JP3011067B2 - Low permeable concrete structures for radioactive waste disposal sites - Google Patents
Low permeable concrete structures for radioactive waste disposal sitesInfo
- Publication number
- JP3011067B2 JP3011067B2 JP7225067A JP22506795A JP3011067B2 JP 3011067 B2 JP3011067 B2 JP 3011067B2 JP 7225067 A JP7225067 A JP 7225067A JP 22506795 A JP22506795 A JP 22506795A JP 3011067 B2 JP3011067 B2 JP 3011067B2
- Authority
- JP
- Japan
- Prior art keywords
- permeable concrete
- radioactive waste
- waste disposal
- permeable
- disposal site
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、放射性廃棄物処
分場用低透水コンクリート構造体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a low permeable concrete structure for a radioactive waste disposal site.
【０００２】[0002]
【従来の技術】放射性廃棄物の処分場として、岩盤中に
これを構築することが検討されている。図３，４にその
構造の一例を示している。同図に示す放射性廃棄物処分
場は、岩盤ａ中に、例えば、５０ｍ×３０ｍ程度の円筒
状空間をくり抜き形成し、この円筒状空間内に処分場を
構築する。処分場内には、複数の鉄筋コンクリート製の
コンテナ容器ｂが収容され、各コンテナ容器ｂ内には、
セメント固化された放射廃棄物ｃが密閉収納されてい
る。2. Description of the Related Art Construction of a radioactive waste disposal site in a bedrock has been studied. 3 and 4 show an example of the structure. In the radioactive waste disposal site shown in the figure, a cylindrical space of, for example, about 50 m × 30 m is formed in a bedrock a, and a disposal site is constructed in this cylindrical space. A plurality of reinforced concrete container containers b are accommodated in the disposal site, and in each container container b,
The radiation waste c solidified in cement is stored in a closed state.
【０００３】複数のコンテナ容器ｂは、円筒状空間内に
上下左右方向に所定の間隔を隔てて配置され、各コンテ
ナ容器ｂの外周を囲繞するようにして、透気性コンクリ
ート層ｄが設けられる。そして、この透気性コンクリー
ト層ｄの外周には、これをさらに囲繞する鉄筋コンクリ
ート製の外周シェル体ｅが形成される。ところが、この
ような鉄筋コンクリートを主体とした処分場の構造で
は、鉄筋コンクリートを貫通するひび割れの発生を回避
することが避けがたく、この種の処分場に要求されてい
る透水性が小さく、透気性が良好に保たれるという条件
を満足することができない。A plurality of container containers b are arranged at predetermined intervals in the vertical and horizontal directions in a cylindrical space, and an air-permeable concrete layer d is provided so as to surround the outer periphery of each container container b. An outer peripheral shell e made of reinforced concrete is further formed on the outer periphery of the permeable concrete layer d to further surround it. However, in the structure of such a repository mainly composed of reinforced concrete, it is unavoidable to avoid the occurrence of cracks that penetrate reinforced concrete. It is not possible to satisfy the condition of keeping good.
【０００４】そこで、同図に示す処分場では、外周シェ
ル体ｅの外周にベントナイトを締め固めた人工バリアｆ
を設けることが検討されており、このような人工バリア
ｆを設けると、ベントナイトが水分を吸収して膨潤する
ので、透水性を低くすることができる。しかしながら、
このような構造の廃棄物処分場には、以下に説明する課
題があった。Therefore, in the disposal site shown in FIG. 1, an artificial barrier f in which bentonite is compacted around the outer periphery of the outer shell body e.
The provision of such an artificial barrier f causes the bentonite to absorb water and swell, so that the water permeability can be reduced. However,
The waste disposal site having such a structure has the following problems.
【０００５】[0005]
【発明が解決しようとする課題】すなわち、人工バリア
ｆとしてのベントナイト層は、カルシウムないしはナト
リウムベントナイトを原位置で高密度に締め固める方法
が、最も経済的であると判断されているが、それでもな
お原材料が非常に高価であり、経済的な不利益が非常に
大きい。The bentonite layer as the artificial barrier f is determined to be most economical by compacting calcium or sodium bentonite in situ and at a high density. The raw materials are very expensive and the economic disadvantage is very great.
【０００６】また、施工性や品質管理の都合などから、
例えば、事前に締め固めたベントナイトを使用すると、
さらに工費が増加するという問題もある。本発明は、こ
のような従来の問題点に鑑みて案出されたものであり、
その目的は、経済的な放射性廃棄物処分場用の低透水コ
ンクリート構造体を提供することにある。Also, from the viewpoint of workability and quality control,
For example, if you use pre-compacted bentonite,
There is another problem that the construction cost increases. The present invention has been devised in view of such conventional problems,
The purpose is to provide a low-permeability concrete structure for an economical radioactive waste repository.
【０００７】[0007]
【課題を解決するための手段】上記目的を達成するため
に、本発明は、岩盤中に構築され、放射性廃棄物を収納
する鉄筋コンクリート製のコンテナ容器と、所定の間隔
をおいて設置される複数の前記コンテナ容器のそれぞれ
の外周を囲繞するようにして形成される透気性コンクリ
ート層と、この透気性コンクリート層の外周を囲繞する
ようにして形成される外周シェル体とを備えた放射性廃
棄物処分場において、前記外周シェル体は、複数の透気
性コンクリート層と、この透気性コンクリート層間に挟
持された低透水性かつ高透気性の繊維層とで構成した。
この構成の低透水性コンクリート構造体によれば、外周
シェル体が複数の透気性コンクリート層と、この透気性
コンクリート層間に挟持された低透水性かつ高透気性の
繊維層とで構成されているので、低透水性と高透気性と
が確保される。繊維層は、化学的，熱的に安定で、長期
耐候性に優れた、ポリテトラフルオロエチレン（ＰＴＦ
Ｅ）などの微細な連続多孔質構造のものであって、人工
バリアに要求されている透水係数は、１０-9〜１０-10
ｃｍ／ｓｅｃ以下で、透気係数が１０-7 ｃｍ／ｓｅｃ
程度以上なので、例えば、ゴアテックス（ジャパンゴア
テックス製：商品名）を採用すると、十分に要求性能を
満足することができる。また、上記放射性廃物処分場に
おいては、前記外周シェル体を、コンクリート層と、こ
のコンクリート層の外表面に付設された低透水性かつ高
透気性の繊維層とで構成することができる。In order to achieve the above object, the present invention provides a reinforced concrete container container which is constructed in a bedrock and stores radioactive waste, and is provided with a plurality of containers arranged at predetermined intervals. Radioactive waste disposal comprising a permeable concrete layer formed so as to surround the outer periphery of each of the container containers described above, and an outer peripheral shell formed so as to surround the outer periphery of the permeable concrete layer In the field, the outer peripheral shell was composed of a plurality of air-permeable concrete layers and a low water-permeable and high air-permeable fiber layer sandwiched between the air-permeable concrete layers.
According to the low-water-permeable concrete structure of this configuration, the outer shell is composed of a plurality of air-permeable concrete layers and a low-water-permeability and high-air-permeability fiber layer sandwiched between the air-permeable concrete layers. Therefore, low water permeability and high air permeability are ensured. The fiber layer is made of polytetrafluoroethylene (PTF) which is chemically and thermally stable and has excellent long-term weather resistance.
E) and the like, and have a fine continuous porous structure, and the permeability required for the artificial barrier is 10 −9 to 10 −10
cm / sec or less and air permeability coefficient of 10 -7 cm / sec
Therefore, for example, if Gore-Tex (trade name, manufactured by Japan Gore-Tex) is adopted, the required performance can be sufficiently satisfied. Further, in the radioactive waste disposal site, the outer peripheral shell body can be constituted by a concrete layer and a fiber layer having low water permeability and high air permeability attached to an outer surface of the concrete layer.
【０００８】[0008]
【発明の実施の形態】以下、本発明の実施の形態につい
て、添付図面に基づいて詳細に説明する。図１は、本発
明にかかる廃棄物処分場用低透水コンクリート構造体１
０の一実施例を示している。同図に示すコンクリート構
造体１０は、図３，４に示した岩盤ａ中に構築される放
射性廃棄物処分場に適用されるものであって、処分場
は、岩盤ａ中に、例えば、５０ｍ×３０ｍ程度の円筒状
空間をくり抜き形成し、この円筒状空間内に処分場を構
築する。処分場内には、複数の鉄筋コンクリート製のコ
ンテナ容器ｂが収容され、各コンテナ容器ｂ内には、セ
メント固化された放射廃棄物ｃが密閉収納されている。Embodiments of the present invention will be described below in detail with reference to the accompanying drawings. FIG. 1 shows a low-permeable concrete structure 1 for a waste disposal site according to the present invention.
0 shows one embodiment. The concrete structure 10 shown in the figure is applied to a radioactive waste disposal site constructed in the bedrock a shown in FIGS. 3 and 4, and the disposal site is, for example, 50 m in the bedrock a. A cylindrical space of about 30 m is hollowed out, and a disposal site is constructed in this cylindrical space. A plurality of reinforced concrete container containers b are accommodated in the disposal site, and radiant waste c solidified in cement is accommodated in each container container b in a closed manner.
【０００９】複数のコンテナ容器ｂは、円筒状空間内に
上下左右方向に所定の間隔を隔てて配置され、各コンテ
ナ容器ｂの外周を囲繞するようにして、透気性コンクリ
ート層ｄが設けられる。そして、この透気性コンクリー
ト層ｄの外周には、これをさらに囲繞する鉄筋コンクリ
ート製の外周シェル体ｅが形成され、処分場としての基
本的な構成は、従来のこの種のものと同じである。A plurality of container containers b are arranged at predetermined intervals in the vertical and horizontal directions in a cylindrical space, and an air-permeable concrete layer d is provided so as to surround the outer periphery of each container container b. An outer peripheral shell e made of reinforced concrete is further formed on the outer periphery of the permeable concrete layer d to further surround the permeable concrete layer d, and the basic configuration as a disposal site is the same as that of this type of the related art.
【００１０】ところが、鉄筋コンクリートを主体とした
処分場の構造では、鉄筋コンクリートを貫通するひび割
れの発生を回避することが避けがたく、この種の処分場
に要求されている透水性が小さく、透気性が良好に保た
れるという条件を満足することができないので、従来
は、外周シェル体ｅの外周にベントナイト製の人工バリ
アｆを設けていたが、本実施例では、この外周シェル体
ｅとベントナイト製の人工バリアｆに代えて、低透水コ
ンクリート構造体１０を採用した。However, in the structure of a disposal site mainly composed of reinforced concrete, it is unavoidable to avoid the occurrence of cracks penetrating the reinforced concrete. Conventionally, an artificial barrier f made of bentonite is provided on the outer periphery of the outer shell body e because the condition of being kept satisfactorily cannot be satisfied. In place of the artificial barrier f, a low water permeable concrete structure 10 was employed.
【００１１】図１に示した低透水コンクリート構造体１
０は、所定厚みの３層からなる透気性コンクリート層１
０ａ，１０ｂ，１０ｃと、これらの透気性コンクリート
層１０ａ，１０ｂ，１０ｃに挟持された低透水性かつ高
透気性の繊維層１０ｄ，１０ｅとから構成されている。
繊維層１０ｄ，１０ｅは、非常に薄い膜状のものであっ
て、化学的，熱的に安定で、長期耐候性に優れた、ポリ
テトラフルオロエチレン（ＰＴＦＥ）などの微細な連続
多孔質構造のものであって、人工バリアに要求されてい
る透水係数は、１０-9〜１０-10 ｃｍ／ｓｅｃ以下で、
透気係数が１０-7 ｃｍ／ｓｅｃ程度以上なので、例え
ば、ゴアテックス（ジャパンゴアテックス製：商品名）
を採用すると、十分に要求性能を満足することができ
る。[0011] The low permeable concrete structure 1 shown in FIG.
0 is an air-permeable concrete layer 1 consisting of three layers of a predetermined thickness
0a, 10b, and 10c, and fiber layers 10d and 10e having low water permeability and high air permeability sandwiched between the air permeable concrete layers 10a, 10b, and 10c.
The fiber layers 10d and 10e are very thin films and have a fine continuous porous structure such as polytetrafluoroethylene (PTFE), which is chemically and thermally stable and has excellent long-term weather resistance. And the permeability required for the engineered barrier is 10 −9 to 10 −10 cm / sec or less,
Since the air permeability is about 10 −7 cm / sec or more, for example, Gore-Tex (trade name, manufactured by Japan Gore-Tex)
By adopting, the required performance can be sufficiently satisfied.
【００１２】このような低透水性コンクリート構造体１
０は、プレキャスト版として、予め形成してもよいし、
現場打ちで形成してもよい。このように構成の低透水性
コンクリート構造体１０を外周シェル体として採用する
と、内部のガスなどの気体は、透気性コンクリート層１
０ａ，１０ｂ，１０ｃおよび繊維層１０ｄ，１０ｅを通
過して、外部に放出されるとともに、外部から侵入する
水分は、繊維層１０ｄ，１０ｅにより阻止されて、構造
体１０の内部まで到達することができない。Such a low water permeable concrete structure 1
0 may be formed in advance as a precast plate,
It may be formed by casting in place. When the low water permeable concrete structure 10 having such a configuration is employed as the outer peripheral shell, the gas such as the gas inside the permeable concrete layer 1 is removed.
0a, 10b, 10c and the fiber layers 10d, 10e, the water is released to the outside, and the moisture that enters from the outside is blocked by the fiber layers 10d, 10e and reaches the inside of the structure 10. Can not.
【００１３】この場合、特に、低透水性かつ高透気性の
繊維層１０ｄ，１０ｅが非常に薄い膜状のもので構成さ
れるので、人工バリアの厚みを従来のものよりも大幅に
薄くすることができ、例えば、ゴアテックス（ジャパン
ゴアテックス製：商品名）は、既に市販されていて、そ
の価格もベントナイトと比べて低価格なので、経済的に
人工バリアを形成することができる。In this case, in particular, since the fiber layers 10d and 10e having low water permeability and high air permeability are formed of a very thin film, the thickness of the artificial barrier should be made much smaller than the conventional one. For example, Gore-Tex (trade name, manufactured by Japan Gore-Tex) is already commercially available and its price is lower than that of bentonite, so that an artificial barrier can be formed economically.
【００１４】なお、上記実施例では、低透水コンクリー
ト構造体１０を３層の透水コンクリート層１０ａ，１０
ｂ，１０ｃと、２層の繊維層１０ｄ，１０ｅとで構成し
た５層構造のものを例示したが、これが２層のコンクリ
ート層と１層の繊維層であってもよい。図２は、本発明
にかかる放射性廃棄物処分場用低透水コンクリート構造
体の他の実施例を示している。同図に示すコンクリート
構造体１０’は、図３，４に示した廃棄物処分場のシェ
ル体ｅの部分に採用され、所定厚みのコンクリート層１
０１と、このコンクリート層１０１の外表面に付設され
た低透水性かつ高透気性の繊維層１０２とから構成され
ている。In the above embodiment, the low permeable concrete structure 10 is divided into three permeable concrete layers 10a and 10a.
Although a five-layer structure composed of b and 10c and two fiber layers 10d and 10e has been illustrated, this may be a two-layer concrete layer and a single fiber layer. FIG. 2 shows another embodiment of the low-permeable concrete structure for a radioactive waste disposal site according to the present invention. The concrete structure 10 'shown in the figure is used for the shell body e of the waste disposal site shown in FIGS.
01 and a fiber layer 102 having low water permeability and high air permeability provided on the outer surface of the concrete layer 101.
【００１５】コンクリート層１０１は、透気性コンクリ
ートであってもよいし、通常のコンクリートであっても
よい。また、繊維層１０２は、上記実施例と同様なもの
が採用され、コンクリート層１０１の外表面の全部を覆
うようにして、例えば、接着剤などで固定される。この
ように構成されたコンクリート構造体１０’を放射性廃
棄物処分場の外周に設けられるシェル体として採用する
と、上記実施例と同等の作用効果が得られる。The concrete layer 101 may be air-permeable concrete or ordinary concrete. Further, the fiber layer 102 is the same as that in the above embodiment, and is fixed with, for example, an adhesive so as to cover the entire outer surface of the concrete layer 101. When the concrete structure 10 'configured as described above is adopted as a shell provided on the outer periphery of the radioactive waste disposal site, the same operation and effect as in the above embodiment can be obtained.
【００１６】[0016]
【発明の効果】以上、実施例で詳細に説明したように、
本発明にかかる放射性廃棄物処分場用低透水コンクリー
ト構造体によれば、要求性能を満足する人工バリアを経
済的に構築することができる。As described above in detail in the embodiments,
According to the low-permeable concrete structure for a radioactive waste disposal site according to the present invention, an artificial barrier satisfying required performance can be economically constructed.
【図１】本発明にかかる放射性廃棄物処分場用低透水コ
ンクリート構造体の一実施例を示す要部断面図である。FIG. 1 is a cross-sectional view of an essential part showing one embodiment of a low-permeable concrete structure for a radioactive waste disposal site according to the present invention.
【図２】本発明にかかる放射性廃棄物処分場用低透水コ
ンクリート構造体の他の実施例を示す要部断面図であ
る。FIG. 2 is a sectional view of a main part showing another embodiment of the low-permeable concrete structure for a radioactive waste disposal site according to the present invention.
【図３】従来の放射性廃棄物処分場の一例を示す説明図
である。FIG. 3 is an explanatory view showing an example of a conventional radioactive waste disposal site.
【図４】図３のＡ部拡大図である。FIG. 4 is an enlarged view of a portion A in FIG. 3;
１０ 低透水コンクリート構造体 １０ａ，１０ｂ，１０ｃ 透気コンクリート層 １０ｄ，１０ｅ 繊維層 10 Low permeable concrete structure 10a, 10b, 10c Air permeable concrete layer 10d, 10e Fiber layer
Claims (2)
する鉄筋コンクリート製のコンテナ容器と、所定の間隔
をおいて設置される複数の前記コンテナ容器のそれぞれ
の外周を囲繞するようにして形成される透気性コンクリ
ート層と、この透気性コンクリート層の外周を囲繞する
ようにして形成される外周シェル体とを備えた放射性廃
棄物処分場において、 前記外周シェル体は、複数の透気性コンクリート層と、
この透気性コンクリート層間に挟持された低透水性かつ
高透気性の繊維層とからなることを特徴とする放射性廃
棄物処分場用低透水コンクリート構造体。1. A container made of reinforced concrete, which is constructed in a bedrock and stores radioactive waste, and is formed so as to surround an outer periphery of each of a plurality of container containers installed at a predetermined interval. A radioactive waste disposal site comprising an air permeable concrete layer and an outer shell formed so as to surround the outer periphery of the air permeable concrete layer, wherein the outer shell includes a plurality of air permeable concrete layers, ,
A low permeable concrete structure for a radioactive waste disposal site, comprising a low permeable and high permeable fiber layer sandwiched between the permeable concrete layers.
する鉄筋コンクリート製のコンテナ容器と、所定の間隔
をおいて設置される複数の前記コンテナ容器のそれぞれ
の外周を囲繞するようにして形成される透気性コンクリ
ート層と、この透気性コンクリート層の外周を囲繞する
ようにして形成される外周シェル体とを備えた廃棄物処
分場において、 前記外周シェル体は、コンクリート層と、このコンクリ
ート層の外表面に付設された低透水性かつ高透気性の繊
維層とからなることを特徴とする放射性廃棄物処分場用
低透水コンクリート構造体。2. A reinforced concrete container container which is constructed in a bedrock and stores radioactive waste, and is formed so as to surround an outer periphery of each of the plurality of container containers installed at a predetermined interval. In a waste disposal site comprising a permeable concrete layer and an outer shell formed so as to surround the outer periphery of the permeable concrete layer, the outer shell includes a concrete layer and a concrete layer. A low water permeable concrete structure for a radioactive waste disposal site, comprising a low water permeable and high air permeable fiber layer attached to an outer surface.