JP2853972B2 - Concrete block and its greening method - Google Patents
Concrete block and its greening methodInfo
- Publication number
- JP2853972B2 JP2853972B2 JP7051329A JP5132995A JP2853972B2 JP 2853972 B2 JP2853972 B2 JP 2853972B2 JP 7051329 A JP7051329 A JP 7051329A JP 5132995 A JP5132995 A JP 5132995A JP 2853972 B2 JP2853972 B2 JP 2853972B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete block
- aggregate
- size
- present
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、コンクリートブロック
およびその緑化方法に関するものである。さらに詳しく
は本発明は、植物の生長に極めて有効な連続した空隙の
形成されたコンクリートブロックおよびその緑化方法に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a concrete block and a method for greening the concrete block. More specifically, the present invention relates to a concrete block in which continuous voids are formed, which is extremely effective for plant growth, and a method for greening the concrete block.
【０００２】[0002]
【従来の技術】人間の環境衛生にとって、植物の緑は極
めて重要なものの一つであるが、近時、産業の発展や都
市開発などに伴う人為的な自然破壊により、植物の緑が
次第に失われていく傾向にあり、その回復対策が強く要
望されている。そこで、河川の土手や道路の法面を補強
するコンクリート等のような、通常では植物を育成する
ことのできない基盤を緑化の被対象物にすることが行わ
れている。2. Description of the Related Art Plant greenery is one of the most important aspects of human environmental hygiene, but recently plant greenery has been gradually lost due to artificial destruction accompanying industrial development and urban development. There is a strong demand for recovery measures. Therefore, a base that cannot normally grow plants, such as concrete that reinforces a bank of a river or a slope of a road, is used as an object to be greened.
【０００３】特開昭５３−１１４２０４号公報には、粗
骨材、まぶしバインダーおよび水を配合して硬化させて
連続した空隙を有するコンクリート硬化体を得、該硬化
体に形成された空隙に植物の種子を混入した培養土壌材
を充填し、該種子を発芽生長させ、コンクリート硬化体
の表面を植物で覆う植物緑化方法が開示されている。こ
の方法は、自然土壌では困難とされていた壁面の緑化施
工ができ、有用なものである。Japanese Patent Application Laid-Open No. 53-114204 discloses that a concrete hardened body having continuous voids is obtained by blending a coarse aggregate, a glaze binder and water and hardening, and a plant is formed in the voids formed in the hardened body. A plant greening method is disclosed in which a culture soil material mixed with a seed is filled, the seed is germinated and grown, and the surface of a hardened concrete body is covered with a plant. This method is useful because it enables greening of the wall, which has been difficult with natural soil.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上記の
従来の方法で得られるコンクリート硬化体は、連通して
いない空隙や、植物の根が通りにくい空隙が幾分か存在
し、さらに、このような空隙には培養土壌材の充填が困
難であるため、植物の生育が不良となる場合があった。However, in the concrete hardened body obtained by the above-mentioned conventional method, there are some gaps that are not communicated and some gaps through which plant roots do not easily pass. Since it is difficult to fill the gap with the culture soil material, the growth of the plant sometimes becomes poor.
【０００５】本発明は上記のような従来の課題を解決
し、植物の生長に極めて有効である空隙を有するコンク
リートブロックおよびその緑化方法を提供することを目
的とするものである。An object of the present invention is to solve the above-mentioned conventional problems and to provide a concrete block having a void which is extremely effective for plant growth and a method for greening the concrete block.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、主原料と
して骨材、セメントおよび水を配合し硬化させてなるコ
ンクリートブロックにおいて、一定の寸法範囲の粗骨材
を規定量含有させることにより、植物の生長に極めて有
効である連通した空隙が、好適な空隙率および空隙サイ
ズでもってコンクリートブロックに形成されるという驚
くべき事実を見いだし、本発明を完成することができ
た。Means for Solving the Problems The present inventors have found that a concrete block obtained by mixing and hardening aggregate, cement and water as main raw materials contains a specified amount of coarse aggregate in a certain size range. The present inventors have found the surprising fact that interconnected voids, which are extremely effective for plant growth, are formed in concrete blocks with a suitable porosity and void size, and the present invention has been completed.
【０００７】すなわち本発明は、主原料として骨材、セ
メントおよび水を配合し硬化させてなる空隙率２５〜３
５％の連続した空隙を有するコンクリートブロックにお
いて、該骨材の８０重量％以上が８〜１８mmの範囲内の
寸法を有する粗骨材であり、および２０〜２５mmの寸法
を有する粗骨材が５重量％以下であり、且つ５mm以下の
寸法を有する骨材が５重量％以下であることを特徴とす
る、コンクリートブロックを提供するものである。That is, according to the present invention, a porosity of 25 to 3 obtained by mixing and hardening aggregate, cement and water as main raw materials.
In a concrete block having 5% continuous voids, more than 80% by weight of the aggregate is coarse aggregate having a size in the range of 8 to 18 mm, and coarse aggregate having a size of 20 to 25 mm is 5%. It is an object of the present invention to provide a concrete block characterized in that an aggregate having a size of not more than 5% by weight is 5% by weight or less.
【０００８】また本発明は、骨材の７０重量％以上が１
０〜１５mmの範囲内の寸法を有する粗骨材である、前記
のコンクリートブロックを提供するものである。In the present invention, more than 70% by weight of the aggregate is 1%.
It is an object of the present invention to provide the concrete block, which is a coarse aggregate having a size in a range of 0 to 15 mm.
【０００９】さらに本発明は、前記のコンクリートブロ
ックの空隙内に、植物の種子および培養土壌材を充填
し、該種子を発芽させ生長させることを特徴とする、コ
ンクリートブロックの緑化方法を提供するものである。Further, the present invention provides a method for greening a concrete block, which comprises filling seeds of a plant and a culture soil material in the voids of the concrete block, and germinating and growing the seeds. It is.
【００１０】以下、本発明をさらに詳細に説明する。 （骨材）上記のように、本発明のコンクリートブロック
は、植物の生長に極めて有効である連通した空隙が、好
適な空隙率および空隙サイズでもって形成されているも
のであるが、そのためには、一定の寸法範囲の粗骨材を
規定量含有させることが必要である。すなわち、本発明
のコンクリートブロックは、８〜１８mmの寸法の粗骨材
を、骨材全体に対して８０重量％以上含む必要がある。
８０重量％未満であると、植物の生長に有効な連通した
空隙が得にくい。好ましくは、８５〜１００重量％であ
る。Hereinafter, the present invention will be described in more detail. (Aggregate) As described above, in the concrete block of the present invention, connected voids that are extremely effective for plant growth are formed with a suitable porosity and void size. It is necessary to contain a specified amount of coarse aggregate in a certain size range. That is, the concrete block of the present invention needs to contain the coarse aggregate having a size of 8 to 18 mm in an amount of 80% by weight or more based on the whole aggregate.
When the content is less than 80% by weight, it is difficult to obtain a communicating void effective for plant growth. Preferably, it is 85 to 100% by weight.
【００１１】また、８〜１８mmの寸法の粗骨材が、骨材
全体に対して８０重量％以上であることに加え、１０〜
１５mmの寸法の粗骨材が、骨材全体に対して７０重量％
以上であることが好ましく、このようにすると、得られ
るコンクリートブロックの強度が増加する。[0011] In addition to the fact that the coarse aggregate having a size of 8 to 18 mm accounts for 80% by weight or more of the whole aggregate,
70% by weight of coarse aggregate of 15mm in size
It is preferable that the above is satisfied. In this case, the strength of the obtained concrete block increases.
【００１２】さらに、２０〜２５mmの寸法の粗骨材が、
骨材全体に対して５重量％以下、且つ５mm以下の寸法の
骨材が５重量％以下であるのが好ましい。２０〜２５mm
の寸法の粗骨材が、骨材全体に対して５重量％を超えて
存在した場合、コンクリートブロック成形後に破損する
恐れがあり、また５mm以下の寸法の骨材が５重量％を超
えると、空隙のサイズが小さくなりすぎる場合があり好
ましくない。骨材の最大寸法は２５mm以下であることが
望ましい。Further, coarse aggregate having a size of 20 to 25 mm is
It is preferable that the aggregate having a size of 5% by weight or less and 5mm or less with respect to the whole aggregate is 5% by weight or less. 20-25mm
If the coarse aggregate having the size of more than 5% by weight with respect to the whole aggregate is present, there is a risk of breaking after concrete block molding, and if the aggregate having a size of 5 mm or less exceeds 5% by weight, The size of the void may be too small, which is not preferable. The maximum size of the aggregate is desirably 25 mm or less.
【００１３】なお、骨材の種類は通常使用されているも
のでよく、とくに限定するものではないが、例えば砕石
粗骨材や、スラグ粗骨材等を使用することができる。The type of aggregate may be a commonly used type, and is not particularly limited. For example, coarse crushed stone aggregate, slag coarse aggregate, or the like can be used.
【００１４】（セメント）本発明に使用できるセメント
の種類は、とくに制限するものではないが、例えば、普
通ポルトランドセメント、早強ポルトランドセメント等
が挙げられる。(Cement) The type of cement that can be used in the present invention is not particularly limited, and examples thereof include ordinary Portland cement and early-strength Portland cement.
【００１５】（水／セメント比）本発明においては、水
／セメント比は、例えば２０〜２５％の範囲に設定する
ことができる。(Water / Cement Ratio) In the present invention, the water / cement ratio can be set, for example, in the range of 20 to 25%.
【００１６】（本発明のコンクリートブロックの製造方
法）本発明のコンクリートブロックは、いかなる方法に
よっても製造することができるが、例えばプレキャスト
法により製造することができる。すなわち、上記のよう
な特定の寸法の骨材、セメント、水、さらに必要に応じ
て各種混和材（剤）を配合し混合し、所要の型枠に入
れ、加圧振動により締め固めて硬化させると、骨材はセ
メントを介して点状に連結され、結果として連続空隙を
有するコンクリートブロックが得られる。なおここでブ
ロックとは、本発明のコンクリートブロックを敷設する
場所に応じて、その形状を多様に変化させることがで
き、例えば立方体、直方体のものだけではなく、相対す
る二面が平行に傾斜したもの、相じゃくり構造、その他
異形のものであってもよい。(Method of Manufacturing Concrete Block of the Present Invention) The concrete block of the present invention can be manufactured by any method, for example, by a precast method. That is, an aggregate of a specific size as described above, cement, water, and various admixtures (agents) are blended and mixed if necessary, put into a required formwork, compacted by pressure vibration, and cured. Then, the aggregate is connected in a point-like manner via cement, and as a result, a concrete block having continuous voids is obtained. In addition, the block here can be variously changed in shape according to the place where the concrete block of the present invention is laid, for example, not only a cube, a rectangular parallelepiped, but also two opposite surfaces inclined in parallel. It may be an object, a phased structure, or another irregular shape.
【００１７】このようにして得られた本発明のコンクリ
ートブロックは、その表面に植物を繁茂させ緑化するの
に好適なものである。すなわち、本発明のコンクリート
ブロックは、培養土壌材の充填を容易にし、さらに植物
の根の拡大に有効である連通した空隙を有している。本
発明のコンクリートブロックにおける空隙は、空隙率と
して、２５〜３５％、好ましくは２８〜３２％であるの
がよい。なお、ここで空隙率とは、次式により定義され
るものである。The concrete block of the present invention thus obtained is suitable for growing plants on the surface and greening. That is, the concrete block of the present invention has communicating voids that facilitate filling of the culture soil material and are effective for expanding the roots of plants. The voids in the concrete block of the present invention have a porosity of 25 to 35%, preferably 28 to 32%. Here, the porosity is defined by the following equation.
【００１８】[0018]
【数１】（１−コンクリートブロックの固体容積／コン
クリートブロックの外形の見かけの容積）×１００
（％）## EQU1 ## (1-solid volume of concrete block / apparent volume of concrete block) × 100
(%)
【００１９】本発明のコンクリートブロックは、その強
度も良好であり、通常、圧縮強度１００kgｆ／cm2以
上、曲げ強度も１５kgf／cm2以上を有する。The concrete block of the present invention has good strength, and usually has a compressive strength of 100 kgf / cm 2 or more and a bending strength of 15 kgf / cm 2 or more.
【００２０】本発明のコンクリートブロックの空隙に充
填される培養土壌材は、例えば土壌、パーライト等の土
壌改良剤、植物肥料を混合し、さらに植物種子を混合し
たもので、通気性、吸水性および保水性を有するものが
好ましい。この培養土壌材は、ペースト状にしたもの、
あるいは乾燥したもののいずれでもよい。前者の場合に
は、植物の種子を混入したペースト状の土を例えば振動
台上に固定した型枠に入れ、そのペースト状の土層の上
にコンクリートブロックをおいて振動を加えると、コン
クリートブロックはその自重によって徐々に沈み、その
沈降過程でコンクリートブロック内の空隙にペースト状
の土が充填される。その場合コンクリートブロックをあ
らかじめ濡らしておくと、土の充填作用はより一層円滑
となる。一方、後者の場合には、充填を容易にするため
に、あらかじめ乾燥しておいたコンクリートブロックを
例えば振動台上に固定し、振動を加えながら植物の種子
を混入した粉砕乾燥土を上から散布すると、コンクリー
トブロック内の空隙に乾燥土が充填される。このように
してコンクリートブロックの空隙の中に培養土壌材とと
もに植物の種子を入れた後、若干の散水を行い一定期間
放置しておけば、種子は発芽し、コンクリートブロック
内の連通した空隙に充填された土に根を張って成長し、
コンクリートブロックの表面全体が植物で一様に覆われ
ることになる。The culture soil material to be filled in the voids of the concrete block of the present invention is obtained by mixing a soil conditioner such as soil and perlite, a plant fertilizer, and a plant seed, and has a permeability, a water absorption and Those having water retention are preferred. This culture soil material is in the form of paste,
Alternatively, any of dried ones may be used. In the former case, the paste-like soil mixed with the seeds of the plant is placed in a formwork fixed on a shaking table, for example, and a concrete block is placed on the paste-like soil layer and vibrated. Gradually sinks due to its own weight, and during the settling process, the voids in the concrete block are filled with paste-like soil. In that case, if the concrete block is wetted in advance, the soil filling action becomes even smoother. On the other hand, in the latter case, in order to facilitate filling, a pre-dried concrete block is fixed on a shaking table, for example, and crushed and dried soil mixed with plant seeds is applied from above while applying vibration. Then, the dry soil is filled in the voids in the concrete block. After putting the seeds of the plant together with the culture soil material into the voids of the concrete block in this way, if the water is slightly sprinkled and left for a certain period of time, the seeds germinate and fill the open voids in the concrete block. Rooted in the soil that has been grown,
The entire surface of the concrete block will be uniformly covered with plants.
【００２１】[0021]
【作用】本発明によれば、一定の寸法範囲の粗骨材を規
定量含有させることにより、植物の生長に極めて有効で
ある連通した空隙が、好適な空隙率および空隙サイズで
もってコンクリートブロックに形成される。特開昭第５
３−１１４２０４号公報に開示された方法は、骨材の寸
法を規定しておらず、このような効果が奏されない。According to the present invention, by including a specified amount of coarse aggregate in a certain size range, open cavities that are extremely effective for plant growth can be formed into concrete blocks with a suitable porosity and pore size. It is formed. JP-A-5
The method disclosed in Japanese Unexamined Patent Publication No. 3-114204 does not specify the size of the aggregate, and does not provide such an effect.
【００２２】[0022]
【実施例】以下、本発明を実施例により説明する。本発
明のコンクリートブロックの製造のために、次の原料を
用いた。 骨材：岩瀬町産砕石。 セメント：普通ポルトランドセメント（秩父小野田株式
会社製）。 混和剤：マイテイ１５０（花王（株）製）。 水／セメント比：２５％。The present invention will be described below with reference to examples. The following raw materials were used for manufacturing the concrete block of the present invention. Aggregate: crushed stone from Iwase-cho. Cement: ordinary Portland cement (made by Chichibu Onoda Co., Ltd.). Admixture: Mighty 150 (manufactured by Kao Corporation). Water / cement ratio: 25%.
【００２３】実施例１〜４ 表１に示される寸法割合の骨材１４８０kg（コンクリー
ト１m3当たり、以下同じ）、セメント２５０kg、混和剤
１.５kgおよび水を混練りし、得られた混練物を型枠に
打設し、硬化後、１４日間養生させて、図１に示すよう
なコンクリートブロック１を１００個製造した。このコ
ンクリートブロック１のサイズは、縦４００mm×横４０
０mm×厚さ１００mmであり、セメントにより固定された
骨材３の間に、植物の生長に極めて有効な連通した空隙
２を有していた。得られたコンクリートブロックの圧縮
強度および曲げ強度は、それぞれ１００kgf／cm2以上お
よび１５kgf／cm2以上であった。次に、コンクリートブ
ロック１の空隙率、不良率および充填性を評価した。得
られた結果を表１に示す。なお不良率とは、コンクリー
トブロックの脱型時および成形後に、骨材が剥がれ落ち
たブロックの個数を、ブロック製造総数（１００個）で
割った百分率である。また充填性とは、成形したコンク
リートブロックの空隙１リットルあたりに培養土壌材が
充填された量の平均である。培養土壌材の充填は、あら
かじめ乾燥しておいたコンクリートブロックを振動台上
に固定し、振動を加えながら培養土壌材を上から散布す
ることにより行った。また、培養土壌材の充填は、２回
に分けて行い、初めに培養土壌材のみを充填し、次に種
子を混入した培養土壌材を充填した。なお、空隙の容積
は、次式を用いて算出される。 Examples 1 to 4 1480 kg of aggregate having the dimensions shown in Table 1 (1 m 3 of concrete, the same applies hereinafter), 250 kg of cement, 1.5 kg of admixture and water were kneaded, and the obtained kneaded material was mixed. After being poured into a mold and cured, it was cured for 14 days to produce 100 concrete blocks 1 as shown in FIG. The size of this concrete block 1 is 400mm in height x 40 in width.
It was 0 mm × 100 mm thick and had communicating voids 2 between the aggregates 3 fixed by cement, which were extremely effective for plant growth. The compressive strength and the bending strength of the obtained concrete block were 100 kgf / cm 2 or more and 15 kgf / cm 2 or more, respectively. Next, the porosity, the defective rate, and the filling property of the concrete block 1 were evaluated. Table 1 shows the obtained results. Note that the defective rate is a percentage obtained by dividing the number of blocks from which the aggregate has peeled off at the time of demolding and molding of the concrete block by the total number of blocks manufactured (100). The filling property is an average of the amount of the culture soil material filled per liter of the void of the molded concrete block. The culture soil material was filled by fixing a previously dried concrete block on a shaking table and spraying the culture soil material from above while applying vibration. The filling of the culture soil material was performed twice, first, only the culture soil material was filled, and then the culture soil material mixed with seeds was filled. Note that the volume of the gap is calculated using the following equation.
【００２４】[0024]
【数２】コンクリートブロックの外形の見かけの容積×
空隙率（％）／１００[Formula 2] Apparent volume of concrete block outer shape ×
Porosity (%) / 100
【００２５】培養土壌材の組成は、黒土９０％、パーラ
イト９.７％、肥料０.３％とし、乾燥し、粉砕したもの
を用い、植物の種子は芝とした。このコンクリートブロ
ックは、地表に設置してかん水を行ったところ、３０日
でその表面全体に均一に芝が良好に生長した。芝の生長
には、０.４７kg／リットルの充填性が必要である。The composition of the culture soil material was black soil 90%, perlite 9.7%, fertilizer 0.3%, dried and pulverized, and the plant seeds were turf. When the concrete block was placed on the surface of the ground and watered, the turf grew uniformly over the entire surface in 30 days. Turf growth requires a fillability of 0.47 kg / liter.
【００２６】比較例１〜３ 骨材の寸法が５mm以下のもの１０重量％および／または
２０〜２５mmのもの１０重量％使用したこと以外は、実
施例１〜４を繰り返し、コンクリートブロックを製造
し、その性能を評価した。得られた結果を表２に示す。 Comparative Examples 1 to 3 Examples 1 to 4 were repeated except that 10% by weight of aggregate having a size of 5 mm or less and / or 10% by weight of aggregate having a size of 20 to 25 mm was used to produce concrete blocks. And evaluated its performance. Table 2 shows the obtained results.
【００２７】[0027]
【表１】 [Table 1]
【００２８】[0028]
【表２】 [Table 2]
【００２９】[0029]
【発明の効果】本発明によれば、植物の生長に極めて有
効である連通した空隙が、好適な空隙率および空隙サイ
ズでもって形成されているコンクリートブロックおよび
その緑化方法が提供される。According to the present invention, there is provided a concrete block in which connected voids extremely effective for plant growth are formed with a suitable porosity and void size, and a method for greening the concrete block.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明のコンクリートブロックの一例を示す斜
視図である。FIG. 1 is a perspective view showing an example of a concrete block according to the present invention.
１ コンクリートブロック ２ 空隙 ３ 骨材 1 concrete block 2 void 3 aggregate
フロントページの続き (56)参考文献 特開 平７−315904（ＪＰ，Ａ) 特開 平７−315903（ＪＰ，Ａ) 特開 平４−295038（ＪＰ，Ａ) 特開 平８−143382（ＪＰ，Ａ) 特開 平８−118327（ＪＰ，Ａ) 特開 平５−117059（ＪＰ，Ａ) 特開 昭53−114204（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) C04B 28/00 - 28/36 C04B 14/00 - 20/12Continuation of front page (56) References JP-A-7-315904 (JP, A) JP-A-7-315903 (JP, A) JP-A-4-295038 (JP, A) JP-A-8-143382 (JP) JP-A-8-118327 (JP, A) JP-A-5-117059 (JP, A) JP-A-53-114204 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB Name) C04B 28/00-28/36 C04B 14/00-20/12
Claims (3)
配合し硬化させてなる空隙率２５〜３５％の連続した空
隙を有するコンクリートブロックにおいて、該骨材の８
０重量％以上が８〜１８mmの範囲内の寸法を有する粗骨
材であり、および２０〜２５mmの寸法を有する粗骨材が
５重量％以下であり、且つ５mm以下の寸法を有する骨材
が５重量％以下であることを特徴とする、コンクリート
ブロック。1. A concrete block having continuous voids having a porosity of 25 to 35%, which is obtained by mixing and hardening an aggregate, cement and water as main raw materials.
0% by weight or more is coarse aggregate having a size in the range of 8 to 18 mm, and coarse aggregate having a size of 20 to 25 mm is 5% by weight or less and aggregate having a size of 5 mm or less. Concrete block characterized by being 5% by weight or less.
範囲内の寸法を有する粗骨材である、請求項１に記載の
コンクリートブロック。2. The concrete block according to claim 1, wherein at least 70% by weight of the aggregate is coarse aggregate having a size in the range of 10 to 15 mm.
ブロックの空隙内に、植物の種子および培養土壌材を充
填し、該種子を発芽させ生長させることを特徴とする、
コンクリートブロックの緑化方法。3. A method according to claim 1, wherein the concrete block according to claim 1 or 2 is filled with a plant seed and a culture soil material, and the seed is germinated and grown.
Greening method of concrete block.