JP3154882B2 - Residential waterproofing material - Google Patents
Residential waterproofing materialInfo
- Publication number
- JP3154882B2 JP3154882B2 JP26438093A JP26438093A JP3154882B2 JP 3154882 B2 JP3154882 B2 JP 3154882B2 JP 26438093 A JP26438093 A JP 26438093A JP 26438093 A JP26438093 A JP 26438093A JP 3154882 B2 JP3154882 B2 JP 3154882B2
- Authority
- JP
- Japan
- Prior art keywords
- asphalt
- waterproofing material
- tear
- house
- resin film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】この発明は住宅用防水材、特に、
木造住宅の外壁仕上げ材の下張に用いて好適な住宅用防
水材に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a waterproofing material for a house, in particular,
The present invention relates to a waterproofing material for a house which is suitable for use as a subbing for a finishing material for an outer wall of a wooden house.
【０００２】[0002]
【従来の技術】一般に、従来の住宅用防水材は、原紙に
ストレートアスファルトまたはピッチを含浸させたアス
ファルトフェルトからなっていた。このアスファルトフ
ェルトは、まず、安価に製造でき、かつ紙の適度の吸湿
性と、アスファルトの疎水性とを合わせ持つという特徴
を有している。2. Description of the Related Art In general, a conventional waterproofing material for houses has been made of straight asphalt or asphalt felt obtained by impregnating pitch into base paper. The asphalt felt has a feature that it can be manufactured at a low cost and that it has both the moderate hygroscopicity of paper and the hydrophobicity of asphalt.
【０００３】即ち、該アスファルトフェルトに水滴が付
着した場合、アスファルトの疎水性が作用して水滴を離
反させるか滴下させて、水濡れを防ぐことができる。ま
た、外壁用防水材として用いた場合、壁構造内部の湿度
が著しく上昇した時に、紙自体が水分を吸収して湿度上
昇を抑制したり、結露を防止することができる。これに
より、アスファルトフェルトからなる住宅用防水材は、
アスファルトの耐久性をもちながら、天然木と同様の優
れた調湿効果を持つことができるようになっている。[0003] That is, when water droplets adhere to the asphalt felt, the hydrophobicity of the asphalt acts to separate or drop the water droplets, thereby preventing water from being wetted. Further, when used as a waterproofing material for an outer wall, when the humidity inside the wall structure rises remarkably, the paper itself can absorb moisture to suppress the rise in humidity or prevent dew condensation. As a result, the waterproofing material for houses made of asphalt felt
While having the durability of asphalt, it is possible to have the same excellent humidity control effect as natural wood.
【０００４】こうしたアスファルトフェルトからなる住
宅用防水材を使って、建築物の外壁をモルタル仕上げに
する場合、図３に示すように、下地板の上にアスファル
トフェルトを貼付し、その上にラス金網を取り付けてか
らモルタルを塗布し、さらに該モルタル表面に塗料を塗
布（または吹き付け）することを行う。これにより、モ
ルタルの美観を備えた耐候性外壁と、アスファルトフェ
ルトによる調湿性を備えた下張材からなる壁構造が得ら
れることとなる。When an exterior wall of a building is to be mortar-finished using such asphalt felt housing waterproofing material, asphalt felt is stuck on a base plate and a lath wire mesh is placed thereon as shown in FIG. Is applied, mortar is applied, and a paint is applied (or sprayed) on the mortar surface. As a result, a wall structure composed of a weather-resistant outer wall having a mortar appearance and an underlaying material having humidity control properties by asphalt felt can be obtained.
【０００５】[0005]
【発明が解決しようとする課題】上記従来の住宅用防水
材は、安価であって、吸水性と調湿性に富むという特長
を持つが、引裂強度の低い原紙にアスファルトを含浸さ
せた構造であるため、外力が加わると容易に破けること
が多く、建物完成後などに、この破損部分から漏水する
という問題があった。The above-mentioned conventional waterproofing material for houses has a feature that it is inexpensive and has excellent water absorption and humidity control properties, but has a structure in which base paper having a low tear strength is impregnated with asphalt. For this reason, it often breaks easily when an external force is applied, and there is a problem that water leaks from the damaged portion after the building is completed.
【０００６】即ち、強風が吹いて施工中の住宅用防水材
が裂けたり、飛散することがあり、また、釘やステープ
ルを使って住宅用防水材を固定した際に、ステープル部
分から漏水が生じるなどのトラブルが絶えなかった。特
に、近年の建築物では、モルタル壁の厚さが薄肉化し
て、ひび割れなどによる漏水が発生しやすくなっている
ため、下張材の破損は、絶対に避けなければならないも
のである。That is, a strong wind blows, and the waterproofing material for a house under construction may be torn or scattered, and when the waterproofing material for a house is fixed using nails or staples, water leakage occurs from the staple portion. Such troubles did not stop. In particular, in recent buildings, since the thickness of the mortar wall is reduced and water leakage due to cracks and the like is likely to occur, damage to the underlaying material must be absolutely avoided.
【０００７】この発明は上記の点に鑑み、従来のアスフ
ァルトフェルトより丈夫で破れにくい住宅用防水材を提
供することを目的としている。[0007] In view of the above, an object of the present invention is to provide a waterproofing material for a house which is stronger and less likely to be torn than conventional asphalt felt.
【０００８】[0008]
【課題を解決するための手段】上記の目的を達成するた
め、この発明は、原紙にストレートアスファルトまたは
ピッチを含浸してなるアスファルトフェルトの片面に、
シール性を有するアスファルト接着層を介して、合成繊
維不織布または合成樹脂フィルムを設けることにより、
アスファルトフェルトの調湿性と、アスファルト接着層
のシール性と、合成繊維不織布または合成樹脂フィルム
などの耐裂シート材の耐裂性とを合わせ持つ住宅用防水
材を構成できるようにしたものである。特に、合成樹脂
フィルムを用いることにより、高い耐裂性と印刷適合性
を呈するようにしたものである。SUMMARY OF THE INVENTION In order to achieve the above object, the present invention relates to a method for forming a base paper on straight asphalt or
On one side of asphalt felt impregnated with pitch ,
By providing a synthetic fiber nonwoven fabric or a synthetic resin film through an asphalt adhesive layer having a sealing property,
It is possible to constitute a waterproofing material for a house having the humidity control property of asphalt felt, the sealing property of an asphalt adhesive layer, and the tear resistance of a tear-resistant sheet material such as a synthetic fiber nonwoven fabric or a synthetic resin film. Particularly, by using a synthetic resin film, high tear resistance and print compatibility are exhibited.
【０００９】[0009]
【作用】従来の住宅用防水材と同様な構造の防水紙の片
面に、シール性を有するアスファルト接着層（例えば、
ＳＢＳなどを用いた改質アスファルト層）を形成し、さ
らに該アスファルト層の表面に、耐裂シート層（合成繊
維不織布または合成樹脂フィルム）を設ける。即ち、ア
スファルトフェルト、アスファルト接着層、耐裂シート
材からなる３層構造とする。このうち最も内側（居室
側）の防水紙層は、天然木材と同様に、安価で調湿性に
富む防水材として作用する。An asphalt adhesive layer having a sealing property (for example, on one side of waterproof paper having a structure similar to that of a conventional waterproofing material for a house).
A modified asphalt layer using SBS or the like is formed, and a tear-resistant sheet layer (synthetic fiber nonwoven fabric or synthetic resin film) is provided on the surface of the asphalt layer. That is, it has a three-layer structure composed of asphalt felt, an asphalt adhesive layer, and a tear-resistant sheet material. Of these, the innermost (room side) waterproof paper layer acts as an inexpensive and highly moisture-proof waterproof material, like natural wood.
【００１０】また、中間のアスファルト接着層は、仮留
めの釘やステープルに対するシール材として作用し、外
壁仕上材のひびや隙間より侵入する雨水が、ステープル
などの穴を通して木下地に侵入するのを防止する。[0010] The intermediate asphalt adhesive layer acts as a sealant for temporary nails and staples, preventing rainwater from entering cracks and gaps in the outer wall finishing material from penetrating into the wood substrate through holes such as staples. To prevent.
【００１１】また、最も外側（外気側）の耐裂シート材
（合成繊維不織布または合成樹脂フィルム）は高い強度
を持ち、引き裂けを防止する機能を有している。特に、
合成樹脂フィルムの場合は、上記引き裂けを防止機能に
加えて、多彩な印刷が可能であり、建築中の外壁にこの
下張材を用いれば、化粧性に富み、宣伝効果の高い外観
が得られる。The outermost (outside air side) tear-resistant sheet material (synthetic fiber nonwoven fabric or synthetic resin film) has high strength and has a function of preventing tearing. In particular,
In the case of a synthetic resin film, in addition to the function of preventing the tearing, various printings are possible, and by using this underlaying material on the outer wall under construction, a cosmetically rich appearance with a high advertising effect can be obtained. .
【００１２】本願住宅用防水材によれば、施工時の持ち
運び、引っ張り、釘打ちなどの各工程や、強風等で加わ
る外力には、耐裂シート材（合成繊維不織布または合成
樹脂フィルム）が抗して引き裂けを防ぎ、釘打ちなどに
よる穴からの雨水の侵入には、シール性を有するアスフ
ァルト接着層が抗して漏水を防ぎ、周囲空気の湿度変化
による結露には、アスファルトフェルト層が作用して調
湿と結露防止を行うこととなる。According to the waterproofing material for housing of the present invention, the tear-resistant sheet material (synthetic fiber nonwoven fabric or synthetic resin film) resists various steps such as carrying, pulling and nailing during construction, and external force applied by strong wind or the like. The asphalt adhesive layer with a sealing property prevents water leakage from the hole caused by nailing, etc. and prevents water leakage, and the asphalt felt layer acts on dew condensation due to changes in ambient air humidity. Humidity control and condensation prevention will be performed.
【００１３】[0013]
【実施例】以下、この発明を添付の図面に基づく実施例
により説明する。図において、本願住宅用防水材は、最
内層のアスファルトフェルト１、中間層のアスファルト
接着層２、及び最外層の耐裂シート材３からなる３層構
造になっている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below with reference to an embodiment based on the attached drawings. In the figure, the waterproofing material for housing of the present application has a three-layer structure including an asphalt felt 1 as an innermost layer, an asphalt adhesive layer 2 as an intermediate layer, and a tear-resistant sheet material 3 as an outermost layer.
【００１４】前記アスファルトフェルト１は、原紙にス
トレートアスファルトまたはピッチを含浸したアスファ
ルトフェルトであり、これだけでも住宅用防水材として
十分使用可能な防水性を有している。ここで、原紙とし
ては、故紙、パルプ、解繊した綿ボロ、毛屑などを原料
とした紙を用いる。該アスファルトフェルト１は、安価
であり、天然木材と同様の調湿機能を有している。The asphalt felt 1 is asphalt felt in which base paper is impregnated with straight asphalt or pitch, and has a waterproof property that can be sufficiently used as a waterproofing material for houses alone. Here, as the base paper, paper made from waste paper, pulp, defibrated cotton rag, shavings, or the like is used. The asphalt felt 1 is inexpensive and has the same humidity control function as natural wood.
【００１５】ここで、該アスファルトフェルト１として
は、 含浸前 ・・・ ４５〜２２０ｇ／ｍ2 含浸後 ・・・ ６０〜５２０ｇ／ｍ2 なる目付量のものを使用するが、特に、秤量（含浸後）
＝３８０ｇ／ｍ2 以上のものが望ましい。Here, as the asphalt felt 1, one having a basis weight of before the impregnation... 45-220 g / m 2 after the impregnation... 60-520 g / m 2 is used. rear)
= 380 g / m 2 or more is desirable.
【００１６】前記アスファルト接着層２は、シール性を
有する特殊アスファルト層からなっている。該アスファ
ルト接着層２の厚さは、 ０．０５〜０．５ｍｍ なる範囲内であって、一般の防水材などと比較すると、
極めて薄く構成されている。The asphalt adhesive layer 2 is made of a special asphalt layer having a sealing property. The thickness of the asphalt adhesive layer 2 is in the range of 0.05 to 0.5 mm.
It is very thin.
【００１７】該アスファルト接着層２は、例えば、ブロ
ーンアスファルト、防水用３種ブローンアスファルト、
防水用４種ブローンアスファルト、ベースアスファルト
に１〜２０％のＳＢＳ（スチレン・ブタジエン・スチレ
ンブロック共重合体）を混合した改質アスファルトなど
からなり、適度な柔軟性を備えることにより、釘やステ
イプルに対する粘着性と、釘、ステープルに対する高い
シール性、防水性を発揮するように構成されている。こ
こで、ベースアスファルトとしては、ストレートアスフ
ァルト、ブローンアスファルトのいずれを使用してもよ
い。また、必要に応じて、タルク、消石灰などのフィラ
ー材を混入してもよい。The asphalt adhesive layer 2 includes, for example, blown asphalt, three kinds of waterproof blown asphalt,
Made of 4 types of waterproof blown asphalt, modified asphalt mixed with 1-20% SBS (styrene-butadiene-styrene block copolymer) in base asphalt, etc., and with appropriate flexibility, it is suitable for nails and staples. It is configured to exhibit adhesiveness, high sealing properties for nails and staples, and waterproofness. Here, any of straight asphalt and blown asphalt may be used as the base asphalt. If necessary, a filler material such as talc or slaked lime may be mixed.
【００１８】尚、前記改質アスファルトとしては、上記
のようにＳＢＳを混入したものが望ましいが、これ以外
の物質、例えば、天然ゴム、ＳＢＲ，ＮＢＲ，ＢＲ，Ｉ
Ｒ，ＣＲ，ＩＩＲ，ＥＰＲ，ＥＰＤＭ，ＰＩＢ，スチレ
ン・イソプレン・スチレンブロック共重合体，塩素化ポ
リエチレン、エチレン、酢酸ビニル共重合体などの合成
ゴム、またはこれらの再生ゴムの一種または二種以上
を、非加硫もしくは加硫のいずれかの状態で配合して改
質したアスファルトであってもよい。The modified asphalt preferably contains SBS as described above, but other substances such as natural rubber, SBR, NBR, BR, I
Synthetic rubber such as R, CR, IIR, EPR, EPDM, PIB, styrene / isoprene / styrene block copolymer, chlorinated polyethylene, ethylene, vinyl acetate copolymer, or one or more of these recycled rubbers It may be asphalt modified by blending in either unvulcanized or vulcanized state.
【００１９】前記耐裂シート材３は、ポリプロピレン、
ポリエステルなどの不織布からなり、前記アスファルト
フェルト１に比べて数倍以上の引裂強度を有し、住宅用
防水材としての耐裂性を向上できるように構成されてい
る。即ち、従来の住宅用防水材（ＪＩＳのアスファルト
フェルト４３０）において、 引裂強度（長手方向）＝０．４ｋｇ 同 （幅方向） ＝０．６ｋｇ であるのに対し、本願住宅用防水材（不織布タイプ）で
は、 引裂強度（長手方向）＝１．８ｋｇ 同 （幅方向） ＝１．６ｋｇ と３〜４倍以上の引裂強度を有している。The tear-resistant sheet material 3 is made of polypropylene,
It is made of a non-woven fabric such as polyester, has a tear strength several times or more higher than that of the asphalt felt 1, and is configured to improve the tear resistance as a waterproofing material for a house. That is, in the conventional waterproofing material for houses (JIS asphalt felt 430), the tear strength (longitudinal direction) = 0.4 kg and the same (width direction) = 0.6 kg. ), The tear strength (longitudinal direction) = 1.8 kg and the same (width direction) = 1.6 kg, which is 3 to 4 times or more the tear strength.
【００２０】また、引張強度も、従来住宅用防水材が、 引っ張り強度＝５．６ｋｇ／ｃｍ であるのに対し、本願住宅用防水材は、 引っ張り強度＝８．６ｋｇ／ｃｍ と高くなっている。The tensile strength of the conventional waterproofing material for a house is 5.6 kg / cm, whereas the waterproofing material of the present invention is as high as 8.6 kg / cm. .
【００２１】該耐裂シート材３には、合成繊維不織布の
替わりに、ポリプロピレン、塩化ビニル、ポリエステ
ル、ポリエチレンなどの合成樹脂フィルムを用いてもよ
い。この場合、表面の印刷性が向上するから、カラフル
でクリアーな化粧印刷を施して建築現場における美観を
増したり、施工業者やメーカーの企業名を印刷して、広
い壁面を広告・宣伝に用いたりすることができる。As the tear-resistant sheet material 3, a synthetic resin film such as polypropylene, vinyl chloride, polyester, or polyethylene may be used instead of the synthetic fiber nonwoven fabric. In this case, the printability of the surface is improved, so that colorful and clear makeup printing is applied to increase the aesthetics at the construction site, or the name of the contractor or manufacturer is printed, and wide wall surfaces are used for advertising and publicity. can do.
【００２２】該耐裂シート材３として用いる合成繊維不
織布は、 目付量＝１５〜１００ｇ／ｍ2 なる範囲のものが好ましく用いられる。また、該耐裂シ
ート材３として用いる合成樹脂フィルムは、 厚さ＝１０〜１００μｍ なる範囲のものが好ましく用いられる。尚、該耐裂シー
ト材３として、合成繊維不織布と合成樹脂フィルムの中
間的性質を持つ素材である合成紙を用いてもよい。The synthetic fiber nonwoven fabric used as the tear-resistant sheet material 3 preferably has a basis weight of 15 to 100 g / m 2 . The synthetic resin film used as the tear-resistant sheet material 3 preferably has a thickness of 10 to 100 μm. Incidentally, as the tear-resistant sheet material 3, synthetic paper which is a material having intermediate properties between a synthetic fiber nonwoven fabric and a synthetic resin film may be used.
【００２３】上記実施例において、最内層のアスファル
トフェルト１は、前述のように調湿性を備えつつ、住宅
用防水材の主材として、高い防水性を発揮する。また、
中間層のアスファルト接着層２は、それ自体が持つ疎水
性により防水効果を高めるとともに、釘穴をシールして
雨水の侵入などを防ぎ、下地板やベニヤ板の腐食を防止
する。さらに、最外層の耐裂シート材３は、施工段階で
の風等の外力負荷や完成後の建物の動きに伴う負荷によ
る住宅用防水材の引裂を防止することができる。In the above embodiment, the innermost layer of asphalt felt 1 exhibits high waterproofness as a main component of a waterproofing material for a house while providing humidity control as described above. Also,
The asphalt adhesive layer 2 as the intermediate layer enhances the waterproof effect by its own hydrophobicity, seals the nail holes to prevent rainwater from entering, and prevents corrosion of the base plate and the veneer plate. Further, the outermost layer of the tear-resistant sheet material 3 can prevent the waterproofing material for a house from tearing due to an external load such as wind at the construction stage or a load caused by the movement of the completed building.
【００２４】[0024]
【発明の効果】上記のようにこの発明は、原紙にストレ
ートアスファルトまたはピッチを含浸してなるアスファ
ルトフェルトの片面に、シール性を有するアスファルト
接着層を介して、合成繊維不織布または合成樹脂フィル
ムからなる耐裂性シート材を設けているので、アスファ
ルトフェルトによる防水性、アスファルト接着層による
シール性、耐裂シート材による高強度を合わせ持つ住宅
用防水材を提供することができる。As described above, according to the present invention, the base paper
Since one side of asphalt felt impregnated with asphalt or pitch is provided with a tear-resistant sheet material made of a synthetic fiber nonwoven fabric or a synthetic resin film via an asphalt adhesive layer having a sealing property. Thus, it is possible to provide a waterproofing material for a house which has a combination of waterproofness by asphalt felt, sealing by an asphalt adhesive layer, and high strength by a tear-resistant sheet material.
【００２５】特に、耐裂シート材として、印刷適合性に
優れた合成樹脂フィルムを用いる場合、化粧性と広告・
宣伝性に優れた外観を得ることができる。In particular, when a synthetic resin film having excellent printability is used as the tear-resistant sheet material, the cosmetic property and advertisement /
An appearance with excellent advertising properties can be obtained.
【００２６】この結果、従来の住宅用防水材では達成不
可能な作業性の良さと、防水性能の向上を同時に実現で
き、しかも広告・宣伝媒体としての用途をも開拓可能な
住宅用防水材を提供できるという優れた効果を奏するも
のである。As a result, there is provided a housing waterproofing material which can simultaneously achieve good workability which cannot be achieved with the conventional housing waterproofing material and improvement of the waterproofing performance, and which can also be used as an advertising / promotion medium. This is an excellent effect that it can be provided.
【図１】最外層に合成繊維不織布を用いた本願住宅用防
水材の断面図である。FIG. 1 is a cross-sectional view of a waterproofing material for a house according to the present invention using a synthetic fiber nonwoven fabric as an outermost layer.
【図２】最外層に合成樹脂フィルムを用いた本願住宅用
防水材の断面図である。FIG. 2 is a cross-sectional view of a waterproofing material for a house of the present application using a synthetic resin film as an outermost layer.
【図３】従来の住宅用防水材を用いたモルタル壁の断面
図である。FIG. 3 is a cross-sectional view of a mortar wall using a conventional residential waterproof material.
１ アスファルトフェルト ２ アスファルト接着層 ３ 耐裂シート材（合成繊維不織布または合成樹脂フィ
ルム）Reference Signs List 1 asphalt felt 2 asphalt adhesive layer 3 tear-resistant sheet material (synthetic fiber nonwoven fabric or synthetic resin film)
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) D06N 5/00 E04F 13/08 E04D 5/10 ──────────────────────────────────────────────────続 き Continued on front page (58) Field surveyed (Int.Cl. 7 , DB name) D06N 5/00 E04F 13/08 E04D 5/10
Claims (1)
ッチを含浸してなるアスファルトフェルトの片面に、ア
スファルト接着層を介して、合成繊維不織布または合成
樹脂フィルムを設けたことを特徴とする住宅用防水材。(1) A straight asphalt or pi
A waterproofing material for houses, characterized in that a synthetic fiber nonwoven fabric or a synthetic resin film is provided on one side of an asphalt felt impregnated with a stitch through an asphalt adhesive layer.