenediamine-N, N-
A talc treated with aluminum disuccinate was obtained. Comparative Example 1 Talcethylenediamine-N, N-distearoyl-N, N-coated with aluminum N-stearoyl-L-aspartate
N-stearoyl- in place of disodium disuccinate
A treated pigment was produced in the same manner as in Example 1 except that monosodium L-aspartate was used . [0015] Table 1 shows the results of evaluation of the treated pigments obtained in Example 1 and Comparative Example 1 . [Table 1] The treated pigment of Example 1, adhesion to the skin than treated pigment obtained in Comparative Example 1, are remarkably superior in terms of moist feeling. Application Example 1 100 g of an oily foundation titanium oxide, 10 g of talc, 10 g of mica, 10 g of red iron oxide, 20 g of yellow iron oxide, and 3 g of black iron oxide were suspended in 1 liter of water. After 1.4 g of magnesium chloride was dissolved therein, 200 g of a 4.5% aqueous solution of disodium ethylenediamine-N, N-distearoyl-N, N-disuccinate was uniformly added over 20 minutes. After stirring for further 20 minutes, the mixture was filtered, washed with water, and spray-dried at 80 ° C. Then, the mixture was mixed with a Henschel mixer for 3 minutes to obtain a mixed pigment coated with ethylenediamine-N, N-distearoyl-N, N- magnesium disuccinate. This was applied to an oily foundation. The compounding amount is% by weight. Ingredient A: Coated mixed pigment 40.0 Ingredient B: Liquid paraffin 25.8 Isopropyl palmitate 15.0 Sorbitan monooleate 3.0 Microcristan wax 8.0 Ozokerite 7.0 Candelilla wax 1.0 Preservative 0.2 Ingredient C: Fragrance did. Component A was added thereto, and the mixture was kneaded with a roll mill. This was re-melted, cooled under stirring, added with component C at 60 ° C, poured into a container, and allowed to cool to solidify. This oily foundation was remarkably excellent in adhesion to the skin and moist feeling. As described above, it is apparent that the present invention provides a coated pigment which is remarkably excellent in terms of adhesion to skin and moist feeling.
Claims (1)
あり、AはOHまたはカルボキシル基が置換してもよい
C1〜6のアルキレン鎖であり、nは2〜6の整数であ
り、Yはカルボキシル基である。)で示される2鎖2親
水基含有化合物のMg、Ca、Zn、Co、Al、T
i、Fe、Zrから選択される多価金属塩で被覆処理さ
れた被覆顔料。(57) [Claims] [Claim 1] [Formula 1] (Where RCO is a fatty acid residue having 8 to 22 carbon atoms, A is an OH or C1-6 alkylene chain which may be substituted by a carboxyl group, n is an integer of 2-6, and Y is Is a carboxyl group .) Mg, Ca, Zn, Co, Al, T
A coated pigment coated with a polyvalent metal salt selected from i, Fe, and Zr.