JP3166438B2 - Rust prevention sheet - Google Patents

Rust prevention sheet

Info

Publication number
JP3166438B2
JP3166438B2 JP23212493A JP23212493A JP3166438B2 JP 3166438 B2 JP3166438 B2 JP 3166438B2 JP 23212493 A JP23212493 A JP 23212493A JP 23212493 A JP23212493 A JP 23212493A JP 3166438 B2 JP3166438 B2 JP 3166438B2
Authority
JP
Japan
Prior art keywords
rust
sheet
synthetic resin
preventive
nonwoven fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP23212493A
Other languages
Japanese (ja)
Other versions
JPH0789572A (en
Inventor
修 西
明 中西
俊介 塩井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
New Oji Paper Co Ltd
Oji Holdings Corp
Original Assignee
Oji Holdings Corp
Oji Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Oji Holdings Corp, Oji Paper Co Ltd filed Critical Oji Holdings Corp
Priority to JP23212493A priority Critical patent/JP3166438B2/en
Publication of JPH0789572A publication Critical patent/JPH0789572A/en
Application granted granted Critical
Publication of JP3166438B2 publication Critical patent/JP3166438B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は合成樹脂製の基材に気化
性防錆剤を含有させた防錆シートに関し、特に溶融して
再生原料として使用することができる良質の防湿耐水性
防錆シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rust preventive sheet containing a synthetic resin base material containing a vaporizable rust preventive, and more particularly to a high-quality moisture-proof and water-resistant rust preventive which can be melted and used as a recycled material. Regarding the sheet.

【０００２】[0002]

【従来の技術】気化蒸気が金属に対して防錆効果を発揮
する気化性防錆剤を支持体に含有させた防錆シートは一
般に良く知られており、産業用シートとして金属類の保
管、輸送等に巾広く実用されている。2. Description of the Related Art A rust-preventive sheet containing a vaporizable rust-preventive agent in which a vaporized vapor exerts a rust-preventing effect on a metal is generally well known. It is widely used for transportation.

【０００３】防錆シートの支持体としては、一般にクラ
フト紙、ラミネート紙、合成樹脂フィルム、各種繊維の
不織布と合成樹脂フィルムを貼り合わせたシート等が使
用されている。また、特殊用途として合成樹脂不織布と
合成樹脂フィルムと合成樹脂クロスを順次積層したシー
ト、あるいはその合成樹脂クロスの上にさらに合成樹脂
フィルムを積層したシート等も使用されている。As a support for a rust-preventive sheet, kraft paper, laminated paper, a synthetic resin film, a sheet obtained by bonding a nonwoven fabric of various fibers and a synthetic resin film, and the like are generally used. As a special use, a sheet in which a synthetic resin nonwoven fabric, a synthetic resin film, and a synthetic resin cloth are sequentially laminated, or a sheet in which a synthetic resin film is further laminated on the synthetic resin cloth, or the like is used.

【０００４】中でも、合成樹脂不織布と合成樹脂フィル
ムを貼り合わせたシートの不織布面に気化性防錆剤を含
有させた防錆シートは、優れた防湿耐水性があるために
防錆効果が高く、しかも溶融して再生原料とすることが
可能である等優れた面が多い。また、本発明者等が先に
出願した特開平５−６５１６８号公報に記載の、合成樹
脂不織布と合成樹脂フィルムと合成樹脂クロスを順次積
層したシートの不織布面に気化性防錆剤を含有させた防
錆シートは、優れた防湿耐水性を有し再生原料として使
用可能であるというメリットの他に、優れた強度を有し
ているために取扱い中に破れる危険性が低いといった特
性を有する。[0004] Above all, a rust-preventive sheet in which a non-woven fabric surface of a sheet in which a synthetic resin non-woven fabric and a synthetic resin film are bonded together contains a vaporizable rust-preventive agent has a high rust-preventive effect due to its excellent moisture-proof and water-proof properties. Moreover, there are many excellent aspects such as being able to be melted and used as a recycled material. Further, a non-woven fabric surface of a sheet in which a synthetic resin non-woven fabric, a synthetic resin film, and a synthetic resin cloth are sequentially laminated as described in Japanese Patent Application Laid-Open No. 5-65168 filed by the present inventors contains a vaporizable rust inhibitor. The rust-proof sheet has excellent moisture-proof and water-proof properties and can be used as a recycled material. In addition, the rust-proof sheet has excellent strength and therefore has a low risk of being broken during handling.

【０００５】しかし、合成樹脂不織布面に気化性防錆剤
組成物を塗布して含有させたタイプの防錆シートを使用
した結果、その性能に問題があり改良を必要とすること
が分かった。即ち、防錆シートを取扱う際に、塗布され
た防錆剤組成物が脱落し易くて、飛散した防錆剤の粉が
作業環境を悪化させたり、脱落量が多量の場合には防錆
効果が落ちる等の欠点がある。However, as a result of using a rust-preventive sheet of a type in which a vaporizable rust-preventive composition was applied to the surface of a synthetic resin nonwoven fabric, it was found that there was a problem in its performance and improvement was required. That is, when handling the rust preventive sheet, the applied rust preventive composition is easy to fall off, and the scattered rust preventive powder deteriorates the working environment, or the rust preventive effect when the amount of fall off is large. There are drawbacks such as dropping.

【０００６】[0006]

【発明が解決しようとする課題】本発明者等は、不織布
として特定の物性を有するものを使用することによって
防錆剤の脱落が極めて少なくなることを見出した。本発
明の目的は、防錆剤が脱落し難く、原料として再使用可
能な、防湿耐水性防錆シートを提供することにある。SUMMARY OF THE INVENTION The present inventors have found that the use of a nonwoven fabric having specific physical properties significantly reduces the rust inhibitor from falling off. SUMMARY OF THE INVENTION An object of the present invention is to provide a moisture- and water-resistant rust-proof sheet in which a rust preventive agent is hard to fall off and can be reused as a raw material.

【０００７】[0007]

【課題を解決するための手段】本発明は、合成樹脂不織
布と合成樹脂フィルムを積層した基材の不織布面に気化
性防錆剤を含有させた防錆シートにおいて、不織布が密
度（ＪＩＳ−Ｐ−８１１８）０．２０〜０．８０ｇ／ｃ
ｍ3であることを特徴とする防錆シートである。SUMMARY OF THE INVENTION The present invention relates to a rust-preventive sheet comprising a synthetic resin non-woven fabric and a synthetic resin film laminated on a non-woven fabric surface containing a vaporizable rust-preventive agent, wherein the non-woven fabric has a density (JIS-P -8118) 0.20 to 0.80 g / c
a rust sheet which is a m 3.

【０００８】[0008]

【作用】本発明においては、ＪＩＳ−Ｐ−８１１８に基
づく密度が０．２０〜０．８０ｇ／ｃｍ3の合成樹脂不
織布を使用して防腐剤の脱落のすくないものを得る。密
度が０．２０ｇ／ｃｍ3未満のものを使うと脱落に関し
て欠点のあるものしか得られず、０．８０ｇ／ｃｍ3を
越えるものを使うと繊維間の空隙が少なすぎるために、
そこに保持可能な防錆剤量が少量となり、用途によって
は効果の点で見劣りする場合もある。また、本発明にお
いては、エンボス加工した合成樹脂不織布も使用可能で
あるが、その場合にもエンボス加工前の密度が０．２０
〜０．８０ｇ／ｃｍ3のものが使用される。In the present invention, an antiseptic is obtained by using a synthetic resin non-woven fabric having a density of 0.20 to 0.80 g / cm 3 based on JIS-P-8118. If the density is less than 0.20 g / cm 3, only those having a defect with respect to falling off can be obtained, and if the density exceeds 0.80 g / cm 3 , the voids between fibers are too small.
The amount of the rust inhibitor that can be retained there is small, and the effect may be poor depending on the application. In the present invention, an embossed synthetic resin nonwoven fabric can also be used.
Oh Ru, but the density of the pre-embossed even if that is 0.20
０．８0.80 g / cm 3 is used.

【０００９】合成樹脂不織布としては、例えばポリエチ
レン、ポリプロピレン、ポリエステル、ポリアミド等の
合成樹脂を材料として湿式法、乾式法、直接法で製造さ
れた厚さ５μｍ〜５０ｍｍのものが挙げられ、中でも、
ポリエチレン、ポリプロピレン等のポリオレフィン樹脂
はヒートシール性に優れているため特に好ましい。Examples of the synthetic resin non-woven fabric include those made of synthetic resin such as polyethylene, polypropylene, polyester and polyamide by a wet method, a dry method and a direct method and having a thickness of 5 μm to 50 mm.
Polyolefin resins such as polyethylene and polypropylene are particularly preferred because of their excellent heat sealing properties.

【００１０】本発明に用いられる基材は、合成樹脂不織
布と合成樹脂フィルムを積層したものに限定されるもの
ではない。例えばこの積層シートの合成樹脂フィルム上
に、合成樹脂クロスを貼り合わせて得られる合成樹脂不
織布−合成樹脂フィルム−合成樹脂クロスの積層シー
ト、あるいは、合成樹脂クロスと合成樹脂フィルムを順
次積層して得られる合成樹脂不織布−合成樹脂フィルム
−合成樹脂クロス−合成樹脂フィルムの積層シート等が
含まれる。[0010] The substrate used in the present invention is not limited to a laminate of a synthetic resin nonwoven fabric and a synthetic resin film. For example, a laminated sheet of a synthetic resin nonwoven fabric-synthetic resin film-synthetic resin cloth obtained by laminating a synthetic resin cloth on the synthetic resin film of this laminated sheet, or a synthetic resin cloth and a synthetic resin film are sequentially laminated. Synthetic resin nonwoven fabric-synthetic resin film-synthetic resin cloth-synthetic resin film laminated sheet.

【００１１】合成樹脂クロスは防錆シートの機械的強度
を上げるために用いられ、これを貼り合わせることによ
って破れ難くなり、例えば袋に加工してその中に金属部
品等を入れて取り扱った時に、袋が破れて発錆し易い環
境にさらされる危険性が小さくなる。Synthetic resin cloth is used to increase the mechanical strength of a rust-preventive sheet, and it becomes difficult to be torn by sticking the rust-proof sheet. For example, when processed into a bag and metal parts etc. are put in it and handled, The risk of the bag being torn and exposed to a rust-prone environment is reduced.

【００１２】上記のような合成樹脂不織布と合成樹脂フ
ィルム等を貼り合わせた基材の不織布に気化性防錆剤を
含有させた構造の防錆シートは、通常積層した基材の不
織布面に気化性防錆剤組成物を塗布して得られる。A rust preventive sheet having a structure in which a vaporizable rust inhibitor is contained in a nonwoven fabric of a substrate obtained by laminating a synthetic resin nonwoven fabric and a synthetic resin film or the like as described above usually has a vaporized nonwoven fabric surface of a laminated substrate. It is obtained by applying a water-soluble rust inhibitor composition.

【００１３】また、合成樹脂不織布、合成樹脂フィル
ム、合成樹脂クロスを順次積層したシートの不織布に気
化性防錆剤を含有させた構造の防錆シートは、通常
（Ａ）順次積層したシートの不織布面に気化性防錆剤組
成物を塗布することによって、あるいは（Ｂ）不織布と
フィルムを積層したシートの不織布面に気化性防錆剤組
成物を塗布した後に、このシートのフィルム面にさらに
クロスを貼り合わせることによって得られる。A rust preventive sheet having a structure in which a vaporizable rust preventive agent is added to a nonwoven sheet of a sheet in which a synthetic resin nonwoven fabric, a synthetic resin film, and a synthetic resin cloth are sequentially laminated is usually (A) a nonwoven fabric of a sequentially laminated sheet. By applying the vaporizable rust inhibitor composition to the surface of the sheet, or (B) after applying the vaporizable rust inhibitor composition to the nonwoven fabric surface of the sheet obtained by laminating the nonwoven fabric and the film, Are obtained by bonding together.

【００１４】また合成樹脂不織布−合成樹脂フィルム−
合成樹脂クロス−合成樹脂フィルムを順次積層したシー
トの不織布に気化性防錆剤を含有させた構造の防錆シー
トは、通常（Ａ）順次積層したシートの不織布面に気化
性防錆剤組成物を塗布する。（Ｂ）不織布とフィルムと
クロスを順次積層したシートの不織布面に気化性防錆剤
組成物を塗布した後に、このシートのクロス面にフィル
ムを貼り合わせる。（Ｃ）不織布とフィルムを積層した
シートの不織布面に気化性防錆剤組成物を塗布した後
に、このシートのフィルム面にクロスとフィルムを順次
貼り合わせる。（Ｄ）不織布とフィルムを積層したシー
トの不織布面に気化性防錆剤組成物を塗布した後に、こ
のシートのフィルム面にクロスとフィルムを貼り合わせ
たシートのクロス面を貼り合わせる、等の方法によって
得られる。Synthetic resin nonwoven fabric-synthetic resin film-
A rust preventive sheet having a structure in which a vaporizable rust inhibitor is contained in a nonwoven fabric sheet in which a synthetic resin cloth-synthetic resin film is sequentially laminated is usually (A) a vaporizable rust inhibitor composition formed on the nonwoven fabric surface of a sequentially laminated sheet. Is applied. (B) After applying the vaporizable rust preventive composition to the nonwoven fabric surface of a sheet in which a nonwoven fabric, a film, and a cloth are sequentially laminated, the film is bonded to the cloth surface of the sheet. (C) After applying the vaporizable rust inhibitor composition to the nonwoven fabric surface of the sheet in which the nonwoven fabric and the film are laminated, a cloth and a film are sequentially bonded to the film surface of the sheet. (D) a method in which a vaporizable rust inhibitor composition is applied to the nonwoven fabric surface of a sheet in which a nonwoven fabric and a film are laminated, and then the cloth surface of a sheet in which a cloth and a film are bonded to the film surface of the sheet is bonded. Obtained by

【００１５】合成樹脂フィルムとしては、例えばポリエ
チレン、ポリプロピレン、ポリ塩化ビニル、ポリ塩化ビ
ニリデン、エチレン・酢酸ビニル共重合体、ポリエステ
ル、ポリアミド、ポリスチレン等の材質からなる厚さ５
〜５００μｍのものが挙げられる。中でも、ポレエチレ
ン、ポリプロピレン等のポリオレフィン樹脂はヒートシ
ール性に優れ特に好ましい。As the synthetic resin film, for example, a film made of a material such as polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, ethylene / vinyl acetate copolymer, polyester, polyamide, polystyrene, etc.
５００500 μm. Among them, polyolefin resins such as polyethylene and polypropylene are particularly preferable because of their excellent heat sealing properties.

【００１６】合成樹脂クロスとしては、例えばポリエチ
レン、ポリプロピレン、ポリエステル、ポリアミド等の
材質からなる厚さ５〜５００μｍのものが挙げられる。
中でも、ポレエチレン、ポリプロピレン等のポリオレフ
ィン系のものはヒートシール性に優れて好ましい。そし
て、引張り強度が２０ｋｇ／５０ｍｍ以上のものを使用
すると、取扱中に袋が破れる危険性が極めて小さく特に
好ましい。As the synthetic resin cloth, for example, a cloth made of a material such as polyethylene, polypropylene, polyester, polyamide or the like having a thickness of 5 to 500 μm can be mentioned.
Among them, polyolefins such as polyethylene and polypropylene are preferable because of their excellent heat sealing properties. It is particularly preferable to use a material having a tensile strength of 20 kg / 50 mm or more, since the risk of breakage of the bag during handling is extremely small.

【００１７】合成樹脂フィルムや合成樹脂クロスの貼り
合わせには、湿式ラミネート法、乾式ラミネート法、ホ
ットメルトラミネート法、押し出しラミネート法等の公
知の方法が用いられる。Known methods such as a wet laminating method, a dry laminating method, a hot melt laminating method, and an extrusion laminating method are used for laminating a synthetic resin film or a synthetic resin cloth.

【００１８】本発明に用いられる防錆剤としては、例え
ば亜硝酸ジシクロヘキシルアンモニウム、カプリル酸ジ
シクロヘキシルアンモニウム、炭酸ジシクロヘキシルア
ンモニウム、亜硝酸ジイソプロピルアンモニウム、安息
香酸モノエタノールアンモニウム、安息香酸ソーダ、安
息香酸、カプリル酸、カプリン酸、安息香酸イソプロピ
ル、安息香酸ブチル、桂皮酸ブチル、カルバミン酸アン
モニウム、モノエチルアミン、ジエチルアミン、モノエ
タノールアミン、ジエタノールアミン、トリエタノール
アミン、モルホリン、メチルモルホリン、エチルモルホ
リン、ヘキサメチレンテトラミン、ベンゾトリアゾー
ル、トリルトリアゾール、尿素、チオ尿素、亜硝酸ソー
ダ等の公知の材料が挙げられ、塗布に用いられる気化性
防錆剤組成物の塗液は上記防錆剤の単独あるいは複数を
水性系、非水性系媒体、電離放射線硬化性物質等に分
散、溶解、混和し、さらに必要応じて接着剤、浸透剤等
を添加して調製される。Examples of the rust preventive used in the present invention include dicyclohexylammonium nitrite, dicyclohexylammonium caprylate, dicyclohexylammonium carbonate, diisopropylammonium nitrite, monoethanolammonium benzoate, sodium benzoate, benzoic acid, caprylic acid, and the like. Capric acid, isopropyl benzoate, butyl benzoate, butyl cinnamate, ammonium carbamate, monoethylamine, diethylamine, monoethanolamine, diethanolamine, triethanolamine, morpholine, methylmorpholine, ethylmorpholine, hexamethylenetetramine, benzotriazole, tolyl Known materials such as triazole, urea, thiourea, and sodium nitrite are mentioned, and a coating liquid of a vaporizable rust inhibitor composition used for coating is used. The rust inhibitor alone or a plurality of aqueous systems, nonaqueous systems medium, dispersed in the ionizing radiation-curable materials such as dissolving, mixing, and adhesives according necessary, be prepared by adding an osmotic agent.

【００１９】塗液中の防錆剤の濃度は通常５〜８０重量
％の範囲に調整され、接着剤は防錆剤１００重量部に対
して０〜２００重量部、浸透剤は防錆剤１００重量部に
対して０〜１００重量部の範囲で用いられる。The concentration of the rust preventive in the coating solution is usually adjusted within the range of 5 to 80% by weight, the adhesive is 0 to 200 parts by weight with respect to 100 parts by weight of the rust preventive, and the penetrant is 100 parts by weight of the rust preventive. It is used in the range of 0 to 100 parts by weight with respect to parts by weight.

【００２０】水性系媒体としては、水単独あるいはメチ
ルケトン、メタノール、エタノール、ｎ−プロピルアル
コール、イソプロピルアルコール、ｎ−ブタノール、イ
ソブタノール、エチレングリコール、プロピレングリコ
ール等の水と混和する媒体と水との混合液が挙げられ
る。As the aqueous medium, water alone or a mixture of water with a water-miscible medium such as methyl ketone, methanol, ethanol, n-propyl alcohol, isopropyl alcohol, n-butanol, isobutanol, ethylene glycol, propylene glycol, etc. Liquid.

【００２１】非水性系媒体としては、例えばベンゼン、
トルエン、キシレン、ヘキサン、シクロヘキサン、トリ
クロルエチレン、メチルケトン、メチルエチルケトン、
メチルイソブチルケトン、酢酸メチル、酢酸エチル、酢
酸ブチル、メチルセロソルブ、エチルセロソルブ、ブチ
ルセロソルブ、メタノール、エタノール、ｎ−プロピル
アルコール、イソプロピルアルコール、ｎ−ブタノー
ル、イソブタノール、ｎ−ヘキサノール、シクロヘキサ
ノール、エチレングリコール、プロピレングリコール、
ジエチレングリコール等が挙げられる。As the non-aqueous medium, for example, benzene,
Toluene, xylene, hexane, cyclohexane, trichloroethylene, methyl ketone, methyl ethyl ketone,
Methyl isobutyl ketone, methyl acetate, ethyl acetate, butyl acetate, methyl cellosolve, ethyl cellosolve, butyl cellosolve, methanol, ethanol, n-propyl alcohol, isopropyl alcohol, n-butanol, isobutanol, n-hexanol, cyclohexanol, ethylene glycol, Propylene glycol,
Diethylene glycol and the like.

【００２２】電離放射線硬化性物質としては、電子線あ
るいは紫外線で硬化するエチレン性不飽和結合を有する
モノマー、オリゴマー、プレポリマーが挙げられ、具体
的にはスチレン、メチルアクリレート、ブチルアクリレ
ート、ラウリルアクリレート、ポリエチレングリコール
ジアクリレート、プロピレングリコールジアクリレー
ト、トリメチロールプロパンジアクリレート、トリメチ
ロールプロパントリアアクリレート、ペンタエリスリト
ールトリアクリレート、ペンタエリスリトールテトラア
クリレート、ヘキサンジオールジアクリレート、１，２
−ブタンジオールジアクリレート、エポキシ樹脂とアク
リル酸との反応物、マレイン酸とアクリル酸とジエチレ
ングリコールの縮合物等が挙げられる。Examples of the ionizing radiation-curable substance include monomers, oligomers and prepolymers having an ethylenically unsaturated bond which are cured by an electron beam or ultraviolet rays. Specifically, styrene, methyl acrylate, butyl acrylate, lauryl acrylate, Polyethylene glycol diacrylate, propylene glycol diacrylate, trimethylolpropane diacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, hexanediol diacrylate, 1,2
-Butanediol diacrylate, a reaction product of an epoxy resin and acrylic acid, a condensate of maleic acid, acrylic acid and diethylene glycol, and the like.

【００２３】エチレン性不飽和結合を有するモノマー、
オリゴマー、プレポリマーを使用して紫外線で硬化する
場合には、塗液中に光重合開始剤が、また必要に応じて
増感剤が添加される。A monomer having an ethylenically unsaturated bond,
When using an oligomer or prepolymer for curing with ultraviolet light, a photopolymerization initiator and, if necessary, a sensitizer are added to the coating solution.

【００２４】光重合開始剤としては、例えばベンゾキノ
ン、フェナンスレンキノン、ナフトキノン、ベンゾイン
ブチルエーテル、ベンゾイン、ミヒラーケトン等が挙げ
られる。Examples of the photopolymerization initiator include benzoquinone, phenanthrenequinone, naphthoquinone, benzoin butyl ether, benzoin, Michler's ketone and the like.

【００２５】増感剤としては、例えばトリエタノールア
ミン、Ｎ−メチルジエタノールアミン、Ｎ，Ｎ−ジエタ
ノールアミン、Ｎ−メチルモルホリン等が挙げられる。Examples of the sensitizer include triethanolamine, N-methyldiethanolamine, N, N-diethanolamine, N-methylmorpholine and the like.

【００２６】浸透剤としては、例えばイソプロピルアル
コール、イソブチルアルコール等のアルコール類等が挙
げられる。Examples of the penetrant include alcohols such as isopropyl alcohol and isobutyl alcohol.

【００２７】接着剤としては、水性系として塗布する場
合には水溶性バインダー、ラテックス系バインダーが使
用され、非水性系として塗布する場合には油溶性バイン
ダーが使用される。As the adhesive, a water-soluble binder or a latex-based binder is used when applied as an aqueous system, and an oil-soluble binder is used when applied as a non-aqueous system.

【００２８】水溶性バインダーとしては、例えばゼラチ
ン、アルブミン、カゼイン、澱粉、エーテル化澱粉、エ
ステル化澱粉、カルボキシメチルセルロース、ヒドロキ
シエチルセルロース、寒天、アルギン酸ソーダ、アラビ
アゴム等の水溶性天然或いは半合成高分子化合物、ポリ
ビニルアルコール、変性ポリビニルアルコール、ポリビ
ニルピロリドン、ポリアクリル酸、ポリアクリルアミ
ド、エチレン・無水マレイン酸共重合体、スチレン・無
水マレイン酸共重合体、メチルビニルエーテル・無水マ
レイン酸共重合体、イソブチレン・無水マレイン酸共重
合体等の水溶性合成高分子化合物が挙げられる。Examples of the water-soluble binder include water-soluble natural or semi-synthetic polymer compounds such as gelatin, albumin, casein, starch, etherified starch, esterified starch, carboxymethylcellulose, hydroxyethylcellulose, agar, sodium alginate, and gum arabic. , Polyvinyl alcohol, modified polyvinyl alcohol, polyvinylpyrrolidone, polyacrylic acid, polyacrylamide, ethylene / maleic anhydride copolymer, styrene / maleic anhydride copolymer, methyl vinyl ether / maleic anhydride copolymer, isobutylene / maleic anhydride Water-soluble synthetic high molecular compounds such as acid copolymers are exemplified.

【００２９】ラテックス系バインダーとしては、例えば
スチレン・ブタジエンラテックス、アクリロニトリル・
ブタジエンラテックス、アクリル酸エステル系ラテック
ス、酢酸ビニル系ラテックス、塩化ビニリデン系ラテッ
クス及びこれらのカルボキシ変性（例えばアクリル酸）
ラテックス等が挙げられる。Examples of latex binders include styrene-butadiene latex, acrylonitrile-
Butadiene latex, acrylate latex, vinyl acetate latex, vinylidene chloride latex and their carboxy-modified (eg acrylic acid)
Latex and the like.

【００３０】油溶性バインダーとしては、例えばロジ
ン、コパール、ダルマン、ギルソナイト、ゼイン等の天
然樹脂、硬化ロジン、二量化ロジン、重合ロジン、マレ
イン酸樹脂、フマル酸樹脂、メチルセルロース、エチル
セルロース、ヒドロキシプロピルセルロース、エチルヒ
ドロキシエチルセルロース、セルロースアセテートプロ
ピオネート、セルロースアセテートブチラール、ニトロ
セルロース等の半合成樹脂、フェノール樹脂、キシレン
樹脂、尿素樹脂、メラミン樹脂、ケトン樹脂、クマロン
・インデン樹脂、石油樹脂、テルペン樹脂、環化ゴム、
塩化ゴム、アルキド樹脂、ポリアミド樹脂、アクリル樹
脂、ポリ塩化ビニル、ポリ酢酸ビニル、塩化ビニル・酢
酸ビニル共重合体、塩素化ポリプロピレンスチレン樹
脂、エポキシ樹脂、ポリウレタン樹脂、ポリビニルブチ
ラール等が挙げられる。Examples of the oil-soluble binder include natural resins such as rosin, copearl, dalman, gilsonite and zein, cured rosin, dimerized rosin, polymerized rosin, maleic resin, fumaric resin, methyl cellulose, ethyl cellulose, hydroxypropyl cellulose, and the like. Semi-synthetic resins such as ethyl hydroxyethyl cellulose, cellulose acetate propionate, cellulose acetate butyral, nitrocellulose, phenolic resin, xylene resin, urea resin, melamine resin, ketone resin, coumarone-indene resin, petroleum resin, terpene resin, cyclization Rubber,
Examples include chlorinated rubber, alkyd resin, polyamide resin, acrylic resin, polyvinyl chloride, polyvinyl acetate, vinyl chloride / vinyl acetate copolymer, chlorinated polypropylene styrene resin, epoxy resin, polyurethane resin, polyvinyl butyral, and the like.

【００３１】気化性防錆剤組成物の塗布は、通常バーコ
ーター、ロールコーター、グラビアコーター、エアーナ
イフコーター等の塗工機を使って行われる。塗液は、通
常乾燥重量が２〜５０ｇ／ｍ2 となるように塗布され
る。１ｇ／ｍ 2 未満の場合には防錆効果が弱く、５０ｇ
／ｍ2 を越える場合には製造コストが極めて高いものと
なる。The application of the vaporizable rust inhibitor composition is usually carried out using a bar
Coater, roll coater, gravure coater, airna
This is performed using a coating machine such as an if coater. The coating liquid is
Normal dry weight is 2 to 50 g / mTwoIs applied so that
You. 1g / m TwoIf it is less than 50 g, the rust prevention effect is weak and 50 g
/ MTwoIf the production cost exceeds
Become.

【００３２】[0032]

【実施例】以下に実施例を示し本発明をより具体的に説
明するが、勿論これらに限定されるものではない。また
特に断らない限り例中の部および％はそれぞれ重量部及
び重量％を示す。The present invention will be described in more detail with reference to the following Examples, but it should be understood that the present invention is by no means restricted thereto. Unless otherwise specified, parts and% in the examples are parts by weight and% by weight, respectively.

【００３３】実施例１ ＪＩＳ−Ｐ−８１１８に基づく密度が０．２２７ｇ／ｃ
ｍ3 で２８ｇ／ｍ2 のポリエチレン−ポリプロピレン系
不織布（商品名：Ｈ２８４１、ハビックス製）に２０μ
ｍのポリエチレンを貼り合わせて積層した基材を得た。Example 1 A density based on JIS-P-8118 is 0.227 g / c.
20 μm on a polyethylene-polypropylene nonwoven fabric of 28 g / m 2 at m 3 (trade name: H2841, manufactured by Havix)
m of polyethylene was laminated and a substrate was obtained.

【００３４】続いて、水６０重量部に亜硝酸ソーダ２０
重量部、安息香酸１１重量部、トリエチルアミン９重量
部を溶解して調製した防錆塗液を、上記基材の不織布面
にバーコーターでコート量が７ｇ／ｍ2 （乾燥重量）と
なるように塗布し、６０℃下で乾燥して防錆シートを作
成した。Subsequently, sodium nitrite 20 was added to 60 parts by weight of water.
Parts by weight, 11 parts by weight of benzoic acid, and 9 parts by weight of triethylamine were dissolved in a rust-preventive coating solution so that the non-woven fabric surface of the base material had a coating amount of 7 g / m 2 (dry weight) with a bar coater. It was applied and dried at 60 ° C. to prepare a rust preventive sheet.

【００３５】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来た。また、この防錆シートは、取扱中に防錆
剤の不織布面からの脱落が殆ど見られず作業環境は良好
であった。The obtained rust-preventive sheet showed good rust-preventive ability under high temperature and high humidity with respect to iron, and could be used as a recycled material by melting. In addition, the rust preventive sheet showed a good working environment with almost no rust preventive falling off the nonwoven fabric surface during handling.

【００３６】実施例２ ＪＩＳ−Ｐ−８１１８に基づく密度が０．３１ｇ／ｃｍ
3 で４０ｇ／ｍ2 のポリエチレン系不織布（商品名：ル
クサーＨ２０２０ＸＷ、旭化成製）に２０μｍのポリエ
チレンを貼り合わせて積層した基材の、不織布面に実施
例１と同様にして得た防錆塗液をバーコーターでコート
量が７ｇ／ｍ2 （乾燥重量）となるように塗布し、６０
℃下で乾燥して防錆シートを作成した。Example 2 A density based on JIS-P-8118 is 0.31 g / cm.
Polyethylene nonwoven 40 g / m 2 in 3 (trade name: Luxer H2020XW, manufactured by Asahi Kasei Corporation) of a laminated by bonding polyethylene 20μm substrate, anticorrosive coating liquid obtained in the same manner as in Example 1 to nonwoven surface With a bar coater so that the coating amount is 7 g / m 2 (dry weight),
Drying was carried out at ℃ to prepare a rustproof sheet.

【００３７】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来た。また、この防錆シートは、取扱中に防錆
剤の不織布面からの脱落が殆ど見られず作業環境は良好
であった。The obtained rust-preventive sheet showed good rust-preventing ability with respect to iron under high temperature and high humidity, and could be used as a recycled material by melting. In addition, the rust preventive sheet showed a good working environment with almost no rust preventive falling off the nonwoven fabric surface during handling.

【００３８】実施例３ ＪＩＳ−Ｐ−８１１８に基づく密度が０．３２ｇ／ｃｍ
3 で５４ｇ／ｍ2 のポリエチレン系不織布（商品名：タ
イベック１０５６Ｄ、デュポン製）に２０μｍのポリエ
チレンを貼り合わせて積層した基材の、不織布面に実施
例１と同様にして得た防錆塗液をバーコーターでコート
量が７ｇ／ｍ2 （乾燥重量）となるように塗布し、６０
℃下で乾燥して防錆シートを作成した。Example 3 A density based on JIS-P-8118 is 0.32 g / cm.
3 in polyethylene nonwoven 54 g / m 2 (trade name: Tyvek 1056D, manufactured by DuPont) base material layered by bonding a polyethylene 20μm, the anticorrosive coating liquid obtained in the same manner as in Example 1 to nonwoven surface With a bar coater so that the coating amount is 7 g / m 2 (dry weight),
Drying was carried out at ℃ to prepare a rustproof sheet.

【００３９】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来た。また、この防錆シートは、取扱中に防錆
剤の不織布面からの脱落が殆ど見られず作業環境は良好
であった。The obtained rust-preventive sheet exhibited good rust-preventing ability with respect to iron under high temperature and high humidity, and was melted and used as a recycled material. In addition, the rust preventive sheet showed a good working environment with almost no rust preventive falling off the nonwoven fabric surface during handling.

【００４０】実施例４ ＪＩＳ−Ｐ−８１１８に基づく密度が０．３５ｇ／ｃｍ
3 で８０ｇ／ｍ2 のポリエチレン系不織布（商品名：ル
クサーＨ１０４０ＺＺ、旭化成製）に２０μｍのポリエ
チレンを貼り合わせて積層した基材の、不織布面に実施
例１と同様にして得た防錆塗液をバーコーターでコート
量が７ｇ／ｍ2 （乾燥重量）となるように塗布し、６０
℃下で乾燥して防錆シートを作成した。Example 4 A density based on JIS-P-8118 is 0.35 g / cm.
Polyethylene nonwoven 80 g / m 2 in 3 (trade name: Luxer H1040ZZ, manufactured by Asahi Kasei Corporation) of a laminated by bonding polyethylene 20μm substrate, anticorrosive coating liquid obtained in the same manner as in Example 1 to nonwoven surface With a bar coater so that the coating amount is 7 g / m 2 (dry weight),
Drying was carried out at ℃ to prepare a rustproof sheet.

【００４１】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来た。また、この防錆シートは、取扱中に防錆
剤の不織布面からの脱落が殆ど見られず作業環境は良好
であった。The obtained rust-preventive sheet exhibited good rust-preventive ability under high temperature and high humidity with respect to iron, and could be used as a recycled material by melting. In addition, the rust preventive sheet showed a good working environment with almost no rust preventive falling off the nonwoven fabric surface during handling.

【００４２】実施例５ ポリエチレンクロス（商品名：パイオランＵ・Ｓクロ
ス、ダイヤテックス社製）に２０μｍポリエチレンをラ
ミネートしたシートのポリエチレンクロス面に、実施例
１と同様の不織布Ｈ２８４１をポリエチレンをバインダ
ーとして貼り合わせて積層した基材の、不織布面に実施
例１と同様にして得た防錆塗液をバーコーターでコート
量が７ｇ／ｍ2 （乾燥重量）となるように塗布し、６０
℃下で乾燥して防錆シートを作成した。Example 5 The same nonwoven fabric H2841 as in Example 1 was applied to a polyethylene cloth (trade name: Piolan U.S. Cloth, manufactured by Diatex Co., Ltd.) on a polyethylene cloth surface, using polyethylene as a binder. A rust-preventive coating solution obtained in the same manner as in Example 1 was applied to the nonwoven fabric surface of the laminated base material using a bar coater so that the coating amount was 7 g / m 2 (dry weight).
Drying was carried out at ℃ to prepare a rustproof sheet.

【００４３】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来た。また、この防錆シートは、取扱中に防錆
剤の不織布面からの脱落が殆ど見られず作業環境は良好
であったThe obtained rust-preventive sheet showed good rust-preventing ability with respect to iron under high temperature and high humidity, and could be used as a recycled material by melting. In addition, this rust-preventive sheet showed a good working environment with almost no rust-preventive agent falling off from the nonwoven fabric surface during handling.

【００４４】比較例１ ＪＩＳ−Ｐ−８１１８に基づく密度が０．１８３ｇ／ｃ
ｍ3 で２８ｇ／ｍ2 のポリエチレン−ポリプロピレン系
不織布（商品名：ボンリック２８Ｊ、金星製紙製）に２
０μｍのポリエチレンを貼り合わせて積層した基材の、
不織布面に実施例１と同様にして得た防錆塗液をバーコ
ーターでコート量が７ｇ／ｍ2 （乾燥重量）となるよう
に塗布し、６０℃下で乾燥して防錆シートを作成した。Comparative Example 1 A density based on JIS-P-8118 is 0.183 g / c.
m 3 polyethylene of 28 g / m 2 - polypropylene nonwoven (product name: Bonrikku 28 J, Venus made paper) 2
Of a substrate laminated by laminating 0 μm polyethylene,
A rust-preventive coating solution obtained in the same manner as in Example 1 was applied to the nonwoven fabric surface using a bar coater so that the coating amount was 7 g / m 2 (dry weight), and dried at 60 ° C. to prepare a rust-preventive sheet. did.

【００４５】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来たが、取扱中に防錆剤の不織布面からの脱落
が多く見られた。The obtained rust-preventive sheet showed good rust-preventing ability under high temperature and high humidity with respect to iron and could be used as a recycled material by melting. Many drops were seen.

【００４６】比較例２ ポリエチレンクロス（商品名：パイオランＵ・Ｓクロ
ス、ダイヤテックス社製）に２０μｍポリエチレンをラ
ミネートしたシートのポリエチレンクロス面に、比較例
１と同様の不織布ボンリック２８Ｊをポリエチレンをバ
インダーとして貼り合わせて積層した基材の、不織布面
に実施例１と同様にして得た防錆塗液をバーコーターで
コート量が７ｇ／ｍ2 （乾燥重量）となるように塗布
し、６０℃下で乾燥して防錆シートを作成した。Comparative Example 2 A nonwoven woven fabric 28J similar to that of Comparative Example 1 was used on a polyethylene cloth (trade name: PIOLAN US / Cross, manufactured by Diatex Co., Ltd.) with polyethylene binder as a binder. The rust-preventive coating solution obtained in the same manner as in Example 1 was applied to the nonwoven fabric surface of the laminated substrate by a bar coater so that the coating amount was 7 g / m 2 (dry weight), and the coating was performed at 60 ° C. To prepare a rustproof sheet.

【００４７】得られた防錆シートは、鉄に対して高温高
湿下で良好な防錆能を示し、また溶融して再生原料とし
て使用出来たが、取扱中に防錆剤の不織布面からの脱落
が多く見られた。The obtained rust-preventive sheet showed good rust-preventing ability under high temperature and high humidity with respect to iron and could be used as a recycled material by melting. Many drops were seen.

【００４８】[0048]

【発明の効果】本発明の防錆シートは、鉄に対して高温
高湿下でも良好な防錆能を示し、また溶融して再生原料
として使用出来た。また、この防錆シートは、取扱中に
防錆剤の不織布面からの脱落がなく作業環境は良好であ
った。The rust-preventive sheet of the present invention has good rust-preventing ability even under high temperature and high humidity with respect to iron, and can be melted and used as a recycled material. In addition, the rust preventive sheet was free from the rust preventive from the nonwoven fabric surface during handling, and the working environment was favorable.

───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B65D 65/42 B32B 27/12 B32B 27/18 ──────────────────────────────────────────────────続 き Continued on front page (58) Field surveyed (Int.Cl. 7 , DB name) B65D 65/42 B32B 27/12 B32B 27/18

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】合成樹脂不織布と合成樹脂フィルムを積層
した基材の不織布面に気化性防錆剤を含有させた防錆シ
ートにおいて、不織布が密度（ＪＩＳ−Ｐ−８１１８）
０．２０〜０．８０ｇ／ｃｍ3であることを特徴とする
防錆シート。1. A rust-preventive sheet comprising a synthetic resin non-woven fabric and a synthetic resin film laminated on a non-woven fabric surface containing a vaporizable rust-preventive agent, wherein the non-woven fabric has a density (JIS-P-8118).
A rust preventive sheet having a weight of 0.20 to 0.80 g / cm 3 . 【請求項２】合成樹脂が全層ともポリオレフィン樹脂で
ある請求項１記載の防錆シート。2. The rustproof sheet according to claim 1, wherein the synthetic resin is a polyolefin resin in all layers.
JP23212493A 1993-09-20 1993-09-20 Rust prevention sheet Expired - Lifetime JP3166438B2 (en)