JP2553431B2 - Magnetic recording media - Google Patents
Magnetic recording mediaInfo
- Publication number
- JP2553431B2 JP2553431B2 JP4040698A JP4069892A JP2553431B2 JP 2553431 B2 JP2553431 B2 JP 2553431B2 JP 4040698 A JP4040698 A JP 4040698A JP 4069892 A JP4069892 A JP 4069892A JP 2553431 B2 JP2553431 B2 JP 2553431B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- layer
- magnetic pattern
- ink
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、磁気バーコードなど、
パターン状に磁性部分を形成した磁気記録媒体に関す
る。The present invention relates to a magnetic bar code, etc.
The present invention relates to a magnetic recording medium having a magnetic portion formed in a pattern.
【０００２】[0002]
【従来の技術】従来、プリペイドカード等の磁気カード
においては、偽造防止の目的で、バーコードなどの特定
の磁気パターンを磁気インキによって形成し、それによ
ってセキュリティ性を向上させることが行われている。
この磁気パターンは、通常、スクリーン印刷法を用いる
ことによって形成されているが、最近、磁気パターンを
目視で認識できないようにするために、その上にさらに
着色隠蔽層を設けることが行われるようになった。とこ
ろで、通常、上記着色隠蔽層は、溶剤可溶型の熱可塑性
樹脂を、トルエン、メチルエチルケトン等の汎用の溶剤
に溶解し、その中に染料や顔料を溶解または分散させた
インキを用いて形成している。2. Description of the Related Art Conventionally, in a magnetic card such as a prepaid card, a specific magnetic pattern such as a bar code is formed by magnetic ink for the purpose of preventing forgery, thereby improving security. .
This magnetic pattern is usually formed by using a screen printing method, but recently, in order to make the magnetic pattern invisible, it is necessary to further provide a colored hiding layer on it. became. By the way, usually, the colored hiding layer is formed by using a solvent-soluble thermoplastic resin, an ink prepared by dissolving a general-purpose solvent such as toluene or methyl ethyl ketone, and dissolving or dispersing a dye or a pigment therein. ing.
【０００３】[0003]
【発明が解決しようとする課題】ところが、上記従来の
磁気記録媒体においては、着色隠蔽層を形成する際に、
磁気バーコードが着色隠蔽層インキ中の溶剤に溶解し、
磁気特性が劣化してしまったり、あるいは着色隠蔽層が
溶剤可溶型の熱可塑性樹脂を用いて形成されているた
め、溶剤によって容易に剥離され、磁気パターンが露出
するため、磁気パターンとしては、溶剤に対して損傷を
受けにくい１液または２液タイプの硬化性樹脂を使用し
て形成しなければならなかった。そのため、磁気パター
ン形成時に硬化のための工程を必要とするという問題が
あった。さらにまた、着色隠蔽層が溶剤により除去され
る結果、磁気パターンが目視によって容易に認識できる
という問題があり、偽造防止の点でも充分なものではな
かった。本発明は、従来の技術における上記のような問
題点に鑑みてなされたものであって、その目的は、従来
の磁気記録媒体の製造上の問題点を解決すると共に、セ
キュリティ性が改善された磁気記録媒体を提供すること
にある。However, in the above-mentioned conventional magnetic recording medium, when the colored hiding layer is formed,
The magnetic bar code dissolves in the solvent in the colored hiding layer ink,
Since the magnetic characteristics are deteriorated, or because the colored hiding layer is formed using a solvent-soluble thermoplastic resin, it is easily peeled off by the solvent and the magnetic pattern is exposed. It has to be formed by using a one-component or two-component type curable resin that is not easily damaged by a solvent. Therefore, there is a problem that a step for curing is required when forming the magnetic pattern. Furthermore, as a result of the colored hiding layer being removed by the solvent, there is a problem that the magnetic pattern can be easily visually recognized, which is not sufficient from the viewpoint of forgery prevention. The present invention has been made in view of the above problems in the conventional technique, and an object thereof is to solve the problems in manufacturing the conventional magnetic recording medium and to improve the security. It is to provide a magnetic recording medium.
【０００４】[0004]
【課題を解決するための手段】本発明の磁気記録媒体
は、支持体上に形成された磁気パターン層および該磁気
パターン層を隠蔽する着色隠蔽層よりなり、そして磁気
パターン層が磁性粉末が分散された溶剤可溶性熱可塑性
樹脂含有インキにより形成されたものであり、また着色
隠蔽層が顔料または染料を含有する紫外線または電子線
硬化型の無溶剤型インキにより形成されたものであるこ
とを特徴とする。The magnetic recording medium of the present invention comprises a magnetic pattern layer formed on a support and a colored masking layer for masking the magnetic pattern layer, and the magnetic pattern layer has magnetic powder dispersed therein. Characterized in that it is formed by a solvent-soluble thermoplastic resin-containing ink, and the colored hiding layer is formed by a UV or electron beam curable solventless ink containing a pigment or a dye. To do.
【０００５】以下、本発明を詳細に説明する。本発明に
おいて、支持体としては、従来公知のものであれば如何
なるものでも使用することができ、例えば、紙、合成
紙、プラスチックフィルムでラミネートした紙、ポリエ
ステルフィルム、ポリオレフィンフィルム、ポリアミド
フィルム、ポリイミドフィルム、金属フォイル、セラミ
ックシート、ガラスなどがあげられる。The present invention will be described in detail below. In the present invention, as the support, any conventionally known one can be used, and examples thereof include paper, synthetic paper, paper laminated with a plastic film, polyester film, polyolefin film, polyamide film, polyimide film. , Metal foil, ceramic sheet, glass, etc.
【０００６】磁気パターン層は、磁性粉末が分散された
溶剤可溶性熱可塑性樹脂含有インキを用いて形成され
る。磁性粉末としては、γ−Ｆｅ2 Ｏ3 、バリウムフェ
ライト、ストロンチウムフェライト等の強磁性体の微粉
末が使用されるが、磁気記録情報が通常の永久磁石によ
り消失または減衰するのを防止するためには、バリウム
フェライトやストロンチウムフェライト等のような１５
００〜５０００エルステッド程度の高い保磁力を有する
磁性材料を使用するのが好ましい。溶剤可溶性熱可塑性
樹脂としては、皮膜形成性のものであれば如何なるもの
でも使用することができ、例えば、スチレン−ブタジエ
ン共重合体、塩化ビニル−酢酸ビニル−ポリビニルアル
コール共重合体、ポリアクリレート、ポリメタクリレー
ト、塩化ビニル樹脂等のビニル系樹脂、ポリエステル樹
脂、ポリオレフィン樹脂、ポリアミド樹脂、ポリウレタ
ン樹脂等があげられる。磁気パターン層は、上記の溶剤
可溶性熱可塑性樹脂を適当な有機溶剤に溶解し、磁性粉
末を分散させて得たインキを、スクリーン印刷法等によ
って、パターン状に塗布し、加熱して乾燥することによ
り形成される。膜厚は、通常１〜１０μｍに設定され
る。The magnetic pattern layer is formed by using an ink containing a solvent-soluble thermoplastic resin in which magnetic powder is dispersed. As the magnetic powder, fine powder of ferromagnetic material such as γ-Fe 2 O 3 , barium ferrite, strontium ferrite, etc. is used, but in order to prevent magnetic recording information from being lost or attenuated by an ordinary permanent magnet. Is 15 such as barium ferrite or strontium ferrite.
It is preferable to use a magnetic material having a high coercive force of about 00 to 5000 oersted. As the solvent-soluble thermoplastic resin, any film-forming one can be used, and examples thereof include styrene-butadiene copolymer, vinyl chloride-vinyl acetate-polyvinyl alcohol copolymer, polyacrylate, and polyacrylate. Examples thereof include vinyl resins such as methacrylate and vinyl chloride resins, polyester resins, polyolefin resins, polyamide resins, polyurethane resins and the like. The magnetic pattern layer is prepared by dissolving the above solvent-soluble thermoplastic resin in an appropriate organic solvent and dispersing the magnetic powder to obtain an ink, which is applied in a pattern by a screen printing method or the like and heated and dried. Is formed by. The film thickness is usually set to 1 to 10 μm.
【０００７】本発明において着色隠蔽層は、有彩色顔料
または染料により着色された隠蔽層のみならず、白色顔
料や金属粉末を含有する白色または金属光沢を有する隠
蔽層をも意味する。着色隠蔽層に使用される顔料または
染料としては、磁気パターンに影響を与えないものなら
ば如何なるものでも使用でき、例えば、チタン白、亜鉛
華、アルミニウム粉末等の無機顔料が好ましく使用され
る。着色隠蔽層を形成するための紫外線または電子線硬
化型の無溶剤型インキとしては、公知のものならば如何
なるものでも使用することができる。紫外線硬化型の無
溶剤型インキは、基本的には、顔料、オリゴマ−（プレ
ポリマー、光重合性低重合体）、モノマ−（反応性希釈
剤、光重合性単量体）、光重合開始剤より構成される。
また、電子線硬化型の無溶剤型インキは、紫外線よりも
かなり高いエネルギーを持つ電子線の照射により、瞬時
に硬化乾燥するものであって、上記紫外線硬化型のもの
の必須成分である光重合開始剤を用いない以外は、ほぼ
同一の組成を有する。In the present invention, the colored hiding layer means not only a hiding layer colored with a chromatic color pigment or dye, but also a hiding layer having a white or metallic luster containing a white pigment or metal powder. As the pigment or dye used in the colored hiding layer, any pigment or dye that does not affect the magnetic pattern can be used. For example, inorganic pigments such as titanium white, zinc white, and aluminum powder are preferably used. Any known ultraviolet or electron beam curable solventless ink for forming the colored hiding layer can be used as long as it is known. UV curable solventless ink is basically pigment, oligomer (prepolymer, photopolymerizable low polymer), monomer (reactive diluent, photopolymerizable monomer), photopolymerization initiation. Composed of agents.
Further, the electron beam curable solventless ink is one which is instantly cured and dried by irradiation with an electron beam having an energy considerably higher than that of ultraviolet rays, and photopolymerization initiation which is an essential component of the above ultraviolet curable type ink. It has almost the same composition except that no agent is used.
【０００８】より具体的には、オリゴマーとしては、例
えば、ポリエステルアクリレート、エポキシアクリレー
ト、ウレタンアクリレート、ポリオールアクリレート、
不飽和ポリエステルオリゴマー等があげられ、モノマー
としては、２−ヒドロキシエチルアクリレート、２−ヒ
ドロキシプロピルアクリレート、Ｎ−ビニルピロリド
ン、メトキシテトラエチレングリコールアクリレート、
Ｎ，Ｎ−ジメチルアクリルアミド、Ｎ−メチロールアク
リルアミド、Ｎ，Ｎ−ジメチルアミノプロピルアクリル
アミド、Ｎ，Ｎ−ジメチルアミノエチルアクリレート、
Ｎ，Ｎ−ジメチルアミノプロピルアクリレート等の単官
能モノマー、ジエチレングリコールジアクリレート、ト
リエチレングリコールジアクリレート、１，６−ヘキサ
ンジオールジアクリレート、トリメチロールプロパント
リアクリレート、グリセリンジグリシジルエーテルジア
クリレート、ペンタエリスリトールトリアクリレート、
ペンタエリスリトールテトラアクリレート、ペンタエリ
スリトールヘキサアクリレート等の多官能モノマーがあ
げられる。また、光重合開始剤としては、例えば、ベン
ゾイン、ベンゾインエチルエーテル、ベンゾインイソブ
チルエーテル、ベンゾインプロピルエーテル等のベンゾ
インアルキルエーテル系、２−ヒドロキシ−２−メチル
プロピオフェノン等のプロピオフェノン系、アセトフェ
ノン、２、２−ジメトキシ−２−フェニルアセトフェノ
ン、２、２−ジエトキシアセトフェノン等のアセトフェ
ノン系、２−エチルアントラキノン、２−クロルアント
ラキノン等のアントラキノン系、２，４−ジメチルチオ
キサントン、２−クロロチオキサントン等のチオキサン
トン系を例示することができる。More specifically, as the oligomer, for example, polyester acrylate, epoxy acrylate, urethane acrylate, polyol acrylate,
Examples of the unsaturated polyester oligomer include 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, N-vinylpyrrolidone, methoxytetraethylene glycol acrylate, and the like.
N, N-dimethylacrylamide, N-methylolacrylamide, N, N-dimethylaminopropylacrylamide, N, N-dimethylaminoethyl acrylate,
Monofunctional monomers such as N, N-dimethylaminopropyl acrylate, diethylene glycol diacrylate, triethylene glycol diacrylate, 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, glycerin diglycidyl ether diacrylate, pentaerythritol triacrylate. ,
Examples thereof include polyfunctional monomers such as pentaerythritol tetraacrylate and pentaerythritol hexaacrylate. As the photopolymerization initiator, for example, benzoin, benzoin ethyl ether, benzoin isobutyl ether, benzoin alkyl ethers such as benzoin propyl ether, propiophenone such as 2-hydroxy-2-methylpropiophenone, acetophenone, 2,2-dimethoxy-2-phenylacetophenone, 2,2-diethoxyacetophenone and other acetophenones, 2-ethylanthraquinone, 2-chloroanthraquinone and other anthraquinones, 2,4-dimethylthioxanthone, 2-chlorothioxanthone, etc. A thioxanthone system can be illustrated.
【０００９】着色隠蔽層は、上記の成分よりなる紫外線
または電子線硬化型の無溶剤型インキを、例えばスクリ
ーン印刷方式によって、上記磁気パターンが形成された
支持体の表面に、磁気パターンが隠蔽するように塗布
し、公知の手段によって紫外線または電子線を照射する
ことによって形成する。紫外線または電子線の照射量は
適宜設定されるが、硬化は瞬時に完了する。膜厚は、通
常１〜５μｍに設定される。本発明においては、支持体
上に磁気記録層を全面に設け、その磁気記録層上に磁気
パターン層、着色隠蔽層を積層することもできる。この
場合、磁気パターン層の磁気特性は、磁気記録層のそれ
と異なるようにすることが必要である。また、着色隠蔽
層上に感熱記録層を設けたり、各種印刷を施すことも可
能である。The colored masking layer masks the ultraviolet or electron beam curable solventless ink containing the above components on the surface of the support on which the magnetic pattern is formed, for example, by a screen printing method. It is formed by irradiating it with ultraviolet rays or electron beams by a known means. The irradiation dose of ultraviolet rays or electron beams is appropriately set, but curing is instantaneously completed. The film thickness is usually set to 1 to 5 μm. In the present invention, a magnetic recording layer may be provided on the entire surface of a support, and a magnetic pattern layer and a colored hiding layer may be laminated on the magnetic recording layer. In this case, the magnetic characteristics of the magnetic pattern layer need to be different from that of the magnetic recording layer. Further, it is also possible to provide a heat-sensitive recording layer on the colored hiding layer or perform various printing.
【００１０】[0010]
【作用】本発明の磁気記録媒体においては、磁気パター
ン層が非硬化型の溶剤可溶性熱可塑性樹脂を用いて形成
されており、他方、着色隠蔽層が紫外線または電子線硬
化型の無溶剤型インキで含有インキを用い、硬化させる
ことによって形成されているため、磁気記録媒体の作製
に際して、磁気パターン層の形成に硬化工程を必要とし
なくなると共に、着色隠蔽層の硬化が、紫外線または電
子線で瞬時に完了する。また、着色隠蔽層を有機溶剤に
よって除去しようとしても、着色隠蔽層が除去されると
同時またはそれ以前には、磁気パターン層が有機溶剤に
溶解してしまい、磁気パターン層の磁気パターンを目視
することが不可能になる。In the magnetic recording medium of the present invention, the magnetic pattern layer is formed using a non-curable solvent-soluble thermoplastic resin, while the colored hiding layer is an ultraviolet or electron beam curable solventless ink. Since it is formed by curing with the ink contained in, the curing step is not required for forming the magnetic pattern layer when manufacturing the magnetic recording medium, and the curing of the colored hiding layer is instantaneous by ultraviolet rays or electron beams. To be completed. Further, even if the colored hiding layer is removed by an organic solvent, the magnetic pattern layer is dissolved in the organic solvent at the same time as or before the removal of the colored hiding layer, and the magnetic pattern of the magnetic pattern layer is visually observed. Becomes impossible.
【００１１】[0011]
【実施例】下記の成分をペイントコンディショナーを用
いて３時間分散することにより、磁気パターン形成用の
インキを調製した。 γ−酸化鉄 １００重量部 塩化ビニル−酢酸ビニル−ビニルアルコール共重合体 ４０重量部 （商品名：エスレックＡ、積水化学工業社製） ポリウレタン樹脂（商品名：ニッポランＮ−２３０４ ４０重量部 日本ポリウレタン社製） キシレン ６０重量部 イソホロン ６０重量部 メチルイソブチルケトン ６０重量部 得られたインキを、白色ポリエステルフィルム上に、ス
クリーン印刷方式によってバーコード状に塗布し、８０
℃のオーブン内で５分間乾燥させて、膜厚５μｍのバー
コード状の磁気パターンを形成した。続いて、アルミニ
ウム粉末入りの紫外線硬化性無溶剤型インキ（商品名：
ＵＶ３１００スーパーシルバーＧＶ，女神インキ社製）
を用いて上記バーコード状の磁気パターンが形成された
ポリエステルフィルムの全面に、スクリーン印刷方式に
よって塗布し、１２００Ｗ水銀灯紫外線硬化装置内を通
過させて、無溶剤型インキを硬化させ、膜厚３．５μｍ
の銀色の隠蔽層を形成した。以上のようにして得たフィ
ルム積層物を、カード状に打ち抜き、磁気バーコード付
きの磁気カードを得た。Example An ink for magnetic pattern formation was prepared by dispersing the following components for 3 hours using a paint conditioner. γ-iron oxide 100 parts by weight Vinyl chloride-vinyl acetate-vinyl alcohol copolymer 40 parts by weight (Product name: S-REC A, Sekisui Chemical Co., Ltd.) Polyurethane resin (Product name: Nipporan N-2304 40 parts by weight Nippon Polyurethane Company) Xylene 60 parts by weight Isophorone 60 parts by weight Methyl isobutyl ketone 60 parts by weight The obtained ink was applied on a white polyester film in a bar code shape by a screen printing method, and 80
It was dried in an oven at 0 ° C. for 5 minutes to form a bar code-shaped magnetic pattern having a film thickness of 5 μm. Next, UV curable solventless ink containing aluminum powder (trade name:
UV3100 Super Silver GV, made by Megami Ink Co., Ltd.)
2. The polyester film on which the bar code-shaped magnetic pattern was formed was applied by a screen printing method using, and passed through a 1200 W mercury lamp UV curing device to cure the solventless ink, and a film thickness of 3. 5 μm
To form a silvery hiding layer. The film laminate obtained as described above was punched into a card shape to obtain a magnetic card with a magnetic barcode.
【００１２】この磁気カードの隠蔽層表面を、トルエン
−メチルエチルケトン（１：１）を含ませた綿棒で擦っ
たところ、隠蔽層が剥離される以前に、バーコード状の
磁気パターンが溶解して消失し、磁気パターン形状を目
視により確認することができなかった。When the surface of the hiding layer of this magnetic card was rubbed with a cotton swab containing toluene-methylethylketone (1: 1), the bar code-like magnetic pattern was dissolved and disappeared before the hiding layer was peeled off. However, the magnetic pattern shape could not be visually confirmed.
【００１３】（比較例）下記の成分をペイントコンディ
ショナーを用いて３時間分散することにより、磁気パタ
ーン形成用のインキを調製した。 γ−酸化鉄 １００重量部 塩化ビニル−酢酸ビニル−ビニルアルコール共重合体 ４０重量部 （商品名：エスレックＡ、積水化学工業社製） ポリウレタン樹脂（商品名：ニッポランＮ−２３０４ ４０重量部 日本ポリウレタン社製） ＴＤＩ系硬化剤（商品名：コロネートＬ、 ５重量部 日本ポリウレタン社製） キシレン ６０重量部 イソホロン ６０重量部 メチルイソブチルケトン ６０重量部 得られたインキを、白色ポリエステルフィルム上に、ス
クリーン印刷方式によってバーコード状に塗布し、８０
℃のオーブン内で６０分間乾燥・硬化させて、膜厚５μ
ｍのバーコード状の磁気パターンを形成した。続いて、
下記の混合物を、３本ロールミルを用い分散し、溶剤型
インキを調製した。 アルミニウム粉末 １０重量部 ポリエステル樹脂（商品名：バイロン２００、東洋紡社製） １４重量部 キシレン ３０重量部 イソホロン ３０重量部 メチルイソブチルケトン ３０重量部 得られた無溶剤型インキを、上記バーコード状の磁気パ
ターンが形成されたポリエステルフィルムの全面に、ス
クリーン印刷方式によって塗布し、８０℃のオーブン内
で６０分間乾燥・硬化させ、膜厚３μｍの銀色の隠蔽層
を形成した。以上のようにして得たフィルム積層物を、
カード状に打ち抜き、磁気バーコード付きの磁気カード
を得た。Comparative Example An ink for magnetic pattern formation was prepared by dispersing the following components for 3 hours using a paint conditioner. γ-iron oxide 100 parts by weight Vinyl chloride-vinyl acetate-vinyl alcohol copolymer 40 parts by weight (Product name: S-REC A, Sekisui Chemical Co., Ltd.) Polyurethane resin (Product name: Nipporan N-2304 40 parts by weight Nippon Polyurethane Company) TDI-based curing agent (trade name: Coronate L, 5 parts by weight manufactured by Nippon Polyurethane Company) Xylene 60 parts by weight Isophorone 60 parts by weight Methyl isobutyl ketone 60 parts by weight The obtained ink is screen-printed on a white polyester film. Apply in a bar code by
Drying and curing for 60 minutes in an oven at ℃, film thickness 5μ
A m-shaped bar code-like magnetic pattern was formed. continue,
The following mixture was dispersed using a three-roll mill to prepare a solvent type ink. Aluminum powder 10 parts by weight Polyester resin (trade name: Byron 200, Toyobo Co., Ltd.) 14 parts by weight Xylene 30 parts by weight Isophorone 30 parts by weight Methyl isobutyl ketone 30 parts by weight It was applied to the entire surface of the patterned polyester film by a screen printing method, dried and cured in an oven at 80 ° C. for 60 minutes to form a silver-colored hiding layer having a thickness of 3 μm. The film laminate obtained as described above,
It was punched into a card shape to obtain a magnetic card with a magnetic barcode.
【００１４】この磁気カードの隠蔽層表面を、トルエン
−メチルエチルケトン（１：１）を含ませた綿棒で擦っ
たところ、隠蔽層が溶解して磁気パターンが現れた。こ
の磁気パターンは、溶解せずに残留しているため、磁気
パターン形状は目視により確認することが可能であっ
た。When the surface of the masking layer of this magnetic card was rubbed with a cotton swab containing toluene-methylethylketone (1: 1), the masking layer was dissolved and a magnetic pattern appeared. Since this magnetic pattern remained without being dissolved, the shape of the magnetic pattern could be visually confirmed.
【００１５】[0015]
【発明の効果】本発明の磁気記録媒体は、その作製に際
して、磁気パターン層の形成に硬化剤を用いないため、
スクリーン印刷の印刷安定性が向上し、長時間の印刷が
可能になり、また、硬化工程を必要としなくなると共
に、着色隠蔽層の硬化が、紫外線または電子線で瞬時に
完了するため、従来の磁気パターン層の作製に比して、
生産性が向上するという効果を奏する。また、本発明の
磁気記録媒体は、磁気パターン層が非硬化型の溶剤可溶
性熱可塑性樹脂を用いて形成され、他方、着色隠蔽層が
紫外線または電子線硬化型の無溶剤型インキで含有イン
キを用い、硬化させることによって形成されているた
め、着色隠蔽層を有機溶剤によって除去しようとして
も、除去されがたく、また除去される場合にも、着色隠
蔽層が除去されると同時またはそれ以前に、磁気パター
ン層が有機溶剤に溶解してしまう。したがって、着色隠
蔽層を除去して磁気パターン層の磁気パターンを目視す
ることが不可能であり、従来の磁気記録媒体に比して、
セキュリティ性が著しく向上している。The magnetic recording medium of the present invention does not use a curing agent in the formation of the magnetic pattern layer during its production.
The printing stability of screen printing is improved, printing for a long time is possible, the curing step is not required, and the curing of the colored concealing layer is completed instantaneously by ultraviolet rays or electron beams. Compared to the fabrication of the pattern layer,
This has the effect of improving productivity. Further, in the magnetic recording medium of the present invention, the magnetic pattern layer is formed by using a non-curable solvent-soluble thermoplastic resin, while the colored hiding layer is an ultraviolet or electron beam curable solventless ink containing ink. Since the colored hiding layer is formed by being used and cured, it is difficult to remove the colored hiding layer with an organic solvent, and even when it is removed, at the same time as or before the removal of the colored hiding layer. , The magnetic pattern layer is dissolved in the organic solvent. Therefore, it is impossible to remove the colored concealing layer to visually observe the magnetic pattern of the magnetic pattern layer, and compared with the conventional magnetic recording medium,
The security is remarkably improved.
Claims (1)
よび該磁気パターン層を隠蔽する着色隠蔽層よりなる磁
気記録媒体において、該磁気パターン層が磁性粉末が分
散された溶剤可溶性熱可塑性樹脂含有インキにより形成
されたものであり、該着色隠蔽層が顔料または染料を含
有する紫外線または電子線硬化型の無溶剤型インキによ
り形成されたものであることを特徴とする磁気記録媒
体。1. A magnetic recording medium comprising a magnetic pattern layer formed on a support and a colored masking layer for masking the magnetic pattern layer, wherein the magnetic pattern layer contains a solvent-soluble thermoplastic resin in which magnetic powder is dispersed. A magnetic recording medium, which is formed of an ink, wherein the colored hiding layer is formed of an ultraviolet or electron beam curable solventless ink containing a pigment or a dye.