JP3149866U

JP3149866U - Blackboard sheet

Info

Publication number: JP3149866U
Application number: JP2009000516U
Authority: JP
Inventors: 希予稲垣
Original assignee: 株式会社ライト黒板製作所
Priority date: 2009-02-05
Filing date: 2009-02-05
Publication date: 2009-04-16
Anticipated expiration: 2019-02-05

Abstract

【課題】嵩が低く且つ軽量で、一人でも持ち運びや取り付け作業ができると共に、新たな黒板の他、既存の黒板表面やその他のボード面等に取り付けることで新たな黒板を製作することができ、皺が付き難く、磨耗も少ない黒板シートの提供を課題とする。【解決手段】既存の黒板表面に張り付けることで新しい黒板表面とすることができる黒板シート１０であって、最下層をなす剥離紙１１で両面接着材１２の下面を被覆し、該両面接着材１２の上面にプラスチックフィルム１３を接着し、該プラスチックフィルム１３の上表面には黒板塗料１４を積層して、全体を１枚の巻回自在な柔軟シートとした。【選択図】図１[PROBLEMS] To be low in weight and light weight, and can be carried and attached by one person, and in addition to a new blackboard, a new blackboard can be manufactured by attaching to an existing blackboard surface or other board surface, The challenge is to provide a blackboard sheet that is less prone to wrinkles and wear. A blackboard sheet (10) that can be used as a new blackboard surface by pasting on an existing blackboard surface, the lower surface of a double-sided adhesive material (12) is covered with a release paper (11) that forms the lowermost layer, and the double-sided adhesive material A plastic film 13 was adhered to the upper surface of 12, and a blackboard paint 14 was laminated on the upper surface of the plastic film 13, so that the whole was made into one flexible sheet that could be wound. [Selection] Figure 1

Description

本考案は既存の黒板の表面に張り付けることで、新たな黒板表面とすることができる黒板シートに関する。 The present invention relates to a blackboard sheet that can be used as a new blackboard surface by sticking to the surface of an existing blackboard.

従来、黒板は一般に、ベニア板等の上に塗料を施した鉄板等を張り付けた形で構成されており、学校やその他の場所で使用されている。その黒板が古くなると、黒板の表面の塗装剥離や表面全体が白ボケするようになり、チョークの乗りが悪くなったりするので、黒板全体を新しいものに取り替えたり、或いは黒板の表面を補修する必要がある。
前記黒板表面の補修は、例えば表面に黒板用塗料を塗った鉄板やホーロー板、或いはそれにベニア板を裏打ちしたものを、黒板用張り付けボードとして既存の黒板の表面の更に上から糊付けして張り合わせて新たな黒板表面とすることができる。
一方、特開２００２−２１８６号公報には、合板製の基板（１）の表面に接着剤（６）によってマグネットシート（５）を貼着し、このマグネットシート（５）の表面に合成樹脂製の剥離シート（１３）を介して磁気吸引力によって鋼板製の黒板表面材（７）を貼着した黒板が提供されている（特許文献１）。
また特開２００２−２７４０９５号公報には、木質基板（１）に接着剤（６）で層状に構成されたシート構成部材（２ｂ）からなる剥離可能なシート部材（２）を貼着し、更に該シート部材（２）を介して金属製の黒板用表面板（３）を接着剤（８）で貼着した黒板が提供されている（特許文献２）。
また特開２００３−１１８２９４号公報には、木製等の基板（１）上に接着剤（２）等を介して取り付けられた鋼板（３）や既存の鋼鉄製黒板、鋼鉄製の建物壁面等の上方に、両面に磁気吸着力を有するシート状磁石（４）を介在させて、この磁気吸着力によって鋼板製表示部材（５）又はシート状磁石製表示部材（７）を取り付けた表示装置が提供されている（特許文献３）。
また特開２００４−１６０９３４号公報には、基板（１）の片面（１ａ）又は両面（１ａ、１ｂ）に、両面粘着シート（２）を介して表記用金属製表面板（３）を貼着した表記又は掲示板及び表記掲示兼用板が提供されている（特許文献４）。 Conventionally, a blackboard is generally configured by sticking an iron plate or the like with a paint on a veneer plate or the like, and is used in schools or other places. When the blackboard becomes old, the paint on the blackboard surface is peeled off and the entire surface becomes white blurred, and the riding of the chalk becomes worse, so it is necessary to replace the entire blackboard with a new one or repair the surface of the blackboard There is.
The blackboard surface is repaired by, for example, pasting an iron plate or enamel plate coated with blackboard paint on the surface, or veneer board backed, and pasting it from above the surface of the existing blackboard as a blackboard pasting board. It can be a new blackboard surface.
On the other hand, in JP 2002-2186 A, a magnet sheet (5) is adhered to the surface of a plywood substrate (1) with an adhesive (6), and the surface of the magnet sheet (5) is made of synthetic resin. A blackboard is provided in which a blackboard surface material (7) made of a steel plate is attached by magnetic attraction force through a release sheet (13) (Patent Document 1).
In JP 2002-274095 A, a peelable sheet member (2) composed of a sheet constituent member (2 b) configured in layers with an adhesive (6) is attached to a wooden substrate (1), and further There is provided a blackboard in which a metal blackboard surface plate (3) is bonded with an adhesive (8) through the sheet member (2) (Patent Document 2).
Japanese Patent Laid-Open No. 2003-118294 discloses a steel plate (3) attached to a wooden substrate (1) via an adhesive (2), an existing steel blackboard, a steel building wall, etc. Provided is a display device in which sheet-like magnets (4) having magnetic attractive force are interposed on both sides and a steel plate display member (5) or a sheet-like magnet display member (7) is attached by this magnetic attractive force. (Patent Document 3).
Japanese Patent Application Laid-Open No. 2004-160934 has a notation metal surface plate (3) attached to one side (1a) or both sides (1a, 1b) of a substrate (1) through a double-sided adhesive sheet (2). There is provided a notation or bulletin board and a sign-posting board (Patent Document 4).

特開２００２−２１８６号公報Japanese Patent Laid-Open No. 2002-2186 特開２００２−２７４０９５号公報JP 2002-274095 A 特開２００３−１１８２９４号公報JP 2003-118294 A 特開２００４−１６０９３４号公報JP 2004-160934 A

ところが上記黒板用張り付けボードを既存の黒板表面に糊付けする従来の方法では、ボードが広面積であるために、嵩をとると共に数人でなければこれを持ち運ぶことができず、また面積の割には厚みが薄いので、持ち運んだりしている間にボードが捩じれて歪んだりする欠点があった。更にボードを黒板表面に張り付ける際には、黒板表面若しくはボードの裏面に接着剤を塗布しなければならず、しかも糊を塗布した後に広面積のボードを上手く張り付けるのは容易ではなく、作業に人手が必要となる問題があった。
一方、特許文献１に示す黒板の場合、接着剤等を使用することなく、マグネットシート（５）の磁気吸着力によって合板製基板（１）に鋼板製の黒板表面材（７）を取り付けることができると共に、剥離シート（１３）を剥がすだけで、古い黒板表面材（７）を容易に取り外して新しい黒板表面材（７）に張り替えることができる。しかし、黒板表面材（７）には強磁性の金属（鋼板）を用いる必要があり、鋼板製の黒板表面材（７）の場合、小さく丸め難く、また１人での取り付け作業が難しい問題がある。
また特許文献２に示す黒板の場合、シート構成部材（２ｂ）をシート層（２ａ）間で剥離させることで、木質基板（１）から古い金属製の黒板用表面板（３）を容易に取り外せ、新しい鋼板製の黒板表面材（３）と張り替えることができる。しかしながら、黒板表面材（７）は鋼板製であり、またそれぞれを接着剤（６、８）で取り付けているので、１人では運搬や張り替え作業を満足に出来ない問題がある。
また特許文献３に示す表示装置の場合、シート状磁石（４）を用いているため、前述の特許文献１に示す黒板の場合と同様の問題がある。
また特許文献４も示す表記または掲示板及び表記掲示兼用板の場合、基板（１）に両面粘着シート（２）で表記用金属製表面板（３）を貼着しているので、接着剤を用いる場合に比べて、作業が簡単で衛生上安全である。しかしながら、表記用板には金属製のものを使用しているので、現場で新しい表記用金属製表面板（３）と張り替えるには重く、１人では作業が満足に出来ない問題がある。 However, in the conventional method of pasting the blackboard pasting board on the surface of the existing blackboard, the board has a large area, so it is bulky and can only be carried by a few people. Because of its thin thickness, there was a drawback that the board was twisted and distorted while being carried. Furthermore, when sticking the board to the blackboard surface, it is necessary to apply an adhesive to the blackboard surface or the back side of the board, and it is not easy to stick a large area board well after applying glue. There was a problem that required manpower.
On the other hand, in the case of the blackboard shown in Patent Document 1, the blackboard surface material (7) made of steel plate can be attached to the plywood substrate (1) by the magnetic adsorption force of the magnet sheet (5) without using an adhesive or the like. At the same time, the old blackboard surface material (7) can be easily removed and replaced with a new blackboard surface material (7) simply by peeling off the release sheet (13). However, it is necessary to use a ferromagnetic metal (steel plate) for the blackboard surface material (7). In the case of the blackboard surface material (7) made of steel plate, there is a problem that it is difficult to round and difficult to install by one person. is there.
In the case of the blackboard shown in Patent Document 2, the old metal blackboard surface plate (3) can be easily removed from the wooden board (1) by peeling the sheet constituent member (2b) between the sheet layers (2a). It can be replaced with a new blackboard surface material (3) made of steel plate. However, since the blackboard surface material (7) is made of a steel plate and each is attached with an adhesive (6, 8), there is a problem that one person cannot satisfy the transportation and reworking work.
Further, in the case of the display device shown in Patent Document 3, since the sheet-like magnet (4) is used, there is a problem similar to the case of the blackboard shown in Patent Document 1 described above.
In addition, in the case of the notation shown in Patent Document 4 or a bulletin board and a notation display combined plate, the notable metal surface plate (3) is adhered to the substrate (1) with the double-sided pressure-sensitive adhesive sheet (2), and therefore an adhesive is used. Compared to the case, the work is simple and hygienic. However, since the notation plate is made of metal, it is heavy to replace with a new notation metal surface plate (3) on site, and there is a problem that one person cannot satisfactorily work.

そこで本考案は上記従来技術の問題を解消し、嵩が低く且つ軽量で、一人でも持ち運びや取り付け作業ができると共に、既存の黒板表面やその他のボード面等に取り付けることで新たな黒板を製作することができ、皺が付き難く、表面の磨耗も少ない黒板シートの提供を課題とする。 Therefore, the present invention solves the above-mentioned problems of the prior art, is low in volume and light in weight, and can be carried and attached by one person, and a new blackboard is manufactured by attaching it to the surface of an existing blackboard or other board surface. It is an object to provide a blackboard sheet that can be easily scratched and has little surface wear.

上記課題を達成するため本考案の黒板シートは、既存の黒板表面に張り付けることで新しい黒板表面とすることができる黒板シートであって、最下層をなす剥離紙で両面接着材の下面を被覆し、該両面接着材の上面にプラスチックフィルムを接着し、該プラスチックフィルムの上表面には黒板塗料を積層して、全体を１枚の巻回自在な柔軟シートとしたことを第１の特徴としている。
また本考案の黒板シートは、上記第１の特徴に加えて、シートの張り付け対象は、黒板表面の他、平らな板面、平らな壁面、その他の平面とすることを第２の特徴としている。
また本考案の黒板シートは、上記第１又は第２の特徴に加えて、プラスチックフィルムはポリエステルフィルムとしたことを第３特徴としている。
また本考案の黒板シートは、上記第３の特徴に加えて、ポリエステルフィルムの厚みを数十〜数百μｍとしたことを第４特徴としている。
また本考案の黒板シートは、上記第１〜第４の何れかの特徴に加えて、表面層の黒板塗料はグリーン、ブラック、ホワイトの何れか１つの色としたことを第５特徴としている。 In order to achieve the above object, the blackboard sheet of the present invention is a blackboard sheet that can be used as a new blackboard surface by pasting it on the surface of an existing blackboard, and the lower surface of the double-sided adhesive material is covered with a release paper that forms the bottom layer. The first feature is that a plastic film is adhered to the upper surface of the double-sided adhesive, and a blackboard paint is laminated on the upper surface of the plastic film to form a single flexible sheet that can be rolled up. Yes.
In addition to the first feature described above, the blackboard sheet of the present invention has a second feature that the object to which the sheet is attached is a flat plate surface, a flat wall surface, and other flat surfaces in addition to the blackboard surface. .
In addition to the first or second feature, the blackboard sheet of the present invention has a third feature that the plastic film is a polyester film.
In addition to the third feature, the blackboard sheet of the present invention has a fourth feature that the thickness of the polyester film is several tens to several hundreds of micrometers.
Further, the blackboard sheet of the present invention has a fifth feature that, in addition to any of the first to fourth features, the blackboard paint of the surface layer is any one of green, black, and white.

請求項１に記載の黒板シートによれば、既存の黒板表面に張り付けることで新しい黒板表面とすることができる黒板シートであって、最下層をなす剥離紙で両面接着材の下面を被覆し、該両面接着材の上面にプラスチックフィルムを接着し、該プラスチックフィルムの上表面には黒板塗料を積層して、全体を１枚の巻回自在な柔軟シートとしたので、
鉄板等を使用した従来のボードに比べて重量を非常に軽くすることができ、黒板張り替えの際等における持ち運びが非常に容易である。
また剥離紙が付く両面接着材とプラスチックフィルムと、その上に積層された黒板塗料からなる巻回自在な柔軟シートであるので、これを適当に巻回した状態で持ち運びすることができる。また黒板張り替えの際等の機械を用いて吊り上げる作業等を全く必要とすることなく、１人で運んで１人で張り替えを行うことができる。
また両面接着材による均一で強力な接着力で黒板表面に密着させるようにしているので、糊付けする場合に比べて、皺等の発生を抑制することができ、また失敗しても部分的に両面接着材を取り替えて張り直すことができ、結果として非常に綺麗な表面の黒板を確実に再生することができる。
またこの黒板シートが古くなった場合には、元の黒板から黒板シートを取り外し、何度でも新しい黒板シートに取り替えることができるので、長期間に渡って綺麗な黒板として使用することができる。
その他、本考案の黒板シートは、ハサミやナイフでも容易にカットして所望の形状、寸法にすることができ、汎用性よく、種々の形状や寸法の黒板に対して臨機応変に適応させることができる。これに対して従来の黒板では、電動鋸等の専用のカット機械や器具が必要であった。 According to the blackboard sheet of claim 1, a blackboard sheet that can be made a new blackboard surface by pasting it on the surface of an existing blackboard, wherein the lower surface of the double-sided adhesive is covered with a release paper that forms the bottom layer. Since the plastic film is bonded to the upper surface of the double-sided adhesive, and the blackboard paint is laminated on the upper surface of the plastic film, the whole is made into one flexible sheet that can be wound.
Compared with a conventional board using an iron plate or the like, the weight can be made very light, and it is very easy to carry when replacing the blackboard.
In addition, since it is a flexible sheet that can be wound, comprising a double-sided adhesive and a plastic film with release paper and a blackboard paint laminated thereon, it can be carried in a properly wound state. Moreover, it is possible to carry it by one person and perform the renewal by one person without requiring any lifting work using a machine such as a blackboard repainting.
In addition, since it is made to adhere to the blackboard surface with a uniform and strong adhesive force with double-sided adhesive, it can suppress the occurrence of wrinkles compared to the case of gluing, and even if it fails, it is partially on both sides The adhesive material can be replaced and re-stripped, and as a result, a very clean blackboard can be reliably regenerated.
When this blackboard sheet becomes old, the blackboard sheet can be removed from the original blackboard and replaced with a new blackboard sheet any number of times, so that it can be used as a beautiful blackboard for a long period of time.
In addition, the blackboard sheet of the present invention can be easily cut into scissors and knives to have the desired shape and dimensions, and can be flexibly adapted to blackboards of various shapes and dimensions with good versatility. it can. In contrast, conventional blackboards require special cutting machines and tools such as electric saws.

また請求項２に記載の黒板シートによれば、請求項１又は２に記載の構成による作用効果に加えて、シートの張り付け対象は、黒板表面の他、平らな板面、平らな壁面、その他の平面とするので、
黒板シートの取付対象が固定された既存の黒板に限定されることなく、その用途と設置場所の対象を広げることができる。自由に持ち運びができる平らな板に黒板シートを取り付けることで、自由に移動可能な黒板として利用したり、また平らで両面接着材による接着が可能な板面、壁面に直接黒板シートを張り付けることで、壁面自体を黒板として利用することもでき、黒板の製作に対する速さとコストの軽減、そして黒板の用途と設置を自由に創造することができる。
更に本考案の黒板シートを壁紙材として、壁や床面、家具の一部分等の平面に張り付けることで、どこでも、誰でも、手軽に、書き消しできる黒板面を構成することができる。
また黒板表面の他、平らな板面、平らな壁面、その他の平面に張り付けても、黒板シートが古くなった場合には、黒板シートのみを取り外して丸めて回収すればよいので、黒板シートを何度も取り替えることで、長期間に渡って綺麗な黒板を使用することができる。 Further, according to the blackboard sheet of claim 2, in addition to the function and effect of the configuration of claim 1 or 2, the sheet is attached to a flat plate surface, flat wall surface, etc. in addition to the blackboard surface Because it is the plane of
Without being limited to the existing blackboard on which the blackboard sheet is attached, the range of uses and installation locations can be expanded. By attaching the blackboard sheet to a flat board that can be freely carried, you can use it as a freely movable blackboard, or stick the blackboard sheet directly to the flat or wall surface that can be bonded with double-sided adhesive. The wall itself can be used as a blackboard, and the speed and cost of making the blackboard can be reduced, and the use and installation of the blackboard can be freely created.
Further, by sticking the blackboard sheet of the present invention as a wallpaper material to a flat surface such as a wall, a floor surface, or a part of furniture, a blackboard surface that can be easily erased by anyone can be constructed.
In addition, if the blackboard sheet becomes old even if it is pasted on the flat board surface, flat wall surface, or other flat surface other than the blackboard surface, only the blackboard sheet can be removed, rolled up, and collected. By changing it many times, you can use a beautiful blackboard for a long time.

また請求項３に記載の黒板シートによれば、請求項１又は２に記載の構成による作用効果に加えて、プラスチックフィルムはポリエステルフィルムとしたので、
黒板シートの強度と柔軟性とを適度にすることができ、また黒板塗料との密着性を良好にして、シートを巻回したり延ばしたりしても黒板塗料に皺が入るのを確実に防止することができる。 Moreover, according to the blackboard sheet of claim 3, in addition to the function and effect of the configuration of claim 1 or 2, the plastic film is a polyester film,
The strength and flexibility of the blackboard sheet can be moderated, and the adhesion to the blackboard paint is good, so that the blackboard paint is surely prevented from wrinkling even if the sheet is wound or extended. be able to.

また請求項４に記載の黒板シートによれば、請求項３に記載の構成による作用効果に加えて、ポリエステルフィルムの厚みを数十〜数百μｍとしたので、
黒板シートに充分な強度と柔軟性とを持たせることができると共に、チョーク等を押し当てて書くのに適度な硬さを提供することができる。 Moreover, according to the blackboard sheet of Claim 4, in addition to the effect by the structure of Claim 3, since the thickness of the polyester film was made dozens to several hundreds of micrometers,
The blackboard sheet can have sufficient strength and flexibility, and can provide an appropriate hardness for writing by pressing a chalk or the like.

また請求項５に記載の黒板シートによれば、請求項１〜４の何れかに記載の構成による作用効果に加えて、表面層の黒板塗料はグリーン、ブラック、ホワイトの何れか１つの色としたので、
予め好みの色の黒板シートを用意することで、黒板の表面をグリーンにも、ブラックにも、ホワイトにも張り替えることができる。 Moreover, according to the blackboard sheet of claim 5, in addition to the function and effect of the structure according to any one of claims 1 to 4, the blackboard paint of the surface layer is any one of green, black, and white. So
By preparing a blackboard sheet of a favorite color in advance, the surface of the blackboard can be replaced with green, black, or white.

本考案の実施形態に係る黒板シートの斜視図である。It is a perspective view of a blackboard sheet concerning an embodiment of the present invention. 本考案の黒板シートの剥離紙を剥がす状態を示す斜視図である。It is a perspective view which shows the state which peels the release paper of the blackboard sheet | seat of this invention. 本考案の黒板シートを既存の黒板表面に張り付ける状態を説明する図である。It is a figure explaining the state which sticks the blackboard sheet | seat of this invention on the existing blackboard surface.

図１を参照して、本考案の黒板シート１０は、最下層を剥離紙１１とし、該剥離紙１１を下面に被覆して接着力を保持する両面接着材１２と、その両面接着材１２の上面に取り付けたプラスチックフィルム１３と、該プラスチックフィルム１３の上表面に黒板塗料１４を積層して、巻回自在で柔軟なシートに構成している。 Referring to FIG. 1, a blackboard sheet 10 of the present invention has a release paper 11 as a lowermost layer, a double-sided adhesive 12 that covers the release paper 11 on the lower surface and maintains adhesive force, and a double-sided adhesive 12 A plastic film 13 attached to the upper surface and a blackboard paint 14 are laminated on the upper surface of the plastic film 13 to form a flexible sheet that can be wound around.

剥離紙１１は、前記両面接着材１２の下面、即ち既存の黒板表面等の被張り付け対象に前記黒板シート１０を張り付ける側の面に被着され、前記両面接着材１２が他のものに接着したり、埃等によって接着力が損なわれないよう保持できる紙とする。紙の片面（両面接着材１２を被覆する面）にはコーティング加工が施されており、これによって前記両面接着材１２の接着面に被着しても、コーティング加工によって接着せず、着脱自在に取り付けることができる。
剥離紙１１は、前記両面接着材１２の下面側の接着力を保持するために被着されているので、大きさは該両面接着材１２と同等のものを用いる。
剥離紙１１によって、前記両面接着材１２の上面を前記プラスチックフィルム１３の裏面全体に取り付ける際にも、他のものに該両面接着材１２が触れて汚れたり、誤って接着することを防ぐことができると共に、前記黒板シート１０を既存の黒板表面や平らな板面或いは壁面等に取り付ける時点まで新しい接着力の状態を保持することができる。 The release paper 11 is attached to the lower surface of the double-sided adhesive material 12, that is, the surface on the side where the blackboard sheet 10 is attached to the surface to be attached such as the existing blackboard surface, and the double-sided adhesive material 12 is adhered to the other surface. Or paper that can be held so that the adhesive strength is not impaired by dust or the like. One side of the paper (the side that covers the double-sided adhesive 12) is coated, so that even if it is attached to the adhesive surface of the double-sided adhesive 12, it does not adhere to the coating and is detachable. Can be attached.
Since the release paper 11 is attached to maintain the adhesive force on the lower surface side of the double-sided adhesive material 12, the size is the same as that of the double-sided adhesive material 12.
Even when the upper surface of the double-sided adhesive 12 is attached to the entire back surface of the plastic film 13 by the release paper 11, the double-sided adhesive 12 can be prevented from being soiled or adhered by mistake to other things. In addition, the state of the new adhesive force can be maintained until the blackboard sheet 10 is attached to an existing blackboard surface, flat plate surface, wall surface, or the like.

両面接着材１２は、下面に前記剥離紙１１を被着し、上面に前記プラスチックフィルム１３の裏面を取り付ける。それにより前記黒板シート１０を取り付ける際には、現場での糊付け作業を不要とし、該黒板シート１０を接着する対象物に対しては、前記両面接着材１２に被着した前記剥離紙１１を剥がして簡単に張り付けることができる。
なお両面接着材１２としては、例えば両面テープのような貼着が簡単で接着力もある材質が好ましい。 The double-sided adhesive 12 attaches the release paper 11 to the lower surface and attaches the back surface of the plastic film 13 to the upper surface. Thus, when the blackboard sheet 10 is attached, no on-site gluing work is required, and the release paper 11 attached to the double-sided adhesive 12 is peeled off from the object to which the blackboard sheet 10 is bonded. Can be attached easily.
In addition, as the double-sided adhesive material 12, for example, a material such as a double-sided tape that is easy to stick and has an adhesive force is preferable.

プラスチックフィルム１３は、芯部材を構成すると共に表面に黒板塗料１４を積層して前記黒板シート１０の基礎部材を構成する役割を果たすものである。材質の特性としては、適度な柔軟性があり、その柔軟性によって前記黒板塗料１４を確実に密着させ、これによって卷回したり延ばしたりしても皺が入ることなく基礎部材としての役割を果たす。
プラスチックフィルム１３は、ポリエステル（ＰＥＴ）フィルムとすることができる。
またこのポリエステルフィルムの厚みは、例えば数十〜数百μｍとすることができるが、黒板シートに充分な強度と柔軟性とを持たせることができると共に、チョーク等を押し当てて書くのに適度な硬さを必要とすることから、本実施形態では１００μｍ程度としている。ポリエステルフィルムとすることで、黒板シート１０として相応しい強度と硬度を備え、且つ巻回することができ、巻回を解いた際にも表面が凸凹しないフラットな面を提供することができる。ポリエステルフィルムの代わりに金属シート、金属フィルムを用いる場合には、巻回したり、それを解いたりすることで表面が凸凹になり易い。 The plastic film 13 serves as a core member and a base member of the blackboard sheet 10 by laminating blackboard paint 14 on the surface. As a characteristic of the material, there is an appropriate flexibility, and the blackboard paint 14 is securely adhered by the flexibility, and thus plays a role as a basic member without being wrinkled even if it is rolled or extended.
The plastic film 13 can be a polyester (PET) film.
The thickness of this polyester film can be, for example, several tens to several hundreds of μm. However, the blackboard sheet can have sufficient strength and flexibility and is suitable for writing with chalk or the like. In this embodiment, the thickness is set to about 100 μm. By using the polyester film, the blackboard sheet 10 can have appropriate strength and hardness and can be wound, and a flat surface whose surface is not uneven when unwinding can be provided. When a metal sheet or metal film is used instead of the polyester film, the surface tends to be uneven by winding or unwinding.

黒板塗料１４は、前記プラスチックフィルム１３の上表面に積層される塗料として、熱硬化性アクリル樹脂１００部、架橋剤としてアミノ樹脂１０〜１００部、エポキシ樹脂１〜３０部を配合したものを基本樹脂組成としている。この基本樹脂１００部に平均粒径が１〜１００μｍのグリーン、ブラック、ホワイトの各種着色顔料、体質顔料を１００〜３５０部の割合で配合し、これをボールミル、ロールミル、サンドグラインドミル等により分散させ、グラインドゲージによる分散度を３０〜５０μｍになるように調整する。前記ホワイトの場合は紫外線カット塗料とすることができる。
ポリエステルからなる前記プラスチックフィルム１３の上表面を静電処理した後、上記黒板塗料１４を高温塗装する。高温塗装は、例えばエポキシ系プライマーを５μｍ、１４０〜１６０℃以下で２０秒焼き付け、乾燥塗布量が１０〜３０μｍになるようにリバースコーターで連続的に塗布し、１４０〜１６０℃以下で６０秒焼き付けを行う。 The blackboard paint 14 is a basic resin in which 100 parts of thermosetting acrylic resin is blended on the upper surface of the plastic film 13, 10 to 100 parts of amino resin is used as a crosslinking agent, and 1 to 30 parts of epoxy resin is blended. It has a composition. 100 parts of this basic resin are blended with 100 to 350 parts of green, black and white colored pigments and extender pigments having an average particle diameter of 1 to 100 μm, and are dispersed by a ball mill, roll mill, sand grind mill or the like. The dispersion degree by a grind gauge is adjusted to 30 to 50 μm. In the case of the white, it can be an ultraviolet cut paint.
After the upper surface of the plastic film 13 made of polyester is electrostatically treated, the blackboard paint 14 is coated at a high temperature. For high temperature coating, for example, an epoxy primer is baked at 5 μm and 140 to 160 ° C. for 20 seconds, continuously applied with a reverse coater so that the dry coating amount is 10 to 30 μm, and baked at 140 to 160 ° C. and below for 60 seconds. I do.

上記のようにしてできた黒板シート１０は、図２に示すように巻回してロール状にすることで、軽くて持ち運びが容易な状態とすることができる。よって運搬や吊り上げのための機械を必要とせず、運搬人も１人で充分となる。 The blackboard sheet 10 made as described above can be made light and easy to carry by winding it into a roll as shown in FIG. Therefore, a machine for transporting and lifting is not required, and one transporter is sufficient.

本考案の黒板シート１０は、厚みが非常に薄く、しかも強度と柔軟性を有するので、既存の黒板Ｂの上に張り合わせても嵩張らず、新しい黒板として使用することができる。
また両面接着材１２を用いているので、既存の黒板Ｂのみならず、平らな板面、平らな壁面等、平らな面をもつものであれば、張り付け対象の材質や場所を限定されることはなく、種々のものに簡単に張り付けて黒板とすることができる。
また黒板シートは、電動鋸等の専用の機械、器具を用いることなく、ハサミ、ナイフで簡単にカットして、その場でも所望の形状にすることができる。よって、一種の壁紙として、張り付け対象物の形状や寸法に合わせて、自在に、黒板面を構成することができる。
勿論、壁面や床、家具の一部に小さな形状にカットした本考案の黒板シートをワッペン状に張り付けて、書き消しできるようにすることができる。 Since the blackboard sheet 10 of the present invention is very thin and has strength and flexibility, it is not bulky even when pasted on the existing blackboard B, and can be used as a new blackboard.
Moreover, since the double-sided adhesive 12 is used, not only the existing blackboard B but also a flat surface such as a flat plate surface or a flat wall surface, the material and location to be pasted are limited. Rather, it can be easily pasted on various things to make a blackboard.
Further, the blackboard sheet can be easily cut with scissors and a knife without using a dedicated machine or instrument such as an electric saw, and can be formed into a desired shape on the spot. Therefore, as a kind of wallpaper, the blackboard surface can be freely configured according to the shape and size of the object to be pasted.
Of course, the blackboard sheet of the present invention cut into a small shape on the wall surface, floor, or part of the furniture can be pasted in a patch shape so that it can be erased.

図３を参照して、本考案の黒板シート１０を既存の黒板Ｂに取り付ける場合を説明する。
まず既存の黒板Ｂの周縁の押え縁Ｅを外す。次にロール状に巻回された黒板シート１０の端部１０ａの前記剥離紙１１を少し捲り、押え縁Ｅの外された黒板表面Ｓの左右の何れか一辺（図３では右辺）に前記端部１０ａの接着面を合わせる。次に前記剥離紙１１を他辺側へ少しずつ引き捲り、前記黒板シート１０を押さえ延ばしながら、歪みや隙間のないように黒板表面Ｓに張り合わせていく。これによって、前記両面接着材１２の強力な接着力によって、前記黒板シート１０を既存の黒板Ｂの表面Ｓへの密着固定を完成させることができる。前記黒板シート１０の張り付けが終わると、前記外した押え縁Ｅで黒板表面Ｓの周縁を固定することで、前記黒板シート１０が確実に密着した、新しい黒板表面を持つ黒板が完成される。
このように、黒板シート１０の取り付け作業を一人で簡単に行うことができる。
また本考案の黒板シート１０を既存の黒板Ｂ以外のものに適用する場合には、張り付け対象物である壁やその他の平面の寸法、形状に合わせて黒板シート１０をカットし、或いは張り付けて使用したい黒板シート１０の形状（例えば、○や△その他の所望のデザイン形状）、寸法に合わせて黒板シート１０をカットし、カットした黒板シート１０を対象物の表面に張り付けることで黒板面を完成する。 With reference to FIG. 3, the case where the blackboard sheet | seat 10 of this invention is attached to the existing blackboard B is demonstrated.
First, the presser edge E on the peripheral edge of the existing blackboard B is removed. Next, the release paper 11 of the end portion 10a of the blackboard sheet 10 wound in a roll shape is slightly wound, and the edge is placed on one of the left and right sides (right side in FIG. 3) of the blackboard surface S from which the presser edge E is removed. Match the adhesive surface of the part 10a. Next, the release paper 11 is pulled little by little to the other side, and the blackboard sheet 10 is pressed and stretched while being stuck to the blackboard surface S without any distortion or gap. Accordingly, the blackboard sheet 10 can be fixed to the surface S of the existing blackboard B by the strong adhesive force of the double-sided adhesive material 12. When the pasting of the blackboard sheet 10 is finished, the blackboard surface S with the new blackboard surface in which the blackboard sheet 10 is securely adhered is completed by fixing the peripheral edge of the blackboard surface S with the removed pressing edge E.
In this way, the blackboard sheet 10 can be easily attached alone.
In addition, when the blackboard sheet 10 of the present invention is applied to an object other than the existing blackboard B, the blackboard sheet 10 is cut or pasted according to the size and shape of the wall and other planes to be pasted. Cut the blackboard sheet 10 according to the shape (for example, ○, △ or other desired design shape) and dimensions of the blackboard sheet 10 you want to make, and paste the cut blackboard sheet 10 on the surface of the object to complete the blackboard surface To do.

１０黒板シート
１０ａ端部
１１剥離紙
１２両面接着材
１３プラスチックフィルム
１４黒板塗料
Ｂ黒板
Ｓ黒板表面
Ｅ押え縁 DESCRIPTION OF SYMBOLS 10 Blackboard sheet 10a Edge 11 Release paper 12 Double-sided adhesive 13 Plastic film 14 Blackboard paint B Blackboard S Blackboard surface E Presser edge

Claims

A blackboard sheet that can be used as a new blackboard surface by pasting it onto the surface of an existing blackboard. The bottom surface of the double-sided adhesive is covered with the release paper that forms the bottom layer, and a plastic film is bonded to the top surface of the double-sided adhesive A blackboard sheet characterized in that a blackboard paint is laminated on the upper surface of the plastic film so that the whole is a single flexible sheet that can be wound.

The blackboard sheet according to claim 1, wherein the sheet is attached to a flat plate surface, a flat wall surface, or another flat surface in addition to the blackboard surface.

The blackboard sheet according to claim 1 or 2, wherein the plastic film is a polyester film.

The blackboard sheet according to claim 3, wherein the thickness of the polyester film is several tens to several hundreds of μm.

The blackboard sheet according to any one of claims 1 to 4, wherein the blackboard paint of the surface layer is one of green, black and white.