JP2601325Y2 - Glass color printing wall tile - Google Patents

Description

[Detailed description of the invention]

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a glass color printing wall tile, and more particularly to a glass color printing wall tile which can be used as a wall decoration or a surface decoration of a building.

[0002]

2. Description of the Related Art In the decoration work of a building, generally,
Pottery wall tiles are used. This ceramic wall tile has a color pattern.

[0003]

[Problems to be solved by the invention] However, in the case of ceramic wall tiles that are often used in decorative work of buildings,
If the surface of the product is not smooth and glossy, the product variation will be large or the thickness is not standard, so if only the silk printing method is adopted, the printing color will be monotonous, the appearance of the pattern, However, natural cracks are formed on the surface, and the design is easily polished. Therefore, there are problems with the decorative performance and the service life of the ceramic wall tile. From the perspective of the future, there was an inconvenience that the demand for high-class development in the construction industry could not be satisfied.

[0004]

SUMMARY OF THE INVENTION In order to eliminate the above-mentioned disadvantages, the present invention firstly comprises a glass layer, a color design layer, a binder layer, and a magnesium oxide lightly fired brick layer. The glass layer is on the surface, the glass design layer is printed on the glass layer, the binder layer is applied on the color design layer, and the magnesium oxide light foaming imitation brick layer is It is a bottom layer and can be directly attached to a wall or the ground.

Second, the glass layer is a hardened glass.

[0006]

According to the constitution of the present invention, a photographed pattern can be printed with a high accuracy of 95% by a kind of offset printing technique,
Also, no natural crack phenomenon occurs. Further, it is possible to make the color design difficult to polish.

[0007]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described below in detail with reference to the drawings. FIG. 1 shows an embodiment of the present invention. In FIG. 1, 1 is a glass layer, 2 is a color design layer,
Reference numeral 3 denotes a binder layer, and reference numeral 4 denotes a magnesium oxide light foaming imitation brick layer. The glass color printing wall tile is composed of the glass layer 1, the color design layer 2, the binder layer 3, and the magnesium oxide light foaming imitation brick layer 4. The glass layer 1
It is a colorless and transparent flat glass or hardened glass produced by the usual float method, and is in the surface layer. The color design layer 2 is a color design printed on glass by an offset printing technique. The binder layer 3 is a silicone rubber binder that is solidified at room temperature and is applied on the color design layer 2. Magnesium oxide light foam mock brick layer 4 is made of industrial-grade magnesium oxide, magnesium chloride, and fine sand of about 200 meshes, and has a weight of 150.
Constructed by room temperature imitation with expanded peridotite of -250 cubic meters / km, foaming agent and fast coagulant. This layer 4
Located on the bottom layer of the wall tile. It is a stack of glass layer 1, color design layer 2, and binder layer 3, which can be applied directly to a wall or to the ground.

Next, the operation of this embodiment will be described.

The glass-color printed wall tile is composed of four layers: a glass layer 1, a color design layer 2, a binder layer 3, and a magnesia oxide light foam imitation brick layer 4. Glass layer 1
Is a surface layer made of a colorless and transparent flat glass or hardened glass manufactured by an ordinary float method. The color design layer 2 is a color design printed on the glass upper surface by the offset printing technique. The binder layer 3 is composed of a silicone rubber binder at room temperature. It is smeared on the color design layer 2. After mixing magnesium oxide, magnesium chloride, fine sand, expansive peridotite, foaming agent, and quick-coagulant, this layer produced by room temperature imitation is the bottom layer of wall tile, which is glass layer 1, color pattern layer 2 and viscous layer. It is a carrier of the binder layer 3, which is directly attached to the wall or the ground.

According to this embodiment, the surface layer of the glass-color printed wall tile is the glass layer 1, and the glass is printed with a 95% high-precision halftone dot, which can adopt an offset printing technique after a special treatment. It has a very intense three-dimensional feeling and a sense of truth that can be reproduced and that all color patterns of nature can be reproduced. The decoration effect of wall tiles was greatly improved. This is what makes ceramic wall tiles incomparable with silk printing methods.

The surface layer of the glass / color printed wall tile is 3-5% glass, and its physical and chemical performances are sufficiently stable, and natural cracking phenomenon cannot occur.
Thus, the technical problems that ceramic wall tiles cannot solve and the disadvantages that cannot be overcome can be solved.

In addition, the color design layer 2 of the glass color printing wall tile is on the back side of the glass. The color pattern layer 2 cannot be directly polished because it is inserted between the glass, the binder, and the magnesium oxide light impression model brick layer 4.

Furthermore, the bottom layer of the glass-color printed wall tile is a magnesium oxide light foaming imitation brick layer 4 having a water absorption of 20% or more. Normal 45 普通^# directly
Concrete was stuck to the wall, solving the technical problem of sticking concrete directly to the wall, which glass could not solve. Significantly lowering the cost of wall decoration on glass.

Also, in the process of producing the glass color printing wall tile, high temperature sintering is not a demand, energy saving, no exhaust emission, and no pollution to the atmosphere.

Furthermore, glass and color printed wall tiles are mainly made of glass, and do not require materials such as clay and porcelain. Therefore, they do not use arable land and do not destroy the balance between land resources and ecology.

That is, the glass / color printed wall tile of this embodiment comprises a glass layer 1, a color design layer 2, a binder layer 3, and a magnesium oxide light foaming imitation brick layer 4. The color design layer 2 uses offset printing technology and can print 95% high-accuracy photography patterns on glass. All natural color patterns can be reproduced. In addition, the glass layer 1 does not exhibit a natural crack phenomenon.
And color pattern layer 2 is not as polished as porcelain wall tiles. It is a new generation of ceramic wall tiles, and the building industry is also a new product in the development of high-class decoration. This product is great for active widespread use because it is easy to produce and does not destroy land resources and ecological environment.

[0017]

[Effects of the Invention] As is apparent from the above detailed description, according to the present invention, the glass layer, the color design layer, the binder layer, and the magnesium oxide light foaming imitation brick layer, On the surface, the glass design layer is printed on the glass layer, the binder layer is smeared on the color design layer,
The magnesia oxide light foam imitation brick layer is a bottom layer and can be directly attached to a wall or the ground, thereby reproducing all the color patterns of nature and preventing a natural crack phenomenon from occurring.

[Brief description of the drawings]

FIG. 1 is a partially cutaway configuration view of a glass-color printing wall tile.

[Explanation of symbols]

 Reference Signs List 1 glass layer 2 color design layer 3 binder layer 4 magnesium oxide light fired impression brick layer

──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int.Cl. ⁶ , DB name) E04F 13/04-13/18 B32B 1/00-35/00

Claims (2)

(57) [Scope of request for utility model registration] 1. A glass layer, a color design layer, a binder layer, and a magnesia oxide light foaming imitation brick layer, wherein the glass layer is on a surface, and the glass design layer is printed on the glass layer. Wherein the binder layer is applied on the color design layer, and the magnesium oxide light foam imitation brick layer is a bottom layer and is directly attached to a wall or the ground. Color printing wall tile. 2. The glass color printed wall tile according to claim 1, wherein the glass layer is hardened glass.