JP3215515B2 - Manufacturing method of waterproof sheet - Google Patents
Manufacturing method of waterproof sheetInfo
- Publication number
- JP3215515B2 JP3215515B2 JP22622992A JP22622992A JP3215515B2 JP 3215515 B2 JP3215515 B2 JP 3215515B2 JP 22622992 A JP22622992 A JP 22622992A JP 22622992 A JP22622992 A JP 22622992A JP 3215515 B2 JP3215515 B2 JP 3215515B2
- Authority
- JP
- Japan
- Prior art keywords
- waterproof sheet
- emulsion
- mixture
- asphalt emulsion
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【産業上の利用分野】本発明は、特に、ビル等の各種コ
ンクリート構造物の屋根の防水に効果的に使用できる防
水シートの製造方法及び貼着方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a waterproof sheet and a method for attaching a waterproof sheet which can be effectively used for waterproofing a roof of various concrete structures such as buildings.
【０００２】[0002]
【従来の技術】従来、各種のコンクリート製のビルの屋
根構造として、コンクリート製の屋根材の外面に防水シ
ートを貼着したものがある。2. Description of the Related Art Conventionally, as a roof structure of various concrete buildings, there is a structure in which a waterproof sheet is attached to an outer surface of a concrete roof material.
【０００３】かかる防水シートとして、その防水効果を
高めるために、複数の合成樹脂層からなるラミネートシ
ート等の完全防水シートが用いられている。As such a waterproof sheet, a complete waterproof sheet such as a laminate sheet comprising a plurality of synthetic resin layers is used in order to enhance the waterproof effect.
【０００４】[0004]
【発明が解決しようとする課題】しかし、かかる従来の
防水シートは、未だ、以下の解決すべき課題を有してい
た。However, such a conventional waterproof sheet still has the following problems to be solved.
【０００５】即ち、かかるラミネートシートからなる防
水シートは、一般に、水の透過を防止するのみならず、
空気の透過も完全に遮断するものである。[0005] That is, the waterproof sheet made of such a laminate sheet generally not only prevents water permeation, but also
It completely shuts off air transmission.
【０００６】従って、コンクリート製の屋根材の内部の
水分が水蒸気として上方に抜けようとしても、防水シー
トによって外部への放出が阻害されるので、水蒸気が防
水シートを上方に押上げ、防水シートを破ることにもな
っていた。Therefore, even if the water inside the concrete roofing material tries to escape upward as water vapor, the release to the outside is hindered by the waterproof sheet, so that the water vapor pushes the waterproof sheet upward, and the waterproof sheet is removed. It was supposed to break.
【０００７】本発明は、上記した課題を解決することが
できる防水シートの製造方法及び貼着方法を提供するこ
とを目的とする。An object of the present invention is to provide a method for manufacturing a waterproof sheet and a method for attaching the waterproof sheet, which can solve the above-mentioned problems.
【０００８】[0008]
【課題を解決するための手段】本発明は、可撓性を有す
る基布に、アスファルト乳剤とポリマーエマルジョンと
の混合物、アスファルト乳剤とポリマーセメントとの混
合物、アスファルト乳剤と水性ポリウレタン系樹脂と珪
砂等の砂状粒子との混合物のいずれかを塗布・含浸して
製造する防水シートの製造方法であって、前記ポリマー
セメントは、酸化珪素、酸化カルシウム、酸化鉄を主成
分とした主材に、少なくともアクリル酸エステル共重合
体を主成分としてなる複合ポリマーエマルジョンを混和
して生成したものからなることを特徴とする防水シート
の製造方法に係るものである。According to the present invention, there is provided a flexible base cloth comprising a mixture of an asphalt emulsion and a polymer emulsion, a mixture of an asphalt emulsion and a polymer cement, an asphalt emulsion, an aqueous polyurethane resin and silica sand. A method for producing a waterproof sheet by applying and impregnating any of the mixture with the sand-like particles of the above, wherein the polymer cement comprises at least a silicon oxide, a calcium oxide, and a main material mainly composed of iron oxide. The present invention relates to a method for producing a waterproof sheet, comprising a mixture produced by mixing a composite polymer emulsion containing an acrylate copolymer as a main component.
【０００９】上記方法において用いる可撓性を有する基
布としては、通気性の優れた織布や不織布を好適に用い
ることができる。As the flexible base fabric used in the above method, a woven fabric or a nonwoven fabric having excellent air permeability can be suitably used.
【００１０】アスファルト乳剤は、60/80 系列を用いる
ことができる。Asphalt emulsions of 60/80 series can be used.
【００１１】[0011]
【００１２】また、上記した防水シートの製造方法は、
防水シートを建築現場で塗布して仕上げる方法と、予め
工場で所定の大きさの防水シートを製作しておき、現場
に持ち込み、ビル等の構造物の屋根面等の壁面に所望の
接着剤を用いて貼着する方法とが考えられる。Further, the above-mentioned method for manufacturing a waterproof sheet comprises:
Applying a waterproof sheet at the construction site and finishing it, and preparing a waterproof sheet of a predetermined size at the factory in advance, bringing it to the site, applying the desired adhesive to the wall surface such as the roof surface of structures such as buildings It is possible to use this method.
【００１３】なお、接着剤としては、防水シートの素材
である、アスファルト乳剤、アスファルト乳剤とポリマ
ーエマルジョンとの混合物、アスファルト乳剤とポリマ
ーセメントとの混合物のいずれかを用いることができ
る。As the adhesive, any one of asphalt emulsion, a mixture of asphalt emulsion and polymer emulsion, and a mixture of asphalt emulsion and polymer cement, which are materials of a waterproof sheet, can be used.
【００１４】[0014]
【実施例】以下、添付図である図１(a) 〜図１(c) に示
す実施例を参照して、本発明に係る防水シートの製造方
法を、具体的に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a method for manufacturing a waterproof sheet according to the present invention will be specifically described with reference to the accompanying drawings shown in FIGS. 1 (a) to 1 (c).
【００１５】まず、図１(a) に示すように、可撓性を有
する基布10を用意する。かかる基布10の大きさ、形状、
厚みは、ビル等のコンクリート壁面等の基布貼着面の大
きさや形状に合わせて任意に選択することができる。First, as shown in FIG. 1A, a flexible base cloth 10 is prepared. The size, shape,
The thickness can be arbitrarily selected according to the size and shape of the base cloth sticking surface such as a concrete wall surface of a building or the like.
【００１６】また、基布10は、シート状、ロール状のい
ずれでも用意しておくことができ、ロール状とした場合
は、倉庫管理や搬送に便宜である。The base fabric 10 can be prepared in either a sheet shape or a roll shape. When the base fabric 10 is in a roll shape, it is convenient for warehouse management and transportation.
【００１７】また、好ましくは、基布10は、ガラス繊維
や、ナイロン、ポリエステル、ポリアミド等の合成樹脂
繊維等を素材とした織布や不織布を用いる。Preferably, the base fabric 10 is made of a woven or non-woven fabric made of glass fiber, synthetic resin fiber such as nylon, polyester or polyamide.
【００１８】次に、図１(b) に示すように、リシンガン
等の吹付装置11を用いて、アスファルト乳剤12を、基布
10の一側面、他側面、両側面に吹付ける。この吹付によ
って、アスファルト乳剤12は、基布10の表面に塗膜を形
成するとともに、その内部に含浸し、一定時間経過した
後に、基布10と一体をなすことになり、防水シートＡを
形成することになる。Next, as shown in FIG. 1 (b), the asphalt emulsion 12 is ground using a spraying device 11 such as a ricin gun.
10 spray one side, the other side, both sides. By this spraying, the asphalt emulsion 12 forms a coating film on the surface of the base fabric 10 and impregnates the inside thereof, and after a certain period of time, becomes integral with the base fabric 10 to form the waterproof sheet A. Will do.
【００１９】なお、アスファルト乳剤12の塗膜の厚さ
は、水の通過を確実に防止することができるとともに、
空気の円滑な通過は確保できる厚さ、例えば、0.2 〜0.
8 mmとするのが好ましい。Incidentally, the thickness of the coating film of the asphalt emulsion 12 can surely prevent the passage of water,
Thickness that ensures smooth passage of air, for example, 0.2 to 0.
It is preferably 8 mm.
【００２０】かかるアスファルト乳剤12としては、乳剤
粘度 (20℃.10 rpm)cP が 9150 で固形分が60％である
を60/80 を用いることができ。As the asphalt emulsion 12, 60/80 emulsion viscosity (20 ° C., 10 rpm) having a cP of 9150 and a solid content of 60% can be used.
【００２１】また、アスファルト乳剤12に代えて、アス
ファルト乳剤12と以下に説明するポリマーエマルジョン
との混合物や、アスファルト乳剤12と以下に説明するポ
リマーセメントとの混合物等を用いることができる。こ
の場合も、混合物の塗膜の厚さは、水の通過は確実に防
止することがきるとともに、空気の円滑な通過は確保で
きる厚さ、例えば、0.2 〜0.8 mmとするのが好ましい。In place of the asphalt emulsion 12, a mixture of the asphalt emulsion 12 and a polymer emulsion described below, a mixture of the asphalt emulsion 12 and a polymer cement described below, and the like can be used. Also in this case, it is preferable that the thickness of the coating film of the mixture is set to a thickness that can prevent the passage of water without fail and ensure the smooth passage of air, for example, 0.2 to 0.8 mm.
【００２２】その後、図１(c) に示すように、所望の接
着剤13、例えば、上記したアスファルト乳剤12、アスフ
ァルト乳剤12と以下に説明するポリマーエマルジョンと
の混合物や、アスファルト乳剤12と以下に説明するポリ
マーセメントとの混合物を用いて、ビル等のコンクリー
ト製の屋根材14に貼着することによって、防水作業を完
了する。Thereafter, as shown in FIG. 1 (c), a desired adhesive 13, for example, the above-mentioned asphalt emulsion 12, a mixture of the asphalt emulsion 12 and the polymer emulsion described below, or an asphalt emulsion 12 and the following The waterproofing operation is completed by attaching the mixture to the concrete roof material 14 of a building or the like using the mixture with the polymer cement to be described.
【００２３】しかして、上記した防水シートＡに含浸さ
せたアスファルト乳剤12、ポリマーエマルジョン及びポ
リマーセメントは、それぞれ、十分な防水機能を有する
一方で、適当な通気性を有する。Thus, the asphalt emulsion 12, the polymer emulsion and the polymer cement impregnated in the waterproof sheet A described above each have a sufficient waterproofing function, while having an appropriate air permeability.
【００２４】従って、防水シートＡは、雨水等の屋根材
14を通した構造物内部への侵入を確実に防止することが
できるとともに、コンクリート製の屋根材14の内部から
同屋根材14の表面に上昇して水蒸気を、速やかに通過さ
せて、大気中に放出することができ、シート内部滞留水
蒸気による防水シートＡの破損も確実に防止することが
できる。Therefore, the waterproof sheet A is made of a roof material such as rainwater.
In addition to reliably preventing intrusion into the interior of the structure through the interior of the roofing material, the water vapor rises from the inside of the concrete roofing material 14 to the surface of the roofing material 14, allowing water vapor to pass quickly, and The waterproof sheet A can be reliably prevented from being damaged due to water vapor retained inside the sheet.
【００２５】即ち、可撓性を有する基布10に、アスファ
ルト乳剤12、アスファルト乳剤12とポリマーエマルジョ
ンとの混合物、アスファルト乳剤12とポリマーセメント
との混合物のいずれかを塗布・含浸して製造する防水シ
ートＡは、防水シートとしての機能を必要十分に果たす
ことができる。That is, a waterproof fabric produced by coating and impregnating a flexible base cloth 10 with any of an asphalt emulsion 12, a mixture of an asphalt emulsion 12 and a polymer emulsion, or a mixture of an asphalt emulsion 12 and a polymer cement. The sheet A can fulfill the function as a waterproof sheet sufficiently and sufficiently.
【００２６】また、接着剤13もアスファルト乳剤12、ア
スファルト乳剤12とポリマーエマルジョンとの混合物、
アスファルト乳剤12とポリマーセメントとの混合物のい
ずれかとすることによって、防水シートＡは、さらに、
防水シートとしての機能を向上することができる。The adhesive 13 is also composed of an asphalt emulsion 12, a mixture of the asphalt emulsion 12 and a polymer emulsion,
By using any of the mixture of the asphalt emulsion 12 and the polymer cement, the waterproof sheet A further
The function as a waterproof sheet can be improved.
【００２７】特に、ポリマーセメントは、後述するよう
な成分・組成を有するので、防水シートＡは、防水性及
び耐候性、確実な接着性等の、屋根材14に不可欠な条件
も、全て十分に充足することができる。In particular, since the polymer cement has the components and compositions as described below, the waterproof sheet A has sufficient waterproofing, weather resistance, reliable adhesiveness, and other essential conditions for the roofing material 14. Can be satisfied.
【００２８】また、基布10は可撓性を有するとともに、
アスファルト乳剤12も一定の伸縮性を有するので、ビル
等の屋根材14の表面が曲面をなしている場合であって
も、容易に、同屋根材14表面に沿って防水シートＡを貼
着することができる。The base cloth 10 has flexibility,
Since the asphalt emulsion 12 also has a certain elasticity, even when the surface of the roofing material 14 such as a building has a curved surface, the waterproof sheet A can be easily adhered along the surface of the roofing material 14. be able to.
【００２９】また、上記した防水シートＡの製造方法に
用いるポリマーセメントとしては、例えば、酸化珪素、
酸化カルシウム、酸化鉄を主成分とした主材に、少なく
ともアクリル酸エステル共重合体を主成分としてなる複
合ポリマーエマルジョンを混和して生成したものを用い
ることができ、以下に、具体的成分及び配合割合を示
す。As the polymer cement used in the method for producing the waterproof sheet A, for example, silicon oxide,
A mixture obtained by mixing at least a composite polymer emulsion mainly composed of an acrylate ester copolymer with a main material mainly composed of calcium oxide and iron oxide can be used. Indicates the ratio.
【００３０】本実施例では、ポリマーエマルジョンとし
て、以下の組成を有する複合ポリマーエマルジョンＰを
用いた。In this embodiment, a composite polymer emulsion P having the following composition was used as the polymer emulsion.
【００３１】（複合ポリマーエマルジョンＰ) （実施例１） （実施例２） また、上記した防水シートＡの製造方法に用いるポリマ
ーセメントとしては、上記した組成を有する複合ポリマ
ーエマルジョンＰと以下の組成を有する主剤Ｍとを混合
して生成したものを用いた。(Composite Polymer Emulsion P) (Example 1) (Example 2) As the polymer cement used in the method for producing the waterproof sheet A described above, a polymer cement produced by mixing the composite polymer emulsion P having the above-described composition with the main agent M having the following composition was used.
【００３２】そして、このようにして製造したポリマー
エマルジョンＰを、アスファルト乳剤12に、１：４の混
合比で混合し、基布10の塗布・含浸させて防水シートＡ
を製造した。Then, the polymer emulsion P thus produced is mixed with the asphalt emulsion 12 at a mixing ratio of 1: 4, and the base fabric 10 is applied and impregnated to form a waterproof sheet A.
Was manufactured.
【００３３】 なお、上記白色セメントの成分重量比は、以下の通りで
あった。[0033] The component weight ratio of the white cement was as follows.
【００３４】 また、上記した主剤Ｍに代えて、砂とセメントを混合し
たモルタルを用いることができる。[0034] In addition, mortar obtained by mixing sand and cement can be used in place of the main agent M described above.
【００３５】そして、複合ポリマーエマルジョンＰを攪
拌容器に入れ、主剤Ｍを徐々に加えながらハンドミキサ
ーで攪拌し、ポリマーセメントを製造した。Then, the composite polymer emulsion P was put into a stirring vessel, and the mixture was stirred with a hand mixer while gradually adding the base material M to produce a polymer cement.
【００３６】なお、ポリマーセメントの配合比は、複合
ポリマーエマルジョンＰの１重量部に対して、主剤Ｍを
３〜５重量部とすることが望ましい。本実施例では、
１：４であった。The compounding ratio of the polymer cement is desirably 3 to 5 parts by weight of the main agent M to 1 part by weight of the composite polymer emulsion P. In this embodiment,
1: 4.
【００３７】そして、このようにして製造したポリマー
セメントを、アスファルト乳剤12に、１：１の混合比で
混合し、基布10の塗布・含浸させて、防水シートＡを製
造した。Then, the polymer cement thus produced was mixed with the asphalt emulsion 12 at a mixing ratio of 1: 1 and the base fabric 10 was applied and impregnated to produce a waterproof sheet A.
【００３８】また、接着剤13も、アスファルト乳剤12に
混合するポリマーエマルジョンやポリマーセメントとし
ては、上記したポリマーエマルジョンやポリマーセメン
トと同一組成のものを用いることができる。ただし、ポ
リマーセメントの場合、流動性を考慮して、ポリマーエ
マルジョンＰと主剤Ｍとの混合比は、１：３とした。As the adhesive 13, the same composition as the polymer emulsion or polymer cement described above can be used as the polymer emulsion or polymer cement mixed with the asphalt emulsion 12. However, in the case of the polymer cement, the mixing ratio between the polymer emulsion P and the main agent M was 1: 3 in consideration of fluidity.
【００３９】さらに、図２に上記した防水シートＡを接
着剤13を用いずに釘15によってコンクリート製又は木製
野地板からなる屋根材13に貼着する場合を示す。Further, FIG. 2 shows a case where the waterproof sheet A described above is attached to the roofing material 13 made of concrete or a wooden base plate by using the nail 15 without using the adhesive 13.
【００４０】この場合においても、アスファルト乳剤12
の特性によって、防水シートＡが釘15に弾性的に絡まる
ので、同釘打付部を通しての水の侵入も確実に防止する
ことができる。In this case, asphalt emulsion 12
Due to the above characteristics, the waterproof sheet A is elastically entangled with the nail 15, so that intrusion of water through the nail driving portion can be reliably prevented.
【００４１】なお、アスファルト乳剤とポリマーセメン
トの混合物を塗布・含浸して製造した防水シートについ
て、気体通過試験及び防水試験を行ったので、その結果
を以下に示す。A waterproof sheet manufactured by applying and impregnating a mixture of an asphalt emulsion and a polymer cement was subjected to a gas passage test and a waterproof test. The results are shown below.
【００４２】なお、気体通過試験はＪＩＳ Ｋ7126- Ａ
法 (差圧法) に基づいて、防水試験はＪＩＳ Ｋ6328に
基づいて行った。また、試料ａ, ｂ, ｃ, ｄ, ｅは、そ
れぞれ、ナイロン織布からなる厚さ0.2 mmの基布10にア
スファルト乳剤とポリマーセメントとの混合物を0.3 mm
の厚さで塗布・含浸したものを用いた。The gas passage test was performed according to JIS K7126-A.
The waterproof test was performed based on JIS K6328 based on the pressure method (differential pressure method). Samples a, b, c, d and e were prepared by mixing a mixture of asphalt emulsion and polymer cement with 0.3 mm on a 0.2 mm thick base cloth 10 made of a woven nylon fabric.
The one coated and impregnated with a thickness of.
【００４３】 (気体通過試験)(試験気体: 空気) (気体透過度 ml/m2・24h ・atm) 試料ａ 10000以上 試料ｂ 10000以上 試料ｃ 10000以上 試料ｄ 10000以上 試料ｅ 10000以上 (防水試験)全ての試料ａ〜ｅについて 1kfg/cm2 で１分
間保持したが、漏水その他の異常は認められなかった。[0043] (gas passage test) (test gas: air) (gas permeability ml / m 2 · 24h · atm ) samples a 10000 or more samples b 10000 more samples c 10000 more samples d 10000 more samples e 10000 or more (Waterproof Test ) All samples a to e were kept at 1 kfg / cm 2 for 1 minute, but no water leakage or other abnormalities were observed.
【００４４】このように、以上の試験結果からも明らか
なように、本発明に係る防水シートＡは、十分な防水機
能を有する一方で、適当な通気性を有し、防水シートと
して好適に用いることができる。As is clear from the above test results, the waterproof sheet A according to the present invention has a sufficient waterproof function, has appropriate air permeability, and is suitably used as a waterproof sheet. be able to.
【００４５】また、本発明に係る防水シートを製造する
に際して、アスファルト乳剤に混合する物質としては、
上記したポリマーエマルジョンやポリマーセメントの他
に、以下の性質を有する水性ポリウレタン系樹脂を用い
ることができ、この場合、さらに、混合物中に珪砂等の
砂状粒子を混入する。In producing the waterproof sheet according to the present invention, the substance to be mixed with the asphalt emulsion includes:
In addition to the above-described polymer emulsion and polymer cement, an aqueous polyurethane resin having the following properties can be used. In this case, sand-like particles such as silica sand are further mixed into the mixture.
【００４６】なお、図３において、22は内部に砂状粒子
23を混入したアスファルト乳剤と水性ポリウレタン系樹
脂とからなる混合物であり、接着剤13によって屋根材14
に接着されるものである。In FIG. 3, reference numeral 22 denotes sandy particles inside.
A mixture comprising an asphalt emulsion mixed with 23 and an aqueous polyurethane resin.
Is to be adhered to.
【００４７】(水性ポリウレタン系樹脂の樹脂恒数） 不揮発分 （％) : 38 ± 1.5 粘度(cp/25℃) : 1000 〜2000 pH : 7.5〜8.5 外観 :黄褐色分散体 比重 : 1.0 また、アスファルト乳剤と、水性ポリウレタン系樹脂
と、砂状粒子とは、以下の組成割合とするのが好まし
い。(Constant number of water-based polyurethane resin) Non-volatile content (%): 38 ± 1.5 Viscosity (cp / 25 ° C.): 1000-2000 pH: 7.5-8.5 Appearance: Yellow-brown dispersion Specific gravity: 1.0 It is preferable that the emulsion, the aqueous polyurethane resin, and the sand-like particles have the following composition ratios.
【００４８】 アスファルト乳剤 : 70重量部 水性ポリウレタン系樹脂 : 30重量部 砂状粒子 : 30〜100 重量部 上記した防水シートについて耐水圧試験 (JIS L 1092-A
法 (低水圧法) 及び水蒸気透過試験(JIS Z 0208)を行っ
たところ、その結果は、それぞれ、2000 mmH(0.2 kgf/c
m2) 、及び、2000 ml/cm2 ・24H であった。Asphalt emulsion: 70 parts by weight Aqueous polyurethane resin: 30 parts by weight Sandy particles: 30 to 100 parts by weight Water resistance test (JIS L 1092-A) for the above waterproof sheet
Method (low water pressure method) and water vapor permeation test (JIS Z 0208), the results were 2000 mmH (0.2 kgf / c
m 2 ) and 2000 ml / cm 2 · 24H.
【００４９】これらの結果から明らかなように、アスフ
ァルト乳剤に水性ポリウレタン系樹脂及び珪砂等の砂状
粒子を混合したものを基布に塗布したものは、アスファ
ルト乳剤にポリマーエマルジョンを混合したものを基布
に塗布した場合と比較して、水蒸気、即ち、気体透過性
を100 倍向上できることがわかった。As is apparent from these results, the asphalt emulsion mixed with an aqueous polyurethane resin and sandy particles such as silica sand was applied to the base cloth, and the asphalt emulsion mixed with the polymer emulsion was mixed with the asphalt emulsion. It was found that the water vapor, that is, the gas permeability, could be improved 100 times as compared with the case where it was applied to a cloth.
【００５０】[0050]
【効果】上記したように、本発明に係る防水シートは、
可撓性を有する基布に、アスファルト乳剤、アスファル
ト乳剤とポリマーエマルジョンとの混合物、アスファル
ト乳剤とポリマーセメントとの混合物、アスファルト乳
剤と水性ポリウレタン系樹脂と珪砂等の砂状粒子との混
合物のいずれかを塗布・含浸することによって製造する
ことにしている。As described above, the waterproof sheet according to the present invention is
Either an asphalt emulsion, a mixture of an asphalt emulsion and a polymer emulsion, a mixture of an asphalt emulsion and a polymer cement, or a mixture of an asphalt emulsion, an aqueous polyurethane resin, and sand-like particles such as silica sand on a flexible base fabric. Is applied and impregnated.
【００５１】従って、以下の効果を奏する。Therefore, the following effects are obtained.
【００５２】 上記した防水シートに含浸させたアス
ファルト乳剤、ポリマーエマルジョン、ポリマーセメン
ト及び水性ポリウレタン系樹脂は、それぞれ、十分な防
水機能を有する一方で、適当な通気性を有する。従っ
て、防水シートは、雨水等の構造物内部への侵入を確実
に防止することができるとともに、コンクリート製の屋
根材等の内部から同屋根材等の表面に上昇して水蒸気
を、速やかに通過させて、大気中に放出することがで
き、シート内部滞留水蒸気による防水シートの破損も確
実に防止することができる。The asphalt emulsion, the polymer emulsion, the polymer cement, and the aqueous polyurethane resin impregnated in the above-mentioned waterproof sheet each have a sufficient waterproof function and also have appropriate air permeability. Therefore, the waterproof sheet can reliably prevent rainwater or the like from entering the inside of the structure, and ascends from the inside of the concrete roofing material or the like to the surface of the roofing material or the like and quickly passes water vapor. As a result, the waterproof sheet can be released into the atmosphere, and damage to the waterproof sheet due to water vapor retained in the sheet can be reliably prevented.
【００５３】基布は可撓性を有するとともに、アスフ
ァルト乳剤等も一定の伸縮性を有するので、ビル等の屋
根材等のコンクリート壁面が曲面をなしている場合であ
っても、容易に、同壁面に沿って防水シートを貼着する
ことができる。Since the base cloth is flexible and the asphalt emulsion and the like also have a certain degree of elasticity, even when the concrete wall surface of a roof material of a building or the like has a curved surface, the same can be easily obtained. A waterproof sheet can be attached along the wall surface.
【００５４】基布は可撓性を有するとともに、アスフ
ァルト乳剤等も一定の伸縮性を有するので、ひび割れ追
随性もあり、コンクリートにある程度のひび割れが起き
ても、防水シートは十分に伸びて、外部からの水の侵入
を防ぐことができる。The base cloth is flexible and the asphalt emulsion and the like also have a certain degree of elasticity, so that the base cloth has cracking followability. Water from the water can be prevented.
【００５５】[0055]
【図１】本発明に係る防水シートの製造方法の工程説明
図である。FIG. 1 is a process explanatory view of a method for producing a waterproof sheet according to the present invention.
【図２】本発明に係る防水シートの他の貼着方法の説明
図である。FIG. 2 is an explanatory view of another method of attaching a waterproof sheet according to the present invention.
【図３】本発明に係る防水シートの他の貼着方法の説明
図である。FIG. 3 is an explanatory view of another method of attaching the waterproof sheet according to the present invention.
Ａ 防水シート 10 基布 11 吹付装置 12 アスファルト乳剤 13 接着剤 14 屋根材 15 釘 22 混合物 23 砂状粒子 A Waterproof sheet 10 Base cloth 11 Sprayer 12 Asphalt emulsion 13 Adhesive 14 Roofing material 15 Nail 22 Mixture 23 Sandy particles
Claims (2)
とポリマーエマルジョンとの混合物、アスファルト乳剤
とポリマーセメントとの混合物、アスファルト乳剤と水
性ポリウレタン系樹脂と珪砂等の砂状粒子との混合物の
いずれかを塗布・含浸して製造する防水シートの製造方
法であって、前記ポリマーセメントは、酸化珪素、酸化
カルシウム、酸化鉄を主成分とした主材に、少なくとも
アクリル酸エステル共重合体を主成分としてなる複合ポ
リマーエマルジョンを混和して生成したものからなるこ
とを特徴とする防水シートの製造方法。A base fabric having 1. A flexible, a mixture of asphalt emulsion and polymer emulsion, a mixture of asphalt emulsion and polymer cement, a mixture of bitumen emulsion and an aqueous polyurethane resin and sand-like particles such as silica sand How to make a waterproof sheet manufactured by applying and impregnating any of
Wherein the polymer cement is silicon oxide, oxidized
At least the main material mainly composed of calcium and iron oxide
A composite resin containing an acrylate copolymer as a main component
A method for producing a waterproof sheet, comprising a product formed by mixing a rimer emulsion .
あることを特徴とする請求項１記載の防水シートの製造
方法。2. The method for producing a waterproof sheet according to claim 1, wherein the flexible base fabric is a woven fabric or a non-woven fabric.