JP3197456B2 - Anti-slip cardboard - Google Patents
Anti-slip cardboardInfo
- Publication number
- JP3197456B2 JP3197456B2 JP05703595A JP5703595A JP3197456B2 JP 3197456 B2 JP3197456 B2 JP 3197456B2 JP 05703595 A JP05703595 A JP 05703595A JP 5703595 A JP5703595 A JP 5703595A JP 3197456 B2 JP3197456 B2 JP 3197456B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- slip
- resin layer
- water
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、梱包用段ボ−ルケ−ス
の運搬時等の荷崩れ防止対策として防滑性、且つ流通段
階における雨等に対する耐水性を向上させ、かつ土埃等
の汚れも付着しにくい段ボ−ルに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention improves slip resistance and water resistance to rain and the like at the distribution stage as a countermeasure for preventing the collapse of the packing when transporting the corrugated ball case, and dirt such as dust. This also relates to a step ball that is difficult to adhere to.
【０００２】[0002]
【従来の技術】梱包用段ボ−ルケ−スの運搬時等の荷崩
れ防止対策としては、バンド掛け、シュリンク包装、ス
トレッチラップ、また接着剤による固定等の方法が使用
されてきた。しかし、これらの方法では、いずれも流通
段階において設備、材料等の負担があり、かつ積替えを
行った際、再度固定しなければならない問題があった。
特に接着剤による固定方法では表面に剥がれが起きる、
あるいは接着剤が残るため美粧性を大きく損ねる問題が
あった。2. Description of the Related Art As a countermeasure for preventing the collapse of a packing when carrying a corrugated ball case, methods such as banding, shrink wrapping, stretch wrap, and fixing with an adhesive have been used. However, all of these methods have a problem that equipment and materials are burdened at the distribution stage, and that they must be fixed again when transshipment is performed.
Especially with the fixing method with adhesive, peeling occurs on the surface,
Alternatively, there is a problem in that the adhesive remains and the cosmetics are greatly impaired.
【０００３】この問題を解決するため、段ボ−ルの表面
に樹脂層を形成して防滑性を持たせ、運搬時の荷崩れを
防止する方法が各種提案されている（特開昭６１−２９
６１９８号、特公昭６３−５２０６５号等）。この方法
では滑り角度４０°以上の高い防滑性を持たせることは
不可能であった。そこでこの点をさらに改良して、環境
安定性にも優れた防滑性段ボ−ルが提案されている（特
開平３−１１８１４７号）。この方法では高い防滑性及
び耐ブロッキング性が得られるが、汚れが付き易く、落
ちにくい。そして、水に濡れた場合、段ボ−ルの強度が
低下するという問題があった。In order to solve this problem, various methods have been proposed for forming a resin layer on the surface of the corrugated ball so as to have an anti-slipping property and to prevent collapse of the load during transportation (Japanese Patent Laid-Open No. 61-1986). 29
No. 6198, JP-B-63-52065, etc.). With this method, it was impossible to provide high slip resistance of a slip angle of 40 ° or more. In view of the above, a slip-resistant corrugated ball with improved environmental stability has been proposed (JP-A-3-118147). With this method, high anti-slip properties and anti-blocking properties can be obtained, but they are easily stained and hard to remove. When wet with water, there is a problem that the strength of the corrugated ball is reduced.
【０００４】その他、ポリエ−テル変性シリコ−ンオイ
ルを添加してブロッキングや汚れを改良する方法も提案
されている（特開平５−３３２９５号）が、この方法で
は防滑性段ボ−ルを製造した直後の性能は良好だが、経
時により添加したポリエ−テル変性シリコ−ンオイルが
表面に浮き、防滑性が低下するという問題があった。[0004] In addition, there has been proposed a method of improving blocking and stain by adding a polyether-modified silicone oil (Japanese Patent Application Laid-Open No. 5-33295). However, in this method, an anti-slip corrugated ball was manufactured. Although the performance immediately after was good, there was a problem that the polyether-modified silicone oil added over time floated on the surface and the slip resistance was reduced.
【０００５】[0005]
【発明が解決しようとする課題】本発明は上記のような
従来技術の問題点に着目したもので、更に高い防滑性を
有し、撥水性、耐汚染性に優れ、かつ経時安定性にも優
れた防滑性段ボ−ルを提供することを目的とする。SUMMARY OF THE INVENTION The present invention focuses on the above-mentioned problems of the prior art, and has higher slip resistance, excellent water repellency, excellent stain resistance, and stability over time. An object of the present invention is to provide an excellent anti-slip corrugated ball.
【０００６】[0006]
【課題を解決するための手段】本発明は上記課題を解決
するために考えられたもので、防滑性を低下させない反
応性樹脂及びモノマーからなる撥水性のある添加剤を添
加した樹脂を用いて撥水性のある下地樹脂層を設けた上
に防滑性樹脂層を設けたことを特徴とする防滑性段ボー
ルであり、さらに本発明は前記防滑性樹脂層の樹脂が、
アクリル樹脂、スチレン樹脂、酢酸ビニル樹脂、ウレタ
ン樹脂、ゴム、塩化ビニル樹脂、あるいはこれらをブレ
ンドしたものの中から選ばれた一つであり、この樹脂に
シリカ等の無機粒子を添加したものであることを特徴と
する防滑性段ボールである。 また本発明は、前記下地樹
脂層の樹脂が、不飽和カルボン酸またはそのエステルで
あって、アクリル酸、メタクリル酸、マレイン酸、フタ
ル酸、あるいはそれらのエステルを重合させたもの、ま
たは、スチレン、酢酸ビニル、塩化ビニル、ウレタンゴ
ム、あるいはこれらを混合したものの中から選ばれた一
つであり、この樹脂に前記防滑性を低下させない反応性
樹脂及びモノマーからなる撥水性のある添加剤を添加し
たものであることを特徴とする防滑性段ボールである。
また、本発明は、前記下地樹脂層の添加剤が、撥水性を
有するシリル基を持つ反応性モノマーまたはポリマー、
有機樹脂とシリコーンを反応させた変性樹脂、撥水性を
有するフッ素を含有するモノマーまたはポリマー、ある
いはこのモノマーまたはポリマーとビニルモノマーを共
重合させた樹脂、フッ素を含有するエポキシ樹脂、また
はフッ素を含有するシリコーンの中から選ばれた少なく
とも一つであることを特徴とする防滑性段ボールであ
る。 また本発明は、前記下地樹脂層が成膜性に優れ、防
滑性樹脂層を浸透させないことを特徴とする防滑性段ボ
ールである。 また本発明は、前記防滑性樹脂層が額縁、
ストライプ等のパターン状に印刷により設けられている
ことを特徴とする防滑性段ボールである。 DISCLOSURE OF THE INVENTION The present invention has been conceived to solve the above-mentioned problems, and is not limited to a method which does not lower the slip resistance.
Add a water-repellent additive consisting of reactive resin and monomer
After providing a water-repellent base resin layer using the added resin
Anti-slip corrugated board characterized by providing an anti-slip resin layer on the
Is Le, further the present invention is a resin of the slip resistant resin layer,
Acrylic resin, styrene resin, vinyl acetate resin, urethane
Resin, rubber, vinyl chloride resin, or
One selected from the
It is characterized by adding inorganic particles such as silica.
Is a non-slip corrugated cardboard. Further, the present invention provides
The resin of the fatty layer is an unsaturated carboxylic acid or its ester.
Acrylic acid, methacrylic acid, maleic acid, lid
Or a polymerized version of phosphoric acid or their esters, or
Or styrene, vinyl acetate, vinyl chloride, urethane
Or a mixture of these
The reactivity of this resin does not reduce the slip resistance.
Add water-repellent additives consisting of resin and monomer
It is a non-slip corrugated cardboard characterized by the following.
Further, the present invention provides the base resin layer, wherein the additive has a water repellency.
A reactive monomer or polymer having a silyl group having
Modified resin made by reacting organic resin and silicone, water repellency
A fluorine-containing monomer or polymer, having
Or vinyl monomer with this monomer or polymer
Polymerized resin, epoxy resin containing fluorine, or
Is selected from among fluorine-containing silicones
A non-slip corrugated cardboard characterized in that
You. Further, in the present invention, the undercoat resin layer has excellent film-forming properties,
Anti-slip corrugated board characterized by not penetrating the lubricating resin layer
It is. Further, in the present invention, the anti-slip resin layer is a frame,
It is provided by printing in a pattern such as a stripe
A non-slip corrugated cardboard characterized in that:
【０００７】以下、本発明を詳細に説明する。（図１）
は、本発明の防滑性段ボ−ルの断面図である。防滑性段
ボ−ルは表紙（１）、印刷層（２）、下地樹脂層
（３）、防滑性樹脂層（４）及び片面段ボール（５）か
ら構成されている。また、防滑性樹脂層（４）は（図
２）（図３）に示すように額縁状、ストライプ状等のパ
ターン状に設けてもよい。Hereinafter, the present invention will be described in detail. (Fig. 1)
FIG. 1 is a sectional view of a non-slip corrugated ball of the present invention. The slip-resistant cardboard ball comprises a cover (1), a printed layer (2), a base resin layer (3), a slip-resistant resin layer (4), and a single-sided cardboard (5). Further, the anti-slip resin layer (4) may be provided in a pattern such as a frame shape or a stripe shape as shown in FIGS.
【０００８】本発明に使用される表紙（１）としては通
常段ボ−ルライナ−として利用されるものならば何れも
利用可能で、クラフトライナ−、白ライナ−、コートボ
ール等が利用可能である。As the cover (1) used in the present invention, any cover can be used as long as it is generally used as a corrugated ball liner, and a craft liner, a white liner, a coated ball and the like can be used. .
【０００９】また、本発明に使用される印刷層（２）
は、通常の紙用印刷インキによって形成が可能であり、
スチレン、アクリル等をバインダ−とし顔料を加えた任
意のインキが使用できる。The printing layer (2) used in the present invention
Can be formed with ordinary paper printing ink,
Any ink containing styrene, acrylic or the like as a binder and a pigment can be used.
【００１０】本発明に使用される下地樹脂層（３）は、
以下に述べる樹脂と添加剤がブレンドされたワニスが使
用される。The undercoat resin layer (3) used in the present invention comprises:
A varnish in which a resin and additives described below are blended is used.
【００１１】樹脂としては、不飽和カルボン酸またはそ
のエステル、すなわち、アクリル酸、メタクリル酸、マ
レイン酸、フタル酸やそれらのエステルを重合させたも
の、また、スチレン、酢酸ビニル、塩化ビニル、ウレタ
ンゴム、あるいはこれらを混合したものが用いられる。As the resin, unsaturated carboxylic acids or esters thereof, that is, those obtained by polymerizing acrylic acid, methacrylic acid, maleic acid, phthalic acid or esters thereof, styrene, vinyl acetate, vinyl chloride, urethane rubber Or a mixture of these is used.
【００１２】添加剤としては、撥水性を持つシリル基を
持つ反応性モノマ−またはポリマー、すなわち、メタク
リル変性シリコ−ン、長鎖アルキル変性シリコ−ン、ビ
ニルメチルポリシロキサン、メチルハイドロジェルポリ
シロキサン、あるいは有機樹脂とシリコ−ンレジンを反
応させた変性樹脂、すなわちシリコ−ンアルキッド、シ
リコ−ンポリエステル、シリコ−ンアクリル、シリコ−
ンエポキシ、シリコ−ンフェノ−ル等が用いられる。ま
た、撥水性を持つフッ素を含有するモノマ−またはポリ
マー、あるいはこのモノマ−またはポリマーとビニルモ
ノマ−を共重合させた樹脂、フッ素を含有するエポキシ
樹脂、フッ素を含有するシリコ−ン等の含フッ素樹脂が
用いられる。Examples of the additive include a reactive monomer or polymer having a silyl group having water repellency, that is, methacryl-modified silicone, long-chain alkyl-modified silicone, vinylmethylpolysiloxane, methylhydrogelpolysiloxane, Alternatively, a modified resin obtained by reacting an organic resin with a silicone resin, that is, silicone alkyd, silicone polyester, silicone acryl, silicone
Epoxy, silicone phenol, and the like are used. Further, a fluorine-containing monomer or polymer having water repellency, or a resin obtained by copolymerizing this monomer or polymer with a vinyl monomer, a fluorine-containing epoxy resin, or a fluorine-containing resin such as a fluorine-containing silicone. Is used.
【００１３】添加剤の添加量としては、モノマ−の場
合、樹脂固形分に対し、０．１乃至３％が好ましい。こ
れは０．１％未満では撥水性、耐水性の性能が殆ど、見
られず、３％を越えると添加剤の分散性が悪いため、樹
脂との混合が不充分になるか、あるいは添加剤が分離し
てしまうためである。但し、変性樹脂の場合、２乃至５
０％まで添加することが可能である。この場合も２％未
満では撥水性、耐水性の性能が殆ど、見られず、５０％
を越えると添加剤の分散性が悪いため、樹脂との混合が
不充分になるか、あるいは添加剤が分離してしまうため
である。In the case of a monomer, the amount of the additive is preferably 0.1 to 3% based on the solid content of the resin. When the content is less than 0.1%, water repellency and water resistance are hardly observed, and when it exceeds 3%, the dispersibility of the additive is poor. Is to be separated. However, in the case of a modified resin, 2 to 5
It is possible to add up to 0%. Also in this case, if less than 2%, almost no water repellency and water resistance performance is observed, and 50%
If the ratio exceeds the above range, the dispersibility of the additive is poor, so that the mixing with the resin becomes insufficient or the additive is separated.
【００１４】防滑性樹脂層（４）としては、アクリル樹
脂、スチレン樹脂、酢酸ビニル樹脂、ウレタン樹脂、ゴ
ム、塩化ビニル樹脂、あるいはこれらをブレンドしたも
のが用いられ、さらに耐熱性、ブロッキング性を向上さ
せるためにシリカ等の無機粒子を添加すると良い。As the anti-slip resin layer (4), an acrylic resin, a styrene resin, a vinyl acetate resin, a urethane resin, a rubber, a vinyl chloride resin, or a blend thereof is used, and the heat resistance and the blocking property are further improved. For this purpose, it is preferable to add inorganic particles such as silica.
【００１５】本発明に使用する片面段ボ−ル（５）の素
材としては通常使用されているライナー・中芯であれば
何れも利用可能である。As the material of the single-sided step ball (5) used in the present invention, any commonly used liner / core can be used.
【００１６】インキ、下地樹脂層、防滑性樹脂層の印刷
はグラビア印刷、フレキソ印刷、オフセット印刷、コン
マコ−ト、マイクログラビアコ−ト等任意の印刷方式が
可能であるが、パタ−ン印刷ができる方式が望ましい。The printing of the ink, the underlying resin layer, and the anti-slip resin layer can be performed by any printing method such as gravure printing, flexographic printing, offset printing, comma coating, and microgravure coating. A system that can do so is desirable.
【００１７】[0017]
【作用】本発明によれば、防滑性樹脂層により高い防滑
性及び下地樹脂層における撥水性添加剤により耐水性、
耐汚染性が付与された優れた防滑性段ボ−ルを提供する
ことを可能とする。また、下地樹脂層に添加する撥水性
樹脂を反応性の樹脂及びモノマ−を用いることにより経
時安定性も向上する。また、防滑性樹脂層を額縁、スト
ライプ等のパタ−ン状に設けることにより、防滑性を防
滑性樹脂層で持たせ、撥水性、耐汚染性に優れる下地樹
脂層が表面に一部だけ現れることになるため、高い防滑
性を維持したまま、撥水性、耐汚染性を更に向上させる
ことが可能となる。According to the present invention, the anti-slip resin layer has a high anti-slip property, and the water-repellent additive in the base resin layer has water resistance.
It is possible to provide an excellent anti-slip corrugated ball provided with stain resistance. Further, by using a reactive resin and a monomer as the water-repellent resin to be added to the base resin layer, the stability over time is also improved. Further, by providing the anti-slip resin layer in a pattern such as a frame or a stripe, the anti-slip property is imparted to the anti-slip resin layer, and only a part of the base resin layer having excellent water repellency and stain resistance appears on the surface. Therefore, it is possible to further improve water repellency and stain resistance while maintaining high slip resistance.
【００１８】[0018]
【実施例】以下、本発明の実施例を説明する。Embodiments of the present invention will be described below.
【００１９】＜実施例１＞ 〔ライナ−〕 Ｋ１８０ （東海パルプ株式会社製） 坪量 １８０ｇ／ｍ2 〔印刷層〕 ＸＧＷ ＮＤ （サカタインクス株式会社製） 塗布量 １．５ｇ／ｍ2 〔下地樹脂層〕 モビニ−ル ８０２０ （ヘキスト合成株式会社製） １００部 アルコキシシラン−メタクリレ−トラジカル重合樹脂 ５部 （信越シリコーン株式会社製） 塗布量 ２．０ｇ／ｍ2 〔防滑性樹脂層〕 アクリル酸エチル−コロイダルシリカ複合エマルション １００部 （東洋インキ製造株式会社製） 塗布量 ２．５ｇ／ｍ2 上記材料を用い、印刷層、下地樹脂層、防滑性樹脂層す
べてを全面に塗布し、片面段ボ−ルと貼合し、段ボ−ル
シ−トを作成した。<Example 1> [Liner] K180 (manufactured by Tokai Pulp Co., Ltd.) Basis weight 180 g / m 2 [printing layer] XGW ND (manufactured by Sakata Inx Co., Ltd.) Coating amount 1.5 g / m 2 [base resin layer Movinyl 8020 (manufactured by Hoechst Gosei Co., Ltd.) 100 parts Alkoxysilane-methacrylate radical polymerized resin 5 parts (manufactured by Shin-Etsu Silicone Co., Ltd.) Coating amount 2.0 g / m 2 [anti-slip resin layer] Ethyl acrylate-colloidal Silica composite emulsion 100 parts (manufactured by Toyo Ink Mfg. Co., Ltd.) Coating amount 2.5 g / m 2 Using the above materials, apply a printing layer, a base resin layer, and a non-slip resin layer all over the surface, The sheets were laminated to form a corrugated ball sheet.
【００２０】＜実施例２＞実施例１と同様のライナ−、
印刷層、下地樹脂層、防滑性樹脂層を用い、印刷層、下
地樹脂層は全面に塗布し、防滑性樹脂層は幅２０ｍｍの
ストライプパタ−ンにて塗布し、片面段ボ−ルと貼合
し、段ボ−ルシ−トを作成した。<Embodiment 2> A liner similar to that of Embodiment 1
Using a printing layer, a base resin layer, and a non-slip resin layer, the print layer and the base resin layer are applied over the entire surface, and the anti-slip resin layer is applied with a stripe pattern having a width of 20 mm. Then, a corrugated ball sheet was prepared.
【００２１】＜実施例３＞実施例１と同様のライナ−、
印刷層、防滑性樹脂層と下記下地樹脂層を用い、すべて
を全面に塗布し、片面段ボ−ルと貼合し、段ボ−ルシ−
トを作成した。 〔下地樹脂層〕 モビニ−ル ８０００ （ヘキスト合成株式会社製） １００部 水性シリコ−ンポリエステル （信越シリコ−ン株式会社製） ３部 塗布量 ２．０ｇ／ｍ2 <Embodiment 3> A liner similar to that of Embodiment 1
Using a printing layer, an anti-slip resin layer and the undercoating resin layer described below, apply all over the entire surface and paste it on a single-sided step ball to form a step ball seal.
Created. [Base resin layer] Movinyl 8000 (manufactured by Hoechst Gosei Co., Ltd.) 100 parts Water-based silicone polyester (manufactured by Shin-Etsu Silicone Co., Ltd.) 3 parts Coating amount 2.0 g / m 2
【００２２】＜実施例４＞実施例１と同様のライナ−、
印刷層、防滑性樹脂層と下記下地樹脂層を用い、すべて
を全面に塗布し、片面段ボ−ルと貼合し、段ボ−ルシ−
トを作成した。 〔下地樹脂層〕 モビニ−ル ８０００ （ヘキスト合成株式会社製） １００部 クロロトリフルオロエチレン（デュポン株式会社製） ０．５部 塗布量 ２．０ｇ／ｍ2 <Embodiment 4> A liner similar to that of Embodiment 1
Using a printing layer, an anti-slip resin layer and the undercoating resin layer described below, apply all over the entire surface and paste it on a single-sided step ball to form a step ball seal.
Created. [Base resin layer] Movinyl 8000 (manufactured by Hoechst Gosei Co., Ltd.) 100 parts Chlorotrifluoroethylene (manufactured by DuPont) 0.5 part Coating amount 2.0 g / m 2
【００２３】＜比較例１＞実施例１と同様のライナ−、
印刷層と下記樹脂層を用い、すべての層を全面に塗布
し、片面段ボ−ルと貼合し、段ボ−ルシ−トを作成し
た。 〔下地樹脂層〕 スチレン−アクリル共重合体エマルション １００部 （東洋インキ製造株式会社製） シリカ（東洋インキ製造株式会社製） ４０部 ポリエ−テル変性シリコ−ンオイル ０．５部 （東レ・ダウコ−ティング株式会社製） 塗布量 ２．５ｇ／ｍ2 Comparative Example 1 A liner similar to that of Example 1
Using a printed layer and the following resin layer, all the layers were coated on the entire surface and bonded to a single-sided step ball to form a step ball sheet. [Base resin layer] Styrene-acrylic copolymer emulsion 100 parts (Toyo Ink Mfg. Co., Ltd.) Silica (Toyo Ink Mfg. Co., Ltd.) 40 parts Polyether-modified silicone oil 0.5 part (Toray Dow Coating) Co., Ltd.) Coating amount 2.5g / m 2
【００２４】＜比較例２＞実施例１と同様のライナ−、
印刷層、防滑性樹脂層及び比較例１と同様の下地樹脂層
を用い、印刷層と下地樹脂層は全面に、防滑性樹脂層は
幅２０ｍｍのストライプパタ−ンにて塗布し、片面段ボ
−ルと貼合し、段ボ−ルシ−トを作成した。Comparative Example 2 A liner similar to that of Example 1
A printing layer, an anti-slip resin layer and an under resin layer similar to that of Comparative Example 1 were used. The printing layer and the under resin layer were applied over the entire surface, and the anti-slip resin layer was applied with a stripe pattern having a width of 20 mm. To form a corrugated ball sheet.
【００２５】＜比較例３＞実施例１と同様のライナ−、
印刷層、防滑性樹脂層と下記下地樹脂層を用い、すべて
の層を全面に塗布し、片面段ボ−ルと貼合し、段ボ−ル
シ−トを作成した。 スチレン樹脂（サカタインクス株式会社製） 塗布量 ３．５ｇ／ｍ2 Comparative Example 3 A liner similar to that of Example 1
Using a printing layer, an anti-slip resin layer, and the undercoating resin layer described below, all layers were coated on the entire surface and bonded to a single-sided step ball to form a step ball sheet. Styrene resin (made by Sakata Inx Co., Ltd.) Coating amount 3.5 g / m 2
【００２６】＜比較例４＞実施例１と同様のライナ−、
印刷層、防滑性樹脂層を用い、下地樹脂層をコ−トせ
ず、印刷層、防滑性樹脂層を全面に塗布し、片面段ボ−
ルと貼合し、段ボ−ルシ−トを作成した。Comparative Example 4 A liner similar to that of Example 1
Using a printing layer and a non-slip resin layer, without coating the underlying resin layer, apply the printing layer and the non-slip resin layer to the entire surface,
To form a corrugated ball sheet.
【００２７】上記実施例及び、比較例で得た、段ボ−ル
シ−トを用い、防滑性、撥水性、耐汚染性、耐水性を評
価した。その結果を（表１）に示す。Using the stepped ball sheets obtained in the above Examples and Comparative Examples, the slip resistance, water repellency, stain resistance and water resistance were evaluated. The results are shown in (Table 1).
【００２８】[0028]
【表１】 [Table 1]
【００２９】防滑性はＪＩＳＰ８１１１に規定する標準
状態（２０℃ ６５％）にてＪＩＳＰ８１４７に規定さ
れる傾斜方式によりすべり角度を測定した。測定は、シ
−ト作成から３日後と３週間後行った。撥水性はＪＩＳ
Ｐ８１１１に規定する標準状態にてＪＩＳＰ８１３７に
規定される方法にて測定した。耐汚染性はＪＩＳＰ８１
１１に規定する標準状態にてシ−ト表面をゼロックスト
ナ−で汚染させ、余分なトナ−を叩き落とした後、汚染
させる前との色差（ΔＥ）を測定した。色差が４０以上
の場合を×、３０から３９の場合を△、１０から２９の
場合を○、１０未満の場合を◎とした。耐水性はＪＩＳ
Ｐ８１１１に規定する標準状態にてＪＩＳＰ８１４０に
規定される方法にて行った。試験時間は２分、単位はｇ
／ｍ2 である。For the slip resistance, the slip angle was measured in a standard condition (20 ° C., 65%) specified by JISP8111 by a tilt method specified by JISP8147. The measurement was performed three days and three weeks after the preparation of the sheet. Water repellency is JIS
It was measured by the method specified in JISP8137 under the standard conditions specified in P8111. Stain resistance is JISP81
After the sheet surface was contaminated with Xerox toner under the standard condition specified in No. 11, the excess toner was knocked down, and the color difference (ΔE) from before the contamination was measured. The case where the color difference was 40 or more was rated X, the case where the color difference was 30 to 39 was rated Δ, the case where the color difference was 10 to 29 was rated Good, and the case where the color difference was less than 10 was rated Excellent. Water resistance is JIS
The measurement was performed by the method specified in JISP8140 under the standard condition specified in P8111. Test time is 2 minutes, unit is g
/ M 2 .
【００３０】[0030]
【発明の効果】本発明により高い防滑性及び耐水性、撥
水性、耐汚染性に優れた防滑性段ボ−ルを提供すること
ができる。また、下地樹脂層に、防滑性を低下させない
反応性樹脂及びモノマーから成る撥水性添加剤を添加し
たものを用いれば、さらに高い防滑性を維持しつつ、耐
水性、撥水性、耐汚染性を付与することができる。According to the present invention, it is possible to provide an anti-slip corrugated ball having excellent anti-slip properties and excellent water resistance, water repellency and stain resistance. In addition, if a base resin layer containing a water-repellent additive made of a reactive resin and a monomer that does not reduce the slip resistance is used, water resistance, water repellency, and stain resistance can be improved while maintaining higher slip resistance. Can be granted.
【００３１】さらに下地樹脂層として成膜性に優れ、防
滑性樹脂層を浸透させない樹脂を用いることにより防滑
性樹脂が印刷層、表紙に吸い込まれず、経時によって防
滑効果が劣化することがなく、防滑性樹脂層を額縁、ス
トライプ等のパタ−ン状に設ければ、防滑性を維持しつ
つ、撥水性、耐汚染性に優れる下地樹脂層が段ボールの
表面に一部現れるため、さらに高い撥水性、耐汚染性を
得ることができるという面で、さらに実用性の優れた防
滑性段ボ−ルシートが得られる。Further, by using a resin which is excellent in film-forming properties and does not penetrate the anti-slip resin layer as the base resin layer, the anti-slip resin is not absorbed into the printed layer and the cover, and the anti-slip effect is not deteriorated with the passage of time. If the conductive resin layer is provided in a pattern such as a frame or a stripe, the base resin layer having excellent water repellency and contamination resistance appears on the surface of the corrugated cardboard while maintaining the slip resistance. Thus, a non-slip corrugated ball sheet which is more practical in terms of obtaining stain resistance can be obtained.
【００３２】また、下地樹脂層の樹脂及び添加剤として
は様々の種類の樹脂を用いることができ、その組合せも
幾通りも考えられるので、要求される撥水性、耐汚染
性、防滑性に応じて選択することができ、広い用途に展
開することができる。Further, various kinds of resins can be used as the resin of the base resin layer and the additives, and various combinations of the resins can be considered. Therefore, depending on the required water repellency, stain resistance and slip resistance, Can be selected for use in a wide range of applications.
【図１】本発明の一実施例の断面図である。FIG. 1 is a sectional view of one embodiment of the present invention.
【図２】本発明の防滑性樹脂層の形成パターンの一例を
示す平面図である。FIG. 2 is a plan view showing an example of a formation pattern of a slip resistant resin layer of the present invention.
【図３】本発明の防滑性樹脂層の形成パターンの別の例
を示す平面図である。FIG. 3 is a plan view showing another example of the formation pattern of the anti-slip resin layer of the present invention.
１ 表紙 ２ 印刷層 ３ 下地樹脂層 ４ 防滑性樹脂層 ５ 片面段ボール DESCRIPTION OF SYMBOLS 1 Cover 2 Printing layer 3 Base resin layer 4 Anti-slip resin layer 5 Single-sided cardboard
───────────────────────────────────────────────────── フロントページの続き (72)発明者 長幡 信昭 東京都渋谷区神宮前六丁目26番１号 麒 麟麦酒株式会社内 審査官 川端 康之 (56)参考文献 特開 昭58−197394（ＪＰ，Ａ) 特開 平４−178476（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 D21H 11/00 - 27/42 ──────────────────────────────────────────────────続 き Continuation of the front page (72) Nobuaki Nagahata Inventor, Kirin Brewery Co., Ltd. 6-26-1, Jingumae, Shibuya-ku, Tokyo Investigator Yasuyuki Kawabata (56) References JP-A-58-197394 (JP, A) JP-A-4-178476 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) B32B 1/00-35/00 D21H 11/00-27/42
Claims (6)
マーからなる撥水性のある添加剤を添加した樹脂を用い
て撥水性のある下地樹脂層を設けた上に防滑性樹脂層を
設けたことを特徴とする防滑性段ボール。Claims: 1. A reactive resin and a monolithic resin which do not lower the slip resistance.
1. A non-slip corrugated cardboard comprising a water-repellent base resin layer provided on a water-repellent base resin layer using a resin to which a water-repellent additive made of a polymer is added.
脂、スチレン樹脂、酢酸ビニル樹脂、ウレタン樹脂、ゴ
ム、塩化ビニル樹脂、あるいはこれらをブレンドしたも
のの中から選ばれた一つであり、この樹脂にシリカ等の
無機粒子を添加したものであることを特徴とする請求項
１記載の防滑性段ボール。Wherein the resin of said slip resistant resin layer, an acrylic resin, styrene resin, vinyl acetate resin, urethane resin, rubber is one selected from among a blend vinyl chloride resin, or these, the 2. A non-slip corrugated cardboard according to claim 1, wherein said resin is made by adding inorganic particles such as silica.
酸またはそのエステルであって、アクリル酸、メタクリ
ル酸、マレイン酸、フタル酸、あるいはそれらのエステ
ルを重合させたもの、または、スチレン、酢酸ビニル、
塩化ビニル、ウレタンゴム、あるいはこれらを混合した
ものの中から選ばれた一つであり、この樹脂に前記防滑
性を低下させない反応性樹脂及びモノマーからなる撥水
性のある添加剤を添加したものであることを特徴とする
請求項１記載の防滑性段ボール。Resins wherein the base resin layer, an unsaturated carboxylic acid or its esters, those obtained by polymerizing acrylic acid, methacrylic acid, maleic acid, phthalic acid or esters thereof, or styrene, Vinyl acetate,
Is one selected from among a mixture of vinyl chloride, urethane rubber, or these, the to the resin slip
Water-repellent made of reactive resin and monomer that does not reduce the water-repellency
The anti- slip corrugated cardboard according to claim 1, wherein a corrugated additive is added .
るシリル基を持つ反応性モノマーまたはポリマー、有機
樹脂とシリコーンを反応させた変性樹脂、撥水性を有す
るフッ素を含有するモノマーまたはポリマー、あるいは
このモノマーまたはポリマーとビニルモノマーを共重合
させた樹脂、フッ素を含有するエポキシ樹脂、またはフ
ッ素を含有するシリコーンの中から選ばれた少なくとも
一つであることを特徴とする請求項３記載の防滑性段ボ
ール。4. An additive of the undercoat resin layer is a reactive monomer or polymer having a silyl group having water repellency, a modified resin obtained by reacting an organic resin with silicone, and a monomer or polymer containing fluorine having water repellency. Or
A resin obtained by copolymerizing the monomer or the polymer with a vinyl monomer, a fluorine-containing epoxy resin , or a fluorine-containing silicone. Item 4. An anti-slip corrugated cardboard according to item 3.
脂層を浸透させないことを特徴とする請求項１記載の防
滑性段ボール。 5. The non-slip corrugated cardboard according to claim 1, wherein the undercoat resin layer has excellent film-forming properties and does not penetrate the anti-slip resin layer.
パターン状に印刷により設けられていることを特徴とす
る請求項１記載の防滑性段ボール。 6. The non- slip corrugated cardboard according to claim 1, wherein the anti-slip resin layer is provided by printing in a pattern such as a picture frame or a stripe.