JP2706295B2 - Painting for support - Google Patents

Painting for support

Info

Publication number
JP2706295B2
JP2706295B2 JP1022588A JP2258889A JP2706295B2 JP 2706295 B2 JP2706295 B2 JP 2706295B2 JP 1022588 A JP1022588 A JP 1022588A JP 2258889 A JP2258889 A JP 2258889A JP 2706295 B2 JP2706295 B2 JP 2706295B2
Authority
JP
Japan
Prior art keywords
alloy
painting
surface
copper
metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP1022588A
Other languages
Japanese (ja)
Other versions
JPH02204099A (en
Inventor
青史 小作
正博 辻
Original Assignee
青史 小作
日鉱金属株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 青史 小作, 日鉱金属株式会社 filed Critical 青史 小作
Priority to JP1022588A priority Critical patent/JP2706295B2/en
Publication of JPH02204099A publication Critical patent/JPH02204099A/en
Application granted granted Critical
Publication of JP2706295B2 publication Critical patent/JP2706295B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Description

【発明の詳細な説明】 〔産業上の利用分野〕 この出願の発明は、油絵や日本画等を描くときに使用する銅箔を基底材とした絵画用支持体に関する。 DETAILED DESCRIPTION OF THE INVENTION [relates to] the invention of the present application relates to a painting support for the copper foil to be used was a base material when drawing the oil painting and Japanese painting and the like.

〔従来の技術及び発明が解決しようとする課題〕 [Challenge BACKGROUND OF INVENTION Problems to be Solved]

通常油絵を描く場合、木枠に張った麻製のキャンバス(画布)が使用されている。 If you draw a normal oil, hemp made of canvas stretched on a wooden frame (canvas) is used. このキャンバスの材料は木綿製のものもあるし、また板や石などにも描いてはいけないという制約があるわけでもないので、ベニヤ板に描き上げて展覧会等に出品する例も多く見かけられる。 To the canvas of the material it is also made of cotton, also because there is nor a constraint that should not be painted, such as the plate or stone, an example of an exhibition in the exhibition, such as raising draw in plywood is also apparent many.

しかしながら、多くは布製のキャンバスが用いられている。 However, many of the fabric of the canvas is used. それは布には生地目があり、絵具ののりが良く、 It has the dough first is the cloth, good glue paint,
比較的書いた時の絵具の置き具合が良いという長所があるためと考えられる。 Place the degree of paint at the time of relatively writing is considered to be because there is an advantage in that good.

油絵は明治時代に西洋から導入されたものであるが、 Although oil painting is one that has been introduced from the West during the Meiji era,
簡単に言えばヤニ分で絵具を固めたものと言える。 In a nutshell it can be said that hardened paint in the tar content.

画用液として、水彩画は水で日本画はニカワで溶くように、油絵(油彩画)は油が非常に大切な役割をもっている。 As an image for the solution, watercolor Japanese painting with water to dissolve in the glue, oil painting (oil painting) oil has a very important role.

この油は大きく分けると油絵具をそれぞれの技法に合わせて溶く役目の溶き油と、絵そのものに油絵本来のつやを与える役目の油と、また絵を大切に保存するための油とがある。 The oil is there and beaten oil role solving the combined oil paint in each of the technique roughly divided into, and the oil of the role that gives the oil painting original luster to the picture itself, also the oil in order to carefully save the picture.

通常、市販されている油絵具自体はすでに使いやすいように練りあげられている。 Usually, have raised the batter so easy to use oil paint itself is already on the market.

油絵を簡単に紹介すると上記のようなことであるが、 Referring briefly to introduce the oil painting but is that as described above,
他方日本画の方は従来、麻紙に顔料をしみ込ませ、多くは巻き物として保存しておくことが多かった。 Conventionally, those of the other Japanese painting, the pigment soaked in hemp paper, was often many stored as scroll. このため巻回することのできないほど絵具を厚くぬることはできなかった。 For this reason it was not possible to slather the paint as that can not be wound.

しかしながら、上記の油絵が普及するに従い、日本画も額に入れるようになり、絵具を厚くする傾向に変ってきている。 However, according to the above oil is spread, Japanese painting also becomes to put on the forehead, it has been turned into a tendency to increase the thickness of the paint. すなわち、麻紙の上に「どうさ」(ニカワ) In other words, "How Is the" on top of the hemp paper (glue)
を塗って絵具がしみ込まないようにし、その上に絵具を厚く盛り上げるように変ってきたのである。 The paint as paint is not soaked, it had been turned into as liven up increasing the thickness of the paint on it. このため日本画独自の画法と並行して油絵的な日本画も発生した。 For this reason oil painting specific Japanese painting in parallel with the Japanese painting your own picture method is also generated.

このように油絵や日本画から出発した種々の技法を発達せしめ、すぐれた絵画が数多く生まれることとなったが、作成された絵画に非常に大きな問題を有している。 In this way it allowed to develop a variety of techniques, starting from oil painting and Japanese painting, but became that good painting is born many, has a very big problem in the paintings that have been created.

それは、絵画のひび割れ(クラック)であり、場合によっては剥落の危険すらある。 It is the painting of cracks (cracks), and in some cases even the risk of flaking. 特に乾湿のはげしい日本では気候の変動でよりもろくなり、破損し易すい状況にあると言える。 In particular, become more brittle in the change of climate in the wet and dry vigorous Japan, it can be said that there is damage to ease crowded conditions.

乾燥し安定した気候である西欧においてすらも過去の有名絵画に、近づいて観察すると無数のひび割れが見られる。 In a dry stable the past of famous paintings even in Western Europe is a climate, a myriad of cracks can be seen and approached to observe. ひび割れにごみがたまって製作時における鮮烈な絵画が維持できず長年のうちに絵画が変質してくるのみならず、剥落による絵画の消失になるおそれもあり、無念の情を禁じ得ない人も多いと思われる。 Cracks in not only painting in one of the many years can not be vivid paintings maintenance at the time of manufacture accumulated dust comes altered, there is also in you being in the disappearance of paintings by flaking, many people that can not prohibit the chagrin of information I think that the.

このような絵画のひび割れは絵画や地塗りなども原因するところもあるが、キャンパスなどの基底材の乾湿の変化や温度変化による伸縮が原因となるところが大きい。 Although cracks of such paintings is also the place to cause as well, such as paintings and earth fill, largely expansion and contraction caused by dry and wet changes and temperature changes in the base material, such as a campus cause.

上記のような絵画におけるひび割れは、厚塗りをする絵画のみならず、油絵的傾向をもつ日本画などにもみられている。 Cracks in the painting, such as described above, not only painting a thick coating, has also been seen in such as Japanese painting with oil painting trends.

このような問題をかかえながら、高級絵画においてはそれを保有するために、修復のための研究すら行われているのが実情である。 While suffering such problems, because in the fine painting carrying it, a reality is even being done research for repair. また、古い絵画においては金属板、特に腐食に強い銅板が基底材として用いられたことがある。 Further, there is a metal plate, in particular a strong copper corrosion was used as the base material in the old paintings.

これは主として宗教改革後、カトリック側が新世界への布教の地を求めて宣教師たちを送り出すと同時に、聖像を銅板に描いた油彩画を携帯させたものである。 After this is mainly the Reformation, and at the same time sending out missionaries Catholic side in search of the land of the missionary to the New World, it is obtained by carrying the oil paintings depicting the Kiyoshizo to the copper plate.

これは板より軽く、かさがなく、布よりもはるかに剥落やひび割れの心配がなく、また多少の雨や、熱にも強いという特徴があったためと考えられる。 It is lighter than the plate, there is no umbrella, there is no fear of much flaking and cracking than the cloth, also is considered to be because there was a little rain and, characterized by strong even in the heat.

しかしながら、銅そのものが高価であり、平面さを得ることができず、また絵画ののりが悪く、非常に特殊な技法でのみ製作が可能であったために、18世紀以降殆ど姿をみせなくなり現在に至っている。 However, it is expensive copper itself, it is not possible to obtain a plane is, also bad paintings of glue, because it was can only be produced in a very special technique, hardly show up the 18th century and later becomes the current It has come.

〔課題を解決するための手段〕 [Means for Solving the Problems]

以上のような絵画用支持体の問題を解決するために、 In order to solve the problem of more of such paintings for support,
本発明者らは金属板に着目し改善を試みた。 The present inventors have tried to improve focus on a metal plate. すなわち、 That is,
ひび割れ防止に有効であり、その他虫、環境等による腐食の問題もなく、下塗りしなくてよい。 Is effective in preventing cracks, and other insects, without corrosion problems caused by environment, it may not be primed. 又形も自由に塑性加工でき強度も強いという長所がある事から金属板に着目した。 Matakatachi was also focused on the metal plate from the fact that there is an advantage of strong free plastic working can strength. そして、唯一の欠点である絵具の密着性、のりの悪さの改善を行ったものである。 Then, the adhesion of paint is the only drawback, is having been subjected to the improvement of the evil of the glue. すなわち、銅または銅合金製基底材の表面に、バフ研磨,ショットブラスト加工,エンボス加工,重ね圧延加工,ダル加工のいずれか1種以上の機械的処理によって得られる機械的凹凸が設けられ、かつその凹凸表面は圧潰された圧延面を形造り、さらにその圧延表面には銅もしくは銅合金,錫もしくは錫合金,インジウムもしくはインジウム合金,亜鉛もしくは亜鉛合金,クロムもしくはクロム合金,ニッケルもしくはニッケル合金,鉄もしくは鉄合金,コバルトもしくはコバルト合金および、上記各金属の酸化物または上記各金属と前記酸化物との複合物のうちから選ばれる少なくとも一種以上のものからなる表面被覆層によって覆われ、そして、この基底材の裏面は、麻,木綿, That is, the surface of the copper or copper alloy base material, buffing, shot blasting, embossing, superimposed rolling, mechanical irregularities obtained by mechanical treatment of any one or more dull machining provided, and its uneven surface shape building the crushed rolled surface, further copper or copper alloy on its rolling surface, a tin or tin alloy, indium or an indium alloy, zinc or zinc alloy, chromium or chromium alloys, nickel or nickel alloys, iron or iron alloy, cobalt or cobalt alloys and covered by a surface coating layer composed of at least one or more of those selected from among the composite of the oxide or the respective metal and the oxide of the metal, and this the rear surface of the base material, hemp, cotton,
ベニヤ,木材板,紙,石膏,樹脂およびタイルのいずれか一種の裏材が設けられていることを特徴とする絵画用支持体を提供するものである。 Veneer, there is provided timber board, paper, plaster, painting a support, wherein the backing of any one resin and tiles are provided.

これによって絵画がひび割れや剥離することを抑制し、絵画製作当時の鮮烈さを維持するとともに、絵具ののりを良好にし、密着性を高め安定した品質の保持可能とするものである。 This suppresses that the painting is cracking and peeling, while maintaining vivid of painting manufacturing time and improving the glue paints, that are likely retain adhesion enhanced with stable quality.

〔発明の具体的説明〕 [DETAILED DESCRIPTION OF THE INVENTION

金属製の基底材を使用することは、乾湿や温度変化によるひび割れや剥落を防止する大きな役割をになうのであるが、この場合の大きな欠点である絵具の密着性、のりの良さを改善することは極めて重要なことであり、この出願の発明の金属において初めて達成されたものである。 The use of metallic base material, although the play a major role to prevent cracking and spalling due dry and wet and temperature changes, the adhesion of the paint is a major disadvantage in this case, to improve the goodness of glue it is a very important, but for the first time achieved in the metal of the invention of this application.

すなわち、金属製基底材の表面に機械的凹凸をつけることにより、絵具ののりや密着性が著しく向上するものであり、特に、バフ等による研摩や、ショットブラスト、エンボス加工、ダルロールによる圧延、重ね圧延による重ね面などが、量産性もあり極めて有効である。 That is, by attaching a mechanical irregularities on the surface of the metal base material, which glue or adhesion paint is remarkably improved, in particular, grinding or by buffing or the like, shot blasting, embossing, rolling by dull, overlapping such overlapped surface by rolling, also mass productivity is very effective. さらに機械的凹凸をつけたものの表面をさらに圧延して押し潰した圧延面は、第1図(ロ)に示すような表面になるため、密着性はさらに改善される。 Rolling surfaces crushed further rolling surface but still gave a mechanical irregularities, since the surface as shown in FIG. 1 (b), the adhesion is further improved. また、機械的凹凸をつけた表面に各種被覆層を施すことにより、被覆層の電着粒子が凸部に集中し、さらに凹凸を強調するとともに、絵具の密着性も向上する。 Further, by applying various coating layers on the surface wearing mechanical irregularities, electrodeposition particles of the coating layer is concentrated on the convex portion, further with emphasis irregularities, also improve the adhesion of the paint.

金属の種類としてはあらゆるものが適用できるが、特に銅及び銅合金の場合、微生物等に対する殺菌作用があり、保存という観点から極めて優れた材料であるといえる。 Although the kind of metal can be applied and all things, especially in the case of copper and copper alloys, there is a bactericidal action against microorganisms, it can be said that an extremely excellent material from the viewpoint of storage.

さらにこれらの工程の後、キャンバス等の絵画用支持体の使用時に、手で引剥しできる保護シートを被覆することができる。 Further After these steps, when using the painting support of the canvas or the like, can be coated with a protective sheet which can then peel by hand. この保護シートは手の脂等が金属のつかないように汚染防止の役目をもっている。 The protective sheet butter, and the like of the hand has a role of pollution not to tell of the metal.

このようにして得られた金属製基底材は在来の木や布と比較するとさらにいくつかの長所をもっている。 The thus obtained metal base material has a few more advantages when compared to conventional wood and cloth. それは、絵具の密着性を保有していると同時に平坦性に優れ、なめらかであり、気孔や表面の起伏を地塗りで充填する必要もないことである(もちろん地塗りをすることはさしつかえなく、本願発明はこれを包含している。)。 It is excellent at the same time the flatness of as having adhesion paint is smooth, that there is no need to fill the undulations of the pores and the surface in the land fill (of course possible to the ground coat is not permissible, the present invention encompasses this.). そして金属の色調や被覆材の色調は同時に下塗りとして使用することもできるからである。 The color tone of the metal color and dressing because it may be used as a primer simultaneously. 金属材料の選択により赤、白、シルバー色、さらに黄銅色から黄金色、黒色、茶褐色まで多種多様に変えることができる。 Red by the selection of the metal material, white, silver color, and even golden color from the brass color, black color, it is possible to change a wide variety until brown.

さらに、強度があるとともに、塑性加工できるため自由な形に加工できる長所を持ち合わせている。 Furthermore, with certain strength, and ready the advantage that can be processed into free form since it plastic working.

裏材には麻、木綿などの従来のキャンバス材の他、ベニヤ、木材板、紙、石膏、樹脂、タイルなどが使用できる。 Hemp the backing, other conventional canvas material such as cotton, veneer, wood board, paper, plaster, resin, etc. tiles can be used. また、裏材を用いず使用することもできる。 It is also possible to use without a backing.

これは絵画人の好みによって選択できるが、金属を用いた特徴は失われることがない。 While this can be selected by the painting's favorite feature is not lost using metal.

また、金属製基底材としてカッター等で簡単に切断できる薄板を用いる事により、キャンバス・ボード、ピンナップ、さらには壁画用支持体とすることができる。 Further, by using a thin plate that can be easily cut with a cutter or the like as a metal base material, canvas board, pinup, further can be a mural support. またこれらは、一般建造物への接着が可能であるから内装、外装品、ドア、棚などのインテリア品として使用できるとともに、交換や保管も容易にできるという特徴を有している。 They are also, since it is possible to adhere to the general building interior, exterior parts, doors, has a feature that it is possible to use as an interior article, such as a shelf, exchange and storage can be easily performed.

キャンバスとする場合には、適度な強度と弾力性を保有しているので、布などの裏材を張り合わせて木枠に緊張させ、絵筆をキャンバス地にあてたときに感じられる心地よい弾力を感じとることができる。 In the case of the canvas, because it holds a moderate strength and elasticity, by laminating the backing, such as a cloth to tension in the wood frame, comfortable resilient feel the feel that when you rely on the paintbrush to canvas can.

なお、ここでいう絵画用とは、商業用としてレタリング、ポスター、イラストレーション、レイアウトといったグラフィックデザインを包含するものである。 Here, and for the paintings say, it is intended to cover lettering, posters, illustration, graphic design, such as the layout as commercial.

絵としての手法は油彩画(油絵)、アクリルペイント画、日本画、パステル画、水墨画などに適しているが、 Technique as a picture is oil painting (oil), acrylic paint image, Japanese paintings, pastels, are suitable for such ink painting,
他の画法に適用することはなんらさしつかえない。 It is not in any way permissible to be applied to the other of the field method.

いずれも絵具との密着性に優れており、また、ひび割れの発生、剥離は大きく改善され、絵画の鮮烈さの維持と保存性に優れており、さらに絵筆のタッチに快感を強く与えるものである。 Both have excellent adhesion to the paint and the occurrence of cracking, peeling is significantly improved, and excellent in maintenance and storage of vivid of painting and gives further strong pleasure paintbrush touch .

〔発明の効果〕 〔Effect of the invention〕

以上で述べたように、本願発明の金属を基底材とすることにより、金属特有の色感を得、平坦性に優れ、あるいは故意に部分的に塑性加工させ立体感も出せるとともに、強度に優れしかも絵筆のタッチに優れた快感を得ることができ、また、保存、修復の観点から見ると半永久的に保存できるとともに、金属のもつ大きな欠点であった絵具との密着性を著しく改善したものであり、従来の絵画用支持体として極めて優れたものである。 As mentioned above, by a metal of the present invention as the base material, to give a feeling of metallic color specific, excellent flatness, or with partially plastically working put out even stereoscopic effect intentionally, excellent in strength Moreover it is possible to obtain an excellent pleasure paintbrush touch, also saved, it is possible to semi-permanently store from the standpoint of repair, which was significantly improved adhesion between the paint was a major drawback with the metal There, is very excellent as a conventional painting support.

しかも従来の絵画特にキャンバス使用において著しかったひび割れの発生を防ぐことができる著しい特性を有するものである。 Moreover those having a significant characteristic that can prevent the occurrence of remarkable was cracking in conventional painting especially canvas used.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

第1図は、機械的凹凸をつけた後、圧延を行った時の金属表面を示す概念図である。 The first figure after applying mechanical irregularities, is a conceptual view showing a metal surface when subjected to rolling. (イ):機械的凹凸をつけた金属表面 (ロ):圧延を行った後の金属表面 (B): metal surfaces with a mechanical irregularities (b): the metal surface after the rolling

Claims (1)

    (57)【特許請求の範囲】 (57) [the claims]
  1. 【請求項1】銅または銅合金製基底材の表面に、バフ研磨,ショットブラスト加工,エンボス加工,重ね圧延加工,ダル加工のいずれか1種以上の機械的処理によって得られる機械的凹凸が設けられ、かつその凹凸表面は圧潰された圧延面を形造り、さらにその圧延面の表面には銅もしくは銅合金,錫もしくは錫合金,インジウムもしくはインジウム合金,亜鉛もしくは亜鉛合金,クロムもしくはクロム合金,ニッケルもしくはニッケル合金,鉄もしくは鉄合金,コバルトもしくはコバルト合金および、上記各金属の酸化物または上記各金属と前記酸化物との複合物のうちから選ばれる少なくとも一種以上のものからなる表面被覆層によって覆われ、そして、この基底材の裏面は、麻,木綿,ベニヤ,木材板,紙,石膏, To 1. A copper or copper alloy surfaces made base material, buffing, shot blasting, embossing, superimposed rolling, mechanical irregularities obtained by any one or more mechanical processing Dar processing provided is, and the uneven surface shape building the crushed rolled surface, further that the rolled surface copper or copper alloy on the surface of the tin or tin alloy, indium or an indium alloy, zinc or zinc alloy, chromium or chromium alloys, nickel or nickel alloy, iron or iron alloys, cobalt or cobalt alloy and, covered by a surface coating layer composed of at least one or more of those selected from among the composite of the oxide or the respective metal and the oxide of each metal We, and the back surface of the base material, hemp, cotton, veneer, wood board, paper, plaster,
    樹脂およびタイルのいずれか一種の裏材が設けられていることを特徴とする絵画用支持体。 Painting for support, characterized in that the backing of any one resin and tiles are provided.
JP1022588A 1989-02-02 1989-02-02 Painting for support Expired - Lifetime JP2706295B2 (en)