JP2950700B2 - Fabric-like composite material and its manufacturing method - Google Patents
Fabric-like composite material and its manufacturing methodInfo
- Publication number
- JP2950700B2 JP2950700B2 JP5025589A JP2558993A JP2950700B2 JP 2950700 B2 JP2950700 B2 JP 2950700B2 JP 5025589 A JP5025589 A JP 5025589A JP 2558993 A JP2558993 A JP 2558993A JP 2950700 B2 JP2950700 B2 JP 2950700B2
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- shape memory
- fabric
- alloy
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】この発明は、布状複合素材とその
製造方法に関するものである。さらに詳しくは、この発
明は、形状記憶合金の機械的特性を活かしつつ、滑らか
で自然な素材感を有し、美観と意匠性を向上させること
のできる、新しい形状記憶合金を用いた布状複合素材と
その製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cloth-like composite material and a method for producing the same. More specifically, the present invention provides a cloth-like composite using a new shape memory alloy, which has a smooth and natural feel of a material while improving the appearance and design while utilizing the mechanical properties of the shape memory alloy. The present invention relates to a material and a manufacturing method thereof.
【０００２】[0002]
【従来の技術】従来より、衣料品、寝具、カーテン等に
用いられる布地については、天然繊維または合成繊維か
らなる布や不繊布の各種のものが提供されてきており、
製品の種類や意匠などに応じて適宜なものが選択され使
用されている。一方、衣料品の一つとして、着用者の体
型を補整する整体用の下着が知られており、ブラジャ
ー、ガードル、ボディスーツ、ボディシャイパー、ウェ
ストニッパー等が広く用いられている。2. Description of the Related Art Conventionally, various types of cloths and non-woven cloths made of natural fibers or synthetic fibers have been provided for clothing, bedding, curtains and the like.
Appropriate products are selected and used according to the type of product, design, and the like. On the other hand, as one of the clothing items, underwear for manipulative treatment for adjusting a wearer's body shape is known, and brassiere, girdle, body suit, body shiper, waist nippers and the like are widely used.
【０００３】最近、これらの整体用下着については、布
のたるみを防止し、整体機能を向上させるために、補強
部材としてのボーンなどに各種の形状記憶合金を使用す
ることが提案されている。たとえばＮｉＴｉ系形状記憶
合金線を単独または他の金属線と組み合わせて紐状、編
物、織物などに成形し、所望の形状に形状記憶熱処理を
施した後に、これを下着に縫い付ける。この下着を着用
すると、着用温度でオーステナイト相が発現する。オー
ステナイト相は超弾性状態にあり、鋼などの他の金属に
比べると低弾性率を有し、しかも弾性を保つ変形の範囲
が広く、しなやかであるという特性がある。この機械的
特性によって、整体用下着の保形性が確保されるのであ
る。[0003] Recently, it has been proposed to use various shape memory alloys for a bone as a reinforcing member in order to prevent the cloth from sagging and improve the function of the underwear for manipulative treatment. For example, a NiTi-based shape memory alloy wire alone or in combination with another metal wire is formed into a string, knit, woven fabric, etc., subjected to shape memory heat treatment into a desired shape, and then sewn to underwear. When this underwear is worn, an austenitic phase develops at the wearing temperature. The austenitic phase is in a super-elastic state, has a lower elastic modulus than other metals such as steel, and has a characteristic that the range of deformation maintaining elasticity is wide and flexible. The mechanical properties ensure the shape retention of the manipulative underwear.
【０００４】このような形状記憶合金の衣料品への応用
は、上記の下着の他、上着などにも広げられつつある。[0004] The application of such a shape memory alloy to clothing is being expanded to outerwear in addition to the underwear described above.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、形状記
憶合金については、上記の優れた機械的特性を有するも
のの、その表面には酸化物が形成しているため黒色を呈
しており、また、その酸化物を取り除いても金属色であ
るため、白色やピンク、肌色などの多い下着や淡い色の
上着に使用すると、形状記憶合金の色が透けて見え、違
和感が生じ、美観が損なわれるという問題があった。こ
のため、使用に際しては、白色のナイロン樹脂等をコー
ティングなどしなければならないという制約がある。However, although the shape memory alloy has the above-mentioned excellent mechanical properties, it has a black color due to the formation of an oxide on the surface thereof. Even if the object is removed, it is still a metal color, so when used for underwear or light-colored outerwear with many whites, pinks, and skin colors, the color of the shape memory alloy can be seen through, causing a sense of incongruity and impairing the appearance. was there. For this reason, when used, there is a restriction that white nylon resin or the like must be coated.
【０００６】また、従来では、形状記憶合金線を用いた
編物または織物は、衣料品等に単に直接縫い付けられて
使用されるのみであり、布との間で相互に動き、摩擦に
より布が摩耗したり損傷するなどの問題もあった。この
ように、形状記憶合金と布とのマッチングは悪かった。
さらには、形状記憶合金線を用いた編物または織物が、
たとえば人体に直接接触する場合には、金属特有の違和
感があり、着心地の悪いものとなっていた。[0006] Conventionally, a knitted or woven fabric using a shape memory alloy wire is merely used by being directly sewn to clothing or the like. There were also problems such as wear and damage. Thus, the matching between the shape memory alloy and the cloth was poor.
Furthermore, a knitted or woven fabric using a shape memory alloy wire,
For example, in the case of direct contact with the human body, there is a sense of discomfort peculiar to metal, and it is uncomfortable to wear.
【０００７】このように、形状記憶合金の衣料品等への
応用には解決しなければならない課題が少なくないのが
実情であった。この発明は、以上の通りの事情に鑑みて
なされたものであり、従来の形状記憶合金線を用いた衣
料品等における欠点を解消し、形状記憶合金の機械的特
性を活かしつつ、滑らかで自然な素材感を有し、美観と
意匠性を向上させることのできる布状複合素材とその製
造方法を提供することを目的としている。As described above, there are many problems to be solved in applying the shape memory alloy to clothing and the like. The present invention has been made in view of the above circumstances, and solves the drawbacks of clothing and the like using a conventional shape memory alloy wire, while making the most of the mechanical properties of the shape memory alloy while maintaining a smooth and natural appearance. It is an object of the present invention to provide a cloth-like composite material having a natural material feeling and capable of improving the appearance and design, and a method for producing the same.
【０００８】[0008]
【課題を解決するための手段】この発明は、上記の課題
を解決するものとして、ＮｉＴｉ系、Ｔｉ系、銅系また
は鉄系の形状記憶合金の細いワイヤーが単独で、または
ステンレス鋼、チタン、チタン合金、アルミニウム、ア
ルミニウム合金あるいはアモルファス合金の１種以上の
細いワイヤーと組み合わされて、編まれまたは織られ、
所望の形状に形状記憶熱処理された布状体の片面または
両面に、布が、２液反応型シアノアクリレート系の液状
接着剤を介して接着一体化されたことを特徴とする布状
複合素材を提供する。SUMMARY OF THE INVENTION The present invention, as to solve the foregoing problems, NiTi-based, Ti-based, thin wire by itself a copper-based or iron-based shape memory alloy, or stainless steel, titanium, titanium alloy, aluminum, is combined with one or more thin wires of aluminum alloy or amorphous alloy, knitted rare or be woven,
On one or both sides of the shape memory heat-treated cloth-like material into a desired shape, fabric, two-liquid reaction type cyanoacrylate liquid
Providing cloth-like composite material is characterized in that the integrally bonded via an adhesive.
【０００９】またこの発明は、ＮｉＴｉ系、Ｔｉ系、銅
系または鉄系の形状記憶合金の細いワイヤーを単独で、
またはステンレス鋼、チタン、チタン合金、アルミニウ
ム、アルミニウム合金あるいはアモルファス合金の１種
以上の細いワイヤーと組み合わせて、編みまたは織った
後に、所望の形状に形状記憶熱処理して布状体を作製
し、次いでこの布状体の片面または両面に布を２液反応
型シアノアクリレート系の液状接着剤で接着一体化する
ことを特徴とする布状複合素材の製造方法を提供するも
のでもある。[0009] The present invention also provides a thin wire made of a NiTi-based, Ti-based, copper-based or iron-based shape memory alloy alone,
Or, in combination with one or more thin wires of stainless steel, titanium, titanium alloy, aluminum, aluminum alloy or amorphous alloy , knitting or weaving, and then performing shape memory heat treatment to a desired shape to produce a cloth-like body, Two-pack reaction of cloth on one or both sides of this cloth
Another object of the present invention is to provide a method for producing a cloth-like composite material, which comprises bonding and integrating with a liquid cyanoacrylate adhesive.
【００１０】この発明においては、たとえば図１に示し
たように、ＮｉＴｉ系、Ｔｉ系、銅系または鉄系の形状
記憶合金の細いワイヤーを単独で、またはステンレス
鋼、チタン、チタン合金、アルミニウム、アルミニウム
合金あるいはアモルファス合金の１種以上の細いワイヤ
ーと組み合わせて編みまたは織った後に、使用する製品
等の形状に対応させて形状記憶熱処理した編物または織
物（１）を作製する。形状記憶合金線および他の金属線
の径の大きさ、その編み方や織り方、さらに編み目また
は織り目の粗さ等については任意とすることができる。
この形状記憶合金線を用いた編物または織物（１）の片
面または両面に布（２）を接着により一体化する。布
（２）の材質についても特に制限はなく、天然繊維や合
成繊維、または不繊布を適宜に選択して使用することが
できる。天然繊維としてはたとえば植物繊維である綿や
麻、また、動物繊維としての絹、羊毛等が例示される。
一方、合成繊維としては、たとえばナイロン、ポリエス
テル、アクリル、ポリウレタン、レーヨン、アセテート
等とすることができる。In the present invention, for example, as shown in FIG. 1, a thin wire made of a NiTi-based, Ti-based, copper-based or iron-based shape memory alloy is used alone, or stainless steel, titanium, a titanium alloy, aluminum, After knitting or weaving in combination with one or more thin wires of an aluminum alloy or an amorphous alloy, a knit or woven fabric (1) subjected to shape memory heat treatment corresponding to the shape of a product to be used is produced. The size of the diameter of the shape memory alloy wire and the other metal wire, the method of knitting and weaving, and the roughness of the stitch or weave can be arbitrarily determined.
A cloth (2) is integrated with one side or both sides of a knitted or woven fabric (1) using the shape memory alloy wire by bonding. There is also no particular limitation on the material of the cloth (2), and natural fibers, synthetic fibers, or non-woven cloths can be appropriately selected and used. Examples of the natural fiber include cotton and hemp, which are vegetable fibers, and silk and wool, which are animal fibers.
On the other hand, as synthetic fibers, for example, nylon, polyester, acrylic, polyurethane, rayon, acetate and the like can be used.
【００１１】形状記憶合金を用いた編物または織物
（１）と布（２）との接着一体化に当たっては、２液反
応型シアノアクリレート系の液状接着剤を使用する。こ
の２液反応型シアノアクリレート系の液状接着剤を布
（２）の接着面に塗布または吹き付け、形状記憶合金線
による編物または織物（１）をその接着面に押さえつけ
る。上記液状接着剤は、形状記憶合金線による編物また
は織物（１）と布（２）の間に染み込み、常温で硬化
し、形状記憶合金線による編物または織物（１）と布
（２）とが接着一体化される。２液反応型シアノアクリ
レート系の液状接着剤は、熱可塑性樹脂接着剤に比べ、
接着させるための加熱工程が不要であり、接着作業が簡
便となる。 In bonding and integrating a knitted or woven fabric (1) and a cloth (2) using a shape memory alloy , a two-liquid
A liquid cyanoacrylate adhesive is used. This
Cloth with two-component reactive cyanoacrylate adhesive
Applying or spraying on the bonding surface of (2), shape memory alloy wire
The knitted or woven fabric (1) by the adhesive surface
You. The liquid adhesive is knitted with a shape memory alloy wire or
Penetrates between fabric (1) and fabric (2) and cures at room temperature
Knitted or woven fabric (1) and cloth with shape memory alloy wire
(2) is bonded and integrated. Two-component reaction type cyanoacryl
Rate-based liquid adhesives, compared to thermoplastic resin adhesives,
A heating step for bonding is not required, making bonding work simple.
It becomes a stool.
【００１２】[0012]
【作 用】[Operation]
この発明の布状複合素材とその製造方法におThe cloth-like composite material of the present invention and the method of manufacturing the same
いては、形状記憶合金線による編物または織物の片面まOf the knitted or woven fabric with the shape memory alloy wire
たは両面に布を２液反応型シアノアクリレート系の液状Or a cloth on both sides Two-liquid reaction type cyanoacrylate liquid
接着剤で接着一体化するため、形状記憶合金線による編Knitting with shape memory alloy wire to bond and integrate with adhesive
物または織物と布とが一体となった布状の複合素材が提A cloth-like composite material that integrates
供される。この複合素材は、形状記憶合金の機械的特性Provided. This composite material has the mechanical properties of a shape memory alloy.
を有しつつ、布との色や人体への違和感のない新しい布A new cloth that does not disturb the color and the human body
状素材である。任意の色の布との組合せが可能であり、Material. Combination with cloth of any color is possible,
白色をはじめとする様々な色の布状素材を作製することProducing fabrics of various colors including white
ができ、美観とともに意匠性が向上する。この布状素材And the design is improved as well as the appearance. This cloth-like material
は、衣料品ばかりでなく、運動靴、帽子、絨毯、カーテIs not only clothing, but also sports shoes, hats, carpets, cartes
ン、シーツ等の寝具などのパーツ（部品）として広く応Widely used as parts (parts) such as beddings and sheets
用可能である。Is available.
【００１３】また、この発明の布状複合素材では、形状
記憶合金線を用いた編物または織物と布が相互に移動す
ることはなく、摩擦が防止され、布は保護される。しか
も、布の存在により衣料品等へ縫付けが容易ともなる。 Further, in the cloth-like composite material of the present invention, the shape
Knit or woven fabric using memory alloy wire and fabric move with each other
No friction, friction is prevented and the fabric is protected. Only
In addition, sewing can be easily performed on clothing and the like due to the presence of the cloth.
【００１４】以下実施例を示し、この発明の布状複合素
材とその製造方法についてさらに詳しく説明する。 実施例１ ＮｉＴｉ系、Ｔｉ系、銅系または鉄系の形状記憶合金に
よる直径５０〜140 μｍの細いワイヤーで編物と織物を
作製した。編み目または折り目の粗さは１０〜６０ゲー
ジとした。この編物および織物を、ブラジャー、ガード
ル、ボディスーツ、ボディシェイパーおよびウエストニ
ッパーの一部の形状に形状記憶熱処理した。この後に、
布と接着一体化し、布状の複合素材を作製した。次い
で、複合素材を、使用するパーツ（部品）に切り抜き、
上記の下着に使用した。 Examples will be shown below, and the cloth-like composite element of the present invention will be described.
The material and its manufacturing method will be described in more detail. Example 1 NiTi-based, Ti-based, copper-based or iron-based shape memory alloy
Knitted and woven fabrics with a thin wire with a diameter of 50 to 140 μm
Produced. Knit or fold roughness 10-60 games
And This knit and woven fabric, bra, guard
, Body suits, body shapers and waist knees
Shape memory heat treatment was applied to a part of the shape of the upper. After this,
It was bonded and integrated with the fabric to produce a fabric-like composite material. Next
Then, cut out the composite material into parts to be used,
Used for the above underwear.
【００１５】このようにして作製した下着を種々の体型
の３０人の女性に着用してもらい、その着心地について
モニター試験を行った。被験者の着用前後および従来の
下着との比較試験の結果、この発明による下着は、身体
への圧迫感が少なく、着心地が良好であることが確認さ
れた。また、身体の線がきれいになるという効果も認め
られた。 実施例２ 実施例１と同様の形状記憶合金の細いワイヤーと、ステ
ンレス鋼、チタン、チタン合金、アルミニウム、アルミ
ニウム合金またはアモルファス合金の１種以上の細いワ
イヤーとから編物と織物を作製し、形状記憶熱処理を行
った後に、布と接着一体化した。この素材を切り抜き、
実施例１と同様の下着を作製した。モニター試験の結
果、身体への圧迫感が少なく、着心地が良好であること
が確認された。また、身体の線がきれいになるという効
果も認められた。 実施例３ 実施例１と同様の形状記憶合金の細いワイヤーを用いて
編物および織物を作製し、運動靴および帽子の一部の形
状に形状記憶熱処理した。そして、布と接着一体化し、
運動靴と帽子を作製した。布状複合素材の運動靴および
帽子への使用は容易であった。また、モニター試験の結
果、型崩れが発生せず、着用感が良好であることも確認
された。 [0015] The underwear produced in this manner is variously shaped.
About 30 women to wear and their comfort
A monitor test was performed. Before and after subject wear
As a result of comparative tests with underwear, the underwear according to the present invention
It is confirmed that there is little feeling of pressure on
Was. In addition, the effect that the body line becomes clean is also recognized
Was done. Example 2 A thin wire of the same shape memory alloy as in Example 1 was used.
Stainless steel, titanium, titanium alloy, aluminum, aluminum
One or more fine alloys of an aluminum alloy or an amorphous alloy
Knitted and woven fabrics are made from the ears and subjected to shape memory heat treatment.
After that, it was bonded and integrated with the cloth. Cut out this material,
Underwear similar to that of Example 1 was produced. Monitor test results
As a result, there is little feeling of pressure on the body and good comfort
Was confirmed. In addition, the effect that the line of the body becomes clean
Fruit was also observed. Example 3 The same shape memory alloy thin wire as in Example 1 was used.
Manufactures knitted and woven fabrics and forms part of athletic shoes and hats
Shape heat treatment. Then, it is bonded and integrated with the cloth,
Athletic shoes and hats were made. Athletic shoes made of cloth-like composite material and
Use for the hat was easy. In addition, the results of the monitor test
As a result, it was confirmed that the shape did not occur and the wearing feeling was good
Was done.
【００１６】もちろんこの発明は以上の例により限定さ
れることはない。細部については様々な態様が可能であ
ることはいうまでもない。 Of course, the invention is limited by the above examples.
It will not be. Various aspects are possible for details
Needless to say.
【００１７】[0017]
【発明の効果】【The invention's effect】
以上詳しく説明した通り、この発明によAs described in detail above, the present invention
って、保形性に優れ、しかも滑らかで自然な素材感を有It has excellent shape retention and has a smooth and natural texture.
し、美観と意匠性とを向上させることのできる、作製もIn addition, production that can improve aesthetics and design
容易な布状の複合素材が提供される。An easy cloth-like composite material is provided.
【００１８】[0018]
【００１９】[0019]
【００２０】[0020]
【図１】この発明の布状複合素材の構成を例示した分解
斜視図である。FIG. 1 is an exploded perspective view illustrating the configuration of a cloth-like composite material according to the present invention.
１ 形状記憶合金線を用いた編物または織物 ２ 布 1. Knitted or woven fabric using shape memory alloy wire 2. Cloth
───────────────────────────────────────────────────── フロントページの続き (72)発明者 池田 利治 奈良県橿原市南八木町３丁目５番20号 マルコ株式会社内 (72)発明者 三村 文代 奈良県橿原市南八木町３丁目５番20号 マルコ株式会社内 (72)発明者 大森 譲 三重県桑名市大字東方1601の18 (56)参考文献 特開 平２−307982（ＪＰ，Ａ) 特開 昭53−123434（ＪＰ，Ａ) 特公 平１−37481（ＪＰ，Ｂ２) 特公 昭47−9231（ＪＰ，Ｂ１) ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Toshiharu Ikeda 3-5-20 Minamiyagicho, Kashihara City, Nara Prefecture Inside Marco Co., Ltd. (72) Inventor Fumiyo Mimura 3-20-20 Minamiyagicho, Kashihara City, Nara Prefecture No. Marco Co., Ltd. (72) Inventor Joru Omori 186-1, Tozai east, Kuwana-shi, Mie (56) References JP-A-2-307982 (JP, A) JP-A-53-123434 (JP, A) Hei 1-337481 (JP, B2) JP 47-9231 (JP, B1)
Claims (4)
形状記憶合金の細いワイヤーが単独で、またはステンレ
ス鋼、チタン、チタン合金、アルミニウム、アルミニウ
ム合金あるいはアモルファス合金の１種以上の細いワイ
ヤーと組み合わされて、編まれまたは織られ、所望の形
状に形状記憶熱処理された布状体の片面または両面に、
布が、２液反応型シアノアクリレート系の液状接着剤を
介して接着一体化されたことを特徴とする布状複合素
材。1. A NiTi-based, Ti-based, thin wire by itself a copper-based or iron-based shape memory alloy or stainless steel, titanium, titanium alloys, aluminum, one or more thin wires of aluminum alloy or amorphous alloy, It is combined with, knitted rare or are woven on one side or both sides of the shape memory heat-treated cloth-like material into a desired shape,
The cloth uses a two-part reactive cyanoacrylate liquid adhesive.
A cloth-like composite material characterized by being integrated by bonding through a fabric.
編物あるいは織物、または不繊布である請求項１の布状
複合素材。2. A fabric, natural fibers or knitted or woven fabric made of synthetic fiber or fabric-like composite material according to claim 1 which is nonwoven.
形状記憶合金の細いワイヤーを単独で、またはステンレ
ス鋼、チタン、チタン合金、アルミニウム、アルミニウ
ム合金あるいはアモルファス合金の１種以上の細いワイ
ヤーと組み合わせて、編みまたは織った後に、所望の形
状に形状記憶熱処理して布状体を作製し、次いでこの布
状体の片面または両面に布を２液反応型シアノアクリレ
ート系の液状接着剤で接着一体化することを特徴とする
布状複合素材の製造方法。3. A thin wire made of NiTi, Ti, copper or iron-based shape memory alloy alone, or one or more thin wires of stainless steel, titanium, titanium alloy, aluminum, aluminum alloy or amorphous alloy in combination with, after knitting or weaving, to produce a fabric-like material with shape memory heat treatment into a desired shape, and then two-liquid reaction type cloth on one side or both sides of the cloth-like member cyanoacrylate
A method for producing a cloth-like composite material , comprising bonding and integrating with a sheet-type liquid adhesive .
るいは織物、または不繊布を前記布状体の片面または両
面に接着一体化する請求項３の製造方法。4. A knitted or woven fabric made of natural fibers or synthetic fibers, or a non-woven fabric on one side or both sides of the cloth-like body.
The production method according to claim 3, wherein the surface is bonded and integrated.