JP3301892B2 - Ground coil device for magnetic levitation railway - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a ground coil device for a magnetic levitation railway having a propulsion coil and a levitation coil in a concrete track.

[0002]

2. Description of the Related Art FIG.
JP-A-5-276607 and JP-A-5-3047
No. 61 is a sectional view of a conventional ground coil device of a magnetically levitated railway, and FIGS. 7 and 8 are sectional views showing a main part of FIG.

FIGS. 6 to 8 show a side wall 1a and a bottom wall 1b.
Thus, a concrete track 1 having a U-shaped cross section is formed. Then, a propulsion coil 2 for generating a propulsion force of a vehicle (not shown) is connected to a side wall 1 a by a fastening means 4 via a spacer 3.
It is fixed to. A levitation coil 5 for guiding the levitation of a vehicle (not shown) is arranged closer to the center of the concrete track 1 than the propulsion coil 2 and is fixed to the side wall 1a by fastening means 6. The propulsion coil 2 has a conductor 2a formed of an epoxy resin jacket 2.
b. The spacer 3 is formed of a short glass fiber reinforced resin of a sheet molding compound (hereinafter, referred to as SMC). Further, the flying coil 5 is formed by covering the outer periphery of the conductor 5a with a jacket 5b formed of SMC. Incidentally, SMC, for example, a compound of a thermosetting polyester resin and a short glass fiber base material,
In the form of a sheet having a thickness of about 2 mm, in consideration of the fluidity in a mold at the time of heating and pressure molding, generally, short glass fibers of about 3 to 6 mm (maximum 25 mm) are used. It is selected to contain 30 wt% .

[0004]

The ground coil device of a conventional magnetic levitation railway is configured as described above.
Since the density of the glass fiber of the SMC tends to decrease due to the resin flowing during the heating and pressure molding,
There is a problem that there is variation in mechanical strength, and it is difficult to secure a sufficient margin against external force.

[0005] The present invention has been made to solve the above problems, and an object of the present invention is to provide a ground coil device of a magnetic levitation railway capable of improving mechanical strength.

[0006]

According to the first aspect of the present invention, there is provided a ground coil device for a magnetic levitation type railway, in which a vehicle having a U-shaped cross section including both side walls and a bottom wall has a vehicle inside a side wall. The levitation coil that generates the propulsion force is fixed to the side wall, and the levitation coil that guides the levitation of the vehicle is placed on the center side of the concrete track from the propulsion coil and fixed to the side wall. The jacket of the coil is formed of a continuous glass fiber reinforced resin in which continuous glass fibers are arranged in a spiral .

According to a second aspect of the present invention, there is provided a ground coil device for a magnetically levitated railway according to the first aspect, wherein the content of the continuous glass fiber of the continuous glass fiber reinforced resin is 30 wt. % To 40 wt% ,
It is a non-dispersed one.

[0008]

FIG. 1 is a sectional view showing an embodiment of the invention, FIG. 2 is a front view taken along the line II-II in FIG.
3 is a front view as seen from the line III-III in FIG. 1, FIG. 4 is a sectional view along the line IV-IV in FIG. 2, and FIG. 5 is a sectional view along the line VV in FIG.

In FIGS. 1 to 5, reference numeral 7 denotes a concrete track having a U-shaped cross section, which is constituted by a side wall 7a and a bottom wall 7b. Reference numeral 8 denotes a propulsion coil fixed to the inside of the side wall 7a of the concrete track 7 with a spacer 9 described later.
Is covered with a jacket 8b formed of epoxy resin. 9 is a spacer formed of SMC of short glass fiber reinforced resin,
The propulsion coil 8 is pressed and fixed to the side wall 7a of the concrete track 7 by fastening means 14 described later. 10 is an insert buried in the side wall 7a, 11 is a bolt screwed to the insert 10, 12 is a washer, and 13 is a nut screwed to the bolt 11. The spacer 8 is fixed to the side wall 7a and is propelled through the spacer 8. The coil 8 is fixed to the side wall 7a. In addition, the fastening means 14 is comprised by 11-13. Reference numeral 15 denotes a levitation coil arranged on the center side of the concrete track 7 from the propulsion coil 8, and covers the conductor 15a with a jacket 15b formed of L-SMC made of continuous glass fiber reinforced resin. 16
Is an insert buried in the side wall 7a of the concrete track 7, 17 is a bolt screwed into the insert 16,
The levitation coil 15 is pressed and fixed to the side wall 7a through the fin 8. The fastening means 19 is constituted by 17 and 18. As described in, for example, Japanese Patent Application Laid-Open No. 5-301221, L-SMC of a continuous glass fiber reinforced resin is obtained by arranging continuous glass fibers in a thermosetting polyester resin in a spiral shape so as to have a uniform density. It contains about 40 wt% and is formed into a sheet having a thickness of about 1 to 2 mm. Therefore, since the continuous glass fibers are arranged in a spiral shape, the glass fibers are entangled with each other, thereby preventing movement during pressurization and heat molding.

[0010] Table 1 shows the results of a study on the mechanical strength (bending strength), the appearance of the cured product, and the moldability of the internal cutting inspection when the content of the continuous glass fiber was changed.

[0011]

[Table 1]

From the results shown in Table 1, when the content of continuous glass fibers is less than 30% by weight based on the entire L-SMC, the strength as a molded product is slightly less than 20% higher than that of the conventional product (see Table 2 described later). However, it is insufficient to secure a margin in strength. On the other hand, if the content exceeds 40 wt% , the fluidity of the resin is poor at the time of production of a molded article, and cavities may be generated inside the molded article to adversely affect the strength. Therefore, the content of the continuous glass fiber is 30 wt% to 40 wt.
wt% is suitable.

Next, Table 2 shows L of the continuous glass fiber reinforced resin.
-It is a mechanical strength characteristic which compared SMC with the conventional glass fiber reinforced resin SMC.

[0014]

[Table 2]

From the results shown in Table 2, the L-SMC of the continuous glass fiber reinforced resin is the same as that of the conventional short glass fiber reinforced resin.
Compared with, the initial strength is improved by about 50% or more, and the long-term strength (plane bending fatigue strength) is improved by about 40%. This is because the continuous glass fibers are arranged in a spiral shape, so that the glass fibers are entangled with each other, so that the movement of the glass fibers is suppressed even if the resin flows during heating and pressurization, and the density of the glass fibers is hardly sparse and dense. It is.

[0016]

According to the first aspect of the present invention, since the casing of the floating coil is formed of a continuous glass fiber reinforced resin in which continuous glass fibers are spirally arranged , the initial strength and the long-term strength are improved. Since a sufficient margin can be secured against external forces such as electromagnetic force and thermal stress, the floating coil can be stably held for a long period of time.

According to the second aspect of the present invention, in the ground coil device for a magnetically levitated railway according to the first aspect, the continuous glass fiber reinforced resin has a continuous glass fiber content of 30 wt%.
Since it is dispersed in a non-directional manner at a concentration of from about 40 wt% , a resin having good fluidity during production of a molded article and having a stable strength can be obtained.

[Brief description of the drawings]

FIG. 1 is a sectional view showing an embodiment of the present invention.

FIG. 2 is a front view taken along line II-II in FIG.

FIG. 3 is a front view taken along line III-III in FIG. 1;

FIG. 4 is a sectional view taken along the line IV-IV in FIG. 2;

FIG. 5 is a sectional view taken along line VV of FIG. 3;

FIG. 6 is a cross-sectional view of a conventional ground coil device of a magnetic levitation railway.

FIG. 7 is a sectional view showing a main part of FIG. 6;

FIG. 8 is a sectional view showing a main part of FIG. 6;

[Explanation of symbols]

7 concrete track, 7a side wall, 7b bottom wall, 8
Propulsion coil, 15 levitation coil, 15b jacket.

Continued on the front page (72) Inventor Masatoshi Shinobu 1-4-1 Meieki Station, Nakamura-ku, Nagoya-shi Tokai Passenger Railway Co., Ltd. (56) References JP-A-5-301221 (JP, A) (58) Field surveyed (Int.Cl. ⁷ , DB name) B60L 13/03-13/10

Claims (2)

(57) [Claims] 1. A propulsion coil for generating a propulsion force of a vehicle is fixed to the inside of the side wall of a concrete track having a U-shaped cross section including both side walls and a bottom wall. In the ground coil device of a magnetic levitation railway in which a levitation coil is disposed on the center side of the concrete track from the propulsion coil and fixed to the side wall, the wrapping coil has a continuous glass fiber spirally arranged. A ground coil device for a magnetic levitation railway, which is formed of a continuous glass fiber reinforced resin. 2. The ground coil device of a magnetically levitated railway according to claim 1, wherein the continuous glass fiber reinforced resin has a continuous glass fiber content of 30 wt% to 40 wt% and is dispersed in a non-directional manner. A terrestrial coil device for a magnetic levitation railway, characterized in that: