JP2935006B2 - Manufacturing method of decorative board - Google Patents
Manufacturing method of decorative boardInfo
- Publication number
- JP2935006B2 JP2935006B2 JP18311594A JP18311594A JP2935006B2 JP 2935006 B2 JP2935006 B2 JP 2935006B2 JP 18311594 A JP18311594 A JP 18311594A JP 18311594 A JP18311594 A JP 18311594A JP 2935006 B2 JP2935006 B2 JP 2935006B2
- Authority
- JP
- Japan
- Prior art keywords
- veneer
- adhesive
- synthetic resin
- resin sheet
- transparent synthetic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は家屋における建材や家具
用板として用いられる化粧板の製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing a decorative board used as a building material or a board for furniture in a house.
【0002】[0002]
【従来の技術】従来から、基板の表面に接着剤を介して
化粧単板を貼着し、次いで化粧単板面に着色塗料を塗布
して着色塗装を施し、更に上塗り塗料を塗布して上塗り
塗装を施して表面保護層を形成し、化粧板とすることが
広く行われている。2. Description of the Related Art Conventionally, a decorative veneer is adhered to the surface of a substrate via an adhesive, and then a colored paint is applied to the surface of the decorative veneer to apply a colored coating. It is widely practiced to apply a coating to form a surface protective layer to form a decorative plate.
【0003】[0003]
【発明が解決しようとする課題】上記従来技術におい
て、表面保護層に十分な機能を与えるためには上塗り塗
料を何度も塗り重ねて厚塗りする必要があり、作業工程
が煩雑化する。In the above-mentioned prior art, in order to give a sufficient function to the surface protective layer, it is necessary to repeatedly apply a top coat and to apply it thickly, which complicates the working process.
【0004】また、粘度の高い塗料を用いて厚塗りを行
おうとする場合、塗装速度または乾燥速度が速いと、均
一塗装ができず、また乾燥時に発泡が生ずるため、実際
には塗装速度および乾燥速度をいずれも遅くしてこれら
の問題を回避しているが、反面、生産性の低下が不可避
となる。[0004] When a thick coating is to be performed using a high-viscosity paint, if the coating speed or the drying speed is high, uniform coating cannot be performed and foaming occurs during drying. These problems are avoided by reducing the speed, but on the other hand, a decrease in productivity is inevitable.
【0005】また、上記のような事情から、上塗り塗料
の厚塗りを断念し、比較的薄い表面保護層を形成するこ
とも行われているが、この場合には表面保護層の強度が
弱くなるため、傷がつきやすく、耐摩耗性に乏しいもの
となり、また深みのある化粧表面を得ることができない
等の問題を有する。In view of the above circumstances, it has been practiced to abandon the thick coating of the top coat to form a relatively thin surface protective layer. In this case, however, the strength of the surface protective layer is reduced. Therefore, there are problems that the surface is easily scratched and has poor abrasion resistance, and a deep decorative surface cannot be obtained.
【0006】更に、従来の化粧板の製造方法において
は、化粧単板に乾燥収縮に伴う反りやあばれが生じやす
く、これを防止するために裏打ち材を貼着することが行
われているが、裏打ち材貼着に伴う工程の繁雑化および
製造コスト上昇が避けられなかった。[0006] Further, in the conventional method of manufacturing a decorative veneer, a decorative veneer is liable to be warped or warped due to drying shrinkage, and a backing material is stuck to prevent this. The complication of the process and the increase in manufacturing cost associated with the attachment of the backing material were inevitable.
【0007】[0007]
【課題を解決するための手段】本発明は上記従来技術の
問題点を解消することを目的とし、より具体的には、高
品質の化粧板を比較的簡単な作業工程により安定的に供
給し、生産性も向上させると共に、裏打ち材の貼着を不
要化しつつ化粧単板の乾燥収縮に伴う問題を解決するこ
とを目的とする。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems of the prior art, and more specifically, to stably supply a high-quality decorative board by a relatively simple work process. It is also an object of the present invention to improve the productivity and solve the problem associated with drying shrinkage of the decorative veneer while eliminating the need for attaching a backing material.
【0008】かかる目的を達成するために鋭意工夫の末
に創案された本発明による化粧板の製造方法は、湿潤木
材を切削して得られる湿潤状態の化粧単板の上面に、透
明あるいは硬化すると透明となる接着剤を介して透明合
成樹脂シートを載置して、圧締接着すると同時に湿潤状
態の化粧単板を乾燥させた後、得られた透明合成樹脂シ
ート貼り化粧単板を、表面に接着剤が塗布された基板の
上面に載置して圧締接着することにより、該透明合成樹
脂シート貼り化粧単板を該基板上に貼着し、更に、表面
からエンボス加工を施して凹所を刻設形成することを特
徴とする。In order to achieve the above object, the method for producing a decorative panel according to the present invention, which has been devised after elaborate devising, has been proposed in which a transparent or hardened veneer veneer obtained by cutting wet wood is coated on the upper surface. After placing the transparent synthetic resin sheet via the transparent adhesive, pressing and bonding and simultaneously drying the wet veneer veneer, the resulting transparent synthetic resin sheet pasted veneer is applied to the surface. The transparent synthetic resin sheet-attached decorative veneer is adhered to the substrate by placing it on the upper surface of the substrate to which the adhesive has been applied and pressure-bonding, and further embossing the surface to form a recess. Is formed by engraving.
【0009】本発明方法の実施においては、まず、湿潤
木材を切削して湿潤状態の化粧単板を得る。すなわち、
生木材、木材を煮沸した煮沸木材、生木材ブロックを複
数接着した積層ブロック、木材ブロックを複数積層した
後煮沸した煮沸積層ブロック等の繊維飽和点以上の含水
率を有する湿潤木材を、スライサー、ロータリーレー
ス、ハーフランドロータリーレース、丸鋸、帯鋸、鉋鋸
等の切断切削装置により切断切削してスライス単板、ロ
ータリー単板、ハーフランド単板、ソード単板等の湿潤
状態の化粧単板を得、これを乾燥することなく本発明方
法に用いるものである。In carrying out the method of the present invention, first, wet wood is cut to obtain a wet veneer veneer. That is,
Raw wood, boiled wood obtained by boiling wood, laminated blocks obtained by bonding a plurality of raw wood blocks, boiled laminated blocks obtained by laminating a plurality of wood blocks, and then boiling wet wood having a water content equal to or higher than the fiber saturation point are sliced by a slicer or rotary. Cut and cut with a cutting machine such as lace, half land rotary lace, circular saw, band saw, plane saw, etc. to obtain wet veneer veneer such as slice veneer, rotary veneer, half land veneer, sword veneer. This is used in the method of the present invention without drying.
【0010】用いられる化粧単板の厚さは、一般に、
0.15〜5mmの範囲であることが好ましい。The thickness of the decorative veneer used is generally
Preferably, it is in the range of 0.15 to 5 mm.
【0011】この湿潤状態の化粧単板の表面に、スプレ
ー、スプレッダー、バーコーター、フローコーター、カ
ーテンコーター等の塗布装置を用いて、透明あるいは硬
化すると透明となる接着剤を塗布する。An adhesive which becomes transparent or hardens and becomes transparent is applied to the surface of the wet decorative veneer using an application device such as a sprayer, a spreader, a bar coater, a flow coater and a curtain coater.
【0012】このときに用いられる透明あるいは硬化す
ると透明となる接着剤は、酢酸ビニル樹脂系、ユリア樹
脂系、メラミン樹脂系、フェノール樹脂系、アクリル樹
脂系、ウレタン樹脂系、エポキシ樹脂系、レゾルジノー
ル樹脂系、ポリエステル樹脂系、イソシアネート系等の
接着剤であり、単独であるいは任意混合した混合型接着
剤として用いられる。The adhesive used at this time, which is transparent or hardens when it is cured, is vinyl acetate resin, urea resin, melamine resin, phenol resin, acrylic resin, urethane resin, epoxy resin, resordinol resin. Adhesives, such as polyester-based, polyester resin-based, and isocyanate-based adhesives. These adhesives are used alone or as a mixed adhesive of any mixture.
【0013】また、ポリウレタン樹脂系接着剤のような
湿潤硬化タイプの接着剤を用いることができる。湿潤硬
化タイプの接着剤は、湿潤状態で常温にて硬化するもの
であるため、湿潤状態の化粧単板を用いる本発明方法の
実施において特に好適に用いられる。Further, a wet-curing type adhesive such as a polyurethane resin-based adhesive can be used. Since the wet-curable adhesive is cured at room temperature in a wet state, it is particularly preferably used in the practice of the method of the present invention using a veneer veneer in a wet state.
【0014】用いられる接着剤には必要に応じて着色剤
を添加して、着色接着剤として用いることができる。A coloring agent may be added to the adhesive to be used, if necessary, and used as a coloring adhesive.
【0015】用いられる接着剤は、それ自体が透明ある
いは少なくとも硬化すると透明となるものであり、且
つ、この接着剤を介して化粧単板表面に貼着されるのは
透明合成樹脂シートであるため、得られた化粧板におい
ては化粧単板表面が隠蔽されることなく化粧板表面に現
出される。The adhesive used is transparent or at least becomes transparent when cured, and the transparent synthetic resin sheet is adhered to the surface of the decorative veneer via the adhesive. In the obtained decorative board, the decorative veneer surface appears on the decorative board surface without being concealed.
【0016】透明あるいは硬化すると透明となる接着剤
が塗布された化粧単板の表面に、透明合成樹脂シートを
載置する。A transparent synthetic resin sheet is placed on the surface of a decorative veneer coated with an adhesive which becomes transparent or hardens when cured.
【0017】透明合成樹脂シートとしては、ポリエチレ
ンシート、セロファン、アセテートシート、ポリ塩化ビ
ニルシート、ポリプロピレンシート、ポリスチレンシー
ト、ポリエステルシート、ナイロンシート、サランシー
ト、アクリルシート等が好適に用いられる。一般に透明
合成樹脂シートは0.005〜1mmの厚さを有するも
のとして用いられる。透明合成樹脂シートは、化粧単板
毎葉ごとにあるいは複数の化粧単板に亙って連続して、
化粧単板の接着剤塗布面に載置される。As the transparent synthetic resin sheet, polyethylene sheet, cellophane, acetate sheet, polyvinyl chloride sheet, polypropylene sheet, polystyrene sheet, polyester sheet, nylon sheet, Saran sheet, acrylic sheet and the like are preferably used. Generally, a transparent synthetic resin sheet is used as a sheet having a thickness of 0.005 to 1 mm. The transparent synthetic resin sheet is continuous every decorative veneer or over a plurality of decorative veneers,
It is placed on the adhesive-coated surface of the veneer veneer.
【0018】透明合成樹脂シートとして、任意着色され
た着色透明合成樹脂シートを用いることができる。ま
た、裏面に任意柄模様が印刷された無色または着色した
透明合成樹脂シートを用いてもよい。これにより、化粧
単板の本来の表面意匠と相俟って、木質感を強調し、新
たな樹種を表現し、深みを表現し、あるいはモザイク柄
や抽象柄を表現することができ、化粧板としての意匠性
が更に向上される。As the transparent synthetic resin sheet, an arbitrary colored transparent synthetic resin sheet can be used. Further, a colorless or colored transparent synthetic resin sheet having an arbitrary pattern printed on the back surface may be used. This, combined with the original surface design of the veneer veneer, emphasizes the texture of wood, expresses new tree species, expresses depth, or expresses mosaic patterns and abstract patterns. Is further improved.
【0019】透明あるいは硬化すると透明となる接着剤
を介して表面に透明合成樹脂シートが載置された湿潤状
態の化粧単板を、ホットプレス、ロールプレス、ラミネ
ーター、ラッピング、縁貼り機、真空プレス等の圧締装
置を用いて圧締することにより、透明合成樹脂シートが
化粧単板表面に接着されて、表面保護層が形成される。
また、この圧締接着の際に湿潤状態の化粧単板に高熱が
作用するため、透明合成樹脂シートの貼着と同時に化粧
単板の乾燥が行われる。A wet veneer having a transparent synthetic resin sheet placed on the surface thereof through an adhesive which becomes transparent or hardens when cured, is hot-pressed, roll-pressed, laminator, wrapping, rimping machine, vacuum press The transparent synthetic resin sheet is adhered to the surface of the decorative veneer by pressing using a pressing device such as the above, and a surface protective layer is formed.
In addition, since high heat acts on the wet decorative veneer during the pressure bonding, the decorative veneer is dried simultaneously with the attachment of the transparent synthetic resin sheet.
【0020】次に、基板の表面にスプレー、スプレッダ
ー、バーコーター、フローコーター、カーテンコーター
等の塗布装置を用いて接着剤を塗布する。この接着剤に
は、酢酸ビニル樹脂系、ユリア樹脂系、メラミン樹脂
系、フェノール樹脂系、エポキシ樹脂系、イソシアネー
ト系等の接着剤を、単独であるいは任意混合した混合型
接着剤として用いられる。接着剤には、必要に応じてタ
ルク、炭カル、クレー、チタン白等の無機質粉末、小麦
粉、木粉、プラスチック粉、着色剤、防虫剤、防カビ剤
等を添加混合して用いることができる。接着剤は、一般
に、固形分35〜80%、塗布量50〜300g/m2
の範囲で塗布される。Next, an adhesive is applied to the surface of the substrate using an application device such as a spray, a spreader, a bar coater, a flow coater, and a curtain coater. As the adhesive, an adhesive of a vinyl acetate resin type, a urea resin type, a melamine resin type, a phenol resin type, an epoxy resin type, an isocyanate type, or the like is used alone or as a mixed type adhesive obtained by arbitrary mixing. The adhesive can be used by adding and mixing inorganic powder such as talc, charcoal, clay, titanium white, etc., flour, wood flour, plastic powder, coloring agent, insect repellent, fungicide, etc., if necessary. . The adhesive generally has a solid content of 35 to 80% and a coating amount of 50 to 300 g / m 2.
It is applied in the range.
【0021】基板には、合板、木質板、木質繊維板、木
削片板、集成材、単板積層板等が、単独であるいは任意
積層してなる積層板として用いられる。また、該基板を
任意切断し、表面や木口部にルーター、カッター等の切
削加工機を用いて溝加工、面取加工等の任意加飾を施し
た幅木、廻り縁、モール、ドア、窓等に用いられる面
材、造作材等の基材として用いることもできる。As the substrate, a plywood, a wood board, a wood fiber board, a wood chip board, a glued laminated wood, a veneer laminate board or the like is used alone or as a laminate board obtained by optionally stacking. In addition, the substrate is arbitrarily cut, and a skirting board, a surrounding edge, a molding, a door, a window, which is subjected to optional decoration such as grooving and chamfering using a cutting machine such as a router or a cutter on the surface or the edge of the edge, is provided. It can also be used as a base material for surface materials, construction materials, and the like used for such purposes.
【0022】接着剤を塗布された基板の表面に、前記の
ようにして得た透明合成樹脂シート貼り化粧単板を、該
透明合成樹脂シートを上面として載置する。On the surface of the substrate on which the adhesive has been applied, the transparent synthetic resin sheet-attached decorative veneer obtained as described above is placed with the transparent synthetic resin sheet facing upward.
【0023】本発明方法は、基板の表面に接着剤を介し
て透明合成樹脂シート貼り化粧単板を貼着するものであ
り、上記したように接着剤を基板の表面に塗布するに代
えて、あるいはこれと共に、透明合成樹脂シート貼り化
粧単板の裏面に接着剤を塗布してもよい。透明合成樹脂
シート貼り化粧単板は基板毎葉に貼着しても、あるいは
複数の基板に亙って連続して貼着してもよい。According to the method of the present invention, a decorative veneer with a transparent synthetic resin sheet is adhered to the surface of the substrate via an adhesive. Instead of applying the adhesive to the surface of the substrate as described above, Alternatively, an adhesive may be applied to the back surface of the veneer veneer laminated with the transparent synthetic resin sheet. The transparent synthetic resin sheet-attached veneer may be attached to each substrate or may be attached continuously over a plurality of substrates.
【0024】このようにして接着剤を介して毎葉ごとに
あるいは連続して透明合成樹脂シート貼り化粧単板が載
置された基板を、コールドプレス、ホットプレス、ロー
ルプレス、ラミネーター、ラッピング、縁貼り機,真空
プレス等の貼着装置を用いて圧締して、透明合成樹脂シ
ート貼り化粧単板を基板表面に接着する。The substrate on which the decorative veneer laminated with the transparent synthetic resin sheet is placed on each leaf or continuously through the adhesive in this manner is cold-pressed, hot-pressed, roll-pressed, laminator, wrapped, edged. A transparent synthetic resin sheet-attached veneer is adhered to the surface of the substrate by pressing using a pasting device such as a pasting machine or a vacuum press.
【0025】次いで、透明合成樹脂シートよりなる表面
保護層の表面側からエンボス加工を施して凹所を刻設形
成する。エンボス加工は、エンボス盤、エンボスロー
ル、ワイヤブラシ、サンダー等を用いて行われる。凹所
の深さは任意であり、表面保護層の厚さ範囲内の深さの
凹所、あるいは表面保護層を貫通して化粧単板にまで達
する深さの凹所、あるいはこれらの組み合わせよりなる
凹所が形成される。Next, a recess is formed by embossing from the surface side of the surface protective layer made of a transparent synthetic resin sheet. The embossing is performed using an embossing machine, an embossing roll, a wire brush, a sander, or the like. The depth of the recess is optional, and may be smaller than the depth of the surface protective layer, the depth of the surface penetrating the surface protective layer to the decorative veneer, or a combination thereof. A recess is formed.
【0026】表面保護層に刻設される凹所は、天然木質
材料が有する導管溝、ヘヤライン、虫食い穴等の凹所を
疑似的に表現するものであり、該凹所による陰影効果に
より木質感が強調され、化粧板としての意匠性を大きく
向上させることができる。The recesses engraved in the surface protective layer represent the recesses of the natural woody material, such as conduit grooves, hair lines, wormholes, etc., and the shading effect of the recesses gives the wood texture. Is emphasized, and the design as a decorative board can be greatly improved.
【0027】また、透明合成樹脂シートを化粧単板表面
に貼着する際に、透明あるいは硬化すると透明となる接
着剤が用いられるので、化粧単板表面の導管溝等の凹所
が透明接着剤層および透明な表面保護層を介して化粧板
の表面から露見されることになるため、該化粧単板自体
が持つ凹所と表面保護層の表面に疑似的に形成される凹
所とが組み合わされて、きわめて特徴的な意匠性を発揮
することができる。Further, when the transparent synthetic resin sheet is adhered to the surface of the decorative veneer, an adhesive which is transparent or hardened and becomes transparent is used. The decorative veneer itself is exposed through the surface of the decorative veneer through the layer and the transparent surface protective layer. Therefore, the concave portion of the veneer itself and the concave portion formed on the surface of the surface protective layer are combined. As a result, a very distinctive design can be exhibited.
【0028】更に、この化粧板の全般表面に、前述のよ
うな塗装装置を用いて着色塗料を塗布した後、好ましく
はその直後にリバースロールコーターを用いて、表面保
護層の凹所を除く表面部分に塗布された着色塗料を除去
して凹所内にのみ着色塗料を残存させることにより、表
面保護層の凹所内を着色塗装することができる。これに
より表面保護層の凹所が一層強調的に表現され、意匠性
の向上がなされる。Further, after applying a colored paint to the entire surface of the decorative board using the above-described coating apparatus, preferably immediately after that, using a reverse roll coater, the surface excluding the recesses of the surface protective layer is removed. By removing the colored paint applied to the portion and leaving the colored paint only in the recess, the inside of the recess of the surface protective layer can be colored. As a result, the recesses of the surface protective layer are more emphasized and the design is improved.
【0029】[0029]
【作用】透明合成樹脂シートを用いてこれを透明あるい
は硬化すると透明となる接着剤を介して化粧単板上に接
着することにより表面保護層が形成される。表面保護層
は、用いられる透明合成樹脂シートの厚さに対応し、し
かも均等な厚さに形成される。The surface protective layer is formed by bonding a transparent synthetic resin sheet to a decorative veneer via an adhesive which becomes transparent when cured or cured. The surface protective layer is formed in a uniform thickness corresponding to the thickness of the transparent synthetic resin sheet to be used.
【0030】化粧単板は乾燥処理を施されない湿潤状態
のものが用いられ、透明合成樹脂シートの圧締接着と同
時に化粧単板の乾燥が行われるので、化粧単板の乾燥収
縮に伴う反りやあばれ等を生じさせることがない。The decorative veneer is used in a wet state that is not subjected to a drying treatment. Since the decorative veneer is dried at the same time as the transparent synthetic resin sheet is pressed and adhered, the warp caused by drying shrinkage of the decorative veneer is reduced. There is no rash.
【0031】表面保護層の表面には導管溝等を疑似的に
表現する凹所が刻設形成され、木質感が強調的に表現さ
れる。On the surface of the surface protective layer, a concave portion is formed in a pseudo manner to represent a conduit groove or the like, so that a wooden texture is emphasized.
【0032】[0032]
【実施例】図1は上記した本発明方法によって得られる
化粧板を模式的に示すものであり、基板1の表面に接着
剤層2を介して化粧単板3が積層され、化粧単板3の表
面には透明合成樹脂シートが透明または硬化すると透明
となる接着剤を介して積層接着されて表面保護層4を形
成している。5は透明接着剤層である。FIG. 1 schematically shows a decorative plate obtained by the above-described method of the present invention. A decorative veneer 3 is laminated on the surface of a substrate 1 with an adhesive layer 2 interposed therebetween. A transparent synthetic resin sheet is laminated and adhered to the surface via an adhesive that becomes transparent when cured or cured to form a surface protective layer 4. 5 is a transparent adhesive layer.
【0033】表面保護層4の表面側には導管溝等を疑似
的に表現する凹所6、6’がエンボス加工により刻設形
成されている。この実施例において、凹所6は表面保護
層4の厚さ範囲内において形成され、凹所6’は表面保
護層を貫通して化粧単板3に達する深さのものとして形
成されている。また、この実施例においては、これら凹
所内は着色塗料7により着色塗装されている。On the surface side of the surface protective layer 4, recesses 6 and 6 'for emulating a conduit groove or the like are formed by embossing. In this embodiment, the recess 6 is formed within the thickness range of the surface protection layer 4, and the recess 6 ′ is formed so as to penetrate the surface protection layer and reach the decorative veneer 3. Further, in this embodiment, the insides of these recesses are colored by the colored paint 7.
【0034】[0034]
【発明の効果】本発明方法によれば、化粧板における化
粧単板の表面に均一厚さの表面保護層を簡単な作業工程
で容易に形成することができる。本発明方法によって得
られる化粧板は、強度や耐摩耗性および意匠性に優れた
ものであり、建材用や家具用に好適に用いられる。According to the method of the present invention, a surface protective layer having a uniform thickness can be easily formed on the surface of a decorative veneer in a decorative plate by a simple operation process. The decorative board obtained by the method of the present invention has excellent strength, abrasion resistance and design properties, and is suitably used for building materials and furniture.
【0035】また、用いられる透明合成樹脂シートの厚
さを変更することによって表面保護層の厚さを調整する
ことができる。この場合、製造設備には何ら変更を要し
ない。The thickness of the surface protective layer can be adjusted by changing the thickness of the transparent synthetic resin sheet used. In this case, no change is required for the manufacturing equipment.
【0036】更に、本発明方法においては、湿潤状態の
化粧単板を用いてこの上面に透明合成樹脂シートを圧締
接着すると同時に化粧単板の乾燥を行うものであるた
め、化粧単板の乾燥収縮に伴う反りやあばれ等が発生せ
ず、裏打ち材を用いる必要がなく、歩留まりが顕著に向
上される。Further, in the method of the present invention, the decorative veneer is dried while the transparent veneer veneer is pressed and adhered to the upper surface of the veneer veneer using a wet veneer. There is no warpage or rubbing due to shrinkage, no backing material is required, and the yield is significantly improved.
【0037】更に、表面保護層の表面には導管溝等を疑
似的に表現する凹所が刻設形成され、木質感を強調的に
表現する。Further, a recess is formed in the surface of the surface protection layer to simulate a conduit groove or the like, thereby emphasizing the wood texture.
【図1】本発明による化粧板を模式的に示す断面図であ
る。FIG. 1 is a sectional view schematically showing a decorative board according to the present invention.
1 基板 2 接着剤層 3 化粧単板 4 表面保護層(透明合成樹脂シート) 5 透明接着剤層 6、6’ 凹所 7 着色塗料 DESCRIPTION OF SYMBOLS 1 Substrate 2 Adhesive layer 3 Decorative veneer 4 Surface protective layer (transparent synthetic resin sheet) 5 Transparent adhesive layer 6, 6 'recess 7 Colored paint
Claims (6)
の化粧単板の上面に、透明あるいは硬化すると透明とな
る接着剤を介して透明合成樹脂シートを載置して、圧締
接着すると同時に湿潤状態の化粧単板を乾燥させた後、
得られた透明合成樹脂シート貼り化粧単板を、表面に接
着剤が塗布された基板の上面に載置して圧締接着するこ
とにより、該透明合成樹脂シート貼り化粧単板を該基板
上に貼着し、更に、表面からエンボス加工を施して凹所
を刻設形成することを特徴とする化粧板の製造方法。1. A transparent synthetic resin sheet is placed on the top surface of a veneer veneer in a wet state obtained by cutting wet wood via an adhesive which becomes transparent or hardens when cured, and is pressed and bonded. After drying the wet veneer veneer,
The resulting transparent synthetic resin sheet-attached veneer is placed on the upper surface of the substrate having an adhesive applied to the surface thereof and pressed and adhered, whereby the transparent synthetic resin sheet-attached veneer is placed on the substrate. A method for manufacturing a decorative board, comprising: attaching the sheet; and embossing the surface to form a recess.
れた着色透明合成樹脂シートであることを特徴とする請
求項1の化粧板の製造方法。2. The method for manufacturing a decorative board according to claim 1, wherein said transparent synthetic resin sheet is a colored transparent synthetic resin sheet which is arbitrarily colored.
様が印刷形成されてなることを特徴とする請求項1また
は2の化粧板の製造方法。3. The method for manufacturing a decorative board according to claim 1, wherein a pattern is printed and formed on the back surface of the transparent synthetic resin sheet.
る接着剤が任意着色された着色接着剤であることを特徴
とする請求項1ないし3のいずれかの化粧板の製造方
法。4. The method for manufacturing a decorative board according to claim 1, wherein the adhesive which becomes transparent or becomes transparent when cured is a colored adhesive which is arbitrarily colored.
る接着剤が湿潤硬化タイプの接着剤であることを特徴と
する請求項1ないし4のいずれかの化粧板の製造方法。5. The method for manufacturing a decorative board according to claim 1, wherein said transparent or cured adhesive is a wet-curable adhesive.
装を塗布した後、該凹所を除く表面部分に塗布された着
色塗装を除去して、該凹所内のみに着色塗装を残存させ
ることを特徴とする請求項1ないし5のいずれかの化粧
板の製造方法。6. After applying a colored coating on the surface on which the recess is formed, the colored coating applied to the surface portion excluding the recess is removed to leave the colored coating only in the recess. A method for producing a decorative board according to any one of claims 1 to 5, characterized in that: