JP3073841U - Anti-reflective sheet - Google Patents

Anti-reflective sheet

Info

Publication number
JP3073841U
JP3073841U JP2000003863U JP2000003863U JP3073841U JP 3073841 U JP3073841 U JP 3073841U JP 2000003863 U JP2000003863 U JP 2000003863U JP 2000003863 U JP2000003863 U JP 2000003863U JP 3073841 U JP3073841 U JP 3073841U
Authority
JP
Japan
Prior art keywords
sheet
screen
reflection
antireflection
base sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2000003863U
Other languages
Japanese (ja)
Inventor
佳孝 入谷
豊樹 田中
Original Assignee
株式会社サンキョー
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社サンキョー filed Critical 株式会社サンキョー
Priority to JP2000003863U priority Critical patent/JP3073841U/en
Application granted granted Critical
Publication of JP3073841U publication Critical patent/JP3073841U/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

(57)【要約】 【課題】 液晶等の画面における光反射を効果的に防止
できると共に、画面の明るさをシートを貼り付ける前と
ほぼ同様の明るさに維持できる反射防止シートを提供す
る。 【解決手段】 基材シートとこの基材シートに積層され
た光反射防止層とを備え、ヘイズ度が5%〜40%の範
囲内でかつ全光線透過率が70%〜91.5%の範囲内
である。更に前記光反射防止層は、熱硬化性樹脂のバイ
ンダー成分にシリカ粒子成分が配合された配合物により
形成されていることが好ましい。また前記光反射防止層
の厚みは10〜20μmであることが好ましい。
(57) Abstract: An object of the present invention is to provide an antireflection sheet capable of effectively preventing light reflection on a screen such as a liquid crystal and maintaining the brightness of the screen at almost the same brightness as before the sheet is attached. SOLUTION: It has a base sheet and an antireflection layer laminated on the base sheet, and has a haze degree in a range of 5% to 40% and a total light transmittance of 70% to 91.5%. Within range. Further, it is preferable that the anti-reflection layer is formed of a mixture of a binder component of a thermosetting resin and a silica particle component. The thickness of the anti-reflection layer is preferably from 10 to 20 μm.

Description

【考案の詳細な説明】[Detailed description of the invention]

【0001】[0001]

【考案の属する技術分野】[Technical field to which the invention belongs]

本考案は、液晶画面等の表面に貼り付けて画面の反射を防止する反射防止シー トに関する。 The present invention relates to an antireflection sheet that is attached to a surface of a liquid crystal screen or the like to prevent reflection of the screen.

【0002】[0002]

【従来の技術】[Prior art]

従来から、液晶画面等の反射を防止するため、あるいは画面を保護するために 、液晶画面等の表面に貼り付ける画面用シートが種々開発されている。特に、液 晶画面等における光の反射は、画面のちらつきや画面への作業者の背景の写り込 み等を招き、画面上での作業が阻害されるため、可能な限り防止することが要求 される。 このような観点から、様々な加工を行った画面用シートにより、画面上におけ る光の反射を調節して上述の問題を解決しようとしている。 Conventionally, in order to prevent reflection of a liquid crystal screen or the like or to protect the screen, various screen sheets to be attached to the surface of a liquid crystal screen or the like have been developed. In particular, reflection of light on a liquid crystal screen, etc. causes flickering of the screen and reflection of the background of the worker on the screen, which hinders the work on the screen. Is done. From such a point of view, the screen sheet that has been subjected to various processes is intended to adjust the reflection of light on the screen to solve the above problem.

【0003】[0003]

【考案が解決しようとする課題】[Problems to be solved by the invention]

しかし、従来の画面用シートでは光反射を防止する効果が不十分な場合があり 、また、光反射の防止を効果的に行えても、シートを貼り付ける前よりも画面が 暗くなり、画面が見づらくなる場合があった。 本考案はかかる問題点に鑑みてなされたものであってその目的とするところは 、液晶等の画面における光反射を効果的に防止できると共に、画面の明るさをシ ートを貼り付ける前とほぼ同様の明るさに維持できる反射防止シートを提供する ことにある。 However, the effect of preventing light reflection may not be sufficient with a conventional screen sheet, and even if the effect of preventing light reflection can be effectively performed, the screen becomes darker than before the sheet is pasted, and the screen becomes darker. Sometimes it was hard to see. The present invention has been made in view of such a problem, and its purpose is to effectively prevent light reflection on a screen such as a liquid crystal display and to reduce the brightness of the screen before pasting a sheet. An object of the present invention is to provide an anti-reflection sheet capable of maintaining substantially the same brightness.

【0004】[0004]

【課題を解決するための手段】[Means for Solving the Problems]

上記目的に鑑み、本考案においては以下の手段を採用した。すなわち、本考案 にかかる反射防止シートは、基材シートとこの基材シート面に備えられた光反射 防止層とを備え、ヘイズ度(ヘーズ、以下同様)が5%〜40%の範囲内でかつ 全光線透過率が70%〜91.5%の範囲内であることを特徴とする。 この手段によれば、反射防止シートは光反射を効果的に防止し、かつ良好な光 透過性を具備するので、画面上でのちらつきや背景の写り込みが回避できるとと もに、シートを貼り付けた後でも、画面はシートを貼り付ける前の明るい状態の ままに維持される。 In view of the above object, the present invention employs the following solutions. That is, the antireflection sheet according to the present invention includes a base sheet and a light antireflection layer provided on the base sheet surface, and has a haze (haze, hereinafter the same) within a range of 5% to 40%. The total light transmittance is in the range of 70% to 91.5%. According to this means, the antireflection sheet effectively prevents light reflection and has good light transmittance, so that flicker on the screen and reflection of the background can be avoided, and the sheet can be prevented from being reflected. Even after pasting, the screen remains in the bright state before pasting the sheet.

【0005】 また前記光反射防止層は、熱硬化性樹脂のバインダー成分にシリカ粒子成分が 配合された配合物により形成されていることが好ましい。 この手段によれば、シリカ粒子により光を拡散させて、効果的に光反射防止を 行えるとともに適度な透過性を具備するとともに、熱硬化性樹脂が熱により硬化 してシートにある程度の硬度が付与される。 従って、光反射防止、透過性の機能を備えるとともに、画面の保護もできて好 ましい。更に、前記光反射防止層の厚みは10〜20μmであることがより好ま しい。It is preferable that the anti-reflection layer is formed of a mixture of a binder component of a thermosetting resin and a silica particle component. According to this means, the light is diffused by the silica particles to effectively prevent light reflection and has an appropriate transmittance, and the thermosetting resin is cured by heat to impart a certain degree of hardness to the sheet. Is done. Therefore, it is preferable to have the functions of preventing light reflection and transmitting light, and to protect the screen. Further, the thickness of the light reflection preventing layer is more preferably 10 to 20 μm.

【0006】[0006]

【考案の実施の形態】[Embodiment of the invention]

以下、本考案にかかる反射防止シートについて詳細に説明する。図1は、本考 案にかかる反射防止シートの一実施形態を示した断面図である。反射防止シート (以下、シートという)1は、PET製の基材シート2と、基材シート2の表面 に積層された光反射防止層3とを備え、基材シート2の裏面にはシリコーン系接 着剤により形成された接着層4が設けられている。シート1には、接着層4を介 してポリプロピレン製のセパレータ6が備えられている。 Hereinafter, the antireflection sheet according to the present invention will be described in detail. FIG. 1 is a sectional view showing an embodiment of the antireflection sheet according to the present invention. An antireflection sheet (hereinafter, referred to as a sheet) 1 includes a PET base sheet 2 and a light antireflection layer 3 laminated on the surface of the base sheet 2, and a silicone-based base sheet 2 is provided on the back surface of the base sheet 2. An adhesive layer 4 formed of an adhesive is provided. The sheet 1 is provided with a separator 6 made of polypropylene via an adhesive layer 4.

【0007】 シート1は、液晶等の画面に貼り付けられる状態(セパレータをはがした状態 )において、ヘイズ度が5%〜40%の範囲内かつ全光線透過率が70%〜91 .5%の範囲内である。かかるヘイズ度及び全光線透過率により、先述した光反 射防止効果と透過性とが実現される。 かかる光反射防止効果と透過性とを実現するためには、シート1がいわゆる艶 消し状態(マット加工状態)であることが好ましい。シート1は、光反射防止層 3によりかかる艶消し状態を実現している。The sheet 1 has a haze within a range of 5% to 40% and a total light transmittance of 70% to 91% in a state where the sheet 1 is attached to a screen such as a liquid crystal display (with a separator removed). It is within the range of 5%. With the haze degree and the total light transmittance, the above-described light reflection preventing effect and transmittance are realized. In order to achieve such light reflection preventing effect and transparency, it is preferable that the sheet 1 is in a so-called matte state (mat processing state). The sheet 1 realizes such a matte state by the anti-reflection layer 3.

【0008】 本実施形態における光反射防止層3は、熱硬化性樹脂のバインダー成分中にシ リカ粒子成分が配合された配合物により形成されている。シリカ粒子成分の、バ インダー成分に対する配合比率は、ヘイズ度と全光線透過率が、それぞれ先述の 範囲内になるように適宜に調整する。 光反射防止層3は、基材シート2表面に、バインダーとしての熱硬化性樹脂成 分にシリカ粒子成分が配合された配合物を塗布し、加熱してバインダーの樹脂を 硬化させて、シリカ粒子をこの樹脂中に閉じこめて形成される。The anti-reflection layer 3 according to the present embodiment is formed of a mixture of a binder component of a thermosetting resin and a silica particle component. The mixing ratio of the silica particle component to the binder component is appropriately adjusted so that the haze degree and the total light transmittance fall within the ranges described above. The antireflection layer 3 is formed by applying a mixture of a thermosetting resin component as a binder and a silica particle component to the surface of the base sheet 2 and heating the resin to cure the binder resin. Is formed in this resin.

【0009】 また各部の厚みは、基材シートが100μm、光反射防止層が20μm、接着 層が90μm、セパレータが50μとなっている。 基材シート2、光反射防止層3、接着層4の厚みは、上述のヘイズ度及び全光 線透過率に影響を及ぼす。かかる観点より、光反射防止層3の厚みは10〜20 μm、基材シートは100〜125μm、接着層は50〜90μm程度であるこ とが好ましい。またセパレータは、50〜75μm程度であれば取り扱いが容易 になり好ましい。The thickness of each part is 100 μm for the base sheet, 20 μm for the anti-reflection layer, 90 μm for the adhesive layer, and 50 μm for the separator. The thicknesses of the base sheet 2, the antireflection layer 3 and the adhesive layer 4 affect the haze and the total light transmittance described above. From this viewpoint, the thickness of the antireflection layer 3 is preferably about 10 to 20 μm, the thickness of the base sheet is about 100 to 125 μm, and the thickness of the adhesive layer is about 50 to 90 μm. Further, it is preferable that the separator is about 50 to 75 μm because the handling becomes easy.

【0010】 また本実施形態においては、光反射防止層3はシリカ粒子を配合して形成され ているが、このときシリカ粒子の大きさは、約2〜15μmが好適で、また熱硬 化性樹脂としてはアクリル系、ポリエステル系樹脂等が使用できる。 次に、本考案にかかるシートを二種類作製し(実施例1、実施例2)、ヘイズ 度及び全光線透過率を測定した。その後実際に液晶画面に貼り付けて、その光反 射防止効果及び透過性を評価した。基材シートにはPET(商品名ルミラー、東 レ製)を、光反射防止層にはシリカ粒子(熱硬化性樹脂中に分散されているもの 、商品名サイリシア、富士シリシア製)を、接着層にはシリコン樹脂を用いた。 結果を表1に示す。In this embodiment, the anti-reflection layer 3 is formed by mixing silica particles. At this time, the size of the silica particles is preferably about 2 to 15 μm, Acrylic resin, polyester resin or the like can be used as the resin. Next, two types of sheets according to the present invention were prepared (Examples 1 and 2), and the haze degree and the total light transmittance were measured. Then, the film was actually pasted on a liquid crystal screen, and its light reflection preventing effect and transmittance were evaluated. PET (trade name Lumirror, manufactured by Toray) for the base sheet, silica particles (dispersed in thermosetting resin, trade names Sylysia, Fuji Silysia) for the anti-reflection layer, adhesive layer Silicon resin was used for the sample. Table 1 shows the results.

【0011】[0011]

【表1】 [Table 1]

【0012】 これらのシートはいずれも、ヘイズ度及び全光線透過率が所定範囲内であり、 液晶画面上での光反射を効果的に防止でき、かつ画面の明るさはシートを貼り付 ける前とほぼ同程度に維持された(目視による)。 先述したように、光反射防止層の形成の際には加熱が必要なので、基材シート はこの際の高温に耐える材質で形成される必要がある。具体的には、軟化温度が 高い(200℃以上)樹脂、例えばPET以外のポリエステル系樹脂、ポリカー ボネイト系、ポリアミド系、セルロース系樹脂、フッ素樹脂等が挙げられる。[0012] Each of these sheets has a haze degree and a total light transmittance within a predetermined range, can effectively prevent light reflection on a liquid crystal screen, and has a brightness of a screen before sticking the sheet. It was maintained at about the same level (visually). As described above, since heating is required when forming the anti-reflection layer, the base sheet needs to be formed of a material that can withstand the high temperature at this time. Specific examples include resins having a high softening temperature (200 ° C. or higher), such as polyester resins other than PET, polycarbonate resins, polyamide resins, cellulose resins, and fluororesins.

【0013】 また光反射防止層3は、上述したシリカ粒子の配合以外の手段によっても形成 できる。例えば、基材シート表面を研磨する、あるいは基材シート表面を溶剤で 処理する等の手段により、基材シート表面に微細な凹凸を多数有する層を形成し て、これを光反射防止層としてもよい。シート1を艶消し状態に加工でき、シー ト1のヘイズ度及び全光線透過率が、先述の所定範囲内になるのであれば、適宜 の手段を採用できる。The anti-reflection layer 3 can also be formed by means other than the above-described silica particle mixing. For example, by forming a layer having a large number of fine irregularities on the surface of the base sheet by means such as polishing the surface of the base sheet or treating the surface of the base sheet with a solvent, this may be used as an antireflection layer. Good. As long as the sheet 1 can be processed into a matte state and the haze degree and the total light transmittance of the sheet 1 fall within the above-mentioned predetermined ranges, appropriate means can be adopted.

【0014】[0014]

【考案の効果】[Effect of the invention]

本考案にかかる反射防止シートによれば、所定範囲のヘイズ度と全光線透過率 を有するので、液晶等の画面上における光反射を効果的に防止でき、かつ画面の 明るさを前記シートを貼り付けない状態の画面とほぼ同等に維持できる。 According to the antireflection sheet of the present invention, since the antireflection sheet has a haze degree and a total light transmittance in a predetermined range, light reflection on a screen such as a liquid crystal can be effectively prevented, and the brightness of the screen is adhered to the sheet. It can be maintained almost the same as the screen without attachment.

【図面の簡単な説明】[Brief description of the drawings]

【図1】本考案にかかる反射防止シートの一実施形態を
示した断面図である。
FIG. 1 is a cross-sectional view showing an embodiment of an antireflection sheet according to the present invention.

【符号の説明】[Explanation of symbols]

1 反射防止シート 2 基材シート 3 光反射防止層 4 接着層 5 シート本体 6 セパレータ REFERENCE SIGNS LIST 1 anti-reflection sheet 2 base sheet 3 anti-reflection layer 4 adhesive layer 5 sheet body 6 separator

Claims (3)

【実用新案登録請求の範囲】[Utility model registration claims] 【請求項1】 基材シートとこの基材シート面に備えら
れた光反射防止層とを備え、ヘイズ度が5%〜40%の
範囲内でかつ全光線透過率が70%〜91.5%の範囲
内であることを特徴とする反射防止シート。
1. A base sheet and an antireflection layer provided on a surface of the base sheet, wherein the haze is in the range of 5% to 40% and the total light transmittance is 70% to 91.5. % In the range of%.
【請求項2】 前記光反射防止層は、熱硬化性樹脂のバ
インダー成分にシリカ粒子成分が配合された配合物によ
り形成されていることを特徴とする請求項1に記載の反
射防止シート。
2. The anti-reflection sheet according to claim 1, wherein the anti-reflection layer is formed of a blend of a binder component of a thermosetting resin and a silica particle component.
【請求項3】 前記光反射防止層の厚みは10〜20μ
mであることを特徴とする請求項1又は2に記載の反射
防止シート。
3. The thickness of the anti-reflection layer is 10 to 20 μm.
3. The antireflection sheet according to claim 1, wherein m is m.
JP2000003863U 2000-06-06 2000-06-06 Anti-reflective sheet Expired - Fee Related JP3073841U (en)