JP2602662Y2 - Deflection yoke separator - Google Patents
Deflection yoke separatorInfo
- Publication number
- JP2602662Y2 JP2602662Y2 JP1993033132U JP3313293U JP2602662Y2 JP 2602662 Y2 JP2602662 Y2 JP 2602662Y2 JP 1993033132 U JP1993033132 U JP 1993033132U JP 3313293 U JP3313293 U JP 3313293U JP 2602662 Y2 JP2602662 Y2 JP 2602662Y2
- Authority
- JP
- Japan
- Prior art keywords
- deflection yoke
- yoke separator
- separator
- present
- soft ferrite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本考案は、電磁偏向型陰極管（受
像管）におけるコンバージェンス不良の防止に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to prevention of poor convergence in an electromagnetic deflection type cathode ray tube (picture tube).
【０００２】[0002]
【従来の技術】従来、受像管を組み込んだ機器シャーシ
ー側からの影響、特にフライバックトランスからの高周
波磁界の影響によるコンバージェンス不良を防止するた
めに、種々の方法が提案されている。例えば、図１に一
点鎖線で示されるように、略有底筒形の非磁性材料製の
カバーＡで、偏向ヨーク１、アライメントマグネット２
及び配線基板３の装着部分を覆うことも提案されてい
る。2. Description of the Related Art Conventionally, various methods have been proposed in order to prevent convergence failure due to the influence from a device chassis incorporating a picture tube, particularly the influence of a high-frequency magnetic field from a flyback transformer. For example, as shown by a dashed line in FIG.
It has also been proposed to cover the mounting portion of the wiring board 3.
【０００３】[0003]
【考案が解決しようとする課題】しかしながら、このよ
うな方法では、受像管のソケット部４に設けられる配線
基板３の外形寸法が用途等によって異なるため、一定形
状のカバーＡではこの配線基板３の変更に対応しにく
い。従って、配線基板３の種類に応じたカバーＡを用意
しなければならず、カバーＡの種類が多くなって、その
製造及び管理に手間とコストがかかる問題がある。However, in such a method, since the external dimensions of the wiring board 3 provided in the socket portion 4 of the picture tube differ depending on the application, etc., the cover A having a fixed shape has Difficult to adapt to changes. Therefore, a cover A corresponding to the type of the wiring board 3 must be prepared, and the number of types of the cover A increases.
【０００４】本考案は、このような従来の問題点に鑑み
てなされたもので、配線基板３の外形寸法に拘らず、一
定の部材で、機器シャーシー側からの影響によるコンバ
ージェンス不良を防止できるようにすることを目的とす
る。The present invention has been made in view of such a conventional problem, and it is possible to prevent a convergence defect due to the influence from the equipment chassis with a fixed member regardless of the external dimensions of the wiring board 3. The purpose is to.
【０００５】[0005]
【課題を解決するための手段及び作用】ところで、通
常、コンバージェンスを行う偏向ヨークには、そのコイ
ル形状維持と偏向ヨーク取り付け時の台座としての役割
をなす偏向ヨークセパレーターが設けられている。この
偏向ヨークセパレーターは、通常、難燃性の合成樹脂成
形品となっている。Means for Solving the Problems and Functions Usually, a deflection yoke for performing convergence is provided with a deflection yoke separator serving as a base for maintaining its coil shape and for mounting the deflection yoke. This deflection yoke separator is usually a flame-retardant synthetic resin molded product.
【０００６】本考案は、この偏向ヨークセパレーターに
注目し、従来の提案のように、機器シャーシー側からの
影響を防止するための専用のカバーを設けるのではな
く、全く相違する目的にために設けられている偏向ヨー
クセパレーターで機器シャーシー側からの影響を防止で
きるようにしたものである。The present invention pays attention to this deflection yoke separator, and does not provide a dedicated cover for preventing the influence from the equipment chassis side as in the conventional proposal, but provides it for a completely different purpose. The deflection yoke separator prevents the influence from the equipment chassis side.
【０００７】即ち、本考案は、図１に示される偏向ヨー
クセパレーターＢを、ソフトフェライト粉を１０〜９０
重量％含有する合成樹脂成形品としたものである。That is, in the present invention, the deflection yoke separator B shown in FIG.
It is a synthetic resin molded product containing the same by weight.
【０００８】本考案において、偏向ヨークセパレーター
Ｂを構成する合成樹脂に配合されているソフトフェライ
ト粉は、偏向ヨークセパレーターＢを高透磁率化するも
のである。In the present invention, the soft ferrite powder blended in the synthetic resin constituting the deflection yoke separator B increases the magnetic permeability of the deflection yoke separator B.
【０００９】即ち、偏向ヨーク１が高透磁率化されるこ
とにより、偏向ヨーク１によるコンバージェンスには好
環境となるばかりか、偏向ヨーク１が高透磁率であるこ
とによって、偏向ヨーク１に磁気シールド機能がもたら
される。That is, by increasing the magnetic permeability of the deflection yoke 1, not only is the environment favorable for convergence by the deflection yoke 1, but also because the deflection yoke 1 has a high magnetic permeability, a magnetic shield is provided on the deflection yoke 1. Features are brought.
【００１０】従って、本考案に係る偏向ヨークセパレー
ターＢは、フライバックトランスから等の機器シャーシ
ー側からの高周波磁界の影響を遮断することができ、従
来の提案のようなカバーＡを設けることなくコンバージ
ェンスの低下を防止できるものである。Therefore, the deflection yoke separator B according to the present invention can block the influence of the high-frequency magnetic field from the equipment chassis side such as from the flyback transformer, and can achieve the convergence without providing the cover A unlike the conventional proposal. Can be prevented from decreasing.
【００１１】本考案において、偏向ヨークセパレーター
Ｂを構成する合成樹脂中に配合されているソフトフェラ
イト粉の量は、１０〜９０重量％であることが必要であ
る。ソフトフェライト粉の配合量が１０重量％未満で
は、機器シャーシー側からの高周波磁界を十分遮断する
ことができない。逆に９０重量％を越えると、変更ヨー
クセパレーターＢとしての必要な強度が得られなくな
る。In the present invention, the amount of the soft ferrite powder mixed in the synthetic resin constituting the deflection yoke separator B needs to be 10 to 90% by weight. If the amount of the soft ferrite powder is less than 10% by weight, the high-frequency magnetic field from the equipment chassis cannot be sufficiently blocked. Conversely, if it exceeds 90% by weight, the required strength as the modified yoke separator B cannot be obtained.
【００１２】ソフトフェライト粉の粒径は、偏向ヨーク
セパレーターＢの成形を妨げない範囲であれば足るが、
一般的には１μｍ前後〜数十μｍ程度である。The particle size of the soft ferrite powder is sufficient as long as it does not hinder the molding of the deflection yoke separator B.
Generally, it is around 1 μm to several tens μm.
【００１３】偏向ヨークセパレーターＢを構成する合成
樹脂自体は、従来から使用されているものと同様のもの
で、例えば難燃性ポリオレフィン、難燃性ポリスチレ
ン、難燃性ポリアミド、難燃性ポリエステル、難燃性ポ
リフェニレンエーテル等である。The synthetic resin itself constituting the deflection yoke separator B is the same as that conventionally used, for example, flame-retardant polyolefin, flame-retardant polystyrene, flame-retardant polyamide, flame-retardant polyester, flame-retardant polyester, etc. Flammable polyphenylene ether and the like.
【００１４】[0014]
【実施例】実施例１及び比較例１ 図１に示されるような偏向ヨークセパレーターＢを、変
性ポリフェニレンエーテル（旭化成工業社製「ザイロン
５００Ｚ」）とソフトフェライト（Ｍｎ−Ｚｕ系ソフト
フェライト，戸田工業社製「ＢＳＦ５４７」）を用い
て、通常の射出成形によって成形した。EXAMPLES Example 1 and Comparative Example 1 A deflection yoke separator B as shown in FIG. 1 was prepared by using modified polyphenylene ether ("Zylon 500Z" manufactured by Asahi Kasei Corporation) and soft ferrite (Mn-Zu soft ferrite, Toda Kogyo). ("BSF547", manufactured by the Company).
【００１５】本考案品（イ）は変性ポリフェニレンエー
テル６０重量％とソフトフェライト４０重量％を配合し
た成形品、本考案品（ロ）は変性ポリフェニレンエーテ
ル４０重量％とソフトフェライト６０重量％を配合した
成形品、比較品はソフトフェライトを全く配合しないポ
リフェニレンエーテルの成形品とした。The product of the present invention (a) is a molded product containing 60% by weight of modified polyphenylene ether and 40% by weight of soft ferrite, and the product of the present invention (B) is provided with 40% by weight of modified polyphenylene ether and 60% by weight of soft ferrite. The molded article and the comparative article were molded articles of polyphenylene ether containing no soft ferrite.
【００１６】各偏向ヨークセパレーターを順次同じ受像
機に取り付けて画像の形成を行い、画像状態を比較し
た。Each deflection yoke separator was sequentially mounted on the same receiver to form an image, and the image states were compared.
【００１７】その結果、比較品については、特に画面の
周縁寄りに輝度むらや色彩むらが生じ、永久磁石の付設
等によって更に微調整をしなければ良好な画像状態が得
られなかったのに対して、本考案品（イ）及び（ロ）に
ついては、このような微調整をすることなく良好な画像
状態を得ることができた。As a result, with respect to the comparative product, uneven brightness and color were generated particularly near the periphery of the screen, and a good image state could not be obtained unless further fine adjustment was made by attaching a permanent magnet or the like. Thus, for the products of the present invention (a) and (b), a good image state could be obtained without such fine adjustment.
【００１８】尚、本考案品（イ）及び（ロ）は、夫々透
磁率は１．５９と２．０７、引張強さは４６０と３４０
ｋｇ／ｃｍ2 （ＡＳＴＭ・Ｄ６３８）、曲げ強さは８６
０と６１０ｋｇ／ｃｍ2 で、比較品に比して高い透磁率
を有すると共に、偏向ヨークセパレーターｂとして必要
な十分な機械的強度を備えていた。The products (a) and (b) of the present invention have magnetic permeability of 1.59 and 2.07 and tensile strengths of 460 and 340, respectively.
kg / cm 2 (ASTM D638), flexural strength 86
At 0 and 610 kg / cm 2 , it had a higher magnetic permeability than the comparative product, and also had sufficient mechanical strength necessary for the deflection yoke separator b.
【００１９】[0019]
【考案の効果】本考案は、以上説明した通りのものであ
り、配線基板３の外形寸法とは全く係わりのない偏向ヨ
ークセパレーターＢによって、機器シャーシー側からの
影響によるコンバージェンス不良を防止できる。また、
配線基板３の外形寸法に拘らず同一の偏向ヨークセパレ
ーターＢで良好なコンバージェンスを維持できるもので
ある。更に、偏向ヨーク１からの不要な磁界輻射も抑制
できるものである。The present invention is as described above, and the deflecting yoke separator B which has no relation to the external dimensions of the wiring board 3 can prevent the convergence failure due to the influence from the equipment chassis. Also,
Good convergence can be maintained with the same deflection yoke separator B regardless of the external dimensions of the wiring board 3. Furthermore, unnecessary magnetic field radiation from the deflection yoke 1 can be suppressed.
【図１】本考案及び従来技術の説明図である。FIG. 1 is an explanatory diagram of the present invention and the prior art.
Ａ カバー Ｂ 偏向ヨークセパレーター １ 偏向ヨーク ２ アライメントマグネット ３ 配線基板 ４ ソケット部 A cover B deflection yoke separator 1 deflection yoke 2 alignment magnet 3 wiring board 4 socket part
Claims (1)
含有する合成樹脂成形品であることを特徴とする偏向ヨ
ークセパレーター。1. A soft ferrite powder of 10 to 90% by weight.
A deflection yoke separator characterized in that it is a synthetic resin molded product.