JP2670940B2 - Lime-based hard hydrophobic thin coating material and thin wall coating method - Google Patents
Lime-based hard hydrophobic thin coating material and thin wall coating methodInfo
- Publication number
- JP2670940B2 JP2670940B2 JP4200499A JP20049992A JP2670940B2 JP 2670940 B2 JP2670940 B2 JP 2670940B2 JP 4200499 A JP4200499 A JP 4200499A JP 20049992 A JP20049992 A JP 20049992A JP 2670940 B2 JP2670940 B2 JP 2670940B2
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- lime
- wax emulsion
- thin
- based hard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、石灰系硬質疎水性薄塗
材と壁面薄塗装工法に係り、より詳細には、着色した塗
材であっても色相むらなく仕上げることができる石灰系
硬質疎水性薄塗材と壁面薄塗装工法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lime-based hard hydrophobic thin coating material and a wall thin coating method, and more specifically, a lime-based hard hydrophobic hydrophobic coating material that can finish even a colored coating material without uneven hue. Thin coating materials and wall thin coating method.
【０００２】[0002]
【従来の技術】近年、鉄筋コンクリート構造物において
は、工期の短縮と施工費の引き下げを図る目的で、厚塗
工法が減少し、塗材による薄塗工法が要望されている。
この薄塗工法は、通常、壁面の上に１〜２ｍｍの塗厚で
下地調整をすると共に、その上面に塗装をして仕上げる
ようにしている。2. Description of the Related Art In recent years, for reinforced concrete structures, the number of thick coating methods has decreased and a thin coating method using a coating material has been demanded for the purpose of shortening the construction period and reducing the construction cost.
In this thin coating method, a base is usually adjusted with a coating thickness of 1 to 2 mm on a wall surface, and the upper surface is coated to finish.
【０００３】しかし、この薄塗工法は、特に、塗料に着
色して鏝押さえして仕上げるのに高度な技術を必要と
し、かつ大きな壁面を色相むらなく仕上げるのが至難の
業であることより、熟練工に頼らざるを得ない。ところ
で、ここで用いる壁面仕上げ用の塗材としては、『粘
土、消石灰、石灰クリーム、セメントを単独若しくは二
種以上を混合した主材に、スサ、セメント混和用ポリマ
ーディスパージョンを混合した組成物』よりなる石灰系
塗材等が知られている。しかし、このような石灰系やシ
リカ系の塗材は、内壁用塗材として適しているものの外
壁用塗材としては使用できないという課題がある。However, this thin coating method requires a high level of technology to finish the coating by coloring the paint and troweling, and it is extremely difficult to finish a large wall surface with no hue unevenness. I have no choice but to rely on skilled workers. By the way, as a coating material for the wall surface used here, "composition in which clay, slaked lime, lime cream, a main material obtained by mixing cement alone or two or more kinds, and Susa, a polymer dispersion for admixing cement" are mixed A lime-based coating material and the like are known. However, although such a lime-based or silica-based coating material is suitable as a coating material for the inner wall, there is a problem that it cannot be used as a coating material for the outer wall.
【０００４】そこで、本発明者は、このような課題を解
決するために、この課題の起因について、研究・検討を
行った処、塗材中に、『スサ』を必要とすることに起因
することを究明した。すなわち、 『スサ』があるため、塗装表面を水洗いできず、
０．２〜５ｍｍ厚程度の薄塗塗材として適しない。 塗材が軟らかい状態の時は、光沢が出ない等、色相
むらが出来やすい。 連続して鏝押さえができない。 硬化後は、鏝押さえができない。 等の難点がある。そして、『スサ』を除いた塗材の場
合、クリーム状と塗材であることより、塗厚を０．２〜
０．５ｍｍで仕上げることが可能であり、その作業速度
を速くできるという利点を有する。Therefore, the present inventor has studied and investigated the cause of this problem in order to solve such a problem, and as a result, it requires "susa" in the coating material. I clarified that. In other words, because there is "Susa", the coated surface cannot be washed with water,
Not suitable as a thin coating material having a thickness of about 0.2 to 5 mm. When the coating material is in a soft state, uneven hue is likely to occur, such as lack of gloss. You cannot hold the iron in succession. After curing, the trowel cannot be pressed. There are difficulties such as. In the case of the coating material excluding "Susa", the coating thickness is 0.2-
It is possible to finish with 0.5 mm, which has the advantage that the working speed can be increased.
【０００５】[0005]
【発明が解決しようとする課題】しかし、この『スサ』
を除いた石灰系塗材の場合、次のような課題が残る。す
なわち、 塗材の収縮を吸収できないので、その強度性が低下
する。 ローラー掛けをするに際し、該ローラーに塗材が付
着し、その作業速度が遅くなる。 硬化時期と、鏝押さえ時期との区別が難しく、かつ
硬化後の鏝押さえができないため、色相むらや、鏝むら
の修正が難しい。 等の課題が残る。[Problems to be Solved by the Invention] However, this "Susa"
In the case of the lime-based coating material excluding the above, the following problems remain. That is, since the shrinkage of the coating material cannot be absorbed, its strength is reduced. When the roller is applied, the coating material adheres to the roller, which slows down the working speed. It is difficult to distinguish between the curing time and the trowel pressing time, and since the trowel pressing after curing cannot be performed, it is difficult to correct the uneven hue and the uneven trowel. And other issues remain.
【０００６】本発明は、上述した課題に対処して創作し
た方法であって、その目的とする処は、ローラーを簡単
に使用でき、着色した塗材であっても色相むらなく仕上
げることができ、かつ強度を低下させることがない石灰
系硬質疎水性薄塗材と壁面薄塗装工法を提供することに
ある。[0006] The present invention is a method created in response to the above-mentioned problems, and at its intended purpose, a roller can be easily used and even a colored coating material can be finished without uneven hue. In addition, it is to provide a lime-based hard hydrophobic thin coating material that does not reduce strength and a thin wall coating method.
【０００７】[0007]
【課題を解決するための手段】そして、上記課題を解決
するための手段としての本発明の石灰系硬質疎水性薄塗
材は、石灰クリームと消石灰と細骨材およびセメント混
和用ポリマーを含む主材に、カルナバワックスエマルジ
ョン，パラフィンワックスエマルジョン，パラフィンの
顆粒，低分子ポリエチレンまたはその誘導体のワックス
エマルジョン，植物油より選ばれる１または２以上のワ
ックスを配合した構成よりなる。The lime-based hard hydrophobic thin coating material of the present invention as a means for solving the above problems is a main material containing lime cream, slaked lime, fine aggregate and a polymer for admixing cement. , Carnauba wax emulsion, paraffin wax emulsion, paraffin granules, wax emulsion of low molecular weight polyethylene or its derivatives, and one or more waxes selected from vegetable oils.
【０００８】また、本発明の壁面薄塗装工法は、石灰ク
リームと消石灰と細骨材およびセメント混和用ポリマー
を含む主材に、カルナバワックスエマルジョン，パラフ
ィンワックスエマルジョン，パラフィンの顆粒，低分子
ポリエチレンまたはその誘導体のワックスエマルジョ
ン，植物油より選ばれる１または２以上のワックスを配
合した石灰系硬質疎水性薄塗材を壁面に、塗厚が０．２
〜５ｍｍとなるように塗布・整面し、該塗材が硬化後に
ペーパー等による研ぎ仕上げし、かつ前記ワックスを塗
面に滲出させるようにした構成よりなる。In the thin wall coating method of the present invention, the main material containing lime cream, slaked lime, fine aggregate and polymer for admixing cement, carnauba wax emulsion, paraffin wax emulsion, paraffin granules, low molecular weight polyethylene or the like. A lime-based hard hydrophobic thin coating material containing one or more waxes selected from derivative wax emulsions and vegetable oils, with a coating thickness of 0.2
The coating material is applied and surface-adjusted to be about 5 mm, and after the coating material is cured, it is polished and finished with paper or the like, and the wax is exuded onto the coating surface.
【０００９】[0009]
【作用】本発明の石灰系硬質疎水性薄塗材は、炭酸カル
シウム、寒水クレー、石粉等の細骨材を用いることで、
『スサ』の混入を不要にできると共に、塗材の収縮を止
め、その強度を増加させ得ることができ、かつ該『ス
サ』が不要であるので、薄塗材を形成できるように作用
する。また、塗材中に、カルナバワックスエマルジョ
ン，パラフィンワックスエマルジョン，パラフィンの顆
粒，低分子ポリエチレンまたはその誘導体のワックスエ
マルジョン，植物油より選ばれる１または２以上のワッ
クスを混合・配合し、また『スサ』を用いる場合と異な
り、分散状態が良好である細骨材を用いているので、塗
材の成分が均一状態であることから、経時的変化によっ
て、ブルーミング現象を生じさせ、その成分が、塗材か
ら均一に壁面に滲出するので、壁面がむらなく手触りの
良い疎水性塗材を得ることができ、かつ該壁面の水洗い
等の洗浄が可能となるという作用を有する。The lime-based hard hydrophobic thin coating material of the present invention uses fine aggregates such as calcium carbonate, cold water clay and stone powder,
The mixing of "susa" can be made unnecessary, the contraction of the coating material can be stopped and the strength thereof can be increased, and since the "susa" is not necessary, the thin coating material can be formed. Also, one or more waxes selected from carnauba wax emulsion, paraffin wax emulsion, paraffin granules, wax emulsion of low molecular weight polyethylene or its derivatives, and vegetable oil are mixed and blended in the coating material, and "Susa" is added. Different from when used
Therefore, since fine aggregate that is well dispersed is used,
Since the components of the material are in a uniform state , the blooming phenomenon occurs due to changes over time, and whether the component is a coating material
Since et uniformly exuded to the wall surface, has the effect of wall surface can get a good hydrophobic coating material having evenly hand touch, and it is possible to wash the washing or the like of the wall surface.
【００１０】また、本発明の壁面薄塗装工法は、細骨材
を用い、かつカルナバワックスエマルジョン，パラフィ
ンワックスエマルジョン，パラフィンの顆粒，低分子ポ
リエチレンまたはその誘導体のワックスエマルジョン，
植物油より選ばれる１または２以上のワックスを混合・
配合した石灰系硬質疎水性薄塗材を用い、該塗材を壁面
に、塗厚が０．２〜５ｍｍとなるように塗布・整面する
ので、また耐アルカリ性材が混入していることより、硬
化のための養生期間が不要となり、石膏ボード板上であ
っても塗布でき、かつ剥離しない硬度を有する薄塗工事
ができる。また、その硬化速度が早くなるため、硬化時
期と鏝押さえ時期の判断に左官工による差が少なくな
り、鏝むら等による傷を気にする必要がなくなることよ
り、該左官工によるペーパー処理等による研ぎ仕上げの
差を少なくできる。更に、『スサ』を用いる場合と異な
り、分散状態が良好である細骨材を用いているので、塗
材の成分が均一状態であることから、経時的変化によっ
て、ブルーミング現象を生じさせ、その成分が、塗材か
ら均一に壁面に滲出するので、壁面がむらなく手触りの
良い壁面を形成できる。 The thin wall coating method of the present invention uses fine aggregate and is a carnauba wax emulsion, paraffin wax emulsion, paraffin granule, wax emulsion of low molecular weight polyethylene or its derivative,
Mix one or more waxes selected from vegetable oils
A lime-based hard hydrophobic thin coating material that has been blended is used to coat and surface the coating material on the wall surface so that the coating thickness is 0.2 to 5 mm. Therefore, it is hardened because an alkali resistant material is mixed. A curing period is no longer required, and it is possible to apply even on a gypsum board plate, and it is possible to perform a thin coating work with a hardness that does not peel off. In addition, since the curing speed becomes faster, there is less difference between the plastering worker in the determination of the curing time and the trowel holding time, and it is not necessary to worry about scratches due to murat unevenness, etc. The difference in sharpening finish can be reduced. Furthermore, it is different from the case of using "Susa".
Therefore, since fine aggregate that is well dispersed is used,
Due to the uniform composition of the material,
Cause a blooming phenomenon, and whether the component is a coating material
Since it evenly exudes to the wall surface, the wall surface is even and smooth to the touch.
A good wall surface can be formed.
【００１１】[0011]
【実施例】以下、本発明を具体化した実施例について説
明する。本実施例の石灰系硬質疎水性薄塗材は、次の組
成よりなる。すなわち、 石灰クリーム １０リットル 炭酸カルシウム（細骨材） ３〜４リットル 消石灰 １〜５リットル 合成化学糊料 ７０〜１２０ｇ セメント混和用ポリマーディスパージョン １〜２リットル ポリエチレンワックスエマルジョン ０．３〜１リットル 着色剤 適量 分散剤 適量 消泡剤 適量 ここで、石灰クリームは、微粉末に調整した生石灰を、
沸化した石灰クリーム、又は従来の沸化法による石灰ク
リームの１リットルあたり１．３〜１．４ｋｇを用い、
また炭酸ガスの含有量は６％以内とすることが好まし
い。Embodiments of the present invention will be described below. The lime-based hard hydrophobic thin coating material of this example has the following composition. That is, lime cream 10 liters calcium carbonate (fine aggregate) 3-4 liters slaked lime 1-5 liters synthetic chemical paste 70-120 g polymer dispersion for cement admixture 1-2 liters polyethylene wax emulsion 0.3-1 liter colorant Proper amount Dispersant Proper amount Defoamer Proper amount Here, lime cream is quicklime adjusted to fine powder,
Using 1.3-1.4 kg per liter of boiled lime cream or lime cream from a conventional boil method,
The content of carbon dioxide gas is preferably within 6%.
【００１２】そして、この配合よりなる石灰系硬質疎水
性薄塗材の場合、石灰クリームと消石灰（水分吸収剤）
と細骨材およびセメント混和用ポリマーを含む主材に、
ポリエチレンワックスエマルジョンよりなるワックスエ
マルジョンを混合することによって、壁面に塗装した場
合、該ワックス分が、ブルーミング現象で、経時変化
（２ケ月以内）によって滲出して、手触りの良い疎水性
を付与できることが確認できる。In the case of a lime-based hard hydrophobic thin coating material having this composition, lime cream and slaked lime (water absorbent)
And the main material including fine aggregate and cement admixture polymer,
It was confirmed that when a wax emulsion consisting of polyethylene wax emulsion is applied to the wall surface, the wax content oozes due to a blooming phenomenon due to a change with time (within 2 months), and a hydrophobic property with a good touch can be imparted. it can.
【００１３】次に、本実施例の石灰系硬質疎水性薄塗材
を用いて、壁面に塗装する方法について説明する。本施
工方法は、概略すると、下地調整工程、塗材塗布工
程、整面工程、仕上げ工程、の三工程よりなる。Next, a method of coating the wall surface with the lime-based hard hydrophobic thin coating material of this embodiment will be described. This construction method is roughly composed of three steps: a base adjustment step, a coating material application step, a surface preparation step, and a finishing step.
【００１４】−下地調整工程− 本工程は、建築物の壁面がコンクリート壁面等よりなる
場合は、該壁面を平坦状に調整するためのコンクリート
不陸調整を行う工程である。従って、該調整の必要のな
い石膏ボード、ケイカル板、その他の壁面の場合には、
本工程を省略することができる。ところで、本実施例の
塗材は、種々の壁面に適用できる。-Substrate adjustment step-This step is a step for adjusting the concrete unevenness for adjusting the wall surface of the building to a flat shape when the wall surface of the building is a concrete wall surface or the like. Therefore, in the case of gypsum board, calcareous board, and other wall surfaces that do not require adjustment,
This step can be omitted. By the way, the coating material of this embodiment can be applied to various wall surfaces.
【００１５】−塗材塗布工程− 本工程は、前工程で、コンクリート不陸調整を行った壁
面に塗材を塗布する工程である。ここで、塗材は、その
塗厚を、０．１〜５ｍｍになるように、通常は、吹き付
けによって塗布するが、ハケにより塗布等してもよい。
ところで、ここで用いる塗材は、『スサ』を省き、炭酸
カルシウム、寒水クレー、石粉等の細骨材を混入するこ
とで、該塗材の収縮を止めるようにしている。そして、
『スサ』を省略し、該細骨材を混入することで、塗材の
強度を増すようにしている。ここで、塗材中の『消石
灰』の代わりに、ホワイトカーボンのような吸湿性の高
いものでＰＨが中性のものを用いてもよい。なお、該塗
材には、必要に応じて、海草糊、炭酸繊維、化学繊維等
の『スサ』を入れて使用してもよい。-Coating Material Applying Step-This step is a step of applying the coating material to the wall surface on which the concrete unevenness has been adjusted in the previous step. Here, the coating material is usually applied by spraying so that the coating thickness is 0.1 to 5 mm, but it may be applied by brushing or the like.
By the way, as for the coating material used here, “susa” is omitted, and fine aggregate such as calcium carbonate, cold water clay, stone powder or the like is mixed in to stop the contraction of the coating material. And
By omitting the “susa” and mixing the fine aggregate, the strength of the coating material is increased. Here, instead of “slaked lime” in the coating material, a material having a high hygroscopic property and a neutral pH, such as white carbon, may be used. If necessary, the coating material may be used by adding "sustain" such as seaweed paste, carbonic acid fiber, and chemical fiber.
【００１６】また、該塗材には、壁面を着色する場合、
その顔料としては、耐候性、耐アルカリ性に耐える顔料
を使用する。しかし、水性顔料で、ストレンマレイン
酸、およびメチルメタクリレートよりなるものを主材と
したものに、有機顔料、無機顔料を分散処理加工したも
のを使用してもよい。Further, in the case of coloring the wall surface of the coating material,
As the pigment, a pigment that withstands weather resistance and alkali resistance is used. However, an aqueous pigment mainly composed of strene maleic acid and methyl methacrylate and an organic pigment or an inorganic pigment subjected to a dispersion treatment may be used.
【００１７】−整面工程− 本工程は、前工程で塗材を塗布した壁面を、ローラーま
たは小凹凸のできる器具を使用して整面する工程であ
る。ここで、使用するローラーとしては、表面に螺旋
型、Ｖ型の溝を有するものが好ましく、この構成の場
合、ローラーに塗材が付き難いので、熟練者でなくても
正確で、かつ迅速に塗材を、一定の塗厚に配することか
できる。そして、本工程においては、通常、このローラ
ーを用いて、転圧し、塗材中に含まれる気泡を圧縮しな
がら小不陸も同時に整面する。なお、ローラーで、転圧
した直後に、鏝で軽く整面することが好ましい。そし
て、この整面方法を採用することで、壁面に凹凸を付け
る模様壁を容易に施工できる。-Surface-adjusting step-This step is a step of surface-adjusting the wall surface coated with the coating material in the previous step by using a roller or a device capable of making small irregularities. Here, as the roller to be used, one having a spiral or V-shaped groove on the surface is preferable, and in this structure, the coating material is hard to stick to the roller, so that even an unskilled person can accurately and quickly The coating material can be applied in a constant coating thickness. Then, in this step, normally, this roller is used to roll and compress the bubbles contained in the coating material to simultaneously level small irregularities. Immediately after rolling with a roller, it is preferable to lightly surface the surface with a trowel. Then, by adopting this surface-arranging method, it is possible to easily construct a pattern wall having unevenness on the wall surface.
【００１８】−仕上げ工程− 本工程は、前工程で、整面した塗材が硬化した後、該表
面を磨くことで、磨き壁を形成して、該壁面を仕上げる
工程である。磨き壁は、高度の左官技術を必要とする。
これは、塗材が硬化する時期と、鏝押さえ時期との判別
（見切り）が難しく、塗材があまり硬化しすぎると壁面
によれ等の小クラックが発生したり、該塗材が柔らかい
時は、光沢が出ない等色相むらができ、また連続して鏝
押さえをする必要があり、硬化後には鏝押さえができな
いということによる。-Finishing Step-This step is a step of finishing the wall surface by polishing the surface after the surface-treated coating material is cured in the previous step to form a polished wall. Polished walls require advanced plastering skills.
This is because it is difficult to discriminate between the time when the coating material hardens and the time when the trowel is pressed down. If the coating material hardens too much, small cracks such as due to wall surfaces may occur, or when the coating material is soft. The reason is that uneven hue such as lack of gloss is generated, and it is necessary to continuously hold down the trowel, and the trowel cannot be held after curing.
【００１９】しかし、本実施例の塗材を用いた場合、該
塗材には、『スサ』が混入されてなく、微粉末の骨材を
混入しているだけであるので、硬化時間を見計らい細め
のペーパーで磨くか、またはステンレス鏝、ビニール板
等で、塗面を擦ることで仕上げることができる。また、
必要に応じて、カルナウバワックスエマルジョン、ポリ
エチレンワックスエマルジョンを塗布して磨いた後、ポ
リシャで磨くことにより光沢をだすことができる。However, when the coating material of the present embodiment is used, the coating material is not mixed with "Susa" but only fine powder aggregate, so that the curing time can be estimated. It can be finished by polishing with a thin paper or rubbing the coated surface with a stainless trowel or vinyl plate. Also,
If necessary, a carnauba wax emulsion or a polyethylene wax emulsion is applied and polished, and then polished with polisher to give gloss.
【００２０】ところで、塗材には、カルナウバワックス
エマルジョン、ポリエチレンワックスエマルジョン等の
艶出し助剤を混入（通常、塗材量１０部に対して、０．
２〜０．６部程度混入）することで、塗布後、１週間〜
２ケ月位すると、該艶出し助剤が壁面の表面に滲出して
ワックス磨きしたような手触りの良い光沢のある壁面が
できる。By the way, the coating material is mixed with a glazing aid such as carnauba wax emulsion or polyethylene wax emulsion (usually 0.
By mixing about 2 to 0.6 parts), 1 week after application
After about two months, the glazing aid exudes to the surface of the wall surface, and a glossy wall surface with a smooth feel is obtained.
【００２１】そして、本実施例の施工法の場合、施工時
間を短縮でき、また着色壁、模様壁であっても、その色
相むらがなく、均一な色相に仕上げることができ、また
壁面に手触りの良い疎水性塗材を得ることができ、かつ
該壁面の水洗い等の洗浄が可能となるということが確認
できた。In the case of the construction method of this embodiment, the construction time can be shortened, and even a colored wall or a patterned wall can be finished in a uniform hue without unevenness in hue, and the wall surface can be touched. It was confirmed that a good hydrophobic coating material could be obtained and that the wall surface could be washed with water or the like.
【００２２】なお、本発明は、上述した実施例に限定さ
れるものでなく、本発明の要旨を変更しない範囲内で変
形実施できる構成、方法を含む。The present invention is not limited to the above-described embodiments, but includes configurations and methods that can be modified within the scope of the present invention.
【００２３】[0023]
【発明の効果】以上の説明より明らかなように、本発明
の石灰系硬質疎水性薄塗材によれば、炭酸カルシウム、
寒水クレー、石粉等の細骨材を用いることで、『スサ』
の混入を不要にできると共に、塗材の収縮を止め、その
強度を増加させ得ることができ、かつ該『スサ』が不要
であるので、薄塗材を形成でき、また塗材中に、カルナ
バワックスエマルジョン，パラフィンワックスエマルジ
ョン，パラフィンの顆粒，低分子ポリエチレンまたはそ
の誘導体のワックスエマルジョン，植物油より選ばれる
１または２以上のワックスを混合・配合し、また『ス
サ』を用いる場合と異なり、分散状態が良好である細骨
材を用いているので、塗材の成分が均一状態であること
から、経時的変化によって、ブルーミング現象を生じさ
せ、その成分が、塗材から均一に壁面に滲出するので、
壁面がむらなく手触りの良い疎水性塗材を得ることがで
き、かつ該壁面の水洗い等の洗浄が可能となるという効
果を有する。As is apparent from the above description, according to the lime-based hard hydrophobic thin coating material of the present invention, calcium carbonate,
By using fine aggregate such as cold water clay and stone powder,
It is possible to prevent the coating material from shrinking and increase its strength, and to eliminate the need for the "sustain", so that a thin coating material can be formed, and a carnauba wax emulsion can be formed in the coating material. , Paraffin wax emulsion, paraffin granules, wax emulsion of low molecular polyethylene or derivatives thereof, and one or more waxes selected from vegetable oils .
Fine bones that are well dispersed, unlike when using
Since the material is used, the composition of the coating material must be uniform
From the changes over time, cause blooming phenomenon, its components, since uniformly exuded to the wall surface from the coating material,
Wall has the effect that it is possible to obtain a good hydrophobic coating material having evenly hand touch, and it is possible to wash the washing or the like of the wall surface.
【００２４】また、本発明の壁面薄塗装工法によれば、
カルナバワックスエマルジョン，パラフィンワックスエ
マルジョン，パラフィンの顆粒，低分子ポリエチレンま
たはその誘導体のワックスエマルジョン，植物油より選
ばれる１または２以上のワックスを混合・配合した石灰
系硬質疎水性薄塗材を用い、該塗材を壁面に、塗厚が
０．２〜５ｍｍとなるように塗布・整面するので、また
耐アルカリ性材を混入していることより、硬化のための
養生期間が不要となり、種々の壁面上に塗布でき、かつ
剥離しない硬度を有する薄塗工事ができ、また、その硬
化速度が早くなるため、硬化時期と鏝押さえ時期の判断
に左官工による差が少なくなり、鏝むら等による傷を気
にする必要がなくなることより、該左官工によるペーパ
ー処理等による研ぎ仕上げの差を少なくできるという効
果を有する。更に、『スサ』を用いる場合と異なり、分
散状態が良好である細骨材を用いているので、塗材の成
分が均一状態であることから、経時的変化によって、ブ
ルーミング現象を生じさせ、その成分が、塗材から均一
に壁面に滲出するので、壁面がむらなく手触りの良い壁
面を形成できるという効果を有する。 According to the thin wall coating method of the present invention,
Carnauba wax emulsion, paraffin wax emulsion, paraffin granules, wax emulsion of low molecular weight polyethylene or its derivatives, and a lime-based hard hydrophobic thin coating material in which one or more waxes selected from vegetable oils are mixed and blended. The wall surface is coated and surface-adjusted so that the coating thickness is 0.2-5 mm. Also, because an alkali resistant material is mixed in, there is no need for a curing period for curing, and it is coated on various wall surfaces. It is possible to do a thin coating work that has a hardness that does not peel, and the curing speed is fast, so there is less difference between plasterers in determining the curing time and the trowel holding time, and you are concerned about scratches due to uneven trowels etc. Since it is not necessary, there is an effect that it is possible to reduce the difference in the sharpening finish due to the paper treatment by the plasterer. Moreover, unlike when using "Susa",
Since fine aggregate that is in a well-dispersed state is used,
Since the components are in a uniform state, the
It causes a ruoming phenomenon, and its composition is uniform from the coating material.
Since it exudes to the wall surface, the wall surface is even and feels good.
It has an effect that a surface can be formed.
【００２５】従って、本発明によれば、ローラーを簡単
に使用でき、着色した塗材であっても色相むらなく仕上
げることができ、かつ強度を低下させることがない石灰
系硬質疎水性薄塗材と壁面薄塗装工法が提供できるとい
う効果を有する。Therefore, according to the present invention, the roller can be easily used, and even a colored coating material can be finished without color unevenness, and the strength of the lime-based hard hydrophobic thin coating material and the wall surface are not reduced. It has an effect that a thin coating method can be provided.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０４Ｂ 22:06 14:28 24:24 24:08 24:26） ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location C04B 22:06 14:28 24:24 24:08 24:26)
Claims (2)
びセメント混和用ポリマーを含む主材に、カルナバワッ
クスエマルジョン，パラフィンワックスエマルジョン，
パラフィンの顆粒，低分子ポリエチレンまたはその誘導
体のワックスエマルジョン，植物油より選ばれる１また
は２以上のワックスを配合したことを特徴とする石灰系
硬質疎水性薄塗材。1. A main material containing lime cream, a water absorbing material, a fine aggregate and a polymer for admixing cement, carnauba wax emulsion, paraffin wax emulsion,
A lime-based hard hydrophobic thin coating material comprising one or more waxes selected from paraffin granules, wax emulsion of low molecular weight polyethylene or its derivatives, and vegetable oil.
びセメント混和用ポリマーを含む主材に、カルナバワッ
クスエマルジョン，パラフィンワックスエマルジョン，
パラフィンの顆粒，低分子ポリエチレンまたはその誘導
体のワックスエマルジョン，植物油より選ばれる１また
は２以上のワックスを配合した石灰系硬質疎水性薄塗材
を壁面に、塗厚が０．２〜５ｍｍとなるように塗布・整
面し、該塗材が硬化後にペーパー等による研ぎ仕上げ
し、かつ前記ワックスを塗面に滲出させるようにしたこ
とを特徴とする壁面薄塗装工法。2. A main material containing lime cream, a water absorbent, a fine aggregate and a polymer for admixing cement, carnauba wax emulsion, paraffin wax emulsion,
A lime-based hard hydrophobic thin coating material containing one or more waxes selected from paraffin granules, wax emulsion of low molecular weight polyethylene or its derivatives, and vegetable oil is applied to the wall surface to a coating thickness of 0.2-5 mm. A surface thin coating method characterized in that the surface is conditioned, the coating material is cured and then ground with a paper or the like, and the wax is exuded to the coated surface.