JP2789703B2 - Manufacturing method of magnetic recording card - Google Patents

Manufacturing method of magnetic recording card

Info

Publication number
JP2789703B2
JP2789703B2 JP21042889A JP21042889A JP2789703B2 JP 2789703 B2 JP2789703 B2 JP 2789703B2 JP 21042889 A JP21042889 A JP 21042889A JP 21042889 A JP21042889 A JP 21042889A JP 2789703 B2 JP2789703 B2 JP 2789703B2
Authority
JP
Japan
Prior art keywords
magnetic
magnetic recording
barcode
recording layer
card
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP21042889A
Other languages
Japanese (ja)
Other versions
JPH0376026A (en
Inventor
則之 伊藤
政夫 黒岩
英彦 細
厚憲 長嶋
輝美 平野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP21042889A priority Critical patent/JP2789703B2/en
Publication of JPH0376026A publication Critical patent/JPH0376026A/en
Application granted granted Critical
Publication of JP2789703B2 publication Critical patent/JP2789703B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】 〔産業上の利用分野〕 近年、磁気記録カードはプリペイドカードを主流とし
て広く普及している。本発明は、プリペイドカード等で
用いられる、偽造防止の目的も兼ねた固定データ記録用
に設ける磁気バーコードを有する磁気記録カードにおい
て、磁気バーコードを磁気記録層中に埋め込み、磁気記
録層表面を平滑とならしめることによって隠蔽層表面を
平滑とし、磁気バーコードの存在を目視確認不可能とし
た磁気記録カードを提供することを目的とした製造方法
に関する。
DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] In recent years, magnetic recording cards have become widespread, mainly prepaid cards. The present invention is used in a prepaid card and the like, in a magnetic recording card having a magnetic barcode provided for fixed data recording also for the purpose of forgery prevention, embedded magnetic barcode in the magnetic recording layer, the surface of the magnetic recording layer The present invention relates to a manufacturing method for providing a magnetic recording card in which the surface of a concealing layer is made smooth by making it smooth, and the presence of a magnetic barcode cannot be visually confirmed.

〔従来技術〕 従来より磁気記録カードはIDカードあるいはプリペイ
ドカードとして多用されている。この磁気記録カードの
多くは、磁気バーコード3のダミーバーコード12を組み
合わせてセキュリティ性を付与するために、基材1上に
磁気記録層を塗布した後に、第3図に示すように、磁気
記録層2の上にスクリーン印刷、オフセット印刷等の方
法を用いて低保磁力の磁気バーコード3を設け、さらに
同様の方法で残留磁化のないダミーバーコード12を設け
ている。そして、その上に隠蔽性のインキを塗布して隠
蔽層4を形成し、磁気面を隠蔽している。
[Prior Art] Conventionally, magnetic recording cards have been frequently used as ID cards or prepaid cards. Many of these magnetic recording cards are provided with a magnetic recording layer as shown in FIG. 3 after a magnetic recording layer is applied on the base material 1 in order to provide security by combining the dummy barcode 12 of the magnetic barcode 3. A magnetic bar code 3 having a low coercive force is provided on the layer 2 by using a method such as screen printing or offset printing, and a dummy bar code 12 having no residual magnetization is provided by the same method. Then, a concealing ink is applied thereon to form a concealing layer 4 to conceal the magnetic surface.

〔発明が解決しようとする課題〕[Problems to be solved by the invention]

上記したように、磁気記録層2上に磁気バーコード3
を設けた磁気記録カードにおいては、カード自身のセキ
ュリティ性を、磁気バーコードによって記録された固定
データによって保持されている。
As described above, the magnetic barcode 3
, The security of the card itself is held by fixed data recorded by a magnetic barcode.

しかし、上記した従来の磁気記録カードの製造方法で
は、磁気記録カード3とダミーバーコード12の印刷の際
に見当がずれ易く、従来磁気記録カードをバーコード面
側から見ると、磁気バーコード3並びにダミーバーコー
ド12がお互いに上下にずれていることが多い。また、双
方のバーの材料が異なっているためにその平面性も異な
っている。したがって、隠蔽層4を設けても目視によっ
て真の磁気バーコード3およびダミーバーコード12の存
在確認および識別に比較的容易に可能である。この磁気
バーコード3、およびダミーバーコード12の識別が容易
であるという事実は、貨幣と同等の価値を持つ磁気記録
カードのセキュリティ性を低下させていることに他なら
ない。
However, in the above-described conventional method for manufacturing a magnetic recording card, the register is likely to be misaligned when printing the magnetic recording card 3 and the dummy barcode 12, and when the conventional magnetic recording card is viewed from the barcode surface side, the magnetic barcode 3 In many cases, the dummy barcodes 12 are vertically displaced from each other. Further, since the materials of the two bars are different, their flatness is also different. Therefore, even if the concealing layer 4 is provided, it is relatively easy to visually confirm and identify the presence of the true magnetic barcode 3 and the dummy barcode 12. The fact that the magnetic barcode 3 and the dummy barcode 12 can be easily identified is nothing less than a reduction in the security of a magnetic recording card having a value equivalent to money.

従って、以上のことを考慮すると、従来の製造方法に
よってなる磁気記録カードでは満足のいくセキュリティ
性を保持しているとは言えないのが実情である。
Therefore, in view of the above, it is a fact that a magnetic recording card manufactured by a conventional manufacturing method cannot be said to have satisfactory security.

本発明は上述のような問題を解決するためになされた
もので、磁気バーコード3を目視確認不可能とした磁気
記録カードを製造するための方法を提供することを目的
とする。
The present invention has been made to solve the above-described problem, and has as its object to provide a method for manufacturing a magnetic recording card in which the magnetic barcode 3 cannot be visually confirmed.

〔課題を解決するための手段〕[Means for solving the problem]

上記の目的を達成するため、本発明の製造方法は磁気
記録層2上に設けた磁気バーコード3を加熱加圧によっ
て磁気記録層中に埋め込み、磁気記録層2表面を平滑と
したことを特徴としており、この上に隠蔽層4を設ける
ことにより、磁気バーコード3は目視確認不可能とな
る。
In order to achieve the above object, the manufacturing method of the present invention is characterized in that the magnetic barcode 3 provided on the magnetic recording layer 2 is embedded in the magnetic recording layer by heating and pressing to smooth the surface of the magnetic recording layer 2. By providing the concealing layer 4 thereon, the magnetic barcode 3 cannot be visually checked.

〔作用〕[Action]

本発明の製造方法によってなる磁気記録カードは、目
視による磁気バーコード3の存在確認が不可能となるた
めに、セキュリティ性が向上し、偽造・複製が一段と困
難になり、また、磁気バーコード3と併用されているダ
ミーバーコード12も不用となる。さらには、カード表面
に突起物がなくなることから、磁気ヘッドの耐摩耗性が
向上し、カードの寿命が延びることが期待される。
The magnetic recording card manufactured by the manufacturing method according to the present invention makes it impossible to visually confirm the presence of the magnetic barcode 3, thereby improving security, making forgery / duplication even more difficult. The dummy barcode 12 used in combination with is also unnecessary. Furthermore, since there is no protrusion on the card surface, it is expected that the wear resistance of the magnetic head is improved and the life of the card is extended.

〔実施例〕〔Example〕

以下、本発明の実施例について図面を参照して詳細に
説明する。
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.

第1図は本発明に係る磁気記録カードの構成を示す断
面図である。基材1上に磁気記録層2を設け、加熱加圧
によって磁気バーコード3が磁気記録層2中に埋め込ま
れている。さらにその上から、隠蔽層4を設けている。
FIG. 1 is a sectional view showing a configuration of a magnetic recording card according to the present invention. A magnetic recording layer 2 is provided on a substrate 1, and a magnetic barcode 3 is embedded in the magnetic recording layer 2 by heating and pressing. Further, a concealing layer 4 is provided thereon.

基材1はポリ塩化ビニル、ポリエステル、ポリカーボ
ネート、ポリメタクリル酸メチル、ポリスチレン等のプ
ラスチック類、紙、合成紙などを単独でまたは複合体と
して用いることが出来る。磁気記録層2は、磁性粉、例
えばγ−Fe2O3、Co被着γ−Fe2O3、Fe3O4、CrO2、Fe、F
e−Cr、Fe−Co、Co−Cr、Co−Ni、MnAl、Baフェライ
ト、Srフェライトなどの従来公知の磁性微粒子を適当な
樹脂に分散し、この分散液を基材1上に、バーコード、
ブレードコート、エアナイフコート、グラビアコート、
ロールコート、等のソルベントコート法、あるいはスク
リーン印刷法により、塗布、乾燥して形成する。尚、こ
の際に用いられる樹脂としては、ポリウレタン樹脂、塩
化ビニル−酢酸ビニル共重合体、ポリエステル樹脂等が
考えられるが、磁気記録層2中に磁気バーコード3を埋
め込むためには、熱可塑性が高い樹脂が好ましい。しか
しながら、これに限ることはなく。熱硬化性の樹脂であ
ってもこれを未硬化の状態で用いることが出来る。磁気
バーコード3は、低保磁力の磁性粉、例えば、Fe、Ni、
Zn−フェライト、Ni−Zn−フェライト、Mn−Zn−フェラ
イト、Fe2O3等、あるいはパーマロイ、センダスト等の
合金を適当な樹脂に分散して、スクリーン印刷、オフセ
ット印刷、グラビア印刷等の方法を用いて、磁気記録層
2上に磁気バーコード3を形成する。尚、この際に用い
られる樹脂としては、ポリウレタン樹脂、塩化ビニル−
酢酸ビニル共重合体、ポリエステル樹脂、エポキシ樹脂
等が考えられるが、磁気記録層2中へ磁気バーコード3
をひび割れやつぶれ等が起こらないように埋め込むため
には、磁気バーコード3が十分な強度を有していること
が望ましいため、イソシアネート系等の硬化剤を用い
て、十分に硬化させるのが好ましい。しかしながら、こ
れに限るものではなく、未硬化の状態であっても、磁気
記録層2よりも磁気バーコード3の方が相対的に強度が
高ければ、何等差し仕えはない。
As the substrate 1, plastics such as polyvinyl chloride, polyester, polycarbonate, polymethyl methacrylate, and polystyrene, paper, synthetic paper, and the like can be used alone or as a composite. The magnetic recording layer 2 is made of a magnetic powder such as γ-Fe 2 O 3 , Co-coated γ-Fe 2 O 3 , Fe 3 O 4 , CrO 2 , Fe, F
Conventionally known magnetic fine particles such as e-Cr, Fe-Co, Co-Cr, Co-Ni, MnAl, Ba ferrite, and Sr ferrite are dispersed in a suitable resin, and this dispersion is placed on a substrate 1 by a bar code. ,
Blade coat, air knife coat, gravure coat,
It is formed by applying and drying by a solvent coating method such as a roll coating method or a screen printing method. In addition, as the resin used at this time, a polyurethane resin, a vinyl chloride-vinyl acetate copolymer, a polyester resin, and the like can be considered. In order to embed the magnetic barcode 3 in the magnetic recording layer 2, thermoplastic resin is required. High resins are preferred. However, it is not limited to this. Even a thermosetting resin can be used in an uncured state. The magnetic barcode 3 is made of a magnetic powder having a low coercive force, for example, Fe, Ni,
Zn- ferrite, Ni-Zn- ferrite, Mn-Zn- ferrite, Fe 2 O 3, etc., or permalloy, and dispersed alloy such as sendust in a suitable resin, screen printing, offset printing, a method of gravure printing The magnetic barcode 3 is formed on the magnetic recording layer 2 by using. The resin used at this time was polyurethane resin, vinyl chloride-
A vinyl acetate copolymer, a polyester resin, an epoxy resin, or the like can be considered.
It is preferable that the magnetic barcode 3 has a sufficient strength in order to embed the magnetic barcode 3 so as not to cause cracking or crushing. Therefore, it is preferable that the magnetic barcode 3 is sufficiently cured using a curing agent such as isocyanate. . However, the present invention is not limited to this, and even in an uncured state, if the magnetic barcode 3 has a relatively higher strength than the magnetic recording layer 2, nothing is done.

以上のようにして磁気記録層2上に形成した磁気バー
コード3をプレス機を用いて加熱加圧によって埋め込
む。隠蔽層4としては、金、銀等の隠蔽性のインキを用
いてグラブア印刷、オフセット印刷、スクリーン印刷、
リバースロールコート等の方法を用いて形成する。
The magnetic barcode 3 formed on the magnetic recording layer 2 as described above is embedded by heating and pressing using a press machine. As the concealing layer 4, gravure printing, offset printing, screen printing,
It is formed using a method such as reverse roll coating.

以下、実際の試作例について述べる。 Hereinafter, an actual prototype will be described.

試作例(1) 磁気記録層用インキ: 磁性粉MC−127(戸田工業(株)) 50部 塩化ビニル−酢酸ビニル共重合体樹脂VAGH (ユニオンカーバイド(株)) 20部 溶剤VC202(東洋インキ製造(株)) 100部 以上の組成によってなる磁気塗料を188μm厚のポリ
エチレンテレフタレートフィルムにグラビア法を用いて
塗布し、15μm厚の磁気記録層2を形成した。次に、以
下の組成からなる磁気バーコード用インキを用いて、ス
クリーン印刷法によって盛り厚10μmの磁気バーコード
を形成した後、70℃で48時間のエージングを行い、磁気
バーコード3を十分に硬化させた。
Prototype example (1) Ink for magnetic recording layer: Magnetic powder MC-127 (Toda Kogyo Co., Ltd.) 50 parts Vinyl chloride-vinyl acetate copolymer resin VAGH (Union Carbide Co., Ltd.) 20 parts Solvent VC202 (Toyo Ink Manufacturing) 100 parts of a magnetic paint having the above composition was applied to a 188 μm-thick polyethylene terephthalate film by a gravure method to form a 15 μm-thick magnetic recording layer 2. Next, using a magnetic barcode ink having the following composition, a magnetic barcode having a thickness of 10 μm was formed by a screen printing method, followed by aging at 70 ° C. for 48 hours to sufficiently remove the magnetic barcode 3. Cured.

磁気バーコード用インキ: 鉄粉 50部 塩化ビニル−酢酸ビニル共重合樹脂VAGH (ユニオンカーバイド(株)) 10部 溶剤S−787(東洋インキ製造(株)) 40部 イソシアネート系硬化剤コロネートHL (日本ポリウレタン工業(株)) 2部 さらに、ホットプレス機を用いて、以下の条件で加熱
加圧し、磁気バーコード3を磁気記録層2中に埋め込ん
だ。
Magnetic barcode ink: Iron powder 50 parts Vinyl chloride-vinyl acetate copolymer resin VAGH (Union Carbide Co., Ltd.) 10 parts Solvent S-787 (Toyo Ink Mfg. Co., Ltd.) 40 parts Isocyanate curing agent Coronate HL (Japan Polyurethane Industry Co., Ltd. 2 parts Further, using a hot press machine, the magnetic bar code 3 was embedded in the magnetic recording layer 2 by heating and pressing under the following conditions.

ホットプレス条件: 1次加圧 18kg/cm2、100℃ 2次加圧 50kg/cm2、100℃ 最後に、磁気記録層2の上に、市販の隠蔽性の銀イン
キを用いてスクリーン印刷によって隠蔽層4を設けた。
Hot pressing conditions: primary pressure 18 kg / cm 2 , 100 ° C. secondary pressure 50 kg / cm 2 , 100 ° C. Finally, on the magnetic recording layer 2 by screen printing using a commercially available concealable silver ink The concealing layer 4 was provided.

試作例(2) 磁気記録層用インキ: 磁性粉MC−127(戸田工業(株)) 50部 塩化ビニル−酢酸ビニル共重合体樹脂VAGH (ユニオンカーバイド(株)) 10部 ポリウレタン樹脂ニッポラン2304 (日本ポリウレタン工業(株)) 10部 溶剤VC202(東洋インキ製造(株)) 100部 イソシアネート系硬化剤コロネートHL 4部 以上の組成によってなる磁気塗料を188μm厚のポリ
エチレンテレフタレートフィルムにグラビア法を用いて
塗布し、15μm厚の磁気記録層2を形成した。次に以下
の組成からなる磁気バーコード用インキを用いて、スク
リーン印刷法によって盛り厚10μmの磁気バーコードを
形成した。
Prototype example (2) Ink for magnetic recording layer: Magnetic powder MC-127 (Toda Kogyo Co., Ltd.) 50 parts Vinyl chloride-vinyl acetate copolymer resin VAGH (Union Carbide Co., Ltd.) 10 parts Polyurethane resin Nipporan 2304 (Japan Polyurethane Industry Co., Ltd. 10 parts Solvent VC202 (Toyo Ink Manufacturing Co., Ltd.) 100 parts Isocyanate-based curing agent Coronate HL 4 parts A magnetic paint with the above composition is applied to a 188 μm thick polyethylene terephthalate film by gravure method. The magnetic recording layer 2 having a thickness of 15 μm was formed. Next, using a magnetic barcode ink having the following composition, a magnetic barcode having a thickness of 10 μm was formed by a screen printing method.

磁気バーコード用インキ: 鉄粉 50部 塩化ビニル−酢酸ビニル共重合樹脂VAGH (ユニオンカーバイド(株)) 10部 溶剤S−787(東洋インキ製造(株)) 40部 イソシアネート系硬化剤コロネートHL (日本ポリウレタン工業(株)) 2部 さらに、ホットプレス機を用いて、以下の条件で加熱
加圧し、磁気バーコード3を磁気記録層2中に埋め込ん
だ。その後に、70℃で48時間のエージングを行なった。
Magnetic barcode ink: Iron powder 50 parts Vinyl chloride-vinyl acetate copolymer resin VAGH (Union Carbide Co., Ltd.) 10 parts Solvent S-787 (Toyo Ink Mfg. Co., Ltd.) 40 parts Isocyanate curing agent Coronate HL (Japan Polyurethane Industry Co., Ltd. 2 parts Further, using a hot press machine, the magnetic bar code 3 was embedded in the magnetic recording layer 2 by heating and pressing under the following conditions. Thereafter, aging was performed at 70 ° C. for 48 hours.

ホットプレス条件: 1次加圧 10kg/cm2、100℃ 2次加圧 50kg/cm2、100℃ 最後に、磁気記録層2の上に、市販の隠蔽性の銀イン
キを用いてスクリーン印刷によって隠蔽層4を設けた。
Hot pressing conditions: primary pressurization 10 kg / cm 2 , 100 ° C. secondary pressurization 50 kg / cm 2 , 100 ° C. Finally, on the magnetic recording layer 2 by screen printing using a commercially available concealable silver ink The concealing layer 4 was provided.

以上2例の方法によって得られた磁気記録カードの裏
面は完全に平滑で磁気バーコードの存在の確認は目視に
よっては全く不可能であり、このカードが高いセキュリ
ティ性を保持していることが分かる。
The back surface of the magnetic recording card obtained by the above two methods is completely smooth, and it is impossible to visually confirm the presence of the magnetic barcode at all. It can be seen that this card has high security. .

また、この磁気記録カードに磁場を印加して磁気バー
コード3の出力特性を調べたところ、第2図のような特
性図が得られ、磁気バーコード3は確実に動作している
ことが分かった。
Further, when a magnetic field was applied to the magnetic recording card and the output characteristics of the magnetic barcode 3 were examined, a characteristic diagram as shown in FIG. 2 was obtained, and it was found that the magnetic barcode 3 was operating reliably. Was.

〔発明の効果〕〔The invention's effect〕

以上詳述した通り、磁気バーコード3が目視確認不可
能ということから、本発明は従来と比較してよりセキュ
リティ性の高い磁気記録カードを提供することが可能で
ある。また、従来用いていたダミーバーコード12が不用
となることから、問題点の一つであった磁気バーコード
3とダミーバーコード12の印刷の見当精度に依存しない
セキュリティ性を実現することが出来る。さらには、磁
気記録カード裏面、すなわち磁気記録面側の突起がなく
なることから、磁気ヘッドに対する耐摩耗性が向上し、
カード寿命が延長する事や、カード裏面全体への印刷・
印字が機能となるなど、実用面での効果は大きいと考え
られる。
As described in detail above, since the magnetic barcode 3 cannot be visually checked, the present invention can provide a magnetic recording card with higher security than the conventional one. Also, since the conventionally used dummy barcode 12 becomes unnecessary, it is possible to realize security which does not depend on the registration accuracy of printing of the magnetic barcode 3 and the dummy barcode 12, which is one of the problems. Furthermore, since there is no protrusion on the back side of the magnetic recording card, that is, the magnetic recording surface side, the wear resistance to the magnetic head is improved,
Extending the life of the card, printing on the entire back of the card,
It is considered that the effect in practical use is large, for example, printing becomes a function.

【図面の簡単な説明】[Brief description of the drawings]

図面は本発明の実施例を示すもので、第1図は本発明の
製造方法を用いて作られた磁気記録カードの構成を示す
断面図、第2図は磁気バーコードの出力波形を示す特性
図である。 また、第3図は従来の技術を説明するものであって、磁
気記録カードの構成を示す断面図である。 1……基材、2……磁気記録層、3……磁気バーコー
ド、4……隠蔽層、12……ダミーバーコード
1 shows an embodiment of the present invention. FIG. 1 is a cross-sectional view showing a configuration of a magnetic recording card manufactured by using the manufacturing method of the present invention, and FIG. 2 is a characteristic showing an output waveform of a magnetic bar code. FIG. FIG. 3 is a cross-sectional view illustrating a configuration of a magnetic recording card for explaining a conventional technique. DESCRIPTION OF SYMBOLS 1 ... Base material 2 ... Magnetic recording layer 3 ... Magnetic barcode 4 ... Concealment layer 12 ... Dummy barcode

───────────────────────────────────────────────────── フロントページの続き (72)発明者 平野 輝美 東京都台東区台東1丁目5番1号 凸版 印刷株式会社内 審査官 北岡 浩 (56)参考文献 特開 昭54−71699(JP,A) 特開 昭61−139498(JP,A) (58)調査した分野(Int.Cl.6,DB名) G11B 5/62 - 5/858──────────────────────────────────────────────────続 き Continuation of the front page (72) Inventor Terumi Hirano Examiner Hiroshi Kitaoka, Toppan Printing Co., Ltd., 1-5-1, Taito, Taito-ku, Tokyo (56) References JP-A-54-71699 (JP, A) JP-A-61-139498 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) G11B 5/62-5/858

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】磁気記録層上に磁気バーコードを設けてな
る磁気記録カードにおいて、熱可塑性樹脂を用いた磁気
塗料によって形成された磁気記録層上に熱硬化性樹脂か
らなる磁気バーコードを形成し、かかる磁気バーコード
を加熱硬化させた後に、加熱加圧によって磁気記録層中
に埋め込み、磁気記録層表面を平滑とし、前記磁気記録
層上に隠蔽層を設けることにより、磁気バーコードを目
視確認不可能とならしめたことを特徴とする磁気記録カ
ードの製造方法。
In a magnetic recording card having a magnetic barcode provided on a magnetic recording layer, a magnetic barcode made of a thermosetting resin is formed on a magnetic recording layer formed of a magnetic paint using a thermoplastic resin. After the magnetic barcode is cured by heating, the magnetic barcode is embedded in the magnetic recording layer by heating and pressing, the surface of the magnetic recording layer is smoothed, and a concealing layer is provided on the magnetic recording layer, so that the magnetic barcode can be visually observed. A method for manufacturing a magnetic recording card, characterized in that it is impossible to confirm.
【請求項2】特許請求項第1項記載の磁気記録カードに
おいて、熱硬化性樹脂を樹脂を用いた磁気塗料によって
形成された磁気記録層上に、熱硬化樹脂からなる磁気バ
ーコードを形成し、双方が未硬化の状態で、磁気バーコ
ードを加熱加圧によって磁気記録層中に埋め込み表面を
平滑とならしめた後に加熱硬化させ、かかる磁気記録層
表面上に隠蔽層を設け、磁気バーコードを目視確認不可
能とすることを特徴とする磁気記録カードの製造方法。
2. A magnetic recording card according to claim 1, wherein a magnetic barcode made of a thermosetting resin is formed on a magnetic recording layer formed by a magnetic paint using a thermosetting resin as a resin. In a state in which both are uncured, the magnetic barcode is embedded in the magnetic recording layer by applying heat and pressure, the surface is smoothed, and then cured by heating, and a concealing layer is provided on the surface of the magnetic recording layer, and the magnetic barcode is provided. A method for manufacturing a magnetic recording card, wherein visual confirmation is impossible.
JP21042889A 1989-08-15 1989-08-15 Manufacturing method of magnetic recording card Expired - Fee Related JP2789703B2 (en)