JP3381436B2 - Black pigment composition - Google Patents
Black pigment compositionInfo
- Publication number
- JP3381436B2 JP3381436B2 JP33901694A JP33901694A JP3381436B2 JP 3381436 B2 JP3381436 B2 JP 3381436B2 JP 33901694 A JP33901694 A JP 33901694A JP 33901694 A JP33901694 A JP 33901694A JP 3381436 B2 JP3381436 B2 JP 3381436B2
- Authority
- JP
- Japan
- Prior art keywords
- black
- weight
- parts
- pigment composition
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、絵の具、ポスターカラ
ーなどに使用する黒色顔料組成物に関する。特に、黒さ
に優れた黒色顔料組成物に関する。
【０００２】
【従来の技術】従来、絵の具、ポスターカラーなどに使
用する黒色顔料組成物は、着色材であるカーボンブラッ
クと、増量材や隠蔽材として用いる炭酸カルシウムやシ
リカ等の体質顔料と、定着剤や展色剤として用いるアラ
ビアガム、デキストリンなどの水溶性高分子と、水とを
含むものである。
【０００３】
【発明が解決しようとする課題】上記黒色顔料組成物
は、画用紙、ケント紙などに塗布した時、黒さが満足な
ものではなく、特に塗布跡が乾いた時、黒さが低下して
しまう問題点がある。この問題を解決するためには、黒
さにおいて最も優れているアニリンブラックを併用する
事も考えられるが、アニリンブラックは、重金属を含む
ため、安全性の面で使用できなくなる事が考えられる。
本発明は、安全性の面でも問題なく、黒さに優れる黒色
顔料組成物を得る事を課題とする。
【０００４】
【課題を解決するための手段】本発明は、ボーンブラッ
ク１６〜２５重量％と、鉄黒８〜１５重量％と、カーボ
ンブラック０．５〜２重量％と、水溶性高分子と、湿潤
剤と、水とを少なくとも含む黒色顔料組成物を要旨とす
る。
【０００５】以下、本発明を詳細に説明する。着色材
は、ボーンブラック、鉄黒、カーボンブラックの３種類
の黒色顔料を併用する。ボーンブラックは、象牙や獣の
骨を蒸し焼きにして、水洗いし、精製したもので、主成
分は、燐酸カルシウムであり、他に炭酸カルシウム、炭
素が含まれている。その使用量は、黒色顔料組成物全量
に対して１６〜２５重量％が必要である。
【０００６】鉄黒は四三酸化鉄であり、ベンガラを水蒸
気を含む水素で還元して作られ、粒子は、大きく赤味の
黒さを呈している黒色顔料である。その使用量は、黒色
顔料組成物全量に対して８〜１５重量％が必要である。
【０００７】カーボンブラックは、天然ガスないし液状
炭化水素の不完全燃焼または熱分解によって得られ、大
変着色力が優れた黄身の黒さを呈している黒色顔料であ
る。その使用量は、黒色顔料組成物全量に対して０．５
〜２重量％が必要である。
【０００８】
【０００９】水溶性高分子は、定着剤及び展色剤として
使用するものである。膠、アラビアゴム、デキストリン
等の天然水溶性高分子やカルボキシメチルセルロース、
ヒドロキシエチルセルロース等の半合成水溶性高分子、
ポリビニルアルコール等の合成水溶性高分子が使用でき
る。その使用量は黒色顔料組成物全量に対して５〜２０
重量％が好ましい。
【００１０】湿潤剤は、凍結防止剤、再溶解性向上剤な
どとして使用するものであって、グリセリン、エチレン
グリコール、ジエチレングリコール、プロピレングリコ
ール、ジプロピレングリコール、ソルビトール、ソルビ
タン等が挙げられる。その使用量は、黒色顔料組成物全
量に対して３〜１０重量％が好ましい。
【００１１】水は、主溶剤として用いる。
【００１２】尚、上記成分の外、必要に応じて炭酸カル
シウム、シリカ粉などの体質顔料、防腐剤、防黴剤、防
錆剤、消泡剤などの添加剤を適宜用いても良い。
【００１３】本発明の黒色顔料組成物は、上記成分を三
本ロールミルや横型ボールミル等の分散機にて混合分散
することにより容易に得ることができる。
【００１４】
【作用】本発明に係る黒色顔料組成物では、着色材とし
て１６〜２５重量％のボーンブラックと、８〜１５重量
％の鉄黒と、０．５〜２重量％のカーボンブラックとを
併用することにより、ボーンブラックの光沢のない黒さ
と鉄黒の赤味の黒さとカーボンブラックの着色力のある
黒さとが混ざり合い、さらに鉄黒の粒子が大きいため画
用紙への顔料の浸透を防止する目止め効果により相乗的
に黒さが向上すると考えられる。
【００１５】
【実施例】以下に実施例を説明する。実施例は全て水彩
絵の具で示したが、本発明はこれに限定されるものでは
ない。
実施例１
ボーンブラック（Ｃ.Ｉ.７７２６７） ２０重量部
鉄黒（Ｃ.Ｉ.７７４９９） １０重量部
カーボンブラック（ファーネスブラック）（Ｃ.Ｉ.７７２６６） １重量部
アラビアゴム １５重量部
デキストリン ７重量部
グリセリン ６重量部
水 ３６．５重量部
シリカ粉（Ｃ.Ｉ.７７８１１） ４重量部
防腐剤 ０．５重量部
上記成分をラボミキサーに入れ、１５分間撹拌した後、
三本ロールミルにて３回通しを行い黒色の水彩絵の具を
得た。
【００１６】実施例２
ボーンブラック（Ｃ.Ｉ.７７２６７） １９重量部
鉄黒（Ｃ.Ｉ.７７４９９） １１重量部
カーボンブラック（チャンネルブラック）（Ｃ.Ｉ.７７２６６） １重量部
アラビアゴム ７重量部
デキストリン ６重量部
グリセリン ４重量部
水 ４７．５重量部
シリカ粉（Ｃ.Ｉ.７７８１１） ４重量部
防腐剤 ０．５重量部
上記成分をラボミキサーに入れ、１５分間撹拌した後、
三本ロールミルにて３回通しを行い黒色の水彩絵の具を
得た。
【００１７】実施例３
ボーンブラック（Ｃ.Ｉ.７７２６７） １６．５重量部
鉄黒（Ｃ.Ｉ.７７４９９） １３重量部
カーボンブラック（ファーネスブラック）（Ｃ.Ｉ.７７２６６）１．５重量部
アラビアゴム １３重量部
デキストリン ７重量部
グリセリン ３重量部
エチレングリコール ３重量部
水 ３２．５重量部
炭酸カルシウム（Ｃ.Ｉ.７７２２０） １０重量部
防腐剤 ０．５重量部
上記成分をラボミキサーに入れ、１５分間撹拌した後、
三本ロールミルにて３回通しを行い黒色の水彩絵の具を
得た。
【００１８】比較例１
実施例１のカーボンブラックを鉄黒に変えた以外は、実
施例１と同様になして、黒色の水彩絵具を得た。
【００１９】比較例２
実施例２のボーンブラックを鉄黒に変えた以外は、実施
例２と同様になして、黒色の水彩絵の具を得た。
【００２０】比較例３
ボーンブラック（Ｃ.Ｉ.７７２６７） １８重量部
カーボンブラック（ファーネスブラック）（Ｃ.Ｉ.７７２６６） ５重量部
アラビアゴム １３重量部
デキストリン ７重量部
グリセリン ３重量部
エチレングリコール ３重量部
水 ４０．５重量部
炭酸カルシウム （Ｃ.Ｉ.７７２２０） １０重量部
防腐剤 ０．５重量部
上記成分をラボミキサーに入れ、１５分間撹拌した後、
三本ロールミルにて３回通しを行い黒色の水彩絵の具を
得た。
【００２１】上記、実施例１〜３、比較例１〜３で得た
黒色の水彩絵の具について試験を行った。結果を表１に
示す。
【００２２】
【表１】
【００２３】※１明度（Ｖ）
上記、実施例及び比較例で得た水彩絵具と水とを重量比
２：１で混合し、画筆で画用紙に面塗りを行い、乾燥
後、カラーコンピューター（ＳＭ−４；スガ試験機
（株）製）により明度（Ｖ）を測定した。Ｖの値は小さ
い程、黒い。
【００２４】※２ 筆ムラ試験
上記、実施例及び比較例で得た水彩絵具と水とを重量比
２：１で混合したものを画筆で画用紙に面塗りを行い、
乾燥後目視で判定した。
○：筆ムラなし
×：筆ムラあり
【００２５】
【発明の効果】以上、詳細に説明したように、本発明に
係る黒色顔料組成物は、安全性の面で問題がなく、塗布
した場合、筆ムラが無く、黒さに優れたものである。Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a black pigment composition used for paints, poster colors and the like. In particular, it relates to a black pigment composition having excellent blackness. [0002] Conventionally, a black pigment composition used for paints, poster colors and the like has been prepared by fixing carbon black as a coloring material and extenders such as calcium carbonate and silica as fillers and hiding materials. It contains a water-soluble polymer such as gum arabic and dextrin used as an agent and a vehicle, and water. [0003] When the above black pigment composition is applied to drawing paper, Kent paper, etc., the blackness is not satisfactory. There is a problem. In order to solve this problem, it is conceivable to use aniline black, which is the most excellent in blackness, in combination. However, aniline black contains heavy metals, and thus may not be used in terms of safety.
An object of the present invention is to obtain a black pigment composition having excellent blackness without any problem in terms of safety. SUMMARY OF THE INVENTION The present invention relates to a method for producing 16-25% by weight of bone black, 8-15% by weight of iron black, 0.5-2% by weight of carbon black, and a water-soluble polymer. The gist of the present invention is a black pigment composition containing at least a humectant and water. Hereinafter, the present invention will be described in detail. As the coloring material, three kinds of black pigments of bone black, iron black and carbon black are used in combination. Bone black is obtained by steaming, washing, and purifying ivory and animal bones. The main component is calcium phosphate, and further contains calcium carbonate and carbon. The used amount thereof is required to be 16 to 25% by weight based on the total amount of the black pigment composition . [0006] Iron black is triiron tetroxide, which is made by reducing red iron oxide with hydrogen containing water vapor, and the particles are black pigments having a large reddish black color. The used amount is required to be 8 to 15% by weight based on the total amount of the black pigment composition . [0007] Carbon black is a black pigment which is obtained by incomplete combustion or thermal decomposition of natural gas or liquid hydrocarbon, and has a very good coloring power and exhibits a yolk blackness. The amount used is 0.5 to the total amount of the black pigment composition.
~ 2% by weight is required. [0008] The water-soluble polymer is used as a fixing agent and a vehicle. Glue, gum arabic, natural water-soluble polymers such as dextrin and carboxymethylcellulose,
Semi-synthetic water-soluble polymers such as hydroxyethyl cellulose,
Synthetic water-soluble polymers such as polyvinyl alcohol can be used. The amount used is 5 to 20 with respect to the total amount of the black pigment composition.
% By weight is preferred. The wetting agent is used as an antifreezing agent, a re-dissolving agent, etc., and includes glycerin, ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, sorbitol and sorbitan. The use amount thereof is preferably 3 to 10% by weight based on the total amount of the black pigment composition. Water is used as the main solvent. In addition to the above components, if necessary, extenders such as calcium carbonate and silica powder, and additives such as preservatives, fungicides, rust preventives, and defoamers may be appropriately used. The black pigment composition of the present invention can be easily obtained by mixing and dispersing the above components with a disperser such as a three-roll mill or a horizontal ball mill. According to the black pigment composition of the present invention, 16 to 25% by weight of bone black is used as a coloring material, and 8 to 15 % by weight.
% Of iron black and 0.5 to 2% by weight of carbon black combine with the non-glossy black of bone black, the reddish black of iron black and the black of carbon black coloring. It is considered that the black particles are synergistically improved due to the effect of preventing the pigment from penetrating into the drawing paper because the iron black particles are large. An embodiment will be described below. Although all the embodiments are shown with watercolors, the present invention is not limited to this. Example 1 Bone black (CI.77267) 20 parts by weight Iron black (CI.77499) 10 parts by weight Carbon black (furnace black) (CI.77266) 1 part by weight Arabic gum 15 parts by weight Dextrin 7 Parts by weight Glycerin 6 parts by weight Water 36.5 parts by weight Silica powder (CI.77811) 4 parts by weight Preservative 0.5 parts by weight Put the above ingredients in a lab mixer, stir for 15 minutes,
The mixture was passed through a three-roll mill three times to obtain a black watercolor paint. Example 2 Bone black (CI. 77267) 19 parts by weight Iron black (CI. 77499) 11 parts by weight Carbon black (channel black) (CI. 77266) 1 part by weight Arabic gum 7 parts by weight Parts Dextrin 6 parts by weight Glycerin 4 parts by weight Water 47.5 parts by weight Silica powder (C.I.77811) 4 parts by weight Preservative 0.5 parts by weight Put the above ingredients in a laboratory mixer, stir for 15 minutes,
The mixture was passed through a three-roll mill three times to obtain a black watercolor paint. Example 3 16.5 parts by weight of bone black (CI. 77267) 13 parts by weight of iron black (CI. 77499) 1.5 parts by weight of carbon black (furnace black) (CI. 77266) Gum arabic 13 parts by weight Dextrin 7 parts by weight Glycerin 3 parts by weight Ethylene glycol 3 parts by weight Water 32.5 parts by weight Calcium carbonate (CI. 77220) 10 parts by weight Preservative 0.5 parts by weight Put the above ingredients into a laboratory mixer After stirring for 15 minutes,
The mixture was passed through a three-roll mill three times to obtain a black watercolor paint. Comparative Example 1 A black watercolor was obtained in the same manner as in Example 1 except that carbon black in Example 1 was changed to iron black. Comparative Example 2 A black watercolor was obtained in the same manner as in Example 2 except that bone black in Example 2 was changed to iron black. Comparative Example 3 Bone black (CI. 77267) 18 parts by weight Carbon black (furnace black) (CI. 77266) 5 parts by weight Arabic gum 13 parts by weight Dextrin 7 parts by weight Glycerin 3 parts by weight Ethylene glycol 3 Parts by weight Water 40.5 parts by weight Calcium carbonate (CI. 77220) 10 parts by weight Preservative 0.5 parts by weight Put the above ingredients in a lab mixer, stir for 15 minutes,
The mixture was passed through a three-roll mill three times to obtain a black watercolor paint. Tests were conducted on the black watercolors obtained in Examples 1 to 3 and Comparative Examples 1 to 3 above. Table 1 shows the results. [Table 1] * 1 Lightness (V) The watercolor paints obtained in the above Examples and Comparative Examples were mixed with water at a weight ratio of 2: 1, and the drawing paper was painted on a drawing paper, dried, and then dried with a color computer (SM). -4; manufactured by Suga Test Instruments Co., Ltd.). The smaller the value of V, the darker the black. * 2 Brush unevenness test A mixture of the watercolor paints obtained in the above Examples and Comparative Examples and water at a weight ratio of 2: 1 was painted on a drawing paper with a paintbrush.
It was visually determined after drying. ○: no brush unevenness ×: brush unevenness As described above in detail, the black pigment composition according to the present invention has no problem in terms of safety. There is no brush unevenness and it is excellent in blackness.
フロントページの続き (56)参考文献 特開 平４−225076（ＪＰ，Ａ) 特開 昭63−199775（ＪＰ，Ａ) 特開 昭58−104965（ＪＰ，Ａ) 特開 平４−139266（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C09D 17/00 C09D 7/12 Continuation of front page (56) References JP-A-4-225076 (JP, A) JP-A-63-199775 (JP, A) JP-A-58-104965 (JP, A) JP-A-4-139266 (JP, A) , A) (58) Field surveyed (Int. Cl. 7 , DB name) C09D 17/00 C09D 7/12
Claims (1)
黒８〜１５重量％と、カーボンブラック０．５〜２重量
％と、水溶性高分子と、湿潤剤と、水とを少なくとも含
む黒色顔料組成物。(57) [Claims 1] Bone black 16 to 25% by weight , iron black 8 to 15% by weight , carbon black 0.5 to 2 % by weight
% , A water-soluble polymer, a wetting agent, and water.