JP2935302B2 - Manufacturing method of prepreg - Google Patents
Manufacturing method of prepregInfo
- Publication number
- JP2935302B2 JP2935302B2 JP33235791A JP33235791A JP2935302B2 JP 2935302 B2 JP2935302 B2 JP 2935302B2 JP 33235791 A JP33235791 A JP 33235791A JP 33235791 A JP33235791 A JP 33235791A JP 2935302 B2 JP2935302 B2 JP 2935302B2
- Authority
- JP
- Japan
- Prior art keywords
- prepreg
- drying furnace
- manufacturing
- endless belt
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】本発明は、積層板製造用のプリプ
レグの製造法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a prepreg for producing a laminate.
【0002】[0002]
【従来の技術】積層板製造用のプリプレグは、ガラス織
布やガラス不織布、紙等の長尺の基材にエポキシ樹脂等
の樹脂ワニスを含浸し乾燥炉を通して製造する。乾燥炉
の出口では、プリプレグを冷却されたロールの間隙に通
して引き取り、さらに次の工程へと移送する。2. Description of the Related Art A prepreg for manufacturing a laminate is manufactured by impregnating a long base material such as a glass woven fabric, a glass nonwoven fabric, and paper with a resin varnish such as an epoxy resin and passing through a drying furnace. At the outlet of the drying oven, the prepreg is taken through the gap between the cooled rolls, and is transferred to the next step.
【0003】[0003]
【発明が解決しようとする課題】上記のように、プリプ
レグをロールに通して冷却するだけでは十分に冷却され
ない。このような状態で移送の方向を変えると製造した
プリプレグに曲がりぐせがついてしまう。As described above, it is not sufficient to cool the prepreg simply by passing it through a roll. If the transfer direction is changed in such a state, the manufactured prepreg will bend.
【0004】本発明が解決しようとする課題は、乾燥炉
から引き取ったプリプレグの方向を変えて移送してもプ
リプレグに曲がりぐせがつかないようにすることであ
る。[0004] The problem to be solved by the present invention is to prevent the prepreg from being bent even when the prepreg taken from the drying furnace is transferred in a different direction.
【0005】[0005]
【課題を解決するための手段】上記課題を解決するため
に本発明に係る製造法では、乾燥炉の出口で、プリプレ
グを冷却されたエンドレスベルトに当接して移送するこ
とを特徴とする。In order to solve the above-mentioned problems, a manufacturing method according to the present invention is characterized in that a prepreg is transported at the outlet of a drying furnace in contact with a cooled endless belt.
【0006】[0006]
【作用】本発明に係る製造法では、乾燥炉出口でプリプ
レグを冷却されたエンドレスベルトに当接することによ
り、冷却時間が長くなり十分に冷却することができる。In the manufacturing method according to the present invention, the prepreg is brought into contact with the cooled endless belt at the outlet of the drying furnace, so that the cooling time is prolonged and sufficient cooling can be achieved.
【0007】[0007]
【実施例】本発明に係る実施例を説明する。乾燥炉4の
出口にスチール製のエンドレスベルト2を設置する。ス
チールベルト2は、軸間の距離が1500mmで径が25
0mmの一対のロール3,3’に掛けて駆動するものであ
る。ロール3,3’は、その内部に水を流して20℃に
保持しておく。これによって、エンドレスベルト2は、
常にロール3,3’で冷却されている。乾燥炉4から出
てきたプリプレグ1は、まずエンドレスベルト2に当接
した状態で移送し冷却する。その後、移送方向を120
°程度変えて引き取り、1050×1050mmに裁断し
て400mmの高さに積み重ねた。An embodiment according to the present invention will be described. The endless belt 2 made of steel is installed at the outlet of the drying furnace 4. Steel belt 2 has a distance between shafts of 1500 mm and a diameter of 25 mm.
It is driven by a pair of 0 mm rolls 3, 3 '. The rolls 3 and 3 'are maintained at 20 ° C. by flowing water therein. Thereby, the endless belt 2
It is always cooled by rolls 3, 3 '. The prepreg 1 coming out of the drying furnace 4 is first transferred and cooled while being in contact with the endless belt 2. After that, the transfer direction is changed to 120
° and changed to about 1050 mm, cut into 1050 × 1050 mm, and stacked at a height of 400 mm.
【0008】比較のために、乾燥炉から出てきたプリプ
レグを20℃に保持したロールの隙間に通して引き取
り、その後上記と同様に移送方向を変えて引き取り裁断
して積み重ねた。For comparison, the prepreg coming out of the drying oven was taken out through a gap between rolls maintained at 20 ° C., and thereafter, the prepreg was taken out by changing the transfer direction and stacked in the same manner as described above.
【0009】400mmの高さに積み重ねたプリプレグ
は、カールにより側部が若干厚くなるが、実施例のもの
ではその厚さが中央部より20mm厚くなるのに対し、比
較したものでは50mm厚くなった。これにより、本発明
に係る方法ではプリプレグの曲がりぐせが抑制されてい
ることが分かる。[0009] The prepreg stacked at a height of 400 mm is slightly thicker at the side due to curling, but the thickness of the prepreg of the embodiment is 20 mm thicker than that of the center portion, but is 50 mm thicker in comparison. . This shows that the method according to the present invention suppresses the bending of the prepreg.
【0010】[0010]
【発明の効果】上述のように本発明に係る方法では、乾
燥炉から出てきたプリプレグが十分に冷却されるので、
移送方向を変えてもプリプレグに曲がりぐせがつくのを
抑制することができる。As described above, in the method according to the present invention, the prepreg coming out of the drying furnace is sufficiently cooled.
Even if the transfer direction is changed, it is possible to prevent the prepreg from being bent.
【図1】本発明に係る一実施例を示す説明図である。FIG. 1 is an explanatory diagram showing one embodiment according to the present invention.
1はプリプレグ 2はエンドレスベルト 3,3’はロール 4は乾燥炉 1 is a prepreg 2 is an endless belt 3 is a roll 4 is a drying oven
Claims (1)
を乾燥炉に通してプリプレグとする工程において、乾燥
炉出口に設置した冷却されたエンドレスベルトにプリプ
レグを当接して移送することを特徴とするプリプレグの
製造法。In the step of passing a long sheet-like base material impregnated with a resin varnish into a prepreg by passing it through a drying furnace, transferring the prepreg into contact with a cooled endless belt installed at an outlet of the drying furnace. Characteristic prepreg manufacturing method.