JP3259358B2 - Manufacturing method of plate artificial stone - Google Patents
Manufacturing method of plate artificial stoneInfo
- Publication number
- JP3259358B2 JP3259358B2 JP27429692A JP27429692A JP3259358B2 JP 3259358 B2 JP3259358 B2 JP 3259358B2 JP 27429692 A JP27429692 A JP 27429692A JP 27429692 A JP27429692 A JP 27429692A JP 3259358 B2 JP3259358 B2 JP 3259358B2
- Authority
- JP
- Japan
- Prior art keywords
- artificial stone
- plate
- manufacturing
- raw material
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、特に、人造石カウンタ
ーの周辺部材等に使用することができる板状人造石の製
造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a plate-like artificial stone which can be used, for example, as a peripheral member of an artificial stone counter.
【０００２】[0002]
【従来の技術】従来、ポリエステル樹脂等を原材料とす
る人工大理石を用いた人造石カウンターがあり、かかる
人造石カウンターの取付け下部には、配管類を隠し、見
栄えをよくするためにパネル等を連設している。2. Description of the Related Art Conventionally, there has been an artificial stone counter using artificial marble made of polyester resin or the like as a raw material, and panels and the like are connected at a lower part of the artificial stone counter to hide pipes and improve appearance. Has been established.
【０００３】かかるパネルは、単にカウンター部と色合
いを同じくしただけのものであって、一般に、カウンタ
ー部の材質とは異なるメラミン、ポリ化粧板、タイルユ
ニット等から形成されている。[0003] Such a panel simply has the same color as that of the counter portion, and is generally formed of melamine, poly decorative board, tile unit, or the like, which is different from the material of the counter portion.
【０００４】[0004]
【発明が解決しようとする課題】ところが、上記したパ
ネルは、未だ、以下のような解決すべき課題を有してい
た。However, the above-mentioned panel still has the following problems to be solved.
【０００５】すなわち、上記したように、カウンター部
と異なる材質を使用しているために、質感が異なり一体
感がなく、しかも、見た目に貧弱でどうしても違和感を
生じてしまうものであった。That is, as described above, since a material different from that of the counter portion is used, the texture is different and there is no sense of unity, and the appearance is poor and the feeling of incongruity is inevitably caused.
【０００６】また、メラミンやポリ化粧板等は塗料を塗
布しているだけのものなので、表面に傷等が付くと、か
かる傷から水分が侵入し、色剥げや基板の腐食等の原因
となり、耐水性、耐久性に乏しいものであった。Further, since melamine, poly decorative board and the like are merely coated with a paint, if the surface is scratched, moisture penetrates from the scratch, causing color peeling and corrosion of the substrate. It was poor in water resistance and durability.
【０００７】また、タイルユニット等は重たい材質なの
で、カウンター部への取付け作業が面倒なものとなって
いた。Further, since the tile unit and the like are heavy materials, the work of attaching the tile unit to the counter section has been troublesome.
【０００８】本発明は、上記した課題を解決することの
できる板状人造石の製造方法を提供せんとするものであ
る。An object of the present invention is to provide a method for producing a plate-like artificial stone which can solve the above-mentioned problems.
【０００９】[0009]
【課題を解決するための手段】本発明では、人造石カウ
ンターに接合する周辺部材としての板状人造石の製造方
法であって、底板と、少なくとも一側を離脱自在に構成
した側枠とからなる底浅状の下型内に、前記人造石カウ
ンターと同一の材質からなる樹脂及び充填材を人造石製
造用原材料として注型し、同下型に振動を与えて同原材
料の底板側の気泡を脱泡し、同下型に上型を合わせて型
枠を組み、同型枠を垂直に立てて上側の側枠を外し、さ
らに振動を与えて残留気泡を同原材料中に封じ込め、同
原材料を硬化させた後に脱型して得ることを特徴とする
板状人造石の製造方法を提供せんとするものである。According to the present invention, there is provided a method of manufacturing a plate-like artificial stone as a peripheral member to be joined to an artificial stone counter, comprising a bottom plate and a side frame having at least one side detachable. In a lower mold having a shallow bottom, a resin and a filler made of the same material as the artificial stone counter are cast as a raw material for artificial stone production, and the lower mold is vibrated to generate bubbles on the bottom plate side of the raw material. Remove the upper mold from the lower mold, put the upper mold vertically, remove the upper side frame, remove the upper side frame, and further apply vibration to seal the residual air bubbles in the same raw material and remove the same raw material. It is an object of the present invention to provide a method for manufacturing a plate-shaped artificial stone, which is obtained by removing the mold after curing.
【００１０】また、本発明は、人造石カウンター等に接
合する周辺部材としての板状人造石の製造方法であっ
て、補強板に、前記人造石カウンターと同一の材質から
なる樹脂及び充填材を人造石製造用原材料としてスプレ
ーし、同原材料の硬化後に、表面を研磨して得ることを
特徴とする板状人造石の製造方法を提供せんとするもの
である。The present invention also relates to a method for producing a plate-like artificial stone as a peripheral member to be joined to an artificial stone counter or the like, wherein a resin and a filler made of the same material as the artificial stone counter are provided on a reinforcing plate. It is an object of the present invention to provide a method for producing a plate-like artificial stone, characterized in that the method is sprayed as a raw material for producing artificial stone, and after the raw material is hardened, the surface is polished and obtained.
【００１１】さらに、本発明は、人造石カウンター等に
接合する周辺部材としての板状人造石の製造方法であっ
て、補強板に、前記人造石カウンターと同一の材質から
なる樹脂材料と充填材とを交互にスプレーし、硬化させ
た後、表面を研磨して得ることを特徴とする板状人造石
の製造方法を提供せんとするものである。Further, the present invention relates to a method for producing a plate-like artificial stone as a peripheral member to be joined to an artificial stone counter or the like, wherein the reinforcing plate has a resin material and a filler made of the same material as the artificial stone counter. Are alternately sprayed, cured, and then polished to obtain a plate-like artificial stone.
【００１２】[0012]
【実施例】本発明の実施例を図面に基づき、具体的に説
明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the present invention will be specifically described with reference to the drawings.
【００１３】（第１実施例）図１は本発明に係る製造方
法により得られた板状人造石からなるフロントパネルＦ
の断面側面図、図２は同製造方法に使用する型枠の説明
図、図３は同製造方法のフローチャート、図４は同製造
方法の説明図である。(First Embodiment) FIG. 1 shows a front panel F made of a plate-like artificial stone obtained by a manufacturing method according to the present invention.
2 is an explanatory view of a mold used in the manufacturing method, FIG. 3 is a flowchart of the manufacturing method, and FIG. 4 is an explanatory view of the manufacturing method.
【００１４】図１に示すＦは、本発明に係る製造方法に
より得られた人造石Ｃを人造石カウンターＧのエプロン
部G1に接合したフロントパネルであり、カウンター本体
G2と同一の材質からなる。従って、見た目に自然であ
り、しかも、重厚な高級感を現出することができるもの
で、かかる人造石Ｃは、以下に述べる方法により得るこ
とができる。なお、図１中、15はボウル、16は配管部、
17は床面、Ｗは壁体である。F shown in FIG. 1 is a front panel in which artificial stone C obtained by the manufacturing method according to the present invention is joined to an apron portion G1 of an artificial stone counter G, and a counter body.
Made of the same material as G2. Therefore, the artificial stone C is natural in appearance and can produce a solid luxury feeling. Such artificial stone C can be obtained by the method described below. 1, 15 is a bowl, 16 is a piping section,
17 is a floor surface, and W is a wall.
【００１５】先ず、本発明に係る製造方法に用いる型枠
Ａについて説明する。First, the mold A used in the manufacturing method according to the present invention will be described.
【００１６】型枠Ａは、図２に示すように、平坦な板状
のフロントパネルを形成するために、平坦なガラス、セ
ラミックス、ステンレス等の板状の底板１と側枠２とか
ら構成した底浅状の下型ａと、同下型ａの底板１と同寸
法で、かつ、同下型ａの開口部a1を閉塞可能に形成した
板状の上型ｂとから構成している。As shown in FIG. 2, the mold A is composed of a flat bottom plate 1 made of flat glass, ceramics, stainless steel or the like and a side frame 2 to form a flat plate-shaped front panel. It comprises a lower mold a having a shallow bottom, and an upper mold b having the same dimensions as the bottom plate 1 of the lower mold a and having an opening a1 of the lower mold a capable of being closed.
【００１７】そして、下型ａの側枠２の一側を離脱自在
としており、原材料の注型時等は、原材料の漏れがない
ように固定手段３により密封状態に固定している。One side of the side frame 2 of the lower mold a is detachable, and is fixed in a hermetically sealed state by fixing means 3 so that the raw material does not leak when casting the raw material.
【００１８】上型ｂは、下型ａの開口部a1を閉塞するた
めに、側枠２と密着状態にすべく形成した縁部b1と凸部
b2とを有すると共に、型枠Ａを組立てる際に上型ｂと下
型ａとを固定するための緊締具４を具備している。５は
緊締具４に対応して下枠ａに設けた緊締具４の止め具で
ある。The upper mold b has an edge b1 and a projection formed to be in close contact with the side frame 2 to close the opening a1 of the lower mold a.
b2 and a tightening tool 4 for fixing the upper mold b and the lower mold a when assembling the mold A. Reference numeral 5 denotes a stopper for the fastener 4 provided on the lower frame a corresponding to the fastener 4.
【００１９】なお、製品となる人造石Ｃの厚みは、本実
施例においては、上型ｂの凸部b2の高さを変えたものを
数種類容易することにより対応することができるが、下
型ａの側枠２の高さを変えることにより対応することも
できる。In the present embodiment, the thickness of the artificial stone C, which is a product, can be dealt with by facilitating several types of the upper mold b having different heights of the convex portions b2. This can be dealt with by changing the height of the side frame 2 of a.
【００２０】型枠Ａの構成は上記の通りであり、同型枠
Ａを使用して本発明に係る板状の人造石Ｃを製造する方
法について、図３及び図４を参照して説明する。The configuration of the mold A is as described above. A method of manufacturing the plate-shaped artificial stone C according to the present invention using the mold A will be described with reference to FIGS.
【００２１】注型工程52では、予め、型枠処理工程51に
おいて内外部を清掃し、内部に離型材Ｄを塗布した下型
ａに、ポリエステル樹脂と水酸化アルミニウム、ガラス
粉末、炭酸カルシウム等の無機充填材とからなる原材料
Ｂを注型する（図４（イ）参照）。このときの原材料Ｂ
の厚みは３〜５mmとする。In a casting step 52, the inner and outer surfaces are cleaned in advance in a mold processing step 51, and a lower mold a coated with a mold release material D is filled with a polyester resin and aluminum hydroxide, glass powder, calcium carbonate or the like. Raw material B composed of an inorganic filler is cast (see FIG. 4A). Raw material B at this time
Has a thickness of 3 to 5 mm.
【００２２】次に、第１脱泡工程53において、下型ａを
バイブレータ６で振動させ、原材料Ｂの底板１側、即
ち、製品となった場合の人造石Ｃの表面側に生じる気泡
ｐを除去する（図４（ロ））。Next, in the first defoaming step 53, the lower mold a is vibrated by the vibrator 6, and the bubbles p generated on the bottom plate 1 side of the raw material B, that is, on the surface side of the artificial stone C as a product. It is removed (FIG. 4B).
【００２３】次いで、型組み工程54において、上記型枠
処理工程51で清掃等の表面処理を施した上型ｂを下型ａ
と合わせ、緊締具４で固定して型組みし、型組みされた
型枠Ａを図４の（ハ）に示すように、垂直に立てて保持
し、さらに、かかる状態で、型枠Ａの上側に位置する下
型ａの側枠２を取外す。Next, in a mold assembling step 54, the upper mold b subjected to surface treatment such as cleaning in the mold processing step 51 is replaced with a lower mold a
4 and fixed with the fasteners 4 to form a mold. The assembled form A is held upright as shown in FIG. 4 (C). The side frame 2 of the lower mold a located on the upper side is removed.
【００２４】そして、第２脱泡工程55において、型枠Ａ
をバイブレータ６で振動させる。これにより、第１脱泡
工程53で脱泡した際に原材料Ｂの上型ｂ側にわずかに残
ったわずかな気泡ｐと、上型ｂを合わせた時に発生する
気泡ｐとを上型ｂ側から遊離させ、同気泡ｐを原材料Ｂ
の中に封じ込めることができる（図４（ニ））。Then, in the second defoaming step 55, the mold A
Is vibrated by vibrator 6. As a result, the small bubbles p slightly remaining on the upper mold b side of the raw material B when the defoaming is performed in the first defoaming step 53 and the bubbles p generated when the upper mold b is combined are combined with the upper mold b side. From the raw material B
(Fig. 4 (d)).
【００２５】従って、成形する人造石Ｃを表裏共に気泡
ｐのない高品質のものとすることができる。Therefore, the artificial stone C to be formed can be of high quality without bubbles p on both sides.
【００２６】このときに、原材料Ｂの上側は同材料Ｂの
自重により下方へ少し凹んだ状態となり、しかも、かか
る凹部に気泡ｐが表れることがあるので、その場合は原
材料Ｂを追加して平坦になるようにすればよい。At this time, the upper side of the raw material B is slightly depressed downward due to the weight of the raw material B, and air bubbles p may appear in the concave portion. In this case, the raw material B is added and flattened. What should be done is.
【００２７】次いで、第１硬化工程56において、所定時
間硬化させた後、脱型工程57において、成形された人造
石Ｃを脱型する。Next, in a first curing step 56, after curing for a predetermined time, in a demolding step 57, the formed artificial stone C is demolded.
【００２８】そして、第２硬化工程58において十分な時
間をかけて完全に硬化させた後、人造石Ｃを切断工程59
に送り、同切断工程59においてカッター13等を用いて、
必要長さに寸法を合わせて切断する( 図４（ホ））。Then, after the hardening is completely completed in a second hardening step 58 for a sufficient time, the artificial stone C is cut in the cutting step 59.
Using the cutter 13 etc. in the same cutting step 59,
Cut according to the required length (Fig. 4 (e)).
【００２９】所定の長さに切断された人造石Ｃを、接着
工程60において、人造石Ｃの裏面C1全体に接着剤Ｄを塗
布し、人造石Ｃの約２倍程度の厚みを有する補強板７を
接着し（図４（ヘ））、最終の仕上げ工程61でバリ等を
切りとる等の細かな作業を行うことにより製品を得る。In the bonding step 60, the artificial stone C cut to a predetermined length is coated with an adhesive D over the entire back surface C1 of the artificial stone C, and a reinforcing plate having a thickness of about twice that of the artificial stone C is provided. 7 (FIG. 4 (f)), and a fine work such as cutting off burrs or the like is performed in the final finishing step 61 to obtain a product.
【００３０】なお、上記の接着工程60において、透明感
のある製品であれば、接着剤Ｄは透明度の高いものを使
用する方が好ましい。In the above bonding step 60, if the product has a transparent feeling, it is preferable to use a highly transparent adhesive D.
【００３１】このようにして得られた製品は、人造石カ
ウンターの周辺部材として使用すれば、カウンターと同
材質でできているため、カウンターとの一体感があり、
見た目に違和感がなく、外観上とても自然である。When the product obtained in this way is used as a peripheral member of an artificial stone counter, it is made of the same material as the counter, so that there is a sense of unity with the counter.
It looks natural and looks very natural.
【００３２】また、自然石の風合いがあって重厚感があ
り、高級なイメージをかもしだすことができ、しかも、
人造石Ｃの厚みが薄いので軽量であり、フロントパネル
等に使用する場合、作業が容易、且つ、楽である。In addition, the texture of natural stone has a profound feeling, and it can produce a high-quality image.
Since the artificial stone C is thin, it is lightweight, and when used for a front panel or the like, the work is easy and easy.
【００３３】さらに、メラミンや、ポリ化粧板等と異な
り、傷等で塗料が剥げて水が侵入して腐食する心配もな
く、耐水性に富むので水廻りに使用する材料として最適
である。Furthermore, unlike melamine, poly decorative board, etc., there is no fear of paint coming off due to scratches or the like and water entering and corroding, and it is rich in water resistance, so it is most suitable as a material used around water.
【００３４】（第２実施例）図５は第２実施例による板
状の人造石の製造工程を示すフローチャートであり、図
６は同製造工程を示す説明図である。(Second Embodiment) FIG. 5 is a flowchart showing a manufacturing process of a plate-shaped artificial stone according to a second embodiment, and FIG. 6 is an explanatory diagram showing the manufacturing process.
【００３５】ここで、図５及び図６を参照して、本実施
例による板状の人造石Ｃの製造方法について説明する
と、図６に示す10は補強板であり、同補強板10は、人造
石カウンター等の平坦な板状のフロントパネルを形成す
るために、平板状に形成している。Here, a method of manufacturing the plate-shaped artificial stone C according to the present embodiment will be described with reference to FIGS. 5 and 6. Referring to FIG. 6, reference numeral 10 denotes a reinforcing plate. In order to form a flat plate-shaped front panel such as an artificial stone counter, it is formed in a flat plate shape.
【００３６】先ず、スプレー工程71において、上記の補
強板10の表面に、スプレーガン11を用いて、ポリエステ
ル樹脂と水酸化アルミニウム、ガラス粉末、炭酸カルシ
ウム等の無機充填材からなる原材料Ｂを0.2 〜1.0mm の
厚みでスプレーしてコーティングを施す（図６
（イ））。このとき、石目調の人造石を成形するための
原材料Ｂであれば、モルタルガンを用いるとよい。First, in a spraying step 71, a raw material B composed of a polyester resin and an inorganic filler such as aluminum hydroxide, glass powder, calcium carbonate or the like is applied to the surface of the reinforcing plate 10 using a spray gun 11 in an amount of 0.2 to 0.2. Spray 1.0mm thick to apply coating (Fig. 6
(I)). At this time, a mortar gun may be used as the raw material B for forming the stone-like artificial stone.
【００３７】次いで、硬化工程72において樹脂を十分硬
化させて人造石Ｃを成形し（図６（ロ））、研磨工程73
において研磨機12等を用いて表面の研磨加工を行う（図
６（ハ））。Next, in a curing step 72, the resin is sufficiently cured to form the artificial stone C (FIG. 6B), and a polishing step 73 is performed.
Then, the surface is polished using the polisher 12 or the like (FIG. 6 (c)).
【００３８】そして、仕上げ工程74でバフ等を用いてさ
らに仕上げることにより、製品を得ることができる。Then, in the finishing step 74, a product can be obtained by further finishing using a buff or the like.
【００３９】（第３実施例）図５は第３実施例による板
状の人造石の製造工程を示すフローチャートであり、図
７は同製造工程を示す説明図である。(Third Embodiment) FIG. 5 is a flowchart showing a manufacturing process of a plate-shaped artificial stone according to a third embodiment, and FIG. 7 is an explanatory diagram showing the manufacturing process.
【００４０】ここで、図５及び図７を参照して、本実施
例における板状の人造石の製造方法について説明する
と、図７に示す10は補強板であり、同補強板10は人造石
カウンター等の平坦な板状パネルを形成するために、平
板状に形成している。Here, a method of manufacturing a plate-shaped artificial stone in this embodiment will be described with reference to FIGS. 5 and 7. Reference numeral 10 shown in FIG. 7 is a reinforcing plate, and the reinforcing plate 10 is an artificial stone. In order to form a flat plate-like panel such as a counter, it is formed in a flat plate shape.
【００４１】先ず、スプレー工程71において、上記の補
強板10の表面に、スプレーガン11を用いて、ポリエチレ
ン樹脂からなる人造石製造用原材料(B1)を0.2 〜1.0mm
の厚みでスプレーして、コーティングを施す（図７
（イ））。First, in a spraying step 71, a raw material (B1) made of polyethylene resin for artificial stone production is spread on the surface of the reinforcing plate 10 by using a spray gun 11 in an amount of 0.2 to 1.0 mm.
Spray with a thickness of 3 to apply the coating (Fig. 7
(I)).
【００４２】次に、このスプレーした人造石製造用原材
料(B1)の上面に、水酸化アルミニウム、ガラス粉末、炭
酸カルシウム等の無機充填材(B2)をスプレーガン11を用
いて、0.2 〜1.0mm の厚みでスプレーする（図７
（ロ））。このとき、スプレーガン11はモルタルミキサ
ーを用いるとよい。Next, an inorganic filler (B2) such as aluminum hydroxide, glass powder, calcium carbonate or the like was sprayed on the upper surface of the sprayed raw material (B1) for 0.2 to 1.0 mm using a spray gun 11. Spray with thickness of (Fig. 7
(B)). At this time, a mortar mixer may be used for the spray gun 11.
【００４３】最後に、無機充填材(B2)の上面に、人造石
製造用原材料(B1)を再度スプレーして、コーティングを
施す（図７（ハ））。Finally, the raw material for artificial stone production (B1) is sprayed again on the upper surface of the inorganic filler (B2) to apply a coating (FIG. 7 (c)).
【００４４】これらのスプレー工程を数回繰り返して
も、同様の効果を得ることができる。The same effect can be obtained by repeating these spraying steps several times.
【００４５】次工程の、硬化工程72以降の工程は、第２
実施例と同じで、図６（ロ）が図７（ニ）に当たり、図
６（ハ）が図７（ホ）に当たる。In the next step after the curing step 72, the second step
6 (b) corresponds to FIG. 7 (d), and FIG. 6 (c) corresponds to FIG. 7 (e).
【００４６】本実施例２及び３において得られた製品も
人造石カウンターのフロント及びサイドパネル等の周辺
部材に使用するのに適しており、第１実施例で得られた
製品と同様の効果を奏することができる。しかも、型枠
を必要としないので製造コストを低く抑えることができ
る。The products obtained in Examples 2 and 3 are also suitable for use in peripheral members such as the front and side panels of the artificial stone counter, and have the same effects as the products obtained in Example 1. Can play. In addition, since no formwork is required, manufacturing costs can be reduced.
【００４７】さらに、製造工程が短くてすむので、生産
効率を向上させることができる。Further, since the manufacturing process can be shortened, the production efficiency can be improved.
【００４８】[0048]
【発明の効果】本発明では、人造石カウンターに接合す
る周辺部材としての板状人造石の製造方法であって、底
板と、少なくとも一側を離脱自在に構成した側枠とから
なる底浅状の下型内に、前記人造石カウンターと同一の
材質からなる樹脂及び充填材を人造石製造用原材料とし
て注型し、同下型に振動を与えて同原材料の底板側の気
泡を脱泡し、同下型に上型を合わせて型枠を組み、同型
枠を垂直に立てて上側の側枠を外し、さらに振動を与え
て残留気泡を同原材料中に封じ込め、同原材料を硬化さ
せた後に脱型して得ること、そして、上記方法により得
られた人造石の裏面に接着剤を塗布し、補強板を接着し
て得ること、さらに、同じく人造石カウンター等に接合
する周辺部材としての板状人造石の製造方法であって、
補強板に、前記人造石カウンターと同一の材質からなる
樹脂及び充填材を人造石製造用原材料としてスプレー
し、同原材料の硬化後に、表面を研磨して得ること、並
びに補強板に、前記人造石カウンターと同一の材質から
なる樹脂材料と充填材とを交互にスプレーし、硬化させ
た後、表面を研磨して得ることとしたので、以下の効果
を得ることができる。According to the present invention, there is provided a method of manufacturing a plate-like artificial stone as a peripheral member to be joined to an artificial stone counter, comprising a bottom plate and a shallow bottom including a side frame having at least one side detachable. In the lower mold, a resin and a filler made of the same material as the artificial stone counter are poured as a raw material for artificial stone production, and vibration is applied to the lower mold to remove bubbles on the bottom plate side of the raw material. After the upper mold is assembled with the lower mold, the mold is assembled, the same mold is set upright, the upper side frame is removed, the vibration is further applied, the residual air bubbles are sealed in the same material, and the same material is cured. Demolding and obtaining, and applying an adhesive to the back surface of the artificial stone obtained by the above method, bonding a reinforcing plate to obtain, furthermore, a plate as a peripheral member to be similarly joined to an artificial stone counter or the like A method for producing artificial stone, comprising:
On a reinforcing plate, a resin and a filler made of the same material as the artificial stone counter are sprayed as a raw material for artificial stone production, and after the raw material is hardened, the surface is polished to obtain the reinforcing plate. Since the resin material and the filler, which are made of the same material as the counter, are alternately sprayed and cured, and then the surface is polished, the following effects can be obtained.
【００４９】表面にピンホールのない、高品質の製品
とすることができる。A high quality product having no pinholes on the surface can be obtained.
【００５０】かかる人造石を、例えば、人造石カウン
ター等の周辺部材として使用すれば、カウンターと一体
感があり、見た目に違和感のないものとすることができ
る。When the artificial stone is used as a peripheral member of, for example, an artificial stone counter, it has a sense of unity with the counter and can be made to look natural.
【００５１】自然石の風合いがあって重厚感があり、
高級なイメージをかもしだすことができる。The texture of natural stone has a solid feeling,
You can create a high-quality image.
【００５２】人造石の厚みが薄いので軽量であり、取
付作業等が容易、且つ、楽である。Since the artificial stone has a small thickness, it is lightweight, and the mounting work and the like are easy and easy.
【００５３】耐水性に富むので水廻りにも安心して使
用できる。Since it is rich in water resistance, it can be used safely around water.
【００５４】型枠を必要としないので製造コストを低
く抑えることができる。Since no mold is required, the manufacturing cost can be reduced.
【００５５】製造工程が短くてすむので、生産効率を
向上させることができる。Since the manufacturing process can be shortened, the production efficiency can be improved.
【図１】本発明に係る製造方法により得られた人造石か
らなるフロントパネルの断面側面図である。FIG. 1 is a cross-sectional side view of a front panel made of artificial stone obtained by a manufacturing method according to the present invention.
【図２】本発明に係る板状人造石を製造する方法に使用
する型枠の説明図である。FIG. 2 is an explanatory view of a mold used in the method of manufacturing a plate artificial stone according to the present invention.
【図３】同製造方法のフローチャートである。FIG. 3 is a flowchart of the manufacturing method.
【図４】同製造方法の説明図である。FIG. 4 is an explanatory diagram of the manufacturing method.
【図５】第２、３実施例による板状人造石を製造する方
法のフローチャートである。FIG. 5 is a flowchart of a method of manufacturing a plate artificial stone according to the second and third embodiments.
【図６】第２実施例による板状人造石の製造方法の説明
図である。FIG. 6 is an explanatory view of a method for manufacturing a plate artificial stone according to a second embodiment.
【図７】第３実施例による板状人造石の製造方法の説明
図である。FIG. 7 is an explanatory diagram of a method of manufacturing a plate artificial stone according to a third embodiment.
Ａ 型枠 Ｂ 原材料 Ｃ 人造石 Ｄ 接着剤 ａ 下型 ｂ 上型 １ 底板 ２ 側枠 10 補強板 A Formwork B Raw material C Artificial stone D Adhesive a Lower mold b Upper mold 1 Bottom plate 2 Side frame 10 Reinforcement plate
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ // Ａ４７Ｋ 1/00 Ａ４７Ｋ 1/00 Ｎ Ｂ２９Ｋ 105:16 Ｂ２９Ｋ 105:16 Ｂ２９Ｌ 31:10 Ｂ２９Ｌ 31:10 31:44 31:44 (56)参考文献 特開 平３−120019（ＪＰ，Ａ) 特開 昭63−15712（ＪＰ，Ａ) 特開 平２−127100（ＪＰ，Ａ) 特開 昭59−87075（ＪＰ，Ａ) 特開 平１−176505（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B29C 39/02 - 39/24 B29C 69/00 - 69/02 B29D 31/00 B05D 3/12 B05D 5/06 C04B 26/02 A47K 1/00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI // A47K 1/00 A47K 1/00 NB29K 105: 16 B29K 105: 16 B29L 31:10 B29L 31:10 31:44 31: 44 (56) References JP-A-3-120019 (JP, A) JP-A-63-15712 (JP, A) JP-A-2-127100 (JP, A) JP-A-59-87075 (JP, A) JP-A-1-176505 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) B29C 39/02-39/24 B29C 69/00-69/02 B29D 31/00 B05D 3 / 12 B05D 5/06 C04B 26/02 A47K 1/00
Claims (3)
ての板状人造石の製造方法であって、 底板(1)と、少なくとも一側を離脱自在に構成した側枠
(2)とからなる底浅状の下型(a)内に、前記人造石カウン
ターと同一の材質からなる樹脂及び充填材を人造石製造
用原材料(B)として注型し、同下型(a)に振動を与えて同
原材料(B)の底板(1)側の気泡(p)を脱泡し、同下型(a)に
上型(b)を合わせて型枠(A)を組み、同型枠(A)を垂直に
立てて上側の側枠(2)を外し、さらに振動を与えて残留
気泡(p)を同原材料(B)中に封じ込め、同原材料(B)を硬
化させた後に脱型して人造石(C)を得た後、同人造石(C)
の裏面に接着剤(D)を塗布し、補強板(7)を接着して得る
ことを特徴とする板状人造石の製造方法。1. A peripheral member to be joined to an artificial stone counter
A method for manufacturing plate artificial stones, comprising: a bottom plate (1); and a side frame having at least one side detachable.
(2), the artificial stone counter in the shallow bottom lower mold (a)
A resin and a filler made of the same material as the raw material are poured as a raw material for artificial stone production (B) , and vibration is applied to the lower mold (a) to generate air bubbles on the bottom plate (1) side of the raw material (B). p) is defoamed, the lower mold (a) is combined with the upper mold (b) to form a mold (A), the same mold (A) is set up vertically, and the upper side frame (2) is removed, Vibration is further applied to confine the residual air bubbles (p) in the raw material (B), and after the raw material (B) is cured, the mold is removed to obtain an artificial stone (C), and then the artificial stone (C)
A method for producing a plate-like artificial stone, characterized in that an adhesive (D) is applied to the back surface of the slab, and the reinforcing plate (7) is adhered .
ての板状人造石の製造方法であって、 補強板(10)に、前記人造石カウンターと同一の材質から
なる樹脂及び充填材を人造石製造用原材料(B)としてス
プレーし、同原材料(B)の硬化後に、表面を研磨して得
ることを特徴とする板状人造石の製造方法。2. A peripheral member to be joined to an artificial stone counter.
Manufacturing method of the plate-shaped artificial stone , wherein the reinforcing plate (10) is made of the same material as the artificial stone counter.
Comprising the resin and filler to scan <br/> play as artificial stone manufacturing raw materials (B), after curing of the raw material (B), a method of manufacturing a plate-like artificial stone, characterized in that obtained by polishing the surface .
ての板状人造石の製造方法であって、 補強板(10)に、前記人造石カウンターと同一の材質から
なる樹脂材料(B1)と充填材(B2)とを交互にスプレーし、
硬化させた後、表面を研磨して得ることを特徴とする板
状人造石の製造方法。3. A peripheral member to be joined to an artificial stone counter.
Manufacturing method of the plate-shaped artificial stone , wherein the reinforcing plate (10) is made of the same material as the artificial stone counter.
Made by spraying a resin material (B1) and filler and (B2) alternately,
A method for producing a plate-shaped artificial stone, characterized in that the surface is polished after being cured.