JP3138066B2 - Manufacturing method of offset printing card - Google Patents
Manufacturing method of offset printing cardInfo
- Publication number
- JP3138066B2 JP3138066B2 JP04187303A JP18730392A JP3138066B2 JP 3138066 B2 JP3138066 B2 JP 3138066B2 JP 04187303 A JP04187303 A JP 04187303A JP 18730392 A JP18730392 A JP 18730392A JP 3138066 B2 JP3138066 B2 JP 3138066B2
- Authority
- JP
- Japan
- Prior art keywords
- offset printing
- adhesive
- offset
- card
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、カード表面の全面にオ
フセット印刷が可能なオフセット印刷カードの製造方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing an offset printed card capable of performing offset printing over the entire surface of the card.
【０００２】[0002]
【従来の技術】従来、オフセット印刷カードとして、図
２に示すように骨白塩化ビニルシートの基体１１の表面
に所定のオフセット印刷１２を施したのち、該オフセッ
ト印刷層１２の上面に透明ポリ塩化ビニルフィルムの被
覆１３を、例えばポリウレタン系接着剤層１４を介して
接着した構造のものが知られている。2. Description of the Related Art Conventionally, as an offset printing card, as shown in FIG. 2, a predetermined offset printing 12 is performed on the surface of a substrate 11 of a bone-white vinyl chloride sheet, and then a transparent polychlorinated There is known a structure in which a coating 13 of a vinyl film is bonded via, for example, a polyurethane adhesive layer 14.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、ポリ塩
化ビニルシートには一般のオフセットインキの吸収性が
ほとんどなく、また、前記ポリウレタン系接着剤のよう
な、主に２液反応型の接着剤は常温で硬化が進み、オフ
セットインキが接着しなくなるという問題点があった。
このため、前記被覆１３と基体１１間の接着性を十分な
ものとするには、基体１１の表面に最小限度以上の白地
（オフセット印刷を施さない部分）を残さなければなら
ず、基体全面又は殆ど全面にオフセット印刷を施すこと
ができないので、印刷カードの自由なデザインが妨げら
れていたし、基体表面にエンボス加工やサインパネル加
工を施す場合には、これを白地とするか又は網点印刷を
行わなければならず、カードの印刷デザイン上及び製造
上、大きな支障が伴うものであった。また、シルク印刷
は、これらの問題をある程度解消するものではあるが、
この場合、微細な線や図柄，文字，グラデーション等の
再現性が不良となる欠点がある。本発明は、特定の接着
剤と特定のオフセットインキ組成物との組合せを採用す
ることにより、上記従来の問題点を解決したものであ
る。However, the polyvinyl chloride sheet has almost no absorbability of a general offset ink, and a two-part reactive adhesive such as the polyurethane adhesive is usually at room temperature. , There is a problem that the offset ink does not adhere.
For this reason, in order to make the adhesiveness between the coating 13 and the substrate 11 sufficient, it is necessary to leave a minimum amount of white background (a portion not subjected to offset printing) on the surface of the substrate 11, Since almost no entire surface can be subjected to offset printing, the free design of the print card has been hindered.When embossing or sign panel processing is performed on the substrate surface, make it a white background or use halftone dot printing. This has to be done, and it has a great hindrance in the printing design and manufacturing of the card. Also, silk printing, while solving some of these problems,
In this case, there is a disadvantage that the reproducibility of fine lines, designs, characters, gradations, and the like is poor. The present invention has solved the above-mentioned conventional problems by employing a combination of a specific adhesive and a specific offset ink composition.
【０００４】[0004]
【課題を解決するための手段】本発明は、骨白ポリ塩化
ビニルシート基体の表面に、酢酸ビニル、マレイン酸を
有する塩化ビニル・酢酸ビニル共重合体からなる接着剤
を塗布し、その上からポリエステル樹脂、ポリオール系
アクリレート、光重合開始剤、着色顔料からなる紫外線
硬化型樹脂インキを用いてオフセット印刷を施し、その
表面に前記接着剤を介して透明塩化ビニルフィルムを接
着したことを特徴とするオフセット印刷カードの製造方
法である。According to the present invention, an adhesive comprising a vinyl chloride / vinyl acetate copolymer containing vinyl acetate and maleic acid is applied to the surface of a bone-white polyvinyl chloride sheet substrate, Offset printing was performed using an ultraviolet-curable resin ink composed of a polyester resin, a polyol-based acrylate, a photopolymerization initiator, and a coloring pigment, and a transparent vinyl chloride film was adhered to the surface thereof via the adhesive. This is a method for manufacturing an offset printing card.
【０００５】[0005]
【作用】本発明では、骨白ポリ塩化ビニルシート基体の
表面に、まず、酢酸ビニル、マレイン酸を有する塩化ビ
ニル・酢酸ビニル共重合体からなる接着剤を塗布する。
この接着剤はポリ塩化ビニルシートとの接着が極めてよ
く、基体表面に均一な接着剤層を形成する。次に、この
接着剤層の上から、ポリエステル樹脂、ポリオール系ア
クリレート、光重合開始剤、着色顔料からなる紫外線硬
化型樹脂インキを用いてオフセット印刷し、紫外線照射
によって硬化させるが、このインキは前記接着剤層とな
じみおよびのりがよく、鮮明なオフセット印刷を施すこ
とができる。さらに、このオフセット印刷層の上に前記
接着剤層と同様の接着剤を介して透明ポリ塩化ビニルフ
ィルムを接着する際に、たとえ全面オフセット印刷され
ていてもその接着剤とオフセットインキのなじみがよい
ため接着性は良好で、ポリ塩化ビニルシート基体、オフ
セット印刷層、透明ポリ塩化ビニルフィルムとが完全に
接着したオフセット印刷カードが得られ、全面に鮮明な
オフセット印刷を施した構造の全面オフセット印刷カー
ドの製造が可能となる。According to the present invention, first, an adhesive made of a vinyl chloride / vinyl acetate copolymer containing vinyl acetate and maleic acid is applied to the surface of a bone white polyvinyl chloride sheet substrate.
This adhesive has excellent adhesion to a polyvinyl chloride sheet and forms a uniform adhesive layer on the surface of the substrate. Next, from above the adhesive layer, polyester resin, a polyol-based acrylate, a photopolymerization initiator, offset printing using an ultraviolet curable resin ink composed of a coloring pigment, and cured by ultraviolet irradiation, this ink is the ink The adhesive layer is well-adhered and glued, and clear offset printing can be performed. Further, when a transparent polyvinyl chloride film is bonded on the offset printing layer via the same adhesive as the adhesive layer, even if the entire surface is offset-printed, the adhesive and the offset ink are well adapted. As a result, the adhesiveness is good, and an offset printing card with a completely adhered polyvinyl chloride sheet substrate, offset printing layer, and transparent polyvinyl chloride film is obtained. Can be manufactured.
【０００６】[0006]
【実施例】本発明で使用する接着剤は、酢酸ビニル、マ
レイン酸を有する塩化ビニル・酢酸ビニル共重合体から
なり、オフセットインキ組成物としては、前記ポリエス
テル樹脂としてポリエチレンテレフタレート樹脂又はポ
リエチレンイソフタレート樹脂が、前記ポリオール系ア
クリレートとしてポリエステルアクリレート又はウレタ
ンアクリレートが、前記光重合開始剤としてはイソブチ
ルベンゾインエーテル又は１−ヒドロキシシクロヘキシ
ルフェニルケトン又はベンジルメチルケトンの組合せが
採用される。また、このオフセットインキ組成物におい
てポリエステル樹脂とポリオール系アクリレートとの重
量比率は、おおよそ１：２〜３の範囲内とすることが好
ましく、これにより全面オフセット印刷カードの製造が
可能となる。またこのインキ組成物におけるポリエステ
ル樹脂とポリオール系アクリレートとの合計配合量はお
およそ６０〜９０％（重量基準、以下％はすべて重量基
準のものである）の範囲内とする。また、前記光重合開
始剤の配合量は前記ポリオール系アクリレートの種類や
配合量を考慮して設定される。このような接着剤とオフ
セットインキ組成物との組合せにより透明ポリ塩化ビニ
ルフィルム被覆とオフセット印刷層及び骨白塩化ビニル
シート基体の接着性が極めて良好となる。The adhesive used in the present invention comprises a vinyl chloride / vinyl acetate copolymer having vinyl acetate and maleic acid. As the offset ink composition, the polyester resin is a polyethylene terephthalate resin or a polyethylene isophthalate resin. However, a polyester acrylate or urethane acrylate is used as the polyol acrylate, and a combination of isobutyl benzoin ether or 1-hydroxycyclohexyl phenyl ketone or benzyl methyl ketone is used as the photopolymerization initiator. Further, in this offset ink composition, the weight ratio between the polyester resin and the polyol-based acrylate is preferably in the range of approximately 1: 2 to 3, which enables production of a full-face offset printing card. The total amount of the polyester resin and the polyol-based acrylate in this ink composition is in the range of about 60 to 90% (by weight, hereinafter, all percentages are by weight). The amount of the photopolymerization initiator is set in consideration of the type and the amount of the polyol acrylate. By the combination of such an adhesive and the offset ink composition, the adhesion between the transparent polyvinyl chloride film coating, the offset printing layer and the bone-white vinyl chloride sheet substrate becomes extremely good.
【０００７】オフセット印刷カード製造の一例を示す
と、縦×横×厚さが１００×５０×０．２７ｍｍの骨白
ポリ塩化ビニルシート基体１（以下、図１を参照）の片
面全面に、酢酸ビニル、マレイン酸を有する塩化ビニル
・酢酸ビニル共重合体からなるＶＭＣＨ接着剤（桜宮化
学株式会社製品）を３μｍの厚さに均一に塗布し、該接
着剤層２1 を４０℃で加温、乾燥させた。次に、この接
着剤層２1 の全面に、ポリエステル樹脂２０％とポリオ
ール系アクリレート５０％との合計配合量７０％のベス
トキュアＵＶ−ＳＴＰ−ＫＰ−Ｎｏ．１なるオフセット
インキ（共同印刷株式会社製品）で２μｍの厚さにオフ
セット印刷し、揮発性成分を十分に乾燥させたのち高圧
水銀灯（８０Ｗ／ｃｍ）で上記印刷面に紫外線（ＵＶ）
を４〜５秒照射して光重合性モノマーを重合・硬化させ
てオフセット印刷層３を形成した。さらに、このオフセ
ット印刷層３の表面に上記接着剤を３μｍの厚さに均一
に塗布し、該接着剤層２2 に縦×横×厚さだが１５０×
７５×０．１ｍｍの透明ポリ塩化ビニルフィルムを重層
して該接着剤層２2 全面を被覆４したのち上記と同一条
件で該接着剤層２2 を加温、乾燥させて片面全面オフセ
ット印刷物となし、この印刷物の前記基体１の下面に上
記と同じ接着剤２3 を３μｍの厚さに均一に塗布し、こ
れに上記と同一要領で作成した片面全面オフセット印刷
物の基体下面を重ね、前記接着剤層２2 を上記と同一条
件で加温、乾燥させ、図１に示す構造の両面全面オフセ
ット印刷カードを得た。One example of the production of an offset printing card is as follows. A bone-white polyvinyl chloride sheet substrate 1 (height x width x thickness 100 x 50 x 0.27 mm) (hereinafter referred to as Fig. 1) has acetic acid on its entire surface. vinyl, VMCH adhesive comprising a vinyl chloride-vinyl acetate copolymer having a maleic acid was uniformly applied (Sakuramiya chemical Co., Ltd. product) to a thickness of 3 [mu] m, the adhesive layer 2 1 warm at 40 ° C., Let dry. Next, on the entire surface of the adhesive layer 2 1, the best cure UV-STP-KP-No total amount 70% 20% and 50% polyol acrylate polyester resins. 1 offset printing (product of Kyodo Printing Co., Ltd.) to a thickness of 2 μm, and after sufficiently drying the volatile components, ultraviolet light (UV) is applied to the printing surface with a high-pressure mercury lamp (80 W / cm).
For 4 to 5 seconds to polymerize and cure the photopolymerizable monomer to form the offset print layer 3. Furthermore, the adhesive was uniformly applied to a thickness of 3μm on the surface of the offset printing layer 3, but length × width × thickness adhesive layer 2 2 0.99 ×
75 × 0.1 mm of the transparent polyvinyl chloride film overlaid with the adhesive layer 2 2 entirely covering 4 was then the same conditions as described above the adhesive layer 2 2 heated by the entire one surface offset printed matter was dried No, the same adhesive 2 3 above the lower surface of the substrate 1 of the printed matter was uniformly applied to a thickness of 3 [mu] m, this superimposed substrate lower surface of the entire one surface offset printed material created in the same manner, the adhesive warming the adhesive layer 2 2 above the same condition, and dried to obtain a double-sided entire offset printing card of the structure shown in FIG.
【０００８】[0008]
【発明の効果】以上述べたように、本発明では骨白ポリ
塩化ビニルシート基体の表面に特定の接着剤層を介して
特定のオフセットインキを用いてオフセット印刷を施
し、その表面に上記特定の接着剤を介して透明ポリ塩化
ビニルフィルムを接着したことにより、透明ポリ塩化ビ
ニルフィルムの被覆とオフセット印刷層及び骨白ポリ塩
化ビニルシート基体の接着強度が十分なものとなり、こ
の結果、オフセット印刷カードにおけるオフセット印刷
層の面積比率を任意の大きさに設定することができて全
面オフセット印刷カードの製造が容易となり、微細な
線，図柄，文字，グラテーション等の再現性に優れたオ
フセット印刷技術を印刷カードに好都合に適用すること
が可能となり、隠ぺいカードにも容易に応用されうるも
のである。As described above, according to the present invention, offset printing is performed on the surface of a bone-white polyvinyl chloride sheet substrate with a specific offset ink via a specific adhesive layer, and the surface of the specific By bonding the transparent polyvinyl chloride film via the adhesive, the adhesive strength of the coating of the transparent polyvinyl chloride film and the offset printing layer and the bone white polyvinyl chloride sheet substrate becomes sufficient, and as a result, the offset printing card The offset printing layer area ratio can be set to any size, making it easy to manufacture full-size offset printing cards, and using offset printing technology with excellent reproducibility of fine lines, designs, characters, and gradations. It can be conveniently applied to printed cards and can be easily applied to hidden cards.
【図１】本発明の実施例に係る両面全面オフセット印刷
カードの一部の縦断面図である。FIG. 1 is a longitudinal sectional view of a part of a double-sided full-face offset printing card according to an embodiment of the present invention.
【図２】従来例のオフセット印刷カードの一部の縦断面
図である。FIG. 2 is a longitudinal sectional view of a part of a conventional offset printing card.
１ 基体 ２1 接着剤層 ２2 接着剤層 ２3 接着剤層 ３ オフセット印刷層 ４ 被覆DESCRIPTION OF SYMBOLS 1 Substrate 2 1 Adhesive layer 2 2 Adhesive layer 2 3 Adhesive layer 3 Offset printing layer 4 Coating
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B42D 15/00 341 B42D 15/10 501 B32B 27/00 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int. Cl. 7 , DB name) B42D 15/00 341 B42D 15/10 501 B32B 27/00
Claims (1)
に、酢酸ビニル、マレイン酸を有する塩化ビニル・酢酸
ビニル共重合体からなる接着剤を塗布し、その上からポ
リエステル樹脂、ポリオール系アクリレート、光重合開
始剤、着色顔料からなる紫外線硬化型樹脂インキを用い
てオフセット印刷を施し、その表面に前記接着剤を介し
て透明塩化ビニルフィルムを接着したことを特徴とする
オフセット印刷カードの製造方法。1. An adhesive made of vinyl acetate / vinyl chloride / vinyl acetate copolymer having maleic acid is applied to the surface of a bone-white polyvinyl chloride sheet substrate, and a polyester resin, a polyol-based acrylate, and a A method for producing an offset printing card, wherein offset printing is performed using an ultraviolet curable resin ink composed of a polymerization initiator and a coloring pigment, and a transparent vinyl chloride film is adhered to the surface thereof via the adhesive.