JP2511379B2 - Polyolefin fastener-attached packaging material and method for producing the same - Google Patents
Polyolefin fastener-attached packaging material and method for producing the sameInfo
- Publication number
- JP2511379B2 JP2511379B2 JP5289835A JP28983593A JP2511379B2 JP 2511379 B2 JP2511379 B2 JP 2511379B2 JP 5289835 A JP5289835 A JP 5289835A JP 28983593 A JP28983593 A JP 28983593A JP 2511379 B2 JP2511379 B2 JP 2511379B2
- Authority
- JP
- Japan
- Prior art keywords
- fastener
- packaging material
- male
- female
- polyolefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ポリオレフィン製ファ
スナー付包材およびその製造方法に関するものであり、
さらに詳しくは高周波誘電加熱により融着・溶断可能で
ある特定のポリオレフィン系樹脂あるいはその組成物を
用いて製造される、焼却しても有毒ガスなどの発生がな
く、リサイクルが容易など地球環境に優しいポリオレフ
ィン製ファスナー付包材およびその製造方法に関するも
のである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyolefin wrapping material with a fastener and a method for producing the same.
More specifically, it is manufactured using a specific polyolefin resin or its composition that can be fused and cut by high frequency dielectric heating, does not generate toxic gas even when incinerated, and is easy to recycle and is environmentally friendly. The present invention relates to a packaging material with a fastener made of polyolefin and a manufacturing method thereof.
【０００２】[0002]
【従来の技術】従来、ポリ塩化ビニルのフィルムやシー
トを使用して高周波誘電加熱により融着・溶断して製造
されたファスナー付包材が知られている。しかしポリ塩
化ビニルはフィルムやシートの溶融成形時に塩酸、塩素
などの酸性有毒ガスが発生して作業環境を悪化する、押
出機などの成形加工機を腐食する、可塑剤の安全性の問
題がある、又焼却すると上記有害ガスが発生して地球環
境を汚染するなどの問題がある。2. Description of the Related Art Hitherto, there has been known a packaging material with a fastener which is manufactured by fusion-melting and melting by high frequency dielectric heating using a polyvinyl chloride film or sheet. However, polyvinyl chloride has acidic and toxic gases such as hydrochloric acid and chlorine during melt molding of films and sheets, which worsens the working environment, corrodes molding machines such as extruders, and has a safety problem with plasticizers. Further, when incinerated, there is a problem that the harmful gas is generated and pollutes the global environment.
【０００３】一方、ポリオレフィン系樹脂あるいはその
組成物はポリ塩化ビニルのような問題が全くなく、焼却
しても有毒ガスなどの発生がなく地球環境に優しい素材
であるが、ポリオレフィン系樹脂あるいはその組成物は
高周波誘電加熱による融着・溶断が困難であり、上記の
ようなポリ塩化ビニル製ファスナー付包材は製造されて
いなかった。ポリオレフィン系樹脂あるいはその組成物
は通常のヒートシール法、超音波融着法などにより融着
可能であるので、これらの方法により上記ポリ塩化ビニ
ル製ファスナー付包材を製造する試みがなされている
が、製造効率が悪く、コスト高になる欠点があった。On the other hand, the polyolefin resin or its composition has no problems like polyvinyl chloride, and is a material which is kind to the global environment without generating toxic gas even when incinerated. It is difficult to fuse and melt the product by high frequency dielectric heating, and the above-mentioned packaging material with a polyvinyl chloride fastener has not been manufactured. Since the polyolefin resin or its composition can be fused by the usual heat sealing method, ultrasonic welding method, etc., attempts have been made to produce the polyvinyl chloride fastener packaging material by these methods. However, the manufacturing efficiency is poor and the cost is high.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、焼却
しても有毒ガスなどの発生がなく地球環境に優しいポリ
オレフィン系樹脂あるいはその組成物を用いて、高周波
誘電加熱法により安価に効率よく製造できる上、優れた
特性を有するファスナー付包材を提供することである。SUMMARY OF THE INVENTION The object of the present invention is to produce a high-frequency product by using a polyolefin resin or its composition that is environmentally friendly and does not generate toxic gas even when incinerated.
Another object of the present invention is to provide a packaging material with a fastener that can be manufactured inexpensively and efficiently by the dielectric heating method and that has excellent characteristics.
【０００５】[0005]
【問題を解決するための手段】本発明者らは、鋭意検討
の結果、ファスナー部と包材本体とをそれぞれ別個の高
周波誘電加熱により融着・溶断可能な特定のポリオレフ
ィン系樹脂あるいはその組成物を用いて製造することに
より、従来のポリ塩化ビニル用高周波ウエルダーを用い
て容易に優れた特性を有するポリオレフィン製ファスナ
ー付包材を得ることができることを見出し、本発明を成
すに至った。As a result of intensive studies, the inventors of the present invention have made a specific polyolefin resin or a composition thereof capable of fusing and fusing the fastener portion and the packaging material body by separate high frequency dielectric heating. It was found that a polyolefin-based fastener packaging material having excellent characteristics can be easily obtained by using a conventional high-frequency welder for polyvinyl chloride by manufacturing the same with the conventional method.
【０００６】本発明の第一の発明は、高周波誘電加熱に
より融着・溶断されてなるスライダー付ファスナー部と
包材本体とからなるファスナー付包材において、該ファ
スナー部および該包材本体はそれぞれ下記の特性を有す
るポリオレフィン系樹脂あるいはその組成物からなるこ
とを特徴とするポリオレフィン製ファスナー付包材であ
る。 該ファスナー部： 誘電率２．３以上で高周波誘電加熱により融着・溶断可
能であると共に該ファスナー雌雄嵌合強度１．０Ｋｇ以
上となる剛性を有し、かつ該ファスナー部同士のシール
強度が４．８Ｋｇ／１５ｍｍ以上、該ファスナー部と該
包材本体とのシール強度が２．５Ｋｇ／１５ｍｍ以上と
なるポリオレフィン系樹脂あるいはその組成物。 該包材本体： 誘電率２．３以上で高周波誘電加熱により融着・溶断可
能であり、かつ該包材本体同士のシール強度が２．９Ｋ
ｇ／１５ｍｍ以上、該ファスナー部と該包材本体とのシ
ール強度が２．５Ｋｇ／１５ｍｍ以上が得られるような
ポリオレフィン系樹脂あるいはその組成物。The first invention of the present invention is a fastener-equipped packaging material comprising a slider-equipped fastener portion and a packaging material body, which are fused and fused by high frequency dielectric heating, wherein the fastener portion and the packaging material body are respectively A polyolefin-based packaging material with a fastener, comprising a polyolefin resin or a composition thereof having the following characteristics. The fastener part has a dielectric constant of 2.3 or more and can be fused and melted by high frequency dielectric heating, has a rigidity such that the male and female fitting strength of the fastener is 1.0 kg or more, and has a sealing strength of 4 between the fastener parts. A polyolefin-based resin or a composition thereof, which has a sealing strength of 2.5 kg / 15 mm or more and a sealing strength between the fastener part and the packaging material body of 2.5 kg / 15 mm or more. The packaging material body: A dielectric constant of 2.3 or more, which can be fused and cut by high frequency dielectric heating, and a sealing strength between the packaging material bodies is 2.9K.
g / 15 mm or more, and a polyolefin resin or a composition thereof, which can obtain a sealing strength between the fastener part and the packaging material body of 2.5 kg / 15 mm or more.
【０００７】本発明の第二の発明は、下記の工程からな
ることを特徴とする請求項１記載のポリオレフィン製フ
ァスナー付包材の製造方法である。 （１）請求項１記載のポリオレフィン系樹脂あるいはそ
の組成物を用いてファスナー雌部およびファスナー雄部
を異型成形する。 （２）請求項１記載のポリオレフィン系樹脂あるいはそ
の組成物を用いて包材本体用フィルムあるいはシートを
成形する。 （３）ファスナー雌部あるいはファスナー雄部を包材本
体用フィルムあるいはシートの一端に高周波誘電加熱に
より融着する工程。 （４）ファスナー雄部あるいはファスナー雌部を該包材
本体用フィルムあるいはシートの他端に高周波誘電加熱
により融着するか、あるいはファスナー雄部あるいはフ
ァスナー雌部を他の包材本体用フィルムあるいはシート
の一端に高周波誘電加熱により融着する工程。 （５）一端にファスナー雄部を他端にファスナー雌部を
高周波誘電加熱により融着した該包材本体用フィルムあ
るいはシートの該ファスナー雄部と該ファスナー雌部と
をスライダーを用いて雌雄嵌合させるか、あるいはファ
スナー雌部あるいはファスナー雄部を包材本体用フィル
ムあるいはシートの一端に高周波誘電加熱により融着し
たものと、ファスナー雄部あるいはファスナー雌部を他
の包材本体用フィルムあるいはシートの一端に高周波誘
電加熱により融着したものの該ファスナー雄部と該ファ
スナー雌部とをスライダーを用いて雌雄嵌合させ、高周
波誘電加熱により融着・溶断してスライダーが付いたフ
ァスナー付包材を製造する工程。A second invention of the present invention is the method for producing a polyolefin-made packaging material with a fastener according to claim 1, which comprises the following steps. (1) Using the polyolefin-based resin or the composition thereof according to claim 1, the female fastener portion and the male fastener portion are molded by atypical molding. (2) A film or sheet for a packaging material body is molded using the polyolefin resin or its composition according to claim 1. (3) A step of fusion-bonding the female fastener portion or the male fastener portion to one end of the packaging material body film or sheet by high-frequency dielectric heating. (4) A male fastener part or a female fastener part is fused to the other end of the film or sheet for a packaging material body by high frequency dielectric heating, or a male fastener part or a female fastener part is formed on another film or sheet for a packaging material body. The process of fusion-bonding to one end by high frequency dielectric heating. (5) Male / female fitting of the male fastener portion and the female fastener portion of the film or sheet for the packaging material main body in which a male male portion at one end and a female female portion at the other end are fused by high frequency dielectric heating using a slider. Or a female fastener part or a male fastener part fused to one end of a packaging material film or sheet by high frequency dielectric heating, and a male fastener part or a female fastener part of another packaging material film or sheet. High frequency induction at one end
A step of manufacturing a fastener-equipped packaging material with a slider by fusion-bonding the male fastener portion and the female female portion of the fastener, which are fused by electric heating, by using a slider, and fusing and fusing by high-frequency dielectric heating.
【０００８】[0008]
【作用】図１および図２は、本発明のポリオレフィン製
ファスナー付包材１およびファスナー部を開いた状態を
示す斜視図である。スライダー２、ファスナー部３、包
材本体４、ファスナー雌部本体１１ａのあるファスナー
雌部３ａ、ファスナー雄部本体１１ｂのあるファスナー
雄部３ｂ、ファスナー雌部本体１１ａとファスナー雄部
本体１１ｂの雌雄嵌合部１１、ファスナー部３同士のシ
ール部１２、ファスナー部３と包材本体４とのシール部
１３、包材本体４同士のシール部１４などから構成され
ている。1 and 2 are perspective views showing the state in which the polyolefin wrapping material with a fastener 1 and the fastener portion of the present invention are opened. The slider 2, the fastener portion 3, the packaging body 4, the female fastener portion 3a having the female fastener portion body 11a, the male fastener portion 3b having the male fastener portion body 11b, and the male and female fitting of the female fastener portion body 11a and the male fastener portion body 11b. It includes a joint portion 11, a seal portion 12 between the fastener portions 3, a seal portion 13 between the fastener portion 3 and the packaging material body 4, a seal portion 14 between the packaging material bodies 4, and the like.
【０００９】図３〜図８に本発明のポリオレフィン製フ
ァスナー付包材の他の実施態様を示す。図９は、本発明
のポリオレフィン製ファスナー付包材のファスナー雌部
３ａおよびファスナー雄部３ｂ［横型レールファスナー
３ＰＶＨ（吉田工業（株）製）成形用金型を用いて異型
成形したもの］の拡大説明図である。本発明のポリオレ
フィン製ファスナー付包材はこれらに限定されるもので
はなく、大きさ、厚さ、形状、色、透明性、印刷の有無
など使用目的により適宜決めることができる。本発明の
ポリオレフィン製ファスナー付包材の前面の包材本体に
透明なものを使用し、後面の包材本体に不透明なものを
使用して内容物を入れた時、外から内容物が見えるよう
にしたり、前面と後面との色を変えたりすることも適宜
選択して行われる。スライダー２の材質、形状、様式な
どは公知のものを使用することができ、材質としては例
えばポリオキシメチレン樹脂、ナイロンなどのエンジニ
ヤリング樹脂を挙げることができる。ファスナーの雌雄
嵌合方式も特に限定されるものではなく、公知のものを
用いることができる。3 to 8 show another embodiment of the packaging material with a fastener made of polyolefin of the present invention. FIG. 9 is an enlarged view of the female fastener portion 3a and the male fastener portion 3b of the polyolefin-based packaging material with a fastener according to the present invention [atypically molded using a horizontal rail fastener 3PVH (manufactured by Yoshida Kogyo KK)]. FIG. The polyolefin wrapping material with a fastener of the present invention is not limited to these, and can be appropriately determined depending on the purpose of use such as size, thickness, shape, color, transparency, and presence of printing. When the transparent packaging material body of the polyolefin fastener packaging material of the present invention is used and the wrapping material body of the rear surface is opaque, the contents can be seen from the outside. Alternatively, the color of the front surface and the color of the rear surface may be appropriately selected. As the material, shape, style, etc. of the slider 2, known materials can be used, and examples of the material include an engineering resin such as polyoxymethylene resin and nylon. The male and female fitting method of the fastener is not particularly limited, and a known one can be used.
【００１０】本発明においては、ファスナー部３と包材
本体４とをそれぞれ別個の高周波誘電加熱により融着・
溶断可能な特定のポリオレフィン系樹脂あるいはその組
成物を用いることが肝要である。In the present invention, the fastener portion 3 and the packaging material body 4 are fused and welded by separate high frequency dielectric heating.
It is important to use a specific polyolefin resin that can be blown or a composition thereof.
【００１１】該ファスナー部用ポリオレフィン系樹脂あ
るいはその組成物は、ファスナー雌部３ａおよびファス
ナー雄部３ｂを押出成形などの公知の成形方法により反
りや曲がりなしに容易に寸法精度よく異型成形すること
ができ、かつ誘電率（ＪＩＳＫ６７６０に準じて測定し
たもの）２．３以上で高周波誘電加熱により融着・溶断
可能であると共に、厚さ約３００μｍの該ファスナー雌
部３ａと同厚さの該ファスナー雄部３ｂ［横型レールフ
ァスナー３ＰＶＨ（吉田工業（株）製）成形用金型を用
いて異型成形したもの］を嵌合させてその雌雄嵌合強度
を１８０°方向、引張速度２５０ｍｍ／分で試験した
時、１．０Ｋｇ／１５ｍｍ以上となるような剛性を有す
ると共に、下記条件で高周波誘電加熱により融着した該
ファスナー部３同士のシール部１２のシール強度を１８
０°方向、引張速度２５０ｍｍ／分で試験した時、４．
８Ｋｇ／１５ｍｍ以上であり、該ファスナー部３と厚さ
約１００μｍの該包材本体４とのシール部１３の同シー
ル強度が２．５Ｋｇ／１５ｍｍ以上を示すものであるこ
とが好ましい。The polyolefin resin for the fastener portion or the composition thereof can be easily molded with high dimensional accuracy without warping or bending by a known molding method such as extrusion molding of the female fastener portion 3a and the male fastener portion 3b. It has a dielectric constant (measured according to JIS K 6760) of 2.3 or more, and can be fused and cut by high frequency dielectric heating, and has the same thickness as the female fastener 3a having a thickness of about 300 μm. Part 3b [horizontal rail fastener 3PVH (manufactured by Yoshida Kogyo Co., Ltd.) to be molded by atypical molding] was fitted, and the male and female fitting strength was tested at 180 ° in a pulling speed of 250 mm / min. At this time, the fastener parts 3 have rigidity such that they are 1.0 kg / 15 mm or more, and the fastener parts 3 are fused by high frequency induction heating under the following conditions. The seal strength of the seal part 12 is 18
3. When tested at 0 ° direction and a pulling speed of 250 mm / min, 4.
It is preferably 8 kg / 15 mm or more, and the sealing strength of the seal part 13 between the fastener part 3 and the packaging material body 4 having a thickness of about 100 μm is 2.5 kg / 15 mm or more.
【００１２】該ファスナー部の剛性が低く、雌雄嵌合強
度が１．０Ｋｇ／１５ｍｍ以下であると雌雄嵌合が各種
の用途に対して実用上不十分となる。シール部１２のシ
ール強度が４．８Ｋｇ／１５ｍｍ以下であると強度が不
十分であり、使用時にシール部１２の一部あるいは全部
剥離などが起こり、スライダー２が脱落するなどの不都
合が起こる。シール部１３のシール強度が２．５Ｋｇ／
１５ｍｍ以下であると強度が不十分であり実用上好まし
くない。さらに、該ファスナー雌部３ａとファスナー雄
部３ｂとの嵌合が容易であり、スライダー２の摺動回数
を重ねても摺動面が荒れたりせず、またスライダー２の
摺動時に削りかすがでず、容易に摺動させることができ
るポリオレフィン系樹脂あるいはその組成物であること
が望ましい。When the rigidity of the fastener portion is low and the male / female fitting strength is 1.0 kg / 15 mm or less, the male / female fitting becomes practically insufficient for various applications. If the seal strength of the seal portion 12 is 4.8 kg / 15 mm or less, the strength is insufficient, and part or all of the seal portion 12 may be peeled off during use, causing a problem such as the slider 2 falling off. The sealing strength of the sealing portion 13 is 2.5 kg /
If it is 15 mm or less, the strength is insufficient, which is not preferable in practical use. Further, the female fastener portion 3a and the male fastener portion 3b can be easily fitted to each other, the sliding surface does not become rough even if the slider 2 is slid many times, and scrapes are generated when the slider 2 slides. It is desirable that the polyolefin resin or its composition can be easily slid.
【００１３】高周波ウエルド条件； 高周波ウエルダー（精電舎電子工業株式会社製：ＫＷ−
４０００ＴＲ、高周波出力４ＫＷ、発振周波数４０．４
６ＭＨｚ±０．５９９％） ウエルド形式およびウエルド巾：ローレット、３ｍｍ
巾。 ウエルド圧力：４０ｋｇ／ｃｍ２。 ウエルド時間：３〜４秒（但し、ファスナー部３と包材
本体４の場合のみ１．３秒とする）。 ウエルドバー温度：７０〜７５℃。High-frequency weld condition; high-frequency welder (KW- manufactured by Seidensha Electronics Co., Ltd.)
4000TR, high frequency output 4KW, oscillation frequency 40.4
6 MHz ± 0.599%) Weld type and weld width: knurled, 3 mm
Width. Weld pressure: 40 kg / cm 2 . Weld time: 3 to 4 seconds (however, 1.3 seconds only for the fastener part 3 and the packaging material body 4). Weld bar temperature: 70-75 ° C.
【００１４】上記の特性を有していればエチレン酢酸ビ
ニル共重合体、エチレンアクリル酸共重合体、エチレン
メタクリル酸共重合体、エチレンアクリル酸アルキルエ
ステル共重合体、エチレンメタクリル酸アルキルエステ
ル共重合体、アイオノマーなどの２元あるいは３元以上
の共重合体あるいはそれらの混合物などのポリオレフィ
ン系樹脂であってもよく、あるいは高密度ポリエチレ
ン、低密度ポリエチレン、線状低密度ポリエチレン、ポ
リプロピレンなどと前記ポリオレフィン系樹脂などとの
組成物であっても差し支えない。An ethylene vinyl acetate copolymer, an ethylene acrylic acid copolymer, an ethylene methacrylic acid copolymer, an ethylene acrylic acid alkyl ester copolymer, or an ethylene methacrylic acid alkyl ester copolymer if it has the above-mentioned characteristics. It may be a polyolefin resin such as a binary or ternary or more copolymer such as an ionomer or a mixture thereof, or a high density polyethylene, a low density polyethylene, a linear low density polyethylene, polypropylene or the like and the above polyolefin series. It may be a composition with a resin or the like.
【００１５】該ファスナー部用ポリオレフィン系樹脂あ
るいはその組成物は、該包材本体用ポリオレフィン系樹
脂あるいはその組成物より特に剛性が要求される場合が
多いので上記の雌雄嵌合強度が１．０Ｋｇ／１５ｍｍ以
上となるような剛性を有することが肝要である。Since the polyolefin resin for the fastener portion or the composition thereof is required to have particularly higher rigidity than the polyolefin resin for the packaging material body or the composition thereof, the above-mentioned male and female fitting strength is 1.0 kg / It is important to have a rigidity of 15 mm or more.
【００１６】一方、該包材本体用ポリオレフィン系樹脂
あるいはその組成物は、シートやフィルムを押出成形な
どの公知の成形方法により容易に成形することができ、
かつ誘電率２．３以上で高周波誘電加熱により融着・溶
断可能であると共に、上記条件で高周波誘電加熱により
融着した厚さ約１００μｍの該包材本体４同士のシール
部１４のシール強度が２．９Ｋｇ／１５ｍｍ以上、該フ
ァスナー部３と該包材本体４とのシール部１３の同シー
ル強度が２．５Ｋｇ／１５ｍｍ以上を示すものであるこ
とが好ましい。シール部１４のシール強度が２．９Ｋｇ
／１５ｍｍ以下であると強度が不十分であり実用上好ま
しくない。また、シール部１３のシール強度が２．５Ｋ
ｇ／１５ｍｍ以下であると強度が不十分であり実用上好
ましくない。On the other hand, the polyolefin resin for the body of the packaging material or its composition can be easily molded into a sheet or film by a known molding method such as extrusion molding.
In addition, the dielectric constant of 2.3 or more enables fusion and fusing by high frequency dielectric heating, and the sealing strength of the seal portion 14 between the packaging body main bodies 4 having a thickness of about 100 μm fused by high frequency dielectric heating under the above conditions. It is preferable that the seal strength of the seal portion 13 between the fastener portion 3 and the packaging material body 4 is 2.9 kg / 15 mm or more and 2.5 kg / 15 mm or more. The sealing strength of the sealing portion 14 is 2.9 kg.
If it is / 15 mm or less, the strength is insufficient and it is not preferable in practical use. Also, the sealing strength of the seal portion 13 is 2.5K.
If it is g / 15 mm or less, the strength is insufficient and it is not preferable in practical use.
【００１７】上記の特性を有していれば該ファスナー部
の場合と同様にエチレン酢酸ビニル共重合体、エチレン
アクリル酸共重合体、エチレンメタクリル酸共重合体、
エチレンアクリル酸アルキルエステル共重合体、エチレ
ンメタクリル酸アルキルエステル共重合体、アイオノマ
ーなど２元あるいは３元以上の共重合体あるいはそれら
の混合物などのポリオレフィン系樹脂であってもよく、
あるいは高密度ポリエチレン、低密度ポリエチレン、線
状低密度ポリエチレン、ポリプロピレンなどと前記ポリ
オレフィン系樹脂などとの組成物であっても差し支えな
い。As long as it has the above-mentioned characteristics, as in the case of the fastener portion, ethylene vinyl acetate copolymer, ethylene acrylic acid copolymer, ethylene methacrylic acid copolymer,
It may be a polyolefin resin such as an ethylene acrylic acid alkyl ester copolymer, an ethylene methacrylic acid alkyl ester copolymer, an ionomer binary or ternary copolymer or a mixture thereof.
Alternatively, a composition of high-density polyethylene, low-density polyethylene, linear low-density polyethylene, polypropylene or the like and the polyolefin resin or the like may be used.
【００１８】以上の該ファスナー部３と該包材本体４を
使用すれば、使用する高周波ウエルダーやウエルド条件
は特に限定されるものではなく、通常ポリ塩化ビニルで
用いられている市販の高周波ウエルダーおよびウエルド
条件を使用することができる。しかし環境温度や高周波
ウエルドするフィルムやシートの温度、厚さなどの諸条
件が変化しても優れた高周波ウエルドを行うために、ウ
エルドバー温度は４０〜１００℃、好ましくは５０〜８
０℃、より好ましくは７０〜７５℃とし、ウエルドバー
と受台の間に高周波ウエルドするフィルムやシートを介
在させた時、受台と高周波ウエルドするフィルムやシー
トの間にテフロンコートクロスなどの易剥離性絶縁シー
トをさらに介在させると、高周波ウエルドしたフィルム
やシートの引き剥がれ性がよく、スパークを発してフィ
ルムやシートが焼けたり、ちじんだりしないので好まし
い。また、ウエルドバーの表面を剥離性にすることも好
ましい。If the fastener part 3 and the packaging material body 4 described above are used, the high-frequency welder and welding conditions to be used are not particularly limited, and commercially available high-frequency welders commonly used for polyvinyl chloride and Weld conditions can be used. However, the weld bar temperature is 40 to 100 ° C., preferably 50 to 8 ° C., in order to perform excellent high frequency welding even when various conditions such as the environmental temperature and the temperature and thickness of the film or sheet to be welded at high frequency are changed.
0 ° C, more preferably 70 to 75 ° C. When a high frequency welding film or sheet is interposed between the weld bar and the pedestal, a Teflon coat cloth or the like can be easily formed between the pedestal and the high frequency welding film or sheet. It is preferable to further interpose a peelable insulating sheet because the high-frequency welded film or sheet is easily peeled off and sparks do not cause the film or sheet to burn or crease. It is also preferable to make the surface of the weld bar releasable.
【００１９】図１０の（ａ）〜（ｆ）および図１１の
（ａ）〜（ｆ）に本発明のポリオレフィン製ファスナー
付包材の製造工程例を示す。まず図１０の（ａ）に示す
ように、（１）上記ポリオレフィン系樹脂あるいはその
組成物を用いてファスナー雌部３ａおよびファスナー雄
部３ｂを押出成形などの公知の成形方法により反りや曲
がりなしに寸法精度よく異型成形し、一方、（２）上記
ポリオレフィン系樹脂あるいはその組成物を用いて押出
成形などの公知の成形方法により包材本体４用フィルム
あるいはシートを成形して用意する。次いで、図１０の
（ｂ）〜（ｃ）に示すように、（３）ファスナー雄部３
ｂを包材本体４用フィルムあるいはシートの一端に公知
の高周波ウエルダーを用いて高周波誘電加熱により融着
し、（４）ファスナー雌部３ａを該包材本体４用フィル
ムあるいはシートの他端に高周波誘電加熱により融着す
る。そして図１０の（ｄ）〜（ｆ）に示すように、
（５）ファスナー部をウエルドした該包材本体４を折り
曲げて、該ファスナー雄部３ｂと該ファスナー雌部３ａ
とをスライダー２を用いて雌雄嵌合させ、複数個取りの
場合は複数のスライダーを用いて雌雄嵌合させて、高周
波誘電加熱により融着・溶断してスライダー２が付いた
ファスナー付包材１を製造する。FIGS. 10 (a) to 10 (f) and FIGS. 11 (a) to 11 (f) show an example of the manufacturing process of the polyolefin fastener-equipped packaging material of the present invention. First, as shown in FIG. 10 (a), (1) the above-mentioned polyolefin resin or composition thereof is used to form the female fastener portion 3a and the male fastener portion 3b by a known molding method such as extrusion molding without warping or bending. On the other hand, (2) a film or sheet for the packaging material main body 4 is prepared by molding using a known molding method such as extrusion molding using the above-mentioned polyolefin resin or its composition, while performing the profile molding with high dimensional accuracy. Next, as shown in (b) to (c) of FIG. 10, (3) Fastener male part 3
b is fused to one end of the film or sheet for the packaging material body 4 by high-frequency dielectric heating using a known high-frequency welder, and (4) the fastener female portion 3a is applied to the other end of the film or sheet for the packaging material body 4 with a high frequency wave. It fuses by dielectric heating. Then, as shown in (d) to (f) of FIG.
(5) The packaging material body 4 with the fastener portion welded is bent to form the fastener male portion 3b and the fastener female portion 3a.
And male and female are fitted together by using the slider 2, and when plural pieces are taken, male and female are fitted by using a plurality of sliders, which are fused and melted by high frequency dielectric heating to attach the fastener 2 to the fastener. To manufacture.
【００２０】また、図１１の（ａ）に示すように、
（１）上記ポリオレフィン系樹脂あるいはその組成物を
用いてファスナー雌部３ａおよびファスナー雄部３ｂを
押出成形などの公知の成形方法により反りや曲がりなし
に寸法精度よく異型成形し、一方、（２）上記ポリオレ
フィン系樹脂あるいはその組成物を用いて押出成形など
の公知の成形方法により包材本体４および４’用フィル
ムあるいはシートを成形して用意する。次いで、図１１
の（ｂ）〜（ｃ）に示すように、（３）ファスナー雄部
３ｂを包材本体４用フィルムあるいはシートの一端に公
知の高周波ウエルダーを用いて高周波誘電加熱により融
着し、（４）ファスナー雌部３ａを包材本体４’用フィ
ルムあるいはシートの一端に高周波誘電加熱により融着
する。そして図１１の（ｄ）〜（ｆ）に示すように、
（５）ファスナー部をウエルドした該包材本体４と４’
を重ねて、該ファスナー雄部３ｂと該ファスナー雌部３
ａとをスライダー２を用いて雌雄嵌合させ、複数個取り
の場合は複数のスライダーを用いて雌雄嵌合させて、高
周波誘電加熱により融着・溶断してスライダー２が付い
たファスナー付包材１’を製造する。公知の高周波ウエ
ルダーを用いて高周波誘電加熱により融着・溶断できる
ので作業は容易であり、効率よく本発明のポリオレフィ
ン製ファスナー付包材を製造することができる。Further, as shown in FIG. 11 (a),
(1) Using the above-mentioned polyolefin-based resin or its composition, the fastener female portion 3a and the fastener male portion 3b are profile-molded with good dimensional accuracy without warping or bending by a known molding method such as extrusion molding, while (2) A film or sheet for the packaging material main bodies 4 and 4'is prepared by molding a known molding method such as extrusion molding using the above polyolefin resin or its composition. Then, FIG.
As shown in (b) to (c) of (3), the male part 3b of the fastener is fused to one end of the film or sheet for the packaging material body 4 by high frequency dielectric heating using a known high frequency welder, and (4) The fastener female portion 3a is fused to one end of the film or sheet for the packaging body 4'by high frequency dielectric heating. Then, as shown in (d) to (f) of FIG.
(5) The packaging material main body 4 and 4'welded with the fastener part
The fastener male part 3b and the fastener female part 3
a and male and female are fitted together by using the slider 2, and when plural pieces are taken, male and female are fitted together, and the slider 2 is attached with the slider 2 by fusing and fusing by high frequency dielectric heating. 1'is manufactured. Since it can be fused and cut by high-frequency dielectric heating using a well-known high-frequency welder, the work is easy and the polyolefin fastener-wrapping material of the present invention can be efficiently produced.
【００２１】[0021]
【実施例】以下本発明を実施例により、具体的に説明す
るが、本発明はこれら実施例によって限定されるもので
はない。 （実施例１） 下記の組成の誘電率２．５〜２．７のポリオレフィン系
樹脂組成物を用いて、図９に示す厚さ約３００μｍのフ
ァスナー雌部３ａおよびファスナー雄部３ｂを押出成形
により成形した［横型レールファスナー３ＰＶＨ（吉田
工業（株）製）成形用金型を用いた］が、寸法精度よく
異型成形できた。 エチレン・メチルメタクリレート共重合体（商品名；アクリフトＷＫ３０７ 住友化学（株）製、エチレン７５重量％、ＭＭＡ２５重量％、ＥＭＭＡと略 す） ７０重量％ 高密度ポリエチレン（商品名；ハイゼックス３３００Ｆ、ＨＤＰＥと略す） ３０重量％ 滑剤（脂肪酸アマイド） ５００ｐｐｍEXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. Example 1 Using a polyolefin resin composition having a dielectric constant of 2.5 to 2.7 having the following composition, a female fastener portion 3a and a male fastener portion 3b having a thickness of about 300 μm shown in FIG. 9 were extruded. The formed [horizontal rail fastener 3PVH (manufactured by Yoshida Kogyo Co., Ltd.) molding die] was able to be profile-formed with high dimensional accuracy. Ethylene / methyl methacrylate copolymer (trade name; Acryft WK307 manufactured by Sumitomo Chemical Co., Ltd., ethylene 75% by weight, MMA 25% by weight, abbreviated as EMMA) 70% by weight High density polyethylene (trade name; Hi-Zex 3300F, abbreviated as HDPE) ) 30 wt% lubricant (fatty acid amide) 500 ppm
【００２２】下記の組成の誘電率２．４のポリオレフィ
ン系樹脂組成物を用いて押出成形により厚さ約１００μ
ｍの包材本体４用シートを成形した。成形性は良好であ
った。 ＥＭＭＡ ７０重量％ ＨＤＰＥ ２０重量％ ＥＶＡ ３重量％ 帯電防止剤 ２重量％ 白色顔料 ５重量％ 但し、上記ＥＶＡはエチレン酢酸ビニル共重合体（商品
名；エバテートＨ４０１１、ＶＡ含有量２０重量％、住
友化学（株）製）である。次いで、ファスナー雌部３ａ
を包材本体４用シートの一端に上記の高周波ウエルダー
を用いて上記条件で高周波誘電加熱により融着し、ファ
スナー雄部３ｂを該包材本体４用シートの他端に同様に
して高周波誘電加熱により融着した。そしてファスナー
雄部とファスナー雌部とをポリオキシメチレン樹脂製ス
ライダーを用いて雌雄嵌合させ、４連型を用いて２００
０ショット／日の製造速度で同様にして高周波誘電加熱
により融着・溶断して、本発明のスライダーが付いたフ
ァスナー付包材を製造した。この包材のファスナー雌雄
嵌合強度、ファスナー部同士のシール強度、ファスナー
部と包材本体とのシール強度、包材本体同士のシール強
度、スライダーをスライドさせた時のスライド性などを
試験した結果をまとめて表１に示す。Using a polyolefin resin composition having a dielectric constant of 2.4 having the following composition, a thickness of about 100 μm was obtained by extrusion molding.
The sheet for the packaging material main body 4 of m was formed. The moldability was good. EMMA 70% by weight HDPE 20% by weight EVA 3% by weight Antistatic agent 2% by weight White pigment 5% by weight However, the above EVA is an ethylene vinyl acetate copolymer (trade name; Evatate H4011, VA content 20% by weight, Sumitomo Chemical Manufactured by Co., Ltd.). Then, the fastener female portion 3a
The fused by high-frequency dielectric heating under the above conditions by using the high-frequency welder to one end of the sheet for packaging material body 4, in the same manner fastener male part 3b at the other end of the sheet for該包material body 4 high-frequency dielectric heating Fused. Then, the male fastener portion and the female fastener portion are mated with each other by using a slider made of polyoxymethylene resin, and a quadruple type is used.
Similarly, at the production rate of 0 shots / day, fusion and fusion were performed by high frequency dielectric heating to produce a fastener-equipped packaging material with a slider of the present invention. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1.
【００２３】（実施例２） 下記の組成の誘電率２．５〜２．７のポリオレフィン系
樹脂組成物を用いて、実施例１と同様にして図９に示す
厚さ約３００μｍのファスナー雌部３ａおよびファスナ
ー雄部３ｂを押出成形により寸法精度よく異型成形し
た。 ＥＭＭＡ ７０重量％ ＨＤＰＥ ３０重量％ 滑剤（脂肪酸アマイド） １０００ｐｐｍ 実施例１で成形した包材本体を用いて、実施例１と同様
にして、本発明のスライダーが付いたファスナー付包材
を製造した。この包材のファスナー雌雄嵌合強度、ファ
スナー部同士のシール強度、ファスナー部と包材本体と
のシール強度、包材本体同士のシール強度、スライダー
をスライドさせた時のスライド性などを試験した結果を
まとめて表１に示す。Example 2 Using a polyolefin resin composition having a dielectric constant of 2.5 to 2.7 having the following composition, a fastener female portion having a thickness of about 300 μm shown in FIG. 3a and the male part 3b of the fastener were molded by extrusion molding with high dimensional accuracy. EMMA 70 wt% HDPE 30 wt% Lubricant (fatty acid amide) 1000 ppm Using the packaging material body molded in Example 1, a slider-attached packaging material with a slider of the present invention was manufactured in the same manner as in Example 1. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1.
【００２４】（実施例３） 下記の組成の誘電率２．５〜２．７のポリオレフィン系
樹脂組成物を用いて、実施例１と同様にして図９に示す
厚さ約３００μｍのファスナー雌部３ａおよびファスナ
ー雄部３ｂを押出成形により寸法精度よく異型成形し
た。 ＥＭＭＡ ７０重量％ ＨＤＰＥ ３０重量％ 滑剤（脂肪酸アマイド） １０００ｐｐｍ 以上の組成物に対してＥＶＡを１２重量％配合した組成
物。実施例１で成形した包材本体を用いて、実施例１と
同様にして、本発明のスライダーが付いたファスナー付
包材を製造した。この包材のファスナー雌雄嵌合強度、
ファスナー部同士のシール強度、ファスナー部と包材本
体とのシール強度、包材本体同士のシール強度、スライ
ダーをスライドさせた時のスライド性などを試験した結
果をまとめて表１に示す。(Example 3) A polyolefin resin composition having a dielectric constant of 2.5 to 2.7 having the following composition was used, and in the same manner as in Example 1, a fastener female portion having a thickness of about 300 μm shown in FIG. 9 was obtained. 3a and the male part 3b of the fastener were molded by extrusion molding with high dimensional accuracy. EMMA 70% by weight HDPE 30% by weight Lubricant (fatty acid amide) Composition in which 12% by weight of EVA is blended with 1000 ppm or more of the composition. Using the packaging material body molded in Example 1, a fastener-equipped packaging material with a slider of the present invention was manufactured in the same manner as in Example 1. The fastener mating strength of this packaging material,
Table 1 shows a summary of the results of testing the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, the slidability when the slider is slid, and the like.
【００２５】（比較例１） アイオノマー（商品名；ハイミラン１６５２、三井デュ
ポン（株）製）を用いて、実施例１と同様にして図９に
示す厚さ約３００μｍのファスナー雌部３ａおよびファ
スナー雄部３ｂを押出成形により異型成形した。実施例
１で成形した包材本体を用いて、実施例１と同様にし
て、スライダーが付いたファスナー付包材を製造した。
この包材のファスナー雌雄嵌合強度、ファスナー部同士
のシール強度、ファスナー部と包材本体とのシール強
度、包材本体同士のシール強度、スライダーをスライド
させた時のスライド性などを試験した結果をまとめて表
１に示す。ファスナー雌雄嵌合強度は高いが、ファスナ
ー成形性が悪くファスナーがやや反ったり、曲がったり
した。また、スライダーの摺動が重く、スライダー摺動
時に削りかすがでた。ファスナー同士の融着ができず、
シール性が悪い。(Comparative Example 1) Using an ionomer (trade name: Himilan 1652, manufactured by Mitsui DuPont Co., Ltd.), a female fastener portion 3a and a male fastener portion having a thickness of about 300 μm shown in FIG. The part 3b was molded by extrusion molding. Using the packaging material body formed in Example 1, a slider-attached packaging material with a fastener was manufactured in the same manner as in Example 1.
The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. Fasteners Male and female mating strength is high, but the fastener moldability was poor and the fastener was slightly warped or bent. In addition, the slider slides heavily, and some shavings were generated when the slider slid. The fasteners cannot be fused together,
Poor sealing.
【００２６】（比較例２） ＥＭＭＡとアイオノマーとの重量比１：２の組成物を用
いて、実施例１と同様にして図９に示す厚さ約３００μ
ｍのファスナー雌部３ａおよびファスナー雄部３ｂを押
出成形により異型成形した。実施例１で成形した包材本
体を用いて、実施例１と同様にして、スライダーが付い
たファスナー付包材を製造した。この包材のファスナー
雌雄嵌合強度、ファスナー部同士のシール強度、ファス
ナー部と包材本体とのシール強度、包材本体同士のシー
ル強度、スライダーをスライドさせた時のスライド性な
どを試験した結果をまとめて表１に示す。ファスナー雌
雄嵌合強度は高いが、ファスナー成形性が悪く、ファス
ナーが反ったり、曲がったり、寸法精度が悪いので雌雄
嵌合しない時があった。スライダーの摺動が重い。ファ
スナー同士の融着ができず、シール性が悪い。(Comparative Example 2) A composition having a weight ratio of EMMA and ionomer of 1: 2 was used in the same manner as in Example 1 to obtain a thickness of about 300 μm as shown in FIG.
The fastener female part 3a and the male fastener part 3b of m were molded by extrusion molding. Using the packaging material body formed in Example 1, a slider-attached packaging material with a fastener was manufactured in the same manner as in Example 1. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. Although the male-female fitting strength of the fastener is high, the fastener moldability is poor, and the fastener is warped or bent, and the dimensional accuracy is poor, so that the male-male fitting may not be performed. The slider slides heavily. The fasteners cannot be fused together and the sealing performance is poor.
【００２７】（比較例３） アイオノマーとＥＶＡ（商品名；エバテートＨ４０１
１、ＶＡ含有量１０重量％、住友化学（株）製）の重量
比１：２の組成物を用いて、実施例１と同様にして図９
に示す厚さ約３００μｍのファスナー雌部３ａおよびフ
ァスナー雄部３ｂを押出成形により異型成形した。実施
例１で成形した包材本体を用いて、実施例１と同様にし
て、スライダーが付いたファスナー付包材を製造した。
この包材のファスナー雌雄嵌合強度、ファスナー部同士
のシール強度、ファスナー部と包材本体とのシール強
度、包材本体同士のシール強度、スライダーをスライド
させた時のスライド性などを試験した結果をまとめて表
１に示す。ファスナー雌雄嵌合強度は高いが、ファスナ
ー成形性が悪く、ファスナーがやや反ったり、曲がった
り、寸法精度が悪いので雌雄嵌合しない時があった。ス
ライダーの摺動が重い。ファスナー同士の融着ができ
ず、シール性が悪い。(Comparative Example 3) Ionomer and EVA (trade name: EvaTate H401)
9 was carried out in the same manner as in Example 1 except that the composition having the VA content of 10% by weight and the weight ratio of Sumitomo Chemical Co., Ltd. of 1: 2 was used.
The fastener female portion 3a and the fastener male portion 3b having a thickness of about 300 μm shown in FIG. Using the packaging material body formed in Example 1, a slider-attached packaging material with a fastener was manufactured in the same manner as in Example 1.
The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. Although the male-female fitting strength of the fastener is high, the moldability of the fastener is poor, and the fastener is slightly warped or bent, and the dimensional accuracy is poor, so that the male-male fitting is sometimes not performed. The slider slides heavily. The fasteners cannot be fused together and the sealing performance is poor.
【００２８】（比較例４） ＰＶＣ製ファスナー雌部３ａおよびＰＶＣ製ファスナー
雄部３ｂ（吉田工業（株）製、商品名；３ＰＶＨ）を用
い、実施例１で成形した包材本体を用いて、実施例１と
同様にして、スライダーが付いたファスナー付包材を製
造した。この包材のファスナー雌雄嵌合強度、ファスナ
ー部同士のシール強度、ファスナー部と包材本体とのシ
ール強度、包材本体同士のシール強度、スライダーをス
ライドさせた時のスライド性などを試験した結果をまと
めて表１に示す。ファスナー部と包材本体が融着でき
ず、シール性が悪い。(Comparative Example 4) Using the female part 3a made of PVC and the male part 3b made of PVC (manufactured by Yoshida Kogyo Co., Ltd., trade name: 3PVH), the packaging material body molded in Example 1 was used. In the same manner as in Example 1, a fastener-attached packaging material with sliders was manufactured. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. The fastener part and the packaging material body cannot be fused and the sealing performance is poor.
【００２９】（比較例５） ＨＤＰＥを用いて、実施例１と同様にして図９に示す厚
さ約３００μｍのファスナー雌部３ａおよびファスナー
雄部３ｂを押出成形により異型成形した。実施例１で成
形した包材本体を用いて、実施例１と同様にして、スラ
イダーが付いたファスナー付包材を製造した。この包材
のファスナー雌雄嵌合強度、ファスナー部同士のシール
強度、ファスナー部と包材本体とのシール強度、包材本
体同士のシール強度、スライダーをスライドさせた時の
スライド性などを試験した結果をまとめて表１に示す。
ファスナー雌雄嵌合強度は高いが、ファスナー同士の融
着ができず、シール性が悪い。Comparative Example 5 Using HDPE, the female fastener portion 3a and the male fastener portion 3b having a thickness of about 300 μm shown in FIG. 9 were molded by extrusion molding in the same manner as in Example 1. Using the packaging material body formed in Example 1, a slider-attached packaging material with a fastener was manufactured in the same manner as in Example 1. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1.
Fastener male and female mating strength is high, but the fasteners cannot be fused and the sealing performance is poor.
【００３０】（比較例６） ＥＶＡ（商品名；エバテートＨ４０１１、ＶＡ含有量５
重量％、住友化学（株）製）を用いて、実施例１と同様
にして図９に示す厚さ約３００μｍのファスナー雌部３
ａおよびファスナー雄部３ｂを押出成形により異型成形
した。実施例１で成形した包材本体を用いて、実施例１
と同様にして、スライダーが付いたファスナー付包材を
製造した。この包材のファスナー雌雄嵌合強度、ファス
ナー部同士のシール強度、ファスナー部と包材本体との
シール強度、包材本体同士のシール強度、スライダーを
スライドさせた時のスライド性などを試験した結果をま
とめて表１に示す。ファスナー雌雄嵌合強度が低く、フ
ァスナー同士の融着ができず、シール性が悪い。Comparative Example 6 EVA (trade name: Evatate H4011, VA content 5)
% By weight, manufactured by Sumitomo Chemical Co., Ltd., in the same manner as in Example 1 and shown in FIG.
The a and the male part 3b of the fastener were molded by extrusion molding. Example 1 using the packaging material body molded in Example 1
In the same manner as described above, a packaging material with a fastener having a slider was manufactured. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. The male and female fasteners have low mating strength, the fasteners cannot be fused together, and the sealing performance is poor.
【００３１】（比較例７） ＥＶＡ（商品名；エバテートＨ４０１１、ＶＡ含有量７
重量％、住友化学（株）製）を用いて、実施例１と同様
にして図９に示す厚さ約３００μｍのファスナー雌部３
ａおよびファスナー雄部３ｂを押出成形により異型成形
した。実施例１で成形した包材本体を用いて、実施例１
と同様にして、スライダーが付いたファスナー付包材を
製造した。この包材のファスナー雌雄嵌合強度、ファス
ナー部同士のシール強度、ファスナー部と包材本体との
シール強度、包材本体同士のシール強度、スライダーを
スライドさせた時のスライド性などを試験した結果をま
とめて表１に示す。ファスナー成形性、スライド性が悪
く、ファスナー雌雄嵌合強度が低く、ファスナー同士の
融着ができず、シール性が悪い。Comparative Example 7 EVA (trade name: Evatate H4011, VA content 7)
% By weight, manufactured by Sumitomo Chemical Co., Ltd., in the same manner as in Example 1 and shown in FIG.
The a and the male part 3b of the fastener were molded by extrusion molding. Example 1 using the packaging material body molded in Example 1
In the same manner as described above, a packaging material with a fastener having a slider was manufactured. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. The fastener moldability and slidability are poor, the fastener male and female fitting strength is low, the fasteners cannot be fused together, and the sealing property is poor.
【００３２】（比較例８） ＥＶＡ（商品名；エバテートＨ４０１１、ＶＡ含有量１
５重量％、住友化学（株）製）を用いて、実施例１と同
様にして図９に示す厚さ約３００μｍのファスナー雌部
３ａおよびファスナー雄部３ｂを押出成形により異型成
形した。実施例１で成形した包材本体を用いて、実施例
１と同様にして、スライダーが付いたファスナー付包材
を製造した。この包材のファスナー雌雄嵌合強度、ファ
スナー部同士のシール強度、ファスナー部と包材本体と
のシール強度、包材本体同士のシール強度、スライダー
をスライドさせた時のスライド性などを試験した結果を
まとめて表１に示す。ファスナー成形性、スライド性が
悪く、ファスナー雌雄嵌合強度は高いが、ファスナー同
士の融着ができず、シール性が悪い。Comparative Example 8 EVA (trade name: Evatate H4011, VA content 1)
Using 5% by weight of Sumitomo Chemical Co., Ltd., the fastener female portion 3a and the fastener male portion 3b having a thickness of about 300 μm shown in FIG. 9 were molded by extrusion in the same manner as in Example 1. Using the packaging material body formed in Example 1, a slider-attached packaging material with a fastener was manufactured in the same manner as in Example 1. The results of testing the fastener male and female mating strength of this packaging material, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slidability when the slider is slid Are collectively shown in Table 1. The fastener moldability and slidability are poor, and the fastener male / female fitting strength is high, but the fasteners cannot be fused and the sealing performance is poor.
【００３３】 ファスナー成形性の評価； ○；反り、曲がりがなく、寸法精度よく成形できる。 △；反り、曲がりがややでる。寸法精度がやや悪い。 ×；反り、曲がりがでる。寸法精度が悪い。成形不能の場合もある。 スライド性の評価； ○；スライダーをスムースに摺動でき、けずりかすがでない。 △；２０〜３０回のスライダーの摺動でけずりかすがでる。 ×；スライダーをスムースに摺動できない。Evaluation of fastener moldability: ◯: Molding can be performed with high dimensional accuracy without warping or bending. Δ: Warp and bend are slightly. The dimensional accuracy is a little poor. ×: Warp or bend. The dimensional accuracy is poor. In some cases it cannot be molded. Evaluation of slidability; ◯; The slider can be slid smoothly and there is no scum. Δ: Scrape is generated by sliding the slider 20 to 30 times. ×: The slider cannot be slid smoothly.
【００３４】[0034]
【表１】[Table 1]
【００３５】[0035]
【発明の効果】本発明はポリオレフィン製ファスナー付
包材に関するものであり、ファスナー部と包材本体とを
それぞれ別個の高周波誘電加熱により融着・溶断可能な
特定のポリオレフィン系樹脂あるいはその組成物を用い
ることにより寸法精度よくファスナー部を異型成形でき
ると共に、ファスナー雌雄嵌合強度、ファスナー部同士
のシール強度、ファスナー部と包材本体とのシール強
度、包材本体同士のシール強度、スライダーをスライド
させた時のスライド性などの優れたポリオレフィン製フ
ァスナー付包材を、従来のポリ塩化ビニル用高周波ウエ
ルダーを用いて容易に安価に効率よく製造することがで
きる。本発明のポリオレフィン製ファスナー付包材は、
焼却しても有毒ガスなどの発生がなく、リサイクルが容
易など地球環境に優しいポリオレフィン系樹脂あるいは
その組成物を用いているので産業上の利用価値が高い。INDUSTRIAL APPLICABILITY The present invention relates to a wrapping material with a fastener made of polyolefin, and a specific polyolefin resin or a composition thereof capable of fusing and fusing the fastener part and the wrapping material body by separate high frequency dielectric heating. By using it, it is possible to mold the fastener part with high dimensional accuracy, and the strength of the fitting between male and female fasteners, the sealing strength between the fastener parts, the sealing strength between the fastener part and the packaging material body, the sealing strength between the packaging material bodies, and the slider slide. By using the conventional high-frequency welder for polyvinyl chloride, it is possible to easily and efficiently produce a polyolefin-made packaging material with a fastener that is excellent in sliding property. The polyolefin-made packaging material with a fastener of the present invention,
Since it uses a polyolefin resin or its composition that is friendly to the global environment and does not generate toxic gases even when incinerated, and is easy to recycle, it has high industrial utility value.
【図１】 本発明のポリオレフィン製ファスナー付包材
の斜視図である。FIG. 1 is a perspective view of a packaging material with a fastener made of polyolefin of the present invention.
【図２】 本発明のポリオレフィン製ファスナー付包材
のファスナー部を開けた時の斜視図である。FIG. 2 is a perspective view of the packaging material with a fastener made of polyolefin of the present invention when the fastener portion is opened.
【図３】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 3 is a perspective view of another packing material with a fastener made of polyolefin of the present invention.
【図４】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 4 is a perspective view of another packing material with a fastener made of polyolefin of the present invention.
【図５】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 5 is a perspective view of another polyolefin-made packaging material with a fastener of the present invention.
【図６】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 6 is a perspective view of another polyolefin-made fastener wrapping material of the present invention.
【図７】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 7 is a perspective view of another packaging material with a fastener made of polyolefin of the present invention.
【図８】 本発明の他のポリオレフィン製ファスナー付
包材の斜視図である。FIG. 8 is a perspective view of another packaging material with a fastener made of polyolefin of the present invention.
【図９】 ファスナー雌部３ａおよびファスナー雄部３
ｂの拡大斜視図である。FIG. 9: Female fastener 3a and male fastener 3
It is an expansion perspective view of b.
【図１０】 本発明のポリオレフィン製ファスナー付包
材の製造工程を示す説明図である。FIG. 10 is an explanatory view showing a manufacturing process of the packaging material with a fastener made of polyolefin of the present invention.
【図１１】 本発明のポリオレフィン製ファスナー付包
材の他の製造工程を示す説明図である。FIG. 11 is an explanatory view showing another manufacturing process of the packaging material with a fastener made of polyolefin of the present invention.
１、１’、１ａ、１ｂ、１ｃ、１ｄ、１ｅ、１ｆ 本発
明のポリオレフィン製ファスナー付包材の例 ２ スライダー ３ ファスナー部 ３ａ ファスナー雌部 ３ｂ ファスナー雄部 ４ 包材本体 １１ 雌雄嵌合部 １１ａ ファスナー雌部本体 １１ｂ ファスナー雄部本体 １２ ファスナー部同士のシール部 １３ ファスナー部と包材本体とのシール部 １４ 包材本体同士のシール部1, 1 ', 1a, 1b, 1c, 1d, 1e, 1f Examples of the packaging material with a fastener of the present invention 2 Slider 3 Fastening portion 3a Fastening female portion 3b Fastening male portion 4 Packaging material main body 11 Female / male fitting portion 11a Fastener female part main body 11b Fastener male part main body 12 Sealing part between fastener parts 13 Sealing part between fastener part and packaging material body 14 Sealing part between packaging material bodies
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ２９Ｌ 22:00 Ｂ２９Ｌ 22:00 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location B29L 22:00 B29L 22:00
Claims (2)
なるスライダー付ファスナー部と包材本体とからなるフ
ァスナー付包材において、該ファスナー部および該包材
本体はそれぞれ下記の特性を有するポリオレフィン系樹
脂あるいはその組成物からなることを特徴とするポリオ
レフィン製ファスナー付包材。 該ファスナー部： 誘電率２．３以上で高周波誘電加熱により融着・溶断可
能であると共に該ファスナー雌雄嵌合強度１．０Ｋｇ／
１５ｍｍ以上となる剛性を有し、かつ該ファスナー部同
士のシール強度が４．８Ｋｇ／１５ｍｍ以上、該ファス
ナー部と該包材本体とのシール強度が２．５Ｋｇ／１５
ｍｍ以上となるポリオレフィン系樹脂あるいはその組成
物。 該包材本体： 誘電率２．３以上で高周波誘電加熱により融着・溶断可
能であり、かつ該包材本体同士のシール強度が２．９Ｋ
ｇ／１５ｍｍ以上、該ファスナー部と該包材本体とのシ
ール強度が２．５Ｋｇ／１５ｍｍ以上が得られるような
ポリオレフィン系樹脂あるいはその組成物。1. A fastener packaging material comprising a fastener portion with slider and a packaging material body fused and melted by high frequency dielectric heating, wherein the fastener portion and the packaging material body each have a polyolefin-based material having the following characteristics. A packaging material with a fastener made of polyolefin, which is made of a resin or a composition thereof. The fastener part: With a dielectric constant of 2.3 or more, it can be fused and melted by high frequency dielectric heating, and the male and female fitting strength of the fastener is 1.0 kg /
It has a rigidity of 15 mm or more, the sealing strength between the fastener parts is 4.8 kg / 15 mm or more, and the sealing strength between the fastener part and the packaging material body is 2.5 kg / 15.
A polyolefin resin or a composition thereof having a size of not less than mm. The packaging material body: A dielectric constant of 2.3 or more, which can be fused and cut by high frequency dielectric heating, and a sealing strength between the packaging material bodies is 2.9K.
g / 15 mm or more, and a polyolefin resin or a composition thereof, which can obtain a sealing strength between the fastener part and the packaging material body of 2.5 kg / 15 mm or more.
求項１記載のポリオレフィン製ファスナー付包材の製造
方法。 （１）請求項１記載のポリオレフィン系樹脂あるいはそ
の組成物を用いてファスナー雌部およびファスナー雄部
を異型成形する。 （２）請求項１記載のポリオレフィン系樹脂あるいはそ
の組成物を用いて包材本体用フィルムあるいはシートを
成形する。 （３）ファスナー雌部あるいはファスナー雄部を包材本
体用フィルムあるいはシートの一端に高周波誘電加熱に
より融着する工程。 （４）ファスナー雄部あるいはファスナー雌部を該包材
本体用フィルムあるいはシートの他端に高周波誘電加熱
により融着するか、あるいはファスナー雄部あるいはフ
ァスナー雌部を他の包材本体用フィルムあるいはシート
の一端に高周波誘 電加熱により融着する工程。 （５）一端にファスナー雄部を他端にファスナー雌部を
高周波誘電加熱により融着した該包材本体用フィルムあ
るいはシートの該ファスナー雄部と該ファスナー雌部と
をスライダーを用いて雌雄嵌合させるか、あるいはファ
スナー雌部あるいはファスナー雄部を包材本体用フィル
ムあるいはシートの一端に高周波誘電加熱により融着し
たものと、ファスナー雄部あるいはファスナー雌部を他
の包材本体用フィルムあるいはシートの一端に高周波誘
電加熱により融着したものの該ファスナー雄部と該ファ
スナー雌部とをスライダーを用いて雌雄嵌合させ、高周
波誘電加熱により融着・溶断してスライダーが付いたフ
ァスナー付包材を製造する工程。2. The method for manufacturing a packaging material with a fastener made of polyolefin according to claim 1, comprising the following steps. (1) Using the polyolefin-based resin or the composition thereof according to claim 1, the female fastener portion and the male fastener portion are molded by atypical molding. (2) A film or sheet for a packaging material body is molded using the polyolefin resin or its composition according to claim 1. (3) A step of fusion-bonding the female fastener portion or the male fastener portion to one end of the packaging material body film or sheet by high-frequency dielectric heating. (4) A male fastener part or a female fastener part is fused to the other end of the film or sheet for a packaging material body by high frequency dielectric heating, or a male fastener part or a female fastener part is formed on another film or sheet for a packaging material body. a step of fusing by high-frequency induction electric heating end. (5) Male / female fitting of the male fastener portion and the female fastener portion of the film or sheet for the packaging material main body in which a male male portion at one end and a female female portion at the other end are fused by high frequency dielectric heating using a slider. Or a female fastener part or a male fastener part fused to one end of a packaging material film or sheet by high frequency dielectric heating, and a male fastener part or a female fastener part of another packaging material film or sheet. High frequency induction at one end
A step of manufacturing a fastener-equipped packaging material with a slider by fusion-bonding the male fastener portion and the female female portion of the fastener, which are fused by electric heating, by using a slider, and fusing and fusing by high-frequency dielectric heating.